U.S. patent application number 11/783131 was filed with the patent office on 2007-08-30 for method for fabricating semiconductor device.
This patent application is currently assigned to Matsushita Electric Industrial Co., Ltd.. Invention is credited to Masayuki Endo, Yoshihiko Hirai, Hideo Nakagawa, Masaru Sasago.
Application Number | 20070202666 11/783131 |
Document ID | / |
Family ID | 18824078 |
Filed Date | 2007-08-30 |
United States Patent
Application |
20070202666 |
Kind Code |
A1 |
Nakagawa; Hideo ; et
al. |
August 30, 2007 |
Method for fabricating semiconductor device
Abstract
After a fluid film is formed by supplying a material with
fluidity to the surface of a substrate formed with a stepped layer,
the fluid film is pressed against the substrate by a pressing
member having a planar pressing surface so that the surface of the
fluid film is planarized. The fluid film is heated in this state
and thereby solidified to form a solidified film having a planar
surface.
Inventors: |
Nakagawa; Hideo;
(Omihachiman-shi, JP) ; Sasago; Masaru; (Osaka,
JP) ; Endo; Masayuki; (Osaka, JP) ; Hirai;
Yoshihiko; (Osaka, JP) |
Correspondence
Address: |
MCDERMOTT WILL & EMERY LLP
600 13TH STREET, NW
WASHINGTON
DC
20005-3096
US
|
Assignee: |
Matsushita Electric Industrial Co.,
Ltd.
Osaka
JP
|
Family ID: |
18824078 |
Appl. No.: |
11/783131 |
Filed: |
April 6, 2007 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10399755 |
Apr 22, 2003 |
|
|
|
11783131 |
Apr 6, 2007 |
|
|
|
Current U.S.
Class: |
438/478 ;
257/E21.243; 257/E21.58 |
Current CPC
Class: |
H01L 21/76819 20130101;
H01L 21/31051 20130101 |
Class at
Publication: |
438/478 ;
257/E21.243; 257/E21.58 |
International
Class: |
H01L 21/36 20060101
H01L021/36 |
Foreign Application Data
Date |
Code |
Application Number |
Nov 17, 2000 |
JP |
2000-350934 |
Claims
1-25. (canceled)
26. A method for fabricating a semiconductor device, the method
comprising: a film forming step of supplying a material with
fluidity to a surface of a substrate to form a film with fluidity;
a planarizing step of pressing the film with fluidity against the
substrate by a planar pressing surface of a pressing member to
planarize a surface of the film with fluidity; and a solidifying
step of solidifying the film with fluidity having the surface
planarized.
27. The method of claim 26, wherein the pressing surface of the
pressing member has a hydrophibic property.
28. The method of claim 26, wherein the material with fluidity is
an insulating material.
29. The method of claim 26, wherein the material with fluidity is
in the state of a liquid or a gel.
30. The method of claim 26, wherein the film forming step is
performed while the substrate is rotated.
31. The method of claim 26, wherein the film forming step includes
the step of rotating the substrate supplied with the material with
fluidity.
32. The method of claim 26, wherein the film forming step is
performed by supplying the material with fluidity in a showering or
spraying manner while rotating the substrate.
33. The method of claim 26, wherein the material with fluidity is
an insulating material including siloixane.
Description
RELATED APPLICATIONS
[0001] The present application is a Continuation of U.S.
application Ser. No. 10/399,755, filed on Apr. 22, 2003, which
claims priority of Japanese Application No. 2000-350934 filed Nov.
17, 2000, the contents of which are hereby incorporated by
reference.
[0002] 1. Technical Field
[0003] The present invention relates to a method for fabricating a
semiconductor device and, particularly, to a method for forming a
film with a planar surface on a substrate.
[0004] 2. Background Art
[0005] In recent years, semiconductor devices have been fabricated
by defining feature sizes as small as around 100 nm or less through
miniaturization using lithographic technology which employs, as
exposing light, a beam at a wavelength of about 100 nm or less.
[0006] In such lithographic technology using short-wavelength
light, a focal depth is extremely lowered so that it is inevitable
to constantly keep planar a surface of a film formed on a
substrate. In fabricating a next-generation semiconductor device
(100 nm or less in feature size), therefore, the technology for
planarizing the film on the substrate is significantly important.
In the present specification, a substrate is defined as a substrate
on which a semiconductor device is formed such as a semiconductor
substrate, a liquid crystal substrate (LCD), or the like.
[0007] At present, CMP (Chemical Mechanical Polishing) is
main-stream technology for planarizing a film in a device ranging
in size from 0.13 .mu.m to 0.25 .mu.m. There has also been proposed
a method for forming a planar film (planarized film) by laminating
two films that have been formed preliminarily.
[0008] The description of the former CMP technology will be omitted
since it has been well known. Instead, a description will be given
herein below to a method for forming a planar film by laminating
two films disclosed in, e.g., Japanese Laid-Open Patent Publication
No. HEI 10-32198.
[0009] First, as shown in FIG. 20(a), a semiconductor device is
constructed on a substrate 101 through a microfabrication process
performed with respect thereto so that a stepped layer 102 is
formed. Hereinafter, the substrate 101 formed with the stepped
layer 102 will be termed a stepped substrate (101, 102).
[0010] Then, a plate 104 to which a film 103 formed as a sheet has
been adhered preliminarily is disposed such that the sheet-like
film 103 and the stepped layer 102 are opposed to each other.
[0011] Next, as shown in FIG. 20(b), the plate 104 formed with the
sheet-like film 103 and the stepped substrate (101, 102) are
brought closer to each other and pressed against each other with
the application of heat.
[0012] Next, as shown in FIG. 20(c), only the plate 104 is peeled
off, while the sheet-like film 103 is left on the stepped substrate
(101, 102).
[0013] As a result, the sheet-like film 103 with a planar surface
is formed on the stepped substrate (101, 102), as shown in FIG.
20(d). In FIG. 20(d), 105 denotes an unburied portion resulting
from a depressed portion with a high aspect ratio formed between
interconnect patterns which has remained unfilled.
[0014] However, the conventional method for fabricating a
semiconductor device has the problem that a global step (a
difference in height from the substrate surface between locations
at a distance), e.g., a step between the points A and B in FIG.
20(d) occurs, though a step in a dense pattern portion adjacent the
point A is removed and the film 103 can be planarized.
[0015] If the spacing between the interconnect patterns, i.e., the
spacing between step patterns is 100 nm or less, the aspect ratio
of a depressed portion formed between the step patterns is
increased so that the depressed portion is not filled
consistently.
[0016] Although the use of the CMP technology prevents the
occurrence of the problem that a depressed portion with a high
aspect ratio remains unfilled, the essential problem that the
global step cannot be suppressed remains unsolved.
DISCLOSURE OF THE INVENTION
[0017] In view of the foregoing, it is therefore an object of the
present invention to allow the formation of a film without a global
step, having a planar surface across the entire substrate, and
capable of consistently filling a depressed portion with a high
aspect ratio.
[0018] To attain the object, a first method for fabricating a
semiconductor device according to the present invention comprises:
a film forming step of supplying a material with fluidity to a
surface of a substrate to form a film with fluidity; a planarizing
step of pressing the film with fluidity against the substrate by a
planar pressing surface of a pressing member to planarize a surface
of the film with fluidity; and a solidifying step of solidifying
the film with fluidity having the surface planarized.
[0019] Since the first method for fabricating a semiconductor
device forms the film with fluidity (fluid film) on the surface of
the substrate, planarizes the fluid film by pressing the fluid film
by the planar pressing surface of the pressing member, and
solidifies the fluid film having the planarized surface, a global
step does not occur and a depressed portion with a high aspect
ratio is filled completely so that an unburied portion is not
formed.
[0020] In the first method for fabricating a semiconductor device,
the pressing surface of the pressing member preferably has a
hydrophobic property.
[0021] The arrangement allows easy removal of the pressing member
from the solidified film so that a planar film with a smaller
number of defects is formed.
[0022] In the first method for fabricating a semiconductor device,
the material with fluidity is preferably an insulating
material.
[0023] The arrangement enables the formation of an insulating film
without a global step.
[0024] In the first method for fabricating a semiconductor device,
the material with fluidity is preferably in the state of a liquid
or a gel.
[0025] The arrangement enables easy and reliable formation of the
film with fluidity on the surface of the substrate.
[0026] In the first method for fabricating a semiconductor device,
the film forming step is preferably performed while the substrate
is rotated.
[0027] The arrangement allows the material with fluidity to be
filled even in an inner part of a depressed portion with a high
aspect ratio.
[0028] In the first method for fabricating a semiconductor device,
the film forming step preferably includes the step of rotating the
substrate supplied with the material with fluidity.
[0029] The arrangement allows the material with fluidity to be
filled even in an inner part of a depressed portion with a high
aspect ratio.
[0030] In the first method for fabricating a semiconductor device,
the film forming step is preferably performed by supplying the
material with fluidity in a showering or spraying manner while
rotating the substrate.
[0031] The arrangement enables the formation of the film with
fluidity having a relatively small thickness.
[0032] In the first method for fabricating a semiconductor device,
the film forming step is preferably performed by supplying, while
moving a nozzle having fine outlets and the substrate relative to
each other in an in-plane direction, the material with fluidity
from the outlets to the surface of the substrate.
[0033] In the arrangement, the thickness of the film with fluidity
can be controlled to a desired value by adjusting the relative
moving speeds of the nozzle and the substrate. By adjusting the
viscosity of the material with fluidity, the degree of fluidity of
the film with fluidity can also be changed. By adjusting the number
of nozzles, the processing speed can also be controlled.
[0034] In the first method for fabricating a semiconductor device,
the film forming step is preferably performed by supplying, to the
surface of the substrate, the material with fluidity adhered to a
surface of a roller, while rotating the roller.
[0035] In the arrangement, the thickness of the film with fluidity
can be controlled by adjusting the distance between the roller and
the substrate and the force with which the roller is pressed
against the substrate. In addition, a material with fluidity having
a high viscosity can be used.
[0036] Preferably, the first method for fabricating a semiconductor
device further comprises, after the film forming step, the step of
selectively removing a peripheral portion of the film with
fluidity.
[0037] The arrangement facilitates the mechanical holding of the
peripheral portion of the substrate in the process of fabricating a
semiconductor device.
[0038] In this case, the step of removing the peripheral portion of
the film with fluidity is preferably performed by supplying a
solution for dissolving the material with fluidity to the
peripheral portion of the film with fluidity, while rotating the
substrate.
[0039] The arrangement ensures the removal of the peripheral
portion of the substrate having a plan configuration which is a
circle or a polygon with a large number of angles.
[0040] In this case, the step of removing the peripheral portion of
the film with fluidity is also preferably performed by irradiating
the peripheral portion of the film with fluidity with light to
modify the peripheral portion and removing the modified peripheral
portion.
[0041] The arrangement ensures the removal of the peripheral
portion of the substrate having a plan configuration which is not
only a circle or a polygon with a large number of angles but also a
polygon having a small number of angles, such as a triangle or
quadrilateral.
[0042] In the first method for fabricating a semiconductor device,
the planarizing step preferably includes the step of measuring a
plurality of distances between the surface of the substrate and the
pressing surface and pressing the film with fluidity by the
pressing surface such that the plurality of distances become
equal.
[0043] The arrangement allows the distance from the substrate
surface to the surface of the film with fluidity to be held
constantly equal and obviates the necessity to perform the
operation of adjusting the distance between the surface of the
substrate and the pressing surface of the pressing member to be
equal every specified period.
[0044] In the first method for fabricating a semiconductor device,
the planarizing step preferably includes the step of measuring a
plurality of distances between a surface of a stage on which the
substrate is placed and the pressing surface and pressing the film
with fluidity by the pressing surface such that the plurality of
distances become equal. The arrangement allows the distance from
the substrate surface to the surface of the film with fluidity to
be held constantly equal and obviates the necessity to perform the
operation of adjusting the distance between the surface of the
substrate and the pressing surface of the pressing member to be
equal every specified period.
[0045] In these cases, the step of measuring the plurality of
distances is preferably performed by measuring an electrostatic
capacitance per unit area at a position at which the measurement is
performed.
[0046] The arrangement enables easy and reliable measurement of the
plurality of distances.
[0047] In the first method for fabricating a semiconductor device,
the solidifying step is preferably performed by heating the film
with fluidity, while pressing the film with fluidity by the
pressing surface in the planarizing step.
[0048] The arrangement allows easy solidification of the film with
fluidity by a thermochemical reaction.
[0049] In the first method for fabricating a semiconductor device,
the solidifying step is preferably performed by irradiating the
film with fluidity with light, while pressing the film with
fluidity by the pressing surface in the planarizing step.
[0050] The arrangement allows easy solidification of the film with
fluidity by a photochemical reaction or a thermochemical
reaction.
[0051] In this case, the step of irradiating the film with fluidity
with light is preferably performed while cooling the film with
fluidity or after temporarily solidifying the film with fluidity by
cooling.
[0052] The arrangement ensures the solidification of the film with
fluidity without impairing the planarity thereof even if the film
has a high degree of fluidity.
[0053] In the first method for fabricating a semiconductor device,
the solidifying step is preferably performed by irradiating the
film with fluidity with light and heating the film with fluidity,
while pressing the film with fluidity by the pressing surface in
the planarizing step.
[0054] The arrangement allows rapid solidification of the film with
fluidity by a photochemical reaction or a thermochemical
reaction.
[0055] Preferably, the first method for fabricating a semiconductor
device further comprises, after the solidifying step, the step of
thinning the entire film with fluidity.
[0056] The arrangement makes it possible to form the film with
fluidity having a thickness larger than a desired value and then
thin it to form the film with the desired thickness so that a
stable process with a wide process window is implemented.
[0057] In this case, the step of thinning the entire film with
fluidity is preferably performed by plasma etching.
[0058] The arrangement improves the accuracy of the thickness of
the thinned film.
[0059] In this case, the step of thinning the film with fluidity is
also preferably performed by chemical mechanical polishing.
[0060] The arrangement facilitates the step of thinning the
film.
[0061] A second method for fabricating a semiconductor device
according to the present invention comprises the steps of:
supplying an insulating material with fluidity to a surface of a
substrate to form an insulating film with fluidity; pressing the
insulating film with fluidity against the substrate by a planar
pressing surface of a pressing member to planarize a surface of the
insulating film with fluidity; solidifying the insulating film with
fluidity having the surface planarized; performing selective
etching with respect to the solidified insulating film to form a
depressed portion in the solidified insulating film; and burying a
metal material in the depressed portion to form a buried
interconnect or plug.
[0062] Since the second method for fabricating a semiconductor
device allows the formation of the insulating film without a global
step, a reduction in focal depth margin resulting from a step can
be suppressed in the step of forming a mask pattern on the
insulating film by lithographic technology. This achieves a
significant increase in processing margin (process window),
compared with the prior art technology, so that a high-precision
semiconductor device is fabricated.
[0063] In the second method for fabricating a semiconductor device,
the insulating film is preferably an organic film, an inorganic
film, an organic/inorganic hybrid film, a photoforming film, a
photosensitive resin film, or a porous film.
[0064] The arrangement allows the formation of the insulating film
having a compact texture and excellent planarity.
[0065] In the second method for fabricating a semiconductor device,
a relative dielectric constant of the insulating film is preferably
approximately 4 or less.
[0066] The arrangement achieves a reduction in wire-to-wire
capacitance so that the performance of the semiconductor device is
improved.
BRIEF DESCRIPTION OF THE DRAWINGS
[0067] FIG. 1 is a cross-sectional view illustrating the individual
process steps of a method for fabricating a semiconductor device
according to a first embodiment;
[0068] FIG. 2 is a cross-sectional views illustrating the
individual process steps of the method for fabricating a
semiconductor device according to the first embodiment;
[0069] FIG. 3(a) is a cross-sectional view showing a sheet-like
film obtained by a conventional method for fabricating a
semiconductor device and FIG. 3(b) is a cross-sectional view
showing a solidified film obtained by the method for fabricating a
semiconductor device according to the first embodiment;
[0070] FIGS. 4(a) to 4(d) are cross-sectional views illustrating
the individual process steps of a first example of the first
embodiment;
[0071] FIGS. 5(a) to 5(c) are cross-sectional views illustrating
the individual process steps of a second example of the first
embodiment;
[0072] FIGS. 6(a) to 6(c) are cross-sectional views illustrating
the individual process steps of a third example of the first
embodiment;
[0073] FIGS. 7(a) to 7(c) are cross-sectional views illustrating
the individual process steps of a fourth example of the first
embodiment;
[0074] FIGS. 8(a) to 8(c) are cross-sectional views illustrating
the individual process steps of a method for fabricating a
semiconductor device according to a second embodiment;
[0075] FIGS. 9(a) to 9(c) are cross-sectional views illustrating
the individual process steps of the method for fabricating a
semiconductor device according to the second embodiment;
[0076] FIGS. 10(a) and 10(b) are cross-sectional views illustrating
the individual process steps of a method for fabricating a
semiconductor device according to a third embodiment;
[0077] FIGS. 11(a) and 11(b) are cross-sectional views illustrating
the individual process steps of the method for fabricating a
semiconductor device according to the third embodiment;
[0078] FIGS. 12(a) and 12(b) are cross-sectional views illustrating
the individual process steps of a method for fabricating a
semiconductor device according to a fourth embodiment;
[0079] FIGS. 13(a) and 13(b) are cross-sectional views illustrating
the individual process steps of a method for fabricating a
semiconductor device according to a fifth embodiment;
[0080] FIGS. 14(a) and 14(b) are cross-sectional views illustrating
the individual process steps of a method for fabricating a
semiconductor device according to a first example of a sixth
embodiment;
[0081] FIGS. 15(a) and 15(c) are cross-sectional views illustrating
the individual process steps of a method for fabricating a
semiconductor device according to a second example of the sixth
embodiment;
[0082] FIGS. 16(a) and 16(b) are cross-sectional views illustrating
the individual process steps of a method for fabricating a
semiconductor device according to a seventh embodiment;
[0083] FIGS. 17(a) to 17(c) are cross-sectional views illustrating
the individual process steps of a method for fabricating a
semiconductor device according to an eighth embodiment;
[0084] FIGS. 18(a) to 18(d) are cross-sectional views illustrating
the individual process steps of the method for fabricating a
semiconductor device according to the eighth embodiment;
[0085] FIGS. 19(a) to 19(d) are cross-sectional views illustrating
the individual process steps of the method for fabricating a
semiconductor device according to the eighth embodiment; and
[0086] FIGS. 20(a) to 20(d) are cross-sectional views illustrating
the individual process steps of the conventional method for
fabricating a semiconductor device.
BEST MODE FOR CARRYING OUT THE INVENTION
Embodiment 1
[0087] A method for fabricating a semiconductor device according to
a first embodiment will be described herein below with reference to
FIGS. 1(a) to 1(c) and FIGS. 2(a) to 2(c).
[0088] First, as shown in FIG. 1(a), a material with fluidity such
as a material in the state of a liquid or gel is supplied to a
surface of a stepped substrate (1, 2) consisting of a substrate 1
composed of a semiconductor wafer and a stepped layer 2 to form a
film 3 with fluidity (hereinafter simply referred to as the fluid
film).
[0089] As examples of the fluid film, there can be listed an
organic film, an inorganic film, an organic/inorganic composite
film (organic/inorganic hybrid film), a photoforming film which is
cured under the radiation of light, a photosensitive resist film
such as a resist film, and a porous film having therein numerous
pores ranging in diameter from several nanometers to about 10
nanometers.
[0090] As examples of a method for forming the fluid film 3, there
can be listed a spin coating method, a microscopic spraying method,
and a rotating roller method. The thickness of the fluid film 3 can
be adjusted by selecting among the methods for forming the fluid
film 3, though the adjustment of the thickness of the fluid film 3
differs from one method to another. The methods for forming the
fluid film 3 will be described in detail in first to fourth
examples.
[0091] The plan configuration of the substrate 1 is not
particularly limited. The substrate 1 may have any configuration
such as a circle or polygon.
[0092] In the case where the fluid film 3 is used as an interlayer
film in multilayer interconnection, an insulating material is used
preferably as the material with fluidity.
[0093] Next, as shown in FIG. 1(b), a pressing member 4 having a
planar pressing surface is disposed such that the pressing surface
thereof is opposed to the surface of the fluid film 3. Then, as
shown in FIG. 1(c), a pressure in the direction of the substrate is
applied to the pressing member 4 to press the fluid film 3 against
the substrate 1 and thereby planarize the surface of the fluid film
3.
[0094] In this case, the surface of the fluid film 3 is planarized
over the entire surface of the substrate 1 by merely pressing it by
the pressing surface of the pressing member 4. If the pressing
operation performed by the pressing member 4 is interrupted,
however, the fluid film 3 is transformed into a configuration which
is stable in terms of energy by the surface tension of the fluid
film 3.
[0095] To prevent this, the fluid film 3 is heated while it is
pressed by the pressing member 4 against the substrate 1 so that a
chemical reaction occurs within the fluid film 3 and the fluid film
3 is solidified. Consequently, a solidified film with a planar
surface (hereinafter simply referred to as the solidified film) 5
is formed.
[0096] Then, the heating is completed and the temperature of the
solidified film 5 is reduced to a room temperature. If the pressing
member 4 is removed from the solidified film 5 thereafter, as shown
in FIG. 2(b), the solidified film 5 with a planar surface can be
formed on the surface of the stepped substrate (1, 2), as shown in
FIG. 2(c).
[0097] Preferably, a Teflon coating treatment or a surface
treatment using a silicon coupling material is performed with
respect to the pressing surface such that the planar pressing
surface of the pressing member 4 has a hydrophobic property. This
facilitates the removal of the pressing member 4 from the
solidified film 5 so that a planar solidified film 5 with a smaller
number of defects is formed.
[0098] FIG. 3(a) shows a cross-sectional configuration of the
sheet-like film 103 with a planar surface obtained by the
conventional method for fabricating a semiconductor device. FIG.
3(b) shows the cross-sectional configuration of the solidified film
5 with a planar surface obtained by the method for fabricating a
semiconductor device according to the first embodiment.
[0099] In the sheet-like film 103 obtained by the conventional
method, the relationship represented by h.sub.1>h.sub.2 exists
between a film thickness h1 at the point A and a film thickness
h.sub.2 at the point B. This is because the conventional method has
pressed the sheet-like film 103 adhered to the plate 104 against
the stepped substrate (101, 102) with the application of heat and
then peeled the plate 104 off. As a result, not only a global step
(h.sub.2-h.sub.1) occurs but also the unburied portion 105 occurs
since a depressed portion with a high aspect ratio remains
unfilled.
[0100] In the solidified film 5 obtained according to the first
embodiment, by contrast, the relationship represented by
h.sub.3=h.sub.4 exists between a film thickness h3 at the point A
and a film thickness h.sub.4 at the point B. This is because the
first embodiment has formed the fluid film 3 by supplying the
material with fluidity to the surface of the stepped substrate (1,
2), planarized the surface of the fluid film 3, and then solidified
the fluid film 3 to provide the solidified film 5. As a result, a
global step does not occur and an unburied portion is not formed
since a depressed portion with a high aspect ratio is filled
completely.
[0101] A description will be given herein below to the material
with fluidity.
[0102] As an example of the material with fluidity for forming an
organic film, there can be listed an aromatic polymer containing
aryl ether as a main skeleton and, specifically, FLARE
(commercially available from Honeywell Corporation) and SiLK
(commercially available from Dow Chemical Co.) can be listed.
[0103] As an example of the material with fluidity for forming an
inorganic film, there can be listed HSQ (Hydrogen Silsquioxane) or
an organic SOG such as an alkylsiloxane polymer can be listed. As a
specific example of the HSQ, Fox (commercially available from Dow
Coming Corporation) can be listed. As a specific example of the
organic SOG, HSG-RZ25 (commercially available from Hitachi Chemical
Co., Ltd.) can be listed.
[0104] As an example of the material with fluidity for forming an
organic/inorganic hybrid film, there can be listed organic siloxane
containing an organic group such as a methyl group in a siloxane
skeleton. As a specific example, there can be, listed HOSP (Hybrid
Organic Siloxane Polymer commercially available from Honeywell
Corporation).
[0105] As an example of the material with fluidity for forming a
photoforming film, there can be listed PDGI (Poly Dimethyl Glutar
Imide) can be listed. As a specific example, SAL101 (commercially
available from Shipley Far East Ltd.) can be listed.
[0106] As an example of the material with fluidity for forming a
photosensitive resin film, there can be used a typical resist
material used for lithographic technology.
[0107] As an example of the material with fluidity for forming a
porous film, there can be listed an organic or inorganic material
or an organic/inorganic hybrid material. As a specific example of
the organic material with pores, FLAIRE (commercially available
from Honeywell Corporation) can be listed. As a specific example of
the inorganic material with pores, KLK (commercially available from
Dow Coming Corporation) having pores in HSQ (Hydrogen Silsquioxane)
can be listed. As an example of the organic/inorganic hybrid
material with pores, Nanoglass (commercially available from
Honeywell Corporation) can be listed.
[0108] If the solidified film 5 obtained by solidifying the fluid
film 3 formed by using any of the foregoing materials is used as an
interlayer insulating film in multilayer interconnection, an
interlayer insulating film having a compact texture and a
dielectric constant lower than that of a normal silicon oxide film
(having a relative dielectric constant of about 4) is obtainable so
that a film suitable for use in a semiconductor device formed
through microfabrication for defining a feature size of 100 nm or
less is implemented. If a porous film is used, in particular, an
interlayer insulating film having an extremely low dielectric
constant of 2 or less can be formed.
[0109] Although the foregoing materials are for forming insulating
films, the present invention is not limited to the formation of the
insulating films and can also be used as a method for forming a
conductive polymer film or metal film.
EXAMPLE 1
[0110] A description will be given herein below to a method for
forming a fluid film according to a first example, i.e., to a first
spin coating method with reference to FIGS. 4A(a) to 4(d).
[0111] First, as shown in FIG. 4(a), a stepped substrate 21 is
carried by vacuum suction on a stage 20 provided rotatable, a
proper amount of material 23 with fluidity is supplied dropwise
onto the stepped substrate 21, and then the stage 20 is rotated. Or
alternatively, the stepped substrate 21 is carried by vacuum
suction on the stage 20 provided rotatable and then a material with
fluidity is supplied onto the stepped substrate 21 from a drop
nozzle 24, while the stage 20 and the stepped substrate 21 are
rotated, as shown in FIG. 4(b).
[0112] As a result, a fluid film 22 with a planar surface is formed
on the stepped substrate 21, as shown in FIG. 4(c). FIG. 4(d) shows
the portion enclosed by the dash-dot lines in FIG. 4(c), in which
the fluid film 3 having a planar surface is formed on the stepped
layer 2 formed on the substrate 1.
[0113] In either of the case where the method shown in FIG. 4(a) is
used and the case where the method shown in FIG. 4(b) is used, the
fluid film 22(3) having a hardness suitable for the step of
planarizing the surface of the fluid film 22(3) by the foregoing
pressing member 4 is obtainable by optimizing the viscosity of the
material 23 with fluidity and the rotating speed of the stage
20.
[0114] The first example is suitable for the case where the fluid
film 22(3) having a relatively large thickness is formed.
EXAMPLE 2
[0115] A description will be given herein below to a method for
forming a fluid film according to a second example, i.e., to a
second spin coating method with reference to FIGS. 5(a) to
5(c).
[0116] First, as shown in FIG. 5(a), the stepped substrate 21 is
carried by vacuum suction on the stage 20 provided rotatable. Then,
a material 26 with fluidity is supplied in a showering or spraying
manner from the outlets of an eject nozzle 25 onto the stepped
substrate 21.
[0117] After the material 26 with fluidity is supplied in a
specified amount, the stage 20 is rotated continuously for a
specified time so that the fluid film 22 having a planar surface is
formed on the stepped substrate 21, as shown in FIG. 5(b). FIG.
5(c) shows the portion enclosed by the dash-dot lines in FIG. 5(b),
in which the fluid film 3 having a planar surface is formed on the
stepped layer 2 formed on the substrate 1.
[0118] The second example is suitable for the case where the fluid
film 22(3) having a relatively small thickness is formed.
EXAMPLE 3
[0119] A description will be given herein below to a method for
forming a fluid film according to a third example, i.e., to a
microscopic spraying method with reference to FIGS. 6(a) to
6(c).
[0120] First, as shown in FIG. 6(a), a material 28 with fluidity is
supplied stepwise in specified amounts from a drop nozzle 27 onto
the stepped substrate 21, while the stepped substrate 21 is moved
in one of two orthogonal directions in 2-D orthogonal coordinate
systems, e.g., in the horizontal direction of FIG. 6(a) and the
drop nozzle 27 is moved in the other of the two orthogonal
directions, e.g., in the vertical direction of FIG. 6(a).
Specifically, the operation of stopping the stepped substrate 21
that has moved over a specified distance in the leftward direction
in FIG. 6(a) is performed repeatedly and the material with fluidity
is supplied stepwise in specified amounts from the drop nozzle 27
onto the stepped substrate 21, while the drop nozzle 27 is moved in
the upward or downward direction in FIG. 6(a) during a period
during which the stepped substrate 21 is stopped.
[0121] As a result, the fluid film 22 with a planar surface is
formed on the stepped substrate 21, as shown in FIG. 6(b). FIG.
6(c) shows the portion enclosed by the dash-dot lines in FIG. 6(b),
in which the fluid film 3 with a planar surface is formed on the
stepped layer 2 formed on the substrate 1.
[0122] According to the third example, the thickness of the fluid
film 22(3) can be controlled in a range from a small value to a
large value by adjusting the amount of the material with fluidity
supplied from the drop nozzle 27 and the moving speed of the drop
nozzle 27.
[0123] Moreover, the degree of fluidity of the fluid film 22(3) can
be changed by adjusting the viscosity of the material with fluidity
supplied from the drop nozzle 27.
[0124] Furthermore, the processing speed can be controlled by
adjusting the number of drop nozzles 27.
EXAMPLE 4
[0125] A description will be given herein below to a method for
forming a fluid film according to a fourth example, i.e., to a
rotating roller method with reference to FIGS. 7(a) to 7(c).
[0126] As shown in FIGS. 7(a) and 7(b), a rotating roller 29 is
moved rotatively along the surface of the stepped substrate 2 with
a material 30 with fluidity being evenly adhered to the
circumferential surface of the rotating roller 29.
[0127] As a result, the material 30 with fluidity is transferred
onto the surface of the stepped substrate 21 so that the fluid film
22 with a planar surface is formed on the stepped substrate 21.
FIG. 7(c) shows the portion enclosed by the dash-dot lines in FIG.
7(b), in which the fluid film 3 with a planar surface is formed on
the stepped layer 2 formed on the substrate 1.
[0128] According to the fourth example, the thickness of the fluid
film 22(3) can be controlled by adjusting the distance between the
rotating roller 29 and the stepped substrate 21 and the force with
which the rotating roller 29 is pressed against the stepped
substrate 21.
[0129] The fourth example is suitable for the case where the
material 30 with fluidity is in the state of a highly viscous
liquid or gel.
Embodiment 2
[0130] A method for fabricating a semiconductor device according to
a second embodiment will be described herein below with reference
to FIGS. 8(a) to 8(c) and FIGS. 9(a) to 9(c).
[0131] The second embodiment provides methods for selectively
removing the peripheral portion of the fluid film obtained
according to the first embodiment, of which the first one supplies
a solution for dissolving the fluid film to the peripheral portion
thereof, while rotating the substrate formed with the fluid film,
and thereby removes the peripheral portion of the fluid film and
the second one modifies the peripheral portion of the fluid film by
irradiating it with light and then removes the modified peripheral
portion.
[0132] The first embodiment has formed the fluid film 3 over the
entire surface of the substrate 1, i.e., even on the peripheral
portion of the substrate 1.
[0133] However, there are cases where the peripheral portion of the
substrate 1 should be held mechanically.
[0134] The second embodiment has been achieved to solve such a
problem. Since the second embodiment selectively removes the
peripheral portion of the fluid film 3, it becomes easier to
mechanically hold the peripheral portion of the substrate 1.
[0135] A description will be given herein below to the first method
for selectively removing the peripheral portion of the fluid film
22 with reference to FIGS. 8(a) to 8(c).
[0136] First, as shown in FIG. 8(a), the stepped substrate 21
formed with the fluid film 22 is vacuum-sucked on the stage 20
provided rotatable. Then, the stage 20 is rotated to rotate the
fluid film 22, while a release agent 33 is supplied from a first
nozzle 31 to the peripheral portion of the fluid film 22 and a
release agent 34 is supplied from a second nozzle 32 to the back
surface of the peripheral portion of the stepped substrate 21.
[0137] This allows the removal of the peripheral portion of the
fluid film 22 and the removal of the material with fluidity adhered
to the back-surface peripheral portion of the stepped substrate 21,
as shown in FIG. 8(b).
[0138] The rotation of the stage 20 is performed continuously,
while the supply of the release agents 33 and 34 is stopped, so
that the fluid film 22 is dried.
[0139] Although the first method may be implement before or after
the surface of the fluid film 22 is planarized, it is preferably
implemented before the fluid film 22 is solidified.
[0140] Since the first method removes the peripheral portion of the
fluid film 22, while rotating the stage 22 and the fluid film 22,
it is suitable for the stepped substrate 21 having a plan
configuration which is a circle or a polygon with a large number of
angles.
[0141] A description will be given herein below to the second
method for selectively removing the peripheral portion of the fluid
film 22 with reference to FIGS. 9(a) to 9(c).
[0142] First, as shown in FIG. 9(a), the stepped substrate 21
formed with the fluid film 22 is vacuum-sucked on the stage 20
provided rotatable. Then, the stage 20 is rotated to rotate the
fluid film 22, while the peripheral portion of the fluid film 22 is
irradiated with light 36 from an irradiating apparatus 35, so that
a photochemical reaction is caused in the peripheral portion
(portion irradiated with the light) of the fluid film 22 and the
peripheral portion is modified. In this case, a UV beam or a beam
at a wavelength shorter than that of the UV beam is used preferably
as the light 36.
[0143] Next, as shown in FIG. 9(b), the rotation of the stage 20
and the rotation of the fluid film 22 are stopped and then a
solution 37 such as a developing solution is supplied onto the
entire surface of the fluid film 22. As a result, the modified
peripheral portion of the fluid film 22 is dissolved in the
solution 37 so that the peripheral portion of the fluid film 22 is
removed selectively.
[0144] Next, as shown in FIG. 9(c), the stage 20 and the fluid film
22 are rotated again such that the solution 37 remaining on the
fluid film 22 is removed by a centrifugal force to the outside. In
this case, it is preferable to supply a rinsing agent onto the
fluid film 22 while removing the solution 37 or after removing the
solution 37 and thereby remove the solution 37. As a result, the
fluid film 22 from which the peripheral portion has been removed
selectively can be obtained.
[0145] Although the second method may be implemented before or
after the surface of the fluid film 22 is planarized, it is
performed preferably before the fluid film 22 is solidified.
[0146] Since the second method selectively irradiates the
peripheral portion of the fluid film 22 with the light 36, it is
applicable not only to the stepped substrate 21 having a plan
configuration which is a circle or a polygon with a large number of
angles but also to the stepped substrate 21 having a polygonal plan
configuration with a small number of angles, such as a triangle or
quadrilateral.
Embodiment 3
[0147] A method for fabricating a semiconductor device according to
a third embodiment will be described herein below with reference to
FIGS. 10(a) and 10(b) and FIGS. 11(a) and 11(b).
[0148] The third embodiment provides a method preferred to
planarize the surface of the fluid film obtained according to the
first embodiment, which measures a plurality of distances between
the surface of the substrate or the surface of the stage and the
pressing surface of the pressing member and presses the fluid film
such that the plurality of distances become equal.
[0149] First, as shown in FIG. 10(a), a fluid film 52 is formed on
a substrate 51 by the method according to the first embodiment and
then planarized by using a pressing member 53 having a plurality of
distance sensors 54 on the pressing surface thereof. In this case,
a plurality of distances between the surface of the substrate 51 or
the surface of the stage 20 (see FIG. 4(c) or 5(b). In the third
embodiment, the outer size of the stage 20 is adjusted preferably
to be larger than that of the substrate 51) on which the substrate
51 is placed and the pressing surface of the pressing member 53 are
measured by using the plurality of distance sensors 54, while the
fluid film 52 is pressed by the pressing member 53 to be planarized
such that the plurality of distances become equal. Data on the
plurality of distances measured by using the plurality of distance
sensors 54 is feedbacked to pressing means for pressing the
pressing member 53 and the fluid film 52 is pressed such that the
plurality of distances become equal. Feedback control may be
performed appropriately by using a computer.
[0150] Referring to FIG. 10(b), a description will be given herein
below to a method for measuring a plurality of distances between
the surface of the substrate 51 and the pressing surface of the
pressing member 53.
[0151] In FIG. 10(b), a, b, c . . . , and q denote positions at
which the distance sensors 54 are disposed. The positions a to q of
the distance sensors 54 are optimized preferably depending on the
mechanism of the pressing member 53. The distance sensors 54 may be
disposed appropriately at the positions which allow efficient
measurement of the distances between the surface of the substrate
51 or the surface of the stage on which the substrate 51 is placed
and the surface of the fluid film 52. For example, the positions a
to i of the sensors are suitable for measuring the distances
between the surface of the substrate 51 and the surface of the
fluid film 52 and the positions j to q of the sensors are suitable
for measuring the distances between the surface of the stage on
which the substrate 51 is placed and the surface of the fluid film
52.
[0152] Accordingly, it is possible to measure only the distances
between the surface of the substrate 51 and the surface of the
fluid film 52 by using only the distance sensors 54 at the
positions a to i, measure only the distances between the surface of
the stage on which the substrate 51 is placed and the surface of
the fluid film 52 by using only the distance sensors 54 at the
positions j to q, or measure the distances between the surface of
the substrate 51 and the surface of the fluid film 52 as well as
the distances between the surface of the stage on which the
substrate 51 is placed and the surface of the fluid film 52 by
using the distance sensors 54 at the positions a to q.
[0153] If the roughness of the pressing surface of the pressing
member 54 can be adjusted finely, it is also possible to adjust the
distance between the surface of the substrate 51 and the surface of
the fluid film 52 by using the distance sensors 54 at the positions
a to i and then adjust the distance between the surface of the
substrate 51 and the surface of the fluid film 52 by using the
distance sensors 54 at the positions a to i. This implements
higher-precision planarization. The number and positions of the
distance sensors 54 may be optimized appropriately depending on the
degree of planarity required.
[0154] According to the first embodiment, it is important but not
easy to equalize the distance from the substrate surface to the
surface of the fluid film 3. Although the first embodiment allows
the distance from the substrate surface to the surface of the fluid
film 3 to become equal by preliminarily adjusting the distance
between the surface of the substrate 1 and the pressing surface of
the pressing member 4 to be equal, the method requires the distance
between the surface of the substrate 1 and the pressing surface of
the pressing member 4 to be adjusted equal every specified period,
i.e., every time the surfaces of a specified number of fluid films
3 are planarized.
[0155] By contrast, since the third embodiment allows the distance
from the substrate surface to the surface of the fluid film 3 to be
held constantly equal, the operation of adjusting the surface of
the substrate 1 and the pressing surface of the pressing member 4
to be equal, which is performed every specified period, can be
omitted.
[0156] The step of adjusting the distance between the surface of
the substrate 1 and the pressing surface of the pressing member 4
to be equal may be performed before, during, or after the process
of pressing the fluid film 3 by the pressing member 4.
[0157] FIG. 11(a) shows the cross-sectional condition of the fluid
film 3 when the distance between the pressing surface of the
pressing member 4 and the surface of the substrate 1 is unequal.
FIG. 11(b) shows the cross-sectional condition of the fluid film 3
when the distance between the pressing surface of the pressing
member 4 and the surface of the substrate 1 is held equal.
[0158] As will be understood from a comparison between FIGS. 11(a)
and 11(b), if the fluid film 3 is pressed with the distance between
the pressing surface of the pressing member 4 and the surface of
the substrate 1 being held equal, the surface of the fluid film 3
can be planarized with the distance from the surface of the
substrate 1 to the fluid film 3 being held equal.
Embodiment 4
[0159] A method for fabricating a semiconductor device according to
a fourth embodiment will be described herein below with reference
to FIGS. 12A(a) and 12(b).
[0160] In contrast to the first embodiment which has formed the
solidified film 5 with a planar surface by solidifying the fluid
film 3 with the application of heat, as shown in FIG. 2(a), the
fourth embodiment provides a method for forming the solidified film
5 with a planar surface by irradiating the fluid film 3 with light
and thereby solidifying it.
[0161] As shown in FIG. 12(a), the fluid film 3 under a pressure
applied thereto is irradiated with light with the surface thereof
being planarized by pressing it against the substrate 1 by the
pressing member 4 made from a light transmitting material, such as
quartz. If the fluid film 3 is to be solidified by a photochemical
reaction, a UV beam or a beam at a wavelength shorter than that of
the UV beam is used preferably as the light for irradiation. If the
fluid film 3 is to be solidified by a thermochemical reaction, an
infrared beam is used preferably as the light for irradiation. As
the light, either continuous light or pulsative light may be used.
If the light is intended to act only on the fluid film 3 such that
the action thereof on the substrate 1 is reduced, in particular,
the pulsative light is appropriate.
[0162] As a result, the fluid film 3 is solidified by a
photochemical or thermochemical reaction so that the solidified
film 5 is obtained as shown in FIG. 12(b).
[0163] The method of solidifying the fluid film 3 by a
photochemical reaction is appropriate for a photoforming film,
e.g., a photosensitive resin film such as a photoresist used in
lithographic technology. The method of solidifying the fluid film 3
by a photothermal reaction is appropriate for an organic film, an
inorganic film, and an organic/inorganic hybrid film.
Embodiment 5
[0164] A method for fabricating a semiconductor device according to
a fifth embodiment will be described herein below with reference to
FIGS. 13(a) and 13(b).
[0165] In contrast to the fourth embodiment which has solidified
the fluid film 3 by irradiating it with light, the fifth embodiment
provides a method of irradiating the fluid film 3 with light, while
heating it, and thereby solidifying the fluid film 3.
[0166] As shown in FIG. 13(a), the fluid film 3 under a pressure
applied thereto is irradiated with light, while it is heated, with
the surface thereof being planarized by pressing it against the
substrate 1 by the pressing member 4 made from a light transmitting
material, such as quartz. In this case also, a UV beam or a beam at
a wavelength shorter than that of the UV beam is used preferably as
the light for irradiation if the fluid film 3 is to be solidified
by a photochemical reaction and an infrared beam is used preferably
as the light for irradiation if the fluid film 3 is to be
solidified by a thermochemical reaction.
[0167] As a result, the fluid film 3 is solidified by a
photochemical reaction or a thermochemical reaction so that the
solidified film 5 is obtained as shown in FIG. 13(b).
[0168] The method of solidifying the fluid film 3 by a
photochemical reaction is appropriate for a photoforming film,
e.g., a photosensitive resin film such as a photoresist used in
lithographic technology. The method of solidifying the fluid film 3
by a photothermal reaction is appropriate for an organic film, an
inorganic film, and an organic/inorganic hybrid film.
[0169] Whether the step of irradiating the fluid film 3 with light
or the step of heating the fluid film 3 should be performed prior
to the other is determined preferably depending on the properties
of the material with fluidity composing the fluid film 3.
Embodiment 6
[0170] A method for fabricating a semiconductor device according to
a first example of a sixth embodiment will be described herein
below with reference to FIGS. 14(a) and 14(b).
[0171] In contrast to the fourth embodiment which has solidified
the fluid film 3 by irradiating it with light, the first example of
the sixth embodiment provides a method of irradiating the fluid
film 3 with light, while cooling it from the substrate side.
[0172] As shown in FIG. 14(a), the fluid film 3 under a pressure
applied thereto has a surface thereof irradiated with light, while
it is cooled from the substrate side, with the surface thereof
being planarized by pressing it against the substrate 1 by the
pressing member 4 made from a light transmitting material, such as
quartz. In this case also, a UV beam or a beam at a wavelength
shorter than that of the UV beam is used preferably as the light
for irradiation if the fluid film 3 is to be solidified by s
photochemical reaction and an infrared beam is used preferably as
the light for irradiation if the fluid film 3 is to be solidified
by a thermochemical reaction.
[0173] As a result, the fluid film 3 is solidified by a
photochemical reaction or a thermochemical reaction, though it is
cooled from the substrate side, so that the solidified film 5 is
obtained as shown in FIG. 14(b).
[0174] The first example of the sixth embodiment is suitable for
the case where the fluid film 3 readily flows under a pressure. The
first example suppresses the flowing of the fluid film 3 and allows
the fluid film 3 to be solidified by irradiating the fluid film 3
with light, while cooling it from the substrate side.
[0175] A method for fabricating a semiconductor device according to
a second example of the sixth embodiment will be described herein
below with reference to FIGS. 15(a) and 15(c).
[0176] In contrast to the first example which has solidified the
fluid film 3 by irradiating with light, while cooling it from the
substrate side, the second example provides a method of temporarily
solidifying the fluid film 3 by cooling it and then irradiating the
fluid film 3 with light.
[0177] First, as shown in FIG. 15(a), the fluid film 3 has the
surface thereof planarized by pressing it against the substrate 1
by the pressing member 4 made from a light transmitting material,
such as quartz, and is temporarily solidified under a pressure
applied thereto by cooling it from the substrate side.
[0178] Then, as shown in FIG. 15(b), the fluid film 3 is irradiated
with light after the cooling of the fluid film 3 is stopped, while
the pressure is applied continuously to the fluid film 3. In this
case also, a UV beam or a beam at a wavelength shorter than that of
the UV beam is used preferably as the light for irradiation if the
fluid film 3 is to be solidified by a photochemical reaction and an
infrared beam is used preferably as the light for irradiation if
the fluid film 3 is to be solidified by a thermochemical reaction.
In the case of using the thermochemical reaction, rapid thermal
annealing (RTA) for rapidly heating the fluid film 3 is performed
preferably.
[0179] As a result, the fluid film 3 is solidified by a
photochemical or thermochemical reaction so that the solidified
film 5 is obtained as shown in FIG. 15(c).
[0180] The second example is suitable for the case where the fluid
film 3 flows even under a low pressure. The second example
suppresses the flowing of the fluid film 3 and allows the fluid
film 3 to be solidified by cooling the fluid film 3 from the
substrate side such that it is temporarily solidified and then
irradiating the fluid film 3 with light.
[0181] Since the second example provides the method of solidifying
the fluid film 3 by temporarily solidifying the fluid film 3 and
then irradiating it with light, irradiation with light can be
performed after removing the pressing member 4 so that the pressing
member 4 need not be transparent.
[0182] It will easily be appreciated that heating performed in each
of the first, fourth, and fifth embodiments and the first example
of the sixth embodiment may also be performed by rapid thermal
annealing in the same manner as in the second example of the sixth
embodiment.
Embodiment 7
[0183] A method for fabricating a semiconductor device according to
a seventh embodiment will be described herein below with reference
to FIGS. 16(a) and 16(b).
[0184] The seventh embodiment provides a method for thinning the
solidified film obtained according to the first embodiment.
[0185] As shown in FIG. 16(a), the solidified film 5 with a planar
surface is formed in the same manner as in the first embodiment.
Then, plasma etching or chemical mechanical polishing (CMP) is
performed with respect to the solidified film 5, thereby removing
the surface portion of the solidified film 5 and thinning the
solidified film 5, as shown in FIG. 16(b).
[0186] In the case of using plasma etching, a gas containing
fluorine such as a CF.sub.4 gas or CHF.sub.3 gas, a gas mixture of
a gas containing fluorine and an oxygen gas, or an ammonia gas may
be used as an etching gas and film thickness adjustment excellent
in uniformity can be performed.
[0187] Since the seventh embodiment forms the solidified film 5
having a thickness larger than a desired value and then adjusts the
thickness of the solidified film 5 to a specified value by a
thinning process, a more stable process with a wide process window
can be provided.
Embodiment 8
[0188] A method for fabricating a semiconductor device according to
an eighth embodiment will be described herein below with reference
to FIGS. 17(a) to 17(c), FIGS. 18(a) to 18(d), and FIGS. 19(a) to
19(d).
[0189] First, as shown in FIG. 17(a), a lower interlayer insulating
film 62 is formed on a semiconductor substrate 61. Then, plugs are
formed in the lower interlayer insulating film 62, though they are
not depicted, and a metal interconnect 60 is formed on the lower
interlayer insulating film 62.
[0190] Next, as shown in FIG. 17(b), an insulating material with
fluidity in the state of a liquid or gel is supplied to the entire
surface of a semiconductor substrate 61 by a spin coating method, a
microscopic spraying method, or a rotating roller method in the
same manner as in the first embodiment, thereby forming a fluid
insulating film 63. The thickness of the fluid insulating film 63
may be set to an appropriate value.
[0191] As the fluid insulating film 63, an insulating film as
described in the first embodiment, i.e., an organic film, an
inorganic film, an organic/inorganic hybrid film, a porous film, or
the like can be used. Since an insulating film having a compact
texture and a dielectric constant lower than that of a normal
silicon oxide film can be obtained, a film suitable for use in a
semiconductor device having a feature size of 100 nm or less
through miniaturization can be implemented. In particular, the use
of a porous film allows an insulating film having an extremely low
dielectric constant of 2 or less to be formed.
[0192] Next, as shown in FIG. 17(c), a pressing member 64 having a
planar pressing surface is brought into contact with the surface of
the fluid insulating film 63. Then, as shown in FIG. 18(a), a
pressure is applied to the pressing member 64 to planarize the
surface of the fluid insulating film 63. In other words, the height
of the fluid insulating film 63 from the surface of the
semiconductor substrate 61 is entirely equalized.
[0193] Next, as shown in FIG. 18(b), the semiconductor substrate 61
including the fluid insulating film 63 is heated such that a
thermochemical reaction occurs in the insulating material to
solidify the fluid insulating film 63 and thereby form a planarized
upper interlayer insulating film 65.
[0194] After heating is stopped and the temperature of the
semiconductor substrate 61 is lowered to a room temperature, the
pressing member 64 is removed from the upper interlayer insulating
film 65, as shown in FIG. 18(c), so that the planarized upper
interlayer insulating film 65 is exposed, as shown in FIG.
18(d).
[0195] Next, as shown in FIG. 19(a), a mask pattern 66 composed of
a resist pattern or a hard mask and having openings is formed on
the upper interlayer insulating film 65 by using well-known
lithographic technology. Then, dry etching is performed with
respect to the upper interlayer insulating film 65 by using the
mask pattern 66 as a mask, thereby forming openings 67 for plugs in
the upper interlayer insulating film 65, as shown in FIG.
19(b).
[0196] After the mask pattern 66 is removed, a metal film 68 is
deposited over the entire surface of the upper interlayer
insulating film 65 such that the openings 67 for plugs are filled
therewith. Then, an unneeded portion of the metal film 68 located
on the upper interlayer insulating film 65 is removed by CMP so
that connection plugs 69 composed of the metal film 68 are
formed.
[0197] Instead of the openings 67 for plugs, grooves for
interconnection may also be formed in the upper interlayer
insulating film 65. In the arrangement, a buried interconnect is
formed in the upper interlayer insulating film 65 in place of the
connection plugs 69.
[0198] If the individual process steps described above are
repeatedly performed, a multi-layer interconnection structure
having the planar upper interlayer insulating films 65 in the
individual layers can be formed, though it is not depicted.
[0199] According to the eighth embodiment, the upper interlayer
insulating film 65 without a global step can be formed so that a
reduction in focal depth margin resulting from a step can be
suppressed in the step of forming a mask pattern on the upper
interlayer insulating film 65 by lithographic technology. This
achieves a significant increase in processing margin (process
window), compared with the prior ail technology, so that a
high-precision semiconductor device is fabricated.
[0200] It will easily be appreciated that the present invention is
also applicable to a dual damascene method for forming a connection
plug and a buried interconnect simultaneously.
INDUSTRIAL APPLICABILITY
[0201] In accordance with a first method for fabricating a
semiconductor device, there can be implemented a film in which a
global step does not occur, a depressed portion with a high aspect
ratio is filled completely, and no unburied portion is formed.
[0202] In accordance with a second method for fabricating a
semiconductor device, an insulating film without a global step can
be formed so that a reduction in focal depth margin resulting from
a step is suppressed in the step of forming a mask pattern on an
insulating film by lithographic technology. This achieves a
significant increase in processing margin (process window),
compared with the prior art technology, so that a high-precision
semiconductor device is fabricated.
* * * * *