U.S. patent application number 10/215115 was filed with the patent office on 2004-02-12 for polymer-embedded solder bumps for reliable plastic package attachment.
Invention is credited to Chiu, Tz-Cheng, Variyam, Manjula N..
Application Number | 20040027788 10/215115 |
Document ID | / |
Family ID | 31494804 |
Filed Date | 2004-02-12 |
United States Patent
Application |
20040027788 |
Kind Code |
A1 |
Chiu, Tz-Cheng ; et
al. |
February 12, 2004 |
POLYMER-EMBEDDED SOLDER BUMPS FOR RELIABLE PLASTIC PACKAGE
ATTACHMENT
Abstract
A plastic package for use in semiconductor devices, which has a
plurality of metallic terminals exposed on a package surface and a
metallic bump attached to each of said terminals. The bumps are
made of reflowable metal and have approximately uniform height. An
adherent layer of polymer material covers the package surface and
surrounds each of the bumps to form a solid meniscus. The layer has
a thickness between a quarter and one half of the bump height. An
analogous methodology applies to plastic assembly boards.
Inventors: |
Chiu, Tz-Cheng; (Plano,
TX) ; Variyam, Manjula N.; (Plano, TX) |
Correspondence
Address: |
TEXAS INSTRUMENTS INCORPORATED
P O BOX 655474, M/S 3999
DALLAS
TX
75265
|
Family ID: |
31494804 |
Appl. No.: |
10/215115 |
Filed: |
August 8, 2002 |
Current U.S.
Class: |
361/329 ;
257/E21.503; 257/E23.069 |
Current CPC
Class: |
H01L 2224/73203
20130101; H01L 21/563 20130101; H01L 2924/01019 20130101; H01L
2924/01079 20130101; H05K 2203/0786 20130101; H05K 2201/10977
20130101; H01L 2924/10253 20130101; H01L 2924/01087 20130101; Y02P
70/613 20151101; H01L 23/3128 20130101; H01L 2924/01322 20130101;
H05K 2203/095 20130101; H01L 23/3114 20130101; H05K 2203/0582
20130101; H01L 2924/12044 20130101; Y02P 70/50 20151101; H05K
3/3436 20130101; H01L 23/49816 20130101; H01L 2924/10253 20130101;
H01L 2924/00 20130101 |
Class at
Publication: |
361/329 |
International
Class: |
H05K 005/06 |
Claims
We claim:
1. A plastic package for use in semiconductor devices, said package
having a plurality of metallic terminals exposed on a package
surface, comprising: a metallic bump attached to each of said
terminals, said bumps made of reflowable metal and having
approximately uniform height; and an adherent layer of polymer
material covering said package surface and surrounding each of said
bumps to form a solid meniscus, said layer having a thickness
between a quarter and one half of said bump height.
2. The package according to claim 1 wherein said plastic is any
polymeric material used in semiconductor encapsulation, including
molding compounds as well as thermoset and thermoplastic
formulations.
3. The package according to claim 1 wherein said semiconductor
devices include any product of the ball-grid array and chip-scale
package families.
4. The package according to claim 1 wherein said reflowable metal
is selected from a group consisting of tin, indium, tin alloys
including tin/indium, tin/silver, tin/bismuth, and tin/lead,
conductive adhesives, and z-axis conductive materials.
5. The package according to claim 1 wherein said bumps have a
diameter from about 50 to 700 .mu.m and a center-to-center spacing
between about 100 and 1300 .mu.m.
6. The package according to claim 1 wherein said polymer material
for said adherent layer includes non-electrically conductive
adhesives, epoxies filled or unfilled with inorganic particulate
fillers including boron nitride or aluminum nitride, bisphenol A
with an anhydride cross-linking agent, having a viscosity of
<8000 cps and an elasticity modulus between about 1 and 5
GPa.
7. A polymeric substrate for use in electronic assembly boards,
said substrate having a plurality of metallic terminals exposed on
a substrate surface, comprising: a metallic bump attached to each
of said terminals, said bumps made of reflowable metal and having
approximately uniform height; and an adherent layer of polymer
material covering said substrate surface and surrounding each of
said bumps to form a solid meniscus, said layer having a thickness
between a quarter and one half of said bump height.
8. The substrate according to claim 7 wherein said assembly board
is selected from a group consisting of organic materials, including
FR-4, FR-5, and BT resin, with or without strengthening or
thermally modulating fibers or fillers, including a grid of glass
fibers.
9. A method for completing a polymer plastic package for use in
semiconductor devices, comprising the steps of: providing a polymer
package having a plurality of metallic terminals exposed on a
package surface, said terminals spaced apart; attaching a metallic
bump to each of said terminals, said bumps made of reflowable metal
and having approximately uniform mass and height; reflowing said
bumps, while maintaining approximate uniformity of predetermined
height; stencil-printing a water-soluble polymer to coat the top
surface of said bumps; positioning said packages in the vacuum
chamber of a plasma apparatus so that said surface faces the plasma
source; initiating a plasma and controlling the ion mean free path
so that said ions reach said surface with predetermined energy;
exposing said surface to said plasma for a length of time
sufficient to roughen said polymer surface; clean said polymer
surface from organic contamination; and improve the surface
affinity to adhesion; removing said package from said vacuum
chamber; distributing an adherent polymeric precursor between and
around said bumps, to form a meniscus on each of said bumps and to
fill said space between said bumps by a layer having a thickness
between a quarter and one half of said height of said bumps;
supplying additional thermal energy for curing said polymeric
precursor, whereby said layer and said meniscus solidify; cooling
the package to ambient temperature; and washing said package in DI
water to remove said water-soluble polymeric bump coating,
completing said plastic package.
10. The method according to claim 9 wherein said water-soluble
polymer is polyvinyl alcohol.
11. The method according to claim 9 further comprising the process
step of slightly polishing said bump surfaces before said step of
washing to remove excess polymer.
Description
FIELD OF THE INVENTION
[0001] The present invention is related in general to the field of
electronic systems and semiconductor devices and more specifically
to the field of plastic packages attached to boards by solder
balls, wherein an auxiliary plastic layer between the solder balls
enhances the temperature cycling reliability of the plastic
package.
DESCRIPTION OF THE RELATED ART
[0002] The structure of contact pad metallizations and solder bumps
for connecting integrated circuit (IC) chips to semiconductor
packages or outside parts, as well as the thermomechanical stresses
and reliability risks involved, have been described in a series of
detailed publications by the International Business Machines
Corporation in 1969 (IBM J. Res. Develop., Vol. 13, pp.
226-296).
[0003] During and after assembly of the IC chip to an outside part
such as a substrate or circuit board by solder reflow, and then
during device operation, significant temperature differences and
temperature cycles appear between semiconductor chip and the
substrate. The reliability of the solder joint is strongly
influenced by the coefficients of thermal expansion of the
semiconductor material and the substrate material. For example,
there is more than one order of magnitude difference between the
coefficients of thermal expansion of silicon and FR-4. This
difference causes thermomechanical stresses, which the solder
joints have to absorb. Detailed calculations, in the literature
cited above and in other publications of the early 1980's,
involving the optimum height and volume of the solder connection
and the expected onset of fatigue and cracking proposed a number of
solder design solutions.
[0004] The fabrication methods and reliability problems involving
flip-chips re-appear in somewhat modified form for ball-grid array
type packages. In their book "Chip Scale Package" (McGraw-Hill,
1999), John H. Lau and Shi-Wei Ricky Lee describe various
semiconductor devices and packages of contemporary "chip-scale"
families, as they are fabricated by a number of semiconductor
companies worldwide. The newest designs and concepts in
microelectronics assembly and packaging are aiming for a package
with a planar area not substantially greater than the silicon chip
itself, or at most 20% larger area. This concept, known as
Chip-Scale Package (CSP), is finding particular favor with those
electronics industries where the product size is continually
shrinking such as cellular communications, pagers, hard disk
drivers, laptop computers and medical instrumentation. Most CSP
approaches are based on assembly with solder bumps or solder balls
on the exterior of the package, to interface with system or wiring
boards.
[0005] The ball grid array or CSP may be attached directly to a
printed circuit board (PCB), or alternatively, coupled to a second
interconnection surface such as an interposer. In the latter case,
attaching the ball grid array to the next interconnect is carried
out by aligning the solder bumps or balls on the package to contact
pads on the second level interconnection and then performing a
second solder reflow operation. During the reflow, the bumps or
balls liquefy and make a bond to the next interconnect level which
has pads or traces to receive the solder. Following the solder
reflow step, a polymeric underfill is often used between the
package and the interposer (or PCB) to alleviate mechanical stress
caused by the mismatch in the coefficients of thermal expansion
(CTE) between the package, the interposer, if any, and the PCB.
Many reliability problems occur due to the stress placed on the
solder bumps or balls when the assembly is cycled from hot to cool
during operation.
[0006] One method of drastically reducing the thermomechanical
stress on the solder bumps has been utilized in Tessera's
Micro-Ball Grid Array packages. A sheet-like compliant elastomer
substantially de-couples the solder bumps, affixed to the outside
PCB, from the IC chip and the interposer, thus relieving the
thermal mismatch. Among the drawbacks of this method are assembly
hurdles and cost considerations.
[0007] Another method aims at absorbing part of the
thermomechanical stress on the solder joints by plastic material
surrounding the joints and filling the gap between chip and
substrate. See for instance, U.S. Patents # 6,228,680, issued on
May 8, 2001; # 6,213,347, issued on Apr. 10, 2001, and # 6,245,583,
issued on Jun. 12, 2001 (Thomas et al. , Low Stress Method and
Apparatus for Underfilling Flip-Chip Electronic Devices). However,
the underfilling method represents an unwelcome process step after
device attachment to the motherboard.
[0008] In a recent wafer-level process approach by Kulicke &
Soffa, flux-impregnated epoxy is screened on the wafer, with
openings for the chip contact pads. The solder balls are placed on
the pads; during the reflow process, the epoxy softens and forms a
fillet at the base of the solder ball. An epoxy "collar" extends
about 50 to 100 .mu.m up the side of the solder ball from the chip
surface, where stress-induced cracks typically originate. This
collar restricts the creep flow of the solder, where cracks
typically form. The wafer-level process with the required high
temperature of solder reflow cannot be transferred to individual
plastic packages. As another drawback, the adhesion between the
solder balls and the plastic fillet is weak at best and often
non-existent.
[0009] An urgent need has arisen for a coherent, low-cost method of
preventing stress-induced solder bump cracks during temperature
cycling for ball-grid array packages. The method should be flexible
enough to be applied for different semiconductor product families
and a wide spectrum of plastic package design and process
variations. Preferably, these innovations should be accomplished
using the installed equipment base so that no investment in new
manufacturing machines is needed.
SUMMARY OF THE INVENTION
[0010] A plastic package for use in semiconductor devices is
described, which has a plurality of metallic terminals exposed on a
package surface and a metallic bump attached to each of said
terminals. The bumps are made of reflowable metal and have
approximately uniform height. An adherent layer of polymer material
covers the package surface and surrounds each of the bumps to form
a solid meniscus. The layer has a thickness between a quarter and
one half of the bump height. An analogous methodology applies to
plastic assembly boards.
[0011] In the method for completing a polymer plastic package
according to the invention, the solder bumps are attached and
reflowed first, resulting in an approximately uniform predetermined
height. Then, a water-soluble polymer is stencil-printed to coat
the top surface of the bumps. In a vacuum chamber, an
energy-controlled plasma roughens and cleans the polymer surface,
improving the surface affinity to adhesion. An adherent polymeric
precursor is distributed between and around the bumps to form a
meniscus on each of the bumps and fill the space between the bumps
with a layer having a thickness between a quarter and one half of
the height of the bumps. Additional thermal energy cures the
polymeric precursor, solidifying the layer and the meniscus.
Finally, DI water removes the water-soluble polymeric bump
coating.
[0012] Detailed model calculations as well as experimental data
show that the polymer coat on plastic packages, applied by the
method of the invention, reduces the plastic energy density by 50%
and increases the board-level reliability in temperature cycling
from -40 to +125.degree. C. by 50% compared to standard plastic
packages.
[0013] It is an aspect of the present invention to provide a
flexible methodology of fabrication and material selection to
achieve the benefit of the stress-relieving polymer coat.
[0014] Another aspect of the invention is to provide a methodology
for a wide range of plastic ball-grid array and chip-scale
packages.
[0015] It is a technical advantage of the present invention that a
wide variety of solder alloys and reflow temperatures can be
employed for the stress-reduced packages.
[0016] Another technical advantage is the possibility to apply the
new methodology to plastic assembly boards with solder bumps for a
wide variety of applications.
[0017] Other technical advantages of the present invention include
an improved reliability of the assembled device without the need of
a polymer interface layer at the contact pads, or a polymer
underfill for the bump-assembled device, reducing the manufacturing
cost.
[0018] The technical advances represented by the invention, as well
as the aspects thereof, will become apparent from the following
description of the preferred embodiments of the invention, when
considered in conjunction with the accompanying drawings and the
novel features set forth in the appended claims.
BRIEF DESCRIPTION OF THE DRAWINGS
[0019] FIG. 1 is a schematic and simplified cross section of a
package assembled on an external part using reflowable metal
bumps.
[0020] FIG. 2 is an enlargement of a portion of FIG. 1.
[0021] FIG. 3 is an enlargement of a portion of FIG. 1 showing the
development of a crack through the reflowable metal bump.
[0022] FIG. 4 is a schematic cross section of a portion of a
plastic package having a reflowable metal bump attached to an
external part, and an adherent polymer layer surrounding the
package-near portion of the solder joint.
[0023] FIG. 5 is a schematic cross section of a portion of a
substrate having a solder interconnection to a semiconductor
package, and an adherent polymer layer surrounding the
substrate-near portion of the solder joint.
[0024] FIGS. 6 to 10 are schematic cross sections of a plastic
package and a plurality of solder bumps, illustrating the process
flow for completing a plastic semiconductor package with
polymer-embedded solder bumps.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0025] The present invention is related to U.S. patent application
# 09/952,454, filed on Sep. 14, 2001 (Owens et al., "Improved
Adhesion by Plasma Conditioning of Semiconductor Chip Surfaces"),
which is incorporated herewith by reference.
[0026] The present invention is further related to U.S. Patents #
6,213,347, issued Apr. 10, 2001, and # 6,228,680, issued May 8,
2001 (both Thomas, "Low Stress Method and Apparatus for
Underfilling Flip-Chip Electronic Devices"); and # 6,245,583,
issued Jun. 12, 2001 (Amador et al., "Low Stress Method and
Apparatus of Underfilling Flip-Chip Electronic Devices").
[0027] The present invention provides the process to minimize the
thermomechanical stress in a microelectronic assembly of a plastic
package and a printed circuit board as shown schematically and
simplified in FIG. 1. A portion of the assembly in FIG. 1 is
enlarged in FIG. 2 to show some detail of the thin layer structure.
An integrated circuit package, preferably formed of plastic
material such as molding compound surrounding silicon 10 on a
flexible substrate 11, comprises a package surface 11a where a
plurality of terminal pads 13 are located. These terminal pads 13
are preferably made of the package metallization such as copper or
gold flash over copper.
[0028] Package 10 and 11 is mounted to a substrate or board 14,
integral with interconnections and a plurality of terminal pads 15,
yet spaced apart by a gap 16. Substrate 14 preferably comprises a
printed circuit board made of FR-4 or a glass-epoxy laminate;
contact pads 15 are preferably composed of solder-wettable copper.
Package 10 and 11 is attached by reflowable bump interconnections
17 which extend across the gap and connect the terminal pads 13 on
the package to the terminal pads 15 on the substrate both
electrically and mechanically. Preferably, tin or a tin alloy (such
as tin/indium, tin/bismuth, tin/lead) of a desirable melting
temperature is chosen for bumps 17 to accomplish the reflow at a
practical temperature. Bumps 17 are often referred to as "solder"
bumps. For silicon packages, the protective "soldermask" 19 in
FIGS. 1 and 2 can be made of a variety of insulating materials
including polymers such as polyimide.
[0029] In known technology, the gap 16 is often filled with a
polymeric encapsulant that extends over the printed circuit board
about the perimeter of the package. The main purpose of
encapsulant, commonly referred to as the "underfill" material, is a
reduction of mechanical stress in the assembly; another purpose is
the protection of the active chip surface. The thermomechanical
stress originates from the difference of the coefficient of thermal
expansion between silicon and the board material in the process of
board assembly (solder bump reflow) and temperature cycle testing
(usually from -40 to +125.degree. C.).
[0030] Silicon, the preferred semiconductor material of chip 10,
has a CTE between 2 and 3 ppm/.degree. C., typical substrates 14
however a CTE between about 15 and 22 ppm/.degree. C.; CTEs of the
metals in the assembly vary from 4.3 to 17.0. The materials are
mechanically coupled intimately, even rigidly, to each other in the
assembly of a ball-grid array package. For the standard assembly
process flow, the temperature reaches the maximum of 220.degree. C.
because of an overshoot over the melting temperature of 183.degree.
C. of the eutectic tin-lead alloy (63 weight % tin). After the
solder has molten and is beginning to cool, the stress is zero and
stays zero to the eutectic temperature of 183.degree. C. With
continued cooling of the assembly, though, stress starts appearing
and increases rapidly. When ambient temperature is reached, the
stress levels reach levels so high that damage by nascent cracking
has often been inflicted to the structurally weakest parts of the
assembly, especially the solder joints, the chip multilevel
dielectric films, or the protective soldermask 19 in FIGS. 1 and 2.
The package 10 and 11 in FIGS. 1 and 2 is now arranged on substrate
14 such that each of the substrate terminal pads 15 registers with
a package terminal pad 13, with the solder bumps therebetween. By
way of example, the gap 16 between active surface 11 of the chip
and the substrate is preferably between 300 and 700 .mu.m.
[0031] Computer stress modeling can be applied according to
Darveaux's fatigue model to solder bump interconnections as shown
in FIGS. 1 and 2 (see R. Darveaux, K. Banerji, A. Mawer, and G.
Dody, "Reliability of plastic ball grid array assembly", Ball Grid
Array Technology, J. Lau Editor, McGraw-Hill, Inc. New York, 1995;
R. Darveaux, "Effect of simulation methodology on solder joint
crack growth correlation", Proc. IEEE, 50th Elec. Comp. Tech.
Conf., pp.1048-1058, 2000). The computer results reveal that the
regions of highest stress in temperature cycling is the zone
designated 17a in FIG. 2. In a typical assembly design with a
solder joint width of 0.45 mm, the average plastic energy density
in zone 17a is about 115 kJ/m.sup.3, and the maximum energy density
is a high as 703 kJ/m.sup.3. These high values cause the damage to
initiate already at 588 cycles (between -40 and +125.degree. C.),
the rate of crack propagation per cycle to reach 0.159 .mu.m/cycle,
and thus the number of cycles to complete crack propagation to be
2836 cycles. The board level reliability is thus limited to 3424
cycles. The schematic FIG. 3 illustrates a complete crack 30
through the solder joint region of a package 31 assembled by bumps
32 to board 33.
[0032] The stress relief provided by the present invention focuses
exactly on the region 34 of highest stress. The cross section of
schematic FIG. 4 depicts an adherent layer 44 of polymer material
covering the surface 41a of the package 41 and surrounding bump 42
to form a solid meniscus 44a. The thickness 44a of the layer 44 is
between about one quarter and one half of the height 42b of bump
42.
[0033] In FIG. 4, the plastic package 41 may be made of any
polymeric material used in semiconductor encapsulation, including
molding compounds, thermoset or thermoplastic formulations, and
plastic films. The package 41 may belong to the ball grid array or
chip-scale families, or any package design using reflow
interconnectors 42 for the assembly to external parts.
[0034] The reflowable metal of bumps 42 is selected from a group
consisting of tin, indium, tin alloys including tin/indium,
tin/silver, tin/bismuth, and tin/lead, conductive adhesives, and
z-axis conductive materials. The bumps 42 have a diameter from
about 50 to 700 .mu.m, a center-to-center spacing between about 100
and 1300 .mu.m, and approximately uniform height.
[0035] The polymer for the adherent layer 42 includes
non-electrically conductive adhesives, epoxies filled or unfilled
with inorganic particulate fillers including boron nitride or
aluminum nitride, bisphenol A with an anhydride cross-linking
agent, having a viscosity of <8000 cps and an elasticity modulus
between about 1 and 5 GPa. Suitable adhesive polymer precursors are
commercially available, for instance, from the company Loctite,
Rocky Hill, Conn. 06067, USA, under the trade name Hysol.RTM. QMI
536HT; Hysol.RTM. FP4450HA; or Product 3563.
[0036] By way of example, the assembly design having a solder joint
width of 0.45 mm, discussed earlier for Darveaux's fatigue model,
shows significant improvements after implementing the adhesive
polymer layer. For the zone 17b of highest stress (see FIG. 4), the
computer results indicate now an average plastic energy density of
only about 97 kJ/m.sup.3, and a maximum plastic energy density of
only about 513 kJ/m.sup.3. These lower values postpone the
initiation of a nascent crack in temperature cycling (between -40
to +125.degree. C.) to 768 cycles. The rate of crack propagation
per cycle is now 0.134 .mu.m/cycle, for 4285 cycles to complete the
crack propagation (the crack length is also extended to 0.573 mm
due to the wider bump diameter at the location of highest stress).
The board level reliability is thus extended to 5053 cycles, an
almost 50% improvement compared to the board level reliability
before the application of the polymer layer.
[0037] As illustrated in FIG. 5, it is an important aspect of the
present invention that a stress-reducing polymer layer similar to
layer 44 depicted in FIG. 4 can be used for reliability
improvements of bumps attached to polymeric substrates such as
assembly boards. These substrates 53 have a plurality of metallic
terminals 51 exposed on a substrate surface 53a. A metallic bump 52
is then attached to each of these terminals 51, wherein these bumps
are made of reflowable metal and have approximately uniform height.
An adherent layer 54 of polymer material covers the substrate
surface 53a and surrounds each of the bumps 52 to form a solid
meniscus 54a. This layer has a thickness 54b between about one
quarter and one half of the bump height 52a.
[0038] The substrates or assembly boards are selected from a group
consisting of organic materials including FR-4, FR-5, and BT resin,
with or without strengthening or thermally modulating fibers or
fillers, including a grid of glass fibers.
[0039] The method for completing a plastic package for
semiconductor devices by fabricating polymer-embedded solder bumps
progresses in the steps illustrated in FIGS. 6 to 10. The process
flow is as follows:
[0040] FIG. 6:
[0041] Step 1: Providing a plastic package 60 having a plurality of
metallic terminals 61 exposed on the package surface 62; the
terminals are spaced apart by some distance 63.
[0042] Step 2: Attaching a metallic bump to each of the terminals;
the bumps are made of reflowable metal and have approximately
uniform mass and height 65.
[0043] Step 3: Reflowing the bumps, while maintaining approximate
uniformity of predetermined height 65.
[0044] FIG. 7:
[0045] Step 4: Applying a water-soluble polymer 71 to coat the top
surface of the bumps 64.
[0046] Step 5: Positioning the package 60 in the vacuum chamber of
a plasma apparatus so that the surface 62 faces the plasma
source.
[0047] Step 6: initiating a plasma and controlling the ion mean
free path so that the ions 72 reach the surface 62 with
predetermined energy.
[0048] Step 7: Exposing the surface 62 to the plasma 72 for a
length of time sufficient to
[0049] roughen the polymer surface 62;
[0050] clean the polymer surface 62 from organic contamination;
and
[0051] improve the surface affinity to adhesion.
[0052] Step 8: Removing the package 60 from the vacuum chamber.
[0053] FIG. 8: and FIG. 9:
[0054] Step 9: Distributing an adherent polymeric precursor 81
between (91) and around the bumps 64, to form a meniscus 92 on each
of the bumps 64 and to fill the space 63 between the bumps 64 by a
layer 93 having a thickness 93a between one quarter and one half of
the height 65 of the bumps 64.
[0055] FIG. 9:
[0056] Step 10: Supplying additional thermal energy for curing the
polymeric precursor, whereby the layer 93 and said meniscus 92
solidify.
[0057] Step 11: Cooling the package to ambient temperature.
[0058] FIG. 10:
[0059] Step 12: Polishing off excessive polymer on top of solder
balls 64.
[0060] Step 13: Washing the assembled package, generally designated
100, in DI water to remove the water-soluble polymeric bump
coating, completing the plastic package.
[0061] While this invention has been described in reference to
illustrative embodiments, this description is not intended to be
construed in a limiting sense. Various modifications and
combinations of the illustrative embodiments, as well as other
embodiments of the invention, will be apparent to persons skilled
in the art upon reference to the description. It is therefore
intended that the appended claims encompass any such modifications
or embodiments.
* * * * *