U.S. patent application number 10/983257 was filed with the patent office on 2005-05-05 for reducing dopant losses during annealing processes.
Invention is credited to Miles, Donald S..
Application Number | 20050093034 10/983257 |
Document ID | / |
Family ID | 32990174 |
Filed Date | 2005-05-05 |
United States Patent
Application |
20050093034 |
Kind Code |
A1 |
Miles, Donald S. |
May 5, 2005 |
Reducing dopant losses during annealing processes
Abstract
A method of reducing dopant losses is provided. The method
includes providing a transistor structure having a first region,
implanting a dopant into the first region, depositing a control
layer adjacent the first region, and performing a first annealing
process on the transistor structure. The control layer is operable
to prevent at least a portion of the dopant in the first region
from diffusing out of the first region toward the control layer
during the first annealing process.
Inventors: |
Miles, Donald S.; (Plano,
TX) |
Correspondence
Address: |
TEXAS INSTRUMENTS INCORPORATED
P O BOX 655474, M/S 3999
DALLAS
TX
75265
|
Family ID: |
32990174 |
Appl. No.: |
10/983257 |
Filed: |
November 4, 2004 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
10983257 |
Nov 4, 2004 |
|
|
|
10404704 |
Mar 31, 2003 |
|
|
|
6833292 |
|
|
|
|
Current U.S.
Class: |
257/288 ;
257/316; 257/328; 257/344; 257/408; 257/E21.438; 257/E29.266 |
Current CPC
Class: |
H01L 29/6656 20130101;
H01L 29/6659 20130101; H01L 29/7833 20130101; H01L 29/665
20130101 |
Class at
Publication: |
257/288 ;
257/316; 257/328; 257/344; 257/408 |
International
Class: |
H01L 029/76; H01L
031/062; H01L 031/119 |
Claims
1-14. (canceled)
15. An integrated circuit, comprising: a transistor comprising a
first active region, the first active region having been formed at
least by: implanting a dopant into a first region of a transistor
structure; forming a control layer adjacent the first region, the
control layer operable to prevent at least a portion of the dopant
in the first region from diffusing from the first region toward the
control layer during annealing; and performing a first annealing
process on the transistor structure.
16. The integrated circuit of claim 15, wherein: the first active
region is an active source region; the transistor further comprises
an active drain region; the active drain region having been formed
at least by: implanting a dopant into a second region of the
transistor structure; forming the control layer adjacent the second
region, the control layer operable to prevent at least a portion of
the dopant in the second region from diffusing from the second
region toward the control layer during annealing; and performing
the first annealing process on the transistor structure.
17. The integrated circuit of claim 16, wherein: the transistor
further comprises an active gate region; the active gate region
having been formed at least by: implanting a dopant into a third
region of the transistor structure; forming the control layer
adjacent the third region, the control layer operable to prevent at
least a portion of the dopant in the third region from diffusing
from the third region toward the control layer during annealing;
and performing the first annealing process on the transistor
structure.
18. The integrated circuit of claim 15, wherein the control layer
comprises an oxide layer.
19. The integrated circuit of claim 15, wherein the control layer
has a thickness of at least 50 angstroms.
20. The integrated circuit of claim 15, wherein the control layer
is formed over a thin oxide layer adjacent the first region.
21. The integrated circuit of claim 15, the first active region of
the transistor having been formed at least by: removing a first
portion of the control layer such that a second first portion of
the control layer adjacent a first portion of a first surface of
the doped first region remains; and depositing a metal layer
adjacent the doped first region and the remaining second portion of
the control layer such that the remaining second portion of the
control layer prevents the metal layer from contacting the first
portion of the first surface the doped first region.
22. The integrated circuit of claim 21, wherein the first region of
the transistor comprises a gate poly region.
23. The integrated circuit of claim 22, wherein the first surface
of the doped first region is a side surface of the gate poly
region.
24. The integrated circuit of claim 21, the first active region of
the transistor having been formed at least by performing a second
annealing process on the transistor structure.
Description
TECHNICAL FIELD OF THE INVENTION
[0001] This invention relates in general to annealing processes in
semiconductor device fabrication, and, more particularly, to
reducing dopant losses during annealing processes in semiconductor
device fabrication.
BACKGROUND OF THE INVENTION
[0002] Integrated circuits include various semiconductor devices,
such as transistors and capacitors, for example. During the
fabrication of such semiconductor devices, particular regions may
be implanted with a dopant, or "doped," and annealed to activate
the doped regions. For example, during fabrication of a transistor
structure, a source, drain and gate poly region may be doped, and
the transistor structure may subsequently be placed in a furnace
for one or more annealing process, such as a source/drain anneal,
in order to activate the source, drain and gate regions. In
addition, fabrication may include one or more silicidation
processes which may include a silicide annealing process.
[0003] However, during these annealing processes, a portion of the
dopant may escape or diffuse away from the source, drain and gate
regions toward adjacent regions of the transistor structure. Such
dopant losses in the source, drain and gate regions of the
transistor structure reduce the effectiveness of the resulting
transistor, and may even cause the transistor to operate
improperly, such as by failing to turn on or off as desired.
Compensating for such dopant losses may require an increase in the
amount of energy or implant dosage used to implant dopant into the
doped regions, which places additional strain on the implanting
equipment.
[0004] For example, FIG. 1 illustrates an example prior art
transistor structure 10 including dopant losses occurring during a
source/drain anneal. Transistor structure 10 comprises an active
source region 12 and an active drain region 14 formed in a
substrate 16, as well as a gate region 18. Substrate 16 may be
formed from silicon, gallium arsenide, or any other material
suitable to form a transistor substrate.
[0005] A gate dielectric layer 30 may be formed partially or
completely over or around gate 18. As shown in FIG. 1, gate
dielectric 30 may also extend over source region 12 and/or drain
region 14. Gate dielectric layer 30 may comprise silicon dioxide or
any other material suitable for forming a gate dielectric
layer.
[0006] Source and drain regions 12 and 14 are formed by implanting
one or more dopants through dielectric layer 30 into a first and
second region 20 and 22, respectively, of substrate 16 using any
suitable known doping method. Dielectric layer 30 may be at least
partially or significantly removed or degraded due to various
fabrication processes performed prior to the implanting of dopants
to form source and drain regions 12 and 14. In some situations,
dielectric layer 30 may be completely removed or degraded prior to
the dopant being implanted. In such situations, upper portions of
first and second regions 20 and 22 may be damaged by the dopant
implanting process.
[0007] A first and second moderately doped region (MDD) 24 and 26
may also be formed in substrate 16 adjacent source region 12 and
drain region 14, respectively. Moderately doped regions 24 and 26
may be formed by implanting a lower concentration of dopant (as
compared with source and drain regions 12 and 14) into substrate 16
using any suitable known doping method.
[0008] Gate 18 is formed adjacent substrate 16 between source and
drain regions 12 and 14. It should be noted that the term
"adjacent" as used throughout this document includes immediately
adjacent (or contacting), as well as proximate to. Thus, for
example, as shown in FIG. 1, gate 18 may be adjacent to substrate
16 with a thin dielectric layer 30 disposed between gate 18 and
substrate 16, as discussed below.
[0009] Gate 18 may comprise one or more conductive materials
suitable for use as a transistor gate, such as titanium, titanium
nitride, tungsten, polysilicon, or amorphous silicon. In some
embodiments, gate 18 is formed by implanting one or more dopants
into a gate poly region 28 of transistor structure 10 using any
suitable known doping method. Source and drain regions 12 and 14
and gate 18 may be doped using one or more of the same or different
doping processes.
[0010] A first deposited oxide layer 32 may be formed adjacent a
first side 34 and a second side 36 of gate 18, and may extend over
at least a portion of source region 12, drain region 14 and/or
moderately doped regions 24 and 26. A nitride layer 38 may be
formed adjacent first deposited oxide layer 32 on each of the first
and second sides 34 and 36 of gate 18. In addition, a second
deposited oxide layer 40 may be formed over nitride layer 38 on
each of the first and second sides 34 and 36 of gate 18.
[0011] It should be understood that although transistor structure
10 as shown in FIG. 1 includes various layers 30, 32, 38 and 40, in
alternative embodiments transistor structure 10 may include any
suitable combination of similar and/or different layers.
[0012] As discussed above, source and drain regions 12 and 14 are
formed by implanting a dopant (or a plurality of dopants) through
dielectric layer 30 into first and second regions 20 and 22 of
substrate 16. The dopant in source and drain regions 12 is then
"activated" in order to define an active source 42 and an active
drain 44 of a transistor by performing a source/drain anneal, or
heat treatment, on transistor structure 10.
[0013] During the source/drain anneal, a portion of the dopant
within source region 12, drain region 14 and gate poly region 28
diffuses or escapes into adjacent or surrounding areas. For
example, arrows 46 and 48 indicate dopant diffusing from source and
drain regions 12 and 14, respectively, through dielectric layer 30
during the source/drain anneal. Similarly, arrows 50 indicate
dopant diffusing from gate poly region 28 through dielectric layer
30 during the source/drain anneal.
[0014] Dielectric layer 30 may be operable to prevent a portion of,
or reduce the amount of, dopant loss from source region 12, drain
region 14 and gate poly region 28 during the source/drain anneal,
depending on the thickness of dielectric layer 30. However, in
conventional and advanced fabrication processes, dielectric layer
30 may be relatively thin (such as less than 20 angstroms, for
example) or nonexistent, and therefore unable to prevent a
significant amount of the dopant loss from source region 12, drain
region 14 and gate poly region 28.
[0015] In addition, dielectric layer 30 may vary in thickness
across the area of dielectric layer 30, as well as throughout the
various steps or sub-processes of the fabrication process, and, as
discussed above, may be partially or even completely removed or
degraded due to various fabrication processes, all of which may
allow relatively large amounts of dopant to diffuse away from all
or portions of source region 12, drain region 14 and gate poly
region 28 during the source/drain anneal.
[0016] At some time subsequent to the source/drain anneal shown in
FIG. 1, one or more silicide regions may be formed in transistor
structure 10, which formation includes a silicide anneal process,
as discussed below regarding FIG. 2.
[0017] FIG. 2 illustrates prior art transistor structure 10
including dopant losses occurring during a silicide anneal. After
the source/drain anneal (discussed above with reference to FIG. 1)
is performed, dielectric layer 30 is removed (assuming that at
least a portion of dielectric layer 30 still remains). As shown in
FIG. 2, a metal layer (such as a layer of titanium, cobalt, nickel,
or platinum, or other suitable metal), or film, 60 is deposited
adjacent transistor structure 10, such as by using a sputtering
process, for example. Transistor structure 10 is then heated using
a thermal cycle, which may include one or more heating processes,
during which metal layer 60 reacts with the silicon in active
source 42, active drain 44 and gate 18 to form silicide regions 62,
64 and 66 in active source 42, active drain 44 and gate 18,
respectively.
[0018] During at least a portion of the thermal cycle, which may be
referred to as a silicide anneal, a portion of the remaining dopant
within active source 42, active drain 44 and gate 18 diffuses or is
pulled into silicide regions 62, 64 and 66. For example, arrows 68,
70 and 72 indicate dopant loss from active source 42, active drain
44 and gate 18 into silicide regions 62, 64 and 66, respectively,
during the silicide anneal.
[0019] Dopant losses occurring during the source/drain anneal
(shown in FIG. 1) and silicide anneal (shown in FIG. 2) reduce the
effectiveness of the transistor resulting from transistor structure
10, and may even cause the transistor to operate improperly, such
as by failing to turn on or off as desired. In order to compensate
for such dopant losses, designers may be required to increase the
amount of energy or implant dosage used to implant dopant into
source region 12, drain region 14 and gate poly region 28, which
places additional strain on the implanting equipment.
SUMMARY OF THE INVENTION
[0020] In accordance with the present invention, a system and
method is provided that reduces or substantially eliminates dopant
losses caused by annealing processes used during the fabrication of
semiconductor devices, such as transistors.
[0021] According to one embodiment, a method of reducing dopant
losses is provided. The method includes providing a transistor
structure having a first region, implanting a dopant into the first
region, depositing a control layer adjacent the first region, and
performing a first annealing process on the transistor structure.
The control layer is operable to prevent at least a portion of the
dopant in the first region from diffusing out of the first region
toward the control layer during the first annealing process.
[0022] According to another embodiment, an integrated circuit is
provided. The integrated circuit includes a transistor comprising a
first active region having been formed at least by implanting a
dopant into a first region of a transistor structure, depositing a
control layer adjacent the first region, and performing a first
annealing process on the transistor structure. The control layer is
operable to prevent at least a portion of the dopant in the first
region from diffusing out of the first region toward the control
layer during the first annealing process.
[0023] Various embodiments of the present invention may benefit
from numerous advantages. It should be noted that one or more
embodiments may benefit from some, none, or all of the advantages
discussed below.
[0024] One advantage is that a cap or control layer may be used to
reduce dopant losses occurring during a source/drain anneal
performed during the fabrication of a transistor. Such dopant
losses may reduce the effectiveness of the transistor and cause the
transistor to operate improperly, such as by failing to turn on or
off as desired.
[0025] Another advantage is that dopant losses occurring during a
silicide anneal performed during the fabrication of the transistor
may also be reduced. In some embodiments, an anisotropic etch may
be used to remove a portion of the control layer while leaving
sidewalls remaining on each side of the transistor gate. The
sidewalls operate to reduce the area of contact between the gate
and a deposited silicide layer, which reduces the size of the
silicide region formed in the gate, which in turn reduces the
amount of dopant losses occurring during the subsequent silicide
anneal.
[0026] Other advantages will be readily apparent to one having
ordinary skill in the art from the following figures, descriptions,
and claims.
BRIEF DESCRIPTION OF THE DRAWINGS
[0027] For a more complete understanding of the present invention
and for further features and advantages, reference is now made to
the following description, taken in conjunction with the
accompanying drawings, in which:
[0028] FIG. 1 illustrates a prior art transistor structure
including dopant losses occurring during a source/drain anneal;
[0029] FIG. 2 illustrates a prior art transistor structure
including dopant losses occurring during a silicide anneal;
[0030] FIG. 3 illustrates a transistor structure including a
control layer for reducing dopant losses occurring during a
source/drain anneal in accordance with an embodiment of the present
invention;
[0031] FIG. 4 illustrates the transistor structure of FIG. 3
including dopant losses occurring during a subsequent silicide
anneal;
[0032] FIG. 5 illustrates the transistor structure of FIG. 3
including residual gate sidewalls for reducing dopant losses
occurring during a subsequent silicide anneal in accordance with an
embodiment of the present invention; and
[0033] FIG. 6 illustrates a method of reducing dopant losses
associated with both a source/drain anneal and a silicide anneal
performed during the fabrication of a transistor in accordance with
an embodiment of the present invention.
DETAILED DESCRIPTION OF THE DRAWINGS
[0034] Example embodiments of the present invention and their
advantages are best understood by referring now to FIGS. 1 through
6 of the drawings, in which like numerals refer to like parts.
[0035] Among other things, various embodiments of the present
invention are directed toward reducing dopant losses during
transistor fabrication processes. FIG. 3 illustrates a transistor
structure 100 including a control layer for reducing dopant losses
occurring during a source/drain anneal in accordance with an
embodiment of the present invention. Transistor structure 100 is
similar to transistor structure 10 shown in FIGS. 1 and 2, and
includes source region 12, drain region 14, and gate 18. However,
as shown in FIG. 3, a cap or control layer 102 is formed over
transistor structure 100 before performing the source/drain anneal.
Control layer 102 is generally operable to reduce the amount of
dopant loss from source region 12, drain region 14 and gate 18,
indicated by arrows 146, 148 and 150, respectively, during the
source/drain anneal performed to activate active source 42 and
active drain 44.
[0036] Control layer 102 may comprise a layer of oxide or any other
suitable material or combination of materials operable to prevent
or reduce dopant loss during an anneal or heating process. Control
layer 102 may be deposited and/or grown, and may be formed over
dielectric layer 30, as shown in FIG. 3. As discussed above,
dielectric layer 30 may be partially or completely removed or
degraded due to various fabrication processes performed. Thus, in a
situation in which dielectric layer 30 has been completely removed,
control layer 102 may be formed directly adjacent at least some
portions of source and drain regions 42 and 44.
[0037] Control layer 102 may be relatively thick, at least compared
to dielectric layer 30. For example, in some embodiments, control
layer 102 has a thickness approximately equal to or greater than 50
angstroms. In a particular embodiment, control layer 102 has a
thickness greater than 100 angstroms. The thickness of control
layer 102 may be predetermined and selected to achieve a desired
maximum level of dopant loss or diffusion, or to prevent a
particular amount of dopant loss or diffusion.
[0038] FIG. 4 illustrates transistor structure 100 of FIG. 3
including dopant losses occurring during a subsequent silicide
anneal. After the source/drain anneal discussed above with
reference to FIG. 3, control layer 102 and dielectric layer 30 are
removed using an isotropic etch, such as a wet, or chemical,
etch.
[0039] A metal layer 60 is deposited adjacent transistor structure
100, such as by using a sputtering process, for example, and
transistor structure 100 is then heated using a thermal cycle, or
silicide anneal, which may include one or more heating
processes.
[0040] During the thermal cycle, metal layer 60 reacts with the
portions of active source 42, active drain 44 and gate 18 in which
metal layer 60 is in direct contact to form source and drain
silicide regions 62 and 64, as well as gate silicide region 66,
within active source 42, active drain 44 and gate 18, respectively.
In addition, during the thermal cycle, a portion of the remaining
dopant within active source 42, active drain 44 and gate 18
diffuses or is pulled into silicide regions 62, 64 and 66, as
indicated by arrows 68, 70 and 72.
[0041] FIG. 5 illustrates the transistor structure 100 of FIG. 3
including residual sidewalls of control layer 102 for reducing
dopant losses occurring during the silicide anneal in accordance
with an embodiment of the present invention. FIG. 5 illustrates an
alternative embodiment to that shown in FIG. 4. In the embodiment
shown in FIG. 4, a control layer 102 is removed using an isotropic
etch, as discussed above. In contrast, in the embodiment shown in
FIG. 5, a portion of control layer 102 is removed using an
anisotropic etch, such as a dry etch, reactive ion etch (RIE), or
plasma etch, for example, which leaves a second portion (or
portions) of control layer 102 remaining adjacent gate 18, which
may be useful for reducing the amount of dopant loss during the
thermal cycle, or silicide anneal, performed during a subsequent
silicidation process. In the embodiment shown in FIG. 5, the
remaining portion of control layer 102 comprises a first sidewall
104 adjacent a first portion 108 of a first surface 110 of gate 18
and a second sidewall 106 adjacent a first portion 112 of a second
surface 114 of gate 18.
[0042] A metal layer 60 is deposited adjacent transistor structure
100, such as by using a sputtering process, for example, and
transistor structure 100 is then heated using a thermal cycle, or
silicide anneal, which may include one or more heating processes.
During the thermal cycle, metal layer 60 reacts with the portions
of active source 42 and active drain 44 in which metal layer 60 is
in direct contact to form silicide regions 62 and 64, respectively.
In addition, metal layer 60 reacts with the portion of the gate 18
in which metal layer 60 is in direct contact to form gate silicide
region 116.
[0043] As shown in FIG. 5, metal layer 60 contacts, and thus reacts
with, a second portion 118 of first surface 110 of gate 18 and a
second portion 120 of second surface 114 of gate 18. However, first
and second sidewalls 104 and 106 prevent metal layer 60 from
contacting, and thus reacting with, first portion 108 of first
surface 110 of gate 18 and first portion 112 of second surface 114
of gate 18. Thus, the depth of gate silicide region 116 shown in
the embodiment of FIG. 5 is less than the depth of gate silicide
region 66 shown in the embodiment discussed in connection with FIG.
4.
[0044] During the thermal cycle, or silicide anneal, a portion of
the remaining dopant within active source 42, active drain 44 and
gate 18 diffuses or is pulled into silicide regions 62, 64 and 116,
as indicated by arrows 68, 70 and 72, respectively. The reduced
size of gate silicide region 116 as compared with gate silicide
region 66 results in a lower amount of dopant loss (indicated in
FIG. 5 by arrow 72) from gate 18 into silicide region 116 during
the silicide anneal because this amount of dopant loss is directly
related to the size of the gate silicide region. In other words, by
using sidewalls 104 and 106 remaining from control layer 102 to
reduce the size of gate silicide region 116 formed in gate 18 (as
compared with the size of gate silicide region 66), the amount of
dopant loss occurring during the silicide anneal is reduced.
[0045] Thus, using control layer 102 as shown in FIG. 3, dopant
losses during a source/drain anneal may be reduced. In addition,
using sidewalls 104 and 106 shown in FIG. 5, dopant losses during a
silicide thermal cycle, or silicide anneal, may be reduced.
[0046] FIG. 6 illustrates a method of reducing dopant losses
associated with both a source/drain anneal and a silicide anneal in
transistor fabrication in accordance with an embodiment of the
present invention. At step 200, a transistor structure 100 is
provided. Transistor structure 100 includes a first region 20, a
second region 22, and a gate poly region 28.
[0047] At step 202, a dielectric layer 30 is formed over transistor
structure 100. Dielectric layer 30 may be relatively thin (such as
less than 20 angstroms, for example) and may vary in thickness
during the various steps in the fabrication process.
[0048] At step 204, one or more dopants are implanted through
dielectric layer 30 into first region 20, second region 22, and
gate poly region 28 to form a source region 12, a drain region 14,
and a gate 18. Step 204 may comprise one or more implant processes
that may be performed at different times within the fabrication
process. As discussed above, in some situations, dielectric layer
30 may partially or completely removed or degraded due to various
fabrication processes performed prior to the implanting of dopants
at step 204.
[0049] At step 206, a control layer 102 is formed over dielectric
layer 30 adjacent source region 12, drain region 14, and gate 18.
Control layer 102 may be deposited and/or grown over dielectric
layer 30 (assuming that at least a portion of dielectric layer 30
still remains). Control layer 102 may comprise a layer of oxide
having a thickness greater than that of dielectric layer 30. The
thickness of control layer 102 may be selected to prevent a
particular amount of dopant loss or diffusion.
[0050] In an alternative embodiment, control layer 102 is formed
over transistor structure 100 prior to the implanting of dopants at
step 204. For example, in a situation in which dielectric layer 30
is partially or completely removed or degraded prior to the
implanting of dopants at step 204, control layer 102 may be formed
prior to the implanting of dopants at step 204 in order to protect
upper portions of transistor structure 100 during the implant
processes. The dopants may then be implanted through control layer
102 and any remaining portions of dielectric layer 30 into first
region 20, second region 22, and gate poly region 28 to form source
region 12, drain region 14, and gate 18, respectively.
[0051] At step 208, a source/drain annealing process is performed
on the transistor structure 100 in order to activate the dopant in
source region 12 and drain region 14 to form active source 42 and
active drain 44 for the transistor resulting from transistor
structure 100. During the source/drain anneal, an amount of dopant
typically escapes or diffuses from source region 12, drain region
14, and gate 18 toward adjacent or surrounding or areas. However,
control layer 102 reduces or prevents at least a portion of dopant
loss from source region 12, drain region 14, and gate 18, at least
in the direction of control layer 102 (as indicated, for example,
by arrows 146, 148 and the top three arrows 150 in FIG. 3).
[0052] At step 210, a first portion of control layer 102 and
dielectric layer 30 is removed using an anisotropic etch, leaving a
second portion (or portions) of control layer 102 which form a
first sidewall 104 adjacent a first portion 108 of a first surface
110 of gate 18 and a second sidewall 106 adjacent a first portion
112 of a second surface 114 of gate 18, as shown in FIG. 5. A
portion of dielectric layer 30 may also remain between each
sidewall 104 and 106 and gate 18, as shown in FIG. 5.
[0053] At step 212, a metal layer 60 is deposited adjacent
transistor structure 100, such as shown in FIG. 5, and transistor
structure 100 is heated using a thermal cycle, or silicide anneal.
During the thermal cycle, metal layer 60 reacts with the portions
of active source 42 and active drain 44 in which metal layer 60 is
in direct contact to form silicide regions 62 and 64, respectively.
In addition, metal layer 60 reacts with the portion of the gate 18
in which metal layer 60 is in direct contact to form gate silicide
region 116. In particular, as shown in FIG. 5, metal layer 60
contacts, and thus reacts with, a second portion 118 of first
surface 110 of gate 18 and a second portion 120 of second surface
114 of gate 18 to form gate silicide region 116. However, first and
second sidewalls 104 and 106 prevent silicide layer 60 from
reacting with first portion 108 of first surface 110 of gate 18 and
first portion 112 of second surface 114 of gate 18. Thus, sidewalls
104 and 106 operate to reduce the depth of gate silicide region
116.
[0054] During the thermal cycle, or silicide anneal, a portion of
the remaining dopant within active source 42, active drain 44 and
gate 18 diffuses or is pulled into silicide regions 62, 64 and 116,
such as indicated by arrows 68, 70 and 72, respectively, shown in
FIG. 5. As discussed above with respect to FIG. 5, the reduced size
of gate silicide region 116 due to the use of sidewalls 104 and 106
during the formation of gate silicide region 116 reduces the amount
of dopant loss occurring during the silicide anneal. At step 214,
the transistor fabrication may continue, which may include one or
more various fabrication steps or processes.
[0055] Thus, dopant losses during a source/drain anneal may be
reduced by using control layer 102, as discussed above with
reference to steps 206 and 208. In addition, dopant losses during a
silicide thermal cycle, or silicide anneal, may be reduced by using
an anisotropic etch to create sidewalls 104 and 106, as discussed
above with reference to steps 210 and 212.
[0056] Although embodiments of the invention and its advantages
have been described in detail, a person skilled in the art could
make various alterations, additions, and omissions without
departing from the spirit and scope of the present invention as
defined by the appended claims.
* * * * *