U.S. patent application number 12/019135 was filed with the patent office on 2008-05-22 for gate dielectric having a flat nitrogen profile and method of manufacture therefor.
This patent application is currently assigned to Texas Instruments Incorporated. Invention is credited to Husam N. Alshareef, Rajesh Khamankar, Hiroaki Niimi, Toan Tran.
Application Number | 20080116542 12/019135 |
Document ID | / |
Family ID | 35504732 |
Filed Date | 2008-05-22 |
United States Patent
Application |
20080116542 |
Kind Code |
A1 |
Niimi; Hiroaki ; et
al. |
May 22, 2008 |
Gate Dielectric Having a Flat Nitrogen Profile and Method of
Manufacture Therefor
Abstract
The present invention provides a gate dielectric having a flat
nitrogen profile, a method of manufacture therefor, and a method of
manufacturing an integrated circuit including the flat nitrogen
profile. In one embodiment, the method of manufacturing the gate
dielectric includes forming a gate dielectric layer (410) on a
substrate (310), and subjecting the gate dielectric layer (410) to
a nitrogen containing plasma process (510), wherein the nitrogen
containing plasma process (510) has a ratio of helium to nitrogen
of 3:1 or greater.
Inventors: |
Niimi; Hiroaki; (Dallas,
TX) ; Alshareef; Husam N.; (Plano, TX) ;
Khamankar; Rajesh; (Coppell, TX) ; Tran; Toan;
(Rowlett, TX) |
Correspondence
Address: |
TEXAS INSTRUMENTS INCORPORATED
P O BOX 655474, M/S 3999
DALLAS
TX
75265
US
|
Assignee: |
Texas Instruments
Incorporated
Dallas
TX
|
Family ID: |
35504732 |
Appl. No.: |
12/019135 |
Filed: |
January 24, 2008 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10875482 |
Jun 24, 2004 |
7345001 |
|
|
12019135 |
Jan 24, 2008 |
|
|
|
60482194 |
Jun 24, 2003 |
|
|
|
Current U.S.
Class: |
257/632 ;
257/E23.002 |
Current CPC
Class: |
H01L 21/02329 20130101;
H01L 21/0234 20130101; H01L 29/6656 20130101; H01L 21/28202
20130101; H01L 29/518 20130101; H01L 21/3144 20130101; H01L 29/512
20130101; H01L 21/3115 20130101; H01L 21/0214 20130101 |
Class at
Publication: |
257/632 ;
257/E23.002 |
International
Class: |
H01L 23/58 20060101
H01L023/58 |
Claims
1-9. (canceled)
10. A semiconductor device, comprising: a gate dielectric layer
located on a substrate, the gate dielectric layer having nitrogen
included therein, wherein a concentration of the nitrogen in the
gate dielectric layer varies by less than about 10%; and a gate
electrode located over the gate dielectric layer.
11. The semiconductor device as recited in claim 10 wherein the
gate dielectric layer has a thickness of 2.5 nm or less.
12. The semiconductor device as recited in claim 10 wherein the
gate dielectric layer has a thickness ranging from about 2.5 nm to
about 1.5 nm.
13-20. (canceled)
Description
CROSS-REFERENCE TO RELATED APPLICATION
[0001] This application claims the benefit of U.S. Provisional
Application Ser. No. 60/482,194 filed on Jun. 24, 2003, entitled
"METHOD FOR FORMULATION OF ULTRATHIN HOMOGENOUS SILICON OXYNITRIDE
GATE DIELECTRIC USING He/N2 PLASMA", commonly assigned with the
present invention and incorporated herein by reference.
TECHNICAL FIELD OF THE INVENTION
[0002] The present invention is directed, in general, to a gate
dielectric and, more specifically, to a gate dielectric having a
flat nitrogen profile and a method of manufacture therefor.
BACKGROUND OF THE INVENTION
[0003] The trend in semiconductor technology to double the
functional complexity of its products every 18 months (Moore's
"law"), which is still valid today after having dominated the
industry for the last three decades, has several implicit
consequences. First, the cost per functional unit should drop with
each generation of complexity so that the cost of the product with
its doubled functionality would increase only slightly. Second, the
higher product complexity should largely be achieved by shrinking
the feature sizes of the chip components while holding the package
dimensions constant; preferably, even the packages should shrink.
Third, the increased functional complexity should be paralleled by
an equivalent increase in reliability of the product. And fourth,
but not least, the best financial profit rewards were held out for
the ones who were ahead in the marketplace in reaching the
complexity goal together with offering the most flexible products
for application.
[0004] The scaling of the components in the lateral dimension
requires vertical scaling as well so as to achieve adequate device
performance. This vertical scaling requires the thickness of the
gate dielectric, commonly silicon dioxide (SiO.sub.2) to be
reduced. Thinning of the gate dielectric provides a smaller barrier
to dopant diffusion from a polysilicon gate structure (or metal
diffusion from a metal gate structure) through the underlying
dielectric, often resulting in devices with diminished electrical
performance and reliability. In ultra-thin dielectric layers,
interfaces with their unwelcome electronic states and carrier traps
may finally dominate the electrical characteristics.
[0005] One way of reducing these problems is to use silicon nitride
as the gate dielectric layer instead of silicon dioxide. Silicon
nitride has a higher dielectric constant than typical thermally
grown SiO.sub.2 and provides greater resistance to impurity
diffusion. However, the electrical properties of standard deposited
silicon nitride films are far inferior to thermal oxides. One
approach for silicon nitride films as gate insulators employs an
oxide layer between the nitride layer and the substrate.
Unfortunately, this technique has numerous practical
shortcomings.
[0006] Another approach of maintaining the benefit of the
electrical properties of the oxide film while also getting the
barrier properties of a nitride film is to incorporate nitrogen
into a gate oxide layer. In known technology, this is accomplished
by a nitrided oxide process involving ammonia to penetrate the gate
oxide at temperatures in excess of 1000.degree. C. Once the high
temperature reaction has begun, it is difficult to control the
concentration of the nitrogen incorporated into the gate oxide.
Excessive nitrogen near the interface between the semiconductor
substrate and the gate oxide can adversely affect the threshold
voltage and degrade the channel mobility of the device due to
charged interface traps associated with the nitrogen.
[0007] As described by S. V. Hattangady et al., "Controlled
Nitrogen Incorporation at the Gate Oxide Surface," Appl. Phys.
Lett. vol. 66. p. 3495, 1995, a high pressure and low power process
provides nitrogen incorporation specifically at the gate/conductor
interface. The long exposure time to the plasma increases the
probability of charge-induced damage to the oxide and reduces the
production throughput.
[0008] In U.S. Pat. No. 6,136,654, issued on Oct. 24, 2000 (Kraft
et al., "Method of Forming Thin Silicon Nitride or Silicon
Oxynitride Gate Dielectrics"), the SiO.sub.2 (or oxynitride) layer
is subjected to a nitrogen containing plasma so that the nitrogen
is either incorporated into the SiO.sub.2 layer or forms a nitride
layer at the surface of the substrate. The source of nitrogen in
the plasma comprises a material consisting of N.sub.2, NH.sub.3,
NO, N.sub.2O, or mixtures thereof. This method provides a
non-uniform nitrogen distribution in the SiO.sub.2 layer and is
applicable to relatively thick oxide layers (2 to 15 nm), however,
it is not suitable for ultra-thin SiO.sub.2 layers (0.5 to 2
nm).
[0009] An urgent need has, therefore, arisen for a coherent,
low-cost method of plasma nitridation of ultra-thin gate oxide
layers. The method should further produce excellent electrical
device performance, mechanical stability and high reliability. The
fabrication method should be simple, yet flexible enough for
different semiconductor product families and a wide spectrum of
design and process variations. Preferably, these innovations should
be accomplished without extending production cycle time, and using
the installed equipment, so that no investment in new manufacturing
machines is needed.
SUMMARY OF THE INVENTION
[0010] To address the above-discussed deficiencies of the prior
art, the present invention provides a gate dielectric having a flat
nitrogen profile, a method of manufacture therefor, and a method of
manufacturing an integrated circuit including the flat nitrogen
profile. In one embodiment, the method of manufacturing the gate
dielectric includes forming a gate dielectric layer on a substrate,
and subjecting the gate dielectric layer to a nitrogen containing
plasma process, wherein the nitrogen containing plasma process has
a ratio of helium to nitrogen of 3:1 or greater.
[0011] Additionally, the present invention provides a semiconductor
device. The semiconductor device includes: (1) a gate dielectric
layer located on a substrate, the gate dielectric layer having
nitrogen included therein, wherein a concentration of the nitrogen
in the gate dielectric layer varies by less than about 10%
throughout the depth, and (2) a gate electrode located over the
gate dielectric layer.
[0012] Further included within the present invention is a method of
manufacturing an integrated circuit including the gate dielectric.
In addition to that disclosed above, the method for forming the
integrated circuit includes forming an interlevel dielectric layer
having interconnects located therein over the gate structure,
wherein the interconnects contact the semiconductor device to form
an operational integrated circuit.
[0013] The foregoing has outlined preferred and alternative
features of the present invention so that those skilled in the art
may better understand the detailed description of the invention
that follows. Additional features of the invention will be
described hereinafter that form the subject of the claims of the
invention. Those skilled in the art should appreciate that they can
readily use the disclosed conception and specific embodiment as a
basis for designing or modifying other structures for carrying out
the same purposes of the present invention. Those skilled in the
art should also realize that such equivalent constructions do not
depart from the spirit and scope of the invention.
BRIEF DESCRIPTION OF THE DRAWINGS
[0014] The invention is best understood from the following detailed
description when read with the accompanying FIGUREs. It is
emphasized that in accordance with the standard practice in the
semiconductor industry, various features are not drawn to scale. In
fact, the dimensions of the various features may be arbitrarily
increased or reduced for clarity of discussion. Reference is now
made to the following descriptions taken in conjunction with the
accompanying drawings, in which:
[0015] FIG. 1 illustrates a cross-sectional view of one embodiment
of a semiconductor device constructed according to the principles
of the present invention;
[0016] FIG. 2 illustrates two graphs, each representing the
nitrogen concentration per unit depth for a device manufactured
using the prior art method and a device manufactured in accordance
with the principles of the present invention, respectively;
[0017] FIG. 3 illustrates a cross-sectional view of a partially
completed semiconductor device;
[0018] FIG. 4 illustrates a cross-sectional view of the partially
completed semiconductor device illustrated in FIG. 3 after
formation of a gate dielectric layer on the substrate;
[0019] FIG. 5 illustrates a cross-sectional view of the partially
completed semiconductor device illustrated in FIG. 4 after
subjecting the gate dielectric layer to a nitrogen containing
plasma process;
[0020] FIG. 6 illustrates a cross-sectional view of the partially
completed semiconductor device illustrated in FIG. 5 after forming
a gate electrode layer over the gate dielectric layer, and
patterning the gate dielectric layer and gate electrode layer to
form a gate structure;
[0021] FIG. 7 illustrates a cross-sectional view of the partially
completed semiconductor device illustrated in FIG. 6 after
formation of lightly doped source/drain implants within the
substrate;
[0022] FIG. 8 illustrates a cross-sectional view of the partially
completed semiconductor device illustrated in FIG. 7 after
formation of conventional gate sidewall spacers and after placing
halo implants within the substrate;
[0023] FIG. 9 illustrates a cross-sectional view of the partially
completed semiconductor device illustrated in FIG. 8 after
formation of highly doped source/drain implants within the
substrate; and
[0024] FIG. 10 illustrates a cross-sectional view of a conventional
integrated circuit (IC) incorporating semiconductor devices
constructed according to the principles of the present
invention.
DETAILED DESCRIPTION
[0025] Referring initially to FIG. 1, illustrated is a
cross-sectional view of one embodiment of a semiconductor device
100 constructed according to the principles of the present
invention. In the embodiment illustrated in FIG. 1, the
semiconductor device 100 includes a substrate 110. Located within
the substrate 110 in the embodiment of FIG. 1 is a well region 120.
In the illustrative embodiment of FIG. 1, a gate structure 130,
including a gate 134 electrode, a gate dielectric layer 136, and
gate sidewall spacers 138, is located over the substrate 110.
[0026] The gate dielectric layer 136, when manufactured in
accordance with the principles of the present invention, includes
nitrogen therein. For instance, in one embodiment of the invention
the gate dielectric layer 136 is a silicon oxynitride gate
dielectric layer. In contrast to silicon oxynitride gate dielectric
layers of the prior art, the gate dielectric layer 136 has a
concentration of nitrogen that varies by less than about 10% across
the thickness (e.g., depth) thereof.
[0027] Turning briefly to FIG. 2, illustrated are two graphs 210,
220, each representing the nitrogen concentration per unit depth
for a device manufactured using the prior art method and a device
manufactured in accordance with the principles of the present
invention, respectively. Notice the large swing in nitrogen
concentration that exists across the thickness of the gate
dielectric layer in the first graph 210, which represents a gate
dielectric layer manufactured using the prior art method. In
comparison, notice the small swing in nitrogen concentration that
exists across the thickness of the gate dielectric layer in the
second graph 220, which represents a device manufactured in
accordance with the principles of the present invention. Thus, the
manufacturing method of the present invention provides a
substantially consistent nitrogen concentration along the entire
thickness of the gate dielectric layer. The aforementioned
consistent nitrogen concentration is particularly beneficial in
gate dielectric layer thicknesses of about 2.5 nm or less, and more
particularly thicknesses ranging from about 2.5 nm to about 1.5 nm,
such as illustrated in FIG. 1.
[0028] Turning back to FIG. 1, the semiconductor device 100 further
includes halo implants 140 and conventional source/drain regions
150 located within the substrate 110. The source/drain regions 150,
as is common, generally include a lightly doped source/drain
implant 154 as well as a higher doped source/drain implant 158.
[0029] Turning now to FIGS. 3-8, illustrated are cross-sectional
views of detailed manufacturing steps instructing how one might, in
an advantageous embodiment, manufacture a semiconductor device
similar to the semiconductor device 100 depicted in FIG. 1. FIG. 3
illustrates a cross-sectional view of a partially completed
semiconductor device 300. The partially completed semiconductor
device 300 includes a substrate 310. The substrate 310 may, in an
exemplary embodiment, be any layer located in the partially
completed semiconductor device 300, including a wafer itself or a
layer located above the wafer (e.g., epitaxial layer). In the
embodiment illustrated in FIG. 3, the substrate 310 is a P-type
semiconductor substrate; however, one skilled in the art
understands that the substrate 310 could be an N-type substrate
without departing from the scope of the present invention. In such
a case, each of the dopant types described throughout the remainder
of this document would be reversed. For clarity, no further
reference to this opposite scheme will be discussed.
[0030] Located within the substrate 310 in the embodiment shown in
FIG. 3 are shallow trench isolation regions 320. The shallow trench
isolation regions 320 isolate the semiconductor device 300 from
other devices located proximate thereto. As those skilled in the
art understand the various steps used to form these conventional
shallow trench isolation regions 320, no further detail will be
given.
[0031] In the illustrative embodiment of FIG. 3, also formed within
the substrate 310 is a well region 330. The well region 330, in
light of the P-type semiconductor substrate, would more than likely
contain an N-type dopant. For example, the well region 330 would
likely be doped with an N-type dopant dose ranging from about 1E13
atoms/cm.sup.2 to about 1E14 atoms/cm.sup.2 and at a power ranging
from about 100 keV to about 500 keV. What generally results is the
well region 330 having a peak dopant concentration ranging from
about 5E17 atoms/cm.sup.3 to about 1E19 atoms/cm.sup.3. As those
skilled in the art are well aware of the steps generally used to
form the well regions 330, no further details will be given.
[0032] Turning now to FIG. 4, illustrated is a cross-sectional view
of the partially completed semiconductor device 300 illustrated in
FIG. 3 after formation of a gate dielectric layer 410 on the
substrate 310. In an exemplary embodiment of the invention the gate
dielectric layer 410 has a thickness of less than about 2.5 nm, and
more particularly a thickness ranging from about 2.5 nm to about
1.5 nm. While the thickness of the gate dielectric layer 410 in the
embodiment of FIG. 3 is relatively small, those skilled in the art
understand that the gate dielectric layer 410 thickness may be much
larger than the 2.5 nm discussed, while staying within the scope of
the present invention.
[0033] The gate dielectric layer 410, which happens to be a silicon
dioxide gate dielectric layer in the disclosed embodiment, in the
exemplary embodiment of FIG. 3 is thermally grown. The thermal
growth allows for a high quality appropriate thickness gate
dielectric layer 410 to be formed. While thermal growth is
disclosed, those skilled in the art understand that a deposition
process might also be used.
[0034] Turning now to FIG. 5, illustrated is a cross-sectional view
of the partially completed semiconductor device 300 illustrated in
FIG. 4 after subjecting the gate dielectric layer 410 to a nitrogen
containing plasma process 510. Unique to the present invention, the
nitrogen containing plasma process 510 has a ratio of helium to
nitrogen of about 3:1 or greater. In an exemplary embodiment, the
ratio is up to about 9:1 or greater and in an even more exemplary
embodiment the ratio is about 19:1 or greater. As disclosed above,
the high amounts of helium cause the nitrogen concentration in the
gate dielectric layer 410 per unit depth to be substantially
identical throughout the thickness. In the embodiment shown, the
nitrogen concentration varies by less than about 10%.
[0035] The nitrogen, as those skilled in the art appreciate, may be
supplied by a number of different sources. For instance, in one
exemplary embodiment of the invention the nitrogen is supplied
using nitrogen gas (N.sub.2). In other embodiment of the invention,
however, the nitrogen may be supplied using a source selected from
the group consisting of NH.sub.3, NO, N.sub.2O, or mixtures
thereof. Other nitrogen sources may nonetheless also be used.
[0036] While it is believed that the most important parameter of
the nitrogen containing plasma process 510 is the ratio of helium
to nitrogen, other process parameters are also important. For
example, a low pressure is desired. In one embodiment this low
pressure is less than about 20 mTorr, and in another embodiment the
pressure ranges from about 20 mTorr to about 10 mTorr. Similarly,
the RF power and temperature may be tailored. For instance the RF
power may range from about 1000 watts to about 300 watts and the
temperature may range from about room temperature to about
500.degree. C. While specific ranges have been given for pressure,
power and temperature, other pressures, powers and temperatures
outside of the disclosed ranges may obviously be used.
[0037] After completing the nitrogen containing plasma process 510,
the gate dielectric layer 410 may be subjected to an anneal. This
anneal, which may include temperatures ranging from about
900.degree. C. to about 1200.degree. C. for a time period ranging
from about 5 seconds to about 60 seconds, is designed to stabilize
the nitrided oxide and minimize nitrogen out-diffusion. Other
temperatures and times could nonetheless be used for the
anneal.
[0038] Turning now to FIG. 6, illustrated is a cross-sectional view
of the partially completed semiconductor device 300 illustrated in
FIG. 5 after forming a gate electrode layer 610 over the gate
dielectric layer 410, and patterning the gate dielectric layer 410
and gate electrode layer 610 to form a gate structure 620. As the
gate structure 620, but for the unique nitrogen containing plasma
process, is conventional, those skilled in the art understand the
standard steps used for its manufacture, including using
photolithography to define the gate structure 620.
[0039] Turning now to FIG. 7, illustrated is a cross-sectional view
of the partially completed semiconductor device 300 illustrated in
FIG. 6 after formation of lightly doped source/drain implants 710
within the substrate 310. The lightly doped source/drain implants
710 are conventionally formed and generally have a peak dopant
concentration ranging from about 1E19 atoms/cm.sup.3 to about 2E20
atoms/cm.sup.3. As is standard in the industry, the lightly doped
source/drain implants 710 have a dopant type opposite to that of
the well region 330 they are located within. Accordingly, in the
illustrative embodiment shown in FIG. 7, the lightly doped
source/drain implants 710 are doped with a P-type dopant.
[0040] Turning now to FIG. 8, illustrated is a cross-sectional view
of the partially completed semiconductor device 300 illustrated in
FIG. 7 after formation of conventional gate sidewall spacers 810
and after placing halo implants 820 within the substrate 310. The
formation of the gate sidewall spacers 810 is conventional. Often
the gate sidewall spacers 810 comprise an oxide material that has
been anisotropically etched.
[0041] The halo implants 820, in the particular embodiment
discussed herein, comprise an N-type dopant. For example, in the
illustrative embodiment shown in FIG. 8, the halo implants 820
include a phosphorous or arsenic dopant and have a peak dopant
concentration ranging from about 1E18 atoms/cm.sup.3 to about 1E19
atoms/cm.sup.3. While the particular dopant used and dopant
concentration of the halo implants 820 have been given, those
skilled in the art understand that the present invention should not
be limited to such dopants and concentrations. The use and location
of the halo implants 820 is particularly designed to reduce short
channel effects in the semiconductor device 300.
[0042] Turning now to FIG. 9, illustrated is a cross-sectional view
of the partially completed semiconductor device 300 illustrated in
FIG. 8 after formation of highly doped source/drain implants 910
within the substrate 310. The highly doped source/drain implants
910 are conventionally formed and generally have a peak dopant
concentration ranging from about 1E18 atoms/cm.sup.3 to about 1E21
atoms/cm.sup.3. Also, the highly doped source/drain implants 910
should typically have a dopant type opposite to that of the well
region 330 they are located within. Accordingly, in the
illustrative embodiment shown in FIG. 9, the highly doped
source/drain implants 910 are doped with a P-type dopant. What
results after formation of the highly doped source/drain implants
910 is a device similar to the semiconductor device 100 illustrated
in FIG. 1.
[0043] Referring finally to FIG. 10, illustrated is a
cross-sectional view of a conventional integrated circuit (IC) 1000
incorporating semiconductor devices 1010 constructed according to
the principles of the present invention. The IC 1000 may include
devices, such as transistors used to form CMOS devices, BiCMOS
devices, Bipolar devices, or other types of devices. The IC 1000
may further include passive devices, such as inductors or
resistors, or it may also include optical devices or optoelectronic
devices. Those skilled in the art are familiar with these various
types of devices and their manufacture. In the particular
embodiment illustrated in FIG. 10, the IC 1000 includes the
semiconductor devices 1010 having dielectric layers 1020 located
thereover. Additionally, interconnect structures 1030 are located
within the dielectric layers 1020 to interconnect various devices,
thus, forming the operational integrated circuit 1000.
[0044] Although the present invention has been described in detail,
those skilled in the art should understand that they can make
various changes, substitutions and alterations herein without
departing from the spirit and scope of the invention in its
broadest form.
* * * * *