U.S. patent application number 12/173483 was filed with the patent office on 2008-11-20 for electrically conductive line.
Invention is credited to Yongjun Jeff Hu, Jiutao Li, Allen McTeer, Qi Pan.
Application Number | 20080284025 12/173483 |
Document ID | / |
Family ID | 36943362 |
Filed Date | 2008-11-20 |
United States Patent
Application |
20080284025 |
Kind Code |
A1 |
Pan; Qi ; et al. |
November 20, 2008 |
Electrically Conductive Line
Abstract
The invention includes an electrically conductive line, methods
of forming electrically conductive lines, and methods of reducing
titanium silicide agglomeration in the fabrication of titanium
silicide over polysilicon transistor gate lines. In one
implementation, a method of forming an electrically conductive line
includes providing a silicon-comprising layer over a substrate. An
electrically conductive layer is formed over the silicon-comprising
layer. An MSi.sub.xN.sub.y-comprising layer is formed over the
electrically conductive layer, where "x" is from 0 to 3.0, "y" is
from 0.5 to 10, and "M" is at least one of Ta, Hf, Mo, and W. An
MSi.sub.z-comprising layer is formed over the
MSi.sub.xN.sub.y-comprising layer, where "z" is from 1 to 3.0. A
TiSi.sub.a-comprising layer is formed over the MSi.sub.z-comprising
layer, where "a" is from 1 to 3.0. The silicon-comprising layer,
the electrically conductive layer, the MSi.sub.xN.sub.y-comprising
layer, the MSi.sub.z-comprising layer, and the
TiSi.sub.a-comprising layer are patterned into a stack comprising
an electrically conductive line. Other aspects and implementations
are contemplated.
Inventors: |
Pan; Qi; (Boise, ID)
; Li; Jiutao; (Boise, ID) ; Hu; Yongjun Jeff;
(Boise, ID) ; McTeer; Allen; (Eagle, ID) |
Correspondence
Address: |
Qi Pan
4832 East Sagewood Court
Boise
ID
83716
US
|
Family ID: |
36943362 |
Appl. No.: |
12/173483 |
Filed: |
July 15, 2008 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
11074106 |
Mar 7, 2005 |
|
|
|
12173483 |
|
|
|
|
Current U.S.
Class: |
257/757 ;
257/E21.169; 257/E21.2; 257/E21.582 |
Current CPC
Class: |
H01L 2924/0002 20130101;
H01L 21/2855 20130101; H01L 21/76838 20130101; H01L 29/4933
20130101; H01L 2924/00 20130101; H01L 21/28061 20130101; H01L
2221/1078 20130101; H01L 23/485 20130101; H01L 2924/0002 20130101;
H01L 21/28518 20130101; H01L 27/10891 20130101 |
Class at
Publication: |
257/757 ;
257/E21.169 |
International
Class: |
H01L 23/52 20060101
H01L023/52 |
Claims
1-34. (canceled)
35. An electrically conductive line comprising: a conductively
doped silicon-comprising layer; an electrically conductive layer
received over the conductively doped silicon-comprising layer; an
MSi.sub.xN.sub.y-comprising layer received over the electrically
conductive layer, where "x" is greater than zero and less than or
equal to 3.0, "y" is from 0.5 to 10, and "M" is at least one of Ta,
Hf, Mo, and W; an MSi.sub.z-comprising layer received over the
MSi.sub.xN.sub.y-comprising layer, where "z" is from 1 to 3.0; and
a TiSi.sub.a-comprising layer received over the
MSi.sub.z-comprising layer, where "a" is from 1 to 3.0.
36. Memory integrated circuitry incorporating the electrically
conductive line of claim 35.
37. An electronic system incorporating the electrically conductive
line of claim 35.
38. The conductive line of claim 35 wherein "x" is at least 1.
39. The conductive line of claim 35 wherein the
MSi.sub.z-comprising layer is received on the
MSi.sub.xN.sub.y-comprising layer.
40. The conductive line of claim 39 wherein the
TiSi.sub.a-comprising layer is received on the MSi.sub.z-comprising
layer.
41. The conductive line of claim 35 wherein the electrically
conductive layer is void of detectable nitrogen.
42. The conductive line of claim 35 wherein the electrically
conductive layer comprises MSi.sub.w, where "w" is from 1 to
3.0.
43. The conductive line of claim 42 wherein the electrically
conductive layer and the MSi.sub.z-comprising layer are of the same
composition.
44. The conductive line of claim 42 wherein the electrically
conductive layer and the MSi.sub.z-comprising layer are of
different compositions.
45. The conductive line of claim 42 wherein the
MSi.sub.xN.sub.y-comprising layer is received on the MSi.sub.w.
46. The conductive line of claim 42 wherein the
MSi.sub.z-comprising layer is received on the
MSi.sub.xN.sub.y-comprising layer.
47. The conductive line of claim 42 wherein the
MSi.sub.xN.sub.y-comprising layer is received on the MSi.sub.w and
the MSi.sub.z-comprising layer is received on the
MSi.sub.xN.sub.y-comprising layer.
48. The conductive line of claim 42 wherein the
MSi.sub.xN.sub.y-comprising layer is received on the MSi.sub.w, the
MSi.sub.z-comprising layer is received on the
MSi.sub.xN.sub.y-comprising layer, and the TiSi.sub.a-comprising
layer is received on the MSi.sub.z-comprising layer.
49. The conductive line of claim 48 wherein the MSi.sub.w is
received on the silicon-comprising layer.
50. The conductive line of claim 35 wherein the electrically
conductive layer, the MSi.sub.xN.sub.y-comprising layer, and the
MSi.sub.z-comprising layer have a combined thickness which is less
than that of the TiSi.sub.a-comprising layer.
51. The conductive line of claim 35 wherein the electrically
conductive layer, the MSi.sub.xN.sub.y-comprising layer, and the
MSi.sub.z-comprising layer have a combined thickness which is less
than that of the silicon-comprising layer.
52. The conductive line of claim 35 wherein the electrically
conductive layer, the MSi.sub.xN.sub.y-comprising layer, and the
MSi.sub.z-comprising layer have a combined thickness which is less
than that of each of the TiSi.sub.a-comprising layer and the
silicon-comprising layer.
53. The conductive line of claim 35 wherein the electrically
conductive layer and the MSi.sub.z-comprising layer have respective
thicknesses from 5 Angstroms to 500 Angstroms.
54. The conductive line of claim 35 wherein the
MSi.sub.xN.sub.y-comprising layer has a thickness from 10 Angstroms
to 500 Angstroms.
55. The conductive line of claim 54 wherein the
MSi.sub.xN.sub.y-comprising layer has a thickness from 10 Angstroms
to 50 Angstroms.
56. The conductive line of claim 35 wherein the conductive line
comprises a transistor gate line received over a gate
dielectric.
57. The conductive line of claim 35 wherein M comprises Ta.
58. The conductive line of claim 35 wherein M comprises at least
one of Hf, Mo and W.
59. An electrically conductive line comprising: a conductively
doped silicon-comprising layer; an MSi.sub.w-comprising layer
received on the silicon-comprising layer, where "w" is from 1 to
3.0 and "M" is at least one of Ta, Hf, Mo, and W, the
MSi.sub.w-comprising layer having a thickness from 5 Angstroms to
500 Angstroms; an MSi.sub.xN.sub.y-comprising layer received on the
MSi.sub.w-comprising layer, where "x" is from 1 to 3.0 and "y" is
from 0.5 to 10, the MSi.sub.xN.sub.y-comprising layer having a
thickness from 10 Angstroms to 500 Angstroms; an
MSi.sub.z-comprising layer received on the
MSi.sub.xN.sub.y-comprising layer, where "z" is from 1 to 3.0, the
MSi.sub.z-comprising layer having a thickness from 5 Angstroms to
500 Angstroms; and a TiSi.sub.a-comprising layer received on the
MSi.sub.z-comprising layer, where "a" is from 1 to 3.0, the
TiSi.sub.a-comprising layer having a thickness from 100 Angstroms
to 1000 Angstroms. The conductive line of claim 0 wherein each of
the MSi.sub.w-comprising layer, the MSi.sub.xN.sub.y-comprising
layer, and the MSi.sub.z-comprising layer has a thickness no
greater than 50 Angstroms.
60. The conductive line of claim 59 wherein each of the
MSi.sub.w-comprising layer, the MSi.sub.xN.sub.y-comprising layer,
and the MSi.sub.w-comprising layer has a thickness no greater than
50 Angstroms.
61. The conductive line of claim 59 wherein the
MSi.sub.w-comprising layer and the MSi.sub.z-comprising layer are
of the same composition.
62. The conductive line of claim 59 wherein the
MSi.sub.w-comprising layer and the MSi.sub.z-comprising layer are
of different compositions.
Description
RELATED PATENT DATA
[0001] This application is a divisional of U.S. patent application
Ser. No. 11/074,106, filed on Mar. 7, 2005, entitled "Electrically
Conductive Line, Method of Forming an Electrically Conductive Line,
and Method of Reducing Titanium Silicide Agglomeration in
Fabrication of Titanium Silicide Over Polysilicon Transistor Gate
Lines", naming Qi Pan, Jiutao Li, Yongjun Jeff Hu, and Allen
McTeer, as Inventors, the disclosure of which is incorporated
herein by reference.
TECHNICAL FIELD
[0002] This invention relates to electrically conductive lines, to
methods of forming electrically conductive lines, and to methods of
reducing titanium silicide agglomeration in the fabrication of
titanium silicide over polysilicon transistor gate lines.
BACKGROUND OF THE INVENTION
[0003] One common component found in integrated circuits is an
electrically conductive line. Such might form part of a device or
subcircuit, or interconnect various devices. One common conductive
line is a transistor gate of a field effect transistor device. Such
are commonly used in memory integrated circuitry, for example
dynamic random access memory (DRAM) circuitry. Individual memory
cells of DRAM circuitry include a field effect transistor having
one source/drain region thereof electrically connected with a
storage capacitor, and the other source/drain region electrically
connected with a bitline. The conductive transistor gate lines are
commonly referred to as wordlines, with individual gate lines
constituting a part of several memory cell field effect
transistors.
[0004] A common wordline construction includes titanium silicide
(TiSi.sub.x) received over conductively doped polysilicon. The
titanium silicide might be provided over the polysilicon in a
number of manners. For example, elemental titanium might be
deposited upon polysilicon and thereafter annealed to react the
polysilicon and titanium to form titanium silicide. Alternately by
way of examples only, titanium silicide might be chemical vapor
deposited upon polysilicon or physical vapor deposited by
sputtering from a titanium silicide target. Further and regardless,
the titanium silicide which is formed might initially be amorphous
or crystalline. Crystallinity is desired for reduced
resistance/higher conductance. Amorphous titanium silicide can be
converted to crystalline titanium suicide by high temperature
anneal.
[0005] Crystalline stoichiometric titanium silicide (TiSi.sub.2)
typically exists in one of two different crystalline phases. A
first phase is an orthorhombic base-centered phase having twelve
atoms per unit cell, a resistivity of about 60 to 90 microohm-cm,
and is known as the C49 phase. A second phase is a more
thermodynamically-favored orthorhombic face-centered phase, which
has 24 atoms per unit cell and a resistivity of about 12 to 20
microohm-cm, and is known as the C54 phase. Regardless of
deposition method, it is common for the less-desired C49 phase to
be initially deposited or formed. This C49 phase can then be
converted to a desired C54 phase through appropriate annealing
conditions.
[0006] One problem associated with the fabrication of such lines is
known as agglomeration of the titanium silicide relative to the
underlying polysilicon. Such typically manifests when the substrate
is exposed to temperatures in excess of 900.degree. C. and which
typically inherently occurs during the fabrication of the
circuitry. Agglomeration is characterized by the titanium silicide
migrating/extending into the underlying polysilicon. Such can be to
such a degree to extend completely through the polysilicon. For
transistor gate lines, the migration can even be to completely
through the gate dielectric, thereby causing a fatal short.
Further, the degree of agglomeration is not predictable or
controllable from device to device. For transistor gates that are
not fatally shorted, this undesirably creates different operating
characteristics for different devices. Specifically, the degree of
agglomeration within the polysilicon affects its work function and,
accordingly, the threshold voltage along the gate line at which
individual transistors are turned "on" and "off".
[0007] In an effort to reduce titanium silicide agglomeration,
previous studies have focused on applying different annealing
processes or adding other elements to the titanium silicide. Still,
needs remain for improved methods of reducing titanium silicide
agglomeration in the fabrication of titanium silicide over
polysilicon transistor gate lines, and particularly in the
fabrication of DRAM circuitry. Yet while the invention was
motivated in addressing these issues, it is in no way so limited.
The invention is only limited by the accompanying claims as
literally worded, without interpretative or other limiting
reference to the specification, and in accordance with the doctrine
of equivalents.
SUMMARY
[0008] The invention includes an electrically conductive line,
methods of forming electrically conductive lines, and methods of
reducing titanium suicide agglomeration in the fabrication of
titanium silicide over polysilicon transistor gate lines. In one
implementation, a method of forming an electrically conductive line
includes providing a silicon-comprising layer over a substrate. An
electrically conductive layer is formed over the silicon-comprising
layer. An MSi.sub.xN.sub.y-comprising layer is formed over the
electrically conductive layer, where "x" is from 0 to 3.0, "y" is
from 0.5 to 10, and "M" is at least one of Ta, Hf, Mo, and W. An
MSi.sub.z-comprising layer is formed over the
MSi.sub.xN.sub.y-comprising layer, where "z" is from 1 to 3.0. A
TiSi.sub.a-comprising layer is formed over the MSi.sub.z-comprising
layer, where "a" is from 1 to 3.0. The silicon-comprising layer,
the electrically conductive layer, the MSi.sub.xN.sub.y-comprising
layer, the MSi.sub.z-comprising layer, and the
TiSi.sub.a-comprising layer are patterned into a stack comprising
an electrically conductive line.
[0009] In one implementation, the invention contemplates an
electrically conductive line independent of the method of
fabrication.
[0010] In one implementation, a method of reducing titanium suicide
agglomeration in fabrication of titanium silicide over polysilicon
transistor gate lines comprises interposing a composite of an
MSi.sub.z-comprising layer over an MSi.sub.xN.sub.y-comprising
layer over an MSi.sub.w-comprising layer intermediate the titanium
silicide and polysilicon, where "w" and "z" respectively are from 1
to 3.0, where "x" is from 0 to 3.0, "y" is from 0.5 to 10, and "M"
is at least one of Ta, Hf, Mo, and W.
[0011] Other aspects and implementations are contemplated.
BRIEF DESCRIPTION OF THE DRAWINGS
[0012] Preferred embodiments of the invention are described below
with reference to the following accompanying drawings.
[0013] FIG. 1 is a diagrammatic, cross-sectional view of a
semiconductor wafer fragment in process in accordance with an
aspect of the invention.
[0014] FIG. 2 is a view of the FIG. 1 wafer fragment at a point of
processing subsequent to that depicted by FIG. 1.
[0015] FIG. 3 is a view of the FIG. 2 wafer fragment at a point of
processing subsequent to that depicted by FIG. 2.
[0016] FIG. 4 is a view of the FIG. 3 wafer fragment at a point of
processing subsequent to that depicted by FIG. 3.
[0017] FIG. 5 is a view of the FIG. 4 wafer fragment at a point of
processing subsequent to that depicted by FIG. 4.
[0018] FIG. 6 is a view of the FIG. 5 wafer fragment at a point of
processing subsequent to that depicted by FIG. 5.
[0019] FIG. 7 is a view of the FIG. 6 wafer fragment at a point of
processing subsequent to that depicted by FIG. 6.
[0020] FIG. 8 is a view of the FIG. 7 wafer fragment at a point of
processing subsequent to that depicted by FIG. 7.
[0021] FIG. 9 is a view of the FIG. 8 wafer fragment at a point of
processing subsequent to that depicted by FIG. 8.
[0022] FIG. 10 is a diagrammatic view of a computer illustrating an
exemplary application of the present invention.
[0023] FIG. 11 is a block diagram showing particular features of
the motherboard of the FIG. 10 computer.
[0024] FIG. 12 is a high-level block diagram of an electronic
system according to an exemplary aspect of the present
invention.
[0025] FIG. 13 is a simplified block diagram of an exemplary
electronic system according to an aspect of the present
invention.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0026] This disclosure of the invention is submitted in furtherance
of the constitutional purposes of the U.S. Patent Laws "to promote
the progress of science and useful arts" (Article 1, Section
8).
[0027] A preferred method of forming an electrically conductive
line, and particularly a field effect transistor gate line, is
initially described with reference to FIGS. 1-9. Referring to FIG.
1, a substrate fragment is indicated generally with the reference
numeral 10. Such preferably comprises a semiconductor substrate,
for example a substrate comprising a bulk monocrystalline silicon
region 12 having a gate dielectric layer 14 formed thereover. In
the context of this document, the term "semiconductor substrate" or
"semiconductive substrate" is defined to mean any construction
comprising semiconductive material, including, but not limited to,
bulk semiconductive materials such as a semiconductive wafer
(either alone or in assemblies comprising other materials thereon),
and semiconductive material layers (either alone or in assemblies
comprising other materials). The term "substrate" refers to any
supporting structure, including, but not limited to, the
semiconductive substrates described above. Accordingly, substrate
fragment 10 might comprise semiconductor-on-insulator substrates or
other substrates, and whether existing or yet-to-be developed.
Discussion proceeds with an exemplary preferred fabrication of a
transistor gate line with a gate dielectric layer 14 thereby being
provided. Of course, electrically conductive lines other than field
effect transistor gates are also contemplated. An exemplary
preferred material 14 is silicon dioxide deposited or grown to an
exemplary thickness of from 10 Angstroms to 100 Angstroms.
[0028] Referring to FIG. 2, a silicon-comprising layer 16 has been
formed over substrate 12/14. An exemplary preferred
silicon-comprising material 16 is polysilicon. By way of example
only, alternate silicon-comprising materials include
monocrystalline silicon, such as epitaxially grown silicon, and
silicon combined with other materials in a non-compound or
non-stoichiometric manner, for example silicon and germanium.
Silicon-comprising layer 16 will ultimately form a conductive
portion of the conductive line, and will thereby at some point be
electrically conductive. Accordingly, silicon-comprising layer 16
might be electrically conductive as-deposited, for example by in
situ doping with a conductivity enhancing impurity during
deposition. Alternately, such might be implanted or otherwise
processed later to render such layer electrically conductive if not
in such state as initially deposited. An exemplary preferred
thickness range for silicon-comprising layer 16 is from 400
Angstroms to 5,000 Angstroms, with 700 Angstroms being a specific
preferred example.
[0029] Referring to FIG. 3, an electrically conductive layer 18 has
been formed over silicon-comprising layer 16. Further preferably
and as shown, layer 18 is formed "on" silicon-comprising layer 16,
with "on" in the context of this document meaning in at least some
direct physical contacting relationship with the stated layer. By
way of example only, an exemplary preferred material is MSi.sub.w,
where "w" is from 1 to 3.0 and "M" is at least one of Ta, Hf, Mo,
and W. In one preferred embodiment, conductive layer 18 is
preferably void of detectable nitrogen to preclude risk of forming
an insulative silicon nitride. An exemplary preferred thickness
range for electrically conductive layer 18 is from 5 Angstroms to
500 Angstroms, with from 5 Angstroms to 50 Angstroms being more
preferred, and a 50 Angstroms MSi.sub.2 layer (i.e., even more
specifically TaSi.sub.2) being a specific preferred example. Such
might be deposited by any suitable method, including by way of
example only sputtering, chemical vapor deposition and atomic layer
deposition. If chemical vapor depositing or atomic layer
depositing, exemplary precursors/gasses include SiH.sub.4 and
TaCl.sub.4.
[0030] Referring to FIG. 4, an MSi.sub.xN.sub.y-comprising layer 20
has been formed over, and preferably on as shown, electrically
conductive layer 18, and where "x" is from 0 (zero) to 3.0, "y" is
from 0.5 to 10, and "M" is at least one of Ta, Hf, Mo, and W.
Preferably, "x" is greater than zero, and even more preferably "x"
is at least 1. An exemplary preferred thickness range for
MSi.sub.xN.sub.y-comprising layer 20 is from 10 Angstroms to 500
Angstroms, with from 10 Angstroms to 50 Angstroms being more
preferred. A specific example is a 40 Angstroms thick
MSi.sub.xN.sub.y-comprising layer where "x" equals 2 and "y" equals
5. MSi.sub.xN.sub.y-comprising layer might be deposited by any
existing or yet-to-be developed method, for example including by
sputtering, by chemical vapor deposition and by atomic layer
deposition. A preferred exemplary sputtering technique comprises a
gas sputtered against a target comprising MSi.sub.w, with nitrogen
being provided at least in part from gaseous N.sub.2 and/or
NH.sub.3. For example in one specific preferred embodiment, an
inert gas and N.sub.2 are injected (together or separately) into a
sputtering chamber in which the substrate is received at a ratio of
inert gas to N.sub.2 of about 3:1 by volume.
[0031] Referring to FIG. 5, an MSi.sub.z-comprising layer 22 is
formed over, and preferably on as shown,
MSi.sub.xN.sub.y-comprising layer 20, and where "z" is from 1 to
3.0 and "M" is at least one of Ta, Hf, Mo, and W.
MSi.sub.z-comprising layer 22 and electrically conductive layer 18
might be of the same composition (meaning of the same components
and in their respective quantities), or of different compositions
(meaning of one or both of different components or quantities of
the same components). An exemplary preferred thickness range for
MSi.sub.z-comprising layer 22 is from 5 Angstroms to 500 Angstroms,
more preferably from 5 Angstroms to 50 Angstroms, with a 60
Angstroms thick MSi.sub.2 layer being a specific preferred
example.
[0032] Referring to FIG. 6, a TiSi.sub.a-comprising layer 24 has
been formed over, and preferably on as shown, MSi.sub.z-comprising
layer 22, where "a" is from 1 to 3.0. An exemplary preferred
thickness range is from 100 Angstroms to 5,000 Angstroms, with a
400 Angstroms thick layer of TiSi.sub.2 being a specific preferred
example. In specific preferred examples, electrically conductive
layer 18, MSi.sub.xN.sub.y-comprising layer 20, and
MSi.sub.z-comprising layer 22 have a combined thickness which is
less than that of TiSi.sub.a-comprising layer 24, and in certain
preferred embodiments less than that of silicon-comprising layer
16.
[0033] Referring to FIG. 7, an electrically insulative layer 26 has
been formed over, and preferably on as shown, TiSi.sub.a-comprising
layer 24. Exemplary preferred materials include one or both of
silicon dioxide and silicon nitride. Not being electrically
conductive, layer 26 will not constitute a conductive portion of
the line being formed, and is of course optional.
[0034] Referring to FIG. 8, silicon-comprising layer 16,
electrically conductive layer 18, MSi.sub.xN.sub.y-comprising layer
20, MSi.sub.z-comprising layer 22 and TiSi.sub.a-comprising layer
24 have been patterned into a stack comprising an electrically
conductive line 30. In the depicted exemplary preferred FIG. 8
embodiment, gate dielectric layer 14 and insulative layer 26 have
also been patterned commensurate with the patterning of
electrically conductive layers 16, 18, 20, 22 and 24. Any
patterning technique is contemplated, and whether existing or
yet-to-be developed. By way of example only, exemplary techniques
include photolithographic patterning and etch, and laser
patterning. An exemplary dry anisotropic etching chemistry for
etching TiSi.sub.a includes CF.sub.4 and Cl.sub.2. An exemplary dry
anisotropic etching chemistry for etching MSi.sub.w,
MSi.sub.xN.sub.y and MSi.sub.x collectively also includes CF.sub.4
and Cl.sub.2. An exemplary dry anisotropic etching chemistry for
etching a polysilicon-comprising layer includes HBr, He and
O.sub.2.
[0035] MSi.sub.x has been previously promoted for use as a titanium
silicide agglomeration-barrier and as a C54 phase titanium silicide
promoter, for example as disclosed in our U.S. patent application
Ser. No. 10/609,282, filed on Jun. 26, 2003, entitled "Methods of
Forming Metal Silicide, and Semiconductor Constructions Comprising
Metal Silicide", and naming Yongjun Jeff Hu as an inventor, now
U.S. Pat. No. 7,282,443, the disclosure of which is hereby fully
incorporated by reference as if included in its entirety herein.
Without being limited by any theory or effect unless literally
appearing in a claim in this application, the provision of an
additional MSi.sub.xN.sub.y-comprising layer can further reduce
titanium silicide agglomeration relative to underlying
silicon-comprising layers in the fabrication of electrically
conductive lines, and regardless of amorphous or crystalline
phases. An electrically conductive layer is ideally interposed
between the silicon-comprising layer and the
MSi.sub.xN.sub.y-comprising layer towards precluding nitrogen of
the MSi.sub.xN.sub.y-comprising layer from coming into contact with
the silicon which might undesirably form an insulative silicon
nitride. Further using the above described etching chemistries, it
was found that a conductive line stack in accordance with an aspect
of the invention having MSi.sub.2 over MSi.sub.2N.sub.y over
MSi.sub.2 exhibited less undercut than a line stack having
MSi.sub.2 which was void of MSi.sub.2N.sub.y.
[0036] In one aspect, the invention also contemplates a method of
reducing titanium silicide agglomeration in the fabrication of
titanium silicide over polysilicon transistor gate lines, which
comprises interposing a composite of an MSi.sub.z-comprising layer
over an MSi.sub.xN.sub.y-comprising layer over an
MSi.sub.w-comprising layer intermediate the titanium silicide and
polysilicon, where "w" and "z", respectively, are from 1 to 3.0,
where "x" is from zero to 3.0, where "y" is from 0.5 to 10, and "M"
is at least one of Ta, Hf, Mo, and W.
[0037] The invention also contemplates electrically conductive
lines, for example as described above, independent of the method of
fabrication, and of course independent of the preferred effects
described above.
[0038] Referring to FIG. 9, electrically conductive line 30 can be
utilized as a wordline or other field effect transistor gate line,
and can be fabricated into transistor gate structures at
appropriate locations. Specifically and by way of example only,
FIG. 9 shows a location where line 30 has been incorporated into a
transistor structure 32. Source/drain regions 34 and 36 have been
formed within substrate 12. Such exemplary source/drain regions are
depicted as comprising a deep, heavily-doped portion, 38 and a
shallow, lightly-doped, portion 40. Source/drain regions 34 and 36
can be formed utilizing conventional methods or yet-to-be developed
methods, and the conductivity-enhancing dopant within regions 38
and 40 can comprise either p-type dopant or n-type dopant, by way
of example. Electrically insulative sidewall spacers 42 have been
formed along the sidewalls of electrically conductive line 30.
Exemplary preferred materials include one or both of silicon
nitride and silicon dioxide.
[0039] Transistor device 32 can be incorporated into a memory cell.
In the depicted exemplary construction, device 32 is incorporated
into a DRAM cell. Specifically, source/drain region 34 is
electrically connected to a storage device 50, and the other
source/drain region 36 is electrically connected to a bitline 52.
Storage device 50 can comprise any suitable device, including a
capacitor, for example. Bitline 52 can comprise any suitable
construction. Electrically conductive line 30 can be considered to
be part of an integrated circuit, for example the DRAM integrated
circuitry just described.
[0040] FIG. 10 illustrates generally, by way of example, but not by
way of limitation, an embodiment of a computer system 400 according
to an aspect of the present invention. Computer system 400 includes
a monitor 401 or other communication output device, a keyboard 402
or other communication input device, and a motherboard 404.
Motherboard 404 can carry a microprocessor 406 or other data
processing unit, and at least one memory device 408. Memory device
408 can comprise various aspects of the invention described above,
including, for example, one or more of the wordlines, bitlines and
DRAM unit cells. Memory device 408 can comprise an array of memory
cells, and such array can be coupled with addressing circuitry for
accessing individual memory cells in the array. Further, the memory
cell array can be coupled to a read circuit for reading data from
the memory cells. The addressing and read circuitry can be utilized
for conveying information between memory device 408 and processor
406. Such is illustrated in the block diagram of the motherboard
404 shown in FIG. 11. In such block diagram, the addressing
circuitry is illustrated as 410 and the read circuitry is
illustrated as 412.
[0041] In particular aspects of the invention, memory device 408
can correspond to a memory module. For example, single in-line
memory modules (SIMMs) and dual in-line memory modules (DIMMs) may
be used in the implementation which utilizes the teachings of the
present invention. The memory device can be incorporated into any
of a variety of designs which provide different methods of reading
from and writing to memory cells of the device. One such method is
the page mode operation. Page mode operations in a DRAM are defined
by the method of accessing a row of a memory cell arrays and
randomly accessing different columns of the array. Data stored at
the row and column intersection can be read and output while that
column is accessed.
[0042] An alternate type of device is the extended data output
(EDO) memory which allows data stored at a memory array address to
be available as output after the addressed column has been closed.
This memory can increase some communication speeds by allowing
shorter access signals without reducing the time in which memory
output data is available on a memory bus. Other alternative types
of devices, by way of example only, include SDRAM, DDR SDRAM,
SLDRAM, VRAM and Direct RDRAM, as well as others such as SRAM or
Flash memories.
[0043] FIG. 12 illustrates a simplified block diagram of a
high-level organization of various embodiments of an exemplary
electronic system 700 of the present invention. System 700 can
correspond to, for example, a computer system, a process control
system, or any other system that employs a processor and associated
memory. Electronic system 700 has functional elements, including a
processor or arithmetic/logic unit (ALU) 702, a control unit 704, a
memory device unit 706 and an input/output (I/O) device 708.
Generally, electronic system 700 will have a native set of
instructions that specify operations to be performed on data by
processor 702 and other interactions between processor 702, memory
device unit 706 and I/O devices 708. Control unit 704 coordinates
all operations of processor 702, memory device 706 and I/O devices
708 by continuously cycling through a set of operations that cause
instructions to be fetched from memory device 706 and executed. In
various embodiments, memory device 706 includes, but is not limited
to, random access memory (RAM) devices, read-only memory (ROM)
devices, and peripheral devices such as a floppy disk drive and a
compact disk CD-ROM drive. One of ordinary skill in the art will
understand, upon reading and comprehending this disclosure, that
any of the illustrated electrical components are capable of being
fabricated to include DRAM cells, wordlines and bitlines in
accordance with various aspects of the present invention.
[0044] FIG. 13 is a simplified block diagram of a high-level
organization of various embodiments of an exemplary electronic
system 800. The system 800 includes a memory device 802 that has an
array of memory cells 804, address decoder 806, row access
circuitry 808, column access circuitry 810, read/write control
circuitry 812 for controlling operations, and input/output
circuitry 814. Memory device 802 further includes power circuitry
816, and sensors 820, such as current sensors for determining
whether a memory cell is in a low-threshold conducting state or in
a high-threshold non-conducting state. The illustrated power
circuitry 816 includes power supply circuitry 880, circuitry 882
for providing a reference voltage, circuitry 884 for providing the
first wordline with pulses, circuitry 886 for providing the second
wordline with pulses, and circuitry 888 for providing the bitline
with pulses. System 800 also includes a processor 822, or memory
controller for memory accessing.
[0045] Memory device 802 receives control signals 824 from
processor 822 over wiring or metallization lines. Memory device 802
is used to store data which is accessed via I/O lines. It will be
appreciated by those skilled in the art that additional circuitry
and control signals can be provided, and that memory device 802 has
been simplified to help focus on the invention. At least one of
processor 822 or memory device 802 can include a DRAM cell of the
type described previously in this disclosure.
[0046] The various illustrated systems of this disclosure are
intended to provide a general understanding of various applications
for the circuitry and structures of the present invention, and are
not intended to serve as a complete description of all the elements
and features of an electronic system using memory cells in
accordance with aspects of the present invention. One of ordinary
skill in the art will understand that the various electronic
systems can be fabricated in single-package processing units, or
even on a single semiconductor chip, in order to reduce the
communication time between the processor and the memory
device(s).
[0047] Applications for memory cells, wordlines and bitlines can
include electronic systems for use in memory modules, device
drivers, power modules, communication modems, processor modules,
and application-specific modules, and may include multilayer,
multichip modules. Such circuitry can further be a subcomponent of
a variety of electronic systems, such as a clock, a television, a
cell phone, a personal computer, an automobile, an industrial
control system, an aircraft, and others.
[0048] In compliance with the statute, the invention has been
described in language more or less specific as to structural and
methodical features. It is to be understood, however, that the
invention is not limited to the specific features shown and
described, since the means herein disclosed comprise preferred
forms of putting the invention into effect. The invention is,
therefore, claimed in any of its forms or modifications within the
proper scope of the appended claims appropriately interpreted in
accordance with the doctrine of equivalents.
* * * * *