U.S. patent application number 13/682162 was filed with the patent office on 2014-05-22 for copper seed layer for an interconnect structure having a doping concentration level gradient.
This patent application is currently assigned to INTERNATIONAL BUSINESS MACHINES CORPORATION. The applicant listed for this patent is INTERNATIONAL BUSINESS MACHINES CORPORATION, STMICROELECTRONICS, INC.. Invention is credited to Chengyu Niu, Andrew Simon, Yun-Yu Wang, Keith Kwong Hon Wong.
Application Number | 20140138832 13/682162 |
Document ID | / |
Family ID | 50692227 |
Filed Date | 2014-05-22 |
United States Patent
Application |
20140138832 |
Kind Code |
A1 |
Niu; Chengyu ; et
al. |
May 22, 2014 |
COPPER SEED LAYER FOR AN INTERCONNECT STRUCTURE HAVING A DOPING
CONCENTRATION LEVEL GRADIENT
Abstract
A trench is opened in a dielectric layer. The trench is then
lined with a barrier layer and a metal seed layer. The metal seed
layer is non-uniformly doped and exhibits a vertical doping
gradient varying as a function of trench depth. The lined trench is
then filled with a metal fill material. A dielectric cap layer is
then deposited over the metal filled trench. Dopant from the
non-uniformly doped metal seed layer is then migrated to an
interface between the metal filled trench and the dielectric cap
layer to form a self-aligned metal cap.
Inventors: |
Niu; Chengyu; (Fishkill,
NY) ; Simon; Andrew; (Fishkill, NY) ; Wong;
Keith Kwong Hon; (Wappingers Falls, NY) ; Wang;
Yun-Yu; (Poughquag, NY) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
STMICROELECTRONICS, INC.
INTERNATIONAL BUSINESS MACHINES CORPORATION |
Coppell
Armonk |
TX
NY |
US
US |
|
|
Assignee: |
INTERNATIONAL BUSINESS MACHINES
CORPORATION
Armonk
NY
STMICROELECTRONICS, INC.
Coppell
TX
|
Family ID: |
50692227 |
Appl. No.: |
13/682162 |
Filed: |
November 20, 2012 |
Current U.S.
Class: |
257/751 ;
204/298.08; 438/643 |
Current CPC
Class: |
H01L 23/481 20130101;
H01L 21/76871 20130101; H01L 21/76865 20130101; H01L 2924/0002
20130101; H01L 2924/0002 20130101; H01L 21/2855 20130101; H01L
21/76849 20130101; H01L 21/76858 20130101; H01L 2924/00 20130101;
H01L 21/76867 20130101; C23C 14/34 20130101; H01L 21/76873
20130101; H01L 2221/1089 20130101; C23C 14/3464 20130101; C23C
14/046 20130101 |
Class at
Publication: |
257/751 ;
438/643; 204/298.08 |
International
Class: |
H01L 23/48 20060101
H01L023/48; C23C 14/34 20060101 C23C014/34; H01L 21/768 20060101
H01L021/768 |
Claims
1. A process, comprising: opening a trench in a dielectric layer;
lining the trench with a barrier layer; lining the trench with a
metal seed layer, wherein the metal seed layer is non-uniformly
doped and exhibits a vertical doping gradient varying as a function
of trench depth; and filling the trench with a metal fill.
2. The process of claim 1, wherein opening the trench comprises
opening the trench at a location for an interconnect structure of
an integrated circuit.
3. The process of claim 1, wherein the barrier layer is formed of
tantalum nitride.
4. The process of claim 1, wherein the metal seed layer comprises
copper.
5. The process of claim 4, wherein a dopant material of the metal
seed layer is selected from the group consisting of manganese and
aluminum.
6. The process of claim 1, wherein lining the trench with the metal
seed layer comprises: a) depositing an initial metal seed layer
having a doping concentration less than 0.5% with a substantially
vertical deposition direction; b) depositing a doped metal seed
layer having a doping concentration in excess of 0.5% with a
non-vertical angled deposition direction that cause deposition of
the doped metal seed layer at least primarily at upper portions of
the trench.
7. The process of claim 6, further comprising repeating a)
depositing and b) depositing.
8. The process of claim 6, further comprising c) depositing a final
metal seed layer having a doping concentration less than 0.5% with
a substantially vertical deposition direction.
9. The process of claim 6, wherein the doping concentration in
excess of 0.5% is in the range of >0.5% to 10%.
10. The process of claim 1, further comprising depositing a
dielectric cap layer over the metal filled trench.
11. The process of claim 10, further comprising migrating dopant
from the non-uniformly doped metal seed layer to an interface
between the metal filled trench and the dielectric cap layer to
form a self-aligned metal cap.
12. An apparatus, comprising: a trench formed in a dielectric
layer; a barrier layer lining the trench; a metal seed layer lining
the trench, wherein the metal seed layer has a non-uniform dopant
concentration and exhibits a vertical doping gradient varying as a
function of trench depth; and a metal fill that fills the
trench.
13. The apparatus of claim 12, wherein the metal filling the trench
defines an interconnect structure of an integrated circuit.
14. The apparatus of claim 12, wherein the barrier layer is formed
of tantalum nitride.
15. The apparatus of claim 12, wherein the metal seed layer
comprises copper.
16. The apparatus of claim 15, wherein a dopant material of the
metal seed layer is selected from the group consisting of manganese
and aluminum.
17. The apparatus of claim 12, wherein the metal seed layer
comprises: an initial metal seed layer having a doping
concentration less than 0.5%; and a doped metal seed layer having a
doping concentration in excess of 0.5% present at least primarily
at upper portions of the trench.
18. The apparatus of claim 17, further comprising a final metal
seed layer having a doping concentration less than 0.5%.
19. The apparatus of claim 17, wherein the doping concentration in
excess of 0.5% is in the range of >0.5% to 10%.
20. The apparatus of claim 12, further comprising a dielectric cap
layer formed over the metal filled trench.
21. The apparatus of claim 20, further comprising a self-aligned
metal cap formed at an interface between the metal filled trench
and the dielectric cap layer from dopant migrated from the
non-uniformly doped metal seed layer.
22. A sputter chamber, comprising: an enclosure; an inlet to the
enclosure configured to receive processing gas; a sputter target
formed of a metal material and having a doping concentration less
than about 0.5%; an RF coil formed of said metal material and
having a doping concentration in excess of about 0.5%; and a
pedestal configured to support an integrated circuit wafer within
the enclosure.
23. The chamber of claim 22, wherein the doping concentration of
the RF coil in excess of about 0.5% is in the range of >0.5% to
10%.
24. The chamber of claim 22, wherein the metal material comprises
copper.
25. The chamber of claim 24, wherein a dopant material is selected
from the group consisting of manganese and aluminum.
26. The chamber of claim 22, wherein the RF coil is configurable to
operate as an additional sputter target for sputter deposition of
the doped metal material on a surface of the integrated circuit
wafer.
Description
TECHNICAL FIELD
[0001] The present invention relates to a method for manufacturing
integrated circuits and, in particular, to a method for
manufacturing a metal seed layer of an interconnect structure for
an integrated circuit.
BACKGROUND
[0002] The damascene and dual damascene processes for forming
interconnect structures such as metal lines, vias and other
interconnects in integrated circuits are well known to those
skilled in the art. These processes typically require the formation
of a metal seed layer over a wafer surface (including on the side
walls and floor of any trench structures produced at locations
where metal interconnect structures are desired). The seed layer is
required in order to provide a low-resistance electrical path which
supports a subsequent uniform metal electroplating over the wafer
surface to be accomplished. The metal electroplating process fills
the lined trench structures and defines the resulting interconnect
structures of a metallization layer for the integrated circuit.
[0003] Reference is now made to FIGS. 1A-1F (not drawn to scale)
which illustrate process steps for forming a metal interconnect
structure of an integrated circuit in accordance with the prior
art. The known damascene process may generally be described as
follows: As shown in FIG. 1A, a wafer 10 is formed which comprises
a semiconductor substrate 12 including integrated circuit devices
formed in and/or on the substrate (not shown), a pre-metal
dielectric (PMD) layer 14 overlying the substrate, and a plurality
of electrical contact members 16, such as tungsten plugs or the
like, extending through the PMD layer to reach the integrated
circuit devices. The pre-metal dielectric (PMD) layer 14 is
planarized using, for example, chemical mechanical polishing (CMP)
to provide a flat surface for supporting metallization layers of
the integrated circuit device. Next, a low-k intermetal dielectric
layer 18 is provided over the PMD layer 14 (FIG. 1B), the
dielectric layer 18 for example being formed of a multilayer
structure including a low-k layer and one or mask layers (for
example including a TEOS mask and titanium nitride mask). This
low-k intermetal dielectric layer 18 is also planarized. A trench
20 is then formed extending into and perhaps through the low-k
intermetal dielectric layer 18 (FIG. 1C). The trench 20 is provided
at a location where an interconnect structure is to be located, and
in a preferred implementation will have a depth sufficient to
expose the top surface of the underlying electrical contact member
16. A blanket formation of a diffusion barrier layer 22 is then
made (FIG. 1D) on the wafer (including over the top of the low-k
intermetal dielectric layer 18 and on the side walls and floor
within the trench 20). This diffusion barrier layer 22 serves to
block the migration of subsequently deposited metal atoms for the
interconnect structure into the low-k intermetal dielectric layer,
as well as block the diffusion in the opposite direction of
contaminants from the low-k intermetal dielectric layer to the
interconnect structure. Next, a metal seed layer 24 is formed on
the wafer (FIG. 1E) using any suitable deposition process such as
sputtering over the diffusion barrier layer 22. This seed layer 24
covers the diffusion barrier layer 22 on the top surface of the
low-k intermetal dielectric layer 18 as well as the side walls and
floor of the trench 20. Optionally, a metal liner layer (not shown)
may be deposited between the diffusion barrier layer 22 and the
metal seed layer 24. Further optionally, a seed layer etchback (not
shown) may be performed to reduce metal overhang at the top corners
of the trench 20. An electroplating process is then performed on
the wafer to cause the remaining open portion of the trench 20 to
be filled with metal 26 (FIG. 1F). Electroplated metal is also
produced above the top of the wafer. Chemical mechanical polishing
(CMP) is then performed to remove the excess and unwanted portions
of the diffusion barrier layer 22, the metal seed layer 24 and the
electroplated metal 26 which are located outside of the trench
(FIG. 1G). The polishing operation further provides a flat top
surface for the wafer that is ready for further integrated circuit
processing. As part of that further processing, a dielectric cap
layer 28 may be deposited on the flat top surface to protect the
low-k intermetal dielectric layer and the metal layers and
materials of the formed metal lines and interconnects (FIG.
1H).
[0004] The processes of FIGS. 1B-1H may then be repeated, as
needed, to form additional metallization layers for the integrated
circuit device. In this context, it will be understood that the
underlying electrical contact member 16 could thus comprise the
metal filled trench of an underlying metallization layer and the
dielectric cap layer 28 could thus comprise one of the layers
within the low-k intermetal dielectric layer 18.
[0005] The metal selected for the metal seed layer 24 and the
electroplated metal 26 is typically copper. The diffusion barrier
layer 22 is typically tantalum nitride. It will, of course, be
understood that other materials could instead be chosen.
[0006] It is known in the art to add a dopant material to the
copper sputtering target used in the deposition of the metal seed
layer 24 (i.e., the sputtering target is formed of copper alloyed
with another material). For example, the dopant may comprise
manganese (Mn) or aluminum (Al). The added dopant material will
typically be substantially uniformly distributed throughout the
deposited copper seed layer 24. In other words, and with reference
to concentration line 302 in FIG. 3, there will exist a relatively
uniform doping concentration as a function of trench depth for the
metal seed layer 24.
[0007] During the high temperature process used to form the
dielectric cap layer 28, as well as during further other thermal
cycles and processing operations associated with completing
fabrication of the integrated circuit (such as with the addition of
further metallization layers), those skilled in the art understand
that the added dopant species may migrate from the copper seed
layer 24 and diffuse through the electroplated copper metal 26 fill
to form a self-aligned metal cap located at the interface 30
between the dielectric cap layer 28 and the electroplated copper
metal 26 which fills the trench 20. It is desirable for a high
percentage of the added dopant species to migrate from the seed
layer 24 to the interface 30 between the dielectric cap layer 28
and the electroplated metal 26 which fills the trench 20 because
this interface tends to be the initiation area of copper
electromigration which can lead to circuit failure. However, a not
insignificant fraction of the added dopant species, especially the
dopant species located in the copper seed layer 24 near the bottom
of the trench 20, have difficulty in successfully migrating to the
interface 30 area for the self-aligned metal cap. The reasons for
this failure include: the traveling distance is too long, the
migration time is too short, and dopant species trapping locations
may exist within the electroplated metal 26 fill near the bottom of
the trench 20. The trapped or unsuccessfully migrated doping
species can significantly affect subsequent copper grain growth and
produce an unacceptable increase in copper line resistance.
[0008] Thus, it is desirable to segregate the doping species toward
the interface 30. The failure to segregate can result in shorter
electromigration life time and increased metal line resistance. The
retention of doping species in the seed layer or fill away from the
interface affects copper grain growth resulting in copper
microstructures with high electrical resistance.
[0009] As semiconductor processing techniques move to finer
geometries, the interface 30 between the electroplated copper metal
26 fill and the dielectric cap layer 28 presents a significant
challenge to ensuring satisfactory reliability performance. There
would be an advantage to having a seed layer formation process
which supports better segregation of the dopant species from the
seed layer 24 to the interface 30 in order to form a self-aligned
metal cap where there would otherwise not exist a sufficient
barrier or adhesion layer.
SUMMARY
[0010] In an embodiment, a process comprises: opening a trench in a
dielectric layer; lining the trench with a barrier layer; lining
the trench with a metal seed layer, wherein the metal seed layer is
non-uniformly doped and exhibits a vertical doping gradient varying
as a function of trench depth; and filling the trench with a metal
fill.
[0011] In an embodiment, an apparatus comprises: a trench formed in
a dielectric layer; a barrier layer lining the trench; a metal seed
layer lining the trench, wherein the metal seed layer has a
non-uniform dopant concentration and exhibits a vertical doping
gradient varying as a function of trench depth; and a metal fill
that fills the trench.
[0012] In an embodiment, a sputter chamber comprises: an enclosure;
an inlet to the enclosure configured to receive processing gas; a
sputter target formed of a metal material and having a doping
concentration less than about 0.5%; an RF coil formed of said metal
material and having a doping concentration in excess of about 0.5%;
and a pedestal configured to support an integrated circuit wafer
within the enclosure.
BRIEF DESCRIPTION OF THE DRAWINGS
[0013] For a better understanding of the embodiments, reference
will now be made by way of example only to the accompanying figures
in which:
[0014] FIGS. 1A to 1H illustrate process steps for forming a metal
interconnect structure of an integrated circuit in accordance with
the prior art;
[0015] FIGS. 2A to 2I illustrate process steps for forming a metal
interconnect structure of an integrated circuit;
[0016] FIG. 3 is a graph illustrating doping concentration of the
metal seed layer as a function of trench depth;
[0017] FIGS. 4A to 4E illustrate process steps for forming a
non-uniformly doped metal seed layer; and
[0018] FIG. 5 is a diagram of a sputter chamber suited for
implementing the processes described above for forming a
non-uniformly doped metal seed layer.
DETAILED DESCRIPTION OF THE DRAWINGS
[0019] Reference is now made to FIGS. 2A-2I (not drawn to scale)
which illustrate process steps for forming a metal interconnect
structure of an integrated circuit. As shown in FIG. 2A, a wafer
110 is formed which comprises a semiconductor substrate 112
including integrated circuit devices formed in and/or on the
substrate (not shown), a pre-metal dielectric (PMD) layer 114
overlying the substrate, and a plurality of electrical contact
members 116, such as tungsten plugs or the like, extending through
the PMD layer to reach the integrated circuit devices. The
pre-metal dielectric (PMD) layer 114 is planarized using, for
example, chemical mechanical polishing (CMP) to provide a flat
surface for supporting metallization layers of the integrated
circuit device. Next, a low-k intermetal dielectric layer 118 is
provided over the PMD layer 114 (FIG. 2B), the dielectric layer 118
for example being formed of a multilayer structure including a
low-k layer and one or mask layers (for example including a TEOS
mask and titanium nitride mask). This low-k intermetal dielectric
layer 118 is also planarized. A trench 120 is then formed extending
into and perhaps through the low-k intermetal dielectric layer 118
(FIG. 2C). The trench 120 is provided at a location where an
interconnect structure is to be located, for example exposing a top
surface of the underlying electrical contact member 116. A blanket
formation of a diffusion barrier layer 122 is then made (FIG. 2D).
This diffusion barrier layer 122 serves to block the migration of
subsequently deposited metal atoms for the interconnect structure
into the low-k intermetal dielectric layer, as well as block the
diffusion in the opposite direction of contaminants from the low-k
intermetal dielectric layer to the interconnect structure.
[0020] Next, a metal seed layer 124 is formed on the wafer (FIG.
2E) using a unique deposition process for sputtering metal over the
diffusion barrier layer 122. This seed layer covers the diffusion
barrier layer 122 on the top surface of the low-k intermetal
dielectric layer 118 as well as the side walls and floor of the
trench 120. While the metal seed layer 24 of the prior art process
(deposited as shown in FIG. 1E using conventional techniques) was
either un-doped or substantially uniformly doped (for example, with
manganese (Mn) or aluminum (Al)), the metal seed layer 124 in FIG.
2E is non-uniformly doped and indeed uniquely exhibits a vertical
doping gradient (i.e., the concentration of dopant species in the
metal seed layer 124 varies by decreasing as a function of depth).
The stippling of the metal seed layer 124 in FIG. 2E illustrates
the vertical doping gradient where a higher concentration of dopant
species is present on the top surface of the low-k intermetal
dielectric layer 118 and at and near the top of the trench 120,
while there is little to no dopant present in the metal seed layer
124 at or near the bottom of the trench 120.
[0021] Reference is now made to FIG. 3 which shows a graph
illustrating the doping concentration 300 of the metal seed layer
124 as a function of trench depth. For comparison purposes, the
relatively uniform doping concentration 302 as a function of trench
depth for the metal seed layer 24 of the prior art process (FIG.
1E) is also illustrated. As an exemplary implementation, the
relatively uniform doping concentration 302 may be at or about 0.5%
and the gradient for the non-uniform doping concentration 300 may
extend from about 0% at the bottom of the trench to about 5%-10% at
the top of the trench. Trench depth may, for example, be about
100-200 nm and more particularly be about 150 nm.
[0022] Optionally, a metal liner layer (not shown) may be deposited
between the diffusion barrier layer 122 and the metal seed layer
124.
[0023] The formation of the non-uniformly doped metal seed layer
124 may be accomplished using the process illustrated in FIGS.
4A-4E (not drawn to scale). In FIG. 4A, a metal layer 124(1) is
deposited over the diffusion barrier layer 122. The metal layer
124(1) is preferably a pure copper layer. Alternatively, the metal
layer 124(1) may be very lightly and uniformly doped (for example,
with a dopant concentration of 0.5% or less). This metal layer
124(1) comprises an initial copper seed layer that is preferably
deposited from a copper sputter target 400 in a substantially
vertical direction (as shown by the dotted arrows) in a manner
known to those skilled in the art. The sputter target 400 is
preferably pure copper, but may be very lightly doped (for example,
with a dopant concentration of 0.5% or less).
[0024] The metal layer 124(1) typically will not exhibit a uniform
thickness in its deposition and will include overhang areas 224
near the top of the trench 120. In FIG. 4B, an etchback is
performed to remove the overhang areas 224 leaving a metal layer
124(2) having a more uniform thickness. It will be understood that
the performance of the overhang etchback step is optional, and not
needed in instances where thickness of the metal layer 124(1)
deposition is more uniformly controllable or where the aspect ratio
of the trench 120 is relatively low or where the width of the
trench 120 is relatively large). The etchback process is
accomplished, for example, by the use of positively charged copper
ions (generated by self-ionized plasma near the copper sputter
target 400) and/or argon ions (generated by RF power (from supply
404) that is supplied to an RF coil 402 located between the copper
sputter target 400 and the wafer 110 substrate 112) that are
accelerated by a negative wafer bias voltage (applied by supply
406). The energetic ions function to remove the copper overhang
areas 224 at the top of the trench 120, thereby providing a larger
gap opening 408 in support of subsequent process steps.
[0025] In FIG. 4C, a metal layer 124(3) is deposited over the metal
layer 124(2). The metal layer 124(3) is a doped copper layer (for
example, having a dopant concentration far in excess of 0.5%, and
for example having a dopant concentration in the range of 0.5% to
10%, and more specifically in the range of 5% to 10%). The metal
layer 124(3) is deposited as a sputter primarily (and perhaps
exclusively) from the RF coil 402. To support sputter deposition of
the doped copper layer 124(3), the RF coil 402 is provided as a
copper coil that has been doped with a dopant concentration far in
excess of 0.5%. The RF coil 402 can be used instead of the sputter
target 400 as the sputter source, for example, through an
appropriate configuration of power supplied by the power supply
404. Because the sputter target for doped copper deposition is the
RF coil 402 instead of the sputter target 400, the sputtered
deposition has an angular orientation (i.e., it is non-vertically
directional as illustrated by the dotted arrows) and occurs
primarily on the top of the wafer 110, at the top corners of the
trench 120 and at the top of the trench side walls. Very little, if
any, deposition is made on the floor of the trench or bottom of the
trench side walls. The non-vertically directional deposition may,
for example, have an angle of 20 to 60 degrees measured from the
surface of the wafer and is determined by the placement of the RF
coil 402 relative to the wafer.
[0026] As the metal layer 124(3) and metal layer 124(2) are both
copper layers, the layered distinction illustrated in FIG. 4C is
not representative of the actual structure and is instead more
illustrative of the processing operation. In actuality, the metal
layers 124(2) and 124(3) will merge. The merged metal layers 124(2)
and 124(3) will not exhibit a uniform thickness and will include
overhang areas 226 near the top of the trench 120. Furthermore, the
merged metal layers 124(2) and 124(3) will exhibit a non-uniform
doping concentration where the concentration of dopant present in
the merged metal layers decreases as a function of trench
depth.
[0027] In FIG. 4D an etchback is performed to remove the overhang
areas 226 leaving a non-uniformly doped metal layer 124(4) having a
more uniform thickness. It will be understood that the performance
of the overhang etchback step is optional. The etchback process is
accomplished, for example, by the use of positively charged copper
ions (generated by self-ionized plasma near the copper sputter
target) and/or argon ions (generated by RF power (from supply 404)
that is supplied to the RF coil 402 located between the copper
sputter target 400 and the wafer 110 substrate 112) that are
accelerated by a negative wafer bias voltage (from supply 406). The
energetic ions function to remove the copper overhang areas 226 at
the top of the trench 120, thereby providing a larger gap opening
408 for subsequent process steps. Additionally, or alternatively,
thermal or ion-assisted reflow can be performed to open the top of
the trench 120.
[0028] The process steps illustrated in FIGS. 4C and 4D can be
repeated as often as necessary to produce a non-uniformly doped
metal seed layer 124 with a desired doping level, coverage profile
and/or thickness. Such a non-uniformly doped metal seed layer 124
is shown in FIG. 2E.
[0029] In FIG. 4E, a metal layer 124(5) is optionally deposited
over the non-uniformly doped metal layer 124(4). The metal layer
124(5) is preferably a pure copper layer. Alternatively, the metal
layer 124(5) may be very lightly doped (for example, with a dopant
concentration of 0.5% or less). This metal layer 124(5) comprises a
final copper flash layer that is preferably deposited from the
copper sputter target 400 in a substantially vertical direction (as
shown by the dotted arrows) in a manner known to those skilled in
the art. The sputter target 400 is preferably pure copper, but may
be very lightly doped (for example, with a dopant concentration of
0.5% or less). This optional final copper flash layer serves to
cover up areas in the trench 120 that may have marginal copper seed
due to performance of the previously executed etchback and reflow
operations. This completes the formation of the metal seed layer
124 shown in FIG. 2E.
[0030] Reference is once again made to FIGS. 2A-2I. An
electroplating process is then performed on the wafer to fill the
remaining open portion of the trench 120 with metal 126 (FIG. 2F).
Electroplated metal is also produced above the top of the wafer.
Chemical mechanical polishing (CMP) is then performed to remove the
excess and unwanted portions of the diffusion barrier layer 122,
the metal seed layer 124 and the electroplated metal 126 that are
located outside of the trench (FIG. 2G). The polishing operation
further provides a flat top surface for the wafer that is ready for
further integrated circuit processing. As part of that further
processing, a dielectric cap layer 128 may be deposited on the flat
top surface to protect the low-k intermetal dielectric layer and
the metal layers and materials of the formed metal lines and
interconnects (FIG. 2H).
[0031] The processes of FIGS. 2B-2H may then be repeated, as
needed, to form additional metallization layers for the integrated
circuit device. In this context, it will be understood that the
underlying electrical contact member 116 could thus comprise the
filled trench of an underlying metallization layer and the
dielectric cap layer 128 could thus comprise one of the layers
within the low-k intermetal dielectric layer 118.
[0032] The performance of the high temperature process used to form
the dielectric cap layer 128, as well as the performance of other
thermal cycles and processing operations associated with completing
fabrication of the integrated circuit (such as with the addition of
further metallization layers), causes a migration of the dopant
species from the non-uniformly doped seed layer 124 towards the
interface 130 between the dielectric cap layer 128 and the
electroplated metal 126 which fills the trench 120. This migration
forms a self-aligned metal cap 132 (FIG. 2I). Because the
non-uniformly doped seed layer 124 has a doping gradient presenting
a higher dopant concentration close to the top of the trench 120,
the dopant species are presented with a shorter migration distance
to reach the interface 130 location for the self-aligned metal cap
132. Furthermore, there is less likelihood of the doping species
being trapped before completing migrating to the interface 130. As
a result, an integrated circuit including the structure shown in
FIG. 2I possesses decreased copper liner resistance, better
formation of a barrier or adhesion layer at the interface, and
better reliability (lower circuit failure rate) relative to the
embodiment shown in FIG. 1H.
[0033] The metal selected for the metal seed layer 124 and the
electroplated metal 126 is typically copper. The diffusion barrier
layer 122 is typically tantalum nitride. The dopant species may
comprise manganese (Mn) or aluminum (Al).
[0034] Although illustrated in connection with a damascene process,
it will be understood that the method described herein for forming
a non-uniformly doped seed layer 124 is equally applicable to the
dual damascene process as well as to other processes known in the
art which are used to fill trench-like structures in integrated
circuit devices with a metal material.
[0035] Reference is now made to FIG. 5 (not drawn to scale) wherein
there is shown a diagram of a sputter chamber suited for
implementing the process described above for forming a
non-uniformly doped metal seed layer. An argon gas source 500
supplies argon through a flow controller 502 to the inside of
chamber 504. The argon gas is used as a sputter working gas during
sputtering operations, or as a sputtering etching gas during
etching operations. The chamber 504 further includes a copper
sputtering target 506. The target 506 is preferably pure copper,
but may include a very light dopant (for example, less than 0.5%).
A first power supply 508, for example a DC power supply, applies a
negative voltage to the target 506 to excite the argon into a
plasma. The copper target 506 may be configured for self-sustained
sputtering. Positively charged argon ions are attracted to the
negatively biased target 506, and a vertically directional copper
sputter 520 is produced. The sputtered copper deposits on a wafer
510. The wafer 510 is supported by a pedestal or chuck 512. An RF
coil 514 is wrapped around the region directly above the wafer 510
between the target 506 and the chuck 512. A second power supply 514
is coupled to the RF coil 514. In conventional operation the second
power supply 514 supplies a high frequency RF signal (for example,
of about 2 MHz) to the RF coil 514 to generate an argon plasma
during etching. As discussed above, the RF coil 514 is formed of
doped copper and is used in connection with an additional
sputtering operation to deposit a vertically graded doped copper
layer on certain portions of the wafer 510. The dopant well exceeds
0.5%. For this purpose, the second power supply 514 alternatively
applies a negative voltage and RF power to the RF coil 514 to
excite the argon into a plasma and cause non-vertically directional
sputtering 522 of doped copper on the wafer 510. A bias RF supply
518 electrically biases the chuck 512. When a plasma is developed
above the wafer 510, using any of the techniques described above,
the RF bias on the chuck 512 attracts and accelerates ions from the
plasma towards the wafer 510. During sputtered deposition, the
attracted ions are copper ions or doped copper ions sputtered from
the target 506 or RF coil 514, respectively. Alternatively, the
attracted ions are argon ions used in etching the wafer 510.
[0036] It will accordingly be noted that the sputter chamber can be
used for both the conventional copper sputter from target 506 and
the directional doped copper sputter from RF coil 514 and further
the etchback operation. Thus, the process steps described herein
can be performed in a single process chamber without need to break
seal.
[0037] Advantages of the formation of a non-uniformly doped metal
seed layer 124 include: a) minimal copper grain growth penalty from
doping species present in the seed layer; b) easier segregation
(i.e., migration) of the doping species from the seed layer to a
destination region such as the interface; c) flexibility to change
doping level for the copper seed layer using the same processing
equipment (chamber); and d) ability to present seed layers with
different doping characteristics on different metallization layers,
for example, using a pure copper seed layer on some metallization
layers and a doped copper seed layer on other layers, or using a
first doping concentration on one metallization layer and a
different doping concentration on another layer.
[0038] The foregoing description has provided by way of exemplary
and non-limiting examples a full and informative description of the
exemplary embodiment of this invention. However, various
modifications and adaptations may become apparent to those skilled
in the relevant arts in view of the foregoing description, when
read in conjunction with the accompanying drawings and the appended
claims. However, all such and similar modifications of the
teachings of this invention will still fall within the scope of
this invention as defined in the appended claims.
* * * * *