U.S. patent application number 10/641432 was filed with the patent office on 2005-02-17 for method of manufacturing an array of bi-directional nonvolatile memory cells.
Invention is credited to Chen, Bomy, Kianian, Sohrab.
Application Number | 20050037576 10/641432 |
Document ID | / |
Family ID | 34136348 |
Filed Date | 2005-02-17 |
United States Patent
Application |
20050037576 |
Kind Code |
A1 |
Chen, Bomy ; et al. |
February 17, 2005 |
METHOD OF MANUFACTURING AN ARRAY OF BI-DIRECTIONAL NONVOLATILE
MEMORY CELLS
Abstract
A method of making an array of bi-directional non-volatile
memory cells in a substrate of a substantially single crystalline
semiconductive material, where the material has a first
conductivity type with the substrate having a substantially planar
surface, comprises forming a plurality of spaced apart
substantially parallel trenches in a first direction in the planar
surface. Each of the trenches has a sidewall and a bottom. A region
of a second conductivity type is formed in the bottom of each
trench. A floating gate is formed in each trench insulated and
spaced apart from the sidewall of the trench. The floating gate has
a first end near the bottom and a second end furthest away from the
bottom. A layer of tunneling oxide is formed about the second end
of each floating gate. A layer of word region is formed on the
layer of tunneling oxide. The layer of word region extends in a
second direction substantially perpendicular to the first
direction. The layer of word region is cut into a plurality of
strips in the second direction to form a plurality of spaced apart
word lines. Each strip is spaced apart from one another and
substantially parallel to one another, and cuts through the
floating gate in each of the trenches. Electrical connections are
made to each of the region of second conductivity type and each of
the plurality of spaced apart word lines.
Inventors: |
Chen, Bomy; (Cupertino,
CA) ; Kianian, Sohrab; (Los Altos Hills, CA) |
Correspondence
Address: |
GRAY CARY WARE & FREIDENRICH LLP
2000 UNIVERSITY AVENUE
E. PALO ALTO
CA
94303-2248
US
|
Family ID: |
34136348 |
Appl. No.: |
10/641432 |
Filed: |
August 14, 2003 |
Current U.S.
Class: |
438/259 ;
257/E21.682; 257/E27.103 |
Current CPC
Class: |
H01L 27/115 20130101;
H01L 27/11521 20130101 |
Class at
Publication: |
438/259 |
International
Class: |
H01L 021/336 |
Claims
What is claimed is:
1. A method of forming an array of bi-directional non-volatile
memory cells in a substrate of a substantially single crystalline
semiconductive material having a first conductivity type, said
substrate having a substantially planar surface, said method
comprising: forming a plurality of spaced apart substantially
parallel trenches in a first direction in said planar surface; each
trench having a sidewall and a bottom; forming a region of a second
conductivity type in said bottom of each trench; forming a floating
gate in each trench insulated and spaced apart from said sidewall
of said trench; said floating gate having a first end near said
bottom and a second end furthest away from said bottom; forming a
layer of tunneling oxide about said second end of each floating
gate; forming a layer of word region on said layer of tunneling
oxide; said layer of word region extending in a second direction
substantially perpendicular to said first direction; cutting said
layer of word region in a plurality of strips in said second
direction to form a plurality of spaced apart word lines; each
strip spaced apart from one another and substantially parallel to
one another, and cutting through the floating gate in each trench;
and forming an electrical connection to each of said region of
second conductivity type and each of said plurality of spaced apart
word lines.
2. The method of claim 1 further comprising the steps of: forming a
plurality of spaced apart strips of protective material on said
planar surface; using said plurality of spaced apart strips of
protective material as mask to form said plurality of spaced apart
substantially parallel trenches.
3. The method of claim 2 wherein said protective material is
silicon nitride.
4. The method of claim 1 wherein said step of forming a floating
gate in each trench further comprises: depositing a layer of
insulating material along said sidewall and bottom of each trench;
and conformally depositing a layer of polysilicon on said layer of
insulating material; anisotropically etching said polysilicon to
form said floating gate.
5. The method of claim 4 wherein each floating gate is insulated
and spaced apart from said bottom of each trench.
6. The method of claim 1 wherein said forming a region step
comprises ion implanting dopants of said second conductivity into
the bottom of each trench.
Description
TECHNICAL FIELD
[0001] The present invention relates to a method of manufacturing
an array of bi-directional nonvolatile memory cells using a
floating gate for storage of charges.
BACKGROUND OF THE INVENTION
[0002] Nonvolatile memory cells have a floating gate for the
storage of charges thereon to control the conduction of current in
a channel in a substrate of a semiconductive material is well known
in the art. See, for example, U.S. Pat. No. 5,029,130 whose
disclosure is incorporated herein by reference in its entirety. In
U.S. Pat. No. 5,029,130, a split gate nonvolatile memory cell
having a floating gate with source side injection and poly to poly
tunneling is disclosed. The memory cell has a first region and a
second region with a channel region therebetween with the channel
region having a first portion and a second portion. A floating gate
is disposed over a first portion of the channel region is insulated
therefrom and controls the conduction of current in the channel
region depending upon the charges stored in the floating gate. A
word line/erase gate is disposed over a second portion of the
channel region and is insulated therefrom and controls the
conduction of current in the second portion of the channel region.
The cell is programmed when electrons through the mechanism of hot
electron channel injection are injected from the channel region
onto the floating gate. The cell is erased by electrons from the
floating gate tunneling to the erase gate through the mechanism of
Fowler-Nordheim tunneling. The floating gate is characterized by
having a sharp tip to facilitate the tunneling of electrons from
the floating gate to the control gate. In U.S. Pat. No. 5,029,130,
the control gate/erase gate performs two functions. First, it
controls the conduction of current in the second portion of the
channel region during the operations of programming and read.
Secondly, it is supplied with a high voltage during the erase
operation to attract the electrons from the spaced apart and
insulated floating gate. These two functions have compromised the
design of a single member which must perform both functions.
Specifically, during programming and read, the word line/control
gate receives low voltage whereas during erase, it must receive a
high voltage.
[0003] Bidirectional non-volatile memory cells using trapping
charge materials are well known in the art. See, for example, U.S.
Pat. Nos. 5,768,192 and 6,011,725.
[0004] It is therefore, an object of the present invention to
overcome this and other difficulties.
SUMMARY OF THE INVENTION
[0005] The present invention relates to a method of forming an
array of bi-directional non-volatile memory cells in a substrate of
a substantially single crystalline semiconductive material. The
material has a first conductivity type with the substrate having a
substantially planar surface. The method comprises forming a
plurality of spaced apart substantially parallel trenches in a
first direction in the planar surface. Each of the trenches has a
sidewall and a bottom. A region of a second conductivity type is
formed in the bottom of each trench. A floating gate is formed in
each trench insulated and spaced apart from the sidewall of the
trench. The floating gate has a first end near the bottom and a
second end furthest away from the bottom. A layer of tunneling
oxide is formed about the second end of each floating gate. A layer
of word region is formed on the layer of tunneling oxide. The layer
of word region extends in a second direction substantially
perpendicular to the first direction. The layer of word region is
cut into a plurality of strips in the second direction to form a
plurality of spaced apart word lines. Each strip is spaced apart
from one another and substantially parallel to one another, and
cuts through the floating gate in each of the trenches. Electrical
connections are made to each of the region of second conductivity
type and each of the plurality of spaced apart word lines.
BRIEF DESCRIPTION OF THE DRAWINGS
[0006] FIG. 1A is a cross-sectional view of a portion of an array
of nonvolatile memory cells made by the method of the present
invention.
[0007] FIG. 1B is a schematic circuit diagram of an array of memory
cells made by the method of the present invention.
[0008] FIGS. 2A-2K are the steps showing the method of the present
invention for manufacturing the array of non-volatile memory
cells.
DETAILED DESCRIPTION OF THE INVENTION
[0009] Referring to FIG. 1A, there is shown a cross-sectional view
of a portion of an array of nonvolatile memory cells 10 made by the
method of the present invention. The cell 10 is similar to the cell
shown and described in U.S. Pat. No. 5,029,130, whose disclosure is
incorporated herein in its entirety by reference. However, unlike
the cell shown and described in U.S. Pat. No. 5,029,130, which has
one floating gate and operates in one direction, the cell 10 has
two floating gates and as will be seen, operates bidirectionally.
The memory cell 10 is formed in a substantially single crystalline
semiconductor substrate 12, such as silicon. The substrate 12 is of
a first conductivity type, such as P type. The substrate 12 also
has a planar surface 8. Within the substrate 12 is a first region
14 of a second conductivity type. A second region 16 of a second
conductivity type is spaced apart from the first region 14. Between
the first region 14 and the second region 16 is a channel region.
Each of the first region 14 and a second region 16, however, lies
in a trench in the substrate 12 with a portion of the channel
region being a planar surface 8. Each of the trenches has a bottom
and a side wall with the first region 14 and the second region 16
being at the bottom of each trench. Thus, the channel region has
three portions: a first portion 4 which is along a sidewall of a
first trench, a second portion 6 which is along a sidewall of a
second trench, and the planar surface portion 8 which is between
the first portion 4 and the second portion 6. A first floating gate
18A and a second floating gate 18B are along the side of the
sidewalls, 4 and 6, respectively, and spaced apart therefrom and
insulated therefrom. Thus, each of the floating gate 18A and 18B
controls the conduction of the portions 4 and 6, respectively of
the channel region. Further, each cell 10 has a control gate 26.
The control gate 26 is substantially parallel to the planar surface
8 and controls the portion 8 of the channel region which is along
the planar surface 8. A first contact 30 contacts the first region
14 and a second contact 28 contacts the second region 16. Thus,
each of the contacts 30 and 28 extend into the trench. Each of the
floating gates 18A and 18B has a tip 22A and 22B respectively which
are pointed away from the bottom of the trenches where the first
region 14 and second region 16 lie. Thus, the tips 22A and 22B are
adjacent to but spaced apart and insulated from the control gate 26
by a layer of tunneling oxide.
[0010] The operation of the cell 10 is as follows.
[0011] To program, the first region 14 is held at a small positive
voltage such as 3.0 volts, the control gate 26 is at a voltage
sufficient to turn on the third portion 8 of the channel region,
and the second region 16 is held at a programming voltage such
as+12 volts. With the first region 14 at 3.0 volts, the depletion
region of the first region 14 would expand through the first
portion 4 of the channel region. With the third portion 8 of the
channel region being turned on by the control gate 26, and the
first portion 4 being turned on, electrons are accelerated as they
traverse to the second region 16 and are injected onto the second
floating gate 18B through the mechanism of hot channel electron
injection similar to the operation described in U.S. Pat. No.
5,029,130. To program the first floating gate 18A, the voltages on
the first region 14 and the second region 16 are reversed.
[0012] To erase both the first floating gate 18A and the second
floating gate 18B, the first region 14 and the second region 16 are
held at ground. The control gate 26 is held at a high potential
such as+12 volts. In such a case, the electrons stored on the
floating gate 18A and 18B are attracted by the high positive
potential on the control gate 26 and through the mechanism of
Fowler-Nordheim tunneling, they tunnel from the tips 22 of the
floating gate 18 through the interpoly oxide to the control gate
26.
[0013] To read the cell 10 and to determine if the floating gate
18B is programmed, the second region 16 is held at ground. The
control gate line 26 is held at+2 volts sufficient to turn on the
third portion 8 of the channel region. A positive potential such
as+3 volts is applied to the first region 14. With the first region
14 at+3 volts and the contact 30 at+3 volts, even if the first
floating gate 18A were charged, the depletion region would extend
to the third portion 8 of the channel region. Conduction of the
electrons in the channel region between the first region 14 and the
second region 16 would then depend upon the state of the floating
gate 18B. If floating gate 18B were erased, then the portion 6 of
the channel region adjacent to the second floating gate 18B would
conduct and a read current would pass from the first region 14 to
the second region 16. If the second floating gate 18B were
programmed, then the negatively charged electrons on the second
floating gate 18B would prevent a read current from passing between
the first region 14 and the second region 16. To read the cell 10
to determine whether the first floating gate 18A is programmed, the
voltages applied to the first region 14 and the second region 16
are reversed.
[0014] From the foregoing, it is seen that the operation of the
cell 10 is similar to the operation of cell disclosed in U.S. Pat.
No. 5,029,130, except the cell 10 operates bidirectionally.
[0015] A schematic view of an array 110 employing a plurality of
cells 10 arranged in a plurality of rows and columns is shown in
FIG. 1B. The terms "row" and "column" are interchangeable. For the
cells 10 that are in the same row such as cells 10A, 10B and 10C,
the control gate 26 is connected together. For cells that are in
the same column, i.e. cells 10A, 10E and 101, the contact line 30
connects the first regions 14 together. In addition, the contact
line 28 connects the second region 16 together.
[0016] Consistent with the foregoing, the voltages applied to the
various selected and unselected cells 10 and portions thereof for
the operations of program, erase and read for the array 110 are as
follows:
1 Control Gate 24 First Region 14 Second Region 16 Sel Unused Sel
Unused Sel Unused Erase +12 v 0 0 0 0 0 Program V.sub.t 0 +12 v 0
V.sub.t 0 gate 18a Program V.sub.t 0 V.sub.t 0 +12 v 0 gate 18b
Read V.sub.t 0 0 0 V.sub.t 0 gate 18a Read V.sub.t 0 V.sub.t 0 0 0
gate 18b
[0017] A method of manufacturing the cell 10 and the array 110 is
as follows. Referring to FIG. 2A there is shown a cross-sectional
view of the first step in the process of making the cell 10 and the
array 110.
[0018] A layer of silicon dioxide ("oxide") 20 is deposited on a
first type (typically P type) single crystalline substrate 12. The
oxide layer 20 is between 60 and 100 angstroms. This is followed by
a deposition of a layer 24 of between 200-300 angstroms of silicon
nitride ("nitride"). The resultant structure is shown in FIG.
2A.
[0019] The structure shown in FIG. 2A is then subject to a masking
operation in which portions of nitride 24 are masked and the
unmasked portions are etched. The resultant structure is shown in
FIG. 2B.
[0020] Using the layer 24 of nitride as a mask, the layer of oxide
20 and the underlying silicon substrate 12 are etched forming
trenches. Each trench has a bottom and a sidewall. The trench is
etched to a depth, such as 300-500 angstroms. The resultant
structure is shown in FIG. 2C.
[0021] A layer of sacrificial oxide (not shown) is then deposited.
This is followed by a shallow N++diffusion implant forming the
first region 14 and the second region 16. Although the first and
second regions 14 and 16 are shown as being implanted into the
substrate 12, they can also be implanted into a well within a
substrate 12. The implant can occur at an angle of approximately 0
to 7 degrees, and at approximately 5 to 20 Kev energy. After the
implant, the structure is subject to a 950.degree. C. heating for
about 15-60 minutes to cause the regions 14 and 16 to diffuse out
from the bottom of the trench to wrap around a portion of the
sidewall of the trench. The layer of sacrificial oxide is then
removed. The resultant structure is shown in FIG. 2D.
[0022] A layer of oxide 32, approximately 80 angstroms thick, is
then conformally deposited onto the structure shown in FIG. 2D.
This would cover bottom and sidewalls of the trenches, and the
oxide 20 and nitride 24. A layer of polysilicon 18 is then
conformally deposited on the layer 32 of oxide. The resultant
structure is shown in FIG. 2E.
[0023] The polysilicon 18 is then anisotropically etched stopping
at the oxide layer 32 forming the resultant first floating gate 18A
and the second floating gate 18B. Each floating gate 18 has a tip
22. The resultant structure is shown in FIG. 2F.
[0024] The structure shown in FIG. 2F is then subject to a high
temperature oxide deposition step in which a layer 56 of high
temperature deposit oxide, approximately 500-1000 angstroms thick,
is conformally deposited on the structure shown in FIG. 2F. The
structure is then subject to a CMP step stopping on the silicon
nitride layer 24. The resultant structure is shown in FIG. 2G.
[0025] MOL [what is that] 58, such as BPSG, is then deposited
everywhere to a depth of approximately 500-1000 angstroms. The
resulting structure is shown in FIG. 2H.
[0026] CMP is then applied to the structure shown in FIG. 2H with
the silicon nitride layer 24 used as the polished stop. The
resultant structure is shown in FIG. 21.
[0027] The silicon nitride 24 is then removed by wet etch or dry
etch. The resultant structure is shown in FIG. 2J.
[0028] A layer 60 of high temperature oxide is then deposited
everywhere covering the tips 22A and 22B of the floating gates 18A
and 18B respectively. Over the oxide layer 20 however, because the
layer 20 was covered by nitride 24 and the removal of the nitride
24 would not have been absolutely complete, the amount of oxide 60
deposited over the layer 20 would only be on the order of 3-10
angstroms. The high temperature oxide 60 is deposited to a depth of
approximately 130-210 angstroms. Thereafter, polysilicon 26 to form
the control gate 26 is deposited on the tunneling oxide 60 to a
thickness of approximately 500-1000 angstroms. The resultant
structure is shown in FIG. 2K.
[0029] A masking step is then performed. Photoresist is applied to
the structure shown in FIG. 2K. Strips of photoresist, parallel to
one another lying in planes above and below the paper shown in FIG.
2K are removed by the masking process. Where the photoresist is
removed, the polysilicon 26 is anisotropically etched. Further, the
oxide 60 is anisotropically etched. Finally, the floating gates 18A
and 18B are also etched in the regions where the photoresists are
removed, thereby cutting the continuity of the floating gates 18A
and 18B. The regions 14 and 16, however, maintain their continuity
in a direction substantially perpendicular to the plane of the
paper on which FIG. 2K is shown.
[0030] Contacts are then formed to the structure shown in FIG. 2K
forming the cross-section view shown in FIG. 1A. As is apparent,
adjacent cells 10 share the same either first region contact 30 or
the second contact region 28. Further, since the regions 14 and 16
are buried diffusion lines, contacts 28 and 30 need not be made to
every cell 10. The contacts 28 and 30 are made only for the purpose
of strapping to the regions 14 and 16.
* * * * *