U.S. patent application number 17/605015 was filed with the patent office on 2022-05-12 for dual cure composition.
The applicant listed for this patent is Dow Silicones Corporation. Invention is credited to David M. ALTERGOTT, Junying LIU, Steven SWIER.
Application Number | 20220145020 17/605015 |
Document ID | / |
Family ID | |
Filed Date | 2022-05-12 |
United States Patent
Application |
20220145020 |
Kind Code |
A1 |
LIU; Junying ; et
al. |
May 12, 2022 |
DUAL CURE COMPOSITION
Abstract
A composition contains: (a) a silicon-free mercapto compound
comprising 2 or more mercapto groups; (b) a linear
polyorganosiloxane containing one or more than one terminally
unsaturated alkenyl group, 40 mole-percent or more phenyl groups
relative to moles of silicon atoms and at least one alkoxysilyl
group per molecule; (c) a resinous polyorganosiloxane containing
one or more than one terminally unsaturated alkenyl group and 20
mole-percent or more phenyl groups relative to moles of silicon
atoms; (d) a photoinitiator; and (e) a moisture cure catalyst; and
wherein the molar ratio of mercapto groups to terminally
unsaturated alkenyl groups in the composition is in a range of 0.3
to 2.0.
Inventors: |
LIU; Junying; (Auburn,
MI) ; ALTERGOTT; David M.; (Bay City, MI) ;
SWIER; Steven; (Midland, MI) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Dow Silicones Corporation |
Midland |
MI |
US |
|
|
Appl. No.: |
17/605015 |
Filed: |
August 3, 2020 |
PCT Filed: |
August 3, 2020 |
PCT NO: |
PCT/US2020/044708 |
371 Date: |
October 20, 2021 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
62883141 |
Aug 6, 2019 |
|
|
|
International
Class: |
C08J 3/24 20060101
C08J003/24; C08L 83/04 20060101 C08L083/04; C08K 5/37 20060101
C08K005/37; C08K 5/5419 20060101 C08K005/5419; C08G 77/08 20060101
C08G077/08; C08G 77/18 20060101 C08G077/18; C08G 77/20 20060101
C08G077/20; C08G 77/00 20060101 C08G077/00 |
Claims
1. A composition comprising: a. a silicon-free mercapto compound
comprising 2 or more mercapto groups; b. a linear
polyorganosiloxane containing one or more linear polyorganosiloxane
having one or more than one terminally unsaturated alkenyl group,
40 mole-percent or more phenyl groups relative to moles of silicon
atoms and at least one alkoxysilyl group per molecule; c. a
resinous polyorganosiloxane containing at least one terminally
unsaturated alkenyl group and 20 mole-percent or more phenyl groups
relative to moles of silicon atoms; d. a photoinitiator; and e. a
moisture cure catalyst; and wherein the molar ratio of mercapto
groups to terminally unsaturated alkenyl groups in the composition
is in a range of 0.3 to 2.0.
2. The composition of claim 1, wherein: a. the silicon-free
mercapto compound is present at a concentration of 5 to 45
weight-percent based on composition weight; b. the linear
polyorganosiloxane has the following formula:
(R.sup.1R.sub.2SiO.sub.1/2)(R.sup.2.sub.2SiO.sub.2/2).sub.a'(Ph-
RSiO.sub.2/2).sub.a(XR.sub.2SiO.sub.1/2) where: R is independently
in each occurrence selected from a group consisting of C.sub.2-8
terminally unsaturated alkenyl groups, C.sub.1-8 alkyl groups,
C.sub.1-8 substituted alkyl groups and phenyl groups; R.sup.1 is
selected from C.sub.2-8 terminally unsaturated alkenyl groups;
R.sup.2 is independently in each occurrence selected from a group
consisting of C.sub.2-8 terminally unsaturated alkenyl groups,
C.sub.1-8 saturated alkyl groups and X; Ph is a phenyl group; X is
an alkoxysilyl group; and subscript a is the average number of
(PhRSiO.sub.2/2) units per molecule and has a value in a range of
2-800; subscript a' is the average number of
((R.sup.2).sub.2SiO.sub.2/2) units per molecule and has a value of
zero or more and 200 or less; provided that the average
concentration of phenyl groups per molecule is 40 mole-percent or
more relative to moles of silicon atoms per molecule; where the
concentration of the linear polyorganosiloxane is 10-80
weight-percent of the composition weight; c. the resinous
polyorganosiloxane has the following formula:
(R.sup.5.sub.3SiO.sub.1/2).sub.w(R.sup.5.sub.2SiO.sub.2/2).sub.x(R.sup.5S-
iO.sub.3/2).sub.y(SiO.sub.4/2).sub.z where: R.sup.5 is
independently in each occurrence selected from a group consisting
of C.sub.2-8 terminally unsaturated alkenyl groups, C.sub.1-8 alkyl
groups, phenyl groups, alkoxy groups and alkoxysilyl groups;
subscripts w, x, y and z correspond to the average mole-percent of
the corresponding siloxane unit based on moles of siloxane units in
the molecule and subscript w is a value in a range of 0-75, x is a
value in a range of 0-70, y is a value in a range of 0-100 and z is
a value in a range of 0-60; provide that (w+x+y+z) is 100, (y+z) is
20 or more, (x+w) is 10 or more, and the average concentration of
phenyl groups per molecule is 20 mole-percent or more relative to
mole of silicon atoms and at least one R.sup.5 of a
(R.sup.5.sub.3SiO.sub.1/2) unit is a C.sub.2-8 terminally
unsaturated alkenyl group; where the concentration of the resinous
polyorganosiloxane is 30-70 weight-percent of the composition
weight; d. A photoinitiator is present at a concentration of 0.01
to 5.0 weight-percent based on composition weight; and e. A
moisture cure catalyst is present at a concentration of 0.1 to 3.0
weight-percent based on composition weight.
3. The composition of any one previous claim, wherein the
silicon-free mercapto compound contains 3 or more mercapto
groups.
4. The composition of claim 1, wherein the composition comprises a
combination of silicone-free mercapto compounds including a
dimercapto compound and a silicone-free mercapto compound with 3 or
more mercapto groups.
5. The composition of claim 1, wherein the silicon-free dimercapto
compound has the following structure:
HS--(CH.sub.2CH.sub.2O).sub.eCH.sub.2CH.sub.2SH, where subscript e
is the average number of ethoxy units per molecule and is a value
in a range of one to five.
6. The composition of claim 1, wherein the silicon-free dimercapto
compound is present at a concentration of 5 to 45 weight-percent
based on composition weight.
7. The composition of claim 1, the composition further comprising
0.5 wt % or more and 20 wt % or less of an alkoxy silane compound
based on composition weight.
8. The composition of claim 7, wherein the alkoxy silane is a
dialkoxy silane, a trialkoxy silane or a combination thereof.
9. The composition of claim 7, wherein the trialkoxy silane is
methyl trimethoxy silane.
Description
BACKGROUND OF THE INVENTION
Field of the Invention
[0001] The present invention relates to a composition containing a
silicon-free mercapto compound having two or more thiol
functionalities, a linear polyorganosiloxane containing a
terminally unsaturated alkenyl group, an alkoxysilyl group and
phenyl groups and a resinous polyorganosiloxane containing a
terminally unsaturated alkenyl group and phenyl groups.
INTRODUCTION
[0002] Light and moisture dual cure compositions are useful, for
example, in coating, encapsulation, potting and adhesive
applications where exposure of all portions of a coating to light
is difficult yet rapid curing of the coating is desirable. The
moisture cure mechanism serves to cure composition blocked from
exposure to light ("shadow areas"). Dual cure mechanisms are
valuable in coatings to enable moisture curing to complete curing
when light cannot access all areas of a coating.
[0003] Dual cure compositions can comprise (meth)acrylate-based
curing systems. However, (meth)acrylate-based systems are sensitive
to and inhibited by oxygen so inert conditions are necessary during
curing, at least the composition surface. Providing the necessary
inert atmosphere adds undesirable expense and complexity to a
curing process.
[0004] For elastomer and silicone rubber applications, dual cure
compositions can include thiol-ene reactive components (thiol-ene
systems) that participate in light initiated curing instead of
(meth)acrylate-based curing systems. Thiol-ene systems contain
thiol-containing reactants and carbon-carbon double bond
unsaturated reactants. Upon exposure to light the thiol
functionality reacts with and adds across the double bond of the
unsaturated reactant. Dual cure systems utilizing thiol-ene
chemistry typically contain thiol-containing siloxane and
unsaturated siloxane reactants. Thiol-ene reactants have been
limited in application to elastomer and silicone rubber
applications presumably because the miscibility of the thiol-ene
reactive components is insufficient to achieve high enough
crosslink density for hard and scratch resistant cured
compositions. When enough crosslinking functionalities are present
to achieve a hard cured composition, the composition is
inhomogeneous, which results in poor scratch-resistance. It is
valuable to form cured compositions that are both hard and
scratch-resistant to avoid developing defects in the cured
composition as it contacts other objects during and after
processing.
[0005] It would advance the art to identify a thiol-ene based dual
cure composition that produces a cured silicone composition that is
both hard (Shore A hardness of at least 50, preferably at least 60)
and that is scratch-resistant (Pencil Scratch Resistance of at
least 4B).
BRIEF SUMMARY OF THE INVENTION
[0006] The present invention provides a thiol-ene based dual cure
composition that produces a cured silicone composition that is both
hard (Shore A hardness of at least 50, preferably at least 60) and
that is scratch-resistant (Pencil Scratch Resistance of at least
4B).
[0007] The present invention is a result of discovering how to make
thiol components and alkene components more compatible so they can
be present at high enough concentrations to produce coatings with
the specified hardness and be compatible enough to obtain
scratch-resistant coatings. Siloxane thiols and siloxane alkenes
are typically insufficiently compatible to make compositions that
are both hard and scratch-resistant. However, it has now been
discovered as part of this invention that silicon-free thiol
containing components are sufficiently miscible with
phenyl-containing polyorganosiloxane having one or more terminally
unsaturated alkenyl group and one or more alkoxysilyl group
(especially one or more di- and/or trialkoxysilyl group) so as to
form a composition that can dual cure into a coating that is hard
and scratch-resistant.
[0008] Moreover, the present invention has discovered that
compositions containing a combination of silicon-free dimercapto
materials and silicone-free mercapto materials having three or more
mercapto groups can have a low viscosity for ease of processing and
cure to cured compositions having particularly high hardness and/or
scratch-resistance.
[0009] Still more, the present invention is further a result a
discovering that alkoxy silanes can be included as reactive
diluents that lower composition viscosity, while increasing one or
more than one of clarity, hardness and/or scratch-resistance of a
cured composition made from the composition.
[0010] In a first aspect, the present invention is a composition
comprising: (a) a silicon-free mercapto compound comprising 2 or
more, preferably 3 or more mercapto groups; (b) a linear
polyorganosiloxane having one or more than one terminally
unsaturated alkenyl group, 40 mole-percent or more phenyl groups
relative to moles of silicon atoms and at least one alkoxysilyl
group per molecule; (c) a resinous polyorganosiloxane containing
one or more than one terminally unsaturated alkenyl group and 20
mole-percent or more phenyl groups relative to moles of silicon
atoms; (d) a photoinitiator; and (e) a moisture cure catalyst; and
wherein the molar ratio of mercapto groups to terminally
unsaturated alkenyl groups in the composition is in a range of 0.3
to 2.0.
[0011] The composition of the present invention is useful for
making hard and scratch resistant cured composition for use as, for
example, coatings and encapsulating materials.
DETAILED DESCRIPTION OF THE INVENTION
[0012] Test methods refer to the most recent test method as of the
priority date of this document when a date is not indicated with
the test method number. References to test methods contain both a
reference to the testing society and the test method number. The
following test method abbreviations and identifiers apply herein:
ASTM refers to ASTM International; EN refers to European Norm; DIN
refers to Deutsches Institut fur Normung; and ISO refers to
International Organization for Standards.
[0013] "Multiple" means two or more. "And/or" means "and, or as an
alternative". All ranges include endpoints unless otherwise
indicated. Products identified by their tradename refer to the
compositions available from the suppliers under those tradenames at
the priority date of this document unless otherwise stated
herein.
[0014] "Light", in its broadest scope as used herein, refers to
electromagnetic radiation. Preferably, light as used herein refers
to visible and/or ultraviolet (UV) light.
[0015] "Organic compound" a chemical compound that contains
carbon.
[0016] "Polyorganosiloxane" is a compound that contains multiple
siloxane units ("polysiloxane"), at least one of which has an
organic group bonded to at least one silicon atom. Polysiloxanes
comprise multiple siloxane linkages (Si--O--Si) and are typically
characterized by what siloxane units make up the siloxane linkages.
Siloxane units can be selected from a group consisting of M-type,
D-type, T-type and Q units. By convention M units have the formula
(CH.sub.3).sub.3SiO.sub.1/2, D units have the formula
(CH.sub.3).sub.2SiO.sub.2/2, T units have the formula
(CH.sub.3)SiO.sub.3/2 and Q units have the formula SiO.sub.4/2.
M-type, D-type and T-type units refer to conventional units that
may have one or more methyl group replaced with hydrogen, or some
other moiety and are often identified by the siloxane unit letter
designation with a suprascript identifying the moiety replacing a
methyl group. For example, D.sup.Ph refers to a D unit where one of
the methyl groups has been replaced with a phenyl group and
D.sup.PhPh refers to a D unit where each of the two methyl groups
have been replace with a phenyl group. Herein, subscripts used in
resinous polyorganosiloxane formulas indicate the average
mole-percent of the associated siloxane unit relative to all
siloxane units in the molecule, while subscripts used in linear
polyorganosiloxane formulas indicate the average absolute number of
the associated siloxane unit in the molecule.
[0017] "Mercapto" group is a group that contains a sulfur-hydrogen
bond (--SH). Thiol groups are an example of a mercapto group where
an organic group (R) is attached to the mercapto group (R--SH).
[0018] "Acrylic compounds". Materials containing a (meth)acrylate
group. "(meth)acrylate" refers to methacrylate, acrylate and
combinations thereof.
[0019] "Alkylene" is a bivalent saturated aliphatic radical.
Alkylenes can be formed by opening a carbon-carbon double bond or
removal of two hydrogen atoms from different carbon atoms.
[0020] "Terminally unsaturated alkenyl group" refers to an alkenyl
group that has a carbon-carbon double bond between a terminal
carbon and an adjacent carbon at the end of a carbon chain remote
from where the hydrogen atom would have been removed to form the
alkenyl group from a corresponding alkene group. For example, allyl
groups are terminally unsaturated alkenyl groups. For avoidance of
doubt, vinyl groups are also considered terminally unsaturated
alkenyl groups.
[0021] An expression of the form "C.sub.x-y" where x and y are
numbers refers to a component have from x to y carbon atoms.
[0022] Room temperature ("R.T.") is 25 degrees Celsius (.degree.
C.).
[0023] Characterize viscosity of materials at 25.degree. C. using a
Brookfield DV1 viscometer using a CPA-42Z cone spindle.
[0024] Characterize the hardness of a cured composition in terms of
Shore A hardness. Cure 800 micron thick films by irradiating with
two Joules per square centimeters (J/cm.sup.2) of UVA+UVB radiation
followed by allowing to set at 23 degrees Celsius (.degree. C.) for
7 days. Layer films together to get a 6.5 millimeter (mm) thick
stack and use that stack to measure Shore A hardness. Determine
Shore A hardness for the stack according to ASTM D2240.
[0025] Characterize tensile strength of a cured composition by
drawing an 889 micrometer (35 mil) film of the composition onto a
polytetrafluoroethylene sheet and curing using a Colight UV-6 by 3
Joules per square centimeters UV irradiation with 300 milliWatt per
square centimeters intensity followed by 25.degree. C. cure for 7
days. Cut dog bone shaped specimens form the resulting cured film
use Drake dies with 5 mm of gauge width and 2.54 cm shoulder
length. Perform tensile tests on an Instron 5566, averaging results
of at least three replicates.
[0026] Characterize the scratch resistance (Pencil Hardness
Measurement) of the cured compositions in terms of the following
Pencil Scratch Test: Prepare a cured coating of a composition by
casting and curing a 60 micrometers thick coating of a composition
on an FR4 board (glass-reinforced epoxy laminated sheets) and cure
by irradiating with 2 J/cm.sup.2 of UVA+UVB radiation followed by
allowing to set at 23.degree. C. for 7 days. Conduct the
characterization using a BYK-Gardner 5800 Wolf-Wilburn Pencil
Hardness Tester with Derwent graphic pencils. Sharpen each pencil
with a draftsman-type sharpener. Hold the sharpened lead point of
each pencil at a 90 degree angle to horizontal on no. 400 grit
abrasive paper and rub to obtain a smooth, flat, circular
cross-section on the lead tip. Starting with the hardest grade of
lead, place the tip of the pencil lead on a firmly positioned cured
coating at a 45 degree angle relative to the surface of the
coating. Push the pencil over the coating for a distance of at
least 3 mm while applying sufficient pressure to wither scratch the
film or rumple the edge of the lead. Repeat the test on an
undamaged portion of the cured coating with the next softer grade
of lead and continue repeating with softer grades of lead until
testing with a grade of lead that does not scratch the coating. The
hardest grade of lead that does not scratch the coating corresponds
to the level of scratch resistance of the cured coating. The grades
of lead for testing, in order from hardest to softest, is: 9H, 8H,
7H, 6H, 5H, 4H, 3H, 2H, H, F, HB, B, 2B, 3B, 4B, 5B, 6B, 7B, 8B,
9xxB.
[0027] Characterize Coefficient of Friction (CoF) by drawing a 60
micrometer thick film onto a FR4 board and UV and moisture curing
to form a cured film. Place the cured film on the testing surface
of a Texture Analyzer and place a 1056 gram sled and weight on the
same with 2.54 centimeters (cm) by 1.54 cm piece of paper between
the sled and the film. Run the test by moving the sled a distance
of 42 mm along the film at a speed of 2.5 mm per second. The
kinetic coefficient of friction (CoKF) is the average of the forces
between 10 to 15 seconds during the test and is an average of 3-5
replicates of the test.
[0028] Molecular weight refers to weight-average molecular weight
unless otherwise stated. Determine weight-average by triple
detection gel permeation chromatography (GPC) using a Waters 515
pump, a Waters 717 autosampler and Waters 2410 differential
refractometer. Conduct separation with two (300 mm by 7.5 mm)
Polymer Laboratories PLgel 5 micrometer (.mu.m) Mixed-C columns
(molecular weight separation range of 200 to 2,000,000 Daltons),
preceded by a PLgel 5 .mu.m guard column (50 mm by 7.5 mm). Conduct
analysis using HPLC grade toluene flowing at 1.0 milliliter (mL)
per minute as the eluent, with the columns and detector at
45.degree. C. Prepare the samples in toluene at 5 milligrams per mL
concentration, solvate at room temperature for about three hours
with occasional shaking, and filter through 0.45 .mu.m
polytetrafluoroethylene syringe filters prior to analysis. Use an
injection volume of 75 microliters and collect data for 25 minutes.
Perform data collection and analysis using ThermoLabsystems Atlas
chromatography software and Polymer Laboratories Cirrus GPC
software. Determine weight-average molecular weight relative to a
calibration curve (3.sup.rd order) created using polystyrene
standards over a molecular weight range of 580 to 2,300,00
Daltons.
[0029] For polysiloxanes, determine the subscript values for how
many, or molar ratio of, siloxane units using .sup.29Si, .sup.13C
and .sup.1H nuclear magnetic resonance spectroscopy (see, e.g., The
Analytical Chemistry of Silicones, Smith, A. Lee, ed., John Wiley
& Sons: NY, 1991, p. 347ff.).
[0030] The composition of the present invention can contain or be
free of acrylic compounds. (Meth) acrylic-based curing systems
suffer from the fact that they are sensitive to and inhibited by
oxygen. The compositions of the present invention can be free of
acrylic compounds and avoid the need to avoid oxygen as they
cure.
[0031] The compositions of the present invention are useful, for
example, as coating, encapsulating materials, potting and adhesive
materials that can be cured by light and moisture for form a hard
(Shore A hardness of at least 50, preferably at least 60) and
scratch resistant (Pencil Scratch Resistance of at least 4B,
preferably at least 3B) cured material.
[0032] The composition of the present invention comprises: (a) a
silicon-free mercapto compound; (b) a linear polyorganosiloxane
with phenyl and terminally unsaturated alkenyl groups; (c) a
resinous polyorganosiloxane with phenyl and terminally unsaturated
alkenyl groups; (d) a photoinitiator; (e) a moisture cure catalyst:
(f) optionally, an alkoxy silane compound.
[0033] Desirably, the combined weight of components (a), (b) and
(c) is 70 wt % or more, 80 wt % or more, 90 wt % or more, 95 wt %
or more, 98 wt % or more, even 99 wt % or more while at the same
time is less than 100 wt % of the composition weight. Desirably,
determine wt % of components (a), (b) and (c) from the formula used
to make the composition.
[0034] The molar ratio of mercapto groups to terminally unsaturated
alkenyl groups in the composition is desirably 0.03 or more, 0.5 or
more, 1.0 or more, 1.5 or more, 2.0 or more while at the same time
is desirably 2.0 or less. Determine molar ratio of mercapto groups
to unsaturated groups in the composition from the components used
to make the composition.
[0035] Component (a)--Silicon-Free Mercapto Compound
[0036] The composition of the present invention comprises a
silicon-free mercapto compound comprising 2 or more, preferably 3
or more mercapto groups (component (a)). Component (a) serves as a
crosslinking agent as the composition cures, with the mercapto
groups participating in thiol-ene reactions with terminally
unsaturated alkenyl groups on polyorganosiloxanes of component
(b).
[0037] The silicon-free mercapto compound is "silicon-free",
meaning that the compound does not contain silicon atoms. However,
the silicon-free mercapto compound does contain 2 or more and can
contain 3 or more, 4 or more, 5 or more, 6 or more, 7 or more, 8 or
more, 9 or more, even 10 or more mercapto groups and at the same
time, while there is no known technical upper limit to the number
of mercapto groups the silicon-free mercapto compound can contain,
the silicon-free mercapto compound typically contains 10 or fewer,
9 or fewer, 8 or fewer, 7 or fewer, 6 or fewer, and can contain 5
or fewer, even 4 or fewer mercapto groups per molecule. The number
of mercapto group is an average value for all the molecules of the
silicon-free mercapto compound. Determine the number of mercapto
groups per molecule of the silicon-free mercapto compound
preferably from knowledge of the structure of the components used
to prepare the composition. If it is unknown what materials are
used to make the composition, determine the number of mercapto
groups per molecule for component (a) using nuclear magnetic
resonance (NMR) spectroscopy and elemental analysis.
[0038] Component (a) is present in the composition at a
concentration of 5 weight-percent (wt %) or more, 6 wt % or more, 7
wt % or more, 8 wt % or more, 9 wt % or more, 10 wt % or more 12 wt
% or more, 13 wt % or more, 14 wt % or more 16 wt % or more, 18 wt
% or more, 20 wt % or more, 25 wt % or more, 30 wt % or more, 35 wt
% or more or even 40 wt % or more while at the same time is
typically present at a concentration of 45 wt % or less, 40 wt % or
less, 35 wt % or less, 30 wt % or less, 25 wt % or less, 20 wt % or
less, 19 wt % or less, 18 wt % or less, 17 wt % or less, 16 wt % or
less, 15 wt % or less, 10 wt % or less, or even 8 wt % or less
based on composition weight. Determine the wt % of component (a) in
the composition preferably from the formula used to make the
composition. If it is unknown how much of each component was
included in making the composition, determine the wt % of component
(a) by gel permeation chromatography (GPC), NMR and elemental
analysis.
[0039] Component (a) can, and desirably does, comprise or consist
of a combination of silicon-free mercapto compounds that includes
both a dimercapto compound (that is a compound containing 2
mercapto group) and a mercapto compound having 3 or more mercapto
groups.
[0040] Examples of suitable silicon-free dimercapto compounds
include those having the following structure:
HS--(CH.sub.2CH.sub.2O).sub.eCH.sub.2CH.sub.2SH
where subscript "e" is the average value of ethoxy groups per
molecule and has a value in a range of one to five.
[0041] Examples of silicon-free mercapto compounds having 3 or more
mercapto groups include any one or any combination of more than one
compound selected from a group consisting of trimethylolpropane
tris(3-merctopoproprionate) and pentaerythritol tetrakis
(3-mercaptoproprionate).
[0042] Component (b)--Linear Polyorganosiloxane
[0043] The composition of the present invention comprises a linear
polyorganosiloxane containing one or more than one terminally
unsaturated alkenyl group, one or more than one alkoxysilyl group
and 40 mole-percent or more phenyl groups relative to silicon atoms
(component (b)). The linear polyorganosiloxane comprising
predominately D-type siloxane units relative to other siloxane
units. Preferably, the linear polyorganosiloxane consists of M-type
and D-type siloxane units. However, the linear polyorganosiloxane
can comprise an average of zero, one or two T-type or Q-type
siloxane units per molecule.
[0044] Terminally Unsaturated Alkenyl Group. Component (b) has an
average of one or more, preferably 2 or more and can have 3 or
more, 4 or more, 5 or more, 6 or more 7 or more, 8 or more, 9 or
more, or even 10 or more while at the same time typically has 10 or
fewer, 9 or fewer, 8 or fewer, 7 or fewer, 6 or fewer, 5 or fewer,
4 or fewer, 3 or fewer or even 2 or fewer terminally unsaturated
alkenyl groups per molecule. Determine the average number of
terminally unsaturated alkenyl groups per molecule of component (b)
preferably from the identity of the structure of the compound used
for component (b) when preparing the composition. If it is unknown
what compound was used for component (b) in preparing the
composition, determine the number of terminally unsaturated alkenyl
groups per molecule of component (b) by .sup.1H, .sup.13C and
.sup.29Si NMR spectroscopy.
[0045] The terminally unsaturated alkenyl group is typically bonded
to a silicon atom of an M-type or D-type siloxane unit of the
polyorganosiloxane, preferably, an M-type.
[0046] Desirably, the polyorganosiloxane of component (b) has a
terminally unsaturated alkenyl group on one or more, possibly even
two or more terminal silicon atoms. A terminal silicon atom is part
of an M-type unit in the polyorganosiloxane. Desirably, the
terminally unsaturated alkenyl group is itself terminal meaning the
unsaturation is between a terminal and neighboring carbon atom in
the group. For example, the terminally unsaturated alkenyl group is
desirably a vinyl group. The terminally unsaturated alkenyl group
is preferably attached directly to a silicon atom.
[0047] Alkoxysilyl Group. The polyorganosiloxane of component (b)
also contains one or more than one alkoxysilyl group. The
alkoxysilyl groups are needed to participate in the moisture cure
reaction. An alkoxysilyl group has an alkoxy group (--OR) extending
off from a silicon atom, where R is selected from a group
consisting of C.sub.1-8 saturated hydrocarbyl groups (such as, for
example, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl and
octyl groups). Component (b) can have one or more, 2 or more, 3 or
more 4 or more, and even 5 or more alkoxysilyl groups per molecule
while at the same time typically contains 10 or fewer, even 5 or
fewer alkoxysilyl groups per molecule. The number of alkoxysilyl
groups is an average number of alkoxysilyl groups per molecule.
Desirably, determine the average number of alkoxysilyl groups from
the materials used to make a composition of the present invention.
If the materials used to make the composition are unknown,
determine average number of alkoxysilyl groups by NMR spectroscopy
and infrared spectroscopy.
[0048] The alkoxysilyl group can have a single alkoxy attached to a
silicon atom (monoalkoxysilyl), or have two alkoxy groups attached
to single silicon atom (dialkoxy group), or have three alkoxy
groups attached to a single silicon atom (trialkoxy group). The
polyorganosiloxane of component (b) can have any combination of
monoalkoxysilyl groups, dialkoxysilyl groups and trialkoxysilyl
groups. For example, component (b) can only have trialkoxysilyl
groups as the requisite alkoxysilyl group. As an alternative
example, component (b) can have only dialkoxysilyl groups as the
requisite alkoxysilyl group. As yet another alternative example,
component (b) can contain a combination of dialkoxysilyl groups and
trialkoxysilyl groups.
[0049] Desirably, the alkoxysilyl group is terminal to the
polyorganosiloxane to make the alkoxysilyl group most accessible
(for example, least sterically hindered) for participating in
curing reactions. The alkoxy group(s) can be part of a terminal
M-type siloxane unit of the polyorganosiloxane.
[0050] Phenyl Groups. The linear polyorganosiloxane of component
(b) contains phenyl groups, preferably bonded to silicon atoms of
the polyorganosiloxanes backbone. The presence of phenyl groups on
the polyorganosiloxane are believed to be what make component (a)
and component (b) sufficiently compatible so as to enable the
present composition to cure into not only a hard cured composition
but a scratch resistant one as well. If components (a) and (b) are
not sufficiently compatible with one another, then either
insufficient concentrations of each will be present in the
composition to allow curing to a hard cured composition or phase
separation will occur in the composition to such an extent so as to
cause weakness in the cured composition evidenced by poor scratch
resistance.
[0051] To achieve suitable compatibility between the silicon-free
mercapto compound (component a) and the linear polyorganosiloxane
(component b), component b contains 40 mole-percent (mol %) or more
phenyl groups relative to silicon atoms in component (b).
Desirably, component (b) contains 40 mol % or more, 45 mol % or
more, 50 mol % or more, 55 mol % or more, 60 mol % or more, 65 mol
% or more, 70 mol % or more, 75 mol % or more, 80 mol % or more, 90
mol % or more, 99 mol % or more, 100 mol % or more, 110 mol % or
more, 120 mol % or more, 130 mol % or more, 140 mol % or more, and
even 150 mol % or more phenyl groups relative to silicon atoms in
component (b) while at the same time component (b) typically
contains 200 mol % or fewer and can contain 190 mol % or fewer, 180
mol % or fewer, 170 mol % or fewer, 160 mol % or fewer, 150 mol %
or fewer, 140 mol % or fewer, 130 mol % or fewer, 120 mol % or
fewer, 110 mol % or fewer, 100 mol % or fewer, 95 mol % or fewer,
and even 90 mol % or fewer phenyl groups relative to silicon atoms
in component (b). Higher concentrations of phenyl groups seem to be
desirable to increase compatibility between components (a) and (b).
The phenyl groups can be substituted or unsubstituted. An
unsubstituted phenyl group has the formula-C.sub.6H.sub.5 (benzene
with one hydrogen atom removed). A substituted phenyl group is a
phenyl group where one or more than one of the hydrogen atoms has
been replaced with another chemical moiety such as a halide, alkyl,
hydroxyl, or vinyl unsaturated group (such as vinyl). Notably, the
composition as a whole can, and preferably does, have on average a
mol % phenyl groups relative to silicon atoms in the aforementioned
mol %. Desirably, determine the mol % phenyl groups relative to
silicon atoms from the materials used to make a composition of the
present invention. If the materials used to make the composition
are unknown, determine mol % phenyl groups relative to silicon
atoms using .sup.1H, .sup.13C and .sup.29Si NMR spectroscopy.
[0052] The linear polyorganosiloxane desirably has the following
structure:
(R.sup.1R.sub.2SiO.sub.1/2)(R.sup.2.sub.2SiO.sub.2/2).sub.a'(PhRSiO.sub.-
2/2).sub.a(XR.sub.2SiO.sub.1/2)
[0053] where:
[0054] R is independently in each occurrence selected from a group
consisting of C.sub.2-8 terminally unsaturated alkenyl groups,
C.sub.1-8 alkyl groups, C.sub.1-8 substituted alkyl groups and
phenyl groups. Desirably, R is independently in each occurrence
selected from a group consisting of methyl and phenyl groups.
[0055] R.sup.1 is selected from a group consisting of C.sub.2-8
terminally unsaturated alkenyl groups. Examples of suitable
C.sub.2-8 terminally unsaturated alkenyl groups include vinyl,
allyl, butenyl, pentenyl, hexenyl, heptenyl and octenyl. Preferably
R' is selected from a group consisting of vinyl, allyl and hexenyl
groups.
[0056] R.sup.2 is independently in each occurrence selected from a
group consisting of C.sub.2-8 terminally unsaturated alkenyl
groups, C.sub.1-8 saturated alkyl groups (such as, for example,
methyl (--CH.sub.3), ethyl (--CH.sub.2CH.sub.3), propyl
(--CH.sub.2CH.sub.2CH.sub.3), butyl, pentyl, hexyl, heptyl, octyl
groups) and X. Preferably, R.sup.2 is selected from methyl and
vinyl groups.
[0057] Ph is a phenyl group.
[0058] Subscript a is the average number of (PhRSiO.sub.2/2) units
per molecule and is typically 2 or more, preferably 4 or more, 6 or
more, 8 or more, 10 or more, 12 or more, 14 or more, 16 or more, 18
or more, even 20 or more, while at the same time is typically 800
or less and can be 600 or less, 400 or less, 200 or less, 180 or
less, 160 or less, 140 or less, 120 or less, 100 or less, 80 or
less, 60 or less, 50 or less, 40 or less, 25 or less and even 20 or
less.
[0059] Subscript a' is the average number of
((R.sup.2).sub.2SiO.sub.2/2) units per molecule and is a value of
zero or more and can be 2 or more, 3 or more, 4 or more, 5 or more,
6 or more, 7 or more, 8 or more, 9 or more, 10 or more while at the
same time is generally 200 or less and can be 180 or less, 160 or
less, 140 or less, 120 or less, 100 or less, 80 or less, 60 or
less, 40 or less and even 20 or less. Desirably, subscript a' is a
smaller number than subscript a.
[0060] Typically, the linear polyorganosiloxane contains zero or
more and can contain 2 or more, 2 or more, 4 or more, 4 or more, 6
or more, 7 or more, 8 or more, 9 or more even 10 or more while at
the same time typically contains 40 or fewer, 20 or fewer, 10 or
fewer and even 5 or fewer (R.sup.2.sub.2SiO.sub.2/2) units
containing an X group.
[0061] X is an alkoxysilyl group. Each occurrence of X is
independently selected from alkoxysilyl groups, meaning that two X
groups in a molecule can be the same or different alkoxysilyl
group. The alkoxysilyl group can be a monoalkoxysilyl,
dialkoxysilyl, or trialkoxysilyl group.
[0062] One example of a suitable alkoxysilyl group has the
following structure:
--R.sup.3SiR.sub.d[(OSiR.sub.2).sub.e--R.sup.3--SiR.sup.1.sub.c(OR.sup.4-
).sub.3-c].sub.3-d
where: R and R.sup.1 are as defined above; R.sup.3 is independently
in each occurrence selected from a group consisting of C.sub.1-8
saturated alkylene groups (such as, for example, methylene
(--CH.sub.2--), ethylene (--CH.sub.2CH.sub.2--), propylene
(--CH.sub.2CH.sub.2CH.sub.2--), butylene
(--CH.sub.2(CH.sub.2).sub.2CH--), pentylene
(--CH.sub.2(CH.sub.2).sub.3CH--), hexylene
(--CH.sub.2(CH.sub.2).sub.4CH--), heptylene
(--CH.sub.2(CH.sub.2).sub.5CH--), and octylene
(--CH.sub.2(CH.sub.2).sub.6CH--) groups), R.sup.4 is selected from
a group consisting of C.sub.1-8 alkyl groups, C.sub.1-8 substituted
alkyl groups, and subscript c is zero, one or two, and subscript d
is a value of zero, one or two, and subscript e is a value in a
range of 1-3. Desirably, the X group is characterized by the
following: R.sup.4 is methyl, R.sup.3 is ethylene in each
occurrence, R is independently in each occurrence selected from a
group consisting of methyl and ethyl (preferably, R in each
occurrence is methyl), subscript c has a value of zero and
subscript d has a value of one or two (preferably, subscript d is
one).
[0063] An example of a suitable polyorganosiloxane for use as
component (b) has the aforementioned structure where each R is
methyl, R.sup.1 is vinyl, subscript a is 20 and X is:
--CH.sub.2CH.sub.2--Si(CH.sub.3).sub.2OSi(CH.sub.3).sub.2--CH.sub.2CH.su-
b.2--Si(OCH.sub.3).sub.3.
[0064] The linear polyorganosiloxane is typically present in the
composition at a concentration of 10 wt % or more, 20 wt % or more,
30 wt % or more, 40 wt % or more, 50 wt % or more and even 60 wt %
or more while at the same time is typically present at a
concentration of 80 wt % or less, 70 wt % or less, 60 wt % or less,
even 50 wt % or less based on composition weight.
[0065] Component (c)--Resinous Polyorganosiloxane
[0066] In order to achieve the desired hardness in the cured
composition, the present composition also comprises a resinous
polyorganosiloxane (component c). Component c contains one or more
than one terminally unsaturated alkenyl group and 20 mole-percent
or more phenyl groups relative to silicon atom.
[0067] Terminally Unsaturated Alkenyl Group. The resinous
polyorganosiloxane has an average of one or more, preferably 2 or
more and can have 3 or more, 4 or more, 5 or more, 6 or more 7 or
more, 8 or more, 9 or more, or even 10 or more while at the same
time typically has 10 or fewer, 9 or fewer, 8 or fewer, 7 or fewer,
6 or fewer, 5 or fewer, 4 or fewer, 3 or fewer or even 2 or fewer
terminally unsaturated alkenyl groups per molecule. Determine the
average number of terminally unsaturated alkenyl groups per
molecule of the resinous polyorganosiloxane preferably from the
identity of the structure of the compound used for the resinous
polyorganosiloxane when preparing the composition. If it is unknown
what compound was used for the resinous polyorganosiloxane in
preparing the composition, determine the number of terminally
unsaturated alkenyl groups per molecule of the resinous
polyorganosiloxane by .sup.1H, .sup.13C and .sup.29Si NMR
spectroscopy. The terminally unsaturated alkenyl group is typically
bonded to a silicon atom of an M-type, D-type, and/or T-type
siloxane unit, preferably an M-type siloxane unit, of the
polyorganosiloxane.
[0068] Desirably, the polyorganosiloxane of the resinous
polyorganosiloxane has a terminally unsaturated alkenyl group on
one or more, possibly even two or more terminal silicon atoms. A
terminal silicon atom is part of an M-type unit in the
polyorganosiloxane. Desirably, the terminally unsaturated alkenyl
group is itself terminal meaning the unsaturation is between a
terminal and neighboring carbon atom in the group. For example, the
terminally unsaturated alkenyl group is desirably a vinyl group.
The terminally unsaturated alkenyl group is preferably attached
directly to a silicon atom.
[0069] Phenyl Groups. The resinous polyorganosiloxane contains
phenyl groups, preferably bonded to silicon atoms of the
polyorgansiloxanes backbone. The presence of phenyl groups on the
polyorganosiloxane is believed to be what make component (a) and
component (c) sufficiently compatible so as to enable the present
composition to cure into not only a hard cured composition but a
scratch resistant one as well. If components (a) and (c) are not
sufficiently compatible with one another, then either insufficient
concentrations of each will be present in the composition to allow
curing to a hard cured composition or phase separation will occur
in the composition to such an extent so as to cause weakness in the
cured composition evidenced by poor scratch resistance.
[0070] To achieve suitable compatibility between the silicon-free
mercapto compound (component a) and the resinous
polyorganosiloxane, the resinous polyorganosiloxane contains 40
mole-percent (mol %) or more phenyl groups relative to silicon
atoms in the resinous polyorganosiloxane. Desirably, the resinous
polyorganosiloxane contains 20 mol % or more, 25 mol % or more, 30
mol % or more, 35 mol % or more, 40 mol % or more, 45 mol % or
more, 50 mol % or more, 55 mol % or more, 60 mol % or more, 65 mol
% or more, 70 mol % or more, 75 mol % or more, 80 mol % or more, 90
mol % or more, 99 mol % or more, 100 mol % or more, 110 mol % or
more, 120 mol % or more, 130 mol % or more, 140 mol % or more, and
even 150 mol % or more phenyl groups relative to silicon atoms in
the resinous polyorganosiloxane while at the same time the resinous
polyorganosiloxane typically contains 200 mol % or fewer and can
contain 190 mol % or fewer, 180 mol % or fewer, 170 mol % or fewer,
160 mol % or fewer, 150 mol % or fewer, 140 mol % or fewer, 130 mol
% or fewer, 120 mol % or fewer, 110 mol % or fewer, 100 mol % or
fewer, 95 mol % or fewer, and even 90 mol % or fewer phenyl groups
relative to silicon atoms in the resinous polyorganosiloxane.
Higher concentrations of phenyl groups seem to be desirable to
increase compatibility between components (a) and (c). The phenyl
groups can be substituted or unsubstituted. An unsubstituted phenyl
group has the formula --C.sub.6H.sub.5 (benzene with one hydrogen
atom removed). A substituted phenyl group is a phenyl group where
one or more than one of the hydrogen atoms has been replaced with
another chemical moiety such as a halide, alkyl, hydroxyl, or vinyl
unsaturated group (such as vinyl). Notably, the composition as a
whole can, and preferably does, have on average a mol % phenyl
groups relative to silicon atoms in the aforementioned mol %.
Desirably, determine the mol % phenyl groups relative to silicon
atoms from the materials used to make a composition of the present
invention. If the materials used to make the composition are
unknown, determine mol % phenyl groups relative to silicon atoms
using .sup.1H, .sup.13C and .sup.29Si NMR spectroscopy.
[0071] Desirably, the resinous polyorganosiloxane has the following
structure:
(R.sup.5.sub.3SiO.sub.1/2).sub.w(R.sup.5.sub.2SiO.sub.2/2).sub.x(R.sup.5-
SiO.sub.3/2).sub.y(SiO.sub.4/2).sub.z
where:
[0072] R.sup.5 is independently in each occurrence selected from a
group consisting of C.sub.2-8 alkenyl groups, C.sub.1-8 alkyl
groups, phenyl groups, alkoxy groups and alkoxysilyl groups;
preferably the alkenyl groups are terminally unsaturated alkenyl
groups. Desirably, at least one R.sup.5, preferably of a
(R.sup.5.sub.3SiO.sub.1/2) unit and/or a (R.sup.5.sub.2SiO.sub.2/2)
unit, is a C.sub.2-8 terminally unsaturated alkenyl group.
[0073] Subscripts w, x, y and z correspond to the average mol % of
the corresponding siloxane unit based on moles of siloxane units in
the molecule and wherein: w is zero or more, 10 or more, 15 or
more, 20 or more, 25 or more, even 30 or more, 35 or more, 40 or
more, 45 or more, even 50 or more while at the same time is
typically 75 or less, 50 or less, 45 or less, 40 or less, 35 or
less, 30 or less, 25 or less, 20 or less, 15 or less, or even 10 or
less; x is zero or more, 10 or more 15 or more, 20 or more, 30 or
more, 40 or more, even 50 or more while at the same time is
typically 70 or less, 60 or less, 50 or less, 40 or less, 30 or
less, 20 or less or even 10 or less; y is zero or more, 10 or more,
20 or more, 30 or more, 40 or more, 50 or more, 60 or more, 70 or
more, 75 or more, even 80 or more while at the same time is
typically 100 or less, 90 or less, 80 or less, or even 75 or less;
z is zero or more, 5 or more, 10 or more 15 or more, 20 or more, 30
or more, 40 or more, even 50 or more while at the same time is
typically 60 or less, 50 or less, 40 or less, 30 or less, 20 or
less or even 10 or less; provide that (w+x+y+z) equals 100, (y+z)
is 20 or more, (x+w) is 10 or more, and the aforementioned required
concentration of phenyl groups and alkenyl groups is met for
component c.
[0074] The weight-average molecular weight is typically greater
than 350 Daltons (Da) and can be 500 Da or more, 750 Da or more,
1,000 Da or more, 2,000 Da or more, 2,500 Da or more, 5,000 Da or
more, 10,000 Da or more, 20,000 Da or more, 30,000 Da or more, even
40,000 Da or more while at the same time is typically 100,000 Da or
less and can be 45,000 Da or less, 40,000 Da or less, 30,000 Da or
less, 20,000 Da or less, 10,000 Da or less, 5,000 Da or less, even
2,500 Da or less.
[0075] An example of a suitable resinous polyorganosiloxane for use
as component (c) has the following structure:
((CH.sub.3).sub.2ViSiO.sub.1/2).sub.25(PhSiO.sub.3/2).sub.75
where Vi is a vinyl group and Ph is a phenyl group and wherein the
molecule has a weight-average molecular weight of 1590 Da.
[0076] Typically, the concentration of the resinous
polyorganosiloxane is 30 wt % or more and can be 40 wt % or more,
even 50 wt % or more while at the same time is generally 70 wt % or
less, preferably 60 wt % or less and can be 50 wt % or less based
on composition weight.
[0077] Component (d)--photoinitiator
[0078] The composition of the present invention a photoinitiator
(component (d)). A photoinitiator generates free radicals when
exposed to light. Desirably, the photoinitiator is a visible light
photoinitiator, a UV light photoinitiator, or a combination
thereof. Most preferably, the photoinitiator is a UV light
photoinitiator.
[0079] A visible light photoinitiator is a molecule that generates
free radicals upon expose to visible light (wavelength in a range
of 390 to 700 nanometers). Suitable visible light photoinitiators
include any one or any combination of more than one compound
selected from a group consisting of camphoquinone peroxyester
initiators, non-fluorene carboxylic acid peroxyester initiators and
alkyl thioxanthones such an isopropyl thioxanthone.
[0080] A UV light photoinitiator is a molecule that generates free
radicals upon exposure to ultraviolet light. Suitable UV
photoinitiators include any one or any combination of more than one
compound selected from a group consisting of benzophenone,
substituted benzophenones, acetophenone, substituted acetophenone,
benzoin and its alkyl esters, xanthone, and substituted xanthone.
Particularly desirable UV photoinitiators include
diethoxyacetophenone (DEAP), benzoin methyl ether, benzoin ethyl
ether, benzoin isopropyl ether, diethoxyxanthone,
chloro-thioxanthone, azo-bisisobutyronitrile,
N-methyldiethanolaminebenzophenone,
2-hydroxy-2-methylpropiophenone, and any combinations thereof.
[0081] Typically, the photoinitiator is present at a concentration
of 0.1 wt % or more, preferably 0.5 wt % or more, 1.0 wt % or more,
1.5 wt % or more, 2.0 wt % or more, 2.5 wt % or more, 3.0 and at
the same time is desirably 5.0 wt % or less, preferably 4.0 or
less, 3.0 or less, or 2.0 or less based on composition weight.
[0082] Component (e)--moisture cure catalyst
[0083] The composition of the present invention comprises a
moisture cure catalyst (component (e)). Moisture cure catalysts
enhance the rate at which the alkoxysilyl groups on the
polyorganosiloxane react with moisture to cure. Suitable moisture
cure catalysts include any one or combination of more than one
organo-metal catalysts selected from a group consisting of titanium
compounds, tin compounds, and zirconium compounds. Examples of
suitable titanium compounds include tetraisopropylorthotitanate,
tetrabutoxyorthotitanate,
di(isopropoxy)bis(ethylacetoacetate)titanium,
di(isopropoxy)bis(methylacetoacetate)titanium,
di(isopropoxy)bis(acetylacetonate)titanium. Examples of suitable
tin compounds include dibutyltin dilaurate and dibutyltin
dioctoate. Examples of suitable zirconium compounds include
tetra(isopropoxy)zirconium, tetra(n-butoxy)zirconium,
tetra(t-butoxy)zirconium,
di(isopropoxy)bis(ethylacetoacetate)zirconium,
di(isopropoxy)bis(methylacetoacetate)zirconium, and
di(isopropoxy)bis(acetylacetonate)zirconium.
[0084] Typically, the concentration of moisture cure catalyst is
0.1 wt % or more, 0.5 wt % or more, one wt % or more, 2 wt % or
more, and even 3 wt % or more while at the same time is generally 3
wt % or less, 2 wt % or less or even one wt % or less relative to
composition weight.
[0085] Component (f)--Alkoxy Silane
[0086] Compositions of the present invention can optionally further
comprise an alkoxy silane. The alkoxy silane serves as a reactive
diluent. Reactive diluents serve to lower the viscosity of the
composition relative the composition without the reactive diluent.
However, unlike unreactive diluents, reactive diluents participate
in the curing reaction of the composition and become bound into the
resulting cured composition precluding them from being extractible
components from the cured reaction.
[0087] Surprisingly, alkoxy silanes have been found to both work as
reactive diluents and enhance final properties of the cured
composition, presumably by enhancing the compatibility of the
composition components. Surprisingly, when the alkoxy silane
reactive diluent is present in the composition, the composition
cures to a cured composition having higher scratch resistance
and/or hardness relative to an identical composition without the
alkoxy silane.
[0088] Desirably, the alkoxy silane is a dialkoxy silane, a
trialkoxy silane or a combination of dialkoxy and trialkoxy
silanes. Most preferably, the alkoxy silane is a trialkoxy
silane.
[0089] The alkoxy silane compound desirably has the following
structure:
R.sup.5.sub.fSi(OR.sup.5).sub.4-f
where subscript f is one, two or three (preferably one or two, most
preferably one) and R.sup.5 is independently in each occurrence
selected from a group consisting of methyl, ethyl, propyl and butyl
groups. Examples of suitable alkoxy silane compounds include any
one or combination of more than one selected from methyltrimethoxy
silane, ethyltriethoxy silane, and dimethyldimethoxy silane.
[0090] The composition of the present invention can contain zero wt
% or more, 0.5 wt % or more, one wt % or more, 2 wt % or more, 3 wt
% or more, 4 wt % or more, 5 wt % or more, 6 wt % or more, 7 wt %
or more 8 wt % or more, 9 wt % or more, even 10 wt % or more while
at the same time typically contains 20 wt % or less, 19 wt % or
less, 18 wt % or less, 17 wt % or less, 16 wt % or less, 15 wt % or
less, 14 wt % or less, 13 wt % or less, 12 wt % or less, 11 wt % or
less or 10 wt % or less of the alkoxy silane compound based on
composition weight.
[0091] Particular benefit in properties of the cured composition is
surprisingly evident when the alkoxy silane is present at a
concentration of 2 wt % or more, 3 wt % or more, 4 wt % or more,
and even 5 wt % or more while at the same time 10 wt % or less, or
even 8 wt % or less based on composition weight.
EXAMPLES
[0092] Materials: Pentaerythritol tetrakis (3-mercaptopropionate);
Tetraethyleneglycol bis (3-mercaptopropionat; Trimethylolpropane,
and butylated hydoxytoluene are purchased from Aldrich; 1,8
dimercapto-3,6-dioxanoctane is available from Arkema; phenyl based
silicone resins and polymers are can be made according to teachings
in U.S. Pat. No. 7,527,871B2; 2-Hydroxy-2-methylpropiophenone is
available from IGM resin, diisopropoxytitanium
bis(ethylacetoacetate); Pt catalyst; Methyltrimethoxysilane,
dimethyl methyl(mercaptopropyl) siloxane, and dimethylvinylated
siloxanes are commercial available from Gelest;
[0093] Compound A. In a 2 Liter Atlas batch reactor, 500 g of a
vinyl ended-methylphenylsiloxane polymer
(M.sup.Vi.sub.2D.sup.Ph.sub.20) was mixed with the 47.3 g of
HMe.sub.2SiOSiMe.sub.2C.sub.2H.sub.4Si (OMe).sub.3. The mixture was
agitated for 10 minutes at 350 revolutions per minute (rpm), and
then 0.27 g of Pt catalyst (2.15 wt % Pt catalyst in Toluene) was
added into the mixture. The reaction mixture agitated at room
temperature under nitrogen for 3 hours. The infrared spectrum of
the sample showed a complete loss of SiH peak at 2170 cm.sup.-1,
indicating the completion of the hydrosilylation reaction. Part of
the vinyl group on the siloxane converted to moisture curable
trialkoxy containing functionality and result in Compound A.
M.sup.ViD.sup.Ph.sub.20M.sup.A
{A=--CH.sub.2--CH.sub.2--SiMe.sub.2OSiMe.sub.2CH.sub.2CH.sub.2Si(OMe).sub-
.3}
[0094] Blend B. In a 500 g of Atlas batch reactor, 30 g of a
siloxane with composition of M.sup.Vi.sub.3T.sup.Ph was added to 70
g of a silicone resin (M.sup.Vi.sub.25T.sup.Ph.sub.75), then 0.066
g of Pt catalyst (2.15 wt % Pt catalyst in Toluene) was added into
the mixture. The mixture was agitated for 10 minutes at 350 rpm,
and then 42 g HMe.sub.2SiOSiMe.sub.2C.sub.2H.sub.4Si (OMe).sub.3
was slowly added to the mixture by addition funnel in 20 minutes.
The mixture was agitated at room temperature for 30 minutes under
nitrogen, and then heat to 80.degree. C. and was agitated at
80.degree. C. for 1 hour. The reaction was then cool down to room
temperature. The infrared spectrum of the sample showed a complete
loss of SiH peak at 2170 cm.sup.-1, indicating the completion of
the hydrosilylation reaction. The resulting mixture is Blends B. 70
wt % M.sup.Vi.sub.xT.sup.Ph.sub.75M.sup.A.sub.Y (x+y=25) mixed with
30 wt % M.sup.Vi.sub.mT.sup.PhM.sup.A.sub.n (m+n=3);
A=--CH.sub.2--CH.sub.2--SiMe.sub.2OSiMe.sub.2CH.sub.2CH.sub.2Si(OMe).sub.-
3
[0095] Compound C. 163.6 g of 55 wt % siloxane resin
M.sup.Vi.sub.25T.sup.Ph.sub.75 in toluene was added in a 500 mL
round bottle, then 60 g of compound A was slowly added to the
siloxane resin with an agitation speed of 350 rpm. After addition,
the toluene was stripped through a rotovap and result in Compound
C. {60 wt % M.sup.Vi.sub.25T.sup.Ph.sub.75 mixed with 40 wt %
M.sup.ViD.sup.Ph.sub.20M.sup.A
(A=--CH.sub.2--CH.sub.2--SiMe.sub.2OSiMe.sub.2CH.sub.2CH.sub.2Si(OMe).sub-
.3}.
[0096] Example 1. In a 100 milliliters (mL) dental cup, 60 grams
(g) of compound C and 9.2 g of trimethylolpropane
tris(3-mercaptopropionate) was added to make the SH and vinyl mole
ratio of 1:1, the mixture was mixed in a dental mixer at 1000 rpm
for 20 s, and then mixed at 2000 rpm for 30 s. Then 0.7 g of
methyltrimethoxy silane and 0.21 g of
2-Hydroxy-2-methylpropiophenone were added and mixed at 2000 rpm
for 30 s. Finally, 0.11 g of diisopropoxytitanium
bis(ethylacetoacetate) was added to the mixture and was mixed at
2000 rpm for 30 s. The sample was then packaged in 30 mL syringe
and deaired. The sample was subjected to Mechanical Testing as
described above. The cured material has a tensile strength of 1.4
Newtons per square millimeter (N/mm.sup.2), a hardness of Shore A
66.+-.2, and pencil scratch hardness of B.
[0097] Example 2 (compare with Example 1, different structure of SH
organics as X-linker could also lead to hard anti-scratch coating).
In a 100 mL of dental cup, 60 g of compound C and 4.6 g of
trimethylolpropane tris(3-mercaptopropionate) and 4.3 g of
pentaerythritol tetrakis(3-mercaptopropionate) were added make the
SH and vinyl ratio of 1:1, the mixture was mixed in a dental mixer
at 1000 rpm for 20 s, and then mixed at 2000 rpm for 30 s. Then 0.7
g of methyltrimethoxy silane and 0.21 g of
2-hydroxy-2-methylpropiophenone were added and mixed at 2000 rpm
for 30 s. Finally 0.11 g of diisopropoxytitanium
bis(ethylacetoacetate) was added to the mixture and was mixed at
2000 rpm for 30 s. The sample was then packaged in 30 mL syringe
and deaired. Cure the material and test it for Shore A hardness,
tensile strength and pencil scratch hardness as described herein
above. The cured material has a hardness of Shore A 72.+-.3,
tensile strength of 2.29 N/mm.sup.2, and pencil scratch hardness of
H.
[0098] Example 3 (Compare with Exs 1 and 2; different phenyl
siloxanes compositions in the formulation also provides hard
anti-scratch coating). In a 100 ml of dental cup, 10 g of Compound
B, 40 g of compound C, and 9.4 g of Trimethylolpropane
tris(3-mercaptopropionate) were added make the SH and vinyl ratio
of 1:1, the mixture was mixed at 1000 rpm for 20 s, and then mixed
at 2000 rpm for 30 s. Then 0.7 g of methyltrimethoxy silane and
0.21 g of 2-Hydroxy-2-methylpropiophenone was added and mixed at
2000 rpm for 30 s. Finally 0.11 g of diisopropoxytitanium
bis(ethylacetoacetate) was added to the mixture and was mixed at
2000 rpm for 30 s. The sample was then packaged in 30 mL syringe
and deaired. Cure the material and test it for Shore A hardness,
tensile strength and pencil scratch hardness as described herein
above. The cured material has a hardness of shore A 72.+-.2,
tensile strength of 2.21 N/mm.sup.2, and pencil scratch hardness of
H.
[0099] Example 4. In a 60 mL dental cup, 30 g of Compound C and
3.82 g of 1,8 dimercapto-3,6-dioxanoctane were added. The mixture
was mixed in a dental mixer at 2000 rpm for 30 s then 0.106 g of
butylated hydroxytoluene and 1.42 g of methyltrimethoxysilane
mixture was added and mixed at 2000 rpm for 30 s. Finally, 0.271 g
and 2-hydroxy-methylpropiophenone and 0.068 g of
diisopropoyxytitanium bis(ethylacetoacetate) were added to the
mixture and the mixture was mixed at 2000 rpm for 60 s. The sample
was then packaged in 30 mL syringe and deaired. Cure the material
and test it for Shore A hardness, tensile strength and pencil
scratch hardness as described herein above. The cured sample has a
Shore A hardness of 54.+-.2, a tensile strength of 1.17 N/mm.sup.2,
and a pencil scratch hardness of 3B.
[0100] Comparative Example A (compare with Example 1, demonstrate
the phenyl vinyl silicone is not compatible with SH functionalized
methyl based silicone). In a 40 ml dental cup, 10 g of Compound C,
and 12.7 g of dimethyl methyl(mercaptopropyl) siloxane which
contains 3.5 wt % SH were added make the SH and vinyl ratio of 1:1.
The mixture was mixed at 1000 rpm for 20 s, and then mixed at 2000
rpm for 30 s. After dental mixing, it is still not fully mixed.
Then 0.219 g of premade 0.17 wt % butylated hydoxytoluene in
methyltrimethoxy silane and 0.079 g of
2-Hydroxy-2-methylpropiophenone were added and mixed at 2000 rpm
for 30 s. Finally, 0.041 g of diisopropoxytitanium
bis(ethylacetoacetate) was added to the mixture and was mixed at
2000 rpm for 30 s; then followed by another 2000 rpm for 120 s. The
mixture was unable to be mixed. The final mixture contains a very
thick phenyl silicone resin polymer phase and a very dilute phase
with other compositions. The sample did not cure under UV
irradiation due to the separated vinyl polymer/resin phase and
mercaptan silicone phase.
[0101] Comparative Example B. (compare with Example 1, demonstrate
the vinyl methyl based silicone is not compatible with SH
functionalized organics). In a 40 ml dental cup, 6.8 g of
dimethylvinylated siloxane (M.sup.ViD.sub.nM.sup.Vi) which contains
0.45 wt % vinyl; 7 g of dimethylvinylated siloxane which contains
1.2 wt % vinyl, and 4 g of trialkoxy and vinyl functional siloxanes
which has 0.45 wt % vinyl content and 0.8 wt % trialkoxy group, 3.2
g of hexamethyldisilazane treated fumed silica were mixed at 1000
rpm for 20 s, the mixture is translucent. Then 0.68 gram of
trimethylolpropane tris(3-mercaptopropionate) were added to make SH
and vinyl ratio of 1:1. The mixture was mixed at 2000 rpm for 30 s.
After fully mixing, the mixture becomes white. Then 0.219 g of
premade 0.17 wt % butylated hydoxytoluene in methyltrimethoxy
silane and 0.075 g of 2-Hydroxy-2-methylpropiophenone were added
and mixed at 2000 rpm for 30 s. Finally 0.040 g of
diisopropoxytitanium bis(ethylacetoacetate was added to the mixture
and was mixed at 2000 rpm for 30 s. The final formulation is milk
white. A 35 mil wet film as made by draw-down formulation on a
Teflon sheet. The coating was then went through Colight UV-6 by 2
J/cm.sup.2 UV irradiation with 300 mW/cm.sup.2 intensity. The
coating remained liquid after UV irradiation.
[0102] Comparative Example C. (compare with Example 1, demonstrate
methyl based vinyl and SH functionalized silicone are compatible
but lead to low cross-linking density and to low hardness). In a
100 ml dental cup, 4.6 g of dimethyl methyl(mercaptopropyl)
siloxane (which contains 3.5 wt % SH; 6.8 g of dimethylvinylated
siloxane which contains 0.45 wt % vinyl; 7 g of dimethylvinylated
siloxane which contains 1.2 wt % vinyl, and 4 g of trialkoxy and
vinyl functional siloxanes which has 0.45 wt % Vinyl content and
0.8 wt % trialkoxy group, 3.2 g of hexamethyldisilazane treated
fumed silica, were added to make SH and vinyl ratio of 1:1. The
mixture was mixed at 1000 rpm for 20 s, and then mixed at 2000 rpm
for 30 s. 0.219 g of premade 0.17 wt % butylated hydoxytoluene in
methyltrimethoxy silane and 0.075 g of
2-Hydroxy-2-methylpropiophenone were added and mixed at 2000 rpm
for 30 s. Finally 0.040 g of diisopropoxytitanium
bis(ethylacetoacetate was added to the mixture and was mixed at
2000 rpm for 30 s. The sample was then packaged in 30 mL syringe
and deaired. Cure the material and test it for Shore A hardness,
tensile strength and pencil scratch hardness as described herein
above. The cured material has a hardness of Shore A 25.+-.1,
tensile strength of 0.61 N/mm.sup.2.
[0103] Comparative Example D. (Increase the SH content in the
methylsilicone lead to incompatibility of vinyl silicone
polymer/resin with cross-linker). In a 100 ml dental cup, 2.3 g of
dimethyl methyl(mercaptopropyl) siloxane (which contains 7.0 wt %
SH; 6.8 g of dimethylvinylated siloxane which contains 0.45 wt %
vinyl; 7 g of dimethylvinylated siloxane which contains 1.2 wt %
vinyl, and 4 g of trialkoxy and vinyl functional siloxanes which
has 0.45 wt % Vinyl content and 0.8 wt % trialkoxy group, 3.2 g of
hexamethyldisilazane treated fumed silica, were added to make SH
and vinyl ratio of 1:1. The mixture was mixed at 1000 rpm for 20 s,
and then mixed at 2000 rpm for 30 s. The mixture turned to whitish
haze. 0.219 g of premade 0.17 wt % butylated hydoxytoluene in
methyltrimethoxy silane and 0.075 g of
2-Hydroxy-2-methylpropiophenone were added and mixed at 2000 rpm
for 30 s. Finally 0.040 g of diisopropoxytitanium
bis(ethylacetoacetate was added to the mixture and was mixed at
2000 rpm for 30 s. Cure and test the material for Shore A hardness
and tensile strength as described herein above. The cured material
has a hardness of Shore A 20.+-.1.
TABLE-US-00001 TABLE 1 Ex Ex Ex Ex Comp Comp Comp Comp Component
(grams)/Property 1 2 3 4 Ex A Ex B Ex C Ex D 60 wt %
M.sup.Vi.sub.25T.sup.Ph.sub.75 mixed with 60 60 40 30 10 40 wt %
M.sup.ViD.sup.Ph.sub.20M.sup.A 70 wt %
M.sup.Vi.sub.xT.sup.Ph.sub.75M.sup.A.sub.n mixed with 10 30 wt %
M.sup.Vi.sub.mT.sup.PhM.sup.A.sub.n Dimethylsiloxane polymers and
resins 21 21 21 Trimethylolpropane tris(3- 9.2 4.6 9.4 0.68
mercaptopropionate) Pentaerythritol tetrakis(3- 4.3
mercaptopropionate) 1,8 dimercapto-3,6-dioxaneoctane 3.82 dimethyl
methyl(mercaptopropyl) 12.7 4.6 siloxane (3.5 wt % SH) dimethyl
methyl(mercaptopropyl) 2.3 siloxane (7.0 wt % SH)
2-Hydroxy-2-methylpropiophenone 0.21 0.21 0.21 0.27 0.079 0.075
0.075 diisopropoxytitanium 0.11 0.11 0.11 0.068 0.041 0.040 0.040
bis(ethylacetoacetate) UV exposure area 2J/cm.sup.2 UV Yes Yes Yes
Yes No No Yes Yes irradiation: Cure yes or no? Shadow Area Cure 72
hrs. at R.T.: Yes Yes Yes No Slight Yes Yes N/A Cure yes or no?
cured Shore A Hardness dual cured coating 66 72 72 56 N/A N/A 25 20
Tensile Strength 1.40 2.29 2.21 1.17 N/A N/A 0.61 NM (N/mm.sup.2)
Pencil scratch Hardness B H H 3B N/A N/A <B N/A
[0104] Compound D. In a 250 ml Atlas batch reactor, 84 g of a vinyl
ended-methylphenylsiloxane M.sup.Vi.sub.2D.sup.Ph.sub.20 and 16 g
of a vinyl ended-methylphenylsiloxane M.sup.Vi.sub.3T.sup.Ph were
mixed with the 25 g of HMe.sub.2SiOSiMe.sub.2C.sub.2H.sub.4Si
(OMe).sub.3. The mixture was agitated for 10 minutes at 350 rpm,
and then 0.116 g of Pt catalyst (2.15 wt % Pt catalyst in Toluene)
was added into the mixture. The reaction mixture agitated at room
temperature under nitrogen for 2 hours, then under 45.degree. C.
for another 2 hours. The infrared spectrum of the sample showed a
complete loss of SiH peak at 2170 cm.sup.-1, indicating the
completion of the hydrosilylation reaction. Part of the vinyl group
on the siloxane converted to moisture curable trialkoxy containing
functionality and result in Compound D. {84 wt %
M.sup.ViD.sup.Ph.sub.20M.sup.A mixed with 16 wt %
M.sub.x.sup.ViT.sup.PhM.sub.y.sup.A x+y=3;
A=--CH.sub.2--CH.sub.2--SiMe.sub.2OSiMe.sub.2CH.sub.2CH.sub.2Si(OMe).sub.-
3}.
[0105] Compound E. 255 g of 55 wt % siloxane resin
M.sup.Vi.sub.25T.sup.Ph.sub.75 (molecular weight of 1690 Da) in
toluene was added in a 500 mL round bottle, then 60 g of Compound D
was slowly added to the siloxane resin with an agitation speed of
350 rpm. After addition, the toluene was stripped through a rotovap
and result in Compound E. {60 wt % M.sup.Vi.sub.25T.sup.Ph.sub.75
mixed with 33.6 wt % M.sup.ViD.sup.Ph.sub.20M.sup.A and 6.4 wt %
M.sub.x.sup.ViT.sup.PhM.sub.y.sup.A x+y=3;
A=--CH.sub.2--CH.sub.2--SiMe.sub.2OSiMe.sub.2CH.sub.2CH.sub.2Si(OMe).sub.-
3}.
[0106] Example 5. In a 20 ml of dental cup, 10 g of compound E and
0.66 g of 1,8 dimercapto-3,6-dioxanoctane were added, the mixture
was mixed in a dental mixer at 2000 rpm for 30 s, and then 1.32 g
of trimethylolpropane tris(3-mercaptopropionate) was added, the
mixture was mixed at 2000 rpm for 60 s. Then 0.05 g of butylated
hydroxytoluene and 0.25 g of methyltrimethoxylsilane mixture was
added and mixed at 2000 rpm for 30 s. Finally 0.10 g of
2-Hydroxy-2-methylpropiophenone and 0.37 g of diisopropoxytitanium
bis(ethylacetoacetate were added to the mixture and was mixed at
2000 rpm for 60 s. Cure and test the material for Shore A hardness
and tensile strength as described herein above. The cured material
has a tensile strength of 1.12 N/mm.sup.2 and hardness of shore
A72.+-.2; and pencil hardness of H.
[0107] Example 6. In a 20 ml of dental cup, 10 g of compound E and
0.77 g of 1,8 dimercapto-3,6-dioxanoctane were added, the mixture
was mixed in a dental mixer at 2000 rpm for 30 s, and then 1.15 g
of trimethylolpropane tris(3-mercaptopropionate) was added, the
mixture was mixed at 2000 rpm for 60 s. Then 0.05 g of butylated
hydroxytoluene and 0.25 g of methyltrimethoxylsilane mixture was
added and mixed at 2000 rpm for 30 s. Finally 0.10 g of
2-Hydroxy-2-methylpropiophenone and 0.03 g of diisopropoxytitanium
bis(ethylacetoacetate were added to the mixture and was mixed at
2000 rpm for 60 s. Cure and test the material for Shore A hardness
and tensile strength as described herein above. The cured material
has a tensile strength of 1.93 N/mm.sup.2 and hardness of shore
A70.+-.2 and pencil hardness of H.
[0108] Example 7. In a 20 ml of dental cup, 10 g of compound E and
0.92 g of 1,8 dimercapto-3,6-dioxanoctane were added, the mixture
was mixed in a dental mixer at 2000 rpm for 30 s, and then 0.92 g
of trimethylolpropane tris(3-mercaptopropionate) was added, the
mixture was mixed at 2000 rpm for 60 s. Then 0.05 g of butylated
hydroxytoluene and 0.25 g of methyltrimethoxylsilane mixture was
added and mixed at 2000 rpm for 30 s. Finally 0.10 g of
2-Hydroxy-2-methylpropiophenone and 0.03 g of diisopropoxytitanium
bis(ethylacetoacetate) were added to the mixture and was mixed at
2000 rpm for 60 s. Cure the and test the material for Shore A
hardness and tensile strength as described herein above. The cured
material has a tensile strength of 1.81 N/mm.sup.2 and hardness of
shore A68.+-.2 and pencil hardness of HB.
[0109] Example 8. In a 20 ml of dental cup, 10 g of compound E and
2.27 g of trimethylolpropane tris(3-mercaptopropionate) were added,
the mixture was mixed at 2000 rpm for 45 s. Then 0.05 g of
butylated hydroxytoluene and 0.25 g of methyltrimethoxylsilane
mixture was added and mixed at 2000 rpm for 30 s. Finally 0.10 g of
2-Hydroxy-2-methylpropiophenone and 0.03 g of diisopropoxytitanium
bis(ethylacetoacetate) were added to the mixture and was mixed at
2000 rpm for 60 s. Cure the and test the material for Shore A
hardness and tensile strength as described herein above. The cured
material has a hardness of shore A 73.+-.2, tensile strength of
2.34 N/mm.sup.2 and pencil hardness of H.
[0110] Example 9. In a 20 ml of dental cup, 10 g of compound E and
1.55 g of 1,8 dimercapto-3,6-dioxanoctane were added, the mixture
was mixed in a dental mixer at 2000 rpm for 30 s. Then 0.05 g of
butylated hydroxytoluene and 0.25 g of methyltrimethoxylsilane
mixture was added and mixed at 2000 rpm for 30 s. Finally 0.210 g
of 2-Hydroxy-2-methylpropiophenone and 0.03 g of
diisopropoxytitanium bis(ethylacetoacetate were added to the
mixture and was mixed at 2000 rpm for 60 s. Cure and test the
material for Shore A hardness and tensile strength as described
herein above. The cured material has a tensile strength of 1.14
N/mm.sup.2 and hardness of shore A50.+-.2 and pencil hardness of
3B.
TABLE-US-00002 TABLE 2 Formulation Ex 5 Ex 6 Ex 7 Ex 8 Ex 9 60 wt %
M.sup.Vi.sub.25T.sup.Ph.sub.75 mixed 10 g 10 g 10 g 10 g 10 g with
33.6 wt % M.sup.ViD.sup.Ph.sub.20M.sup.A and 6.4 wt %
M.sub.x.sup.ViT.sup.PhM.sub.y.sup.A trimethylolpropane 1.32 g 1.15
g 0.92 g 2.27 g tris(3-mercaptopropionate) 1,8
dimercapto-3,6-dioxanoctane ratio 0.66 g 0.77 g 0.92 g 1.55 g
2-Hydroxy-2-methylpropiophenone 0.1 g 0.1 g 0.1 g 0.1 g 0.1 g
diisopropoxytitanium 0.03 g 0.03 g 0.03 g 0.03 g 0.03 g
bis(ethylacetoacetate) Coating after UV Cured Cured Cured Cured
Cured Shadow area cure Cured Cured Cured Cured cured Tensile
Strength (N/mm.sup.2) 2.24 1.93 1.81 2.34 1.14 Shore A hardness 72
.+-. 2 70 .+-. 2 68 .+-. 2 73 .+-. 2 50 .+-. 2 Pencil hardness H H
HB H 3B CoKF 0.237 0.341 0.368 N/A 0.417
[0111] Example 10. In a 40 ml of dental cup, 20 grams of compound C
and 3.74 grams of trimethylolpropane tris(3-mercaptopropionate)
were added, the mixture was mixed at 2000 rpm for 60 seconds. The
resulting mixture is haze. Then 0.47 grams of
methyltrimethoxylsilane was added and mixed at 2000 rpm for 60
seconds. The mixture tuned to slightly haze. Finally 0.16 grams of
2-Hydroxy-2-methylpropiophenone and 0.048 grams of
diisopropoxytitanium bis(ethylacetoacetate) were added to the
mixture and was mixed at 2000 rpm for 60 seconds. Cure and test the
material for Shore A hardness and tensile strength as described
herein above. The cured material has a hardness of shore A 76.+-.2,
tensile strength of 3.01 N/mm.sup.2, and pencil scratch hardness of
H.
[0112] Example 11. In a 40 ml of dental cup, 20 grams of compound C
and 3.74 grams of trimethylolpropane tris(3-mercaptopropionate)
were added, the mixture was mixed at 2000 rpm for 60 seconds. The
resulting mixture is haze. Then 1.9 grams of
methyltrimethoxylsilane was added and mixed at 2000 rpm for 120
seconds. The mixture turns to clear. Finally 0.16 grams of
2-Hydroxy-2-methylpropiophenone and 0.048 grams of
diisopropoxytitanium bis(ethylacetoacetate were added to the
mixture and was mixed at 2000 rpm for 60 seconds. Cure and test the
material for Shore A hardness and tensile strength as described
herein above. The cured material has a hardness of shore A 80.+-.2,
tensile strength of 3.92 N/mm.sup.2 and pencil scratch hardness of
H.
[0113] Example 12. In a 40 ml of dental cup, 20 grams of compound C
and 3.74 grams of trimethylolpropane tris(3-mercaptopropionate)
were added, the mixture was mixed at 2000 rpm for 60 seconds. The
resulting mixture is haze. Then 2.61 grams of
methyltrimethoxylsilane was added and mixed at 2000 rpm for 120
seconds. The mixture turns to clear. Finally 0.16 grams of
2-Hydroxy-2-methylpropiophenone and 0.048 grams of
diisopropoxytitanium bis(ethylacetoacetate were added to the
mixture and was mixed at 2000 rpm for 60 seconds. Cure and test the
material for Shore A hardness and tensile strength as described
herein above. The cured material has a hardness of shore A 80.+-.2,
tensile strength of 3.85 N/mm.sup.2 (559 psi), and pencil scratch
hardness of H.
TABLE-US-00003 TABLE 3 Formulation Ex 10 Ex 11 Ex 12 60 wt %
M.sup.Vi.sub.25T.sup.Ph.sub.75 mixed 20 g 20 g 20 g with 40 wt %
M.sup.ViD.sup.Ph.sub.20M.sup.A trimethylolpropane 3.74 g 3.74 g
3.74 g tris(3-mercaptopropionate) Methytrimethoxysilane 0.47 g 1.9
g 2.61 g 2-Hydroxy-2-methylpropiophenone 0.1 g 0.1 g 0.1 g
diisopropoxytitanium 0.048 g 0.048 g 0.048 g bis(ethylacetoacetate)
Coating after UV Cured Cured Cured Shadow area cure Cured Cured
Cured Viscosity (mPa*s) 6389 2870 1832 Tensile Strength
(N/mm.sup.2) 3.01 3.70 3.85 Shore A hardness 76 .+-. 2 80 .+-. 2 80
.+-. 2 Pencil hardness H H H CoKF 0.287 0.213 0.234
* * * * *