U.S. patent application number 17/653674 was filed with the patent office on 2022-06-16 for carbon sheet.
This patent application is currently assigned to ZEON CORPORATION. The applicant listed for this patent is ZEON CORPORATION. Invention is credited to Mitsugu UEJIMA, Tomoko YAMAGISHI.
Application Number | 20220185669 17/653674 |
Document ID | / |
Family ID | 1000006178074 |
Filed Date | 2022-06-16 |
United States Patent
Application |
20220185669 |
Kind Code |
A1 |
YAMAGISHI; Tomoko ; et
al. |
June 16, 2022 |
CARBON SHEET
Abstract
Provided is a material that has excellent handleability and
processability, and that when used as a support for a different
material, enables support of the different material up to an inner
part thereof. A carbon sheet contains one or more carbon nanotubes
and has a porosity of not less than 48% and not more than 90%. The
carbon sheet preferably includes: a porous substrate made from
carbon; and the carbon nanotubes, attached to the porous substrate.
The carbon nanotubes contained in the carbon sheet are preferably
single-walled carbon nanotubes. Moreover, the carbon nanotubes
contained in the carbon sheet preferably have a nitrogen adsorption
specific surface area of 600 m.sup.2/g or more.
Inventors: |
YAMAGISHI; Tomoko; (Tokyo,
JP) ; UEJIMA; Mitsugu; (Tokyo, JP) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
ZEON CORPORATION |
Chiyoda-ku Tokyo |
|
JP |
|
|
Assignee: |
ZEON CORPORATION
Chiyoda-ku Tokyo
JP
|
Family ID: |
1000006178074 |
Appl. No.: |
17/653674 |
Filed: |
March 7, 2022 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
16647872 |
Mar 17, 2020 |
11305996 |
|
|
PCT/JP2018/036117 |
Sep 27, 2018 |
|
|
|
17653674 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C01P 2006/12 20130101;
C01B 32/159 20170801 |
International
Class: |
C01B 32/159 20060101
C01B032/159 |
Foreign Application Data
Date |
Code |
Application Number |
Sep 28, 2017 |
JP |
2017-189154 |
Claims
1. A carbon sheet comprising one or more carbon nanotubes and
having a porosity of not less than 48% and not more than 90%.
2. The carbon sheet according to claim 1, comprising: a porous
substrate made from carbon; and the carbon nanotubes, attached to
the porous substrate.
3. A carbon sheet comprising one or more carbon nanotubes and
having a void fraction of not less than 40% and not more than
95%.
4. The carbon sheet according to claim 1, wherein the carbon
nanotubes are single-walled carbon nanotubes.
5. The carbon sheet according to claim 1, wherein the carbon
nanotubes have a nitrogen adsorption specific surface area of 600
m.sup.2/g or more.
6. The carbon sheet according to claim 1, composed of only the
carbon nanotubes.
7. The carbon sheet according to claim 3, wherein the carbon
nanotubes are single-walled carbon nanotubes.
8. The carbon sheet according to claim 3, wherein the carbon
nanotubes have a nitrogen adsorption specific surface area of 600
m.sup.2/g or more.
9. The carbon sheet according to claim 3, composed of only the
carbon nanotubes.
10. The carbon sheet according to claim 3, having a void fraction
of not less than 42%.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] The present application is a continuation application of
U.S. patent application Ser. No. 16/647,872 filed Mar. 17, 2020,
which is a National Stage Application of PCT/JP2018/036117 filed
Sep. 27, 2018, which claims priority of Japanese Patent Application
No. 2017-189154 filed Sep. 28, 2017. The disclosures of the prior
applications are hereby incorporated by reference herein in their
entirety.
TECHNICAL FIELD
[0002] The present disclosure relates to a carbon sheet and a
method of producing a carbon sheet. More specifically, the present
disclosure relates to a carbon nanotube-containing carbon sheet and
a method of producing the same.
BACKGROUND
[0003] Carbon nanotubes (hereinafter, also referred to as "CNTs")
have been attracting attention in recent years as light-weight
materials that also have excellent electrical conductivity, thermal
conductivity, and mechanical properties.
[0004] It has been proposed that due to CNTs having a large surface
area, a different material may be supported on the surfaces of CNTs
so that the CNTs can be used as a CNT composite material that is
provided with another function such as catalytic activity (for
example, refer to Patent Literature (PTL) 1).
[0005] On the other hand, CNTs are fine structures having
nanometer-size diameters, which means that individual CNTs have
poor handleability and processability. In view of the above, it has
been proposed that by producing a solution in which CNTs are
dispersed and then carrying out papermaking using this solution,
for example, multiple CNTs can be caused to assemble into the form
of a film and can be used as a carbon nanotube film referred to as
"buckypaper" (for example, refer to PTL 2).
[0006] Moreover, it has been reported that a CNT sheet containing
CNTs that have a median length and an aspect ratio that are not
less than specific values and that are arranged in a randomly
oriented, uniformly distributed pattern, and in which the CNT basis
weight is not less than a specific value, can have electromagnetic
wave absorption characteristics (for example, refer to PTL 3).
[0007] It has also been reported that an infrared absorbing member
containing a CNT assembly in which CNTs are oriented in a length
direction can have high infrared absorbance (for example, refer to
PTL 4).
CITATION LIST
Patent Literature
[0008] PTL 1: WO 2016/013245 A1
[0009] PTL 2: JP 2010-105909 A
[0010] PTL 3: JP 2017-529298 A
[0011] PTL 4: JP 2012-188305 A
SUMMARY
Technical Problem
[0012] Studies carried out by the inventors have revealed that in a
case in which buckypaper is used to support a different material
from a viewpoint of obtaining a CNT composite material having
excellent handleability and processability, the different material
cannot penetrate to an inner part of the buckypaper due to the
dense structure thereof.
[0013] Accordingly, one objective of the present disclosure is to
provide a material that has excellent handleability and
processability, and that when used as a support for a different
material, enables support of the different material up to an inner
part thereof.
[0014] The inventors conducted further studies, and when they
attempted to use the buckypaper described above as an
electromagnetic wave absorbing material and/or infrared absorbing
material, the inventors found that electromagnetic wave absorption
characteristics and infrared absorption characteristics were
inadequate.
[0015] Accordingly, another objective of the present disclosure is
to provide a material having excellent electromagnetic wave
absorption characteristics and infrared absorption
characteristics.
Solution to Problem
[0016] The inventors conducted diligent studies with the aim of
solving the problems set forth above. The inventors discovered that
a carbon sheet containing one or more carbon nanotubes and having a
porosity within a specific range has excellent handleability and
processability, and when used as a support for a different
material, enables support of the different material up to an inner
part of the sheet, and, in this manner, the inventors completed the
present disclosure.
[0017] Specifically, the present disclosure aims to advantageously
solve the problems set forth above by disclosing a carbon sheet
comprising one or more carbon nanotubes and having a porosity of
not less than 5% and not more than 90%. A carbon sheet that
contains carbon nanotubes and has a porosity within the numerical
range set forth above in this manner has excellent handleability
and processability, and when used as a support for a different
material, enables support of the different material up to an inner
part of the sheet. Note that the porosity referred to in the
present disclosure can be measured by mercury intrusion
porosimetry.
[0018] The presently disclosed carbon sheet set forth above
preferably comprises: a porous substrate made from carbon; and the
carbon nanotubes, attached to the porous substrate. Through
inclusion of a porous substrate made from carbon and carbon
nanotubes attached to the porous substrate, the porosity of an
inner part of the carbon sheet increases, and thus a larger amount
of a different material can be supported up to the inner part of
the carbon sheet. Moreover, mechanical strength of the carbon sheet
can be increased, and thus the carbon sheet can be provided with
excellent processability.
[0019] The inventors also discovered that a carbon sheet containing
one or more carbon nanotubes and having a void fraction within a
specific range has excellent electromagnetic wave absorption
characteristics and infrared absorption characteristics, and, in
this manner, completed the present disclosure.
[0020] Specifically, the present disclosure aims to advantageously
solve the problems set forth above by disclosing a carbon sheet
comprising one or more carbon nanotubes and having a void fraction
of not less than 30% and not more than 95%. A carbon sheet that
contains carbon nanotubes and has a void fraction within a specific
range in this manner has excellent electromagnetic wave absorption
characteristics and infrared absorption characteristics.
[0021] Note that the void fraction referred to in the present
disclosure can be measured by a method described in the EXAMPLES
section of the present specification.
[0022] In the presently disclosed carbon sheet, the carbon
nanotubes are preferably single-walled carbon nanotubes. By using
single-walled carbon nanotubes, a larger amount of a different
material can be supported on the surfaces of the carbon nanotubes,
and electromagnetic wave absorption characteristics and infrared
absorption characteristics of the carbon sheet can be further
enhanced.
[0023] In the presently disclosed carbon sheet, the carbon
nanotubes preferably have a nitrogen adsorption specific surface
area of 600 m.sup.2/g or more. By using carbon nanotubes having a
nitrogen adsorption specific surface area of 600 m.sup.2/g or more,
a larger amount of a different material can be supported on the
surfaces of the carbon nanotubes, and electromagnetic wave
absorption characteristics and infrared absorption characteristics
of the carbon sheet can be further enhanced.
[0024] Note that the nitrogen adsorption specific surface area of
the carbon nanotubes referred to in the present disclosure can be
measured in accordance with the BET (Brunauer-Emmett-Teller) method
using a fully automated specific surface area analyzer (produced by
Mountech Co., Ltd.; product name: Macsorb.RTM. HM model-1210
(Macsorb is a registered trademark in Japan, other countries, or
both)).
[0025] The presently disclosed carbon sheet is preferably composed
of only the carbon nanotubes. When the carbon sheet is composed of
only carbon nanotubes, the weight of the carbon sheet can be
reduced. Moreover, in a configuration in which the carbon sheet is
formed using only carbon nanotubes, the void fraction of the carbon
sheet can be adjusted, and thus electromagnetic wave absorption
characteristics and infrared absorption characteristics of the
carbon sheet can be further enhanced, by appropriately altering the
conditions under which the carbon nanotubes are dispersed in a
solvent or the like.
Advantageous Effect
[0026] According to the present disclosure, it is possible to
provide a carbon sheet that has excellent handleability and
processability, and that when used as a support for a different
material, enables support of the different material up to an inner
part of the sheet.
[0027] Moreover, according to the present disclosure, it is
possible to provide a material that has excellent electromagnetic
wave absorption characteristics and infrared absorption
characteristics.
DETAILED DESCRIPTION
[0028] The following provides a detailed description of embodiments
of the present disclosure.
[0029] The presently disclosed carbon sheet contains one or more
carbon nanotubes and has a porosity and/or void fraction that is
within a specific range.
[0030] (Carbon Sheet Having Defined Porosity)
[0031] The presently disclosed carbon sheet that has a porosity
within a specific range can suitably be used as a support for a
different material such as a metal (tin, platinum, gold, palladium,
etc.) or a metal oxide (silicon oxide, lithium oxide, lithium
titanate, etc.). These different materials may, for example, be in
the form of particles of 5 .mu.m or smaller.
[0032] <Carbon Sheet>
[0033] The presently disclosed carbon sheet contains one or more
carbon nanotubes, has a porosity within a specific range, and may
optionally include a porous substrate made from carbon. The
presently disclosed carbon sheet that has a porosity within the
aforementioned specific range has excellent handleability and
processability, and when used as a support for a different
material, enables support of the different material up to an inner
part of the sheet.
[0034] Note that the presently disclosed carbon sheet that has a
porosity within a specific range is a sheet that contains only
carbon. However, the phrase "only carbon" used in the above
description does not rule out the inclusion of small amounts of
components other than carbon, such as impurities.
[0035] <<Structure of Carbon Sheet>>
[0036] More specifically, the presently disclosed carbon sheet that
has a porosity within a specific range may, for example, have a
structure such as (1) a structure in which only carbon nanotubes
are intertwined in a manner such that the porosity is not less than
5% and not more than 90%, or (2) a structure in which carbon
nanotubes are attached to a porous substrate made from carbon in a
manner such that the porosity is not less than 5% and not more than
90%. Note that a carbon sheet having structure (1) is light and
easy to handle. Moreover, such a carbon sheet can suitably be used
as a support for a different material. On the other hand, the use
of a porous substrate in the case of a sheet having structure (2)
makes it easy to increase the porosity of an inner part of the
carbon sheet, and can also increase mechanical strength of the
carbon sheet and provide the carbon sheet with excellent
processability.
[0037] <<Properties of Carbon Sheet>>
[0038] The carbon sheet preferably also has the following
properties.
[0039] [Porosity]
[0040] The porosity in the presently disclosed carbon sheet that
has a porosity within a specific range is required to be 5% or
more, and is preferably 40% or more, more preferably 48% or more,
and even more preferably 70% or more. Moreover, the porosity is
required to be 90% or less, and is preferably 88% or less. When the
porosity of the carbon sheet is 5% or more, sufficient space in an
inner part of the carbon sheet can be ensured, and thus a different
material can be well supported up to the inner part of the sheet
when the carbon sheet is used as a support for the different
material. Moreover, when the porosity is 90% or less, sufficient
free-standing ability of the carbon sheet can be ensured, and thus
a carbon sheet having good handleability and processability can be
provided.
[0041] [Thickness]
[0042] The thickness of the carbon sheet is preferably 2 .mu.m or
more, more preferably 5 .mu.m or more, and even more preferably 10
.mu.m or more. Moreover, the thickness of the carbon sheet is
preferably 5,000 .mu.m or less, more preferably 4,500 .mu.m or
less, and even more preferably 4,000 .mu.m or less. When the
thickness of the carbon sheet is 2 .mu.m or more, strength of the
obtained carbon sheet can be ensured. As a result, processability
of the carbon sheet can be increased. On the other hand, good
handleability of the obtained carbon sheet can be maintained when
the thickness of the carbon sheet is 5,000 .mu.m or less.
[0043] [Density]
[0044] The density of the carbon sheet is preferably 0.01
g/cm.sup.3 or more, more preferably 0.1 g/cm.sup.3 or more, and
even more preferably 0.50 g/cm.sup.3 or more, and is preferably
1.80 g/cm.sup.3 or less, more preferably 1.50 g/cm.sup.3 or less,
and even more preferably 1.20 g/cm.sup.3 or less. When the density
of the carbon sheet is 0.01 g/cm.sup.3 or more, strength of the
obtained carbon sheet can be ensured. As a result, processability
of the carbon sheet can be increased. On the other hand, a larger
amount of a different material can be supported up to an inner part
of the carbon sheet when the density of the carbon sheet is 1.80
g/cm.sup.3 or less.
[0045] Note that the "density of the carbon sheet" referred to in
the present disclosure is the "bulk density", which can be
determined by measuring the mass, area, and thickness of the carbon
sheet, and then dividing the mass of the carbon sheet by the volume
(area x thickness) of the carbon sheet.
[0046] <<Carbon Nanotubes>>
[0047] The carbon nanotubes contained in the presently disclosed
carbon sheet are not specifically limited and may be single-walled
carbon nanotubes and/or multi-walled carbon nanotubes, but are
preferably CNTs having from 1 to 5 walls, and more preferably
single-walled CNTs. When single-walled CNTs are used, a larger
amount of a different material can be supported on the surfaces of
the carbon nanotubes compared to a case in which multi-walled CNTs
are used.
[0048] The average diameter of the CNTs is preferably 0.5 nm or
more, more preferably 1 nm or more, and even more preferably 2 nm
or more, and is preferably 15 nm or less, more preferably 10 nm or
less, and even more preferably 5 nm or less. When the average
diameter of the CNTs is 0.5 nm or more, sufficient space between
CNTs can be ensured when producing the carbon sheet. This enables
good support of a different material by the CNTs when the carbon
sheet is used as a support for the different material. Moreover,
when the average diameter of the CNTs is 15 nm or less, physical
properties of the carbon sheet, such as electrical conductivity,
can be enhanced.
[0049] Note that the "average diameter of the CNTs" can be
determined by measuring the diameters (external diameters) of 100
randomly selected CNTs using a transmission electron microscope.
Moreover, the average diameter of the CNTs may be adjusted by
altering the production method and production conditions of the
CNTs, or may be adjusted by combining a plurality of types of CNTs
that are obtained by different production methods.
[0050] The aspect ratio (length/diameter) of the CNTs is preferably
more than 10. Note that the aspect ratio of the CNTs can be
determined by measuring the diameters and lengths of 100 randomly
selected CNTs using a transmission electron microscope, and then
calculating an average value of the ratio of diameter and length
(length/diameter).
[0051] The nitrogen adsorption specific surface area of the CNTs is
preferably 600 m.sup.2/g or more, more preferably 800 m.sup.2/g or
more, and even more preferably 1,000 m.sup.2/g or more. Moreover,
the nitrogen adsorption specific surface area of the CNTs is
preferably 2,500 m.sup.2/g or less, and more preferably 1,600
m.sup.2/g or less. When the nitrogen adsorption specific surface
area of the CNTs is 600 m.sup.2/g or more, a larger amount of a
different material can be supported on the surfaces of the carbon
nanotubes in the carbon sheet. Moreover, when the nitrogen
adsorption specific surface area of the CNTs is 2,500 m.sup.2/g or
less, this inhibits excessively dense packing of the CNTs and
enables good support of a different material by the CNTs when the
carbon sheet is used as a support for the different material.
[0052] CNTs having the properties set forth above can be
efficiently produced, for example, by a method in which, during
synthesis of CNTs through chemical vapor deposition (CVD) by
supplying a feedstock compound and a carrier gas onto a substrate
having a catalyst layer for carbon nanotube production at the
surface thereof, a trace amount of an oxidant (catalyst activating
material) is provided in the system so as to dramatically improve
catalytic activity of the catalyst layer (super growth method;
refer to WO 2006/011655 A1). Hereinafter, carbon nanotubes that are
obtained by the super growth method are also referred to as
"SGCNTs".
[0053] <<Porous Substrate Made From Carbon>>
[0054] The porous substrate made from carbon is composed of only a
carbon material.
[0055] Note that "only" in the above description does not rule out
the inclusion of small amounts of components other than the carbon
material, such as impurities.
[0056] Examples of the porous substrate made from carbon include,
but are not specifically limited to, graphite, woven fabric or
non-woven fabric of carbon fiber, and carbon paper.
[0057] One of these materials may be used individually, or two or
more of these materials may be used as a mixture.
[0058] Although no specific limitations are placed on the porosity
of the porous substrate made from carbon, the porosity of the
porous substrate is preferably 5% or more, more preferably 40% or
more, and even more preferably 70% or more from a viewpoint of
increasing the porosity of the produced carbon sheet. Moreover, the
porosity of the porous substrate is preferably 90% or less.
[0059] <Production Method of Carbon Sheet Having Defined
Porosity>
[0060] No specific limitations are placed on the production method
of the presently disclosed carbon sheet set forth above. For
example, the production method of the carbon sheet having the
previously described structure (1) may be the following method 1)
and the production method of the carbon sheet having the previously
described structure (2) may be the following method 2).
[0061] 1) A method in which solvent is removed from a dispersion
liquid containing CNTs, spacer particles, and a solvent to obtain a
primary sheet and then the spacer particles are removed from the
primary sheet
[0062] 2) A method in which a porous substrate made from carbon is
impregnated with a dispersion liquid containing CNTs and a solvent
and then the solvent is removed
[0063] Method 1) in which a carbon sheet composed of only CNTs is
obtained is preferable from a viewpoint of providing a lighter
carbon sheet.
[0064] On the other hand, method 2) in which a carbon sheet having
higher porosity is obtained through inclusion of a porous substrate
made from carbon and CNTs attached to the porous substrate is
preferable from a viewpoint of supporting a larger amount of a
different material up to an inner part of the carbon sheet.
[0065] <<Carbon Sheet Production Method 1)>>
[0066] In more detail, carbon sheet production method 1) includes a
step of removing solvent from a dispersion liquid containing CNTs,
spacer particles, and a solvent to obtain a primary sheet
containing the CNTs and the spacer particles (primary sheet
production step) and a step of removing the spacer particles from
the primary sheet (spacer particle removal step).
[0067] [Primary Sheet Production Step]
[0068] In the primary sheet production step, solvent is removed
from a dispersion liquid containing carbon nanotubes, spacer
particles, and a solvent to obtain a primary sheet that contains
the carbon nanotubes and the spacer particles.
[0069] -Dispersion Liquid-
[0070] The dispersion liquid used in production of the primary
sheet is not specifically limited and may be a dispersion liquid
obtained by dispersing an assembly of CNTs and spacer particles in
a solvent using a known method of dispersing treatment.
Specifically, the dispersion liquid may be a dispersion liquid that
contains CNTs, spacer particles, and a solvent, and that optionally
further contains dispersion liquid additives such as a
dispersant.
[0071] --Components in Dispersion Liquid--
[0072] The CNTs may be the CNTs that were previously described in
the "Carbon sheet" section.
[0073] The spacer particles are not specifically limited so long as
they disperse well in the dispersion liquid and are efficiently
removed in the spacer particle removal step.
[0074] Examples of types of spacer particles that can be used
include carbon black, glass particles, titanium oxide particles,
aluminum oxide particles, and resin particles. In a case in which
the spacer particle removal step is implemented through heat
treatment, the spacer particles are preferably resin particles, and
more preferably hollow resin particles from a viewpoint of
efficiently removing the spacer particles through heating.
[0075] Specific examples of resins that can be used as the resin
particles include plastics (polyethylene, polypropylene,
polystyrene, ABS resin, methacrylic resin, polyvinyl chloride,
polyamide, polyacetal, polycarbonate, polybutylene terephthalate,
polyethylene terephthalate, polyphenylene oxide, polyamide-imide,
polyether ether ketone, polyphenylene sulfide,
polytetrafluoroethylene, phenolic resin, urea resin, melamine
resin, unsaturated polyester resin, epoxy resin, etc.), synthetic
rubbers (isoprene rubber, butadiene rubber, styrene-butadiene
rubber, chloroprene rubber, nitrile rubber, polyisobutylene rubber,
ethylene propylene rubber, chlorosulfonated polyethylene, acrylic
rubber, fluororubber, epichlorohydrin rubber, urethane rubber,
silicone rubber, etc.), and natural rubbers.
[0076] One of these resins may be used individually, or two or more
of these resins may be used as a mixture.
[0077] The particle diameter of the spacer particles is not
specifically limited so long as it does not impair formation of the
primary sheet and the carbon sheet in the form of sheets, but is
preferably 5 nm or more, more preferably 10 nm or more, and even
more preferably 100 nm or more, and is preferably 1,000 nm or less,
more preferably 800 nm or less, and even more preferably 600 nm or
less.
[0078] Examples of the solvent of the dispersion liquid (i.e., the
dispersion medium of the CNTs and the spacer particles) include,
but are not specifically limited to, water; alcohols such as
methanol, ethanol, n-propanol, isopropanol (isopropyl alcohol),
n-butanol, isobutanol, t-butanol, pentanol, hexanol, heptanol,
octanol, nonanol, decanol, and amyl alcohol; ketones such as
acetone, methyl ethyl ketone, and cyclohexanone; esters such as
ethyl acetate and butyl acetate; ethers such as diethyl ether,
dioxane, and tetrahydrofuran; amide-based polar organic solvents
such as N,N-dimethylformamide and N-methylpyrrolidone; and aromatic
hydrocarbons such as toluene, xylene, chlorobenzene,
orthodichlorobenzene, and paradichlorobenzene. One of these
solvents may be used individually, or two or more of these solvents
may be used as a mixture.
[0079] Examples of dispersion liquid additives that may optionally
be compounded in the dispersion liquid include additives typically
used in production of dispersion liquids, such as dispersants,
without any specific limitations.
[0080] Note that the additive amount of a dispersion liquid
additive such as a dispersant is preferably low from a viewpoint of
preventing filter paper blocking in a situation in which the
solvent is removed from the dispersion liquid by filtration and a
viewpoint of inhibiting deterioration of physical properties (for
example, electrical conductivity) of the obtained carbon sheet, for
example.
[0081] A surfactant, a synthetic polymer, or a natural polymer can
be adopted as a dispersant used in production of the dispersion
liquid without any specific limitations other than that it enables
dispersion of the CNTs and the spacer particles and can dissolve in
the previously described solvent.
[0082] Examples of surfactants that can be used include sodium
dodecylsulfonate, sodium deoxycholate, sodium cholate, and sodium
dodecylbenzenesulfonate.
[0083] Examples of synthetic polymers that can be used include
polyether diols, polyester diols, polycarbonate diols, polyvinyl
alcohol, partially saponified polyvinyl alcohol, acetoacetyl
group-modified polyvinyl alcohol, acetal group-modified polyvinyl
alcohol, butyral group-modified polyvinyl alcohol, silanol
group-modified polyvinyl alcohol, ethylene-vinyl alcohol
copolymers, ethylene-vinyl alcohol-vinyl acetate copolymer resins,
dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate,
acrylic resins, epoxy resins, modified epoxy resins, phenoxy
resins, modified phenoxy resins, phenoxy ether resins, phenoxy
ester resins, fluororesins, melamine resins, alkyd resins, phenolic
resins, polyacrylamide, polyacrylic acid, polystyrene sulfonic
acid, polyethylene glycol, and polyvinyl pyrrolidone.
[0084] Examples of natural polymers that can be used include
polysaccharides such as starch, pullulan, dextran, dextrin, guar
gum, xanthan gum, amylose, amylopectin, alginic acid, gum Arabic,
carrageenan, chondroitin sulfate, hyaluronic acid, curdlan, chitin,
chitosan, cellulose, and salts and derivatives thereof.
[0085] One of these dispersants may be used individually, or two or
more of these dispersants may be used as a mixture.
[0086] --Properties of Dispersion Liquid--
[0087] The concentration of the CNTs in the dispersion liquid
depends on the type of CNTs that are used, but is preferably not
less than 0.001 mass % and not more than 5 mass %. If the CNT
concentration is less than 0.001 mass %, the amount of carbon sheet
obtained through removal of the solvent and the spacer particles
decreases, and it may not be possible to achieve sufficiently high
production efficiency. Moreover, if the CNT concentration is more
than 5 mass %, dispersibility of the CNTs in the dispersion liquid
may decrease, viscosity of the dispersion liquid increases, and
fluidity of the dispersion liquid decreases.
[0088] --Production of Dispersion Liquid--
[0089] The dispersion liquid can be produced by a known method of
dispersing treatment such as dispersing treatment by a jet mill,
dispersing treatment by high-shear stirring, or dispersing
treatment using a BERYU SYSTEM PRO (product name; produced by Beryu
corp.).
[0090] Also note that addition of the spacer particles to the
dispersion liquid can be performed at any timing without any
specific limitations so long as the desired effects are obtained.
For example, the spacer particles can be added during addition of
the CNTs to the solvent to produce a coarse dispersion liquid.
[0091] -Solvent Removal-
[0092] Known solvent removal methods such as drying and filtration
can be used as the method by which the solvent is removed from the
dispersion liquid without any specific limitations. Of such
methods, the use of drying under reduced pressure, vacuum drying,
or filtration as the solvent removal method is preferable from a
viewpoint of efficiently removing the solvent. Moreover, the
solvent removal method is preferably filtration, and more
preferably filtration under reduced pressure from a viewpoint of
simple and fast removal of the solvent. By quickly and efficiently
removing the solvent, reaggregation of the dispersed CNTs and
spacer particles can be inhibited, and uneven density of the
obtained carbon sheet can be inhibited.
[0093] Note that it is not essential that the solvent in the
dispersion liquid is completely removed, and some of the solvent
may remain so long as the CNTs and spacer particles remaining after
solvent removal are in a state that enables handling thereof as an
assembly (primary sheet).
[0094] [Spacer Particle Removal Step]
[0095] In the spacer particle removal step, the spacer particles
are removed from the primary sheet obtained through the primary
sheet production step described above to obtain a carbon sheet.
[0096] The method by which the spacer particles are removed from
the primary sheet described above is not specifically limited and
may be a known method of removing spacer particles from a
substrate.
[0097] Specifically, a method such as causing detachment of the
spacer particles by imparting physical shock on the primary sheet
or removing the spacer particles by heat treatment may be adopted.
Of these methods, removal of the spacer particles by heat treatment
is preferable from a viewpoint of more efficiently removing the
spacer particles and increasing porosity of an inner part of the
carbon sheet.
[0098] Note that in a case in which a method involving heat
treatment is adopted, the used spacer particles are preferably a
material that is easily removed by heat treatment, such as hollow
resin particles.
[0099] Note that it is not essential that the spacer particles in
the primary sheet are completely removed, and a small amount of the
spacer particles may remain so long as this does not affect the
performance of the carbon sheet obtained after spacer particle
removal.
[0100] <<Carbon Sheet Production Method 2)>>
[0101] In more detail, carbon sheet production method 2) includes a
step of impregnating a porous substrate made from carbon with a
dispersion liquid containing CNTs and a solvent (dispersion liquid
impregnation step) and a step of removing the solvent from the
dispersion liquid-impregnated porous substrate (solvent removal
step). Moreover, the production method 2) may optionally include a
washing step performed once or a plurality of times before and/or
after the solvent removal step. Moreover, in a case in which a
washing step is implemented after the solvent removal step, a
solvent removal step may be implemented once again after the
washing step. Furthermore, washing steps and solvent removal steps
may be implemented repeatedly in carbon sheet production method
2).
[0102] [Dispersion Liquid Impregnation Step]
[0103] In the dispersion liquid impregnation step, a porous
substrate made from carbon is impregnated with a dispersion liquid
containing CNTs and a solvent to obtain a dispersion
liquid-impregnated porous substrate.
[0104] -Dispersion Liquid-
[0105] A dispersion liquid obtained by dispersing an assembly of
CNTs in a solvent by a known method of dispersing treatment can be
adopted without any specific limitations as the dispersion liquid
used in the dispersion liquid impregnation step. Specifically, the
dispersion liquid can be a dispersion liquid that contains CNTs and
a solvent, and that optionally further contains dispersion liquid
additives such as a dispersant.
[0106] --Components of Dispersion Liquid--
[0107] The CNTs, solvent, and dispersion liquid additives used in
the dispersion liquid may be the same as any of those that can be
used in the dispersion liquid used in carbon sheet production
method 1). The properties and production method of the dispersion
liquid may also be the same as those of the dispersion liquid used
in carbon sheet production method 1).
[0108] -Porous Substrate Made From Carbon-
[0109] The porous substrate made from carbon that was previously
described in the "Carbon sheet" section can be adopted as the
porous substrate made from carbon that is used in the dispersion
liquid impregnation step.
[0110] -Method of Impregnation of Porous Substrate Made From Carbon
With Dispersion Liquid-
[0111] Any known method can be adopted as the method by which the
porous substrate made from carbon is impregnated with the
dispersion liquid without any specific limitations so long as the
porous substrate can be uniformly impregnated with the dispersion
liquid. Specifically, a method such as applying the dispersion
liquid onto the porous substrate, spraying the dispersion liquid
onto the porous substrate, or immersing the porous substrate in the
dispersion liquid may be adopted.
[0112] [Solvent Removal Step]
[0113] In the solvent removal step, the solvent is removed from the
dispersion liquid-impregnated porous substrate described above to
obtain a carbon sheet.
[0114] Known solvent removal methods such as drying can be used as
the method by which the solvent is removed from the dispersion
liquid-impregnated porous substrate without any specific
limitations. Of such methods, the use of drying under reduced
pressure or vacuum drying as the solvent removal method is
preferable from a viewpoint of efficiently removing the solvent.
Efficient removal of the solvent can inhibit reaggregation of CNTs
that have been dispersed and can inhibit uneven density of the
obtained carbon sheet.
[0115] [Washing Step]
[0116] Carbon sheet production method 2) may optionally include a
washing step performed once or a plurality of times before and/or
after the solvent removal step described above.
[0117] In the washing step, the dispersion liquid-impregnated
porous substrate obtained through the dispersion liquid
impregnation step or the carbon sheet obtained through the solvent
removal step is washed to remove dispersant, originating from the
dispersion liquid, from the dispersion liquid-impregnated porous
substrate or the carbon sheet.
[0118] The specific method of washing may be a known washing method
without any specific limitations so long as it enables suitable
removal of dispersant from the dispersion liquid-impregnated porous
substrate or the carbon sheet and does not cause detachment of the
CNTs that are attached to the porous substrate made from carbon.
Specifically, a method such as rinsing the dispersion
liquid-impregnated porous substrate or the carbon sheet with a
washing liquid or immersing the dispersion liquid-impregnated
porous substrate or the carbon sheet in a washing liquid may be
adopted.
[0119] The washing liquid used in the washing step described above
is not specifically limited, and the solvent of the dispersion
liquid described above may, for example, be used as the washing
liquid.
[0120] Note that it is not essential that dispersant contained in
the dispersion liquid-impregnated porous substrate or carbon sheet
is completely removed, and the dispersant may remain to the extent
that the desired effects can still be achieved.
[0121] (Carbon Sheet Having Defined Void Fraction)
[0122] The presently disclosed carbon sheet that has a void
fraction within a specific range can display excellent
electromagnetic wave absorption characteristics, and thus can
suitably be adopted as an electromagnetic wave absorbing material
used in an electronic device, a communication device, or the like.
Moreover, the presently disclosed carbon sheet that has a void
fraction within a specific range can display excellent infrared
absorption characteristics, and thus can suitably be adopted as an
infrared absorbing material used in a heat proof sheet or the
like.
[0123] <Carbon Sheet>
[0124] The presently disclosed carbon sheet has excellent
electromagnetic wave absorption characteristics and infrared
absorption characteristics as a result of containing one or more
carbon nanotubes and having a void fraction that is within a
specific range. The presently disclosed carbon sheet that has a
void fraction within a specific range is a sheet that contains only
carbon. The phrase "only carbon" used in the above description does
not rule out the inclusion of small amounts of components other
than carbon, such as impurities.
[0125] <<Structure of Carbon Sheet>>
[0126] Specifically, the presently disclosed carbon sheet that has
a void fraction within a specific range may have a structure such
as (3) a structure in which only carbon nanotubes are intertwined
in a manner such that the void fraction is not less than 30% and
not more than 95%.
[0127] <<Properties of Carbon Sheet>>
[0128] The carbon sheet preferably also has the following
properties.
[0129] [Void Fraction]
[0130] The void fraction in the presently disclosed carbon sheet
that has a void fraction within a specific range is required to be
30% or more, and is preferably 35% or more, and more preferably 40%
or more. Moreover, the void fraction is required to be 95% or less,
and is preferably 94% or less, and more preferably 93% or less.
When the void fraction of the carbon sheet is 30% or more,
electromagnetic wave absorption characteristics and infrared
absorption characteristics of the carbon sheet can be further
enhanced. Moreover, when the void fraction is 95% or less,
sufficient free-standing ability of the carbon sheet can be
ensured, and thus a carbon sheet having good handleability and
processability can be provided.
[0131] [Porosity]
[0132] In addition to having a void fraction that is within any of
the specific ranges set forth above, the presently disclosed carbon
sheet may have a specific porosity such as previously described in
the "Carbon sheet having defined porosity" section. In other words,
the porosity in the presently disclosed carbon sheet that has a
void fraction within a specific range may be within any of the
specific ranges previously described in the "Carbon sheet having
defined porosity" section.
[0133] Specifically, the porosity of the presently disclosed carbon
sheet that has a void fraction within a specific range is
preferably 5% or more, more preferably 40% or more, even more
preferably 48% or more, and further preferably 70% or more.
Moreover, the porosity is preferably 90% or less, and more
preferably 88% or less. When the porosity of the carbon sheet is 5%
or more, sufficient space in an inner part of the carbon sheet can
be ensured, and good support of a different material up to the
inner part of the carbon sheet can be achieved when the carbon
sheet is used as a support for the different material. Moreover,
when the porosity is 90% or less, sufficient free-standing ability
of the carbon sheet can be ensured, and thus a carbon sheet having
good handleability and processability can be provided.
[0134] [Thickness]
[0135] The thickness of the carbon sheet is preferably 2 .mu.m or
more, more preferably 5 .mu.m or more, and even more preferably 10
.mu.m or more. Moreover, the thickness of the carbon sheet is
preferably 5,000 .mu.m or less, more preferably 4,500 .mu.m or
less, and even more preferably 4,000 .mu.m or less. When the
thickness of the carbon sheet is 2 .mu.m or more, strength of the
obtained carbon sheet can be ensured. As a result, processability
of the carbon sheet can be increased. On the other hand, good
handleability of the obtained carbon sheet can be maintained when
the thickness of the carbon sheet is 5,000 .mu.m or less.
[0136] [Density]
[0137] The density of the carbon sheet is preferably 0.01
g/cm.sup.3 or more, more preferably 0.1 g/cm.sup.3 or more, and
even more preferably 0.50 g/cm.sup.3 or more, and is preferably
1.80 g/cm.sup.3 or less, more preferably 1.50 g/cm.sup.3 or less,
and even more preferably 1.20 g/cm.sup.3 or less. When the density
of the carbon sheet is 0.01 g/cm.sup.3 or more, strength of the
obtained carbon sheet can be ensured. As a result, processability
of the carbon sheet can be increased. On the other hand,
electromagnetic wave absorption characteristics and infrared
absorption characteristics of the carbon sheet can be further
enhanced when the density of the carbon sheet is 1.80 g/cm.sup.3 or
less.
[0138] Note that the "density of the carbon sheet" referred to in
the present disclosure is the "bulk density", which can be
determined by measuring the mass, area, and thickness of the carbon
sheet, and then dividing the mass of the carbon sheet by the volume
(area.times.thickness) of the carbon sheet.
[0139] <<Carbon Nanotubes>>
[0140] The carbon nanotubes contained in the presently disclosed
carbon sheet are not specifically limited and may be single-walled
carbon nanotubes and/or multi-walled carbon nanotubes, but are
preferably CNTs having from 1 to 5 walls, and more preferably
single-walled CNTs. By using single-walled CNTs, electromagnetic
wave absorption characteristics and infrared absorption
characteristics of the carbon sheet can be further enhanced
compared to a case in which multi-walled CNTs are used.
[0141] The average diameter of the CNTs is preferably 0.5 nm or
more, more preferably 1 nm or more, and even more preferably 2 nm
or more, and is preferably 15 nm or less, more preferably 10 nm or
less, and even more preferably 5 nm or less. When the average
diameter of the CNTs is 0.5 nm or more, sufficient space between
the CNTs can be ensured when producing the carbon sheet. Moreover,
when the average diameter of the CNTs is 15 nm or less, physical
properties such as electromagnetic wave absorption characteristics,
infrared absorption characteristics, and electrical conductivity of
the carbon sheet can be enhanced.
[0142] Note that the "average diameter of the CNTs" can be
determined by measuring the diameters (external diameters) of 100
randomly selected CNTs using a transmission electron microscope.
Moreover, the average diameter of the CNTs may be adjusted by
altering the production method and production conditions of the
CNTs, or may be adjusted by combining a plurality of types of CNTs
that are obtained by different production methods.
[0143] The aspect ratio (length/diameter) of the CNTs is preferably
more than 10. Note that the aspect ratio of the CNTs can be
determined by measuring the diameters and lengths of 100 randomly
selected CNTs using a transmission electron microscope, and then
calculating an average value of the ratio of diameter and length
(length/diameter).
[0144] The nitrogen adsorption specific surface area of the CNTs is
preferably 600 m.sup.2/g or more, more preferably 800 m.sup.2/g or
more, and even more preferably 1,000 m.sup.2/g or more. Moreover,
the nitrogen adsorption specific surface area of the CNTs is
preferably 2,500 m.sup.2/g or less, and more preferably 1,600
m.sup.2/g or less. When the nitrogen adsorption specific surface
area of the CNTs is within any of the ranges set forth above,
electromagnetic wave absorption characteristics and infrared
absorption characteristics of the carbon sheet can be further
enhanced.
[0145] CNTs having the properties set forth above can be
efficiently produced, for example, by a method in which, during
synthesis of CNTs through chemical vapor deposition (CVD) by
supplying a feedstock compound and a carrier gas onto a substrate
having a catalyst layer for carbon nanotube production at the
surface thereof, a trace amount of an oxidant (catalyst activating
material) is provided in the system so as to dramatically improve
catalytic activity of the catalyst layer (super growth method;
refer to WO 2006/011655 A1). Hereinafter, carbon nanotubes that are
obtained by the super growth method are also referred to as
"SGCNTs".
[0146] <Production Method of Carbon Sheet Having Defined Void
Fraction>
[0147] The method by which the presently disclosed carbon sheet set
forth above is produced is not specifically limited but is
preferably the following method 3), for example, from a viewpoint
of producing a carbon sheet that has a void fraction within any of
the specific ranges set forth above.
[0148] 3) A method in which solvent is removed from a dispersion
liquid obtained by dispersing CNTs in a solvent
[0149] <<Carbon Sheet Production Method 3)>>
[0150] In more detail, carbon sheet production method 3) includes a
step of dispersing CNTs in a solvent to obtain a dispersion liquid
(dispersion liquid production step) and a step of removing the
solvent from the dispersion liquid (solvent removal step).
[0151] [Dispersion Liquid Production Step]
[0152] In the dispersion liquid production step, CNTs are dispersed
in a solvent to obtain a CNT dispersion liquid.
[0153] The CNTs may be the CNTs that were previously described in
the "Carbon sheet" section.
[0154] Moreover, the solvent may be any of the previously described
solvents that can be used in carbon sheet production method 1).
[0155] The method by which the CNTs are dispersed in the solvent is
not specifically limited and may be a known method of dispersing
treatment such as dispersing treatment by ultrasound, dispersing
treatment by a jet mill, dispersing treatment by high-shear
stirring, or dispersing treatment using a BERYU SYSTEM PRO (product
name; produced by Beryu corp.).
[0156] The CNTs in the obtained CNT dispersion liquid are normally
present in the form of "bundles" in which a plurality of CNTs are
assembled.
[0157] The average bundle diameter of the CNTs can be adjusted by
altering the method of the above-described dispersing treatment,
the conditions thereof, and so forth.
[0158] The average bundle diameter of the CNTs in the CNT
dispersion liquid is preferably 0.5 .mu.m or more, and is
preferably 1,000 .mu.m or less, and more preferably 100 .mu.m or
less. When the average bundle diameter of the CNTs in the CNT
dispersion liquid is 0.5 .mu.m or more, the void fraction of the
produced carbon sheet can be sufficiently increased. On the other
hand, an excessive increase in the void fraction of the produced
carbon sheet can be inhibited when the average bundle diameter of
the CNTs in the CNT dispersion liquid is 1,000 .mu.m or less.
Therefore, it easy to keep the void fraction of the produced carbon
sheet within any of the specific ranges set forth above when the
average bundle diameter of the CNTs dispersed in the solvent is
within any of the specific ranges set forth above.
[0159] Note that the average bundle diameter of the CNTs can be
measured by a method described in the EXAMPLES section of the
present specification.
[0160] [Solvent Removal Step]
[0161] In the solvent removal step, the solvent is removed from the
CNT dispersion liquid to obtain a carbon sheet.
[0162] The method by which the solvent is removed from the
dispersion liquid may be any of the previously described methods
that can be used in the solvent removal step of carbon sheet
production method 1).
EXAMPLES
[0163] The following provides a more specific description of the
present disclosure based on examples. However, the present
disclosure is not limited to the following examples.
[0164] In the examples and comparative examples, the following
methods were used to evaluate the free-standing ability, electrical
conductivity, porosity, air permeability, thickness, density (bulk
density), void fraction, electromagnetic wave absorption
characteristics, and infrared absorption characteristics of a
carbon sheet, and the average bundle diameter of CNTs.
[0165] <Free-Standing Ability of Carbon Sheet>
[0166] A produced carbon sheet was inspected by eye to confirm
whether or not the carbon sheet maintained a film state on its own,
and the free-standing ability of the carbon sheet was evaluated by
the following standard.
[0167] A: Maintains film state as a single film (has free-standing
ability)
[0168] B: Does not maintain film state as a single film (does not
have free-standing ability)
[0169] <Electrical Conductivity>
[0170] The electrical conductivity of a produced carbon sheet was
measured by a four-pin method (produced by Mitsubishi Chemical
Analytech Co., Ltd.; product name: Loresta GX).
[0171] <Porosity>
[0172] The porosity of a produced carbon sheet was measured by
mercury intrusion porosimetry (AutoPore IV 9510 produced by
Shimadzu Corporation).
[0173] <Air Permeability>
[0174] The air permeability of a produced carbon sheet was measured
by the Frazier method and was evaluated by the following standard.
In a case in which the air permeability of the carbon sheet is not
less than 5 cc/cm.sup.2/s and not more than 60 cc/cm.sup.2/s, a
different material can be well supported up to an inner part of the
sheet when the carbon sheet is used as a support for the different
material. On the other hand, a different material cannot be
supported up to an inner part of the carbon sheet when the air
permeability is less than 5 cc/cm.sup.2/s, and mechanical strength
of the carbon sheet decreases when the air permeability is more
than 60 cc/cm.sup.2/s.
[0175] A: Air permeability of not less than 5 cc/cm.sup.2/s and not
more than 60 cc/cm.sup.2/s
[0176] B: Air permeability of less than 5 cc/cm.sup.2/s or more
than 60 cc/cm.sup.2/s
[0177] <Thickness, Density (Bulk Density), and Void
Fraction>
[0178] A 1 cm square was cut out from a produced carbon sheet. The
thickness of the obtained test specimen was measured using a
micrometer (Digimatic Standard Outside Micrometer produced by
Mitutoyo Corporation) and was taken to be the thickness of the
carbon sheet.
[0179] Next, the mass (g) of the test specimen was measured, and
the density (bulk density) of the carbon sheet was calculated by
the following formula (1).
Carbon sheet bulk density (g/cm.sup.3)=Test specimen mass (g)/{1
cm.sup.2.times.Test specimen thickness (cm)} (1)
[0180] The obtained bulk density was then used to calculate the
void fraction of the carbon sheet by the following formula (2).
Void fraction=[1-{Carbon sheet bulk density
(g/cm.sup.3)/1.3}].times.100 (2)
[0181] Note that "1.3" in formula (2) is the true density
(g/cm.sup.3) of carbon.
[0182] <Average Bundle Diameter of CNTs>
[0183] An obtained dispersion liquid was applied onto a silicon
base plate and bundles of assembled CNTs were observed using a
scanning electron microscope (SEM; JSM-7800F Prime produced by JEOL
Ltd.). One hundred bundles were randomly selected, the bundle
diameters thereof were measured, and an average value of the
measured bundle diameters was taken to be a value for the average
bundle diameter of CNTs.
[0184] <Electromagnetic Wave Absorption Characteristics>
[0185] The free space method was used to measure electromagnetic
wave absorption (dB) of a produced carbon sheet in a millimeter
wave band (W-band: 60 GHz to 120 GHz). Electromagnetic wave
absorption characteristics of the carbon sheet were evaluated by
the following standard based on results for electromagnetic wave
absorption at 80 GHz and 110 GHz.
[0186] A: Electromagnetic wave absorption of 5 dB or more
[0187] B: Electromagnetic wave absorption of less than 5 dB
[0188] <Infrared Absorption Characteristics>
[0189] Infrared absorption (%) of a produced carbon sheet in a
range of 3 .mu.m to 15 .mu.m was measured by total reflection
measurement using an integrating sphere. Infrared absorption
characteristics of the carbon sheet were evaluated by the following
standard.
[0190] A: Infrared absorption of 90% or more
[0191] B: Infrared absorption of less than 90%
Example 1-1
<Production of Carbon Sheet>
[0192] A coarse dispersion liquid was obtained by weighing out 400
mg of CNTs (produced by Zeon Nanotechnology Co., Ltd.; product
name: ZEONANO.RTM. SG101 (ZEONANO is a registered trademark in
Japan, other countries, or both); SGCNTs including mainly
single-walled CNTs; average diameter: 3.3 nm; nitrogen adsorption
specific surface area: 1,000 m.sup.2/g or more) and 100 mg in terms
of solid content of a hollow latex (Nipol MH5055 produced by ZEON
CORPORATION; average particle diameter: 500 nm) as spacer
particles, mixing these materials in 2 L of methyl ethyl ketone as
a solvent, and then performing stirring thereof for 2 minutes using
a homogenizer. A wet-type jet mill (JN-20 produced by Jokoh Co.,
Ltd.) was used to disperse the CNTs in the methyl ethyl ketone
through two cycles of passing the obtained coarse dispersion liquid
along a 0.5 mm flow channel of the wet-type jet mill at a pressure
of 100 MPa so as to obtain a dispersion liquid A. The obtained
dispersion liquid A was filtered under reduced pressure using
Kiriyama filter paper (No. 5A) to obtain a primary sheet.
[0193] The obtained primary sheet was subjected to 12 hours of heat
treatment at 350.degree. C. to remove the hollow latex particles
and obtain a carbon sheet having a thickness of 100 .mu.m and a
density of 1.15 g/cm.sup.3.
[0194] The obtained carbon sheet was used to evaluate free-standing
ability, electrical conductivity, porosity, and air permeability of
the sheet. The results are shown in Table 1.
<Production of Metal Oxide-Supporting Sheet>
[0195] A solution of 2 g of titanium(IV) butoxide (produced by Wako
Pure Chemical Industries, Ltd.) and 20 g of isopropyl alcohol was
prepared, a 20 mm square of the produced carbon sheet was immersed
in this solution, and treatment thereof was performed for 10
minutes in a planetary mill (Thinky Mixer AR-100 produced by Thinky
Corporation). Next, a solution of 0.5 g of lithium acetate
(produced by Tokyo Chemical Industry Co., Ltd.), 1 g of acetic
acid, 1 g of pure water, and 3 g of isopropyl alcohol was added,
and a further 10 minutes of treatment was performed. Thereafter,
the produced carbon sheet was removed from the planetary mill, was
dried under reduced pressure at 80.degree. C. for 10 hours, and was
subsequently heat treated at 400.degree. C. in a nitrogen
atmosphere to obtain a carbon sheet supporting a metal oxide (metal
oxide-supporting sheet). A cross-section of the produced metal
oxide-supporting sheet was cut using a cryomicrotome and was then
observed using a scanning electron microscope. It was confirmed
that a metal oxide having an average diameter of 27 nm was
supported at the sheet surface.
Examples 1-2 and 1-3
[0196] A carbon sheet was produced in the same way as in Example
1-1 and the same evaluations were performed with the exception that
the additive amount of the spacer particles was changed such that
the porosity of the carbon sheet was a value shown in Table 1. The
results are shown in Table 1.
[0197] Moreover, treatment was performed in the same way as in
Example 1-1 to produce a metal oxide-supporting sheet, and the
average diameter of the metal oxide was measured. The result is
shown in Table 1.
Example 1-4
[0198] A coarse dispersion liquid was obtained by weighing out 1.0
g of CNTs (produced by Zeon Nanotechnology Co., Ltd.; product name:
ZEONANO.RTM. SG101; SGCNTs including mainly single-walled CNTs;
average diameter: 3.3 nm; nitrogen adsorption specific surface
area: 1,000 m.sup.2/g or more), and mixing these CNTs with 500 mL
of a 1 mass % aqueous solution of sodium dodecylbenzenesulfonate
(SDBS) as a solvent containing a dispersant.
[0199] The obtained coarse dispersion liquid was loaded into a
high-pressure homogenizer (produced by Beryu corp.; product name:
BERYU SYSTEM PRO) including a multistage pressure control device
(multistage depressurizer) for applying back pressure during
dispersing, and was subjected to dispersing treatment at a pressure
of 100 MPa.
[0200] Specifically, the CNTs were dispersed by imparting shear
force to the coarse dispersion liquid while also applying back
pressure. Note that this dispersing treatment was performed for 10
minutes while returning out-flowing dispersion liquid back into the
high-pressure homogenizer. A dispersion liquid B was obtained
through the dispersing treatment described above.
[0201] Carbon paper (produced by Toray Industries, Inc.; product
name: TGP-H-090; porosity: 78%) was impregnated with the obtained
dispersion liquid B, and then the dispersion liquid B-impregnated
carbon paper was washed with isopropyl alcohol (IPA) and pure water
in this order to remove SDBS used as a dispersant. Vacuum drying
was subsequently performed at 80.degree. C. for 24 hours to obtain
a carbon sheet.
[0202] The obtained carbon sheet was used to perform the same
evaluations. The results are shown in Table 1.
[0203] In addition, treatment was performed in the same way as in
Example 1-1 to produce a metal oxide-supporting sheet, and the
average diameter of the metal oxide was measured. The result is
shown in Table 1.
Comparative Example 1-1
[0204] A carbon sheet was produced in the same way as in Example
1-1 and the same evaluations were performed with the exception that
spacer particles were not added. The results are shown in Table
1.
[0205] In addition, treatment was performed in the same way as in
Example 1-1 to produce a metal oxide-supporting sheet. When the
metal oxide was observed, metal oxide had not been formed in an
inner part of the sheet.
TABLE-US-00001 TABLE 1 Supported Sheet particle free- Electrical
average Porosity standing conductivity Air diameter Sheet structure
(%) ability (S/cm) permeability (nm) Example 1-1 Only CNTs 8 A 150
A 27 Example 1-2 Only CNTs 48 A 88 A 19 Example 1-3 Only CNTs 70 A
33 A 15 Example 1-4 CNTs + Porous 88 A 53 A 11 substrate made from
carbon Comparative Only CNTs 0 A 240 B Example 1-1
Example 2-1
[0206] A dispersion liquid was obtained by adding 20 mg of CNTs
(produced by Zeon Nanotechnology Co., Ltd.; product name:
ZEONNANO.RTM. SG101; SGCNTs including mainly single-walled CNTs;
average diameter: 3.3 nm; nitrogen adsorption specific surface
area: 1,000 m.sup.2/g or more) to 20 mL of isopropyl alcohol (IPA),
and then performing dispersing treatment thereof for 20 minutes in
a bath-type ultrasonic disperser. The average bundle diameter of
CNTs in the obtained dispersion liquid was 100 .mu.m. The obtained
dispersion liquid was loaded into a reduced pressure filtration
device including a membrane filter and was filtered at 0.09 MPa.
The membrane filter was then peeled off to obtain a carbon sheet.
The void fraction, electromagnetic wave absorption characteristics,
and infrared absorption characteristics of the obtained carbon
sheet were measured and evaluated. The results are shown in Table
2. The measured thickness of the obtained carbon sheet was 3,390
.mu.m and the measured density of the obtained carbon sheet was 0.1
g/cm.sup.3.
Example 2-2
[0207] A carbon sheet was produced in the same way as in Example
2-1 and the same measurements and evaluations were performed with
the exception that the dispersing treatment time was changed from
20 minutes to 40 minutes such that the average bundle diameter of
CNTs in the obtained dispersion liquid changed from 100 .mu.m to 1
.mu.m. The results are shown in Table 2. The measured thickness of
the obtained carbon sheet was 1,870 .mu.m and the measured density
of the obtained carbon sheet was 0.4 g/cm.sup.3.
Example 2-3
[0208] A carbon sheet was produced in the same way as in Example
2-1 and the same measurements and evaluations were performed with
the exception that the dispersing treatment time was changed from
20 minutes to 60 minutes such that the average bundle diameter of
CNTs in the obtained dispersion liquid changed from 100 .mu.m to
0.5 .mu.m. The results are shown in Table 2. The measured thickness
of the obtained carbon sheet was 850 .mu.m and the measured density
of the obtained carbon sheet was 0.7 g/cm.sup.3.
Comparative Example 2-1
[0209] A dispersion liquid was obtained by adding 200 mg of sodium
dodecyl sulfate (Sodium Dodecyl Sulfate produced by FUJIFILM Wako
Pure Chemical Corporation) as a surfactant and 20 mg of CNTs
(produced by Zeon Nanotechnology Co., Ltd.; product name:
ZEONNANO.RTM. SG101; SGCNTs including mainly single-walled CNTs;
average diameter: 3.3 nm; nitrogen adsorption specific surface
area: 1,000 m.sup.2/g or more) to 20 mL of pure water, and then
performing dispersing treatment thereof for 60 minutes in a
bath-type ultrasonic disperser. The average bundle diameter of CNTs
in the obtained dispersion liquid was 0.05 .mu.m. The obtained
dispersion liquid was loaded into a reduced pressure filtration
device including a membrane filter and was filtered at 0.09 MPa.
The membrane filter was then peeled off to obtain a carbon sheet.
The void fraction, electromagnetic wave absorption characteristics,
and infrared absorption characteristics of the obtained carbon
sheet were measured and evaluated. The results are shown in Table
2. The measured thickness of the obtained carbon sheet was 102
.mu.m and the measured density of the obtained carbon sheet was 1.0
g/cm.sup.3.
TABLE-US-00002 TABLE 2 Average bundle Void Electromagnetic wave
Infrared absorption diameter of CNTs in fraction absorption
characteristics characteristics dispersion liquid [.mu.m] [%] 80
GHz 110 GHz (3 .mu.m to 15 .mu.m) Example 2-1 100 92 A A A Example
2-2 1 85 A A A Example 2-3 0.5 42 A A A Comparative 0.05 23 B B B
Example 2-1
[0210] It can be seen from Table 1 that the carbon sheets of
Examples 1-1 to 1-4, which each contain carbon nanotubes and have a
porosity of not less than 5% and not more than 90%, have
free-standing ability, have an air permeability within a range of 5
cc/cm.sup.2/s to 60 cc/cm.sup.2/s, and have supported particles
observed in an inner part of the sheet when used to support a metal
oxide, and thus the carbon sheets of Examples 1-1 to 1-4 are
materials that have excellent handleability and processability, and
that when used as a support for a different material, enable
support of the different material up to an inner part thereof.
[0211] It can also be seen that compared to Examples 1-1 to 1-4,
the carbon sheet of Comparative Example 1-1, which has a porosity
that does not satisfy the specific range, has an air permeability
that is not within the aforementioned range and does not have
supported particles observed in an inner part of the sheet when the
carbon sheet is used to support a metal oxide, and thus has poor
performance in terms of supporting a different material up to an
inner part of the carbon sheet.
[0212] It can be seen from Table 2 that the carbon sheets of
Examples 2-1 to 2-3, which each contain carbon nanotubes and have a
void fraction of not less than 30% and not more than 95%, have
excellent electromagnetic wave absorption characteristics and
infrared absorption characteristics.
[0213] It can also be seen that the carbon sheet of Comparative
Example 2-1, which does not have a void fraction within the
specific range, has poor electromagnetic wave absorption
characteristics and infrared absorption characteristics compared to
the carbon sheets of Examples 2-1 to 2-3.
INDUSTRIAL APPLICABILITY
[0214] Through the presently disclosed carbon sheet, it is possible
to provide a material that has excellent handleability and
processability, and that when used as a support for a different
material, enables support of the different material up to an inner
part thereof.
[0215] Moreover, through the presently disclosed carbon sheet, it
is possible to provide a material that has excellent
electromagnetic wave absorption characteristics and infrared
absorption characteristics.
* * * * *