U.S. patent application number 14/030601 was filed with the patent office on 2015-03-19 for self-alignment for using two or more layers and methods of forming same.
This patent application is currently assigned to Taiwan Semiconductor Manufacturing Company, Ltd.. The applicant listed for this patent is Taiwan Semiconductor Manufacturing Company, Ltd.. Invention is credited to Shih-Ming Chang, Tsai-Sheng Gau, Ken-Hsien Hsieh, Chih-Ming Lai, Ru-Gun Liu, Ming-Feng Shieh.
Application Number | 20150079774 14/030601 |
Document ID | / |
Family ID | 52472931 |
Filed Date | 2015-03-19 |
United States Patent
Application |
20150079774 |
Kind Code |
A1 |
Chang; Shih-Ming ; et
al. |
March 19, 2015 |
Self-Alignment for using Two or More Layers and Methods of Forming
Same
Abstract
Embodiments of the present disclosure include self-alignment of
two or more layers and methods of forming the same. An embodiment
is a method for forming a semiconductor device including forming at
least two gates over a substrate, forming at least two alignment
structures over the at least two gates, forming spacers on the at
least two alignment structures, and forming a first opening between
a pair of the at least two alignment structures, the first opening
extending a first distance from a top surface of the substrate. The
method further includes filling the first opening with a first
conductive material, forming a second opening between the spacers
of at least one of the at least two alignment structures, the
second opening extending a second distance from the top surface of
the substrate, and filling the second opening with a second
conductive material.
Inventors: |
Chang; Shih-Ming; (Zhubei
City, TW) ; Liu; Ru-Gun; (Zhubei City, TW) ;
Hsieh; Ken-Hsien; (Taipei City, TW) ; Shieh;
Ming-Feng; (Yongkang City, TW) ; Lai; Chih-Ming;
(Hsin-Chu, TW) ; Gau; Tsai-Sheng; (Hsin-Chu,
TW) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Taiwan Semiconductor Manufacturing Company, Ltd. |
Hsin-Chu |
|
TW |
|
|
Assignee: |
Taiwan Semiconductor Manufacturing
Company, Ltd.
Hsin-Chu
TW
|
Family ID: |
52472931 |
Appl. No.: |
14/030601 |
Filed: |
September 18, 2013 |
Current U.S.
Class: |
438/586 |
Current CPC
Class: |
H01L 21/31053 20130101;
H01L 21/28123 20130101; H01L 21/76897 20130101; H01L 27/088
20130101; H01L 21/823475 20130101; H01L 21/823437 20130101; H01L
21/76816 20130101 |
Class at
Publication: |
438/586 |
International
Class: |
H01L 21/768 20060101
H01L021/768; H01L 21/28 20060101 H01L021/28 |
Claims
1. A method for forming a semiconductor device, the method
comprising: forming at least two gates over a substrate; forming at
least two alignment structures over the at least two gates; forming
spacers on opposite sidewalls of the at least two alignment
structures; forming a first opening between a pair of the at least
two alignment structures, a portion of the first opening exposing a
top surface of at least one of the pair, the first opening
extending a first distance from a top surface of the substrate;
filling the first opening with a first conductive material to form
a first conductive feature; forming a second opening between the
spacers of at least one of the at least two alignment structures,
the second opening extending a second distance from the top surface
of the substrate, the second distance being different than the
first distance; and filling the second opening with a second
conductive material to form a second conductive feature.
2. The method of claim 1 further comprising: forming a first
dielectric layer over the at least two gates, the at least two
alignment structures being formed on a top surface of the first
dielectric layer; and forming a second dielectric layer over the at
least two alignment structures.
3. The method of claim 2, wherein the forming the first opening
further comprises: forming and patterning a photoresist on the
second dielectric layer; etching through the second dielectric
layer, the etching exposing the top surface of the at least one of
the pair; and etching through the first dielectric layer to the
first distance from the top surface of the substrate.
4. The method of claim 2, wherein the forming the second opening
further comprises: recessing the first conductive material to
expose the top surface of the at least one alignment structure;
removing the at least one alignment structure from between the
spacers of the at least one alignment structure, the removing
exposing the top surface of the first dielectric layer; and etching
through the first dielectric layer to the second distance from the
top surface of the substrate.
5. The method of claim 2 further comprising: removing the at least
two alignment structures; removing the second dielectric layer; and
planarizing the top surfaces of the first dielectric layer and the
first and second conductive features, wherein the top surfaces of
the first dielectric layer and the first and second conductive
features is substantially coplanar.
6. The method of claim 1, wherein one of the first and second
conductive features is electrically and physically coupled to one
of the at least two gates, and wherein the other one of the first
and second conductive features is electrically and physically
coupled to the top surface of the substrate.
7. The method of claim 1 further comprising forming gate spacers on
opposite sidewalls of each of the at least two gate, the first
opening and the second opening being laterally spaced from the each
of the gate spacers.
8. The method of claim 1, wherein each of the at least two
alignment structures is aligned with one of the at least two
gates.
9. The method of claim 1, wherein each of the at least two
alignment structures is aligned between an adjacent pair of the at
least two gates.
10. A method of forming a semiconductor device, the method
comprising: forming a plurality of gates over a semiconductor
substrate; forming a first inter-layer dielectric (ILD) over the
plurality of gates; forming at least two alignment structures over
the first ILD; forming a second ILD over the at least two alignment
structures; forming a first set of conductive contacts through the
first and second ILDs to a top surface of the semiconductor
substrate, one of the at least two alignment structures being
between an adjacent pair of the first set of conductive contacts;
and forming a second set of conductive contacts through the second
ILD and partially through the first ILD to the plurality of gates,
at least one of the second set of contacts extending through one of
the alignment structures.
11. The method of claim 10, wherein each of the at least two
alignment structures comprises alignment spacers on sidewalls of
the alignment structures, one of the first set of contacts being
laterally separated from one of the second set of contacts by an
alignment spacer.
12. The method of claim 10, wherein forming the first set of
conductive contacts further comprises: etching a first set of
openings through the second ILD and partially through the first
ILD, one of the first set of openings having sidewalls that extend
to a top surface of the second ILD, and another one of the first
set of openings having a first sidewall that extends to the top
surface of the second ILD and a second sidewall that extends to a
top surface of one of the at least two alignment structures;
etching through the remaining portion of the first ILD to expose
the top surface of the semiconductor substrate; and filling the
first set of openings with a conductive material to form the first
set of conductive contacts.
13. The method of claim 12, wherein the first sidewall extends to a
first height from the top surface of the semiconductor substrate,
and wherein the second sidewall extends to a second height from the
top surface of the semiconductor substrate, the second height being
different than the first height.
14. The method of claim 10, wherein one of the plurality of gates
is embedded within one of the first set of conductive contacts.
15. The method of claim 10, wherein each of the plurality of gates
comprises gate spacers on opposite sidewalls of the gates, both of
the gate spacers of one of the plurality of gates contacting at
least one of the first set of conductive contacts.
16. The method of claim 10, wherein each of the at least two
alignment structures comprises alignment spacers on opposite
sidewalls of the alignment structures, the at least one of the
second set of contacts extending between the alignment spacers of
one of the alignment structures.
17. A method of forming a semiconductor device, the method
comprising: forming a plurality of gates on a substrate; forming an
inter-layer dielectric (ILD) over the plurality of gates; forming a
first dielectric layer over the ILD; forming a first and a second
opening in the first dielectric layer, a portion of the first
dielectric layer between the first and the second opening forming a
primary alignment structure; forming secondary alignment structures
inside the first and second openings; forming a first contact
through the primary alignment structure and the ILD to a top
surface of the substrate; and forming a second contact through one
of the secondary alignment structures to a top surface of one of
the plurality of gates.
18. The method of claim 17 further comprising forming alignment
spacers inside the first and the second openings, an alignment
spacer laterally separating the primary alignment structure from
one of the secondary alignment structures.
19. The method of claim 17, wherein the primary alignment structure
comprises a different material composition than the secondary
alignment structures.
20. The method of claim 17 further comprising: at a same time as
forming the second contact, forming a third contact through another
one of the secondary alignment structures to a top surface of
another one of the plurality of gates; and at a same time as
forming the first contact, forming a fourth contact through the ILD
to the top surface of the substrate, the fourth contact being
laterally between an adjacent pair of the plurality of gates.
Description
BACKGROUND
[0001] Semiconductor devices are used in a variety of electronic
applications, such as personal computers, cell phones, digital
cameras, and other electronic equipment, as examples. Semiconductor
devices are typically fabricated by sequentially depositing
insulating or dielectric layers, conductive layers, and
semiconductive layers of material over a semiconductor substrate,
and patterning the various material layers using lithography to
form circuit components and elements thereon.
[0002] The semiconductor industry continues to improve the
integration density of various electronic components (e.g.,
transistors, diodes, resistors, capacitors, etc.) by continual
reductions in minimum feature size, which allow more components to
be integrated into a given area.
[0003] In particular, as designs shrink, conductive features
connecting to layers above and below may become shorted if the
conductive feature is misaligned. Generally, this occurs when the
etching process through the layer is misaligned such that the
conductive feature exposes portions of an adjacent conductive
feature on the layer below.
BRIEF DESCRIPTION OF THE DRAWINGS
[0004] For a more complete understanding of the present
embodiments, and the advantages thereof, reference is now made to
the following descriptions taken in conjunction with the
accompanying drawings, in which:
[0005] FIGS. 1A through 1N illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment;
[0006] FIGS. 2A through 2G illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment;
[0007] FIGS. 3A through 3L illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment;
[0008] FIGS. 4A through 4N illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment;
[0009] FIGS. 5A through 5T illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment; and
[0010] FIGS. 6A through 6X illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment.
DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS
[0011] Reference will now be made in detail to embodiments
illustrated in the accompanying drawings. Wherever possible, the
same reference numbers are used in the drawings and the description
to refer to the same or like parts. In the drawings, the shape and
thickness may be exaggerated for clarity and convenience. This
description will be directed in particular to elements forming part
of, or cooperating more directly with, methods and apparatus in
accordance with the present disclosure. It is to be understood that
elements not specifically shown or described may take various forms
well known to those skilled in the art. Many alternatives and
modifications will be apparent to those skilled in the art, once
informed by the present disclosure.
[0012] Reference throughout this specification to "one embodiment"
or "an embodiment" means that a particular feature, structure, or
characteristic described in connection with the embodiment is
included in at least one embodiment. Thus, the appearances of the
phrases "in one embodiment" or "in an embodiment" in various places
throughout this specification are not necessarily all referring to
the same embodiment. Furthermore, the particular features,
structures, or characteristics may be combined in any suitable
manner in one or more embodiments. It should be appreciated that
the following figures are not drawn to scale; rather, these figures
are merely intended for illustration.
[0013] Embodiments will be described with respect to a specific
context, namely a self-alignment scheme between two layers. Other
embodiments may also be applied, however, to align three or more
layers.
[0014] FIGS. 1A through 1N illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment. FIG. 1A illustrates a
semiconductor device includes a substrate 102, gates 104, hard
masks 106 on the gates 104, gate spacers 108 on the sidewalls of
the gates 104, and an inter-layer dielectric (ILD) 110 over the
gates 104, the hard masks 106, and the gate spacers 108. The
substrate 102 may be made of a semiconductor material such as
silicon, germanium, diamond, or the like. Alternatively, compound
materials such as silicon germanium, silicon carbide, gallium
arsenic, indium arsenide, indium phosphide, silicon germanium
carbide, gallium arsenic phosphide, gallium indium phosphide,
combinations of these, and the like, may also be used.
Additionally, the substrate 102 may be a silicon-on-insulator (SOI)
substrate. Generally, an SOI substrate includes a layer of a
semiconductor material such as epitaxial silicon, germanium,
silicon germanium, SOI, silicon germanium on insulator (SGOI), or
combinations thereof.
[0015] The substrate 102 may include active and passive devices
(not shown in FIG. 1A). As one of ordinary skill in the art will
recognize, a wide variety of devices such as transistors,
capacitors, resistors, combinations of these, and the like may be
used to generate the structural and functional requirements of the
semiconductor device. The devices may be formed using any suitable
methods. Only a portion of the substrate 102 is illustrated in the
figures, as this is sufficient to fully describe the illustrative
embodiments.
[0016] The substrate 102 may also include metallization layers (not
shown). The metallization layers may be formed over the active and
passive devices and are designed to connect the various devices to
form functional circuitry. The metallization layers may be formed
of alternating layers of dielectric (e.g., low-k dielectric
material) and conductive material (e.g., copper) and may be formed
through any suitable process (such as deposition, damascene, dual
damascene, or the like).
[0017] The gates 104 are formed over the substrate 102. The gates
104 may include a gate dielectric layer (not shown), a hard mask
106, and gate spacers 108. The gate dielectric layer may be formed
by thermal oxidation, chemical vapor deposition (CVD), sputtering,
or any other methods known and used in the art for forming a gate
dielectric. In some embodiments, the gate dielectric layer includes
dielectric materials having a high dielectric constant (k value),
for example, greater than 3.9. The gate dielectric materials
include silicon nitrides, oxynitrides, metal oxides such as
HfO.sub.2, HfZrO.sub.x, HfSiO.sub.x, HfTiO.sub.x, HfAlO.sub.x, the
like, or combinations and multi-layers thereof.
[0018] The gate electrode layer (not shown) may be formed over the
gate dielectric layer. The gate electrode layer may comprise a
conductive material and may be selected from a group comprising
polycrystalline-silicon (poly-Si), poly-crystalline
silicon-germanium (poly-SiGe), metallic nitrides, metallic
silicides, metallic oxides, and metals. In one embodiment,
amorphous silicon is deposited and recrystallized to create
polycrystalline silicon (poly-silicon). The gate electrode layer
may be deposited by physical vapor deposition (PVD), CVD, sputter
deposition, or other techniques known and used in the art for
depositing conductive materials. The top surface of the gate
electrode layer usually has a non-planar top surface, and may be
planarized prior to patterning of the gate electrode layer or gate
etch. Ions may or may not be introduced into the gate electrode
layer at this point. Ions may be introduced, for example, by ion
implantation techniques.
[0019] A hard mask layer (not shown) is formed over the gate
electrode layer. The hard mask layer may be made of SiN, SiON,
SiO.sub.2 the like, or a combination thereof. The hard mask layer
is then patterned. The patterning of the hard mask layer may be
accomplished by depositing mask material (not shown) such as
photoresist over the hard mask layer. The mask material is then
patterned and the hard mask layer is etched in accordance with the
pattern to form hard masks 106. The gate electrode layer and the
gate dielectric layer may be patterned to form the gates 104. The
gate patterning process may be accomplished by using the hard mask
106 as a pattern and etching the gate electrode layer and the gate
dielectric layer to form the gates 104.
[0020] The gate spacers 108 are formed on opposite sides of the
gates 104. The gate spacers 108 are formed by blanket depositing a
spacer layer (not shown) on the previously formed gates 104 and
hard masks 106. In an embodiment, the gate spacers 108 include a
spacer liner (not shown). The spacer liner may be made of SiN, SiC,
SiGe, oxynitride, oxide, the like, or a combination thereof. The
spacer layer may comprise SiN, oxynitride, SiC, SiON, oxide,
combinations thereof, or the like and may be formed by methods
utilized to form such a layer, such as CVD, plasma enhanced CVD
(PECVD), low pressure CVD (LPCVD), atomic layer deposition (ALD),
sputter, the like, or a combination thereof. The gate spacers 108
are then patterned, for example, by an anisotropic etch to remove
the spacer layer from top surfaces 106A of the hard masks 106.
[0021] Although the description above described the formation of a
gate 104, the structure 104 is not limited to a gate. In some
embodiments, the structure 104 is a conductive line 104 that is to
be aligned and coupled with another conductive feature by the
subsequently formed conductive feature 126 (see FIG. 1N).
[0022] After the gates 104, hard masks 106, and gate spacers 108
are formed, the ILD 110 is formed over these structures and the
substrate 102. The ILD 110 may be formed of oxides such as silicon
oxide, borophosphosilicate glass (BPSG), undoped silicate glass
(USG), fluorinated silicate glass (FSG), low-k dielectrics such as
carbon doped oxides, extremely low-k dielectrics such as porous
carbon doped silicon dioxide, a polymer such as polyimide, the
like, or a combination thereof. The low-k dielectric materials may
have k values lower than 3.9. The ILD 110 may be deposited by CVD,
PVD, ALD, a spin-on-dielectric (SOD) process, the like, or a
combination thereof. In an embodiment, the ILD 24 is formed
directly on a top surface 102A of the substrate 102. In other
embodiments, the ILD 110 is formed on intermediate layers and/or
structures (not shown) which are on substrate 102. In some
embodiments, the ILD 110 is planarized by a chemical mechanical
polish (CMP) process or an etching process to form a substantially
planar top surface 110A.
[0023] FIG. 1B illustrates the formation of alignment structures
112 and alignment spacers 114 on the top surface 110A of the ILD
110. The alignment structures 112 and the spacers 114 may be formed
of similar materials and by similar processes as the gates 104 and
the spacers 108, respectively, and the descriptions will not be
repeated herein, although the materials and processes need not be
the same. In an embodiment, each of the alignment structures 112 is
aligned with a gate 104 in the layer below the respective alignment
structure 112. In some embodiments, the alignment spacers 114 are
formed to have a width W.sub.1 in a range from about 10% to about
40% of a minimum space between adjacent alignment structures
112.
[0024] FIG. 1C illustrates the formation of an ILD 116 and a
patterning layer 118 over the ILD 110. The ILD 116 is formed over
the alignment structures 112 and the alignment spacers 114 and on
the ILD 110. The ILD 116 may be formed of similar materials and by
similar processes as the ILD 110 and the description will not be
repeated herein, although the ILD 116 and the ILD 110 need not be
the same.
[0025] The patterning layer 118 is formed and patterned over the
ILD 116. In an embodiment, the patterning layer 118 is formed of a
photoresist material, such as a deep ultraviolet (DUV) photoresist,
an extreme ultraviolet (EUV) photoresist, an electron beam direct
write (EBDW) photoresist, or the like, and is deposited on the
surface of the ILD 116 by using a spin-on process to place the
patterning layer 118. However, any other suitable material or
method of forming or placing a photoresist material may
alternatively be utilized. In this embodiment, once the patterning
layer 118 has been placed on the ILD 116, the patterning layer 118
is exposed to energy, e.g. light, through a patterned reticle in
order to induce a reaction in those portions of the patterning
layer 118 exposed to the energy. The patterning layer 118 is then
developed, and portions of the patterning layer 118 are removed
forming openings 120A, 120B, and 120C, exposing a top surface 116A
of the ILD 116 through the openings 120A, 120B, and 120C. In
another embodiment, the patterning layer 118 is a hard mask. In
this embodiment, the patterning layer 118 is formed of and by
similar processes as the hard masks 106, and the details will not
be repeated herein, although the patterning layer 118 and the hard
masks 106 need not be the same.
[0026] FIG. 1D illustrates the formation of the openings 120A,
120B, and 120C through the ILD 116 and partially through the ILD
110. Although a portion of the opening 120A extends over a top
surface 112A of the alignment structure 112, the alignment
structure 112 and the alignment spacers 114 self-align the opening
120 between a pair of the adjacent gates 104. The opening 120B is
self-aligned by another spacer 114 to be between a pair of adjacent
gates 104. The opening 120C does not require an alignment by an
alignment structure 112 or alignment spacer 114. The openings 120A,
120B, and 120C may be formed by using acceptable etching
techniques. In an embodiment, the openings 120A, 120B, and 120C are
formed by an anisotropic dry etch.
[0027] FIG. 1E illustrates the removal of the patterning layer 118
to expose the top surface 116A of the ILD 116. The patterning layer
118 may be removed by a CMP process, an etch process, the like, or
a combination thereof.
[0028] FIG. 1F illustrates forming the openings 120A, 120B, and
120C through the remaining portion of the ILD 110 to expose
portions of the top surface 102A of the substrate 102. The opening
120A is formed between a pair of alignment structures 112 with
their respective alignment spacers 114 and a pair of gates 104 with
their gate spacers 108. The opening 120B is formed between an
alignment structure 112 with its respective alignment spacer 114
and a patterned portion of ILD 116 and between a pair of gates 104
with their respective gate spacers 108. The opening 120C is formed
between patterned portions of ILD 116 and between a gate 104 with
its respective gate spacer 108 and a portion of patterned ILD 110.
In an embodiment, the openings 120A, 120B, and 120C are extended
through ILD 110 by using an anisotropic dry etch.
[0029] FIG. 1G illustrates the formation of a conductive layer 122
in the openings 120A, 120B, and 120C contacting the top surface
102A of the substrate 102 and along top surfaces 116A of the ILD
116, top surfaces 112A of the alignment structures 112, and
alignment spacers 114. In some embodiments, the conductive layer
122 includes a barrier layer (not shown). The barrier layer helps
to block diffusion of the subsequently formed conductive layer 122
into adjacent dielectric materials such as ILD 110. The barrier
layer may be made of titanium, titanium nitride, tantalum, tantalum
nitride, manganese, manganese oxide, cobalt, cobalt oxide, cobalt
nitride, nickel, nickel oxide, nickel nitride, silicon carbide,
oxygen doped silicon carbide, nitrogen doped silicon carbide,
silicon nitride, aluminum oxide, aluminum nitride, aluminum
oxynitride, a polymer such as polyimide, polybenzoxazole (PBO) the
like, or a combination thereof. The barrier layer may be formed by
CVD, PVD, plasma enhanced CVD (PECVD), ALD, SOD, the like, or a
combination thereof. In some embodiments, the barrier layer is
omitted.
[0030] The conductive layer 122 may be made of tungsten, copper,
aluminum, the like, or a combination thereof. The conductive layer
122 may be formed through a deposition process such as
electrochemical plating, PVD, CVD, the like, or a combination
thereof. In some embodiments, the conductive layer 122 is formed on
a copper seed layer.
[0031] FIG. 1H illustrates the recessing of the conductive layer
122 to form conductive features 122A, 122B, and 122C in the
openings 120A, 120B, and 120C, respectively. In some embodiments,
the top surfaces 122A1, 122B1, and 122C1 of the conductive features
122A, 122B, and 122C, respectively, is below the top surface 112A
of the alignment structure 112 and the top surface 116A of the ILD
116 after the recessing. In an embodiment, the recessing is
performed by a dry etch process with a plasma source and an etchant
gas such as CF.sub.4, SF.sub.6, the like, or a combination
thereof.
[0032] FIG. 1I illustrates the formation of openings 124 by
removing the alignment structures 112 from between the alignment
spacers 114 to expose the top surface 110A of the ILD 110. The
alignment structures 112 may be removed by an etch process, such as
a wet etch process, that is selective to the alignment structures
112.
[0033] FIG. 1J illustrates extending the openings 124 through the
ILD 110 to expose the top surfaces 106A of the hard masks 106. The
openings 124 may be extended through the ILD 110 by using
acceptable etching techniques such as, for example, an anisotropic
dry etch.
[0034] FIG. 1K illustrates extending the openings 124 through the
hard masks 106 to expose top surfaces 104A of the gates 104. The
openings 124 may be extended through the hard masks 106 by using
acceptable etching techniques such as, for example, an anisotropic
dry etch.
[0035] FIG. 1L illustrates the formation of a conductive layer 126
in the openings 124 contacting the top surface 104A of the gates
104 and over the conductive features 122A, 122B, and 122C. The
conductive layer 126 may be formed of similar materials and by
similar processes as the conductive layer 122 discussed above and
the description will not be repeated herein, although the
conductive layers 122 and 126 need not be the same.
[0036] FIG. 1M illustrates the recessing of the conductive layer
126 to form conductive features 126A and 126B in the openings 124
and the recessing of the conductive features 122A, 122B, and 122C.
In some embodiments, the top surfaces 126A1 and 126B1 of the
conductive features 126A and 126B, respectively, and the top
surfaces 122A1, 122B1, and 122C1 of the conductive features 122A,
122B, and 122C, respectively, are substantially coplanar after the
recessing. In an embodiment, the recessing is performed by a dry
etch process that etches conductive layer 126 conductive features
122A, 122B, and 122C with a plasma source and an etchant gas such
as CF.sub.4, SF.sub.6, the like, or a combination thereof.
[0037] FIG. 1N illustrates the removal of the alignment spacers 114
and the remaining portions of ILD 116 and the planarization of the
ILD 110, conductive features 126A, 126B, 122A, 122B, and 122C. The
planarization process may be a CMP process, an etch process, the
like, or a combination thereof. In some embodiments, the top
surfaces 126A1 and 126B1 of the conductive features 126A and 126B,
respectively, the top surfaces 122A1, 122B1, and 122C1 of the
conductive features 122A, 122B, and 122C, respectively, and the top
surface 110A of the ILD 110 are substantially coplanar after the
planarization process. In an embodiment, the conductive features
126 (126A and 126B) are formed to have a width W.sub.2 in a range
from about 50% to about 150% of a width of the gate 104 below the
respective conductive feature 126. In an embodiment, the conductive
features 122 (122A, 122B, and 122C) are formed to have a width
W.sub.3 in a range from about 50% to about 150% of a width between
adjacent gates 104. In some embodiments where the gates 104 are
gate electrodes, the conductive features 126A and 126B are used as
contacts to couple the gates 104 to layers above the ILD 110 and
the conductive features 122A, 122B, and 122C are used as contacts
to couple the substrate 102 and devices and layers (e.g.
source/drain features) formed therein to layers above ILD 110. In
other embodiments where the structure 104 is a conductive line 104,
the conductive features 126 and 126B are used to couple the
conductive line 104 to another conductive feature above the ILD 110
and the conductive features 122A, 122B, and 122C are used as
contacts to couple the substrate 102 and devices and metallization
layers formed therein to layers above ILD 110.
[0038] By having only spacers surrounding the gates in the ILD
layer, the ILD layer is able to be kept clean and free from residue
from other spacers and/or hard masks as the alignment structures
are formed in ILD layer above the ILD layer containing the gates.
Further, the process described above allows line patterns (e.g.
alignment structure 112) to self-align to another line pattern
(
[0039] FIGS. 2A through 2G illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment. Details regarding this embodiment
that are similar to those for the previously described embodiment
will not be repeated herein.
[0040] FIGS. 2A and 2B are similar to FIGS. 1A and 1B,
respectively, and the descriptions will not be repeated herein.
FIG. 2C is similar to FIG. 1C except that in FIG. 2C, the openings
120A and 120B do not have portion of patterning layer 118 between
them. FIG. 2D illustrates the formation of the openings 120A, 120B,
and 120C through the ILD 116 and partially through the ILD 110. In
this embodiment, there is no portion of ILD 116 between openings
120A and 120B as the ILD 116 was removed because there was no
portion of patterning layer 118 between the openings 120A and 120B.
Also, in this embodiment, there is a portion of ILD 116 between
openings 120B and 120C.
[0041] FIG. 2E illustrates the removal of the patterning layer 118
to expose the top surface 116A of the ILD 116. The patterning layer
118 may be removed by a CMP process, an etch process, the like, or
a combination thereof.
[0042] FIG. 2F illustrates forming the openings 120A, 120B, and
120C through the remaining portion of the ILD 110 to expose
portions of the top surface 102A of the substrate 102. The
semiconductor device in FIG. 2F is similar to the semiconductor
device in FIG. 1F and the description will not be repeated herein.
In this embodiment, even though the patterning layer 118 did not
include a portion between the openings 120A and 120B (see FIG. 2C),
the openings 120A and 120B ended up the same as the embodiment
illustrated in FIG. 1F because the alignment structure 112 and
alignment spacer 114 separate the openings 120A and 120B in both
embodiments.
[0043] FIG. 2G illustrates the semiconductor device with conductive
features 126A, 126B, 122A, 122B, and 122C similar to those
described above in FIG. 1N. The processing steps between FIGS. 2F
and 2G are similar to those illustrate in FIGS. 1G through 1N and
are not repeated herein.
[0044] FIGS. 3A through 3L illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment. Details regarding this embodiment
that are similar to those for the previously described embodiment
will not be repeated herein.
[0045] FIGS. 3A and 3B are similar to FIGS. 1A and 1B,
respectively, and the descriptions will not be repeated herein.
FIG. 3C is similar to FIG. 1C except that in FIG. 3C, the openings
120B and 120C of FIG. 1C do not have a portion of patterning layer
118 between them forming a single opening 120D in FIG. 2C.
[0046] FIG. 3D illustrates the formation of the openings 120A and
120D through the ILD 116 and partially through the ILD 110. In this
embodiment, the opening 120D includes the entire top surface 106A
of a hard mask 106 on a gate 104 as there was no portion of ILD 116
on the hard mask 106.
[0047] FIG. 3E illustrates the removal of the patterning layer 118
and forming the openings 120A and 120D through the remaining
portion of the ILD 110 to expose portions of the top surface 102A
of the substrate 102. In this embodiment, the opening 120D includes
a gate 104, hard mask 106, and gate spacers 108 along a bottom of
the opening 120D.
[0048] FIG. 3F illustrates the formation of a conductive layer 122
in the openings 120A and 120D contacting the top surface 102A of
the substrate 102 and along the top surface 106A of a hard mask
106, gate spacers 108, top surfaces 116A of the ILD 116, top
surfaces 112A of the alignment structures 112, and alignment
spacers 114.
[0049] FIG. 3G illustrates the recessing of the conductive layer
122 to form conductive features 122A and 122D in the openings 120A
and 120D, respectively. In this embodiment, the conductive feature
122D coupled to the substrate 102 on at least two sides of a gate
104. In some embodiments, a single gate 104 is embedded in the
conductive feature 122D. In other embodiments, more than one gate
104 is embedded in the conductive feature 122D.
[0050] FIG. 3H illustrates the formation of openings 124 by
removing the alignment structures 112 from between the alignment
spacers 114 and extending the openings 124 through the ILD 110 to
expose the top surfaces 106A of the hard masks 106. In some
embodiments, after the openings 124 are extended to the hard masks
106, the top surfaces 122A1 and 122D1 are higher than the top
surface 116A of the ILD 116. FIG. 3I illustrates extending the
openings 124 through the hard masks 106 to expose top surfaces 104A
of the gates 104.
[0051] FIG. 3J illustrates the formation of the conductive layer
126 in the openings 124 contacting the top surface 104A of the
gates 104 and over the alignment spacers 114 and the conductive
features 122A and 122D. The conductive layer 126 may be formed of
similar materials and by similar processes as the conductive layer
122 discussed above and the description will not be repeated
herein, although the conductive layers 122 and 126 need not be the
same.
[0052] FIG. 3K illustrates the recessing of the conductive layer
126 to form conductive features 126A and 126B in the openings 124
and the recessing of the conductive features 122A, 122B, and 122C.
In some embodiments, the top surfaces 126A1 and 126B1 of the
conductive features 126A and 126B, respectively, and the top
surfaces 122A1 and 122D1 of the conductive features 122A and 122D,
respectively, are substantially coplanar after the recessing.
[0053] FIG. 3L illustrates the removal of the alignment spacers 114
and the remaining portions of ILD 116 and the planarization of the
ILD 110, conductive features 126A, 126B, 122A, and 122D. The
planarization process may be a CMP process, an etch process, the
like, or a combination thereof. In some embodiments, the top
surfaces 126A1 and 126B1 of the conductive features 126A and 126B,
respectively, the top surfaces 122A1 and 122D1 of the conductive
features 122A and 122D, respectively, and the top surface 110A of
the ILD 110 are substantially coplanar after the planarization
process. The conductive features 126A and 126B may be used as
contacts to couple the gates 104 to layers above the ILD 110 and
the conductive features 122A and 122D may be used as contacts to
couple the substrate 102 and devices and metallization layers
formed therein to layers above ILD 110. In some embodiments, the
conductive feature 122D is used to couple devices that have higher
current requirements than the devices coupled to the conductive
feature 122A.
[0054] FIGS. 4A through 4N illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment. Details regarding this embodiment
that are similar to those for the previously described embodiment
will not be repeated herein.
[0055] FIG. 4A illustrates a semiconductor device includes a
substrate 302, gates 304, hard masks 306 on the gates 304, gate
spacers 308 on the sidewalls of the gates 304, and an ILD 310 over
the gates 304, the hard masks 306, and the gate spacers 308. The
substrate 302, gates 304, hard masks 306, gate spacers 308, and ILD
310 may be formed of similar materials and similar processes as the
substrate 102, gates 104, hard masks 106, gate spacers 108, and ILD
110 described above and the descriptions will not be repeated
herein. However, the materials and processes of the two embodiments
of the semiconductor device need not be the same.
[0056] FIG. 4B illustrates the formation of alignment structures
312 and alignment spacers 314 on the top surface 310A of the ILD
310. The alignment structures 312 and the alignment spacers 314 may
be formed of similar materials and by similar processes as the
alignment structures 112 and the alignment spacers 114,
respectively, described above and the descriptions will not be
repeated herein, although the materials and processes need not be
the same. In embodiment, each of the alignment structures 312 is
aligned between a pair of adjacent gates 304 in the layer below the
respective alignment structure 312.
[0057] FIG. 4C illustrates the formation of an ILD 316 and a
patterning layer 318 over the ILD 310. The ILD 316 is formed over
the alignment structures 312 and the alignment spacers 314 and on
the ILD 310. The ILD 316 may be formed of similar materials and by
similar processes as the ILD 116 described above and the
description will not be repeated herein, although the ILD 316 and
the ILD 116 need not be the same.
[0058] The patterning layer 318 is formed and patterned over the
ILD 316. The patterning layer 318 may be formed of similar
materials and patterned by similar processes as the patterning
layer 118 described above and the description will not be repeated
herein. The patterning layer 318 is patterned to form openings 320
exposing portions of the top surface 316A of the ILD 316. In some
embodiments, each of the openings 320 is aligned directly over a
gate 304.
[0059] FIG. 4D illustrates extending the openings 320 through the
ILD 316 and partially through the ILD 310 to expose portions of top
surfaces 306A of the hard masks 306. The openings 320 may be formed
by using acceptable etching techniques such as, for example, an
anisotropic dry etch.
[0060] FIG. 4E illustrates the removal of the patterning layer 318
to expose the top surface 316A of the ILD 316. The patterning layer
318 may be removed by a CMP process, an etch process, the like, or
a combination thereof.
[0061] FIG. 4F illustrate the thinning of the ILD 316 to expose top
surfaces 312A of the alignments structures 312. The thinning
process may be by a CMP process, an etch process, the like, or a
combination thereof.
[0062] FIG. 4G illustrates extending the openings 320 through the
hard masks 306 to expose top surfaces 304A of the gates 304. The
openings 320 may be extended through the hard masks 306 by using
acceptable etching techniques such as, for example, an anisotropic
dry etch.
[0063] FIG. 4H illustrates the formation of a conductive layer 322
in the openings 320 contacting the top surface 304A of the gates
304 and along the top surfaces 312A of the alignment structures
312, the alignment spacers 314, and the ILD 36. The conductive
layer 322 may be formed of similar materials and by similar
processes as the conductive layer 122 discussed above and the
description will not be repeated herein, although the conductive
layers 322 and 122 need not be the same.
[0064] FIG. 4I illustrates the recessing of the conductive layer
322 to form conductive features 322 in the openings 320. In some
embodiments, the top surfaces 322A of the conductive features 322
are lower than the top surfaces 312A of the alignment structures
312 and the top surface 316A of the ILD 316. This recessing process
may be similar to the recessing process of conductive layer 122
described above and the description will not be repeated herein,
although the recessing processes need not be the same.
[0065] FIG. 4J illustrates the formation of openings 324 by
removing the alignment structures 312 from between the alignment
spacers 314 to expose the top surface 310A of the ILD 310. The
alignment structures 312 may be removed by a wet etch process that
is selective to the alignment structures 312.
[0066] FIG. 4K illustrates extending the openings 324 through the
ILD 310 to expose portions of the top surface 302A of the substrate
302. The openings 324 may be extended through the ILD 310 by using
acceptable photolithography and etching techniques such as, for
example, an anisotropic dry etch.
[0067] FIG. 4L illustrates the formation of a conductive layer 326
in the openings 324 contacting the top surface 302A of the
substrate 302 and over the conductive features 322. The conductive
layer 326 may be formed of similar materials and by similar
processes as the conductive layer 122 discussed above and the
description will not be repeated herein.
[0068] FIG. 4M illustrates the recessing of the conductive layer
326 to form conductive features 326 in the openings 324. In some
embodiments, the top surfaces 326A of the conductive features 326
and the top surfaces 322A the conductive features 322 are
substantially coplanar after the recessing. This recessing process
may be similar to the recessing process of conductive layer 122
described above and the description will not be repeated herein,
although the recessing processes need not be the same.
[0069] FIG. 4N illustrates the removal of the alignment spacers 314
and the remaining portions of ILD 116 and the planarization of the
ILD 310 and the conductive features 322 and 326. The planarization
process may be a CMP process, an etch process, the like, or a
combination thereof. In some embodiments, the top surfaces 326A of
the conductive features 326, the top surfaces 322A of the
conductive features 322, and the top surface 310A of the ILD 310
are substantially coplanar after the planarization process. The
conductive features 322 may be used as contacts to couple the gates
304 to layers above the ILD 310 and the conductive features 326 may
be used as contacts to couple the substrate 302 and devices and
metallization layers formed therein to layers above ILD 310.
[0070] FIGS. 5A through 5T illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment. Details regarding this embodiment
that are similar to those for the previously described embodiment
will not be repeated herein.
[0071] FIG. 5A illustrates a semiconductor device includes a
substrate 402, gates 404, hard masks 406 on the gates 404, gate
spacers 408 on the sidewalls of the gates 404, and an ILD 410 over
the gates 404, the hard masks 406, and the gate spacers 408. The
semiconductor device further includes an anti-reflective coating
(ARC) layer 412, a hardmask layer 414, an ARC layer 416, a
dielectric layer 418, an ARC layer 420, a hardmask layer 422, an
ARC layer 424, a dielectric layer 426, a hardmask layer 428, and a
photoresist 430. The substrate 402, gates 404, hard masks 406, gate
spacers 408, and ILD 410 may be formed of similar materials and
similar processes as the substrate 102, gates 104, hard masks 106,
gate spacers 108, and ILD 110 described above and the descriptions
will not be repeated herein. However, the materials and processes
of the two embodiments of the semiconductor device need not be the
same.
[0072] The ARC layer 412 is formed over the ILD 410. The ARC layer
412 prevents radiation in a subsequent photolithographic process to
reflect off layers below and interfering with the exposure process.
Such interference can increase the critical dimension of the
photolithography process. The ARC layer 412 may comprise SiON, a
polymer, the like, or a combination thereof and may be formed by
CVD, a spin-on process, the like, or a combination thereof. In an
embodiment the ARC layer 412 is formed to a thickness of between
about 200 .ANG. and about 400 .ANG..
[0073] The hardmask layer 414 is formed over the ARC layer 412. The
hardmask layer 414 may be a masking material such as poly-silicon,
silicon nitride, the like, or a combination thereof may be formed
using a process such as plasma enhanced chemical vapor deposition
(PECVD). However, any other suitable hardmask material, such as
silicon oxide, and any other process of formation, such as CVD, may
alternatively be utilized. In an embodiment the hardmask layer 414
is formed to a thickness of between about 200 .ANG. and about 400
.ANG..
[0074] The ARC layer 416 is formed over the hardmask layer 414. The
ARC layer 416 may be formed of similar materials and by similar
processes as the ARC layer 412 described above and the description
is not repeated herein, although the first and ARC layers 412 and
416 need not be the same. In an embodiment the ARC layer 416 is
formed to a thickness of from about 200 .ANG. to about 400
.ANG..
[0075] The dielectric layer 418 is formed over the ARC layer 416.
The dielectric layer 418 may be formed of oxides such as silicon
oxide, BPSG, USG, FSG, low-k dielectrics such as carbon doped
oxides, extremely low-k dielectrics such as porous carbon doped
silicon dioxide, a polymer such as polyimide, the like, or a
combination thereof. The low-k dielectric materials may have k
values lower than 3.9. The dielectric layer 418 may be deposited by
CVD, PVD, ALD, an SOD process, the like, or a combination thereof.
In an embodiment, the dielectric layer 418 is formed to a thickness
of from about 300 .ANG. to about 700 .ANG..
[0076] The ARC layer 420, the hardmask layer 422, the ARC layer
424, and the dielectric layer 426 are formed over the dielectric
layer 418. The ARC layer 420, the hardmask layer 422, the ARC layer
424, and the dielectric layer 426 may be formed of similar
materials and by similar processes as the ARC layer 412, the
hardmask layer 414, the ARC layer 416, and the dielectric layer
418, respectively, described above and the descriptions are not
repeated herein.
[0077] The hardmask layer 428 is formed over the dielectric layer
426. The hardmask layer may be formed of similar materials and by
similar processes as the hardmask layer 414 described above and the
description is not repeated herein. The photoresist 430 is formed
over the hardmask layer 428. The photoresist 430 may be formed of a
conventional photoresist material, such as a deep ultra-violet
(DUV) photoresist. The photoresist 430 may be deposited on the
surface of the hardmask layer 428, for example, by using a spin-on
process to place the photoresist 430. However, any other suitable
material or method of forming or placing a photoresist material may
alternatively be utilized.
[0078] FIG. 5B illustrates the semiconductor device after
undergoing a double patterning process to form openings 432. The
double patterning process may be process including two
photolithography exposure steps and two etching steps which may be
referred to as a 2P2E process. The openings 432 extend through the
ARC layer 424 and the hardmask layer 422 and expose portions of the
ARC layer 420. The openings 432 may be formed by using acceptable
photolithography and etching techniques such as, for example, an
anisotropic dry etch.
[0079] FIG. 5C illustrates extending the openings 432 through the
ARC layer 420 and the dielectric layer 418 to expose portions of
the ARC layer 416. In an embodiment, the openings 432 are extended
through the ARC layer 420 and the dielectric layer 418 by using an
anisotropic dry etch.
[0080] FIG. 5D illustrates forming an alignment layer 434 on the
ARC layer 420 and in the openings 432. The alignment layer 434 may
be formed of a polycrystalline-silicon (poly-Si), poly-crystalline
silicon-germanium (poly-SiGe), oxides, nitrides, the like, or a
combination thereof. In one embodiment, amorphous silicon is
deposited and recrystallized to create polycrystalline silicon
(poly-silicon). The alignment layer 434 may be deposited by PVD,
CVD, sputter deposition, the like, or a combination thereof. The
top surface of the alignment layer 434 may have a non-planar top
surface, and may be planarized by, for example, a CMP process.
[0081] FIG. 5E illustrates the thinning of the alignment layer 434
and the removal of the ARC layer 420 and the dielectric layer 418
to form alignment structures 436. The thinning and removal steps
may include a CMP process, an etch process, the like, or a
combination thereof. In embodiment, each of the alignment
structures 436 is aligned with a gate 404 in layers below the
respective alignment structure 436.
[0082] FIG. 5F illustrates the formation of alignment spacers 438
on the sidewalls of the alignment structures 436. The alignment
spacers 438 may be formed of similar materials and by similar
processes as the alignment spacers 114 described above the
description is not repeated herein.
[0083] FIG. 5G illustrates the formation of dielectric layer 440,
hardmask layer 442, and photoresist 444 over the alignment
structures 436 with openings 446 formed in the photoresist 444. The
openings 446 are aligned between the alignment structures 436. FIG.
5G illustrates extending the openings 446 through the hardmask
layer 442, the dielectric layer 440, and the ARC layer 416 to
portions of the top surface 414A of the hardmask layer 414.
[0084] FIG. 5I illustrates the formation of dielectric layer 448,
hardmask layer 450, and photoresist 452 over the alignment
structures 436 and in the openings 446 and the formation of an
opening 454 formed in the photoresist 452. The opening 446 is
aligned adjacent an alignment structures 436 and between gates 404.
FIG. 5J illustrates extending the opening 454 through the hardmask
layer 450, the dielectric layer 448, and the ARC layer 416 to
expose portions of the top surface 414A of the hardmask layer
414.
[0085] FIG. 5K illustrates removing the dielectric layer 448 to
expose the alignment structures 436 and the ARC layer 416. FIG. 5L
illustrate extending the openings 446 and 454 to form openings 456
through the hardmask layer 414, the ARC layer 412, and the ILD 410
to expose portions of the top surface 402A of the substrate 402.
FIG. 5M illustrates forming a conductive layer 458 in the openings
456 and over the alignment structures 436 and the ARC layer 416.
The conductive layer 458 may be formed of similar materials and by
similar processes as the conductive layer 122 described above and
the description is not repeated herein.
[0086] FIG. 5N illustrates the recessing of the conductive layer
458 and removing the alignment structures 436 to expose the top
surface 416A of the ARC layer 416 between the alignment spacers
438. The alignment structures 436 may be removed by a wet etch
process that is selective to the alignment structures 436.
[0087] FIG. 5O illustrates forming openings 460 through the ARC
layer 416, the hardmask layer 414, the ARC layer 412, and partially
through the ILD 410 to expose the top surfaces 406A of the hard
masks 406. The openings 460 may be formed by using acceptable
photolithography and etching techniques such as, for example, an
anisotropic dry etch.
[0088] FIG. 5P illustrates extending the openings 460 through the
hard masks 406 to expose top surfaces 404A of the gates 104. The
openings 460 may be extended through the hard masks 406 by using
acceptable photolithography and etching techniques such as, for
example, an anisotropic dry etch.
[0089] FIG. 5Q illustrates removing the conductive layer 458 from
the openings 456 to expose the portions of the top surface 402A of
the substrate 402 in the openings 456. The conductive layer 458 may
be removed by a wet etch process that is selective to the
conductive layer 458.
[0090] FIG. 5R illustrates forming a conductive layer 462 in the
openings 456 and 460. FIG. 5S illustrates recessing the conductive
layer 462 to form conductive features 464 in the openings 460
contacting the top surfaces 404A of the gates 404 and conductive
features 466 in the openings 456 contacting the top surface 402A of
the substrate 402. In an embodiment, the recessing is performed by
a dry etch process with a plasma source and an etchant gas such as
H.sub.2, NH.sub.3, Ar, He, the like, or a combination thereof.
[0091] FIG. 5T illustrates removing the alignment spacers 438, the
ARC layers 416 and 412, and the hardmask layer 414 and the
planarization of the ILD 510 and the conductive features 466 and
464. The planarization process may be a CMP process, an etch
process, the like, or a combination thereof. In some embodiments,
the top surfaces 466A of the conductive features 466, the top
surfaces 464A of conductive features 464, and the top surface 410A
of the ILD 410 are substantially coplanar after the planarization
process. The conductive features 464 may be used as contacts to
couple the gates 404 to layers above the ILD 410 and the conductive
features 466 may be used as contacts to couple the substrate 402
and devices and metallization layers formed therein to layers above
ILD 410.
[0092] FIGS. 6A through 6X illustrate cross-sectional views of
intermediate stages in the manufacturing of a semiconductor device
in accordance with an embodiment. Details regarding this embodiment
that are similar to those for the previously described embodiment
will not be repeated herein.
[0093] FIG. 6A illustrates an intermediate stage of manufacture of
a semiconductor device similar to FIG. 5C described above and the
description is not repeated herein.
[0094] FIG. 6B illustrates the formation of alignment spacers 468
inside the openings 432. The alignment spacers 468 may be formed
similar to the alignment spacers 114 described above and the
description is not repeated herein. In this embodiment, the
alignment spacers 468 are formed on the sidewalls of openings,
whereas in the previous embodiments, the alignment spacers were
formed on sidewalls of a structure (e.g. an alignment structure).
By forming the alignment spacers 468 in the openings 432, a portion
of the dielectric layer 418 between the openings 432 forms an
alignment structure 467.
[0095] FIG. 6C illustrates forming an alignment structure 470
between the alignment spacers 468. The alignment structures 470 are
formed after the alignment spacers 468 and are referred to as
secondary alignment structures 470 with the alignment structure 467
being a primary alignment structure 467. The secondary alignment
structures 470 may be formed of a polycrystalline-silicon
(poly-Si), poly-crystalline silicon-germanium (poly-SiGe), oxides,
nitrides, the like, or a combination thereof. In one embodiment,
amorphous silicon is deposited and recrystallized to create
polycrystalline silicon (poly-silicon). The secondary alignment
structures 470 may be deposited by PVD, CVD, sputter deposition,
the like, or a combination thereof. In an embodiment, the top
surfaces 470A of the secondary alignment structures 470 are
recessed by an etching process to make the top surfaces 470A lower
than the top surface 420A of the ARC layer 420.
[0096] FIG. 6D illustrates the formation of a dielectric layer 472,
a hardmask layer 474, and a photoresist 476 over the primary
alignment structure 467, the secondary alignment structures 470,
and the ARC layer 420. FIG. 6E illustrates the formation of
openings 478A and 478B in the photoresist 476 with opening the 478A
aligned over a portion of a secondary alignment structure 470 and a
portion over the primary alignment structure 467. The opening 478B
is aligned adjacent one of the gates 404.
[0097] FIG. 6F illustrates extending the openings 478A and 478B
through the hardmask layer 474 and the dielectric layer 472 to
expose portions of the top surfaces 420A of the ARC layer 420, a
portion of the top surface 470A of the secondary alignment
structure 470, and a portion of an alignment spacer 468. In an
embodiment, both the openings 478A and 478B expose a portion of the
top surface 420A of the ARC layer 420.
[0098] FIG. 6G illustrates extending the openings 478A and 478B
through the ARC layer 420 to expose a top surface 467A of the
primary alignment structure 467 and a portion of the top surface
418A of the dielectric layer 418. FIG. 6H illustrates removing the
hardmask layer 474, the dielectric layer 472, and the primary
alignment structure 467 and extending the openings 478A and 478B
through the dielectric layer 418. In this embodiment, the opening
478A extends between a pair of alignment spacers 468 to expose a
top surface 416A of the ARC layer 416.
[0099] FIG. 6I illustrates extending the openings 478A and 478B
through the ARC layer 416 to expose portions of the top surface
414A of the hardmask layer 414. FIG. 6J illustrates the formation
of a dielectric layer 480, a hardmask layer 482, and a photoresist
in the openings 478A and 478B and over the secondary alignment
structures 470 and the dielectric layer 418. An opening 486 is
formed in the photoresist 484 with opening 486 aligned over a
portion of a secondary alignment structure 470.
[0100] FIG. 6K illustrates extending the opening 486 through the
hardmask layer 482 and the dielectric layer 480 to expose portions
of the top surfaces 416A of the ARC layer 416, a portion of the top
surface 470A of a secondary alignment structure 470, and a portion
of an alignment spacer 468. FIG. 6L illustrates extending the
opening 486 through the ARC layer 416 to expose portions of the top
surface 414A of the hardmask layer 414. FIG. 6M illustrates
removing the dielectric layer 480 and the dielectric layer 418.
[0101] FIG. 6N illustrates extending the openings 478A, 478B, and
486 through the hardmask layer 414 to expose portions of the top
surface 412A of the ARC layer 412. FIG. 6O illustrates extending
the openings 478A, 478B, and 486 through the ARC layer 412 to
expose portions of the top surface 410A of the ILD 410.
[0102] FIG. 6P illustrates extending the openings 478A, 478B, and
486 through the ILD 410 to expose portions of the top surface 402A
of the substrate 402. FIG. 6Q illustrates forming a conductive
layer 488 in the openings 478A, 478B, and 486 and over the
secondary alignment structures 470 and the hardmask layer 414. The
conductive layer 488 may be formed of similar materials and by
similar processes as the conductive layer 122 described above and
the description is not repeated herein.
[0103] FIG. 6R illustrates the recessing of the conductive layer
488 to have a top surface 488A lower than top surfaces 470A of the
secondary alignment structures 470. FIG. 6S illustrates removing
the secondary alignment structures 470 to form openings 490. The
secondary alignment structures 470 may be removed by a wet etch
process that is selective to the secondary alignment structures
470. FIG. 6S also illustrates extending the openings 490 through
the ARC layers 416 and 412 and the hardmask layer 414.
[0104] FIG. 6T illustrates forming the openings 490 partially
through the ILD 410 and through the hardmasks 406 to expose top
surfaces 404A of the gates 404. FIG. 6U illustrates removing the
conductive layer 488 from the openings 478A, 478B, and 486 to
expose the portions of the top surface 402A of the substrate 402 in
the openings 478A, 478B, and 486. The conductive layer 488 may be
removed by a wet etch process that is selective to the conductive
layer 488.
[0105] FIG. 6V illustrates forming a conductive layer 492 in the
openings 478A, 478B, 486, and 490. FIG. 6W illustrates recessing
the conductive layer 492 to form conductive features 492 in the
openings 490 contacting the top surfaces 404A of the gates 404 and
conductive features 494 in the openings 478A, 478B, and 486
contacting the top surface 402A of the substrate 402. In an
embodiment, the recessing is performed by a dry etch process with a
plasma source and an etchant gas such as H.sub.2, NH.sub.3, Ar, He,
the like, or a combination thereof.
[0106] FIG. 6X illustrates removing the alignment spacers 468, the
hardmask layer 414, the ARC layer 412, and the planarization of the
ILD 410 and the conductive features 492 and 494. The planarization
process may be a CMP process, an etch process, the like, or a
combination thereof. In some embodiments, the top surfaces 492A of
the conductive features 492, the top surfaces 494A of conductive
features 494, and the top surface 410A of the ILD 410 are
substantially coplanar after the planarization process. The
conductive features 492 may be used as contacts to couple the gates
404 to layers above the ILD 410 and the conductive features 494 may
be used as contacts to couple the substrate 402 and devices and
metallization layers formed therein to layers above ILD 410.
[0107] The embodiments described above provide self-alignment of
conductive contacts and conductive lines between two or more
layers. The embodiments include alignment structures and alignment
spacers on opposite sides of the alignment structures in layers
above the gates. The alignment structures and alignment spacers
allow for self-alignment between the alignment spacers of a single
alignment structure and for self-alignment between alignment
spacers of different alignment structures. Further, by having only
spacers surrounding the gates in the ILD layer, the ILD layer is
able to be kept clean and free from residue from other spacers
and/or hard masks as the alignment structures are formed in ILD
layer above the ILD layer containing the gates. Also, the process
described above allows the conductive features landing on the gates
and on the substrate to be self-aligning.
[0108] An embodiment is a method for forming a semiconductor
device, the method including forming at least two gates over a
substrate, and forming at least two alignment structures over the
at least two gates. The method further includes forming spacers on
opposite sidewalls of the at least two alignment structures, and
forming a first opening between a pair of the at least two
alignment structures, a portion of the first opening exposing a top
surface of at least one of the pair, the first opening extending a
first distance from a top surface of the substrate. The method
further includes filling the first opening with a first conductive
material to form a first conductive feature, forming a second
opening between the spacers of at least one of the at least two
alignment structures, the second opening extending a second
distance from the top surface of the substrate, the second distance
being different than the first distance, and filling the second
opening with a second conductive material to form a second
conductive feature.
[0109] Another embodiment is a method of forming a semiconductor
device, the method including forming a plurality of gates over a
semiconductor substrate, forming a first inter-layer dielectric
(ILD) over the plurality of gates, and forming at least two
alignment structures over the first ILD. The method further
includes forming a second ILD over the at least two alignment
structures, forming a first set of conductive contacts through the
first and second ILDs to a top surface of the semiconductor
substrate, one of the at least two alignment structures being
between an adjacent pair of the first set of conductive contacts,
and forming a second set of conductive contacts through the second
ILD and partially through the first ILD to the plurality of gates,
at least one of the second set of contacts extending through one of
the alignment structures.
[0110] Yet another embodiment is a method of forming a
semiconductor device, the method including forming a plurality of
gates on a substrate, forming an inter-layer dielectric (ILD) over
the plurality of gates, and forming a first dielectric layer over
the ILD. The method further includes forming a first and a second
opening in the first dielectric layer, a portion of the first
dielectric layer between the first and the second opening forming a
primary alignment structure, and forming secondary alignment
structures inside the first and second openings. The method further
includes forming a first contact through the primary alignment
structure and the ILD to a top surface of the substrate, and
forming a second contact through one of the secondary alignment
structures to a top surface of one of the plurality of gates.
[0111] Although the present embodiments and their advantages have
been described in detail, it should be understood that various
changes, substitutions, and alterations can be made herein without
departing from the spirit and scope of the disclosure as defined by
the appended claims. Moreover, the scope of the present application
is not intended to be limited to the particular embodiments of the
process, machine, manufacture, composition of matter, means,
methods, and steps described in the specification. As one of
ordinary skill in the art will readily appreciate from the
disclosure, processes, machines, manufacture, compositions of
matter, means, methods, or steps, presently existing or later to be
developed, that perform substantially the same function or achieve
substantially the same result as the corresponding embodiments
described herein may be utilized according to the present
disclosure. Accordingly, the appended claims are intended to
include within their scope such processes, machines, manufacture,
compositions of matter, means, methods, or steps.
* * * * *