U.S. patent application number 17/453033 was filed with the patent office on 2022-08-18 for solid-state laminate electrode assemblies and methods of making.
This patent application is currently assigned to PolyPlus Battery Company. The applicant listed for this patent is PolyPlus Battery Company. Invention is credited to Lutgard C. De Jonghe, Bruce D. Katz, Vitaliy Nimon, Yevgeniy S. Nimon, Steven J. Visco, Ian Wogan.
Application Number | 20220263137 17/453033 |
Document ID | / |
Family ID | |
Filed Date | 2022-08-18 |
United States Patent
Application |
20220263137 |
Kind Code |
A1 |
Visco; Steven J. ; et
al. |
August 18, 2022 |
SOLID-STATE LAMINATE ELECTRODE ASSEMBLIES AND METHODS OF MAKING
Abstract
Solid-state laminate electrode assemblies and various methods
for making the solid-state laminate electrode assemblies involve a
lithium metal layer reactively bonded to a lithium ion conducting
sulfide glass layer. During manufacture, highly reactive surfaces
of the lithium metal layer and the lithium ion conducting sulfide
glass layer are maintained in its substantially unpassivated state
until they have been reactively bonded.
Inventors: |
Visco; Steven J.; (Berkeley,
CA) ; Nimon; Vitaliy; (San Francisco, CA) ;
Wogan; Ian; (Oakland, CA) ; Nimon; Yevgeniy S.;
(Danville, CA) ; De Jonghe; Lutgard C.;
(Lafayette, CA) ; Katz; Bruce D.; (Moraga,
CA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
PolyPlus Battery Company |
Berkeley |
CA |
US |
|
|
Assignee: |
PolyPlus Battery Company
Berkeley
CA
|
Appl. No.: |
17/453033 |
Filed: |
November 1, 2021 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
15929959 |
May 29, 2020 |
11171364 |
|
|
17453033 |
|
|
|
|
15592102 |
May 10, 2017 |
10707536 |
|
|
15929959 |
|
|
|
|
62448817 |
Jan 20, 2017 |
|
|
|
62447637 |
Jan 18, 2017 |
|
|
|
62424240 |
Nov 18, 2016 |
|
|
|
62352972 |
Jun 21, 2016 |
|
|
|
62351211 |
Jun 16, 2016 |
|
|
|
62334327 |
May 10, 2016 |
|
|
|
International
Class: |
H01M 10/0585 20060101
H01M010/0585; H01M 4/1395 20060101 H01M004/1395; H01M 4/04 20060101
H01M004/04; H01M 10/052 20060101 H01M010/052; H01M 4/38 20060101
H01M004/38; H01M 10/0525 20060101 H01M010/0525; H01M 10/0562
20060101 H01M010/0562 |
Goverment Interests
STATEMENT OF GOVERNMENT SUPPORT
[0002] This invention was made with Government support under Award
No.: DE-AR0000772 awarded by the Advanced Research Projects
Agency--Energy (ARPA-E), U.S. Department of Energy. The Government
has certain rights in this invention.
Claims
1-14. (canceled)
15. A lithium metal laminate structure, the laminate comprising: i)
a lithium metal layer having a first and second major surface,
wherein the first major surface is substantially unpassivated; and
ii) a protective material layer that removably covers and protects
the lithium first major surface in direct contact.
16. The lithium metal laminate structure of claim 15, wherein the
substantially unpassivated lithium metal surface is stable.
17. The lithium metal laminate structure of claim 15, wherein the
protective material layer is a liquid phase super dry hydrocarbon
liquid.
18. An inorganic solid electrolyte laminate structure, the laminate
comprising: i) a lithium ion conducting sulfide glass layer having
a first and second major surface; and ii) a protective material
layer that removably covers and protects the sulfide glass first
major surface.
19. The solid electrolyte laminate structure of claim 18, wherein
the protective material layer is a super dry liquid phase
hydrocarbon liquid.
20. (canceled)
21. (canceled)
22. A method for storing a sulfide glass layer having a clean first
major surface, the method comprising the steps of cleaning the
first major surface in an argon plasma, and immersing the sulfide
glass layer into a bath of a liquid phase protective fluid.
23. (canceled)
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is a continuation of U.S. patent
application Ser. No. 15/929,959, filed May 29, 2020, titled
SOLID-STATE LAMINATE ELECTRODE ASSEMBLIES AND METHODS OF MAKING,
which is a continuation of U.S. patent application Ser. No.
15/592,102, filed May 10, 2017, titled SOLID-STATE LAMINATE
ELECTRODE ASSEMBLIES AND METHODS OF MAKING, which claims priority
to U.S. Provisional Patent Application No. 62/334,327, filed May
10, 2016, titled PRISTINE LITHIUM METAL LAYERS AND ASSOCIATED
COMPOSITIONS, STRUCTURES, COMPONENTS, BATTERY CELLS AND METHODS;
62/351,211, filed Jun. 16, 2016, titled PRISTINE LITHIUM METAL
LAYERS AND ASSOCIATED COMPOSITIONS, STRUCTURES, COMPONENTS, BATTERY
CELLS AND METHODS; 62/352,972, filed Jun. 21, 2016, titled PRISTINE
LITHIUM METAL LAYERS AND ASSOCIATED COMPOSITIONS, STRUCTURES,
COMPONENTS, BATTERY CELLS AND METHODS; 62/424,240, filed Nov. 18,
2016, titled PRISTINE LITHIUM METAL LAYERS AND ASSOCIATED
COMPOSITIONS, STRUCTURES, COMPONENTS, BATTERY CELLS AND METHODS;
62/447,637, filed Jan. 18, 2017, titled PRISTINE LITHIUM METAL
LAYERS AND ASSOCIATED COMPOSITIONS, STRUCTURES, COMPONENTS, BATTERY
CELLS AND METHODS; 62/448,817, filed Jan. 20, 2017, titled
STANDALONE LITHIUM METAL LAYER STRUCTURES, STANDALONE Li-ION
CONDUCTIVE SOLID ELECTROLYTE LAYER STRUCTURES, AND ASSOCIATED
COMPOSITIONS, LAMINATE STRUCTURES, COMPONENTS, BATTERY CELLS AND
METHODS; the disclosures of which are incorporated by reference
herein in their entirety and for all purposes.
BACKGROUND
[0003] There is a continuing need for high performance battery
cells, and their associated cell components, and particularly for
high energy density rechargeable lithium metal batteries.
SUMMARY
[0004] The present disclosure describes solid-state laminate
electrode assemblies and various methods for making the solid-state
laminate electrode assemblies.
[0005] In one aspect the present disclosure provides methods for
making a solid-state laminate electrode assembly.
[0006] In various embodiments the solid-state laminate electrode
assembly comprises a lithium metal layer reactively bonded to a
lithium ion conducting sulfide glass layer. Preferably, the
reactive bond is sufficiently complete that it forms a continuous
solid electrolyte interphase (SEI) at the boundary between the
layers.
[0007] In various embodiments, to bring about a continuous SEI, the
lithium metal layer should have a major surface, which, just prior
to bonding (e.g., by laminating), is in a highly reactive state
(i.e., it is substantially unpassivated). In various embodiments
the method involves making a pristine lithium metal layer having a
substantially unpassivated first major surface, and therefore
highly reactive, and maintaining the highly reactive surface in its
substantially unpassivated state until it has been reactively
bonded with the sulfide glass layer.
[0008] In various embodiments the method comprises:
A method for making a solid-state laminate electrode assembly, the
method comprising the steps of [0009] i) providing a lithium metal
laminate structure the laminate comprising: [0010] a. a lithium
metal layer having a first major surface that is substantially
unpassivated; and [0011] b. an inert protective material layer that
removably covers the lithium metal first major surface, the
protective material layer in direct contact with the lithium first
major surface; [0012] ii) providing an inorganic solid electrolyte
laminate structure, the laminate comprising: [0013] a. an inorganic
lithium ion conducting sulfide glass layer having a first major
surface and an opposing second major surface; and [0014] b. an
inert protective material layer that removably covers the sulfide
glass first major surface, the protective material layer in direct
contact with the sulfide glass; [0015] iii) removing the inert
protective material layer from the lithium metal first major
surface; [0016] iv) removing the inert protective material layer
from the sulfide glass first major surface; [0017] v) reactively
bonding the sulfide glass layer with the lithium metal layer via
their first major surfaces; and [0018] wherein the reactive bond is
such that the interface between the sulfide glass layer and the
lithium metal is defined by a continuous solid electrolyte
interphase.
[0019] In various embodiments, the inert protective material layer
on the sulfide glass first major surface is a liquid phase layer of
a dry hydrocarbon liquid, and the inert protective material layer
on the substantially unpassivated lithium metal first major surface
is a liquid phase layer of a dry hydrocarbon liquid.
[0020] In various embodiments, the hydrocarbon liquid on the
lithium metal surface is removed substantially immediately prior to
the reactive bonding step, and optionally the hydrocarbon liquid on
the sulfide glass is removed substantially immediately prior to
reactively bonding step.
[0021] In various embodiments, the removal of the hydrocarbon
liquid is accelerated by the application of one or more heat
(conductive or convective), vacuum suction, blowing a jet of dry Ar
or He, and blowing a jet of high vapor pressure protective liquid
followed by vacuum suction.
[0022] In various embodiments, the step of cleaning the first major
surface of the sulfide glass layer under an argon plasma, by ion
etching; wherein the cleaning step is performed after the liquid
phase layer of protective fluid has been removed.
[0023] In various embodiments, the step of treating the clean first
major surface of the sulfide glass under a nitrogen containing
plasma, wherein the treatment modifies the surface composition of
the sulfide glass by introducing nitrogen into/onto the glass
surface.
[0024] In various embodiments, the step of treating the clean
sulfide glass first major surface to form a precursor film
consisting of 1 to 5 monolayers of a halogen (e.g., iodine) or an
interhalogen, or nitrogen onto the clean glass surface, wherein the
monolayer(s) react with lithium on bonding to form a solid
electrolyte interphase.
[0025] In various embodiments, the step of treating the clean
sulfide glass first major surface to form a precursor film of
nitrogen molecules on the glass surface.
[0026] In various embodiments, the solid electrolyte interphase
comprises Li3N.
[0027] In various embodiments, a method of making a lithium metal
layer having a substantially unpassivated first major surface, and
preferably a pristine surface, includes extruding lithium metal
directly into a liquid phase of protective fluid (e.g., super dry
liquid hydrocarbon).
[0028] In various embodiments, a method of making a lithium metal
layer having a substantially unpassivated first major surface, and
preferably a pristine surface, includes extruding lithium metal and
substantially immediately covering the freshly formed lithium metal
surfaces with a liquid phase protective fluid.
[0029] In various embodiments, the extrusion comprises at least two
extrusions performed by roll reduction, and the as-extruded lithium
metal layers are substantially immediately covered in liquid phase
protective fluid right after each roll reduction step, and
maintained under liquid phase protective fluid throughout the
process.
[0030] In various embodiments, the lithium metal layer is in the
form of a long continuous roll, and the method further comprises
the step of placing the lithium metal roll into a hermetic canister
filled with liquid phase protective fluid, the lithium metal layer
completely immersed within the protective fluid.
[0031] In various embodiments, the substantially unpassivated first
major surface of the lithium metal layer has never been in direct
touching contact with a gas phase atmosphere or vacuum.
[0032] In various embodiments, a lithium metal laminate structure
is provided. The laminate includes: [0033] i) a lithium metal layer
having a first and second major surface, wherein the first major
surface is substantially unpassivated; and [0034] ii) a protective
material layer that removably covers and protects the lithium first
major surface in direct contact.
[0035] In various embodiments, the substantially unpassivated
lithium metal surface is stable.
[0036] In various embodiments, the protective material layer is an
liquid phase hydrocarbon liquid, preferably super dry.
[0037] In various embodiments, an inorganic solid electrolyte
laminate structure is provided. The laminate includes: [0038] i) a
lithium ion conducting sulfide glass layer having a first and
second major surface; and [0039] ii) a protective material layer
that removably covers and protects the sulfide glass first major
surface.
[0040] In various embodiments, the protective material layer is a
liquid phase hydrocarbon liquid, preferably super dry.
[0041] In various embodiments, a method for storing a solid-state
laminate electrode assembly is provided. The method includes making
a solid-state laminate electrode assembly as described herein, and
immersing the laminate electrode assembly into a bath of a liquid
phase protective fluid (e.g., a super dry liquid hydrocarbon).
[0042] In various embodiments, a method for storing a lithium metal
layer having a substantially unpassivated first major surface is
provided. The method includes making the substantially unpassivated
first major surface, and immersing the lithium metal layer into a
bath of a liquid phase protective fluid (e.g., a super dry liquid
hydrocarbon).
[0043] In various embodiments, a method for storing a sulfide glass
layer having a clean first major surface is provided. The method
includes cleaning the first major surface in an argon plasma, and
immersing the sulfide glass layer into a bath of a liquid phase
protective fluid (e.g., a super dry liquid hydrocarbon).
[0044] In various embodiments, a method for making a battery cell
is provided. The method includes making a solid-state electrode
assembly as described herein, and placing a positive electrode
layer adjacent to the second surface of the sulfide glass
layer.
[0045] These and other aspects of the present disclosure are
described in further detail below, including with reference to the
drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
[0046] FIG. 1 is a process flow diagram for making a solid-state
laminate electrode assembly in accordance with one embodiments of
the present disclosure.
[0047] FIGS. 2A-D illustrate cross section depictions of standalone
alkali metal laminate structures in accordance with various
embodiments of the present disclosure.
[0048] FIGS. 2E-H illustrate cross section depictions of standalone
inorganic solid electrolyte laminate structures in accordance with
various embodiments of the present disclosure.
[0049] FIGS. 3A-E illustrate cross section and top down depictions
of lithium metal layers and lithium metal surfaces.
[0050] FIGS. 4A-G illustrate apparatus' and method' for making a
lithium metal layer having substantially unpassivated surfaces, in
accordance with various embodiments of the present disclosure.
[0051] FIGS. 5A-B illustrate a lithium roll assembly cartridge
according to one embodiment of the present disclosure.
[0052] FIG. 6A illustrates an apparatus and method for cleaning and
treating an inorganic solid electrolyte layer, in accordance with
an embodiment of the present disclosure.
[0053] FIG. 6B illustrates a cross section depiction of an
inorganic solid electrolyte layer coated with a thin precursor
film, in accordance with one embodiment of the present
disclosure.
[0054] FIG. 7 illustrates a cross section depiction of a
solid-state laminate electrode assembly in accordance with one
embodiment of the present disclosure.
[0055] FIG. 8 illustrates an apparatus and method for making a
solid-state laminate electrode assembly in accordance with one
embodiment of the present disclosure.
[0056] FIG. 9 illustrates a roll assembly cartridge containing a
solid-state laminate electrode assembly according to one embodiment
of the present disclosure.
[0057] FIG. 10 illustrates a cross section depiction of a battery
cell in accordance with one embodiment of the present
disclosure.
DETAILED DESCRIPTION OF SPECIFIC EMBODIMENTS
[0058] Reference will now be made in detail to specific embodiments
of this disclosure. Examples of the specific embodiments are
illustrated in the accompanying drawings. While this disclosure
will be described in conjunction with these specific embodiments,
it will be understood that it is not intended to limit this
disclosure to such specific embodiments. On the contrary, it is
intended to cover alternatives, modifications, and equivalents as
may be included within the spirit and scope of this disclosure. In
the following description, numerous specific details are set forth
in order to provide a thorough understanding of this disclosure.
This disclosure may be practiced without some or all of these
specific details. In other instances, well known process operations
have not been described in detail in order to not unnecessarily
obscure this disclosure.
Introduction
[0059] The present disclosure describes solid-state laminate
electrode assemblies and various methods for making the solid-state
laminate electrode assemblies.
[0060] In various embodiments the solid-state laminate electrode
assembly comprises a lithium metal layer reactively bonded to a
lithium ion conducting sulfide glass layer. Preferably, the
reactive bond is sufficiently complete that it forms a continuous
solid electrolyte interphase (SEI) at the boundary between the
layers.
[0061] In various embodiments, to bring about a continuous SEI, the
lithium metal layer should have a major surface, which, just prior
to bonding (e.g., by laminating), is in a highly reactive state
(i.e., it is substantially unpassivated). In various embodiments
the method involves making a pristine lithium metal layer having a
substantially unpassivated first major surface, and therefore
highly reactive, and maintaining the highly reactive surface in its
substantially unpassivated state until it has been reactively
bonded with the sulfide glass layer.
[0062] In various embodiments, the present disclosure provides
methods for making a solid-state laminate electrode assembly. Such
a method includes: [0063] ii) providing a lithium metal laminate
structure the laminate comprising: [0064] a. a lithium metal layer
having a first major surface that is substantially unpassivated;
and [0065] b. an inert protective material layer that removably
covers the lithium metal first major surface, the protective
material layer in direct contact with the lithium first major
surface; [0066] ii) providing an inorganic solid electrolyte
laminate structure, the laminate comprising: [0067] c. an inorganic
lithium ion conducting sulfide glass layer having a first major
surface and an opposing second major surface; and [0068] d. an
inert protective material layer that removably covers the sulfide
glass first major surface, the protective material layer in direct
contact with the sulfide glass; [0069] iii) removing the inert
protective material layer from the lithium metal first major
surface; [0070] iv) removing the inert protective material layer
from the sulfide glass first major surface; [0071] v) reactively
bonding the sulfide glass layer with the lithium metal layer via
their first major surfaces; and [0072] wherein the reactive bond is
such that the interface between the sulfide glass layer and the
lithium metal is defined by a continuous solid electrolyte
interphase.
[0073] In various embodiments the reactive bonding step is a
lamination process performed in a chamber filled with a dry gas
(e.g., dry argon). Typically the laminating step involves applying
both heat and pressure.
[0074] In various embodiments the inert protective material layer
removably covering one or both of the sulfide glass first major
surface and the substantially unpassivated lithium metal surface is
a liquid phase protective fluid.
[0075] In various embodiments the liquid phase protective fluid
removably covering the lithium metal surface is removed just prior
to the reactive bonding step (e.g., the period of time between
removing the liquid phase protective fluid and reactive bonding is
less than 10 seconds, and preferably less than 5 seconds, and even
more preferably less than 2 seconds).
[0076] In various embodiments to ensure that the interface formed
between the lithium metal layer and the lithium ion conducting
sulfide glass is electrochemically operable or otherwise optimized,
an SEI may be engineered by coating a first major surface of the
sulfide glass with a thin precursor film that reacts with lithium
metal during the bonding step to form a solid electrolyte
interphase.
[0077] In some embodiments the sulfide glass surface may be treated
under a nitrogen containing plasma to incorporate nitrogen into the
surface of the glass, and then forming a lithium nitride.
[0078] In various embodiments the method further comprises the step
of cleaning the first major surface of the sulfide glass under an
argon plasma, by ion etching, this step performed after removing
the inert protective material layer from of the sulfide glass but
before reactive bonding.
[0079] In various embodiments the method further comprises the step
of treating the clean sulfide glass first major surface to modify
its surface composition. In various embodiments the surface
composition is modified by placing the clean first major surface of
the sulfide glass under a nitrogen containing plasma, wherein the
treatment modifies the surface composition of the sulfide glass by
introducing nitrogen into/onto the surface.
[0080] In various embodiments the method further comprises the step
of coating the clean sulfide glass first major surface with a thin
precursor film having a composition that will react in direct
contact with lithium metal.
[0081] In various embodiments the thin precursor film is formed by
condensing between 1 to 5 monolayers of a halogen (e.g., iodine) or
interhalogen or nitrogen onto the clean sulfide glass surface;
wherein the iodine monolayers leads to reactive wetting during the
reactive bonding step.
[0082] In various embodiments the method further comprises coating
the clean sulfide glass surface to form a precursor film that
reacts with lithium during the reactive bonding step to form a
solid electrolyte interphase between the lithium metal layer and
sulfide glass layer.
[0083] In various embodiments the inert protective material layer
removably covering one or both of the sulfide glass first major
surface and the substantially unpassivated lithium metal surface is
a liquid phase protective fluid.
[0084] In one aspect the present disclosure provides methods for
making a pristine lithium metal layer having a substantially
unpassivated first major surface, as defined herein below. In
various embodiments the opposing second major surface of the
pristine lithium metal layer is adhered to a current collector
(e.g., a copper foil)
[0085] In various embodiments the pristine lithium metal layer is
in the form of a long continuous roll of lithium that is immersed
in liquid phase protective fluid for storage and/or downstream
processing of battery cells (e.g., the pristine lithium metal layer
at least 100 cm in length).
[0086] In various embodiments the method involves making the
pristine lithium metal layer in a protective inert fluid, and
maintaining the pristine lithium metal layer in protective fluid
(e.g., protective liquid) to prevent directly exposing the surface
to the ambient gaseous atmosphere (including dry argon of a glove
box or dry Air of a dry room). In various embodiments the
protective fluid is an inert liquid or the vapor of an inert liquid
(i.e., protective vapor). In various embodiments the lithium metal
layer is in the form of a long continuous ribbon (e.g., more than
50 cm in length).
[0087] In various embodiments the method for making the
substantially unpassivated lithium metal surface includes an
extrusion step that produces a fresh substantially unpassivated
lithium first major surface inside or surrounded by protective
fluid (e.g., a protective and super dry liquid hydrocarbon). By use
of the term super dry it is meant that the amount of moisture in
the liquid hydrocarbon is not greater than 0.1 ppm. In various
embodiments the pristine lithium metal layer and its substantially
unpassivated surface is extruded directly into liquid phase
protective fluid (i.e., protective liquid), and then optionally the
method further includes winding the lithium metal layer into a long
continuous roll while it is immersed in liquid phase protective
fluid.
[0088] In various embodiments the extrusion step is die extrusion
of lithium ingot directly into a super dry liquid hydrocarbon bath.
In various embodiments the extrusion step is a roller extrusion
wherein the lithium metal foil thickness is roll reduced in
protective liquid, and in the process forms fresh lithium
substantially unpassivated lithium metal surfaces, wherein the area
of the fresh surfaces so formed is proportional to the reduction in
thickness of the lithium layer. In various embodiments multiple
roll reduction steps are performed (e.g., 2, 3, 4 or 5 or more) in
order to produce the desired thickness and to perfect the
substantially unpassivated surface (e.g., a pristine surface). In
various embodiments, the stock foil used for the roll reduction
process has been pre-passivated, to improve reproducibility of the
starting surface condition. In a particular embodiment a lithium
ingot is die extruded directly into protective fluid to form a
pristine lithium metal layer, and then that layer is immediately
roll reduced in protective fluid to the desired thickness, and
throughout the process the substantially unpassivated lithium metal
surface remains covered or immersed in liquid phase protective
fluid. The pristine lithium metal as formed may then be wound into
a long continuous roll of pristine lithium metal, the winding
performed in protective fluid (e.g., the winding performed inside
liquid phase protective fluid).
[0089] In various embodiments the substantially unpassivated
lithium metal surfaces are stored in a canister of protective
liquid, or they are formed and immediately transferred into the
canister, without exposing the surfaces to the ambient gaseous
environment.
[0090] In another aspect the present disclosure provides a
standalone electrochemical material laminate structure for
maintaining a major surface of a battery active material layer in a
substantially unpassivated and/or substantially uncontaminated
condition during handling, storage and/or battery cell
fabrication.
[0091] In various embodiments the battery active material layer
reacts with water and/or oxygen, and even under fairly dry ambient
conditions, such as that of a dry air room or a dry argon filled
glove box the battery material surfaces chemically degrade or
passivate rather quickly. The laminate structures of the present
disclosure protect the battery material surfaces by encapsulating
them underneath an inert removable layer, which inhibits moisture
and/or oxygen from reaching the surfaces.
[0092] Accordingly, the standalone electrochemical material
laminate structures of the present disclosure are particularly
useful for making, storing and transporting moisture sensitive
battery active material layers, and for making downstream battery
cells and laminate electrode assemblies from those material
layers.
[0093] In accordance with the present disclosure, a standalone
electrochemical material laminate structure may be composed of two
or more continuous material layers, wherein at least one of the
material layers (i.e., a first material layer) is a "battery active
solid material" having a clean (i.e., substantially uncontaminated)
and/or substantially unpassivated surface, and another material
layer (i.e., a second material layer) is a "protective material"
that is inert, not battery active, and removably covers, in direct
contact, a first major surface of the battery active material.
[0094] When referring to a material as "battery active" it
generally means that the material is active in an electrochemical
sense and useful in a battery cell (i.e., it is either an
electro-active material or an electrolyte material). As used
herein, the term "battery active solid material layer" means either
a solid alkali metal or an inorganic solid electrolyte having
utility as a continuous solid layer in a battery cell (e.g., a
lithium metal layer or a Li-ion conducting sulfide glass sheet,
respectively).
[0095] In contrast to the battery active material layer, the
protective material layer is inert and not battery active. By use
of the term "inert" it means that the referenced inert material
does not chemically react in contact with the battery active solid
material on which it is intended to protect. And when referring to
the protective material layer as "not battery active," it is meant
that the material layer is not useful in a battery cell, and is
furthermore not intended for use in a battery cell, and not active
in a battery/electrochemical sense (i.e., not an electroactive
material or alkali metal ion conductor).
[0096] In accordance with the present disclosure the protective
material layer: i) provides an encapsulating barrier against direct
touching exposure between the first major surface of the battery
active material layer and the ambient gaseous atmosphere or
contaminants in a vacuum chamber about the layer; ii) is inert in
direct contact with the first major surface; and iii) is readily
removed without physically damaging the surface. To achieve these
objectives, in various embodiments the protective material layer is
an inert liquid (e.g., a super dry hydrocarbon liquid) that
encapsulates the surface on which it is applied, and may be
evaporatively removed in the absence of solid to solid touching
contact
[0097] In a first embodiment, the battery active material layer is
an electroactive alkali metal layer having a substantially
unpassivated first major surface (e.g., a pristine lithium metal
layer), and in such embodiments the standalone electrochemical
material laminate structure is generally referred to herein as a
standalone alkali metal laminate structure; e.g., a standalone
lithium metal laminate structure.
[0098] In a second embodiment, the battery active material layer is
an inorganic solid electrolyte layer having a substantially
uncontaminated first major surface (e.g., a lithium ion conducting
sulfide glass sheet), and in such embodiments the standalone
electrochemical material laminate structure is generally referred
to herein as a standalone solid electrolyte laminate structure;
e.g., a standalone sulfide glass laminate structure.
[0099] By use of the term "standalone" when referring to an
electrochemical material laminate structure, such as a standalone
alkali metal laminate structure or a standalone solid electrolyte
laminate structure, it is meant to emphasis that the battery active
material layer in the standalone laminate is a discrete battery
active material layer that has not yet been combined or coupled
with a second battery active material layer, or yet been placed in
a battery cell.
[0100] In another aspect the present disclosure provides methods
for making lithium metal layers having substantially unpassivated
surfaces and preventing passivation by encapsulating them with
inert liquid. In various embodiments the methods include making a
lithium metal foil having substantially unpassivated surfaces by
die extruding a lithium ingot into a bath of super dry liquid
hydrocarbons. In various embodiments the as made substantially
unpassivated lithium metal foil may be further reduced in thickness
by roller reduction and applying hydrocarbon liquid onto the
freshly formed surfaces to ensure that they remain substantially
unpassivated. In various embodiments a pre-passivated lithium metal
layer of thickness (t) may be roller reduced in a roller mill using
multiple roll reduction steps while at all times maintaining liquid
hydrocarbon on the freshly formed lithium metal layer surfaces. By
using pre-passivated lithium metal (e.g., passivated by exposure to
CO.sub.2), reproducibility is unproved because the initial surface
condition of the lithium is itself reproducible, as opposed to
using lithium metal that is passivated in a less or uncontrolled
fashion. Moreover, the area of freshly formed lithium is
proportional to the decrease in thickness of the layer.
[0101] In another aspect the present disclosure provides methods
for making inorganic lithium ion conducting sulfide glass sheets
having substantially uncontaminated surfaces, and for preventing
hydrolysis of those surfaces by encapsulating them underneath an
inert super dry hydrocarbon fluid (e.g., liquid). For instance, in
various embodiments the inorganic sulfide glass sheets are cleaned
by ion etching in an Ar plasma to etch away any contaminated
surface(s), and then substantially immediately after the ion
etching step, the cleaned sulfide glass sheet may be immersed in a
liquid hydrocarbon bath, or the clean surface encapsulated by a
protective liquid layer, as described above. In various
embodiments, the surface composition of the sulfide glass may be
modified during or immediately after cleaning by using an
argon/nitrogen plasma mixture for incorporating nitrogen into the
surface of the sulfide glass sheet, or the surfaces may be treated
sequentially, using a first ion etch in argon plasma, followed by a
second treatment in a nitrogen containing plasma (e.g., pure
nitrogen or an argon/nitrogen mixture).
[0102] In yet another aspect the present disclosure provides
methods of making a strongly adhered fully solid-state inorganic
laminate electrode assembly having a substantially contaminate free
inorganic interface. In various embodiments the method includes
providing a first battery active material as a component of a
lithium metal laminate structure (e.g., a lithium metal layer
having a first major surface which is substantially unpassivated
and protected by an inert hydrocarbon liquid layer); providing a
second battery active material layer as a component of an inorganic
solid electrolyte laminate structure (e.g., a lithium ion
conducting sulfide glass sheet having a clean first major surface
that is devoid of hydrolysis reaction products and protected by an
inert hydrocarbon liquid layer); removing the inert hydrocarbon
liquid layers; and then, substantially immediately thereafter,
reactively bonding the substantially unpassivated lithium metal
surface to the clean inorganic sulfide glass surface, to form a
strongly adhered laminate having a clean inorganic interface with a
low area resistance (preferably, less than 50.OMEGA.-cm.sup.2).
Preferably the peel strength of the laminate electrode assembly is
greater than the tensile strength of its lithium metal layer, such
that any attempt to peel off the lithium from the laminate results
in the lithium tearing prior to peeling.
[0103] In various embodiments, an improved laminate interface is
formed by laminating the fluid protected lithium metal surface to a
solid electrolyte sheet using techniques whereby the fluid is
removed substantially immediately prior to, or during, the
laminating step, as the solid electrolyte comes into direct contact
with the fluid and the lithium metal layer. In various embodiments,
the laminating step effects a three phase boundary of lithium metal
layer, solid electrolyte, and protective fluid, and causes the
fluid to be removed from the surface substantially instantaneously
as the solid electrolyte layer reactively adheres to the pristine
lithium metal layer surface.
[0104] In another aspect, the present disclosure relates to methods
and reagents to form a thin, dense and lithium ion conductive layer
between a lithium metal layer and an inorganic solid electrolyte
layer (e.g., a lithium ion conducting sulfide glass). The layer is
sometimes referred to herein as a solid electrolyte interphase
(SEI) as it is formed by reacting a first major surface of the
lithium metal layer with a coating on the glass surface that allows
for the glass electrolyte to be optimized for high ionic
conductivity and processability, regardless of its chemical
compatibility with lithium metal.
[0105] In another aspect the present disclosure provides methods of
making battery cells by combining the fully solid-state inorganic
laminate electrode assembly of the present disclosure with a
positive electrode (e.g., a lithium ion intercalating positive
electrode).
[0106] A list of suitable hydrocarbons which may be used as
protective fluid (e.g., inert liquid) in accordance with the
various embodiments and aspects of the present disclosure is
provided below, as well as their structural formulas and vapor
pressure (and/or boiling point) values. In various embodiments, the
protective fluid is selected from a group of saturated hydrocarbons
with the number of carbon atoms from 5 to 15. In one particular
case, the protective fluid is isododecane. The protective fluids
may be a combination of these various fluids. The fluids generally
contain no dissolved or dispersed chemicals (e.g., salts,
lubricants and/or greases) that would coat the surface of the
lithium metal layer or solid electrolyte layer with a solid film or
residue. Accordingly the protective fluid is devoid of any
dissolved salts (e.g., lithium salts).
[0107] Suitable protective fluids are chemically inert to Li metal
or Li alloys and contain less than 0.1 ppm of moisture, less than 1
ppm of moisture, less than 5 ppm of moisture, less than 10 ppm of
moisture. In the case when a protective fluid is used in
combination with a glass coating designed to form a solid
electrolyte interphase (SEI) upon contact with Li, the protective
fluid is chosen to be non-reactive with the glass coating.
[0108] Protective Fluids
Saturated Hydrocarbons (Alkanes) C.sub.nH.sub.2n+2 Straight-Chain
Alkanes C.sub.5-C.sub.15 n-Pentane C.sub.5H.sub.12 BP=36.degree.
C., Vapor Pressure: 434 mmHg at 20.degree. C.
##STR00001##
n-Hexane C.sub.6H.sub.14 HP=69.degree. C., Vapor Pressure: 121 mmHg
at 20.degree. C.
##STR00002##
n-Heptane C.sub.7H.sub.16 BP=99.degree. C., Vapor Pressure: 46 mmHg
at 20.degree. C.
##STR00003##
n-Octane C.sub.8H.sub.18 R BP=125.degree. C., Vapor Pressure: 11
mmHg at 20.degree. C.
##STR00004##
n-Nonane C.sub.9H.sub.20 BP=151.degree. C., Vapor Pressure: 3 8
mmHg at 25.degree. C.
##STR00005##
n-Decane C.sub.10H.sub.22 BP=174.degree. C., Vapor Pressure: 2.7
mmHg at 20.degree. C.
##STR00006##
n-Undecane C.sub.11H.sub.24 BP=196.degree. C., Vapor Pressure: 0.4
mmHg at 25.degree. C.
##STR00007##
n-Dodecane C.sub.12H.sub.26 BP=216.degree. C., Vapor Pressure: 0.14
mmHg at 25.degree. C.
##STR00008##
Branched-Chain Alkanes C.sub.5-C.sub.15 Isopentane C.sub.5H.sub.12
BP=28.degree. C., Vapor Pressure: 577 mmHg at 20.degree. C.
##STR00009##
Isohexane C.sub.6H.sub.14 BP=61.degree. C., Vapor Pressure: 172
mmHg at 20.degree. C.
##STR00010##
Isohentane C.sub.7H.sub.16 BP=90.degree. C., Vapor Pressure: 66
mmHg at 20.degree. C.
##STR00011##
Isooctane C.sub.8H.sub.18 BP=99.degree. C., Vapor Pressure: 41 mmHg
at 21.degree. C.
##STR00012##
Tetraethylmethane C.sub.9H.sub.20 BP=146.degree. C., Vapor
Pressure: 7.3 mmHg at 25.degree. C.
##STR00013##
Isodecane C.sub.10H.sub.22 BP=167.degree. C., Vapor Pressure: 2.3
mmHg at 25.degree. C.
##STR00014##
3-Methyldecane C.sub.11H.sub.24 BP=188.degree. C., Vapor Pressure:
N/A
##STR00015##
Isododecane C.sub.12H.sub.26 BP=180.degree. C., Vapor Pressure:
0.301 mmHg at 20.degree. C.
##STR00016##
Cycloalkanes C.sub.6-C.sub.8 C.sub.nH.sub.2n Cyclohexane
C.sub.6H.sub.12 BP=81.degree. C., Vapor Pressure: 78 mmHg at
20.degree. C.
##STR00017##
Cycloheptane C.sub.7H.sub.14 BP=118.degree. C., Vapor Pressure: 22
mmHg at 20.degree. C.
##STR00018##
Cyclooctane C.sub.8H.sub.16 BP=149.degree. C., Vapor Pressure: 16
mmHg at 37.7.degree. C.
##STR00019##
Unsaturated Acyclic Hydrocarbons
[0109] C.sub.nH.sub.2(n-m-1), n=number of carbon atoms m=number of
double bonds Alkenes C.sub.6-C.sub.11, C.sub.nH.sub.2n 1-Hexene
C.sub.6H.sub.12 BP=64.degree. C., Vapor Pressure: 155 mmHg at
21.degree. C.
##STR00020##
1-Heptene C.sub.7H.sub.14 BP=94.degree. C., Vapor Pressure: 101
mmHg at 37.7.degree. C.
##STR00021##
1-Octene C.sub.8H.sub.16 BP=122.degree. C., Vapor Pressure: 36 mmHg
at 37.7.degree. C.
##STR00022##
1-Nonene C.sub.9H.sub.18 BP=146.degree. C., Vapor Pressure: 11 mmHg
at 37.7.degree. C.
##STR00023##
1-Docene C.sub.10H.sub.20 BP=172.degree. C., Vapor Pressure: 1.67
mmHg at 25.degree. C.
##STR00024##
1-Undecene C.sub.11H.sub.22 BP=192.degree. C. Vapor Pressure:
N/A
##STR00025##
1-Dodecene C.sub.12H.sub.24 BP=214.degree. C., Vapor Pressure:
N/A
##STR00026##
Alkadienes: C.sub.6-C.sub.12 C.sub.nH.sub.2n-2 1,5-Hexadiene
C.sub.6H.sub.10 BP=60.degree. Vapor Pressure: 367 mmHg at
37.7.degree. C.
##STR00027##
2,4-Hexadiene C.sub.6H.sub.10 BP=82.degree. C. Vapor Pressure:
N/A
##STR00028##
1,6-Heptadiene C.sub.7H.sub.12 BP=90.degree. C., Vapor Pressure:
N/A 1,7-Octadiene C.sub.8H.sub.14 BP=118.degree. C., Vapor
Pressure: 19 mmHg at 25.degree. C.
##STR00029##
1,8-Nonadiene C.sub.9H.sub.16 BP=141.degree. C., Vapor Pressure: 7
mmHg at 25.degree. C.
##STR00030##
1,9-Decadiene C.sub.10H.sub.18 BP=169.degree. C., Vapor Pressure: 4
mmHg at 20.degree. C.
##STR00031##
1,10-Undecadiene C.sub.11H.sub.20 BP=187.degree. C., Vapor
Pressure: N/A
##STR00032##
1,11-Dodecadiene C.sub.12H.sub.22 BP=207.degree. C., Vapor
Pressure: N/A
##STR00033##
Unsaturated Cyclic Hydrocarbons
[0110] C.sub.nH.sub.2(n-m), n=number of carbon atoms m=number of
double bonds Cycloalkenes C.sub.6-C.sub.8, C.sub.nH.sub.2n-2
Cyclohexene C.sub.6H.sub.10 BP=83.degree. C., Vapor Pressure: 160
mmHg at 20.degree. C.
##STR00034##
Cycloheptene C.sub.7H.sub.12 BP=113.degree. C., Vapor Pressure: 22
mmHg at 20.degree. C.
##STR00035##
Cyclooctene C.sub.8H.sub.14 BP=145.degree. C., Vapor Pressure:
N/A
##STR00036##
Cycloalkadienes C.sub.6-C.sub.8, C.sub.nH.sub.2n-4
1.3-Cyclohexadiene C.sub.6H.sub.8 BP=80.degree. C., Vapor Pressure:
56 mmHg at 25.degree. C.
##STR00037##
1,4-Cyclohexadiene C.sub.6H.sub.8 BP=88.degree. C., Vapor Pressure:
N/A
##STR00038##
1.3-Cycloheptadiene C.sub.7H.sub.12 BP=120.degree. C., Vapor
Pressure: N/A
##STR00039##
1,3-Cyclooctadiene C.sub.8H.sub.14 BP=143.degree. C., Vapor
Pressure: 13.4 mmHg at 25.degree. C.
##STR00040##
[0111] Generally, the protective inert liquid layer is devoid of
dissolved and/or dispersed chemicals (e.g., salts, lubricants
and/or greases) that would coat the surface of the battery active
material layer with a solid film or leave behind a sticky residue.
Accordingly, the protective inert liquid layer is generally devoid
of dissolved salts (e.g., lithium salts, or more generally alkali
metal salts).
[0112] In order to be inert in direct contact with the battery
active material layer, the liquid hydrocarbon(s) should have a very
low concentration of moisture. Preferably the concentration of
moisture in the inert liquid hydrocarbon layer is less than 10 ppm
of water, more preferably less than 5 ppm of water, even more
preferably less than 1 ppm of water, and yet even more preferably
less than 0.1 ppm of water (i.e., super dry). In various
embodiments the inert liquid is actively dried in the presence of
sacrificial alkali metal surfaces (e.g., pieces/chips of lithium or
sodium metal) that getter oxygen, water and nitrogen impurities.
Moreover, the liquid hydrocarbons may be passed through a drying a
chamber in order to maintain very low moisture levels. The drying
chamber may contain drying agents and oxygen getters. Examples of
drying agents for liquid hydrocarbons include molecular sieves (3A,
4A, or 5A depending on the hydrocarbon type), magnesium oxide, zinc
chloride, calcium sulfate, calcium chloride, calcium hydride, and
alumina (neutral or basic). In various embodiments, the cumulative
area of the sacrificial alkali metal surfaces in direct contact
with the inert liquid is greater than the first major surface of
the battery active material layer on which the inert liquid covers
in direct contact, for instance when the battery active material
layer is disposed in a protective liquid bath, as described in more
detail herein below.
Depicted Embodiments
[0113] In one aspect the present disclosure provides methods for
making a solid-state laminate electrode assembly. In various
embodiments, the solid-state laminate electrode assembly is a
lithium metal layer reactively bonded with a lithium ion conducting
sulfide glass layer.
[0114] With reference to FIG. 1 there is illustrated process flow
diagram 5 for making a solid-state laminate electrode assembly in
accordance with various embodiments of the present disclosure.
[0115] The process includes initial steps 10 and 20, for making or
providing a first and a second standalone electrochemical material
laminate structure, respectively. Notably, first and second
electrochemical material laminate structures are not the same.
[0116] As used herein, the term electrochemical material laminate
structure means a laminate of two or more continuous material
layers, wherein at least one of the material layers (i.e., a first
material layer) is a "battery active solid material layer" having a
clean (i.e., substantially uncontaminated) and/or substantially
unpassivated first major surface, and another material layer (i.e.,
a second material layer) is a "protective material layer" that is
inert, not battery active, and removably covers, in direct intimate
contact, the first major surface of the battery active material
layer. In various embodiments the protective material layer is a
liquid phase layer of a protective fluid, such as a super dry
hydrocarbon liquid that is spread out evenly over the first major
surface of the battery active material layer.
[0117] Generally, the battery active material layer is highly
reactive with water and/or oxygen, and its surfaces chemically
degrade or passivate rather quickly, even under dry or vacuum
conditions, including that of a dry air room suited for handling
lithium metal (e.g., having a dew point between -20 to -40.degree.
C.) or a dry argon filled glove box (e.g., having a low moisture
and oxygen content of between 1 to 5 ppm). Accordingly, the
electrochemical laminate structure is used to shield a battery
active material layer against adverse reactions with the
environment in which the battery active material layer is made,
processed and/or stored. And by the term "solid battery active
material layer" it is meant either a solid alkali metal layer
(e.g., typically embodied herein as a lithium metal layer) or an
inorganic solid electrolyte layer (e.g., typically embodied herein
as a lithium ion conducting sulfide glass). When the battery active
material layer is a lithium metal layer, the laminate structure is
referred to generally as an alkali metal laminate structure (or
more specifically in this case as a lithium metal laminate
structure), and when the battery active material layer is an
inorganic lithium ion conducting sulfide glass, the laminate
structure is referred generally as a solid electrolyte laminate
structure (or more specifically in this case as a sulfide glass
laminate structure). Furthermore, by use of the term "standalone"
when referring to an electrochemical material laminate structure,
such as a standalone alkali metal laminate structure or a
standalone solid electrolyte laminate structure, it is meant to
emphasis that the battery active material layer in the standalone
laminate is a discrete battery active material layer that has not
yet been combined or coupled with a second battery active material
layer, or yet been placed in a battery cell. For instance, when
standalone lithium laminate structures are absent of an electrolyte
and standalone sulfide glass solid electrolyte laminate structures
are absent of battery electroactive materials.
[0118] Continuing with reference to FIG. 1 the first
electrochemical material laminate structure, which is provided or
made in process step 10 is a standalone lithium metal laminate
structure, and the second electrochemical material laminate
structure, which is provided in process step 20, is a standalone
sulfide glass laminate structure. Once the laminate structures are
provided (or made), the protective material layer on their
respective first major surfaces is removed during process steps 12
and 22, and done without physically damaging the surfaces. As
mentioned above, in various embodiments the protective material
layer is an inert liquid phase layer of a super dry liquid
hydrocarbon. Moreover, the liquid hydrocarbon employed herein as a
protective material layer is selected, in part, based on its
ability to remain on the surface of the lithium metal or sulfide
glass layer until such time that it is to be controllably removed,
rather than evaporating off by happenstance. Processes for
accelerating and controllably removing the protective liquid layer
from the battery active material layer can be performed in a
chamber designed for that purpose. Such processes include one or
more of heating, vacuum suction, blowing a jet of dry inert gas,
blowing a jet of high vapor pressure protective fluid followed by
vacuum suction, as well as rinsing the surfaces with protective
fluids having progressively higher vapor pressures.
[0119] Once the protective material layer has been removed, it is
important to minimize any exposure to gaseous or vacuum
environments in order to maintain the respective battery active
material layer surfaces clean and unpassivated. Accordingly, in
some embodiments the chamber or conduit through which the battery
active material layers are translated may be filled with vapor
phase protective fluid right up until the layers are combined for
lamination, according to process step 30, wherein the layers are
reactively bonded to each other.
[0120] In various embodiments, once the liquid phase layer of
protective fluid has been removed from the surface of the sulfide
glass, the glass first major surface may be processed and/or
treated prior to laminating with lithium metal in order to engineer
a solid electrolyte interphase (SEI) with improved electrochemical
properties, or when the sulfide glass is not chemically compatible
with lithium metal. As described in more detail herein below, the
sulfide glass may undergo a cleaning process 24A, exemplified by an
ion etch treatment under an Ar plasma followed by a surface
treating process 24B, wherein the cleaned glass surface may be
coated with a thin lithium metal reactive precursor film or treated
to modify the surface composition of the glass (e.g., by placing
the glass first major surface under a nitrogen containing
plasma).
[0121] The material laminate structures, methods and processes
briefly described above with reference to process flow diagram in
FIG. 1 are now described in more detail herein below, beginning
with a description of the various architectures embodied for the
standalone material laminate structures, followed by methods for
making lithium metal layers having substantially unpassivated
surfaces, as well as methods for treating the sulfide glass to an
engineered solid electrolyte interphase.
Standalone Electrochemical Material Laminate Structure
[0122] In one aspect the present disclosure provides a standalone
electrochemical material laminate structure for maintaining a major
surface of a battery active material layer in a substantially
unpassivated and/or substantially uncontaminated condition during
storage and/or battery cell component fabrication (e.g.,
fabrication of a fully solid-state laminate electrode
assembly).
[0123] In accordance with the present disclosure, the standalone
electrochemical material laminate structure is composed of two or
more continuous material layers, wherein at least one of the
material layers (i.e., a first material layer) is a "battery active
solid material layer" having a clean (i.e., substantially
uncontaminated) and/or substantially unpassivated first major
surface, and another material layer (i.e., a second material layer)
is a "protective material layer" that is inert, not battery active,
and removably covers, in direct contact, the first major surface of
the battery active material layer.
[0124] In various embodiments the battery active material layer is
highly reactive with water and/or oxygen, and its surfaces will
chemically degrade or passivate rather quickly, even under fairly
dry conditions of a dry Air room (e.g., having a dew point of
-20.degree. C.) or a dry argon filled glove box (e.g., having a low
moisture and oxygen content of between 1 to 5 ppm).
[0125] In accordance with the present disclosure the protective
material layer: i) minimizes, and preferably prevents, direct
touching exposure between the first major surface of the battery
active material layer and the ambient gaseous atmosphere or vacuum
environment about the layer (e.g., during handling, processing
and/or storage); ii) is inert in direct contact with the first
major surface; and iii) is readily removed without physically
damaging the surface. Accordingly, in various embodiments the
protective material layer is an inert liquid (e.g., a super dry
hydrocarbon liquid) that encapsulates the surface on which it is
applied, and may be evaporatively removed in the absence of solid
to solid touching contact.
[0126] In a first inventive embodiment, the battery active material
layer is an electroactive alkali metal layer having a substantially
unpassivated first major surface (e.g., a pristine lithium metal
layer), and in such embodiments the standalone electrochemical
material laminate structure is generally referred to herein as a
standalone alkali metal laminate structure; e.g., a standalone
lithium metal laminate structure. Preferably, the first major
surface is pristine.
[0127] In a second inventive embodiment, the battery active
material layer is an inorganic solid electrolyte layer (e.g., a
lithium ion conducting sulfide glass sheet), and in such
embodiments the standalone electrochemical material laminate
structure is generally referred to herein as a standalone solid
electrolyte laminate structure; e.g., a standalone sulfide glass
laminate structure. In various embodiments the sulfide glass layer
has a first major surface that is clean (i.e., substantially
uncontaminated).
[0128] The standalone electrochemical material laminate structure
of the present disclosure can be constructed using a number of
different architectures, some of which are described in more detail
herein below
[0129] With reference to FIGS. 2A-D and FIGS. 2E-H there are
illustrated cross sectional depictions of standalone
electrochemical material laminate structures in accordance with
various embodiments of the present disclosure. The main differences
between the structures shown in FIGS. 2A-D and those shown FIGS.
2E-H are the battery active material layer. Specifically, in FIGS.
2A-D the battery active material layer is lithium metal, and the
electrochemical material laminate structure is a lithium metal
laminate structure. In FIGS. 2E-H the battery active material layer
is a lithium ion conducting sulfide glass, and the electrochemical
material laminate structure is an inorganic solid electrolyte
laminate structure. The laminate structures may take on a variety
of shared architectures and these architectures are now described
with reference to a battery active material layer. Thereafter,
details particular to the lithium metal layer and to the sulfide
glass layer are provided.
[0130] With reference to FIG. 2A and FIG. 2E there are illustrated
fully encapsulated electrochemical material laminate structures
100A/200E in accordance with various embodiments of the present
disclosure. Structure 100A/200E is composed of: i) freestanding
battery active material layer 101/201 having first and second major
surfaces (101i/201i and 101ii/201ii) and lengthwise edge surfaces
(101iii/201iii and 101iv/201iv); and ii) inert liquid layer 102/202
encapsulating the major surfaces and the lengthwise edge surfaces
(e.g., a super dry liquid hydrocarbon layer). In various
embodiments inert liquid layer 102/202 is a super dry hydrocarbon
that fully wets out the first and second major opposing surfaces
and lengthwise edge surfaces (101i, 101ii, 101iii, and 101iv as
well as 201i, 201ii, 201iii, and 201iv).
[0131] With reference to FIG. 2B and FIG. 2F there is illustrated a
substrate supported electrochemical material laminate structure in
accordance with various embodiments of the present disclosure.
Structure 100B/200F is composed of battery active material layer
101/201 and material backing layer 103/203, which may be rigid or
flexible, in various embodiments layer 103/203 is a substrate onto
which the battery active material layer is formed, or it (the
backing layer) may be applied to second major surface 101ii/201ii
after layer 101/201 has already been formed. Inert liquid layer
102/202 encapsulates first major surface 101i/201i, and may
additionally encapsulate its lengthwise edge surfaces, as shown. In
various embodiments backing layer 103 extends beyond layer 101/201,
and the inert liquid wets out the lengthwise edges, as shown. In
various embodiments, backing layer 103/203 is electronically
irnsulating, and used generally as a supporting layer 101/201
during handling, storage and processing (e.g., as an interleave to
facilitate winding and unwinding). For example, when the battery
active material layer is sulfide glass solid electrolyte layer 201,
backing layer 103 may be an inert organic polymer (e.g., a
polyethylene or polypropylene film). In other embodiments, when the
battery active material layer is lithium metal layer 101, backing
layer 103 (flexible or rigid) may be electronically conductive, and
thereon serve as a current collector in a battery cell. For
instance, backing layer 103 may be a metal foil or mesh (e.g.,
copper), or it (backing layer 103) may be a thin copper film
deposited on a polymer support layer (e.g., a polyester film). When
hacking layer 103 is intended to serve as a current collector,
standalone electrochemical material laminate structure 100B is
sometimes referred to herein as having electrode architecture.
[0132] With reference to FIG. 2C and FIG. 2G there is illustrated
standalone electrochemical material layer structure 100C/200G,
which, in accordance with various embodiments of the present
disclosure has, what is termed herein, a wet-decal architecture,
and for this reason structure 100C/200G is sometimes referred to
herein more simply as a wet-decal or decal (e.g., Li-decal 100C or
sulfide glass decal 200G). Laminate structure 100C/200G includes
solid material release layer 104/204 covering but not touching
battery active material layer surface 101i/201i, and inert liquid
layer 102/202 sandwiched therebetween, and encapsulating the
surface on which it is applied (101i/201i).
[0133] Preferably, the inert liquid of layer 102/202 completely
wets out surface 101i/201i as well as the surface of release layer
104/204, and this leads to the formation of a liquid bridge between
the layers and an associated wet adhesive force that assists in
maintaining the release layer on the battery active material during
handling and processing. The degree of wettability may be
determined by the contact angle (.theta.). Accordingly, in various
embodiments one criterion that may be used for selecting the
protective liquid is based, in part, on its ability to fully wet
out the battery active material surface on which it is disposed. To
effect wetting the contact angle that the liquid makes with the
solid surface should be in the range of
0.degree..gtoreq..theta.<90.degree., and preferably .theta. is
near 0.degree. for complete wet out (.epsilon...gamma..,
.theta.=0.degree.). Preferably the ability of the inert liquid to
wet out both surface 101i/201i and layer 104/204 is sufficient to
spread the inert liquid layer evenly and intimately over surface
101i/201i, to encapsulate it (the first major surfaces) and prevent
the solid release layer from touching the battery active material.
Preferably, inert liquid layer 102/202 is thin enough to bring
about a tight liquid bridge that is capable of maintaining the
solid release on the battery active material during handling and
processing.
[0134] Continuing with reference to FIG. 2C and FIG. 2G, in various
embodiments the average thickness of protective liquid layer
102/202 is not greater than 50 um, or not greater than 25 .mu.m, or
not greater than 10 .mu.m, or not greater than 5 .mu.m, but
sufficiently thick and uniform, nonetheless, to prevent contact
between the release layer and surface 101i (e.g., 50
.mu.m>t>5 .mu.m; or 5 .mu.m>t>100 nm). In various
embodiments, inert liquid layer 102/202 has an average thickness in
the range of 1 .mu.m>t>100 nm; or in the range of 5
.mu.m>t>1 .mu.m; or in the range of 50 .mu.m>t>5 .mu.m.
However, the present disclosure is not limited as such, and it is
contemplated that structure 100C/200C may have pockets or isolated
locations that are not covered by protective liquid, and in such
embodiments, it is especially important that release layer 104/204
is inert in contact with the battery active material.
[0135] The wet decal architecture, as described above, has a number
of advantages, including: i) protecting surface 101i/102i against
physical damage during handling; ii) enhancing the utility and/or
the ability to use medium to high vapor pressure inert liquids by
lessening their effective evaporation rate; iii) improving
protection against degradation of surface 101i/201i against
impurity molecules from the ambient atmosphere, as the release
layer itself provides an additional barrier against contaminating
molecules entering the protective liquid from the ambient
atmosphere; iv) extending storage shelf life and service lifetimes
due to the additional barrier properties and lower evaporation rate
of the inert liquid layer; and finally v) the solid release layer
may serve as an interleave for winding or stacking the laminate
structures.
[0136] With reference to FIG. 2D and FIG. 2H, in various
embodiments the wet-decal architecture is sealed along its
lengthwise edges by seal 113/213, the seal providing an additional
barrier against diffusion of impurity molecules from the ambient
atmosphere seeping into the inert liquid layer and for minimizing
evaporation of the inert liquid out from the laminate. When sealed,
the lengthwise edges are preferably also covered in direct contact
with inert liquid. Lengthwise edge seal 113/213 may be made by heat
and pressure applied between release layer 104/204 and backing
layer 103/203, which, in various wet-decal embodiments is simply a
second release layer, similar or the same as layer 104/204. In
embodiments wherein structure 100D/200H includes current collector
layer 103, an additional sealable backing layer may be placed
behind the current collecting layer, for sealing the lengthwise
edges. During downstream processing, when the release layer needs
to be removed, the edge seal may be broken by slicing with a sharp
edge.
[0137] In various embodiments the laminate thickness, as measured
from the second major surface of the battery active material layer
101ii/201ii to the top surface of inert liquid layer 102/202 is no
greater than lmm thick, and more typically no greater than 500 um
thick. For instance, in various embodiments the laminate thickness
(as defined above) is less than 500 um, and typically less than 200
um, and in some embodiments less than 100 um, or less than 50 um
(e.g., between 5-100 um). The laminate thickness, as defined above,
does not include the thickness of the solid release layer, or
backing layer when present.
Liquid Phase Protective Fluid Layer
[0138] In accordance with the present disclosure one function of
protective material layer 102/202 (e.g., inert liquid layer) is to
removably cover and protect (e.g., encapsulate) at least the first
major surface of the battery active material layer, and thereon
provide a degree of protection against facile degradation caused by
direct exposure of the lithium metal layer or sulfide glass layer
to ambient gaseous atmospheres during handling, processing anollor
storage. By use of the term "removably cover and protect" when
describing the protective inert liquid layer it is meant that the
layer: i) covers the first surface of the battery active material
in a manner that sufficiently protects the surface against chemical
attack; ii) remains on the first surface during handling and
storage; and iii) can be controllably removed without damaging the
battery active material layer. By use of the term "controllably
remove" or "controllably removed" when referring to the protective
material layer it is meant that the laminate structure is
engineered to facilitate removal of the protective material layer
in a controlled fashion, and is otherwise not easily removed (e.g.,
by happenstance, such as incidental evaporation during handling and
processing of downstream components). Accordingly, the chemical
make-up and physical properties of the protective material layer is
properly selected to enable its controlled removal without damaging
the battery active material layer, and the laminate structure
engineered to ensure that the inert material layer stays intact as
a protective layer for the desired time frame.
[0139] In various embodiments protective material layer 102/202 is
an inert liquid that intimately covers and spans substantially the
first major surface of the battery active material layer (i.e., it
is a continuous inert liquid layer). Accordingly, in various
embodiments the composition of the inert liquid is selected, in
part, based on it having a lower surface energy than the battery
active material layer surface, and therefore capable of wetting out
the battery active first major surface, and, thus, intimately
covering it in direct contact, the liquid flowing and spreading out
evenly to span substantially the entire surface (i.e., encapsulate
the surface); e.g., encapsulate the first major surface.
[0140] Preferably inert liquid layer 102/202 readily wets the first
major surface of the battery active material layer. In various
embodiments, the wetting angle (.theta.) that the inert liquid
makes in contact with the battery active material layer is less
than 90.degree. (e.g., 0.gtoreq..theta.<90.degree.), preferably
less than 60.degree., more preferably less than 30.degree., even
more preferably .theta. is less than 10.degree., and yet even more
preferably about 0.degree.. Accordingly, in various embodiments,
the ability of the inert liquid layer to wet the battery active
material layer surface is sufficient to encapsulate the one or more
surfaces that it covers in direct contact.
[0141] Generally, the thickness of inert liquid layer 102/202 is
less than 1 mm. In embodiments the thickness of the continuous
inert liquid layer is in the range of 500 to 1000 um; or in the
range of 200 to 500 um; or in the range of 100 to 200 um; or in the
range of 50 to 100 um; or in the range of 20-50 um; or in the range
of 10-20 um or in the range of 5-10 um; or in the range of 1-5 um;
or, in some embodiments, it is contemplated that it may be less
than 1 um.
[0142] In various embodiments, in order to retain inert liquid
layer 102/202 on surface of the battery active material layer
during handling and processing, and controllably remove it (the
inert liquid layer) without imparting damage or leaving behind a
chemical residue, the inert liquid is selected based on a
combination of its vapor pressure and boiling point.
[0143] In various embodiments, in order to mitigate uncontrolled
evaporation of inert liquid layer 102/202, while facilitating its
controlled removal, the inert liquid of the protective material
layer (i.e., the inert liquid layer) is selected, in part, based on
having a room temperature vapor pressure in the range of 0.1-10
mmHg (e.g., 0.1-1 mmHg), and/or based, in part, on having a boiling
temperature in the range of 100-200.degree. C.
[0144] In various embodiments, the inert liquid of protective
material layer 102/202 is selected based on having a sufficiently
low vapor pressure at room temperature (e.g., less than 10 mmHg, or
less than 1 mmHg).
[0145] In various embodiments, the inert liquid of protective
material layer 102/202 is selected based on having a sufficiently
high boiling point temperature (e.g., greater than 100.degree. C.,
or greater than 150.degree. C. or greater than 200.degree. C.).
[0146] In various embodiments the inert liquid of protective
material layer 102/202 is selected based on having a room
temperature vapor pressure that is less than 10 mmHg and a boiling
point temperature greater than 100.degree. C.
[0147] In various embodiments protective material layer 102/202 is
composed of one or more inert hydrocarbon liquids (e.g.,
isododecane). Particularly suitable hydrocarbon liquids for use as
a protective material layer are saturated hydrocarbons (e.g.,
having a number of carbon atoms per molecule ranging from 5 to
15).
[0148] In various embodiments the inert hydrocarbon liquid is a
saturated hydrocarbon liquid.
[0149] In some embodiments the protective inert liquid saturated
hydrocarbon is a straight chain alkane (typically having between 5
and 15 carbon atoms per molecule), such as n-pentane, n-hexane,
n-heptane, n-octane, n-nonane, n-decane, n-undecane,
n-dodecane.
[0150] In some embodiments the protective inert liquid saturated
hydrocarbon is a branched chain alkane (typically having 5 to 15
carbon atoms per molecules), such as isopentane, isodecane,
isoheptane, isooctane, tetraethylmethane, isodecane,
3-methyldecane, isododecane.
[0151] In some embodiments the protective inert liquid saturated
hydrocarbon is a cycloalkane, such as cyclohexane, and
cycloheptane, cyclooctane.
[0152] In some embodiments the protective inert liquid hydrocarbon
is an unsaturated acyclic hydrocarbon (e.g., C.sub.nH.sub.2(n-m-1)
wherein n is the number of carbon atoms and m is the number of
double bonds), such as alkenes (e.g., 1-hexane, 1-octane, 1-nonene,
1-docene, 1-undecene, 1-dodecene, or alkadienes (e.g.,
1,5-hexadiene; 2,4-hexadiene; 1,6-heptadiene; 1,7-octadiene;
1,8-nonadiene; 1,9-decadiene; 1,10-undecadiene; and
1,11-dodecadiene.
[0153] In various embodiments the inert hydrocarbon liquid is an
unsaturated hydrocarbon liquid.
[0154] In some embodiments the protective inert liquid is an
unsaturated cyclic hydrocarbon (e.g., of the type
C.sub.nH.sub.2(n-m) wherein n is the number of carbon atoms and m
is the number of double bonds), such as cyclohexane, cycloheptane,
and cyclooctene).
[0155] In some embodiments the protective inert liquid is an
unsaturated cyclic hydrocarbon (e.g., one or more cycloalkadienes),
such as 1,3-cyclohexadiene; 1,4-cyclohexadiene;
1,3-cyclotreptadiene; and 1,3-cyclooctadiene).
[0156] Generally, protective inert liquid layer 102/202 is devoid
of dissolved and/or dispersed chemicals (e.g., salts, lubricants
and/or greases) that would coat the surface of the battery active
material layer with a solid film or leave behind a sticky residue.
Accordingly, the protective inert liquid layer is generally devoid
of dissolved salts (e.g., lithium salts, or more generally alkali
metal salts).
[0157] In order to be inert in direct contact with the battery
active material layer, the liquid hydrocarbon(s), and, more
generally, the protective inert liquid layer should have a very low
concentration of moisture. Preferably the concentration of moisture
in the inert liquid hydrocarbon layer is less than 10 ppm of water,
more preferably less than 5 ppm of water, even more preferably less
than 1 ppm of water, and yet even more preferably less than 0.1 ppm
of water (i.e., super dry). In various embodiments the inert liquid
is actively dried in the presence of sacrificial alkali metal
surfaces (e.g., pieces/chips of lithium metal) that getter oxygen,
water and nitrogen impurities. In various embodiments, the
cumulative area of the sacrificial alkali metal surfaces in direct
contact with the inert liquid is greater than the first major
surface of the battery active material layer on which the inert
liquid covers in direct contact, for instance, when the battery
active material layer is disposed in a protective liquid bath, as
described in more detail herein below.
Standalone Alkali Metal Laminate Structures
[0158] In accordance with the standalone electrochemical material
laminate structure embodiments described with reference to FIGS.
2A-D, the laminate structures 100A-D are alkali metal laminate
structures wherein battery active material layer 101 is an alkali
metal layer having substantially unpassivated first major surface
10E, and preferably surface 101i is pristine.
[0159] In various embodiments alkali metal layer 101 is a dense
alkali metal layer. In various embodiments it is a lithium metal
layer or sodium metal layer. It is also contemplated that the
alkali metal layer may be a lithium metal alloy or a sodium metal
alloy, which may include one or more of the following alloying
elements, including Ca, Mg, Sn, Ag, Zn, Bi, Al, Cd, Ga, In and Sb.
In various embodiments alkali metal layer 101 is a lithium metal
layer.
[0160] In various embodiments thickness of lithium metal layer 101
is typically no greater than 50 microns, and more typically no
greater than 25 microns (e.g., 50 .mu.m.gtoreq.t>30 .mu.m; or 30
.mu.m t.gtoreq.20 .mu.m; or 20 .mu.m.gtoreq.t>10 .mu.m; or 10
.mu.m.gtoreq.t.gtoreq.5 .mu.m). In some embodiments lithium metal
layer 101 is a thin film coating on a current collector having a
scant amount of lithium, with thickness no greater than 5 um thick,
and typically thinner, such as about 4 .mu.m or about 3 .mu.m or
about 2 .mu.m or about 1 .mu.m, or less than 1 .mu.m. (e.g., 5
.mu.m>t.gtoreq.0.1 .mu.m). For example, the thin film of lithium
metal may be coated by evaporation onto a copper current collector
in a vacuum chamber, and then prior to backfilling the chamber with
a dry inert gas, such as argon or helium, the first major surface
of the coated film is immersed in protective liquid or coated with
a layer of inert protective liquid.
[0161] In accordance with the present disclosure, in various
embodiments, lithium metal surface 101i is substantially
unpassivated and preferably pristine, as defined herein below. And
even more preferably, lithium metal surface 101i is 100%
unpassivated. Preferably, lithium metal surface 101i is 100%
unpassivated and molecularly or atomically clean.
[0162] Continuing with reference to the lithium metal laminate
structures described herein above with reference to FIGS. 2A-D, in
various embodiments first major surface 101i of lithium metal layer
101 is substantially unpassivated (or pristine), and is able to
remain substantially unpassivated (or pristine) for a duration of
at least 10 seconds, or at least 1 minute, or at least 5 minutes,
or at least 10 minutes when it (the laminate structure) is disposed
in a dry chamber having a water and oxygen content of about 1 to 10
ppm (e.g., about 5 ppm).
[0163] By use of the term "pristine surface" with reference to
alkali metal layer 101 (e.g., a lithium metal layer), it is meant a
substantially unpassivated lithium metal surface that is also
sufficiently clean to i) facilitate complete reactive bonding to an
opposing solid electrolyte layer, wherein the adherence created by
the complete bond is sufficiently strong to prevent mechanical
non-destructive release or delamination between the layers; and ii)
effectuate a sufficiently uncontaminated interface (with the solid
electrolyte layer) that is conductive to Li ions and does not
result in a prohibitively large interface resistance (preferably no
greater than 50.OMEGA.-cm.sup.2) between the alkali metal layer
(e.g., a lithium metal layer) and the solid electrolyte layer
(e.g., a sulfide glass layer).
[0164] By "substantially unpassivated" when referring to an alkali
metal layer surface (e.g., a lithium metal surface) it is meant
that the surface is predominately defined by a continuous
unpassivated and substantially unoxidized surface region that
accounts for at least 70% of the area of the referenced lithium
metal surface (e.g., first major surface 101i). When referring to a
lithium metal layer surface as pristine it is meant that the
continuous unpassivated and substantially unoxidized surface region
accounts for at least 90% of the area of the referenced lithium
metal surface, and preferably at least 95%, and even more
preferably the pristine surface is entirely unpassivated (i.e.,
100% of the surface is unpassivated). In various embodiments, as
described in more detail herein below, the substantially
unpassivated or pristine surface may contain a certain amount of
discrete passivated surface portions (i.e., passivated
islands).
[0165] By "sufficiently clean" when referring to the pristine
lithium metal surface, it is meant that the continuous unpassivated
and substantially unoxidized surface region, as described above, is
not poisoned by an unduly thick non-self-limiting surface-layer,
which, if otherwise present would preclude complete reactive
bonding and strong adherence to a reactive solid electrolyte layer
(e.g., as defined with respect to peel strength), and would degrade
electrochemical interface properties (e.g., as defined by interface
resistance, and uneven plating and stripping reactions).
Notwithstanding the preference to eliminate any poisoning of the
pristine surface, a minimal non-self-limiting surface-layer
covering the continuous unpassivated region may be acceptable, as
described in more detail herein below.
[0166] Top down and cross sectional depictions of alkali metal
layers (e.g., lithium metal layers) having pristine surfaces in
accordance with various embodiments of the present disclosure are
depicted in FIGS. 3A-D; and for comparison, passivated lithium
metal layer 3E-101 is depicted in FIG. 3E.
[0167] Briefly, in FIG. 3A, lithium metal layer 3A-101 is shown
having pristine surface 3A-101i that is 100% unpassivated, and
molecularly or atomically clean; in FIG. 3B, pristine surface
3B-101i of lithium metal layer 3B-101 contains a certain amount of
passivating islands 3B-160 dispersed on continuous unpassivated
region 3B-165; in FIG. 3C, the pristine surface of lithium metal
layer 3-101C is covered by minimal surface-layer 3C-181, which
defines the surface of its unpassivated region, and has an average
thickness that is preferably less than 10 nm; and in FIG. 3D
pristine surface 3D-101i includes passivating islands 23D-160 and
minimal surface-layer 3D-181 which defines the surface of its
unpassivated region. Prior to describing these embodiments in more
detail, it is instructive, for the purpose of comparison, to first
depict the make-up of a fully passivated lithium layer.
[0168] With reference to FIG. 3E, a depiction of fully passivated
lithium metal layer 3E-101 which may be a lithium metal foil that
was made by extrusion and/or roller reduction in a dry air, dry
oxygen and/or dry CO.sub.2 gaseous environment (e.g., dry air
room), or it (layer 3E-101) may be an evaporated thin lithium film
deposited on a current collector (not shown) under vacuum in a
chamber, and then breaking the vacuum by bleeding a stream of dry
air, dry oxygen and/or dry CO.sub.2 (e.g., dry air) into the
chamber. The exposure to dry air immediately upon making the
lithium foil/film results in the formation of passivation film
3E-179, which is a dense substantially self-limiting film of
lithium oxide, and it may be several hundred angstroms thick (e.g.,
about 500 A), or thicker, when formed in a dry room atmosphere
(i.e., dry air). The exact stoichiometry of the passivating film is
difficult to ascertain, and so is generally referred to as
Li.sub.2O.sub.x. Alternatively, if formed in the presence of dry
CO.sub.2 gas, the composition of the passivating film is primarily
lithium carbonate. By use of the term substantially self-limiting
it is meant that the passivating film, formed as such, is
sufficiently dense and thick to effectively block further reactions
and thereby mitigate subsequent film growth. For instance, lithium
passivating film 3E-179, once completely formed, is chemically
stable to exposure to dry room air unless subjected to an
atmosphere having a prohibitively high concentration of a reactive
impurity such as water, which is known to breakdown lithium
passivating films overtime.
[0169] With reference to FIG. 3-A, pristine surface 3A-101i of
lithium metal layer 3A-101 is 100% unpassivated and substantially
unoxidized, and absent of even a minimal surface-layer
contaminant.
[0170] With reference to FIG. 38, pristine surface 38-101i of
alkali metal layer 3B-101 contains passivated islands 3B-160
dispersed throughout continuous unpassivated and substantially
unoxidized surface region 3B-165. The cumulative area of the
islands is less than 10% of the total area of the first major
surface, and preferably the cumulative area is less than 5%, and
even more preferably less than 1%. Preferably, the area size of the
islands does not exceed 1 mm.sup.2, and more preferably does not
exceed 0.5 mm.sup.2, and even more preferably does not exceed 0.1
mm.sup.2. In certain embodiments the method of making alkali metal
layer 38-101 results in first major surface 38-101i that is
characterized as predominately unpassivated (as opposed to
pristine), wherein the area of continuous unpassivated region
38-165 accounts for less than 90%, but at least 70%, of the area of
first major surface 38-101i.
[0171] With reference to FIG. 3C, pristine surface 3C-101i of
alkali metal layer 3C-101 is defined, in part, by the presence of
non-self-limiting minimal surface-layer 3C-181 composed of an
ionically and/or covalently bonded compound which forms as a result
of alkali metal atoms of the continuous unpassivated region
oxidizing in contact with reactive impurity molecules derived from
the external environment about the alkali metal layer structure,
and especially oxygen, nitrogen and/or water impurities which may
be present in the ambient gas or ambient vacuum of the external
environment in which the alkali metal layer is formed, stored
and/or handled, and/or as impurities in the protective liquid in
which it (the pristine surface) is preserved. In various
embodiments, minimal surface-layer 3C-181 is a compound product of
the alkali metal atoms reacting with one or both of oxygen and
water present as an impurity, and generally derived from the
ambient gas of the external environment; for instance,
surface-layer 3C-181, an alkali metal oxyhydroxide compound (e.g.,
lithium oxyhydroxide). Minimal surface-layer 3C-181 is not
necessarily continuous as shown in FIG. 3C, and may be spread out
as discrete sections over the continuous unpassivated region. When
present, surface-layer 3C-181 is minimal and exceptionally thin,
having an average thickness that is less than 200 .ANG., and more
preferably less than 100 .ANG., and even more preferably less than
50 .ANG. or less than 40 .ANG. or less than 30 .ANG.. Even more
preferably, the pristine surface is characterized as molecularly
clean, which is to mean that the average thickness of surface-layer
3C-181 is less than 25 .ANG., and even more preferably the pristine
surface is atomically clean, with surface-layer 3C-181 181 having
an average thickness of less than 10 .ANG..
[0172] With reference to FIG. 3D, lithium metal layer 3D-101 has
pristine surface 3D-101i which is similar to that shown in FIG. 3C
in that the unpassivated surface region is defined by a minimal
surface-layer 3D-181, similar to 3C-181 (as described above and
shown in FIG. 3C), but also containing passivating islands 3D-160,
similar to the passivating islands described above with reference
to FIG. 3B.
Methods of Making Pristine Lithium Metal Layers and Lithium Metal
Layers Having Substantially Unpassivated Surfaces
[0173] As described above, the present disclosure provides methods
and apparatus' for making lithium metal layers having substantially
unpassivated and preferably pristine surfaces, and, in particular,
for making lithium metal layers wherein at least one major surface
is maintained in its pristine or substantially unpassivated
condition under, or immersed in, a protective fluid (e.g., a
protective liquid).
[0174] With reference to FIGS. 4A-D there are illustrated
apparatus' 400A-D for the manufacture of lithium metal layer 101,
having first and second major opposing surfaces 101i/101ii, wherein
at least first surface 101i. Is formed in direct contact with
protective fluid 102 (e.g., super dry inert hydocarbon liquid,
vapor or combination thereof), and therewith surfaces 101i and
101ii are substantially unpassivated, and in some embodiments
pristine.
[0175] Apparatus' 400A-D may be divided into two main sections or
regions. First section 410i (typically a staging section) is where
the initial stock of lithium metal 430 (e.g., an ingot or foil of
lithium) is positioned for entry or disposition into second section
410ii (surface generating section), and, in particular, surface
forming chatAber 450 wherein lithium layer 101 and/or its pristine
first surface 101i (and optionally 101i) are formed in direct
contact with protective fluid 402 (e.g., super dry inert
hydrocarbon liquid as described above). Chamber 450 includes
enclosure 451, and is equipped with surface forming device 452, and
interior environmental controls not shown. Once created, as-formed
lithium layer 101 may be wound and/or stored in protective liquid
of the same or different composition as that in which the layer
itself (or at least its first surface) was generated. As shown in
FIG. 4A, as formed lithium layer 101 is wound to form lithium roll
401-R. The winding may be performed inside chatAber 450 (as shown),
or lithium layer 101 may be fed to a separate downstream chamber
for subsequent winding and storage in roll form.
[0176] In various embodiments, a lithium decal (as shown in FIG.
2D) may be formed by interleaving one or a pair of solid release
layers (e.g., a polyolefin sheet or film) into the roll during
winding. As described above, in a lithium decal of the present
discosure, the solid release layer is positioned on the first
and/or second major surface where it keeps the inert liquid in
place, ensures that the liquid spreads evenly over surface 101i,
mitigates evaporative losses because it (the solid release)
enhances barrier properties, provides physical protection against
contact damage, enables the use of protective liquids having
relatively high vapor pressures, and serves as an interleave when
stacking or rolling the layer(s) to avoid sticking. Once the decal
is wound, surface 101i is encapsulated by a protective liquid
layer, and in some embodiments the liquid may be caused to form a
sheath about the layer, which encapsulates both first and second
surfaces.
[0177] With reference to FIGS. 4A-B and FIG. 4D, in various
embodiments, both first and second major opposing surfaces (101i
and 101ii; see figure inserts) are formed in direct contact with
protective liquid by action of surface forming device 452 having
surface forming component(s) 456a/b that directly contact lithium
metal layer 101 as it forms. As shown, surface forming device 452
may be a roller reduction mill that reduces thickness of the
lithium metal layer and in so doing produces substantially
unpassivated lithium surfaces by extruding initial stock 430, or
lithium layer 405 (as shown in FIG. 4A), between rollers 456a/b.
When roller reducing a lithium metal foil, the area of the new
surface created is proportional to the decrease in thickness.
[0178] Surface forming device 452 contacts protective liquid 402
such that as lithium metal layer 101 is formed, or surface 101i
and/or surface 101i is created, the as-formed surfaces
substantially instantaneously become immersed in protective fluid
(e.g., inert liquid). Once the layer is formed, the inert liquid is
caused to remain on the freshly created lithium layer surfaces
(e.g., by using a solid release layer on that surface), typically
fully encompassing (i.e., encapsulating) the surface, and thereon
protecting it (the pristine surface) from direct contact with
lithium reactive constituents that may be present as contaminats in
of the ambient environment about the layer. In various embodiments,
the protective fluid in which pristine lithium metal surface 101a
is formed may be exchanged with protective fluid having a different
composition for downstream processing and/or storage. For instance,
surface 101i formed in or under a first protective liquid having a
first vapor pressure or boiling point and that first inert liquid
is replaced by a second inert liquid having a second vapor pressure
or boiling point (e.g., the second liquid having a higher vapor
pressure and lower boiling point than the first liquid, or
vice-versa).
[0179] In various embodiments, surface forming device 452 is fully,
or at least partially, immersed in protective fluid 402. For
instance, active surface forming component 456, may be fully
submerged or encompassed inside a bath of protective liquid. To
contain protective liquid 102, surface generating section 410ii
includes enclosure 451 (e.g., an environmental chamber). In various
embodiments, the surface forming device, and in particular its
surface forming components, are also housed in the enclosure.
[0180] In various embodiments protective fluid 402 is a liquid at
room temperature 18.degree. C. to 25.degree. C.) and standard
pressure (1 atm), and is primarily contained in the enclosure as a
liquid. In various embodiments the interior environment of the
enclosure is substantially filled by inert liquid, and as described
above, and in more detail herein below, in various embodiments
surface forming component 456 is immersed in the inert liquid phase
protective fluid, and specficially that portion of the surface
forming component which directly contacts lithium metal surface
101i is immersed in the liquid phase. Accordingly, surface 101i, or
both surfaces 101i and 101bii, are formed in direct contact with
liquid phase protective fluid, and preferably the as-formed
surfaces are fully encompassedlencapsulated by the liquid phase,
and as such the surfaces are formed in the absence of direct
contact with a gaseous phase environment (e.g., dry air or an inert
gas phase environment, including one or more noble gases), and thus
also not formed in a vacuum environment. For instance, the lithium
metal layer and/or its associated surfaces are fully formed
immersed in a protective liquid. For example, formed inside a bath
of protective liquid or inside a chamber filled with protective
vapor of an inert liquid.
[0181] As described in more detail herein below, once formed within
the protective liquid, lithium metal layer 101, or its first and/or
second major surface(s) 101i/101ii are maintained in the protective
liquid for subesequent winding to form a roll of lithium metal foil
101-R (typically on a spool) and/or storage. By this expedient,
as-formed lithium metal layer 101, and/or surface 101i, or both
surfaces 101i and 101ii, have never been exposed to a gaseous phase
environment or to a vacuum environment. In such embodiments, the
lithium metal foil and its associated pristine surfaces, are
formed, and thereafter stored in a pristine state, never exposed in
direct contact with a gaseous atmosphere. For example, the foils so
formed are maintained pristine during storage inside a bath of
protective liquid for more than 24 hours, or more than 1 week, or
more than 1 month. The pristine foils may then be sold and/or
transported as such to a facility for manufacture of downstream
battery cell components, including solid-state electrode laminates
and battery cells of the present disclosure. In various embodiments
the lithium foils are stored under protective liquid, and are
preferably never been exposed in direct contact with gaseous
atmospheres, including dry noble gases such as dry argon gas, or
dry Helium gas, or some combination thereof, or even dry air (i.e.,
air having a very low moisture content, such as that typical of a
dry room). When rolled with a solid release layer, the release
removably covers and protects the substantially unpassivated
lithium metal surface 101i, and optionally its opposing surface
101ii, When a solid release is used the inert liquid layer is
formed and sandwiched between the solid release layer and the
lithium metal laver, and this laminate structure is sometimes
referred to herein as a wet-decal architecture, or more simply a
wet-decal. Preferably, the inert liquid is capable of wetting out
both the lihtium metal surface and the release layer.
[0182] In alternative embodiments the interior environment of
chamber 450 is primarily composed of protective fluid as a vapor.
In such embodiments, the vapor molecules may condense on the
as-formed lithium metal surfaces. When a vapor phase protective
fluid is used, the enclosure is typically vacuum evacuated,
followed by evaporating the protective liquid inside the chamber to
form the inert vapor. Notably, when referring to vapor phase
protective fluid it is not meant a noble gas such as argon or
Helium, or the like. By protective fluid in the vapor phase it is
meant vapor of the inert liquid.
[0183] With reference to FIG. 4A there is illustrated apparatus
400A for making pristine lithium metal layer 101 in protective
fluid 402; for example, a super dry liquid hydrocarbon. With
particular reference to FIG. 4A, initial lithium metal stock 430
(e.g., a lithium ingot) is extruded via die press 440 to form
relatively thick freshly extruded lithium layer 405 (typically in
the range of 75 to 500 um thick). Specifically, lithium ingot 430
is loaded and pressed against extrusion die 444 via plunger 442 and
die plate 443, as is known in the art for making extruded lithium
foil from lithium ingots in a gaseous dry room atmosphere.
[0184] As-formed, layer 405 is generally substantially upassivated
and preferably pristine upon exiting die 444. If formed in direct
contact with a gaseous dry room environment the freshly made
lithium metal surface would immediately start chemically reacting
with the oxygen and carbon dioxide in the dry room, which would
passivate the exposed surfaces. With respect to various embodiments
of the present disclosure, because layer 405 is formed direcly in
protective liquid 102, its major opposing surfaces 105a/105b are
fully covered in direct contact with protective liquid 102
substantially immediately upon formation (e.g., in less than one
second). In the instant embodiment, thickness of layer 405 is
reduced in a subsequent roll reduction step, as shown in section
410ii of FIG. 4A. Once formed, layer 405 is caused (e.g., by a
pulling tension) to enter roll reduction device 452, which can be a
rolling mill having reduction work rolls 456a/456b, both of which
are immersed in protective. liquid inside enclosure 451. Work rolls
456a-b may be made of compatible metal or plastic (e.g.,
polyacetal), or plastic coated metal rolls. Because the work rolls
are immersed in protective hydrocarbon liquid, the issue of lithium
metal sticking to the rolls is mitigated. In various embodiments
roll reduction reduces the lithium layer down to a thickness of no
greater than 50 um. Thin lithium metal layer 101 is formed upon
exiting the roller mill; the roller reduction step effectively
transforms pristine lithium layer 405 (e.g., 500 um thick) to
thinner layer 101 having fresh surfaces 101i and 101ii formed in
direct contact with protective liquid 402. Once formed, layer 101
may be transferred from chamber 450 to a distinct/discrete winding
chamber, or the winding device may be incorporated in chamber 450,
and layer 101 subsequently wound to yield lithium foil roll 401-R,
which, in its wound condition, remains directly exposed in contact
with protective liquid (e.g., the protective liquid forming a thin
layer of liquid between the lithium metal layer and a solid release
layer, not shown). As described in more detail herein below, and
with reference to a lithium roll package assembly of the present
disclosure, wound roll 401-R may be stored in a functional canister
containing protective liquid of the same or different composition
as that of protective liquid 402, and a sealable port for ease of
dispensing the lithium layer during battery cell or battery cell
component manufacture. In various embodiments a solid release layer
is positioned on the substantially unpassivated lithium surface
(e.g., during winding or stacking), and the laminate structure so
formed has, what is termed herein, a wet-decal architecture as
described in more detail herein below.
[0185] Continuing with reference to FIGS. 4A-D, in various
embodiments lithium metal layer 101 is a thin lithium metal layer,
typically of thickness no greater than 50 .mu.m, and more typically
no greater than 25 .mu.m (e.g., the thickness (t) of layer 101 is
in the range of: 25 .mu.m.gtoreq.t>20 .mu.m; or 20
.mu.m.gtoreq.t>15 .mu.m; or 15 .mu.m.gtoreq.t>10 .mu.m; or 10
.mu.m .gtoreq.t>5 .mu.m). The standalone lithium metal layer may
be self-supporting (if thicker than about 20 .mu.m) or supported on
a substrate layer. As described in more detail herein below, in
various embodiments the lithium metal layer may be supported on a
thin substrate layer that also serves as a current collector, the
combination of current collector and thin lithium metal layer is
sometimes referred to herein as having an electrode
architecture.
[0186] As shown in FIG. 4B, in an alternative embodiment, initial
lithium stock 430 may be a continuous foil of lithium (e.g., in the
form of wound roll 430-R). As stock 430 is already in foil form, it
may be contained inside a chamber that is configured for entry into
chamber 450 via portal 455, or the layer may be exposed to the
ambient external environment about chamber 450 (e.g., a dry box or
dry room environemnt), and in this instance the stock layer would
have passivated surfaces. In operation, stock foil 430 is unwound
and caused, by pulling tension, to extrude through work rolls
456a/b immersed in protective liquid 402. As described above, once
foil 430 is extruded through roller reduction mill. 452, it is
wound in a similar fashion as described above, to form lithium roll
401-R immersed in protective liquid. In various embodiments stock
lithium foil 130 may be pre-passivated (e.g., by exposing its
surfaces to dry CO.sub.2), and by this expedient improve
reproducibility of the surface conditon of the initial stock
foil.
[0187] As shown in FIG. 4C, in yet another alternative embodiment
stock foil 430 may be surface treated inside chamber 450 to expose
a fresh lithium surface in direct contact with protective fluid 402
(e.g., ground with an abrasive element such as a brush or rough
polymeric sheet). For instance, surface forming device 456 (e.g.,
an abrasive brush) may be positioned over stock foil 430 as it
enters the chamber, and caused to engage with a surface of stock
layer 430 to form pristine layer 101 and its associated pristine
surface 101i. In this embodiment the stock foil does not undergo a
significant reduction in thickness, as the transformation of the
foil from stock 430 to pristine layer 101 is based on forming
pristine surface 101i in direct contact with protective fluid 402
(e.g., liquid phase, vapor phase, or both). As shown in FIG. 4C, in
various embodiments the stock may be a laminate of lithium layer
430 and a. current collecting layer 461 in direct contact with the
second surface of layer 430. In other embodiments, the stock is a
lithium foil, and one or both surfaces are formed in the protective
fluid, (e.g., by brushing/grinding).
[0188] With reference to FIG. 4D there is illustrated yet another
alternative apparatus for making pristing lithium metal layer in
the presence of protective fluid, and in accordance with the
instant disclosure. The apparatus is similar to that described
above for fresh surfaces produced by roll reduction, except in this
embodiment the work rolls 456a/b are positioned at the interface
between the staging section 110i and surface forming section 110ii.
Lithium stock foil 430 is configured for entry into the chamber via
roller mill 455. In particular, work rolls 456a/b effectively
provide the portal into chamber 450, and the protective liquid is
distributed to completely cover the freshly extruded surfaces
(e.g., by spraying the inert liquid from nozzles 457 onto one or
both surfaces 101i/ii). Chamber 450 may be held under a dynamic
vacuum with the protective fluid, in vapor form, or the chamber
environment may be a combination of protective fluid in vapor form
(i.e., protective vapor) and a dry noble gas such as argon or
helium.
[0189] As described above, in various embodiments protective fluid
402 is a liquid. In sonic embodiments the interior environment of
the chamber is held under a dynamic vacuum with protective fluid in
the vapor phase. In some embodiments the protective fluid is
present in the chamber in both the vapor and liquid phases. In some
embodiments the chamber is substantially filled with liquid phase
protective fluid (e.g., more than 90% of chamber volume is
accounted for by protective liquid). Generally the protective fluid
is a hydrocarbon composed of one or snore hydrocarbon molecules
that do not react in direct contact with lithium atoms.
[0190] With reference to FIG. 4E there is illustrated another
embodiment in accordance with the instant disclosure for a process
and apparatus 400E for fabricating pristine lithium metal layer 101
using a series of roller reduction mills (e.g., two or more).
Apparatus 400E is generally disposed in a closed environmentally
controlled chamber, similar or the same as chamber 451, as
described above. Liquid phase protective fluid 402 is applied
directly onto the major opposing surfaces of lithium stock 430
(e.g., by dripping or spraying), and is configured for extrusion
rolling (i.e., roller reduction). Care should be taken to ensure
that the major surfaces are entirely covered with protective liquid
throughout the process. Additionally, protective liquid 402 is
dispensed from fluid reservoir 432 for application directly onto
work roll pairs 456a/456b and 456c/456d. A further application of
the protective liquid is dispensed onto surface 101i of the
as-formed lithium metal layer 101 to ensure that the entirety of
that surface is coated with a sufficient amount of protective
liquid layer 102 to encapsulate the surfaces and provide sufficient
protection for conveyance of the lithium foil 101 downstream for
laminating processes, or for disposition into a canister for
storage as a Li roll package assembly, as described below with
reference to FIG. 6.
[0191] With reference to FIG. 4F there is illustrated top down
views and cross sectional views qualitatively depicting the
evolution of a lithium surface resulting from multiple roll
reduction steps performed in protective liquid in accordance with
various embodiments of the present disclosure. The initial lithium
foil is stock and may be pre-passivated as shown (e.g., by
treatment with carbon dioxide on its surface to form a lithium
carbonate passivation layer). After the first roll reduction, the
lithium thickness is reduced (as shown in the cross section
depiction), and the lithium carbonate passivating layer has been
broken apart to expose fresh lithium metal surfaces and scattered
passivated islands. Because the steps are performed in protective
liquid, and the lithium metal layer is maintained covered in
protective liquid throughout the entire process, the freshly formed
surfaces can remain unpassivted. With each consecutive roll
reduction the thickness of the layer decreases and the area of the
unpassivated surface region increases (also the passivated islands
become smaller in size and area). As noted above, the decrease in
lithium thickness is proportional to the increase in the
unpassivated surface region. Accordingly, in various embodiments
the method of making a thin lithium metal layer having a pristine
surface includes: i) determining a final lithium metal layer
thickness: determining the thickness of the stock of pre-passivated
lithium metal layer necessary to create a pristine surface (i.e.,
at least 90% of the surface is defined by the unpassivated surface
region); roll reduce the stock lithium metal foil under protective
liquid. For instance, if the desired lithium metal thickness is 25
um, starting with a 50 um passivated lithium foil will produce a
surface that is just 50% passivated and 50% unpassivated, which is
insufficient for forming a pristine first major surface. To create
a pristine lithium metal layer that is 25 um thick from
pre-passivated lithium metal foil requires that the stock foil be
at least 250 um. thick.
[0192] With reference to FIG. 4G, stock lithium foil 430 may be
simultaneously roller extruded and laminated to substrate layer 490
(e.g., a copper current collecting layer) using roller reduction
mill 452 equipped with fluid dispensing reservoir 432 and work
rolls 456a/b as described above. Once processed, laminate structure
100B (as described with referenece to FIG. 1B), has an electrode
architecture that is composed of lithium metal layer 101 laminated
with copper current collector 490F as the backing layer behind
second major surface 101ii, First major surface of layer 101 is
entirely covered, in direct contact, with liquid phase protective
fluid 102 (i. e., it is encapsulated). As-formed, laminate 100B may
be subsequently wound and disposed into canister *** (as shown in
FIG. 5) to form laminate roll package assembly for storage and
ultimately downstream production of a lithium battery cell. In
various embodiments the lithium metal layer may be roller extruded
directly onto an inorganic solid electrolyte layer serving as
substrate, such as a lithium ion conducting sulfide glass layer,
the roll extrusion exposing substantialy unpassivated lithium metal
directly onto the sulfide glass to effect a reactive bond between
the layers.
[0193] In accordance with the methods and apparatus' shown in FIGS.
4A-F, the process steps of: i) roller reducing the thickness of
stock lithium metal foil; ii) forming freshly extruded lithium
metal surfaces; iii) and laminating the second major surface 101b
to a copper current collector, may be performed in a conventional
dry box or dry chamber having a noble gas atmosphere (e.g., argon
or helium), with the interior environment of the dry box at low
moisture content, preferably less than 10 ppm water, more
preferably less than 5 ppm, even more preferably less than 1 ppm,
and yet even more preferably less than 0.1 ppm. However, the
embodiment is not limited to the apparatus being disposed in a
conventional dry box, and in a manner similar to that shown in
FIGS. 4A-D, apparatus' 400E/400F may be configured inside art
environmenally controlled chamber, similar to that of chamber 450,
with an interior atmosphere primarily composed of protective fluid
(e.g., protective vapor).
[0194] With reference to FIGS. 5A-B there is illustrated a lithium
metal roll assembly cartridge 500 (sometimes referred to herein as
a lithium roll assembly package) in accordance with various
embodiments of the present disclosure. Cartridge 500 includes Li
decal laminate 100C in roll form 100C-Roll, and entirely immersed
in protective inert liquid 502, which is iteself contained in
cannister 571. The cartridge also includes sealable port 572 and
associated sealing cap 573. FIG. 5A shows cartridge 500 in an
hermetically closed state. FIG. 5B illustrates a mechanism for
removing Li-decal laminate 100C from the cannister, via sealable
port 572, with sealing cap 573 configured to assist in dispensing
the decal out of the cannister. Cartridge 500 is suitable for
storing the decal over extended time periods, including hours,
days, or even weeks. The interior volume of cannister 571 is
substantially enitrely filled with protective liquid, and may
include moisture and oxygen gettering material, such as high
surface area lithium metal in the form of numerbable metal pieces
immersed in the protective liquid.
[0195] Preferably cartridge 500 is sufficiently hermetic, and the
protective liquid sufficiently dry (e.g., super dry), that lithium
metal layer 101 is able to maintain its substantially unpassivated
or pristine surface condition for at least 60 minutes, or at least
5 hours, or at least 10 hours, or at least 24 hours, or at least
several days, weeks, or months (e.g., more than 3 days, more than 7
days, or more than 30 days).
Standalone Solid Electrolyte Laminate Structures
[0196] In accordance with the standalone electrochemical material
laminate structure embodiments described with reference to FIGS.
2E-H, in various embodiments battery active material layer 201 is
an inorganic alkali metal ion conducting solid electrolyte layer,
and the laminate structure in such embodiments is referred to
herein as an inorganic solid electrolyte laminate structure (e.g.,
a lithium ion conducting sulfide glass laminate structure). The
room temperature alkali metal ion conductivity of the inorganic
solid electrolyte layer is at least 10.sup.-6 S/cm, preferably at
least 10.sup.-5 S/cm, and even more preferably at least 10.sup.-4
S/cm (e.g., between 10.sup.-3 S/cm and 10.sup.-4 S/cm or between
10.sup.-4 S/cm and 10.sup.-3 S/cm), with room temperature defined
as 18.degree. C.-25.degree. C.
[0197] Continuing with reference to FIG. 2E-H in various
embodiments inorganic alkali metal ion conductive solid electrolyte
layer 201 is an inorganic lithium ion conductive solid electrolyte
layer. In particular embodiments the inorganic lithium ion
conductive solid electrolyte layer is an inorganic glass. In
embodiments it is an oxide glass (in the absence of sulfur). In
various embodiments inorganic solid electrolyte layer 201 is an
lithium ion conductive sulfide glass. In various embodiments the
inorganic solid electrolyte layer is moisture sensitive and
chemically reacts in contact with water, and in particular the
surface of the solid electrolyte layer degrades in the presence of
the ambient atmosphere of a dry room (e.g., having a dew point at
or below -20.degree. C.) or that of a dry argon glove box (e.g.,
having between 0.1 to 10 ppm of water). In various embodiments,
solid electrolyte layer 201 is a moisture sensitive Li ion
conductive sulfide glass comprising lithium, sulfur and one or more
of boron, silicon, and/or phosphorous. Particular sulfide solid
electrolyte glasses that can benefit from incorporation into a
solid electrolyte laminate structure of the present disclosure
include those described in U.S. Patent Publication No.:
20160190640, which is hereby incorporated by reference for all that
it contains; for example:
0.7Li.sub.2S-0.29P.sub.2S.sub.5-0.01P.sub.2O.sub.5;
0.7Li.sub.2S-0.28P.sub.2S.sub.5-0.02P.sub.2O.sub.5;
0.7Li.sub.2S-0.27P.sub.2S.sub.5-0.03P.sub.2O.sub.5;
0.7Li.sub.2S-0.26P.sub.2S.sub.5-0.04P.sub.2O.sub.5;
0.7Li.sub.2S-0.25P.sub.2S.sub.5-0.05P.sub.2O.sub.5;
0.7Li.sub.2S-0.24P.sub.2S.sub.5-0.06P.sub.2O.sub.5;
0.7Li.sub.2S-0.23P.sub.2S.sub.5-0.07P.sub.2O.sub.5;
0.7Li.sub.2S.sub.5S-0.22P.sub.2S.sub.5-0.08P.sub.2O.sub.5;
0.7Li.sub.2S-0.21P.sub.2S.sub.5-0.09P.sub.2O.sub.5;
0.7Li.sub.2S-0.2P.sub.2S.sub.5-0.1P.sub.2O.sub.5;
0.7Li.sub.2S-0.29B.sub.2S.sub.3-0.01B.sub.2O.sub.3;
0.7Li.sub.2S-0.28B.sub.2S.sub.3-0.02B.sub.2O.sub.3;
0.7Li.sub.2S-0.27 B.sub.2S.sub.3-0.03B.sub.2O.sub.3;
0.7Li.sub.2S-0.26B.sub.2S.sub.3-0.04B.sub.2O.sub.3;
0.7Li.sub.2S-0.25B.sub.2S.sub.3-0.05B.sub.2O.sub.3;
0.7Li.sub.2S-0.24 B.sub.2S.sub.3-0.06B.sub.2O.sub.3;
0.7Li.sub.2S-0.23B.sub.2S.sub.3-0.07B.sub.2O.sub.3;
0.7Li.sub.2S-0.22B.sub.2S.sub.3-0.08B.sub.2O.sub.3;
0.7Li.sub.2S-0.21 B.sub.2S.sub.3-0.09B.sub.2O.sub.3;
0.7Li.sub.2S-0.20B.sub.2S.sub.3-0.1B.sub.2O.sub.3;
0.7Li.sub.2S-0.29B.sub.2S.sub.3-0.01P.sub.2O.sub.5;
0.7Li.sub.2S-0.28 B.sub.2S.sub.3-0.02P.sub.2O.sub.5;
0.7Li.sub.2S-0.27B.sub.2S.sub.3-0.03P.sub.2O.sub.5;
0.7Li.sub.2S-0.26 B.sub.2S.sub.3-0.04P.sub.2O.sub.5;
0.7Li.sub.2S-0.25 B.sub.2S.sub.3-0.05P.sub.2O.sub.5;
0.7Li.sub.2S-0.24B.sub.2S.sub.3-0.06P.sub.2O.sub.5;
0.7Li.sub.2S-0.23B.sub.2S.sub.3-0.07P.sub.2O.sub.5;
0.7Li.sub.2S-0.22 B.sub.2S.sub.3-0.08P.sub.2O.sub.5;
0.7Li.sub.2S-0.21B.sub.2S.sub.3-0.09P.sub.2O.sub.5;
0.7Li.sub.2S-0.20B.sub.2S.sub.3-0.1P.sub.2O.sub.5;
0.7Li.sub.2S-0.29 B.sub.2S.sub.3-0.01SiS.sub.2;
0.7Li.sub.2S-0.28B.sub.2S.sub.3-0.02SiS.sub.2; 0.7Li.sub.2S-0.27
B.sub.2S.sub.3-0.03SiS.sub.2; 0.7Li.sub.2S-0.26
B.sub.2S.sub.3-0.04SiS.sub.2;
0.7Li.sub.2S-0.25B.sub.2S.sub.3-0.05SiS.sub.2; 0.7Li.sub.2S-0.24
B.sub.2S.sub.3-0.06SiS.sub.2; 0.7Li.sub.2S-0.23
B.sub.2S.sub.3-0.07SiS.sub.2;
0.7Li.sub.2S-0.22B.sub.2S.sub.3-0.08SiS.sub.2;
0.7Li.sub.2S-0.21B.sub.2S.sub.3-0.09SiS.sub.2;
0.7Li.sub.2S-0.20B.sub.2S.sub.3-0.1SiS.sub.2.
[0198] In other embodiments inorganic solid electrolyte layer 201
is a polycrystalline ceramic or a glass-ceramic layer (e.g., a
garnet solid electrolyte layer). These include
Li.sub.6BaLa.sub.2Ta.sub.2O.sub.12;
Li.sub.7La.sub.3Zr.sub.2O.sub.12, Li.sub.5La.sub.3Nb.sub.2O.sub.12,
Li.sub.5La.sub.3M.sub.2O.sub.12 (M.dbd.Nb,
Ta)Li.sub.7+xA.sub.xLa.sub.3-xZr.sub.2O.sub.12 where A may be Zn.
These materials and methods for making them are described in U.S.
Patent Application Pub. No.: 2007/0148533 (application Ser. No.
10/591,714) and is hereby incorporated by reference in its entirety
and suitable garnet like structures, are described in International
Patent Application Pub. No.: WO/2009/003695 which is hereby
incorporated by reference for all that it contains. Suitable
ceramic ion active metal ion conductors are described, for example,
in U.S. Pat. No. 4,985,317 to Adachi et al., incorporated by
reference herein in its entirety and for all purposes.
LiM.sub.2(PO.sub.4).sub.3 where M may be Ti, Zr, Hf, Ge) and
related compositions such as Li those into which certain ion
substitutions are made including
Li.sub.1+xTi.sub.2-xAl.sub.x(PO.sub.4).sub.3 and the like which are
known in the lithium battery arts.
[0199] Generally, the thickness of the inorganic sold electrolyte
layer is in a range that is sensible for use in a battery cell, and
generally depends, in part, on its ionic conductivity. In various
embodiments the thickness of the solid electrolyte layer is in the
range of 200-1 um thick, and more typically in the range of 100-5
.mu.m, and even more typically in the range of 50-10 .mu.m thick
(e.g., about 10 .mu.m or about 15 .mu.m or about 20 .mu.m or about
25 .mu.m or about 30 .mu.m or about 35 .mu.m or about 40 .mu.m or
about 45 .mu.m or about 50 .mu.m thick).
[0200] Solid Electrolyte Interphase (Engineered SEI)
[0201] With reference to FIG. 6A, there is illustrated an apparatus
600 and method for cleaning a sulfide solid electrolyte glass layer
and treating its surface to engineer a solid electrolyte interphase
(SEI). The apparatus includes environmental chamber 650 having a
very low moisture and oxygen content (e.g., less than 1 ppm),
supply roll 605-R of sulfide glass sheet in roll form, web carrier
for translating sheet 201 through cleaning chamber 620 and surface
treatment chamber 630. Cleaning chamber 620 is a plasma treatment
chamber for ion etching the glass under argon plasma. The
ion-etching/plasma etching step removes products of sulfide glass
hydrolysis by etching off a thin layer of glass from the surface,
typically in the range of 0.5 to 10 nm. Once surface 2011 has been
etched clean, it may be brought substantially immediately into
cartridge 680 which is canister 681 filled with super dry
hydrocarbon protective liquid 602, as described and listed above.
Cartridge 680 receives the cleaned glass by rolling to form sulfide
glass roll 610-R. Once immersed in the protective liquid, the
cleaned surface can be preserved as such. Cartridge 680 is suitable
for storing the decal over extended time periods, including hours,
days, or even weeks. The interior volume of canister 571 is
substantially entirely filled with protective liquid, and may
include moisture and oxygen getter* material, such as high surface
area lithium metal in the form of numerous metal pieces immersed in
the protective liquid,
[0202] In various embodiments the sulfide glass surface 201i is not
chemically compatible in contact with lithium metal, and so
coatings on the glass surface are described herein which are useful
for creating a solid electrolyte interphase (SEI), the SRI forming
as result of the coating reacting With the substantially
unpassivated lithium metal surface during the step of reactive
bonding e.g., during lamination of the layers, typically using heat
and pressure).
[0203] In various embodiments, after ion etching, sulfide glass
layer 201 is translated via the carrier web into surface treating
chamber 630. In various embodiments surface treating chamber 630 is
a second plasma unit, and glass 201 is subjected to nitrogen plasma
and/or a nitrogen/argon plasma mixture, the process cleans the
glass and also modifys the glass surface composition by introducing
nitrogen into/onto the surface. Thereafter, the glass is wound into
roll 610-R and immersed in protective liquid 602, as described
above. In alternative embodiments, as opposed to bringing the
cleaned and nitrogen treated glass into protective fluid (e.g.,
liquid or vapor phase), it is stored in a dry oxygen free argon
filled enclosure.
[0204] Continuing with reference to FIG. 6A, in another embodiment,
protective liquid 602 contains dissolved reactive species such as
nitrogen and Halogens (e.g., iodine), which treast the glass
surface as it (the glass layer) is immersed in protective
hydrocarbon liquid. Additional reactive species such as nitrogen
and Halogens may be injected into the canister as well. In yet
another embodiment, the glass surface may be cleaned and surface
treated in the same chamber. For example, inside chamber 620 the
glass surface is cleaned with argon plasma, and then the argon gas
in the chamber is displaced by protective fluid in the vapor phase
containing sulfide glass reactive species such as nitrogen or
Halogens (e.g., iodine I.sub.2 and iodine compounds).
[0205] In various embodiments the sulfide glass first major surface
is treated in chamber 630 to form a thin precursor film that reacts
with lithium metal to form an engineered solid electrolyte
interphase (SEI). Various processes, reagents and treatments for
engineering the SEI are described below.
[0206] With reference to FIG. 6B, in various embodiments a thin
precursor film 640 may coated onto the clean first major surface of
sulfide glass 201 to effect a solid electrolyte interphase via
reaction with lithium metal during lamination, and preferably via
reaction with pristine lithium metal surface.
[0207] In one embodiment precursor layer 640 is a halogen or
interhalogen (diatomic or multi-atomic). For instance a monolayer,
or several monolayers (e.g., up to 5 monolayers) of iodine or
bromine molecules on the solid electrolyte glass surface is formed
by condensation from the gas or liquid phase (e.g., gaseous or
liquid phase iodine).
[0208] In one embodiment precursor layer is nitrogen. For example,
a monolayer or several monolayers (e.g., up to 5 monolayers) of
nitrogen molecules on the surface of the solid electrolyte gas is
formed by condensation of nitrogen onto the solid electrolyte
surface (from a gas or liquid phase). In a particular embodiment
the nitrogen coated onto the surface of the solid electrolyte glass
via a liquid carrier, such as liquid hydrocarbons, containing
dissolved nitrogen molecules. The liquid hydrocarbons should be
dry, as defined above, especially if the solid electrolyte is
sensitive to moisture. Preferably the solubility of nitrogen in the
hydrocarbon is large. For instance, the liquid carrier (e.g.,
liquid hydrocarbon) having a room temperature solubility of greater
than 1 mole (nitrogen molecule) per mole of the liquid hydrocarbon,
and preferably a ratio that is greater than 1.1, and even more
preferably greater than 1.2. Particularly suitable liquid
hydrocarbons include n-Octane, n-Nonane, n-Decane, n-Undecane, and
n-Dodecane.
[0209] In other embodiments the solid electrolyte surface may be
coated with a precursor of SO.sub.2 or sulfur molecules, as
described in more detail herein below.
[0210] While lithium is primarily referenced as the akali metal
layer material herein, it should be understood that other alkali
metals or alloys of lithium may also be used.
Examples: Coatings on Glass Electrolyte Surface to Form SEI via
Reaction with Li
[0211] 1. Halogens or Interhalogens (Diatomic or Multi-Atomic)
[0212] A monolayer, a few layers or condensed films are formed by
iodine or bromine molecules on a glass surface from gas phase or
from liquid phase. Halogen coating on the glass surface helps to
improve wettahility of Li metal towards glass (reactive wetting).
In this case, the SEI formed on the clean Li surface consists of
LiHal, in particular LiI or LiBr. [0213] a. Halogen adsorption from
the gas phase onto a glass surface at elevated temperatures, room
temperature, or low temperatures.
[0214] In order to minimize the coating thickness the source of
iodine or bromine vapor is not a molecular halogen, but a
halogen-containing compound having a lower halogen vapor pressure.
The coating thickness can be optimized by using halogen-containing
compounds with appropriate vapor pressure and by adjusting duration
and temperature of the coating process. Among the compounds that
are used as sources of halogen vapor are solid polyhalogens. Solid
polyiodides with various cations described in (Per H. Svensson,
Lars Kloo, Chemical Reviews, 2003, Vol. 103, No. 5) can be used as
iodine sources (these compositions are incorporated by reference
herein). Applicable polyhalogens include quaternary
ammonium-polyhalogen compounds, in particular, tetraalkylammonium
polyhalogens, inorganic polyiodides, such as RhI.sub.3 CsI.sub.3
and Cu--(NH.sub.3).sub.4]I.sub.4, charge transfer complexes between
dioxane, pyridine, polyvinyl, pyrrolidone, polyethyleneoxide and
halogens (as acceptors), such poly(2vinylpyridine)iodine and
poly(4-vinylpyridine)bromine complexes. Other examples include
metal-halogen compounds, for instance, CuI. [0215] b. Halogen
coating of a glass surface from the liquid phase
[0216] The glass surface is coated with halogens by its treatment
in solutions containing molecular halogens (iodine, bromine) or
polyhalogens that are dissolved in dry (less than 1 ppm of
moisture), non-polar solvents. In the preferred case, the solvents
are selected from a group of unsaturated hydrocarbons or benzene
and its homologues. In another case, the solvents are halogenated
hydrocarbons, in particular, carbon tetrachloride. In another case,
the solvent is carbon disulfide. The glass surface is brought into
contact with or the glass is immersed into a solvent containing
dissolved coating material (halogens or polyhalogens). Then the
solvent is allowed to evaporate. In one case, Li--Mg or Li--Ca
alloys (solid solution range) are used instead of Li metal. As a
result, the SEI consists of LiI or LiBr doped with corresponding
halides of Mg or Ca and has increased Li ion conductivity due to
formation of Li cation vacancies (Schottky defects). In one case,
both the glass surface and Li are treated in halogen vapor
containing atmosphere. As a result, the halogen coating
(preferentially, a very thin coating that consists of one or two
molecular layers) is formed on the glass surface and a thin layer
of LiHal is formed on the Li surface. After Li lamination onto
glass, halogen molecules react with LiHal layer on Li forming an
SEI consisting of a LiHal layer with increased thickness.
[0217] 2. Nitrogen
[0218] A monolayer, a few layers or condensed films formed by
nitrogen molecules on a glass surface from gas phase or from liquid
phase at RT or low temperatures. At RT only one or two layers of
nitrogen molecules are adsorbed onto metal surfaces. nitrogen can
be adsorbed onto glass surfaces either in pure nitrogen atmosphere
(the volume having been previously evacuated to high vacuum) or in
a mixed nitrogen/inert gas atmosphere (Ar/N.sub.2). In order to
coat a long strip of glass, either a flow of pure nitrogen or a
flow of carrier gas (Ar) mixed with nitrogen can be used.
[0219] In various embodiments, the resulting SEI is, or includes,
Li.sub.3N with a high Li ion conductivity.
[0220] In various embodiments the molecular nitrogen precursor
layer is formed by coating the surface of the solid electrolyte
glass sheet with a thin layer of a liquid hydrocarbon containing an
amount of dissolved nitrogen molecules. In various embodiments the
mole ratio of nitrogen molecules dissolved in the hydrocarbon
carrier liquid is at least 0.05 moles of nitrogen molecules per
mole of liquid hydrocarbon (N.sub.2-moles/liq.hyd-moles). For
instance, at least 0.1 N.sub.2-moles/liq.hyd-moles, at least 0.2
N.sub.2-moles/liq.hyd-moles, at least 0.3
N.sub.2-moles/liq.hyd-moles, at least 0.4
N.sub.2-moles/liq.hyd-moles, at least 0.5
N.sub.2-moles/liq.hyd-moles, at least 1.0
N.sub.2-moles/liq.hyd-moles. Particular suitable liquid hydrocarbon
carriers are n-octane, n-nonane, n-decane, n-undecane, and
n-dodecane.
[0221] When using a liquid carrier containing dissolved nitrogen
molecules, the SEI formed when the nitrogen coated solid
electrolyte layer is directly contacted with lithium metal is a
lithium nitride compound (e.g., Li.sub.3N), preferably fully
reduced and highly conductive to lithium ions. As described above,
the formation of the SEI may be effected during the lamination
step, and the liquid hydrocarbons on the surface of the solid
electrolyte layer and/or the lithium metal layer removed prior to
and/or as a result of bond laminating the layers together.
[0222] 3. SO.sub.2 [0223] a. SO2 adsorption from the gas phase onto
a glass surface at elevated temperatures, RT or low temperatures.
SO2 can be adsorbed onto glass surfaces either in pure SO2
atmosphere (the volume having been previously evacuated to high
vacuum) or in a mixed SO2/inert gas atmosphere (Ar/SO2). [0224] b.
SO2 coating of a glass surface at low temperature using liquid SO2.
In various embodiments, the resulting SEI is, or includes, Li2S2O4,
which is a known Li ion conductor.
[0225] 4. Sulfur [0226] a. Sublimation onto glass surface. S8 ring
sulfur is known to be the dominant sublimation phase. [0227] b.
Glass surface oxidation leading to formation of an elemental S
layer. In various embodiments, the resulting SEI is, or includes,
Li2S.
Solid-State Laminate Electrode Assembly
[0228] With reference to FIG. 7 there is illustrated standalone
fully solid-state laminate electrode assembly 700 in accordance
with various embodiments of the present disclosure. Laminate
electrode assembly 700 is a laminate of alkali metal layer 101
having first major surface 101i and ii) inorganic alkali metal ion
conducting solid electrolyte layer 201 having first major surface
201i. In various embodiments the alkali metal layer is a lithium
metal layer and the inorganic solid electrolyte layer is an
inorganic lithium ion conducting sulfide glass sheet, also as
described above. In various embodiments, laminate 700 is formed by
reactively bonding layer 101 (lithium metal) with layer 201
(sulfide glass) to form inorganic interface 705 (also referred to
herein as the solid electrolyte interphase (SEI)) as 4/5 described
in more detail herein below. The thickness of laminate 700
generally ranges from about 100 um down to as thin as about 5 um,
and typically has a thickness in the range of 10 to 50 um.
Preferably, the lithium ion resistance across the interface is less
than 50.OMEGA.-cm.sup.2, and more preferably less than
2.5.OMEGA.-cm.sup.2.
[0229] The quality of inorganic interface 705 is a key aspect for
determining how well the laminate electrode assembly will operate
in a battery cell. Preferably, inorganic interface 705 is
substantially uncontaminated by organic material, including organic
residues of any inert liquid that may have been used in making,
storing and processing of the laminate structures. In various
embodiments the inorganic interface may be further characterized as
"sufficiently uncontaminated by passivated alkali metal." by which
it is meant that at least 70% of the geometric area of the
solid-state interface is uncontaminated by the presence of
passivated alkali metal, such as patches of passivated alkali metal
film (i.e., filmy patches), as well as pieces of passivated alkali
metal that break off during battery cell cycling and/or handling,
and could become trapped at the interface in the form of solid
flakes, flecks or material bits of passivated alkali metal.
Preferably, at least 80% of the geometric area of the solid-state
interface is uncontaminated as such, and more preferably at least
90%, and even more preferably at least 95%, and yet even more
preferably the entire geometric area of the solid-state interface
is uncontaminated by the presence of passivated alkali metal
flakes, flecks, filmy patches or material bits. To achieve an
inorganic interface that is sufficiently uncontaminated by
passivated alkali metal, surface 101i of lithium metal layer 101
should be substantially unpassivated prior to bonding, and
preferably the lithium metal layer surface is pristine.
Additionally, the surface of the sulfide glass should be cleaned
(e.g., by ion etching) immediately prior to bonding in order to
remove solid products of sulfide glass hydrolysis.
[0230] When the reactive bond between the layers is continuous and
complete, the laminate should exhibit exceptional adherence. In
various embodiments the reactively bonded solid-state interface
imparts exceptionally high peel strength to the standalone
solid-state laminate electrode assembly (i.e., room temperature
peel strength). For instance, the room temperature peel strength of
the solid-state laminate electrode assembly is significantly
greater than the tensile strength of the lithium metal layer to
which it is bonded, such that during room temperature peel strength
testing the lithium metal layer starts to deform, or tears, prior
to peeling.
Methods of Making a Solid-State Laminate Electrode Assembly
[0231] With reference to FIG. 8 there is illustrated a process and
apparatus 800 for making a fully solid-state laminate electrode
assembly 700 in accordance with various embodiments of the present
disclosure. The process takes place in an environmentally
controlled chamber 850, and involves: i) providing a lithium metal
laminate structure for processing into chamber 850, the laminate
structure (as described above with reference to FIGS. 1A-D), the
laminate structure composed of lithium metal layer 101 removably
covered by protective inert liquid layer 102, which encapsulates
first major surface 101i, and second major surface 101ii is held
adjacent to current collector layer 103; providing for processing
into chamber 850 an inorganic solid electrolyte laminate structure
(as described above in various embodiments with reference to FIGS.
2A-D, the laminate composed of sulfide glass layer 201 having first
major surface 201i encapsulated by protective liquid layer 202. As
shown in FIG. 8, sulfide glass layer is supported on its second
major surface 102ii by web carrier 805, which is not a component of
the sulfide glass laminate structure. When the laminate structures
include a solid release layer, it is removed on a take-up roll not
shown. Both layers 101 and 201 enter chamber 830 for removing the
inert liquid layer 102 and 202 respectively. Removal of the inert
liquid layer can involve a series of steps which may be performed
sequentially and/or in parallel. In various embodiments one or more
of the following steps is taken to remove the inert liquid layer,
including: applying heat to the layers (convectively and/or
conductively), applying a vacuum suction over the respective
layers, applying a jet of dry gas (Ar or He preferably) and/or a
jet of a high vapor pressure hydrocarbon, replacing a low vapor
pressure fluid with another higher pressure fluid, or some
combination thereof.
[0232] Once the liquid layer has been removed from sulfide glass
surface 201i, the surface may be cleaned in ion etching chamber 820
using argon plasma (as described above with reference to chamber
620 in FIG. 6). The cleaned sulfide glass may then be transferred
into surface treating station 850 where it may undergo a second
plasma treatment with nitrogen or a mixture of nitrogen and argon,
or it may be coated in chamber 850 to form a thin precursor film
that is reactive with substantially unpassivated lithium metal to
form a conductive solid electrolyte interphase. For instance, in
various embodiments it may be coated with a thin layer of iodine or
an iodine compound (e.g., condensing the iodine on the glass
surface). Once the glass has been cleaned and/or its surface
composition modified or coated with a thin precursor film, layers
101 and 201 are brought into laminating station 860 where they are
reactive bonded to each other, generally by an application of both
heat and pressure (via rollers 812) to form a fully solid-state
laminate electrode assembly of the present disclosure.
[0233] Laminate electrode assembly 700, which may be formed as
described above, includes second major surface 201ii of the sulfide
glass, and which may be highly sensitive to moisture. Accordingly,
in various embodiments, after laminate electrode assembly 700 has
been formed it may be stored in a sealed cartridge 900, as shown in
FIG. 9. Cartridge 900 contains a bath of super dry hydrocarbon
protective liquid 902 and laminate assembly 700 immersed in the
bath, and in this way preserves the sulfide glass second major
surface. Cartridge 900 is suitable for storing laminate electrode
assembly 704) over extended time periods, including hours, days, or
even weeks.
Battery Cells
[0234] With reference to FIG. 10 there is illustrated battery cell
1000 composed of fully solid-state laminate electrode assembly 700
combined with positive electrode 1030, such as a lithium ion
intercalating material electrode (e.g., intercalating transition
metal oxides), and battery electrolyte 1010, disposed between the
second major surface of sulfide glass layer 201 and positive
electrode 1010. In various embodiments it is contemplated that the
battery cell is fully solid-state. In some fully solid-state
battery embodiments, it is contemplated that the positive electrode
is disposed in direct contact with the sulfide glass second major
surface, in the absence of battery electrolyte layer 1010. In other
embodiments, battery cell 1000 may be a liquid or gel electrolyte
battery wherein electrolyte layer 1010 is a liquid electrolyte
impregnated porous polymer membrane and/or a gel electrolyte layer.
The method of making the battery cell may include providing the
solid state laminate electrode assembly and disposing it in a
battery cell housing adjacent to a liquid electrolyte impregnated
in a Celgard-like porous polymer layer, and placing the positive
electrode adjacent to it.
Conclusion
[0235] It is understood that the examples and embodiments described
herein are for illustrative purposes only and that various
modifications or changes in light thereof will be suggested to
persons skilled in the art. Although various details have been
omitted for clarity's sake, various design alternatives may be
implemented. Therefore, the present examples are to be considered
as illustrative and not restrictive, and the disclosure is not to
be limited to the details given herein, but may be modified within
the scope of the appended claims.
* * * * *