U.S. patent application number 13/066178 was filed with the patent office on 2012-10-11 for pmr write head with assisted magnetic layer.
This patent application is currently assigned to Headway Technologies, Inc.. Invention is credited to Lijie Guan, Tai Min, Suping Song, Yuhui Tang.
Application Number | 20120257305 13/066178 |
Document ID | / |
Family ID | 46964252 |
Filed Date | 2012-10-11 |
United States Patent
Application |
20120257305 |
Kind Code |
A1 |
Tang; Yuhui ; et
al. |
October 11, 2012 |
PMR WRITE HEAD WITH ASSISTED MAGNETIC LAYER
Abstract
A PMR writer is disclosed wherein a magnetic assist layer (MAL)
made of an anisotropic (-Ku) or (+Ku) magnetic material is formed
along a main pole trailing side to optimize the vertical magnetic
field and field gradient at the air bearing surface. A Ru seed
layer is formed between the main pole and (-Ku) MAL to induce a
hard axis direction toward the main pole. A (-Ku) MAL is preferably
comprised of hcp-CoIr while CoPt and FePt are examples of a (+Ku)
MAL. The MAL has a down-track thickness from 5 to 20 nm, a width
equal to the track width in a cross-track direction, and extends
100 to 500 nm in a direction toward a back end of the main pole. As
a result, flux leakage from the main pole to trailing shield is
reduced and aerial density is increased. A method for fabricating
the PMR writer is provided.
Inventors: |
Tang; Yuhui; (Milpitas,
CA) ; Guan; Lijie; (Milpitas, CA) ; Min;
Tai; (San Jose, CA) ; Song; Suping; (Fremont,
CA) |
Assignee: |
Headway Technologies, Inc.
|
Family ID: |
46964252 |
Appl. No.: |
13/066178 |
Filed: |
April 8, 2011 |
Current U.S.
Class: |
360/125.03 ;
29/603.07; G9B/5.077 |
Current CPC
Class: |
G11B 5/315 20130101;
G11B 5/3116 20130101; G11B 5/1278 20130101; Y10T 29/49032 20150115;
G11B 5/3163 20130101; G11B 5/3146 20130101 |
Class at
Publication: |
360/125.03 ;
29/603.07; G9B/5.077 |
International
Class: |
G11B 5/31 20060101
G11B005/31; G11B 5/127 20060101 G11B005/127 |
Claims
1. A perpendicular magnetic recording (PMR) writer, comprising: (a)
a main pole comprised of a trailing side and a leading side with
respect to a down-track direction, the leading side has a leading
edge at an air bearing surface (ABS) and the trailing side has a
trailing edge at the ABS and is further comprised of a tapered
trailing side section that extends from the ABS to a section of
trailing side that is aligned perpendicular to the ABS; (b) a gap
layer adjacent to and surrounding the main pole at the ABS wherein
said gap layer comprises a write gap formed along the trailing edge
and trailing side including the tapered trailing side section; (c)
a magnetic assist layer comprising an anisotropic magnetic layer
formed between the write gap and the tapered trailing side section;
and (d) a shield structure comprising a trailing shield that
adjoins a side of the write gap that faces away from the main
pole.
2. The PMR writer of claim 1 wherein the magnetic assist layer has
a thickness between about 5 and 20 nm in the down-track
direction.
3. The PMR writer of claim 2 wherein the magnetic assist layer has
a (-Ku) crystalline energy constant and is made of hcp-CoIr wherein
the Ir content is between about 10 and 40 atomic %, dhcp-CoFe,
a'-Fe--C, or NiAs-type Mn.sub.50Sb.sub.50.
4. The PMR writer of claim 1 wherein the magnetic assist layer has
a (+Ku) crystalline energy constant and is made of CoPt or
FePt.
5. The PMR writer of claim 3 further comprised of a non-magnetic
seed layer made of Ru formed between the tapered trailing side
section and the magnetic assist layer.
6. The PMR writer of claim 1 wherein the magnetic assist layer has
a width in a cross-track direction that is equal to a track width
of the trailing edge.
7. The PMR writer of claim 1 wherein the magnetic assist layer
extends a distance between about 100 and 500 nm from the ABS
towards a back end of the main pole.
8. A perpendicular magnetic recording (PMR) writer, comprising: (a)
a main pole comprised of a trailing side and a leading side with
respect to a down-track direction, the leading side has a leading
edge at an air bearing surface (ABS) and the trailing side has a
trailing edge at the ABS and is further comprised of a tapered
trailing side section that extends from the ABS to a section of
trailing side that is aligned perpendicular to the ABS; (b) a gap
layer adjacent to and surrounding the main pole at the ABS wherein
said gap layer comprises a write gap formed along the trailing edge
and trailing side including the tapered trailing side section; (c)
a magnetic assist layer made of an anisotropic magnetic layer and
comprising a first section formed between the write gap and the
tapered trailing side section, and a second section formed between
the write gap and a portion of the trailing side section that is
aligned perpendicular to the ABS; and (d) a shield structure
comprising a trailing shield that adjoins a side of the write gap
that faces away from the main pole.
9. The PMR writer of claim 8 wherein the magnetic assist layer has
a thickness between about 5 and 20 nm in a down-track
direction.
10. The PMR writer of claim 9 wherein the magnetic assist layer has
a (-Ku) crystalline energy constant and is made of hcp-CoIr wherein
the Ir content is between about 10 and 40 atomic %, dhcp-CoFe,
a'-Fe--C, or NiAs-type Mn.sub.50Sb.sub.50.
11. The PMR writer of claim 10 further comprised of a non-magnetic
seed layer made of Ru formed between the tapered trailing side
section and the magnetic assist layer, and between the magnetic
assist layer and the portion of trailing side section that is
aligned perpendicular to the ABS.
12. The PMR writer of claim 8 wherein the magnetic assist layer has
a (+Ku) crystalline energy constant and has a magnetization in a
direction perpendicular to the ABS and toward a back end of the
main pole.
13. The PMR writer of claim 8 wherein the magnetic assist layer
extends a distance between about 100 and 500 nm from the ABS
towards a back end of the main pole.
14. The PMR writer of claim 8 wherein the magnetic assist layer has
a width in a cross-track direction that is equal to a track width
of the trailing edge.
15. A method of fabricating a PMR writer with a magnetic assist
layer formed adjacent to a trailing side of a main pole at an air
bearing surface (ABS), comprising: (a) sequentially forming a
leading shield layer and a side shield layer on a substrate, said
side shield layer has an opening formed therein which is bounded by
side shield sidewalls and a top surface of the leading shield
layer; (b) depositing a side gap along the side shield sidewalls
and a leading gap on the top surface of the leading shield layer;
(c) plating a main pole layer on the side gap and leading gap to
fill the opening in the side shield layer, and planarizing a top
surface of the main pole to be coplanar with the side shield layer
and thereby forming a main pole trailing side with a trailing edge
at the ABS; (d) depositing a magnetic assist layer made of an
anisotropic magnetic material on a portion of the main pole
trailing side including the trailing edge; (e) depositing a write
gap on the magnetic assist layer and on a top surface of the side
gap; and (f) plating a trailing shield on the write gap and
portions of the side shield layer.
16. The method of claim 15 further comprised of tapering a section
of the trailing side of the main pole after the planarizing step
and prior to depositing the magnetic assist layer, the tapered
section connects the trailing edge at the ABS to a section of
trailing side that is aligned perpendicular to the ABS.
17. The method of claim 15 wherein the magnetic assist layer is
comprised of an anisotropic (-Ku) magnetic material such that the
hard axis of the magnetic assist layer is aligned in a direction
toward the main pole trailing side.
18. The method of claim 17 further comprised of depositing a
non-magnetic seed layer on the main pole trailing side prior to
depositing the magnetic assist layer.
19. The method of claim 15 wherein the magnetic assist layer is
made of an anisotropic (+Ku) magnetic material.
20. The method of claim 19 wherein the magnetic assist layer is
deposited by a tilted angle sputter technique to form a hard axis
aligned perpendicular to the ABS.
21. The method of claim 15 wherein the magnetic assist layer has a
thickness between about 5 to 20 nm in a down-track direction and a
width in a cross-track direction that is equal to a track width of
the trailing edge.
22. The method of claim 15 wherein the magnetic assist layer
extends a distance between about 100 and 500 nm from the ABS
towards a back end of the main pole.
23. The method of claim 16 wherein the magnetic assist layer is
formed on the tapered section of trailing side and on a portion of
the trailing side section aligned perpendicular to the ABS.
Description
RELATED PATENT APPLICATION
[0001] This application is related to the following: Docket #
HT10-031, Ser. No. ______; filing date ______; assigned to a common
assignee, and herein incorporated by reference in its entirety.
FIELD OF THE INVENTION
[0002] The invention relates to a thin magnetic film with an
anisotropic magnetic property that is added to the trailing side of
a main pole and thereby provides additional magnetic charge on the
ABS surface to improve writability and field gradient.
BACKGROUND OF THE INVENTION
[0003] In today's perpendicular magnetic recording (PMR)
technology, an all wrapped around (AWA) shield writer is widely
used by the major hard disk drive (HDD) manufacturers. The function
of a trailing shield in an AWA structure is to improve the magnetic
field gradient along a down track direction which is a key
requirement for high bits per inch (BPI). Meanwhile, side shields
and a leading shield serve to define a narrower writer bubble which
is important for realizing higher tracks per inch (TPI). In order
to achieve higher area density (i.e. higher BPI and TPI) in
advanced writer designs, the gap between the main pole and all
shields, including the write gap adjoining the trailing shield,
side gaps to the side shields, and lead gap next to the leading
shield must be as narrow as possible. However, the material used
for conventional AWA shields is a soft magnetic material without
preferred anisotropy. Therefore, narrowing the gap between a shield
and main pole will only lead to an unwanted flux path from the main
pole to the shield which in turn reduces the writability (magnetic
field) of the writer on magnetic recording media. This dilemma is
considered one of the most significant challenges to improving
current writer designs and performance.
[0004] Referring to FIG. 1, internal flux loss is depicted in a
conventional PMR writer 1 comprising a main pole 11 and shield 12
that can represent a trailing shield, side shield, or leading
shield depending on the direction of movement of the writer over
magnetic medium 10 during a write process. Magnetic charges 7a, 8a
of opposite sign are shown on an air bearing surface (ABS) side of
the shield 12, and main pole 11, respectively, and are responsible
during a write process for the preferred direction 5 of flux Bs1
from the main pole to the magnetic medium, and returning from the
magnetic medium to the shield. Magnetic flux Bs0 is provided to the
main pole from coils (not shown). As the gap (distance) between
main pole and shield becomes smaller, flux loss Bs2 in a direction
6 from main pole to shield becomes more severe due to magnetic
charges 7b, 8b on opposing sides of the shield, and main pole,
respectively. Consequently, the write field Bs1 on the magnetic
recording medium will be degraded. With the constraint of write
field amplitude on the magnetic medium 10, further reduction of the
gap between main pole and shields is not productive which limits
achieving a higher recording area density. In particular,
decreasing the write gap between main pole and trailing shield has
been an effective way in improving field gradient and BPI during
the past few years. However, current technology does not enable
further field gradient improvement when the write gap shrinks below
20 nm. One possible reason is the magnetic charges 7b, 8b for main
pole and trailing shield are more concentrated on opposing sides as
pictured in FIG. 1 than on the ABS surface when the write gap
becomes too narrow in conventional designs. Thus, an improved
writer design is needed to minimize flux loss Bs2 and maximize
write field Bs1.
[0005] A search of the prior art revealed the following references.
U.S. Patent Application 2010/0157484 shows a magnetic field
auxiliary pole and a non-magnetic layer stacked on the main pole to
increase field strength and gradient. However, the stacked layers
are recessed from the ABS and are not expected to entirely prevent
flux leakage from the main pole to an adjacent trailing shield.
[0006] In U.S. Patent Application 2010/0149687, a trailing shield
is shown with multiple layers and is separated from the trailing
side of a main pole by a gap layer.
[0007] U.S. Pat. No. 7,657,992 discloses a small trailing shield
stitched onto the main pole at the ABS but separated from the main
pole by a write gap layer.
[0008] U.S. Pat. No. 6,530,141 describes a magnetic pole
construction resulting in a high field gradient.
[0009] A. Hashimoto et al. describe the use of a negative Ku
magnetic material in "A soft magnetic underlayer with negative
uniaxial magnetocrystalline anisotropy for suppression of spike
noise and wide adjacent track erasure in perpendicular magnetic
recording media", Journal of Applied Physics, 99, 08Q907
(2006).
[0010] A composite grain of easy plane material (CoIr with negative
Ku) and perpendicular anisotropy material (CoPt with positive Ku)
are used in a magnetic medium to improve the head field gradient
and amplitude as described by Park et al in "A novel crystalline
soft magnetic intermediate layer for perpendicular recording
media", Journal of Applied Physics, 105, 07B723 (2009), and in
"Co-7% Ir Soft Magnetic Intermediate Layer for Perpendicular
Media", IEEE Transactions on Magnetics, Vol. 46, No. 6, June
2010.
[0011] Takahashi et al. discuss structural and magnetic analyses of
a'-Fe--C films in "Magnetocrystalline Anisotropy for a'-Fe--C and
a'-Fe--N Films", IEEE Transactions on Magnetics, Vol. 37, No. 4,
July 2001.
SUMMARY OF THE INVENTION
[0012] One objective of the present invention is to provide
additional magnetic charge at the trailing edge of the recording
field to improve field amplitude and field gradient at the ABS and
thereby increase BPI as required for high area density PMR
writers.
[0013] Another objective of the present invention is to provide a
method of forming a PMR writer with improved field amplitude and
field gradient according to the first objective.
[0014] According to the embodiments of the present invention, the
first objective is achieved with a magnetic assist layer formed on
a trailing side of a main pole and adjoining a write gap layer. The
magnetic assist layer has a width in a cross-track direction that
is essentially equal to that of the main pole track width, a
thickness in a down track direction of 5 to 20 nm, and extends a
distance of 100 to 500 nm from the ABS toward a back end of the PMR
writer. Preferably, the magnetic assist layer is comprised of an
anisotropic magnetic material. In one embodiment, the magnetic
assist layer (MAL) has a negative crystalline anisotropy energy
constant (-Ku) at room temperature. Alternatively, the magnetic
assist layer has a positive crystalline anisotropy constant (+Ku).
A magnetic assist layer with a (-Ku) energy constant may be
deposited on a seed layer such as Ru that aligns the c-axis (hard
axis) of the hexagonal crystalline MAL structure toward the main
pole. The c-axis (hard axis) is preferably aligned toward the main
pole for a MAL with (-Ku) energy constant while the c-axis is
preferably vertical to the ABS for a MAL with a (+Ku) energy
constant. Thus, magnetization of the magnetic assist layer can only
be induced in a direction toward the main pole with a strong
magnetic field. Furthermore, the magnetic assist layer is totally
soft in a 2D plane orthogonal to the hard axis which means the
magnetization of the MAL can be easily induced in any direction
orthogonal to the hard axis with a weak magnetic field. As a
result, magnetic charges are minimized on the trailing side of the
MAL facing the trailing shield such that flux loss from the main
pole to the trailing shield is insignificant thereby increasing
field amplitude and field gradient at the ABS
[0015] According to a first embodiment, the shield structure may
comprise a trailing shield, leading shield, and side shields.
Moreover, the trailing shield may be a composite with a first layer
adjoining the write gap made of a high Ms (24 kG) magnetic material
and a second (19 kG) magnetic layer formed on a side of the first
layer that faces away from the main pole. In one aspect, the shield
structure may be an AWA design that completely surrounds the main
pole. Furthermore, the main pole may have both of a tapered leading
side and a tapered trailing side. A key feature is that a magnetic
assist layer made of an anisotropic magnetic material is formed on
a portion of the main pole trailing side and extends from the ABS
toward the back end of the main pole. In a first embodiment, the
MAL is formed along the tapered trailing side of the main pole and
continues along a portion of the trailing side that connects the
tapered trailing side with a back end of the main pole. The present
invention also encompasses a second embodiment wherein the magnetic
assist layer is formed only along the tapered trailing side of the
main pole.
[0016] A method is provided for forming a PMR writer with a
magnetic assist layer comprised of an anisotropic magnetic material
adjoining a trailing side of a main pole. According to one
embodiment, a leading shield and a side shield layer made of an
isotropic soft magnetic material are sequentially formed on a
substrate. An opening with sidewalls is formed in the side shield
to expose a portion of the leading shield top surface. Side gap and
leading gap layers are conformally deposited in the opening
followed by plating the main pole to fill the opening. After a CMP
process to planarize the main pole, a taper may be formed on the
main pole trailing side by ion beam milling. Then a non-magnetic
seed layer, and an anisotropic (-Ku) magnetic assist layer are
sequentially deposited on a portion of the main pole trailing side
including the trailing edge. Alternatively, an anisotropic (+Ku)
magnetic assist layer is directly deposited on the main pole
trailing side by an oblique sputtering method. Subsequently, the
write gap is deposited on the magnetic assist layer. Finally, the
trailing shield is plated on the write gap to complete the shield
structure.
BRIEF DESCRIPTION OF THE DRAWINGS
[0017] FIG. 1 is an oblique view of a prior art PMR writer where
there is considerable flux loss from the main pole in a direction
toward an adjacent shield.
[0018] FIG. 2 is an oblique view of a PMR writer with a shield made
of an anisotropic magnetic material to minimize flux leakage from
the main pole to an adjacent shield.
[0019] FIG. 3 is a cross-sectional view of a PMR writer structure
previously fabricated by the inventors that has a composite
trailing shield and a leading shield adjacent to a main pole with
tapered leading and trailing sides.
[0020] FIG. 4 is a cross-sectional view of a PMR writer formed
according to an embodiment of the present invention wherein a
magnetic assist layer made of an anisotropic magnetic material is
formed along a trailing side of a main pole.
[0021] FIG. 5 is an ABS view of the embodiment depicted in FIG. 4
and further includes side shields that connect with the trailing
shield and leading shield.
[0022] FIG. 6 is a cross-sectional view of a PMR writer according
to a second embodiment of the present invention wherein a magnetic
assist layer comprising an anisotropic magnetic material is formed
only along a tapered trailing side of a main pole.
[0023] FIG. 7 is a plot of vertical magnetic field vs. down-track
position for the PMR writer structures depicted in FIGS. 3 and
4.
[0024] FIGS. 8-12 show intermediate steps during the fabrication of
the PMR writer depicted in FIG. 4.
[0025] FIG. 13 shows an alternative method of forming a magnetic
assist layer made of an anisotropic magnetic material on a main
pole trailing side.
DETAILED DESCRIPTION OF THE INVENTION
[0026] The present invention is a PMR writer design which takes
advantage of the discovery that an anisotropic magnetic material
may be used as a magnetic assist layer on a main pole trailing side
to minimize flux loss from the main pole to a trailing shield and
thereby maximize the flux field and field gradient at the main pole
interface with the ABS. Although the exemplary embodiment depicts a
trapezoidal shaped main pole at the ABS, the present invention also
encompasses other main pole shapes. Furthermore, the main pole may
have one or both of a tapered trailing edge and a tapered leading
edge. Width in the context of shield structures and layers defined
herein refers to a distance in a cross-track direction, and
thickness or depth relates to a distance in a down-track direction.
The gap layer as illustrated herein may not have a uniform
thickness and the write gap portion between the main pole and
trailing shield is typically thinner than the lead gap.
[0027] Referring to FIG. 2, we described in related patent
application HT10-031 how a shield 20 made of anisotropic magnetic
material and formed adjacent to a main pole 11 may be used to
maximize the magnetic charges 7a, 8a at the ABS of shield 20, and
main pole 11, respectively. In the absence of a strong magnetic
field, there are essentially no magnetic charges formed on a side
of the shield facing the main pole which prevents a portion of
magnetic field Bs0 from being diverted to the shield. Thus, the
magnetic field Bs1 at the ABS is maximized compared with the
condition previously shown in FIG. 1 and the gap between main pole
and trailing shield may be reduced with a minimum amount of flux
loss to enable a significant gain in BPI for advanced PMR writer
designs. Herein, we disclose additional PMR writer designs where an
anisotropic magnetic layer is placed at other locations adjacent to
a main pole to prevent flux loss to a trailing shield and increase
the flux field and field gradient at the ABS.
[0028] Referring to FIG. 3, a cross-sectional view of a PMR writer
previously fabricated by the inventors is shown having a main pole
9 formed along an ABS 50-50 and a trailing shield and leading
shield 42 formed on either side of the main pole along the
cross-track (x-axis) direction. The y-axis is the down-track
direction while the z-axis direction is toward the back end 9v of
the main pole. In the exemplary embodiment, there is a tapered
leading side 9c1 formed at an angle .theta.1 with respect to a
plane B-B aligned perpendicular to the ABS, and connected to a
leading side 9f1 which terminates at the back end 9v. There is also
a tapered trailing side 9c2 formed at an angle .theta.2 of about 0
to 45 degrees, and preferably 25 to 30 degrees, with respect to a
plane A-A aligned perpendicular to the ABS, and connected to a
trailing side 9f2 that terminates at the back end. Main pole 9 has
a trailing edge 9t and leading edge 9e at the ABS, and is separated
from leading shield 42 by a lead gap 47. In the exemplary
embodiment, there is a composite trailing shield comprised of a
high Ms (24 kG) magnetic shield layer 49 formed adjacent to a write
shield 45 and a 19 kG magnetic shield layer 43 adjoining the high
Ms layer on a side that faces away from the main pole. In one
aspect, side 43s of the 19 kG magnetic shield layer that interfaces
with high Ms shield layer 49, and side 49s of the high Ms shield
layer that interfaces with write gap 45 may be formed substantially
parallel to tapered trailing side 9c2.
[0029] Referring to FIG. 4, a first embodiment of the present
invention is shown that retains all of the features of the PMR
writer in FIG. 3 and also has a magnetic assist layer 3 made of an
anisotropic magnetic material formed on tapered trailing side 9c2
and along a portion of trailing side 9f2 which is aligned
perpendicular to the ABS. According to one embodiment, the magnetic
assist layer has an anisotropy (-Ku) energy constant with a hard
axis aligned toward the main pole 9. Alternatively, the magnetic
assist layer may be comprised of a material such as CoPt or FePt
having an anisotropy (+Ku) energy constant with a hard axis in a
direction perpendicular to the ABS. In one aspect, the magnetic
assist layer is comprised of a first section 3a that extends from
the ABS 50-50 to a corner 3c where the tapered trailing side
terminates, and a second section 3b which extends from the corner
3c to an end 3e which is a distance d along trailing side 9f2.
Preferably, end 3e is a distance of 100 to 500 nm from the ABS.
Moreover, magnetic assist layer 3 has a thickness in a y-axis
direction of 5 to 20 nm. Typically, the write gap 45 has a
thickness of about 20 to 30 nm between magnetic assist layer
section 3a and side 49s of the first trailing shield layer. Note
that FIG. 4 is a cross-sectional view taken along the plane 2-2 in
the ABS view illustrated in FIG. 5. It should be understood that
the magnetic assist layer 3 also provides an improvement in
writability in an embodiment (not shown) wherein the trailing
shield is a single layer made of isotropic magnetic material such
as CoFeNi or CoFe.
[0030] Referring to FIG. 5, the first embodiment anticipates that
the shield structure further includes side shields 44 that connect
with first trailing shield layer 49 and leading shield 42 to form
an AWA shield structure. However, it should be understood that the
magnetic assist layer 3 of the present invention is equally
beneficial in increasing flux amplitude and improving field
gradient at the ABS if a partial side shield structure is employed.
The plane 2-2 bisects the main pole in a down-track (y-axis)
direction. In the exemplary embodiment, the main pole 9 has a
trapezoidal shape with a leading edge 9e having a smaller width in
a cross-track (x-axis) direction than the trailing edge 9t. Sloped
sides 9s1, 9s2 of the main pole are adjoined by a side gap 41 made
of a dielectric material. Main pole 9 may include a seed layer (not
shown) along sides 9s1, 9s2 and along leading edge 9e that
facilitates a deposition method wherein main pole material is
plated in an opening (not shown) bounded by side gaps 41 and lead
gap 47. In the exemplary embodiment, the side gap has a uniform
width in the x-axis direction and conforms to the shape of the
sides 9s1, 9s2. There is also a write gap 45 having a width w that
adjoins a top surface of each side gap 41 and interfaces with the
magnetic assist layer (MAL) 3 along a side of the MAL that faces
away from the trailing edge 9t. The write gap may be comprised of
the same dielectric material as in the side gap. A leading gap 47
interfaces with the leading edge 9e and adjoins a bottom surface of
each side gap. Thus, there is a gap layer completely surrounding
main pole 9 but the thickness along the plane 2-2 is typically less
for the write gap 45 than for leading gap 47. The width of the
trailing edge 9t is referred to as the track width TW and is
preferably the same as the width of the magnetic assist layer
3.
[0031] In an alternative embodiment shown in FIG. 6, the magnetic
assist layer may be formed only along tapered trailing side 9c2 and
terminates at corner 3c where trailing side 9f2 connects with
tapered trailing side 9c2. In other words, the alternative
embodiment in FIG. 6 is the same as the first embodiment in FIG. 4
except the magnetic assist layer is shortened in vertical height
with respect to the ABS and is not formed along the section of
trailing side 9f2 that is perpendicular to the ABS 50-50.
[0032] According to embodiments relating to a magnetic assist layer
made of an anisotropy (-Ku) magnetic material, a non-magnetic seed
layer 62 (FIG. 9) may be formed between the MAL 3 and the main pole
9 in order to induce the hard axis of the MAL in a direction
perpendicular to the trailing edge 9t and perpendicular to tapered
trailing side 9c2, and to trailing side 9f2 (FIG. 4). Furthermore,
the non-magnetic layer 62 prevents exchange coupling between the
magnetic assist layer and the isotropic magnetic material in the
main pole. Preferably, the non-magnetic seed layer is made of Ru
with a thickness from 5 to 20 Angstroms. Optionally, the
non-magnetic seed layer is omitted and a hard axis is induced in
the magnetic assist layer 3 by sputter depositing the MAL at a
tilted angle with respect to the ABS.
[0033] A key feature is that the magnetic assist layer is
preferably comprised of an anisotropic magnetic material which may
have a (-Ku) crystalline energy constant such as hcp-CoIr wherein
the Ir content is from 10 to 40 atomic %, and preferably between 17
and 22 atomic %, dhcp-CoFe, a'-Fe--C, or NiAs-type
Mn.sub.50Sb.sub.50. The present invention also anticipates that the
magnetic assist layer may be comprised of an anisotropic magnetic
material such as CoPt or FePt with a (+Ku) crystalline energy
constant. As a result of incorporating a magnetic assist layer 3
adjacent to a trailing side of the main pole, the write gap
thickness may be thinner than in prior art shield designs thereby
enabling a higher BPI than previously realized. Note that side
shields 44 adjoin side gap 41 on either side of main pole 9, and
leading shield 42 interfaces with leading gap 47 and side shields
in FIG. 5. A bottom surface of first trailing shield layer 49
contacts side shield sections 44 at distances greater than 1/2 w
from the center plane 2-2. Side shields 44 and leading shield 42
may be formed of the same soft magnetic material as in second
trailing shield layer 43.
[0034] Referring to FIG. 7, a plot of vertical magnetic field
profile along the down-track direction is shown for the PMR writers
in FIG. 3 (solid line) and in FIG. 4 (dashed line), respectively.
In each case, the write gap thickness is held constant at 26 nm and
the track width is 60 nm. The results (dashed line) that represent
an embodiment of the present invention were generated with an
assisted magnetic layer thickness of 5 nm, and a vertical height
(distance between ABS and end of MAL) of 200 nm. The overwrite is
improved by 4 dB with the example in FIG. 4 when the magnetic
assist layer has a 1 Telsa Ms and 1 Telsa Hk along a direction
perpendicular to the ABS. A gain in both field amplitude and field
gradient is observed for the design with the magnetic assist layer.
Additional improvement may be realized with adjustments in the
geometry of the magnetic assist layer and in its magnetic
property.
[0035] Referring to FIG. 8, an ABS view of an intermediate
structure formed during the fabrication of a PMR writer according
to the first embodiment (FIG. 4) is shown. A leading shield 42 and
side shield layer 44 are sequentially formed on a substrate (not
shown) by a conventional plating method. Next, an opening (not
shown) that is bounded by sidewalls 44s and top surface 42s is
formed in the side shield layer 44 by a well known photoresist
patterning and ion beam milling (IBE) sequence. A dielectric
material is deposited in the opening to form lead gap 47 on a
portion of top surface 42s, and to form a side gap 41 on sidewalls
44s. Thereafter, main pole 9 is plated on side gap 41 and lead gap
47 to fill the opening. Typically, a chemical mechanical polish
(CMP) process is used to form a main pole top surface including
trailing edge 9t that is coplanar with top surfaces of side shields
44 and side gaps 41. A photoresist layer 48 is coated on the side
shields, side gaps, and main pole and then patterned to form an
opening 52 that uncovers a portion of main pole top surface
including leading edge 9t. An ion beam milling process that
comprises ion beams 50 is employed to taper the trailing side (9f2
in FIG. 4) and form a tapered side 9c2 having a taper angle
.theta.2 as depicted in FIG. 3. Note that the tapered leading side
9c1 connected to leading side 9f1 may be formed by a standard
process prior to ion beam milling process which tapers the trailing
side.
[0036] Referring to FIG. 9, photoresist layer 48 remains in place
while a non-magnetic seed layer 62 preferably made of Ru is sputter
deposited on the tapered side 9c1 within opening 52 according to
one process flow sequence. Next, the magnetic assist layer 3 is
sputter deposited on the non-magnetic seed layer. In a preferred
embodiment, the MAL is made of Co.sub.83Ir.sub.17 although an Ir
content between 10 and 40 atomic % is also acceptable. The MAL 3
and non-magnetic seed layer 62 have essentially the same width as
the TW for trailing edge 9t. The photoresist mask 48 is now removed
by a standard method.
[0037] Referring to FIG. 10, a second photoresist layer 60 is
coated on side shields 44, side gaps 41, and on magnetic assist
layer 3, and is then patterned to form an opening 61 which uncovers
the MAL and a top surface 41t of each side gap. The size of the
opening 61 corresponds to the desired width w (and length in a
z-axis direction which is not shown) of the subsequently deposited
write gap.
[0038] Referring to FIG. 11, a write gap layer is deposited by an
atomic layer deposition (ALD) method to form a conformal write gap
45 on the tapered main pole trailing side 9c2 (not shown) including
magnetic assist layer 3, and on side gap top surfaces 41t.
Preferably, the write gap has a thickness of about 20 to 30 nm
above the side gap 41. Thereafter, the second photoresist layer is
stripped by a conventional process.
[0039] Referring to FIG. 12, the high Ms (24 kG) trailing shield
layer 49 is plated by a well known method followed by plating the
19 kG trailing shield layer 43 to complete the shield structure for
the PMR writer.
[0040] Referring to FIG. 13, an alternative process flow sequence
that relates to a magnetic assist layer having a (+Ku) crystalline
energy constant is shown and begins with the intermediate structure
shown in FIG. 8. In this case, a non-magnetic seed layer is not
deposited and the MAL 3 made of CoPt or FePt, for example, is
deposited by a tilted (oblique) angle sputter deposition method.
The resulting magnetic assist layer is exchange coupled with the
main pole 9 and has anisotropy induced in a direction perpendicular
to the ABS along a z-axis direction. Thereafter, the processes
described with respect to FIGS. 10-12 are followed to form the
write gap and trailing shield structure.
[0041] The advantages of the present invention are that flux
leakage from a main pole to a trailing shield is significantly
reduced compared with prior art shield designs such that BPI is
improved to enable higher performance in advanced PMR writer
designs. Furthermore, write field amplitude and field gradient are
improved over a prior art design that does not have a magnetic
assist feature on the main pole when a constant write gap distance
is employed.
[0042] While this invention has been particularly shown and
described with reference to, the preferred embodiment thereof, it
will be understood by those skilled in the art that various changes
in form and details may be made without departing from the spirit
and scope of this invention.
* * * * *