U.S. patent application number 10/491959 was filed with the patent office on 2004-12-23 for container, and thermal forming device and thermal forming method therefor.
Invention is credited to Nakazato, Shinsaku, Takeshita, Yasuo, Yokoyama, Toshiyuki.
Application Number | 20040256397 10/491959 |
Document ID | / |
Family ID | 26624204 |
Filed Date | 2004-12-23 |
United States Patent
Application |
20040256397 |
Kind Code |
A1 |
Nakazato, Shinsaku ; et
al. |
December 23, 2004 |
Container, and thermal forming device and thermal forming method
therefor
Abstract
The present invention provides a bottomed cylindrical container,
comprising a body wall, a bottom wall, and a ring-shaped foot
downwardly extending from the bottom wall, said container being
produced by thermo-molding a resin sheet, characterized in that
said foot is formed by folding an inner wall by compressed fluid to
be fusion-bonded with an outer wall, so as to form the foot
comprising the inner wall and the outer wall. The present invention
also provides a bottomed cylindrical container, comprising a body
wall having a grounding edge at a lower end thereof, and a bottom
wall, said container being produced by thermo-molding a resin
sheet, characterized in that said bottom wall connects with an
upper edge of an inner wall produced by folding back the body wall
along the grounding edge and by fusion-bonding it to an inner
periphery of the body wall. In addition, the present invention
provides the methods for thermo-molding these containers and their
apparatuses.
Inventors: |
Nakazato, Shinsaku;
(Koto-Ku, JP) ; Takeshita, Yasuo; (Iwata-Gun,
JP) ; Yokoyama, Toshiyuki; (Koto-ku, JP) |
Correspondence
Address: |
OLIFF & BERRIDGE, PLC
P.O. BOX 19928
ALEXANDRIA
VA
22320
US
|
Family ID: |
26624204 |
Appl. No.: |
10/491959 |
Filed: |
April 8, 2004 |
PCT Filed: |
October 30, 2002 |
PCT NO: |
PCT/JP02/11284 |
Current U.S.
Class: |
220/628 |
Current CPC
Class: |
B29C 51/343 20130101;
B65D 3/12 20130101; B65D 1/26 20130101; B29C 2791/006 20130101;
B29C 51/10 20130101; B29L 2031/7132 20130101; B29C 51/04 20130101;
B29C 51/36 20130101; B29C 51/40 20130101; B29C 2791/001 20130101;
B65D 1/42 20130101; B29C 2791/007 20130101 |
Class at
Publication: |
220/628 |
International
Class: |
B65D 025/24 |
Foreign Application Data
Date |
Code |
Application Number |
Oct 30, 2001 |
JP |
2001-332447 |
Sep 30, 2002 |
JP |
2002-286938 |
Claims
1. A bottomed cylindrical container, comprising a body wall, a
bottom wall, and a ring-shaped foot downwardly extending from the
bottom wall, said container being produced by thermo-molding a
resin sheet, characterized in that said foot is formed by folding
an inner wall by compressed fluid to be fusion-bonded with an outer
wall, so as to form the foot comprising the inner wall and the
outer wall.
2. The bottomed cylindrical container according to claim 1, wherein
said bottom wall comprises a central section and a peripheral
section, and the peripheral portion is made thin.
3. A bottomed cylindrical container, comprising a body wall having
a grounding edge at a lower end thereof, and a bottom wall, said
container being produced by thermo-molding a resin sheet,
characterized in that said bottom wall connects with an upper edge
of an inner wall produced by folding back the body wall along the
grounding edge and by fusion-bonding it to an inner periphery of
the body wall.
4. An apparatus for thermo-molding a resin sheet to a bottomed
cylindrical container, comprising an upper mold having a plug, and
a lower mold having a female mold and a bottom bush, wherein said
female mold has mold surfaces for forming a body wall of the
container, and said bottom bush has compressed air blow-in
holes.
5. An apparatus for thermo-molding a resin sheet to a bottomed
cylindrical container with a ring-shaped foot, comprising an upper
mold having a plug, and a lower mold having a female mold and a
bottom bush, wherein said female mold is provided with suction
holes, said female mold has a mold surface for forming a body wall
of the container, a mold surface for forming a bottom peripheral
wall of the container, and a mold surface for forming an outer wall
of the foot, and said bottom bush has compressed fluid blow-in
holes.
6. The apparatus according to claim 4, wherein said lower mold
comprises a mold base, the bottom bush in the mold base, and the
female mold on the mold base, a gap is formed between a lower
surface of the female mold and the mold base, and an annular
suction groove is formed between a lower surface of the female mold
and the mold base, and communicates with the gap.
7. A method for thermo-molding a footed and bottomed cylindrical
container, comprising heating a thermoplastic resin sheet, pressing
the heated sheet by a plug of an upper mold with vacuum-sucking, to
contact the sheet with mold surfaces of a female mold of a lower
mold, so as to form a body wall and an outer wall of a foot of the
container, and blowing compressed fluid through blow-in holes of a
bottom bush of the lower mold into the female mold with
vacuum-sucking, to contact the sheet on a top surface of the bottom
bush with a bottom surface of the plug, so as to form a bottom wall
and an inner wall of the foot, said inner wall being fusion-bonded
with the outer wall.
8. A method for thermo-molding a bottomed cylindrical container,
comprising: heating a thermoplastic resin sheet, pressing the
heated sheet by a plug of an upper mold with vacuum-sucking, to
contact the sheet with mold surfaces of a femal mold of a lower
mold, so as to form a body wall of the container, and blowing
compressed fluid through blow-in holes of a bottom bush of the
lower mold into the female mold with vacuum-sucking, to contact the
sheet on a top surface of the bottom bush with a bottom surface of
the plug, so as to form a bottom wall and an inner wall being
fusion-bonded with the body wall.
9. The apparatus according to claim 5, wherein said lower mold
comprises a mold base, the bottom bush in the mold base, and the
female mold on the mold base, a gap is formed between a lower
surface of the female mold and the mold base, and an annular
suction groove is formed between a lower surface of the female mold
and the mold base, and communicates with the gap.
Description
BACKGROUND OF THE INVENTION
[0001] This invention relates to a container and a thermo-molding
apparatus and a thermo-molding method for molding such a container.
More particularly, the present invention relates to a legged and
bottomed cylindrical thin wall container or a bottomed cylindrical
container having the bottom wall connected to the inner barrel of
the body section produced by folding the latter back at the
grounding edge of the container, which is molded by thermo-molding
and made free from any gap in the inside of the junction of the leg
or the body inner barrel and the body wall, and also a
thermo-molding apparatus and a thermo-molding method for molding
such a container.
[0002] Legged and bottomed containers molded by thermo-molding a
thermoplastic resin sheet and made free from any gap in the inside
at the site corresponding to the leg shaped by bending the sheet
and thermo-molding apparatus and thermo-molding methods for molding
such bottomed containers are known to date. For example, Japanese
Patent Laid-open Nos. 2000-225642 and 2001-001395 disclose such
bottomed containers and thermo-molding apparatus and thermo-molding
methods for molding such bottomed containers.
[0003] According to the above patent documents describing the prior
art, a bottomed container is thermo-molded either by using a
thermo-molding apparatus comprising an upper plug unit having a
pressure molding plug and cooling male mold, and a unit of female
mold including an upper mold for forming the mouth section and the
body peripheral section of the container, an intermediate mold for
forming the lower part of the body peripheral section and the outer
peripheral surface of the bottom rim (or foot) and a bottom mold
for forming the inner peripheral surface of the bottom rim and the
bottom wall or by using a thermo-molding apparatus comprising a
pressure molding plug, a female mold and a bottom mold.
[0004] More specifically, a container is molded by pushing the
pressure molding plug into the female mold to shape the container
so as to make it show the profile of the surface of the female
mold, while holding the bottom mold to the lowered position, and
subsequently raising the bottom mold to form the bottom wall and
the bottom rim respectively on the upper surface of the bottom mold
and between the bottom mold and the female mold.
[0005] The bottom rim is made either to flare toward the lower end
and show a triangular cross section or to show a cylindrical
profile that is vertically extending with a same diameter.
[0006] With the prior art, regardless if the bottom rim is flared
or made to show a vertically extending cylindrical profile, the
difference between the outer diameter of the upper end of the mold
surface of the female mold (more particularly its intermediate
mold) for forming the outer peripheral surface of the bottom rim
and the outer diameter of the mold surface of the bottom mold for
forming the inner peripheral surface of the bottom rim is greater
than the thickness of the resin sheet and slightly smaller than the
twice of the thickness because the bottom rim is formed between the
mold surface of the mold surface of the female mold (more
particularly its intermediate mold) and that of the bottom
mold.
[0007] Therefore, if twice of the resin sheet that is used for
producing the container is smaller than the difference of the
diameters, a gap is produced along the inner surface of the
container at the site that corresponds to the bottom rim.
[0008] This means that, with either of the above described
thermo-molding apparatus and the corresponding molding method, it
is not feasible to use resin sheets having different thicknesses
and particularly thin resin sheets cannot be used.
[0009] If thin resin sheets are to be used, the difference between
the outer diameter of the upper end of the mold surface of the
female mold (more particularly its intermediate mold) for forming
the outer peripheral surface of the bottom rim and the outer
diameter of the mold surface of the bottom mold for forming the
inner peripheral surface of the bottom rim needs to be reduced.
[0010] Additionally, the thickness of resin sheet can show
variances in the stages before forming the bottom rim because the
thickness of the original roll, the thermo-molding temperature, the
degree of vacuum and the timing of applying compressed air can vary
significantly. Therefore, it is very difficult to constantly
maintain the molding conditions that make the thickness of the bent
resin sheet slightly greater than the gap between the metal
molds.
[0011] Thus, while the above described problem may be relatively
insignificant when molding a large container by using a thick resin
sheet, the thickness may have to be more rigorously controlled when
a relatively thin resin sheet is used. In other words, the prior
art is not suited for molding small containers.
SUMMARY OF THE INVENTION
[0012] Therefore, it is the object of the present invention to
dissolve the above identified problem and provide a legged and
bottomed cylindrical container having no gap in the inside of the
foot or a bottomed cylindrical container having no gap between the
inner barrel of the body produced by bending the original resin
sheet at the grounding edge and the body wall, a thermo-molding
apparatus and a thermo-molding method for molding such a
container.
[0013] According to the invention, the above object is achieved by
providing a bottomed cylindrical container, comprising a body wall,
a bottom wall, and a ring-shaped foot downwardly extending from the
bottom wall, said container being produced by thermo-molding a
resin sheet; characterized in that said foot is formed by folding
an inner wall by compressed fluid to be fusion-bonded with an outer
wall, so as to form the foot comprising the inner wall and the
outer wall. Preferably, said bottom wall comprises a central
section and a peripheral section, and the peripheral portion is
made thin.
[0014] According to another aspect of the invention, the above
object is achieved by providing a bottomed cylindrical container,
comprising a body wall having a grounding edge at a lower end
thereof, and a bottom wall, said container being produced by
thermo-molding a resin sheet, characterized in that said bottom
wall connects with an upper edge of an inner wall produced by
folding back the body wall along the grounding edge and by
fusion-bonding it to an inner periphery of the body wall.
[0015] The present invention also provides an apparatus for
thermo-molding a resin sheet to a bottomed cylindrical container,
comprising an upper mold having a plug, and a lower mold having a
female mold and a bottom bush; wherein said female mold has mold
surfaces for forming a body wall of the container; and said bottom
bush has compressed air blow-in holes. Also, it provides an
apparatus for thermo-molding a resin sheet to a bottomed
cylindrical container with a ring-shaped foot, comprising an upper
mold having a plug, and a lower mold having a female mold and a
bottom bush, wherein; said female mold is provided with suction
holes; said female mold has a mold surface for forming a body wall
of the container, a mold surface for forming a bottom peripheral
wall of the container, and a mold surface for forming an outer wall
of the foot; and said bottom bush has compressed fluid blow-in
holes. Preferably, said lower mold comprises a mold base, the
bottom bush in the mold base, and the female mold on the mold base;
a gap is formed between a lower surface of the female mold and the
mold base; and an annular suction groove is formed between a lower
surface of the female mold and the mold base, and communicates with
the gap.
[0016] Another aspect of the present invention provides a method
for thermo-molding a footed and bottomed cylindrical container;
comprising heating a thermoplastic resin sheet; pressing the heated
sheet by a plug of an upper mold with vacuum-sucking, to contact
the sheet with mold surfaces of a female mold of a lower mold, so
as to form a body wall and an outer wall of a foot of the
container; and blowing compressed fluid through blow-in holes of a
bottom bush of the lower mold into the female mold with
vacuum-sucking, to contact the sheet on a top surface of the bottom
bush with a bottom surface of the plug, so as to form a bottom wall
and an inner wall of the foot, said inner wall being fusion-bonded
with the outer wall.
[0017] Still another aspect of the present invention provides a
method for thermo-molding a bottomed cylindrical container;
comprising heating a thermoplastic resin sheet; pressing the heated
sheet by a plug of an upper mold with vacuum-sucking, to contact
the sheet with mold surfaces of a femal mold of a lower mold, so as
to form a body wall of the container; and blowing compressed fluid
through blow-in holes of a bottom bush of the lower mold into the
female mold with vacuum-sucking, to contact the sheet on a top
surface of the bottom bush with a bottom surface of the plug, so as
to form a bottom wall and an inner wall being fusion-bonded with
the body wall.
BRIEF DESCRIPTION OF THE DRAWINGS
[0018] FIG. 1A is a schematic front view of the first embodiment of
legged and bottomed container according to the invention, showing
it partly in cross section.
[0019] FIG. 1B is an enlarged partial view of the embodiment,
showing a principal part thereof.
[0020] FIG. 2 is a schematic front view of the first embodiment of
thermo-molding apparatus according to the invention, showing it
partly in cross section.
[0021] FIG. 3 is a schematic front view of the first embodiment of
thermo-molding apparatus of FIG. 2, showing it partly in cross
section and illustrating the state where the molds are closed and
the plug is made to start lowering.
[0022] FIG. 4A is a schematic front view of the first embodiment of
thermo-molding apparatus of FIG. 2, showing it partly in cross
section and illustrating the state where the plug reaches the
lowest position and the vacuum molding operation is completed.
[0023] FIG. 4B is an enlarged partial view of the embodiment of
FIG. 4A.
[0024] FIG. 5 is a schematic front view of the first embodiment of
thermo-molding apparatus of FIG. 2, showing it partly in cross
section and illustrating the state the bottom of the container is
molded by applying compressed air.
[0025] FIG. 6 is a schematic front view of the first embodiment of
thermo-molding apparatus of FIG. 2, showing it partly in cross
section and illustrating the state where the operation of molding
the bottom of the container by applying compressed air is
completed.
[0026] FIG. 7 is a schematic front view of the second embodiment of
legged and bottomed container according to the invention, showing
it partly in cross section.
[0027] FIG. 8 is a schematic front view of the second embodiment of
thermo-molding apparatus, showing it partly in cross section and
illustrating the state where the plug reaches the lowest position
and the vacuum molding operation is completed.
[0028] FIG. 9 is a schematic front view of the second embodiment of
thermo-molding apparatus of FIG. 8, showing it partly in cross
section and illustrating the state where the operation of molding
the bottom of the container by applying compressed air is
completed.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0029] Now, the present invention will be described in detail by
referring to the accompanying drawings that illustrate preferred
embodiments of the invention.
[0030] Firstly, the first embodiment of footed and bottomed
cylindrical container or footed bowl-shaped container A will be
described.
[0031] As shown in FIG. 1, a footed and bottomed cylindrical
container A comprises a body wall 2 having an outwardly directed
flange 1 arranged along a peripheral edge of a top opening, a
bottom wall 3, and a ring-shaped foot 4 extending downwardly from
the bottom wall 3.
[0032] The body wall 2 is curved inwardly at and near a lower end
thereof until it becomes horizontal and reaches to the foot 4. Such
horizontal part is a bottom peripheral wall 5 which connects to the
bottom wall 3. The bottom wall 3 is located within the foot 4, and
comprises a central section 6a and a thin peripheral section
6b.
[0033] The foot 4 comprises an outer wall 7a and an inner wall 7b
which is produced by inwardly folding back the outer wall 7a along
at a lower edge thereof and welded to the outer wall. An outwardly
bulge 8 is formed along a lower peripheral edge of the foot 4.
[0034] Preferable resin materials that can be used for forming the
container A include poly-olefin type resins such as polypropylene
(PP) and polyethylene (PE), although other thermo-moldable
synthetic resin materials or thermoplastic resin material such as
polyethyleneterephthala- te (PET) can also suitably be used. The
synthetic resin sheet to be used for molding may be of single layer
or of multilayer (or laminate).
[0035] The synthetic resin sheet to be used for molding has a
thickness between 0.3 and 3.0 mm, while the wall thickness of the
body wall of the container obtained by thermo-molding the sheet is
between about 0.1 and about 0.45 mm.
[0036] Now, the first embodiment of thermo-molding apparatus B to
be used for thermo-molding the first embodiment of container will
be described.
[0037] As shown in FIG. 2, the thermo-molding apparatus B comprises
an upper mold C and a lower mold D.
[0038] The upper mold C comprises a cylindrical clamp 11 for
pinching the sheet S, and a plug 10 vertically movable relative to
the clamp 11. The sheet S is heated by a heater (not shown). The
clamp 11 is not limited to cylindrical shape.
[0039] The plug 10 has a cylindrical wall surface 12 and a flat
bottom surface 13. While the clamp 11 is so designed that
compressed fluid (such as compressed air) is blown into it from
above, it is not essential to blow compressed fluid into the clamp
11.
[0040] While the plug 10 of the illustrated embodiment shows a
cylindrical profile, it may alternatively show some other profile
such a conical profile. Similarly, while the bottom surface 13 of
plug of the illustrated embodiment is flat, it may alternatively be
outwardly or inwardly curved depending on the molded product to be
produced by using it.
[0041] The lower mold D comprises a mold base 15, a female mold 16
arranged on the mold base 15, and a bottom bush 17 arranged in an
inside of the mold base 15.
[0042] The female mold 16 has a mold surface 18 for forming the
body wall 2 of the container A to be molded, a mold surface 19 for
forming the bottom peripheral wall 5, and a mold surface 20 for
forming the outer peripheral surface of the foot 4. A passage 21 is
arranged at the lower peripheral edge of the mold surface 20, so
that a gap 21 is provided between the lower surface of the female
mold 16 and the mold base 15. The gap 21 communicates with an
annular suction groove 22.
[0043] The suction groove 22 communicates with a connection hole 23
arranged in the mold base 15. The connection hole 23 communicates
with a vacuum unit (not shown). The female mold 16 is provided with
a communication hole 24. The communication hole 24 communicates
with the connection hole 23. A number of suction holes 25 are
arranged near the upper edge and along the lower edge of the mold
surface 18 of the female mold 16, and each of the suction holes 25
communicates with the communication hole 24. Thus, air can be drawn
from the inside of the female mold 16 through the connection hole
23, the suction groove 23, the gap 21 and the suction holes 25.
[0044] A number of blow-in holes 27 are formed at a center of the
top surface 26 of the bottom bush 17. A connection hole 28 is
formed in the bottom bush 17, and communicates with a source of
compressed fluid (not shown). Thus, compressed fluid is blown into
the inside of the female mold 16 through the communication hole 28
and the blow-in holes 27.
[0045] The bottom bush 17 is provided with a heater 29.
[0046] Now, the method of thermo-molding the container according to
the first embodiment of the invention will be described below.
[0047] For the purpose of thermo-molding, the sheet S is heated by
a heater (not shown) to the molding temperature that is somewhat
lower than a melting point of the synthetic resin. The female mold
16 and the bottom bush 17 of the thermo-molding apparatus B are
also heated and maintained to a predetermined temperature level
(usually about 80 to about 150.degree. C., about 50 to about
180.degree. C. depending on the material of the sheet) by the
heater 29. In this case, the temperature of the female mold 16 and
the bottom bush 17 should be controlled not to cool the heated
sheet.
[0048] If the resin sheet S is made of PP and has a thickness of
1.0 mm, it is heated to about 140 to 200.degree. C.
[0049] The upper mold C is lowered, and the lower mold is raised
from the state of FIG. 2. As shown in FIG. 3, the heated sheet
becomes pinched and pressed between the clamp 11 of the upper mold
C and the top surface of the female mold 16 of the lower mold D.
The plug 10 is further lowered relative to the clamp 11, the sheet
S is forced to extend downwardly by the lower surface 13 of the
plug 10, because the sheet is already heated and softened. At this
time, since air is drawn through the gap 21 and the suction holes
25, the sheet S is drawn by the suction holes 25, and comes to be
held in tight contact with the inner surface of female mold above
the suction holes 25. At this time, compressed fluid may be blown
into the clamp 11 from above.
[0050] When the plug 10 is further lowered, the sheet S comes to be
held in tight contact with the mold surfaces 18, 19, 20 of the
female mold 16 and the top surface 26 of the bottom bush 17, as
illustrated in FIG. 4. Thus, the sheet S is molded by the mold
surfaces 18, 19, 20 and the top surface 26, to produce the body
wall 2, the bottom peripheral wall 5 and the outer wall 7a of the
foot 4 of the container A.
[0051] As shown in FIGS. 4A and 4B, the plug 10 is stopped before
it contacts with the mold surface 19. As a result, a gap is formed
between the sheet S on the mold surface 19 and the lower surface 13
of the plug 10. Air is drawn out through the gap when compressed
air is blown into the female mold 16 in a subsequent step as will
be described hereinafter. In the case of the illustrated
embodiment, the gap is about 0.1 to 0.5 mm.
[0052] By the above described vacuum sucking, resin "a" is drawn
into the gap 21 to produce the bulge 8 of the container. Since the
resin "a" is drawn into the gap 21, the gap 21 is filled with the
resin, so that eventually no resin is further drawn into the gap 21
any more. The bottom bush 17 is heated to the above described
predetermined temperature level by the heater 29, and the part of
the sheet S that contacts with the top surface 26 of the bottom
bush 17 is held to the molding temperature that is close to the
melting point.
[0053] As described above, the sheet S is pressed and held in
contact with the mold surface 19 as a result of the air suction
through the suction holes 25 for producing vacuum (and due to the
compressed air in the clamp 11, if desired), the resin "a" of the
lower end of the sheet S is drawn into the gap 21, and the part of
the sheet S that is held in contact with the top surface 26 is held
to the molding temperature that is close to the melting point.
Under these circumstances, when compressed fluid is blown into the
female mold 16 through the blow-in holes 27, the part of the sheet
S with the temperature level close to the melting point is folded
back along the lower edge of the outer wall 7a, and is moved
upwardly, as illustrated in FIG. 5. Thus, the central portion of
the part of the sheet S with the temperature level close to the
melting point is brought into tight contact with the bottom surface
13 of the plug 10, while the peripheral portion is folded back
along the lower edge of the outer wall 7a, and drawn to come into
tight contact with and fusion-bonded to the outer wall 7a. In this
way, the foot 4 is formed by fusion-bonding the outer wall 7a and
the inner wall 7b as integral parts thereof. FIG. 6 schematically
illustrates a state where the operation of producing the footed and
bottomed cylindrical container by molding is completed.
[0054] At this time, since the peripheral part of the sheet S is
expanded, the peripheral section 6b of the molded bottom wall 3
shows a thickness smaller than the central section 6a. Besides,
since the temperature of the sheet is maintained to a level close
to the melting point, the folded portion is fusion-bonded to the
portion of the sheet S that is held in tight contact with the mold
surface 20.
[0055] The central section can be made thin by using a plug having
an upwardly curved lower surface for the molding operation using
compressed air.
[0056] The thus formed container A is then cooled, and removed from
the mold. Subsequently, the outwardly directed flange 1 is formed
by cutting in a desired profile, to complete the operation of
producing the footed and bottomed cylindrical container A.
[0057] The inner wall 7b and the outer wall 7a of the foot 4 of the
obtained container A are in a completely fusion-bonded. In other
words, they are integrally formed without any gap. It is a thin
wall container whose body wall 2 and the bottom wall 3 are about
0.2 mm thick.
[0058] The above described first embodiment can be modified as
follows.
[0059] In the above described embodiment, the plug 10 is stopped
before it contacts the mold surface 19 of the female mold 16, and a
gap is formed between the sheet S on the mold surface 19 and the
lower surface 13 of the plug 10, to allow the air (between the
sheet S on the bush 17 and the lower surface 13) left there to be
drawn out. Alternatively, the plug 10 may be replaced by a plug 10
having a vent arranged between the lower surface 13 and the
cylindrical wall surface 12. In such modification, the lower
surface 13 of the plug 10 presses the sheet S against the mold
surface 19 for forming the bottom peripheral wall.
[0060] When the compressed fluid is blown through the blow-in holes
27 in this modified embodiment, air between the sheet S on the
bottom bush 17 and the bottom surface 13 can be removed by the
above described vent.
[0061] Still alternatively, if the bottom surface 13 of the plug 10
is stopped further before the mold surface 19 of the female mold 16
to produce a gap of 0.5 to 1.5 mm between itself and the sheet
surface after the vacuum forming, and if the compressed fluid is
blown through the blow-in holes 27, the bottom wall 3 will project
above the bottom peripheral wall 5 by pressure forming.
[0062] Now, the second embodiment of the container, the
thermo-molding apparatus and the thermo-molding method to be used
for molding the container will be described below.
[0063] This embodiment of the invention relates to a bottomed
cylindrical container (cup-shaped container).
[0064] Referring to FIG. 7, A' denotes the bottomed cylindrical
container that comprises a body wall 31 having an outwardly
directed flange 30 arranged along a peripheral edge of the opening,
and a bottom wall 32.
[0065] A lower end of the body wall 31 is a grounding edge 33 of
the container. The body wall 31 is inwardly folded back along the
grounding edge 33 to produce an inner wall 34. A top edge 35 of the
inner wall 34 connects to the bottom wall 32.
[0066] The inner wall 34 is fusion-bonded or welded to an inner
periphery of the part of the body wall 31 located under the top
edge 35, and no gap is found between the body wall 31 and the inner
wall 34.
[0067] The method of thermo-molding the container according to the
second embodiment of the invention will be described below.
[0068] The thermo-molding apparatus in the second embodiment is
obtained by modifying the lower mold of the first embodiment of the
invention. Therefore, the components that are same as those of the
first embodiment are denoted by the same reference numerals and
affixed by "a". The differences of the second embodiment and the
first embodiment will be described specifically.
[0069] Referring to FIG. 8, reference symbol C' denotes the upper
mold, and D' denotes the lower mold.
[0070] As in the case of the above described first embodiment, the
upper mold C' comprises a cylindrical clamp 11a and a plug 10a
vertically movable relative to the clamp 11a. The sheet S' is
heated by a heater (not shown). The plug 10a has a cylindrical wall
surface 12a and a flat bottom surface 13a. While the clamp 11a is
so designed that compressed fluid (such as compressed air) is blown
into it from above, it is not essential to blow compressed fluid
into the clamp 11a.
[0071] The lower mold D' comprises a mold base 15a, a female mold
16a arranged on the mold base 15a, and a bottom bush 17a arranged
in an inside of the mold base 15a.
[0072] The female mold 16a has a mold surface 40 for forming the
body wall 31 of the container A' to be molded. A passage 21a is
arranged at the lower peripheral edge of the mold surface 40, so
that a gap 21a is provided between the lower surface of the female
mold 16a and the mold base 15a. The gap 21a communicates with an
annular suction groove 22a, which suction groove 22a communicates
with a vacuum device (not shown).
[0073] A number of blow-in holes 27a are formed at a center of the
top surface 26a of the bottom bush 17a. The blow-in holes 27a
communicate with a source of compressed fluid (not shown).
[0074] The bottom bush 17a is provided with a heater 29a.
[0075] Now, the method of thermo-molding the container according to
the second embodiment of the invention will be described below.
[0076] For the purpose of thermo-molding, the sheet S' is heated by
a heater (not shown) to the molding temperature that is somewhat
lower than the melting point of the synthetic resin. The female
mold 16a and the bottom bush 17a of the thermo-molding apparatus B'
are also maintained to the above described predetermined
temperature level by the heater 29a.
[0077] The heated sheet S' is pinched and pressed between the clamp
11a of the upper mold C' and the top surface of the female mold 16a
of the lower mold D'. The plug 10a is further lowered relative to
the clamp 11a, the sheet S' is forced to extend downwardly by the
lower surface 13a of the plug 10a, because the sheet is already
heated and softened. At this time, compressed air is blown from the
above, and air is drawn through the gap 21a on the lower surface of
the female mold 16a to produce vacuum, so that the sheet S' is
drawn by the gap 21a. As a result, the sheet S' comes to be held in
tight contact with mold surface 40 of female mold 16a.
[0078] The plug 10a is further lowered and stopped before it
contacts with the mold surface 40 of the female mold 16a, as shown
in FIG. 8. As a result, the sheet S' is brought into tight contact
with the mold surface 40 of the female mold 16a and the top surface
26a of the bottom bush 17a, and molded to show a profile defined by
the mold surface 40 of the female mold 16a and the top surface 26a
of the bottom bush 17a. At this time, the sheet produces portions
that become the body wall 31 and the bottom wall 32 of the
container A'.
[0079] As in the case of the above described first embodiment,
resin a is drawn into the gap 21a by the air drawing operation or
the vacuum sucking. The bottom bush 17a is heated to the above
described predetermined temperature level by the heater 29a. The
part of the sheet that contacts with the top surface 26a of the
bottom bush 17a is held to the molding temperature that is close to
the melting point.
[0080] In this way, by the vacuum sucking and the compressed fluid,
the sheet S' is pressed between the mold surface 40 and the top
surface 26a of the bottom bush 17a, and the resin "a" of the lower
end portion of the body wall 31 of the sheet S' is drawn into the
gap 21a. Then, as shown in FIG. 9, compressed air is blown into
through the blow-in holes 27a of the bottom bush 17a. The portion
of the sheet held on the top surface 26a is folded back along the
grounding edge 33. In this case, the central portion of the sheet
is brought into tight contact with the bottom surface 13a of the
plug 10a, while the peripheral portion of the sheet is brought into
tight contact with and fusion-bonded to the inner peripheral
surface of the body wall 31. Thus, as shown in FIG. 7, a bottomed
cylindrical container A' whose inner wall 34 produced by folding
back along the grounding edge 33 of the body wall 31 is
fusion-bonded to the body wall 31 is obtained.
[0081] The present invention provides the following advantages.
[0082] A footed and bottomed cylindrical container according to the
invention does not have any gap on the inner surface of the
container at a site corresponding to the foot where food can
enter.
[0083] In a bottomed cylindrical container according to the
invention, the inner wall produced by folding back the body wall
along the grounding edge thereof is welded to the body wall and
hence no gap where food can enter is produced there.
[0084] When a bottomed cylindrical container according to the
invention is filled with hot food, sealed and then cooled to reduce
the inner pressure, the bottom wall of the container operates to
absorb the impact of pressure reduction to prevent any deformation
or recession of the sealed surface because the container has a thin
the bottom wall, or at least a then peripheral portion in the
bottom wall.
[0085] Since a thermo-molding method and a thermo-molding apparatus
according to the invention is adapted to mold a ring-shaped foot or
a bottom wall by using compressed air and welding the resin layer
of the inner peripheral portion and that of the outer peripheral
portion of the foot for a bottomed cylindrical container, the foot
is formed without gap if the thickness of the material resin sheet
fluctuates. Similarly, since the inner wall produced by folding
back the body wall along the grounding edge thereof and welded to
the body wall for a cup-shaped container, no gap is formed between
the body wall and the inner wall if the thickness of the material
resin sheet fluctuates.
[0086] Therefore, containers showing a same profile can be produced
by using different material resin sheets that may have different
thicknesses by means of a same thermo-molding apparatus.
[0087] Thus, containers having a small wall thickness can be
produced by using a thin material resin sheet to save the material
depending on the applications of the containers.
[0088] Since the present invention imposes no restrictions on the
thickness of the material resin sheet, a bottomed cylindrical
container can be produced simply by bringing the bottom surface of
the plug of a thermo-molding apparatus according to the invention
into contact with or close to the mold surface of the peripheral
wall of the bottom of the female mold of the apparatus regardless
of the size of container.
[0089] Small containers can be produced by using a thin material
resin sheet.
* * * * *