U.S. patent application number 15/599026 was filed with the patent office on 2017-09-07 for methods to form multi threshold-voltage dual channel without channel doping.
The applicant listed for this patent is GLOBALFOUNDRIES Inc.. Invention is credited to Hoon KIM, Chanro PARK, Min-gyu SUNG, Ruilong XIE.
Application Number | 20170256455 15/599026 |
Document ID | / |
Family ID | 59387137 |
Filed Date | 2017-09-07 |
United States Patent
Application |
20170256455 |
Kind Code |
A1 |
KIM; Hoon ; et al. |
September 7, 2017 |
METHODS TO FORM MULTI THRESHOLD-VOLTAGE DUAL CHANNEL WITHOUT
CHANNEL DOPING
Abstract
Methods to form multi V.sub.t channels, including a single type
of WF material, utilizing lower annealing temperatures and the
resulting devices are disclosed. Embodiments include providing an
interfacial-layer on a semiconductor substrate; forming a first
high-k dielectric-layer on the interfacial-layer; forming a second
high-k dielectric-layer and a first cap-layer, respectively, on the
first high-k dielectric-layer; removing the second high-k
dielectric and first cap layers in first and second regions;
forming a second cap-layer on the first high-k dielectric-layer in
the first and second regions and on the first cap-layer in a third
region; performing an annealing process; removing the second
cap-layer from all regions and the first cap-layer from the third
region; forming a third high-k dielectric-layer over all regions;
forming a work-function composition-layer and a barrier-layer on
the third high-k dielectric-layer in all regions; removing the
barrier-layer from the first region; and forming a gate electrode
over all regions.
Inventors: |
KIM; Hoon; (Clifton Park,
NY) ; SUNG; Min-gyu; (Latham, NY) ; XIE;
Ruilong; (Niskayuna, NY) ; PARK; Chanro;
(Clifton Park, NY) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
GLOBALFOUNDRIES Inc. |
Grand Cayman |
|
KY |
|
|
Family ID: |
59387137 |
Appl. No.: |
15/599026 |
Filed: |
May 18, 2017 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
15014150 |
Feb 3, 2016 |
|
|
|
15599026 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
H01L 27/088 20130101;
H01L 21/82345 20130101; H01L 29/517 20130101; H01L 21/28185
20130101; H01L 29/4966 20130101; H01L 21/823462 20130101 |
International
Class: |
H01L 21/8234 20060101
H01L021/8234; H01L 21/28 20060101 H01L021/28; H01L 29/49 20060101
H01L029/49; H01L 29/51 20060101 H01L029/51; H01L 27/088 20060101
H01L027/088 |
Claims
1. A semiconductor device comprising: an interfacial layer on a
semiconductor substrate; a first high-k dielectric layer on the
interfacial layer; a second high-k dielectric layer, different from
the first, diffused through the first high-k dielectric layer and
into the interfacial layer in a third of three regions; a third
high-k dielectric layer over the first high-k dielectric layer in
first and second regions and over the second high-k dielectric in
the third region; a work-function composition layer on the third
high-k dielectric layer in all regions; a barrier layer on the
work-function composition layer in the second and third regions;
and a gate electrode over all regions.
2. The semiconductor device according to claim 1, wherein the
semiconductor substrate is n-type, the semiconductor device
comprising: a high-voltage threshold region in the first region; a
low-voltage threshold region in the second region; and a super
low-voltage threshold region in the third region.
3. The semiconductor device according to claim 1, wherein the
semiconductor substrate is p-type, the semiconductor device
comprising: a super low-voltage threshold region in the first
region; a low-voltage threshold region in the second region; and a
high-voltage threshold region in the third region.
4. The semiconductor device according to claim 1, wherein: the
second high-k dielectric layer is based on a threshold-voltage
shift target, and the third high-k dielectric layer is based on a
leakage current behavior of the second high-k dielectric layer.
5. The semiconductor device according to claim 1, wherein: the
work-function composition layer comprises a work-function metal
layer sandwiched between two layers of titanium nitride.
6. The semiconductor device according to claim 1, wherein the first
high-k dielectric layer comprises hafnium-oxide with a thickness of
10 to 30 .ANG..
7. The semiconductor device according to claim 1, wherein the
second high-k dielectric layer comprises lanthanum-oxide with a
thickness of 0.1 to 20 .ANG..
8. The semiconductor device according to claim 1, wherein the
second high-k dielectric layer is driven into the first high-k
dielectric layer with a higher concentration in proximity to the
semiconductor substrate than near the gate electrode.
9. A semiconductor device comprising: an interfacial layer along
the entirety of and on an upper surface of a semiconductor
substrate; a first conformal high-k dielectric layer along the
entirety of and on the interfacial layer in first, second, and
third regions; a second conformal high-k dielectric layer along and
on the first high-k dielectric layer in only the third region,
wherein the second conformal high-k dielectric layer is based on a
threshold-voltage shift target; a third high-k dielectric layer
over the first, second, and third regions, wherein the third high-k
dielectric layer is based on a leakage current behavior of the
second high-k dielectric layer; a conformal work-function
composition layer on the third high-k dielectric layer in the
first, second, and third regions; a barrier layer on only the
second and third regions; and a gate electrode over the first,
second, and third regions.
10. The semiconductor device according to claim 9, wherein the
semiconductor substrate is n-type and includes a high-voltage
threshold region in the first region, a low-voltage threshold
region in the second region, and a super low-voltage threshold
region in the third region, and
11. A semiconductor device comprising: an interfacial layer along
the entirety of and on an upper surface of a semiconductor
substrate; a first conformal high-k dielectric layer along the
entirety of and on the interfacial layer in first, second, and
third regions; a second conformal high-k dielectric layer along and
on the first high-k dielectric layer in only the third region; a
third high-k dielectric layer over the first, second, and third
regions; a conformal work-function composition layer on the third
high-k dielectric layer in the first, second, and third regions; a
barrier layer on the conformal work-function composition layer only
in the second and third regions; and a gate electrode over the
first, second, and third regions.
12. The semiconductor device according to claim 11, wherein the
semiconductor substrate is n-type, the first region comprises a
high-voltage threshold region; the second region comprises a
low-voltage threshold region, and the third region comprises a
super low-voltage threshold region.
13. The semiconductor device according to claim 11, wherein the
semiconductor substrate is p-type, the first region comprises a
super low-voltage threshold region, the second region comprises a
low-voltage threshold region, and the third region comprises a
high-voltage threshold region.
14. The semiconductor device according to claim 11, wherein the
third high-k dielectric layer is chosen based on a leakage current
behavior of the second high-k dielectric layer.
15. The semiconductor device according to claim 11, wherein the
second high-k dielectric layer is chosen based on a
threshold-voltage shift target.
16. The semiconductor device according to claim 11, wherein the
work-function composition layer comprises a work-function metal
layer sandwiched between two layers of titanium nitride.
17. The semiconductor device according to claim 11, wherein the
first high-k dielectric layer comprises hafnium-oxide to a
thickness of 10 to 30 .ANG..
18. The semiconductor device according to claim 11, wherein the
second high-k dielectric layer comprises lanthanum-oxide to a
thickness of 0.1 to 20 .ANG..
19. The semiconductor device according to claim 11, wherein the
second high-k dielectric layer is driven into the first high-k
dielectric layer with a higher concentration in proximity to the
semiconductor substrate than near the gate electrode.
20. The semiconductor device according to claim 9, wherein the
semiconductor substrate is p-type and includes a super low-voltage
threshold region in the first region, a low-voltage threshold
region in the second region, and a high-voltage threshold region in
the third region.
Description
RELATED APPLICATION
[0001] The present application is a Divisional of application No.
Ser. 15/014,150, filed on Feb. 3, 2016, which is incorporated
herein by reference in its entirety.
TECHNICAL FIELD
[0002] The present disclosure relates generally to designing and
fabricating integrated circuit (IC) devices. The present disclosure
is particularly applicable to forming multi threshold-voltage
(V.sub.t) dual channels in an IC device for 7 nanometer (nm)
technology node and beyond.
BACKGROUND
[0003] Generally, various advanced processes may be utilized in the
design and fabrication of IC devices, particularly to aid with
forming multi V.sub.t channels in an IC device. Current processes,
for example, utilizing lanthanum-oxide (La.sub.2O.sub.3) and
channel doping in 10 nm node devices, may cause performance
degradation and be unsuitable in smaller technology nodes. Such
processes may include higher thermal ranges as well as a chemical
reaction to achieve uniform V.sub.t shift in short and long
channels in an IC device. A plasma channel doping process may be
inconsistent due to plasma life time difference in short and long
channels. Additionally, different work-function (WF) materials are
utilized in different device types (e.g. n-type or p-type) that may
require additional lithography steps.
[0004] Therefore, a need exists for a methodology enabling
formation of multi V.sub.t channels in an IC device, including a
single type of WF material, utilizing lower annealing temperatures
and the resulting devices.
SUMMARY
[0005] An aspect of the present disclosure is a method of forming
multi V.sub.t channels in an IC device, including a single type of
WF material, utilizing lower annealing temperatures.
[0006] An aspect of the present disclosure is an IC device
including multi V.sub.t channels and a single type of WF
material.
[0007] Additional aspects and other features of the present
disclosure will be set forth in the description which follows and
in part will be apparent to those having ordinary skill in the art
upon examination of the following or may be learned from the
practice of the present disclosure. The advantages of the present
disclosure may be realized and obtained as particularly pointed out
in the appended claims.
[0008] According to the present disclosure some technical effects
may be achieved in part by a method including providing an
interfacial layer on an upper surface of a semiconductor substrate;
forming conformally a first high-k dielectric layer on the
interfacial layer; forming conformally a second high-k dielectric
layer and a first cap layer, respectively, on the first high-k
dielectric layer; removing the second high-k dielectric and first
cap layers in first and second regions; forming a second cap layer
on the first high-k dielectric layer in the first and second
regions and on the first cap layer in a third region; performing an
annealing process; removing the second cap layer from all regions
and the first cap layer from the third region; forming a third
high-k dielectric layer over all regions; forming conformally a
work-function composition layer and a barrier layer, respectively,
on the third high-k dielectric layer in all regions; removing the
barrier layer from the first region; and forming a gate electrode
over all regions.
[0009] In one aspect where the semiconductor substrate is n-type, a
high-voltage threshold region is formed in the first region, a
low-voltage threshold region is formed in the second region, and a
super low-voltage threshold region is formed in the third
region.
[0010] In another aspect where the semiconductor substrate is
p-type, a super low-voltage threshold region is formed in the first
region, a low-voltage threshold region is formed in the second
region, and a high-voltage threshold region is formed in the third
region.
[0011] An additional aspect includes forming the third high-k
dielectric layer based on a leakage current behavior of the second
high-k dielectric layer.
[0012] One aspect includes forming the second high-k dielectric
layer based on a threshold-voltage shift target.
[0013] A further aspect includes forming the work-function
composition layer by sandwiching a work-function metal layer
between two layers of titanium nitride (TiN).
[0014] Another aspect includes forming the first high-k dielectric
layer of hafnium-oxide (HfO.sub.2) to a thickness of 10 to 30
angstroms (.ANG.), for example 17 .ANG..
[0015] One aspect includes forming the second high-k dielectric
layer of La.sub.2O.sub.3to a thickness of 0.1 to 20 .ANG., for
example 10 .ANG..
[0016] In one aspect, after the annealing process, the second
high-k dielectric layer is driven into the first high-k dielectric
layer with a higher concentration in proximity to the semiconductor
substrate than near the gate electrode.
[0017] An additional aspect includes determining an annealing
temperature based on a concentration level of a metalloid in the
second high-k dielectric layer.
[0018] Another aspect of the present disclosure is a device
including: an interfacial layer on a semiconductor substrate; a
first high-k dielectric layer on the interfacial layer; a second
high-k dielectric layer, different from the first, defused through
the first high-k dielectric layer and into the interfacial layer in
a third of three regions; a third high-k dielectric layer over the
first high-k dielectric layer in first and second regions and over
the second high-k dielectric in the third region; a work-function
composition layer on the third high-k dielectric layer in all
regions; a barrier layer on the work-function composition layer in
the second and third regions; and a gate electrode over all
regions.
[0019] In another aspect, the semiconductor substrate is n-type and
includes a high-voltage threshold region in the first region, a
low-voltage threshold region in the second region, and a super
low-voltage threshold region in the third region.
[0020] In another aspect, the semiconductor substrate is p-type and
includes a super low-voltage threshold region in the first region,
a low-voltage threshold region in the second region, and a
high-voltage threshold region in the third region.
[0021] In one aspect, the second high-k dielectric layer is based
on a threshold-voltage shift target, and the third high-k
dielectric layer is based on a leakage current behavior of the
second high-k dielectric layer.
[0022] In an additional aspect, the work-function composition layer
includes a work-function metal layer sandwiched between two layers
of TiN.
[0023] In a further aspect, the first high-k dielectric layer
includes HfO.sub.2 with a thickness of 10 to 30 .ANG., for example
17 .ANG..
[0024] In one aspect, the second high-k dielectric layer includes
La.sub.2O.sub.3with a thickness of 0.1 to 20 .ANG., for example 10
.ANG..
[0025] In another aspect, the second high-k dielectric layer is
driven into the first high-k dielectric layer with a higher
concentration in proximity to the semiconductor substrate than near
the gate electrode.
[0026] Additional aspects and technical effects of the present
disclosure will become readily apparent to those skilled in the art
from the following detailed description wherein embodiments of the
present disclosure are described simply by way of illustration of
the best mode contemplated to carry out the present disclosure. As
will be realized, the present disclosure is capable of other and
different embodiments, and its several details are capable of
modifications in various obvious respects, all without departing
from the present disclosure. Accordingly, the drawings and
description are to be regarded as illustrative in nature, and not
as restrictive.
BRIEF DESCRIPTION OF THE DRAWINGS
[0027] The present disclosure is illustrated by way of example, and
not by way of limitation, in the figures of the accompanying
drawing and in which like reference numerals refer to similar
elements and in which:
[0028] FIGS. 1A through 1J illustrate a process for forming multi
V.sub.t channels in an IC device, in accordance with an exemplary
embodiment.
DETAILED DESCRIPTION
[0029] For the purposes of clarity, in the following description,
numerous specific details are set forth to provide a thorough
understanding of exemplary embodiments. It should be apparent,
however, that exemplary embodiments may be practiced without these
specific details or with an equivalent arrangement. In other
instances, well-known structures and devices are shown in block
diagram form in order to avoid unnecessarily obscuring exemplary
embodiments. In addition, unless otherwise indicated, all numbers
expressing quantities, ratios, and numerical properties of
ingredients, reaction conditions, and so forth used in the
specification and claims are to be understood as being modified in
all instances by the term "about."
[0030] The present disclosure addresses and solves the problem of
variations and inaccuracies attendant upon forming multi V.sub.t
channels in an IC device. The present disclosure addresses and
solves such problems, for instance, by, inter alia, including a
single type of WF material (e.g. for p and n type channels),
utilizing lower annealing temperatures (e.g. less than 900 degrees
Celsius (900.degree. C.)), wherein a low-voltage channel does not
require channel doping or doping of a high-k dielectric.
Additionally, the proposed method provides for a reduction in the
number of lithography masks (e.g. two masks) utilized in the
proposed process.
[0031] FIG. 1A illustrates a semiconductor substrate 101 (e.g.,
silicon (Si), silicon-germanium (SiGe), etc.), an interfacial layer
103 (e.g. oxide) on an upper surface of the semiconductor substrate
101, and a first high-k dielectric layer 105 (e.g. HfO.sub.2 with a
thickness of 10 to 30 .ANG.) on an upper surface of the interfacial
layer 103. In an n-type semiconductor substrate 101 (e.g. for
n-type field-effect-transistor (nFET)), there may be first, 107,
second, 109, and third, 111, regions corresponding, respectively,
to a high (RVT), low (LVT), and super low (SLVT) threshold voltage.
A high threshold voltage (VT) corresponds to a voltage greater than
300 millivolts (mV), a super low VT corresponds to a voltage less
than 200 mV, and a low VT corresponds to a voltage between 225 mV
and 300 mV.
[0032] In FIG. 1B, a second high-k dielectric layer 113 (e.g.
La.sub.2O.sub.3 with a thickness of 0.1 to 20 .ANG.) and a first
cap layer 115 (e.g. TiN with a thickness of 10 to 20 .ANG., for
example 15 .ANG.), respectively, may be formed conformally on the
first high-k dielectric layer 105 across all three regions 107,
109, and 111. The second high-k dielectric layer may be based on a
threshold-voltage shift target.
[0033] illustrated in FIG. 1C, the second high-k dielectric 113 and
first cap layer 115 may be removed from the first and second,
107/109, regions.
[0034] Adverting to FIG. 1D, a second cap layer, including layers
117 and 119 (e.g., TiN and amorphous-silicon), may be formed on the
first high-k dielectric layer 105 in the first and second regions
107/109, and on the first cap layer 115 in the third region
111.
[0035] As illustrated in FIG. 1E, an annealing process may be
performed to drive a concentration of the second high-k dielectric
layer 113 through the first high-k dielectric layer 105 and into
the interfacial layer 103 in the third region 111. The annealing
temperature (e.g. less than 900.degree. C.) may be based on a
concentration level of a metalloid in the semiconductor substrate
101. Concentration of the second high-k dielectric layer is at a
closer proximity to the semiconductor substrate than to the gate
electrode. The second cap layer, 117/119, may be removed from all
regions, and the first cap layer 115 may be removed from the third
region 111.
[0036] In FIG. 1F, a third high-k dielectric layer 121 (e.g.
HfO.sub.2) may be formed over all three regions to a thickness of
0.1 to 20 .ANG.. In FIG. 1G, a work-function composition layer 123
and a barrier layer 125 (e.g. fluorine barrier such as 20 to 30
.ANG. of titanium-aluminum-carbide (TiAlC)), respectively, may be
formed on the third high-k dielectric layer 121 in all regions. The
work-function composition layer 123 may be formed by sandwiching a
work-function metal layer 127 (e.g. TiAlC for an n-type
work-function (nWF) metal) between two TiN layers 129 and 131.
Formation and/or material of the third high-k dielectric layer 121
may be based on a leakage current behavior of the second high-k
dielectric layer.
[0037] In FIG. 1H, a section of the barrier layer 125 may be
removed from the first region 107, for example, by a removal (e.g.
etching) process selective to the TiN layer 123. As illustrated in
FIG. 1I, a wetting layer 133 (e.g. 10 .ANG. TiN layer formed by
chemical vapor deposition) and a gate electrode 135, respectively,
may be formed over the work-function composition layer 123 (e.g. on
the TiN layer 131) in all regions.
[0038] FIG. 1J illustrates a similar structure to that of FIG. 1I,
wherein if the semiconductor substrate 137 is a p-type, then first,
139, second, 141, and third, 143, regions, respectively, correspond
to SLVT, LVT, and RVT regions. It is noted that due to
properties/characteristics of the substrate 137 (e.g. band offset
of SiGe), an n-type WF metal (e.g. TiAlC) may still be utilized as
a WF metal in a pFET device.
[0039] The embodiments of the present disclosure can achieve
several technical effects including utilizing efficient and
reliable processes to form multi V.sub.t channels, including a
single type of WF material, with a reduced annealing temperature
budget. Furthermore, the embodiments enjoy utility in various
industrial applications as, for example, microprocessors, smart
phones, mobile phones, cellular handsets, set-top boxes, DVD
recorders and players, automotive navigation, printers and
peripherals, networking and telecom equipment, gaming systems,
digital cameras, or other devices utilizing logic or high-voltage
technology nodes. The present disclosure therefore enjoys
industrial applicability in any of various types of highly
integrated semiconductor devices, including devices that use SRAM
cells (e.g., liquid crystal display (LCD) drivers, digital
processors, etc.), particularly for the 7 nm technology node and
beyond.
[0040] In the preceding description, the present disclosure is
described with reference to specifically exemplary embodiments
thereof. It will, however, be evident that various modifications
and changes may be made thereto without departing from the broader
spirit and scope of the present disclosure, as set forth in the
claims. The specification and drawings are, accordingly, to be
regarded as illustrative and not as restrictive. It is understood
that the present disclosure is capable of using various other
combinations and embodiments and is capable of any changes or
modifications within the scope of the inventive concept as
expressed herein.
* * * * *