U.S. patent application number 17/172609 was filed with the patent office on 2022-08-11 for method for coating a separator for a battery.
This patent application is currently assigned to GM GLOBAL TECHNOLOGY OPERATIONS LLC. The applicant listed for this patent is GM GLOBAL TECHNOLOGY OPERATIONS LLC. Invention is credited to Mei Cai, Shuru Chen, Fang Dai, Ruchira R. Dharmasena.
Application Number | 20220255187 17/172609 |
Document ID | / |
Family ID | 1000005490939 |
Filed Date | 2022-08-11 |
United States Patent
Application |
20220255187 |
Kind Code |
A1 |
Dharmasena; Ruchira R. ; et
al. |
August 11, 2022 |
METHOD FOR COATING A SEPARATOR FOR A BATTERY
Abstract
A method for coating a separator for a battery includes creating
an electrostatic field and disposing a substrate material within
the electrostatic field. The method further includes applying a
coating material to the substrate material in a presence of the
electrostatic field and drying the coating material upon the
substrate material.
Inventors: |
Dharmasena; Ruchira R.;
(Shelby Township, MI) ; Chen; Shuru; (Troy,
MI) ; Dai; Fang; (Troy, MI) ; Cai; Mei;
(Bloomfield Hills, MI) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
GM GLOBAL TECHNOLOGY OPERATIONS LLC |
Detroit |
MI |
US |
|
|
Assignee: |
GM GLOBAL TECHNOLOGY OPERATIONS
LLC
Detroit
MI
|
Family ID: |
1000005490939 |
Appl. No.: |
17/172609 |
Filed: |
February 10, 2021 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
H01M 10/05 20130101;
B05D 1/02 20130101; B05D 1/04 20130101; B05D 1/18 20130101; B05D
1/007 20130101; H01M 50/403 20210101 |
International
Class: |
H01M 50/403 20060101
H01M050/403; B05D 1/00 20060101 B05D001/00 |
Goverment Interests
GOVERNMENT CONTRACT
[0001] This application was made with government support under
contract no. DE-EE008230 awarded by the Department of Energy. The
government has certain rights in the invention.
Claims
1. A method for coating a separator for a battery, comprising:
providing a flow of a metal foil backer over a plurality of
rollers; creating an electrostatic field; disposing a substrate
material provided upon the metal foil backer within the
electrostatic field, wherein the electrostatic field acts to retain
the substrate material upon and thereby take a flat shape of the
metal foil backer and wherein the substrate material includes a
polyolefin sheet; applying a coating material to the substrate
material in a presence of the electrostatic field, wherein the
electrostatic field is used to uniformly apply the coating material
to the substrate material; and in an operation subsequent to
applying the coating material, drying the coating material upon the
substrate material, wherein disposing the substrate material
provided upon the metal foil backer within the electrostatic field,
applying the coating material to the substrate material in the
presence of the electrostatic field, and the operation are
configured for drying the coating material upon the substrate
material without buckling or bending.
2. The method of claim 1, wherein creating the electrostatic field
includes creating a positive charge upon a metallic tip and
creating a negative charge upon a metallic sheet; and wherein
disposing the substrate material within the electrostatic field
includes placing the substrate material between the metallic tip
and the metallic sheet.
3. The method of claim 1, wherein applying the coating material
includes spray coating the coating material upon the substrate
material.
4. The method of claim 1, wherein applying the coating material
includes immersing the substrate material in a pool of precursor
material.
5. (canceled)
6. The method of claim 1, wherein the polyolefin sheet includes one
of a polypropylene monolayer sheet, a polyethylene monolayer sheet,
or a polypropylene/polyethylene/polypropylene sheet.
7. The method of claim 1, wherein the coating material includes a
titanium dioxide and carbon black mixture.
8. A method for coating a separator for a battery, comprising:
supplying a flow of a flexible substrate material from a supply
roll; running the flow of the flexible substrate material around an
applicator roller; disposing a liquid precursor pool in contact
with the applicator roller; creating an electrostatic field by
creating a positive charge upon a metal container for the liquid
precursor pool and by creating a negative charge upon the
applicator roller; immersing the flow of the flexible substrate
material running around the applicator roller within the liquid
precursor pool to apply a coating material upon the flow of the
flexible substrate material in a presence of the electrostatic
field; drying the coating material upon the flow of the flexible
substrate material; and coiling the flow of the flexible substrate
material upon a final product roll.
9. The method of claim 8, further comprising applying a second
electrostatic field to the flow of the flexible substrate material
between the applicator roller and the final product roll.
10. The method of claim 9, further comprising utilizing a drying
unit upon the flow of the flexible substrate material between the
applicator roller and the final product roll.
11. The method of claim 8, further comprising utilizing a drying
unit upon the flow of the flexible substrate material between the
applicator roller and the final product roll.
12. The method of claim 8, wherein the flow of the flexible
substrate material includes a flexible polyolefin including one of
polypropylene monolayer, polyethylene monolayer, and
polypropylene/polyethylene/polypropylene trilayer.
13. The method of claim 12, wherein the flow of the flexible
substrate material further includes an aluminum foil backer.
14. The method of claim 8, wherein the coating material includes a
titanium dioxide and carbon black mixture.
15. An equipment configuration to apply a coating upon a separator
for a battery, comprising: a supply roll providing a flow of a
flexible substrate material; an applicator roller receiving and
being in contact with the flow of the flexible substrate material,
wherein the applicator roller includes a negative charge; a liquid
precursor pool disposed in contact with the applicator roller; a
metal container containing the liquid precursor pool, wherein the
metal container includes a positive charge; a final product roll
receiving the flow of the flexible substrate material from the
applicator roller and coiling the flow of the flexible substrate
material; and wherein the applicator roller including the negative
charge and the metal container including the positive charge create
an electrostatic field therebetween; wherein the flow of the
flexible substrate material, while being in the contact with the
applicator roller, is immersed in and receives the coating within
the liquid precursor pool; and wherein the coating is dried between
the applicator roller and the final product roll.
16. The equipment configuration of claim 15, wherein the positive
charge includes a first positive charge; wherein the negative
charge includes a first negative charge; wherein the electrostatic
field includes a first electrostatic field; and further comprising
a metallic tip including a second positive charge and a metallic
sheet creating a second negative charge, wherein the metallic tip
and the metallic sheet are disposed to create a second
electrostatic field between the applicator roller and the final
product roll.
17. The equipment configuration of claim 15, further comprising a
drying unit disposed between the applicator roller and the final
product roll.
18. The equipment configuration of claim 15, wherein the flow of
the flexible substrate material includes a flexible polyolefin
including one of polypropylene monolayer, polyethylene monolayer,
or polypropylene/polyethylene/polypropylene trilayer; and wherein
the flow of the flexible substrate material further includes an
aluminum foil backer.
19. The equipment configuration of claim 15, wherein the liquid
precursor pool includes a slurry of titanium dioxide and carbon
black mixture.
Description
INTRODUCTION
[0002] The disclosure generally relates to a method for coating a
separator for a battery.
[0003] Electric and hybrid electric vehicles utilize battery
devices to store electrical energy. Vehicular batteries such as
lithium-ion batteries include an anode, a cathode, and a separator
providing a physical barrier between the anode and the cathode
while enabling an exchange of ions across the separator.
SUMMARY
[0004] A method for coating a separator for a battery is disclosed.
The method includes creating an electrostatic field and disposing a
substrate material within the electrostatic field. The method
further includes applying a coating material to the substrate
material in a presence of the electrostatic field and drying the
coating material upon the substrate material.
[0005] In some embodiments, creating the electrostatic field
includes creating a positive charge upon a metallic tip and
creating a negative charge upon a metallic sheet. In some
embodiments, disposing the substrate within the electrostatic field
includes placing the substrate material between the metallic tip
and the metallic sheet.
[0006] In some embodiments, applying the coating material includes
spray coating the coating material upon the substrate material.
[0007] In some embodiments, applying the coating material includes
immersing the substrate material in a pool of precursor
material.
[0008] In some embodiments, the substrate material includes a
polyolefin sheet.
[0009] In some embodiments, the polyolefin sheet includes one of a
polypropylene monolayer sheet, a polyethylene monolayer sheet, or a
polypropylene/polyethylene/polypropylene sheet.
[0010] In some embodiments, the coating material includes a
titanium dioxide and carbon black mixture.
[0011] According to one alternative embodiment, a method for
coating a separator for a battery is disclosed. The method includes
supplying a flow of a flexible substrate material from a supply
roll, running the flow of the flexible substrate material around an
applicator roller, and disposing a liquid precursor pool in contact
with the applicator roller. The method further includes creating an
electrostatic field by creating a positive charge upon a metal
container for the liquid precursor pool and by creating a negative
charge upon the applicator roller and immersing the flow of
flexible substrate material running around the applicator roller
within the liquid precursor pool to apply a coating material upon
the substrate material in a presence of the electrostatic field.
The method further includes drying the coating material upon the
substrate material and coiling the substrate material upon a final
product roll.
[0012] In some embodiments, the method further includes applying a
second electrostatic field to the flow of flexible substrate
material between the applicator roller and the final product
roll.
[0013] In some embodiments, the method further includes utilizing a
drying unit upon the flow of flexible substrate material between
the applicator roller and the final product roll.
[0014] In some embodiments, the method further includes utilizing a
drying unit upon the flow of flexible substrate material between
the applicator roller and the final product roll.
[0015] In some embodiments, the flexible substrate material
includes a flexible polyolefin including one of polypropylene
monolayer, polyethylene monolayer, and
polypropylene/polyethylene/polypropylene trilayer.
[0016] In some embodiments, the flexible substrate material further
includes an aluminum foil backer.
[0017] In some embodiments, the coating material includes a
titanium dioxide and carbon black mixture.
[0018] According to one alternative embodiment, an equipment
configuration to apply a coating upon a separator for a battery
includes a supply roll providing a flow of flexible substrate
material and an applicator roller receiving and being in contact
with the flow of flexible substrate material. The applicator roller
includes a negative charge. The equipment configuration further
includes a liquid precursor pool disposed in contact with the
applicator roller and a metal container containing the liquid
precursor pool. The metal container includes a positive charge. The
equipment configuration further includes a final product roll
receiving the flow of flexible substrate material from the
applicator roller and coiling the flexible substrate material. The
applicator roller including the negative charge and the metal
container including the positive charge create an electrostatic
field therebetween. The flow of flexible substrate material, while
being in contact with the applicator roller, is immersed in and
receives the coating within the liquid precursor pool. The coating
is dried between the applicator roller and the final product
roll.
[0019] In some embodiments, the positive charge includes a first
positive charge and the negative charge includes a first negative
charge. In some embodiments, the electrostatic field includes a
first electrostatic field. In some embodiments, the equipment
configuration further includes a metallic tip including a second
positive charge and a metallic sheet creating a second negative
charge. The metallic tip and the metallic sheet are disposed to
create a second electrostatic field between the applicator roller
and the final product roll.
[0020] In some embodiments, the equipment configuration further
includes a drying unit disposed between the applicator roller and
the final product roll.
[0021] In some embodiments, the flexible substrate material
includes a flexible polyolefin including one of polypropylene
monolayer, polyethylene monolayer, or
polypropylene/polyethylene/polypropylene trilayer. In some
embodiments, the flexible substrate material further includes an
aluminum foil backer.
[0022] In some embodiments, the liquid precursor pool includes a
slurry of titanium dioxide and carbon black mixture.
[0023] The above features and advantages and other features and
advantages of the present disclosure are readily apparent from the
following detailed description of the best modes for carrying out
the disclosure when taken in connection with the accompanying
drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
[0024] FIG. 1 schematically illustrates an exemplary equipment
configuration 5 operable to utilize a method to coat separators for
battery applications, accordance with the present disclosure;
[0025] FIG. 2 schematically illustrates the negatively charged
sheet 30 and the separator substrate of FIG. 1 in enlarged scale,
accordance with the present disclosure;
[0026] FIG. 3 illustrates an exemplary equipment configuration 100
operable to utilize a method to coat separators for battery
applications in a roll-to-roll operation, accordance with the
present disclosure;
[0027] FIG. 4 illustrates a method to coat separators for battery
applications, accordance with the present disclosure;
[0028] FIG. 5 illustrates a method to coat separators for battery
applications in a roll-to-roll operation, accordance with the
present disclosure;
[0029] FIG. 6 schematically illustrates a portion of an equipment
configuration operable to utilize a method to coat separators for
battery applications in a roll-to-roll operation, accordance with
the present disclosure;
[0030] FIG. 7 illustrates an alternative method to coat separators
for battery applications in a roll-to-roll operation, accordance
with the present disclosure;
[0031] FIG. 8 graphically illustrates test results from a prior art
battery system, accordance with the present disclosure; and
[0032] FIG. 9 graphically illustrates test results from a battery
system utilizing a separator created with the disclosed method,
accordance with the present disclosure.
DETAILED DESCRIPTION
[0033] A coating method is provided to produce uniform and thin
layer coating of metal particles, metal oxides particles,
conductive carbon particles, and/or their mixtures, onto battery
separators using electrostatic force. According to one embodiment,
the method may be implemented in a roll-to-roll coating process.
The coated separators may improve the performance and robustness of
high energy density batteries.
[0034] Methods in the art to coat a membrane may include
transitioning the membrane through a bath and drying the liquid of
the bath upon the membrane. However, coatings created by methods in
the art result in brittle coatings or coatings likely to peel away
from the substrate or coatings likely to buckle or bend. The
disclosed method creates a coated membrane without buckling or
bending of the coating during drying. In one embodiment, the
electrostatic field may be initially established and then the
coating may be applied in the presence of the established
electrostatic field. In another embodiment, the coating may be
first applied to a substrate material, and then the electrostatic
field may be subsequently established, with the substrate and the
liquid coating material being disposed or moved into the
electrostatic field.
[0035] The disclosed method utilizes electrostatic force to retain
the separators on a substrate. Use of the electrostatic force
enables formation of a controllable, thin, and uniform coating. The
disclosed process is facile and quick to operate and may easily be
scaled up at a low cost. Electrostatic force may be used to retain
the separators on a metal substrate with buckling/bending during
drying.
[0036] The coating utilized in the disclosed process may include a
variety of coating source materials, including carbon, metal,
oxides, and/or their mixtures. In one embodiment, the coating
includes a titanium dioxide/carbon black mixture.
[0037] Electrostatic force is used to adhere polypropylene or
similar membranes onto thin film metal substrates such as aluminum.
Substrates may include a polyolefin (such as polypropylene (PP)
monolayer, polyethylene (PE) monolayer and
polypropylene/polyethylene/polypropylene (PP/PE/PP) trilayer)
sheet. Electrostatic force may be used to uniformly spray coating
materials onto separators and enhance the adhesion. Uniform coating
enables fabrication of ion selective membranes which may be used in
Li--S batteries, Li-ion batteries, and fuel cells. The disclosed
process may include rapid drying of thin film membranes, for
example, by passing heated air over the film membrane, thereby
allowing roll to roll coating. The disclosed coating may be thin or
microscopic, for example, provided as nanoparticles upon the
separator.
[0038] FIG. 1 schematically illustrates an exemplary equipment
configuration 5 operable to utilize a method to coat separators for
battery applications. The equipment configuration 5 is illustrated
including a positively charged tip 20 and a negatively charged
sheet 30. The positively charged tip 20 may include a conductive
metallic part with a triangular cross-section. A difference in
electrostatic charge between the positively charged tip 20 and the
negatively charged sheet 30 create an electrostatic field 40
extending between the positively charged tip 20 and the negatively
charged sheet 30. A separator substrate 10 is provided as an
exemplary substrate in a presence of the electrostatic field 40. By
being applied to separator substrate 10 in the presence of the
electrostatic field 40, coating particles, for example, as applied
through a spray coating, are electrostatically adhered to the
substrate. FIG. 2 schematically illustrates the negatively charged
sheet 30 and the separator substrate 10 of FIG. 1 in enlarged
scale. The negatively charged sheet 30 is illustrated including a
first surface 32. An entirety of the negatively charged sheet 30
including the first surface 32 includes a negative charge, which
may be induced by attachment of the negatively charged sheet 30 to
a negative terminal of a direct current power source. The separator
substrate 10 is illustrated and exists within the electrostatic
field 40 of FIG. 1. As a result, a negative charge/positive charge
separation exists across the separator substrate 10, with a
negative charge existing on a first surface 12 of the separator
substrate 10 and a positive charge existing on a second surface 14
of the separator substrate 10. The negative charge upon the first
surface 12 attracts the coating particles and electrostatically
adhere the coating particles upon the first surface 12 of the
separator substrate 10. The separator substrate 10 may be
constructed of many different materials. In one embodiment, the
separator substrate 10 may be a polypropylene separator.
[0039] FIG. 3 illustrates an exemplary equipment configuration 100
operable to utilize a method to coat separators for battery
applications in a roll-to-roll operation. The equipment
configuration 100 includes a supply roll 120, an applicator roller
130, and a finished product roll 140. The supply roll 120, the
applicator roller 130, and the finished product roll 140 are
collectively operable to transfer a supply of flexible substrate
material 110 from the supply roll 120, over the applicator roller
130, and onto the finished product roll 140. In one embodiment, the
flexible substrate material 110 may be a polypropylene sheet. In
one embodiment, the polypropylene sheet may be provided upon an
aluminum foil backer. As the flexible substrate material 110
transitions from the supply roll 120 to the applicator roller 130,
the flexible substrate material 110 conforms to the outer shape of
the applicator roller 130 and moves through a liquid precursor pool
160 contained within container 150. The liquid precursor pool 160
may include the particles which are intended to be provided upon
the flexible substrate material 110 as a coating. In one
embodiment, the liquid precursor pool 160 may include titanium
dioxide (TiO.sub.2).
[0040] The container 150 may be constructed of a conductive
metallic material and may be positively charged. The applicator
roller 130 may be metallic or may contain a metallic portion, the
applicator roller 130 may be negatively charged. By creating a
positive charge upon the container 150 and a negative charge upon
the applicator roller 130, an electrostatic field may be created
between the container 150 and the applicator roller 130. As the
flexible substrate material 110 moves through the liquid precursor
pool 160, particles from the liquid precursor pool 160 are adhered
to the flexible substrate material 110 in a presence of the
electrostatic field created by the positive charge of the container
150 and the negative charge of the applicator roller 130. As a
result, a coating 112 is provided upon the flexible substrate
material 110. The flexible substrate material 110 including the
coating 112 progresses to the final product roll 140 where it is
coiled upon the final product roll 140 for storage.
[0041] FIG. 4 illustrates a method 200 to coat separators for
battery applications. The method 200 starts at step 202. At step
204, an electrostatic field is created, a substrate material is
disposed within the electrostatic field. At step 206, a coating
material is applied to the substrate material in the presence of
the electrostatic field. The application of the coating material
may include spraying or brushing the coating material upon the
substrate, dipping or immersing the substrate material in a coating
material pool, or other similar application processes. At step 208,
the coating material is dried upon the substrate material. At step
210, the method 200 ends. A number of additional or alternative
steps are envisioned, and the disclosure is not intended to be
limited to the exemplary method steps provided herein.
[0042] FIG. 5 illustrates a method 300 to coat separators for
battery applications in a roll-to-roll operation. The method 300
starts at step 302. At step 304, a supply roll of flexible
substrate material is provided to supply a flow of flexible
substrate material. At step 306, an electrostatic field is created
between an applicator roller and a metallic precursor pool
container. At step 308, the flow of flexible substrate material is
moved through a pool of liquid precursor material within the
metallic precursor pool container, such that the flexible substrate
material is immersed in the liquid precursor material in the
presence of the electrostatic field which results in the flexible
substrate material being coated with the liquid precursor material.
The pool of liquid precursor material may include titanium dioxide
or a slurry of titanium dioxide and carbon black material. At step
310, the flow of flexible substrate material is coiled upon a final
product roll. The liquid precursor material upon the flexible
substrate material dries upon the flexible substrate material as it
transitions between the applicator roller and the final product
roll. At step 312, the method 300 ends. A number of additional or
alternative steps are envisioned, and the disclosure is not
intended to be limited to the exemplary method steps provided
herein.
[0043] FIG. 6 schematically illustrates a portion of an equipment
configuration 100' operable to utilize a method to coat separators
for battery applications in a roll-to-roll operation. The equipment
configuration 100' is similar to the equipment configuration 100 of
FIG. 3 and includes the applicator roller 130, the liquid precursor
pool 160, the flexible substrate material 110, and the final
product roll 140. The coating 112 is illustrated upon the flexible
substrate material 110 transitioning from the applicator roller 130
to the final product roll 140. A positively charged tip 170 and a
negatively charged plate 180 are illustrated creating an
electrostatic field 190. Because the liquid precursor material of
the coating 112 is in liquid form, the electrostatic field 190 may
electrostatically adhere the liquid precursor material of coating
112 to the flexible substrate material 110. In one embodiment, the
electrostatic field 190 may be applied in the alternative to the
electrostatic field described in FIG. 3 in relation to the
container 150 and the applicator roller 130. In another embodiment,
the electrostatic field described in FIG. 3 may be applied in the
configuration of FIG. 6, and the electrostatic field 190 may be an
auxiliary or second electrostatic field. A drying unit 192 is
illustrated providing a flow of heated air 194 upon the flexible
substrate material 110 to dry the coating 112. In another
embodiment, the drying unit 192 may alternatively include a heat
lamp or similar device to heat and dry the coating 112.
[0044] FIG. 7 illustrates an alternative method 400 to coat
separators for battery applications in a roll-to-roll operation.
The method 400 starts at step 402. At step 404, a supply roll of
flexible substrate material is provided to supply a flow of
flexible substrate material. At step 406, an electrostatic field is
created between an applicator roller and a metallic precursor pool
container. At step 408, the flow of flexible substrate material is
moved through a pool of liquid precursor material within the
metallic precursor pool container, such that the flexible substrate
material is immersed in the liquid precursor material in the
presence of the electrostatic field which results in the flexible
substrate material being coated with the liquid precursor material.
At step 410, an auxiliary or second electrostatic field is created
between the applicator roller and a final product roll, and the
flow of flexible substrate material is moved through the second
electrostatic field. At step 412, a drying unit is used to dry the
coating upon the flow of flexible substrate material. At step 414,
the flow of flexible substrate material is coiled upon the final
product roll. At step 416, the method 400 ends. A number of
additional or alternative steps are envisioned, and the disclosure
is not intended to be limited to the exemplary method steps
provided herein.
[0045] As an example, the disclosed method can be used for coating
Titania (TiO.sub.2) nanoparticles and carbon black mixture on
polypropylene (PP) separators, which can be used in lithium-sulfur
batteries to improve their capacities and cell cycle life. FIG. 8
graphically illustrates test results from a lithium-sulfur battery
system. A vertical axis 502 represents potential Volts
(Li/Li.sup.+). A horizontal axis 504 represents gravimetric
capacity (mAh g.sup.-1) which describes a capacity of the battery
per unit mass of sulfur cathode. The test data is generated at 0.1
C discharge/charge rate after first formation cycle at 0.05 C rate.
Potential vs. specific capacity curves in the test data correspond
to a sulfur cathode with an uncoated polypropylene separator. Plot
510 represents a first charging cycle. Plot 520 represents a fifth
charging cycle. Plot 530 represents a fifteenth charging cycle.
Plot 512 represents a first discharging cycle. Plot 522 represents
a fifth discharging cycle. Plot 532 represents a fifteenth
discharging cycle. FIG. 9 graphically illustrates test results from
a lithium-sulfur battery system utilizing a separator created with
a layer of TiO.sub.2/carbon (90:10 mass ratio) with a thickness of
10 um using the disclosed method. A vertical axis 602 represents
potential Volts (Li/Li.sup.+). A horizontal axis 604 represents
gravimetric capacity (mAh g.sup.-1). The test data is generated at
0.1 C discharge/charge rate after first formation cycle at 0.05 C
rate. Potential vs. specific capacity curves in the test data
correspond to a sulfur cathode with an uncoated polypropylene
separator. Plot 610 represents a first charging cycle. Plot 620
represents a fifth charging cycle. Plot 630 represents a fifteenth
charging cycle. Plot 612 represents a first discharging cycle. Plot
622 represents a fifth discharging cycle. Plot 632 represents a
fifteenth discharging cycle. In FIG. 8, first cycle gravimetric
capacity is observed around 1200 mAh g.sup.-1 at 0.05 C
discharge/charge rate. When increasing discharge rate to 0.1 C
starting from 2nd cycle, the specific capacity decreases to around
800 mAh FIG. 9 shows that the first cycle of the lithium-sulfur
battery with TiO.sub.2/carbon coated separator gives a gravimetric
capacity of 950 mAh g.sup.-1 which is lower than the initial
capacity with un-coated PP separator. But from the first cycle
onward, higher stable gravimetric capacity of -1100 mAh g.sup.-1 at
0.1 C was observed. Comparing the plots of FIG. 8 with the plots of
FIG. 9, improvement in gravimetric capacity of a lithium-sulfur
battery with a separator with a functional coating is apparent.
This proves that TiO.sub.2/carbon coating on separator by the
disclosed method can adsorb and re-utilize the polysulfides which
dissolve into the electrolyte from sulfur cathode during discharge
process, thus mitigating the substation capacity loss of
lithium-sulfur batteries.
[0046] While the best modes for carrying out the disclosure have
been described in detail, those familiar with the art to which this
disclosure relates will recognize various alternative designs and
embodiments for practicing the disclosure within the scope of the
appended claims.
* * * * *