U.S. patent application number 13/821020 was filed with the patent office on 2013-06-27 for thermoform labeling.
This patent application is currently assigned to AVERY DENNISON CORPORATION. The applicant listed for this patent is Farid F. Ghiam, Kevin O. Henderson, Victor P. Holbert, Michael Zajaczkowski. Invention is credited to Farid F. Ghiam, Kevin O. Henderson, Victor P. Holbert, Michael Zajaczkowski.
Application Number | 20130164502 13/821020 |
Document ID | / |
Family ID | 44652030 |
Filed Date | 2013-06-27 |
United States Patent
Application |
20130164502 |
Kind Code |
A1 |
Ghiam; Farid F. ; et
al. |
June 27, 2013 |
Thermoform Labeling
Abstract
Processes for forming a thermoformed labeled article are
described. Labels are attached to a sheet to be thermoformed or to
a section thereof. Label attachment can optionally use an adhesive.
If the label material is completely or partially compatible with
the sheet then the use of adhesive may not be necessary. The labels
may also receive various graphics or other designs, such as by
printing. After appropriate placement of the label relative to the
sheet, the assembly of both sheet and label is thermoformed. After
thermoforming, a finished and labeled article is produced. Also
described are various labels and label assemblies which are
uniquely suited for use in the processes described herein.
Inventors: |
Ghiam; Farid F.; (Beachwood,
OH) ; Holbert; Victor P.; (Newbury, OH) ;
Zajaczkowski; Michael; (Bellefonte, PA) ; Henderson;
Kevin O.; (Willoughby Hills, OH) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Ghiam; Farid F.
Holbert; Victor P.
Zajaczkowski; Michael
Henderson; Kevin O. |
Beachwood
Newbury
Bellefonte
Willoughby Hills |
OH
OH
PA
OH |
US
US
US
US |
|
|
Assignee: |
AVERY DENNISON CORPORATION
Pasadena
CA
|
Family ID: |
44652030 |
Appl. No.: |
13/821020 |
Filed: |
September 8, 2011 |
PCT Filed: |
September 8, 2011 |
PCT NO: |
PCT/US11/50896 |
371 Date: |
March 6, 2013 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
61381015 |
Sep 8, 2010 |
|
|
|
Current U.S.
Class: |
428/187 ;
156/196; 428/343 |
Current CPC
Class: |
B32B 27/08 20130101;
Y10T 428/24736 20150115; B32B 27/32 20130101; B29C 2043/185
20130101; B32B 2519/00 20130101; B32B 2307/7244 20130101; B32B
2307/75 20130101; Y10T 156/1002 20150115; B32B 27/10 20130101; B29C
51/16 20130101; B29C 43/28 20130101; B32B 27/12 20130101; B32B
27/308 20130101; B32B 38/145 20130101; B29C 51/02 20130101; Y10T
428/28 20150115; B29C 43/30 20130101; B29C 43/00 20130101; B32B
27/34 20130101; B29C 43/14 20130101 |
Class at
Publication: |
428/187 ;
156/196; 428/343 |
International
Class: |
B29C 51/16 20060101
B29C051/16 |
Claims
1. A method for producing a labeled article, the method comprising:
providing a thermoforming apparatus having a thermoform surface;
providing a label defining a first face and a second face; forming
a visual design on at least one of the first face and the second
face of the label; providing a sheet defining a first face and a
second face; positioning the label along one of the first and
second faces of the sheet to form an article intermediate;
immediately thermoforming the article intermediate using the
thermoforming apparatus, whereby the article intermediate deforms
to the thermoform surface to thereby form the labeled article.
2. The method of claim 1, further comprising: cooling the labeled
article; removing the labeled article from the thermoforming
apparatus.
3. The method of claim 1, further comprising: attaching the label
to the sheet.
4. (canceled)
5. The method of claim 1, wherein forming a visual design on the
label is performed by: printing an ink on the label to form the
visual design.
6.-9. (canceled)
10. The method of claim 1, wherein thermoforming includes: heating
at least one of the label, the sheet, and the article intermediate;
and contacting the article intermediate with the thermoform
surface.
11. The method of claim 1, wherein the sheet includes a material
selected from the group consisting of polymeric materials,
paper-based materials, and composite materials.
12. The method of claim 11, wherein the sheet includes a polymeric
material.
13. The method of claim 11, wherein the polymeric material in the
sheet is selected from the group consisting of polystyrene,
poly(ethylene terephthalate), poly(ethylene terephthalate glycol),
polyacrylates, polycarbonates, polyolefins, and combinations
thereof.
14. The method of claim 13, wherein the polymeric material in the
sheet is polyolefin.
15. The method of claim 14, wherein the polyolefin is selected from
the group consisting of polyethylene, polypropylene, and
combinations thereof.
16. The method of claim 1, wherein the label includes a polymeric
material.
17.-19. (canceled)
20. The method of claim 1, wherein the label includes at least one
functional additive.
21. The method of claim 20, wherein the functional additive is
selected from the group consisting of barrier agent(s),
colorant(s), UV resistant agent(s), fragrance agent(s), light
enhancement agent(s), gloss promoting agent(s), gloss reducing
agent(s), and combinations thereof.
22. The method of claim 1, wherein the label is free of functional
additives.
23. The method of claim 1, wherein the labeled article defines an
outer face and the label partially covers the outer face.
24. The method of claim 1, wherein the labeled article defines an
outer face and the label entirely covers the outer face.
25. The labeled thermoformed article produced by the method of
claim 1.
26. A method of forming a labeled article, the method comprising:
providing a polymeric sheet, the sheet including a first material;
providing a polymeric label, the label including a second material;
printing a visual design on the label; attaching the label
alongside the sheet to form an article intermediate; immediately
thermoforming the article intermediate to thereby form the labeled
article.
27.-29. (canceled)
30. The method of claim 26, further comprising: cooling the labeled
article.
31.-35. (canceled)
36. The method of claim 26, wherein the thermoforming operation
includes: heating at least one of the label, the sheet, and the
article intermediate.
37. The method of claim 26, wherein printing on the label occurs
before attaching the label.
38. The method of claim 26, wherein attaching the label occurs
before printing on the label.
39. The method of claim 26, wherein the first material in the sheet
is selected from the group consisting of polystyrene, poly(ethylene
terephthalate), poly(ethylene terephthalate glycol), polyacrylates,
polycarbonates, polyolefins, and combinations thereof.
40. The method of claim 39, wherein the first material in the sheet
is polyolefin.
41. The method of claim 40, wherein the polyolefin is selected from
the group consisting of polyethylene, polypropylene, and
combinations thereof.
42. The method of claim 26, wherein the label includes at least one
functional additive.
43. The method of claim 42, wherein the functional additive is
selected from the group consisting of barrier agent(s),
colorant(s), UV resistant agent(s), fragrance agent(s), light
enhancement agent(s), gloss promoting agent(s), gloss reducing
agent(s), and combinations thereof.
44. The method of claim 26, wherein the label is free of functional
additives.
45. The method of claim 26, wherein the labeled article defines an
outer face and the label partially covers the outer face.
46. The method of claim 26, wherein the labeled article defines an
outer face and the label entirely covers the outer face.
47. The labeled article produced by the method of claim 26.
48.-69. (canceled)
70. A label adapted for placement on a sheet and concurrently
thermoforming the label and the sheet, the label comprising: at
least one layer of a polymeric film defining an underside; and a
layer of an adhesive disposed on the underside of the polymeric
film; wherein the material of the polymeric film has a softening
point, the material of the sheet has a softening point, and the
difference between the softening point of the material of the
polymeric film and the softening point of the sheet is less than
10.degree. C.
Description
CROSS REFERENCES TO RELATED APPLICATIONS
[0001] The present application claims priority from U.S.
Provisional Application No. 61/381,015 filed Sep. 8, 2010, which is
incorporated herein by reference in its entirety.
FIELD OF THE INVENTION
[0002] The present invention relates to methods for labeling a
sheet and then thermoforming the labeled sheet to obtain a labeled
finished article. The invention also relates to labels and
combinations of labeled sheets which are thermoformed.
BACKGROUND OF THE INVENTION
[0003] A wide array of consumer goods and retail products are
packaged in containers or articles that are produced by
thermoforming. Such thermoformed articles are typically labeled
after they are formed. To produce a thermoformed article, a
polymeric sheet or film is first heated to its softening point.
Once the sheet or film becomes pliable, the sheet is positioned
into a mold cavity by application of vacuum to a side of the sheet
while the sheet is appropriately positioned relative to the mold.
Alternatively, a male member can be used to urge or otherwise
position the sheet into the female mold cavity. In either
technique, the heated and pliable sheet is pressed or otherwise
drawn to matingly contact the mold cavity. As a result, the sheet
adopts a desired configuration corresponding to that of the mold
cavity. After cooling, the formed article is removed from the
cavity. The article is then subsequently labeled in a separate
operation either by the thermoforming manufacturer or by a third
party such as a convertor or end user downstream. These
conventional processes are generally satisfactory. However,
requiring separate labeling operations to produce a final labeled
article increases production costs, complexity, and inventory.
[0004] In-mold labeling techniques are also known in which a label
is incorporated into an article during thermoforming of the
article. In these methods, labels are placed or otherwise
positioned in the mold cavity. Upon contact with the heated article
during thermoforming, the label is then affixed to the article.
In-mold labeling techniques suffer from several disadvantages and
may require special molding equipment, practices, and controls to
accommodate placement and retention of labels within the molding
cavity.
[0005] Alternatively, another technique is known in which label
markings or indicia are incorporated into a sheet or film assembly
prior to thermoforming. In this technique, a preprinted formable
web is manufactured by first reverse printing one ply of a
multilayer formable web and then adhesively laminating the reverse
printed film to a second layer of the same (or different) material
in an offline lamination process to produce a finished formable web
that is provided to the thermoforming operation as a finished roll.
This technique offers certain advantages, however does not remedy
all of the disadvantages associated with conventional or other
known thermoforming and labeling operations.
[0006] Therefore, a need remains for a strategy for readily
producing a labeled finished thermoformed article. Specifically, a
need exists for a method of thermoforming to produce a finished and
labeled article, in which the method does not require any
pre-lamination operations involving one or more layers. It would be
particularly desirable to provide a method for producing a finished
and labeled article in a single continuous process.
SUMMARY OF THE INVENTION
[0007] The difficulties and drawbacks associated with previously
known practices are addressed in the present methods for producing
a finished and labeled thermoformed article.
[0008] In one aspect, the present invention provides a method for
producing a labeled article. The method comprises providing a
thermoforming apparatus having a thermoform surface, and providing
a label defining a first face and a second face. The method also
comprises forming a visual design on at least one of the first face
and the second face of the label. The method additionally comprises
providing a sheet defining a first face and a second face. And, the
method comprises positioning the label along one of the first and
second faces of the sheet to form an article intermediate. In
addition, the method comprises immediately thermoforming the
article intermediate using the thermoforming apparatus, whereby the
article intermediate deforms to the thermoform surface to thereby
form the labeled article.
[0009] In another aspect, the invention provides a method of
forming a labeled article. The method comprises providing a
polymeric sheet and a polymeric label. The sheet includes a first
material, and the label includes a second material. The method also
comprises printing a visual design on the label. The method
additionally comprises attaching the label alongside the sheet to
form an article intermediate. And, the method comprises immediately
thermoforming the article intermediate to thereby form the labeled
article.
[0010] In yet another aspect, the invention provides a label
adapted for placement on a sheet and concurrently thermoformed
therewith. The label comprises at least one layer of a polymeric
film which defines an underside and a layer of an adhesive disposed
on the underside of the polymeric film. The various materials are
selected such that the material of the polymeric film has a
softening point, the material of the sheet has a softening point,
and the difference between the softening point of the material of
the polymeric film and the softening point of the sheet is less
than 10.degree. C.
[0011] As will be realized, the invention is capable of other and
different embodiments and its several details are capable of
modifications in various respects, all without departing from the
invention. Accordingly, the drawing and description are to be
regarded as illustrative and not restrictive.
BRIEF DESCRIPTION OF THE DRAWINGS
[0012] FIG. 1 is a schematic depiction of a preferred embodiment
method for producing a labeled thermoformed article in accordance
with the present invention.
[0013] FIG. 2 is a schematic illustration of a preferred labeling
configuration in accordance with the present invention.
[0014] FIG. 3 is a schematic illustration of another preferred
labeling configuration in accordance with the present
invention.
[0015] FIG. 4 is a schematic illustration of yet another preferred
labeling configuration in accordance with the present
invention.
[0016] FIG. 5 is a schematic cross sectional view of a preferred
embodiment label assembly according to the present invention.
[0017] FIG. 6 is a schematic cross sectional view of another
preferred embodiment label assembly according to the present
invention.
[0018] FIG. 7 is a schematic cross sectional view of another
preferred embodiment label assembly according to the present
invention.
DETAILED DESCRIPTION OF THE EMBODIMENTS
[0019] The present invention provides various methods for producing
a labeled and finished thermoformed article. The methods avoid the
use of an offline pre-lamination process. In the present invention,
a label is attached or positioned and retained in place in a
desired area of a base sheet or film which forms the article. The
label is preferably attached or positioned immediately prior to
thermoforming. Most preferably, the label is printed immediately
prior to thermoforming and typically, prior to attachment or
positioning of the label relative to the base sheet or film. During
thermoforming, the thermoforming heat softens the label and the
sheet, and the label becomes pliable and stretches with the sheet
while the article is being formed. Upon completion of the
thermoforming operation, the finished article includes all desired
labeling, thereby eliminating the need for an additional step of
labeling.
[0020] In the preferred embodiments described herein, containers or
decorative items of nearly any shape can be labeled in their
entirety. For instance, a semi-circular thermoformed container can
be labeled using the preferred embodiment methods. In contrast, it
is generally not possible to label such containers in their
entirety after formation by conventional thermoforming and
application of a pressure sensitive label. This is because pressure
sensitive labels will not uniformly wrap around a container with
sharp curves or a complex geometrical shape. Many other advantages
of the preferred embodiment techniques exist as compared to
traditional practices involving labeling of thermoformed pieces.
For example, these advantages include but are not limited to late
stage differentiation for articles, inventory reduction of
articles, increased flexibility for end users such as when changing
from one shelf-keeping unit (SKU) to another, ease of promotional
product preparation, and cost reduction.
[0021] The present invention also provides various labels and label
assemblies which are particularly useful in conjunction with the
methods described herein and/or in forming various labeled
containers, packages, and/or substrates.
Sheet or Film of the Article
[0022] A wide array of materials can be used for the sheet(s) or
film(s) that receive labels and which are then subjected to
thermoforming to form the article(s) of interest. For example,
polymeric films or sheets made from standard thermoformable
materials and their blends such as polystyrene (PS), poly(ethylene
terephthalate) (PET), poly(ethylene terephthalate glycol) (PETG),
acrylic polymers, polycarbonates, polyethylene or other
polyolefins, or other polymers and combinations thereof typically
used in thermoforming in applications such as trays, food/vegetable
packages, cups, decorative or functional items, etc. are all
suitable for the preferred embodiment methods.
[0023] Additional specific examples of polymeric materials suitable
for the sheet or film to be thermoformed include polypropylene and
modified polypropylene. When thermoforming polypropylene,
high-performance nucleating agents may be used to improve speed,
physical properties and part aesthetics. And, various clarifying
agents can be included in the polymeric material to provide clarity
approaching that of glass and amorphous polymers. High performance
nucleating agents can improve the quality of extruded polypropylene
sheet feedstock. Further, clarifying agents for polypropylene
enable this polymer to replace polystyrene and poly(ethylene
terephthalate) in see-through articles, particularly shallow draw
lids and containers and high end applications.
[0024] Homopolymer polypropylene is widely used in sheet extrusion
and thermoforming applications because of its stiffness, clarity
and cost effectiveness. Random copolymer polypropylene may be used
to provide even higher levels of clarity and gloss and better cold
temperature impact properties. Form an environmental standpoint,
polypropylene's low density helps reduce the amount of material
needed as well as overall packaging weight, which helps minimize
landfilling and reduce fuel usage during shipping. Polypropylene
also has a low carbon footprint, as a result of fewer emissions
released during manufacture. Polypropylene is easily recycled in
existing waste management systems, allowing the material to be
reused indefinitely. In addition, polypropylene is generally free
from undesirable side effects during recycling, such as
crosslinking and forming a gel, or outgassing.
[0025] In addition, or instead of polymeric materials for the
sheet(s) or films, the present invention includes the use of
certain paper-based materials. For example, paper-based materials
formed primarily from renewable resources are believed to also be
suitable candidates for sheets or films to be thermoformed.
[0026] Furthermore, various composite materials can be used such as
paper-based materials coated or coextruded with polymeric materials
and in particular, polymer barrier materials such as polyethylene
(PE) and ethylene vinyl alcohol (EVOH). Composite materials can
include polymeric material(s), paper-based materials(s), metal(s)
and alloy(s) which can for example be in the form of foils, and
combinations thereof.
[0027] The material(s) forming the sheet(s) or film(s) can also
include one or more additives. For example, various structural
additives could be included such as fibrous high tensile strength
materials. Agents providing certain barrier properties such as
oxygen or water permeability can be included. Density adjusting
agents, coloring agents, environmental protective agents such as
for UV protection, and other agents for imparting particular
properties or characteristics to the article can be used in the
material of the sheet or film.
[0028] The sheet or film which forms the article(s) of interest can
be of a single or monolayer, or can comprise multiple layers. For
multilayer assemblies, the layers may be formed from different
materials or from the same materials. In addition, it is
contemplated that a variety of coatings and/or functional additives
can be included in the sheet or film which forms the article(s) of
interest. It is also contemplated that a wide array of packaging
provisions could be included such as layer assemblies that provide
resealing or closure function, tamper indicators, and the like.
[0029] Any material selected for use as the sheet or film to be
thermoformed preferably exhibits a softening point that is suitable
for the end use application and for the thermoforming equipment to
be used in forming the finished and labeled articles. The term
"softening point" as used herein refers to the temperature at which
a material becomes sufficiently pliable so that the material can be
thermoformed, however does not excessively flow or deform. For many
materials, their softening point may be within a range of
temperatures. For end use applications at ambient temperatures, it
is generally preferred that the softening point of the material
forming the sheet or film is greater than about 60.degree. C.
However, the present invention includes the use of materials having
softening points less than 60.degree. C. The term "softening point"
also includes the glass transition temperature (Tg) if a material
is used which is more accurately described by its Tg.
[0030] Another preferred characteristic of the material selected
for use in the sheet or film to be thermoformed is that the
material not tear, rip, or fracture during thermoforming. This
characteristic also depends upon the particular thermoforming
process and configuration of the thermoforming mold and surface. It
will be appreciated by those skilled in the art of thermoforming
that in many if not most thermoforming operations, the material is
stretched, drawn, and/or expanded in one or more directions. This
occurs as a result of the material deforming as it adopts the
contour and/or configuration of the thermoforming surface.
Label and Other Aspects
[0031] The label material used in the preferred embodiment methods
has characteristics such that the label material stretches or
expands with the sheet or film during the thermoforming process
without tearing. The label material therefore can be made from the
same material as that of the sheet or film being thermoformed to
ensure their compatibility during the thermoforming process.
However, the label material and the base sheet do not necessarily
need to be made from the same material. It is the ability of the
label to stretch or otherwise deform at the thermoforming
temperature which is important for formation of a labeled
thermoformed piece. That is, at the thermoforming temperature, the
stretching characteristics of the label and the base sheet are
compatible with one another and preferably at least equal or
substantially so. A label and a sheet are deemed to be compatible
with one another if at the temperature at which thermoforming
occurs, neither the label nor the sheet tears or fractures during
the particular thermoforming operation. For example, a PETG film
can be used as the label film material for a finished article made
from PETG. At the thermoforming temperature, if the label does not
stretch to the same magnitude and/or at the same rate as that of
the base sheet, the label could potentially tear during the
process. On the other hand, at the thermoforming temperature, if
the label is capable of higher stretch magnitudes than the base
sheet desirable results may be obtained. For instance, a PETG label
material could be used in applications where the base sheet/film
polymer is PET since a PETG label would exhibit compatible stretch
characteristics at the PET forming temperature. On the other hand,
a PET label film is generally not desirable for labeling a
thermoformed container made from PETG as the label film will not
stretch sufficiently at PETG forming temperatures. Similarly, a PET
label film material will not be suitable in applications were the
forming sheet material is made from low density polyethylene
(LDPE). The reverse of this latter example is also not feasible as
the LDPE label could melt at PET thermoforming temperatures. Thus,
the materials of the label and the sheet to be thermoformed must
exhibit compatible stretch characteristics and preferably exhibit
equivalent stretch characteristics at the temperature at which
thermoforming occurs.
[0032] In addition to the stretch magnitudes, softening and melting
points of the label and the base sheet must be considered and
chosen properly. As will be appreciated, the materials of the label
and sheet are preferably selected such that neither material
undergoes excessive melting at any point in the process. Thus, it
is preferred that the melting points of the materials of the label
and sheet are significantly greater than the temperature at which
thermoforming occurs. It is also preferred that the softening
points of the label and the sheet are similar to one another. In
certain embodiments, it is preferred that the difference in
softening points of the label and of the sheet to be thermoformed
is less than 10.degree. C., and more preferably less than 5.degree.
C. When comparing softening point temperature ranges to one
another, the difference is determined by using the upper or lower
temperatures that are closest to one another. The closer the
softening points of the label and sheet are to one another, and
more similar the stretching characteristics of the label and sheet
are to one another at the thermoforming temperature, the better the
labeling quality and uniformity in the finished article.
[0033] In another aspect of the invention, the label material can
be selected, formed, and/or have particular characteristics so as
to impart desired functionalities to the finished article. That is,
a "functional label" can be used to impart its functionality to the
finished article. For example, the label could be partially drawn
during an initial extrusion process. Once such label is drawn
further during the thermoforming process, the barrier properties of
the finished article could be improved. A label formed from a
barrier film could impart such characteristic(s) to the finished
article. Another example of a functional label is the use of
colorant or UV resistant additives in the label to impart the same
to the finished article. In addition to imparting additional
container functionality, such a labeling technique could result in
an overall cost reduction as the quantity of a specific additive or
colorant needed for the film would be much less than the same
required for the base sheet if instead, the base sheet were to be
thermoformed and labeled with a pressure sensitive label.
Additional non-limiting examples of functional agents that can be
incorporated into a label or label assembly for subsequent
affixment to layer(s) prior to thermoforming include fragrance
agents, light enhancement agents, gloss promoting or gloss
reduction agents, and other aesthetic or appearance promoting
agents.
[0034] As previously described for the sheets or films, the label
can be a single layer or comprise multiple layers. For multilayer
label assemblies, the layers may be formed from different materials
or from the same materials. The label can include one or more
functional agents as noted, or be free of such agents.
[0035] In accordance with the invention, various preferred
embodiment labels and label assemblies are provided. In certain
embodiments, a label assembly generally comprises one or more
polymeric layers or films and one or more adhesive layers for
adhesively securing the polymeric layer(s) to another sheet or film
of interest as described herein. The polymeric layers or films
comprise one or more polyolefin layers and/or one or more polyamide
layers. FIG. 5 illustrates a schematic cross sectional view of a
preferred embodiment label 400 comprising a polymeric film layer
410 and an adhesive layer 420. The polymeric film layer 410 defines
an outer surface 402. And the adhesive layer 420 defines an
oppositely directed inner face or underside 422. A wide array of
polymers can be used for the film layer 410. Preferably, the film
layer 410 comprises at least one polyolefin and/or polyamide.
[0036] FIG. 6 is a schematic cross sectional view of another
preferred embodiment label assembly 500 comprising a first film
layer 510 defining an outer face 502, a second film layer 520, and
an adhesive layer 530 defining an underside 532. The first film
layer 510 can comprise one or more of a polyolefin and/or a
polyamide. The second film layer 520 can also comprise one or more
of a polyolefin and/or a polyamide. The second layer may also
include one or more tie components as described in greater
detail.
[0037] The polyolefins used in the preferred embodiment label
assemblies can include a wide array of polyolefins known in the
art. The polyolefin may be a homopolymer or a copolymer. The
olefins which may be used to prepare the polyolefins include those
having from about two to about ten, or from two to about eight, or
from about two to about four carbon atoms. Examples of useful
olefins include ethylene, propylene, butylene, methyl-pentene,
hexene, octene, etc. In a preferred embodiment, the polyolefin is a
homopolymer or copolymer derived of ethylene, propylene or
butylene. In one embodiment, the polyolefin is an ethylene
homopolymer or an ethylene copolymer. The copolymer is prepared
from ethylene, propylene, or butylene and an olefin having from
about 3 to about 100 or from about 4 to about 30 carbon atoms. In
one embodiment, the olefin has from about three to about twelve, or
from about four to about ten carbon atoms. In another embodiment,
the olefin has from about 10 to about 100, or from about 12 to
about 30 carbon atoms. In one embodiment, the olefin used to
prepare the copolymer is an alpha-olefin. Examples of useful
olefins include propylene, butylene, pentene, 4-methyl-1-pentene,
hexene, heptene, octene, nonene, decene, undecene, dodecene,
tetradecene, hexadecene, octadecene, and docosene. Typically, the
olefin is present in an amount from about 1% up to about 50%, or
from about 5% to about 30%, or from about 7% up to about 25% by
mole. Examples of copolymers of ethylene include ethylene/propylene
copolymers, ethylene/butylene copolymers, ethylene/hexene
copolymers, ethylene/octene copolymers and ethylene/dodecene
copolymers of ethylene and olefins, such as alpha-olefins are
disclosed in U.S. Pat. No. 5,475,075, issued to Brant et al, and
U.S. Pat. No. 5,530,054, issued to Tse et al. These patents are
incorporated by reference for their disclosure of ethylene olefins
and processes for making the same. Preferably, the polyolefin is
polyethylene.
[0038] The polyamides used in the preferred embodiment label
assemblies can include a range of polyamides. For example, useful
polyamide resins include those commercially available from, for
example, Union Camp of Wayne, N.J. under the UNI-REZ product line,
and dimer-based polyamide resins available from Bostik, Emery,
Fuller, Henkel (under the VERSAMID product line). Other suitable
polyamides include those produced by condensing dimerized vegetable
acids with hexamethylene diamine. It is also contemplated to
utilize one or more aliphatic nylons such as nylon-MXD6 which is a
generic name for a range of polyamides produced from xylenediamine
(MXDA).
[0039] It is also contemplated that the preferred embodiment label
assembly 500 can include one or more tie layers (not shown)
disposed between the first and second film layers 510 and 520,
and/or disposed on either of both faces of the second film layer
520. Depending on the particular polymeric materials used to form
the coextruded face stock, in some embodiments, it is advantageous
to extrude, simultaneously, one or more charges of material which
become "tie" layers between coextruded layers. In particular, where
two layers of material would not otherwise sufficiently adhere or
bond to each other when coextruded, a "tie" layer is coextruded
with and between the two layers, to hold them together in a
substantially permanent unitary state. For example, nylon 6 and
polyethylene can be coextruded to form a substantially permanent,
unitary coextrudate by simultaneously extruding nylon 6,
polyethylene, and a polymer having good affinity for both
materials, such as a modified polyethylene or an ethylene vinyl
acetate copolymer. Such a polymer becomes a "tie" layer between the
nylon 6 and polyethylene layers. In general, the choice of "tie"
layer material depends, at least in part, on various properties of
the materials to be joined, or "tied," together, including, for
example, the materials' polar vs. nonpolar nature, modulus, flow
properties, etc.
[0040] A silicone release layer and corresponding liner can be
provided on the exposed underside of the adhesive layer in label
assemblies 400 and 500.
[0041] It is also contemplated that any of the preferred embodiment
label assemblies may comprise one or more oxygen barriers or other
films. A preferred example of an oxygen barrier used in film
assemblies is a layer including ethylene vinyl alcohol (EVOH).
Instead of or in addition to an oxygen barrier, the preferred film
assemblies may also comprise one or more barriers for reducing or
preventing passage or migration or other agents or chemical
species. For example, in certain applications, it may be desired to
include one or more layers that reduce or prevent the migration of
water vapor or moisture. Furthermore, the preferred embodiment
labels and label assemblies include barrier layers against oxygen,
carbon dioxide, aromas/odors, moisture, oils, chemicals, and/or any
combination thereof. Representative barrier materials include, but
are not limited to, nylon (all types), nylon-MXD6, EVOH, PVOH,
G-polymer, acrylonitrile methyl acrylate (ANMA) such as
commercially available under the designation BAREX, cyclic olefin
copolymers (COC), cyclic olefin polymers (COP), polyepichlorohydrin
(ECO) polymers, liquid crystal polymers (LCP), polyglycolic acid
polymers (PGA) such as those available commercially under the
designation KUREDUX from Kureha Corporation, and poly(methyl
methacrylate) (PMMA). A wide range of barrier coating technologies
are also commercially available such as those under the designation
NANOLOK from Inmat Inc.; NANOSEAL from Nanopack Inc.; and GOSHENOL
from Nippon Gosher which are all PVOH-based materials. In addition,
SiOX materials from Ceramis, which is a silicon dioxide layer
applied by liquid-vapor deposition can be used. In addition,
whey-based coatings such as those available from Wheylayer could
also possibly be used. Barrier coatings formed by vacuum
metallization can also be included in the preferred
embodiments.
[0042] FIG. 7 is a schematic cross sectional view of a preferred
embodiment label assembly 600 comprising a first film layer 610
defining an outer surface 602, a first tie layer 620, an oxygen
barrier layer 630, a second tie layer 640, and a second film layer
650 defining an underside 652. The label assembly 600 also
comprises an adhesive layer 660 defining a first outer face 662 and
an oppositely directed second outer face 664. The label assembly
600 preferably further comprises a silicone release layer 670
defining a release face 672, and a release liner 680 in contact
with the release layer 670 and having an exposed underside 682.
[0043] The preferred embodiment label assemblies include several
particularly preferred labels as follows. In one construction, the
first film layer 610 includes a polyolefin and most preferably
polyethylene and the second film layer 650 includes a polyamide.
The oxygen barrier layer 63 preferably includes ethylene vinyl
alcohol. The adhesive layer 660 is preferably a UV hotmelt acrylic
based adhesive. The release liner 680 can be provided in a wide
range of materials such as for example paper or polyester and
preferably polyethylene terephthalate (PET).
[0044] In another preferred construction, instead of a UV hotmelt
acrylic based adhesive for adhesive layer 660, an emulsion acrylic
based adhesive is used.
[0045] In still another construction, the first film layer 610 is a
polyamide and the second film layer 650 is a polyolefin such as
polyethylene. The adhesive layer 660 used in this construction is
preferably a UV hotmelt acrylic based adhesive.
[0046] In yet another construction, the first film layer 610 is a
polyamide and the second film layer 650 is a polyolefin such as
polyethylene. The adhesive layer 660 is an emulsion acrylic based
adhesive.
[0047] As previously noted, the preferred embodiment labels and
label assemblies may optionally include one or more barrier layers
and preferably one or more oxygen barrier layers.
[0048] The oxygen (O.sub.2) barrier coating materials are typically
water soluble, and may include for example, PVOH-based co- or
terpolymers, ethylene vinyl alcohol based copolymers (such as
SOARNOL by Nippon Gohsei), and/or materials that contain
hydrophilic functional groups such as --OH, --NH, amide, as well as
zwitterionic moiety, etc. The oxygen barrier coating is typically
coated onto a clear film, although in alternative embodiments the
film may be translucent or opaque. Another preferred material in
certain embodiments is polyglycolic acid. Moreover, in still
additional embodiments, it may be preferred to include
acrylonitrile methyl acrylate (ANMA), such as those commercially
available under the designation BAREX from Ineos Barex, a division
of Ineos USA, LLC.
[0049] Barrier properties for moisture or oxygen may be enhanced
further by adding an additional layer. The coating materials may
be, for example, either water based or solvent based. Some
preferred coating materials include PVDC latex coating or PVAc
latex coating.
[0050] Moreover, the invention includes the use of one or more
agents and/or barrier layers for reducing transmission and/or
providing protection from ultraviolet (UV) light. As is known,
exposure to UV light may detrimentally impact the taste or other
properties of a food or beverage. Furthermore, exposure to UV light
may also impact the efficacy of numerous vitamins, drugs, and the
like. Thus, one or more UV blocking agents and/or absorbers that
can be incorporated in any of the layers, materials, and/or
components described herein are as follows. Among families of UV
absorbers which may be used where appropriate are benzophenones,
salicyclates, benzotriazoles, hindered amines and alkoxy (e.g.,
methoxy) cinnamates. Recitation of these classes is not meant to be
a limitation on other classes of UV absorbers which may be used.
Among the benzotriazole UV absorbers which may be used are
2-(2-hydroxy-5-methylphenyl) benzotriazole which is available as
TINUVIN P from Ciba-Geigy Corp. of Tarrytown, N.Y. Water soluble UV
absorbers particularly useful include, but are not limited to:
phenyl benzimidazole sulfonic acid (sold as NEO HELIOPAN, Type
Hydro by Haarmann and Reimer Corp.),
2-hydroxy-4-methoxybenzophenone-5-sulfonic acid (sold as SYNTASE
230 by Rhone-Poulenc and UVINUL MS-40 by BASF Corp.), sodium
2,2-dihydroxy-4,4'-dimethoxy-5-sulfobenzophenone (sold as UVINUL
DS-49 by BASF Corp.), and PEG-25 paraaminobenzoic acid (sold as
UVINUL P-25 by BASF Corp.). Other UV absorbers which may be used
are defined in McCutcheon's Volume 2, Functional Materials, North
American Edition, published by the Manufacturing Confectioner
Publishing Company (1997), which is hereby incorporated by
reference. UV absorber if used, may be present in each of the label
and optionally the package and/or sheet at from about 0.001% to
about 3 wt. %, preferably, if present, between 0.001 and 0.05 wt.
%, although in certain cases preferred ranges may be from 0.05% to
1 wt. %.
[0051] It is also contemplated that in certain applications, it may
be possible to include one or more paper or paper-based materials
in the label assembly. Such paper or paper-based materials may
include additional amounts of other materials such as polymeric
resins, inorganic additives, and other agents to tailor their
resulting characteristics.
Optional Adhesives
[0052] In certain embodiments, the label is preferably attached to
the thermoformable sheet by use of an adhesive that can withstand
the thermoforming conditions and retain its adhesive properties at
the thermoforming temperatures and draw magnitudes. Non-limiting
examples of such adhesives include solvent based adhesives, and UV
and/or thermally curable epoxy and/or acrylic or rubber adhesives
which are designed to endure these harsh processing conditions. For
a successful operation, in addition to the adhesive properties at
high temperatures, viscosity of the adhesive is preferably chosen
such that the adhesive will not become fluid at the thermoforming
temperature and flow out from the label and sheet interface.
[0053] Use of an adhesive, however, may not be required in certain
preferred methods of thermoform labeling. For instance, if the
label and the forming film/sheet are fully miscible or compatible
with one another such as a PETG label and a PETG base sheet, and if
the label is maintained in a suitable position by mechanical means
or air flow, etc.; the label could soften and adhere to the sheet
at elevated thermoforming temperatures without the aid of an
adhesive. In this manner, partial miscibility of the label film and
the base sheet may also suffice. An example is the use of a label
that contains styrene ethylene butylene styrene (SEBS) copolymer in
its surface structure when such label is used in conjunction with a
polystyrene base sheet. Even if such a label could not be kept in
place on the sheet by any other means but by use of an adhesive,
its partial miscibility with the base sheet increases adhesion and
hence allows reduction of the amount of adhesive otherwise needed
for labeling, thereby resulting in a substantial cost reduction.
Inclusion of adhesive polymers in the label skin side which will be
attached to the article using polymers such as ethylene vinyl
acetate (EVA), ethylene butyl acrylate (EBA), or others could also
allow adhesion of the label to the base sheet without the use of an
adhesive depending on the chemistry of the base sheet. Additional
examples of suitable adhesive polymers which could be included in
the label skin side for subsequent contact with the sheet forming
the article of interest are certain ethylene vinyl acetate,
polyethylene, polypropylene, acid copolymers, and ethylene/acrylate
copolymers commercially available from DuPont under the designation
BYNEL.RTM.. These polymers are functionalized with reactive
monomers, such as acid groups or anhydride groups. Additional
examples of adhesive polymers that can be used in the preferred
embodiments include, but are not limited to materials commercially
available under the designations KRATON from Kraton Polymers,
SEPTON from Kuraray Co., VECTOR from Dexco Polymers, and ADMER from
Mitsui.
Printing
[0054] The preferred embodiment label can be printed with an ink
prior to its application or attachment to the thermoforming sheet.
The ink, similar to the adhesive, preferably exhibits appropriate
characteristics such that the ink can withstand high thermoforming
temperature(s) and the required draw magnitudes. If the ink cannot
stretch with the label, the ink will potentially crack or fracture,
and will have an unacceptable appearance. After stretching, the ink
should not excessively lose its opacity as the quality of the
printed material may not be acceptable. For example, inks
formulated with polyurethanes or similar elastic polymers in their
compositions are suitable materials for such an application. The
incorporation of polyurethane in the ink composition generally
allows stretching of the ink. The amount or percentage of
polyurethane or other similar elastic polymer component in the ink
formulation can most likely be correlated to the amount of stretch
that the thermoformed article endures. Non-limiting examples of
preferred inks include LIOVALUE and AQUALIONA inks from Toyo Ink
Company of Japan. These inks have been developed for packaging
applications where the printed (and laminated) package containing
food is sterilized at elevated temperatures of from about
121.degree. C. (250.degree. F.) to about 135.degree. C.
(275.degree. F.). Similar inks that are designed for package
boiling applications may also be suitable. In many applications, it
is preferred to utilize solvent inks designed for thermoforming. A
preferred new low viscosity oligomer designated as CN2285 from
Sartomer Company, may in certain applications be used in a UV flexo
ink. This new oligomer can be used in applications in which high
deformation occurs. The amount of pigment in the ink formulation
and the required stretch magnitude of the label during
thermoforming are factors affecting print quality and opacity.
Metallic inks containing polyurethane may also prove advantageous
in providing prints with high gloss enabling application on
contoured shape thermoformed containers. Other materials and ink
formulations known by those skilled in the art to meet such
requirements may also be utilized.
[0055] The labels are typically formed to exhibit graphics.
Graphics can include for example, designs, indicia, markings, text,
or patterns. The graphics can be incorporated in or upon the label
in nearly any fashion. As described in greater detail herein, the
graphics are preferably formed by printing one or more inks on the
label.
[0056] The graphics of the printed label typically distort during
the stretching stage of the thermoforming process. This distortion
will therefore need to be accounted for when designing and
constructing a printing cylinder or plate in anticipation of
printing. Preferably, a distortion printing process that
compensates for the expansion that the label will undergo during
the thermoforming process is used. In one approach, the stretch
magnitude at various locations of a thermoformed piece is first
determined. A grid patterned printed label facilitates distortion
measurements at various locations on the formed piece, similar to a
method described by Marcinkowski, Stanley, Michael, et al. in
International Publication WO 2008/111000 A1. The distortion profile
along with an accurate measure of thickness variation at various
part locations are parameters typically used for print cylinder or
plate design in order to print the graphics "distortedly". Upon
stretching of the printed label during thermoforming, the graphics
of the finished article will then appear normal. Because stretch
magnitudes differ from one application or object to another, each
label may need its own "distortion" printing depending upon its
material, location on the finished article, and thermoforming
operation.
[0057] Printing on the label can be performed in nearly any manner.
Although conventional printing techniques such as offset,
flexographic, and gravure printing can be used, it is generally
preferred to use digital printing processes for forming the desired
markings, indicia, text, patterns, and/or designs on the label
especially if the inks used in digital printing have the desired
stretch characteristics. These are collectively referred to herein
as "visual designs." Digital printing is performed by an electronic
controller or processer that stores information as to the subject
matter to be printed, and one or more printheads or other
components that form the desired markings, indicia, text, patterns,
and/or designs, i.e. the visual designs. As previously noted, if
desired, the visual designs may be initially formed or deposited in
a distorted fashion. After thermoforming, such distorted visual
designs appear in their intended manner.
Methods
[0058] FIG. 1 is a schematic illustration of a preferred embodiment
process for forming a labeled thermoformed article 50 in accordance
with the present invention. Specifically, a label sheet or film 10
is provided defining a first face 12 and an oppositely directed
second face 14. The label sheet 10 preferably includes one or more
polymeric film materials and preferably, as described herein. One
or more markings, indicia such as text 20, and/or designs are
printed or otherwise formed on one or both faces 12, 14 to form a
printed label 10a. The text or indicia may be formed "distortedly"
as schematically shown in FIG. 1. The label 10a is then attached or
otherwise positioned relative to a polymeric sheet or film 30 which
is thermoformed to form article 50. The sheet 30 defines a first
face 32 and an oppositely directed second face 34. As previously
described herein, the label 10 can be adhered, affixed, or
otherwise secured to the sheet 30, in nearly any fashion.
Preferably, a layer of adhesive is used. However, the invention
includes merely positioning the label 10a relative to the sheet 30
and contacting the two components. Exposure to heat, such as from
the thermoforming operation, can be used to render the interface
between the label 10a and the sheet 30, sufficiently tacky to
thereby retain the components in a desired position relative to one
another. The label 10a may be positioned alongside either face 32
or 34 of the sheet 30. In many applications, it is preferred to
locate the label 10a along a face of the sheet 30 that will form or
constitute an outer face of the article that is eventually formed.
For example, referring to FIG. 1, the face of the sheet 30 that
will eventually form the outer face of article 50, is face 34. And
so, the label 10a is positioned alongside the face 34 of the sheet
30. However, it will be appreciated that the present invention
includes other arrangements and configurations.
[0059] The sheet 30 and the label 10a are then preferably subjected
to a thermoforming operation involving one or more molding or
forming cavities as known in the art. For example, a mold 40
defining a recessed cavity and a thermoforming surface 42 can be
used. The thermoform surface, e.g. surface 42, is the surface that
contacts the material to be thermoformed. As will be appreciated,
the thermoform surface has a contour and/or configuration such that
upon intimate contact with the material to be thermoformed, the
contour and/or configuration of the thermoform surface is
transferred to the material undergoing thermoforming. Upon
thermoforming, a labeled article 50 for example is produced.
Thermoforming technology is well known in the art. Details as to
thermoforming polymeric blanks, sheets, and films are readily
available in the art.
[0060] The present invention includes numerous alternative versions
of the process schematically depicted in FIG. 1. That is, in no way
is the invention limited to the specific process illustrated in
FIG. 1. For example, although the preferred embodiment process
schematically shown in FIG. 1 depicts the face 34 of the sheet
carrying the label 10a, it will be understood that the label 10a
could be positioned alongside the face 32 of the sheet 30.
Similarly, the collection of the sheet 30 and the label 10a can be
positioned relative to the thermoform surface 42 such that the
label 10a contacts the surface 42, or so that a corresponding side
of the sheet 30, opposite the side along which the label 10a
resides, contacts the thermoform surface 42.
[0061] The present invention and its various techniques can be used
in a multitude of labeling strategies. For example, labels can be
incorporated in an article in which only a portion of the article
or article face is covered by the label. An example of this is
depicted in FIG. 1. In other embodiments, one or more labels can be
incorporated in an article in which the entirety or substantially
so, of the article or article face is covered by the label. An
example of this is shown in FIG. 2. FIG. 2 illustrates a label 110
having an area approximately the same or greater than that of a
thermoformable sheet 130 positioned alongside one another prior to
thermoforming. In still other embodiments, one or more labels can
be incorporated along the entirety of an article face in a single
span, such as across the entire width or height of the article or
article face, as depicted in FIGS. 3 and 4. FIG. 3 depicts a label
210 positioned along a thermoformable sheet 230 prior to
thermoforming. The label 210 extends across the width of the sheet
230. FIG. 4 shows a label 310 positioned along a thermoformable
sheet 330 prior to thermoforming. The label 310 extends across the
length of the sheet 330. Use of the various labeling practices
provides great flexibility in packaging and container designs.
[0062] In many of the preferred embodiment processes of the
invention, it is particularly preferred that the label is printed
and attached or otherwise positioned along a face of the sheet to
be thermoformed, immediately prior to thermoforming. This practice
avoids having to store and maintain inventory of multiple
pre-printed labels which must then be selected, accessed, and
integrated into a thermoforming process. This practice of
thermoforming directly after printing and applying a label in-situ
and as part of a thermoforming process to form an article of
interest, is referred to herein as "immediately thermoforming."
That is, thermoforming is performed immediately after either
printing or applying a label to a sheet to be thermoformed. Thus,
the invention includes processes in which a label is printed and
then applied (or positioned) to the sheet immediately followed by
thermoforming. And, the invention includes processes in which a
label is attached to a sheet to be thermoformed, one or more
printing operations are then performed to form indicia, text,
and/or designs on the label and sheet assembly, and then the
printed assembly is immediately thermoformed to produce an article
of interest.
[0063] The preferred embodiment methods of the invention should
enable significant reductions in floor space otherwise required for
container packaging and forming operations. Furthermore, the
preferred embodiment methods are environmentally friendly and
should result in less waste in materials and improve overall
process efficiency. In addition, the preferred embodiment processes
can be readily implemented in just-in-time (JIT) practices.
[0064] Although the present invention and its various preferred
embodiments have been described primarily with reference to a
single label and/or a single sheet, it will be appreciated that the
invention includes forming multiple labeled articles on a single
sheet. Thus, the invention includes operations in which multiple
products or objects are formed by thermoforming a single labeled
sheet. A single sheet can receive multiple labels, one or more
labels being positioned at a region of the sheet identified for
forming one or more products of interest. The partially or
completely labeled sheet is then subjected to one or more
thermoforming operations whereby a plurality of products or objects
of interest are formed.
[0065] Applications for the present technology include but are not
limited to a transparent food packaging such as for example
products such as snack chips and coffee; pharmaceutical packaging
such as for example tablets, capsules and gel-caps which can gain
longer shelf life and extended protection from water and oxygen;
and health and beauty packaging such as for example products such
as toothpaste and lotions.
[0066] Although it is believed that the present invention will find
utility in numerous industries and applications, producing and
labeling of food packaging is a prime area for use of the
invention.
[0067] Many other benefits will no doubt become apparent from
future application and development of this technology.
[0068] All patents, published applications, and articles noted
herein are hereby incorporated by reference in their entirety.
[0069] It will be understood that any one or more feature or
component of one embodiment described herein can be combined with
one or more other features or components of another embodiment.
Thus, the present invention includes any and all combinations of
components or features of the embodiments described herein.
[0070] As described hereinabove, the present invention solves many
problems associated with previously known practices. However, it
will be appreciated that various changes in the details, materials
and arrangements of components and/or operations, which have been
herein described and illustrated in order to explain the nature of
the invention, may be made by those skilled in the art without
departing from the principle and scope of the invention, as
expressed in the appended claims.
* * * * *