U.S. patent application number 15/438383 was filed with the patent office on 2018-08-23 for patterned sidewall smoothing using a pre-smoothed inverted tone pattern.
The applicant listed for this patent is International Business Machines Corporation. Invention is credited to Kafai Lai, Hari V. Mallela, Hiroyuki Miyazoe, Reinaldo A. Vega, Rajasekhar Venigalla.
Application Number | 20180240892 15/438383 |
Document ID | / |
Family ID | 63167608 |
Filed Date | 2018-08-23 |
United States Patent
Application |
20180240892 |
Kind Code |
A1 |
Lai; Kafai ; et al. |
August 23, 2018 |
PATTERNED SIDEWALL SMOOTHING USING A PRE-SMOOTHED INVERTED TONE
PATTERN
Abstract
Embodiments are directed to a method and resulting structures
for smoothing the sidewall roughness of a post-etched film. A
sacrificial layer is formed on a substrate. A patterned mask is
formed by removing portions of the sacrificial layer to expose a
surface of the substrate. The sidewalls of the patterned mask are
smoothed and a target layer is formed over the patterned mask and
the substrate. Portions of the target layer are removed to expose a
surface of the patterned mask and the patterned mask is
removed.
Inventors: |
Lai; Kafai; (Poughkeepsie,
NY) ; Mallela; Hari V.; (Poughquag, NY) ;
Miyazoe; Hiroyuki; (White Plains, NY) ; Vega;
Reinaldo A.; (Mahopac, NY) ; Venigalla;
Rajasekhar; (Hopewell Junction, NY) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
International Business Machines Corporation |
Armonk |
NY |
US |
|
|
Family ID: |
63167608 |
Appl. No.: |
15/438383 |
Filed: |
February 21, 2017 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
H01L 29/161 20130101;
H01L 29/66795 20130101; H01L 29/165 20130101; H01L 29/785 20130101;
H01L 21/0331 20130101; H01L 27/0924 20130101; H01L 21/823821
20130101 |
International
Class: |
H01L 29/66 20060101
H01L029/66; H01L 29/78 20060101 H01L029/78; H01L 21/308 20060101
H01L021/308; H01L 29/161 20060101 H01L029/161 |
Claims
1. A method for forming a semiconductor device, the method
comprising: forming a sacrificial layer on a substrate; forming a
patterned mask by removing portions of the sacrificial layer to
expose a surface of the substrate, thereby forming one or more
cavities in the sacrificial layer at one or more locations where
the surface of the substrate is exposed; smoothing sidewalls of the
patterned mask; forming a target layer over the patterned mask and
the substrate, such that the target layer completely fills in the
one or more cavities; removing portions of the target layer to
expose a surface of the patterned mask; and removing the patterned
mask.
2. The method of claim 1, wherein after smoothing the sidewalls of
the patterned mask each sidewall of the patterned mask comprises a
one sigma root-mean-square (RMS) roughness of less than about 10
atomic layers, or less than about 3 nm.
3. The method of claim 1, wherein after smoothing the sidewalls of
the patterned mask each sidewall of the patterned mask comprises a
one sigma root-mean-square (RMS) roughness of less than about 3
atomic layers, or less than about 1 nm.
4. The method of claim 1, wherein smoothing sidewalls of the
patterned mask comprises a high temperature furnace annealing or a
hot mold embossing process at a temperature of greater than about
500 degrees Celsius.
5-6. (canceled)
7. The method of claim 1, wherein after removing the patterned mask
each sidewall of the target layer comprises a one sigma
root-mean-square (RMS) roughness of less than about 10 atomic
layers, or less than about 3 nm.
8. The method of claim 1, wherein after removing the patterned mask
each sidewall of the target layer comprises a one sigma
root-mean-square (RMS) roughness of less than about 3 atomic
layers, or less than about 1 nm.
9. The method of claim 1, wherein removing the patterned mask
comprises an etch selective to the target layer.
10. A method for forming a semiconductor device, the method
comprising: forming a sacrificial layer on a substrate; forming a
patterned mask by removing portions of the sacrificial layer to
expose a surface of the substrate; smoothing sidewalls of the
patterned mask; forming a semiconductor layer over the patterned
mask and the substrate; forming a semiconductor fin by removing
portions of the semiconductor layer to expose a surface of the
patterned mask; removing the patterned mask; and forming a gate
over a channel region of the semiconductor fin.
11. The method of claim 10, wherein smoothing sidewalls of the
patterned mask comprises a high temperature furnace annealing or a
hot mold embossing process at a temperature of greater than about
500 degrees Celsius.
12. The method of claim 10, wherein a sidewall angle of the
semiconductor fin after removing the patterned mask is greater than
about 90 degrees as measured from a top surface of the
semiconductor fin.
13. The method of claim 10, wherein after removing the patterned
mask each sidewall of the semiconductor fin comprises a one sigma
root-mean-square (RMS) roughness of less than about 10 atomic
layers, or less than about 3 nm.
14. The method of claim 10, wherein after removing the patterned
mask each sidewall of the semiconductor fin comprises a one sigma
root-mean-square (RMS) roughness of less than about 3 atomic
layers, or less than about 1 nm.
15. The method of claim 10, wherein removing the patterned mask
comprises an etch selective to the semiconductor fin.
16. The method of claim 10, wherein the semiconductor fin comprises
silicon germanium (SiGe).
17. The method of claim 16 further comprising forming a doped
region on the semiconductor fin and adjacent to the gate; wherein
the doped region comprises p-type dopants selected from the group
consisting of gallium (Ga), boron (B), difluoroboron (BF2), and
aluminum (Al).
18-20. (canceled)
Description
BACKGROUND
[0001] The present invention relates in general to semiconductor
and optoelectronic device fabrication methods and resulting
structures. More specifically, the present invention relates to
fabrication methods and resulting structures for smoothing the
sidewall roughness of a post-etched film.
[0002] In contemporary semiconductor device fabrication processes a
large number of microelectronic and on-chip photonics devices, such
as field effect transistors (FETs) and semiconductor optical
waveguides, respectively, are fabricated on a single wafer. FETs
are well known in the electronic arts and form the basis of modern
integrated circuit design, logic, and memory applications.
Semiconductor optical waveguides, on the other hand, are a very
important part of modern integrated optoelectronic systems,
especially for electrically active devices. Applications range from
semiconductor lasers, optical filters, switches, modulators,
isolators, and photodetectors. To increase device density, improve
performance, and decrease the power load of these devices, device
fabricators employ increasingly sophisticated fabrication
techniques that include a combination of lithography, sidewall
image transfer, spacer imaging and other processes to form final
device structures having progressively decreasing critical
dimensions.
SUMMARY
[0003] According to one or more embodiments of the present
invention, a method for smoothing the sidewall roughness of a
post-etched film is provided. The method includes forming a
sacrificial layer on a substrate. A patterned mask is formed by
removing portions of the sacrificial layer to expose a surface of
the substrate. The sidewalls of the patterned mask are smoothed,
and a target layer is formed over the patterned mask and the
substrate. Portions of the target layer are removed to expose a
surface of the patterned mask, and the patterned mask is
removed.
[0004] According to one or more embodiments of the present
invention, a method for smoothing the sidewall roughness of a
post-etched film is provided. The method includes forming a
sacrificial layer on a substrate. A patterned mask is formed by
removing portions of the sacrificial layer to expose a surface of
the substrate. Sidewalls of the patterned mask are smoothed, and a
semiconductor layer is formed over the patterned mask and the
substrate. A semiconductor fin is formed by removing portions of
the semiconductor layer to expose a surface of the patterned mask.
The patterned mask is removed, and a gate is formed over a channel
region of the semiconductor fin.
[0005] According to one or more embodiments of the present
invention, a semiconductor device having smoothed sidewalls is
provided. The structure includes a semiconductor fin formed on a
substrate and a gate formed over a channel region of the
semiconductor fin. Each sidewall of the semiconductor fin includes
a one sigma root-mean-square (RMS) roughness of less than about 10
atomic layers, or less than about 3 nanometers (nm).
BRIEF DESCRIPTION OF THE DRAWINGS
[0006] The subject matter of the present invention is particularly
pointed out and distinctly defined in the claims at the conclusion
of the specification. The foregoing and other features and
advantages are apparent from the following detailed description
taken in conjunction with the accompanying drawings in which:
[0007] FIG. 1 depicts a cross-sectional view of a structure having
a sacrificial layer formed on a substrate during an intermediate
operation of a method of fabricating a semiconductor device
according to one or more embodiments of the present invention;
[0008] FIG. 2 depicts a cross-sectional view of the structure after
patterning the sacrificial layer to form a patterned mask during an
intermediate operation of a method of fabricating a semiconductor
device according to one or more embodiments of the present
invention;
[0009] FIG. 3 depicts a cross-sectional view of the structure after
smoothing the sidewalls of the patterned mask during an
intermediate operation of a method of fabricating a semiconductor
device according to one or more embodiments of the present
invention;
[0010] FIG. 4 depicts a cross-sectional view of the structure after
smoothing the sidewalls of the patterned mask causes the sidewalls
of the patterned mask to become tapered during an intermediate
operation of a method of fabricating a semiconductor device
according to one or more embodiments of the present invention;
[0011] FIG. 5 depicts a cross-sectional view of the structure after
forming a target layer over the patterned mask and the substrate
during an intermediate operation of a method of fabricating a
semiconductor device according to one or more embodiments of the
present invention;
[0012] FIG. 6 depicts a cross-sectional view of the structure after
removing portions (i.e., the overburden) of the target layer to
form a target structure over the substrate during an intermediate
operation of a method of fabricating a semiconductor device
according to one or more embodiments of the present invention;
[0013] FIG. 7 depicts a cross-sectional view of the structure after
selectively removing the patterned mask from the substrate during
an intermediate operation of a method of fabricating a
semiconductor device according to one or more embodiments of the
present invention;
[0014] FIG. 8 depicts a cross-sectional view of the structure
having tapered sidewalls during an intermediate operation of a
method of fabricating a semiconductor device according to one or
more embodiments of the present invention;
[0015] FIG. 9 depicts a cross-sectional view of a structure along a
direction X-X' (parallel to fin direction) after forming a
semiconductor fin on a substrate during an intermediate operation
of a method of fabricating a semiconductor device according to one
or more embodiments of the present invention; and
[0016] FIG. 10 depicts a cross-sectional view of the structure of
FIG. 9 along the lines Y-Y' (fin cross section under gate) and Z-Z'
(fin cross section under source/drain) during an intermediate
operation of a method of fabricating a semiconductor device
according to one or more embodiments of the present invention.
DETAILED DESCRIPTION
[0017] Various embodiments of the present invention are described
herein with reference to the related drawings. Alternative
embodiments can be devised without departing from the scope of this
invention. It is noted that various connections and positional
relationships (e.g., over, below, adjacent, etc.) are set forth
between elements in the following description and in the drawings.
These connections and/or positional relationships, unless specified
otherwise, can be direct or indirect, and the present invention is
not intended to be limiting in this respect. Accordingly, a
coupling of entities can refer to either a direct or an indirect
coupling, and a positional relationship between entities can be a
direct or indirect positional relationship. As an example of an
indirect positional relationship, references in the present
description to forming layer "A" over layer "B" include situations
in which one or more intermediate layers (e.g., layer "C") is
between layer "A" and layer "B" as long as the relevant
characteristics and functionalities of layer "A" and layer "B" are
not substantially changed by the intermediate layer(s).
[0018] The following definitions and abbreviations are to be used
for the interpretation of the claims and the specification. As used
herein, the terms "comprises," "comprising," "includes,"
"including," "has," "having," "contains" or "containing," or any
other variation thereof, are intended to cover a non-exclusive
inclusion. For example, a composition, a mixture, process, method,
article, or apparatus that comprises a list of elements is not
necessarily limited to only those elements but can include other
elements not expressly listed or inherent to such composition,
mixture, process, method, article, or apparatus.
[0019] Additionally, the term "exemplary" is used herein to mean
"serving as an example, instance or illustration." Any embodiment
or design described herein as "exemplary" is not necessarily to be
construed as preferred or advantageous over other embodiments or
designs. The terms "at least one" and "one or more" are understood
to include any integer number greater than or equal to one, i.e.
one, two, three, four, etc. The terms "a plurality" are understood
to include any integer number greater than or equal to two, i.e.
two, three, four, five, etc. The term "connection" can include an
indirect "connection" and a direct "connection."
[0020] References in the specification to "one embodiment," "an
embodiment," "an example embodiment," etc., indicate that the
embodiment described can include a particular feature, structure,
or characteristic, but every embodiment may or may not include the
particular feature, structure, or characteristic. Moreover, such
phrases are not necessarily referring to the same embodiment.
Further, when a particular feature, structure, or characteristic is
described in connection with an embodiment, it is submitted that it
is within the knowledge of one skilled in the art to affect such
feature, structure, or characteristic in connection with other
embodiments whether or not explicitly described.
[0021] For purposes of the description hereinafter, the terms
"upper," "lower," "right," "left," "vertical," "horizontal," "top,"
"bottom," and derivatives thereof shall relate to the described
structures and methods, as oriented in the drawing figures. The
terms "overlying," "atop," "on top," "positioned on" or "positioned
atop" mean that a first element, such as a first structure, is
present on a second element, such as a second structure, wherein
intervening elements such as an interface structure can be present
between the first element and the second element. The term "direct
contact" means that a first element, such as a first structure, and
a second element, such as a second structure, are connected without
any intermediary conducting, insulating or semiconductor layers at
the interface of the two elements. The term "selective to," such
as, for example, "a first element selective to a second element,"
means that a first element can be etched and the second element can
act as an etch stop. The term "conformal" (e.g., a conformal layer)
means that the thickness of the layer is substantially the same on
all surfaces, or that the thickness variation is less than 15% of
the nominal thickness of the layer.
[0022] As used herein, the terms "about," "substantially,"
"approximately," and variations thereof are intended to include the
degree of error associated with measurement of the particular
quantity based upon the equipment available at the time of filing
the application. For example, "about" can include a range of .+-.8%
or 5%, or 2% of a given value.
[0023] For the sake of brevity, conventional techniques related to
semiconductor device and integrated circuit (IC) fabrication may or
may not be described in detail herein. Moreover, the various tasks
and process steps described herein can be incorporated into a more
comprehensive procedure or process having additional steps or
functionality not described in detail herein. In particular,
various steps in the manufacture of semiconductor devices and
semiconductor-based ICs are well known and so, in the interest of
brevity, many conventional steps will only be mentioned briefly
herein or will be omitted entirely without providing the well-known
process details.
[0024] By way of background, however, a more general description of
the semiconductor device fabrication processes that can be utilized
in implementing one or more embodiments of the present invention
will now be provided. Although specific fabrication operations used
in implementing one or more embodiments of the present invention
can be individually known, the described combination of operations
and/or resulting structures of the present invention are unique.
Thus, the unique combination of the operations described according
to the present invention utilize a variety of individually known
physical and chemical processes performed on a semiconductor (e.g.,
silicon) substrate, some of which are described in the immediately
following paragraphs.
[0025] In general, the various processes used to form a micro-chip
that will be packaged into an IC fall into four general categories,
namely, film deposition, removal/etching, semiconductor doping and
patterning/lithography. Deposition is any process that grows,
coats, or otherwise transfers a material onto the wafer. Available
technologies include physical vapor deposition (PVD), chemical
vapor deposition (CVD), plasma-enhanced chemical vapor deposition
(PECVD), electrochemical deposition (ECD), molecular beam epitaxy
(MBE), and more recently, atomic layer deposition (ALD) and
plasma-enhanced atomic layer deposition (PEALD), among others.
[0026] Removal/etching is any process that removes material from
the wafer. Examples include etch processes (either wet or dry), and
chemical-mechanical planarization (CMP), and the like. A reactive
ion etch (RIE), for example, is a type of dry etch that uses
chemically reactive plasma to remove a material, such as a masked
pattern of semiconductor material, by exposing the material to a
bombardment of ions that dislodge portions of the material from the
exposed surface. The plasma is generated under low pressure
(vacuum) by an electromagnetic field.
[0027] Semiconductor doping is the modification of electrical
properties by doping, for example, transistor sources and drains,
generally by diffusion and/or by ion implantation. These doping
processes are followed by furnace annealing or by rapid thermal
annealing (RTA). Annealing serves to activate the implanted
dopants. Films of both conductors (e.g., poly-silicon, aluminum,
copper, etc.) and insulators (e.g., various forms of silicon
dioxide, silicon nitride, etc.) are used to connect and isolate
transistors and their components. Selective doping of various
regions of the semiconductor substrate allows the conductivity of
the substrate to be changed with the application of voltage. By
creating structures of these various components, millions of
transistors can be built and wired together to form the complex
circuitry of a modern microelectronic device.
[0028] Semiconductor lithography is the formation of
three-dimensional relief images or patterns on the semiconductor
substrate for subsequent transfer of the pattern to the substrate.
In semiconductor lithography, the patterns are formed by a light
sensitive polymer called a photo-resist. To build the complex
structures that make up a transistor and the many wires that
connect the millions of transistors of a circuit, lithography and
etch pattern transfer steps are repeated multiple times. Each
pattern being printed on the wafer is aligned to the previously
formed patterns and slowly the conductors, insulators and
selectively doped regions are built up to form the final
device.
[0029] Turning now to a description of technologies that are more
specifically relevant to the present invention, as previously noted
herein, device fabricators rely on an increasingly sophisticated
combination of lithography, sidewall image transfer, spacer imaging
and other processes to form microelectronic and on-chip photonics
device structures having progressively smaller critical dimensions.
There are challenges, however, in scaling these devices beyond the
10 nm node. As semiconductor device critical dimensions
continuously scale downward, sidewall surface smoothness at
relevant scales becomes increasingly difficult to achieve. The
vertical walls of conventional non-planar finFETs, for example, are
ideally smooth on an atomic scale with a consistent fin width.
Sidewall variations (also known as sidewall roughness) can degrade
gate insulator integrity and reduce charge carrier mobility.
Sidewall roughness similarly impedes photonics devices, causing
light scattering and negatively impacting mode efficiencies,
resonator fitness, extinction ratios, modulator bandwidth, and
insertion loss.
[0030] Conventional fabrication processes for these devices
typically result in a one sigma root-mean-square (RMS) sidewall
surface roughness of a few nanometers (typically greater than about
10 atomic layers, or about 3 nm). Accordingly, various approaches
have been explored for reducing or effectively eliminating sidewall
roughness. Current sidewall surface smoothing techniques are
limited, however, to high temperature processes (e.g., high
temperature H.sub.2 annealing and hot silicon mold embossing) that
are poorly suited to temperature-sensitive applications and
materials. Hot embossing techniques are further limited in that
these processes require the removal of the final polymer structure
from the mold which introduces frictional forces that can break or
distort the structure. While post-passivation processes can
somewhat mitigate frictional coefficients, these techniques are
generally limited to the formation of polymer patterns.
[0031] Turning now to an overview of the aspects of the present
invention, one or more embodiments provide methods for smoothing
the sidewall roughness of a post-etched film. An inverted image
structure (also known as a sacrificial film) is formed on a
substrate using a wet etch, a dry etch, or a combination of
sequential wet or dry etches. Known sidewall surface smoothing
techniques are then applied to the inverted image structure (i.e.,
post-etch smoothing). A target layer is formed over the patterned
mask and the substrate. The target layer is planarized to a surface
of the patterned mask and the patterned mask is removed. In this
manner, the target layer is decoupled from the actual smoothing
process (i.e., the sidewall smoothness of the patterned mask is
effectively transferred to the target layer). Consequently, the use
of conventional high temperature sidewall smoothing processes are
restricted to the inverted image structure and subsequent
processing of the target layer can be accomplished at a much lower
temperature--allowing the process to be used in
temperature-sensitive applications and with materials unavailable
to prior art methods. Moreover, separating the target layer from
the sacrificial film using a selective etch eliminates the
introduction of frictional forces and allows for the process to be
applied to a wide range of polymers, inorganic films, and
non-polymer structures.
[0032] Example methods for smoothing the sidewall roughness of a
post-etched film and the resulting structures therefrom in
accordance with embodiments of the present invention are described
in detail below by referring to the accompanying drawings in FIGS.
1-10.
[0033] FIG. 1 illustrates a cross-sectional view of a structure 100
having a sacrificial layer 102 formed on a substrate 104 during an
intermediate operation of a method of fabricating a semiconductor
device according to one or more embodiments. In some embodiments,
the sacrificial layer 102 is formed using a CVD, PECVD, ALD, PVD,
chemical solution deposition, or other like process in combination
with a wet or dry etch process. In some embodiments, the
sacrificial layer 102 has a thickness of about 2 nm to about 50 nm,
or about 4 nm to about 50 nm, although other thicknesses are within
the contemplated scope of the invention. The sacrificial layer 102
can be made of any suitable material capable of being removed
selective to the target structure 600 (as depicted in FIG. 5), such
as, for example, a nitride, silicon nitride (SiN), or silicoboron
carbonitride (SiBCN). In some embodiments, the sacrificial layer
102 is a hard mask layer, such as, for example, silicon dioxide
(SiO.sub.2), silicon oxynitride (SiON), or silicon oxygen
carbonitride (SiOCN).
[0034] In some embodiments, the sacrificial layer 102 is an
epitaxially grown film, such as, for example, monocrystalline
silicon (Si), germanium (Ge), or silicon germanium (SiGe). In some
embodiments, the epitaxially grown films are formed from gaseous or
liquid precursors. In some embodiments, epitaxial regions are
epitaxially grown over the substrate 104.
[0035] The terms "epitaxial growth", "epitaxial deposition" and/or
"epitaxially formed and/or grown" mean the growth of a
semiconductor material (crystalline material) on a deposition
surface of another semiconductor material (crystalline material),
in which the semiconductor material being grown (crystalline
overlayer) has substantially the same crystalline characteristics
as the semiconductor material of the deposition surface (seed
material). In an epitaxial deposition process, the chemical
reactants provided by the source gases are controlled and the
system parameters are set so that the depositing atoms arrive at
the deposition surface of the semiconductor substrate with
sufficient energy to move about on the surface such that the
depositing atoms orient themselves to the crystal arrangement of
the atoms of the deposition surface. Therefore, an epitaxially
grown semiconductor material has substantially the same crystalline
characteristics as the deposition surface on which the epitaxially
grown material is formed. For example, an epitaxially grown
semiconductor material deposited on a {100} orientated crystalline
surface will take on a {100} orientation. In some embodiments,
epitaxial growth and/or deposition processes are selective to
forming on semiconductor surface, and generally do not deposit
material on exposed non-semiconductor surfaces, such as silicon
dioxide or silicon nitride surfaces.
[0036] Epitaxial semiconductor materials can be grown using
vapor-phase epitaxy (VPE), MBE, liquid-phase epitaxy (LPE), or
other suitable processes. In some embodiments, the gas source for
the deposition of epitaxial semiconductor material includes a
silicon containing gas source, a germanium containing gas source,
or a combination thereof. For example, an epitaxial silicon layer
can be deposited from a silicon gas source that is selected from
the group consisting of silane, disilane, trisilane, tetrasilane,
hexachlorodisilane, tetrachlorosilane, dichlorosilane,
trichlorosilane, methylsilane, dimethylsilane, ethylsilane,
methyldisilane, dimethyldisilane, hexamethyldisilane and
combinations thereof. An epitaxial germanium layer can be deposited
from a germanium gas source that is selected from the group
consisting of germane, digermane, halogermane, dichlorogermane,
trichlorogermane, tetrachlorogermane and combinations thereof. An
epitaxial silicon germanium alloy layer can be formed utilizing a
combination of such gas sources. Carrier gases like hydrogen,
nitrogen, helium and argon can be used.
[0037] The substrate 104 can be made of any suitable substrate
material, such as, for example, monocrystalline Si, SiGe, SiC,
III-V compound semiconductor, II-VI compound semiconductor, or
semiconductor-on-insulator (SOI). Group III-V compound
semiconductor materials include materials having at least one group
III element and at least one group V element, such as, for example,
one or more of aluminum gallium arsenide (AlGaAs), aluminum gallium
nitride (AlGaN), aluminum arsenide (AlAs), aluminum indium arsenide
(AlIAs), aluminum nitride (AlN), gallium antimonide (GaSb), gallium
aluminum antimonide (GaAlSb), gallium arsenide (GaAs), gallium
arsenide antimonide (GaAsSb), gallium nitride (GaN), indium
antimonide (InSb), indium arsenide (InAs), indium gallium arsenide
(InGaAs), indium gallium arsenide phosphide (InGaAsP), indium
gallium nitride (InGaN), indium nitride (InN), indium phosphide
(InP) and alloy combinations including at least one of the
foregoing materials. The alloy combinations can include binary (two
elements, e.g., gallium (III) arsenide (GaAs)), ternary (three
elements, e.g., InGaAs) and quaternary (four elements, e.g.,
aluminum gallium indium phosphide (AlInGaP)) alloys. Group II-VI
compound semiconductor materials include Group II elements selected
from zinc, cadmium, the alkaline earth metals (such as beryllium,
magnesium calcium, strontium, and barium, and mixtures thereof),
and Group VI elements selected from oxygen, sulfur, selenium,
tellurium, and mixtures thereof. Group II-VI semiconductor
compounds can be doped with one or more p-type dopant, such as, but
not limited to, nitrogen, phosphorus, arsenic, antimony, bismuth,
copper, chalcogenides of the foregoing, and mixtures thereof. In
some embodiments, the substrate 104 includes a buried oxide layer
(not depicted). In some embodiments, the substrate 104 includes
both an nFET region and a pFET region. In some embodiments, the
substrate 104 includes either an nFET region or a pFET region.
[0038] FIG. 2 illustrates a cross-sectional view of the structure
100 after patterning the sacrificial layer 102 to form a patterned
mask 200 during an intermediate operation of a method of
fabricating a semiconductor device according to one or more
embodiments. The patterned mask 200 is an inverted image of the
target structure 600 (as depicted in FIG. 5). The sacrificial layer
102 can be patterned using known processes, such as, for example,
lithography or wet or dry etching. In some embodiments, the
sacrificial layer 102 is patterned using a RIE selective to the
substrate 104. The patterning process results in a rough surface
202 on the sidewalls of the patterned mask 200 (i.e., the rough
surface 202 can have a 1 sigma RMS roughness of greater than about
10 atomic layers, or greater than about 3 nm).
[0039] FIG. 3 illustrates a cross-sectional view of the structure
100 after smoothing the sidewalls (i.e., removing the rough surface
202) of the patterned mask 200 during an intermediate operation of
a method of fabricating a semiconductor device according to one or
more embodiments. Any known manner for smoothing the sidewalls of a
film or polymer can be used, such as, for example, high temperature
H.sub.2 furnace annealing or hot mold embossing. The smoothing
processes (e.g., a high temperature anneal at a temperature of
greater than about 500 degrees Celsius, or greater than about 800
degrees Celsius) induces surface migration along the sidewalls of
the patterned mask 200, reducing high frequency roughness.
Consequently, a 1 sigma RMS roughness of the sidewalls of the
smoothed patterned mask 200 of less than about 10 atomic layers, or
less than about 3 nm, or less than about 3 atomic layers, or less
than about 1 nm, can be achieved.
[0040] In some embodiments, smoothing the sidewalls of the
patterned mask 200 causes the sidewalls of the patterned mask 200
to become tapered and the sidewall angle .PHI..sub.1, as depicted
in FIG. 4, can be less than about 90 degrees. The sidewall angle
.PHI..sub.1 is measured from the horizontal plane (i.e., the top
surface of the patterned mask 200).
[0041] FIG. 5 illustrates a cross-sectional view of the structure
100 after forming a target layer 500 over the patterned mask 200
and the substrate 104 during an intermediate operation of a method
of fabricating a semiconductor device according to one or more
embodiments. The target layer 500 can be formed using any known
process, such as, for example, CVD, PECVD, ALD, PVD, chemical
solution deposition, or other like process. The target layer 500
can be made of any suitable material, such as, for example,
semiconductor materials, photonics materials, polymers, and
non-polymers (e.g., monocrystalline Si, SiGe, SiC, III-V compound
semiconductor, II-VI compound semiconductor, poly methyl
methacrylate (PMMA), InP, or other suitable materials). In some
embodiments, the target layer 500 is overfilled, forming an
overburden above a surface of the patterned mask 200.
[0042] FIG. 6 illustrates a cross-sectional view of the structure
100 after removing portions (i.e., the overburden) of the target
layer 500 to form a target structure 600 over the substrate 104
during an intermediate operation of a method of fabricating a
semiconductor device according to one or more embodiments. In some
embodiments, a CMP selective to the patterned mask 200 removes the
target layer 500 overburden and exposes a top surface of the
patterned mask 200. In other embodiments, portions of the target
layer 500 are removed and a top surface of the patterned mask 200
is exposed using a wet etch, a dry etch, or a combination of
sequential wet or dry etches. In some embodiments, the wet or dry
etches are selective to the patterned mask 200.
[0043] FIG. 7 illustrates a cross-sectional view of the structure
100 after selectively removing the patterned mask 200 from the
substrate 104 during an intermediate operation of a method of
fabricating a semiconductor device according to one or more
embodiments. As discussed previously herein, the patterned mask 200
is made of a material chosen such that the patterned mask 200 can
be removed selective to the target structure 600. In this manner,
the 1 sigma RMS roughness of the sidewalls of the target structure
600 of less than about 10 atomic layers, or less than about 3 nm,
or less than about 3 atomic layers, or less than about 1 nm can be
achieved. The patterned mask 200 can be removed using any suitably
selective process, such as, for example, a wet etch selective to
the target structure 600. In some embodiments, the patterned mask
200 is removed using a hydrochloric acid (HCl) etch, which can
include a mixture of hydrochloric acid, hydrogen peroxide
(H.sub.2O.sub.2), sulfuric acid (H.sub.2SO.sub.4), and water.
[0044] In embodiments where smoothing the sidewalls of the
patterned mask 200 causes the sidewalls of the patterned mask 200
to become tapered, as depicted in FIG. 4, the sidewall angle
.PHI..sub.2 of the target structure 600 will be greater than about
90 degrees (i.e., the sidewall angle .PHI..sub.2 of the target
structure 600 will be 180 degrees--.PHI..sub.1), as depicted in
FIG. 8. The sidewall angle .PHI..sub.2 is measured from the
horizontal plane (i.e., the top surface of the target structure
600).
[0045] FIG. 9 illustrates a cross-sectional view of a structure 900
along a direction X-X' (parallel to fin direction) after forming
the target structure 600 (here referred to as a semiconductor fin
600) on the substrate 104 during an intermediate operation of a
method of fabricating a finFET semiconductor device according to
one or more embodiments of the present invention. In some
embodiments, the target structure 600 is a semiconductor fin formed
on the substrate 104 during an intermediate operation of a method
of fabricating a finFET semiconductor device according to one or
more embodiments of the present invention. In some embodiments, a
semiconductor buffer layer 902 is formed between the semiconductor
fin 600 and the substrate 104. The semiconductor buffer layer 902
can be made of any suitable material, such as, for example, Si,
SiGe, III-V compound semiconductor material, or other suitable
materials. In embodiments where the target structure 600 is an
InGaAs semiconductor fin and the substrate 104 is made of InP, for
example, the semiconductor buffer layer 902 can be made of indium
aluminum arsenide (InAlAs).
[0046] A sacrificial gate 904 is formed over channel regions of the
semiconductor fin 600. Any known method for patterning a
sacrificial gate (also known as a dummy gate) can be used, such as,
for example, a wet etch, a dry etch, or a combination of sequential
wet and/or dry etches. For example, in some embodiments, a layer of
a-Si is etched using a patterned hard mask (not depicted). In some
embodiments, hard mask 906 is formed on the sacrificial gate 904.
The hard mask 906 can be made of any suitable material, such as,
for example, a silicon nitride, silicon dioxide, SiON, SiC, SiOCN,
or SiBCN. In some embodiments, a thin silicon oxide film (not
depicted) is formed between the hard mask 906 and the sacrificial
gate 904.
[0047] The sacrificial gate 904 can be replaced with a conductive
gate (not depicted) using known finFET processes. The conductive
gate can be made of any suitable conducting material, such as, for
example, metal (e.g., tungsten, titanium, tantalum, ruthenium,
zirconium, cobalt, copper, aluminum, lead, platinum, tin, silver,
gold), conducting metallic compound material (e.g., tantalum
nitride, titanium nitride, tantalum carbide, titanium carbide,
titanium aluminum carbide, tungsten silicide, tungsten nitride,
ruthenium oxide, cobalt silicide, nickel silicide), carbon
nanotube, conductive carbon, graphene, or any suitable combination
of these materials.
[0048] In some embodiments, a high-k dielectric 908 is formed
between the conductive gate after replacing the sacrificial gate
904) and the semiconductor fin 600. In some embodiments, the high-k
dielectric 908 modifies the work function of the gate. The high-k
dielectric 908 can be made of, for example, silicon oxide, silicon
nitride, silicon oxynitride, boron nitride, high-k materials, or
any combination of these materials. Examples of high-k materials
include but are not limited to metal oxides such as hafnium oxide,
hafnium silicon oxide, hafnium silicon oxynitride, lanthanum oxide,
lanthanum aluminum oxide, zirconium oxide, zirconium silicon oxide,
zirconium silicon oxynitride, tantalum oxide, titanium oxide,
barium strontium titanium oxide, barium titanium oxide, strontium
titanium oxide, yttrium oxide, aluminum oxide, lead scandium
tantalum oxide, and lead zinc niobate. The high-k materials can
further include dopants such as lanthanum and aluminum. In some
embodiments, the high-k dielectric 908 can have a thickness of
about 0.5 nm to about 4 nm, or about 2 nm to about 3 nm, although
other thicknesses are within the contemplated scope of the
invention.
[0049] In some embodiments, work function layers (not depicted) are
formed between the high-k dielectric 908 and the conductive gate.
The work function layers can be made of work function materials,
such as, for example, aluminum, lanthanum oxide, magnesium oxide,
strontium titanate, strontium oxide, titanium nitride, titanium
aluminum nitride, titanium aluminum carbide, tantalum nitride, and
combinations thereof. In some embodiments, the work function layers
further modify the work function of the gate.
[0050] In some embodiments, spacers 910 are formed on sidewalls of
the sacrificial gate 904 and on surfaces of the semiconductor fin
600. In some embodiments, the spacers 910 are formed using a CVD,
PECVD, ALD, PVD, chemical solution deposition, or other like
process in combination with a wet or dry etch process. The spacers
910 can be made of any suitable material, such as, for example, a
low-k dielectric, a nitride, silicon nitride, silicon dioxide,
SiON, SiC, SiOCN, or SiBCN.
[0051] Doped regions 912 are formed on the semiconductor fin 600.
The doped regions 912 can be source or drain regions formed in the
substrate 104 by a variety of methods, such as, for example,
in-situ doped epitaxy, doped following the epitaxy, or by
implantation and plasma doping. In some embodiments, the doped
regions 912 are complementary, such that one of the doped regions
is a source while the other is a drain. The doped regions 912 can
be formed by any suitable process, including but not limited to,
ultrahigh vacuum chemical vapor deposition (UHVCVD), rapid thermal
chemical vapor deposition (RTCVD), metalorganic chemical vapor
deposition (MOCVD), low-pressure chemical vapor deposition (LPCVD),
limited reaction processing CVD (LRPCVD), and MBE. In some
embodiments, the doped regions 912 include epitaxial semiconductor
materials grown from gaseous or liquid precursors. In some
embodiments, epitaxial regions are epitaxially grown over the
substrate 104 and/or the semiconductor fin 600. Epitaxial
semiconductor materials can be grown using vapor-phase epitaxy
(VPE), MBE, liquid-phase epitaxy (LPE), or other suitable
processes. The doped regions 912 can be doped during deposition
(in-situ doped) by adding dopants, n-type dopants (e.g., phosphorus
or arsenic) or p-type dopants (e.g., Ga, B, BF.sub.2, or Al). The
dopant concentration in the doped regions 912 can range from
1.times.10.sup.19 cm.sup.-3 to 2.times.10.sup.21 cm.sup.-3, or
between 1.times.10.sup.20 cm.sup.-3 and 1.times.10.sup.21
cm.sup.-3.
[0052] The doped regions 912 can be made of any suitable material,
such as, for example, Si, SiGe, III-V compound semiconductor, or
other suitable materials. In some embodiments, the doped regions
912 are raised source/drain regions formed from III-V compound
semiconductor material. In some embodiments, the gas source for the
deposition of epitaxial semiconductor material includes a silicon,
a germanium, or a III-V compound semiconductor containing gas
source, or a combination thereof. For example, an epitaxial InGaAs
layer can be deposited from a gas source that is selected from the
group consisting of arsine, trimethyl indium, and trimethyl
gallium. An epitaxial germanium layer can be deposited from a
germanium gas source that is selected from the group consisting of
germane, digermane, halogermane, dichlorogermane, trichlorogermane,
tetrachlorogermane and combinations thereof. An epitaxial silicon
germanium alloy layer can be formed utilizing a combination of such
gas sources. Carrier gases like hydrogen, nitrogen, helium and
argon can be used. In some embodiments, the doped regions 912
include silicon. In some embodiments, the doped regions 912 include
carbon doped silicon (Si:C). This Si:C layer can be grown in the
same chamber used for other epitaxy steps or in a dedicated Si:C
epitaxy chamber. The Si:C can include carbon in the range of about
0.2 percent to about 3.0 percent.
[0053] Conductive contacts (gate contacts and source/drain
contacts, not depicted) can be formed or deposited using known
finFET metallization techniques. In some embodiments, an interlayer
dielectric (ILD, not depicted) is patterned with open trenches and
the contacts are deposited into the trenches. In some embodiments,
the contacts are overfilled into the trenches, forming overburdens
above a surface of the ILD. In some embodiments, a CMP selective to
the ILD removes the overburden. The contacts can be made of any
suitable conducting material, such as, for example, metal (e.g.,
tungsten, titanium, tantalum, ruthenium, zirconium, cobalt, copper,
aluminum, lead, platinum, tin, silver, gold), conducting metallic
compound material (e.g., tantalum nitride, titanium nitride,
tantalum carbide, titanium carbide, titanium aluminum carbide,
tungsten silicide, tungsten nitride, ruthenium oxide, cobalt
silicide, nickel silicide), carbon nanotube, conductive carbon,
graphene, or any suitable combination of these materials. The
conductive material can further include dopants that are
incorporated during or after deposition. In some embodiments, the
contacts can be copper and can include a barrier metal liner. The
barrier metal liner prevents the copper from diffusing into, or
doping, the surrounding materials, which can degrade their
properties. Silicon, for example, forms deep-level traps when doped
with copper. An ideal barrier metal liner must limit copper
diffusivity sufficiently to chemically isolate the copper conductor
from the surrounding materials and should have a high electrical
conductivity, for example, tantalum nitride and tantalum (TaN/Ta),
titanium, titanium nitride, cobalt, ruthenium, and manganese.
[0054] FIG. 10 illustrates a cross-sectional view of the structure
900 along the lines Y-Y' (fin cross section under gate) and Z-Z'
(fin cross section under source/drain) of FIG. 9 during an
intermediate operation of a method of fabricating a semiconductor
device according to one or more embodiments of the present
invention. In some embodiments, a dielectric layer 1000 is formed
on a surface of the substrate 104. The dielectric layer 1000 can be
made of any suitable dielectric material, such as, for example,
porous silicates, carbon doped oxides, silicon dioxide, silicon
nitrides, silicon oxynitrides, or other dielectric materials. Any
known manner of forming the dielectric layer 1000 can be utilized.
The dielectric layer 1000 can be formed using, for example, CVD,
PECVD, ALD, flowable CVD, spin-on dielectrics, or PVD. In some
embodiments, the dielectric layer 1000 is a shallow trench
isolation (STI) region. The STI region prevents electrical current
leak between adjacent semiconductor device components.
[0055] The descriptions of the various embodiments of the present
invention have been presented for purposes of illustration, but are
not intended to be exhaustive or limited to the embodiments
described. Many modifications and variations will be apparent to
those of ordinary skill in the art without departing from the scope
and spirit of the invention. The terminology used herein was chosen
to best explain the principles of the embodiment, the practical
application or technical improvement over technologies found in the
marketplace, or to enable others of ordinary skill in the art to
understand the embodiments described herein.
* * * * *