U.S. patent application number 16/693845 was filed with the patent office on 2021-06-03 for process for pure carbon production, compositions, and methods thereof.
This patent application is currently assigned to WEST VIRGINIA UNIVERSITY RESEARCH CORPORATION. The applicant listed for this patent is WEST VIRGINIA UNIVERSITY RESEARCH CORPORATION. Invention is credited to Alfred H. STILLER.
Application Number | 20210163291 16/693845 |
Document ID | / |
Family ID | 1000005399879 |
Filed Date | 2021-06-03 |
United States Patent
Application |
20210163291 |
Kind Code |
A1 |
STILLER; Alfred H. |
June 3, 2021 |
PROCESS FOR PURE CARBON PRODUCTION, COMPOSITIONS, AND METHODS
THEREOF
Abstract
The disclosure provides for methods of oxidizing carbide anions,
or negative ions, from salt like carbides at temperatures from
about 150.degree. C. to about 750.degree. C. In another aspect, the
disclosure provides for reactions with intermediate transition
metal carbides. In yet another aspect, the disclosure provides for
a system of reactions where salt-like carbide anions and
intermediate carbide anions are oxidized to produce pure carbon of
various allotropes.
Inventors: |
STILLER; Alfred H.;
(Morgantown, WV) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
WEST VIRGINIA UNIVERSITY RESEARCH CORPORATION |
MORGANTOWN |
WV |
US |
|
|
Assignee: |
WEST VIRGINIA UNIVERSITY RESEARCH
CORPORATION
MORGANTOWN
WV
|
Family ID: |
1000005399879 |
Appl. No.: |
16/693845 |
Filed: |
November 25, 2019 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
16022193 |
Jun 28, 2018 |
10494264 |
|
|
16693845 |
|
|
|
|
15618804 |
Jun 9, 2017 |
10035709 |
|
|
16022193 |
|
|
|
|
14772629 |
Sep 3, 2015 |
9764958 |
|
|
PCT/US14/28755 |
Mar 14, 2014 |
|
|
|
15618804 |
|
|
|
|
61798198 |
Mar 15, 2013 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C01B 32/26 20170801;
B01J 19/24 20130101; C01F 7/58 20130101; C01B 32/05 20170801; C01F
11/28 20130101; C01B 32/36 20170801; C01B 32/184 20170801; C01B
32/942 20170801; C01B 32/25 20170801; C01B 32/914 20170801 |
International
Class: |
C01B 32/05 20170101
C01B032/05; B01J 19/24 20060101 B01J019/24; C01B 32/184 20170101
C01B032/184; C01F 7/58 20060101 C01F007/58; C01B 32/942 20170101
C01B032/942; C01B 32/25 20170101 C01B032/25; C01B 32/914 20170101
C01B032/914; C01F 11/28 20060101 C01F011/28; C01B 32/36 20170101
C01B032/36; C01B 32/26 20170101 C01B032/26 |
Claims
1. A method of oxidizing carbide anions and/or negative ions from
carbides, said method comprising: oxidizing carbide anions at a
reaction temperature range from about 150.degree. C. to about
750.degree. C., wherein the reaction produces an allotrope of
carbon in an sp1 and/or sp3 configuration.
2. The method of claim 1, wherein said carbide anions are salt-like
or intermediate carbide anions.
3. The method of claim 2, wherein said salt-like carbide anions are
selected from the group consisting of methanides, acetylides, and
sesquicarbides.
4. The method of claim 2, wherein said salt-like carbide anions are
acetylides.
5. The method of claim 1, wherein said reaction produces an
allotrope of carbon in an sp1 configuration.
6. The method of claim 1, wherein said reaction produces an
allotrope of carbon in an sp3 configuration.
7. The method of claim 1, wherein said reaction temperature is in a
range selected from the group consisting of from about 150.degree.
C. to about 200.degree. C., from about 150.degree. C. to about
250.degree. C., from about 200.degree. C. to about 250.degree. C.,
from about 200.degree. C. to about 300.degree. C., from about
200.degree. C. to about 350.degree. C., from about 200.degree. C.
to about 400.degree. C., from about 250.degree. C. to about
400.degree. C., from about 200.degree. C. to about 500.degree. C.,
from about 250.degree. C. to about 500.degree. C.
8. The method of claim 1, wherein said reaction temperature is in a
range selected from the group consisting of from about 300.degree.
C. to about 600.degree. C., from about 400.degree. C. to about
600.degree. C., from about 500.degree. C. to about 700.degree. C.,
from about 200.degree. C. to about 700.degree. C., from about
250.degree. C. to about 750.degree. C., and from about 150.degree.
C. to about 750.degree. C.
9. The method of claim 1, wherein said reaction temperature is in a
range from about from about 250.degree. C. to about 400.degree.
C.
10. The method of claim 1, wherein said carbide anions comprise
calcium carbide.
11. The method of claim 1, wherein said reaction further comprises
adding a salt with a melting point of less than 250.degree. C. as a
reactant.
12. A method of producing pure elemental allotropes of carbon
comprising: oxidizing salt-like carbide anions and/or intermediate
carbide anions at a reaction temperature range from about
150.degree. C. to about 750.degree. C.
13. The method of claim 12, wherein said salt-like carbide anions
are selected from the group consisting of methanides, acetylides,
and sesquicarbides.
14. The method of claim 12, wherein the reaction produces pure
elemental allotropes of carbon with a sp1 or sp3 configuration.
15. The method of claim 12, wherein said reaction produces pure
elemental allotropes of carbon with a sp1 configuration.
16. The method of claim 12, wherein said reaction produces pure
elemental allotropes of carbon with a sp3 configuration.
17. The method of claim 12, wherein said reaction temperature is in
a range selected from the group consisting of from about
150.degree. C. to about 200.degree. C., from about 150.degree. C.
to about 250.degree. C., from about 200.degree. C. to about
250.degree. C., from about 200.degree. C. to about 300.degree. C.,
from about 200.degree. C. to about 350.degree. C., from about
200.degree. C. to about 400.degree. C., from about 250.degree. C.
to about 400.degree. C., from about 200.degree. C. to about
500.degree. C., from about 250.degree. C. to about 500.degree.
C.
18. The method of claim 12, wherein said reaction temperature is in
a range selected from the group consisting of from about
300.degree. C. to about 600.degree. C., from about 400.degree. C.
to about 600.degree. C., from about 500.degree. C. to about
700.degree. C., from about 200.degree. C. to about 700.degree. C.,
from about 250.degree. C. to about 750.degree. C., and from about
150.degree. C. to about 750.degree. C.
19. The method of claim 12, wherein said reaction temperature is in
a range from about from about 250.degree. C. to about 400.degree.
C.
20. The method of claim 12, wherein the reaction further comprises
utilizing a salt with a melting point of less than 250.degree. C.
as a reactant.
21. The method of claim 12, wherein said reaction comprises
reacting a sesquicarbide with a molten metallic halide salt to
produce a pure allotrope of carbon in the sp1 configuration.
22. A method for producing diamonds by reacting carbides with
molten metallic halide salts at a reaction temperature range from
about 150.degree. C. to about 750.degree. C.
23. The method of claim 22, wherein said reaction temperature is in
a range selected from the group consisting of from about
150.degree. C. to about 200.degree. C., from about 150.degree. C.
to about 250.degree. C., from about 200.degree. C. to about
250.degree. C., from about 200.degree. C. to about 300.degree. C.,
from about 200.degree. C. to about 350.degree. C., from about
200.degree. C. to about 400.degree. C., from about 250.degree. C.
to about 400.degree. C., from about 200.degree. C. to about
500.degree. C., from about 250.degree. C. to about 500.degree.
C.
24. The method of claim 22, wherein said reaction temperature is in
a range selected from the group consisting of from about
300.degree. C. to about 600.degree. C., from about 400.degree. C.
to about 600.degree. C., from about 500.degree. C. to about
700.degree. C., from about 200.degree. C. to about 700.degree. C.,
from about 250.degree. C. to about 750.degree. C., and from about
150.degree. C. to about 750.degree. C.
25. The method of claim 22, wherein said reaction temperature is in
a range from about from about 250.degree. C. to about 400.degree.
C.
26. A method of controlling a carbon allotrope comprising:
controlling the reduction potential of a low melting point halide
salt reactant by varying the reduction potential of a cation and/or
changing the temperature of the melt.
27. A method of oxidizing carbide anions and/or negative ions from
carbides according to claim 1, wherein the reaction takes place
under an environment that is void or substantially void of oxygen
and/or moisture.
28. A method of producing pure elemental allotropes of carbon
according to claim 12, wherein the reaction takes place under an
environment that is void or substantially void of oxygen and/or
moisture.
Description
CROSS REFERENCE TO RELATED APPLICATIONS
[0001] This application claims priority to U.S. Provisional
Application No. 61/798,198, filed Mar. 15, 2013, which is
incorporated herein by reference in its entirety.
FIELD
[0002] The disclosure provides for methods of oxidizing carbide
anions, or negative ions, from salt like carbides at temperatures
from about 150.degree. C. to about 750.degree. C. In another
aspect, the disclosure provides for reactions with intermediate
transition metal carbides. In yet another aspect, the disclosure
provides for a system of reactions where salt-like carbide anions
and intermediate carbide anions are oxidized to produce pure carbon
of various allotropes.
BACKGROUND
[0003] Carbides are chemical compounds containing carbon and an
element with lower electronegativity, or less of an ability to
attract electrons. Nearly all elements react with elemental carbon
to produce carbides. They are further classified into four groups:
salt-like carbides, covalent carbides, interstitial carbides, and
intermediate transition metal carbides. Salt-like carbides react
with water and dilute acids to produce ions and hydrocarbon gases.
Intermediate transition metal carbides also react with dilute acid
and sometimes water to produce metallic cations, hydrocarbons and
sometimes hydrogen.
[0004] Salt-like carbides are further broken down into methanides,
acetylides, and sesquicarbides. Methanides react with water to
produce methane. Methane is a carbon atom bonded to four hydrogen
atoms in an sp3 hybridization. Two examples of methanides are
aluminum carbide (Al.sub.4C.sub.3) and beryllium carbide
(Be.sub.2C). Acetylides are salts of the acetylide anion
C.sub.2.sup.-2 and also have a triple bond between the two carbon
atoms. Triple bonded carbon has an sp1 hybridization and two
examples of acetylides are sodium carbide (Na.sub.2C.sub.2) and
calcium carbide (CaC.sub.2). Sesquicarbides contain the polyatomic
anion C.sub.3.sup.-4 and contains carbon atoms with an sp1
hybridization. Two examples of sesquicarbides are magnesium
(Mg.sub.2C.sub.3) and lithium (Li.sub.4C.sub.3).
[0005] U.S. Pat. No. 1,319,148 defined an oxidization reaction to
produce potassium metal by reacting potassium cations (positive
ions) with acetylide anions from calcium carbide. The reacting
medium was molten potassium fluoride (mp =876.degree. C.). This is
shown in the reaction in Scheme (1) below.
Scheme I
CaC.sub.2+2KFCaF.sub.2+2K+2C.sub.(graphite)reaction
T>800.degree. C. (1)
The other products of this reaction are calcium fluoride and
graphite. Graphite is the most thermodynamically stable form of
elemental carbon, and this is therefore the favored product at high
temperature. This reaction, the reduction of the potassium ion,
takes place above 800.degree. C. which would be considered high
temperature since 600.degree. C. is red heat.
[0006] Alkali metals can be prepared from electrolysis of molten
salts. However, U.S. Pat. No. 1,319,148 indicates that an
oxidization reaction was used to make alkali metals. Additionally,
Concepts and Models of Inorganic Chemistry; Douglas B. McDaniel D.
1965 Xerox Corp. describes how they purified alkali metals before
the electrolysis of the molten salts came into use.
[0007] To produce the alkali metal, the temperature is above the
melting point of KF (mp=858.degree. C.) which is high enough to
vaporize K. (bp=744.degree. C.). The products were indicated as
being CaF.sub.2, K.degree., and the most thermodynamically stable
form of carbon, graphite, C.sub.(graphite).
SUMMARY
[0008] The disclosure provides for a method of oxidizing carbide
anions and/or negative ions from carbides by oxidizing carbide
anions at a reaction temperature of from about 150.degree. C. to
about 750.degree. C., wherein the reaction produces an allotrope of
carbon in an sp1 and/or sp3 configuration.
[0009] In another aspect, the disclosure provides for a method of
producing pure elemental allotropes of carbon by oxidizing
salt-like carbide anions and/or intermediate carbide anions at a
reaction temperature of from about 150.degree. C. to about
750.degree. C.
[0010] In yet another aspect, the disclosure provides for a method
of producing diamonds by reacting carbides with molten metallic
halide salts at a reaction temperature at a reaction temperature of
from about 150.degree. C. to about 750.degree. C.
[0011] The disclosure also provides for a method of controlling a
carbon allotrope by controlling the reduction potential of a low
melting point halide salt reactant by varying the reduction
potential of cations and/or changing the temperature of the
melt.
[0012] In an aspect, the carbide anions are salt-like or
intermediate carbide anions. In another aspect, the salt-like
carbide anions are selected from the group consisting of
methanides, acetylides, and sesquicarbides. In another aspect, the
salt-like carbide anion is calcium carbide.
[0013] In an aspect, the methods described herein produce an
allotrope of carbon in an sp1 configuration. In yet another aspect,
the methods described herein produce an allotrope of carbon in an
sp3 configuration.
[0014] The disclosure also provides for methods described herein
wherein the reaction temperature is below about 150.degree. C.,
below about 200.degree. C., below about 250.degree. C., below about
300.degree. C., below about 400.degree. C., below about 500.degree.
C., below about 600.degree. C., below about 700.degree. C., or
below about 800.degree. C.
[0015] In yet another aspect, the disclosure provides for methods
of oxidizing carbide anions, or negative ions, from salt like
carbides at temperatures in a range from about 150.degree. C. to
about 200.degree. C., from about 150.degree. C. to about
250.degree. C., from about 200.degree. C. to about 250.degree. C.,
from about 200.degree. C. to about 300.degree. C., from about
200.degree. C. to about 350.degree. C., from about 200.degree. C.
to about 400.degree. C., from about 250.degree. C. to about
400.degree. C., from about 200.degree. C. to about 500.degree. C.,
from about 250.degree. C. to about 500.degree. C., from about
300.degree. C. to about 600.degree. C., from about 400.degree. C.
to about 600.degree. C., from about 500.degree. C. to about
700.degree. C., from about 200.degree. C. to about 700.degree. C.,
from about 250.degree. C. to about 750.degree. C., from about
150.degree. C. to about 750.degree. C., from about 150.degree. C.
to less than 800.degree. C., from about 250.degree. C. to less than
800.degree. C., from about 300.degree. C. to less than 800.degree.
C., from about 400.degree. C. to less than 800.degree. C., from
about 500.degree. C. to less than 800.degree. C., or from about
600.degree. C. to less than 800.degree. C.
BRIEF DESCRIPTION OF THE FIGURES
[0016] FIG. 1 is a chart that provides the enthalpies of formation
for various allotropes of carbon.
[0017] FIG. 2 provides for a representative block flow diagram for
formation of various allotropes of carbon, including a (1) reaction
preparation, (2) chemical reaction, (3) carbon separation, and (4)
diamond purification aspect.
DETAILED DESCRIPTION
[0018] In an aspect, the disclosure provides for a method of
diamond production comprising, consisting of, or consisting
essentially of (1) reaction preparation, (2) chemical reaction, (3)
separation, and (4) purification methodologies described herein. A
representative methodology is described in FIG. 2.
[0019] In an aspect, the process starts by preparing the reactor in
the controlled atmosphere void of moisture and oxygen (1). In an
aspect, the chemical reaction (2) follows the reaction preparation
portion. In another aspect, the separation and purification aspects
follow the chemical reaction (2). In yet another aspect, the
separation and purification aspects follow the chemical reaction
(2) because the separation (3) is defined by the removal of
material that is not elemental carbon from the products of the
chemical reaction (2) and the purification (4) is the removal of
any undesired elemental carbon produced by the chemical reaction as
well as any other trace materials remaining from the separation
(3).
[0020] The (1) reaction preparation aspect of the process deals
with preparing the reactants to control the variables and the
conditions of reaction; (2) the chemical reaction of the respective
reactants in a manner that is described herein; (3) the Separation
aspect includes the initial removal of the un-reacted carbides and
metallic salts, the metallic salts produced by the reaction, the
elemental metals produced by the reaction, and any/or metal oxide
produced; and the (4) Purification aspect is where the product is
produced, for example, diamonds. In an embodiment, (4) the
purification aspect of the process can include the removal of the
sp2 and mixed hybridization carbon produced by the reaction along
with the removal of any remaining carbides, metallic salts,
elemental metals, and metal oxides. In another aspect, the
disclosure provides for a method of carbon production comprising,
consisting of, or consisting essentially of any of the sub groups
described in the (1) reaction preparation, (2) chemical reaction,
(3) separation, and (4) purification methodologies described
herein.
[0021] While, in an aspect, the overall process of producing
diamonds can involve at least three parts in an aspect, the
disclosure also provides for a method of streamlining this process
by combining (3) separation and (4) purification aspects into a
single aspect or single step. For example, in an aspect, the
disclosure provides for a method comprising, consisting of,
consisting essentially of (1) reaction preparation, (2) chemical
reaction, and (3) separation and the (4) purification methodologies
as described herein.
(1) Reaction Preparation:
Reaction Preparation in a Moisture Free Environment:
[0022] Different salt like and intermediate carbides react with
water and/or dilute acids to produce hydrocarbon gases and metal
oxide. Almost all salt like and intermediate carbides also react
with moisture in the air. The reaction rate increases, as the
carbide is ground to the smaller particle sizes due to the increase
in surface area exposed to the environment. Certain reactants, for
instance aluminum carbide, will react with the moisture in the air
to produce alumina (aluminum oxide) which can complicate the
separation process. In an aspect, the disclosure provides for a
method of removing the elemental metals and metal oxides from the
products of the reaction using dilute or concentrated acid while
the elemental carbon produced by the reaction remains
unchanged.
[0023] In addition, metal salts, such as halide reactants, can also
attract moisture from the air to form a solution of the ions in
water. Any moisture accumulated in the salt can enter the reactor
and react with the carbide. The moisture can also vaporize at the
reaction temperature increasing the pressure and altering the
reaction conditions. Therefore, in an aspect, the reactants can be
loaded in an atmosphere controlled glove box. In another aspect,
the reaction conditions include an environment void of any moisture
and oxygen. To accomplish such a moisture free environment, the
atmosphere can be prepared by flushing the glove box many times
with dry inert gas, for example, but not limited to, argon.
Additional steps can be taken to further reduce and control the
moisture in the glove box. These steps can include, for example,
using a metallic salt as a desiccant inside the glove box and a
circulation system, which may include a fine particle separator and
several moisture separators. In an aspect, the glove box loading
procedure includes evacuating the transfer chamber several times to
remove or minimize any moisture from entering the controlled
atmosphere.
[0024] In an aspect, the disclosure provides for a method of
preparing the reactants and the reactor in an inert environment
where the reactants remain unchanged chemically prior to the start
of the reaction. In another aspect, the inert environment is void
or substantially void of oxygen and moisture. In an aspect, the
inert environment contains only trace amounts of oxygen and
moisture. In yet another aspect, only the physical properties of
the reactant are altered prior to the start of the reaction.
Reaction Preparation in an Oxygen Free Environment:
[0025] In an aspect, preparation in an oxygen free environment is
similar to preparation in a moisture free environment. The
preparation can be accomplished in a glove box that has been
flushed multiple times with a dry inert gas. In an aspect, one
difference between the reaction preparation in an "oxygen free
environment" verses a "moisture free environment" is the removal of
any trace amounts of oxygen remaining in the glove box after the
inert gas flush along with the trace amounts of oxygen entering
from the transfer chamber when materials are loaded and unloaded.
In an aspect, to remove the trace amounts of oxygen, an oxygen
scrubber or series of scrubbers, depending upon the reactants used
and the other conditions of the reaction, can be added to the glove
box circulation system. The circulation can also be designed to add
additional items or bypass existing ones to achieve the proper
conditions for any carbide and metallic salts to be analyzed as
reactants.
Reducing the Particle Size of the Carbide:
[0026] Many of the commercially available carbides are of the size
of gravel, so the particle size, generally, may be reduced to the
size required for the reaction. In order to reduce the particle
size of the carbide, the disclosure provides a method to be used
inside the glove box. In an aspect of this method, the carbide is
first cut into smaller pieces using a tile cutter, then crushed
with a pair of channel locks pliers, and finally ground to the
proper particle size using a mortar and pestle. The crushed carbide
is thereafter passed through a series of sieves to collect the
desired particle size carbide for the process. As an alternative to
the above-described method, a small hand-operated roller mill or
suitable crushing device, which can be adjusted to create the
desired particle size for the experiments, can be used to produce
the proper sized carbide particles.
[0027] In an aspect, the reaction described herein is a diffusion
controlled reaction. As such, the rate of reaction will be
controlled by the overall surface area available for reaction. The
rate of reaction includes properties such as porosity of the
carbide and viscosity of the liquid medium, not just the particle
size of the reactant. In an aspect, the aluminum carbide has a
particle size of -300 mesh (44 microns) and the calcium carbide is
in the form of gravel. In another aspect, the calcium carbide is
crushed to particle sizes of -20 mesh to -6 mesh. In yet another
aspect, the calcium carbide is size is from about 10 microns to
about 5 millimeters, from about 30 microns to about 3 millimeters,
from about 100 microns to about 2 millimeters, or from about 30
microns to about 200 microns.
Reactor Shape and Orientation:
[0028] Through experimentation and analysis of the materials
produced by the reaction, it was determined that once the metallic
salts became molten and the reactants were in a liquid solution and
the contents of the reactor reach steady-state (this is also given
that the reactor is not agitated), the different material inside
the reactor separated into layers based on their respective
specific gravities. Carbides do not dissolve in the molten salts.
Therefore, the reaction is between a solid phase and a liquid
phase. It is not homogenous. The reaction takes place at the
contact surfaces of the molten salt and solid carbide. Such a
mechanism further confirms why surface area, in an aspect, can be
an important parameter to consider. Therefore, in an aspect, the
reaction can occur at one vertical height where the reactants were
physically able to come together under the proper conditions to
react.
[0029] In an aspect, it is advantageous to limit the contact
surface of our reactor configuration to have a limited contact
area. This is another parameter which has an influence on the
kinetics of the diffusion controlled reaction in reaction systems
described herein, which is non-turbulent inside of the reactor.
Limiting the contact area allows the reaction to proceed at a rate
slow enough so that the latent heat of crystallization does not
increase the temperature of the contact area to a point that sp2
carbon is produced. So this parameter is influenced by the other
reaction conditions. The importance of the parameter can also
decrease if we agitate the reactor. Any means that has the ability
to increase the contact area would make a higher effective reaction
zone. This can also be accomplished, for example, by changing
reactor orientation or by stirring. As a result, different reactor
designs and orientations may be utilized in an attempt to maximize
the surface area of the horizontal interface where the reaction can
occur. In an aspect, the reactor prepared in the glove box is made
of glass and the reactants are loaded inside. The glass reactor can
be sealed in a stainless steel tube so it can be removed from the
glove box and the controlled atmosphere conditions can be
maintained inside throughout the reaction process. Initially, the
reactors included simple glass test tubes which varied in diameter
based on the desired mass and ratio of the reactants to be
used.
[0030] To increase the surface area of the horizontal interface
where the reaction occurs, the height of the reactors are decreased
while maintaining the same amount of material that the reactors can
hold. One way to accomplish this is by orienting the reactors in
the horizontal rather than the vertical direction. But, because the
reaction occurs in a liquid medium, the open top test tube style
reactors may not be sufficient. As a result, for some experiments
described herein, ampoule style glass reactors were utilized. This
design provides for both a simple and effective design.
[0031] In an aspect, the disclosure provides for a method of
altering the dimensions and orientation of the chemical reaction
vessel to control the surface area, shape, and thickness of the
reaction interface.
[0032] In an aspect, several of the horizontally oriented reactors
are progressing through the purification part of the process. This
has led to unexpectedly good results. In another attempt to
increase the interface surface area, in an aspect, multiple glass
Petri dishes are stacked one on top of the next in the same
stainless steel tube. This allows for numerous, large surface area
reaction interfaces to be contained in the same stainless steel
tube.
(2) Chemical Reaction:
[0033] Methods of Oxidizing Carbide Anions and/or Negative Ions
from Carbides
[0034] In an aspect, the disclosure provides for methods of
oxidizing carbide anions, or negative ions, from salt like carbides
at low temperatures below about 600.degree. C. In another aspect,
the disclosure provides for methods of oxidizing carbide anions, or
negative ions, from salt like carbides at temperatures below about
150.degree. C., below about 200.degree. C., below about 250.degree.
C., below about 300.degree. C., below about 400.degree. C., below
about 500.degree. C., below about 600.degree. C., below about
700.degree. C., or below about 800.degree. C. In yet another
aspect, the disclosure provides for methods of oxidizing carbide
anions, or negative ions, from salt like carbides at temperatures
in a range from about 150.degree. C. to about 200.degree. C., from
about 150.degree. C. to about 250.degree. C., from about
200.degree. C. to about 250.degree. C., from about 200.degree. C.
to about 300.degree. C., from about 200.degree. C. to about
350.degree. C., from about 200.degree. C. to about 400.degree. C.,
from about 250.degree. C. to about 400.degree. C., from about
200.degree. C. to about 500.degree. C., from about 250.degree. C.
to about 500.degree. C., from about 300.degree. C. to about
600.degree. C., from about 400.degree. C. to about 600.degree. C.,
from about 500.degree. C. to about 700.degree. C., from about
200.degree. C. to about 700.degree. C., from about 250.degree. C.
to about 750.degree. C., from about 150.degree. C. to about
750.degree. C., from about 150.degree. C. to less than 800.degree.
C., from about 250.degree. C. to less than 800.degree. C., from
about 300.degree. C. to less than 800.degree. C., from about
400.degree. C. to less than 800.degree. C., from about 500.degree.
C. to less than 800.degree. C., or from about 600.degree. C. to
less than 800.degree. C.
[0035] Oxidization means that the ion being oxidized gives up
electrons. The negative ions of the salt like carbides are reacted
to produce elemental carbon in its various allotropes, or crystal
structures, with sp1, sp2, and/or sp3 hybridizations. In another
aspect, the disclosure provides for reactions with intermediate
transition metal carbides. In yet another aspect, the disclosure
provides for a system of reactions where salt-like carbide anions
and intermediate carbide anions are oxidized to produce pure carbon
of various allotropes.
[0036] In an aspect, the first step of the reaction system is to
oxidize the carbide ions at temperatures described herein. The
reactions use low melting point salts, for example stannous
chloride (SnCl.sub.2), that have melting points less than
280.degree. C. as the reactants. The reaction medium is the molten
salt, for example, molten stannous chloride. This means that there
is an excess of salt during the reaction which takes place in the
molten salt liquid. Chemically, the cation (positive ion) of the
salt is reduced to the elemental state. Therefore, the stannous ion
Sn.sup.+2 would become elemental tin (Sn.degree.). The standard
reduction potential of the stannous ion Sn.sup.+2 is only about
-0.136V. Reduction potential refers to the ability of a chemical
species to acquire electrons and thus have its charge reduced. So
not much energy is required to reduce the stannous ion, therefore
the reaction reacts to completion. There is an excess of reduction
potential in the carbide anions since they are shown to reduce the
potassium ion in Equation (1) which requires -2.94V.
[0037] The reduction of Sn.sup.+2 by acetylide or any carbide anion
is not mentioned anywhere in the literature. Only certain metallic
salts are applicable for this reaction. It is preferred that the
cation of the salt does not produce a carbide by direct reaction
with carbon at low temperatures or the temperature of the reduction
reaction. If the cation does produce carbide, then pure carbon
would not be produced. Examples of the preferred salts contain tin,
lead, mercury, and zinc. Furthermore, the salts must have a low
melting point. The temperature of the reaction must be high enough
to melt the salts but low enough to control the electronic
hybridization of the carbon. As mentioned in the background
information, graphite is the most thermodynamically stable form of
pure carbon. So if the temperature of the reaction is too high, the
pure carbon will form crystalline graphite in the sp2 hybridization
instead of the desired sp1 or sp3 hybridizations.
[0038] The next item in the reaction system is the low temperature
oxidation of methanides to produce diamond, or carbon in that has
an sp3 hybridization. Aluminum carbide (Al.sub.4C.sub.3) and
beryllium carbide (Be.sub.2C) are the only two known salt like
carbides that produce methane when they react with water. The
methane molecule contains a carbon atom in the sp3 hybridized
state, which is the same as diamond. The idea is to oxidize the
methanide anion in a controlled manner at temperatures low enough
to maintain the electronic configuration, or sp3 hybridization and
produce diamond. Thus, the controlled oxidization of aluminum
carbide at low enough temperatures will preferentially produce
diamonds. This reduction takes place at about 280.degree. C. and
atmospheric pressure.
[0039] Oxidation of the methanide (aluminum carbide) anion in
molten tin halide salt blends to produce diamond. There is no
literature that mentions the reduction of aluminum carbide much
less anything that mentions this reaction to produce diamond, or
sp3 hybridized carbon. Experiments for this reaction have been
carried out using stannous fluoride (SnF.sub.2) and stannous
chloride (SnCl.sub.2), which have melting points of 214.degree. C.
and 235.degree. C., respectively. These reactions can be seen in
Equation (2) and Equation (3) below:
Equation 2
Al.sub.4C.sub.3+6SnF.sub.26Sn.degree.+4AlF.sub.3+3C.degree..sub.(diamond-
)reaction at T=235.degree. C. (2)
Equation 3
Al.sub.4C.sub.3+6SnCl.sub.26Sn.degree.+4AlCl.sub.3+3C.degree..sub.(diamo-
nd)reaction at T=280.degree. C. (3)
The proof of the diamond, or carbon with sp3 hybridization,
material produced was established using X-Ray Diffraction patterns.
Early diamond production studied certain metallic catalysts needed
to make diamonds. The fact that diamonds were produced using
conditions described herein is unexpected and provides support for
the methodology described herein.
[0040] Since the chemical hypothesis to maintain the sp3
hybridization of pure carbon is confirmed with the production of
diamonds, it can extended to include the potential superconducting
material to maintain the sp1 hybridization of pure carbon. There
have been many different attempts to make this material but none
have been successful. The process begins with a carbide that
contains carbon in an sp1 hybridized state. As mentioned in the
background information, acetylides have the ability to satisfy this
requirement. The most common example is calcium carbide
(CaC.sub.2). However, sp1 carbon in the acetylide anion can be
reconfigured even at very low energy or low temperatures. A more
desired reactant is one that has a tendency to maintain the sp1
configuration throughout the rigors of the reaction. The disclosure
provides for two compounds that have the ability to act as a
sufficient reactant: magnesium sesquicarbide (Mg.sub.2C.sub.3) and
lithium sesquicarbide (Li.sub.4C.sub.3), also mentioned in the
background information. From the literature, for example "Crystal
Structure of Magnesium Sesquacarbide," Fjellvaag, H., and Karen, P.
Inorganic Chemistry, Vol. 31 (1992): 3260-3263 which is herein
incorporated by reference in its entirety, a structural analysis
using X-Ray diffraction was completed and shows that two of the
carbon atoms are equivalent with an sp1 configuration. With a
hydrolysis reaction, methyl acetylene (CH.sub.3C.sub.2H) is
produced. One terminal carbon, the methyl carbon (CH.sub.3) end is
sp3 in nature while the other two carbons maintain their sp1
character. The goal is to polymerize the carbon atoms while
maintaining the sp1 configuration. This would produce a new
allotrope of carbon that has an sp1 configuration. Due to the
electronic properties of such a material, it may be a high
temperature superconductor.
[0041] In another aspect, about less than 0.5%, about less than 1%,
about less than 2%, about less than 3%, about less than 4%, about
less than 5%, about less than 7.5%, about less than 10%, about less
than 15%, about less than 20%, about less than 25%, about less than
30%, about less than 35%, about less than 40%, about less than 45%,
about less than 50%, about less than 60%, or about less than 75% of
the total yield includes material with a diamond structure, for
example, an sp3 carbon structure. In another aspect, about more
than 0.5%, about more than 1%, about more than 2%, about more than
3%, about more than 4%, about more than 5%, about more than 7.5%,
about more than 10%, about more than 15%, about more than 20%,
about more than 25%, about more than 30%, about more than 35%,
about more than 40%, about more than 45%, about more than 50%,
about more than 60%, or about more than 75%, about more than 85%,
or about more than 95% of the total yield includes material with a
diamond structure. In yet another aspect, about 0.1% to about 1%,
about 0.5% to about 2%, about 1% to about 2%, about 2% to about 5%,
about 2% to about 7.5%, about 0.5% to about 10%, about 3% to about
10%, about 5% to about 10%, about 5% to about 25%, about 0.1% to
about 35%, about 0.1% to about 40%, about 0.1% to about 50%, about
1% to about 50%, about 5% to about 50%, about 10% to about 50%,
about 15% to about 50%, about 25% to about 50%, or about 1% to
about 95% of the total yield includes material with a diamond
structure. In an aspect, the yields of diamond are relative to the
"possible" products described in FIG. 1.
[0042] In another aspect, about less than 0.5%, about less than 1%,
about less than 2%, about less than 3%, about less than 4%, about
less than 5%, about less than 7.5%, about less than 10%, about less
than 15%, about less than 20%, about less than 25%, about less than
30%, about less than 35%, about less than 40%, about less than 45%,
about less than 50%, about less than 60%, or about less than 75% of
the yield includes material with a diamond structure relative to
the amount of graphene and amorphous carbon also recovered. In
another aspect, about more than 0.5%, about more than 1%, about
more than 2%, about more than 3%, about more than 4%, about more
than 5%, about more than 7.5%, about more than 10%, about more than
15%, about more than 20%, about more than 25%, about more than 30%,
about more than 35%, about more than 40%, about more than 45%,
about more than 50%, about more than 60%, or about more than 75%,
about more than 85%, or about more than 95% of the yield includes
material with a diamond structure relative to the amount of
graphene and amorphous carbon also recovered. In yet another
aspect, about 0.1% to about 1%, about 0.5% to about 2%, about 1% to
about 2%, about 2% to about 5%, about 2% to about 7.5%, about 0.5%
to about 10%, about 3% to about 10%, about 5% to about 10%, about
5% to about 25%, about 0.1% to about 35%, about 0.1% to about 40%,
about 0.1% to about 50%, about 1% to about 50%, about 5% to about
50%, about 10% to about 50%, about 15% to about 50%, about 25% to
about 50%, or about 1% to about 95% of the yield includes material
with a diamond structure relative to the amount of graphene and
amorphous carbon also recovered.
[0043] In another aspect, the disclosure provides for a process
wherein the yield from the carbide starting material is more than
about 5% pure carbon, more than about 10% pure carbon, more than
about 20% pure carbon, more than about 30% pure carbon, more than
about 40% pure carbon, more than 50% pure carbon, more than 60%
pure carbon, more than 70% pure carbon, about more than 80% pure
carbon, more than 90% pure carbon, or more than 95% pure
carbon.
[0044] As discussed in the Chemical Reaction section, in an aspect,
diamond growth occurs at one vertical level inside the reactor, for
example, at steady state with no agitation, where the reactants
meet at the proper conditions. The reaction that occurs is
exothermic, which means that it gives off heat. As the reaction
progresses more heat is generated and that heat is transferred
through the rest of the reactor. Using the reaction conditions
described in, for example, Examples 1-3 heat is generated at the
reaction site at a greater rate than is transferred away from the
reaction site. This means that as the reaction progresses and the
diamond crystal grows this area inside of the reactor will continue
to increase in temperature. If the temperature at the reaction site
increases above a certain level the thermodynamics of the reaction
will change. Specifically, if the temperature gets too high, the
reaction will cease producing diamonds and begin producing sp2
carbon. As this new reaction progresses, the sp2 carbon will
encapsulate the diamond and the growth of the crystal will stop.
The diamond crystal will then have a coating (armoring) of sp2
carbon at the surface.
Use of Inert Material to Alter the Heat and Mass Transfer of the
Reaction and Increase the Area of the Reaction Zone:
[0045] In addition to the carbide and metallic salt, in an aspect,
additional materials can be added to the reactor in order to alter
the heat transfer and mass transfer during the chemical reaction
step of the process. In an aspect, additional materials can be any
material that is inert relative to the respective reactant and can
withstand the conditions (for example, temperature, molten salt)
inside the reactor. Examples include ceramic pellets or stainless
steel ball bearings. These materials can also increase the overall
surface area or volume of the physical zone in the reactor where
the chemical reaction takes place. These materials are inert and
therefore remain unchanged by the chemical reaction. In an aspect,
the disclosure provides for a method of altering the heat transfer
and mass transfer properties inside the reactor via the addition of
excess reactant or inert materials that remain chemically unchanged
by the reaction. In another aspect, in addition the carbide and
metallic salt used as reactants, inert material, catalysts (such as
FeCl.sub.3) and additives such as dopants to alter the properties
of the diamonds produced are added to the reactor and can be
utilized with the methodologies described herein.
(3) Product Separation:
[0046] Reduction of Elemental Metal from the Products of
Reaction:
[0047] The products of the carbon producing reaction include
elemental metals which can be removed. In an aspect, removal of
these metals from the other products of reaction can be
accomplished by using a reducing agent such as hydrochloric acid
(HCl). In another aspect, any acid which oxidizes the elemental
metal produced can be used in the separation. One key feature is to
oxidize the metal, therefore removing it, while leaving the
diamonds (sp3 carbon) unchanged. The acid can also leave the sp2
and mixed hybridized carbon unchanged to allow the opportunity to
examine the sp2 and mixed hybridized carbon produced in the future
for additional products from the process. One potential use of the
nondiamond product is in super capacitors. Once the reaction is
complete and the stainless steel transfer tube opened, the products
of reaction are transferred to a separation vessel made of
polypropylene. In an aspect, the separation vessel is made of any
material that is inert to acids used to remove the elemental metals
and metal oxides as well as any other solvents needed for the
separation process. In addition, the vessel should also be able to
withstand the enhanced gravity of the centrifuge which is also used
for the separation process.
Use of Surfactants in the Separation Process:
[0048] During the separation process, salts and sp2 and mixed
hybridized carbon act as a glue to hold the particles together. The
liquids used to dissolve away the salts which are mostly water and
alcohols and acids, create films and agglomerates which act to hold
the particles together, particularly the very fine particle size
diamonds. The addition of surfactants acts to breakup any films and
helps to separate the particles so they can be more easily
dissolved or dispersed by the liquids. In addition to separating
the particles for dissolving, the surfactant solutions act like a
soap and force any undesired material from the surface of the
diamonds. Another advantage to the surfactant solutions in the
separation process is decreasing or increasing the settling rate of
the fine material. Once the acids remove the elemental metals, the
densest material remaining is diamonds. Therefore the diamonds
settle first based on the particle size. The finer particle size
diamonds remain suspended in the solution due to Brownian motion.
The surfactant solution changes the surface tension of the water
used to dissolve the salts. This lower surface tension allows the
finer particle size diamonds to settle out of solution at different
rates.
[0049] In another aspect, surfactants may also allow a better
separation of the diamonds from the other material. In another
aspect, different surfactants or surfactant mixtures can be used to
separate out the various products, and even separate the diamonds
produced in the reaction into various groups of different particle
sizes. In another aspect, a silicone-based surfactant can be used
with the methodology described herein. Suitable surfactants for use
with the described methodology include those described in
"Surfactants: A Practical Handbook," Lange, Robert K. Philadelphia,
Pa.: Hanser Gardner Publications, Inc., 1999, the contents of which
are herein incorporated by reference in their entirety.
[0050] In an aspect, the disclosure provides for a method for
recovering the fine particle sized desired products from the water,
alcohol, surfactant solution, heavy media or acids used in the
separation process by filtering the fine particles from the
solutions.
Gravity Separation of the Diamonds Using Dense or Heavy Media:
[0051] The diamonds produced in the reaction can be separated from
the other products of reaction based on the differences in specific
gravity of the materials. For example, the products of the chemical
reaction can be added to perchloroethylene a liquid with a specific
gravity of about 1.6, dibromomethane, specific gravity=2.4, and/or
halogenated organic compounds used for gravity separation, specific
gravity>2.0. Diamonds, with a specific gravity of about 3.3 will
sink in the liquid and be separated from any material with a
specific gravity less than 1.6 which will float on the surface of
the perchlorotheylene. The gravity separation can be used for
composite particles in the Separation Step as well as for diamonds
in the Purification Step. In another aspect, any chemical material
or chemical compound can be used during this step based on the
difference in specific gravity between the composition of interest,
for example a diamond, and a chemical material or chemical compound
to be separated.
Removal of Un-reacted Carbides:
[0052] It is unlikely that all the reactants in the process will be
completely consumed by the reaction and converted to products,
especially at reaction conditions optimized for economics of the
process. Therefore, un-reacted carbide will remain in the products
of reaction and have to removed or separated. The un-reacted
carbide readily reacts with water to produce hydrocarbon gases and
metal oxide. In many cases, the metal oxide is easily reacted away
using the acid. Therefore in the transfer step from the reactor to
the separation vessel using the acid, water reacts with the carbide
to produce acetylene and a metal oxide which is then reacted by the
acid. If there is any remaining un-reacted carbide in the products
of reaction after the acid treatment, it can be reacted with water
or water in the surfactant solution. Due to subsequent treatments
with acids in the following steps, the metal oxide produced will
eventually be reacted and removed from the products of
reaction.
[0053] In an aspect, the disclosure provides for a method of
removing un-reacted carbide from the respective targeted products
of the reaction by reacting the carbide with water and further
reacting the metal oxide produced with acid.
Removal of Un-reacted Metallic Salts and Metallic Salts Produced in
the Reaction:
[0054] The removal of the metallic salts produced by the reaction
can be accomplished using water or a surfactant solution, alcohols,
or acids. During the separation process the products of reaction
are transferred into a separation vessel. The liquid which
dissolves the un-reacted metallic salts and the metallic salts
produced in the reaction can be added to the separation vessel and
agitated for a period of time. The separation vessel can then be
left to settle and the liquid which dissolved the metallic salts
decanted off or removed. To accelerate the process and also to
perform a better separation where the solid material is forced out
of solution, the separation vessels are placed in the bucket
centrifuge. In an aspect, the liquid in the separation vessel still
contains the dissolved salts, which can now be removed.
[0055] In an aspect, the disclosure provides for a method of
removing the un-reacted metallic salts and the metallic salts
produced by the reaction from the products of the reaction by
dissolving the un-reacted products in water, alcohols, surfactant
solutions, or acids.
[0056] In another aspect, the disclosure provides for a method of
separating and dispersing individual solid particles from the
respective reaction products with the use of surfactant solutions.
In another aspect, the method of separating and dispersing
individual solid particles from the respective reaction further
comprises removing undesired, non-targeted, or trace products of
the reaction by dissolving and/or reacting undesired, non-targeted,
or trace products and subsequently removing from the mixture. In
yet another aspect, the desired products remain chemically
unchanged by the reaction and can be purified and classified into
different products.
[0057] In another aspect, the disclosure provides for a method of
separating, removing, and/or classifying of undesired products of
reaction by specific gravity using heavy media liquids and/or
surfactant solutions.
Reaction Separation of Elemental Metal from the Products of
Reaction:
[0058] Elemental metal produced in the reactions described herein
can also be removed using other materials (for example,
dibromomethane) that diffuses into the composite particles and
reacts with any elemental metals produced in the reaction.
Dibromomethane, for example, has the ability to diffuse into the
composite particles of the products of reaction and react with the
encapsulated metals. This method allows for all of the elemental
metal produced to be removed in a single step prior to the removal
of the sp2 carbon, which separates any of the remaining composite
particles. In an aspect, the products of reaction are exposed to
the material (for example, dibromomethane) for an adequate
resonance time to allow the diffusion into the composite particle
and reaction with the elemental metal. An example of an adequate
resonance is several hours to several days. In another aspect, an
example of an adequate resonance is about 2 or more hours, about 5
or more hours, about 12 or more hours, about 1 or more days, about
2 or more days, about 3 or more days, or about 5 or more days. In
another aspect, an example of an adequate resonance is about 1 to
about 4 hours, about 2 to about 12 hours, about 2 hours to about 1
day, about 6 hours to about 2 days, about 12 hours to about 2 days,
or about 1 hour to about 3 days. This rate of this reaction is
governed by the diffusion of the species into the composite
particles. Therefore, an adequate resonance time will depend
primarily on the size of the composite particles and/or the
viscosity of the liquid reaction medium.
[0059] In an aspect, the disclosure provides for a method of
removing the elemental metal from the products of reaction of other
material (for instance, dibromomethane) that have the ability to
diffuse into composite particles and reduce the elemental
metal.
Removal of Metal Oxides from the Products of Reaction:
[0060] Many of the reactants used herein produce metal oxides that
can be reacted by various acids. However, there are reactants, for
example, aluminum carbide, which produce a metal oxide that does
not react with acid. In the case of aluminum oxide it produces a
product called alumina or aluminum oxide. Aluminum oxide is very
stable and does not react with the acids. But it can be reacted by
a solution of potassium hydroxide. Due to the use of the potassium
hydroxide solution, this is a more difficult separation because it
requires the addition of heat for the potassium hydroxide to remain
in solution.
Recovery of the Fine Particle Size Solids during the Separation
Step:
[0061] While separating the reacted elemental metals and dissolved
metallic salts from the elemental carbon, the liquid removed still
contain a small percentage of solid composite particles. In an
aspect, the liquid removed contains, for example, about less than
0.5%, about less than 1%, about less than 2%, about less than 3%,
about less than 4%, about less than 5%, about less than 7.5%, about
less than 10%, about less than 15%, about less than 20%, about less
than 25% of solid composite materials. In another aspect, the
liquid removed contains, for example, about 0.1% to about 1%, about
0.5% to about 2%, about 1% to about 2%, about 2% to about 5%, about
2% to about 7.5%, about 0.5% to about 10%, about 3% to about 10%,
about 5% to about 10%, about 5% to about 25%, or about 0.1% to
about 35%, of solid composite material. In an aspect, the solid
composite material contains diamonds along with other products of
reaction. These composite particles can be recovered from the
supernatant liquid using filtration or gravity separation. The
recovered material can be further processed to recover the diamonds
produced.
Recovery of the Alcohol Solvents:
[0062] In an aspect, the disclosure provides for a system for
recovery of alcohols and heavy medium liquid. The recovery of
solvents is likely to become important as the scale is increased in
order to accommodate commercialization. An example recovery system
for the alcohols is described herein.
(4) Product Purification:
[0063] The diamond purification aspect is an additional step in the
process which removes the products of reaction that are not sp3
carbon (diamond). This step begins with the removal of the sp2
carbon from the products of reaction. In an aspect, the removal of
the sp2 and mixed hybridized carbon can be accomplished with two
different oxidative procedures, the oxidation of the sp2 and mixed
hybridized carbon in a hot oven and/the oxidation of the sp2 and
mixed hybridized in strong oxidative solutions, such as
H.sub.2O.sub.2 or HNO.sub.3. Depending on the initial reactants and
reaction conditions used for the process, both methods can be
utilized to completely remove the sp2 carbon.
[0064] After the sp2 and mixed hybridized carbon is removed, the
Purification part of the process will be similar to the separation
part which is why we believe we will eventually be able to combine
them into one part of the process. The Purification part of the
process has achieved very good results, especially in removing the
sp2 and mixed hybridized carbon.
[0065] In an aspect, the disclosure provides for method of reacting
the sp2 hybridized carbon from the remaining elemental carbon using
concentrated acids while leaving the remaining elemental carbon
unchanged. The disclosure further provides for a method of removing
the sp2 hybridized carbon from the remaining elemental carbon by
dispersing the sp2 carbon in a surfactant solution while leaving
the remaining elemental carbon unchanged. In yet another aspect,
the disclosure provides for a method of removing the sp2 hybridized
carbon from the remaining elemental carbon and classifying the
remaining elemental carbon into particle sizes using heavy media
liquid or combinations of heavy media liquids.
Chemical Reaction to Remove the sp2 Carbon:
[0066] A factor in removing the sp2 and mixed hybridized carbon
from the products of reaction is to perform this task while leaving
the diamonds (or sp3 carbon) unchanged by the process. In addition
to oxidizing the sp2 carbon to remove it, another option is to
react the sp2 carbon using one or more chemicals under the proper
reaction conditions. One example is the use of trifluoroacetic acid
and concentrated hydrogen peroxide.
Use of Surfactants in the Purification Step:
[0067] In an aspect, the use of surfactants in the purification
process is nearly identical to "Use of Surfactants in the
Separation Step." One difference is the reduced particle size of
the material in the purification step and the absence of sp2 and
mixed hybridized carbon which will alter the conditions produced by
the surfactant or surfactant mixture.
Recovery of the Fine Particle Size Diamonds during the Purification
Step:
[0068] This item is similar to the `Recovery of the Fine Particle
Size Solids during the Separation Step`. One difference is that at
this point in the process, the solid material to be recovered is
diamond and not a composite particle. In addition, the particle
size of the solids will be decreased. In an aspect, the recovery
method will include filtration or gravity separation.
EXAMPLES
Example 1
[0069] In an oxygen moisture free environment, aluminum carbide,
Al.sub.4C.sub.3 was ground to less than 20 mesh. A quantity of
anhydrous stannous chloride, SnCl.sub.2 was blended with the ground
aluminum carbide at twice the stoichiometric ratio for the reaction
below
Al.sub.4C.sub.3+6SnCl.sub.24AlCl.sub.3+6Sn+3C
[0070] The blend was poured into a glass ampoule that was
subsequently placed into a stainless steel tube. The stainless
steel tube was sealed and removed from the controlled environment.
The tube and its contents were heated to 280.degree. C. for 2
hours. The contents of the ampoule were washed with 6M HCl to
remove all the aluminum chloride, excess stannous chloride and Sn
metal. The remaining carbon was in two forms (1) a graphene like
compressed set of platelets and (2) a cubic/orthorhombic diamond
like structure. The preponderance of the carbon product was the
latter structure.
Example 2
[0071] In an oxygen moisture free environment, calcium carbide,
CaC.sub.2 was ground to less than 20 mesh. A quantity of anhydrous
zinc chloride, ZnCl.sub.2 was blended with the ground aluminum
carbide at twice the stoichiometric ratio for the reaction
below
3CaC.sub.2+3ZnCl.sub.23CaCl.sub.2+3Zn+6C
[0072] The blend was poured into a glass ampoule that was
subsequently placed in a stainless steel tube. The stainless steel
tube was sealed and removed from the controlled environment. The
tube and its contents were heated to 425.degree. C. for 2 hours.
The contents of the ampoule were washed with 6M HCl to remove all
the Zinc chloride, calcium chloride, and Zn metal. The remaining
carbon was in two forms (1) a graphene like compressed set of
platelets and (2) a cubic/orthorhombic diamond like structure. The
preponderance of the carbon product was the latter structure.
Example 3
[0073] In an oxygen moisture free environment, calcium carbide,
CaC.sub.2 was ground to less than 20 mesh. A quantity of anhydrous
stannous chloride, SnCl.sub.2 was blended with the ground aluminum
carbide at twice the stoichiometric ratio for the reaction
below
3CaC.sub.2+3SnCl.sub.23CaCl.sub.2+3Sn+6C
[0074] The blend was poured into a glass ampoule that was
subsequently placed in a stainless steel tube. The stainless steel
tube was sealed and removed from the controlled environment. The
tube and its contents were heated to 280.degree. C. for 2 hours.
The contents of the ampoule were washed with 6M HCl to remove all
the stannous chloride, calcium chloride, and Sn metal. The
remaining carbon was in only one form a graphene like compressed
set of platelets
* * * * *