U.S. patent application number 17/355383 was filed with the patent office on 2021-12-09 for edge barrier film for electronic devices.
The applicant listed for this patent is Universal Display Corporation. Invention is credited to Julia J. BROWN, Ruiqing MA, Prashant MANDLIK.
Application Number | 20210384468 17/355383 |
Document ID | / |
Family ID | 1000005784788 |
Filed Date | 2021-12-09 |
United States Patent
Application |
20210384468 |
Kind Code |
A1 |
MANDLIK; Prashant ; et
al. |
December 9, 2021 |
EDGE BARRIER FILM FOR ELECTRONIC DEVICES
Abstract
In some embodiments, a first product is provided. The first
product may include a substrate, a device having a device footprint
disposed over the substrate, and a barrier film disposed over the
substrate and substantially along a side of the device footprint.
The barrier film may comprise a mixture of a polymeric material and
non-polymeric material. The barrier film may have a perpendicular
length that is less than or equal to 3.0 mm from the side of the
device footprint.
Inventors: |
MANDLIK; Prashant;
(Sunnyvale, CA) ; MA; Ruiqing; (Morristown,
NJ) ; BROWN; Julia J.; (Yardley, PA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Universal Display Corporation |
Ewing |
NJ |
US |
|
|
Family ID: |
1000005784788 |
Appl. No.: |
17/355383 |
Filed: |
June 23, 2021 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
15899651 |
Feb 20, 2018 |
11075357 |
|
|
17355383 |
|
|
|
|
15095524 |
Apr 11, 2016 |
9923168 |
|
|
15899651 |
|
|
|
|
13422926 |
Mar 16, 2012 |
9312511 |
|
|
15095524 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
H01L 51/5253 20130101;
Y10T 428/23 20150115; H01L 51/56 20130101 |
International
Class: |
H01L 51/52 20060101
H01L051/52; H01L 51/56 20060101 H01L051/56 |
Claims
1-12. (canceled)
13. A first product comprising: a substrate; a device disposed over
the substrate, the device having a device footprint; and a barrier
film disposed over the device and substantially along at least a
first side of the device footprint, wherein a footprint of the
barrier film is not more than 3.0 mm wider than the device
footprint on the first side of the device.
14. The first product of claim 13, wherein the barrier film is
disposed along a plurality of sides of the device footprint, and
the footprint of the barrier film is not more than 3.0 mm wider
than the device footprint on any of the plurality of sides of the
device.
15. The first product of claim 13, wherein the bulk diffusion
coefficient of the barrier film is less than 10.sup.-13
cm.sup.2/s.
16. The first product of claim 13, wherein the barrier film is a
mixture of polymeric and non-polymeric material.
17. The first product of claim 16, wherein the barrier film
comprises a mixture of polymeric silicon and inorganic silicon.
18. The first product of claim 16, wherein the mixture is
substantially uniform across the layer.
19. The first product of claim 13, wherein at least a portion of
the barrier film disposed over the device comprises a single-layer
barrier film.
20. The first product of claim 13, wherein the barrier film
comprises a uniform material.
21. The first product of claim 13, wherein the barrier film
comprises a mixture of an oxide and polymeric silicone.
22. The first product of claim 13, wherein the barrier film
comprises at least 40% inorganic silicon.
23. The first product of claim 13, further comprising a conductive
layer disposed over an active area of the device, wherein a portion
of the barrier film is disposed at least partially over the
conductive layer.
24. The first product of claim 13, further comprising a conductive
layer disposed over the active device area; wherein a top sealant
layer is disposed over the conductive layer; and wherein the top
sealant layer and the barrier film comprise different
materials.
25. The first product of claim 13, wherein the barrier film
comprises a first film disposed along the first side of the device
footprint and a second film disposed over the device and the first
film.
26. The first product of claim 25, wherein the second film is a
single-layer barrier film.
27. The first product of claim 26, wherein the single-layer barrier
film comprises an inorganic material.
28. The first product of claim 13, wherein the device comprises an
organic light emitting diode (OLED).
29. The first product of claim 13, wherein the first product
comprises any one of: a consumer device, a solar cell, a thin film
battery, an organic electronic device, a lighting panel or a
lighting source having a lighting panel, a display or an electronic
device having a display, a mobile phone, a notebook computer, a
tablet computer, a television, or an OLED.
Description
BACKGROUND OF THE INVENTION
[0001] Opto-electronic devices that make use of organic materials
are becoming increasingly desirable for a number of reasons. Many
of the materials used to make such devices are relatively
inexpensive, so organic opto-electronic devices have the potential
for cost advantages over inorganic devices. In addition, the
inherent properties of organic materials, such as their
flexibility, may make them well suited for particular applications
such as fabrication on a flexible substrate. Examples of organic
opto-electronic devices include organic light emitting devices
(OLEDs), organic phototransistors, organic photovoltaic cells, and
organic photodetectors. For OLEDs, the organic materials may have
performance advantages over conventional materials. For example,
the wavelength at which an organic emissive layer emits light may
generally be readily tuned with appropriate dopants.
[0002] OLEDs make use of thin organic films that emit light when
voltage is applied across the device. OLEDs are becoming an
increasingly interesting technology for use in applications such as
flat panel displays, illumination, and backlighting. Several OLED
materials and configurations are described in U.S. Pat. Nos.
5,844,363, 6,303,238, and 5,707,745, which are incorporated herein
by reference in their entirety.
[0003] One application for phosphorescent emissive molecules is a
full color display. Industry standards for such a display call for
pixels adapted to emit particular colors, referred to as
"saturated" colors. In particular, these standards call for
saturated red, green, and blue pixels. Color may be measured using
CIE coordinates, which are well known to the art.
[0004] One example of a green emissive molecule is tris
(2-phenylpyridine) iridium, denoted Ir(ppy)3, which has the
structure of Formula I:
##STR00001##
[0005] In this, and later figures herein, we depict the dative bond
from nitrogen to metal (here, Ir) as a straight line.
[0006] As used herein, the term "organic" includes polymeric
materials as well as small molecule organic materials that may be
used to fabricate organic opto-electronic devices. "Small molecule"
refers to any organic material that is not a polymer, and "small
molecules" may actually be quite large. Small molecules may include
repeat units in some circumstances. For example, using a long chain
alkyl group as a substituent does not remove a molecule from the
"small molecule" class. Small molecules may also be incorporated
into polymers, for example as a pendent group on a polymer backbone
or as a part of the backbone. Small molecules may also serve as the
core moiety of a dendrimer, which consists of a series of chemical
shells built on the core moiety. The core moiety of a dendrimer may
be a fluorescent or phosphorescent small molecule emitter. A
dendrimer may be a "small molecule," and it is believed that all
dendrimers currently used in the field of OLEDs are small
molecules.
[0007] As used herein, "top" means furthest away from the
substrate, while "bottom" means closest to the substrate. Where a
first layer is described as "disposed over" a second layer, the
first layer is disposed further away from substrate. There may be
other layers between the first and second layer, unless it is
specified that the first layer is "in contact with" the second
layer. For example, a cathode may be described as "disposed over"
an anode, even though there are various organic layers in
between.
[0008] As used herein, "solution processible" means capable of
being dissolved, dispersed, or transported in and/or deposited from
a liquid medium, either in solution or suspension form.
[0009] A ligand may be referred to as "photoactive" when it is
believed that the ligand directly contributes to the photoactive
properties of an emissive material. A ligand may be referred to as
"ancillary" when it is believed that the ligand does not contribute
to the photoactive properties of an emissive material, although an
ancillary ligand may alter the properties of a photoactive
ligand.
[0010] As used herein, and as would be generally understood by one
skilled in the art, a first "Highest Occupied Molecular Orbital"
(HOMO) or "Lowest Unoccupied Molecular Orbital" (LUMO) energy level
is "greater than" or "higher than" a second HOMO or LUMO energy
level if the first energy level is closer to the vacuum energy
level. Since ionization potentials (IP) are measured as a negative
energy relative to a vacuum level, a higher HOMO energy level
corresponds to an IP having a smaller absolute value (an IP that is
less negative). Similarly, a higher LUMO energy level corresponds
to an electron affinity (EA) having a smaller absolute value (an EA
that is less negative). On a conventional energy level diagram,
with the vacuum level at the top, the LUMO energy level of a
material is higher than the HOMO energy level of the same material.
A "higher" HOMO or LUMO energy level appears closer to the top of
such a diagram than a "lower" HOMO or LUMO energy level.
[0011] As used herein, and as would be generally understood by one
skilled in the art, a first work function is "greater than" or
"higher than" a second work function if the first work function has
a higher absolute value. Because work functions are generally
measured as negative numbers relative to vacuum level, this means
that a "higher" work function is more negative. On a conventional
energy level diagram, with the vacuum level at the top, a "higher"
work function is illustrated as further away from the vacuum level
in the downward direction. Thus, the definitions of HOMO and LUMO
energy levels follow a different convention than work
functions.
[0012] More details on OLEDs, and the definitions described above,
can be found in U.S. Pat. No. 7,279,704, which is incorporated
herein by reference in its entirety.
BRIEF SUMMARY OF THE INVENTION
[0013] Some embodiments provided herein may comprise products, and
methods of manufacturing products, that comprise a barrier film
(i.e. an edge sealant film or layer) that may decrease the
degradation of a device and protect sensitive components from
ingress of environmental contaminants such as water vapor (e.g. the
barrier film may be utilized in electronic devices that consist of
atmosphere sensitive components, such as electrodes or organic
layers). The barrier film may be used in conjunction with any form
of top encapsulation (such as a thin film encapsulation or glass
encapsulation) and may provide an edge seal to increase the shelf
lifetime of the encapsulated device. Moreover, the barrier film
that forms the edge seal may have dimensions that are smaller than
traditional edge sealant layers, thereby reducing the size of the
border area (dead space) of the product.
[0014] In some embodiments, a first product is provided. The first
product may include a substrate, a device having a device footprint
disposed over the substrate, and a barrier film disposed over the
substrate and substantially along a side of the device footprint.
The barrier film may comprise a mixture of a polymeric material and
non-polymeric material. The barrier film may have a perpendicular
length that is less than or equal to 3.0 mm from the side of the
device footprint.
[0015] In some embodiments, in the first product as described
above, the device footprint may comprise an active device area and
an inactive device area. In some embodiments, the barrier film may
have a perpendicular length that is less than or equal to 3.0 mm
from the side of the inactive device area. In some embodiments, the
barrier film may not extend to a distance of greater than 3.0 mm
from a side of the active device area.
[0016] In some embodiments, in the first product as described
above, the device footprint may comprise an active device area, and
the barrier film may have a perpendicular length that is less than
or equal to 3.0 mm from the side of the active device area.
[0017] In some embodiments, in the first product as described
above, the barrier film may comprise a mixture of a polymeric
silicon and inorganic silicon. In some embodiments, the mixture of
polymeric silicon and inorganic silicon is substantially uniform
across the layer.
[0018] In some embodiments, in the first product as described
above, the barrier film may have a perpendicular length that is
less than or equal to 2.0 mm from the side of the device footprint.
In some embodiments, the barrier film may have a perpendicular
length that is less than or equal to 1.0 mm from the side of the
device footprint.
[0019] In some embodiments, in the first product as described
above, the barrier film may not have a perpendicular length that is
greater than 3.0 mm from the side of the device footprint. In some
embodiments, the barrier film may not have a perpendicular length
that is greater than 2.0 mm from the side of the device footprint.
In some embodiments, the barrier film does not have a perpendicular
length that is greater than 1.0 mm from the side of the device
footprint.
[0020] In some embodiments, in the first product as described
above, the barrier film may not have a perpendicular length that is
greater than 3.0 mm or less than 1.0 mm from the side of the device
footprint. In some embodiments, the barrier film may not have a
perpendicular length that is greater than 2.0 mm or less than 0.5
mm from the side of the device footprint.
[0021] In some embodiments, in the first product as described
above, the barrier film may comprise a substantially uniform
material. In some embodiments, the barrier film may comprise a
uniform material.
[0022] In some embodiments, in the first product as described
above, the barrier film may comprise a mixture of an oxide and
polymeric silicone. In some embodiments, the barrier film may
comprise at least 40% inorganic silicon. In some embodiments, the
barrier film may comprise at least 60% inorganic silicon. In some
embodiments, the barrier film may comprise at least 80% inorganic
silicon.
[0023] In some embodiments, in the first product as described
above, a surface of the barrier film may be disposed adjacent to a
surface of the substrate to form a first interface, and the ratio
of the index of refraction of the bulk of the barrier film and the
index of refraction of a portion of the barrier film that is within
10 nm of the interface is between 0.9993 and 0.9247.
[0024] In some embodiments, in the first product as described
above, where a surface of the barrier film is disposed adjacent to
a surface of the substrate to form a first interface, the index of
refraction of a portion of the barrier film that is within 10 nm of
the interface may be between 1.35 and 1.459.
[0025] In some embodiments, in the first product as described
above, where a surface of the barrier film is disposed adjacent to
a surface of the substrate to form a first interface, the barrier
film may comprise a material having a bulk diffusion coefficient of
water vapor of less than 10.sup.-13 cm.sup.2/sec. In some
embodiments, the diffusion coefficient of water vapor at the first
interface may be between 10.sup.-8 cm.sup.2/sec and 10.sup.-13
cm.sup.2/sec when exposed to an ambient temperate of 65.degree. C.
and relative humidity of 85%.
[0026] In some embodiments, in the first product as described
above, where a surface of the barrier film is disposed adjacent to
a surface of the substrate to form a first interface, the barrier
film may comprise a material having a bulk diffusion coefficient of
water vapor. The ratio of the bulk diffusion coefficient of water
vapor of the barrier film and a diffusion coefficient of water
vapor near the first interface may be between 1 and 10.sup.-5. In
some embodiments, the ratio of the bulk diffusion coefficient of
water vapor of the barrier film and a diffusion coefficient of
water vapor within 10 nm of the first interface may be between 1
and 10.sup.-5.
[0027] In some embodiments, in the first product as described
above, the device may further comprise a conductive layer disposed
over the active device area. In some embodiments, a portion of the
barrier film may be disposed at least partially over the conductive
layer. In some embodiments, a portion of the barrier film may be
disposed over the entire conductive layer.
[0028] In some embodiments, in the first product as described above
where the device comprises a conductive layer disposed over the
active device area, a top sealant layer may be disposed over the
conductive layer. The top sealant layer and the barrier film may
comprise different materials.
[0029] In some embodiments, in the first product as described
above, the first product may comprise a border area (i.e. dead
space). The border area may have a thickness that is less than 3.0
mm.
[0030] In some embodiments, in the first product as described
above, where the first product comprises a border area, the border
area may have a thickness that is less than 2.0 mm. In some
embodiments, the border area may have a thickness that is less than
1.0 mm.
[0031] In some embodiments, the first product as described above
may comprise a consumer device. In some embodiments, the first
product may comprise anyone of: a solar cell, a thin film battery,
an organic electronic device, a lighting panel or a lighting source
having a lighting panel, a display or an electronic device having a
display, a mobile phone, a notebook computer, a tablet computer, or
a television.
[0032] In some embodiments, in the first product as described
above, the device may comprise an organic layer. In some
embodiments, the organic layer may comprise an electro-luminescent
material. In some embodiments, the device may comprise an OLED.
[0033] In some embodiments, a first method may be provided. The
first method may comprise the steps of providing a substrate having
a device having a device footprint disposed over the substrate, and
fabricating a barrier film over the substrate and substantially
along a side of the device footprint, where the barrier film may be
fabricated so as to have a perpendicular length that is less than
or equal to 3.0 mm from the side of the device footprint.
[0034] In some embodiments, in the first method as described above,
the device footprint may comprise an organic layer. In some
embodiments, the organic layer may comprise an electroluminescent
(EL) material. In some embodiments, the device may comprise an
OLED.
[0035] In some embodiments, in the first method as described above,
the barrier film may be fabricated so as to have a perpendicular
length that is less than or equal to 2.0 mm from the side of the
device footprint. In some embodiments, the barrier film may be
fabricated so as to have a perpendicular length that is less than
or equal to 1.0 mm from the side of the device footprint.
[0036] In some embodiments, in the first method as described above,
the step of fabricating the barrier film may comprise chemical
vapor deposition. In some embodiments, the step of fabricating the
barrier film may utilize an organosilicon precursor.
[0037] In some embodiments, in the first method as decried above,
the step of fabricating the barrier film so as to have a
perpendicular length that is less than or equal to 3.0 mm from the
side of the device footprint may comprise depositing the barrier
film through a mask such that the perpendicular length is less than
or equal to 3.0 mm from the side of the device footprint.
[0038] In some embodiments, in the first method as described above,
the step of fabricating the barrier film so as to have a
perpendicular length that is less than or equal to 3.0 mm from the
side of the device footprint may comprise the steps of: depositing
a barrier film over the substrate and substantially along a side of
the device footprint, wherein the barrier film is deposited so as
to have a perpendicular length that is greater than or equal to 3.0
mm from the side of the device footprint, and, after depositing the
barrier film, breaking the barrier film such that the barrier film
has a perpendicular length that is less than or equal to 3.0 mm
from the side of the device footprint. In some embodiments, the
step of breaking the barrier film may be accomplished by, or in
combination with, breaking the substrate.
[0039] In some embodiments, a first product prepared by a process
may be provided. The process for preparing the first product may
comprise the steps of providing a substrate having a device
disposed over the substrate, where the device has a device
footprint, and fabricating a barrier film over the substrate and
substantially along a side of the device footprint, where the
barrier film may be fabricated so as to have a perpendicular length
that is less than or equal to 3.0 mm from the side of the device
footprint.
[0040] In some embodiments, in the first product prepared by a
process as described above, the device may comprise an organic
layer. In some embodiments, the organic layer may comprise an
organic electroluminescent (EL) material. In some embodiments, the
device may comprise an OLED.
[0041] In some embodiments, in the first product prepared by a
process as described above, the barrier film may be fabricated so
as to have perpendicular length that is less than or equal to 2.0
mm from the side of the device footprint. In some embodiments, the
barrier film is fabricated so as to have perpendicular length that
is less than or equal to 1.0 mm from the side of the device
footprint.
[0042] In some embodiments, in the first product prepared by a
process as described above, the step of fabricating the barrier
film may comprises depositing the first barrier film using an
organosilicon precursor. In some embodiments, the step of
fabricating the barrier film may comprise chemical vapor
deposition. In some embodiments, the step of fabricating the
barrier film may comprise plasma enhance chemical vapor deposition
(PE-CVD). In some embodiments, the barrier film consists
essentially of a mixture of polymeric silicon and inorganic
silicon, where the weight ratio of polymeric silicon to inorganic
silicon is in the range of 95:5 to 5:95, and where the polymeric
silicon and the inorganic silicon are created from the same
precursor material. In some embodiments, at least an 0.1 .mu.m
thickness of the barrier film is deposited under the same reaction
conditions for all the reaction conditions in the deposition
process and the water vapor transmission rate is less than
10.sup.-6 g/m.sup.2/day through the at least 0.1 .mu.m thickness of
the barrier film.
[0043] In some embodiments, in the first product prepared by a
process as described above, where the step of fabricating the
barrier film comprises depositing the first barrier film using an
organosilicon precursor, the precursor material may comprise
hexamethyl disiloxane or dimethyl siloxane. In some embodiments,
the precursor material may comprise a single organosilicon
compound. In some embodiments, the precursor material may comprise
a mixture of organosilicon compounds.
[0044] In some embodiments, in the first product prepared by a
process as described above, the step of fabricating the barrier
film may comprise depositing the barrier film through a mask such
that the perpendicular length is less than or equal to 3.0 mm from
the side of the device footprint. In some embodiments, the
perpendicular length may be less than or equal to 1.0 mm from the
side of the device footprint.
BRIEF DESCRIPTION OF THE DRAWINGS
[0045] FIG. 1 shows an organic light emitting device.
[0046] FIG. 2 shows an inverted organic light emitting device that
does not have a separate electron transport layer.
[0047] FIG. 3 shows a cross-section of an exemplary device having a
multilayer barrier. The footprints of the deposition masks used for
both inorganic and polymer films may be the same, which is larger
than the device footprint by, for example, 1.0 mm in this exemplary
device.
[0048] FIG. 4 shows a cross-section of an exemplary device having a
multilayer barrier. The footprint of the mask used for the polymer
film may be larger than the device footprint by, for example, 1.0
mm, and the footprint of the mask of the inorganic film may be
larger than that of the polymer film by, for example, 1.0 mm.
[0049] FIG. 5 shows a cross-section of an exemplary device having a
multilayer barrier. The footprints of the masks used for each stack
of inorganic and polymer film may be larger than the previous stack
by, for example, 1.0 mm. The footprint of the first stack is larger
than that of the device footprint of the device by, for example,
1.0 mm.
[0050] FIG. 6 shows a cross-section of a barrier film as an edge
sealant for an exemplary device in accordance with some
embodiments. The difference in the footprint of the mask used for
the barrier film as the edge seal of this exemplary device and the
device footprint is shown as ("").
[0051] FIG. 7 shows a cross-section of an exemplary device having a
barrier film as an edge sealant and also as the top encapsulation,
in accordance with some embodiments.
[0052] FIG. 8 comprises photographs of the luminescent areas of a
2.0 mm.sup.2 bottom emitting OLED test pixel coated with a 9.0
.mu.m thick barrier film as a top encapsulation layer, in
accordance with some embodiments. The footprint of the barrier film
as the edge sealant and top encapsulation in this exemplary device
was at least 2.0 mm larger than the footprint of the polymer
material used in the OLED.
[0053] FIGS. 9(a) and 9(b) show experimental results for two tests
conducted by the inventors.
[0054] FIG. 9(a) comprises photographs of the luminescent areas of
three exemplary 1 cm.sup.2 bottom emitting OLED test pixels coated
with a 9.0 .mu.m thick barrier film as the top encapsulation. The
photographs were taken at the start of testing and after periods of
accelerated storage at environmental conditions of 65.degree. C.
and 85% relative humidity (RH). The footprint of the barrier film
as the edge sealant (i.e. the perpendicular length from the side of
the device footprint) for each of the devices was (a) 1.0 mm, (b)
2.0 mm, and (c) 3.0 mm larger than the device footprint that
comprises the organic material used in the exemplary OLED.
[0055] FIG. 9(b) comprises photographs of three exemplary 4.0
mm.sup.2 calcium (Ca) buttons coated with a 9.0 .mu.m thick barrier
film as the top encapsulation. The photographs were taken during
the periods of accelerated storage at environmental conditions of
85.degree. C. and 85% RH. The footprint of the barrier film as the
edge sealant (i.e. the perpendicular length from Ca button) for
each of the devices was (a) 1.0 mm, (b) 2.0 mm, and (c) 3.0 mm
larger than the footprint of Ca button.
[0056] FIG. 10 shows a cross-section of an exemplary device in
which the barrier film is used as the edge sealant and the top
encapsulation, in accordance with some embodiments.
[0057] FIG. 11 shows a cross-section of an exemplary device in
which the barrier film is used as an edge sealant, but is not used
as the top encapsulation in accordance with some embodiments. The
top encapsulation in this exemplary device comprises a single layer
barrier film. The footprints of the mask used for the top
encapsulation film in this exemplary embodiment may be
approximately the same size as that used for the device footprint.
The footprint of the mask used to deposit the barrier film as the
edge sealant may be, for example, 1.0 mm larger than that of the
device footprint.
[0058] FIG. 12 shows a cross-section of an exemplary device in
which the barrier film is an edge sealant, but it does not comprise
the top encapsulation in accordance with some embodiments. The top
encapsulation in this exemplary device is a multilayer barrier
film. In this example, the footprint of the mask used for the top
encapsulation may be the same size as that used for the device
footprint. The footprint of the mask used to deposit the barrier
film as the edge sealant may be, for example, 1.0 mm larger (or any
suitable value) than that of the device footprint.
[0059] FIG. 13 shows a cross-section of an exemplary device in
which the barrier film is an edge sealant, but it is not the top
encapsulation in accordance with some embodiments. The top
encapsulation in this example comprises a glass encapsulation using
epoxy. The footprint of the mask used for the top encapsulation in
this example may be the same size as that used for the device
footprint. The footprint of the mask used to deposit the barrier
film as the edge sealant may be 1.0 mm larger (or any suitable
value) than that of the device footprint.
[0060] FIG. 14 shows a cross-section of an exemplary device in
which the barrier film is an edge sealant and where the top
encapsulation comprises a glass encapsulation using epoxy, in
accordance with some embodiments. In this example, the epoxy is not
deposited directly on the device (e.g. on one or more layers of the
device such as a conductive layer), but a layer of barrier film is
disposed between the epoxy and the device (or the one or more
layers of the device).
[0061] FIG. 15 shows a top-view of an exemplary product in
accordance with some embodiments.
[0062] FIG. 16 shows a cross-sectional view of the exemplary
product shown in FIG. 15 in accordance with some embodiments.
[0063] FIG. 17 shows a cross-sectional view of the exemplary
product shown in FIG. 15 in accordance with some embodiments.
DETAILED DESCRIPTION OF THE INVENTION
[0064] Generally, an OLED comprises at least one organic layer
disposed between and electrically connected to an anode and a
cathode. When a current is applied, the anode injects holes and the
cathode injects electrons into the organic layer(s). The injected
holes and electrons each migrate toward the oppositely charged
electrode. When an electron and hole localize on the same molecule,
an "exciton," which is a localized electron-hole pair having an
excited energy state, is formed. Light is emitted when the exciton
relaxes via a photoemissive mechanism. In some cases, the exciton
may be localized on an excimer or an exciplex. Non-radiative
mechanisms, such as thermal relaxation, may also occur, but are
generally considered undesirable.
[0065] The initial OLEDs used emissive molecules that emitted light
from their singlet states ("fluorescence") as disclosed, for
example, in U.S. Pat. No. 4,769,292, which is incorporated by
reference in its entirety. Fluorescent emission generally occurs in
a time frame of less than 10 nanoseconds.
[0066] More recently, OLEDs having emissive materials that emit
light from triplet states ("phosphorescence") have been
demonstrated. Baldo et al., "Highly Efficient Phosphorescent
Emission from Organic Electroluminescent Devices," Nature, vol.
395, 151-154, 1998; ("Baldo-I") and Baldo et al., "Very
high-efficiency green organic light-emitting devices based on
electrophosphorescence," Appl. Phys. Lett., vol. 75, No. 3, 4-6
(1999) ("Baldo-II"), which are incorporated by reference in their
entireties. Phosphorescence is described in more detail in U.S.
Pat. No. 7,279,704 at cols. 5-6, which are incorporated by
reference.
[0067] FIG. 1 shows an organic light emitting device 100. The
figures are not necessarily drawn to scale. Device 100 may include
a substrate 110, an anode 115, a hole injection layer 120, a hole
transport layer 125, an electron blocking layer 130, an emissive
layer 135, a hole blocking layer 140, an electron transport layer
145, an electron injection layer 150, a protective layer 155, and a
cathode 160. Cathode 160 is a compound cathode having a first
conductive layer 162 and a second conductive layer 164. Device 100
may be fabricated by depositing the layers described, in order. The
properties and functions of these various layers, as well as
example materials, are described in more detail in U.S. Pat. No.
7,279,704 at cols. 6-10, which are incorporated by reference.
[0068] More examples for each of these layers are available. For
example, a flexible and transparent substrate-anode combination is
disclosed in U.S. Pat. No. 5,844,363, which is incorporated by
reference in its entirety. An example of a p-doped hole transport
layer is m-MTDATA doped with F.sub.4-TCNQ at a molar ratio of 50:1,
as disclosed in U.S. Patent Application Publication No.
2003/0230980, which is incorporated by reference in its entirety.
Examples of emissive and host materials are disclosed in U.S. Pat.
No. 6,303,238 to Thompson et al., which is incorporated by
reference in its entirety. An example of an n-doped electron
transport layer is BPhen doped with Li at a molar ratio of 1:1, as
disclosed in U.S. Patent Application Publication No. 2003/0230980,
which is incorporated by reference in its entirety. U.S. Pat. Nos.
5,703,436 and 5,707,745, which are incorporated by reference in
their entireties, disclose examples of cathodes including compound
cathodes having a thin layer of metal such as Mg:Ag with an
overlying transparent, electrically-conductive, sputter-deposited
ITO layer. The theory and use of blocking layers is described in
more detail in U.S. Pat. No. 6,097,147 and U.S. Patent Application
Publication No. 2003/0230980, which are incorporated by reference
in their entireties. Examples of injection layers are provided in
U.S. Patent Application Publication No. 2004/0174116, which is
incorporated by reference in its entirety. A description of
protective layers may be found in U.S. Patent Application
Publication No. 2004/0174116, which is incorporated by reference in
its entirety.
[0069] FIG. 2 shows an inverted OLED 200. The device includes a
substrate 210, a cathode 215, an emissive layer 220, a hole
transport layer 225, and an anode 230. Device 200 may be fabricated
by depositing the layers described, in order. Because the most
common OLED configuration has a cathode disposed over the anode,
and device 200 has cathode 215 disposed under anode 230, device 200
may be referred to as an "inverted" OLED. Materials similar to
those described with respect to device 100 may be used in the
corresponding layers of device 200. FIG. 2 provides one example of
how some layers may be omitted from the structure of device
100.
[0070] The simple layered structure illustrated in FIGS. 1 and 2 is
provided by way of non-limiting example, and it is understood that
embodiments of the invention may be used in connection with a wide
variety of other structures. The specific materials and structures
described are exemplary in nature, and other materials and
structures may be used. Functional OLEDs may be achieved by
combining the various layers described in different ways, or layers
may be omitted entirely, based on design, performance, and cost
factors. Other layers not specifically described may also be
included. Materials other than those specifically described may be
used. Although many of the examples provided herein describe
various layers as comprising a single material, it is understood
that combinations of materials, such as a mixture of host and
dopant, or more generally a mixture, may be used. Also, the layers
may have various sublayers. The names given to the various layers
herein are not intended to be strictly limiting. For example, in
device 200, hole transport layer 225 transports holes and injects
holes into emissive layer 220, and may be described as a hole
transport layer or a hole injection layer. In one embodiment, an
OLED may be described as having an "organic layer" disposed between
a cathode and an anode. This organic layer may comprise a single
layer, or may further comprise multiple layers of different organic
materials as described, for example, with respect to FIGS. 1 and
2.
[0071] Structures and materials not specifically described may also
be used, such as OLEDs comprised of polymeric materials (PLEDs)
such as disclosed in U.S. Pat. No. 5,247,190 to Friend et al.,
which is incorporated by reference in its entirety. By way of
further example, OLEDs having a single organic layer may be used.
OLEDs may be stacked, for example as described in U.S. Pat. No.
5,707,745 to Forrest et al, which is incorporated by reference in
its entirety. The OLED structure may deviate from the simple
layered structure illustrated in FIGS. 1 and 2. For example, the
substrate may include an angled reflective surface to improve
out-coupling, such as a mesa structure as described in U.S. Pat.
No. 6,091,195 to Forrest et al., and/or a pit structure as
described in U.S. Pat. No. 5,834,893 to Bulovic et al., which are
incorporated by reference in their entireties.
[0072] Unless otherwise specified, any of the layers of the various
embodiments may be deposited by any suitable method. For the
organic layers, preferred methods include thermal evaporation,
ink-jet, such as described in U.S. Pat. Nos. 6,013,982 and
6,087,196, which are incorporated by reference in their entireties,
organic vapor phase deposition (OVPD), such as described in U.S.
Pat. No. 6,337,102 to Forrest et al., which is incorporated by
reference in its entirety, and deposition by organic vapor jet
printing (OVJP), such as described in U.S. patent application Ser.
No. 10/233,470, which is incorporated by reference in its entirety.
Other suitable deposition methods include spin coating and other
solution based processes. Solution based processes are preferably
carried out in nitrogen or an inert atmosphere. For the other
layers, preferred methods include thermal evaporation. Preferred
patterning methods include deposition through a mask, cold welding
such as described in U.S. Pat. Nos. 6,294,398 and 6,468,819, which
are incorporated by reference in their entireties, and patterning
associated with some of the deposition methods such as ink jet and
OVJP. Other methods may also be used. The materials to be deposited
may be modified to make them compatible with a particular
deposition method. For example, substituents such as alkyl and aryl
groups, branched or unbranched, and preferably containing at least
3 carbons, may be used in small molecules to enhance their ability
to undergo solution processing. Substituents having 20 carbons or
more may be used, and 3-20 carbons is a preferred range. Materials
with asymmetric structures may have better solution processibility
than those having symmetric structures, because asymmetric
materials may have a lower tendency to recrystallize. Dendrimer
substituents may be used to enhance the ability of small molecules
to undergo solution processing.
[0073] Devices fabricated in accordance with embodiments of the
invention may be incorporated into a wide variety of consumer
products, including flat panel displays, computer monitors,
televisions, billboards, lights for interior or exterior
illumination and/or signaling, heads up displays, fully transparent
displays, flexible displays, laser printers, telephones, cell
phones, personal digital assistants (PDAs), laptop computers,
digital cameras, camcorders, viewfinders, micro-displays, vehicles,
a large area wall, theater or stadium screen, lighting fixtures, or
a sign. Various control mechanisms may be used to control devices
fabricated in accordance with the present invention, including
passive matrix and active matrix. Many of the devices are intended
for use in a temperature range comfortable to humans, such as 18
degrees C. to 30 degrees C., and more preferably at room
temperature (20-25 degrees C.).
[0074] The materials and structures described herein may have
applications in devices other than OLEDs. For example, other
optoelectronic devices such as organic solar cells and organic
photodetectors may employ the materials and structures. More
generally, organic devices, such as organic transistors, may employ
the materials and structures.
[0075] The terms halo, halogen, alkyl, cycloalkyl, alkenyl,
alkynyl, arylkyl, heterocyclic group, aryl, aromatic group, and
heteroaryl are known to the art, and are defined in U.S. Pat. No.
7,279,704 at cols. 31-32, which are incorporated herein by
reference.
[0076] As used herein, the "active device area" of a device may
refer to the portion of the device in which electrons, holes,
and/or photons are generated or absorbed and may comprise one or
more organic and/or semi-conductor materials (such as organic
semi-conductors or doped silicon). For organic electronic devices,
the active device area may comprise one or more organic layers. For
example, the active device area of an OLED may refer to the
emissive area of the device (i.e. the portion of the device that
emits light) and may include an organic electroluminescent
material. The active device area of a solar cell may refer to the
portion of the device where photons are absorbed and electrons are
released (e.g. it may refer to the portion of the device that
comprises a semi-conductor material). For a thin film battery, the
active device area may refer to the electrolyte and may comprise,
for example, lithium phosphorus oxynitride. These are just a few
examples of active device areas of exemplary devices, and it should
be appreciated that embodiments disclosed herein are not so
limited.
[0077] As used herein, a "barrier film" or "barrier layer" may
refer to a layer of material that may be utilized to decrease the
permeation of gases, vapors, and/or moisture (or other
environmental particulates) into the active device area of the
device so as to increase lifetime and/or reduce performance
degradation. In some embodiments, the barrier film may comprise a
hybrid layer comprising a mixture of a polymeric material and a
non-polymeric material. As used herein, the term "non-polymeric"
refers to a material made of molecules having a well-defined
chemical formula with a single, well-defined molecular weight. A
"nonpolymeric" molecule can have a significantly large molecular
weight. In some circumstances, a non-polymeric molecule may include
repeat units. As used herein, the term "polymeric" refers to a
material made of molecules that have repeating subunits that are
covalently linked, and that has a molecular weight that may vary
from molecule to molecule because the polymerizing reaction may
result in different numbers of repeat units for each molecule. For
example, in some embodiments, the barrier film may comprise a
mixture of polymeric silicon and inorganic silicon. Examples of
barrier films are described in more detail below.
[0078] As used herein, the "border area" (i.e. dead space) of the
device may comprise the combination of the "inactive device area"
and the "non-device edge area." As used in this context, the
"thickness" of the border area may refer to the distance from the
device footprint to the edge of the border area (which may also
comprise the edge of the substrate in some embodiments) in a
direction that is perpendicular to a side of the device
footprint.
[0079] As used herein, the term "comprising" is not intended to be
limiting, but may be a transitional term synonymous with
"including," "containing," or "characterized by." The term
"comprising" may thereby be inclusive or open-ended and does not
exclude additional, unrecited elements or method steps when used in
a claim. For instance, in describing a method, "comprising"
indicates that the claim is open-ended and allows for additional
steps. In describing a device, "comprising" may mean that a named
element(s) may be essential for an embodiment, but other elements
may be added and still form a construct within the scope of a
claim. In contrast, the transitional phrase "consisting of"
excludes any element, step, or ingredient not specified in a claim.
This is consistent with the use of the term throughout the
specification.
[0080] As used herein, the "inactive device area" of a device may
refer to portions of the device that comprises one or more layers
of materials (such as organic layers) that are also included in the
active area, but which does not comprise a part of the device where
electrons, holes, and/or photons are generated or absorbed (i.e. it
is not a part of the active device area of the device). For
example, with regard to an OLED, the inactive device area may
include one or more organic layers and/or a portion of an
electrode, but this portion of the device may not include one or
more of the other organic layers (or one or more electrodes) and
therefore does not emit light. The inactive device area is often,
but not always, the result of depositing an organic layer so as to
extend beyond the edges of one of the electrodes to prevent or
reduce the likelihood of shorting. In some instances, an insulating
layer (e.g. "grid layer") may be disposed over the substrate and a
portion of an electrode so as to electrically insulate the
conductive layers of the device (see, e.g., FIGS. 15-17). These
areas generally do not emit light and therefore would comprise a
portion of the "inactive device area." In most instances, the
inactive device area of the device is disposed adjacent to one or
more sides of the active device area.
[0081] As used herein, the "device footprint" may refer to the
total area of the "active device area" of the device and the
"inactive device area" of the device. With reference to an organic
device for illustration purposes, the device footprint may refer to
the portion of the device in which one or more organic layers (i.e.
the organic footprint) and/or one or more insulating grid layers
are disposed over the substrate.
[0082] As used herein, a "non-device edge area" may refer to the
area around the device footprint--that is, the portion of a product
that does not include the "active device area" or the "inactive
device area" of the device. For example, the non-device edge area
may not comprise one or more of the layers that of the active
device area of the device. With reference to organic electronic
devices, the non-device edge area may refer to the portion of
product that typically does not comprise an organic layer or an
insulating layer (such as a grid layer that is disposed over one of
the electrodes of the OLED). For instance, the non-device edge area
may refer to the non-emitting areas of the OLED that do not
comprise a part of the inactive device area. The non-device edge
area may include the portions of the product in which one or more
barrier films or layers are disposed along a side of the device
footprint.
[0083] As used herein, the "perpendicular length" of the barrier
film may refer to the distance from a portion of the barrier film
that is disposed closest to the device footprint (e.g. adjacent to
the active device area or inactive device area) to another portion
of the barrier film that is disposed farthest away from the device
footprint (e.g. an edge of the barrier film) in a direction that is
perpendicular to the side of the device footprint and parallel to
the surface of the substrate that the barrier film is disposed
over. In other words, the perpendicular length may be a measure of
the distance that the barrier film extends away from the device
footprint (i.e. the footprint of the barrier film beyond the device
footprint). The reason for utilizing the "side" of the device
footprint as determining the perpendicular length is to generally
exclude the corner effects, where the length of the barrier film
may vary because of the shape of the device footprint. Thus, in
general, the perpendicular length may correspond to the length of
the barrier film disposed so as to provide resistance to the
horizontal ingress of moisture (and other contaminants) into the
active device area. In some embodiments, the perpendicular length
may also correspond to the length of the barrier film adjacent to
the substrate; however, embodiments are not limited such as when
one or more conductive layers may extend beyond the device
footprint (e.g. to make electrical connections), examples of which
are illustrated in FIGS. 15 and 16 and described below.
[0084] It should be noted that although embodiments described below
may make reference to organic devices such as OLEDs, embodiments
are not so limited. The inventors have found that barrier films
comprising a mixture of a polymeric material and a non-polymeric
material as an edge sealant may be generally used in any thin film
electronic device, particularly those that may have a component (or
components) that is sensitive to environmental permeants such as
water vapor. Moreover, the inventors have found that the exemplary
barrier film may be used as an edge sealant having a perpendicular
length (as described above) that is less than 3.0 mm (preferably
less than 2.0 mm; and more preferably less than 1.0 mm) while still
providing adequate device performance and lifetime. This reduction
in the size of the edge sealant may reduce the size of the
non-active edge areas of such devices and thereby potentially
reduce the border area and/or the overall size of a product (such
as an electronic device) that comprises the exemplary barrier film
as an edge sealant.
[0085] In general, electronic devices having moisture sensitive
electronic components (such as water vapor sensitive electrodes)
may degrade upon storage because of the atmospheric conditions. The
degradation may be in the form of dark spots caused by the ingress
of water vapor and oxygen vertically through the bulk of a thin
film encapsulation (TFE) (or through particles embedded in the
TFE), or by the ingress of water vapor and oxygen horizontally
through the edge of the TFE. The TFE may also be referred to herein
as a barrier layer or barrier film. The edge ingress of the water
vapor typically occurs either via the horizontal permeation of the
permeants (e.g. water vapor molecules) through the TFE itself (see,
e.g., FIG. 6, 604 described below) or via the horizontal permeation
of the permeants through the interface of the TFE with the
underlying substrate (see, e.g., FIG. 6, 605 described below). The
inventors have thereby found that it is preferred that a TFE
providing an edge seal for an electronic device reduces both types
of horizontal permeations (i.e. permeation across the layer itself
and permeation at the interface between the layer and the
substrate). In this regard, embodiments provided herein comprise an
edge seal that may provide for improved performance and may be used
for electronic devices that may be sensitive to atmosphere
conditions, such as moisture.
[0086] Previous edge seals that were widely in use utilized
multilayer barriers. For example, many devices comprised multilayer
barriers that consisted of alternate layers of inorganic and
polymer films. These barriers work on the principle of delaying the
permeant molecules from reaching the device by forming a long and
tortuous diffusion path. Some examples of these multilayer barriers
will be described below.
[0087] One of the prior methods for encapsulating a device with a
multilayer barrier utilizes the same mask for both the inorganic
and the polymer films; however, the size of the mask is larger than
the footprint of a device so as to provide some edge ingress
barrier (and also to allow for mask alignment tolerance). Assuming
an alignment tolerance of 500 .mu.m (which is reasonable for most
fabrication processes) for both the device mask (e.g. the mask that
may be used to deposit the layers that forth the active device
area, inactive device area, and/or other components such as
electrodes) and the encapsulation mask (e.g. the mask used to
deposit the inorganic and the polymer films), this implies that the
encapsulation mask should be about 1.0 mm larger than the device
mask so as to prevent any device exposure when both the deposition
of the device and the alignment of the encapsulation mask is off in
the worst case scenario. It may also be assumed that the thickness
of the inorganic film of the multilayer barrier is about 50 nm, and
the thickness of the polymer film of multilayer barrier is about
800 nm, as is typically the case for such devices. FIG. 3 provides
an example of such a device.
[0088] FIG. 3 shows a product 300 that comprises a substrate 310, a
device 301 having a device footprint (which may include an active
device area and an inactive device area) disposed over the
substrate 310, and a plurality of inorganic layers 302 and polymer
layers 303 that encapsulate the device 301. The product 300 of FIG.
3 shows a multilayer barrier encapsulation process consisting of a
5-layer stack that includes five inorganic layers (302) with four
polymer layers (303) disposed between the organic layers (i.e.
sandwiched between). In general, this type of masking and
deposition method may be relatively simple to fabricate because it
uses a minimum number of mask changes (thus adding minimum
processing time for fabrication)--i.e. after the device 301 and
corresponding components are deposited on the substrate, both the
inorganic layer and the polymer layer may be deposited through a
single mask. As shown in FIG. 3, this exemplary multi-layer barrier
provides a direct path (i.e. Path-1 shown by the arrow 304) for
water vapor to travel across the polymer layer 303 horizontally and
reach the device 301 of product 300 (e.g. an environmentally
sensitive electrode or organic layer) by permeating across just one
inorganic layer 302 (i.e. the inorganic layer disposed adjacent to
the device footprint of the device 301). Thus, the edge seal
provided by this type of multilayer barrier as shown in FIG. 3 is
mostly dependent on the permeation rate of water vapor across the
polymer material 303 (which is typically higher than the permeation
rate of the inorganic material). In general, for device designs
such as those shown in FIG. 3, to achieve suitable device
performance and lifetime, such a device would use a footprint for
the encapsulation layer (e.g. the polymer 303 and inorganic 302
layers) that is much larger than the footprint of device 301. That
is, the use of a single mask size for both inorganic 302 and
organic 303 films that is larger than the device footprint to
deposit the edge seal may not be a working or practical solution to
providing a device with a minimal amount of border area (i.e. dead
space). This is further illustrated in the example provided
below.
[0089] The value of the diffusion constant of water vapor in
polyacrylate polymer (a commonly used encapsulation material) at
25.degree. C. can be calculated by using the diffusion constant
("D") of polyacrylate polymer at 38.degree. C. as calculated by G.
L. Graff, R. E. Williford, and P. E. Burrows, Mechanisms of vapor
permeation through multilayer barrier films: Lag time versus
equilibrium permeation, J. Appl. Phys., 96 (4), pp. 1840-1849
(2004) (i.e. the diffusion constant (D) at 38.degree.
C..about.8.5.times.10.sup.-9 cm.sup.2/sec), which is incorporated
herein by reference in its entirety, and utilizing the activation
energy of water vapor in such a polymer as was calculated by Z.
Chen, Q. Gu, H. Zou, T. Zhao, H. WANG, Molecular Dynamics
Simulation of Water Diffusion Inside an Amorphous Polyacrylate
Latex Film, Journal of Polymer Science: Part B: Polymer Physics,
Vol. 45, 884-891 (2007) (found to be approximately equal to 13
kJ/mole), which is also incorporated herein by reference in its
entirety. In this manner, the diffusion constant of water vapor in
polyacrylate polymer at 25.degree. C. can be estimated to be
.about.6.8.times.10.sup.-9 cm.sup.2/sec. Using this diffusion
constant, the lag time of water vapor diffusion through Path-1
(304) for the device 300 shown in FIG. 3 can be estimated. As used
in this context, the lag time () refers to the approximate
diffusion time of permeant molecules (e.g. water vapor molecules)
across a distance (), and is related to the diffusion constant of
the material by the relation given by: =.sup.2/(6D), as shown by
Graff et al., Mechanisms of vapor permeation through multilayer
barrier films: Lag time versus equilibrium permeation, J. Appl.
Phys., 96 (4), pp. 1840-1849 (2004). Using the diffusion constant
(D) of water vapor in polyacrylate polymer calculated above, the
lag time at 25.degree. C. may be calculated to be close to 70 hours
for a path length of 1.0 mm. That is, for the exemplary
encapsulation method shown in FIG. 3, it would generally take water
vapor approximately 70 hours at room temperature to reach the
inorganic layer 302 adjacent to the footprint of device 301 of the
product 300 when traveling horizontally along Path-1 (304). Once
the permeant crosses the polymer layer 303 along Path-1 (304), it
need only permeate across just a single inorganic film layer 302
(which typically has a thickness of approximately 50 nm) to reach
the footprint of device 301. The permeants can then reach the
active device area quickly through defects (e.g. pinholes, cracks,
particles, etc.) and cause damage. Needless to say, this design may
result in device degradation that is unacceptable for an intended
purpose or application.
[0090] Another approach using a multilayer barrier to encapsulate
the device of a product is shown in FIG. 4. The product 400
comprises a substrate 410, a device 401 having a device footprint
(which may comprise an active device area and an inactive device
area) disposed on the substrate 410, and a plurality of inorganic
layers 402 and polymer layers 403 disposed over the device 401. As
shown, the device 400 uses an inorganic layer mask (used in
depositing the inorganic layers 402) that is larger than the
polymer layer mask (used in depositing the polymer layers 403) such
that an inorganic layer 420 covers the side of the polymer layers
403. As shown in FIG. 4, even in this approach, the horizontal
ingress path (i.e. Path-1 shown by the arrow 404) is the easiest
path for water vapor to travel horizontally and reach the device
401 of the product 400. The barrier layer created by this method
for the horizontal ingress path (i.e. Path-1 (404)) for the
permeation of water vapor (or other permeants) for a 5-layer stack
design is equivalent to a bi-layer barrier consisting of a first
inorganic layer (typically 50 nm in thickness and disposed adjacent
to the footprint of device 401), a second polymer layer (typically
800 nm in thickness), and a third inorganic layer (typically 200 nm
in thickness labeled as 420 in FIG. 4). Therefore, as shown, the
resistance to horizontal permeation that this type of multilayer
barrier design provides is equivalent to a multilayer barrier
consisting of two inorganic layers and a polymer layer disposed
in-between (e.g. sandwiched between). Thus, while the vertical
ingress comprises five inorganic barrier layers 402 and four
polymeric layers 403, the horizontal ingress provides a much easier
permeation path that may determine the lifetime or degradation of
the device 401.
[0091] Yet another approach using a multilayer barrier design for a
product is shown in FIG. 5. The product 500 comprises a substrate
510, a device 501 having a device footprint (which may comprise an
active device area and an inactive device area) disposed over the
substrate 510, and a plurality of inorganic 502 and polymer 503
layers disposed over and along the sides of the footprint of device
501. The barrier layers are deposited using increasingly larger
sized masks for successive polymer 503 and inorganic layers 502. In
this approach the water vapor travelling horizontally along Path-1
(shown by the arrow labeled 504) in the edge region of the product
500 faces the entire multilayer stack in its path before reaching
the device 501 (unlike the products shown in FIGS. 3 and 4
described above). In this case, the edge seal provided by the
multilayer barrier comprising layers 502 and 503 to the water vapor
(or other permeant) travelling across the bulk of the barrier
horizontally along Path-1 (504) is equivalent to the seal provided
by the multilayer barrier to the water vapor travelling vertically
across the bulk of the barrier (i.e. along Path-3 shown by the
arrow 507).
[0092] However, even though the thickness of the polymer film per
unit stack in the horizontal direction (typically .about.1.0 mm
each as shown in FIG. 5) is much greater than that of the thickness
in the vertical direction (typically .about.0.8 .mu.m each), the
resistance to water vapor diffusion across the layers is quite
similar in both of the directions. The reason is that, as described
by G. L. Graff, Mechanisms of vapor permeation through multilayer
barrier films: Lag time versus equilibrium permeation, J. Appl.
Phys., 96 (4), pp. 1840-1849 (2004), the effective thickness to
calculate the length (l) in the lag time calculation (=.sup.2/(6D))
is determined by either the thickness of the polymer film or the
spacing of the defects in the inorganic film. In the vertical
direction (i.e. along Path-3 (507)), the defect spacing of the
inorganic film when assuming good permeation properties of the
barrier layers (e.g. on the order of couple hundred microns) is
much larger than the polymer film thickness. In the horizontal
direction (i.e. along Path-1 (504)) the opposite is the case--that
is, the defect spacing of the inorganic film is smaller than the
polymer film thickness. Therefore, it is reasonable to assume that
the edge ingress (e.g. Path-1 (504)) for the product 500 fabricated
using a progressively increasing mask size approach is comparable
to the vertical permeation (i.e. along Path-3 (507)) in the
multilayer barrier.
[0093] Although two ingress paths were described above--i.e.
horizontal Path-1 (504) and vertical Path-3 (507)--there is another
potential ingress path for permeants (Path-2 shown by the arrow
505). Path-2 (505) corresponds to water vapor permeation along the
interface of the inorganic film with the substrate 510. However,
even if the interface permeation along Path-2 (505) for the
inorganic film is worse than bulk permeation in the inorganic film,
the length of the ingress path is rather large across the interface
(e.g. approximately 5.0 mm as shown in FIG. 5), which is typically
a large enough distance to make it a secondary ingress path in
comparison to the ingress along Path-1 (504) (that is, permeants
are more likely to reach the device 501 through Path-1 (504) before
they reach the device 501 through Path-2 (505). One of the problems
associated with the edge encapsulation approach shown in FIG. 5 of
using progressively larger masks is the complexity associated with
using the plurality of mask changes during fabrication--that is,
each time a new mask is used during the fabrication process, it
requires that the mask be properly aligned (adding to the time and
expense of the process). In addition, the perpendicular length
(e.g. footprint) of the barrier comprising the multiple inorganic
502 and polymer 503 layers is large (i.e. approximately 5.0 mm
wider than that of the device 501 of the product 500 on each side).
This may thereby increase the non-active edge area of the product
around the footprint of device 501, which may, for instance,
correspond to the border area of the device (i.e. non-emitting
regions for an OLED), and also unnecessarily increases product size
to accommodate the multiple barrier layers. Thus, the inventors
have found that when attempting to reduce the edge ingress problem
with an inorganic-polymer multilayer barrier, a long diffusion
length may be needed so as to delay the water vapor (or other
permeant) permeating in the horizontal direction (e.g. along Path-1
(504) or Path 2 (505)) along the edge of the product 500.
[0094] The inventors have discovered a barrier film material that
comprises a mixture of a polymeric material and a non-polymeric
material that can be used as an edge sealant. It should be noted
that, in general, the barrier film comprising a mixture of a
polymeric material and a non-polymeric material when used as an
edge sealant can also be used in conjunction with a, for example,
single layer barrier (i.e. a single layer barrier film), multilayer
barrier (e.g. using multiple barrier layers comprising different
materials), or glass encapsulation and epoxy. This barrier film 606
functioning as an edge sealant may be deposited in any suitable
manner, including through the use of a single chamber PE-CVD
system.
[0095] A cross-section of the barrier film 606 that comprises a
mixture of a polymeric material and a non-polymeric on a product
600 is shown in FIG. 6. As described above, the two horizontal
ingress paths for water vapor permeation are shown (Path-1 (604),
which is the ingress along the bulk of the barrier film 606, and
Path-2 (605), which is the ingress along the interface of the
barrier film 606 with the substrate 610). As was described above,
the barrier film 606 providing an edge seal has a footprint (i.e. a
perpendicular length that extends from a side of the footprint of
device 601 to the edge of the barrier film 606 in a direction that
is perpendicular to the side of the footprint of device 601) that
can be varied based on the longevity requirements of the device.
The inventors have found that the perpendicular length (or
footprint) of the barrier film 606 can be made wider than the
footprint of device 601 of the product 600 by 3.0 mm or less
(preferably less than 2.0 mm and more preferable less than 1.0 mm),
while still providing adequate restriction on the ingress of
environmental particulates. It should be noted that the barrier
film 606 can be made wider than the footprint of device 601 by more
than 3.0 mm for extremely long shelf-life requirements or extremely
harsh testing/storage conditions. As noted above, the exemplary
barrier film that provides an edge seal may be deposited in a
single chamber system. Moreover, in some embodiments, barrier film
may form both the edge seal as well as the top encapsulation
barrier. This can reduce fabrication costs and complexity when
fabricating an electronic device. However, embodiments are not so
limited, and the barrier film 606 may be used in combination with
one or more encapsulation layers or components. Thus, the barrier
film 606 that forms an edge seal may act as a standalone component
of the overall encapsulation package, as described in more detail
with reference to FIGS. 11-14.
[0096] As was described above, with reference to FIG. 6, there are
two basic horizontal permeation paths (Path-1 and Path-2) across
the edge sealant film. With reference to FIG. 7, an exemplary
product 700 is shown that comprises a substrate 710, a device 701
having a device footprint (which may comprise an active device area
and an inactive device area) disposed over the substrate 710, a
barrier film 706 disposed along the sides and over the top of the
device 701. The ingress along Path-1 (704), which is the horizontal
bulk permeation, can be tested when the barrier film is used as
both an edge sealant and as the top encapsulation film, as is the
case with the exemplary product 700 in FIG. 7. In such a case,
Path-3 (707), which is also bulk permeation like Path-1 (704) but
in the vertical direction, has a much shorter diffusion path for
water vapor than Path-1 (704). The length for Path-3 (707) in this
example may be less than 10 .mu.m, whereas the length () for Path-1
(704) (which corresponds to the perpendicular length of the barrier
film) may be about 1000 .mu.m (i.e. 1.0 mm or more). If the barrier
film that is used as an edge sealant works well as a top
encapsulation layer, then any measurable contribution in edge
ingress from water vapor traveling via Path-1 (704) should be very
low for a long duration of time because of the magnitude of the
perpendicular length.
[0097] The inventors have tested an exemplary barrier film
comprising a mixture of a polymeric material and a non-polymeric
material when used as the top encapsulation layer and found that
OLEDs encapsulated with this exemplary barrier film operate at 100%
performance (i.e. with no degradation based on environmental
conditions) for more than 500 hrs of storage at 85.degree. C. and
85% RH. FIG. 8 shows the photographs of the active device area of a
2.0 mm.sup.2 bottom-emission OLED encapsulated with the 9.0 .mu.m
thick exemplary barrier film comprising a mixture of a polymeric
material and a non-polymeric material used as a top encapsulation
stored at 85.degree. C. and 85% relative humidity (RH). In
particular, FIG. 8 shows pictures taken at different operating
times (e.g. 0 hrs, 168 hrs, 240 hrs, 410 hrs, 460 hrs, and 530
hrs). As shown in FIG. 8, no dark spots developed in the device
even after 530 hrs in such relatively harsh atmospheric conditions.
Therefore, based on these results, it may be concluded that for the
exemplary barrier film that is being used as an edge sealant, any
permeation along Path-1 (704) corresponding to the bulk permeation
across the film does not cause device degradation for a relatively
long duration of storage (e.g. in excess of 530 hrs). It should be
noted that when there are particulates embedded in the barrier film
when used as both an edge sealant and a top encapsulation, dark
spots may be observed; however, the dark spots are the results of
permeation of water vapor across the particulates and not the
barrier film itself.
[0098] The inventors then tested the exemplary barrier film's edge
sealing ability by using different perpendicular lengths (i.e. edge
lengths or footprints, such as () shown in FIGS. 6 and 7) for
several devices and then measuring the lag time associated with
those perpendicular lengths in two separate experiments, the
results of which are shown in FIGS. 9(a) and (b). With reference to
the first experiment shown in FIG. 9(a), for each of the three test
devices, the barrier film comprising a mixture of a polymeric
material and a non-polymeric material was also used as the top
encapsulation, but the thickness in the vertical direction of the
film was kept the same for each device. FIG. 9(a) shows the
photographs of the active device area of three 1.0 cm.sup.2
bottom-emission OLEDs encapsulated by the exemplary barrier film
having top encapsulation layer thickness of 9.0 .mu.m and stored at
65.degree. C. and 85% RH. The perpendicular lengths () (measured
from a side of the device footprint of the device) of the barrier
film used to edge seal the devices shown in FIG. 9(a) are 1.0 mm,
2.0 mm, and 3.0 mm for each of the test devices, respectively (that
is, the photos in column 901 are of the active device area of an
exemplary OLED having a barrier film that has a perpendicular
length of 1.0 mm from a side of the device footprint; the photos of
column 902 of the active area of an exemplary OLED having a barrier
film that has a perpendicular length of 2.0 mm measured from a side
of the device footprint; and the photos in column 903 are of the
active area of an exemplary OLED having a barrier film that has a
perpendicular length of 3.0 mm measured from a side of the device
footprint). As was noted above, the perpendicular length in this
case corresponds to the distance between the side of the device
footprint (in this case, the side of an inactive device area that
was disposed adjacent to the active device area of the OLED) and
the edge of the barrier film (i.e. the footprint of the barrier
film layer). Therefore, although the distance that the barrier film
extends away from the device active area may be slightly larger
than the perpendicular length of the barrier film (i.e. by the
thickness of the inactive device area), once water vapor reaches
the organic layers or insulating layers that may comprise the
inactive device area, it would face no barrier in propagating
further into the active device area of the device.
[0099] The exemplary devices tested in FIG. 9(a) were larger area
devices relative to the device tested with reference to FIG. 8 and
therefore had more particulate contamination in the barrier films,
resulting in the development of more dark spots. However, as can be
seen in FIG. 9(a), the inventors did not find an appreciable
difference in the edge ingress performance of the three devices
(that is, after 648 hrs, there is approximately the same amount of
dark spots in each device). Moreover, the inventors found that,
even after a storage time of almost 1,000 hrs at 65.degree. C. and
85% RH, the three devices appeared similar. Thus, as noted above,
the degradation in each of the three devices could be attributed to
ingress based on the particulate contamination of the barrier film.
In view of the results shown in FIG. 9(a), a barrier film having a
3.0 mm perpendicular length or less (e.g. less than 2.0 mm, or less
than 1.0 mm) of this exemplary barrier film comprising a mixture of
polymeric material and a non-polymeric material can provide
adequate resistance to the ingress of environmental permeants for
at least 1,000 hrs or more at 65.degree. C. and 85% RH.
[0100] As was noted above, the horizontal bulk permeation across a
1.0 mm length of the exemplary barrier film comprising a mixture of
a polymeric material and a non-polymeric material would likely not
be possible in such a short duration of time. Therefore, the edge
degradation of these exemplary devices, which was generally held at
acceptable levels for approximately 1,000 hrs, is likely the result
of ingress at the interface (i.e. the ingress across the interface
between the barrier film and the substrate across Path-2 discussed
above). By further using the lag time calculation, the interface
diffusion coefficient for water vapor for this particular exemplary
barrier film comprising a mixture of a polymeric material and a
non-polymeric material (as used on test devices tested in FIG.
9(a)) was determined to be about 4.6.times.10.sup.-10 cm.sup.2/sec
at 65.degree. C. and 85% RH.
[0101] The inventors have further found that the interface
diffusion coefficient for products utilizing a barrier film
comprising a mixture of a polymeric material and a non-polymeric
material as an edge seal may be controlled in some instance by
applying one or more techniques. For example, one such technique
may be to change the nucleation density. The nucleation density is
the thin film growth technique that determines the thickness by
which the growing film becomes dense and coherent. In general,
before the film becomes dense it remains porous, and hence
permeable. The refractive index of the film prior to it becoming
completely dense and coherent will be lower than that of the bulk
film. L. S. Pan, D. R. Kania, Diamond: Electronic Properties and
Applications, Springer, pp. 104-107, (1995), which is incorporated
herein by reference in its entirety, describes that the nucleation
density is inversely proportional to the square of film thickness
by which a film becomes dense. That means that to form a coherent
and continuous film of thickness (d), the nucleation density
(N.sub.d).about.1/d.sup.2. Thus, for a nucleation density of
10.sup.10 cm.sup.-2, the film would become continuous when it
reaches 100 nm.
[0102] In another similar experiment, the results of which are
shown in FIG. 9(b), the inventors again tested the exemplary
barrier film's edge sealing ability by using three test devices
having barrier films with different perpendicular lengths (i.e.
edge lengths or footprints, such as () shown in FIGS. 6 and 7) and
then measuring the lag time associated with those perpendicular
lengths, but under harsher environmental conditions. For each of
the experimental devices, the barrier film comprising a mixture of
a polymeric material and a non-polymeric material was also used as
the top encapsulation, but the thickness in the vertical direction
of the film was kept the same for each device. The platform chosen
for the test was coupons containing 4.0 mm.sup.2 calcium (Ca)
buttons. FIG. 9(b) shows the photographs of the three 4.0 mm.sup.2
Ca buttons encapsulated by the exemplary barrier film having top
encapsulation layer thickness of 9.0 .mu.m and stored at 85.degree.
C. and 85% RH. The perpendicular lengths () (in this case, the
perpendicular distance from the side of the Ca (i.e. the active
device area because there was no inactive device area) to the edge
of the barrier film) of the barrier film used to edge seal the
buttons shown in FIG. 9(b) are 1.0 mm, 2.0 mm, and 3.0 mm for the
buttons shown in the top, middle, and bottom rows, respectively. As
noted above, these tests were even tougher than those described
with reference to FIG. 9(a), as the active device area (i.e. Ca
buttons) was 1.0, 2.0, and 3.0 mm away from the edge of the barrier
film. Once water vapor reaches the Ca button, it would start to
become transparent due to formation of hydroxide.
[0103] The exemplary devices tested in FIG. 9(b) were facing an
even more daunting challenge than those shown in FIG. 9(a). As
noted above, the perpendicular lengths were actually the distance
of the active device area (i.e. Ca) from the edge of the barrier,
and the devices were stored at 85.degree. C. and 85% RH. Even under
such harsh storage conditions, as can be seen in FIG. 9(b), the
inventors did not find an appreciable difference in the edge
ingress performance of the three devices (that is, after 432 hrs,
at 85.degree. C. and 85% RH the buttons look the same regardless of
the thickness of edge seal). In view of the results shown in FIG.
9(b), a barrier film having a 3.0 mm perpendicular length or less
(e.g. less than 2.0 mm, or less than 1.0 mm) of this exemplary
barrier film comprising a mixture of polymeric material and a
non-polymeric material can provide adequate resistance to the
ingress of environmental permeants for at least 400 hrs or more at
85.degree. C. and 85% RH.
[0104] In the exemplary devices described above, the barrier film
that was deposited used HMDSO as the deposition precursor gas and
oxygen as the non-deposition gas (i.e. a gas which will not deposit
any film when run through the plasma by itself) in a PE-CVD system.
However, as described in more detail below, other siloxanes or
silazanes (or onrganosilicons in general), for example, can be used
as precursors. The exemplary barrier film may be an intimate
mixture of oxide with a little residual silicone, which may be
unoxidized precursor. The refractive index for the exemplary
barrier film may be a measure of its composition and to some extent
density. A refractive index close to that of thermal SiO.sub.2
would mean the film is more oxide like with high density. Exemplary
deposition process and conditions and similar considerations are
known in the art based patent applications U.S. Prov. Ser. No.
61/086,047 and U.S. Pat. No. 7,968,146, which are each herein
incorporated by reference in their entireties. With increased
nucleation density, even a thinner film may become continuous.
Nucleation density can be controlled by various factors, such as
deposition power, pressure, substrate temperature, and gas flow
rates and ratio. Performing some surface treatment before the
actual film deposition may also affect the interface. For examples,
nitrogen plasma may leave some nitride bonds on the surface of a
substrate and then a growing thin film may bond better to those
bonds rather than with the substrate directly.
Composition and Fabrication of Exemplary Barrier Film
[0105] Provided below are exemplary compositions (and methods of
fabricating such compositions) of barrier film molecules and
materials that may be used as an edge sealant in some embodiments
as described above. In this regard, exemplary embodiments of
materials (and deposition processes) that may be used as an edge
sealant are described in detail in U.S. Pat. No. 7,968,146 entitled
"Hybrid Layers for Use in Coatings on Electronic Devices or Other
Articles," which is hereby incorporated by references in its
entirety for all purposes. The inventors have found that the
materials and methods described in U.S. Pat. No. 7,968,146, some of
which are provided below, may provide a barrier film that may be
preferred for use as an edge sealant for electronic devices.
However, embodiments are not necessarily limited to the molecules
and methods described therein.
[0106] In this regard, and as was noted above, in some embodiments,
the barrier film may comprise a hybrid layer comprising a mixture
of a polymeric material and a non-polymeric material. The hybrid
layer may have a single phase or multiple phases.
[0107] As used herein, the term "non-polymeric" may refer to a
material made of molecules having a well-defined chemical formula
with a single, well-defined molecular weight. A "nonpolymeric"
molecule may have a significantly large molecular weight. In some
circumstances, a non-polymeric molecule may include repeat units.
As used herein, the term "polymeric" may refer to a material made
of molecules that have repeating subunits that are covalently
linked, and that has a molecular weight that may vary from molecule
to molecule because the polymerizing reaction may result in
different numbers of repeat units for each molecule. Polymers may
include, but are not limited to, homopolymers and copolymers such
as block, graft, random, or alternating copolymers, as well as
blends and modifications thereof. Polymers include, but are not
limited to, polymers of carbon or silicon.
[0108] As used herein, a "mixture of a polymeric material and a
non-polymeric material" may refer to a composition that one of
ordinary skill in the art would understand to be neither purely
polymeric nor purely non-polymeric. The term "mixture" is intended
to exclude any polymeric materials that contain incidental amounts
of non-polymeric material (that may, for example, be present in the
interstices of polymeric materials as a matter of course), but one
of ordinary skill in the art would nevertheless consider to be
purely polymeric. Likewise, this is intended to exclude any
non-polymeric materials that contain incidental amounts of
polymeric material, but one of ordinary skill in the art would
nevertheless consider to be purely non-polymeric. In some cases,
the weight ratio of polymeric to non-polymeric material in the
hybrid layer is in the range of 95:5 to 5:95, and preferably in the
range of 90:10 to 10:90, and more preferably, in the range of 25:75
to 10:90.
[0109] The polymeric/non-polymeric composition of a layer may be
determined using various techniques, including wetting contact
angles of water droplets, IR absorption, hardness, and flexibility.
In certain instances, the hybrid layer has a wetting contact angle
in the range 30.degree. to 85.degree., and preferably, in the range
of 30.degree. to 60.degree., and more preferably, in the range of
36.degree. to 60.degree.. Note that the wetting contact angle is a
measure of composition if determined on the surface of an
as-deposited film. Because the wetting contact angle can vary
greatly by post-deposition treatments, measurements taken after
such treatments may not accurately reflect the layer's composition.
It is believed that these wetting contact angles are applicable to
a wide range of layers formed from organo-silicon precursors. In
certain instances, the hybrid layer has a nano-indentation hardness
in the range 3 to 20 GPa, and preferably, in the range of 10 to 18
GPa. In certain instances, the hybrid layer has a surface roughness
(root-mean-square) in the range of 0.1 nm to 10 nm, and preferably,
in the range of 0.2 nm to 0.35 nm. In certain instances, the hybrid
layer, when deposited as a 4 mm thick layer on a 50 mm thick
polyimide foil substrate, is sufficiently flexible that no
microstructural changes are observed after at least 55,000 rolling
cycles on a 1 inch diameter roll at a tensile strain (.epsilon.) of
0.2%. In certain instances, the hybrid layer is sufficiently
flexible that no cracks appear under a tensile strain (.epsilon.)
of at least 0.35% (typically a tensile strain level which would
normally crack a 4 mm pure silicon oxide layer, as considered by a
person of ordinary skill in the art).
[0110] It should be noted that the term "mixture" is intended to
include compositions having a single phase as well as compositions
having multiple phases. Therefore, a "mixture" excludes
subsequently deposited alternating polymeric and non-polymeric
layers. Put another way, to be considered a "mixture," a layer
should be deposited under the same reaction conditions and/or at
the same time.
[0111] The hybrid layer may be formed by chemical vapor deposition
using a single precursor material (e.g. from a single source or
multiple sources). As used herein, a "single source" of precursor
material may refer to a source that provides all the precursor
materials that are necessary to form both the polymeric and
non-polymeric materials when the precursor material is deposited by
CVD, with or without a reactant gas. This is intended to exclude
methods where the polymeric material is formed using one precursor
material, and the non-polymeric material is formed using a
different precursor material. As would be appreciated by one of
skill in the art, a "single source" of precursor material may
include one or more containers (e.g. crucibles) that may be used
during the process to heat or mix the chemicals that may form or
contain a single precursor material. For instance, a single
precursor material may be mixed or located in a plurality of
containers and then vapor deposited. In general, by using a single
precursor material, the deposition process may be simplified. For
example, a single precursor material will obviate the need for
separate streams of precursor materials and the attendant need to
supply and control the separate streams.
[0112] In general, the precursor material may be a single compound
or a mixture of compounds. Where the precursor material is a
mixture of compounds, in some cases, each of the different
compounds in the mixture is, by itself, able to independently serve
as a precursor material. For example, the precursor material may be
a mixture of hexamethyl disiloxane (HMDSO) and dimethyl siloxane
(DMSO). Other precursors may also be utilized such as
tetraethoxysilane (TEOS) or dimethyl siloxane (DMSO) or
octamethylcyclotetrasiloxane orhexamethyldisilazane or other
organosilanes or organosiloxanes and organosilazanes or their
mixtures.
[0113] In some cases, plasma-enhanced CVD (PE-CVD) may be used for
deposition of the hybrid layer. PE-CVD may be desirable for various
reasons, including low temperature deposition, uniform coating
formation, and controllable process parameters. Various PE-CVD
processes that are suitable for use in forming a hybrid layer that
may comprise a barrier layer for an edge sealant are known in the
art, including those that use RF energy to generate the plasma.
[0114] The precursor material may be a material that is capable of
forming both a polymeric material and a non-polymeric material when
deposited by chemical vapor deposition. Various such precursor
materials are suitable for use in providing a barrier film
comprising a hybrid layer and may be chosen for their various
characteristics. For example, a precursor material may be chosen
for its content of chemical elements, its stoichiometric ratios of
the chemical elements, and/or the polymeric and non-polymeric
materials that are formed under CVD. For instance, organo-silicon
compounds, such as siloxanes, are a class of compounds suitable for
use as the precursor material. Representative examples of siloxane
compounds include hexamethyl disiloxane (HMDSO) and dimethyl
siloxane (DMSO). When deposited by CVD, these siloxane compounds
are able to form polymeric materials, such as silicone polymers,
and non-polymeric materials, such as silicon oxide. The precursor
material may also be chosen for various other characteristics such
as cost, non-toxicity, handling characteristics, ability to
maintain liquid phase at room temperature, volatility, molecular
weight, etc.
[0115] Other organo-silicon compounds suitable for use as a
precursor material include methylsilane; dimethylsilane; vinyl
trimethylsilane; trimethylsilane; tetramethylsilane; ethylsilane;
disilanomethane; bis(methylsilano)methane; 1,2-disilanoethane;
1,2-bis(methylsilano)ethane; 2,2-disilanopropane;
1,3,5-trisilano-2,4,6-trimethylene, and fluorinated derivatives of
these compounds. Phenyl-containing organo-silicon compounds
suitable for use as a precursor material include:
dimethylphenylsilane and diphenylmethylsilane. Oxygen containing
organo-silicon compounds suitable for use as a precursor material
include: dimethyldimethoxysilane;
1,3,5,7-tetramethylcyclotetrasiloxane; 1,3-dimethyldisiloxane;
1,1,3,3-tetramethyldisiloxane; 1,3-bis(silanomethylene)disiloxane;
bis(1-methyldisiloxanyl)methane; 2,2-bis(1-methyldisiloxanyl)
propane; 2,4,6,8-tetramethylcyclotetrasiloxane;
octamethylcyclotetrasiloxane;
2,4,6,8,10-pentamethylcyclopentasiloxane;
1,3,5,7-tetrasilano-2,6-dioxy-4,8-dimethylene;
hexamethylcyclotrisiloxane;
1,3,5,7,9-pentamethylcyclopentasiloxane; hexamethoxydisiloxane, and
fluorinated derivatives of these compounds. Nitrogen-containing
organosilicon compounds suitable for use as a precursor material
include: hexamethyldisilazane; divinyltetramethyldisilizane;
hexamethylcyclotrisilazane; dimethylbis(N-methylacetamido) silane;
dimethylbis-(N-ethylacetamido)silane;
methylvinylbis(N-methylacetamido)silane;
methylvinylbis(Nbutylacetamido) silane;
methyltris(N-phenylacetamido) silane;
vinyltris(N-ethylacetamido)silane; tetrakis(Nmethylacetamido)
silane; diphenylbis(diethylaminoxy) silane;
methyltris(diethylaminoxy)silane; and bis
(trimethylsilyl)carbodiimide.
[0116] When deposited by CVD, the precursor material may form
various types of polymeric materials in various amounts, depending
upon the type of precursor material, the presence of any reactant
gases, and other reaction conditions. The polymeric material may be
inorganic or organic. For example, where organo-silicon compounds
are used as the precursor material, the deposited hybrid layer may
include polymer chains of Si--O bonds, Si--C bonds, or Si--O--C
bonds to form polysiloxanes, polycarbosilanes, and polysilanes, as
well as organic polymers.
[0117] When deposited by CVD, the precursor material may form
various types of non-polymeric materials in various amounts,
depending upon the type of precursor material, the presence of any
reactant gases, and other reaction conditions. The non-polymeric
material may be inorganic or organic. For example, where
organo-silicon compounds are used as the precursor material in
combination with an oxygen-containing reactant gas, the
non-polymeric material may include silicon oxides, such as SiO,
Si0.sub.2, and mixed-valence oxides SiO.sub.x. When deposited with
a nitrogen-containing reactant gas, the non-polymeric material may
include silicon nitrides (SiN.sub.x). Other non-polymeric materials
that may be formed in some instances include silicon oxycarbide and
silicon oxynitrides.
[0118] When using PE-CVD, the precursor material may be used in
conjunction with a reactant gas that reacts with the precursor
material in the PE-CVD process. The use of reactant gases in PE-CVD
is known in the art and various reactant gases are suitable for use
in the present invention, including oxygen containing gases (e.g.,
0.sub.2, ozone, water) and nitrogen-containing gases (e.g.,
ammonia). The reactant gas may be used to vary the stoichiometric
ratios of the chemical elements present in the reaction mixture.
For example, when a siloxane precursor material is used with an
oxygen or nitrogen-containing reactant gas, the reactant gas will
change the stoichiometric ratios of oxygen or nitrogen in relation
to silicon and carbon in the reaction mixture. This stoichiometric
relation between the various chemical elements (e.g., silicon,
carbon, oxygen, nitrogen) in the reaction mixture may be varied in
several ways. One way is to vary the concentration of the precursor
material or the reactant gas in the reaction. Another way is to
vary the flow rates of the precursor material or the reactant gas
into the reaction. Another way is to vary the type of precursor
material or reactant gas used in the reaction.
[0119] Changing the stoichiometric ratios of the elements in the
reaction mixture can affect the properties and relative amounts of
the polymeric and non-polymeric materials in the deposited hybrid
layer. For example, a siloxane gas may be combined with varying
amounts of oxygen to adjust the amount of non-polymeric material
relative to the polymeric material in the hybrid layer. By
increasing the stoichiometric ratio of oxygen in relation to the
silicon or carbon, the amount of non-polymeric material, such as
silicon oxides, may be increased. Similarly, by reducing the
stoichiometric ratio of oxygen, the amount of silicon and
carbon-containing polymeric material may be increased. The
composition of the hybrid layer may also be varied by adjusting
other reaction conditions. For example, in the case of PE-CVD,
process parameters such as RF power and frequency, deposition
pressure, deposition time, and gas flow rates can be varied.
[0120] Thus, by using the exemplary methods as described above, it
is possible to form a hybrid layer of hybrid
polymeric/non-polymeric character and having characteristics
suitable for use in various applications, particular as a barrier
film to reduce edge ingress of permeates. Such characteristics of
the barrier film may include optical transparency (e.g., in some
cases, the hybrid layer may be optically transparent or
semi-transparent), impermeability, flexibility, thickness,
adhesion, and other mechanical properties. For example, one or more
of these characteristics may be adjusted by varying the weight % of
polymeric material in the hybrid layer, with the remainder being
non-polymeric material. For instance, to achieve a desired level of
flexibility and impermeability, the wt % of polymeric material may
preferably be in the range of 5 to 95%, and more preferably in the
range of 10 to 25%. However, other ranges are also possible
depending upon the application.
Exemplary Embodiments
[0121] Described below are exemplary embodiments of products that
comprise a barrier film comprising a mixture of a polymeric
material and a non-polymeric material as an edge sealant. The
embodiments described herein are for illustration purposes only and
are not thereby intended to be limiting. After reading this
disclosure, it may be apparent to a person of ordinary skill in the
art that various components and/or features as described below may
be combined or omitted in certain embodiments, while still
practicing the principles described herein.
[0122] In some embodiments, a first product is provided. The first
product may include a substrate, a device having a device footprint
disposed over the substrate, and a barrier film disposed over the
substrate and substantially along a side of the active area. The
barrier film may comprise a mixture of a polymeric material and
non-polymeric material. The barrier film may have a perpendicular
length that is less than or equal to 3 mm from the side of the
device footprint.
[0123] As described above, the "perpendicular length" of the
barrier film may refer to the distance from a portion of the
barrier film that is disposed closest to the footprint of the
device (e.g. adjacent to the active device area or inactive device
area) to another portion of the barrier film that is disposed
farthest away from the device footprint (e.g. the edge of the
barrier film) in a direction that is perpendicular to the side of
the device footprint and parallel to the surface of the substrate
that the barrier film is disposed over.
[0124] As used in this context, "substantially along a side" of the
device footprint does not necessarily require that the barrier film
be disposed directly adjacent to the device footprint. Moreover,
this does not preclude the barrier film from being disposed in
other locations relative to the device, including embodiments where
a portion of the barrier film may be disposed over one or more
layers (such as a cathode, electron transport layer, hole transport
layer, etc. of an OLED) of the device.
[0125] The use of the term "a perpendicular length" in the phrase
"a barrier film may have a perpendicular length" is generally meant
to cover embodiments where one portion of the barrier film may be
deposited or otherwise fabricated so as to have a perpendicular
length that is greater than 3.0 mm, so long as the edge of any
portion of the barrier film is disposed so as at have a
perpendicular distance that is less than 3.0 mm from a side of the
footprint of the device. As was described above, the lifetime and
performance of a device based on the ingress of contamination by
outside particulates typically depends on the shortest or lease
resistive path of ingress into the sensitive components of a
device. The barrier film provided herein may be utilized such that
the shortest part of horizontal ingress may be less than 3.0 mm
(preferably less than 2.0 mm, and more preferably less than 1.0
mm).
[0126] In general, products that reduce the size of the barrier
film that forms the edge seal (i.e. that reduce the perpendicular
length) may provide for a reduction in the amount of border area
(e.g. "dead space") of the device. Moreover, through the use of
exemplary barrier film materials, embodiments provided herein may
reduce the size of the non-active edge area without substantially
affecting device performance or degradation. The exemplary barrier
film may restrict both horizontal bulk permeation and permeation
across the interface between the barrier film and the substrate.
Reducing the non-active edge area of a device created by an edge
seal may provide additional space for other electronic components
of the device, larger displays, a reduction in the border area
between emitting devices (which may make such areas less noticeable
when, for instance, multiple displays or panels are tiled), or
otherwise increase the efficiency of manufacturing or layout of
such devices. Moreover, embodiments that utilize a single barrier
film layer (e.g. that may be deposited in a single deposition step)
to encapsulate the device may provide a more efficient and less
time consuming fabrication process in comparison to products that
utilize multilayer barriers (such as those described above with
reference to FIGS. 3-5). However, embodiments are not so limited,
and some products that have a barrier film that comprises a mixture
of a polymeric material and non-polymeric material may also utilize
multiple barrier or encapsulation layers (such as FIGS. 11-14).
[0127] In some embodiments, in the first product as described
above, the device footprint may comprise an active device area and
an inactive device area. In some embodiments, the barrier film may
have a perpendicular length that is less than or equal to 3.0 mm
from the side of the inactive device area. That is, the barrier
film may be disposed so as to be adjacent to a side of the inactive
device area and extend in a direction perpendicular to the side of
the inactive area (and thereby the side of the device footprint of
the device) by less than 3.0 mm (preferably less than 2.0 mm, and
more preferably less than 1.0 mm). In some embodiments, the barrier
film may not extend to a distance of greater than 3.0 mm from a
side of the active device area. That is, in some instances, the
barrier film may not be disposed adjacent to the side of the active
device area (e.g. because the active device area may be surrounded
by inactive device area) and thereby the perpendicular length of
the barrier film may not correspond to the distance that the edge
of the barrier film is disposed away from the side of the active
device area. In some such embodiments, the total distance of the
perpendicular length of the barrier film and the thickness of the
inactive device area may be less than 3.0 mm from a side of the
active area (preferably less than 2.0 mm; and more preferably less
than 1.0 mm). In this manner, the border area of the device may be
less than 3.0 mm (preferably less than 2.0 mm and more preferably
less than 1.0 mm).
[0128] In some embodiments, in the first product as described
above, the device footprint may comprise an active device area, and
the barrier film may have a perpendicular length that is less than
or equal to 3.0 mm from the side of the active device area
(preferably less than 2.0 mm and more preferably less than 1.0 mm).
That is, in some embodiments, the device may not comprise an
inactive device area (or at least a portion of the device may not
comprise an inactive device area), and thereby the barrier film may
extend from the side of the active device area.
[0129] Examples of these concepts are illustrated in FIGS. 15-17.
With reference to FIG. 15, a top view of an exemplary product 1500
comprising an OLED is shown. The product 1500 comprises a device
having a device footprint 1501 disposed over the substrate 1510.
The device footprint 1501 comprises an active device area 1550 and
an inactive device area 1551. The product 1500 further comprises a
cathode 1543 that is disposed partially within the device footprint
1501, but that also includes a cathode contact 1544 that extends
away from the device footprint 1501 (to the right in FIG. 15), and
an anode 1540 that is disposed partially within the device
footprint 1501, but that has an anode contact 1541 that extends
away from the device footprint 1501 (to the left in FIG. 15). The
anode contact 1541 and the cathode contact 1544 may form one or
more electrical contacts with electrical components (such as power
source, drive circuitry, etc.) and can extend beyond the edge of
the barrier film 1506 or be encapsulated by the barrier film
1506.
[0130] The device further comprises organic layers 1545 that are
partially disposed within the active device area 1550 and the
inactive device area 1551 of the device. The device further
comprises a grid layer 1546 (which could comprise organic or
inorganic material) that is shown as comprising a part of the
inactive device area 1551, and a barrier film 1506 that is shown as
comprising the non-device edge area 1553, as well as being disposed
over the device and portions of the anode contact 1541 and cathode
contact 1544. The non-device edge area 1553 and the inactive device
area 1551 are shown as comprising the border (dead space) area
1552.
[0131] With reference to FIG. 16, the cross-section along the line
A-A' of the exemplary product 1500 in FIG. 15 is shown. The product
1600 comprises a device disposed over the substrate 1610 having a
device footprint 1601. The device footprint 1601 comprises an
active device area 1650 and an inactive device area 1651. The
product 1600 further comprises a cathode 1643 that is disposed
partially within the device footprint 1601, but that also includes
a cathode contact 1644 that extends away from the device footprint
1601 (to the right in FIG. 16), and an anode 1640 that is disposed
partially within the device footprint 1601, but that has an anode
contact 1641 that extends away from the device footprint 1601 (to
the left in FIG. 16). The device further comprises organic layers
1645 that are partially disposed within the active device area 1650
and inactive device area 1651, a grid layer 1646 (which could
comprise organic or inorganic material) that is shown as comprising
a part of the inactive device area 1651, and a barrier film 1606
that is shown as comprising the non-device edge area 1653, as well
as being disposed over the device and portions of the anode contact
1641 and cathode contact 1644. The non-device edge area 1653 and
the inactive device area 1651 are shown as comprising the border
(dead space) area 1652. Thus, in this example, the grid layer 1646
is shown as being disposed over anode contact 1641 (on the left
side of the device) and over a portion of the anode 1644 and
adjacent to substrate 1610 on the right side of the device. In this
manner, the inactive device area 1651 may comprise two electrodes
and the organic layer(s), this portion of the device may not emit
light (e.g. for an OLED) and thereby does not comprise a part of
the active device area 1650.
[0132] As shown in FIG. 16, in some embodiments, the barrier film
1603 may be disposed adjacent to the inactive device area 1651
(e.g. grid layer 1646 on the left side of the device in FIG. 16).
Thus, the perpendicular length of the barrier film 1606 may
correspond to the distance the barrier film 1606 extends away from
the inactive device area 1651. On the opposite side of the device,
the cathode contact 1644 extends beyond the grid layer 1646 (such
that the grid layer 1646 insulates the anode 1640 and the cathode
contact 1644). The barrier film 1606 is shown as being disposed
adjacent to the cathode contact 1644 and extends away from the
device footprint 1601. Thus, in this example, although the barrier
film 1606 is disposed along a side of the device footprint 1601
(e.g. along the side of the inactive device area 1651) it is not
disposed adjacent to the inactive device area 1651. As noted
above,
[0133] With reference to FIG. 17, a cross-sectional view along the
line B-B' of the exemplary product 1500 shown in FIG. 15 is shown.
The product 1700 comprises a device disposed over the substrate
1710 having a device footprint 1701. The device footprint 1701
comprises an active device area 1750 and an inactive device area
1751. The product 1700 further comprises a cathode 1743 that is
disposed entirely within the device footprint 1701 (unlike FIG. 16)
and an anode 1740 that is disposed entirely within the device
footprint 1701 (again unlike FIG. 16). That is, the cathode and
anode may, but need not, have contacts that extend beyond the
device footprint 1701 in more than one direction. The device
comprises organic layers 1745 that are partially disposed within
the active device area 1750 and inactive device area 1751, a grid
layer 1746 (which could comprise organic or inorganic materials)
that is shown as comprising a part of the inactive device area
1751, and a barrier film 1706 that is shown as comprising the
non-device edge area 1753, as well as being disposed over the
device. In this example, the barrier film 1706 is shown as being
disposed along a side of the inactive area 1751 of the device
footprint 1701 on both sides of the device.
[0134] It should be noted that some of the additional detail and
components shown in FIG. 1507 were omitted from the FIGS. 4-7 and
10-14 for illustration purposes only. That is, the embodiments
shown in ach of those figures could comprise some or all of the
additional layers or materials shown and described in more detail
with reference to FIGS. 15-17. However, these embodiments were
described and shown at a high-level to demonstrate basic design and
implementation concepts, and should thereby not be considered
limiting.
[0135] In some embodiments, in the first product as described
above, the barrier film may comprise a mixture of a polymeric
silicon and inorganic silicon. The "mixture of polymeric silicon
and inorganic silicon" was described above in detail, particular
with reference to U.S. Pat. No. 7,968,146. The inventors have found
that such a mixture may provide a barrier film that may be capable
of restricting ingress of moisture or water vapor (or other
environmental contaminants) while maintaining relatively small
dimensions for the film. In the case of an edge sealant, the
inventors have discovered that such materials may provide adequate
performance while having a perpendicular length of less than 3.0 mm
(preferably less than 2.0 mm; and more preferably less than 1.0 mm)
from the side of the device footprint. Previously, edge seals often
comprised multiple layers to achieve adequate performance, which is
typically inefficient both to manufacture such devices and also
creates relatively large non-active edge areas (and thereby border
areas) on a product.
[0136] In some embodiments, the mixture of polymeric silicon and
inorganic silicon may be substantially uniform across the layer. By
"substantially," it is generally meant that the film comprises a
mixture that does not vary by more than 5% across the layer. As
noted above, the barrier film may be deposited in a single process,
which may increase manufacturing efficiency. The 5% variance may
account for minor fluctuations across the product that may occur
during the manufacturing processes. For products that comprise a
light emitting device (such as a lighting panel or display), a
uniform layer may be preferred because it may reduce micro-cavity
effects or other effects associated with multiple layers having
different optical properties. However, embodiments are not so
limited, and in some instances, the barrier film may vary across
the layer (such as a graded layer), which could, for instance,
increase the resistance to ingress across the bulk of the barrier
layer.
[0137] In some embodiments, in the first product as described
above, the barrier film may have a perpendicular length that is
less than or equal to 2.0 mm. In some embodiments, the barrier film
may have a perpendicular length that is less than or equal to 1.0
mm. As was described above, the barrier film comprising a mixture
of a polymeric material and a non-polymeric material when utilized
as an edge seal may reduce the size of the non-active edge area of
the product in at least one direction, while still providing for
adequate lifetime and performance of the device. In particular, the
inventors have found that using the barrier film comprising a
mixture of a polymeric material and non-polymeric material provides
good performance when having a perpendicular length of less than
2.0 mm (and may even have similar performance at less than 1.0 mm).
This is a substantial improvement over the distances typically
required by multilayer products that were previously used, such as
those shown in FIGS. 3-5.
[0138] In some embodiments, in the first product as described
above, the barrier film may not have a perpendicular length that is
greater than 3.0 mm. That is, some embodiments may not have a
portion of the barrier film that is deposited or disposed at a
location on the substrate so as to have a perpendicular distance
that is greater than 3.0 mm from the side of the device footprint.
For example, the barrier film comprising a mixture of a polymeric
material and a non-polymeric material may be deposited around all
of the sides of the device footprint at a distance of less than 3.0
mm. This may provide products that have a minimum amount of
non-active edge area over the substrate, thereby allowing, for
example, a display or lighting panel to extend closer to the edge
of the product. Moreover, the inventors have unexpectedly found
that such barrier films used as edge sealants have comparable
performance when the barrier film may not have a perpendicular
length that is greater than 2.0 mm (and preferably when the barrier
film does not have a perpendicular length that is greater than 1
mm) from the side of the device footprint. Despite the reduction in
the length of ingress path for such embodiments, as described with
reference to FIGS. 9(a) and (b) and the corresponding experiments,
the inventors have found an equal amount of contamination in
comparable devices over an extended period of time in hostile
environmental conditions. Thus, the inventors have discovered that
the use of the barrier film comprising a mixture of a polymeric
material and a non-polymeric material as an edge seal may be
effective with perpendicular distances less than 3.0 mm (and even
less than 2.0 mm or 1.0 mm).
[0139] In some embodiments, in the first product as described
above, the barrier film may not have a perpendicular length that is
greater than 3.0 mm or less than 1.0 mm. In some embodiments, the
barrier film may not have a perpendicular length that is greater
than 2.0 mm or less than 0.5 mm. That is, some embodiments of
products may have an edge sealant having a range of perpendicular
lengths around the device footprint, but in general it may be
preferred that the range be great enough to provide adequate
performance for the device, but sill have small enough dimensions
so as to reduce the non-active edge area of the product.
[0140] In some embodiments, in the first product as described
above, the barrier film may comprise a substantially uniform
material. As used in this context, "uniform" may refer to when the
material of the barrier layer comprises the same materials or
concentration of materials across the layer. That is, "uniform"
does not require that the film necessarily comprise only a single
material, but could comprise a layer that has the same, or
substantially the same, mixture across the layer. The use of the
term "substantially" in this context is to account for minor
variations that may occur based on manufacturing error or
imperfections, but generally refers to uniformity that does not
vary by more than 5% across the film. In some embodiments, the
barrier film may comprise a uniform material--that is, there may be
less than 1% variation across the film. The use of uniform (or
substantially uniform) barrier films as edge sealants may be the
result of using a single deposition process for depositing the
film, which may reduce the costs of the fabrication process by
reducing the number of fabrication steps/conditions.
[0141] In some embodiments, in the first product as described
above, the barrier film may comprise a mixture of an oxide and
polymeric silicone. In some embodiments, the barrier film may
comprise at least 40% inorganic silicon. The inventors have found
that the use of organic silicon and polymeric silicon may provide
properties that are well-suited for forming an edge seal to prevent
the ingress of contaminants in the device. It should be noted that
the use of the term "at least" in this context does not require
that the mixture or composition of the film be uniform--so long as
there are no portions of the layer that comprise less than 40%
inorganic silicon. In some embodiments, the barrier film may
comprise at least 60% inorganic silicon. In some embodiments, the
barrier film may comprise at least 80% inorganic silicon. As was
noted above, the mixture concentrations and materials may be
fine-tuned or selected to have desired characteristics so that the
edge seal may be determined based on the particular application and
environmental conditions expected for the device, as would be
understood by one of ordinary skill in the art after reading this
disclosure.
[0142] In this regard, in some embodiments, in the first product as
described above, a surface of the barrier film may be disposed
adjacent to a surface of the substrate to form a first interface.
The ratio of the index of refraction of the bulk of the barrier
film and the index of refraction of a portion of the barrier film
that is within 10 nm of the interface may be between 0.9993 and
0.9247. The "index of refraction of the bulk" of the barrier film
may refer to the index of refraction across the barrier film layer
(i.e. index of refraction across the film in a direction
corresponding to a path that light that is perpendicularly incident
on the film propagates through the layer). In general, the
inventors have found that for products that may comprise a light
emitting active area (such as an OLED) or any other transparent or
semi-transparent device, it may be beneficial to deposit a barrier
film such that the index of refraction of the film is similar to
the substrate (particularly near the interface with the substrate).
This may reduce the amount of light that may be trapped between the
barrier film and the substrate and thereby increase the efficiency
of the device. Moreover, less light may be color shifted or
otherwise distorted when passing through the edge seal and then the
substrate.
[0143] In some embodiments, in the first product as described
above, where a surface of the barrier film is disposed adjacent to
a surface of the substrate to form a first interface, the index of
refraction of a portion of the barrier film that is within 10 nm of
the interface may be between 1.35 and 1.459. In many embodiments,
the substrate material may be transparent or semi-transparent such
as a glass or plastic material and will typically have an index of
refraction between 1.35 and 1.459. As was noted above, it is
generally preferred (at least for devices comprising an emissive
active area) that the index of refraction of the barrier film and
the substrate are similar.
[0144] In some embodiments, in the first product as described
above, where a surface of the barrier film is disposed adjacent to
a surface of the substrate to form a first interface, the barrier
film may comprise a material having a bulk diffusion coefficient of
water vapor of less than 10.sup.-13 cm.sup.2/sec. The bulk
diffusion coefficient of the barrier film may refer to the rate of
ingress of water vapor in the horizontal direction across the film
(e.g. along Path-1 (704) in FIG. 7) or in the vertical direction
(e.g. along Path-3 (707) in FIG. 7). The inventors have found that
a bulk diffusion coefficient of less than 10.sup.-13 cm.sup.2/sec
is generally sufficient to provide adequate device lifetime and
performance, even in hostile environments as described above. In
some embodiments, the diffusion coefficient of water vapor at the
first interface may be between 10.sup.-8 cm.sup.2/sec and
10.sup.-13 cm.sup.2/sec when exposed to an ambient temperate of
65.degree. C. and relative humidity of 85%. The diffusion
coefficient at the interface corresponds to the ingress of moisture
across the interface between the film and the substrate (e.g. along
Path-2 (705) in FIG. 7), which may be the limiting factor in some
embodiments for device lifetime or performance based on
environmental contaminants. As was noted above, the inventors have
found that a barrier film that comprises a mixture of a polymeric
material and non-polymeric material may provide a sufficient
diffusion coefficient at the interface for adequate device
performance, even when the ingress path is less than 3.0 mm
(preferably less than 2.0 mm; and more preferably less than 1.0
mm). As a person of ordinary skill in the art would understand, the
properties of the edge seal (including the diffusion coefficient)
may be tuned by adjusting the deposition conditions (including the
precursor material) as was described above, to achieve a desired
set of properties for the barrier film for a particular device or
application.
[0145] In some embodiments, in the first product as described
above, where a surface of the barrier film is disposed adjacent to
a surface of the substrate to form a first interface, the barrier
film may comprise a material having a bulk diffusion coefficient of
water vapor. The ratio of the bulk diffusion coefficient of water
vapor of the barrier film and a diffusion coefficient of water
vapor near the first interface may be between 1 and 10.sup.-5. That
is, for instance, the bulk diffusion coefficient for the barrier
film (e.g. the ingress rate along Path-1 (704) in FIG. 7) may be
equal to or less than the diffusion coefficient at or near the
interface with the substrate (e.g. the ingress rate along Path-2
(705) in FIG. 7). As was noted above, in some embodiments, the
ingress of water vapor along the interface may be the limiting
factor in determining the lifetime or degradation of the device.
The inventors have found that by tuning the properties of the
barrier film, it is possible to adjust both the diffusion
coefficient of the bulk material, as well as the diffusion
coefficient along the interface with the substrate. In some
embodiments, the ratio of the bulk diffusion coefficient of water
vapor of the barrier film and a diffusion coefficient of water
vapor within 10 nm of the first interface is between 1 and
10.sup.-5.
[0146] In some embodiments, in the first product as described
above, the first product may further comprise a conductive layer
disposed over the device (such as a layer of the device--e.g. an
electrode). In some embodiments, a portion of the barrier film may
be disposed at least partially over the conductive layer. In some
embodiments, a portion of the barrier film may be disposed over the
entire conductive layer. That is, for instance and as shown in
FIGS. 7 and 15-17, in some embodiments, the barrier film may be
used both as an edge seal and as an encapsulation layer over the
entire device. This may reduce the cost and complexity of the
fabrication process, as the barrier film could be deposited in a
single step using a mask that is larger than the mask used for
depositing the device footprint. Moreover, as noted above, the
barrier film comprising a mixture of a polymeric material and
non-polymeric material may have a low ingress rate based on the
bulk diffusion coefficient and may thereby be utilized as an
encapsulation layer for the device.
[0147] However, embodiments are not so limited, and in some
instances, in the first product as described above where the device
comprises a conductive layer disposed over one or more device
layers, a top sealant layer may be disposed over the conductive
layer. The top sealant layer and the barrier film may comprise
different materials. Thus, the barrier film comprising a mixture of
a polymeric material and non-polymeric material may be used in
conjunction with other materials to encapsulate the device of the
product. Examples of such embodiments are shown in FIGS. 11-14 and
described in detail below.
[0148] In some embodiments, in the first product as described
above, the first product may comprise a border area. The border
area may have a thickness that is less than 3.0 mm (preferably less
than 2.0 mm; and more preferably less than 1.0 mm) and may depend
at least in part on the size of the barrier film and the size of
the inactive device area. As was noted above, embodiments described
herein that utilize a barrier film comprising a mixture of a
polymeric material and non-polymeric material may have an effective
edge seal against the ingress of environmental contaminants such
that the size of the edge seal may be reduced. This may thereby
allow for products to have smaller non-device edge areas around the
active device area and inactive device areas of the device (thereby
decreasing the size of the border area). Thus, as noted above, in
some embodiments, in the first product as described above, where
the first product comprises a non-device edge area, the non-device
edge area may have a thickness that is less than 3.0 mm. In some
embodiments, the non-active edge area may have a thickness that is
less than 2.0 mm (preferably less than 1.0 mm).
[0149] In some embodiments, the first product as described above
may comprise a consumer device. In some embodiments, the first
product may comprise anyone of: a solar cell, a thin film battery,
an organic electronic device, a lighting panel or a lighting source
having a lighting panel, a display or an electronic device having a
display, a mobile phone, a notebook computer, a tablet computer, or
a television. In general, any product that uses a thin film to
encapsulate or protect sensitive components may use the barrier
film described herein comprising a mixture of polymeric material
and non-polymeric material as an edge seal.
[0150] In some embodiments, in the first product as described
above, the device may comprise an organic layer. In some
embodiments, the organic layer may comprise an electro-luminescent
material. In some embodiments, the device may comprise an OLED.
However, as noted above, while the inventors have found that the
barrier film may perform particularly well as an edge sealant for
an organic device (and thereby some of the examples and
descriptions provided herein may reference OLEDs), embodiments are
not so limited.
[0151] As was noted above, the barrier film that may be used as an
edge sealant film may also be used in some embodiments as a top
encapsulation film as shown in the exemplary embodiment in FIG. 10
or in conjunction with other top encapsulations as shown in FIGS.
11-14.
[0152] FIG. 10 shows an exemplary product 1000 that uses the
barrier film as an edge seal and as a top sealant. The product 1000
comprises a substrate 1010, a device 1001 having a device footprint
disposed over the substrate 1010, and a barrier film 1006 disposed
along the sides of the device footprint and over the top of the
device 1001. The barrier film 1006 is shown as having a
perpendicular length of 1.0 mm. The two ingress paths (Path-1
(1004) and Path-2 (1005)) are shown. As noted above, such
embodiments may provide for increased efficiency in the
manufacturing process, as both the top encapsulation and the edge
sealant comprise the same material (i.e. barrier film 1006).
[0153] As shown in FIG. 11, the edge sealant film 1106 can be used
in conjunction with a single layer top encapsulation film. In this
regard, the exemplary product 1100 comprises substrate 1110, a
device 1101 disposed over the substrate 1110 having a device
footprint, a barrier film 1106 disposed along the sides of the
device footprint of device 1101, and a second barrier layer (or top
encapsulation layer) 1108 disposed over the device footprint 1101.
As noted above, utilizing the barrier film comprising a mixture of
a polymeric material and non-polymeric material may enable the
footprint of the single layer barrier film 1106 to be kept very
close to that of the footprint of device 1101 (i.e. the
perpendicular length of the barrier film 1106 extending away from
the side of the footprint of device 1101 may be kept relatively
small). In some embodiments, after the top encapsulation layer 1108
is formed or deposited, the barrier film 1106 that forms the edge
seal may be deposited. The barrier film 1106 can be deposited just
along the sides of the footprint of device 1101 as shown in FIG. 11
or it can also cover the top encapsulation layer 1108 depending on
the needs of the device and the manufacturing requirements (that
is, it may be more efficient and less expensive to deposit the
barrier film 1106 as a blanket layer over the entire substrate
1110, rather than having to selectively deposit the barrier film
1106 only along the sides of the footprint of device 1101). In
either embodiment, the use of the barrier film 1106 as the edge
sealant may reduce the overall footprint of the encapsulation (i.e.
the top encapsulation barrier 1108 and the edge sealant 1106). As
shown in FIG. 11, in some embodiments, the perpendicular length of
the barrier film 1106 may be equal to or less than 1.0 mm (i.e. the
footprint of the barrier film 1106 may be less than 1.0 mm wider
than the footprint of device 1101 on one or more sides). Similar to
FIG. 11, the same principle is shown in FIG. 12 where the barrier
film 1206 is used as the edge sealant for the device 1201 disposed
over the substrate 1210 in conjunction with a multilayer barrier
film (comprising inorganic 1202 and polymer 1203 layers) used as
the top encapsulation. In this example, the barrier film 1206 is
shown as having a perpendicular length of 1.0 mm.
[0154] As shown in FIG. 13, the barrier film may also be used along
with glass encapsulation. In this regard, FIG. 13 shows an
exemplary product 1300 comprising a substrate 1310, a device 1301
disposed over the substrate 1310 having a device footprint, a
barrier film 1306 disposed along the sides of the footprint of the
device 1301, and a top encapsulation comprising a glass layer 1311
and an epoxy 1312 (e.g. to couple the glass layer 1311 to the
substrate 1310) disposed over the device 1301. In general, glass
encapsulation typically suffers from the problem of edge ingress
when the epoxy 1312 is used as the edge seals. If the epoxy 1312
can be deposited directly over the device 1301, the glass
encapsulation 1311 may then be restricted to being disposed over
the device 1301 only. In such a case, as shown in FIG. 13, the
barrier film 1306 may be used as an edge sealant to cover the edges
of the glass encapsulation 1311 and the epoxy seals 1312 to provide
the edge seal for the glass encapsulation.
[0155] However, in some instances, the epoxy cannot be deposited
directly on top of the device (or the layers disposed thereon).
This is illustrated in FIG. 14, which shows an exemplary device
1400 comprising a substrate 1410, a device 1401 disposed over the
substrate 1410 having a device footprint, a barrier film 1406
disposed along the sides the footprint of the device 1401, and a
top encapsulation comprising the barrier film 1406, a glass layer
1411, and an epoxy 1412 (e.g. to couple the glass layer 1411 to the
barrier film layer 1406) disposed over the device 1401. The barrier
film 1406 can be used on top of the device 1401 to separate the
epoxy 1412 from the active device area (or a layer disposed
thereon) of the device 1401. The epoxy seal 1411 can then be
deposited over the barrier film 1406, followed by the glass
encapsulation 1411. Finally, the barrier film 1406 may be deposited
so to form the edge seal along the sides of the footprint of device
1401, as shown in FIG. 14.
[0156] In some embodiments, a product may comprise a water vapor
sensitive electronic component or layer (e.g. an electrode) that
has an edge sealant barrier film deposited in a single chamber
PE-CVD system using an organosilicon precursor. The composition of
the edge sealant barrier film may not change substantially when
observed moving away from the device footprint of the device,
parallel to the substrate, from the inner edge to the outer edge of
the barrier film, along the entire thickness of the barrier film,
including the interface of the barrier film with the substrate. In
some embodiments, the length of the interface of the barrier film
with the substrate in a direction perpendicular to a side of the
device footprint may be less than or equal to 3.0 mm. In some
embodiments, the length of the interface of the barrier film with
the substrate in a direction perpendicular to a side of the device
footprint may be less than or equal to 2.0 mm. In some embodiments,
the length of the interface of the barrier film with the substrate
in a direction perpendicular to a side of the device footprint may
be less than or equal to 1.0 mm.
[0157] In some embodiments, a product may be provide that comprises
a water vapor sensitive electronic component or layer (such as an
electrode) with an edge sealant comprising a barrier film deposited
in a single chamber PE-CVD system using organosilicon precursor.
The composition of the edge sealant barrier film may not change
substantially when observed moving away from the device footprint,
parallel to the substrate, from the inner edge to the outer edge of
the barrier film, along the entire thickness of the barrier film,
including the interface of the barrier film with the substrate. The
composition and density of the edge sealant barrier film may be
such that the ratio of the refractive index of the interface region
of the barrier film close the substrate (i.e. within 10 nm) with
that of the bulk of the barrier film is less than or equal to
0.9993 but greater than or equal to 0.9247.
[0158] In some embodiments, a product may be provided that
comprises a water vapor sensitive electronic component or layer
(such as an electrode) with an edge sealant barrier film deposited
in a single chamber PE-CVD system using organosilicon precursor.
The composition of the edge sealant barrier film may not change
substantially when observed moving away from the device footprint
of the device, parallel to the substrate, from the inner edge to
the outer edge of the barrier film, along the entire thickness of
the barrier film, including the interface of the barrier with the
substrate. The composition and density of the barrier film may be
such that the refractive index of the interface region close to the
substrate (i.e. with in 10 nm) is more than 1.35 but less than
1.459.
[0159] In some embodiments, the bulk diffusion coefficient of water
vapor in the barrier film may be less than 10.sup.-13 cm.sup.2/sec
and the diffusion coefficient of water vapor at the interface of
the barrier film with the substrate may be less than or equal to
10.sup.-8, but greater than or equal to 10.sup.-13 cm.sup.2/sec
when the external environment is at 65.degree. C. and 85% RH. In
some embodiments, the ratio of the bulk diffusion coefficient of
water vapor in the barrier film compared to the diffusion
coefficient along the interface of the barrier film with the
substrate may be less than or equal to 1.0 (i.e. they may be the
same) but greater than or equal to 10.sup.-5. In some embodiments,
the device may not show any edge shrinkage of the active area for
1,000 hrs of storage at 65.degree. C. and 85% RH.
[0160] In addition to the products described above, the inventors
have also found methods of manufacturing such products. In this
regard, in some embodiments, a first method may comprise the steps
of providing a substrate having a device disposed over the
substrate having a device footprint, and fabricating a barrier film
over the substrate and substantially along a side of the device
footprint, where the barrier film may be fabricated so as to have a
perpendicular length that is less than or equal to 3.0 mm
(preferably less than 2.0 mm, and more preferably less than 1.0 mm)
from the side of the device footprint. In some embodiments, the
barrier film may comprise a mixture of a polymeric material and
non-polymeric material.
[0161] The term "providing" is generally used in this context to be
an inclusive term and encompass any manner of obtaining or making
available a substrate having a device disposed over the substrate
for use in such methods. For instance, in some embodiments, the
substrate and the device (and/or components thereof) may be
acquired, such as by purchase from a third party. In some
embodiments, the substrate and/or active area could be fabricated,
manufactured, or otherwise assembled, or the components could be
provided to a third party that may then fabricate or assemble the
substrate having a device disposed thereon.
[0162] Similarly, the term "fabricating" is also intended to be an
inclusive term, and may comprise any suitable deposition process or
other technique for disposing the barrier film over the substrate.
This could include, by way of example only, vacuum depositing a
blanket layer of barrier film over the substrate and etching,
cutting, or ablating portions of the barrier film so that it has a
perpendicular length that is less than 3.0 mm; deposition of the
barrier film through a mask such that it has a perpendicular length
that is less than 3.0 mm, or any other suitable method known in the
art.
[0163] In some embodiments, in the first method as described above,
the device may comprise an organic layer. In some embodiments, the
organic layer may comprise an electroluminescent (EL) material. In
some embodiments, the device may comprise an OLED. As noted above,
although the inventors have found that the use of a barrier film
having a perpendicular length that is less than 3.0 mm (such as
when the barrier film comprises a mixture of a polymeric material
and non-polymeric material) provide benefits to organic devices
including increasing display and panel sizes (e.g. by decreasing
border area (dead space)), embodiments are not so limited.
[0164] In some embodiments, in the first method as described above,
the barrier film may be fabricated so as to have a perpendicular
length that is less than or equal to 2.0 mm from the side of the
device footprint. In some embodiments, the barrier film may be
fabricated so as to have a perpendicular length that is less than
or equal to 1.0 mm from the side of the device footprint. As noted
above, in general a smaller perpendicular length for the barrier
film may allow for a smaller border area of the product, thereby
reducing the size of the product or reducing the inefficient use of
space. As was described above with reference to an exemplary
product, in some embodiments, the barrier film may be fabricated or
disposed so that it does not have any perpendicular lengths from
the side of the device footprint that are greater than 3.0 mm
(preferably 2.0 mm, and more preferable greater than 1.0 mm).
[0165] In some embodiments, in the first method as described above,
the step of fabricating the barrier film may comprise chemical
vapor deposition. In some embodiments, the step of fabricating the
barrier film may utilize an organosilicon precursor. However, as
described above, the inventors have found that a variety of
precursors may be used to fabricate barrier films that have desired
properties to form an edge seal, and may be selected based on the
particular application or device that the barrier film is being
applied thereto.
[0166] In some embodiments, in the first method as decried above,
the step of fabricating the barrier film so as to have a
perpendicular length that is less than or equal to 3.0 mm from a
side of the device footprint may comprise depositing the barrier
film through a mask such that the perpendicular length is less than
or equal to 3.0 mm from the side of the device footprint. The
deposition may be performed in a vacuum process, such as CVD or
PE-CVD.
[0167] In some embodiments, in the first method as described above,
the step of fabricating the barrier film so as to have a
perpendicular length that is less than or equal to 3.0 mm from the
side of the device footprint may comprise the steps of: depositing
a barrier film over the substrate and substantially along a side of
the device footprint, wherein the barrier film is deposited so as
to have a perpendicular length that is greater than or equal to 3.0
mm from the side of the device footprint, and, after depositing the
barrier film, breaking the barrier film such that the barrier film
has a perpendicular length that is less than or equal to 3.0 mm
from the side of the device footprint. In some embodiments, the
step of breaking the barrier film may be accomplished by, or in
combination with, breaking the substrate. This exemplary
fabrication method may provide for increased efficiencies
(particularly where the barrier film is also disposed over device)
because the barrier film may be deposited as a blanket layer over
the substrate (e.g. a mask need not be precisely aligned for the
deposition process). The substrate may be scribed (or ablated) at a
predetermined location (e.g. within 3.0 mm, preferably within 2.0
mm, and more preferably within 1.0 mm of the side of the device
footprint) so as to be broken along the scribe. When the substrate
is broken, the size of the barrier film disposed on the portion of
the substrate that the device footprint is also disposed on may be
reduced.
[0168] It should be appreciated that the various characteristics
described above with reference to the components of the first
product may apply equally to the components described with respect
to the first method, as would be understood by one of skill in the
art. For example, the various descriptions of the composition of
the barrier film, the fabrication of other components (such as top
sealant or encapsulation layers) etc., may also be performed in
accordance with the first method.
[0169] In some embodiments, a first product prepared by a process
may be provided. The process for preparing the first product may
comprise the steps of providing a substrate having a device
disposed over the substrate having a device footprint, and
fabricating a barrier film over the substrate and substantially
along a side of the device footprint, where the barrier film may be
fabricated so as to have a perpendicular length that is less than
or equal to 3.0 mm from the side of the device footprint. In some
embodiments, the barrier film may comprise a mixture of a polymeric
material and non-polymeric material.
[0170] In some embodiments, in the first device prepared by a
process as described above, the device may comprise an organic
layer. In some embodiments, the organic layer may comprise an
organic electroluminescent (EL) material. In some embodiments, the
device may be an OLED.
[0171] In some embodiments, in the first product prepared by a
process as described above, the barrier film may be fabricated so
as to have perpendicular length that is less than or equal to 2.0
mm from the side of the device footprint. In some embodiments, the
barrier film may be fabricated so as to have perpendicular length
that is less than or equal to 1.0 mm from the side of the device
footprint.
[0172] In some embodiments, in the first product prepared by a
process as described above, the step of fabricating the barrier
film may comprise depositing the first barrier film using an
organosilicon precursor. As noted above, the inventors have found
that the use of an organosilicon precursor may provide a barrier
film that has particular properties that may be well-suited for use
as an edge seal, which properties may be fine tuned based on the
various deposition conditions and methods, as described above and
would be appreciated by a person of ordinary skill in the art after
reading this disclosure. However, any suitable precursor material
may be utilized for some embodiments.
[0173] In some embodiments, the step of fabricating the barrier
film may comprise chemical vapor deposition. In some embodiments,
the step of fabricating the barrier film may comprise plasma
enhance chemical vapor deposition (PE-CVD). In some embodiments,
the barrier film consists essentially of a mixture of polymeric
silicon and inorganic silicon, where the weight ratio of polymeric
silicon to inorganic silicon is in the range of 95:5 to 5:95, and
where the polymeric silicon and the inorganic silicon are created
from the same precursor material. In some embodiments, at least an
0.1 .mu.m thickness of the barrier film is deposited under the same
reaction conditions for all the reaction conditions in the
deposition process and the water vapor transmission rate is less
than 10.sup.-6 g/m.sup.2/day through the at least 0.1 .mu.m
thickness of the barrier film.
[0174] In some embodiments, in the first product prepared by a
process as described above, where the step of fabricating the
barrier film comprises depositing the first barrier film using an
organosilicon precursor, the precursor material may comprise
hexamethyl disiloxane or dimethyl siloxane. In some embodiments,
the precursor material may comprise a single organosilicon
compound. In some embodiments, the precursor material may comprise
a mixture of organosilicon compounds.
[0175] In some embodiments, in the first product prepared by a
process as described above, the step of fabricating the barrier
film may comprise depositing the barrier film through a mask such
that the perpendicular length is less than or equal to 3.0 mm from
the side of the device footprint. In some embodiments, the
perpendicular length may be less than or equal to 2.0 mm (and
preferable less than 1.0 mm) from the side of the device
footprint.
[0176] It should be appreciated that the various characteristics
described above with reference to the components of the first
product and the first method may apply equally to the embodiments
that comprise the first product prepared by a process, as would be
understood by one of skill in the art. This includes the various
materials used, the structures created, and the characteristics of
the product and/or the barrier film.
CONCLUSION
[0177] It is understood that the various embodiments described
herein are by way of example only, and are not intended to limit
the scope of the invention. For example, many of the materials and
structures described herein may be substituted with other materials
and structures without deviating from the spirit of the invention.
The present invention as claimed may therefore include variations
from the particular examples and preferred embodiments described
herein, as will be apparent to one of skill in the art. It is
understood that various theories as to why the invention works are
not intended to be limiting.
[0178] The above description is illustrative and is not
restrictive. Many variations of the invention will become apparent
to those skilled in the art upon review of the disclosure. The
scope of the invention should, therefore, be determined not with
reference to the above description, but instead should be
determined with reference to the pending claims along with their
full scope or equivalents.
[0179] Although many embodiments were described above as comprising
different features and/or combination of features, a person of
ordinary skill in the art after reading this disclosure may
understand that in some instances, one or more of these components
could be combined with any of the components or features described
above. That is, one or more features from any embodiment can be
combined with one or more features of any other embodiment without
departing from the scope of the invention.
[0180] As noted previously, all measurements, dimensions, and
materials provided herein within the specification or within the
figures are by way of example only.
[0181] A recitation of "a," "an," or "the" is intended to mean "one
or more" unless specifically indicated to the contrary. Reference
to a "first" component does not necessarily require that a second
component be provided. Moreover reference to a "first" or a
"second" component does not limit the referenced component to a
particular location unless expressly stated.
[0182] All publications mentioned herein are incorporated herein by
reference to disclose and describe the methods and/or materials in
connection with which the publications are cited. The publications
discussed herein are provided solely for their disclosure prior to
the filing date of the present application. Nothing herein is to be
construed as an admission that the present invention is not
entitled to antedate such publication by virtue of prior invention.
Further, the dates of publication provided may be different from
the actual publication dates, which may need to be independently
confirmed.
* * * * *