U.S. patent application number 14/633508 was filed with the patent office on 2015-07-02 for compact localized rram cell structure realized by spacer technology.
The applicant listed for this patent is GLOBALFOUNDRIES Singapore Pte. Ltd.. Invention is credited to Elgin QUEK, Shyue Seng TAN, Eng Huat TOH.
Application Number | 20150188047 14/633508 |
Document ID | / |
Family ID | 50727068 |
Filed Date | 2015-07-02 |
United States Patent
Application |
20150188047 |
Kind Code |
A1 |
TAN; Shyue Seng ; et
al. |
July 2, 2015 |
COMPACT LOCALIZED RRAM CELL STRUCTURE REALIZED BY SPACER
TECHNOLOGY
Abstract
An RRAM is disclosed with a vertical BJT selector. Embodiments
include defining a STI region in a substrate, implanting dopants in
the substrate to form a first polarity well around and below a
bottom portion of the STI region, a second polarity channel over
the well on opposite sides of the STI region, and a first polarity
active area over each channel at the surface of the substrate,
forming an RRAM liner on the active area and STI region, forming a
sacrificial top electrode on the RRAM liner, forming spacers on
opposite sides of the sacrificial top electrode, implanting a
second polarity dopant in the active area on opposite sides of the
sacrificial top electrode, forming a silicon oxide adjacent the
spacers, removing at least a portion of the sacrificial top
electrode forming a cavity, forming in the cavity inner spacers
adjacent the spacers and a top electrode.
Inventors: |
TAN; Shyue Seng; (Singapore,
SG) ; TOH; Eng Huat; (Singapore, SG) ; QUEK;
Elgin; (Singapore, SG) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
GLOBALFOUNDRIES Singapore Pte. Ltd. |
Singapore |
|
SG |
|
|
Family ID: |
50727068 |
Appl. No.: |
14/633508 |
Filed: |
February 27, 2015 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
13683779 |
Nov 21, 2012 |
8993407 |
|
|
14633508 |
|
|
|
|
Current U.S.
Class: |
257/4 |
Current CPC
Class: |
H01L 45/1675 20130101;
H01L 45/08 20130101; H01L 45/1233 20130101; H01L 45/1691 20130101;
H01L 27/2463 20130101; H01L 27/2445 20130101; H01L 45/1253
20130101; H01L 45/146 20130101 |
International
Class: |
H01L 45/00 20060101
H01L045/00 |
Claims
1. A device comprising: a substrate; a well of a first polarity in
the substrate; a shallow trench isolation (STI) region formed in
the substrate extending partially into the well; a channel of a
second polarity in the substrate, over the well, at opposite sides
of the STI region; an active area of the first polarity in the
substrate over the channel at opposite sides of the STI region; an
RRAM liner on the active area and STI region; a top electrode on
the RRAM liner; spacers on opposite sides of the RRAM liner and top
electrode; and doped regions of the second polarity in the
substrate adjacent the spacers, laterally remote from the RRAM
liner.
2. The device according to claim 1, wherein the RRAM liner
comprises an oxide of a transition metal.
3. The device according to claim 1, wherein a thickness of the RRAM
liner is 1 nm to 100 nm.
4. The device according to claim 1, wherein the top electrode
comprises a transition metal, titanium nitride (TiN), TiN/Ti, or
polysilicon.
5. The device according to claim 1, wherein each spacer comprises a
top section and a bottom section, the device further comprising
inner spacers on the RRAM liner, adjacent the bottom section of the
spacers, wherein the top electrode is between the inner spacers and
between the top sections of the spacers.
6. The device according to claim 1, wherein each spacer comprises a
top section and a bottom section, the device further comprising:
fins on the RRAM liner adjacent the bottom section of the spacers;
and inner spacers on the fins adjacent the top section of the
spacers, wherein the top electrode is between the inner spacers and
between the fins.
7. The device according to claim 1, wherein each spacer comprises a
top section and a bottom section, wherein the top electrode
comprises a portion adjacent the bottom section of each spacer, the
device further comprising: an interlayer dielectric (ILD) between
the top electrode portions; and a metal layer above the top
electrode portions and the ILD, between the top portions of the
spacers.
8. The device according to claim 2, wherein the RRAM liner
comprises nickel oxide (NiOx), aluminum oxide (AlOx), hafnium oxide
(HfOx), tungsten oxide (WOx), tantalum oxide (TaOx), vanadium oxide
(VOx), or copper oxide (CuOx), or a combination thereof.
9. The device according to claim 1, wherein the STI regions extend
in a first direction and the RRAM liner extends in a second
direction perpendicular to the first direction.
10. The device according to claim 5, wherein the inner spacers
comprise silicon dioxide (SiO2) that has been etched.
11. A device comprising: a substrate; a shallow trench isolation
(STI) region in the substrate; a well in the substrate formed by
implanting dopants in the substrate, the well having a first
polarity around and below a bottom portion of the STI region; a
channel having a second polarity, the channel located over the well
on opposite sides of the STI region; an active area of the first
polarity over each channel of second polarity at the surface of the
substrate; an RRAM liner on the active area and the STI region; a
top electrode on the RRAM liner; spacers on opposite sides of the
top electrode and RRAM liner, wherein a dopant of the second
polarity is implanted in the active area on opposite sides of the
top electrode; and a silicon oxide adjacent the spacers.
12. The device according to claim 11, further comprising: a first
cavity formed in the top electrode; and inner spacers, adjacent the
spacers, in the cavity.
13. The device according to claim 12, further comprising: a second
cavity below the inner spacers, the second cavity filled with an
interlayer dielectric; and metal filling the first cavity.
14. The device according to claim 11, wherein the STI regions
extend in a first direction and the RRAM liner extends in a second
direction perpendicular to the first direction.
15. The device according to claim 11, wherein the first cavity is
within the top one third of the top electrode.
16. The device according to claim 11, wherein the RRAM liner has a
thickness of 1 nanometer (nm) to 100 nm.
17. The device according to claim 11, wherein the RRAM liner
comprises an oxide of a transition metal.
18. The device according to claim 11, wherein the inner spacers
comprise silicon dioxide (SiO2) that has been etched.
19. The device according to claim 17, wherein the RRAM liner
comprises nickel oxide (NiOx), aluminum oxide (AlOx), hafnium oxide
(HfOx), tungsten oxide (WOx), tantalum oxide (TaOx), vanadium oxide
(VOx), or copper oxide (CuOx), or a combination thereof.
20. The device according to claim 17, wherein the RRAM liner is
formed of multiple layers.
Description
CROSS-REFERENCE TO RELATED APPLICATION
[0001] This application is a Divisional of U.S. application Ser.
No. 13/683,779, filed Nov. 21, 2012, the content of which is
incorporated herein by reference in its entirety.
TECHNICAL FIELD
[0002] The present disclosure relates to semiconductor memories.
The present disclosure is particularly applicable to nonvolatile
resistive random access memories (RRAMs).
BACKGROUND
[0003] Present flash technologies have encountered significant
challenges for scaling such as scaling of program/erase (P/E)
voltage, speed, reliability, and high densities with non-volatile
data. Attempts to solve such issues have included employing RRAMs
due to their scalability, highly competitive speed, endurance, and
retention properties. However, RRAMs suffer from poor resistance
uniformity, smaller memory margin, and poor performance
back-end-of-line (BEOL) cell selectors.
[0004] The poor resistance distribution has been attributed to more
filament current paths in a planar device, which leads to increased
variations between set and reset, since some cells give more
current paths than others. Single transistor single resistor (1T1R)
RRAMs, which are desirably bipolar and have a high access current,
also have a large cell size of 8F.sup.2 or higher, are not easily
scalable, and have a planar memory margin. Single diode single
resistor (1D1R) RRAMs, on the other hand, have a smaller cell size
of 4F.sup.2 or higher, and are easily scalable, but are unipolar,
have a low access current, and have a planar memory margin. In
addition, 1D1R RRAMs employ metal oxide diodes or organic diodes,
which are compatible with back-end-of-line (BEOL) processes because
of processing temperatures less than 400.degree. C. However, the
diodes of such materials are not tunable, have inferior diode
performance (i.e., low forward current due to large band-gap),
which leads to larger cell area and a high Vdd of 3 to 4.5 V, which
is not compatible with low Vdd technology.
[0005] Attempts to improve the resistance distribution include a
plug bottom electrode instead of a planar bottom electrode to limit
the number of filament current paths for memory cells. The plug
bottom electrode improves reset current distribution and memory
margin by a factor of about four. However, RRAMs using bottom plugs
are not easily scalable.
[0006] A need therefore exists for methodology enabling fabrication
of easily scalable RRAMs which have a small cell size, bipolar
access, and improved resistance distribution and memory margin, and
the resulting product.
SUMMARY
[0007] An aspect of the present disclosure is a method of
fabricating a compact RRAM using a vertical bipolar junction
transistor (BJT) as an access device.
[0008] Another aspect of the present disclosure is a compact RRAM
using a vertical BJT as an access device.
[0009] Additional aspects and other features of the present
disclosure will be set forth in the description which follows and
in part will be apparent to those having ordinary skill in the art
upon examination of the following or may be learned from the
practice of the present disclosure. The advantages of the present
disclosure may be realized and obtained as particularly pointed out
in the appended claims.
[0010] According to the present disclosure, some technical effects
may be achieved in part by a method including: defining a shallow
trench isolation (STI) region in a substrate; implanting dopants in
the substrate to form a well of a first polarity around and below a
bottom portion of the STI region, a channel of a second polarity
over the well on opposite sides of the STI region, and an active
area of the first polarity over each channel of second polarity at
the surface of the substrate; forming an RRAM liner on the active
area and STI region; forming a sacrificial top electrode on the
RRAM liner; forming spacers on opposite sides of the sacrificial
top electrode and RRAM liner; implanting a dopant of the second
polarity in the active area on opposite sides of the sacrificial
top electrode; forming a silicon oxide adjacent the spacers;
removing at least a portion of the sacrificial top electrode,
forming a cavity; forming inner spacers, adjacent the spacers, in
the cavity; and forming a top electrode in the cavity.
[0011] Aspects of the present disclosure include forming the STI
regions extending in a first direction and forming the RRAM liner
extending in a second direction perpendicular to the first
direction. Other aspects include removing all of the sacrificial
top electrode prior to forming the inner spacers; and forming the
inner spacers adjacent a bottom section of the spacers. Further
aspects include removing one third of the sacrificial top electrode
prior to forming the inner spacers; forming the inner spacers
adjacent a top section of the spacers; etching fins below the
spacers subsequent to forming the inner spacers; and forming the
top electrode subsequent to etching the fins. Another aspect
includes forming the RRAM liner to a thickness of 1 nanometer (nm)
to 100 nm. Additional aspects include the RRAM liner including an
oxide of a transition metal. Other aspects include forming the
inner spacers by: conformally depositing SiO.sub.2; and blanket
etching the SiO.sub.2.
[0012] Another aspect of the present disclosure is a method
including: defining a shallow trench isolation (STI) region in a
substrate; implanting dopants in the substrate to form a well of a
first polarity around and below a bottom portion of the STI region,
a channel of a second polarity over the well on opposite sides of
the STI region, and an active area of the first polarity over each
channel of second polarity at the surface of the substrate; forming
an RRAM liner on the active area and STI region; forming a top
electrode on the RRAM liner; forming spacers on opposite sides of
the top electrode and RRAM liner; implanting a dopant of the second
polarity in the active area on opposite sides of the top electrode;
forming a silicon oxide adjacent the spacers; removing a portion of
the top electrode, forming a first cavity; forming inner spacers,
adjacent the spacers, in the cavity; etching fins below the inner
spacers, forming a second cavity; filling the second cavity with an
interlayer dielectric; removing the inner spacers; and filling the
first cavity with metal.
[0013] Aspects include forming the STI regions extending in a first
direction and forming the RRAM liner extending in a second
direction perpendicular to the first direction. Further aspects
include removing one third of the top electrode to form the first
cavity. Other aspects include forming the RRAM liner to a thickness
of 1 nanometer (nm) to 100 nm. Another aspect includes the RRAM
liner including an oxide of a transition metal. Additional aspects
include forming the inner spacers by: conformally depositing
SiO.sub.2; and blanket etching the SiO.sub.2.
[0014] Another aspect of the present disclosure is a device
including: a substrate; a well of a first polarity in the
substrate; a shallow trench isolation (STI) region formed in the
substrate extending partially into the well; a channel of a second
polarity in the substrate, over the well, at opposite sides of the
STI region; an active area of the first polarity in the substrate
over the channel at opposite sides of the STI region; an RRAM liner
on the active area and STI region; a top electrode on the RRAM
liner; spacers on opposite sides of the RRAM liner and top
electrode; and doped regions of the second polarity in the
substrate adjacent the spacers, laterally remote from the RRAM
liner.
[0015] Aspects include a device having an RRAM liner including an
oxide of a transition metal. A further aspect includes a thickness
of the RRAM liner being 1 nm to 100 nm. Another aspect a device
including a top electrode, with the top electrode including a
transition metal, titanium nitride (TiN), TiN/Ti, or polysilicon.
Additional aspects include a device having spacers, with each
spacer including a top section and a bottom section, the device
further including inner spacers on the RRAM liner, adjacent the
bottom section of the spacers, wherein the top electrode is between
the inner spacers and between the top sections of the spacers.
Other aspects include a device having spacers, with each spacer
including a top section and a bottom section, the device further
including: fins on the RRAM liner adjacent the bottom section of
the spacers; and inner spacers on the fins adjacent the top section
of the spacers, wherein the top electrode is between the inner
spacers and between the fins. Further aspects include a device
having a top electrode and spacers, with each spacer including a
top section and a bottom section, wherein the top electrode
includes a portion adjacent the bottom section of each spacer, the
device further including: an interlayer dielectric (ILD) between
the top electrode portions; and a metal layer above the top
electrode portions and the ILD, between the top portions of the
spacers.
[0016] Additional aspects and technical effects of the present
disclosure will become readily apparent to those skilled in the art
from the following detailed description wherein embodiments of the
present disclosure are described simply by way of illustration of
the best mode contemplated to carry out the present disclosure. As
will be realized, the present disclosure is capable of other and
different embodiments, and its several details are capable of
modifications in various obvious respects, all without departing
from the present disclosure. Accordingly, the drawings and
description are to be regarded as illustrative in nature, and not
as restrictive.
BRIEF DESCRIPTION OF THE DRAWINGS
[0017] The present disclosure is illustrated by way of example, and
not by way of limitation, in the figures of the accompanying
drawing and in which like reference numerals refer to similar
elements and in which:
[0018] FIGS. 1A through 6A and 1B through 6B schematically
illustrate top views and cross-sectional views, respectively, of a
process flow, in accordance with an exemplary embodiment;
[0019] FIGS. 7A through 7E schematically illustrate cross-sectional
views of a process flow, in accordance with another exemplary
embodiment;
[0020] FIGS. 8A through 8B schematically illustrate cross-sectional
views of a process flow, in accordance with another exemplary
embodiment; and
[0021] FIGS. 9A through 9C schematically illustrate a layout scheme
for the structures formed by the processes of the first and second
embodiments.
DETAILED DESCRIPTION
[0022] In the following description, for the purposes of
explanation, numerous specific details are set forth in order to
provide a thorough understanding of exemplary embodiments. It
should be apparent, however, that exemplary embodiments may be
practiced without these specific details or with an equivalent
arrangement. In other instances, well-known structures and devices
are shown in block diagram form in order to avoid unnecessarily
obscuring exemplary embodiments. In addition, unless otherwise
indicated, all numbers expressing quantities, ratios, and numerical
properties of ingredients, reaction conditions, and so forth used
in the specification and claims are to be understood as being
modified in all instances by the term "about."
[0023] The present disclosure addresses and solves the current
problems of difficult scalability, low access current, large cell
size and/or unipolarity, as well as poor resistance uniformity and
smaller memory margin attendant upon fabricating a 1T1R or a 1D1R
RRAM. In accordance with embodiments of the present disclosure, a
compact RRAM is formed using a vertical BJT.
[0024] Methodology in accordance with embodiments of the present
disclosure includes defining an STI region in a substrate and
implanting dopants in the substrate to form a well of a first
polarity around and below a bottom portion of the STI region, a
channel of a second polarity over the well on opposite sides of the
STI region, and an active area of the first polarity over each
channel of second polarity at the surface of the substrate. Next,
an RRAM liner is formed on the active area and STI region. A
sacrificial top electrode is then formed on the RRAM liner. After
spacers are formed on opposite sides of the sacrificial top
electrode and RRAM liner, a dopant of the second polarity is
implanted in the active area on opposite sides of the sacrificial
top electrode. Silicon oxide is formed adjacent the spacers, and at
least a portion of the sacrificial top electrode is removed,
forming a cavity Inner spacers are then formed, adjacent the
spacers, in the cavity, and a top electrode is formed in the
cavity.
[0025] Still other aspects, features, and technical effects will be
readily apparent to those skilled in this art from the following
detailed description, wherein preferred embodiments are shown and
described, simply by way of illustration of the best mode
contemplated. The disclosure is capable of other and different
embodiments, and its several details are capable of modifications
in various obvious respects. Accordingly, the drawings and
description are to be regarded as illustrative in nature, and not
as restrictive.
[0026] FIGS. 1A through 6A schematically illustrate a top view for
a process flow in accordance with an exemplary embodiment, and
FIGS. 1B through 6B schematically illustrate corresponding
cross-sectional views of the process flow. Adverting to FIGS. 1A
and 1B, STI regions 103 are defined on a P-type substrate 101. The
STI regions may be formed to a depth of 100 nanometer (nm) to 800
nm and to a width of 30 nm to 100 nm, depending on the technology
node, and may be formed, for example, of SiO.sub.2, silicon nitride
(Si.sub.3N.sub.4), or silicon oxynitride (SiON). N-wells 105 are
formed around the bottom portions of the STI regions by implanting
N-type dopants (e.g., phosphorus (P), arsenic (As), etc.) at a
dosage of 1E11 to 5E12 with an energy of 50 keV to 300 keV
depending on the STI depth and type of dopant. Next, a P-channel
107 is formed over the N-wells on opposite sides of the STI region
by implanting P-type dopant (e.g., boron (B), boron difluoride
(BF.sub.2), indium (In), etc.) at a dosage of 1E12 to 1E14 and with
an energy of 5 keV to 20 keV. Then, a shallower N-type implant is
performed over the P-channel on opposite sides of the STI region by
implanting N-type dopants (e.g., P, As, etc.) at a dosage of 1E12
to 1E14 and with an energy of 1 keV to 10 keV, forming N-type
active area 109.
[0027] As illustrated in FIGS. 2A and 2B, RRAM liners 201 and
sacrificial top electrodes 203 are deposited and patterned on the
N-type active area 109 and STI regions 103, perpendicular thereto.
RRAM liner 201 may be formed of nickel oxide (NiO.sub.x), aluminum
oxide (AlO.sub.x), hafnium oxide (HfO.sub.x), tungsten oxide
(WO.sub.x), tantalum oxide (TaO.sub.x), vanadium oxide (VO.sub.x),
and copper oxide (CuO.sub.x), or a combination thereof. The RRAM
liner 201 may be formed to a thickness of 1 nm to 100 nm.
Sacrificial top electrodes 203 may be formed of amorphous silicon
(a-Si) or polysilicon (poly-Si), with a height of 50 nm to 500 nm,
and a width of 20 nm to 1 .mu.m and a length of 20 nm to 1 .mu.m.
Alternatively, the RRAM liner 201 may be formed of multiple layers
(not shown for illustrative convenience). For example, the RRAM
liner may include a bottom electrode formed on and perpendicular to
the N-type active area 109 and STI regions 102, an interface
material formed on the bottom electrode, and the RRAM material
itself formed on the interface material.
[0028] Next, self-aligned Si.sub.3N.sub.4 spacers 301 are formed on
opposite sides of each sacrificial top electrode 203, as
illustrated in FIGS. 3A and 3B. Subsequently, a P-type dopant
(e.g., B, BF.sub.2, In, etc.) is implanted between the spacers at a
dosage of 1E12 to 1E14 and with an energy of 1 keV to 20 keV to
form P-type regions 303. Alternatively, a multiple P-type implant
with different energy depths can be used to form P-type regions
303. The dopants are then activated, for example by a micro-second
anneal or a rapid thermal anneal (RTA) at a temperature of
1100.degree. C. to 1250.degree. C.
[0029] Adverting to FIGS. 4A and 4B, SiO.sub.2 401 is deposited
over the entire substrate, filling the gaps between spacers 301.
Then, chemical mechanical polishing (CMP) is performed, stopping on
sacrificial top electrode 203.
[0030] As illustrated in FIGS. 5A and 5B, sacrificial top
electrodes 203 are then removed by a wet etch or dry etch process,
forming cavities 501. Other surfaces are protected by SiO.sub.2 401
during the etching of sacrificial top electrodes 203. SiO.sub.2 is
then conformally deposited, for example by chemical vapor
deposition (CVD) or atomic layer deposition (ALD). The thickness of
the SiO.sub.2 may be optimized to less than or equal to one third
of the opening for cavity 501. The SiO.sub.2 is then etched back,
with a blanket etch, to form inner spacers 503.
[0031] As shown in FIGS. 6A and 6B, a top electrode material is
deposited, filling the cavities 501. CMP is performed, stopping on
SiO.sub.2 401, forming top electrodes 601. Top electrode 601 may,
for example, be formed of platinum (Pt), titanium nitride (TiN),
TiN/titanium (Ti), ruthenium (Ru), nickel (Ni), tungsten (W),
aluminum (Al), copper (Cu), or polysilicon. Then, remaining
SiO.sub.2 is optionally removed, and back-end-of-line (BEOL)
processing may continue.
[0032] Alternatively, instead of RRAM liner 201 being formed prior
to sacrificial top electrode 203, a bottom electrode (not shown for
illustrative convenience) may be formed on the N-type active area
109 and STI regions 103, perpendicular thereto. The above process
flow may then continue through formation of inner spacers 503 (with
the bottom electrode instead of RRAM liner 201). Then, RRAM liner
201 may be deposited on the bottom electrode, and top electrode 601
may be formed on RRAM liner 201, filling the rest of cavity
501.
[0033] FIGS. 7A through 7E schematically illustrate cross-sectional
views of a process flow, in accordance with another exemplary
embodiment. Adverting to FIG. 7A, after SiO.sub.2 401 is deposited
and CMP is performed, as illustrated in FIGS. 4A and 4B, the
sacrificial top electrode 203 is partially removed, forming cavity
701. For example, cavity 701 may be formed to a depth of about one
third the thickness of the sacrificial top electrode.
[0034] As illustrated in FIG. 7B, a spacer material 703, such as
SiO.sub.2, SiON, or Si.sub.3N.sub.4, is conformally deposited to a
thickness about one third the width of cavity 701. Inner spacers
705 are then etched, as illustrated in FIG. 7C.
[0035] Adverting to FIG. 7D, sacrificial top electrode 203 is
etched using inner spacers 705 as a mask to form fins 707. The gap
formed between the fins 707 and the remainder of cavity 701 are
then filled with a top electrode 709, as illustrated in FIG. 7E.
Remaining SiO.sub.2 is optionally removed, and back-end-of-line
(BEOL) processing may continue.
[0036] Cross-sectional views of a process flow, in accordance with
another exemplary embodiment, are illustrated in FIGS. 8A through
8B. The process begins substantially the same as the second
embodiment except that a top electrode, for example of Pt, TiN,
TiN/Ti, Ru, Ni, W, Al, Cu, or polysilicon, is formed on RRAM liner
201, etched back, and formed into fins 801, instead of sacrificial
top electrode 203, as illustrated in FIG. 8A.
[0037] Adverting to FIG. 8B, the gap formed between fins 801 is
filled with an ILD 803, and the gap between inner spacers 705 is
filled with a metal 805. Then, remaining SiO.sub.2 is optionally
removed, and back-end-of-line (BEOL) processing may continue.
[0038] A layout of RRAMs of FIGS. 6A and 6B is illustrated in FIGS.
9A through 9C. As shown in FIGS. 9A through 9C, a first word line
901 is connected to the P-type region 303 on one side of STI region
103, and a second word line 903 is connected to the P-type region
303 on the other side of STI region 103. A first bit line 905 is
connected to a first top electrode 601, and a second bit line 909
is connected to a second top electrode 601. A select line 907 is
formed in N-well 105. For a unit cell, the width 911 of top
electrode 601 and the width 913 of P-type region 303 is F. The unit
cell area is therefore 2F.times.2F=4F.sup.2, which yields a high
density memory cell.
[0039] Read, set, and reset operations of the RRAM at the STI can
be achieved by passing current through selected BJTs and RRAM. For
example, for a read operation, a high read voltage may be applied
to the selected bit line, a select read voltage may be applied to
the selected word line, and a low voltage may be applied to the
select line. Similarly, for a set operation, a high set voltage may
be applied to the selected bit line, a select set voltage may be
applied to the selected word line, and a low voltage may be applied
to the select line. For reset operations, a select reset voltage
may be applied to the selected word line. Then, for a unipolar
reset operation, a high reset voltage may be applied to the
selected bit line and a low voltage may be applied to the select
line, whereas for a bipolar operation, a low reset voltage may be
applied to the selected bit line and a high voltage may be applied
to the select line. In addition, for forming operations, a high
forming voltage may be applied to the selected bit line, a select
forming voltage may be applied to the selected word line, and a low
voltage may be applied to the select line. For all forming, read,
set, and reset operations, unselected word lines and unselected bit
lines may be floating.
[0040] The embodiments of the present disclosure can achieve
several technical effects, such as a localized structure which
enables limited filament current paths to control distribution
which in turn improves the memory margin, direct bipolar access to
the RRAM with a high access current through a high performance
silicon-based selector (the BJT), increased scalability being
independent from the gate oxide and gate length, compatibility with
front-end-of-line (FEOL) processes, and high density with a
smallest unit cell area of 4F.sup.2. Further, the structure can be
easily controlled by mature processes such as implantation and
spacer techniques. Embodiments of the present disclosure enjoy
utility in various industrial applications as, for example,
microprocessors, smart phones, mobile phones, cellular handsets,
set-top boxes, DVD recorders and players, automotive navigation,
printers and peripherals, networking and telecom equipment, gaming
systems, digital cameras, or in any memory product. The present
disclosure therefore enjoys industrial applicability in any of
various types of highly integrated semiconductor devices.
[0041] In the preceding description, the present disclosure is
described with reference to specifically exemplary embodiments
thereof. It will, however, be evident that various modifications
and changes may be made thereto without departing from the broader
spirit and scope of the present disclosure, as set forth in the
claims. The specification and drawings are, accordingly, to be
regarded as illustrative and not as restrictive. It is understood
that the present disclosure is capable of using various other
combinations and embodiments and is capable of any changes or
modifications within the scope of the inventive concept as
expressed herein.
* * * * *