U.S. patent application number 14/885080 was filed with the patent office on 2016-02-11 for etching of under bump metallization layer and resulting device.
The applicant listed for this patent is GLOBALFOUNDRIES Inc.. Invention is credited to Tanya Andreeva ATANASOVA, Anh Ngoc DUONG, Reiner WILLEKE.
Application Number | 20160043046 14/885080 |
Document ID | / |
Family ID | 53731534 |
Filed Date | 2016-02-11 |
United States Patent
Application |
20160043046 |
Kind Code |
A1 |
ATANASOVA; Tanya Andreeva ;
et al. |
February 11, 2016 |
ETCHING OF UNDER BUMP METALLIZATION LAYER AND RESULTING DEVICE
Abstract
Methods for wet etching a UBM layer and the resulting devices
are disclosed. Embodiments may include patterning metal bumps on a
wafer that has at least two metal layers thereon; exposing the
wafer to a first acid solution to remove a portion of a first of
the two metal layers exposed by the patterning of the metal bumps;
and exposing the wafer to a second acid solution to remove a
portion a second of the two metal layers exposed by the patterning
of the metal bumps and the exposure of the wafer to the first acid
solution, wherein an undercut below the metal bumps, formed by
removal of the portions of the first and second metal layers, is
less than 1.5 microns.
Inventors: |
ATANASOVA; Tanya Andreeva;
(Dresden, DE) ; WILLEKE; Reiner; (Dresden, DE)
; DUONG; Anh Ngoc; (Fremont, CA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
GLOBALFOUNDRIES Inc. |
Grand Cayman |
|
KY |
|
|
Family ID: |
53731534 |
Appl. No.: |
14/885080 |
Filed: |
October 16, 2015 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
14172323 |
Feb 4, 2014 |
9214436 |
|
|
14885080 |
|
|
|
|
Current U.S.
Class: |
257/737 |
Current CPC
Class: |
H01L 2224/13147
20130101; C23F 1/44 20130101; H01L 2224/05655 20130101; H01L
2224/13139 20130101; H01L 2224/0345 20130101; H01L 2224/03912
20130101; H01L 2924/20102 20130101; H01L 2224/05073 20130101; H01L
2224/0345 20130101; H01L 2924/206 20130101; H01L 2924/2064
20130101; H01L 2224/13016 20130101; H01L 2224/11831 20130101; H01L
2224/13147 20130101; H01L 2224/05073 20130101; H01L 2224/05655
20130101; H01L 2224/0381 20130101; H01L 2224/11614 20130101; H01L
24/11 20130101; H01L 2224/05147 20130101; H01L 24/03 20130101; H01L
24/13 20130101; C23F 1/26 20130101; H01L 2224/11462 20130101; H01L
2224/13111 20130101; H01L 2924/0549 20130101; H01L 2224/05572
20130101; H01L 2224/13082 20130101; H01L 2224/05166 20130101; H01L
2224/05647 20130101; H01L 2224/05027 20130101; H01L 2224/1145
20130101; H01L 2224/05082 20130101; H01L 2224/13111 20130101; H01L
2224/0361 20130101; H01L 2224/03614 20130101; H01L 21/32134
20130101; H01L 2224/13166 20130101; H01L 2224/1181 20130101; H01L
2924/0531 20130101; H01L 24/05 20130101; H01L 2224/05082 20130101;
H01L 2224/05016 20130101; H01L 2224/05147 20130101; H01L 2224/05027
20130101; H01L 2224/05166 20130101; H01L 2224/05647 20130101; H01L
2224/13155 20130101; C23F 1/18 20130101; H01L 2924/00014 20130101;
H01L 2224/05166 20130101; H01L 2924/00014 20130101; H01L 2924/00014
20130101; H01L 2924/01047 20130101; H01L 2924/00014 20130101; H01L
2224/13023 20130101; H01L 2224/05572 20130101; H01L 2224/0401
20130101; H01L 2224/03462 20130101; H01L 2924/00014 20130101; H01L
2924/00014 20130101; H01L 2924/00014 20130101; H01L 2224/05166
20130101; H01L 2224/05655 20130101; H01L 2924/00014 20130101; H01L
2224/05147 20130101; H01L 2924/00014 20130101; H01L 2224/05647
20130101 |
International
Class: |
H01L 23/00 20060101
H01L023/00 |
Claims
1. A device comprising: a substrate; a metal seat layer above the
substrate; and a metal bump above the metal seat layer, wherein the
metal seat layer is formed by a wet etch of an under bump
metallization layer and an undercut of the metal seat layer below
the metal bump is less than 1.5 microns (.mu.m).
2. The device according to claim 1, wherein the metal seat layer
comprises a copper (Cu) layer above a titanium (Ti) layer.
3. The device according to claim 2, wherein the copper layer has a
thickness of 200 to 400 nanometers (nm).
4. The device according to claim 2, wherein the titanium layer has
a thickness of 100 to 200 nm.
5. The device according to claim 1, wherein the undercut of the
metal seat layer below the metal bump is 1 .mu.m.
6. A device comprising: a wafer; a metal seat layer above the
wafer, the metal seat layer including a first and second metal
layer; and a metal bump above the metal seat layer, wherein the
metal seat layer is formed by a wet etch of an under bump
metallization layer and an undercut of the metal seat layer etched
back past an edge of a bottom portion of the metal bump is between
1 and 1.5 microns (.mu.m).
7. The device according to claim 6, wherein the first metal layer
comprises copper (Cu) and is formed over the second metal layer
comprising titanium (Ti).
8. The device according to claim 7, wherein the first metal layer
has a thickness of 200 to 400 nanometers (nm).
9. The device according to claim 7, wherein the second metal layer
has a thickness of 100 to 200 nm.
10. The device according to claim 6, wherein the undercut of the
metal seat layer below the metal bump is 1 .mu.m.
11. The device according to claim 6, wherein the bottom portion of
the metal bump comprises nickel (Ni).
12. The device according to claim 11, wherein the bottom portion of
the metal bump is formed to a thickness of 2.7 to 3.3 microns.
13. The device according to claim 6, wherein the metal bump
comprises a top portion formed over the bottom portion.
14. The device according to claim 13, wherein the top portion
comprises tin (Sn) and silver (Ag).
15. The device according to claim 14, wherein the Sn to Ag ratio is
98:2.
16. The device according to claim 6, wherein the metal bump is
formed to a height of 63 to 77 .mu.m.
17. The device according to claim 16, wherein the metal bump is
formed to a width of 50 to 70 .mu.m.
18. A device comprising: a wafer; a metal seat layer above the
wafer, the metal seat layer including a first metal layer
comprising copper (Cu) formed over a second metal layer comprising
titanium (Ti); and a metal bump formed above the metal seat layer,
the metal bump comprising a top portion and bottom portion, wherein
the metal seat layer is formed by a wet etch of an under bump
metallization layer and an undercut of the metal seat layer etched
back past an edge of the bottom portion of the metal bump is
between 1 and 1.5 microns (.mu.m).
19. The device according to claim 18, wherein the first metal layer
has a thickness of 200 to 400 nanometers (nm).
20. The device according to claim 18, wherein the second metal
layer has a thickness of 100 to 200 nm.
Description
RELATED APPLICATION
[0001] The present application is a Divisional application of
application Ser. No. 14/172,323, filed on Feb. 4, 2014, which is
incorporated herein by reference in its entirety.
TECHNICAL FIELD
[0002] The present disclosure relates to fabrication of a metal
bump, and particularly to reducing the undercut of a metal bump
resulting from etching an under bump metallization (UBM) layer. The
present disclosure is particularly applicable to 20 nanometer (nm)
technology nodes and beyond.
BACKGROUND
[0003] UBM layers may be dry or wet etched to prevent shorts. Wet
etching may be preferred over dry etching because no additional
cleaning of etch residue is required. Wet etching costs also are
less than dry etching. However, wet etching etches beneath mushroom
plated metal bumps causing an undercut.
[0004] More specifically, UBM wet etching removes exposed metal
layers that are masked either by a photoresist, such as in a solder
paste process, or that are masked by a metal bump, such as in an
electroplated solder process. Two issues that are addressed for a
successful UBM etch are complete metal layer removal where left
exposed and control of the undercut caused by undesirably removing
the UBM layer from beneath the metal bump.
[0005] Current wet etching solutions that include sulfuric acid
(H.sub.2SO.sub.4), hydrogen peroxide (H.sub.2O.sub.2), and water,
followed by dilute hydrofluoric acid (HF) cause 2.5 to 3 microns of
undercut of the metal bumps. Such a large amount of undercut
reduces the stability of the metal bump. Further, the current wet
etching solutions also attack layers of the metal bump, such as
nickel or aluminum layers.
[0006] A need, therefore, exists for a method of wet etching a UBM
layer that creates a smaller undercut of a metal bump and the
resulting device.
SUMMARY
[0007] An aspect of the present disclosure is a method of wet
etching a UBM layer that creates an undercut of a metal bump of
less than 1.5 microns.
[0008] Another aspect of the present disclosure is a device having
an undercut of a metal bump of less than 1.5 microns.
[0009] Additional aspects and other features of the present
disclosure will be set forth in the description which follows and
in part will be apparent to those having ordinary skill in the art
upon examination of the following or may be learned from the
practice of the present disclosure. The advantages of the present
disclosure may be realized and obtained as particularly pointed out
in the appended claims.
[0010] According to the present disclosure, some technical effects
may be achieved in part by a method including patterning metal
bumps on a wafer that has at least two metal layers thereon;
exposing the wafer to a first acid solution to remove a portion of
a first of the two metal layers exposed by the patterning of the
metal bumps; and exposing the wafer to a second acid solution to
remove a portion of a second of the two metal layers exposed by the
patterning of the metal bumps and the exposure of the wafer to the
first acid solution, wherein an undercut below the metal bumps,
formed by removal of the portions of the first and second metal
layers, is less than 1.5 microns.
[0011] An aspect of the present disclosure includes the first acid
solution including phosphoric acid (H.sub.3PO.sub.4),
H.sub.2O.sub.2, and water. Another aspect includes the first acid
solution including 0.07% to 0.36% by volume of the H.sub.3PO.sub.4,
0.1% to 0.7% by volume of the H.sub.2O.sub.2, and the water for a
remainder of the volume. A further aspect includes exposing the
wafer to the first acid solution for 30 to 60 seconds at 30.degree.
to 40.degree. C. An additional aspect includes the second acid
solution including dilute HF, HF in an organic solvent, or a
mixture of ammonia, H.sub.2O.sub.2, fluorine and water (APFM). Yet
another aspect includes the second acid solution including 0.1% to
0.49% by volume of the HF with water for a remainder of the volume.
Still another aspect includes exposing the wafer to the second acid
solution for 20 to 40 seconds at 20.degree. to 25.degree. C. An
additional aspect includes rinsing the wafer with deionized water
after exposure with the second acid solution for 60 to 120 seconds
at 20.degree. to 25.degree. C. Another aspect includes the undercut
formed by removal of the portion of the metal layers below the
metal bumps being 1 micron. A further aspect includes the first and
second metal layers including a copper (Cu) layer having a
thickness of 200 to 400 nanometers (nm) and a titanium (Ti) layer
having a thickness of 100 to 200 nm, respectively, and the portions
of the Cu layer and the Ti layer are completely removed after
exposure to the first acid solution and the second acid solution.
Still another aspect includes the metal bumps including a first Cu
layer and the metal layers including a second Cu layer, and the
first acid solution is selective to the second Cu layer over the
first Cu layer. A further aspect includes forming the first Cu
layer by electrochemical deposition (ECD) of Cu; and forming the
second copper layer by physical vapor deposition (PVD) of the
copper.
[0012] Another aspect of the present disclosure is a device
including: a substrate; a metal seat layer above the substrate; and
a metal bump above the metal seat layer, wherein the metal seat
layer is formed by a wet etch of a UBM layer and an undercut of the
metal seat layer below the metal bump is less than 1.5 microns.
[0013] Aspects include the metal seat layer including a Cu layer
above a Ti layer. A further aspect includes the Cu layer having a
thickness of 200 to 400 nm. Another aspect includes the Ti layer
having a thickness of 100 to 200 nm. A further aspect includes the
undercut of the metal seat layer below the metal bump being 1
micron.
[0014] Another aspect of the present disclosure includes a method
including patterning metal bumps on a UBM layer on a wafer;
performing a first wet etch of the under bump metallization layer
on the wafer with a solution including 0.07% to 0.36% by volume of
H.sub.3PO.sub.4, 0.1% to 0.7% by volume of H.sub.2O.sub.2, and
water for a remainder of the volume; rinsing the wafer with
deionized water for 60 to 120 seconds at 20.degree. to 25.degree.
C.; performing a second wet etch of the UBM layer with a solution
including 0.1% to 0.49% by volume of HF with water for a remainder
of the volume; and rinsing the wafer with deionized water for 60 to
120 seconds at 20.degree. to 25.degree. C., wherein an undercut of
the UBM layer under the metal bumps formed by removing the UBM
layer exposed by the metal bumps is 1 micron.
[0015] A further aspect includes the UBM layer including a Cu layer
having a thickness of 200 to 400 nanometers and a Ti layer having a
thickness of 100 to 200 nm, and the Cu layer and the Ti layer are
completely removed where exposed by the metal bumps after the first
wet etch and the second wet etch.
[0016] Additional aspects and technical effects of the present
disclosure will become readily apparent to those skilled in the art
from the following detailed description wherein embodiments of the
present disclosure are described simply by way of illustration of
the best mode contemplated to carry out the present disclosure. As
will be realized, the present disclosure is capable of other and
different embodiments, and its several details are capable of
modifications in various obvious respects, all without departing
from the present disclosure. Accordingly, the drawings and
description are to be regarded as illustrative in nature, and not
as restrictive.
BRIEF DESCRIPTION OF THE DRAWINGS
[0017] The present disclosure is illustrated by way of example, and
not by way of limitation, in the figures of the accompanying
drawings and in which like reference numerals refer to similar
elements and in which:
[0018] FIGS. 1 through 6 schematically illustrate a method for wet
etching a UBM layer to create an undercut of less than 1.5 microns,
in which FIG. 6 illustrates a detailed portion of FIG. 5, in
accordance with an exemplary embodiment.
DETAILED DESCRIPTION
[0019] In the following description, for the purposes of
explanation, numerous specific details are set forth in order to
provide a thorough understanding of exemplary embodiments. It
should be apparent, however, that exemplary embodiments may be
practiced without these specific details or with an equivalent
arrangement. In other instances, well-known structures and devices
are shown in block diagram form in order to avoid unnecessarily
obscuring exemplary embodiments. In addition, unless otherwise
indicated, all numbers expressing quantities, ratios, and numerical
properties of ingredients, reaction conditions, and so forth used
in the specification and claims are to be understood as being
modified in all instances by the term "about."
[0020] The present disclosure addresses and solves the current
problem of an undercut of metal bumps attendant upon wet etching a
UBM layer. In accordance with embodiments of the present
disclosure, acid solutions are used that create an undercut beneath
the metal bumps of less than 1.5 microns.
[0021] Methodology in accordance with an embodiment of the present
disclosure includes patterning metal bumps of a wafer that has at
least two metal layers thereon, such as a UBM layer. The wafer is
then exposed to a first acid solution to remove a portion of a
first of the two metal layers exposed by the patterning of the
metal bumps. The wafer is then exposed to a second acid solution to
remove a portion of a second of the two metal layers exposed by the
patterning of the metal bumps and the exposure of the wafer to the
first acid solution. As a result, an undercut below the metal
bumps, formed by removal of the portions of the first and second
metal layers, is less than 1.5 microns.
[0022] Adverting to FIG. 1, a method for wet etching a UBM layer,
according to an exemplary embodiment, begins with a wafer 101.
Although illustrated as a single layer, the wafer 101 may include
other layers (not shown for illustrative convenience), such as a
polyimide layer. The wafer 101 may further include a metal layer
103 and a metal layer 105. The metal layer 103 may be formed of Ti,
e.g., to a thickness of 90 to 110 nm, such as 100 nm. The metal
layer 105 may be formed of Cu, e.g., to a thickness of 270 to 330
nm, such as 300 nm. Together, the metal layer 103 and the metal
layer 105 may constitute a UBM layer.
[0023] Above the metal layer 105 is a metal bump 111. The metal
bump 111 may be formed to a height of 63 to 77 microns, such as 70
microns, and to a width of 50 to 70 microns, such as 60 microns.
The metal bump 111 includes a bottom portion 107 and a top portion
109. The bottom portion may be formed of nickel (Ni) to a thickness
of 2.7 to 3.3 microns, such as 3 microns. The top portion 109 may
be formed of tin and silver (SnAg), for example, with a ratio of Sn
to Ag of 98:2. Alternatively, the metal bump 111 may be formed of
Cu with a thin portion of SnAg above the Cu (not shown for
illustrative convenience). When the metal bump 111 is formed of Cu,
the Cu of the metal bump 111 may be formed by ECD and the Cu of the
metal layer 105 may be formed by PVD. The metal bump 111 may
further be one of multiple metal bumps that are patterned above the
metal layer 105.
[0024] Adverting to FIG. 2, the metal bump 111 and the metal layer
105 are exposed to an acid solution 201. The acid solution 201 may
include H.sub.3PO.sub.4, H.sub.2O.sub.2, and water. More
specifically, the acid solution 201 may include 0.07% to 0.36% by
volume of the H.sub.3PO.sub.4, 0.1% to 0.7% by volume of the
H.sub.2O.sub.2, and the water for a remainder of the volume. Within
the acid solution 201, the H.sub.2O.sub.2 acts as a buffer to
control the etching of the layers on the wafer 101. The metal bump
111 and the metal layer 105 may be exposed to the acid solution 201
for 30 to 60 seconds at 30.degree. to 40.degree. C. using a batch
or single spray tool.
[0025] As illustrated in FIG. 3, the acid solution 201 completely
removes a portion of the metal layer 105 exposed by the patterning
of the metal bump 111 forming an etched metal layer 301.
Subsequently, the etched metal layer 301 and the metal bump 111 are
rinsed with deionized water 303 to stop the etching and wash away
remaining etchant residue. The rinse of deionized water 303 may be
for 60 to 120 seconds at 20.degree. to 25.degree. C.
[0026] Adverting to FIG. 4, the metal bump 111, the etched metal
layer 301 and the metal layer 103, where exposed by the etched
metal layer 301 are exposed to another acid solution 401. The acid
solution 401 may include dilute HF, HF in an organic solvent, or a
mixture of APFM. Specifically, the acid solution 401 may include
0.1% to 0.49% by volume of the HF with water for a remainder of the
volume. Alternatively, the acid solution 401 may include HF in
ethyleneglycol. The metal bump 111, the etched metal layer 301, and
the metal layer 103 exposed by the etched metal layer 301 may be
exposed to the acid solution 401 for 30 to 60 seconds at 30.degree.
to 40.degree. C.
[0027] As illustrated in FIG. 5, the acid solution 401 completely
removes a portion of the metal layer 103 exposed by the etched
metal layer 301 forming an etched metal layer 501. Subsequently,
the etched metal layer 501, the etched metal layer 301 and the
metal bump 111 are again rinsed with deionized water 503 to stop
the etching and wash away any remaining etchant residue. The rinse
of deionized water 503 may be for 60 to 120 seconds at 20.degree.
to 25.degree. C. using a batch or single spray tool.
[0028] The encircled portion 505 of FIG. 5 is illustrated in
greater detail in FIG. 6, which illustrates the undercut 601 formed
by the metal layer 103 and the metal layer 105 being etched back
past the edge of the bottom portion 107 of the metal bump 111.
Based on the chemistry of the two acid solutions 201 and 401, the
undercut is less than 1.5 microns. The undercut may more
specifically be 1 micron, or even less than 1 micron. An undercut
of less than 1.5 microns, as compared to an undercut of 2.5 to 3
microns, which is formed by conventional wet etchants, creates a
more stable metal bump 111. Further, the two acid solutions 201 and
401 do not attack the bottom portion 107 of the metal bump 111
formed of Ni or, alternatively, Al if present in the metal bump
111. The two acid solutions 201 and 401, particularly the first
acid solution 201, also exhibit selectivity for Cu layers formed by
PVD rather than ECD, such that metal bumps that are formed of Cu
deposited by PVD are selectively etched more than Cu deposited by
ECD.
[0029] The embodiments of the present disclosure achieve several
technical effects, including an undercut of a metal bump being less
than 1.5 microns. The present disclosure enjoys industrial
applicability associated with the designing and manufacturing of
any of various types of highly integrated semiconductor devices
used in microprocessors, smart phones, mobile phones, cellular
handsets, set-top boxes, DVD recorders and players, automotive
navigation, printers and peripherals, networking and telecom
equipment, gaming systems, and digital cameras, particularly for 20
nm technology nodes and beyond.
[0030] In the preceding description, the present disclosure is
described with reference to specifically exemplary embodiments
thereof. It will, however, be evident that various modifications
and changes may be made thereto without departing from the broader
spirit and scope of the present disclosure, as set forth in the
claims. The specification and drawings are, accordingly, to be
regarded as illustrative and not as restrictive. It is understood
that the present disclosure is capable of using various other
combinations and embodiments and is capable of any changes or
modifications within the scope of the inventive concept as
expressed herein.
* * * * *