U.S. patent application number 17/567188 was filed with the patent office on 2022-04-21 for male touch fastener elements.
The applicant listed for this patent is Velcro IP Holdings LLC. Invention is credited to Mark A. Clarner, Christopher M. Gallant, Luis Parellada Armela, James L. Tardiff.
Application Number | 20220117363 17/567188 |
Document ID | / |
Family ID | 1000006066348 |
Filed Date | 2022-04-21 |
![](/patent/app/20220117363/US20220117363A1-20220421-D00000.png)
![](/patent/app/20220117363/US20220117363A1-20220421-D00001.png)
![](/patent/app/20220117363/US20220117363A1-20220421-D00002.png)
![](/patent/app/20220117363/US20220117363A1-20220421-D00003.png)
![](/patent/app/20220117363/US20220117363A1-20220421-D00004.png)
![](/patent/app/20220117363/US20220117363A1-20220421-D00005.png)
![](/patent/app/20220117363/US20220117363A1-20220421-D00006.png)
![](/patent/app/20220117363/US20220117363A1-20220421-D00007.png)
![](/patent/app/20220117363/US20220117363A1-20220421-D00008.png)
![](/patent/app/20220117363/US20220117363A1-20220421-D00009.png)
![](/patent/app/20220117363/US20220117363A1-20220421-D00010.png)
United States Patent
Application |
20220117363 |
Kind Code |
A1 |
Parellada Armela; Luis ; et
al. |
April 21, 2022 |
MALE TOUCH FASTENER ELEMENTS
Abstract
A male touch fastener product with a resin surface and an array
of spaced-apart male touch fastener elements carried on the
surface. Each touch fastener element has a stem extending from the
surface and a head disposed at a distal end of the stem and
extending laterally from the stem to a distal edge overhanging the
surface. The head, stem and surface form a contiguous mass of
resin, the head. The distal edge has multiple toes extending
laterally outward and varying in shape and size about the edge,
with adjacent toes having facing, free-form resin surfaces defining
crevices therebetween. The fastener element is particularly
flexible and engages with very fine fibers.
Inventors: |
Parellada Armela; Luis;
(Palafrugell, ES) ; Gallant; Christopher M.;
(Nottingham, NH) ; Tardiff; James L.; (Manchester,
NH) ; Clarner; Mark A.; (Hopkinton, NH) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Velcro IP Holdings LLC |
Manchester |
NH |
US |
|
|
Family ID: |
1000006066348 |
Appl. No.: |
17/567188 |
Filed: |
January 3, 2022 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
16699790 |
Dec 2, 2019 |
11246380 |
|
|
17567188 |
|
|
|
|
62774459 |
Dec 3, 2018 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
A44B 18/0019 20130101;
A44B 18/0011 20130101 |
International
Class: |
A44B 18/00 20060101
A44B018/00 |
Claims
1-18. (canceled)
19. A male touch fastener product, comprising a resin surface; an
array of spaced-apart male touch fastener elements carried on the
surface, each touch fastener element extending to an overall height
above the resin surface and comprising a stem extending from the
surface and having a minimum lateral extent and a bend height
defined as the perpendicular distance from the resin surface to a
lowermost occurrence of the minimum lateral extent; and a flat,
disc-shaped head disposed at a distal end of the stem, and forming
with the stem and the surface a contiguous mass of resin, the head
extending laterally from the stem to a distal edge overhanging the
surface, the head having an overall lateral extent and having an
overhang midpoint thickness measured parallel to the stem from an
underside of the head to an upper surface of the head at a position
midway between the stem and the distal edge; wherein for at least
most of the fastener elements of the array, the ratio of Edge Flex
Ratio to Stem Bending Coefficient is between 0.3 and 6.0, where
Stem Bending Coefficient is a ratio of a difference between overall
height and bend height to the minimum lateral extent, and Edge Flex
Ratio is a ratio of a difference between the overall lateral extent
of the head and the minimum lateral extent of the stem to the
overhang midpoint thickness.
20. (canceled)
21. The male touch fastener product of claim 19, wherein the distal
edge comprises multiple toes extending laterally outward and
varying in shape and size about the edge, with adjacent toes having
facing, free-form resin surfaces defining crevices therebetween,
the crevices being narrower than the adjacent toes.
22. The male touch fastener product of claim 21, wherein the edge
has between 5 and 50 toes.
23. The male touch fastener product of claim 21, wherein at least
one of the crevices is defined between toe surfaces that are
generally parallel over at least 30 percent of an overall length of
the crevice.
24. The male touch fastener product of claim 19, wherein the stem
has a molded peripheral surface.
25. The male touch fastener product of claim 24, wherein the head
has a molded underside surface.
26. The male touch fastener product of claim 19, wherein the
fastener elements extend to an overall height from the resin
surface of between about 0.08 and 0.3 millimeter.
27. The male touch fastener product of claim 19, wherein the head
has an upper surface defining a central depression.
28. The male touch fastener product of claim 19, wherein the head
has an underside surface that defines a curve extending from a
narrowest portion of the stem to the rim of the head.
29. The male touch fastener product of claim 19, wherein the array
comprises staggered rows of fastener elements.
30. The male touch fastener product of claim 29, wherein each head
is essentially equally spaced from each of six other heads.
31. The male touch fastener product of claim 19, wherein the array
comprises at least one row of the male touch fastener elements
arranged such that heads of adjacent fastener elements of the row
are spaced from each other a distance that is between 1.2 and 2.0
times a minimum lateral dimension of the stems of the adjacent
fastener elements.
32. The male touch fastener product of claim 19, wherein the ratio
of Edge Flex Ratio to Stem Bending Coefficient is between 0.5 and
5.
33. A male touch fastener product, comprising a resin surface; an
array of spaced-apart male touch fastener elements carried on the
surface, each touch fastener element extending to an overall height
above the resin surface and comprising a stem extending from the
surface and having a minimum lateral extent and a bend height
defined as the perpendicular distance from the resin surface to a
lowermost occurrence of the minimum lateral extent; and a head
disposed at a distal end of the stem, and forming with the stem and
the surface a contiguous mass of resin, the head extending
laterally from the stem to a distal edge overhanging the surface,
the head having an overall lateral extent and having an overhang
midpoint thickness measured parallel to the stem from an underside
of the head to an upper surface of the head at a position midway
between the stem and the distal edge; wherein for at least most of
the fastener elements of the array, the product of Stem Bending
Coefficient and Edge Flex Ratio is between 3.0 and 10.0, where Stem
Bending Coefficient is a ratio of a difference between overall
height and bend height to the minimum lateral extent, and Edge Flex
Ratio is a ratio of a difference between the overall lateral extent
of the head and the minimum lateral extent of the stem to the
overhang midpoint thickness.
34. The male touch fastener product of claim 33, wherein the distal
edge comprises multiple toes extending laterally outward and
varying in shape and size about the edge, with adjacent toes having
facing, free-form resin surfaces defining crevices therebetween,
the crevices being narrower than the adjacent toes.
35. The male touch fastener product of claim 33, wherein the stem
has a molded peripheral surface.
36. The male touch fastener product of claim 33, wherein the
fastener elements extend to an overall height from the resin
surface of between about 0.08 and 0.3 millimeter.
37. The male touch fastener product of claim 33, wherein the head
has an upper surface defining a central depression.
38. The male touch fastener product of claim 33, wherein the array
comprises staggered rows of fastener elements.
39. The male touch fastener product of claim 33, wherein the array
comprises at least one row of the male touch fastener elements
arranged such that heads of adjacent fastener elements of the row
are spaced from each other a distance that is between 1.2 and 2.0
times a minimum lateral dimension of the stems of the adjacent
fastener elements.
Description
CROSS REFERENCE TO RELATED APPLICATIONS
[0001] This application is a continuation of U.S. Ser. No.
16/699,790, filed Dec. 2, 2019, which claims priority to U.S.
Provisional Ser. No. 62/774,459, filed Dec. 3, 2018, and each
application is hereby incorporated by reference in its
entirety.
TECHNICAL FIELD
[0002] This invention relates to touch fastener elements, and more
particularly to molded touch fastener elements of the mushroom
type.
BACKGROUND
[0003] Touch fasteners are useful for releasable engagement of
surfaces in products ranging from diapers to construction
materials. In most cases, the engagement is between an array of
very small male fastener elements and a field of fibers or loops,
but in some cases heads of the male fastener elements can be shaped
and spaced so as to releasably engage a similar array. Some male
fastener elements have heads that overhang along only one lateral
direction, while others overhang in multiple directions (or in all
directions). The former (often referred to as J-shaped or palm tree
fasteners) tend to have very directional engagement
characteristics, whereas the latter (often referred to as
mushroom-shaped fasteners) have engagement characteristics that are
more uniform in all directions. Each type of male fastener element
has its preferred uses in commercial products. Mushroom-shaped
fastener elements can be made with fairly thin heads, for
engagement with very low loft fibers as tend to be found in
inexpensive non-woven materials. Improvements in fastener element
shape, and in methods of making such shapes, are continually
sought.
SUMMARY
[0004] Various aspects of the invention feature a male touch
fastener product with a resin surface and an array of spaced-apart
male touch fastener elements carried on the surface. Each touch
fastener element has a stem extending from the surface, and a head
disposed at a distal end of the stem, the head forming with the
stem and the surface a contiguous mass of resin. The head extends
from the stem to a distal edge overhanging the surface.
[0005] According to one aspect of the invention, the distal edge
has multiple toes extending laterally outward and varying in shape
and size about the edge, with adjacent toes having facing,
free-form resin surfaces defining crevices between them, the
crevices being narrower than the adjacent toes. In some examples,
the distal edge has between 5 and 50 toes, and in some cases,
between 10 and 30 toes. Preferably, there are between 30 and 100
toes per millimeter of head perimeter. In some embodiments, at
least one of the crevices is defined between toe surfaces that are
generally parallel over at least 30 percent of an overall length of
the crevice.
[0006] Another aspect of the invention features a touch fastening
having a fibrous surface having exposed fibers, and the male touch
fastener product as recited above releasably engaged with the
fibrous surface, with fibers of the fibrous surface snagged in
crevices between toes of the heads.
[0007] According to another aspect of the invention, the array has
at least one row of the male touch fastener elements arranged such
that heads of adjacent fastener elements of the row are spaced from
each other a distance that is between 1.2 and 2.0 times (preferably
between 1.4 and 1.8 times) a minimum lateral dimension of the stems
of the adjacent fastener elements. Preferably, for at least most of
the fastener elements of the array the ratio of a difference
between the overall lateral extent of the head and a minimum
lateral extent of the stem to the overhang midpoint thickness is
between 1.0 and 5.0 (preferably between 1.4 and 2.0).
[0008] According to another aspect of the invention, the stem has a
minimum lateral extent and a bend height defined as the
perpendicular distance from the resin surface to a lowermost
occurrence of the minimum lateral extent. For at least most of the
fastener elements of the array, the product of Stem Bending
Coefficient and Edge Flex Ratio (as those terms are defined below)
is between 3.0 and 10.0, where Stem Bending Coefficient is a ratio
of a difference between overall height and bend height to the
minimum lateral extent of the stem, and Edge Flex Ratio is a ratio
of a difference between the overall lateral extent of the head and
the minimum lateral extent of the stem to the overhang midpoint
thickness.
[0009] According to another aspect of the invention, for at least
most of the fastener elements of the array, the ratio of Edge Flex
Ratio to Stem Bending Coefficient is between 0.3 and 6.0
(preferably between 0.5 and 5).
[0010] According to yet another aspect of the invention, at least
three adjacent fastener elements each has a Stem Bending
Coefficient of between 1.4 and 2.0.
[0011] In any of these aspects, the product preferably exhibits a
Toccare micro-texture coarseness, as measured on the array, of
between 20 and 30, and/or a Toccare micro-texture roughness, as
measured on the array, of between 25 and 40.
[0012] According to another aspect of the invention, the product
exhibits a Toccare micro-texture coarseness, as measured on the
array, of between 20 and 30.
[0013] According to yet another aspect of the invention, the
product exhibits a Toccare micro-texture roughness, as measured on
the array, of between 25 and 40.
[0014] Embodiments according to any of the above aspects may be
provided with any combination of the following features.
[0015] In some cases, the stem has a molded peripheral surface. In
some examples, the head has a molded underside surface.
[0016] In some embodiments, the stem is of round cross-section
and/or extends perpendicular to the resin surface.
[0017] In some examples, the head is disc-shaped.
[0018] The array preferably has a density of between 1300 and 5500
fastener elements per square centimeter, and the fastener elements
preferably each extend to an overall height from the resin surface
of between about 0.08 and 0.3 millimeter.
[0019] In some cases, the head has an essentially flat upper
surface. In some examples, the head has an upper surface defining a
central depression.
[0020] The head may have a nominal thickness, for example, of
between 0.01 and 0.04 millimeter.
[0021] In some embodiments, the head has an underside surface that
defines a curve extending from a narrowest portion of the stem to
the rim of the head. For example, the curve may follows an arc with
a radius greater than half a lateral extent of a lateral
cross-section of the narrowest portion of the stem.
[0022] In some configurations, the array has staggered rows of
fastener elements. For example, each head may be essentially
equally spaced from each of six other heads.
[0023] In some cases, the array defines a regular row spacing.
[0024] The resin surface may be of a resin base having a thickness
less than about 0.1 millimeter, for example. In some cases, the
resin base is laminated to a web, and may be surrounded by exposed
web surface to form an island of resin. In some examples, the web
comprises fabric.
[0025] Another aspect of the invention features a method of forming
a male touch fastener product. The method includes molding a resin
surface while forming an array of spaced-apart male touch fastener
elements extending from the surface, by pressing moldable resin
into respective molding cavities defined in a mold against which
mold the resin surface is molded, solidifying the pressed resin in
the molding cavities, and then stripping the solidified resin from
the cavities as stems with associated heads disposed at distal ends
of the stems and overhanging the surface. As stripped from the
cavities the heads have distal edges with multiple toes extending
laterally outward and varying in shape and size about the edge,
with adjacent toes having facing, free-form resin surfaces defining
crevices between them, each crevice narrower than the adjacent
toes.
[0026] In some embodiments, an innermost portion of each cavity is
bounded by a smooth rim surface. In some cases, each cavity is
defined by a surface against which an underside of the head is
formed and defines a curve extending from a point forming a
narrowest portion of the stem to the rim surface. Preferably the
curve follows an arc with a radius greater than half a lateral
extent of a lateral cross-section of the cavity at the point
forming the narrowest portion of the stem.
[0027] In some examples the mold features a rotatable mold roll,
and the method is performed continually during rotation of the mold
roll to produce an elongated flexible fastener product.
[0028] In some cases the method also includes, after forming the
array of spaced-apart male touch fastener elements, plastically
stretching the resin surface.
[0029] The fastener elements described herein can be formed at very
high speeds in the production of inexpensive fastener products.
Moreover, due in part to their size, arrangement and specific
design features, arrays of such fastener elements can be made to
exhibit particularly advantageous levels of softness to the human
touch. In some cases such arrays can be formed on resin sheets such
that it can be difficult for a layperson to tell which side of the
sheet is the fastening surface, without engaging the surface with
fibers.
[0030] The details of one or more embodiments of the invention are
set forth in the accompanying drawings and the description below.
Other features, objects, and advantages of the invention will be
apparent from the description and drawings, and from the
claims.
DESCRIPTION OF DRAWINGS
[0031] FIG. 1 is an enlarged, partial perspective view of a touch
fastener being separated.
[0032] FIG. 2 is a perspective view of an array of mushroom-type
male fastener elements extending from a common resin base.
[0033] FIG. 3 is a side view of the array of FIG. 2.
[0034] FIG. 4 is a top view of the array of FIG. 2.
[0035] FIG. 5 is a highly magnified, top perspective view of one
fastener element.
[0036] FIG. 6 is a top view of one fastener element and a portion
of an adjacent fastener element.
[0037] FIG. 7 is a side view of a single fastener element.
[0038] FIG. 8 is a magnified view of a field of microfibers.
[0039] FIG. 9 shows fine fibers engaged with an array of fastener
elements.
[0040] FIG. 10 is an enlarged view of a single engaged fastener
element near the center of FIG. 9.
[0041] FIG. 11 is an enlarged view of an area near the bottom right
corner of FIG. 9.
[0042] FIG. 12 shows fibers caught between toes of a fastener
element head rim.
[0043] FIG. 13 shows fiber loads bending individual toes out of the
plane of the head rim.
[0044] FIG. 14 schematically illustrates a method and apparatus for
forming an array of fastener elements with a continuous base
sheet.
[0045] FIG. 15 shows a cross-section of an individual cavity in
which a fastener element or fastener element preform is molded.
[0046] FIG. 16 illustrates the process of counting toes about a
head perimeter.
[0047] FIG. 17 is a top view of a non-circular touch fastener
element with toes.
[0048] Like reference symbols in the various drawings indicate like
elements.
DETAILED DESCRIPTION
[0049] Referring first to FIG. 1, fastener product 10 has a base
sheet 12 of resin and an array of male touch fastener elements 14
extending from a broad resin side surface 16 of the base sheet. To
give some proportion, base sheet 12 is about 60 .mu.m hick and can
be up to one meter or more in width, and can be manufactured in
continuous length and rolled for transport. The fastener elements
are arranged in an array on the base sheet surface, with a density
of about 2700 per square centimeter, each fastener element
extending only about 0.125 mm from the base sheet surface. The
fastener elements, which are not shown to scale, are illustrated as
having snagged very fine fibers 16 of a mating sheet 18 of
material, such that as the two mated materials are peeled away from
one another, the snagged fibers are stretched taut prior to being
released. In this manner the two materials together form a
releasable fastening. The fibers the fastener elements are designed
to snag and retain are extremely fine, as will be discussed in more
detail below, making fastener product 10 particularly useful in
snagging very low-loft knit materials, such as those formed of
cotton or silk.
[0050] Referring next to FIGS. 2 and 3, the fastener elements 14
are formed with discrete circular stems 20 of resin rising
integrally from a near surface of base sheet 12. The diameter of
each stem 20 may be about the same as the thickness of the base
sheet in some cases. The base of each stem blends into the base
sheet with a generous radius approximately equal to half of the
nominal stem diameter. Above the base radius the stem rises with
essentially a constant diameter to a head or cap 22 that extends
radially or laterally outward from the stem to overhang the base
sheet surface and has an overall diameter about twice the diameter
of the stem. As can be seen in FIG. 3, the diameter of each stem 20
is significantly greater than the thickness of the head on the
stem. The underside of the head is generally frustoconical or
radiused from the stem to the distal edge of the head.
[0051] As shown in FIG. 4, the fastener elements 14 are arranged in
a regular array of staggered rows and columns, with the heads 22 of
adjacent fastener elements spaced apart to allow fibers to enter
the volume between the base sheet and the undersides of the heads
so as to be snagged. Arrow MD in FIG. 4 indicates the machine
direction of the process that manufactured the photographed
product. The column spacing CS and the row spacing RS between
fastener elements of a given column are both about twice the
nominal head diameter, or in this example about 205 .mu.m. The
upper surfaces of the heads are generally flat and parallel to the
base sheet, and have a generally circular perimeter. However, when
highly magnified as in FIG. 5 it is apparent that the heads 22 do
not have exactly circular perimeters. Rather, the head edge has a
series of projections extending radially or laterally outward about
its perimeter. Given their size and shape, we have come to refer to
these projections as toes 24. As evident from the photograph, the
width and shape of the toes vary about the perimeter of the head,
as does the width and length of the gaps separating adjacent toes.
As will be discussed in more detail below, the number, size and
shape of toes about the head perimeter do not correspond with any
features of the cavity in which the head rim was molded. Rather,
the facing sides of adjacent toes are generally curved and have
been free-formed rather than formed against a mold surface. Some
wider toes each appear to have multiple edge projections, while
some appear to neck in width at their base. Moreover, the
arrangement of toes is not precisely duplicated across each
fastener element, although there are similarities in the overall
distribution of toe size across fastener elements of the
product.
[0052] Referring next to FIG. 6, the fastener element head 22 can
be said to have a nominal cap diameter `C` of about 0.077 mm. In
various runs of the product, the average cap diameter `C` was found
to range from 0.077 to 0.123 mm. `C` is measured between the tips
of toes on opposite sides of the head and represents the overall
diameter of the fastener element head. The separation distance CCS
between adjacent heads 22 of the array is about 0.092 mm. In
various runs of the product, the average spacing CCS was found to
range from 0.078 to 0.111 mm.
[0053] As shown in the schematic representation of a fastener
element 14 in FIG. 7, the fastener element has an overall height
`H` as measured perpendicular to the base sheet 12 to the upper
surface of head 22. In this example `H` was measured to be 0.126
mm, but in various runs of the product the average height was found
to range from 0.126 to 0.170 mm. The stem 20 has a circular
cross-section and extends perpendicularly from the base sheet 12.
The stem has a nominal diameter `S` over a length of the stem
including its midpoint height, blending into a radius at the base
of the stem at a distance `J` from the base sheet, and blending
into a flaring of the underside of the head at the top of the stem.
In this example `S` was measured to be 0.049 mm, but in various
runs of the product the average stem diameter was found to range
from 0.049 to 0.066 mm. In this example was measured to be 0.043
mm, but in various runs of the product the average value for `J`
was found to range from 0.032 to 0.051 mm. Distance `J` is related
to the flexibility of the fastener element in response to a lateral
load applied at the head, as the stem will tend to bend at or near
the lowest extent of the straight shank of the stem.
[0054] We have observed how readily the above-described flat-topped
mushroom fastener elements can bend in response to lateral loads
applied to the head, such as by a finger applying light pressure as
it moves across the field. For a given resin, the tendency of the
fastener element to bend over in response to a lateral force at the
head is related both to the moment arm between the upper surface of
the fastener element and its preferred bending point near the base
of the stem, and the minimum lateral stem dimension at that point.
For ease of analysis, we have defined the Stem Bending Coefficient
(SB) as the ratio of H-J to S. Preferably this ratio is between 1.0
and 2.5, more preferably between 1.4 and 2.0. For round stems `S`
is the diameter; for other shapes `S` should be taken as the
minimum lateral dimension. Resins and designs that enable a
fastener element so bent over to recover over time to at least
close to its original vertical orientation upon removal of the
force are preferred. Ideally the upper surface of the fastener
element is essentially flat, as opposed to hemispherical, for
example.
[0055] Referring also back to FIG. 6, the ability of the field to
capture and retain fibers that have penetrated the space beneath
the heads is related to the head separation distance CCS and the
lateral stem dimension `S`. Ideally the head separation distance
CCS is at least 1.2 times, or between 1.2 and 2.0 times, or even
between 1.4 and 1.8 times, the stem dimension `S`, particularly in
arrays in which rows are staggered such that the stems are
staggered and the heads are of similar dimension, such that each
head is essentially equally spaced from each of six other heads,
such as is shown in FIG. 4. We call this ratio of CCS to S the
Spacing Capture Ratio. Maintaining this ratio in the preferred
range is also beneficial to the formation and use of molding
sleeves configured to mold the fastener elements, as discussed
below with respect to FIG. 15.
[0056] The head 22 overhangs the stem on each side a distance `OH`
that is approximately half the difference between the head diameter
`C` and the stem diameter `S` in this example in which both are
circular and the stem is centered under the head. In this example
`OH` was therefore approximately 0.014 mm on each side of the stem.
The head can be said to have a nominal thickness CT, measured
parallel to the stem at a midpoint of the overhand distance OH. In
this example CT was measured to be 17.5 .mu.m, but in various runs
of the product the average head thickness was found to range from
0.012 to 0.028 mm. Similarly, toe thickness TT is measured
perpendicular to the base sheet at the base of a given toe. The
average toe thickness for this example was measured to be 0.0145
mm, but in various runs the average toe thickness ranged from 0.009
to 0.022 mm.
[0057] Referring next to FIG. 8, fibers of a size compatible with
the above-described fastener elements to form releasable fastenings
include organic fibers such as cotton. Such fibers 16 may have a
nominal thickness of only about 5 to 7 .mu.m and be of non-circular
cross-section. FIG. 9 shows a field of such fibers 16 snagged by an
array of the above-described fastener elements 14. As is evident
from this photo, the engagement between discrete fibers and
discrete fastener elements is stochastic, and it will be understood
that the overall performance and load resistance of the fastening
is a function of essentially thousands of discrete engagements.
This photo illustrates several different types of engagements, some
of which are particularly enabled by the fastener element
structural features discussed above.
[0058] For example, the fiber 16 shown in FIG. 10 engages the
visible fastener element by wrapping about the stem (not shown) of
the fastener element but crossing the rim at the lower extent of
the head in the photo. Where it engages the rim it lifts one toe T1
from the plane of the head, passing under that toe and above an
adjacent toe T2. This fiber can be said to engage the edge of the
fastener element between adjacent toes, and it is evident that the
existence of the toes helps to prevent sliding of the fiber across
the rim of the head. In other words, the toes T1 and T2 have a
functional effect in the engagement of this fiber 16.
[0059] FIG. 10 also illustrates that the edge of the fastener
element head can flex upward in response to a fiber-applied point
load. For a given resin, this flexibility is related both to the
head overhang distance and its thickness. For ease of comparison,
we have defined the term Edge Flex Ratio (EF) as the ratio of the
difference between head and stem widths to the nominal cap
thickness. With reference to the dimensions shown in FIGS. 6 and 7,
EF=(C-S)/CT. The Edge Flex Ratio is preferably between 1.0 and 5.0,
particularly for relatively flat mushroom heads with edge toes that
further increase local flexibility as illustrated in FIG. 10.
[0060] In the photo shown in FIG. 11, the fastener element 14 near
the center of the photo is engaged by several fibers 16 wrapped
about its stem under the head, while an adjacent fastener element
to the left is engaged by a fiber that has snagged just the head
but has not wrapped about the stem. In this latter example, the
fiber is caught between adjacent toes of the rim of the head, and
tension in the fiber has deflected at least one of the toes to
enhance retention of the fiber, thus adding to the overall shear
resistance of the fastener.
[0061] FIGS. 12 and 13 show further examples of fibers 16 engaged
by just the rim of the fastener element head. In FIG. 12 the fiber
16 on the right is engaged between adjacent toes and tension in the
fiber will tend to pull the fiber deeper into engagement,
preventing slipping of the fiber along the rim. The fiber on the
left has essentially bent one toe upward, out of its plane, as has
both fibers 16 shown in FIG. 13.
[0062] The fastener elements described above are advantageously
flexible in multiple modes in response to a laterally applied head
load. The stem will tend to elastically bend over to tilt the head;
the rim of the head may flex locally out of its plane to form a
local side depression that helps to retain a fiber pulling on the
head edge; and individual toes to which the load is applied may
bend out of the plane of the rim. We have coined the term Total
Flexure Product (TF) as related to the first two of those three
flexure modes, as the product of the Stem Bending Coefficient (SB)
and the Edge Flex Ratio (EF). Mathematically, TF=SB*EF. The greater
either of the two factors, the greater the overall flexure of the
fastener element in response to a lateral load applied locally at
the edge of the head. For resins suitable for high speed formation
of fastener elements, the Total Flexure Product is preferably
greater than 3.0, or between 3.0 and 10.0. For the product shown in
FIGS. 2-5, the Total Flexure Product was 3.3.
[0063] In some cases the relative flexibility of rim edge and stem
is important. We define Edge Flex Preference as the ratio of Edge
Flex Ratio and Stem Bending Coefficient, or EF/SB. This parameter
relates to the relative flexibility of head edge and stem: the
higher the value, the more the edge (with or without toes) will
flex before the stem itself bends over to help align the load and
prevent release. For resistance of shear loads when engaged with
fine fibers, Edge Flex Preference of a flat disk-headed fastener
element is preferably between 0.3 and 6.0, more preferably between
0.5 and 5.
[0064] Referring next to FIG. 14, resin fastener products such as
shown in FIG. 1 (with any of the fastener element arrays described
above) can be made in a continuous roll-molding process in which
molten resin 56 is introduced into a nip 58 between two
counter-rotating rolls including a pressure roll 60 and a mold roll
62 that defines cavities in the shape of the above fastener
elements. Pressure in nip 58 forces the resin into the cavities,
where it solidifies as contiguous resin solidifies on the surface
of the roll before being stripped off of the mold roll by being
passed around a stripper roll 64 and then spooled for storage. In
some cases a preformed web 66 is introduced to the nip with the
resin, such that while some of the resin is filling the cavities to
form the fastener elements, resin forming the base sheet is
laminated directly to the web surface, such as by the resin
intermingling with surface features of the web, partially
penetrating the web surfaces in the case of a fibrous web. The
spooled product in that case comprises the web with the base sheet
of resin on one side of the web, and the array of fastener elements
extending from the base sheet. The resin can be introduced to the
nip in discontinuous volumes to form the base sheet in separate
islands or patches or width-wise continuous lanes, each bearing
fastener elements. The resin can also be introduced in multiple,
spaced apart lanes across the width of the web, to form a fastener
product with continuous, longitudinal lanes of fastener elements
separated by lanes of exposed web surface.
[0065] The male touch fastener products shown in FIGS. 2-5 and 9-13
were molded from PPC7650 polypropylene, available from TOTAL, with
5% added whitener. The tape was continuously processed as shown in
FIG. 14, at a line speed of 58 meters per minute, resulting in a
tape with an overall weight of 100 grams per square meter and an
overall thickness, including the base and fastener elements, of
0.23 millimeter.
[0066] It is preferred that the heads of the fastener elements be
molded in finished form in the cavities of mold roll 62. However,
in some cases it may be necessary to slightly flatten the heads
after molding, such as by engaging the upper surfaces of the heads
with a heated roller 68 that plastically deforms the heads to
increase their flatness. Preferably, the heat and pressure applied
by roll 68 is sufficient to flatten the upper head surface without
melting away the toe structures formed about its periphery. The
heads shown in the photos described above have, for example, been
slightly flattened by such a roll after being pulled from their
molding cavities. The effect of the flattening can be seen, for
example, in FIG. 2, from which it can be seen that the outer rim
area of the upper surface of each fastener element, containing the
toes, lies in a plane generally perpendicular to the stem, while
the central portion of the upper surface--that portion which may
not have engaged roll 68--forms a shallow depression.
[0067] Referring to FIG. 15, cavities shaped to form the fastener
elements described herein can be defined in a sleeve 70 fit tightly
to an outer surface of a cylindrical core 72 of mold roll 62, with
the cavities extending all of the way through the sleeve such that
the flat upper surfaces of the fastener element heads are formed on
the outer core surface. Methods of laser cutting using a pulsed
fiber laser, tilting the beam axis as it travels about the cavity
perimeter, are capable of forming cavities of this shape and size
in stainless steel, in some cases followed by a light etch. Screens
with such cavities can also be made by electroforming techniques.
Fastener element heads may be formed in rotationally symmetric
cavities, such that the cross-section of the head-forming portion
of the cavity as shown is similar in any plane containing the
centerline of the stem. In other words, the toes may be formed
within a smooth and continuous rim cavity that tapered to a sharp
edge at the surface of core 72, and the inter-toe surfaces and
bounded crevices are not themselves determined or formed by
specific mold surfaces or features. The cavity surface is
generously radiused between the portion forming the narrowest part
of the stem and the core surface, which essentially forms a tangent
to the arc of the cavity surface. The radius `R` defined by this
surface is preferably more than half the narrowest lateral extent
of the cavity, and for molding the underside surface of the heads
shown in FIG. 3 was about 50 .mu.m, for example. As the resin is
pressed at high rate into this ever-narrowing rim portion of the
cavity, the toes form. As can be seen from the curved outer toe
surfaces in the photographs discussed above, the resin flow
eventually freezes and forms non-molded surfaces at the distal toe
ends.
[0068] One hypothesis concerning why the resin flow forming the
head rim splits into discrete flows as it approaches the distal
extent of the rim cavity, with each flow chilling to form a
separate toe structure, is that the rate of chill accelerates as
the resin cross-section narrows, while air trapped in the rim
cavity increasingly resists the advancing flow, causing the rim
cavity to incompletely fill. As the solidified skin of the edge of
the flow stretches circumferentially to fill the cavity, molten
resin behind the skin breaks through in discrete regions to push
forward as a toe, chilling and solidifying without merging with
adjacent flows. Whatever the mechanism involved, we have found the
formation of toes within the cavities and processing parameters
described above to be quite repeatable within standard process
control tolerances.
[0069] With reference to FIG. 16, we use the following procedure to
determine the number of toes about the periphery of a fastener
element head, and we use the word `toe` with reference to this
method of determining whether a particular projection is or is not
a toe. First, an image of the fastener element head is obtained,
looking directly down at the upper surface of the head (i.e., in a
direction perpendicular to the base sheet). Next, a line is drawn
about the head representing the convex hull of the head perimeter.
In this figure such a line is labeled CH. A toe-count line is then
drawn spaced inside the convex hull line by a distance equal to
five percent of the longest distance from the head area centroid to
the convex hull line. The toe count line is labeled TCL in the
figure and represented as a dashed line. Next, the discrete
positions about the head rim where the perimeter extends to within
the TCL are counted. Such spaces are only counted if the width of
the space (i.e., the inter-toe space) at the TCL is less than the
width of the head perimeter along the TCL on each side of the space
before reaching another space. In other words, points at which one
can see through the head inside the TCL are counted. The number of
toes is taken to be equal to the number of such spaces. Note that
in FIG. 16 the thickness of the TCL is increased for visibility,
obscuring open space between some of the toes. In this example, 27
discrete toes labeled T1-T27 were found between corresponding open
spaces.
[0070] Referring next to FIG. 17, cavities may be shaped to form
non-circular heads with edge toes. The head 22 shown in this figure
was formed in a screen cavity of similar shape to the one shown in
FIG. 15, but with a non-circular stem cross-section and a
correspondingly non-circular, smooth opening held against a
cylindrical core surface. As a scale reference, the widest lateral
extent of the head was approximately 0.46 millimeter and the
narrowest lateral extent approximately 0.28 millimeter. As seen,
toes 24 were formed about at least much of the perimeter of the
head and survived the cavity extraction process to define crevices
for snagging microfibers.
[0071] Flexible products may be molded as continuous sheets with
the fastener elements as described above, and then plastically
stretched within their plane after molding to reduce the thickness
of sheet and decrease the density of the fastener elements.
Stretching may be done laterally to improve the tear resistance of
the sheet along the longitudinal direction, or biaxially. The
product may be stretched laterally to increase its area by up to a
factor of seven, for example.
[0072] We have found samples of fastener product produced according
to the above method to be particularly soft to the touch in
comparison with certain other touch fasteners considered to exhibit
softness. To obtain objective measurements of this property, we
subjected representative samples of the product shown in FIGS. 2-5
to testing on a Toccare automated testing system from SynTouch Inc.
of Montrose, Calif. Sample preparation and testing was performed in
accordance with the Toccare User Manual, Software Version 5.0
(2018), with the probe movement aligned with the machine direction
of each of five samples. The mean Toccare micro-texture coarseness
measurement of the representative samples was 21.6, with a standard
deviation of 3.8. The mean Toccare micro-texture roughness
measurement of the representative samples was 26.3, with a standard
deviation of 0.8. Also tested were five samples each of the
fastener product shown in FIGS. 1A-4 of U.S. patent application
Ser. No. 15/680,447 (the contents of which are specifically
incorporated herein by reference as they relate to the materials
and dimensions of the illustrated embodiment), a molded
polypropylene palm-tree hook sold by Velcro USA Inc. under the
designation HTH 819 for use in disposable diapers, and a touch
fastener sold by Gottlieb Binder GmbH under the designation
MicroPlast. These other touch fasteners exhibited mean Toccare
micro-texture coarseness in the machine direction of 49.4, 56.0 and
34.7, respectively, and mean Toccare micro-texture roughness in the
machine direction of 64.6, 83.0 and 49.6, respectively. These
measurements, taken at 20 degrees C. and 30 percent relative
humidity, were consistent with our subjective impression that the
product produced as described above was significantly softer to the
touch.
[0073] While a number of examples have been described for
illustration purposes, the foregoing description is not intended to
limit the scope of the invention, which is defined by the scope of
the appended claims. There are and will be other examples and
modifications within the scope of the following claims.
* * * * *