U.S. patent application number 15/006304 was filed with the patent office on 2017-07-27 for hybrid fin cut etching processes for products comprising tapered and non-tapered finfet semiconductor devices.
The applicant listed for this patent is GLOBALFOUNDRIES Inc.. Invention is credited to Hoon Kim, Chanro Park, Min Gyu Sung, Ruilong Xie.
Application Number | 20170213767 15/006304 |
Document ID | / |
Family ID | 59359159 |
Filed Date | 2017-07-27 |
United States Patent
Application |
20170213767 |
Kind Code |
A1 |
Sung; Min Gyu ; et
al. |
July 27, 2017 |
HYBRID FIN CUT ETCHING PROCESSES FOR PRODUCTS COMPRISING TAPERED
AND NON-TAPERED FINFET SEMICONDUCTOR DEVICES
Abstract
For an integrated circuit product comprising a non-tapered
FinFET device formed in a first region of the substrate and a
tapered FinFET device in a second region of the substrate, the
method includes, among other things, forming the fins for the
non-tapered FinFET device in the first region by performing a
fin-cut-last process and forming the fins for the tapered FinFET by
performing a fin-cut-first process.
Inventors: |
Sung; Min Gyu; (Latham,
NY) ; Xie; Ruilong; (Niskayuna, NY) ; Park;
Chanro; (Clifton Park, NY) ; Kim; Hoon;
(Clifton Park, NY) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
GLOBALFOUNDRIES Inc. |
Grand Cayman |
|
KY |
|
|
Family ID: |
59359159 |
Appl. No.: |
15/006304 |
Filed: |
January 26, 2016 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
H01L 21/845 20130101;
H01L 21/823481 20130101; H01L 21/3083 20130101; H01L 21/823431
20130101 |
International
Class: |
H01L 21/8234 20060101
H01L021/8234; H01L 21/308 20060101 H01L021/308 |
Claims
1. A method of forming an integrated circuit product on a
semiconductor substrate, the product comprising a non-tapered
FinFET device formed in a first region of said substrate and a
tapered FinFET device formed in a second region of said substrate,
the method comprising: while masking said second region, forming a
first plurality of fins for said non-tapered FinFET device in said
first region by performing a fin-cut-last process that comprises:
initially forming said first plurality of fins in said first
region; and performing at least one first etch process to remove a
portion of at least a first fin of said initially formed first
plurality of fins without removing any portions of at least a
second fin of said initially formed first plurality of fins during
said at least one first etch process; and while masking said first
region, forming a second plurality of fins for said tapered FinFET
device in said second region by performing a fin-cut-first process
that comprises: forming a patterned fin-formation etch mask layer
comprising a plurality of line-type fin-formation features above
said second region; modifying said patterned fin-formation etch
mask layer by removing a portion of at least a first feature of
said plurality of line-type fin-formation features of said
patterned fin-formation etch mask layer without removing any
portions of at least a second feature of said plurality of
line-type fin-formation features; and performing a second etch
process through said modified patterned fin-formation etch mask to
define said second plurality of fins for said tapered FinFET
device.
2. The method of claim 1, wherein the step of performing said
second etch process through said modified patterned fin-formation
etch mask to define said second plurality of fins for said tapered
FinFET device is performed prior to the step of removing said
portion of said at least one of said previously formed first
plurality of fins.
3. The method of claim 1, wherein initially forming said first
plurality of fins in said first region comprises performing at
least one anisotropic etching process to initially form said first
plurality of fins in said first region.
4. The method of claim 3, wherein performing said at least said one
first etch process to remove said portion of said at least said
first fin of said initially formed first plurality of fins
comprises performing an isotropic etching process to remove said
portion of said at least said first fin of said initially formed
first plurality of fins.
5. The method of claim 1, wherein performing said second etch
process through said modified patterned fin-formation etch mask to
define said second plurality of fins for said tapered FinFET device
comprises performing at least one anisotropic etching process
through said modified patterned fin-formation etch mask to define
said second plurality of fins for said tapered FinFET device.
6. The method of claim 1, wherein prior to forming said first
plurality of fins for said non-tapered FinFET device in said first
region, the method comprises forming said patterned fin-formation
etch mask layer above said first and second regions.
7. The method of claim 1, wherein said non-tapered FinFET device is
formed above a substantially rectangular active area defined in
said substrate and said tapered FinFET device is formed above a
substantially non-rectangular active area defined in said
substrate.
8. The method of claim 1, wherein performing said second etch
process through said modified patterned fin-formation etch mask to
define said second plurality of fins for said tapered FinFET device
results in at least some of said second plurality of fins having
cut edges.
9. A method of forming an integrated circuit product on a
semiconductor substrate, the product comprising a non-tapered
FinFET device formed in a first region of said substrate and a
tapered FinFET device formed in a second region of said substrate,
the method comprising: forming a patterned fin-formation etch mask
layer above said first and second regions of said substrate; while
masking said patterned fin-formation etch mask layer in said second
region, performing an anisotropic etching process through said
patterned fin-formation etch mask layer to form a first plurality
of fins in said first region; after forming said first plurality of
fins, removing a portion of at least one of a plurality of features
of said patterned fin-formation etch mask layer that are positioned
above said second region; after removing said portion of said at
least one of said plurality of features of said patterned
fin-formation etch mask layer, and while masking said patterned
fin-formation etch mask layer in said first region, performing an
anisotropic etching process through said patterned fin-formation
etch mask layer to form a second plurality of fins in said second
region; and after forming said second plurality of fins, forming a
masking layer that covers said patterned fin-formation etch mask
layer in said second region and thereafter performing an isotropic
etching process through said patterned fin-formation etch mask
layer to remove at least a portion of at least one of said first
plurality of fins in said first region.
10. The method of claim 9, wherein removing said portion of said at
least one of said plurality of features of said patterned
fin-formation etch mask layer that are positioned above said second
region comprises performing an etching process to remove said
portion of said at least one of said plurality of features of said
patterned fin-formation etch mask layer that are positioned above
said second region and to remove a portion of at least one of a
plurality of features of said patterned fin-formation etch mask
layer that are positioned above said first region so as to thereby
expose at least a portion of an upper surface of at least one of
said first plurality of fins in said first region.
11. The method of claim 9, wherein performing said anisotropic
etching process through said patterned fin-formation etch mask
layer to form said second plurality of fins for said tapered FinFET
device results in at least some of said second plurality of fins
having cut edges.
12. The method of claim 11, wherein forming said masking layer that
covers said patterned fin-formation etch mask layer comprises
forming said masking layer that covers said patterned fin-formation
etch mask layer and said cut edges of said at least some of said
second plurality of fins.
13. A method of forming an integrated circuit product on a
semiconductor substrate, the product comprising a non-tapered
FinFET device formed in a first region of said substrate and a
tapered FinFET device formed in a second region of said substrate,
the method comprising: forming a patterned fin-formation etch mask
layer across said first and second regions of said substrate, said
patterned fin-formation etch mask layer comprising a first
plurality of features positioned above said first region and a
second plurality of features positioned above said second region;
while masking said patterned fin-formation etch mask layer in said
second region, performing an anisotropic etching process through
said patterned fin-formation etch mask layer to form a first
plurality of fins in said first region; after forming said first
plurality of fins, performing at least one etching process to:
remove a portion of at least one of said first plurality of
features of said patterned fin-formation etch mask layer positioned
above at least one of said first plurality of fins in said first
region so as to thereby expose a portion of an upper surface of
said at least one of said first plurality of fins in said first
region; and to remove at least a portion of at least one of said
second plurality of features of said patterned fin-formation etch
mask layer that are positioned above said second region; after
performing at least one etching process and while masking said
patterned fin-formation etch mask layer in said first region,
performing an anisotropic etching process through said patterned
fin-formation etch mask layer to form a second plurality of fins in
said second region; and after forming said second plurality of
fins, forming a masking layer that covers said patterned
fin-formation etch mask layer in said second region and thereafter
performing an isotropic etching process to remove at least a
portion of at least one of said first plurality of fins in said
first region having said exposed upper surface.
14. The method of claim 13, wherein performing said anisotropic
etching process through said patterned fin-formation etch mask
layer to form said second plurality of fins for said tapered FinFET
device results in at least some of said second plurality of fins
having cut edges.
15. The method of claim 14, wherein forming said masking layer that
covers said patterned fin-formation etch mask layer comprises
forming said masking layer that covers said patterned fin-formation
etch mask layer and said cut edges of said at least some of said
second plurality of fins.
16. The method of claim 1, further comprising replacing said
removed portion of said at least said first fin with an insulating
material.
17. The method of claim 1, wherein said portion of said at least
said first fin of said initially formed first plurality of fins is
removed after said second plurality of fins for said tapered FinFET
device are formed in said second region.
18. The method of claim 1, wherein said portion of said at least
said first fin of said initially formed first plurality of fins is
removed before said second plurality of fins for said tapered
FinFET device are formed in said second region.
19. The method of claim 1, wherein said second plurality of fins
for said tapered FinFET device are formed in said second region
after initially forming said first plurality of fins in said first
region.
20. The method of claim 1, wherein said modified patterned
fin-formation etch mask is formed above a semiconductor material
layer comprising said semiconductor substrate, wherein performing
said second etch process through said modified patterned
fin-formation etch mask to define said second plurality of fins
comprises etching a plurality of fin-formation trenches in said
semiconductor material layer during said second etch process after
initially forming said first plurality of fins, said plurality of
fin-formation trenches defining said second plurality of fins for
said tapered FinFET device.
Description
BACKGROUND OF THE INVENTION
[0001] 1. Field of the Invention
[0002] The present disclosure generally relates to the fabrication
of integrated circuits, and, more particularly, to various hybrid
fin cut etching processes for integrated circuit products that
include both tapered and non-tapered FinFET semiconductor
devices.
[0003] 2. Description of the Related Art
[0004] In modern integrated circuits, such as microprocessors,
storage devices and the like, a very large number of circuit
elements, especially field effect transistors (FETs), are provided
and operated on a restricted chip area. FETs come in a variety of
different configurations, e.g., planar devices, FinFET devices,
nanowire devices, etc. These FET devices are typically operated in
a switched mode, that is, these devices exhibit a highly conductive
state (on-state) and a high impedance state (off-state). The state
of the field effect transistor is controlled by a gate electrode,
which controls, upon application of an appropriate control voltage,
the conductivity of a channel region formed between a drain region
and a source region.
[0005] In contrast to a planar FET, which, as the name implies, is
a generally planar structure, a so-called FinFET device has a
three-dimensional (3D) structure. FIG. 1A is a perspective view of
an illustrative prior art FinFET semiconductor device 10 that is
formed above a semiconductor substrate 12 that will be referenced
so as to explain, at a very high level, some basic features of a
FinFET device. In this example, the FinFET device 10 includes three
illustrative fins 14, a gate structure 16, a sidewall spacer 18 and
a gate cap layer 20. A plurality of fin-formation trenches 22 are
formed in the substrate 12 to define the fins 14. A recessed layer
of insulating material 13 is positioned between the fins 14 in the
areas outside of the gate structure, i.e., in the source/drain
regions of the device 10. The gate structure 16 is typically
comprised of a layer of gate insulating material (not separately
shown), e.g., a layer of high-k insulating material (k-value of 10
or greater) or silicon dioxide, and one or more conductive material
layers (e.g., metal and/or polysilicon) that serve as the gate
electrode for the device 10. The fins 14 have a three-dimensional
configuration: a height H, a width W and an axial length L. The
axial length L corresponds to the direction of current travel in
the device 10 when it is operational, i.e., the gate length of the
device 10. The portions of the fins 14 covered by the gate
structure 16 are the channel regions of the FinFET device 10. The
gate structures 16 for such FinFET devices 10 may be manufactured
using so-called "gate-first" or "replacement gate" (gate-last)
manufacturing techniques. A FinFET device may have either a
tri-gate or dual-gate channel region.
[0006] Unlike a planar FET, in a FinFET device, a channel is formed
perpendicular to a surface of the semiconducting substrate so as to
reduce the physical size of the semiconductor device. Also, in a
FinFET, the junction capacitance at the drain region of the device
is greatly reduced, which tends to significantly reduce undesirable
short channel effects that were problematic as the gate length of
planar devices was reduced over the years. Multiple fins can be
formed in the same foot-print as that of a planar transistor
device. Accordingly, for a given plot space (or foot-print),
FinFETs tend to be able to generate significantly higher drive
current density than planar transistor devices. Additionally, the
leakage current of FinFET devices after the device is turned "OFF"
is significantly reduced as compared to the leakage current of
planar FETs, due to the superior gate electrostatic control of the
"fin" channel on FinFET devices. In short, the 3D structure of a
FinFET device is a superior FET structure as compared to that of a
planar FET, especially in the 20 nm CMOS technology node and
beyond.
[0007] As FinFET devices have been scaled to meet ever increasing
performance and size requirements, the width W of the fins 14 has
become very small, e.g., 6-12 nm, and the fin pitch has also been
significantly decreased, e.g., the fin pitch may be on the order of
about 30-60 nm. Further reductions in these dimensions are
anticipated in future product generations. Accordingly, accurately
defining these relatively small fin structures can be challenging.
One manufacturing technique that is employed in manufacturing
FinFET devices is to initially form the trenches 22 in the
substrate 12 to define multiple "fins" that extend across the
entire substrate 12 in the regions where FinFET devices will be
formed, and thereafter remove some of the fins where larger
isolation structures will be formed. Using this type of
manufacturing approach, better accuracy and repeatability may be
achieved in forming the fins 14 to very small dimensions due to the
more uniform environment in which the etching process that forms
the trenches 22, and thus the fins 14, is performed.
[0008] After the fins 14 have been formed, some portion of some of
the fins 14 must be removed to create room for or define the spaces
where isolation regions will ultimately be formed to separate the
individual FinFET devices from one another. As noted above, the
fins 14 are typically formed in a regular array. Typically, two
separate fin removal or "fin cut" etching processes, involving two
different fin-cut masking layers, are performed to remove the
unwanted fins (or portions thereof). One of these fin-removal
etching processes is sometimes referred to as a so-called "FH cut"
process.
[0009] The FH cut process involves forming an opening in the mask
layer, wherein the long axis of the opening is substantially
parallel to the long axis of the fins 14, i.e., the long axis of
the opening in the masking layer runs in a direction that
corresponds to the gate length direction of the finished FinFET
devices (or a direction that is parallel to the long axis of the
fins 14). In the FH fin cut process, portions of the axial length
of the fins 14 exposed by an FH cut mask (e.g., photoresist) are
removed. The FH fin cut process essentially defines the axial
length of the active fins 14 that will be positioned above one or
more active regions in completed devices. This FH fin cut process
is typically an anisotropic cut process.
[0010] One such removal technique used for the FH fin cut process
is typically referred to as "Fins-cut-First," as will be described
with reference to FIGS. 1B-1F. However, in this process, the
portion of the fin to be removed is not actually formed in the
substrate. Rather, the patterned fin-formation etch mask 32 is
modified such that the underlying substrate material where such a
fin portion would otherwise be formed is removed when the
fin-formation trenches 22 are etched into the substrate.
Accordingly, FIG. 1B depicts a product 30 after a patterned
fin-formation hard mask layer 32, e.g., a patterned layer of
silicon nitride/silicon dioxide, was formed above the substrate 34
in accordance with the desired fin pattern and pitch. In the
depicted example, only a single fin will be removed, i.e., the fin
36 (or portion thereof) that would otherwise correspond to the
feature 32A, to make room for an isolation region. However, as will
be recognized by those skilled in the art, depending upon the
desired final size of the isolation region, portions of more than
one fin may be removed using this Fins-cut-First approach.
[0011] FIG. 1C depicts the product 30 after a patterned masking
layer 38, e.g., a patterned layer of photoresist, was formed above
the patterned fin-formation hard mask layer 32. The patterned
masking layer 38 has an opening that exposes the feature 32A (for a
certain axial length into and out of the drawing page) for
removal.
[0012] FIG. 1D depicts the product 30 after an etching process was
performed through the patterned masking layer 38 so as to remove
the portions of feature 32A of the patterned fin-formation hard
mask layer 32 that were exposed by the patterned masking layer
38.
[0013] FIG. 1E depicts the device 30 after the patterned masking
layer 38 was removed and after a fin-formation etching process was
performed through the patterned fin-formation hard mask layer 32
(without the feature 32A) so as to define full-depth trenches 40 in
the substrate 34 that define the desired fins 36 across the entire
substrate. Due to the removal of the desired portion of the feature
32A, the fin-formation etching process removes the portions of the
substrate 34 that would have otherwise formed a fin 36 in the area
under the removed portions of the feature 32A. One problem with the
Fins-cut-First approach is that it inevitably causes variations in
fin sizes, i.e., the dimensions 36X and 36Y are different for
different fins. This is especially true between fins 36 inside an
array of fins and the fins at the edge of the active region that is
close to the isolation region. Such variations in fin sizes may
lead to unacceptable variations in device performance. Such
variations in fin sizes are caused by variable etch loading effects
wherein there are different etch rates that result in different
etch profiles for the fins 36 due to differing patterning
densities, pitch, etc. However, one benefit of the Fins-cut-First
approach is that an anisotropic etching process may be performed
when forming the trenches 40 since the technique involves removing
substantially all of the substrate material where the undesired fin
would have otherwise been formed and there is little chance of
damaging laterally adjacent fin structures.
[0014] FIG. 1F depicts the product 30 after several process
operations were performed. First, a layer of insulating material
42, such as silicon dioxide, was formed so as to overfill the
trenches 40. Next one or more chemical mechanical polishing (CMP)
processes were performed to planarize the upper surface of the
insulating material 40 with the top of the fins 36 and thereby
remove the patterned fin-formation hard mask 32. Thereafter, an
etch-back process was performed to recess the layer of insulating
material 42 between the fins 36 and thereby expose the upper
portions of the fins 36, which corresponds to the final fin height
of the fins 36. Next, a gate structure (not shown) for the product
30 may be formed using either gate-first or gate-last manufacturing
techniques.
[0015] Another technique employed during the FH cut process is
typically referred to as "Fins-cut-Last," and it will be generally
described with reference to FIGS. 1G-1L. FIG. 1G depicts the
product 30 after the patterned fin-formation hard mask layer 32 was
formed above the substrate 34 in accordance with the desired fin
pattern and pitch across all areas of the substrate where FinFET
devices will be formed. As before, in the depicted example, only a
single fin (or portion thereof) will be removed, i.e., the fin 36
corresponding to the feature 32A, to make room for the isolation
region.
[0016] FIG. 1H depicts the product 30 after an anisotropic
fin-formation etching process was performed through the patterned
fin-formation hard mask layer 32 so as to define the full-depth
trenches 40 in the substrate 34 that define the fins 36 across the
entire substrate in the areas where FinFET devices will be formed.
Note that, in the Fins-cut-Last approach, the size of the fins is
very uniform, i.e., the dimension 36A is approximately equal to the
dimension 36B. This is primarily due to the fact that, in this
approach, fins 36 are formed everywhere on the wafer where FinFET
devices will be formed in a substantially uniform etch environment,
i.e., there is no undesirable etch loading effects to cause
variations in fin sizes.
[0017] FIGS. 1I-1J depict the device 30 after several process
operations were performed. First, a layer of insulating material
44, such as silicon dioxide, was formed so as to overfill the
trenches 40. Then a CMP process was performed to planarize the
upper surface of the layer of insulating material 44 with the
patterned fin-formation hard mask layer 32. Next, a patterned
fin-cut masking layer 46, e.g., a patterned layer of photoresist,
was formed above the layer of insulating material 44. The patterned
fin-cut masking layer 46 has an opening 46A positioned above the
portion of the underlying fin 36 that is to be removed. FIG. 1J is
a plan view of the patterned fin-cut masking layer 46 with a
generally rectangular-shaped opening 46A that exposes a desired
portion of the axial length of the feature 32A of the patterned
fin-formation hard mask layer 32 that is to be removed along with
the corresponding portion of the axial length of the underlying fin
36.
[0018] FIG. 1K depicts the device 30 after one or more anisotropic
etching processes were performed to remove the exposed portions of
the layer of insulating material 44, the exposed portions of the
feature 32A of the patterned fin-formation hard mask layer 32 and
the underlying portions of the fin 36. This results in the
formation of a trench 45 in the layer of insulating material 44.
Typically, as shown in the plan view in FIG. 1J, the trench 45 will
take the form of a rectangle that corresponds approximately to the
opening 46A in the patterned fin-cut masking layer 46. Inevitably,
there will be some inward tapering of the sidewalls of the trench
45. Although not depicted in the drawings, after the trench 45 is
formed, the patterned fin-cut masking layer 46 will be removed and
additional oxide material (not shown) will be formed through the
opening 45A in the trench 45 where the portion of the fin 36 was
removed. Then a chemical mechanical polishing (CMP) process will be
performed to planarize the upper surface of all of the insulating
materials with the top of the patterned fin-formation hard mask
layer 32. Thereafter, the isolation regions between devices will be
masked and an etch-back process will be performed to recess the
layer of insulating material 44 between the fins 36 for each device
and thereby expose the upper portions of the fins 36, which
corresponds to the final fin height of the fins 36.
[0019] There are at least two possible problems with the
fins-cut-last approach that generally relate to the size or
critical dimension (CD) 45X of the opening 45A of the trench 45.
With reference to FIG. 1L, if the CD 45X of the opening 45A is too
small, there will typically be some residual portion 36X of the fin
36 remaining at the bottom of the trench 45. If the CD 45X of the
opening 45A is increased in an effort to insure complete removal of
the unwanted residual fin materials 36X at the bottom of the trench
45, then there is a much greater likeli-hood of damaging the fins
36 adjacent the trench 45 when the fin removal etch process is
performed. These issues only get worse as the depth of the trench
45 increases and as packing densities increase.
[0020] Some of the aforementioned problems could potentially be
remedied by performing a selective isotropic etching process to
remove the desired portions of the fin 36 instead of performing an
anisotropic etching process. FIGS. 1M-1N depict the device 30 after
an isotropic etching process was performed to remove the desired
portions of the fin 36 exposed by the opening 46A in the patterned
fin-cut masking layer 46. FIG. 1N is a cross-sectional view taken
through the long axis of the fin 36 that is cut during the
isotropic etching process. One benefit of performing an isotropic
fin cut etching process is that, due to the isotropic nature of the
process, any undesirable residual fin material 36X (see FIG. 1L) at
the bottom of the trench 45 may be eliminated. As shown in FIG. 1N,
performing an isotropic fin-removal etching process results in the
formation of a small trench 48 in the substrate 34. Typically, only
a portion of the entire axial length of the fin 36 will be removed
as other portions of the initially formed fin 36 will serve as
permanent fins 36A for other FinFET devices. Due to the isotropic
nature of the fin removal etching process, the cut ends 50 of the
permanent fins 36A that are adjacent the portion of the fin 36 that
was removed may be subjected to relatively severe undercutting, as
depicted in FIG. 1N. That is, due to the nature of an isotropic
etching process, there may be some undesirable loss of the fin
material in the directions indicated by the arrows 47 in FIG.
1J.
[0021] As it relates to the formation of FinFET devices, the number
of fins of a FinFET device is an important consideration. In
general, a FinFET device with a greater number of fins tends to
exhibit greater performance, i.e., drive current, than a FinFET
device with a lesser number of fins. Accordingly, all other things
being equal, a FinFET device with a relatively greater number of
fins would be a candidate for various high performance
applications, such being included as part of a critical path for a
logic circuit on an integrated circuit product. On the other hand,
FinFET devices with a lesser number of fins may be more suitable
for applications involving less relative power consumption, as such
FinFET devices tend to exhibit relatively lower off-state leakage
currents. Accordingly, such FinFET devices may be employed in
non-critical path circuits where power consumption and power
management is an important factor.
[0022] In general, there are two different ways that may be
employed in an attempt to produce FinFET devices with different
numbers of fins. Historically, FinFET devices have been formed in
and above active regions that have a rectangular configuration.
FIG. 1O is a simplistic depiction of one illustrative example of
how different FinFET devices, each having a different number of
fins, may be formed above spaced-apart active regions that have a
rectangular configuration. As shown therein, the product is
comprised of a plurality of fins 36, a plurality of dummy gates 52
and a plurality of active gates 54. First and second FinFET devices
56, 58 (each of which are two-fin devices) are formed in and above
spaced-apart rectangular active regions 60, 62, respectively. FIG.
1O also depicts first and second FinFET devices 64, 66 (each of
which are three-fin devices) formed in and above spaced-apart
rectangular active regions 68, 70, respectively. Such a
configuration does result in a plurality of FinFET devices 56, 58,
64 and 66 having a different number of fins. However, each of the
FinFET devices are formed above spaced-apart, rectangular shaped
active regions 60, 62, 68 and 70, respectively. One positive aspect
of the embodiment shown in FIG. 1O is that there is little or no
undercutting of the cut end surface 50 of the fins, as described in
FIGS. 1M-1N above (see surface 50 in FIG. 1N). One negative aspect
of the approach depicted in FIG. 1O, is that there is a relatively
significant area penalty (e.g., 10-20%) associated with forming the
four spaced-apart, rectangular active regions 60, 62, 68 and
70.
[0023] FIG. 1P depicts another illustrative way wherein FinFET
devices may be formed with a different number of fins. In this
embodiment, so-called "tapered" FinFET devices 80, 82 are formed in
and above substantially non-rectangular shaped active regions 84,
86, respectively, wherein the substantially non-rectangular active
area occupies less area than that of a normal four-sided rectangle
of similar dimensions. This definition of "tapered devices" and
"substantially non-rectangular shaped active regions" shall be used
in the specification and throughout the claims. The term
"substantially" is employed as part of the definition so that
precise geometric precision with respect to the configuration of
the non-rectangular shaped active regions is not required due to
the variabilities that may be encountered when performing etching
processes to define the active regions.
[0024] At the bottom of FIG. 1P, one example of the substantially
non-rectangular shaped active region 86 is shown by itself so as to
clearly show its substantially non-rectangular configuration when
viewed from above. A FinFET device formed above a substantially
non-rectangular shaped active region (as opposed to a traditional
rectangular shaped active region) may be generally referred to as a
"tapered" FinFET device, in that the substantially non-rectangular
shaped active region is configured or tapered (i.e., substantially
non-rectangular) so as to allow formation of FinFET devices (with
different numbers of fins) above that tapered, substantially
non-rectangular shaped active region. In the depicted example, each
of the tapered FinFET devices 80, 82 include a two-fin FinFET
device and a three-fin FinFET device. Such tapered FinFET devices
offer significant scaling benefits as compared to the traditional
FinFET devices shown in FIG. 1O that are formed above the
spaced-apart traditional rectangular active regions 60, 62, 68 and
70.
[0025] After the fins are cut, and the isolation regions are
formed, the gate structures are then formed across the fins. In the
case where a replacement gate process is used to manufacture the
FinFET devices, the initial gate structures are sacrificial gate
structures that will subsequently be removed and replaced with
final gate structures for the devices. Several process operations
are performed after the formation of the sacrificial gate
structures, e.g., the formation of epi semiconductor material in
the source/drain regions of the device. When the epi semiconductor
material is formed in the source/drain regions, it is important
that the epi material not form in unwanted areas of the devices so
as to not create a multitude of problems, e.g., growing around the
end of a gate structure so as to create a short circuit between the
source region and drain region, bridging the space between two
adjacent active regions, etc. Thus, with reference to FIG. 1Q, when
the fins are cut, the cut is located such that the cut ends of the
fins will be positioned under the dummy gate structures when they
are formed. This is sometimes referred to as the fins being
"tucked" in the sense that the cut end of the fin is positioned
under or "tucked under" the dummy gate structure. Such a tucked fin
arrangement is required on many modern integrated circuit products
so as to prevent the undesirable formation of epi semiconductor
material in undesirable places and to produce uniform source/drain
regions (when the epi material is formed) for all of the devices so
as to avoid variances in device performance.
[0026] FIG. 1R is an idealized depiction of a tapered device 80
that is formed above a substantially non-rectangular active area
84. As depicted, all of the fins 36 are properly tucked under a
gate structure 52, as indicated in the dashed line regions 55.
However, in fabricating a real-world device using a single mask to
define the substantially non-rectangular active area 84 and the
fins 36, there is unavoidable corner rounding 85 of a portion of
the active region 84, as shown in FIG. 1S. As a result of this
corner rounding, the fin 36A is axially shorter than intended,
while the fin 36B is axially longer than intended. The net result
is that when the gate 52 (shown in dashed lines) is formed, the
fins 36A and 36B will not be properly tucked under the gate 52.
More specifically, the fin 36A will be short of the gate 52 (as
depicted in the dashed line region 87), while the fin 36B will
extend beyond the gate 52 (as depicted in the dashed line region
89). As a result of the foregoing, the untucked portions of the
fins 36A, 36B can serve as sites for undesirable epi growth when
epi material is formed in the source/drain regions of the FinFET
devices.
[0027] To eliminate the above-described problem of corner rounding
85 of the substantially non-rectangular active area 84 for tapered
devices, two separate masking layers can be used when defining the
fins 36 in the substrate. In the two-mask layer approach, the
separately formed FH mask and the FP mask are formed such that they
overlap so as to define an essentially right-angle corner in the
area where the corner rounding 85 occurs when the single masking
layer approach is used. However, even when the double mask approach
is used, when an isotropic etch process is performed in the fin cut
last process to remove the undesirable portions 36X of the fins 36
(see FIGS. 1L-1N), there will still be some undesirable
undercutting (like the cut ends 50 shown in FIG. 1N) of the fins
for the tapered device. On the other hand, performing a
fin-cut-first process avoids the problem of undercutting of the
fins for the tapered device, but, as noted above, the fin-cut-first
process can lead to undesirable variations in the dimensions of the
fins which can adversely affect the performance of some devices,
such as those devices in high-performance areas like logic circuits
or SRAM circuits, etc.
[0028] The present disclosure is directed to various hybrid fin cut
etching processes for integrated circuit products that include both
tapered and non-tapered FinFET semiconductor devices that may
avoid, or at least reduce, the effects of one or more of the
problems identified above.
SUMMARY OF THE INVENTION
[0029] The following presents a simplified summary of the invention
in order to provide a basic understanding of some aspects of the
invention. This summary is not an exhaustive overview of the
invention. It is not intended to identify key or critical elements
of the invention or to delineate the scope of the invention. Its
sole purpose is to present some concepts in a simplified form as a
prelude to the more detailed description that is discussed
later.
[0030] Generally, the present disclosure is directed to various
hybrid fin cut etching processes for integrated circuit products
that include both tapered and non-tapered FinFET semiconductor
devices. For an integrated circuit product comprising a non-tapered
FinFET device formed in a first region of the substrate and a
tapered FinFET device in a second region of the substrate, the
method includes, among other things, while masking the second
region, forming a first plurality of fins for the non-tapered
FinFET device in the first region by performing a fin-cut-last
process that comprises initially forming the first plurality of
fins in the first region and thereafter removing a portion of at
least one of the previously formed first plurality of fins and,
while masking the first region, forming a second plurality of fins
in the second region by performing a fin-cut-first process that
comprises initially removing a portion of at least one of a
plurality of features of a patterned fin-formation etch mask layer
positioned above the second region so as to define a modified
patterned fin-formation etch mask and thereafter performing an etch
process through the modified patterned fin-formation etch mask to
define the second plurality of fins for the tapered FinFET
device.
[0031] For an integrated circuit product comprising a non-tapered
FinFET device formed in a first region of the substrate and a
tapered FinFET device in a second region of the substrate, another
illustrative method includes, among other things, forming a
patterned fin-formation etch mask layer above both the first and
second regions, while masking the patterned fin-formation etch mask
layer in the second region, performing an anisotropic etching
process through the patterned fin-formation etch mask layer to form
a first plurality of fins in the first region and, after forming
the first plurality of fins, removing a portion of at least one of
a plurality of features of the patterned fin-formation etch mask
layer that are positioned above the second region. In this example,
the method also includes, after removing a portion of at least one
of the plurality of features of the patterned fin-formation etch
mask layer, and while masking the patterned fin-formation etch mask
layer in the first region, performing an anisotropic etching
process through the patterned fin-formation etch mask layer to form
a second plurality of fins in the second region and, after forming
the second plurality of fins, forming a masking layer that covers
the patterned fin-formation etch mask layer in the second region
and thereafter performing an isotropic etching process through the
patterned fin-formation etch mask to remove at least a portion of
at least one of the first plurality of fins in the first
region.
BRIEF DESCRIPTION OF THE DRAWINGS
[0032] The disclosure may be understood by reference to the
following description taken in conjunction with the accompanying
drawings, in which like reference numerals identify like elements,
and in which:
[0033] FIGS. 1A-1S depict various prior art fin removal process
operations and problems that may be encountered when performing
such prior art processes on integrated circuit products comprising
both tapered and non-tapered FinFET devices; and
[0034] FIGS. 2A-2Z depict various hybrid fin cut etching processes
that may be performed on integrated circuit products that include
both tapered and non-tapered FinFET semiconductor devices.
[0035] While the subject matter disclosed herein is susceptible to
various modifications and alternative forms, specific embodiments
thereof have been shown by way of example in the drawings and are
herein described in detail. It should be understood, however, that
the description herein of specific embodiments is not intended to
limit the invention to the particular forms disclosed, but on the
contrary, the intention is to cover all modifications, equivalents,
and alternatives falling within the spirit and scope of the
invention as defined by the appended claims.
DETAILED DESCRIPTION
[0036] Various illustrative embodiments of the invention are
described below. In the interest of clarity, not all features of an
actual implementation are described in this specification. It will
of course be appreciated that in the development of any such actual
embodiment, numerous implementation-specific decisions must be made
to achieve the developers' specific goals, such as compliance with
system-related and business-related constraints, which will vary
from one implementation to another. Moreover, it will be
appreciated that such a development effort might be complex and
time-consuming, but would nevertheless be a routine undertaking for
those of ordinary skill in the art having the benefit of this
disclosure.
[0037] The present subject matter will now be described with
reference to the attached figures. Various structures, systems and
devices are schematically depicted in the drawings for purposes of
explanation only and so as to not obscure the present disclosure
with details that are well known to those skilled in the art.
Nevertheless, the attached drawings are included to describe and
explain illustrative examples of the present disclosure. The words
and phrases used herein should be understood and interpreted to
have a meaning consistent with the understanding of those words and
phrases by those skilled in the relevant art. No special definition
of a term or phrase, i.e., a definition that is different from the
ordinary and customary meaning as understood by those skilled in
the art, is intended to be implied by consistent usage of the term
or phrase herein. To the extent that a term or phrase is intended
to have a special meaning, i.e., a meaning other than that
understood by skilled artisans, such a special definition will be
expressly set forth in the specification in a definitional manner
that directly and unequivocally provides the special definition for
the term or phrase.
[0038] The present disclosure generally relates to various hybrid
fin cut etching processes that may be performed on integrated
circuit products that include both tapered and non-tapered FinFET
semiconductor devices. Moreover, as will be readily apparent to
those skilled in the art upon a complete reading of the present
application, the present method is applicable to a variety of
devices, including, but not limited to, logic devices, memory
devices, etc., and the methods disclosed herein may be employed to
form N-type or P-type semiconductor devices. The methods and
devices disclosed herein may be employed in manufacturing products
using a variety of technologies, e.g., NMOS, PMOS, CMOS, etc., and
they may be employed in manufacturing a variety of different
devices, e.g., memory devices, logic devices, ASICs, etc. As will
be appreciated by those skilled in the art after a complete reading
of the present application, the inventions disclosed herein may be
employed in forming integrated circuit products using a variety of
so-called 3D devices, such as FinFETs. The inventions disclosed
herein should not be considered to be limited to the illustrative
examples depicted and described herein. The various components and
structures of the integrated circuit products 100 disclosed herein
may be formed using a variety of different materials and by
performing a variety of known techniques, e.g., a chemical vapor
deposition (CVD) process, an atomic layer deposition (ALD) process,
a thermal growth process, spin-coating techniques, etc. The
thicknesses of these various layers of material may also vary
depending upon the particular application. With reference to the
attached figures, various illustrative embodiments of the methods
and devices disclosed herein will now be described in more
detail.
[0039] FIGS. 2A-2Z depict various hybrid fin cut etching processes
that may be performed on integrated circuit products that include
both tapered and non-tapered FinFET semiconductor devices. The
illustrative product 100 will be formed in and above a
semiconductor substrate 102. The substrate 102 may have a variety
of configurations, such as the depicted bulk silicon configuration.
The substrate 102 may also have a silicon-on-insulator (SOI)
configuration that includes a bulk silicon layer, a buried
insulation layer and an active layer, wherein semiconductor devices
are formed in and above the active layer. The substrate 102 may be
formed of silicon or silicon germanium or it may be made of
materials other than silicon, such as germanium. Thus, the terms
"substrate" or "semiconductor substrate" should be understood to
cover all semiconducting materials and all forms of such materials.
The substrate 102 may have different layers. When completed, the
illustrative product 100 will include a non-tapered FinFET device
that is formed in a non-tapered device area 102A of the substrate
102; a tapered FinFET device that is formed in a tapered device
area 102B of the substrate 102; and a planar device that is formed
in a planar device area 102C of the substrate 102. The areas 102A,
102B and 102C may be laterally adjacent one another (as depicted)
or they may be spaced apart regions that are spread across the
substrate 102. The present disclosure is directed to unique
processes of cutting undesired portions of the fins for both the
non-tapered and tapered FinFET devices. After the cutting of the
fins as described herein, all of the devices may be manufactured
using known processing techniques. In some application, the planar
device area 102C may be omitted if the product does not include any
planar devices. In many cases, the drawings contain a simplistic
plan view of the cross-sectional views shown in the drawings.
However, it may be the case that all of the features illustrated in
the cross-sectional views are not replicated in the simplistic plan
views.
[0040] FIG. 2A depicts the product 100 after a pad oxide layer 103
and a patterned fin-formation etch mask layer 104, e.g., a
patterned hard mask layer, was formed above the substrate 102. The
patterned fin-formation etch mask layer 104 is comprised of a
plurality of line-type features 104A that correspond to fins that
are to be formed in the non-tapered device area 102A of the
substrate 102, and a plurality of line-type features 104B that
correspond to fins that are to be formed in the tapered device area
102B of the substrate 102. The patterned fin-formation etch mask
layer 104 is intended to be representative in nature as it may be
comprised of a variety of materials, such as, for example, a
photoresist material, silicon nitride, silicon oxynitride, etc.
Moreover, the patterned fin-formation etch mask layer 104 may be
comprised of multiple layers of material, such as, for example, a
silicon nitride layer and a layer of silicon dioxide. The patterned
fin-formation etch mask layer 104 may be formed by depositing the
layer(s) of material that comprise the patterned fin-formation etch
mask layer 104 and thereafter directly patterning the masking layer
104 using known photolithography and etching techniques.
Alternatively, the patterned fin-formation etch mask layer 104 may
be formed by using known sidewall image transfer techniques. Thus,
the particular form and composition of the patterned fin-formation
etch mask layer 104 and the manner in which it is made should not
be considered a limitation of the present invention. In the
depicted example, there are eight of the features 104A that
correspond to the fins to be formed in the non-tapered device area
102A of the substrate 102 and eight of the features 104B that
correspond to the fins that are to be formed in the tapered device
area 102B of the substrate 102. Of course, any number of fins can
be formed in the regions 102A, 102B. The lateral size and the pitch
of the fins in the areas 102A, 102B may vary depending upon the
particular application and these dimensions may or may not be the
same in both of the areas 102A, 102B.
[0041] FIG. 2B illustrates the product 100 after a layer of
material 106, such as a planarization layer like OPL, was formed
across the entire substrate 102. The thickness of the layer of
material 106 may vary depending upon the particular
application.
[0042] FIG. 2C depicts the product 100 after a first patterned
masking layer 108 was formed above the substrate 102. As depicted,
the first patterned masking layer 108 covers substantially all of
the tapered device area 102B of the substrate 102 and the planar
device area 102C of the substrate 102, while exposing all of the
non-tapered device area 102A of the substrate 102. The first
patterned masking layer 108 also comprises an opening 108A between
the tapered device area 102B of the substrate 102 and the planar
device area 102C of the substrate 102. In one embodiment, the first
patterned masking layer 108 may be a patterned layer of photoresist
material that is formed using traditional photolithography tools
and equipment.
[0043] FIG. 2D depicts the product 100 after an etching process was
performed through the first patterned masking layer 108 to remove
exposed portions of the layer of material 106 and thereby pattern
the layer of material 106. As depicted, the etching process stops
on the pad oxide layer 103.
[0044] FIG. 2E depicts the product 100 after several process
operations were performed. First, the first patterned masking layer
108 was removed (although it need not be removed in all
applications). Thereafter, a fin-formation etching process was
performed through the exposed portions of the patterned
fin-formation etch mask layer 104 above the non-tapered device area
102A of the substrate 102 and through the patterned layer of
material 106. This process operation results in the definition of a
plurality of fin-formation trenches 110 in the area 102A of the
substrate 102 which define a plurality of fins 116 in the
non-tapered device area 102A of the substrate 102. Performing the
fin-formation etching process also results in the formation of a
trench 112 in the substrate 102 between the non-tapered device area
102A and the tapered device area 102B, and the formation of a
trench 114 in the substrate 102 between the tapered device area
102B and the planar device area 102C. In the example depicted
herein, there are eight of the fins 116 formed in the non-tapered
device area 102A of the substrate 102. For ease of reference, these
fins have been numbered (from right to left) 116-1, . . . , 116-4,
116-5, . . . ).
[0045] With continuing reference to FIG. 2E, in the illustrative
example depicted in the attached figures, the fin-formation
trenches 110 and the fins 116 (as well as other fins that will be
formed later in the process) are all depicted as being of a uniform
size and shape. However, such uniformity in the size and shape of
the fins 116 (and others) may not be required to practice at least
some aspects of the inventions disclosed herein. In the example
depicted herein, the fin-formation trenches 110 are depicted as
having been formed by performing one or more anisotropic etching
processes, but other etching processes may be used to form the
trenches 110 and define the fins 116. In the depicted example, the
fins 116 (and other fins to be performed later in the process
described below) are simplistically depicted as have a
substantially rectangular cross-sectional configuration for ease of
explanation. However, in a real-world device, the fins 116 (and
other fins) may be formed so as to have a tapered cross-sectional
configuration (wider at the bottom of the fin than at the top of
the fin). Thus, the size and configuration of the fin-formation
trenches, e.g., the trenches 110, and the fins, e.g., the fins 116,
and the manner in which they are made, should not be considered a
limitation of the present invention.
[0046] FIG. 2F depicts the product 100 after the patterned the
layer of material 106 was removed from above the substrate 102.
[0047] FIG. 2G illustrates the product 100 after a layer of
material 118, such as a planarization layer like OPL, was formed
across the entire substrate 102. The thickness of the layer of
material 118 may vary depending upon the particular
application.
[0048] FIG. 2H depicts the product 100 after a second patterned
masking layer 120 was formed above the substrate 102. As noted
above, if desired, two separate masking layers can be used at this
point in the process flow if desired so as to avoid the corner
rounding problem as discussed in the background section of this
application. As depicted, the second patterned masking layer 120
covers substantially all of the planar device area 102C of the
substrate 102, while exposing a portion of the area above the
non-tapered device area 102A and a portion of the area above the
tapered device area 102B. More specifically, the second patterned
masking layer 120 comprises a substantially rectangular opening
120A that exposes an area above axial portions of the fins 116-4,
116-5 that will be removed from the group of fins 116 in the
non-tapered device area 102A of the substrate 102 by performing a
fin-cut-last process, as described more fully below. The second
patterned masking layer 120 also comprises an opening 120C that
exposes an area above the tapered device area 102B where portions
of the axial length of certain of the features 104B of the
patterned fin-formation etch mask layer 104 will be removed using a
fin-cut-first process, as described more fully below. A portion of
the opening 120C also exposes the area above the trench 114.
Lastly, the second patterned masking layer 120 has an opening 120B
that exposes an area above the trench 112. In one embodiment, the
second patterned masking layer 120 may be a patterned layer of
photoresist material that is formed using traditional
photolithography tools and equipment.
[0049] FIG. 2I depicts the product 100 after one or more etching
processes were performed through the second patterned masking layer
120 to remove some of the exposed portions of the layer of material
118 (and thereby pattern the layer of material 118) so as to define
trenches 122A, 122B and 122C in the layer of material 118.
Performing these one or more etching processes also results in the
removal of portions of the axial length of the features 104B of the
patterned fin-formation etch mask layer 104 and the pad oxide layer
103 in the area 102X of the tapered device area 102B (which thereby
exposes the upper surface 102S of the substrate in the area 102X.
More specifically, as will be more apparent when viewing FIG. 2M,
performing this etching process results in the removal of portions
of the axial length of the features 104B1, 104B2, 104B3 and 104B4
prior to the formation of any fins in the tapered device region
102B. As will be appreciated by those skilled in the art after a
complete reading of the present application, this is a
fins-cut-first process that is performed for the fins that will be
formed in the tapered device region 102B. Performing the one or
more etching processes also results in the removal of the portions
of the features 104A1 and 104A2 (above the fins 116-5, 116-4,
respectively) (see FIG. 2H) in the non-tapered device area 102A
within the area defined by the opening 120A in the second patterned
masking layer 120. Importantly, at the conclusion of these one or
more etching processes, the upper surface 117 of the portions of
the axial length of the fins 116-4, 116-5 that are desired to be
removed are exposed. Exposing the surfaces 117 of the fins 116-4
and 116-5 facilitates the removal of the desired portions of these
fins using a fin-cut-last process, as described more fully below.
This process operation effectively results in the definition of a
modified patterned fin-formation etch mask 104 where portions of
the features 104A and portions of the features 104B have been
removed.
[0050] FIG. 2J depicts the product 100 after the second patterned
masking layer 120 was removed from above the substrate 102.
[0051] FIG. 2K depicts the product 100 after additional material of
the layer of material 118, such as a planarization layer like OPL,
was formed in the openings in the layer of material 118 shown in
FIG. 2J. Thus, the layer has been re-identified with the reference
number 118X. Alternatively, the layer of material 118 shown in FIG.
2J could simply be removed and a new layer of material 118 could be
formed on the substrate 102 so as to arrive at the structure
depicted in FIG. 2K.
[0052] FIG. 2L depicts the product 100 after a third patterned
masking layer 130 was formed above the substrate 102. As depicted,
the third patterned masking layer 130 covers substantially all of
the non-tapered device area 102A of the substrate 102 and the
planar device area 102C of the substrate 102. The third patterned
masking layer 130 comprises an opening 130A that exposes an area
above all of the tapered device area 102B of the substrate 102. In
one embodiment, the third patterned masking layer 130 may be a
patterned layer of photoresist material that is formed using
traditional photolithography tools and equipment.
[0053] FIG. 2M depicts the product 100 after one or more etching
processes were performed through the third patterned masking layer
130 to remove exposed portions of the layer of material 118X and
thereby pattern the layer of material 118X. As depicted, the one or
more etching processes also remove remaining exposed portions of
the pad oxide layer 103 in the area 102B of the substrate 102. As
depicted, the removal of the portions of the material 118X reveals
the features 104B1, 104B2, 104B3 and 104B4 that were cut using a
fin-cut-first process as shown in FIG. I.
[0054] The next set of process operations will be described with
reference to FIGS. 2N-2P. These drawings depict the product 100
after several process operations were performed. FIGS. 2O and 2P
are cross-sectional views taken wherein indicated in the plan view
shown in FIG. 2N (with layers above the patterned fin-formation
masking layer 104 removed in FIGS. 2O-2P). First, a second a
fin-formation etching process was performed through the third
patterned masking layer 130, through the patterned layer of
material 118X and though the exposed portions of the patterned
fin-formation etch mask layer 104 positioned above the tapered
device area 102B of the substrate 102. If desired, the third
patterned masking layer 130 may be removed prior to performing the
second fin-formation etching process. This second fin-formation
etching process was performed while the non-tapered device area
102A is masked. Performing the second fin-formation etching process
operation results in the definition of a plurality of fin-formation
trenches 132 in the tapered device area 102B of the substrate 102
which define a plurality of fins 134 in the tapered device area
102B of the substrate 102. Performing the second fin-formation
etching process also results in the formation of a trench 136 in
the substrate 102 in an area of the tapered device area 102B where
portions of the features 104B of the patterned fin-formation etch
mask layer 104 were removed. In the example depicted herein, there
are eight of the fins 134 formed in the tapered device area 102B of
the substrate 102. For ease of reference, these fins 134 have been
numbered (from right to left) 134-1 . . . 134-8). In the depicted
example, by use of the fin-cut-first process in the tapered device
region 102B, portions of what would have been fins 134-1, 134-2,
134-3 and 134-4 are not defined in the substrate 102 due to the
removal of portions of the features 104B1-104B4. The fin 134-2 is
depicted in dashed lines in the bottom drawing in FIG. 2N, because
it is not technically in the drawing plane depicted in the
cross-sectional view in FIG. 2N. That is, it is only depicted for
reference purposes only. FIG. 2O is a cross-sectional view taken
through the long axis of the fin 134-7, while FIG. 2P is a
cross-sectional view taken through the long axis of the fin 134-2.
As depicted, the fin 134-2 has a cut end surface 134C that was
created when the trench 136 was formed in the substrate 102. Note
that the comments above with respect to the formation of the fins
116 apply equally to the formation of the fins 134.
[0055] FIG. 2Q depicts the product 100 after several process
operations were performed. First, if not removed previously, the
third patterned masking layer 130 was removed, followed by the
removal of the layer of material 118X. Thereafter, a liner layer
140 was formed across the substrate 102 by performing a conformal
deposition process. The liner layer 140 may be comprised of a
variety of materials such as, for example, silicon dioxide, silicon
nitride, etc. In general, the liner layer 140 may be comprised of
one or more materials that exhibit some degree of etch selectivity
with respect to the material of the patterned fin-formation etch
mask 104. In one embodiment, the liner layer 140 may be comprised
of an inner layer of silicon dioxide and an outer layer of silicon
nitride. The thickness of the liner layer 140 may vary depending
upon the particular application.
[0056] FIGS. 2R-2S depict the product 100 after a layer of material
142, such as a planarization layer like OPL, was formed across the
entire substrate 102. As shown in FIG. 2S (which is a
cross-sectional view taken through the long axis of the fin 134-2),
the layer of material overfills the trench 136 and covers the cut
ends 134C of the four fins 134-1, 134-2, 134-3 and 134-4. The
thickness of the layer of material 142 may vary depending upon the
particular application.
[0057] FIG. 2T depicts the product 100 after a fourth patterned
masking layer 144 was formed above the substrate 102. As depicted,
the fourth patterned masking layer 144 covers substantially all of
the tapered device area 102B of the substrate 102 and the planar
device area 102C of the substrate 102. However, the fourth
patterned masking layer 144 is patterned so as to expose an area
above all of the non-tapered device area 102A of the substrate 102.
In one embodiment, the fourth patterned masking layer 144 may be a
patterned layer of photoresist material that is formed using
traditional photolithography tools and equipment.
[0058] FIG. 2U depicts the product 100 after a timed recess etching
process was performed through the fourth patterned masking layer
144 to remove portions of the layer of material 142 in the
non-tapered region 102A of the product. The layer of material 142
is recessed such that its recessed upper surface 142X is below the
upper surface 116S of the fins 116. The recessing of the layer of
material 142 exposes upper portions of the liner layer 140 in the
non-tapered region 102A of the product 100.
[0059] FIG. 2V depicts the product 100 after a timed etching
process was performed to remove portions of the liner layer 140.
Performing this etching process exposes the upper surfaces 116S of
the fins 116-4 and 116-5.
[0060] FIG. 2W depicts the product 100 after a timed etching
process was performed to remove the exposed portions of the fins
116-4 and 116-5 in the non-tapered region 102A of the product 100
so as to define removed fin cavities 150. After a complete reading
of the present application, those skilled in the art will
appreciate that this is part of a fins-cut-last process that is
performed on the fins 116 in the non-tapered region 102A of the
product 100. In some cases, all or part of the liner layer 140
adjacent the fins 116-4 and 116-5 may be removed as well, although
that situation is not depicted in the drawings.
[0061] FIG. 2X depicts the product 100 after several process
operations were performed. First, if not removed previously, the
fourth patterned masking layer 144 was removed followed by the
removal of the layer of material 142. Thereafter, a layer of
insulating material 152 was formed across the substrate 102 by
performing a blanket deposition process. The layer of insulating
material 152 may be comprised of a variety of material such as, for
example, silicon dioxide, etc.
[0062] FIG. 2Y depicts the product 100 after several process
operations were performed. First, a CMP process was performed to
planarize the upper surface of the layer of insulating material 152
with the upper surface of the fins 116 and 134 and the upper
surface of the planar device region 120C. This CMP process results
in the removal of portions of the liner layer 140, the remaining
features of the patterned fin formation etch mask 104 and the pad
oxide layer 103 above the planar device region 102C. Next, a timed
recess etching process was performed on the layer of insulating
material 152 such that its recessed upper surface 152X is at a
level that exposes the final desired height of the fins 116 and 134
in both of the regions 102A and 102B. Then, a timed etching process
was performed to remove any remaining portions of the liner layer
140 that might still be positioned on sidewalls of the fins 116,
134. Those skilled in the art will appreciate that other process
flows could also be performed to reach the structure depicted in
FIG. 2Y. For example, the CMP process could be performed so as to
stop on the upper surface of the patterned fin-formation etch mask
104 and thereafter several etching processes could be performed to
remove the mask layer 104, recess the layer of material 152 and
remove the desired portions of the liner layer 140.
[0063] FIG. 2Z is a simplistic plan view of the product 100 after
the completion of the process operations described above with
respect to FIG. 2Y (with the liner layer 140 being omitted in FIG.
2Z). As depicted, portions of the fins 116-4 and 116-5 were removed
from the non-tapered device region 102A by performing a modified
fin-cut-last process. On the other hand, portions of what would
have been fins 134-1, 134-2, 134-3 and 134-4 were not formed in the
tapered device region 102B due to the removal of portions of the
features 104B of the patterned fin-formation etch mask 104 by
performing a fin-cut-first process. Also note that, as depicted in
FIG. 2W, an isotropic etching process can be performed to remove
the desired portions of the fins 116-4 and 116-5 in the non-tapered
device region 102A so as to insure complete removal of the desired
portions of those fins and avoid undesirable remnants of those
fins, i.e., to avoid the fin spiking problem discussed in the
background section of this application. Also note that, as shown in
FIG. 2S, the cut ends 134C of the fins 134-1, 134-2, 134-3 and
134-4 in the tapered device region 102B are fully protected by the
layer of material 142 during the isotropic etching process
performed in FIG. 2W to remove the desired portions of the fins
116-4 and 116-5 in the non-tapered device region 102A. In the
example depicted herein, a fin-cut-first process is performed in
the region 102B followed by performing the fin-cut-last process in
the region 102A. However, as will be recognized by those skilled in
the art after a complete reading of the present invention, the
fin-cut-last process could be performed in the region 102A prior to
performing the fin-cut-first process in the device region 102B.
Thus, the presently disclosed inventions should not be considered
to be limited to the precise order of the steps depicted in the
illustrative process flow disclosed herein.
[0064] At the point of fabrication depicted in FIGS. 2Y-2Z
traditional manufacturing operations may be performed to complete
the formation of the product 100. For example, gate structures (not
shown) for the FinFET devices in regions 102A, 102B and planar
devices in the region 102C may be formed using either gate-first or
gate-last manufacturing techniques. Additionally, various
source/drain and gate contact structures may be formed on the
device, various metallization layers may be formed above the
substrate 102 for the product 100 using known processing
techniques, etc.
[0065] The particular embodiments disclosed above are illustrative
only, as the invention may be modified and practiced in different
but equivalent manners apparent to those skilled in the art having
the benefit of the teachings herein. For example, the process steps
set forth above may be performed in a different order. Furthermore,
no limitations are intended to the details of construction or
design herein shown, other than as described in the claims below.
It is therefore evident that the particular embodiments disclosed
above may be altered or modified and all such variations are
considered within the scope and spirit of the invention. Note that
the use of terms, such as "first," "second," "third" or "fourth" to
describe various processes or structures in this specification and
in the attached claims is only used as a shorthand reference to
such steps/structures and does not necessarily imply that such
steps/structures are performed/formed in that ordered sequence. Of
course, depending upon the exact claim language, an ordered
sequence of such processes may or may not be required. Accordingly,
the protection sought herein is as set forth in the claims
below.
* * * * *