U.S. patent number RE40,751 [Application Number 11/073,392] was granted by the patent office on 2009-06-16 for polymerization catalyst systems comprising substituted hafnocenes.
This patent grant is currently assigned to Univation Technologies, LLC. Invention is credited to Moses O. Jejelowo, Sun-Chueh Kao.
United States Patent |
RE40,751 |
Jejelowo , et al. |
June 16, 2009 |
Polymerization catalyst systems comprising substituted
hafnocenes
Abstract
The present invention relates to a process for the
polymerization of monomers utilizing a bulky ligand hafnium
transition metal metallocene-type catalyst compound, to the
catalyst compound itself and to the catalyst compound in
combination with an activator. The hafnocene comprises at least one
cyclopentadienyl ligand including at least one linear or isoalkyl
substituent of at least 3 carbon atoms.
Inventors: |
Jejelowo; Moses O. (Webster,
NY), Kao; Sun-Chueh (Pearland, TX) |
Assignee: |
Univation Technologies, LLC
(Houston, TX)
|
Family
ID: |
25532662 |
Appl.
No.: |
11/073,392 |
Filed: |
March 4, 2005 |
Related U.S. Patent Documents
|
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
Issue Date |
|
Reissue of: |
08986696 |
Dec 8, 1997 |
06242545 |
Jun 5, 2001 |
|
|
Current U.S.
Class: |
526/160; 502/117;
502/152; 526/127; 526/129; 526/134; 526/943 |
Current CPC
Class: |
C08F
10/00 (20130101); C08F 210/14 (20130101); C08F
210/16 (20130101); C08J 5/18 (20130101); C08F
10/00 (20130101); C08F 4/65925 (20130101); C08F
10/00 (20130101); C08F 4/65927 (20130101); C08F
210/14 (20130101); C08F 4/65922 (20130101); C08F
4/65904 (20130101); C08F 4/65912 (20130101); C08F
4/65916 (20130101); C08F 2410/01 (20130101); C08J
2323/08 (20130101); C08F 210/16 (20130101); C08F
210/08 (20130101); C08F 2500/12 (20130101); C08F
2500/08 (20130101); C08F 2500/26 (20130101); C08F
2500/03 (20130101); C08F 210/16 (20130101); C08F
210/14 (20130101); C08F 2500/12 (20130101); C08F
2500/18 (20130101); C08F 2500/26 (20130101); C08F
210/16 (20130101); C08F 210/14 (20130101); C08F
2500/12 (20130101); C08F 2500/18 (20130101); C08F
210/16 (20130101); C08F 210/08 (20130101); C08F
2500/12 (20130101); C08F 2500/08 (20130101); C08F
210/16 (20130101); C08F 210/08 (20130101); C08F
2500/12 (20130101); C08F 2500/08 (20130101); C08F
2500/26 (20130101); C08F 210/16 (20130101); C08F
210/14 (20130101); C08F 2500/12 (20130101); C08F
2500/18 (20130101); C08F 2500/03 (20130101); C08F
2500/26 (20130101); C08F 210/16 (20130101); C08F
210/14 (20130101); C08F 2500/08 (20130101); C08F
2500/12 (20130101); C08F 2500/03 (20130101); C08F
2500/18 (20130101); C08F 2500/20 (20130101); C08F
2500/26 (20130101); C08F 210/16 (20130101); C08F
210/08 (20130101); C08F 2500/08 (20130101); C08F
2500/12 (20130101); C08F 2500/03 (20130101); C08F
2500/18 (20130101); C08F 2500/26 (20130101); C08F
2500/20 (20130101); Y10S 526/943 (20130101); Y10S
526/901 (20130101) |
Current International
Class: |
C08F
4/64 (20060101); C08F 2/14 (20060101); C08F
2/34 (20060101); C08F 4/6592 (20060101) |
Field of
Search: |
;562/160,127,129,134,943
;502/117,152 |
References Cited
[Referenced By]
U.S. Patent Documents
Foreign Patent Documents
|
|
|
|
|
|
|
0481480 |
|
Apr 1992 |
|
EP |
|
481 480 |
|
Apr 1992 |
|
EP |
|
0495099 |
|
Jul 1992 |
|
EP |
|
0 495 099 |
|
Jul 1992 |
|
EP |
|
0596553 |
|
May 1994 |
|
EP |
|
0612768 |
|
Aug 1994 |
|
EP |
|
612768 |
|
Aug 1994 |
|
EP |
|
612768 |
|
Aug 1994 |
|
EP |
|
0 284 707 |
|
Aug 1995 |
|
EP |
|
0284707 |
|
Aug 1995 |
|
EP |
|
0 316 155 |
|
Feb 1996 |
|
EP |
|
0773239 |
|
May 1997 |
|
EP |
|
0781789 |
|
Jul 1997 |
|
EP |
|
0773239 |
|
Dec 2001 |
|
EP |
|
07-252267 |
|
Oct 1995 |
|
JP |
|
07-330820 |
|
Dec 1995 |
|
JP |
|
WO 94/03509 |
|
Feb 1994 |
|
WO |
|
WO 95/11263 |
|
Apr 1995 |
|
WO |
|
WO 98/02470 |
|
Jan 1998 |
|
WO |
|
Other References
Hawley's Condensed Chemical Dictionary, 13.sup.th Edition, John
Wiley & Sons, p. 34, 1997. cited by examiner .
Tian et al., Macromol. Rapid Commun. 15 (1994) pp. 923-928. cited
by examiner .
Journal of Molecular Catalysis A:Chemical 200 (2003) (323-332), N.
I. Makela-Vaame, et al. cited by other .
Kirstin Heiland, Walter Kaminsky, Comparison on zirconocene and
hafnocene catalysts for the polymerization of ethylene and
1-butene, Makromol. Chem. 193, 601-610 (1992). cited by other .
Jun Tian, Baotong Huang, Ethylene polymerization with catalyst
systems based on metallocenes with varying steric hindrance and
methylaluminoxane, Macromol Rapid Commun. 15, 923-928 (1994). cited
by other.
|
Primary Examiner: Rabago; Roberto
Claims
We claim:
1. A .Iadd.gas-phase .Iaddend.process for polymerizing
olefin(s).Iadd., .Iaddend.excluding cyclic olefin(s).Iadd.,
.Iaddend.in the presence of a catalyst system comprising a hafnium
metallocene catalyst compound .[.having at least one
cyclopentadienyl or cyclopentadienyl derived ligand substituted
with at least one linear or iso alkyl group having from 3 to 10
carbon atoms, and an activator.]. .Iadd.represented by the formula:
(C.sub.5H.sub.5-d-fR''.sub.d).sub.eR'''.sub.fHfQ.sub.4-e wherein
(C.sub.5H.sub.5-d-fR''.sub.d) is a substituted cyclopentadienyl
ligand bonded to Hf, wherein at least one
(C.sub.5H.sub.5-d-fR''.sub.d) is substituted with at least one R'',
wherein said R'' is selected from one or more of n-propyl, or
n-pentyl, each additional R'', which can be the same or different
is hydrogen or a substituted or unsubstituted hydrocarbyl having
from 1 to 30 carbon atoms or combinations thereof or two or more
carbon atoms are joined together to form a part of a substituted or
unsubstituted ring or ring system having 4 to 30 carbon atoms, R'''
is one or more or a combination of the group consisting of carbon,
germanium, silicon, phosphorous and nitrogen atoms containing
radical bridging two (C.sub.5H.sub.5-d-fR''.sub.d) rings, or
bridging one (C.sub.5H.sub.5-d-fR''.sub.d) ring to Hf; each Q which
can be the same or different is selected from the group consisting
of a hydride, substituted and unsubstituted hydrocarbyl having from
1 to 30 carbon atoms, halogen, alkoxides, aryloxides, amides,
phosphides and combination thereof; two Q's together form an
alkylidene ligand or cyclometallated hydrocarbyl ligand or other
divalent anionic chelating ligand; d is 1, 2, 3, or 4, f is 0 or 1,
and e is 1, 2 or 3, said catalyst system further comprising an
activator and a support, wherein the activator and the hafnium
metallocene catalyst compound are premixed in a solvent, and then
combined with the support and then dried, to produce a free-flowing
powder, and wherein the catalyst has a catalyst productivity of
greater than 1000(g polymer)/(g catalyst*h*150 psi) at 85.degree.
C.Iaddend..
2. The process in accordance with claim 1 .[.where the linear or
iso alkyl group has 3 to 5 carbon atoms.]. .Iadd.wherein said
hafnium metallocene catalyst compound is one of: bis (n-propyl
cyclopentadienyl) hafnium dichloride, dimethyl, or dihydride; bis
(n-pentyl cyclopentadienyl) hafnium dichloride, or dimethyl;
(n-propyl cyclopentadienyl)(n-butyl cyclopentadienyl) hafnium
dimethyl or dichloride; bis (2-n-propyl indenyl) hafnium dichloride
or dimethyl; bis (1,2-n-propyl, methyl cyclopentadienyl) hafnium
dichloride or dimethyl; (n-propyl cyclopentadienyl) (1,3-n-propyl,
n-butyl cyclopentadienyl) hafnium dimethyl or
dichloride.Iaddend..
.[.3. The process in accordance with claim 1 wherein the ligand is
one or more cyclopentadienyl ligands, wherein one of the
cyclopentadienyl ligands is substituted with at least one linear or
iso alkyl having 3 or 4 carbon atoms..].
.[.4. The process in accordance with claim 1 wherein the ligands
are two cyclopentadienyl rings each substituted with at least one
linear or iso alkyl group having 3 to 10 carbon atoms..].
.[.5. The process in accordance with claim 2 wherein the linear or
iso alkyl group is selected from one or more of the group
consisting of n-propyl, isopropyl, n-butyl, isobutyl and
n-pentyl..].
6. The process in accordance with claim 1 wherein the olefin(s) are
alpha-olefins having from 2 to 12 carbon atoms.
7. The process in accordance with claim 1 wherein the olefin(s) are
ethylene in combination with one or more other alpha-olefin(s)
having from 3 to 10 carbon atoms.
.[.8. The process in accordance with claim 1 wherein the process is
a gas phase process..].
.[.9. The process in accordance with claim 1 wherein the catalyst
system further comprises a support..].
10. The process in accordance with claim 1 wherein the hafnium
metallocene catalyst compound is bis(n-propyl-cyclopentadienyl)
hafnium dichloride.
11. A continuous gas phase process for polymerizing
olefin(s).Iadd., .Iaddend.excluding cyclic olefin(s).Iadd.,
.Iaddend.in a fluidized bed gas phase reactor in the presence of a
catalyst system to produce a polymer product, the catalyst system
comprising an activator and a hafnium metallocene catalyst compound
.[.having at least one cyclopentadienyl or cyclopentadienyl derived
ligand substituted with at least one linear or iso alkyl group
having from 3 to 10 carbon atoms,.]. .Iadd.represented by the
formula: (C.sub.5H.sub.5-d-fR''.sub.d).sub.eR'''.sub.fHfQ.sub.4-e
wherein (C.sub.5H.sub.5-d-fR''.sub.d) is a substituted
cyclopentadienyl ligand bonded to Hf, wherein at least one
(C.sub.5H.sub.5-d-fR''.sub.d) is substituted with at least one R'',
wherein said R'' is selected from one or more of n-propyl, or
n-pentyl, each additional R'', which can be the same or different
is hydrogen or a substituted or unsubstituted hydrocarbyl having
from 1 to 30 carbon atoms or combinations thereof or two or more
carbon atoms are joined together to form a part of a substituted or
unsubstituted ring or ring system having 4 to 30 carbon atoms, R'''
is one or more or a combination of the group consisting of carbon,
germanium, silicon, phosphorous and nitrogen atoms containing
radical bridging two (C.sub.5H.sub.5-d-fR''.sub.d) rings, or
bridging one (C.sub.5H.sub.5-d-fR''.sub.d) ring to Hf; each Q which
can be the same or different is selected from the group consisting
of a hydride, substituted and unsubstituted hydrocarbyl having from
1 to 30 carbon atoms, halogen, alkoxides, aryloxides, amides,
phosphides and combination thereof; two Q's together form an
alkylidene ligand or cyclometallated hydrocarbyl ligand or other
divalent anionic chelating ligand; d is 1, 2, 3, or 4, f is 0 or 1,
and e is 1, 2 or 3, said catalyst system further comprising a
support, wherein the activator and the hafnium metallocene catalyst
compound are premixed in a solvent, and then combined with the
support and then dried, to produce a free-flowing powder, and
wherein the catalyst has a catalyst productivity of greater than
1000(g polymer)/(g catalyst*h*150 psi) at 85.degree. C.,
.Iaddend.and the polymer product comprising less than 2 ppm
hafnium.
12. The process of claim 11 wherein the polymer product comprises
less than 1 ppm hafnium.
13. The process in accordance with claim 11 wherein .[.the catalyst
system is supported.]. .Iadd.said hafnium metallocene catalyst
compound is one of: bis (n-propyl cyclopentadienyl) hafnium
dichloride, dimethyl, or dihydride; bis (n-pentyl cyclopentadienyl)
hafnium dichloride, or dimethyl; (n-propyl
cyclopentadienyl)(n-butyl cyclopentadienyl) hafnium dimethyl or
dichloride; bis (2-n-propyl indenyl) hafnium dichloride or
dimethyl; bis (1,2-n-propyl, methyl cyclopentadienyl) hafnium
dichloride or dimethyl; (n-propyl cyclopentadienyl) (1,3-n-propyl,
n-butyl cyclopentadienyl) hafnium dimethyl or
dichloride.Iaddend..
14. The process in accordance with claim 11 wherein the polymer
product has a density greater than 0.915 g/cc.
15. The process in accordance with claim 11 wherein the olefin(s)
are ethylene and at least one alpha-olefin(s) having 3 to 8 carbon
atoms.
16. The process in accordance in accordance with claim 11 wherein
the catalyst system is represented by the formula:
(C.sub.5H.sub.5-d-fR''.sub.d).sub.eR'''.sub.fHfQ.sub.g-e wherein
(C.sub.5H.sub.5-d-fR''.sub.d) is an unsubstituted or substituted
cyclopentadienyl ligand bonded to Hf, wherein at least one
(C.sub.5H.sub.5-d-fR''.sub.d) is substituted with at least one R''
which is an alkyl group selected from the group consisting of
n-propyl, isopropyl, isobutyl and n-pentyl, each additional R'',
which can be the same or different, is hydrogen or a substituted or
unsubstituted hydrocarbyl having from 1 to 30 carbon atoms or
combinations thereof.Iadd., .Iaddend.or two or more carbon atoms
are joined together to form a part of a substituted or
unsubstituted ring or ring system having 4 to 30 carbon atoms, R'''
is one or more or a combination of the group consisting of carbon,
germanium, silicon, phosphorous and nitrogen atoms containing
radical bridging two (C.sub.5H.sub.5-d-fR''.sub.d) rings, or
bridging one (C.sub.5H.sub.5-d-fR''.sub.d) ring to Hf; each Q which
can be the same or different is selected from the group consisting
of a hydride, substituted and unsubstituted hydrocarbyl having from
1 to 30 carbon atoms, halogen, alkoxides, aryloxides, amides,
phosphides and combination thereof; two Q's together form an
alkylidene ligand or cyclometallated hydrocarbyl ligand or other
divalent anionic chelating ligand; where g is an integer
corresponding to the formal oxidation state of Hf, d is 0, 1, 2, 3,
4, or 5, f is 0 or 1 and e is 1, 2, or 3, .[.and.]. the polymer
product has a melt index less than 0.1 dg/min without the addition
of hydrogen to the process .Iadd.and wherein the hafnium
metallocene catalyst compound is bis(n-propyl-cyclopentadienyl)
hafnium dichloride and said activator is alumoxane.Iaddend..
17. A continuous slurry phase process for polymerizing
olefin(s).Iadd., .Iaddend.excluding cyclic olefin(s).Iadd.,
.Iaddend.in the presence of a catalyst system to produce a polymer
product in a liquid polymerization medium, the catalyst system
comprising an activator.Iadd., a support .Iaddend.and a hafnium
metallocene catalyst compound .[.having at least one
cyclopentadienyl or cyclopentadienyl derived ligand substituted
with at least one linear or iso alkyl group having from 3 to 10
carbon atoms.]. .Iadd.represented by the formula:
(C.sub.5H.sub.5-d-fR''.sub.d).sub.eR'''.sub.fHfQ.sub.4-e wherein
(C.sub.5H.sub.5-d-fR''.sub.d) is a substituted cyclopentadienyl
ligand bonded to Hf, wherein at least one
(C.sub.5H.sub.5-d-fR''.sub.d) is substituted with at least one R'',
wherein said R'' is selected from one or more of n-propyl, or
n-pentyl, each additional R'', which can be the same or different
is hydrogen or a substituted or unsubstituted hydrocarbyl having
from 1 to 30 carbon atoms or combinations thereof or two or more
carbon atoms are joined together to form a part of a substituted or
unsubstituted ring or ring system having 4 to 30 carbon atoms, R'''
is one or more or a combination of the group consisting of carbon,
germanium, silicon, phosphorous and nitrogen atoms containing
radical bridging two (C.sub.5H.sub.5-d-fR''.sub.d) rings, or
bridging one (C.sub.5H.sub.5-d-fR''.sub.d) ring to Hf; each Q which
can be the same or different is selected from the group consisting
of a hydride, substituted and unsubstituted hydrocarbyl having from
1 to 30 carbon atoms, halogen, alkoxides, aryloxides, amides,
phosphides and combination thereof; two Q's together form an
alkylidene ligand or cyclometallated hydrocarbyl ligand or other
divalent anionic chelating ligand; d is 1, 2, 3, or 4, f is 0 or 1,
and e is 1, 2 or 3, wherein the activator and the hafnium
metallocene catalyst compound are premixed in a solvent, and then
combined with the support and then dried, to produce a free-flowing
powder, and wherein the catalyst has a catalyst productivity of
greater than 1000(g polymer)/(g catalyst*h*150 psi) at 85.degree.
C..Iaddend., and the polymer product comprising less than 2 ppm
hafnium.
18. The process in accordance with claim 17 wherein the polymer
product comprises less than 1 ppm hafnium .Iadd.and wherein said
hafnium metallocene catalyst compound is one of: bis (n-propyl
cyclopentadienyl) hafnium dichloride, dimethyl, or dihydride; bis
(n-pentyl cyclopentadienyl) hafnium dichloride, or dimethyl;
(n-propyl cyclopentadienyl)(n-butyl cyclopentadienyl) hafnium
dimethyl or dichloride; bis (2-n-propyl indenyl) hafnium dichloride
or dimethyl; bis (1,2-n-propyl, methyl cyclopentadienyl) hafnium
dichloride or dimethyl; (n-propyl cyclopentadienyl) (1,3-n-propyl,
n-butyl cyclopentadienyl) hafnium dimethyl or
dichloride.Iaddend..
19. The process in accordance with claim .[.17.]. .Iadd.18
.Iaddend.wherein the density is greater than 0.900 g/cc.
20. The process in accordance with claim .[.17.]. .Iadd.19
.Iaddend.wherein the olefins are ethylene and at least one
alpha-olefin(s) having 3 to 8 carbon atoms.
21. The process in accordance with claim 17 wherein the .[.catalyst
system is represented by the formula:
(C.sub.5H.sub.5-d-fR''.sub.d).sub.eR'''.sub.fHfQ.sub.g-e wherein
(C.sub.5H.sub.5-d-fR''.sub.d) is an unsubstituted or substituted
cyclopentadienyl ligand bonded to Hf, wherein at least one
(C.sub.5H.sub.5-d-fR''.sub.d) is substituted with at least one R''
which is a linear or iso alkyl group having from 3 to 10 carbon
atoms, each additional R'', which can be the same or different is
hydrogen or a substituted or unsubstituted hydrocarbyl having from
1 to 30 carbon atoms or combinations thereof or two or more carbon
atoms are joined together to form a part of a substituted or
unsubstituted ring or ring system having 4 to 30 carbon atoms, R'''
is one or more or a combination of the group consisting of carbon,
germanium, silicon, phosphorous and nitrogen atoms containing
radical bridging two (C.sub.5H.sub.5-d-fR''.sub.d) rings, or
bridging one (C.sub.5H.sub.5-d-fR''.sub.d) ring to Hf; each Q which
can be the same or different is selected from the group consisting
of hydride, substituted and unsubstituted hydrocarbyl having from 1
to 30 carbon atoms, halogen, alkoxides, aryloxides, amides,
phosphides and combinations thereof; two Q's together form an
alkylidene ligand or a cyclometallated hydrocarbyl ligand or other
divalent anionic chelating ligand; where g is an integer
corresponding to the formal oxidation state of Hf, d is 0, 1, 2, 3,
4 or 5, f is 0 or 1 and e is 1, 2 or 3, and the.]. polymer product
has a melt index less than 0.1 dg/min (ASTM D-1238-F or ASTM
D-1238-E) without the addition of hydrogen to the process.Iadd.,
wherein the hafnium metallocene catalyst compound is
bis(n-propyl-cyclopentadienyl) hafnium dichloride and wherein said
activator is alumoxane.Iaddend..
.[.22. The process in accordance with claim 3 wherein the linear or
iso alkyl group has 3 carbon atoms..].
23. A .Iadd.continuous .Iaddend.process for polymerizing
olefin(s).Iadd., .Iaddend.excluding cyclic olefin(s).Iadd.,
.Iaddend.in the presence of a catalyst system comprising a hafnium
transition metal .[.metalloccne.]. .Iadd.metallocene
.Iaddend.catalyst .[.having at least one cyclopentadienyl ring
substituted with at least one alkyl group selected from group
consisting of n-propyl, isopropyl, isobutyl and n-pentyl, and an
activator.]. .Iadd.represented by the formula:
(C.sub.5H.sub.5-d-fR''.sub.d).sub.eR'''.sub.fHfQ.sub.g-e wherein
(C.sub.5H.sub.5-d-fR''.sub.d) is a substituted cyclopentadienyl
ligand bonded to Hf, wherein at least one
(C.sub.5H.sub.5-d-fR''.sub.d) is substituted with at least one R'',
wherein said R'' is selected from one or more of n-propyl, or
n-pentyl, each additional R'', which can be the same or different
is hydrogen or a substituted or unsubstituted hydrocarbyl having
from 1 to 30 carbon atoms or combinations thereof or two or more
carbon atoms are joined together to form a part of a substituted or
unsubstituted ring or ring system having 4 to 30 carbon atoms, R'''
is one or more or a combination of the group consisting of carbon,
germanium, silicon, phosphorous and nitrogen atoms containing
radical bridging two (C.sub.5H.sub.5-d-fR''.sub.d) rings, or
bridging one (C.sub.5H.sub.5-d-fR''.sub.d) ring to Hf; each Q which
can be the same or different is selected from the group consisting
of a hydride, substituted and unsubstituted hydrocarbyl having from
1 to 30 carbon atoms, halogen, alkoxides, aryloxides, amides,
phosphides and combination thereof; two Q's together form an
alkylidene ligand or cyclometallated hydrocarbyl ligand or other
divalent anionic chelating ligand; d is 1, 2, 3, or 4, f is 0 or 1,
and e is 1, 2 or 3, a support and an activator, wherein the
activator and the hafnium metallocene catalyst compound are
premixed in a solvent, and then combined with the support and then
dried, to produce a free-flowing powder, and wherein the catalyst
has a catalyst productivity of greater than 1000(g polymer)/(g
catalyst*h*150 psi) at 85.degree. C.Iaddend..
24. A continuous gas phase process for polymerizing olefins.Iadd.,
.Iaddend.excluding cyclic olefin.Iadd., .Iaddend.in a fluidized bed
gas phase reactor in the presence of a catalyst system to produce a
polymer product, the catalyst system comprising an activator.Iadd.,
a support .Iaddend.and a .[.bulky ligand.]. hafnium transition
metal metallocene catalyst represented by the formula:
(C.sub.5H.sub.5-d-fR''.sub.d).sub.eR'''.sub.fHfQ.sub.g-e wherein
(C.sub.5H.sub.5-d-fR''.sub.d) is an unsubstituted or substituted
cyclopentadienyl ligand bonded to Hf, wherein at least one
(C.sub.5H.sub.5-d-fR''.sub.d) is substituted with at least one R''
which is an alkyl group selected from the group consisting of
n-propyl, .[.isopropyl, isobutyl.]. and n-pentyl, each additional
R'', which can be the same or different, is hydrogen or a
substituted or unsubstituted hydrocarbyl having from 1 to 30 carbon
atoms or combinations thereof.Iadd., .Iaddend.or two or more carbon
atoms are joined together to form a part of a substituted or
unsubstituted ring or ring system having 4 to 30 carbon atoms, R'''
is one or more or a combination of the group consisting of carbon,
germanium, silicon, phosphorous and nitrogen atoms containing
radical bridging two (C.sub.5H.sub.5-d-fR''.sub.d) rings, or
bridging one (C.sub.5H.sub.5-d-fR''.sub.d) ring to Hf; each Q which
can be the same or different is selected from the group consisting
of hydride, substituted and unsubstituted hydrocarbyl having from 1
to 30 carbon atoms, halogen, alkoxides, aryloxides, amides,
phosphides and combinations thereof; two Q's together form an
alkylidene ligand or cyclometallated hydrocarbyl ligand or other
divalent anionic chelating ligand; where g is an integer
corresponding to the formal oxidation state of Hf, d is 0, 1, 2, 3,
4 or 5, f is 0 or 1 and e is 1, 2 or 3, .Iadd.wherein the activator
and the hafnium metallocene catalyst compound are premixed in a
solvent, and then combined with the support and then dried, to
produce a free-flowing powder, and wherein the catalyst has a
catalyst productivity of greater than 1000(g polymer)/(g
catalyst*h*150 psi) at 85.degree. C., .Iaddend.and the polymer
product has a melt index less than 10 dg/min (ASTM D-1238-F or ASTM
D-1238-E) without the addition of hydrogen to the process.
.[.25. The process in accordance with claim 1 wherein the hafnium
metallocene catalyst compound is a bis-cyclopentadienyl hafnium
metallocene compound..].
26. The process in accordance with claim 1 wherein the activator is
alumoxane.
27. The process in accordance with claim .[.4 where in the linear
or iso alkyl group has from 3 to 5 carbon atoms.]. .Iadd.24,
wherein the hafnium metallocene catalyst compound is
bis(n-propyl-cyclopentadienyl) hafnium dichloride and said
activator is alumoxane.Iaddend..
.[.28. The process in accordance with claim 1 wherein the linear or
iso alkyl group has 3 carbon atoms..].
.Iadd.29. A continuous gas-phase process for polymerizing olefins,
excluding cyclic olefin(s), comprising: combining a) one or more of
ethylene, propylene, butene-1, pentene-1, 4-methyl-1-pentene,
hexene-1 and octene-1 b) a catalyst comprising a bis n-propyl
cyclopentadienyl hafnium dichloride, an activator selected from the
group consisting of alumoxane, methyl alumoxane, modified
alumoxane, and ionizing activators, and a support, wherein the
activator and the catalyst are premixed in a solvent, and then
combined with the support and then dried, to produce a free-flowing
powder, and wherein the catalyst has a catalyst productivity of
greater than 1000(g polymer)/(g catalyst*h*150 psi) at 85.degree.
C..Iaddend.
.Iadd.30. A continuous gas-phase process for polymerizing olefins,
excluding cyclic olefin(s), comprising: combining a) one or more of
ethylene, propylene, butene-1, pentene-1, 4-methyl-1-pentene,
hexene-1 and octene-1 b) a catalyst consisting essentially of a bis
n-propyl cyclopentadienyl hafnium dichloride, an activator selected
from the group consisting of alumoxane, methyl alumoxane, modified
alumoxane, and ionizing activators, and a support, wherein the
activator and catalyst are premixed in a solvent, and then combined
with the support and then dried, to produce a free-flowing powder,
and wherein the catalyst has a catalyst productivity of greater
than 1000(g polymer)/(g catalyst*h*150 psi) at 85.degree.
C..Iaddend.
.Iadd.31. A continuous gas-phase process for polymerizing olefins,
excluding cyclic olefin(s), comprising: combining a) one or more of
ethylene, propylene, butene-1, pentene-1, 4-methyl-1-pentene,
hexene-1 and octene-1 b) a catalyst consisting of a bis n-propyl
cyclopentadienyl hafnium dichloride, an activator selected from the
group consisting of alumoxane, methyl alumoxane, modified
alumoxane, and ionizing activators, and a support, wherein the
activator and the catalyst are premixed in a solvent, and then
combined with the support and then dried, to produce a free-flowing
powder, and wherein the catalyst has a catalyst productivity of
greater than 1000(g polymer)/(g catalyst*h*150 psi) at 85.degree.
C..Iaddend.
Description
FIELD OF THE INVENTION
This invention relates to catalysts, catalyst systems and their use
in olefin polymerization. The invention more particularly relates
to substituted hafnium metallocene-type catalyst compounds,
catalyst systems thereof and their use in a polymerizing
process.
BACKGROUND OF THE INVENTION
The use of bulky ligand transition metal catalyst compounds in
polymerization processes to produce a diverse array of new polymers
for use in a wide variety of applications and products is well
known in the art. Typical bulky ligand transition metal compounds,
known as metallocene-type compounds, are generally described as
containing one or more ligands capable of .eta.-5 bonding to the
transition metal atom, usually, cyclopentadienyl derived ligands or
moieties, in combination with a transition metal selected from
Group 4, 5 or 6 or from the lanthanide and actinide series of the
Periodic Table of Elements. Predomiantly in the literature the
transition metal is from Group 4, particularly either titanium,
zirconium or hafnium, and the cyclopentadienyl derived ligand or
moiety is substituted with various radicals, typically alkyl
radicals, or two or more cyclopentadienyl ligands are joined by a
structural bridge, usually an organic or inorganic group,
typically, a carbon or silicon atom containing group.
Other forms of these metallocene-type catalyst compounds contain a
cyclopentadienyl derived ligand or moiety and a heteroatom
containing group bonded to a transition metal, typically titanium,
where the cyclopentadienyl ligand or moiety and the heteroatom
containing group are joined by a structural bridge, usually a
silicon atom containing group. These and other metallocene-type
catalyst compounds in combination with an activator form
metallocene-type catalyst systems capable of polymeriig various
olefin(s), alone or in combination with other olefin(s). Exemplary
of the development of these and other metallocene-type catalyst
compounds and catalyst systems are described in U.S. Pat. Nos.
5,017,714, 5,055,438, 5,096,867, 5,198,401, 5,229,478, 5,264,405,
5,278,119, 5,324,800, 5,384,299, 5,408,017, 5,491,207 and 5,621,126
all of which are herein fully incorporated by reference.
It is well known in the art, although not fully understood, that
where the transition metal of these metallocene-type catalyst
compounds is hafnium, often referred to as a "hafnocene", hafnocene
catalyst systems generally, among other characteristics, perform
relatively poorly in comparison to their titanium, especially their
zirconium equivalents, often referred to as "zirconocenes".
Although hafnocenes will typically polymerize polymers having
higher molecular weights than their zirconocene equivalents under
similar polymerization conditions, their overall poor activity make
them inferior polymerization catalysts. For example, European
patent EP 0 284 707 B1 granted Aug. 30, 1995, which is fully
incorporated herein by reference, describes a process for
polymerizing olefins using a catalyst system, in liquid form
containing a chiral, sterorigid bridged hafnium metallocene
catalyst compound and an aluminum compound.
Thus, it would be highly advantageous to have a hafnium
metallocene-type catalyst system capable of polymerizing olefin(s)
with improved catalyst performance.
SUMMARY OF THE INVENTION
This invention relates to a substituted bulky ligand hafnium
transition metal metallocene-type catalyst compound and a catalyst
system thereof. The invention also relates to a polymerization
process for polymerizing one or more olefin(s) utilizing the
substituted bulky ligand hafnium transition metal metallocene-type
catalyst compound.
In one embodiment, the invention provides for a catalyst system of
a bulky ligand hafnium metallocene-type compound where at least one
bulky ligand is substituted with a substituent having at least 3 or
more non-hydrogen atoms, and an activator. Preferably, the bulky
ligand is substituted with a substituent having at least 3 or more
carbon atoms or silicon atoms or combinations thereof. In a
preferred embodiment, the invention provides for an activated
catalyst system of a bully ligand hafnium metallocenetype catalyst
complex where the bulky ligand is capable of .eta.-5 bonding to the
hafnium transition metal and is substituted with an alkyl
substituent having 3 or more carbon atoms, preferably where the
alkyl substituent has 3 to 5 carbon atoms, more preferably the
alkyl substituent is a linear alky. In one preferred embodiment,
the alkyl substituent is at least one n-butyl group, most
preferably at least one n-propyl group, substituted to at least one
of the bulky ligands.
In yet another embodiment, the invention is directed to a process
for polymerizing, preferably in a continuous process, one or more
monomer(s) in the presence of the catalyst system or activated
catalyst complex described above.
In one preferred embodiment, the above process of the invention is
a continuous slurry or gas phase polymerization process.
In another embodiment, the invention is directed to a polymer
product produced using the hafnocene catalyst systems or complexes
described above, wherein the polymer product contains less than 2
ppm hafnium, preferably less than 1 ppm hafnium.
DETAILED DESCRIPTION OF THE INVENTION
Introduction
The invention is directed toward a hafnium transition metal
metallocene-type catalyst system for polymerizing one or more
olefin(s). It has been surprisingly discovered that by properly
substituting the cyclopentadienyl derived ligand or moiety of a
hafiocene results in an improved catalyst system. Unexpectedly
where the substituent on the bulky ligand or moiety is a
substituent having 3 or more non-hydrogen atoms, preferably 3 or
more carbon atoms, preferably an alkyl substituent, for example
n-propyl or n-butyl, the catalyst activity of the hafnocene
metallocene-type catalyst system is substantially improved. Along
with a sufficiently commercially acceptable activity, the hafnocene
catalyst systems of the invention produces polymers having higher
molecular weights in comparison to its zirconocene equivalents at
the same or similar polymerization conditions. It was surprising
that the substituted hafnocene of the invention will tend to
produce lower density polymer products than its zirconocene
equivalent at substantially the same molecular weight.
Catalyst Components and Catalyst Systems
Preferred metallocene catalysts of the invention, for example, are
typically those bulky ligand transition metal complexes described
by formula (I):
{[(L.sup.p).sub.mM(A.sup.q).sub.n].sup.+k}.sub.h[B'.sup.-j].sub.i
where L is a substituted bulky ligand bonded to M, p is the anionic
charge of L and m is the number of L ligands and m is 1, 2 or 3; at
least one L is substituted with at least one substituent having 3
or more non-hydrogen atoms, preferably having 3 or more carbon
atoms or silicon atoms or combination thereof; A is a ligand bonded
to M and capable of inserting an olefin between the M--A bond, q is
the anionic charge of A and n is the number of A ligands and n is
1, 2, 3 or 4, M is the transition metal hafnium (Hf), and
(p.times.m)+(q.times.n)+k corresponds to the formal oxidation state
of the metal center, where k is the charge on the cation and k is
1, 2, 3 or 4, and B' is a chemically stable, non-nucleophillic
anionic complex, preferably having a molecular diameter of 4 .ANG.
or greater and j is the anionic charge on B', h is the number of
cations of charge k, and i the number of anions of charge j such
that h.times.k=j.times.i.
Any two L and/or A ligands may be bridged to each other and/or
unbridged. The catalyst compound may be fit-sandwich compounds
having two or more ligands L, which include cyclopentadienyl
derived ligands or substituted cyclopentadienyl derived ligands, or
half-sandwich compounds having one ligand L, which is a
cyclopentadienyl derived ligand or heteroatom substituted
cyclopentadienyl derived ligand or hydrocarbyl substituted
cyclopentadienyl derived ligand or moiety such as an indenyl
ligand, a benzindenyl ligand or a fluorenyl ligand and the like
including hydrogenated versions thereof or any other ligand capable
of .eta.-5 bonding to the transition metal atom. One or more of
these bulky ligands is .pi.-bonded to the transition metal atom. At
least one L is substituted with at least one substituent having 3
or more non-hydrogen atoms, preferably having 3 or more carbon
atoms or 3 or more non-hydrogen atoms of which at least one is a
silicon atom, in addition, L can be substituted with a combination
of additional substituents, which can be the same or different.
Non-limiting examples of non-hydrogen atoms include silicon,
germanium, tin, oxygen, nitrogen or carbon and combinations
thereof. Non-limiting examples of additional substituents include
hydrogen or a linear, branched or cyclic alkyl, alkenyl or aryl
radical or combination thereof having from 1 to 30 carbon atoms.
The at least one substituent or the additional substituents can
also be substituted with hydrogen or a linear, branched or cyclic
alkyl, alkenyl or aryl radical having from 1 to 30 carbon atoms or
non-hydrogen atoms. L may also be other types of bulky ligands
including but not limited to bulky amides, phosphides, alkoxides,
aryloxides, imides, carbolides, borollides, porphyrins,
phthalocyanines, corrins and other polyazomacrocycles. Other
ligands may be bonded to the hafnium transition metal, such as a
leaving group, such as but not limited to weak bases such amines,
phosphines, ether and the like. In addition to the transition
metal, these ligands may be optionally bonded to A or L.
Non-limiting examples of catalyst components and catalyst systems
are discussed in for example, U.S. Pat. Nos. 4,530,914, 4,871,705,
4,937,299, 5,124,418, 5,017,714, 5,120,867, 5,210,352, 5,278,264,
5,278,119, 5,304,614, 5,324,800, 5,347,025, 5,350,723, 5,391,790,
5,391,789, 5,399,636, 5,539,124, 5,455,366, 5,534,473, 5,684,098
and 5,693,730 all of which are herein fully incorporated by
reference. Also, the disclosures of European publications EP-A-0
591 756, EP-A-0 520 732, EP-A-0 420 436, EP-B1 0 485 822, EP-B1 0
485 823 and EP-A2-0 743 324 and PCT publications WO 91/04257, WO
92/00333, WO 93/08221, WO 93/08199, WO 94/01471, WO 96/20233, WO
97/15582 and WO 97/19959 are all herein fully incorporated by
reference.
In one embodiment, the activated catalyst of the invention is
formed from a hafnocene catalyst compound represented by the
general formula (II):
(L.sup.p).sub.mM(A.sup.q).sub.n(E.sup.r).sub.o where L is a bulky
ligand substituted with at least one substituent having 3 or more
non-hydrogen atoms, preferably 3 or more carbon atoms, preferably
an alkyl substituent having 3 or more carbon atoms, even more
preferably a linear allyl substituent having 3 or more carbon
atoms, M is Hf, A, and p, m, q and n are as defined above and E is
an anionic leaving group such as but not limited to hydrocarbyl,
hydride, halide or combination thereof or any other anionic
ligands; r is the anionic charge of E and o is the number of E
ligands and o is 1, 2, 3 or 4 such that
(p.times.m)+(q.times.n)+(r.times.o) is equal to the formal
oxidation state of the metal center; and an alnum alkyl, alumoxane,
modified alumoxane or any other oxy-containing organometallic
compound or non-coordinating ionic activators, or a combination
thereof.
In one embodiment of the invention the substituted hafnocene
catalyst compound of the invention includes monocyclopentadienyl
heteroatom containing hafnium transition metal metallocene-type
compounds. This metallocene-type compound is activated by either an
alumoxane, modified alumoxane, a non-coordinating ionic activator,
a Lewis acid or a combination thereof to form an active
polymerization catalyst system. These types of catalyst systems are
described in, for example, PCT publication WO 92/00333, WO
94/07928, WO 91/04257, WO 94/03506, WO 96/00244 and WO 97/15602 and
U.S. Pat. Nos. 5,057,475, 5,096,867, 5,055,438, 5,198,401,
5,227,440 and 5,264,405 and European publication EP-A-0 420 436,
all of which are herein fully incorporated by reference.
Additionally it is within the scope of this invention that the
metallocene catalysts and catalyst systems may be those described
in U.S. Pat. Nos. 5,064,802, 5,145,819, 5,149,819, 5,243,001,
5,239,022, 5,276,208, 5,296,434, 5,321,106, 5,329,031, 5,304,614
and 5,677,401, and PCT publications WO 93/08221, WO 93/08199 and WO
95/07140 and European publications EP-A-0 578 838 and EP-A-0 638
595 all of which are herein fully incorporated by reference.
In another embodiment, the catalyst component is represented by the
formula (III):
(C.sub.5H.sub.5-d-fR''.sub.d).sub.eR'''.sub.fMQ.sub.g-e wherein M
is a Hf transition metal, (C.sub.5H.sub.5-d-fR''.sub.d) is an
unsubstituted or substituted cyclopentadienyl ligand bonded to M,
wherein at least one (C.sub.5H.sub.5-d-fR''.sub.d) has at least one
R'' that is an alkyl substituent having 3 or more carbon atoms,
each additional R'', which can be the same or different is hydrogen
or a substituted or unsubstituted hydrocarbyl having from 1 to 30
carbon atoms or combinations thereof or two or more carbon atoms
are joined together to form a part of a substituted or
unsubstituted ring or ring system having 4 to 30 carbon atoms, R'''
is one or more or a combination of carbon, germanium, silicon,
phosphorous or nitrogen atoms containing radical bridging two
(C.sub.5H.sub.5-d-fR''.sub.d) rings, or bridging one
(C.sub.5H.sub.5-d-fR''.sub.d) ring to M; each Q which can be the
same or different is a hydride, substituted or unsubstituted
hydrocarbyl having from 1 to 30 carbon atoms, halogen, alkoxides,
aryloxides, amides, phosphides or any other univalent anionic
ligand or combination thereof, also, two Q's together form an
allylidene ligand or cyclometallated hydrocarbyl ligand or other
divalent anionic chelating ligand, where g is an integer
corresponding to the formal oxidation state of M, d is 0, 1, 2, 3,
4 or 5, f is 0or 1 and e is 1,2 or 3.
In another preferred embodiment of this invention the catalyst
component is represented by the formula (IV): ##STR00001## wherein
M is Hf; (C.sub.5H.sub.5-y-xR.sub.x) is a cyclopentadienyl ring
which is substituted with from at least one to 5 substituent groups
R, "x" is 1, 2, 3, 4 or 5 denoting the degree of substitution, and
at least one R is a non-hydrogen atom, preferably R is at least 3
carbon atoms or silicon atoms or a combination thereof more
preferably R is an alkyl having 3 or more carbon atoms, for example
n-propyl or n-butyl, and each additional substituent group R is,
independently, a radical selected from a group consisting of
C.sub.1-C.sub.20 hydrocarbyl radicals, substituted C.sub.1-C.sub.20
hydrocarbyl radicals wherein one or more hydrogen atoms is replaced
by a halogen atom, C.sub.1-C.sub.20 hydrocarbyl-substituted
metalloid radicals wherein the metalloid is selected from the Group
14 of the Periodic Table of Elements, and halogen radicals or
(C.sub.5H.sub.5-y-xR.sub.x) is a cyclopentadienyl ring in which two
adjacent R-groups are joined forming C.sub.4-C.sub.20 ring to give
a saturated or unsaturated polycyclic cyclopentadienyl ligand such
as indenyl, tetrahydroindenyl, fluorenyl or octahydrofluorenyl;
(JR'.sub.z-1-y) is a heteroatom ligand in which J is an element
with a coordination number of three from Group 15 or an element
with a coordination number of two from Group 16 of the Periodic
Table of Elements, preferably nitrogen, phosphorus, oxygen or
sulfur with nitrogen being preferred, and each R' is, independently
a radical selected from a group consisting of C.sub.1-C.sub.20
hydrocarbyl radicals wherein one or more hydrogen atoms is replaced
by a halogen atom, y is 0 or 1, and "z" is the coordination number
of the element J; each Q is, independently any univalent anionic
ligand such as halogen, hydride, or substituted or unsubstituted
C.sub.1-C.sub.30 hydrocarbyl, alkoxide, aryloxide, amide or
phosphide, provided that two Q may be an alkylidene, a
cyclometallated hydrocarbyl or any other divalent anionic chelating
ligand; A is a covalent bridging groups containing a Group 15 or 14
element such as, but not limited to, a dialkyl, alkylaryl or diaryl
silicon or germanium radical, alkyl or aryl phosphine or amine
radical, or a hydrocarbyl radical such as methylene, ethylene and
the like; L' is a Lewis base such as diethylether,
tetraethylammonium chloride, tetrahydrofran, dimethylaniline,
aniline, trimethylphosphine, n-butylamine, and the like; and w is a
number from 0 to 3. Additionally, L' may be bonded to any of R, R'
or Q.
In one embodiment of the bulky ligand hafnium transition metal
metallocene-type catalyst compounds described above, at least one
bulky ligand is substituted with a substituent having 3 or more
carbon atoms, preferably 3 to 20 carbon atoms, more preferably 3 to
10 and most preferably 3 to 5 carbon atoms. In another preferred
embodiment, the hafnium transition metal metallocene-type catalyst
system has two bulky ligands that are each substituted with a
linear or branched, preferably linear, alkyl having 3 or more
carbon atoms, preferably 3 to 10 carbon atoms, most preferably 3 to
5 carbon atoms, where at least one bulky ligand is a
cyclopentadienyl derived ligand, preferably a cyclopentadienyl
ring. In a preferred embodiment the bulky ligands of the hafnium
transition metal metallocene are both cyclopentadienyl rings at
least one of which is substituted with one or more branched or
linear alkyls having 3 or more carbon atoms, preferably both
cyclopentadienyl rings are substituted with at least one n-propyl,
isopropyl, n-butyl, isobutyl, n-pentyl, or combination thereof In a
more preferred embodiment the hafnium transition metal
metallocene-type catalyst compound has two bulky ligands that are
each substituted with n-propyl, n-butyl or n-pentyl or combination
thereof in the same or different positions, preferably in the same
position on the bulky ligands.
In another preferred embodiment, the hafnium transition metal
metallocene-type catalyst system has two bulky ligands that are
each substituted with a linear or branched, preferably linear,
silyl having 3 or more non-hydrogen atoms, preferably 3 to 10
non-hydrogen atoms, most preferably 3 to 5 non-hydrogen atoms,
where at least one bulky ligand is a cyclopentadienyl derived
ligand, preferably a cyclopentadienyl ring. In a preferred
embodiment the bulky ligands of the hafnium transition metal
metallocene are both cyclopentadienyl rings at least one of which
is substituted with one or more branched or linear silylalkyls
having 3 or more non-hydrogen atoms. In one embodiment, the
substituent has at least 3 or more non-hydrogen atoms of which at
least one is a silicon atom, for example trimethyl silyl alkyl,
tributyl silyl alkyl or tripropyl silyl alkyl or even cyclopropyl
silyl. Other non-hydrogen substituent atoms include oxygen and/or
nitrogen.
It is contemplated that the substituted bulky ligands of the
hafnium transition metal metallocene-type catalyst compound of the
invention are asymmetrically substituted in terms of additional
substituents or types of substituents, and/or unbalanced in terms
of the number of additional substituents on the bulky ligands.
Non-limiting examples of hafnocenes of the invention include
bis(n-propyl cyclopentadienyl) hafnium dichloride, dimethyl or
dihydride, bis(n-butyl cyclopentadienyl) hafnium dichloride or
dimethyl, bis(n-pentyl cyclopentadienyl) hafnium dichloride or
dimethyl, (n-propyl cyclopentadienyl)(n-butyl cyclopentadienyl)
hafnium dichloride or dimethyl, bis[(2-trimethylsilyl-ethyl)
cyclopentadienyl] hafnium dichloride or dimethyl,
bis(trimethylsilyl cyclopentadienyl) hafnium dichloride or dimethyl
or dihydride, bis(2-n-propyl indenyl) hafnium dichloride or
dimethyl, bis(2-n-butyl indenyl) hafnium dichloride or dimethyl,
dimethylsilyl bis(n-propyl cyclopentadienyl) hafnium dichloride or
dimethyl, dimethylsilyl bis(n-butyl cyclopentadienyl) hafnium
dichloride or dimethyl, bis(9-n-propyl fluorenyl) hafnium
dichloride or dimethyl bis(9-n-butyl fluorenyl) hafnium dichloride
or dimethyl, (9-n propyl fluorenyl)(2-n-propyl indenyl) hafnium
dichloride or dimethyl, bis(1,2-n-propyl, methyl cyclopentadienyl)
hafnium dichloride or dimethyl (n-propyl cyclopentadienyl)
(1,3-n-propyl, n-butyl cyclopentadienyl) hafnium dichloride or
dimethyl and the like.
In one preferred embodiment the hafnocenes of the invention are
unbridged mono- and bis- hafnocenes where a structural bridge is
not required for stereorigidity. It is also contemplated that in
one embodiment, the hafnocenes of the invention include their
structural or optical isomers and mixtures thereof.
For the purposes of this patent specification and appended claims,
the term "activator" is defined to be any compound or component
which can activate a bulky ligand transition metal metallocenetype
catalyst compound as described above, for example, a Lewis acid or
a non-coordinating ionic activator or ionizing activator or any
other compound that can convert a neutral metallocene catalyst
component to a metallocene cation. It is within the scope of this
invention to use alumoxane or modified alumoxane as an activator,
and/or to also use ionizing activators, neutral or ionic, such as
tri (n-butyl) ammonium tetrakis(pentafluorophenyl) boron or a
trisperfluorophenyl boron metalloid precursor which ionizes the
neutral metallocene compound.
There are a variety of methods for preparing alumoxane and modified
alumoxanes, non-limiting examples of which are described in U.S.
Pat. Nos. 4,665,208, 4,952,540, 5,091,352, 5,206,199, 5,204,419,
4,874,734, 4,924,018, 4,908,463, 4,968,827, 5,308,815, 5,329,032,
5,248,801, 5,235,081, 5,157,137, 5,103,031, 5,391,793, 5,391,529,
5,693,838 and European publications EP-A-0 561 476, EP-B1-0 279 586
and EP-A-0 594-218, and PCT publication WO 94/10180, all of which
are herein fully incorporated by reference.
Ionizing compounds may contain an active proton, or some other
cation associated with but not coordinated or only loosely
coordinated to the remaining ion of the ionizing compound. Such
compounds and the like are described in European publications
EP-A-0 570 982, EP-A-0 520 732, EP-A-0 495 375, EP-A-0 426 637,
EP-A-500 944, EP-A-0 277 003 and EP-A-0 277 004, and U.S. Pat. Nos.
5,153,157, 5,198,401, 5,066,741, 5,206,197, 5,241,025, 5,387,568,
5,384,299 and 5,502,124 and U.S. patent application Ser. No.
08/285,380, filed Aug. 3, 1994, now abandoned all, of which are
herein fully incorporated by reference. Combinations of activators
are also contemplated by the invention, for example, alumoxanes and
ionizing activators in combinations, see for example, PCT
publications WO 94/07928 and WO 95/14044 and U.S. Pat. Nos.
5,153,157 and 5,453,410 all of which are herein fully incorporated
by reference.
In an embodiment of the invention two or more bulky ligand hafnium
transition metal metallocene-type catalyst compounds as described
above can be combined to form a catalyst system useful in the
invention. For example, those mixed catalysts described in U.S.
Pat. Nos. 5,281,679, 5,359,015 and 5,470,811, all of which are
herein fully incorporated herein reference. In another embodiment
of the catalyst system of the invention combinations of one or more
of catalyst components of the formulas (III) and/or (IV) are
contemplated.
In one embodiment, metallocene catalyst components can be combined
to form the blend compositions as described in PCT publication WO
90/03414 published Apr. 5, 1990, herein fully incorporated by
reference. In yet another embodiment of the invention mixed
metallocenes as described in U.S. Pat. Nos. 4,937,299 and
4,935,474, both are herein fully incorporated herein by reference,
can be used to produce polymers having a broad molecular weight
distribution and/or a multimodal molecular weight distribution.
In another embodiment of the invention at least one metallocene
catalyst of the invention can be combined with a non-metallocene or
traditional Ziegler-Natta catalyst or catalyst system, or chromium
based catalysts or catalyst systems, non-limiting examples are
described in U.S. Pat. Nos. 4,159,965, 4,325,837, 4,701,432,
5,124,418, 5,077,255, 5,183,867, 5,391,660, 5,395,810 and
5,691,264, all of which are herein fully incorporated by
reference.
It is within the scope of this invention that Ni.sup.2+ and
Pd.sup.2+ complexes described in the articles Johnson, et al., "New
Pd(II)- and Ni(II)- Based Catalysts for Polymerization of Ethylene
and a-Olefins", J. Am. Chem. Soc. 1995, 117, 6414-6415 and Johnson,
et al., "Copolymerization of Ethylene and Propylene with
Functionalaled Vinyl Monomers by Palladium(II) Catalysts", J. Am.
Chem. Soc., 1996, 118, 267-268, and WO 96/23010 published Aug. 1,
1996 which are all herein fully incorporated by reference, can be
used as catalysts in combination with the hafnocenes of the
invention. These complexes can be either dialkyl ether adducts, or
alkylated reaction products of the described dihalide complexes
that can be activated to a cationic state by the activators of this
invention. It is also within the scope of the process of this
invention that the above described complexes can be combined with
one or more of the catalyst compounds represented by formula (III)
and (IV), with one or more activators, and with one or more of the
support materials using one of the support methods that are
described below.
For purposes of this patent specification the terms "carrier" or
"support" are interchangeable and can be any support material,
preferably a porous support material, for example, talc, inorganic
oxides, inorganic chlorides, and magnesium chloride, and resinous
support materials such as polystyrene or polystyrene divinyl
benzene polyolefins or polymeric compounds or any other organic or
inorganic support material and the like, or mixtures thereof.
The preferred support materials are inorganic oxide materials,
which include those of Groups 2, 3, 4, 5, 13 or 14 metal oxides. In
a preferred embodiment, the catalyst support materials include
silica, alumina, silica-alumina, and mixtures thereof. Other
inorganic oxides that may be employed either alone or in
combination with the silica, alumina or silica-alumina and
magnesia, titania, zirconia, and the like.
It is preferred that the carrier of the catalyst of this invention
has a surface area in the range of from about 10 to about 700
m.sup.2/g, pore volume in the range of from about 0.1 to about 4.0
cc/g and average particle size in the range of from about 10 to
about 500 .mu.m. More preferably, the surface area is in the range
of from about 50 to about 500 m.sup.2/g, pore volume of from about
0.5 to about 3.5 cc/g and average particle size of from about 20 to
about 200 .mu.m. Most preferably the surface area range is from
about 100 to about 400 m.sup.2/g, pore volume from about 0.8 to
about 3.0 cc/g and average particle size is from about 20 to about
100 .mu.m. The average pore size of the carrier of the invention
typically has pore size in the range of from 10 to 1000 .ANG.,
preferably 50 to about 500 .ANG., and most preferably 75 to about
350 .ANG..
The catalyst system of the invention can be made and used in a
variety of different ways as described below. In one embodiment the
catalyst is unsupported, preferably in liquid form such as
described in U.S. Pat. Nos. 5,317,036 and 5,693,727 and European
publication EP-A-0 593 083, all of which are herein incorporated by
reference. In the preferred embodiment, the catalyst system of the
invention is supported. Examples of supporting the catalyst system
used in the invention are described in U.S. Pat. Nos. 4,701,432,
4,808,561, 4,912,075, 4,925,821, 4,937,217, 5,008,228, 5,238,892,
5,240,894, 5,332,706, 5,346,925, 5,422,325, 5,466,649, 5,466,766,
5,468,702, 5,529,965, 5,554,704, 5,629,253, 5,639,835, 5,625,015,
5,643,847 and 5,665,665 and U.S. application Ser. Nos. 271,598
filed Jul. 7, 1994, now U.S. Pat. No. 5,468,702, and 788,736 filed
Jan. 23, 1997, now U.S. Pat. No. 6,090,740, and PCT publications WO
95/32995, WO 95/14044, WO 96/06187 and WO 97/02297 all of which are
herein fully incorporated by reference.
In another embodiment, the catalyst system of the invention
contains a polymer bound ligand as described in U.S. Pat. No.
5,473,202 which is herein fully incorporated by reference. In one
embodiment the catalyst system of the invention is spray dried as
described in U.S. Pat. No. 5,648,310 which is fully incorporated
herein by reference. In an embodiment the support of the invention
is functionalized as described in European publication EP-A-0 802
203 or at least one substituent or leaving group is selected as
described in U.S. Pat. No. 5,688,880, both of which are herein
fully incorporated by reference.
In one embodiment of the process of the invention, olefin(s),
preferably C.sub.2 to C.sub.20 olefin(s) or alpha-olefin(s),
preferably ethylene or propylene or combinations thereof are
prepolymerized in the presence of the catalyst or catalyst system
of the invention prior to the main polymerization. The
prepolymerization can be carried out batchwise or continuously in
gas, solution or slurry phase including at elevated pressures. The
prepolymerization can take place with any alpha-olefin monomer or
combination and/or in the presence of any molecular weight
controlling agent such as hydrogen. For details on
prepolymerization see U.S. Pat. Nos. 4,923,833, 4,921,825 and
5,283,278 and European publication EP-B-0279 863 all of which are
herein fully incorporated by reference.
In another embodiment of the invention, the supported catalyst
system of the invention includes an antistatic agent or surface
modifier, for example, those described in U.S. Pat. No. 5,283,278
and PCT publication WO 96/11960 which are herein fully incorporated
by reference. Non-limiting examples of antistatic agents and
surface modifiers include alcohol, thiol, silanol, diol, ester,
ketone, aldehyde, acid, amnine, and ether compounds. Tertiary
amines, ethoxylated amines, and polyether compounds are preferred.
The antistatic agent can be added at any stage in the formation of
the supported catalyst system of the invention, however, it is
preferred that it is added after the supported catalyst system of
the invention is formed, in either a slurry or dried state.
A preferred method for producing the catalyst of the invention is
described below and an be found in U.S. application Ser. Nos.
265,533, filed Jun. 24, 1994, now abandoned and 265,532, filed Jun.
24, 1994, now abandoned and PCT publications WO 96/00245 and WO
96/00243 both published Jan. 4, 1996, all of which are herein fully
incorporated by reference. In a preferred embodiment, the
metallocene-type catalyst component is slurried in a liquid to form
a metallocene solution and a separate solution is formed containing
an activator and a liquid. The liquid can be any compatible solvent
or other liquid capable of forming a solution or the like with at
least one metallocene catalyst component and/or at least one
activator. In the preferred embodiment the liquid is a cyclic
aliphatic or aromatic hydrocarbon, most preferably toluene. The
metallocene and activator solutions are mixed together and added to
a porous support or the porous support is added to the solutions
such that the total volume of the metallocene solution and the
activator solution or the metallocene and activator solution is
less than four times the pore volume of the porous support, more
preferably less than three times, even more preferably less than
two times; preferred ranges being from 1.1 times to 3.5 times range
and most preferably in the 1.2 to 3 times range.
Procedures for measuring the total pore volume of a porous support
are well known in the art. Details of one of these procedures is
discussed in Volume 1, Experimental Methods in Catalytic Research
(Academic Press, 1968) (specifically see pages 67-96). This
preferred procedure involves the use of a classical BET apparatus
for nitrogen absorption. Another method well know in the art is
described in Innes, Total Porosity and Particle Density of Fluid
Catalysts By Liquid Titration, Vol. 28, No. 3, Analytical Chemistry
332-334 (March, 1956).
The mole ratio of the metal of the activator component to the
transition metal of the metallocene component is in the range of
ratios between 0.3:1 to 1000:1, preferably 20:1 to 800:1, and most
preferably 50:1 to 500:1. Where the activator is an aluminum-free
ionizing activator such as those based on the anion
tetrakis(pentafluorophenyl)boron, the mole ratio of the metal of
the activator component to the transition metal component is
preferably in the range of ratios between 0.3:1 to 3:1.
In another embodiment the catalyst loading in millimoles (mmoles)
of metallocene to weight of support catalyst in grams (g) is in the
range of from about 0.001 to about 2.0 mmoles of metallocene per g
of support material, preferably from about 0.005 to about 1.0, more
preferably from about 0.005 to 0.5 and most preferably from about
0.01 to 0.05.
In one embodiment, the catalyst of the invention has a catalyst
productivity of greater than 1000 grams of polymer per gram of the
metallocene catalyst, preferably greater than 1400 grams of polymer
per gram of metallocene catalyst, more preferably greater than 1800
grams of polymer per gram of metallocene catalyst, even more
preferably greater than 2000 grams of polymer per gram of
metallocene catalyst, and most preferably greater than 2500 grams
of polymer per gram of metallocene catalyst.
Polymerization Process of the Invention
The substituted bulky ligand hafnium transition metal
metallocene-type catalyst compounds and catalyst systems of this
invention are suited for the polymerization of monomers, and
optionally one or more comonomers, in any polymerization process,
solution phase, gas phase or slurry phase, most preferably a gas or
slurry phase process is used.
In an embodiment, this invention is directed toward the solution,
slurry or gas phase polymerization or copolymerization reactions
involving the polymerization of one or more of the monomers having
from 2 to 30 carbon atoms, preferably 2-12 carbon atoms, and more
preferably 2 to 8 carbon atoms. The invention is particularly well
suited to the copolymerization reactions involving the
polymerization of one or more of the monomers, for example
alpha-olefin monomers of ethylene, propylene, butene-1, pentene-1,
4-methyl-pentene-1, hexene-1, octene-1, decene-1, and cyclic
olefins such as cyclopentene, and styrene or a combination thereof.
Other monomers can include polar vinyl monomers, diolefins such as
dienes, polyenes, norbornene, norbarnadiene, acetylene and aldehyde
monomers. Preferably a copolymer of ethylene or propylene is
produced. Preferably the comonomer is an alpha-olefin having from 3
to 15 carbon atoms, preferably 4 to 12 carbon atoms and most
preferably 4 to 8 carbon atoms. In another embodiment ethylene or
propylene is polymerized with at least two different comonomers to
form a terpolymer and the like, the preferred comonomers are a
combination of alpha-olefin monomers having 3 to 10 carbon atoms,
more preferably 4 to 8 carbon atoms.
In another embodiment ethylene or propylene is polymerized with at
least two different comonomers to form a terpolymer and the like,
the preferred comonomers are a combination of alpha-olefin monomers
having 3 to 10 carbon atoms, more preferably 3 to 8 carbon atoms,
optionally with at least one diene monomer. The preferred
terpolymers include the combinations such as
ethylene/butene-1/hexene-1, ethylene/propylene/butene-1,
propylene/ethylene/butene-1, propylene/ethylene/hexene-1,
ethylene/propylene/norbornadiene and the like.
In the most preferred embodiment the process of the invention
relates to the polymerization of ethylene and at least one
comonomer having from 4 to 8 carbon atoms. Particularly, the
comonomers are butene-1, 4-methyl-pentene-1, hexene-1 and octene-1,
the most preferred being hexene-1.
Typically in a gas phase polymerization process a continuous cycle
is employed where in one part of the cycle of a reactor, a cycling
gas stream, otherwise known as a recycle stream or fluidizing
medium, is heated in the reactor by the heat of polymerization.
This heat is removed in another part of the cycle by a cooling
system external to the reactor. (See for example U.S. Pat. Nos.
4,543,399, 4,588,790, 5,028,670, 5,317,036, 5,352,749, 5,405,922,
5,436,304, 5,453,471, 5,462,999, 5,616,661 and 5,668,228 all of
which are fully incorporated herein by reference.)
Generally, in a gas fluidized bed process for producing polymers, a
gaseous stream containing one or more monomers is continuously
cycled through a fluidized bed in the presence of a catalyst under
reactive conditions. The gaseous stream is withdrawn from the
fluidized bed and recycled back into the reactor. Simultaneously,
polymer product is withdrawn from the reactor and fresh monomer is
added to replace the polymerized monomer. The reactor pressure may
vary from about 100 psig (680 kPag) to about 500 psig (3448 kPag),
preferably in the range of from about 200 psig (1379 kPag) to about
400 psig (2759 kPag), more preferably in the range of from about
250 psig (1724 kPag) to about 350 psig (2414 kPag). The reactor
temperature may vary between about 60.degree. C. and about
120.degree. C., preferably about 60.degree. C. to about 115.degree.
C., and more preferably in the range of from about 70.degree. C. to
110.degree. C., and most preferably in the range of from about
70.degree. C. to 95.degree. C. The settled bulk density for the
polymers produced by the process of invention are in the range of
from about 10 to 35 lb/ft.sup.3 (160 to 561 kg/m.sup.3), preferably
from about 12 to 35 lb/ft.sup.3 (193 to 561 kg/m.sup.3), more
preferably from about 14 to 32 lb/ft.sup.3 (224 to 513 kg/m.sup.3),
and most preferably from about 15 to 30 lb/ft.sup.3 (240 to 481
kg/m.sup.3).
Other gas phase processes contemplated by the process of the
invention include those described in U.S. Pat. Nos. 5,627,242,
5,665,818 and 5,677,375, and European publications EP-A-0 794 200,
EP-A-0 802 202 and EP-B-634 421 all of which are herein fully
incorporated by reference.
A preferred process of the invention is where the process,
preferably a slurry or gas phase process, most preferably a gas
phase process, is operated in the absence of or essentially free of
any scavengers, such as triethylaluminum, trimethylaluminun
trisobutylaluminum and tri-n-hexylaluminum and diethyl aluminum
chloride and the like. This preferred process is described in PCT
publication WO 96/08520, which is herein fully incorporated by
reference.
A slurry polymerization process generally uses pressures in the
range of about 1 to about 50 atmospheres and even greater and
temperatures in the range of 0.degree. C. to about 200.degree. C.
In a slimy polymerization, a suspension of solid, particulate
polymer is formed in a liquid polymerization medium to which
ethylene and comonomers and often hydrogen along with catalyst are
added. The liquid employed in the polymerization medium can be
alkane or cycloalkane, or an aromatic hydrocarbon such as toluene,
ethylbenzene or xylene. The medium employed should be liquid under
the conditions of polymerization and relatively inert. Preferably,
hexane or isobutane medium is employed.
In one embodiment a preferred polymerization technique of the
invention is referred to as a particle form, or slurry process
where the temperature is kept below the temperature at which the
polymer goes into solution. Such technique is well known in the
art, see for instance U.S. Pat. No. 3,248,179 which is fully
incorporated herein by reference. The preferred temperature in the
particle form process is within the range of about 185.degree. F.
(85.degree. C.)to about 230.degree. F. (110.degree. C.). Two
preferred polymerization methods for the slurry process are those
employing a loop reactor and those utilizing a plurality of stirred
reactors in series, parallel, or combinations thereof. Non-limiting
examples of slurry processes include continuous loop or stirred
tank processes. Also, other examples of slurry processes are
described in U.S. Pat. No. 4,613,484, which is herein fully
incorporated by reference.
It is also contemplated in an embodiment of the invention, that the
process is a multistage polymerization process where one reactor is
operating in slurry phase that feeds into a reactor operating in a
gas phase as described in U.S. Pat. No. 5,684,097, which is fuilly
incorporated herein by reference.
In one embodiment the reactor utilized in the present invention is
capable of producing greater than 500 lbs/hr (227 Kg/hr) to about
200,000 lbs/hr (90,900 Kg/hr)or higher of polymer, preferably
greater than 1000 lbs/hr (455 Kg/hr), more preferably greater than
10,000 lbs/hr (4540 Kg/hr), even more preferably greater than
25,000 lbs/hr (11,300 Kg/hr), still more preferably greater than
35,000 lbs/hr (15,900 Kg/hr), still even more preferably greater
than 50,000 lbs/hr (22,700 Kg/hr) and most preferably greater than
65,000 lbs/hr (29,000 Kg/hr) to greater than 100,000 lbs/hr (45,500
Kg/hr).
The productivity of the catalyst or catalyst system is influenced
by the main monomer partial pressure. The preferred mole percent of
the main monomer, ethylene or propylene, preferably ethylene is
from about 25 to 90 mole percent and the monomer partial pressure
is in the range of from about 75 psia (517 kPa) to about 300 psia
(2069 kPa), which are typical conditions in a gas phase
polymerization process.
In another embodiment of the invention where the hafnocene of the
invention is in particular an unbridged metallocene-type catalyst,
the process of the invention is capable of producing a polymer
product having a melt index of less than 0.1 dg/min without the
addition of hydrogen to the process.
Polymer Product of the Invention
The polymers produced by this invention can be used in a wide
variety of products and end-use applications. The polymers
typically have a density in the range of from 0.86g/cc to 0.97
g/cc, preferably in the range of from 0.88 g/cc to 0.965 g/cc, more
preferably in the range of from 0.900 g/cc to 0.96 g/cc, even more
preferably in the range of from 0.905 g/cc to 0.95 g/cc, yet even
more preferably in the range from 0.910 g/cc to 0.940 g/cc, and
most preferably greater than 0.910 g/cc, preferably greater than
0.915 g/cc. The polymers of the invention typically have a narrow
molecular weight distribution, a weight average molecular weight to
number average molecular weight (M.sub.w/M.sub.n) of greater than
1.5 to about 4, particularly greater than 2 to about 3, more
preferably greater than about 2.2 to less than 3. Also, the
polymers of the invention typically have a narrow composition
distribution. In another embodiment, the polymers produced by the
process of the invention, particularly in a slurry and gas phase
process, contain less than 2 ppm hafnium, preferably less than 1.5
ppm hafnium, more preferably less than 1 ppm hafnium. In an
embodiment, the polymer of the invention contains in the range of
from about 0.01 ppm to about 2 ppm hafnium, preferably in the range
of from about 0.01 ppm to about 1.5 ppm hafnium, more preferably in
the range of from about 0.01 ppm to 1 or less ppm hafnium.
Polymers produced by the process of the invention are usefuil in
such forming operations as film, sheet, and fiber extrusion and
co-extrusion as well as blow molding, injection molding and rotary
molding. Films include blown or cast films formed by coextrusion or
by lamination useful as shrink film, cling film, stretch film,
sealing films, oriented films, snack packaging, heavy duty bags,
grocery sacks, baked and frozen food packaging, medical packaging,
industrial liners, membranes, etc. in food-contact and non-food
contact applications. Fibers include melt spinning, solution
spinning and melt blown fiber operations for use in woven or
non-woven form to make filters, diaper fabrics, medical garments,
geotextiles, etc. Extruded articles include medical tubing, wire
and cable coatings, geomembranes, and pond liers. Molded articles
include single and multi-layered constructions in the form of
bottles, tanks, large hollow articles, rigid food containers and
toys, etc.
EXAMPLES
In order to provide a better understanding of the present invention
including representative advantages thereof, the following examples
are offered.
The properties of the polymer were determined by the following test
methods:
Density is measured in accordance with ASTM-D-1238.
MWD, or polydispersity, is a well-known characteristic of polymers.
MWD is generally descried as the ratio of the weight average
molecular weight (Mw) to the number average molecular weight (Mn).
The ratio of Mw/Mn can be measured by gel permeation chromatography
techniques, or indirectly, by measuring the ratio of I.sub.21 to
I.sub.2 (melt index) as described in ASTM D-1238-F and a ASTM
D-1238-E respectively.
In all the Examples below the methylalumoxane (MAO) is a 30 weight
percent MAO solution in toluene available from Albemarle
Corporation, Baton Rouge, La., the Davision 948 silica is available
from W. R. Grace, Davison Chemical Division, Baltimore, Md. and the
N,N-bis(2-hydroxylethyl) octadecylamine is available as Kemamine
AS-990 from ICI Specialties, Wilmington, Del. The metallocene
components of the examples were prepared in accordance with
procedures well known in the art.
Example 1
Preparation of Catalyst
A solution of methylalumoxane and metallocene was formed by adding
11 cm.sup.3 of 30 wt-% MAO solution in toluene onto 0.202 g of bis
(n-propylcyclopentadienyl) hafnium dichloride in a vial. 40
cm.sup.3 of fresh toluene was added, and the mixture stirred for 1
hour at 25.degree. C. This pre-mixed solution of the MAO and the
metallocene was then added onto 10 g of Davison 948 silica dried to
600.degree. C. The resulting slurry was stirred for 1.5 hours at
25.degree. C. The final catalyst was then dried to free-flowing
powder under vacuum at 65.degree. C.
Polymerization
A sample of the dry catalyst formed in the above Example 1 was then
used in a polymerization process of ethylenell-butene in a 2-liter
semi-batch gas-phase reactor at 85.degree. C. The pressure in the
reactor, about 155 psig (1069 kPag), was held constant by
continuously feeding 5 mol-% 1-butene in ethylene to compensate for
any pressure changes due to polymerization. After 1 h (hour), the
polymer formed was separated from the seed bed material and
analyzed for the molecular properties shown in Table 1 below as Run
1 and 2.
Example 2
Preparation of Catalyst
A solution of methylalumoxane and metallocene was formed by adding
66.5 cm.sup.3 of 30 wt-% MAO solution in toluene onto 1.21 g of bis
(n-propylcyclopentadienyl) hafnium dichloride in a vial. 50
cm.sup.3 of fresh toluene was added, and the mixture stirred for
1.5 hours at 25.degree. C. This pre-mixed solution of the MAO and
the metalocene was then added onto 60 g of Davison 948 silica dried
to 600.degree. C. The resulting slurry was stirred for 1.5 hours at
25.degree. C. Then a solution of 0.41 g of N,N-bis(2-hydroxylethyl)
octadecylamnine in 50 cm.sup.3 toluene was added, and stirring
continued for another 30 minutes. The final catalyst was then dried
to free-flowing powder under vacuum at 65.degree. C.
Polymerization
A sample of the dry catalyst formed in Example 2 was then used in a
polymerization process of ethylene/1-butene in a 2-liter semi-batch
gas-phase reactor at 85.degree. C. The pressure in the reactor,
about 158 psig (1089 kPag), was held constant by continuously
feeding 5 mol-% 1-butene in ethylene to compensate for any pressure
change due to polymerization. After 1 h, the polymer formed was
separated from the seed bed material and analyzed for the molecular
properties shown as Run 3 in Table 1 below.
Example 3
Preparation of Catalyst
a) Methylalumoxane (1155 cm.sup.3 of 30 wt-% solution in toluene)
was charged into a 2-gallon reaction vessel. 1970 cm.sup.3 of fresh
toluene was added. Then a solution of 20.2 g of
bis(n-propylcyclopentadienyl) hafnium dichloride in 355 cm.sup.3
toluene was added. The temperature was maintained at 27.degree. C.
and the mixture stirred for 1.5 hour. b) 1000 g of a Davison 948
silica dehydrated at 600.degree. C. was charged into a 2-gallon
reaction vessel at 27.degree. C. The solution of methylalumoxane
and metallocene from above was added onto the silica in two equal
portions. Then an additional 250 cm.sup.3 toluene was added to the
slurry. After 1 hour, a solution of 6.7 g of
N,N-bis(2-hydroxylethyl) octadecylamine in 70 cm.sup.3 toluene was
added and stirring continued for another 20 minutes. The final
catalyst was then dried to free-flowing powder at 68.degree. C.
under vacuum. Polymerization
Samples of the dry catalyst formed in Example 3 each were then used
in a polymerization process of ethylene/1-butene in a 2-liter
semi-batch gas-phase reactor at 85.degree. C. The pressure in the
reactor, about 158 psig (1089 kPag), was held constant by
continuously feeding 5 mol-% 1-butene in ethylene to compensate for
any pressure change due to polymerization. After 1 h, the polymer
formed was separated from the seed bed material and ayzed for the
molecular properties shown as Runs 4-6 in Table 1 below.
Example 4
Preparation of Catalyst
A solution of methylalumoxane and metallocene was formed by adding
27.8 cm.sup.3 of 30 wt-% MAO solution in toluene onto 0.536 g of
bis (n-butylcyclopentadienyl) hafnium dichloride in a vial. 60
cm.sup.3 of fresh toluene was added, and the mixture stirred for
1.5 hours at 25.degree. C. This pre-mixed solution of the MAO and
the metallocene was then added onto 25 g of Davison 948 silica
dried to 600.degree. C. The resulting slurry was stirred for 1.5
hours at 25.degree. C. Then a solution of 0.166 g of
N,N-bis(2-hydroxylethyl) octadecylamine in 40 cm.sup.3 toluene was
added, and stirring continued for another 30 minutes. The final
catalyst was then dried to free-flowing powder under vacuum at
65.degree. C.
Polymerization
Samples of the dry catalyst formed in Example 4 then were each used
in a polymerization process of ethylene/1-butene in a 2-liter
semi-batch gas-phase reactor at 85.degree. C. The pressure in the
reactor, about 155 psig (1069 kPag), was held constant by
continuously feeding 5 mol-% 1-butene in ethylene to compensate for
any pressure change due to polymerization. After 1 h, the polymer
formed was separated from the seed bed material and analyzed for
the molecular properties shown as Runs 7-9 in Table 1 below.
Comparative Example 5
Preparation of Catalyst
A solution of methylalumoxane and metallocene was formed by adding
27.7 cm.sup.3 of 30 wt-% MAO solution in toluene onto 0.413 g of
bis (cyclopentadienyl) hafnium dichloride in a vial. 50 cm.sup.3 of
fresh toluene was added, and the mixture stirred for 1.5 hours at
25.degree. C. This pre-mixed solution of the MAO and the metalocene
was then added onto 25 g of Davison 948 silica dried to 600.degree.
C. The resulting shiny was stirred for 1.5 hours at 25.degree. C.
Then a solution of 0.166 g of N,N-bis(2-hydroxylethyl)
octadecylamine in 40 cm.sup.3 toluene was added, and stirring
continued for another 30 minutes. The final catalyst was then dried
to free-flowing powder under vacuum at 65.degree. C.
Polymerization
Samples of the dry catalyst formed in Comparative Example 5 were
then each used in a polymerization process of ethylene/1-butene in
a 2-liter semi-batch gas-phase reactor at 85.degree. C. The
pressure in the reactor, about 158 psig (1089 kPag), was held
constant by continuously feeding 5 mol-% 1-butene in ethylene to
compensate for any pressure change due to polymerization. After 1
h, the polymer formed was separated from the seed bed material and
analyzed for the molecular properties shown as Runs C1 and C2 in
Table 1 below.
Comparative Example 6
Preparation of Catalyst
A solution of methylalumoxane and metallocene was formed by adding
27.8 cm.sup.3 of 30 wt-% MAO solution in toluene onto 0.444 g of
bis (methylcyclopentadienyl) hafnium dichloride in a vial. 60
cm.sup.3 of fresh toluene was added, and the mixture stirred for
1.5 hours at 25.degree. C. This pre-mixed solution of the MAO and
the metallocene was then added onto 25 g of Davison 948 silica
dried to 600.degree. C. The resulting slurry was stirred for 1.5
hours at 25.degree. C. Then a solution of 0.169 g of
N,N-bis(2-hydroxylethyl) octadecylamine in 50 cm.sup.3 toluene was
added, and stirring continued for another 30 minutes. The final
catalyst was then dried to freeflowing powder under vacuum at
65.degree. C.
Polymerization
A sample of the dry catalyst formed in Comparative Example 6 was
then used in a polymerization process of ethylene/1-butene in a
2-liter semi-batch gas-phase reactor at 85.degree. C. The pressure
in the reactor, about 154 psig (1062 kPag), was held constant by
continuously feeding 5 mol-% 1-butene in ethylene to compensate for
pressure changes due to polymerization. After 1 h, the polymer
formed was separated from the seed bed material and analyzed for
the molecular properties shown as Run C3 in Table 1 below.
Comparative Example 7
Preparation of Catalyst
A solution of methylalumoxane and metallocene was formed by adding
27.8 cm.sup.3 of 30 wt-% MAO solution in toluene onto 0.475 g of
bis (ethylcyclopentadienyl) hafnium dichloride in a vial. 60
cm.sup.3 of fresh toluene was added, and the mixture stirred for
1.5 hours at 25.degree. C. This pre-mixed solution of the MAO and
the metallocene was then added onto 25 g of Davison 948 silica
dried to 600.degree. C. The resulting slurry was stirred for 1.5
hours at 25.degree. C. Then a solution of 0.167 g of
N,N-bis(2-hydroxylethyl octadecylamine in 50 cm.sup.3 toluene was
added, and stirring continued for another 30 minutes. The final
catalyst was then dried to free-flowing powder under vacuum at
65.degree. C.
Polymerization
A sample of the dry catalyst formed above in Comparative Example 7
was then used in a polymerization process of ethylene/1-butene in a
2-liter semi-batch gas-phase reactor at 85.degree. C. The pressure
in the reactor, about 160 psig (1103 kPag), was held constant by
continuously feeding 5 mol-% 1-butene in ethylene to compensate for
any pressure change due to polymerization. After 1 h, the polymer
formed was separated from the seed bed material and analyzed for
the molecular properties shown as Run C4 in Table 1 below.
Comparative Example 8
Preparation of Catalyst
A solution of methylalumoxane and metallocene was formed by adding
28 cm.sup.3 of 30 wt-% MAO solution in toluene onto 0.585 g of
Me.sub.2Si (Indenyl).sub.2 hafnium dichloride in a vial. 60
cm.sup.3 of fresh toluene was added, and the mixture stirred for
1.5 hours at 25.degree. C. This pre-mixed solution of the MAO and
the metallocene was then added onto 25 g of Davison 948 silica
dried to 600.degree. C. The resulting slurry was stirred for 1.5
hours at 25.degree. C. Then a solution of 0.167 g of
N,N-bis(2-hydroxylethyl) octadecylamine in 40 cm.sup.3 toluene was
added, and stirring continued for another 30 nmnutes. The final
catalyst was then dried to free-flowing powder under vacuum at
65.degree. C.
Polymerization
Samples of the dry catalyst formed above in Comparative Example 8
were then each used in a polymerization process of
ethylene/1-butene in a 2-liter semibatch gas-phase reactor at
85.degree. C. The pressure in the reactor, about 158 psig (1089
kPag), was held constant by continuously feeding 5 mol-% 1-butene
in ethylene to compensate for any pressure change due to
polymerization. After 1 h, the polymer formed was separated from
the seedbed material and analyzed for the molecular properties
shown as Runs C5-C7 in Table 1 below.
While the present invention has been described and illustrated by
reference to particular embodiments, those of ordinary skill in the
art will appreciate that the invention lends itself to variations
not necessarily illustrated herein. It is contemplated that the
catalyst system of this invention can be used in combination with
other catalyst systems comprising more than one catalyst system of
the invention. For this reason, then, reference should be made
solely to the appended claims for purposes of determining the true
scope of the present invention.
TABLE-US-00001 TABLE 1 Run Catalyst Polymer Density I.sub.2
I.sub.21 # (mg) Yield (g) Activity.sup.1 (g/cc) (dg/min) (dg/min)
Mw MWD (nPrCp).sub.2HfCl.sub.2 1 100 211 2126 0.9061 0.096 2.26
278942 2.88 2 50 117 2363 0.9025 0.089 2.5 275100 2.61 3 50 136
2674 NM NM 1.83 NM NM 4 50 159 3159 0.9064 NM 1.76 283282 2.82 5 50
117 2325 0.9091 NM 1.77 272925 2.80 6 50 117 2356 0.9081 NM 2.0
316801 2.88 (nBuCp).sub.2HfCl.sub.2 7 150 271 1821 0.9057 NM 1.2
322890 2.46 8 150 225 1479 0.9056 NM 0.83 NM NM 9 100 195 1935
0.9070 NM 1.51 NM NM (Cp).sub.2HfCl.sub.2 C1 300 12 40 0.9310 NM
0.42 361692 3.98 C2 500 18 36 0.9273 NM 0.67 NM NM
(MeCp).sub.2HfCl.sub.2 C3 150 17 112 0.9234 NM 0.68 291412 3.24
(EtCp).sub.2HfCl.sub.2 C4 150 16 107 0.9275 NM 0.36 375772 3.20
Me.sub.2Si(Ind).sub.2HfCl.sub.2 C5 150 7 48 0.9365 NM 1.74 232475
3.44 C6 150 6 37 0.9265 NM 1.21 263758 4.16 C7 500 25 49 0.9239 NM
1.73 239161 3.40 Note .sup.1Catalyst activity expressed as
g.sub.PE/(gcAT h 150 psi) NM - - Not Measured; "Ind" is indenyl
* * * * *