U.S. patent application number 11/509498 was filed with the patent office on 2007-12-06 for self-assembled mono-layer liner for cu/porous low-k interconnections.
Invention is credited to Tien-I Bao, Chia-Cheng Chou, Chung-Chi Ko, Keng-Chu Lin, Chen-Hua Yu.
Application Number | 20070278682 11/509498 |
Document ID | / |
Family ID | 38789175 |
Filed Date | 2007-12-06 |
United States Patent
Application |
20070278682 |
Kind Code |
A1 |
Ko; Chung-Chi ; et
al. |
December 6, 2007 |
Self-assembled mono-layer liner for cu/porous low-k
interconnections
Abstract
An interconnect structure of an integrated circuit includes a
low-k dielectric layer over a semiconductor substrate, a conductor
in the low-k dielectric layer, and a dielectric transition layer
between the low-k dielectric layer and the conductor, wherein the
dielectric transition layer has a thickness of less than about 50
.ANG..
Inventors: |
Ko; Chung-Chi; (Nautou,
TW) ; Chou; Chia-Cheng; (Keelung City, TW) ;
Lin; Keng-Chu; (Ping-Tung, TW) ; Bao; Tien-I;
(Hsin-Chu, TW) ; Yu; Chen-Hua; (Hsin-Chu,
TW) |
Correspondence
Address: |
SLATER & MATSIL, L.L.P.
17950 PRESTON ROAD, SUITE 1000
DALLAS
TX
75252
US
|
Family ID: |
38789175 |
Appl. No.: |
11/509498 |
Filed: |
August 24, 2006 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
60809754 |
May 31, 2006 |
|
|
|
Current U.S.
Class: |
257/758 ;
257/E23.167 |
Current CPC
Class: |
H01L 23/5329 20130101;
H01L 2924/12044 20130101; H01L 21/76826 20130101; H01L 2924/0002
20130101; H01L 21/76825 20130101; H01L 21/76831 20130101; H01L
23/53238 20130101; H01L 23/53295 20130101; H01L 2924/00 20130101;
H01L 2924/0002 20130101 |
Class at
Publication: |
257/758 |
International
Class: |
H01L 23/52 20060101
H01L023/52; H01L 23/48 20060101 H01L023/48; H01L 29/40 20060101
H01L029/40 |
Claims
1. An integrated circuit comprising: a low-k dielectric layer over
a semiconductor substrate; a conductor in the low-k dielectric
layer; and a dielectric transition layer between the low-k
dielectric layer and the conductor, wherein the dielectric
transition layer has a thickness of less than about 50 .ANG..
2. The integrated circuit of claim 1 further comprising a diffusion
barrier layer on the dielectric transition layer, wherein an atomic
percentage of atoms of the diffusion barrier layer in the
dielectric transition layer is less than about 0.1%.
3. The integrated circuit of claim 2, wherein the diffusion barrier
layer comprises a material selected from the group consisting
essentially of titanium, titanium nitride, tantalum, tantalum
nitride, and combinations thereof.
4. The integrated circuit of claim 2, wherein a bottom portion of
the diffusion barrier layer is located on a metallic feature, and
wherein the metallic feature is in an additional dielectric layer
underlying the low-k dielectric layer, and wherein substantially no
dielectric transition layer exists on the metallic feature.
5. The integrated circuit of claim 1, wherein the dielectric
transition layer has a thickness of between about 10 .ANG.and about
30 .ANG..
6. The integrated circuit of claim 1, wherein the dielectric
transition layer comprises terminals selected from the group
consisting essentially of methyl, ethyl, propyl, and combinations
thereof.
7. The integrated circuit of claim 1, wherein the dielectric
transition layer has a higher carbon concentration than the low-k
dielectric layer has.
8. The integrated circuit of claim 1, wherein the low-k dielectric
layer has a dielectric constant of less than about 2.5.
9. An integrated circuit comprising: a porous dielectric layer over
a semiconductor substrate; a conductor in the porous dielectric
layer; and a mono-layer between and adjoining the porous dielectric
layer and the conductor, wherein the mono-layer comprises terminals
selected from the group consisting essentially of methyl, ethyl,
propyl, and combinations thereof.
10. The integrated circuit of claim 9, wherein the terminals
comprise methyl.
11. The integrated circuit of claim 9, wherein the mono-layer has a
carbon concentration higher than a carbon concentration in the
low-k dielectric layer.
12. The integrated circuit of claim 11, wherein the carbon
concentration in the mono-layer is higher than a carbon
concentration in the low-k dielectric layer by about three to about
15 percent.
13. The integrated circuit of claim 9, wherein the mono-layer
exists only at surfaces of the low-k dielectric layer.
14. The integrated circuit of claim 9, wherein the mono-layer
comprises Si--(CH.sub.3).sub.3 terminals.
15. An integrated circuit comprising: a porous dielectric layer
over a semiconductor substrate; an opening in the porous dielectric
layer; a dielectric transition layer on at least sidewalls of the
porous dielectric layer in the opening, wherein the dielectric
transition layer has a thickness of less than about 50 .ANG., and
wherein a first carbon concentration in the dielectric transition
layer is greater than a second carbon concentration in the porous
dielectric layer; and a diffusion barrier layer on the dielectric
transition layer.
16. The integrated circuit of claim 15, wherein the first carbon
concentration is greater than the second carbon concentration by
about three to about 15 percent.
Description
[0001] This application claims the benefit of U.S. Provisional
Patent Application Ser. No. 60/809,754, filed on May 31, 2006, and
entitled "Self-Assembled Mono-Layer Liner for Cu/Porous Low-k
Interconnections," which application is hereby incorporated herein
by reference.
TECHNICAL FIELD
[0002] This invention relates generally to integrated circuits, and
more particularly to the design and formation methods of
interconnect structures of the integrated circuits.
BACKGROUND
[0003] As the semiconductor industry introduces new generations of
integrated circuits (IC's) having higher performance and greater
functionality, the density of the elements that form the integrated
circuits is increased, and the dimensions, sizes and spacings
between the individual components or elements are reduced. While in
the past such reductions were limited only by the ability to define
the structures photo-lithographically, device geometries having
even smaller dimensions created new limiting factors. For example,
for any two adjacent conductive paths, as the distance between the
conductors decreases, the resulting capacitance (a function of the
dielectric constant (k) of the insulating material divided by the
distance between conductive paths) increases. This increased
capacitance results in increased capacitive coupling between the
conductors, increased power consumption, and an increase in the
resistive-capacitive (RC) time constant. Therefore, continual
improvement in semiconductor IC performance and functionality is
dependent upon developing materials that form a dielectric film
with a lower dielectric constant (k) than that of the most commonly
used material, silicon oxide, in order to reduce capacitance. As
the dimensions of these devices get smaller and smaller,
significant reduction in capacitance into the so-called "ultra
low-k" regime is required.
[0004] New materials with low dielectric constants (known in the
art as "low-k dielectrics") are being investigated for use as
insulators in semiconductor chip designs. A low dielectric constant
material helps to enable further reductions in the integrated
circuit feature dimensions. In conventional IC processing,
SiO.sub.2 was used as a basis for the dielectric material,
resulting in a dielectric constant of about 3.9. Advanced low-k
dielectric materials have dielectric constants below about 2.7. The
substance with the lowest dielectric constant is air (k=1.0).
Therefore, porous dielectrics are very promising candidates, since
they have the potential to provide very low dielectric
constants.
[0005] However, porous films have shortcomings. Poor time-dependent
dielectric breakdown (TDDB) performance has become a severe problem
as a result of the seriously deteriorated barrier integrity. FIG. 1
illustrates a conventional interconnection formation scheme. A
first copper line 4 is formed in a low-k dielectric layer 2. An
etch stop layer 5 is formed on low-k dielectric layer 2. A second
copper line 12 is electrically coupled to copper line 4 through a
via 14. The second copper line 12 and via 14 are formed in a porous
low-k dielectric layer 6. A diffusion barrier layer 10 is formed
over sidewalls of the trench opening and via opening, in which
copper is filled to form second copper line 12 and via 14. As low-k
dielectric layer 6 is porous, the material in diffusion barrier
layer 10 may penetrate into pores that are exposed on sidewalls of
the via opening and trench opening, thus causing clouding effects,
which will adversely affect the subsequent interconnection
formation processes. To solve this problem, a dielectric pore
sealing layer 8 is formed on exposed surfaces of low-k dielectric
layer 6 in the trench and via openings to seal the pores.
Dielectric pore sealing layer 8, however, typically has a higher k
value than low-k dielectric layer 6 has. The RC delay in the
interconnect structure is thus increased. In addition, the adhesion
of dielectric pore sealing layer 8 and diffusion barrier layer 10
is not satisfactory, and delamination may occur in the subsequent
chemical mechanical polish process. Furthermore, dielectric pore
sealing layer 8 is not conductive, and thus the portion on an
interface 16, which is exposed through the via opening, needs to be
removed by an additional liner removal step.
[0006] Accordingly, a method that maximizes the benefit of low-k
dielectrics while reducing the effects of their porous properties
is needed.
SUMMARY OF THE INVENTION
[0007] In accordance with one aspect of the present invention, an
interconnect structure of an integrated circuit includes a low-k
dielectric layer over a semiconductor substrate, a conductor in the
low-k dielectric layer, and a dielectric transition layer between
the low-k dielectric layer and the conductor, wherein the
dielectric transition layer has a thickness of less than about 50
.ANG..
[0008] In accordance with another aspect of the present invention,
an interconnect structure of an integrated circuit includes a
porous dielectric layer over a semiconductor substrate, a conductor
in the porous dielectric layer, and a mono-layer between and
adjoining the porous dielectric layer and the conductor, wherein
the mono-layer comprises terminals selected from the group
consisting essentially of methyl, ethyl, propyl, and combinations
thereof.
[0009] In accordance with yet another aspect of the present
invention, an interconnect structure of an integrated circuit
includes a porous dielectric layer over a semiconductor substrate,
an opening in the low-k dielectric layer, a dielectric transition
layer on at least sidewalls of the low-k dielectric layer in the
opening, wherein the dielectric transition layer has a thickness of
less than about 50 .ANG., and wherein a first carbon concentration
in the dielectric transition layer is greater than a second carbon
concentration in the low-k dielectric layer. The interconnect
structure further includes a diffusion barrier layer on the
dielectric transition layer.
[0010] In accordance with yet another aspect of the present
invention, a method for forming an interconnect structure of an
integrated circuit includes forming a low-k dielectric layer over a
semiconductor substrate, etching the low-k dielectric layer to form
an opening, selectively forming a mono-layer on exposed surfaces of
the low-k dielectric layer, wherein the mono-layer comprises
terminals selected from the group consisting essentially of methyl,
ethyl, propyl, and combinations thereof, and filling the opening
with a conductive material.
[0011] In accordance with yet another aspect of the present
invention, a method for forming an interconnect structure of an
integrated circuit includes forming a porous dielectric layer over
a semiconductor substrate, forming an opening in the porous
dielectric layer, and treating the porous dielectric layer with an
organic chemical to cause a reaction between the porous dielectric
layer and the organic chemical, wherein the organic chemical is
free from silicon.
[0012] In accordance with yet another aspect of the present
invention, a method for forming an interconnect structure of an
integrated circuit includes forming a low-k dielectric layer over a
semiconductor substrate, etching the low-k dielectric layer to form
an opening, treating the low-k dielectric layer with an organic
chemical free from silicon, wherein a molecular weight of the
organic chemical is greater than about 60 g/mole.
[0013] The advantageous features of the present invention include a
reduced effect of RC delay, improved adhesion between the pore
sealing layer and the diffusion barrier layer, and a saved liner
removal step.
BRIEF DESCRIPTION OF THE DRAWINGS
[0014] For a more complete understanding of the present invention,
and the advantages thereof, reference is now made to the following
descriptions taken in conjunction with the accompanying drawings,
in which:
[0015] FIG. 1 illustrates a conventional interconnect structure
including a low-k dielectric material;
[0016] FIGS. 2 through 7 are cross-sectional views of intermediate
stages in the manufacture of a preferred interconnect structure,
wherein a dual damascene process is illustrated;
[0017] FIG. 8 illustrates a cross-sectional view of a single
damascene structure in addition to the structure in FIG. 7; and
[0018] FIG. 9 illustrates a comparison of breakdown electrical
fields of a preferred interconnect structure embodiment and a
conventional interconnect structure embodiment.
DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS
[0019] The making and using of the presently preferred embodiments
are discussed in detail below. It should be appreciated, however,
that the present invention provides many applicable inventive
concepts that can be embodied in a wide variety of specific
contexts. The specific embodiments discussed are merely
illustrative of specific ways to make and use the invention, and do
not limit the scope of the invention.
[0020] A novel method for forming a low-k dielectric layer and a
corresponding interconnect structure is provided. The intermediate
stages for manufacturing the preferred embodiment of the present
invention are illustrated. Variations of the preferred embodiments
are then discussed. Throughout the various views and illustrative
embodiments of the present invention, like reference numbers are
used to designate like elements.
[0021] FIG. 2 illustrates a starting structure having a conductive
line 22 formed in a dielectric layer 20. Conductive line 22 and
dielectric layer 20 are over a semiconductor substrate (not shown),
which is preferably a silicon substrate having semiconductor
devices formed thereon. Conductive line 22 is preferably a metal
line comprising copper, tungsten, aluminum, silver, gold, alloys
thereof, compounds thereof, and combinations thereof. Conductive
line 22 is typically connected to another underlying feature (not
shown), such as a via or a contact plug. Dielectric layer 20 may be
an inter-layer dielectric (ILD) layer or an inter-metal dielectric
(IMD) layer, and preferably has a low k value.
[0022] An etch stop layer (ESL) 24 is formed on dielectric layer 20
and conductive line 22. Preferably, ESL 24 comprises nitrides,
silicon-carbon based materials, carbon-doped oxides, and
combinations thereof. The preferred formation method is plasma
enhanced chemical vapor deposition (PECVD). However, other commonly
used methods such as high-density plasma CVD (HDPCVD), atomic layer
CVD (ALCVD), and the like can also be used. In an exemplary
embodiment wherein ESL 24 comprises silicon nitride or silicon
carbide, the formation is preferably performed in a chamber, in
which gaseous precursors such as silane (SiH.sub.4) and ammonia
(NH.sub.3) are introduced and a chemical reaction occurs.
[0023] In alternative embodiments, dielectric layer 24 is a
diffusion barrier layer preventing undesirable elements, such as
copper, from diffusing into the subsequently formed low-k
dielectric layer. In a more preferred embodiment, dielectric layer
24 acts as both an etch stop layer and a diffusion barrier
layer.
[0024] FIG. 3 illustrates the formation of a low-k dielectric layer
28, which provides insulation between conductive line 22 and
overlying conductive lines that will be formed subsequently.
Accordingly, low-k dielectric layer 28 is sometimes referred to as
an inter-metal dielectric (IMD) layer.
[0025] Low-k dielectric layer 28 preferably has a dielectric
constant (k) value of lower than about 3.5, and more preferably
lower than about 2.5. The preferred materials include
carbon-containing materials, organo-silicate glass,
porogen-containing materials, and combinations thereof. Low-k
dielectric layer 28 may be deposited using a chemical vapor
deposition (CVD) method, preferably plasma enhanced CVD (PECVD),
although other commonly used deposition methods, such as low
pressure CVD (LPCVD), atomic layer chemical vapor deposition
(ALCVD), and spin-on, can also be used.
[0026] A first treatment, which preferably includes a curing
process, is then performed. The curing process can be performed
using commonly used curing methods, such as ultraviolet (UV)
curing, eBeam curing, thermal curing, and the like, and may be
performed in a production tool that is also used for PECVD, atomic
layer deposition (ALD), LPCVD, etc. In an exemplary UV curing
process, an ultraviolet radiator tool is utilized. The exemplary
process conditions include a temperature of between about
250.degree. C. and about 450.degree. C., a curing power of between
about 3000 W and about 6000 W, and a curing time of between about
300 seconds and about 1500 seconds. The curing may be performed in
a vacuum environment or in an environment containing process gases
such as H.sub.2, N.sub.2, inert gases (including He, Ne, Ar, Kr,
Xe, Rn), and combinations thereof. The wavelength of the UV curing
is preferably between about 200 nm and about 400 nm.
[0027] The treatment serves the function of driving porogen out of
low-k dielectric layer 28, thus improving its mechanical property.
Pores will then be generated in low-k dielectric layer 28. In the
preferred embodiment, after the treatment, the porosity of low-k
dielectric layer 28 is preferably greater than about 15%.
[0028] FIG. 4 illustrates the formation of a via opening 30 and a
trench opening 32 in low-k dielectric layer 28. Photo resists (not
shown) are formed and patterned over low-k dielectric layer 28 to
aid in the formation of via opening 30 and trench opening 32. In
the preferred embodiment, an anisotropic etch cuts through low-k
dielectric layer 28 and stops at ESL 24, thereby forming a via
opening 30. Trench opening 32 is then formed. Since there is no
etch stop layer for stopping the etching of trench opening 32,
etching time is controlled so that the etching of the trench
opening 32 stops at a desired depth. In alternative embodiments, a
trench-first approach is taken, in which trench opening 32 is
formed prior to the formation of via opening 30. ESL 24 is then
etched through via opening 30, exposing underlying conductive line
22.
[0029] In alternative embodiments, the previously discussed low-k
dielectric layer 28 may be replaced by a first low-k dielectric
layer, an ESL on the first low-k dielectric layer, and a second
low-k dielectric layer on the ESL. The ESL is used for etching
trench opening 32. One skilled in the art will realize the
appropriate process steps.
[0030] In the preferred embodiment, low-k dielectric layer 28
contains silicon, oxygen and carbon. Carbon may be present in the
form of methyl, ethyl, propyl, and the like. The low-k dielectric
material may be schematically represented as PLK-Si--O--CH.sub.3,
wherein PLK represents a portion of the porous low-k dielectric
material in low-k dielectric layer 28. The etching process,
however, typically causes the depletion of carbon from low-k
dielectric layer 28, particularly on the surface of openings 30 and
32. As a result, a surface portion of the respective low-k
dielectric layer 28 may be represented by PLK-Si--O.about., wherein
the symbol ".about." indicates dangling bonds. As such dangling
bonds are not stable, they can easily form bonds with hydrogen to
form OH terminals, and the resulting material on the surface of the
low-k dielectric layer 28 is schematically represented by
PLK-Si--OH. FIG. 4 schematically illustrates such OH terminals on
the exposed surfaces of low-k dielectric layer 28.
[0031] Referring to FIG. 5, a self-assembled mono-layer (SAM)
formation process is performed to treat the exposed surfaces of
low-k dielectric layer 28. In the preferred embodiment, the SAM
formation process is performed using plasma-assisted treating
processes. Alternatively, thermal treating processes are used. The
process gases preferably include an organic chemical containing
methyl, ethyl, and/or propyl groups. More preferably, the organic
chemical includes a methyl-containing gas. The organic chemical
also preferably contains nitrogen, and/or a ring-type structure
with benzene rings, and is preferably free from silicon. The
molecular weight of the organic chemical is preferably greater than
about 60 g/mole. In addition, carrier gases such as inert gases,
nitrogen, hydrogen, ammonia, and combinations thereof are used. The
organic chemical reacts with the surface portion of the porous
low-k dielectric material, which is represented as PLK-Si--OH. The
reaction causes the bonds between oxygen and hydrogen to break, and
the hydrogen ions are replaced by methyl, ethyl, and/or propyl
groups. The methyl, ethyl, and/or propyl groups are terminals, and
thus the resulting material on the surface of exposed low-k
dielectric layer 28 stops growing after the terminals are attached,
resulting in a substantial mono-layer, which is denoted as layer
34. It should be noted that on the surface of the exposed copper
line 22, there are substantially no OH terminals, and thus the
mono-layer 34 (SAM 34) is substantially not formed on copper line
22. Accordingly, such a process is self-assembled, hence the name
self-assembled mono-layer (SAM) process. Also the deposition
process will stop after the terminals are formed, thus SAM 34 is
very thin. In an exemplary embodiment, SAM 34 has a thickness of
less than about 50 .ANG., and is more likely between about 10 .ANG.
and 30 .ANG.. In an analysis of a sample that generated a
Time-of-Flight Secondary Ion Mass Spectrometry (ToF-SIMS) positive
ion spectra, the presence of methyl group terminals on the surface
of low-k dielectric layer 28 has been observed.
[0032] Due to the formation of carbon-containing terminal groups,
there is a high carbon concentration in a surface layer of low-k
dielectric layer 28. The concentration in the surface layer tends
to be greater than in inner portions of low-k dielectric layer 28.
In an exemplary embodiment, a surface layer with a thickness of 30
.ANG. has a first average carbon concentration higher than a second
average carbon concentration of an underlying portion with a
thickness of 30 .ANG.. In another exemplary embodiment, the first
average carbon concentration is greater than the second average
carbon concentration by about three to about 15 percent. This is
contrary to the prior art interconnect structure, wherein the
carbon concentration of the surface layer is typically lower than
in inner portions due to carbon depletion. As methyl, ethyl, and
propyl have greater volumes than hydrogen, the pores on the surface
of low-k dielectric layer 28 are at least partially sealed.
[0033] An exemplary reaction equation is symbolically illustrated
below. Please note that this equation is only an example, and
should not be used to limit the scope of the present invention:
R.sub.1--Si--RH+PLK-Si--O--H.fwdarw.PLK-Si--O--Si--R.sub.1+RH.sub.x
[Eq. 1]
wherein R.sub.1 may be (CH.sub.3).sub.3, and R may be a functional
group containing nitrogen, and/or a ring-type structure with
benzene rings, and R.sub.1 is methyl, ethyl, and/or propyl groups.
An example of the above-expression is:
(CH.sub.3).sub.3--Si--RH+PLK-Si--O--H.fwdarw.PLK-Si--O--Si--(CH.sub.3).s-
ub.3+RH.sub.x. [Eq. 2]
[0034] FIG. 5 illustrates a resulting structure after the SAM
process. As previously noted, the mono-layer is illustrated as
layer 34. It is to be noted, however, that SAM 34 is so thin that
it may not be visible, and the existence of SAM 34 may need to be
determined using equipment such as time-of-flight secondary ion
mass spectrometry (ToF-SIMS).
[0035] An optional UV curing is then performed on the structure
shown in FIG. 5. In the preferred embodiment, the UV curing may be
performed in a production tool with the presence of hydrogen,
nitrogen, inert gases, and combinations thereof. The preferred
wavelength of the UV light is preferably between about 200 nm and
about 400 nm. The exemplary process conditions include a
temperature of between about 250.degree. C. and about 450.degree.
C., a curing power of between about 3000 W and about 6000 W, and a
curing time of about 300 seconds to about 1500 s seconds.
[0036] FIG. 6 illustrates the formation of a barrier layer 38,
which prevents copper from diffusing into low-k dielectric layer 28
and is preferably formed of a material comprising titanium,
titanium nitride, tantalum, tantalum nitride, and the like. It may
be a single layer or have a composite structure. As the pores on
the surface of low-k dielectric layer 28 are at least partially
sealed, the clouding effects, which cause the atoms of the
diffusion barrier layer to penetrate into pores, is reduced. In an
exemplary embodiment, the atoms of the diffusion barrier layer
penetrating into the SAM 34 are so few that the atomic percentage
of diffusion materials in SAM 34 is less than about 0.1%.
[0037] Referring to FIG. 7, via opening 30 and trench opening 32
are filled with a conductive material, preferably copper or copper
alloys. However, other metals and metal alloys such as aluminum,
tungsten, silver and gold can also be used. A chemical mechanical
polish is then performed to level the surface, forming a via 42 and
a metal line 44.
[0038] The previously discussed embodiment illustrates the
formation of a dual damascene structure. SAMs can also be formed
for single damascene structures. FIG. 8 illustrates a SAM 50 formed
in a single damascene structure. One skilled in the art will
realize the respective process steps.
[0039] Due to the formation of SAM 34, the mechanical and
electrical properties of interconnect structures are improved. SAM
34 has better adhesion to the diffusion barrier layer than the
conventional pore-sealing layer had, and thus delamination is
reduced. As SAM 34 will not be formed on copper line 22, the liner
removal step used in conventional processes to remove the
dielectric pore-sealing layer on the copper line is saved.
[0040] Furthermore, by using the preferred embodiment of the
present invention, electrical properties of the interconnect
structures are improved. FIG. 9 illustrates a comparison of a
preferred interconnect structure formed with a SAM and a
conventional interconnect structure with a barrier layer formed
directly on a low-k dielectric layer. The data obtained from the
preferred embodiment are shown as hollow circles, while data
obtained from the conventional interconnect structure are shown as
solid squares. It is observed that the breakdown electrical field
of the preferred interconnect structure is about twice the
breakdown electrical field of the conventional interconnect
structure. In addition, since SAM is very thin, the RC delay caused
by SAM is substantially eliminated.
[0041] Although the present invention and its advantages have been
described in detail, it should be understood that various changes,
substitutions and alterations can be made herein without departing
from the spirit and scope of the invention as defined by the
appended claims. Moreover, the scope of the present application is
not intended to be limited to the particular embodiments of the
process, machine, manufacture, and composition of matter, means,
methods and steps described in the specification. As one of
ordinary skill in the art will readily appreciate from the
disclosure of the present invention, processes, machines,
manufacture, compositions of matter, means, methods, or steps,
presently existing or later to be developed, that perform
substantially the same function or achieve substantially the same
result as the corresponding embodiments described herein may be
utilized according to the present invention. Accordingly, the
appended claims are intended to include within their scope such
processes, machines, manufacture, compositions of matter, means,
methods, or steps.
* * * * *