U.S. patent application number 10/493867 was filed with the patent office on 2005-03-10 for polishing fluid and polishing method.
Invention is credited to Amanokura, Jin, Anzai, Sou, Fukasawa, Masato, Sakurada, Takafumi, Sasaki, Shouichi.
Application Number | 20050050803 10/493867 |
Document ID | / |
Family ID | 27347759 |
Filed Date | 2005-03-10 |
United States Patent
Application |
20050050803 |
Kind Code |
A1 |
Amanokura, Jin ; et
al. |
March 10, 2005 |
Polishing fluid and polishing method
Abstract
The present invention relates to polishing slurry and polishing
method used for polishing in a process for forming wirings of a
semiconductor device, and the like. There are provided polishing
slurry giving a polished surface having high flatness even if the
polished surface is made of two or more substances, and further,
capable of suppressing metal residue and scratches after polishing,
and a method of chemical mechanical polishing using this. The
polishing slurry of the present invention is polishing slurry
containing at least one of a surfactant and an organic solvent, and
a metal oxide dissolving agent and water, or polishing slurry
containing water and abrasive of which surface has been modified
with an alkyl group, and preferably, it further contains a metal
oxidizer, water-soluble polymer, and metal inhibitor.
Inventors: |
Amanokura, Jin; (Itachi-shi,
Ibaraki, JP) ; Sakurada, Takafumi; (Itachi-shi,
Ibaraki, JP) ; Anzai, Sou; (Itachi-shi, Ibaraki,
JP) ; Fukasawa, Masato; (Hitachi-shi, Ibaraki,
JP) ; Sasaki, Shouichi; (Hitachi-shi, Ibaraki,
JP) |
Correspondence
Address: |
WESTERMAN, HATTORI, DANIELS & ADRIAN, LLP
1250 CONNECTICUT AVENUE, NW
SUITE 700
WASHINGTON
DC
20036
US
|
Family ID: |
27347759 |
Appl. No.: |
10/493867 |
Filed: |
November 5, 2004 |
PCT Filed: |
October 31, 2002 |
PCT NO: |
PCT/JP02/11370 |
Current U.S.
Class: |
51/309 ;
257/E21.304; 51/307; 51/308 |
Current CPC
Class: |
H01L 21/3212 20130101;
C09K 3/1463 20130101; C09G 1/02 20130101; C09K 3/1436 20130101 |
Class at
Publication: |
051/309 ;
051/307; 051/308 |
International
Class: |
B24D 003/02; C09C
001/68; C09K 003/14 |
Foreign Application Data
Date |
Code |
Application Number |
Oct 31, 2001 |
JP |
2001-334376 |
Jan 18, 2002 |
JP |
2002-10280 |
May 31, 2002 |
JP |
2002-160181 |
Claims
1. Polishing slurry comprising a surfactant, metal oxide dissolving
agent and water, and used for polishing of at least a barrier
conductor layer and a conductive substance.
2. Polishing slurry comprising an organic solvent, metal oxide
dissolving agent and water, and used for polishing of at least a
barrier conductor layer and a conductive substance.
3. The polishing slurry according to claim 1 or 2, comprising
abrasive.
4. The polishing slurry according to claim 3, wherein the abrasive
is at least one selected from silica, alumina, ceria, titania,
zirconia and germania.
5. The polishing slurry according to claim 3, wherein the surface
of the abrasive is modified with an alkyl group.
6. Polishing slurry comprising abrasive and water and used for
polishing of at least a barrier conductor layer and a conductive
substance wherein the surface of the abrasive is modified with an
alkyl group.
7. The polishing slurry according to claim 6, wherein the abrasive
is at least one selected from silica, alumina, ceria, titania,
zirconia and germania of which surface is modified with an alkyl
group.
8. The polishing slurry according to claim 6 or 7, comprising a
metal oxide dissolving agent.
9. The polishing slurry according to claim 6 or 7, comprising at
least one of a surfactant and an organic solvent.
10. The polishing slurry according to claim 1 or 2, wherein the
metal oxide dissolving agent is at least one selected from organic
acids, esters of organic acids, ammonium salts of organic acids and
sulfuric acid.
11. The polishing slurry according to claim 2, wherein the organic
solvent is contained in a proportion of 0.1 to 95 wt %.
12. The polishing slurry according to claim 2, wherein the organic
solvent is at least one selected from glycols and derivatives
thereof, alcohols and carbonic esters.
13. The polishing slurry according to claim 1, wherein the
surfactant is at least one selected from nonionic surfactants and
anionic surfactants.
14. The polishing slurry according to claim 1, wherein the
surfactant is at least one selected from perfluoroalkanesulfonic
acids and derivatives thereof.
15. The polishing slurry according to claim 1, wherein the
surfactant is contained in a proportion of 0.00001 to 20 wt %.
16. The polishing slurry according to claim 1 or 2, comprising a
metal oxidizer.
17. The polishing slurry according to claim 16, wherein the metal
oxidizer is at least one selected from hydrogen peroxide, nitric
acid, potassium periodate, hypochlorous acid and ozone water.
18. The polishing slurry according to claim 1 or 2, comprising a
water-soluble polymer having a weight-average molecular weight of
500 or more.
19. The polishing slurry according to claim 18, wherein the
water-soluble polymer is at least one selected from
polysaccharides, polycarboxylic acids, polycarboxylic esters and
salts thereof, and vinyl-based polymers.
20. A polishing method comprising a first polishing process of
polishing a conductive substance layer of a substrate having an
interlayer insulating film carrying a surface composed of a concave
portion and a convex portion, a barrier conductor layer coating the
interlayer insulating film along its surface and a conductive
substance layer filling the concave portion to coat the barrier
conductor layer, to expose the barrier conductor layer on the
convex portion, and a second polishing process of chemical
mechanical polishing at least the barrier conductor layer and the
conductive substance layer on the concave portion while feeding the
polishing slurry according to claim 1 or 2 to expose the interlayer
insulating film on the convex portion.
21. The polishing method according to claim 20, wherein the
interlayer insulating film is a silicon-based film or an organic
polymer film.
22. The polishing method according to claim 20, wherein the
conductive substance is mainly composed of copper.
23. The polishing method according to claim 20, wherein the barrier
conductor layer is a barrier layer of preventing diffusion of the
conductive substance into the interlayer insulating film, and
comprises at least one selected from tantalum, tantalum nitride,
tantalum alloy, other tantalum compounds, titanium, titanium
nitride, titanium alloy, other titanium compounds, tungsten,
tungsten nitride, tungsten alloy, and other tungsten compounds.
24. The polishing slurry according to any of claims 1, 2 and 6,
used for polishing of parts of the interlayer insulating film, in
addition to polishing of the barrier conductor layer and the
conductive substance.
25. The polishing slurry according to claim 24, wherein the
interlayer insulating film is a silicon-based film or an organic
polymer film.
26. The polishing slurry according to any of claims 1, 2 and 6,
wherein the conductive substance is mainly composed of copper.
27. The polishing slurry according to any of claims 1, 2 and 6,
wherein the barrier conductor layer is a barrier layer of
preventing diffusion of the conductive substance into the
interlayer insulating film, and comprises at least one selected
from tantalum, tantalum nitride, tantalum alloy, other tantalum
compounds, titanium, titanium nitride, titanium alloy, other
titanium compounds, tungsten, tungsten nitride, tungsten alloy, and
other tungsten compounds.
28. The polishing method according to claim 20, for polishing of
parts of the interlayer insulating film, in addition to polishing
of the barrier conductor layer and the conductive substance.
Description
FIELD OF THE INVENTION
[0001] The present invention relates to polishing slurry and a
polishing method used for polishing in a process of forming wiring
of a semiconductor device, and the like.
BACKGROUND TECHNOLOGY
[0002] Recently, novel fine processing technologies are being
developed with increase in the degree of integration and the
performance of semiconductor integration circuits (hereinafter,
referred to as LSI). Also a chemical mechanical polishing
(hereinafter, referred to as CMP) method is one of these
technologies, and is a technology frequently used in flattening of
an interlayer insulating film, formation of a metal plug and
formation of implanted wiring in an LSI production process,
particularly, a multi-layer wiring formation process. This
technology is disclosed, for example, in U.S. Pat. No.
4,944,836.
[0003] Recently, for increasing the performance of LSI, utilization
of copper and copper alloy has been tried as a conductive substance
of a wiring material. However, it is difficult to finely process
copper and copper alloy by a conventional dry etching method
frequently used in formation of aluminum alloy wiring. Therefore,
there is mainly adopted what is called damascene method in which a
thin film of copper or copper alloy is piled and implanted on an
insulating film on which trenches have been previously formed, and
the above-mentioned thin film on portions other than the trench
portions is removed by CMP to form implanted wiring. This
technology is disclosed in, for example, Japanese Patent
Application Laid-Open (JP-A) No. H2-278822.
[0004] In a general metal CMP method of polishing a metal for
wiring portions such as copper, copper alloy and the like,
polishing cloth (pad) is pasted on a polishing plate (platen) in
the form of disc, the surface of the substrate on which a metal
film has been formed is pressed to the surface of the polishing
cloth while wetting the surface of the polishing cloth with
polishing slurry for metal, and the polishing plate is rotated
under condition of given pressure applied to the metal film from
the rear surface of the polishing cloth (hereinafter, referred to
as polishing pressure), to remove the metal film at a convex part
by relative mechanical friction between the polishing slurry and
the convex part of the metal film.
[0005] Polishing slurry for metal used for CMP is in general
composed of an oxidizer and abrasive, and if necessary, a metal
oxide dissolving agent and a protective film formation agent are
further added. It is believed a basic mechanism to first oxidize
the surface of a metal film with an oxidizer, and scrape off its
oxidized surface with abrasive. The oxidized layer on the metal
surface at a concave portion does not contact significantly with a
polishing pad and an effect of scraping off with abrasive is not
exerted on the surface, consequently, the metal layer at a convex
portion is removed with progress of CMP, leading to flattening of
the surface of the substrate. The details of this are disclosed in
Journal of Electrochemical Society, vol. 138, No. 11 (1991), pp.
3460 to 3464.
[0006] As a method of enhancing the polishing speed by CMP, it is
the effective to add a metal oxide dissolving agent. The reason for
this is interpreted that if particles of a metal oxide scraped off
by abrasive are dissolved (hereinafter, referred to as etching), an
effect of scraping off with abrasive increases. Though the
polishing speed by CMP is improved by addition of a metal oxide
dissolving agent, when, on the other hand, also an oxide layer on
the surface of a metal film at a concave portion is etched to
expose the surface of the metal film, the surface of the metal film
is further oxidized with the oxidizer, and by repetition of this
procedure, etching of the metal film at a concave portion
progresses. Consequently, a phenomenon of formation of depression
in the form of dish at the central portion of the surface of
implanted metal wiring after polishing (hereinafter, referred to as
dishing) occurs, deteriorating the flattening effect.
[0007] For preventing this, a protective film formation agent is
further added. The protective film formation agent forms a
protective film on an oxide layer of the surface of a metal film,
and resultantly prevents dissolution of the oxide layer into
polishing slurry. It is desired that this protective film can be
easily scraped off by abrasive and does not decrease the polishing
speed by CMP.
[0008] For suppressing corrosion during polishing and dishing of
copper or copper alloy and for forming LSI wiring of high
reliability, there is suggested a method of using polishing slurry
for CMP containing BTA as a protective film formation agent and a
metal oxide dissolving agent composed of amide sulfuric acid or
aminoacetic acid such as glycine and the like. This technology is
described, for example, in Japanese Patent Application Laid-open
No. 8-83780.
[0009] In formation of metal implanting such as formation of
damascene wirings of copper, copper alloy and the like and
formation plug wirings of tungsten and the like, when the speed of
polishing a silicon dioxide film which is an interlayer insulating
film formed on parts other than the implanting formation parts is
also large, thinning in which the thickness of wirings also
including the interlayer insulating film decreases occurs. As a
result, increase in wiring resistance occurs, therefore, a property
is required in which the polishing speed of a silicon dioxide film
is sufficiently small in comparison with the metal film to be
polished. For suppressing the polishing speed of silicon dioxide by
an anion generated by dissociation of an acid, there is suggested a
method of increasing pH of polishing slurry more than pKa-0.5. This
technology is described in, for example, Japanese Patent
Publication No, 2819196.
[0010] On the other hand, as the lower layer of a metal for wiring
part such as copper, copper alloy and the like, a conductor layer
of, for example, a tantalum compound such as tantalum, tantalum
alloy, tantalum nitride and the like is formed, as a barrier
conductor layer for preventing diffusion of copper into an
interlayer insulating film and improving close adherence with this
(hereinafter, referred to as barrier layer). Therefore, on parts
other than wiring parts of implanting copper or copper alloy, an
exposed barrier layer should be removed by CMP. However, the
conductor of this barrier layer has high hardness as compared with
copper or copper alloy, consequently, sufficient polishing speed is
not obtained and its flattening property deteriorates in may cases
even if a polishing material for copper or copper alloy is
combined. Therefore, a two-stage polishing method composed of a
first process of polishing a metal for wiring and a second process
of polishing a barrier layer is investigated.
[0011] In the second process of polishing a barrier layer of the
above-mentioned two-stage polishing method, polishing of an
interlayer insulating film, for example, silicon dioxide, or
organosilicate glass using trimethylsilane as a starting material
which is a Low-k (low permittivity) film, or whole aromatic
ring-based Low-k film is required in some cases for flattening. In
this case, there is mentioned a method of polishing while
maintaining the flatness of the surface of a barrier layer, a metal
for wiring and an interlayer insulating film by approximately
equalizing the polishing speed of a barrier layer and metal for
wiring part and the polishing speed of an interlayer insulating
film so that the polished surface is flat when all of the
interlayer insulating film is exposed.
[0012] For increasing the polishing speed of an interlayer
insulating film corresponding to the polishing speed of a barrier
layer and metal for wiring part, there is envisaged, for example,
to increase the size of abrasives in polishing slurry for conductor
of a barrier layer, however, there is a problem that scratch
occurring on copper or copper alloy and an oxide film, causing a
poor electric property.
[0013] Such a poor electric property is generated also by poor
washing after polishing by CMP. On the other hand, there is a
problem of occurrence of a short-cut defect since the copper
residue on high density wiring parts cannot be removed in a CMP
process.
[0014] The present invention provides polishing slurry giving a
polished surface having high flatness in view of the
above-mentioned problems. Further, there is provided polishing
slurry by which the polishing speed of an interlayer insulating
film is as fast as the polishing speed of a barrier layer and a
metal for wiring part. By this polishing slurry, the speed of
polishing a wiring part can be controlled without decreasing the
speed of polishing a barrier layer. Metal residue and scratches
after polishing can be suppressed. Further, the present invention
provides a polishing method in production of a semiconductor device
excellent in fineness, film thinness, dimension precision and
electric property, and having high reliability, and requiring low
cost.
DISCLOSURE OF THE INVENTION
[0015] The present invention relates to (1) polishing slurry
comprising a surfactant, metal oxide dissolving agent and
water.
[0016] Further, the present invention relates to (2) polishing
slurry comprising an organic solvent, metal oxide dissolving agent
and water.
[0017] Still further, the present invention relates to the
following polishing slurries.
[0018] (3) The polishing slurry according to the above-mentioned
(1) or (2), comprising abrasive.
[0019] (4) The polishing slurry according to the above-mentioned
(3), wherein the abrasive is at least one selected from silica,
alumina, ceria, titania, zirconia and germania.
[0020] (5) The polishing slurry according to the above-mentioned
(3) or (4), wherein the surface of the abrasive is modified with an
alkyl group.
[0021] Further, the present invention relates to (6) Polishing
slurry comprising abrasive and water, wherein the surface of the
abrasive is modified with an alkyl group.
[0022] Still further, the present invention relates to the
following polishing slurries.
[0023] (7) The polishing slurry according to the above-mentioned
(6), wherein the abrasive is at least one selected from silica,
alumina, ceria, titania, zirconia and germania of which surface is
modified with an alkyl group.
[0024] (8) The polishing slurry according to the above-mentioned
(6) or (7), comprising a metal oxide dissolving agent.
[0025] (9) The polishing slurry according to any of the
above-mentioned (6) to (8), comprising at least one of a surfactant
and an organic solvent.
[0026] (10) The polishing slurry according to any of the
above-mentioned (1) to (5), (8) and (9), wherein the metal oxide
dissolving agent is at least one selected from organic acids,
esters of organic acids, ammonium salts of organic acids and
sulfuric acid.
[0027] (11) The polishing slurry according to any of the
above-mentioned (2) to (5), (9) and (10), wherein the organic
solvent is contained in a proportion of 0.1 to 95 wt %.
[0028] (12) The polishing slurry according to any of the
above-mentioned (2) to (5), (9) to (11), wherein the organic
solvent is at least one selected from glycols and derivatives
thereof, alcohols and carbonic esters.
[0029] (13) The polishing slurry according to any of the
above-mentioned (1), (3) to (5), (9) to (12), wherein the
surfactant is at least one selected from nonionic surfactants and
anionic surfactants.
[0030] (14) The polishing slurry according to any of the
above-mentioned (1), (3) to (5), (9) to (13), wherein the
surfactant is at least one selected from perfluoroalkanesulfonic
acids and derivatives thereof.
[0031] (15) The polishing slurry according to any of the
above-mentioned (1), (3) to (5), (9) to (14), wherein the
surfactant is contained in a proportion of 0.00001 to 20 wt %.
[0032] (16) The polishing slurry according to any of the
above-mentioned (1) to (15), comprising a metal oxidizer.
[0033] (17) The polishing slurry according to the above-mentioned
(16), wherein the metal oxidizer is at least one selected from
hydrogen peroxide, nitric acid, potassium periodate, hypochlorous
acid and ozone water.
[0034] (18) The polishing slurry according to any of the
above-mentioned (1) to (17), comprising a water-soluble polymer
having a weight-average molecular weight of 500 or more.
[0035] (19) The polishing slurry according to the above-mentioned
(18), wherein the above-mentioned water-soluble polymer is at least
one selected from polysaccharides, polycarboxylic acids,
polycarboxylic esters and salts thereof, and vinyl-based
polymers.
[0036] The present invention relates to (20) A polishing method
comprising a first polishing process of polishing a conductive
substance layer of a substrate having an interlayer insulating film
carrying a surface composed of a concave portion and a convex
portion, a barrier conductor layer coating the above-mentioned
interlayer insulating film along its surface and a conductive
substance layer filling the above-mentioned concave portion to coat
the barrier conductor layer, to expose the barrier conductor layer
on the above-mentioned convex portion, and a second polishing
process of chemical mechanical polishing at least the barrier
conductor layer and the conductive substance layer on the concave
portion while feeding the polishing slurry according to any of the
above-mentioned (1) to (19) to expose the interlayer insulating
film on the convex portion.
[0037] Further, the present invention relates to the following
polishing methods.
[0038] (21) The polishing method according to the above-mentioned
(20), wherein the above-mentioned interlayer insulating film is a
silicon-based film or an organic polymer film.
[0039] (22) The polishing method according to the above-mentioned
(20) or (21), wherein the conductive substance is mainly composed
of copper.
[0040] (23) The polishing method according to any of the
above-mentioned (20) to (22), wherein the barrier conductor layer
is a barrier layer of preventing diffusion of the above-mentioned
conductive substance into the above-mentioned interlayer insulating
film, and comprises at least one selected from tantalum, tantalum
nitride, tantalum alloy, other tantalum compounds, titanium,
titanium nitride, titanium alloy, other titanium compounds,
tungsten, tungsten nitride, tungsten alloy, and other tungsten
compounds.
BEST MODES FOR CARRYING OUT THE INVENTION
[0041] The first feature of the polishing slurry of the present
invention is comprising at least one of a surfactant and an organic
solvent, and a metal oxide dissolving agent and water. Preferably,
it contains further abrasives and a metal oxidizer. Further, it may
also contain a water-soluble polymer, metal inhibitor and the like,
if necessary.
[0042] Surfactants are classified, in general, into four kinds of
agents of nonionic surfactants, anionic surfactants, cationic
surfactants and ampholytic surfactants.
[0043] As the surfactant in the present invention, fluorine-based
surfactants having a carbon-fluorine chain as a hydrophobic group
can also be used. For example, perfluoroalkanesulfonic acids and
derivatives thereof are exemplified. Preferable are
perfluorooctanesulfonic acid and derivatives thereof. Also
fluorine-based surfactants are classified in four kinds of agents
as described above.
[0044] Examples of the nonionic surfactant include polyoxyethylene
alkyl ethers, polyoxyethylene alkylphenyl ethers,
polyoxyethylenepropyl perfluorooctanesulfoneamide,
polyoxyethylene-polyoxypropylene block polymer, polyoxyethylene
glycerin fatty esters, polyoxyethylene hardened castor oil,
polyethylene glycol fatty esters, propyl-2-hydroxyethyl
perfluorooctanesulfoneamide, sorbitan fatty esters, glycerin fatty
esters, sucrose fatty esters, fatty alkanol amides,
polyoxyethylenealkylamines and derivatives thereof. Also, glycols
such as acetylene diol and ethylene oxide adducts thereof, and the
like are listed. The above-mentioned term "polyoxyethylene" means
inclusion of not only those having a number (n) of ethylene oxide
added of 2 or more but also those having one ethylene oxide
added.
[0045] Examples of the anionic surfactant include salts of
alkylbenzensulfonic acid, perfluorooctanesulfonic acid,
bis[2-(N-propyl perfluorooctanesulfonylamino)ethyl] phosphate,
salts of alkylsulfosuccinates, salts of alkylsulfonic acids, salts
of alkyl ether carboxylic acids, salts of alcohol sulfates, salts
of alkyl ether sulfates, salts of alkylphosphates, and derivatives
thereof.
[0046] Examples of the cationic surfactant include salts of
aliphatic alkylamines, aliphatic quaternary ammonium salts and the
like, and examples of the ampholytic surfactant include salts of
aminocarboxylic acids and the like.
[0047] These surfactants can be used singly or in combination of
two or more.
[0048] As the surfactant in the polishing slurry of the present
invention, preferable are nonionic surfactants and anionic
surfactants, and particularly, those containing no alkali metal are
preferable.
[0049] Further preferable is at least one selected from
polyethylene glycol type nonionic surfactants, polyoxyethylene
alkyl ethers, polyoxyethylene alkylphenyl ethers,
polyoxyethylenepropyl perfluorooctanesulfoneamide, glycols,
glycerin fatty esters, sorbitan fatty esters, fatty alkanolamides,
salts of alcohol sulfates, salts of alkyl ether sulfates, salts of
alkylbenzenesulfonic acids, and salts of alkylphosphates.
[0050] Examples of the polyethylene glycol type nonionic surfactant
include polyethylene glycol fatty esters such as polyethylene
glycol monolaurate, polyethylene glycol monostearate, polyethylene
glycol distearate, polyethylene glycol monooleate and the like.
[0051] The organic solvent contained in the polishing slurry of the
present invention is not particularly restricted, and preferable
are those which can be mixed with water at any ratio.
[0052] Examples thereof include carbonic esters such as ethylene
carbonate, propylene carbonate, dimethyl carbonate, diethyl
carbonate, methyl ethyl carbonate and the like; lactones such as
butyrolactone, propylolactone and the like; glycols such as
ethylene glycol, propylene glycol, diethylene glycol, dipropylene
glycol, triethylene glocyl, tripropylene glycol and the like;
derivatives of glycols such as glycol mono-ethers such as ethylene
glycol monomethyl ether, propylene glycol monomethyl ether,
diethylene glycol monomethyl ether, dipropylene glycol monomethyl
ether, triethylene glycol monomethyl ether, tripropylene glycol
monomethyl ether, ethylene glycol monoethyl ether, propylene glycol
monoethyl ether, diethylene glycol monoethyl ether, dipropylene
glycol monoethyl ether, triethylene glycol monoethyl ether,
tripropylene glycol monoethyl ether, ethylene glycol monopropyl
ether, propylene glycol monopropyl ether, diethylene glycol
monopropyl ether, dipropylene glycol monopropyl ether, triethylene
glycol monopropyl ether, tripropylene glycol monopropyl ether,
ethylene glycol monobutyl ether, propylene glycol monobutyl ether,
diethylene glycol monobutyl ether, dipropylene glycol monobutyl
ether, triethylene glycol monobutyl ether, tripropylene glycol
monobutyl ether and the like, and glycol di-ethers such as ethylene
glycol dimethyl ether, propylene glycol dimethyl ether, diethylene
glycol dimethyl ether, dipropylene glycol dimethyl ether,
triethylene glycol dimethyl ether, tripropylene glycol dimethyl
ether, ethylene glycol diethyl ether, propylene glycol diethyl
ether, diethylene glycol diethyl ether, dipropylene glycol diethyl
ether, triethylene glycol diethyl ether, tripropylene glycol
diethyl ether, ethylene glycol dipropyl ether, propylene glycol
dipropyl ether, diethylene glycol dipropyl ether, dipropylene
glycol dipropyl ether, triethylene glycol dipropyl ether,
tripropylene glycol dipropyl ether, ethylene glycol dibutyl ether,
propylene glycol dibutyl ether, diethylene glycol dibutyl ether,
dipropylene glycol dibutyl ether, triethylene glycol dibutyl ether,
tripropylene glycol dibutyl ether and the like; ethers such as
tetrahydrofuran, dioxane, dimethoxyethane, polyethylene oxide,
ethylene glycol monomethyl acetate, diethylene glycol monoethyl
ether acetate, propylene glycol monomethyl ether acetate and the
like; alcohols such as methanol, ethanol, propanol, n-butanol,
n-pentanol, n-hexanol, isopropanol and the like; ketones such as
acetone, methyl ethyl ketone; other phenols, dimethylformamide,
n-methylpyrrolidone, ethyl acetate, ethyl lactate, sulfolane and
the like.
[0053] The preferable organic solvent is at least one selected from
glycols and derivatives thereof, alcohols, and carbonic esters.
[0054] The second feature of the polishing slurry of the present
invention is comprised of water and abrasives of which surface is
modified with an alkyl group. Preferably, it further contains a
metal oxide dissolving agent, metal oxidizer, organic solvent and
surfactant, if necessary. Further, polymers and metal inhibitors
may also be contained, if necessary.
[0055] As the abrasive in the present invention, any of inorganic
particles of silica, alumina, zirconia, ceria, titania, germania,
silicon carbide and the like and organic particles of polystyrene,
polyacryl, polyvinyl chloride and the like may be used. Of them,
silica, alumina, zirconia, ceria, titania and germania are
preferable, and particularly, colloidal silica and colloidal
alumina showing excellent dispersion stability in polishing slurry,
producing a small number of generation of polishing flaws
(scratches) generated by CMP, and having an average particle size
of 70 nm or less are preferable, and colloidal silica and colloidal
alumina having an average particle size of 40 nm or less are more
preferable. The particle size can be measured, for example, by an
optical diffraction scattering type particle size distribution
meter (for example, COULTER N4 SD manufactured by COULTER
Electronics). Particles obtained by coagulation of less than 2 on
average of primary particles are preferable, and particles obtained
by coagulation of less than 1.2 on average of primary particles are
more preferable. Further, the standard deviation of average
particle size distribution is preferably 10 nm or less, and the
standard deviation of average particle size distribution is more
preferably 5 nm or less. These can be used singly or in combination
of two or more.
[0056] As the abrasive of which surface is modified with an alkyl
group in the second feature of the present invention, the
above-mentioned inorganic particles or the above-mentioned organic
particles of which surface is modified with an alkyl group are
listed. Any of the inorganic particles and organic particles may be
used, of them, preferable particles are also as described above.
The modified particles can be used singly or in admixture of two or
more.
[0057] The method of modifying the surface of an abrasive with an
alkyl group is not particularly restricted, and there is mentioned
a method of reacting a hydroxyl group present on the surface of an
abrasive with alkoxysilane having alkyl group. The alkoxysilane
having alkyl group is not particularly restricted and listed are
monomethyltrimethoxysilane, dimethyldimethoxysilane,
trimethylmonomethoxysilane, monoethyltrimethoxysilane,
diethyldimethoxysilane, triethylmonomethoxysilane,
monomethyltriethoxysilane, dimethyldiethoxysilane and
trimethylmonoethoxysilane. The reaction method is not particularly
restricted and for example, abrasive and alkoxysilane react at room
temperature in polishing slurry, and they may also be heated for
promoting the reaction.
[0058] For obtaining colloidal silica, production methods by
hydrolysis of a silicon alkoxide or ion exchange of sodium silicate
are known, and for obtaining colloidal alumina, production methods
by hydrolysis of aluminum nitrate are known. Regarding the
colloidal silica, those obtained by production methods by
hydrolysis of a silicon alkoxide are most frequently utilized from
the standpoint of control of particle size and alkali metal
impurity. As the silicon alkoxide, TEMS (tetramethoxysilane) or
TEOS (tetraethoxysilane) is generally used. As the parameter
affecting particle size in the method of hydrolysis in an alcohol
solvent, there are mentioned the concentration of a silicon
alkoxide, the concentration of ammonia used as a catalyst and pH,
reaction temperature, the kind (molecular weight) of the alcohol
solvent, reaction time, and the like. By controlling these
parameters, colloidal silica dispersed liquid of given particle
size and degree of coagulation can be obtained.
[0059] The metal oxide dissolving agent in the present invention is
not particularly restricted, and examples thereof include organic
acids such as formic acid, acetic acid, propionic acid, butyric
acid, valeric acid, 2-methylbutyric acid, n-hexanoic acid,
3,3-dimethylbutyric acid, 2-ethylbutyric acid, 4-methylpentanoic
acid, n-heptanoic acid, 2-methylhexanoic acid, n-octanoic acid,
2-ethylhexanoic acid, benzoic acid, glycolic acid, salicylic acid,
glyceric acid, oxalic acid, malonic acid, succinic acid, glutaric
acid, adipic acid, pimelic acid, maleic acid, phthalic acid, malic
acid, tartaric acid, citric acid, p-toluenesulfonic acid and the
like, esters of these organic acids and ammonium salts of these
organic acids, and the like. Further, inorganic acids such as
hydrochloric acid, sulfuric acid, nitric acid and the like, and
ammonium salts of these inorganic acids, for example, ammonium
persulfate, ammonium nitrate, ammonium chloride, chromic acid and
the like are listed. Of them, formic acid, malonic acid, malic
acid, tartaric acid and citric acid are suitable from the
standpoint of efficient control of etching speed, while maintaining
practical CMP speed and sulfuric acid is suitable from the
standpoint of high CMP speed, for a conductive substance mainly
composed of metals. These can be used singly or in admixture of two
or more.
[0060] A metal oxidized may be added to the polishing slurry of the
present invention. As the metal oxidizer, hydrogen peroxide, nitric
acid, potassium periodate, hypochlorous acid, ozone water and the
like are listed, and of them, hydrogen peroxide is particularly
preferable. These can be used singly or in admixture of two or
more. When the substrate is a silicon base plate or the like
containing an element for integrated circuit, oxidizers containing
no non-volatile components are desirable since pollution with
alkali metals, alkaline earth metals, halide and the like is not
desirable. Since ozone water shows remarkable change in composition
by time, hydrogen peroxide is most suitable. When the substrate
which is an application subject is a glass base plate containing no
semiconductor element, or the like, oxidizers containing
non-volatile components may be permissible.
[0061] A water-soluble polymer may be added to the polishing slurry
of the present invention. The weight-average molecular weight of
the water-soluble polymer is preferably 500 or more, more
preferably 1500 or more, and particularly preferably 5000 or more.
The upper limit of the weight-average molecular weight is not
particularly restricted, and it is preferably 5000000 or less from
the standpoint of solubility. When the weight-average molecular
weight is less than 500, there is a tendency that high polishing
speed is not manifested.
[0062] The weight-average molecular weight can be measured using a
calibration curve of standard polystyrene by gel permeation
chromatography.
[0063] The water-soluble polymer having a weight-average molecular
weight of 500 or more is not particularly restricted, and examples
thereof include polysaccharides such as alginic acid, pectic acid,
carboxymethylcellulose, agar, curdlan, Pullulan and the like;
polycarboxylic acids, esters thereof and salts thereof, such as
polyaspartic acid, polyglutamic acid, polylysine, polymalic acid,
polymethacrylic acid, polyammonium methacrylate, polysodium
methacrylate, polyamic acids, polymaleic acid, polyitaconic acid,
polyfumaric acid, poly(p-styrenecarboxylic acid), polyacrylic acid,
polyacrylamide, aminopolyacrylamide, polyammonium acrylate,
polysodium acrylate, polyamic acid, polyammonium amidate,
polysodium amidate, polyglyoxylic acid and the like; vinyl-based
polymers such as polyvinyl alcohol, polyvinylpyrrolidone,
polyacrolein and the like; polyethylene glycol and the like. These
can be used singly or in admixture of two or more. When the
substrate applied is a silicon base plate or the like for
semiconductor integrated circuit, acids or its ammonium salts are
desirable since pollution with alkali metals, alkaline earth
metals, halide and the like is not desirable. When the substrate is
a glass base plate or the like, this is not the case. Of them,
preferable are pectinic acid, agar, polymalic acid, polymethacrylic
acid, ammonium polyacrylate, polyacrylamide, polyvinyl alcohol and
polyvinylpyrrolidone, esters thereof and ammonium salts
thereof.
[0064] A metal inhibitor may be added to the polishing slurry of
the present invention. As the metal inhibitor, there are listed,
for example, 2-mercaptobenzothiazole, 1,2,3-triazole,
1,2,4-triazole, 3-amino-1H-1,2,4-triazole, benzotriazole,
1-hydroxybenzotriazole, 1-dihydroxypropylbenzotriazole,
2,3-dicarboxypropylbenzotriazole, 4-hydroxybenzotriazole,
4-carboxyl(-1H-)benzotriazole, 4-carboxyl(-1H-)benzotriazole methyl
ester, 4-carboxyl(-1H-)benzotriazole butyl ester,
4-carboxyl(-1H-)benzotriazole octyl ester, 5-hexybenzotriazole,
[1,2,3-benzotriazolyl-1-methyl][1,2,4-triazolyl-1-me- thyl][2-et
hylhexyl]amine, tolyltriazole, naphthotriazole,
bis[(1-benzotriazolyl)methyl]phosphonic acid and the like.
[0065] Further listed are pyrimidine,
1,2,4-triazolo[1,5-a]pyrimidine,
1,3,4,6,7,8-hexahydro-2H-pyrimide[1,2-a]pyrimidine,
1,3-diphenyl-pyrimidine-2,4,6-trione, 1,4,5,6-tetrahydropyrimidine,
2,4,5,6-tetraminopyrimidine sulfate, 2,4,5-trihydroxypyrimidine,
2,4,6-triaminopyrimidine, 2,4,6-trichloropyrimidine,
2,4,6-trimethoxypyrimidine, 2,4,6-triphenylpyrimidine,
2,4-diamino-6-hydroxylpyrimidine, 2,4-diaminopyrimidine,
2-acetoamidepyrimidine, 2-aminopyrimidine,
2-methyl-5,7-diphenyl-(1,2,4)t- riazole(1,5-a)pyrimidine,
2-methylsulfanyl-5,7-diphenyl-(1,2,4)-triazolo(1- ,5-a)pydimidin e,
2-methylsulfanyl-5,7-diphenyl-4,7-dihydro-(1,2,4)triazol-
o(1,5-a)pyrimidine, 4-aminopyrazolo[3,4-d]pyrimidine and the like
having a pyrimidine constitution. These can be used singly or in
admixture of two or more.
[0066] The compounding amount in the case of compounding of a
surfactant into the polishing slurry of the present invention is
preferably from 0.00001 to 20 wt % in the polishing slurry from the
standpoints of dispersion and prevention of deposition, further,
scratch. Namely, it is preferably from 0.00001 to 20 g, more
preferably from 0.0001 to 10 g, and particularly preferably from
0.0001 to 5 g based on 100 g of the total amount of the polishing
slurry. When the compounding amount is less than 0.00001 g,
wet-ability of the polishing slurry for the polishing surface of a
substrate is low, and when more than 20 g, polishing speed tends to
lower.
[0067] The compounding amount in the case of compounding an organic
solvent in the polishing slurry of the present invention is
preferably from 0.1 to 95 wt % in the polishing slurry. Namely, it
is preferably from 0.1 to 95 g, more preferably from 0.2 to 50 g,
and particularly preferably from 0.5 to 10 g, based on 100 g of the
total amount of the polishing slurry. When the compounding amount
is less than 0.1 g, sufficient polishing speed is not obtained due
to low wet-ability of the polishing slurry for a substrate, and
when over 95 g, the solubility of a polishing slurry component
deteriorates, undesirably.
[0068] The compounding amount in the case of compounding of a metal
oxide dissolving agent in the polishing slurry of the present
invention is preferably from 0.001 to 20 g, more preferably from
0.002 to 10 g, and particularly preferably from 0.005 to 5 g, based
on 100 g of the total amount of a surfactant, organic solvent,
metal oxide dissolving agent, water, abrasives, metal oxidizer and
water-soluble polymer (hereinafter, referred to as seven
components) in the polishing slurry. When the compounding amount is
less than 0.001 g, polishing speed is low, and when over 20 g,
control of etching is difficult and roughening tends to occur on
the polished surface.
[0069] Of the above-mentioned seven components, the compounding
amount of water may be the remaining part and is not particularly
restricted providing water is contained.
[0070] The compounding amount of abrasives in the case of
compounding of abrasives in the polishing slurry of the present
invention is preferably from 0.01 to 50 g, more preferably from
0.02 to 40 g, and particularly preferably from 0.05 to 30 g based
on 100 g of the total amount of seven components. When the
compounding amount is less than 0.01 g, polishing speed is slow,
and when over 50 g, there is a tendency of occurrence of a lot of
scratches.
[0071] The compounding amount in the case of compounding of a metal
oxidizer in the polishing slurry of the present invention is
preferably from 0 to 50 g, more preferably from 0 to 20 g, and
particularly preferably from 0 to 10 g based on 100 g of the total
amount of seven components. When the compounding amount is over 50
g, there is a tendency of occurrence of roughening on the polished
surface.
[0072] The compounding amount in the case of compounding of a
water-soluble polymer in the polishing slurry of the present
invention is preferably from 0 to 10 g, more preferably from 0 to 5
g, and particularly preferably from 0 to 2 g based on 100 g of the
total amount of seven components. When the compounding amount is
over 10 g, there is a tendency of lowering of polishing speed.
[0073] The compounding amount in the case of compounding of a metal
inhibitor in the polishing slurry of the present invention is
preferably from 0 to 10 g, more preferably from 0 to 5 g, and
particularly preferably from 0 to 2 g based on 100 g of the total
amount of seven components. When the compounding amount is over 10
g, there is a tendency of lowering of polishing speed.
[0074] The polishing slurry of the present invention may contain
coloring agents such as dyes such as Victoria Pure Blue and the
like, pigments such as Phthalocyanine Green and the like, in
addition to the above-mentioned various components.
[0075] The polishing slurry of the present invention as described
above can be used for chemical mechanical polishing (CMP) of a
conductive substance layer, barrier layer and interlayer insulating
film of a semiconductor device. It is preferable that conductive
substance layer/barrier layer/interlayer insulating films are
polished at a polishing speed ratio of 1/0.01 to 20/0.01 to 20 in
CMP under the same conditions. It is more preferably 1/0.05 to
10/0.05 to 10, further preferably 1/0.1 to 10/0.01 to 10.
[0076] As the conductive substance, there are listed substances
mainly composed of metals such as copper, copper alloy, copper
oxide, copper oxide alloy, tungsten, tungsten alloy, silver, gold
and the like, and preferable are conductive substance mainly
composed of copper such as copper, copper alloy, copper oxide,
copper alloy oxide and the like. As the conductive substance layer,
films formed of the above-mentioned substances by a known
sputtering method or plating method can be used.
[0077] As the interlayer insulating film, silicon-based film s and
organic polymer films are listed. As the silicon-based film, listed
are silica-based film s such as silicon dioxide, fluorosilicate
glass, organosilicate glass, silicon oxynitride, silsesquioxane
hydride and the like, silicon carbide and silicon nitride. As the
organic polymer film, a whole aromatic low permittivity interlayer
insulating films are mentioned. In particular, organosilicate glass
is preferable. These films are formed by a CVD method, spin coat
method, dip coat method or spray method.
[0078] The barrier layer is formed to prevent of diffusion of a
conductive substance in an insulating film, and to improve close
adherence of an insulating film and a conductive substance. It is
preferable that a conductor used in a barrier layer contains one or
more selected from tungsten, tungsten nitride, tungsten alloy,
other tungsten compounds, titanium, titanium nitride, titanium
alloy, other titanium compounds, tantalum, tantalum nitride,
tantalum alloy and other tantalum compounds. The barrier layer may
be a single layer composed of one compound or a laminated film
composed of two or more compounds.
[0079] The polishing method of the present invention comprises a
first polishing process of polishing a conductive substance layer
of a substrate having an interlayer insulating film carrying a
surface composed of a concave portion and a convex portion, a
barrier layer coating the above-mentioned interlayer insulating
film along its surface and a conductive substance layer filling the
above-mentioned concave portion to coat the barrier layer, to
expose the barrier layer on the above-mentioned convex portion, and
a second polishing process of chemical and mechanical polishing at
least the barrier layer and the conductive substance layer on the
concave portion while feeding the above-mentioned polishing slurry
of the present invention to expose the interlayer insulating film
on the convex portion.
[0080] Here, for chemical mechanical polishing, a method is
mentioned in which a polishing plate and a substrate are moved
relatively while feeding polishing slurry under condition of
pressing the substrate having a polishing surface onto polishing
cloth (pad) of the polishing plate, to polish the polishing
surface. For exposing an interlayer insulating film, a method of
contacting a brush made of a metal or resin and a method of blowing
polishing slurry at given pressure are mentioned, additionally.
[0081] As the apparatus used for polishing, there can be used a
general polishing apparatus having a holder capable of retaining a
substrate to be polished and having a polishing plate connected to
a motor capable of changing its rotation, and the like, to which
polishing clothe is pasted, in the case, for example, of polishing
with polishing cloth. The polishing cloth is not particularly
restricted, and general non-woven fabric, foamed polyurethane,
porous fluorine resins and the like can be used. The polishing
conditions are not restricted, however, the rotation speed of a
polishing plate is preferably a low rotation of 200 rpm or less so
that a substrate does not jump. The pressure of pressing a
substrate having a polishing surface onto polishing cloth is
preferably from 1 to 100 kPa, and for satisfying uniformity of CMP
speed in wafer plane and flatness of pattern, it is more preferably
from 5 to 50 kPa. During polishing, polishing slurry is
continuously fed to polishing cloth by a pump and the like. Though
the feeding amount is not particularly restricted, it is preferable
that the surface of polishing cloth is always covered with
polishing slurry. It is preferable that a substrate after
completion of polishing is washed thoroughly in flowing water,
then, water drops adhered on the substrate are removed by spin dry
and the like, before drying this.
[0082] For conducting chemical mechanical polishing while making
the surface condition of polishing cloth always constant, it is
preferable to provide a process of conditioning of polishing cloth
before polishing. For example, conditioning of polishing cloth is
conducted with liquid containing at least water using a dresser
with diamond particles. Subsequently, the chemical mechanical
polishing process according to the present invention is performed,
further, a substrate washing process is added, preferably.
[0083] The polishing method of the present invention can be
applied, for example, to formation of a wiring layer in a
semiconductor device. Hereinafter, an embodiment of the polishing
method of the present invention will be illustrated along formation
of a wiring layer in a semiconductor device.
[0084] First, an interlayer insulating film of silicon dioxide and
the like is formed on a substrate made of silicon. Then, a concave
portion (substrate exposed portion) of given pattern is formed on
the surface of the interlayer insulating film by known means such
as forming a resist layer, etching and the like, to give the
interlayer insulating film having a convex portion and concave
portion. On this interlayer insulating film, a barrier layer of
tantalum and the like coating the interlayer insulating film along
the convexoconcave on the surface is formed by vapor deposition or
CVD and the like. Further, a metal conductive substance layer made
of copper and the like coating the barrier layer so as to fill the
above-mentioned convexoconcave is formed by vapor deposition,
plating or CVD and the like. The thickness of formation of the
interlayer insulating film, barrier layer and conductive substance
are preferably about 0.01 to 2.0 .mu.m, about 1 to 100 nm and about
0.01 to 2.5 .mu.m, respectively.
[0085] Next, this conductive substance layer on the surface of a
semiconductor substrate is polished by CMP using, for example, a
polishing slurry for conductive substance showing sufficiently
large above-mentioned polishing speed ratio of conductive
substance/barrier layer (first polishing process). By this, the
barrier layer at the convex portion on the substrate is exposed on
the surface, to obtain a given conductor pattern having the
conductive substance film remaining on the concave portion. The
resulted pattern surface can be polished as a polishing surface for
the second polishing process in the polishing method of the present
invention using the polishing slurry of the present invention.
[0086] In the second polishing process, at least the
above-mentioned exposed barrier layer and the conductive substance
at the concave portion are polished by chemical mechanical
polishing using the polishing slurry of the present invention
capable of polishing a conductive substance, barrier layer and
interlayer insulating film. All of the interlayer insulating film
below the barrier layer at the convex portion is exposed, the
conductive substance layer becoming a wiring layer remains at the
concave portion, to obtain a given pattern in which the section of
the barrier layer is exposed to the boundary between the convex
portion and the concave portion. Polishing is completed at this
stage. Further, for securing excellent flatness in completion of
polishing, polishing may be conducted to depth involving a part of
the interlayer insulating film at the convex portion by over
polishing (for example, when time until obtaining a given pattern
in the second polishing process is 100 seconds, polishing for
additional 50 seconds in addition to this polishing for 100 seconds
is called over polishing 50%).
[0087] On thus formed metal wirings, an interlayer insulating film
and a second layer, metal wirings are formed, and an interlayer
insulating film is again formed between the wirings and on the
wirings, then, polishing is effected to give a smooth surface over
the whole surface of a semiconductor substrate. This process is
repeated given times, a semiconductor device having given number of
wiring layers can be produced.
[0088] The polishing slurry of the present invention can be used
not only for polishing of a silicon compound film formed on a
semiconductor substrate as described above, but also for polishing
of a silicon oxide film formed on a wiring board having given
wirings, an inorganic insulating film of glass, silicon nitride and
the like, optical glass such as photomask, lens, prism and the
like, an inorganic conductive film such as ITO and the like,
photo-integrated circuit, photo-switching element and photo-wave
guiding route constituted of glass and crystalline materials, the
end surface of optical fiber, an optical single crystal of a
scintillator and the like, a solid laser single crystal, a LED
sapphire substrate for blue laser, a semiconductor single crystal
of SiC, GaP, GaAs and the like, a glass base plate for magnetic
disk, a substrate of a magnetic head and the like.
EXAMPLES
[0089] The present invention will be illustrated further in detail
by examples, however, the scope of the invention is not limited to
these examples unless deviating from the technological idea of the
present invention. For example, the kind and compounding ratio of
materials of polishing slurry may be those other than the kinds and
ratios described in the present examples, and also the composition
and constitution of the polishing subject may be those other than
compositions and constitutions described in the present
examples.
[0090] (Polishing Slurry Production Method)
[0091] Materials shown in Tables 1 to 5 were mixed at respective
compositions to prepare polishing slurries used in Examples 1 to 27
and Comparative Examples 1 to 4. Acetylene diol was used as
glycols, and sodium dodecylbenzenesulfonate was used as a salt of
an alkylbenzensulfonic acid, in Tables 3 and 4.
1TABLE 1 Material (parts by weight) Example 1 Example 2 Example 3
Example 4 Example 5 Example 6 Example 7 Organic Ethanol 10 -- -- --
-- -- -- solvent Isopropyl -- 10 -- -- -- -- -- alcohol Propylene
-- -- 10 -- -- -- -- glycol monomethyl ether Propylene -- -- -- 10
-- -- -- glycol Dipropylene -- -- -- -- 10 -- -- glycol monomethyl
ether Ethylene -- -- -- -- -- 10 -- glycol monomethyl ether
Propylene -- -- -- -- -- -- 10 carbonate Metal Malonic acid 0.5 --
0.5 -- 0.5 0.5 -- oxide Malic acid -- 0.5 -- 0.5 -- -- 0.5
dissolving agent Abrasive: Average -- -- -- 2 -- -- -- colloidal
particle silica size of 20 nm Average 6 5 3 -- 3 3 3 particle size
of 50 nm Oxidizer Hydrogen 0.5 0.5 0.5 0.5 0.5 0.5 0.5 peroxide
Metal Benzotriazole 0.1 0.1 0.1 0.1 0.1 0.1 0.1 inhibitor Polymer
Polyacrylic -- -- -- -- -- -- -- acid (*) Water 90 90 90 90 90 90
90 ((*) Weight-average molecular weight: 25000)
[0092]
2TABLE 2 Material Example Example Example Comparative Comparative
(parts by weight) Example 8 Example 9 10 11 12 Example 1 Example 2
Organic Ethanol -- -- -- -- -- -- -- solvent Isopropyl 10 -- -- --
-- -- -- alcohol Propylene -- 10 -- -- -- -- -- glycol monomethyl
ether Propylene -- -- 10 -- -- -- -- glycol monopropyl ether
Dipropylene -- -- -- 10 -- -- -- glycol monomethyl ether Ethylene
-- -- -- -- 10 -- -- glycol monomethyl ether Propylene -- -- -- --
-- -- -- carbonate Metal Malonic acid 0.5 0.5 -- -- 0.5 0.5 --
oxide Malic acid -- -- 0.5 0.5 -- -- 0.5 dissolving agent Abrasive:
Average -- 4 -- 3 -- -- -- colloidal particle silica size of 20 nm
Average -- -- 5 4 5 5 5 particle size of 50 nm Oxidizer Hydrogen --
-- 1 1 1 1 1 peroxide Metal Benzotriazole -- -- -- 0.1 0.1 0.1 0.1
inhibitor Polymer Polyacrylic -- -- -- -- 0.1 -- -- acid (*) Water
90 90 90 90 90 100 100 ((*) Weight-average molecular weight:
25000)
[0093]
3TABLE 3 Material Example Example Example Example Example (parts by
weight) 13 14 15 16 17 Surfactant Glycols 0.1 0.2 -- -- -- Salts of
-- -- 0.1 1 -- alkylbenzene sulfonic acid Poly(n =
3)oxyethylenepropyl -- -- -- -- -- perfluorooctanesulfoneamide
p-nonylphenol -- -- -- -- 0.1 monoethoxylate Metal Malonic acid 0.5
0.5 -- -- 0.5 oxide Malic acid -- -- 0.5 0.5 -- dissolving agent
Abrasive: Average -- -- 7 7 -- colloidal particle size silica of 20
nm Average 5 5 -- -- 3 particle size of 50 nm Oxidizer Hydrogen 1 1
1 1 1 peroxide inhibitor Benzotriazole 0.1 0.1 0.1 0.1 0.1 Polymer
Polyacrylic -- -- -- -- -- acid (*) Water 93.3 93.2 91.3 90.4 95.3
((*) Weight-average molecular weight: 25000)
[0094]
4TABLE 4 Material Example Example Comparative Comparative (parts by
weight) 18 19 Example 3 Example 4 Surfactant Glycols -- -- -- --
Salts of -- -- -- -- alkylbenzene sulfonic acid Poly(n =
3)oxyethylenepropyl -- 0.005 -- -- perfluorooctanesulfoneamide
p-nonylphenol 1 -- -- -- monoethoxylate Metal Malonic acid 0.5 0.5
0.5 -- oxide Malic acid -- -- -- 0.5 dissolving agent Abrasive:
Average -- -- -- -- colloidal particle size silica of 20 nm Average
3 5 5 5 of 50 nm Oxidizer Hydrogen 1 1 1 1 peroxide inhibitor
Benzotriazole 0.1 0.1 0.1 0.1 Polymer Polyacrylic -- -- -- -- acid
(*) Water 94.4 93.35 93.4 93.4 ((*) Weight-average molecular
weight: 25000)
[0095]
5TABLE 5 Material Example Example Example Example Example Example
Example Example (parts by weight) 20 21 22 23 24 25 26 27 Organic
Isopropyl 10 -- -- -- 10 10 -- -- solvent alcohol Propylene -- 10
-- -- -- -- -- -- glycol monomethyl ether Propylene -- -- 10 -- --
-- -- -- glycol monopropyl ether Metal Malonic acid 0.5 -- 0.5 --
0.5 0.5 -- -- oxide Malic acid -- 0.5 -- 0.5 -- -- 0.5 0.5
dissolving agent Abrasive: average -- -- -- 2 -- -- -- -- colloidal
particle silica size of 20 nm average 6 5 3 -- 3 3 3 4 particle
size of 50 nm Alkoxysilane Trimethyl 0.1 0.1 0.1 0.1 -- -- -- 0.1
having monomethoxysilane alkyl Dimethyl -- -- -- -- 0.1 0.1 0.1 --
group Dimethoxysilane Oxidizer Hydrogen 0.5 0.5 0.5 0.5 0.5 0.5 0.5
0.5 peroxide Metal Benzotriazole 0.1 0.1 0.1 0.1 0.1 -- -- --
inhibitor Polymer Polyacrylic -- -- -- -- -- -- 0.1 -- acid (*)
Water 90 90 90 100 90 90 100 95 ((*) Weight-average molecular
weight: 25000)
[0096] (Substrate)
[0097] The following substrates were prepared.
[0098] Blanket substrate (a): Silicon base plate formed of
organosilicate glass (thickness: 1000 nm) by a CVD method.
[0099] Blanket substrate (b): Silicon base plate formed of silicon
dioxide having a thickness of 1000 nm by a CVD method.
[0100] Blanket substrate (c): Silicon base plate formed of a
tantalum film having a thickness of 200 nm by a sputtering
method.
[0101] Blanket substrate (d): Silicon base plate formed of a copper
film having a thickness of 1600 nm by a sputtering method.
[0102] Production of pattern substrate (a): A organosilicate glass
as described above (thickness: 1000 nm) was formed as an interlayer
insulating film on a silicon base plate by a CVD method. On this
organosilicate glass, trenches having a depth of 800 nm were formed
by a photolithography method so that wiring metal parts having a
width of 4.5 .mu.m and interlayer insulating film parts having a
width of 0.5 .mu.m were mutually arranged, to produce stripe
pattern parts (for evaluation of erosion) composed of concave
portions (trenches portions) and convex portions (non-trench
portions) on the surface. Separately, trenches having a depth of
800 nm were likewise formed so that wiring metal parts having a
width of 100 .mu.m and interlayer insulating film parts having a
width of 100 .mu.m were mutually arranged, to produce stripe
pattern parts (for evaluation of dishing) on the surface.
[0103] Further, along this surface, a tantalum film having a
thickness of 200 nm was formed as a barrier layer by a sputtering
method. On the above-mentioned tantalum film, a copper film of 1.6
.mu.m was formed as a conductive substance layer so as to fill all
of the above-mentioned trenches by a sputtering method. The
projected copper film was polished until all of the barrier layer
at the convex portions was exposed on the polishing surface, by CMP
of high selectivity of polishing only copper, as a first polishing
process, to obtain a pattern substrate (a) which had been flattened
(polishing time: 180 seconds, maximum polishing thickness: 1.6
.mu.m).
[0104] Pattern substrate (b): It was produced in the same manner as
for the pattern substrate (a) except that silicon dioxide was used
as the interlayer insulating film.
Examples 1 to 27 and Comparative Examples 1 to 4
[0105] Using each of the above prepared polishing slurry, each
substrate prepared above was chemically and mechanically polished
under the following polishing conditions. The copper etching speed
was measured by immersion into each polishing slurry under the
following conditions. Results of evaluation of the polishing speed
by chemical mechanical polishing, in-plane uniformity of polishing
speed, copper etching speed, dishing amount, erosion amount and
wiring resistance, amount of polishing foreign matters, and
scratches are shown in Tables 6 to 10.
[0106] (Polishing Condition) [Common to First Polishing Process
which is Pre-Treatment of the Above-Mentioned Pattern Substrate,
and the Following Polishing of Each Substrate]
[0107] Polishing pad: foamed polyurethane resin (IC1000
(manufactured by Rodel))
[0108] Polishing pressure: 20.6 kPa (210 g/cm.sup.2)
[0109] Relative speed of substrate and polishing plate: 36
m/min
[0110] (Polishing Process of Each Substrate)
[0111] The blanket substrates (a), (b), (c) and (d) were chemically
and mechanically polished for 60 seconds while feeding each
polishing slurry prepared above at 150 cc/minute, and after
completion of polishing, washing treatment was conducted with
distilled water.
[0112] The pattern substrates (a) and (b) were chemically and
mechanically polished for 90 seconds while feeding each polishing
slurry prepared above at 150 cc/minute, and after completion of
polishing, washing treatment was conducted with distilled water.
Polishing of the pattern substrates (a) and (b) corresponded to the
second polishing process, and the interlayer insulating film at the
convex portion was all exposed on the polished surface at about 30
seconds, and after completion of polishing, it was
over-polished.
[0113] (Evaluation Items)
[0114] (1) Polishing speed: The polishing speeds of the
organosilicate glass (a) and silicon dioxide (b), of the blanket
substrates (a) to (d) polished and washed under the above-mentioned
conditions were obtained by measuring a difference in film
thickness before and after polishing using a film thickness
measuring apparatus manufactured by Dainippon Screen MFG Co. LTD
(product name: Lambda Ace VL-M8000LS). The polishing speeds of the
tantalum film (c) and copper (d) were obtained by converting a
difference in film thickness before and after polishing based on
electric resistance.
[0115] (2) In-plane uniformity of polishing speed: The standard
deviation of the above-mentioned polishing speed (1) was
represented in terms of percentage (%) based on the average
value.
[0116] (3) Copper etching speed: It was obtained by converting a
difference in copper film thickness before and after immersion of
the blanket substrate (d) into polishing slurry (25.degree. C.,
stirring: 100 rpm) under stir for 60 seconds, based on electric
resistance value.
[0117] (4) Flatness (dishing amount): From the surface form of the
stripe pattern parts composed of wiring metal (copper) parts having
a width of 100 .mu.m and interlayer insulating film parts having a
width of 100 .mu.m mutually arranged (hereinafter, referred to as
dishing evaluation part), of the pattern substrates (a) and (b)
polished and washed under the above-mentioned conditions, the
amount of film reduction at the wiring metal part based on the
insulating film part was measured by a stylus type level meter.
[0118] (5) Flatness (erosion amount): The surface form of the
stripe pattern parts having a total width of 2.5 mm composed of
wiring metal parts having a width of 4.5 .mu.m and interlayer
insulating film parts having a width of 0.5 .mu.m mutually arranged
(hereinafter, referred to as erosion evaluation part), formed on
the pattern substrates (a) and (b) was measured by a stylus type
level meter, to obtain the amount of film reduction at the
interlayer insulating film parts around the center of the stripe
pattern parts based on the insulating film parts around the stripe
patterns.
[0119] (6) Wiring resistance: The wiring resistance of a wiring
length of 1 mm was measured at the above-mentioned dishing
evaluation part (4). The wiring resistance of a wiring length of 1
mm was measured at the above-mentioned erosion evaluation part
(4).
[0120] (7) Washing property (amount of polishing foreign
materials): The amount of residue materials remaining on the
surface of the pattern substrates (a) and (b) was observed using
SEM and washing property was evaluated by the number of residue
materials per 1 cm.sup.2.
[0121] (8) Scratches: The amount of scratches was measured from the
pattern substrates (a) and (b) using a pattern wafer defect
detection apparatus 2138 manufactured by KLA Tenocor, and evaluated
by the number of scratches per 1 cm.sup.2.
6TABLE 6 Evaluation result Example 1 Example 2 Example 3 Example 4
Example 5 Example 6 Example 7 Polishing Organosilicate 720 600 780
610 590 750 580 speed glass (.ANG./min) Silicon dioxide 560 670 620
550 540 670 490 Tantalum film 600 520 420 520 600 570 610 Copper
310 300 310 300 290 280 310 In- Organosilicate 4.5 5.8 4.5 3.8 5.2
5.6 5.2 plane glass uniformity Silicon 3.2 4.4 3.1 4.5 5.4 4.5 3.1
(%) dioxide of Tantalum film 5.8 5.5 3.3 5.2 5.3 5.3 5.4 polishing
Copper 7.5 6.9 7.2 6.5 6.9 6.9 7.1 speed Copper etching speed 30 20
50 15 20 30 10 (.ANG./min) Pattern Dishing amount (.ANG.) 370 650
700 700 700 650 480 substrate Erosion amount (.ANG.) 300 630 560
700 640 540 450 (a): Wiring Dishing 0.352 0.368 0.361 0.372 0.362
0.368 0.365 using resistance evaluation organosilicate (.OMEGA.)
part glass Erosion 7.01 7.08 7.10 7.09 7.05 7.10 7.05 evaluation
part Amount of 1.1 0.8 0.2 0.7 1.2 2.0 0.4 polishing foreign
materials (number/cm.sup.2) Amount of scratch 0.1 0.3 0.2 0.2 0.1
0.2 0.7 (number/cm.sup.2) Pattern Dishing amount (.ANG.) 360 450
440 420 520 410 520 substrate Erosion amount (.ANG.) 450 400 440
510 430 530 570 (b): Wiring Dishing 0.364 0.357 0.364 0.355 0.361
0.354 0.363 using resistance evaluation silicon (.OMEGA.) part
dioxide Erosion 7.10 7.06 7.11 7.05 7.10 7.10 7.07 evaluation part
Amount of 1.2 2.0 0.4 0.8 1.2 0.2 0.8 polishing foreign materials
(number/cm.sup.2) Amount of scratch 1.4 0.2 2.0 0.2 1.3 0.7 0.7
(number/cm.sup.2)
[0122]
7TABLE 7 Example Example Example Comp. Comp. Evaluation result
Example 8 Example 9 10 11 12 Example 1 Example 2 Polishing
Organosilicate 320 770 650 625 650 120 150 speed glass (.ANG./min)
Silicon dioxide 290 450 580 520 570 220 210 Tantalum film 550 540
550 560 560 450 510 Copper 120 130 310 310 290 320 300 In-
Organosilicate 4.5 3.1 5.3 3.4 3.3 8.2 10.1 plane glass uniformity
Silicon dioxide 5.2 4.1 4.5 5.3 4.5 8.4 8.3 (%) Tantalum film 3.7
4.2 5.3 4.5 4.1 6.4 6.5 of Copper 7.8 8.2 7.7 6.9 7.3 11.7 10.8
polishing speed Copper etching speed 45 40 50 20 20 20 30
(.ANG./min) Pattern Dishing amount 550 610 500 650 650 2050 3200
substrate (.ANG.) (a): Erosion amount 520 390 540 560 670 2700 2590
using (.ANG.) organosilicate Wiring Dishing 0.363 0.362 0.368 0.359
0.363 0.398 0.450 glass resistance evaluation (.OMEGA.) part
Erosion 7.06 7.07 7.06 7.01 7.03 7.25 8.02 evaluation part Amount
of 0.3 1.9 1.0 0.3 0.2 5.6 5.8 polishing foreign materials
(number/cm.sup.2) Amount of 0.7 1.1 0.3 1.1 0.3 6.9 10.8 scratch
(number/cm.sup.2) Pattern Dishing amount 510 450 530 600 510 1850
2850 substrate (.ANG.) (b): Erosion amount 480 400 610 450 450 2010
2350 using (.ANG.) silicon Wiring Dishing 0.354 0.363 0.364 0.352
0.368 0.418 0.460 dioxide resistance evaluation (.OMEGA.) part
Erosion 7.05 7.08 7.07 7.10 7.05 7.35 7.95 evaluation part Amount
of 0.6 0.6 1.1 1.2 1.1 5.4 5.3 polishing foreign materials
(number/cm.sup.2) Amount of 2.0 0.8 1.2 0.2 0.2 6.3 10.1 scratch
(number/cm.sup.2)
[0123]
8TABLE 8 Example Example Example Example Example Evaluation result
13 14 15 16 17 Polishing Organosilicate 740 760 620 600 510 speed
glass (.ANG./min) Silicon dioxide 570 620 640 570 450 Tantalum film
610 440 530 500 420 Copper 300 310 320 290 280 In- Organosilicate
3.7 4.1 4.9 4.2 5.8 plane glass uniformity Silicon 3.1 4.3 3.6 3.9
5.1 (%) of dioxide polishing Tantalum film 6.1 4.8 6.5 6.1 5.5
speed Copper 8.4 6.5 7.1 6.3 7.3 Copper etching speed 20 10 50 50
30 (.ANG./min) Pattern Dishing amount 390 380 750 700 600 substrate
(.ANG.) (a): Erosion amount 330 310 700 700 540 using (.ANG.)
organosilicate Wiring Dishing 0.353 0.353 0.374 0.369 0.365 glass
resistance evaluation (.OMEGA.) part Erosion 7.02 7.01 7.11 7.10
7.05 evaluation part Polishing 1.2 0.9 2.1 1.8 0.9 foreign
materials amount (number/cm.sup.2) Amount of 0.3 0.2 0.7 0.9 0.5
scratch (number/cm.sup.2) Pattern Dishing amount 370 340 720 700
520 substrate (.ANG.) (b): Erosion amount 320 310 680 650 500 using
(.ANG.) silicon Wiring Dishing 0.354 0.350 0.372 0.371 0.363
dioxide resistance evaluation (.OMEGA.) part Erosion 7.01 7.02 7.09
7.10 7.04 evaluation part Polishing 1.1 1.3 2.4 2.1 1.5 foreign
materials amount (number/cm.sup.2) Amount of 0.1 0.2 0.3 0.5 0.2
scratch (number/cm.sup.2)
[0124]
9TABLE 9 Example Example Comparative Comparative Evaluation result
18 19 Example 3 Example 4 Polishing Organosilicate 590 700 110 140
speed glass (.ANG./min) Silicon dioxide 480 610 410 520 Tantalum
film 530 590 480 530 Copper 280 330 320 300 In-plane Organosilicate
5.3 3.4 8.1 9.4 uniformity glass (%) of Silicon dioxide 5.7 4.6 8.5
8.0 polishing Tantalum film 3.9 5.7 6.8 6.9 speed Copper 9.2 9.0
13.4 11.7 Copper etching speed 20 20 10 30 (.ANG./min) Pattern
Dishing amount (.ANG.) 580 420 1100 1800 substrate Erosion amount
(.ANG.) 620 350 1000 1500 (a): Wiring Dishing 0.363 0.363 0.383
0.389 using resistance evaluation organosilicate (.OMEGA.) part
glass Erosion 7.07 7.03 7.13 7.18 evaluation part Polishing foreign
0.8 0.9 5.6 5.8 materials amount (number/cm.sup.2) Amount of
scratch 0.3 0.2 4.1 4.8 (number/cm.sup.2) Pattern Dishing amount
(.ANG.) 570 350 1000 1900 substrate Erosion amount (.ANG.) 560 330
1200 1500 (b): Wiring Dishing 0.363 0.357 0.381 0.390 using
resistance evaluation silicon (.OMEGA.) part dioxide Erosion 7.07
7.03 7.15 7.18 evaluation part Polishing foreign 1.7 1.1 4.7 5.1
materials amount (number/cm.sup.2) Amount of scratch 0.4 0.1 3.8
3.2 (number/cm.sup.2)
[0125]
10TABLE 10 Exam. Exam. Exam. Exam. Exam. Exam. Exam. Exam.
Evaluation result 20 21 22 23 24 25 26 27 Polishing Organosilicate
420 560 700 640 590 650 560 520 speed glass (.ANG./min) Silicon 660
760 670 650 590 610 480 540 dioxide Tantalum film 480 500 520 510
570 590 560 310 Copper 290 270 310 330 280 290 290 190 In-plane
Organosilicate 4.9 5.1 5.3 4.2 5.1 5.2 5.4 5.1 uniformity glass (%)
of Silicon 4.4 5.8 3.9 5.4 5.6 5.1 4.7 7.1 polishing dioxide speed
Tantalum film 4.5 4.5 4.3 5.1 5.0 5.4 5.7 4.9 Copper 6.3 6.6 5.8
5.8 6.4 6.1 7.5 5.9 Copper etching speed 25 23 25 35 25 35 30 35
(.ANG./min) Pattern Dishing 450 450 650 550 700 570 580 480
substrate amount (.ANG.) (a): Erosion 450 600 740 710 660 640 480
450 using amount (.ANG.) organosilicate Wiring Dishing 0.35 0.37
0.36 0.36 0.37 0.37 0.37 0.37 glass resistance evaluation (.OMEGA.)
part Erosion 7.02 7.03 7.11 7.06 7.09 7.12 7.08 7.10 evaluation
part Amount of 0.1 0.3 0.3 0.9 1.1 2.1 0.2 0.3 polishing foreign
materials (number/cm.sup.2) Amount of 1.3 1.0 0.4 0.5 0.6 0.2 0.9
0.9 scratch (number/cm.sup.2) Pattern Dishing 390 550 480 500 580
460 500 600 substrate amount (.ANG.) (b): Erosion 600 540 410 480
500 510 530 430 using amount (.ANG.) silicon Wiring Dishing 0.36
0.36 0.36 0.36 0.37 0.36 0.36 0.37 dioxide resistance evaluation
(.OMEGA.) part Erosion 7.11 7.16 7.13 7.04 7.11 7.05 7.09 7.10
evaluation part Amount of 2.2 2.1 0.8 0.9 2.2 0.4 0.5 1.1 polishing
foreign materials (number/cm.sup.2) Amount of 0.4 0.6 2.1 0.3 1.1
0.8 0.5 0.9 scratch (number/cm.sup.2)
[0126] In Comparative Examples 1 to 4, the polishing speed of
organosilicate glass is small and the in-plane uniformity of the
polishing speed is large, therefore, dishing and erosion are large
and wiring resistance is increased. Further, in Comparative
Examples 1 to 4, the amount of polishing foreign materials and the
amount of scratches are large. In contrast, in Examples 1 to 27,
the polishing speed of organosilicate glass or silicon dioxide is
large and the in-plane uniformity of the polishing speed is
excellent, therefore, increase in wiring resistance is small due to
excellent dishing and erosion properties. The amount of polishing
foreign materials and the amount of scratches are small, indicating
preferable results.
INDUSTRIAL APPLICABILITY
[0127] According to the polishing slurry of the present invention,
a polished surface having high flatness is obtained even if the
polished surface is made of two or more substances. Metal residue
and scratches after polishing can be suppressed. Further, the
polishing speed of an interlayer insulating film can be increases
without decreasing the polishing speed of the barrier layer, and
the polishing speed of a metal for wiring part can be controlled.
The polishing method of the present invention of effecting chemical
mechanical polishing using this polishing slurry is suitable for
production of a semiconductor device and other electronic
appliances excellent in productivity, fineness, film thinness,
dimension precision and electric property, and having high
reliability.
* * * * *