U.S. patent application number 16/326630 was filed with the patent office on 2021-04-01 for antifouling film.
The applicant listed for this patent is SHARP KABUSHIKI KAISHA. Invention is credited to KEN ATSUMO, KENICHIRO NAKAMATSU, YASUHIRO SHIBAI.
Application Number | 20210096282 16/326630 |
Document ID | / |
Family ID | 1000005325592 |
Filed Date | 2021-04-01 |
![](/patent/app/20210096282/US20210096282A1-20210401-D00000.png)
![](/patent/app/20210096282/US20210096282A1-20210401-D00001.png)
![](/patent/app/20210096282/US20210096282A1-20210401-D00002.png)
United States Patent
Application |
20210096282 |
Kind Code |
A1 |
SHIBAI; YASUHIRO ; et
al. |
April 1, 2021 |
ANTIFOULING FILM
Abstract
The antifouling film includes a substrate, and a polymer layer
disposed on a surface of the substrate and including on a surface
thereof an uneven structure provided with multiple projections at a
pitch not longer than a wavelength of visible light. The polymer
layer is a cured product of a polymerizable composition, the
polymerizable composition containing, in terms of active
constituents, 15 to 40 wt % of an urethane acrylate containing six
or more functional groups, 35 to 60 wt % of a multifunctional
acrylate containing four or more functional groups and 3 to 15
ethylene oxide groups for each functional group, 15 to 30 wt % of a
monofunctional acrylate with no ethylene oxide group, 0.5 to 10 wt
% of a fluorine release agent containing a perfluoropolyether group
and having a fluorine atom concentration of 50 wt % or lower, and
0.5 to 5 wt % of a polymerization initiator.
Inventors: |
SHIBAI; YASUHIRO; (Sakai
City, JP) ; ATSUMO; KEN; (Sakai City, JP) ;
NAKAMATSU; KENICHIRO; (Sakai City, JP) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
SHARP KABUSHIKI KAISHA |
Sakai City,Osaka |
|
CN |
|
|
Family ID: |
1000005325592 |
Appl. No.: |
16/326630 |
Filed: |
June 28, 2017 |
PCT Filed: |
June 28, 2017 |
PCT NO: |
PCT/JP2017/023736 |
371 Date: |
February 19, 2019 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
G02B 1/18 20150115; B32B
27/308 20130101; B32B 27/18 20130101; B32B 2307/746 20130101; B32B
3/30 20130101; G02B 1/118 20130101 |
International
Class: |
G02B 1/18 20060101
G02B001/18; B32B 3/30 20060101 B32B003/30; B32B 27/18 20060101
B32B027/18; B32B 27/30 20060101 B32B027/30; G02B 1/118 20060101
G02B001/118 |
Foreign Application Data
Date |
Code |
Application Number |
Aug 25, 2016 |
JP |
2016-164640 |
Claims
1. An antifouling film comprising: a substrate, and a polymer layer
disposed on a surface of the substrate and including on a surface
thereof an uneven structure provided with multiple projections at a
pitch not longer than a wavelength of visible light, the polymer
layer being a cured product of a polymerizable composition, the
polymerizable composition containing, in terms of active
constituents, 15 to 40 wt % of an urethane acrylate containing six
or more functional groups, 35 to 60 wt % of a multifunctional
acrylate containing four or more functional groups and 3 to 15
ethylene oxide groups for each functional group, 15 to 30 wt % of a
monofunctional acrylate with no ethylene oxide group, 0.5 to 10 wt
% of a fluorine release agent containing a perfluoropolyether group
and having a fluorine atom concentration of 50 wt % or lower, and
0.5 to 5 wt % of a polymerization initiator.
2. The antifouling film according to claim 1, wherein the polymer
layer includes a surface having a coefficient of dynamic friction
of 2.0 or lower.
3. The antifouling film according to claim 1 or 2, wherein the
polymer layer includes a surface having a contact angle of water of
130.degree. or greater and a contact angle of hexadecane of
30.degree. or greater.
4. The antifouling film according to claim 1, wherein the
monofunctional acrylate includes one or both of N-acryloyl
morpholine and N,N-dimethyl acrylamide.
5. The antifouling film according to claim 1, wherein the polymer
layer has a thickness of 5.0 .mu.m or more and 20.0 .mu.m or
less.
6. The antifouling film according to claim 1, wherein the multiple
projections have an average pitch of 100 nm or longer and 400 nm or
shorter.
7. The antifouling film according to claim 1, wherein the multiple
projections have an average height of 50 nm or higher and 600 nm or
lower.
8. The antifouling film according to claim 1, wherein the multiple
projections have an average aspect ratio of 0.8 or more and 1.5 or
less.
Description
TECHNICAL FIELD
[0001] The present invention relates to antifouling films. The
present invention more specifically relates to an antifouling film
including an uneven structure of nanometer scale.
BACKGROUND ART
[0002] Various optical films exhibiting antireflective performance
have been studied (e.g., see Patent Literatures 1 to 3). In
particular, optical films having an uneven structure of nanometer
scale (nanostructure) are known for their excellent antireflective
performance. This uneven structure has a continuously varying
refractive index from the air layer to the substrate, thereby
capable of reducing reflected light significantly.
CITATION LIST
Patent Literature
Patent Literature 1: JP 2012-52125 A
Patent Literature 2: WO 2007/040159
Patent Literature 3: JP 2005-97371 A
SUMMARY OF INVENTION
Technical Problem
[0003] Although such optical films exhibit excellent antireflective
performance, the uneven structure on the surface may cause easy
spread of dirt such as fingerprints (sebaceous dirt) sticking
thereon and may further cause difficulty in wiping off such dirt
present between projections. The sticking dirt tends to be noticed
because of its reflectance significantly different from the
reflectance of the optical film. Accordingly, a functional film
(antifouling film) has been desired which has an uneven structure
of nanometer scale on the surface and is excellent in dirt wiping
performance (e.g., fingerprint wiping performance), i.e., excellent
in antifouling performance.
[0004] The inventors studied on the above issues to find that
conventional antifouling films lack the adhesiveness between the
substrate of the antifouling film and a polymer layer forming the
surface (uneven structure) of the antifouling film, as well as the
antifouling performance. The studies revealed that conventional
antifouling films also lack the rubbing resistance and the
reliability. For example, rubbing the surface (surface of an uneven
structure) of the polymer layer causes projections to adhere to
each other to be never restored (projections are fallen and never
rise again) or breakage of projections. Therefore, increased
rubbing resistance has been desired. Additionally, under high
temperature/high humidity environment, materials forming the
polymer layer may bleed out to reduce optical properties. Thus,
increased reliability has been also required.
[0005] As mentioned, there have been no measures to improve
antifouling performance, adhesiveness, rubbing resistance, and
reliability of conventional antifouling films. For example, Patent
Literatures 1 to 3 lack disclosure relating to adhesiveness or
reliability. Also, there is still room for improving the
antifouling performance and the rubbing resistance.
[0006] The present invention is devised in view of the above state
of the art, and aims to provide an antifouling film excellent in
all of antifouling performance, adhesiveness, rubbing resistance,
and reliability.
Solution to Problem
[0007] The inventors made various studies on antifouling films
excellent in all of antifouling performance, adhesiveness, rubbing
resistance, and reliability. They thereby found a certain scheme in
which predetermined proportions of components improving the
respective properties are contained in a polymerizable composition
that constitutes a polymer layer of an antifouling film. The
inventors thus found measures for the above issues to arrive at the
present invention.
[0008] In other words, an aspect of the present invention may be an
antifouling film including: a substrate, and a polymer layer
disposed on a surface of the substrate and including on a surface
thereof an uneven structure provided with multiple projections at a
pitch not longer than a wavelength of visible light, the polymer
layer being a cured product of a polymerizable composition, the
polymerizable composition containing, in terms of active
constituents, 15 to 40 wt % of an urethane acrylate containing six
or more functional groups, 35 to 60 wt % of a multifunctional
acrylate containing four or more functional groups and 3 to 15
ethylene oxide groups for each functional group, 15 to 30 wt % of a
monofunctional acrylate with no ethylene oxide group, 0.5 to 10 wt
% of a fluorine release agent containing a perfluoropolyether group
and having a fluorine atom concentration of 50 wt % or lower, and
0.5 to 5 wt % of a polymerization initiator.
[0009] The polymer layer may include a surface having a coefficient
of dynamic friction of 2.0 or lower.
[0010] The polymer layer may include a surface having a contact
angle of water of 130.degree. or greater and a contact angle of
hexadecane of 30.degree. or greater.
[0011] The monofunctional acrylate may include one or both of
N-acryloyl morpholine and N,N-dimethyl acrylamide.
[0012] The polymer layer may have a thickness of 5.0 .mu.m or more
and 20.0 .mu.m or less.
[0013] The multiple projections may have an average pitch of 100 nm
or longer and 400 nm or shorter.
[0014] The multiple projections may have an average height of 50 nm
or higher and 600 nm or lower.
[0015] The multiple projections may have an average aspect ratio of
0.8 or more and 1.5 or less.
Advantageous Effects of Invention
[0016] The present invention can provide an antifouling film
excellent in all of antifouling performance, adhesiveness, rubbing
resistance, and reliability.
BRIEF DESCRIPTION OF DRAWINGS
[0017] FIG. 1 is a schematic cross-sectional view of an antifouling
film of an embodiment.
[0018] FIG. 2 is a schematic perspective view of the polymer layer
in FIG. 1.
[0019] FIG. 3 includes schematic cross-sectional views for
illustrating a method for producing an antifouling film of the
embodiment.
DESCRIPTION OF EMBODIMENTS
[0020] Hereinafter, the present invention is described in more
detail based on an embodiment with reference to the drawings. The
embodiment, however, is not intended to limit the scope of the
present invention. Each of the configurations of the embodiment may
appropriately be combined or modified within the spirit of the
present invention.
[0021] The expression "X to Y" herein means "X or more and Y or
less".
Embodiment
[0022] An antifouling film of an embodiment is described below with
reference to FIG. 1 and FIG. 2. FIG. 1 is a schematic
cross-sectional view of an antifouling film of the embodiment. FIG.
2 is a schematic perspective view of the polymer layer in FIG.
1.
[0023] An antifouling film 1 includes a substrate 2 and a polymer
layer 3 disposed on a surface of the substrate 2.
[0024] The substrate 2 may be formed of, for example, a resin such
as triacetyl cellulose (TAC), polyethylene terephthalate (PET), or
methyl methacrylate (MMA). The substrate 2 may appropriately
include an additive such as a plasticizer in addition to the above
material. The substrate 2 may have undergone easy adhesion
treatment on the surface (polymer layer 3 side surface). For
example, a triacetyl cellulose film having undergone easy adhesion
treatment may be used. The substrate 2 may have undergone
saponification treatment on the surface (polymer layer 3 side
surface). For example, a saponified triacetyl cellulose film may be
used. When the antifouling film 1 is attached to a display device
including a polarizer, such as a liquid crystal display device, the
substrate 2 may constitute a part of the polarizer.
[0025] The thickness of the substrate 2 is preferably 50 .mu.m or
more and 100 .mu.m or less in terms of assuring the transparency
and the processability.
[0026] The polymer layer 3 includes on its surface an uneven
structure, i.e., a moth-eye structure (structure like a moth's
eye), provided with multiple projections (protrusions) 4 at a pitch
P (distance between the apexes of adjacent projections 4) not
longer than the wavelength of visible light (780 nm). The
antifouling film 1 can thus exhibit excellent antireflective
performance (low reflectivity) by the moth-eye structure.
[0027] The thickness T of the polymer layer 3 is preferably thin in
terms of distributing fluorine atoms in the later described
fluorine release agent on the surface (the surface opposite to the
substrate 2) of the polymer layer 3 at a high concentration.
Specifically, the thickness T of the polymer layer 3 is preferably
5.0 .mu.m or more and 20.0 .mu.m or less, more preferably 8.0 .mu.m
or more and 12.0 .mu.m or less. As shown in FIG. 1, the thickness T
of the polymer layer 3 indicates the distance from the surface on
the substrate 2 side to the apex of a projection 4.
[0028] Examples of the shape of the projections 4 include those
tapering toward the tip (tapered shapes) such as shapes consisting
of a columnar lower part and a hemispherical upper part
(temple-bell-like shapes) and conical shapes (cone-like shapes,
circular-cone-like shapes). In FIG. 1, the bases of the gaps
between any adjacent projections 4 are inclined. The bases may be
flat without inclination.
[0029] The multiple projections 4 have an average pitch of
preferably 100 nm or longer and 400 nm or shorter, more preferably
100 nm or longer and 200 nm or shorter, in terms of sufficiently
preventing occurrence of optical phenomena such as moire and
iridescence. The average pitch of the multiple projections 4
specifically means the average value of the pitches between all
adjacent projections in a 1-.mu.m square region of a plane
photograph taken with a scanning electron microscope.
[0030] The multiple projections 4 have an average height of
preferably 50 nm or higher and 600 nm or lower, more preferably 100
nm or higher and 300 nm or lower, in terms of satisfying the later
described preferred average aspect ratio of the multiple
projections 4. The average height of the multiple projections 4
specifically means the average height of sequential ten projections
in a cross-sectional photograph taken with a scanning electron
microscope. The ten projections are selected with damaged
projections and deformed projections (e.g., projections deformed in
preparation of a measurement sample) excluded.
[0031] The multiple projections 4 have an average aspect ratio of
preferably 0.8 or more and 1.5 or less, more preferably 1.0 or more
and 1.3 or less. Multiple projections 4 with an average aspect
ratio of less than 0.8 may cause insufficient prevention of optical
phenomena such as moire and iridescence, possibly failing in
achieving excellent antireflective performance. Multiple
projections 4 with an average aspect ratio of more than 1.5 may
deteriorate the processability of the uneven structure, possibly
causing sticking or deteriorated transforming performance in
formation of the uneven structure (e.g., clogging of the later
described die 6, twining of the material). The average aspect ratio
of the multiple projections 4 means a ratio of the average height
of the multiple projections 4 to the average pitch thereof
(height/pitch).
[0032] The projections 4 may be arranged randomly or regularly
(periodically). The projections 4 may be arranged periodically, but
are preferably arranged without periodicity (arranged randomly) as
shown in FIG. 2, thereby preventing occurrence of unnecessary
diffracted light derived from periodical projections.
[0033] The polymer layer 3 is a cured product of a polymerizable
composition. Examples of the polymer layer 3 include a cured
product of an active energy ray-curable polymerizable composition
and a cured product of a heat curable polymerizable composition.
Examples of active energy rays include ultraviolet rays, visible
rays, infrared rays, and plasma. The polymer layer 3 is preferably
a cured product of an active energy ray-curable polymerizable
composition, more preferably a cured product of an ultraviolet
ray-curable polymerizable composition.
[0034] The polymerizable composition contains, in terms of active
constituents, 15 to 40 wt % of an urethane acrylate containing six
or more functional groups (hereinafter, also referred to as
component A), 35 to 60 wt % of a multifunctional acrylate
containing four or more functional groups and 3 to 15 ethylene
oxide groups for each functional group (hereinafter, also referred
to as component B), 15 to 30 wt % of a monofunctional acrylate with
no ethylene oxide group (hereinafter, also referred to as component
C), 0.5 to 10 wt % of a fluorine release agent containing a
perfluoropolyether group and having a fluorine atom concentration
of 50 wt % or lower (hereinafter, also referred to as component D),
and 0.5 to 5 wt % of a polymerization initiator (hereinafter, also
referred to as component E).
[0035] Active constituents of the polymerizable composition (active
constituents of components A to E) mean substances that work as
constituents of the polymer layer 3 after curing and exclude
components that do not contribute to curing reaction
(polymerization reaction) (e.g. solvent). For example, an active
constituent of the component D is a compound containing a fluorine
atom in a molecule.
[0036] The polymerizable composition may contain additional
component(s) as long as the composition contains the components A
to E at the described proportions.
[0037] The components A to E are described below.
(Component A)
[0038] The component A, in which cohesion of urethane bonds
increases the crosslinking density of the polymer layer 3 to give
appropriate hardness (elasticity), improves the rubbing resistance.
The cohesion of urethane bonds further improves the adhesiveness
between the substrate 2 and the polymer layer 3 (hereinafter, also
simply referred to as adhesiveness).
[0039] In the component A, the urethane acrylate contains six or
more, preferably eight or more, more preferably ten or more
functional groups. A urethane acrylate containing five or less
functional groups fails in increasing the crosslinking density of
the polymer layer 3 to cause too low a hardness, thereby
deteriorating the rubbing resistance. A urethane acrylate
containing too many functional groups excessively increases the
viscosity of the urethane acrylate to reduce the compatibility with
other components, thereby possibly deteriorating the rubbing
resistance. In view of these points, the upper limit of the number
of functional groups of the urethane acrylate is preferably 15. The
number of functional groups of the urethane acrylate means the
number of acryloyl groups for each molecule.
[0040] The proportion of the component A in the polymerizable
composition is, in terms of active constituents, 15 to 40 wt %,
preferably 20 to 35 wt %, more preferably 25 to 30 wt %. Less than
15 wt % of the proportion of the component A in terms of active
constituents fails in increasing the crosslinking density of the
polymer layer 3 to cause too low a hardness, thereby deteriorating
the rubbing resistance. Such a proportion also causes too small an
amount of urethane bonds, thereby reducing the adhesiveness. More
than 40 wt % of the proportion of the component A in terms of
active constituents excessively increases the crosslinking density
of the polymer layer 3 to cause insufficient elasticity (reduced
flexibility), thereby deteriorating the rubbing resistance. When
the polymerizable composition contains multiple kinds of components
A, the total proportion of the multiple kinds of components A may
fall within the above range in terms of active constituents.
[0041] Known examples of the component A include an urethane
acrylate component (number of functional groups: 6) in each of
"UA-306H", "UA-306T", "UA-3061", and "UA-510H" available from
Kyoeisha Chemical Co., Ltd.; "KUA-9N" (number of functional groups:
9), "KUA-10N" (number of functional groups: 10), and "KUA-15N"
(number of functional groups: 15) available from KSM Co., Ltd.;
"U-6LPA", "UA-1100H" (number of functional groups: 6), "UA-33H"
(number of functional groups: 9), "U-10HA", "U-10PA" (number of
functional groups: 10), and "UA-53H" (number of functional groups:
15) available from Shin-Nakamura Chemical Co., Ltd.; and
"Ebecryl.RTM. 1290", "Ebecryl 5129" (number of functional groups:
6), "KRM.RTM.8904" (number of functional groups: 9), and "KRM8452"
(number of functional groups: 10) available from Daicel-Allnex
Ltd.
(Component B)
[0042] The component B increases the crosslinking density of the
polymer layer 3 to give appropriate hardness (elasticity), thereby
improving the rubbing resistance. Furthermore, an ethylene oxide
group having a high polarity improves the interaction with the
substrate 2, thereby improving the adhesiveness. The rubbing
resistance is considered to relate to the crosslinking density and
the glass transition temperature of the polymer layer 3. That is,
an increase in crosslinking density and a decrease in glass
transition temperature can significantly improve the rubbing
resistance. For example, in the case where the polymerizable
composition contains a multifunctional acrylate with a propylene
oxide group, the glass transition temperature increases compared
with the case of containing a multifunctional acrylate with an
ethylene oxide group. This is because a branched --CH.sub.3 in the
propylene oxide group inhibits the molecular motion. The propylene
oxide group (the same shall apply to a hydrocarbon group), which
has a polarity lower than an ethylene oxide group and thus lowers
the interaction with the substrate 2, also deteriorates the
adhesiveness. Accordingly, in the present embodiment, an ethylene
oxide group is selected in terms of the rubbing resistance and the
adhesiveness.
[0043] In the component B, the multifunctional acrylate contains
four or more, preferably six or more, more preferably nine or more
functional groups. A multifunctional acrylate containing three or
less functional groups fails in increasing the crosslinking density
of the polymer layer 3 to cause too low a hardness, thereby
deteriorating the rubbing resistance. A multifunctional acrylate
containing too many functional groups causes too high a
crosslinking density of the polymer layer 3 to reduce the
elasticity, thereby possibly deteriorating the rubbing resistance.
In view of these points, the upper limit of the number of
functional groups of the multifunctional acrylate is preferably 15.
The number of functional groups of the multifunctional acrylate
means the number of acryloyl groups for each molecule.
[0044] In the component B, the multifunctional acrylate contains 3
to 15 ethylene oxide groups for each functional group, preferably 4
to 12 ethylene oxide groups for each functional group, more
preferably 6 to 9 ethylene oxide groups for each functional group.
Less than three ethylene oxide groups for each functional group
causes insufficient elasticity of the polymer layer 3 to
deteriorate the rubbing resistance. More than 15 ethylene oxide
groups for each functional group excessively reduce the
crosslinking density of the polymer layer 3 to deteriorate the
rubbing resistance. Here, the number of ethylene oxide groups for
each functional group means (number of ethylene oxide groups for
each molecule)/(number of acryloyl groups for each molecule).
[0045] The proportion of the component B in the polymerizable
composition is, in terms of active constituents, 35 to 60 wt %,
preferably 40 to 55 wt %, more preferably 45 to 50 wt %. Less than
35 wt % of the proportion of the component B in terms of active
constituents causes insufficient elasticity of the polymer layer 3,
thereby deteriorating the rubbing resistance. More than 60 wt % of
the proportion of the component B in terms of active constituents
causes too low a crosslinking density of the polymer layer 3,
thereby deteriorating the rubbing resistance. When the
polymerizable composition contains multiple kinds of components B,
the total proportion of the multiple kinds of components B may fall
within the above range in terms of active constituents.
[0046] Examples of the component B include ethoxylated
pentaerythritol tetraacrylate and ethoxylated polyglycerol
polyacrylate. Known examples of ethoxylated pentaerythritol
tetraacrylate include "ATM-35E" (number of functional groups: 4,
number of ethylene oxide groups: 8.75 for each functional group)
available from Shin-Nakamura Chemical Co., Ltd. Known examples of
ethoxylated polyglycerol polyacrylate include "NK Economer.RTM.
A-PG5027E" (number of functional groups: 9, number of ethylene
oxide groups: 3 for each functional group) and "NK Economer
A-PG5054E" (number of functional groups: 9, number of ethylene
oxide groups: 6 for each functional group) available from
Shin-Nakamura Chemical Co., Ltd.
(Component C)
[0047] The component C improves the compatibility between the
components A, B, and D, thereby improving the rubbing resistance.
Furthermore, the component C, which suppresses cure shrinkage of
the polymerizable composition and thus increases the cohesion with
the substrate 2, improves the adhesiveness. The components A and B,
both having a large molecular weight, have low compatibility
between them. The components A and B, both having multifunctional
groups, have low adhesiveness between them after cure shrinkage.
The component D may have a long chain structure and thereby may
have low compatibility with the components A and B. Thus, the
component C not only increases the cohesion with the substrate 2
but also functions as a reactive diluent (compatibilizer) for the
components A, B, and D.
[0048] The component C contains no ethylene oxide group. A
monofunctional acrylate containing an ethylene oxide group, having
a long chain structure, has a low glass transition temperature but
exhibits low reactivity. Thus, a large amount of the monofunctional
acrylate containing an ethylene oxide group tends to cause bleed
out. The monofunctional acrylate containing an ethylene oxide group
has low compatibility with the component D. Thus, a small amount of
the monofunctional acrylate containing an ethylene oxide group
fails in improving the compatibility while a large amount thereof
tends to cause bleed out though improving the compatibility. Such
inconvenience similarly occurs in the case of a monomer containing
a propylene oxide group and a monomer containing a long chain
hydrocarbon group, for example.
[0049] The proportion of the component C in the polymerizable
composition is, in terms of active constituents, 15 to 30 wt %,
preferably 18 to 28 wt %, more preferably 20 to 25 wt %. Less than
15 wt % of the proportion of the component C in terms of active
constituents deteriorates the smoothness to cause poor rubbing
resistance. Such a proportion fails in suppressing cure shrinkage
of the polymerizable composition to reduce the adhesiveness. More
than 30 wt % of the proportion of the component C in terms of
active constituents excessively reduces the crosslinking density of
the polymer layer 3 to deteriorate the rubbing resistance. When the
polymerizable composition contains multiple kinds of components C,
the total proportion of the multiple kinds of components C may fall
within the above range in terms of active constituents.
[0050] Examples of the component C include monomers containing an
amide group, such as N-acryloyl morpholine, N,N-dimethyl
acrylamide, N,N-diethyl acrylamide, N-(2-hydroxy ethyl)acrylamide,
diacetone acrylamide, and N-n-butoxy methyl acrylamide; monomers
containing an ether group, such as tetrahydrofuran acrylate; and
monomers containing a hydroxyl group, such as 4-hydroxy butyl
acrylate. Known examples of N-acryloyl morpholine include
"ACMO.RTM." available from KJ Chemicals Corporation. Known examples
of N,N-dimethyl acrylamide include "DMAA.RTM." available from KJ
Chemicals Corporation. Known examples of N,N-diethyl acrylamide
include "DEAA.RTM." available from KJ Chemicals Corporation. Known
examples of N-(2-hydroxy ethyl)acrylamide include "HEAA.RTM."
available from KJ Chemicals Corporation. Known examples of
diacetone acrylamide include "DAAM.RTM." available from Nihon Kasei
Co., Ltd. Known examples of N-n-butoxy methyl acrylamide include
"NBMA" available from MCC Unitec Co., Ltd. Known examples of
tetrahydrofuran acrylate include "Viscoat #150" available from
Osaka Organic Chemical Industry Ltd. Known examples of 4-hydroxy
butyl acrylate include "4HBA" available from Nihon Kasei Co.,
Ltd.
[0051] The component C preferably includes one or both of
N-acryloyl morpholine and N,N-dimethyl acrylamide. Such a
composition lowers the viscosity of the component C, thereby
further improving the compatibility with the components A, B, and
D. The adhesiveness is further improved when the substrate 2 is a
triacetyl cellulose film.
(Component D)
[0052] The component D, which allows uniform distribution of
fluorine atoms on the surface (surface opposite to the substrate 2)
of the polymer layer 3 and reduces the surface free energy of the
polymer layer 3, improves the antifouling performance. Furthermore,
the smoothness is improved and thereby the rubbing resistance is
improved.
[0053] The fluorine atom concentration in the component D is 50 wt
% or lower. More than 50 wt % of the fluorine atom concentration
excessively reduces the compatibility with the components A to C to
prevent fluorine atoms from being uniformly distributed on the
surface (surface opposite to the substrate 2) of the polymer layer
3, leading to deterioration in antifouling performance and rubbing
resistance. Such a concentration also tends to cause bleed out
under high temperature/high humidity environment to reduce the
reliability. Too low a fluorine atom concentration excessively
reduces the amount of fluorine atoms distributed on the surface
(surface opposite to the substrate 2) of the polymer layer 3 to
possibly cause deterioration in antifouling performance and rubbing
resistance. In view of these points, the lower limit of the
fluorine atom concentration is preferably 20 wt %.
[0054] The component D contains a perfluoropolyether group. A
release agent without perfluoropolyether group (e.g. fluorine
release agent containing a perfluoro alkyl group, silicon-based
release agent) fails in sufficiently improving the antifouling
performance and the rubbing resistance of the polymer layer 3.
[0055] The proportion of the component D in the polymerizable
composition is, in terms of active constituents, 0.5 to 10 wt %,
preferably 1 to 5 wt %, more preferably 1.5 to 3 wt %. Less than
0.5 wt % of the proportion of the component D in terms of active
constituents excessively reduces the amount of fluorine atoms
distributed on the surface (surface opposite to the substrate 2) of
the polymer layer 3 to deteriorate the antifouling performance.
Such a proportion also deteriorates the smoothness to cause poor
rubbing resistance. More than 10 wt % of the proportion of the
component D in terms of active constituents excessively reduces the
compatibility with the components A to C to fail in uniformly
distributing fluorine atoms on the surface (surface opposite to the
substrate 2) of the polymer layer 3 to deteriorate the antifouling
performance and rubbing resistance. Such a proportion also tends to
cause bleed out under high temperature/high humidity environment to
deteriorate the reliability. When the polymerizable composition
contains multiple kinds of components D, the total proportion of
the multiple kinds of components D may fall within the above range
in terms of active constituents.
[0056] Known examples of the component D include "Fomblin.RTM.
MT70" (fluorine atom concentration: 43 wt %) and "Fomblin AD1700"
(fluorine atom concentration: 24 wt %) available from Solvay.
(Component E)
[0057] The component E improves the curability of the polymerizable
composition.
[0058] The proportion of the component E in the polymerizable
composition is, in terms of active constituents, 0.5 to 5 wt %,
preferably 1 to 4 wt %, more preferably 1.5 to 3 wt %. Less than
0.5 wt % of the proportion of the component E in terms of active
constituents causes insufficient curing of the polymerizable
composition. More than 5 wt % of the proportion of the component E
in terms of active constituents tends to cause bleed out under high
temperature/high humidity environment to deteriorate the
reliability. When the polymerizable composition contains multiple
kinds of components E, the total proportion of the multiple kinds
of components E may fall within the above range in terms of active
constituents.
[0059] Examples of the component E include a photo-polymerization
initiator and a thermal polymerization initiator. The component E
is preferably a photo-polymerization initiator. The
photo-polymerization initiator is active to active energy rays, and
is added so as to initiate a polymerization reaction for
polymerizing monomers.
[0060] Examples of the photo-polymerization initiator include a
radical polymerization initiator, an anionic polymerization
initiator, and a cationic polymerization initiator. Examples of the
photo-polymerization initiator include acetophenones such as
p-tert-butyl trichloro acetophenone, 2,2'-diethoxy acetophenone,
and 2-hydroxy-2-methyl-1-phenylpropan-1-one; ketones such as
benzophenone, 4,4'-bis(dimethylamino)benzophenone, 2-chloro
thioxanthone, 2-methyl thioxanthone, 2-ethyl thioxanthone, and
2-isopropyl thioxanthone; benzoin ethers such as benzoin, benzoin
methyl ether, benzoin isopropyl ether, and benzoin isobutyl ether;
benzyl ketals such as benzyl dimethyl ketal and hydroxy cyclohexyl
phenyl ketone; acylphosphine oxides such as 2,4,6-trimethyl
benzoyl-diphenyl-phosphineoxide and bis(2,4,6-trimethyl
benzoyl)-phenyl phosphineoxide; and alkylphenones such as 1-hydroxy
cyclohexyl phenyl ketone. Known examples of 2,4,6-trimethyl
benzoyl-diphenyl-phosphineoxide include "Lucirin.RTM. TPO" and
"Irgacure.RTM. TPO" available from BASF. Known examples of
bis(2,4,6-trimethyl benzoyl)-phenyl phosphineoxide include
"Irgacure 819" available from BASF. Known examples of 1-hydroxy
cyclohexyl phenyl ketone include "Irgacure 184" available from
BASF.
[0061] The polymerizable composition may further contain a solvent
(component other than active constituents). In this case, the
solvent may be involved in the components A to E with active
constituents, or may be contained separately from the components A
to E.
[0062] Examples of the solvent include alcohols (carbon number 1 to
10: e.g., methanol, ethanol, n- or i-propanol, n-, sec-, or
t-butanol, benzyl alcohol, octanol), ketones (carbon number 3 to 8:
e.g., acetone, methyl ethyl ketone, methyl isobutyl ketone,
diisobutyl ketone, dibutyl ketone, cyclohexanone), esters or ether
esters (carbon number 4 to 10: e.g., ethyl acetate, butyl acetate,
ethyl lactate), y-butyrolactone, ethylene glycol monomethyl
acetate, propylene glycol monomethyl acetate, ethers (carbon number
4 to 10: e.g., EG monomethyl ether (methyl cellosolve), EG
monoethyl ether (ethyl cellosolve), diethylene glycol monobutyl
ether (butyl cellosolve), propylene glycol monomethyl ether),
aromatic hydrocarbons (carbon number 6 to 10: e.g., benzene,
toluene, xylene), amides (carbon number 3 to 10: e.g., dimethyl
formamide, dimethyl acetamide, N-methylpyrrolidone), halogenated
hydrocarbons (carbon number 1 to 2: e.g., methylene dichloride,
ethylene dichloride), and petroleum solvents (e.g., petroleum
ether, petroleum naphtha).
[0063] As mentioned, the present embodiment can achieve the
antifouling film 1 excellent in all of antifouling performance,
adhesiveness, rubbing resistance, and reliability.
[0064] In terms of achieving the antifouling performance, the
polymer layer 3 includes a surface (surface opposite to the
substrate 2) having a contact angle of water of preferably
130.degree. or greater and a contact angle of hexadecane of
preferably 30.degree. or greater.
[0065] In terms of achieving the rubbing resistance, the polymer
layer 3 includes a surface (surface opposite to the substrate 2)
having a coefficient of dynamic friction of preferably 2.0 or
lower, more preferably 1.5 or lower, still more preferably 1.0 or
lower.
[0066] Application of the antifouling film 1 is not particularly
limited as long as the excellent antifouling performance is
exerted. The antifouling film 1 may be applied as an optical film
such as an antireflection film, for example. Such an antireflection
film, when attached to the inside or outside of a display device,
contributively improves the visibility.
[0067] The antifouling performance of the antifouling film 1 may
mean capability of easily removing dirt on the surface (surface
opposite to the substrate 2) of the polymer layer 3 or may mean a
tendency of not capturing dirt on the surface (surface opposite to
the substrate 2) of the polymer layer 3.
[0068] The antifouling film 1 is produced by the following
production method, for example. FIG. 3 includes schematic
cross-sectional views for illustrating a method for producing an
antifouling film of the embodiment.
(Process (1): Application of Polymerizable Composition)
[0069] As shown in FIG. 3(a), a polymerizable composition 5 is
applied to a surface of the substrate 2.
[0070] The polymerizable composition 5 may be applied by, for
example, spraying, gravure coating, slot die coating, or bar
coating. Preferably, the polymerizable composition 5 is applied by
gravure coating or slot die coating in terms of achieving a uniform
thickness and improving the productivity.
[0071] The polymerizable composition 5 contains the components A to
E at the described proportions. When the polymerizable composition
5 further contains a solvent (component other than active
constituents), the production method may include heat treatment
(dry treatment) for removing the solvent after application of the
polymerizable composition 5. The heat treatment is preferably
performed at a temperature not lower than the boiling point of the
solvent.
(Process (2): Formation of Uneven Structure)
[0072] As shown in FIG. 3(b), the substrate 2 is pushed to the die
6 with the polymerizable composition 5 in between. As a result, an
uneven structure is formed on the surface (surface opposite to the
substrate 2) of the polymerizable composition 5.
(Process (3): Curing of Polymerizable Composition)
[0073] The polymerizable composition 5 including an uneven
structure on its surface is cured. As a result, the polymer layer 3
is formed as shown in FIG. 3(c).
[0074] The polymerizable composition 5 may be cured by, for
example, active energy ray irradiation or heating. The
polymerizable composition 5 is cured preferably by active energy
ray irradiation, more preferably by ultraviolet ray irradiation.
Active energy ray irradiation may be performed from the substrate 2
side of the polymerizable composition 5 or the die 6 side of the
polymerizable composition 5. The active energy ray irradiation may
be performed on the polymerizable composition 5 once or multiple
times. Curing the polymerizable composition 5 (Process (3)) may be
simultaneously performed with forming an uneven structure of the
polymerizable composition 5 (Process (2)).
(Process (4): Release of Die)
[0075] As shown in FIG. 3(d), the die 6 is released from the
polymer layer 3. As a result, the antifouling film 1 is
completed.
[0076] In the above production processes, using a rolled substrate
2, for example, enables efficient and sequential performing of the
processes (1) to (4).
[0077] The die 6 may be one produced by the following method.
First, aluminum as a material for the die 6 is formed into a film
on a surface of a supporting substrate by sputtering. Next, the
resulting aluminum layer is repetitively subjected to anodizing and
etching. Thereby, a cavity (die 6) with a moth-eye structure can be
produced. At this time, the uneven structure of the die 6 can be
modified by adjusting the duration of the anodizing and the
duration of the etching.
[0078] Examples of the material for the supporting substrate
include glass; metals such as stainless steel and nickel;
polyolefin resins such as polypropylene, polymethylpentene, cyclic
olefin polymers (typically, "Zeonor.RTM." available from Zeon
Corporation and "Ayton.RTM." available from JSR Corporation, both
of which are a norbornene resin); polycarbonate resins; and other
resins such as polyethylene terephthalate, polyethylene
naphthalate, and triacetyl cellulose. The supporting substrate
provided with an aluminum film on its surface may be replaced by an
aluminum substrate.
[0079] The die 6 may be in a shape of flat plate or roll, for
example.
[0080] The surface of the die 6 has preferably undergone release
treatment. Thereby, the die 6 can be easily released from the
polymer layer 3. Also, the surface free energy of the die 6 is
reduced. Thus, fluorine atoms in the component D can be uniformly
distributed on the surface (surface opposite to the substrate 2) of
the polymerizable composition 5 when the substrate 2 is pushed to
the die 6 in Process (2). Furthermore, this treatment can prevent
early separation of fluorine atoms in the component D from the
surface (surface opposite to the substrate 2) of the polymerizable
composition 5 before curing of the polymerizable composition 5. As
a result, in the antifouling film 1, fluorine atoms in the
component D can be uniformly distributed on the surface (surface
opposite to the substrate 2) of the polymer layer 3.
[0081] Examples of the material used in the release treatment for
the die 6 include fluorine-based materials, silicon-based
materials, and phosphate-based materials. Known examples of the
fluorine-based material include "Optool.RTM. DSX" available from
Daikin Industries, Ltd. and "Optool AES4" available from Daikin
Industries, Ltd.
EXAMPLES AND COMPARATIVE EXAMPLES
[0082] The present invention is described in more detail below
referring to examples and comparative examples. The examples,
however, are not intended to limit the scope of the present
invention.
[0083] The materials used for producing antifouling films in the
examples and comparative examples were as follows.
(Substrate)
[0084] "TAC-TD8OU" available from Fujifilm Corp. was used. The
thickness thereof was 80 .mu.m.
(Polymerizable Composition)
[0085] Polymerizable compositions R1 to R38 with the respective
compositions as shown in Tables 1 to 13 were used. Abbreviations
for the names of the components in the polymerizable compositions
are as follows.
<Urethane Acrylate>
[0086] A1
[0087] "UA-306H" available from Kyoeisha Chemical Co., Ltd.
[0088] Number of functional groups: 6
[0089] Urethane acrylate component (active constituents): 70 wt
%
[0090] Multifunctional acrylate component (active constituents): 30
wt % [0091] A2
[0092] "KUA-9N" available from KSM Co., Ltd.
[0093] Number of functional groups: 9
[0094] Active constituents: 100 wt % [0095] A3
[0096] "KUA-10N" available from KSM Co., Ltd.
[0097] Number of functional groups: 10
[0098] Active constituents: 100 wt % [0099] A4
[0100] "KUA-15N" available from KSM Co., Ltd.
[0101] Number of functional groups: 15
[0102] Active constituents: 100 wt % [0103] A5
[0104] "Ebecryl 4858" available from Daicel-Allnex Ltd.
[0105] Number of functional groups: 2
[0106] Active constituents: 100 wt % [0107] A6
[0108] "Ebecryl 8465" available from Daicel-Allnex Ltd.
[0109] Number of functional groups: 3
[0110] Active constituents: 100 wt % [0111] A7
[0112] "Ebecryl 8210" available from Daicel-Allnex Ltd.
[0113] Number of functional groups: 4
[0114] Active constituents: 100 wt %
<Multifunctional Acrylate>
[0115] B1
[0116] "ATM-35E" available from Shin-Nakamura Chemical Co.,
Ltd.
[0117] Number of functional groups: 4
[0118] Number of ethylene oxide groups: 8.75 for each functional
group
[0119] Active constituents: 100 wt % [0120] B2
[0121] "NK Economer A-PG5027E" available from Shin-Nakamura
Chemical Co., Ltd.
[0122] Number of functional groups: 9
[0123] Number of ethylene oxide groups: 3 for each functional
group
[0124] Active constituents: 100 wt % [0125] B3
[0126] "NK Economer A-PG5054E" available from Shin-Nakamura
Chemical Co., Ltd.
[0127] Number of functional groups: 9
[0128] Number of ethylene oxide groups: 6 for each functional
group
[0129] Active constituents: 100 wt % [0130] B4
[0131] "A-600" available from Shin-Nakamura Chemical Co., Ltd.
[0132] Number of functional groups: 2
[0133] Number of ethylene oxide groups: 7 for each functional
group
[0134] Active constituents: 100 wt % [0135] B5
[0136] "A-TMPT-9E0" available from Shin-Nakamura Chemical Co.,
Ltd.
[0137] Number of functional groups: 3
[0138] Number of ethylene oxide groups: 3 for each functional
group
[0139] Active constituents: 100 wt % [0140] B6
[0141] "AT-30E" available from Shin-Nakamura Chemical Co., Ltd.
[0142] Number of functional groups: 3
[0143] Number of ethylene oxide groups: 10 for each functional
group
[0144] Active constituents: 100 wt % [0145] B7
[0146] "Kayarad.RTM. DPEA-12" available from Nippon Kayaku Co.,
Ltd.
[0147] Number of functional groups: 6
[0148] Number of ethylene oxide groups: 2 for each functional
group
[0149] Active constituents: 100 wt %
<Monofunctional Acrylate>
[0150] C1
[0151] "Viscoat #150" available from Osaka Organic Chemical
Industry Ltd.
[0152] Ethylene oxide group: absent
[0153] Active constituents: 100 wt % [0154] C2
[0155] "ACMO" available from KJ Chemicals Corporation
[0156] Ethylene oxide group: absent
[0157] Active constituents: 100 wt % [0158] C3
[0159] "DMAA" available from KJ Chemicals Corporation
[0160] Ethylene oxide group: absent
[0161] Active constituents: 100 wt % [0162] C4
[0163] "AM-90G" available from Shin-Nakamura Chemical Co., Ltd.
[0164] Ethylene oxide group: present
[0165] Active constituents: 100 wt %
<Release Agent>
[0166] D1
[0167] "Fomblin MT70" available from Solvay
[0168] Perfluoropolyether group: present
[0169] Fluorine atom concentration: 43 wt %
[0170] Active constituents: 80 wt % [0171] D2
[0172] "Fomblin AD1700" available from Solvay
[0173] Perfluoropolyether group: present
[0174] Fluorine atom concentration: 24 wt %
[0175] Active constituents: 70 wt % [0176] D3
[0177] "Fomblin MD700" available from Solvay
[0178] Perfluoropolyether group: present
[0179] Fluorine atom concentration: 52 wt %
[0180] Active constituents: 100 wt % [0181] D4
[0182] "BYK.RTM.-UV3575" available from BYK Additives &
Instruments
[0183] Perfluoropolyether group: absent (silicon-based release
agent)
[0184] Active constituents: 50 wt % [0185] D5
[0186] "X-22-2445" available from Shin-Etsu Chemical Co., Ltd.
[0187] Perfluoropolyether group: absent (silicon-based release
agent)
[0188] Active constituents: 100 wt % [0189] D6
[0190] "TEGO.RTM.Rad 2700" available from Evonik
[0191] Perfluoropolyether group: absent (silicon-based release
agent)
[0192] Active constituents: 100 wt % [0193] D7
[0194] "FM-0711" available from JNC
[0195] Perfluoropolyether group: absent (silicon-based release
agent)
[0196] Active constituents: 100 wt % [0197] D8
[0198] "Cheminox.RTM. FAAC-6" available from Unimatec
Corporation
[0199] Perfluoropolyether group: absent (containing a perfluoro
alkyl group)
[0200] Active constituents: 100 wt % [0201] D9
[0202] "Ftergent.RTM. 601AD" available from Neos Co., Ltd.
[0203] Perfluoropolyether group: absent (containing a perfluoro
alkyl group)
[0204] Active constituents: 25 wt % [0205] D10
[0206] "Megaface.RTM. RS-76-NS" available from DIC Corporation
[0207] Perfluoropolyether group: absent (containing a perfluoro
alkyl group)
[0208] Active constituents: 20 wt %
<Polymerization Initiator>
[0209] E1
[0210] "Lucirin TPO" available from BASF
[0211] Active constituents: 100 wt %
[0212] The "percentage of active constituents" in Tables 1 to 13
represents the proportion of each component (e.g. urethane
acrylate) in the polymerizable composition in terms of active
constituents, i.e., the proportion (unit: wt %) of active
constituents in each component in the entire amount (100 wt %) of
active constituents in the polymerizable composition. In the
polymerizable composition R2, the proportion of the multifunctional
acrylate not belonging to the component B (category: other
component) is 8.1 wt % in terms of active constituents. This is the
percentage of active constituents of the multifunctional acrylate
component contained in the urethane acrylate A1. In the
polymerizable composition R19, the proportion of the
multifunctional acrylate not belonging to the component B
(category: other component) is 5.4 wt % in terms of active
constituents. This is the percentage of active constituents of the
multifunctional acrylate component contained in the urethane
acrylate A1.
TABLE-US-00001 TABLE 1 Polymerizable composition R1 R2 R3
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane acrylate Component A A1
-- 27 27 18.9 -- 27 A2 -- -- 27 A3 27 -- -- A4 -- -- -- Other
component A5 -- 0 -- 0 -- 0 A6 -- -- -- A7 -- -- -- Multifunctional
Component B B1 -- 49 -- 49 -- 49 acrylate B2 -- -- -- B3 49 49 49
Other component B4 -- 0 -- 8.1 -- 0 B5 -- -- -- B6 -- -- -- B7 --
-- -- Monofunctional Component C C1 -- 20 -- 20 -- 20 acrylate C2
-- -- -- C3 20 20 20 Other component C4 -- 0 -- 0 -- 0 Release
agent Component D D1 2.5 2 2.5 2 2.5 2 D2 -- -- -- Other component
D3 -- 0 -- 0 -- 0 D4 -- -- -- D5 -- -- -- D6 -- -- -- D7 -- -- --
D8 -- -- -- D9 -- -- -- D10 -- -- -- Polymerization Component E E1
2 2 2 2 2 2 initiator
TABLE-US-00002 TABLE 2 Polymerizable composition R4 R5 R6
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane Component A A1 -- 27 --
40 -- 27 acrylate A2 -- -- -- A3 -- 40 27 A4 27 -- -- Other
component A5 -- 0 -- 0 -- 0 A6 -- -- -- A7 -- -- -- Multifunctional
Component B B1 -- 49 -- 36 49 49 acrylate B2 -- -- -- B3 49 36 --
Other component B4 -- 0 -- 0 -- 0 B5 -- -- -- B6 -- -- -- B7 -- --
-- Monofunctional Component C C1 -- 20 -- 20 -- 20 acrylate C2 --
-- -- C3 20 20 20 Other component C4 -- 0 -- 0 -- 0 Release agent
Component D D1 2.5 2 2.5 2 2.5 2 D2 -- -- -- Other component D3 --
0 -- 0 -- 0 D4 -- -- -- D5 -- -- -- D6 -- -- -- D7 -- -- -- D8 --
-- -- D9 -- -- -- D10 -- -- -- Polymerization Component E E1 2 2 2
2 2 2 initiator
TABLE-US-00003 TABLE 3 Polymerizable composition R7 R8 R9
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane Component A A1 -- 27 --
17 -- 27 acrylate A2 -- -- -- A3 27 17 27 A4 -- -- -- Other
component A5 -- 0 -- 0 -- 0 A6 -- -- -- A7 -- -- -- Multifunctional
Component B B1 -- 49 -- 59 -- 49 acrylate B2 49 -- -- B3 -- 59 49
Other component B4 -- 0 -- 0 -- 0 B5 -- -- -- B6 -- -- -- B7 -- --
-- Monofunctional Component C C1 -- 20 -- 20 20 20 acrylate C2 --
-- -- C3 20 20 -- Other component C4 -- 0 -- 0 -- 0 Release agent
Component D D1 2.5 2 2.5 2 2.5 2 D2 -- -- -- Other component D3 --
0 -- 0 -- 0 D4 -- -- -- D5 -- -- -- D6 -- -- -- D7 -- -- -- D8 --
-- -- D9 -- -- -- D10 -- -- -- Polymerization Component E E1 2 2 2
2 2 2 initiator
TABLE-US-00004 TABLE 4 Polymerizable composition R10 R11 R12
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane Component A A1 -- 27 --
30 -- 25 acrylate A2 -- -- -- A3 27 30 25 A4 -- -- -- Other
component A5 -- 0 -- 0 -- 0 A6 -- -- -- A7 -- -- -- Multifunctional
Component B B1 -- 49 -- 50 -- 42 acrylate B2 -- -- -- B3 49 50 42
Other component B4 -- 0 -- 0 -- 0 B5 -- -- -- B6 -- -- -- B7 -- --
-- Monofunctional Component C C1 -- 20 -- 16 -- 29 acrylate C2 20
-- -- C3 -- 16 29 Other component C4 -- 0 -- 0 -- 0 Release agent
Component D D1 2.5 2 2.5 2 2.5 2 D2 -- -- -- Other component D3 --
0 -- 0 -- 0 D4 -- -- -- D5 -- -- -- D6 -- -- -- D7 -- -- -- D8 --
-- -- D9 -- -- -- D10 -- -- -- Polymerization Component E E1 2 2 2
2 2 2 initiator
TABLE-US-00005 TABLE 5 Polymerizable composition R13 R14 R15
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane acrylate Component A A1
-- 27 -- 27 -- 25 A2 -- -- -- A3 27 27 25 A4 -- -- -- Other
component A5 -- 0 -- 0 -- 0 A6 -- -- -- A7 -- -- -- Multifunctional
Component B B1 -- 49 -- 49 -- 43 acrylate B2 -- -- -- B3 49 49 43
Other component B4 -- 0 -- 0 -- 0 B5 -- -- -- B6 -- -- -- B7 -- --
-- Monofunctional Component C C1 -- 20 -- 21.5 -- 20 acrylate C2 --
-- -- C3 20 21.5 20 Other component C4 -- 0 -- 0 -- 0 Release agent
Component D D1 -- 2 0.625 0.5 12.5 10 D2 2.86 -- -- Other component
D3 -- 0 -- 0 -- 0 D4 -- -- -- D5 -- -- -- D6 -- -- -- D7 -- -- --
D8 -- -- -- D9 -- -- -- D10 -- -- -- Polymerization Component E E1
2 2 2 2 2 2 initiator
TABLE-US-00006 TABLE 6 Polymerizable composition R16 R17 R18
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane Component A A1 -- 0 -- 0
-- 0 acrylate A2 -- -- -- A3 -- -- -- A4 -- -- -- Other component
A5 27 27 -- 27 -- 27 A6 -- 27 -- A7 -- -- 27 Multifunctional
Component B B1 -- 49 -- 49 -- 49 acrylate B2 -- -- -- B3 49 49 49
Other component B4 -- 0 -- 0 -- 0 B5 -- -- -- B6 -- -- -- B7 -- --
-- Monofunctional Component C C1 -- 20 -- 20 -- 20 acrylate C2 --
-- -- C3 20 20 20 Other component C4 -- 0 -- 0 -- 0 Release agent
Component D D1 2.5 2 2.5 2 2.5 2 D2 -- -- -- Other component D3 --
0 -- 0 -- 0 D4 -- -- -- D5 -- -- -- D6 -- -- -- D7 -- -- -- D8 --
-- -- D9 -- -- -- D10 -- -- -- Polymerization Component E E1 2 2 2
2 2 2 initiator
TABLE-US-00007 TABLE 7 Polymerizable composition R19 R20 R21
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane Component A A1 18 12.6 --
42 -- 27 acrylate A2 -- -- -- A3 -- 42 27 A4 -- -- -- Other
component A5 -- 0 -- 0 -- 0 A6 -- -- -- A7 -- -- -- Multifunctional
Component B B1 -- 58 -- 34 -- 0 acrylate B2 -- -- -- B3 58 34 --
Other component B4 -- 5.4 -- 0 49 49 B5 -- -- -- B6 -- -- -- B7 --
-- -- Monofunctional Component C C1 -- 20 -- 20 -- 20 acrylate C2
-- -- -- C3 20 20 20 Other component C4 -- 0 -- 0 -- 0 Release
agent Component D D1 2.5 2 2.5 2 2.5 2 D2 -- -- -- Other component
D3 -- 0 -- 0 -- 0 D4 -- -- -- D5 -- -- -- D6 -- -- -- D7 -- -- --
D8 -- -- -- D9 -- -- -- D10 -- -- -- Polymerization Component E E1
2 2 2 2 2 2 initiator
TABLE-US-00008 TABLE 8 Polymerizable composition R22 R23 R24
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane Component A A1 -- 27 --
27 -- 27 acrylate A2 -- -- -- A3 27 27 27 A4 -- -- -- Other
component A5 -- 0 -- 0 -- 0 A6 -- -- -- A7 -- -- -- Multifunctional
Component B B1 -- 0 -- 0 -- 0 acrylate B2 -- -- -- B3 -- -- --
Other component B4 -- 49 -- 49 -- 49 B5 49 -- -- B6 -- 49 -- B7 --
-- 49 Monofunctional Component C C1 -- 20 -- 20 -- 20 acrylate C2
-- -- -- C3 20 20 20 Other component C4 -- 0 -- 0 -- 0 Release
agent Component D D1 2.5 2 2.5 2 2.5 2 D2 -- -- -- Other component
D3 -- 0 -- 0 -- 0 D4 -- -- -- D5 -- -- -- D6 -- -- -- D7 -- -- --
D8 -- -- -- D9 -- -- -- D10 -- -- -- Polymerization Component E E1
2 2 2 2 2 2 initiator
TABLE-US-00009 TABLE 9 Polymerizable composition R25 R26 R27
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane Component A A1 -- 14 --
27 -- 32 acrylate A2 -- -- -- A3 14 27 32 A4 -- -- -- Other
component A5 -- 0 -- 0 -- 0 A6 -- -- -- A7 -- -- -- Multifunctional
Component B B1 -- 62 -- 49 -- 50 acrylate B2 -- -- -- B3 62 49 50
Other component B4 -- 0 -- 0 -- 0 B5 -- -- -- B6 -- -- -- B7 -- --
-- Monofunctional Component C C1 -- 20 -- 0 -- 14 acrylate C2 -- --
-- C3 20 -- 14 Other component C4 -- 0 20 20 -- 0 Release agent
Component D D1 2.5 2 2.5 2 2.5 2 D2 -- -- -- Other component D3 --
0 -- 0 -- 0 D4 -- -- -- D5 -- -- -- D6 -- -- -- D7 -- -- -- D8 --
-- -- D9 -- -- -- D10 -- -- -- Polymerization Component E E1 2 2 2
2 2 2 initiator
TABLE-US-00010 TABLE 10 Polymerizable composition R28 R29 R30
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane Component A A1 -- 24 --
27 -- 27 acrylate A2 -- -- -- A3 24 27 27 A4 -- -- -- Other
component A5 -- 0 -- 0 -- 0 A6 -- -- -- A7 -- -- -- Multifunctional
Component B B1 -- 40 -- 49 -- 49 acrylate B2 -- -- -- B3 40 49 49
Other component B4 -- 0 -- 0 -- 0 B5 -- -- -- B6 -- -- -- B7 -- --
-- Monofunctional Component C C1 -- 32 -- 20 -- 22 acrylate C2 --
-- -- C3 32 20 22 Other component C4 -- 0 -- 0 -- 0 Release agent
Component D D1 2.5 2 -- 0 -- 0 D2 -- -- -- Other component D3 -- 0
2 2 -- 0 D4 -- -- -- D5 -- -- -- D6 -- -- -- D7 -- -- -- D8 -- --
-- D9 -- -- -- D10 -- -- -- Polymerization Component E E1 2 2 2 2 2
2 initiator
TABLE-US-00011 TABLE 11 Polymerizable composition R31 R32 R33
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane Component A A1 -- 25 --
27 -- 27 acrylate A2 -- -- -- A3 25 27 27 A4 -- -- -- Other
component A5 -- 0 -- 0 -- 0 A6 -- -- -- A7 -- -- -- Multifunctional
Component B B1 -- 41 -- 49 -- 49 acrylate B2 -- -- -- B3 41 49 49
Other component B4 -- 0 -- 0 -- 0 B5 -- -- -- B6 -- -- -- B7 -- --
-- Monofunctional Component C C1 -- 20 -- 20 -- 20 acrylate C2 --
-- -- C3 20 20 20 Other component C4 -- 0 -- 0 -- 0 Release agent
Component D D1 15 12 -- 0 -- 0 D2 -- -- -- Other component D3 -- 0
-- 2 -- 2 D4 -- 4 -- D5 -- -- 2 D6 -- -- -- D7 -- -- -- D8 -- -- --
D9 -- -- -- D10 -- -- -- Polymerization Component E E1 2 2 2 2 2 2
initiator
TABLE-US-00012 TABLE 12 Polymerizable composition R34 R35 R36
Percentage Percentage Percentage Amount of active Amount of active
Amount of active (parts by constituents (parts by constituents
(parts by constituents Component Category Abbreviation weight) (wt
%) weight) (wt %) weight) (wt %) Urethane Component A A1 -- 27 --
27 -- 27 acrylate A2 -- -- -- A3 27 27 27 A4 -- -- -- Other
component A5 -- 0 -- 0 -- 0 A6 -- -- -- A7 -- -- -- Multifunctional
Component B B1 -- 49 -- 49 -- 49 acrylate B2 -- -- -- B3 49 49 49
Other component B4 -- 0 -- 0 -- 0 B5 -- -- -- B6 -- -- -- B7 -- --
-- Monofunctional Component C C1 -- 20 -- 20 -- 20 acrylate C2 --
-- -- C3 20 20 20 Other component C4 -- 0 -- 0 -- 0 Release agent
Component D D1 -- 0 -- 0 -- 0 D2 -- -- -- Other component D3 -- 2
-- 2 -- 2 D4 -- -- -- D5 -- -- -- D6 2 -- -- D7 -- 2 -- D8 -- -- 2
D9 -- -- -- D10 -- -- -- Polymerization Component E E1 2 2 2 2 2 2
initiator
TABLE-US-00013 TABLE 13 Polymerizable composition R37 R38
Percentage Percentage Amount of active Amount of active (parts by
constituents (parts by constituents Component Category Abbreviation
weight) (wt %) weight) (wt %) Urethane Component A A1 -- 27 -- 27
acrylate A2 -- -- A3 27 27 A4 -- -- Other component A5 -- 0 -- 0 A6
-- -- A7 -- -- Multifunctional Component B B1 -- 49 -- 49 acrylate
B2 -- -- B3 49 49 Other component B4 -- 0 -- 0 B5 -- -- B6 -- -- B7
-- -- Monofunctional Component C C1 -- 20 -- 20 acrylate C2 -- --
C3 20 20 Other component C4 -- 0 -- 0 Release agent Component D D1
-- 0 -- 0 D2 -- -- Other component D3 -- 2 -- 2 D4 -- -- D5 -- --
D6 -- -- D7 -- -- D8 -- -- D9 8 -- D10 -- 10 Polymerization
Component E E1 2 2 2 2 initiator
(Die)
[0213] A die produced by the following method was used. First, a
film of aluminum as a material for the die was formed on a 10-cm
square glass substrate by sputtering. The resulting aluminum layer
had a thickness of 1.0 .mu.m. Next, the resulting aluminum layer
was repetitively subjected to anodizing and etching. Thereby, an
anodizing layer was formed with many fine pores (distance between
the bottom points of adjacent pores (recesses) was not longer than
the wavelength of visible light). Specifically, anodizing, etching,
anodizing, etching, anodizing, etching, anodizing, etching, and
anodizing were performed successively (anodizing: 5 times, etching:
4 times), so that many fine pores (recesses) were formed each
tapering toward the inside of the aluminum layer (a tapered shape).
As a result, a die having an uneven structure was obtained. The
anodizing was performed using oxalic acid (concentration: 0.03 wt
%) at a liquid temperature of 5.degree. C. and an applied voltage
of 80 V. The duration of a single anodizing process was 25 seconds.
The etching was performed using phosphoric acid (concentration: 1
mol/l) at a liquid temperature of 30.degree. C. The duration of a
single etching process was 25 minutes. The die was subjected to
scanning electron microscopic observation to be found to have a
recess depth of 290 nm. The surface of the die had undergone
release treatment with "Optool AES4" available from Daikin
Industries, Ltd.
Example 1
[0214] An antifouling film of Example 1 was produced by the
following production method.
(Process (1): Application of Polymerizable Composition)
[0215] The polymerizable composition R1 was dropped on (applied to)
a surface of the substrate 2 in a stripe pattern. The polymerizable
composition R1 was spread on the whole surface of the substrate 2
with a bar coater. The resulting workpiece, having the
polymerizable composition R1 applied to the surface of the
substrate 2, was put into an oven and heated at a temperature of
80.degree. C. for one minute, whereby the solvent was volatilized
from the polymerizable composition R1.
(Process (2): Formation of Uneven Structure)
[0216] The substrate 2 was pushed to the die 6 using a hand roller
with the polymerizable composition R1 (after solvent
volatilization) in between. As a result, an uneven structure was
formed on the surface (surface opposite to the substrate 2) of the
polymerizable composition R1.
(Process (3): Curing of Polymerizable Composition)
[0217] The polymerizable composition R1 having an uneven structure
on its surface was irradiated with ultraviolet rays (irradiation
dose: 200 mJ/cm.sup.2) from the substrate 2 side to be cured. As a
result, the polymer layer 3 was formed.
(Process (4): Release of Die)
[0218] The die 6 was released from the polymer layer 3. Thereby,
the antifouling film 1 was completed. The thickness T of the
polymer layer 3 was 9.8 .mu.m.
[0219] The surface specifications of the antifouling film 1 were as
follows.
[0220] Shape of projections 4: temple-bell-like shape
[0221] Average pitch of projections 4: 200 nm
[0222] Average height of projections 4: 200 nm
[0223] Average aspect ratio of projections 4: 1.0
[0224] The surface specifications of the antifouling film 1 were
evaluated using a scanning electron microscope "S-4700" (Hitachi
High-Technologies Corp.). For the evaluation, osmium(VIII) oxide
available from Wako Pure Chemical Industries, Ltd. was applied
(thickness: 5 nm) to the surface (surface opposite to the substrate
2) of the polymer layer 3 using an osmium coater "Neoc-ST"
available from Meiwafosis Co., Ltd.
Examples 2 to 15 and Comparative Examples 1 to 23
[0225] An antifouling film of each example/comparative example was
produced as in Example 1 except that the composition of the
polymerizable composition was changed as shown in Tables 14 to
21.
[Evaluation]
[0226] The antifouling film of each example/comparative example was
subjected to the following evaluations. The results are shown in
Tables 14 to 21.
(Transparency of Polymerizable Composition)
[0227] The polymerizable composition (before heat treatment) used
in each example/comparative example was charged in a transparent
test tube and the state thereof was visually observed at an
illuminance of 100 lx (under a fluorescent lamp). Evaluation
criteria were as follows.
[0228] Good: The composition was transparent or very slightly white
turbid.
[0229] Fair: The composition was slightly white turbid but no
sediment was observed after one day leaving.
[0230] Poor: The composition was white turbid and sediment was
observed after one day leaving.
[0231] Higher transparency of the polymerizable composition was
evaluated to show higher compatibility of the release agent in the
polymerizable composition.
(Antifouling Performance)
[0232] Antifouling performance was evaluated in view of water
repellency, oil repellency, and fingerprint wiping performance.
[0233] Water repellency was evaluated from the contact angle of
water on the surface of the antifouling film of each
example/comparative example. Specifically, water was dropped on the
surface (surface opposite to the substrate) of the polymer layer of
the antifouling film of each example/comparative example, and the
contact angle immediately after the dropping was measured.
[0234] Oil repellency was evaluated from the contact angle of
hexadecane on the surface of the antifouling film of each
example/comparative example. Specifically, hexadecane was dropped
on the surface (surface opposite to the substrate) of the polymer
layer of the antifouling film of each example/comparative example,
and the contact angle immediately after the dropping was
measured.
[0235] The contact angle was determined by averaging contact angles
at the following three spots measured with a portable contact angle
meter "PCA-1" available from Kyowa Interface Science Co., Ltd.
using the .theta./2 method (.theta./2=arctan(h/r), .theta.: contact
angle, r: radius of droplet, h: height of droplet). A first
measurement spot was a center portion of the antifouling film of
each example/comparative example. Second and third measurement
spots were two spots that were each 20 mm or more away from the
first measurement spot and were spots symmetrical with each other
with respect to the first measurement spot.
[0236] Fingerprint wiping performance was determined by the
following method. A black acrylic plate was attached to the
antifouling film of each example/comparative example on the surface
opposite to the polymer layer of the substrate via an optical
adhesive layer. Then, fingerprints were made on the surface
(surface opposite to the substrate) of the polymer layer of the
antifouling film of each example/comparative example. The
fingerprints were then reciprocally rubbed 10 times with
"Bemcot.RTM. S-2" available from Asahi Kasei Corp. Whether the
fingerprints had been wiped off or not was visually observed at an
illuminance of 100 lx (under a fluorescent lamp). Evaluation
criteria were as follows.
[0237] Good: The fingerprints were completely wiped off and no
wiping residue was observed.
[0238] Fair: The fingerprints were not obvious, but slight wiping
residue was observed when the light from a fluorescent lamp was
reflected on the surface.
[0239] Poor: The fingerprints were not wiped off at all.
[0240] The case of good or fair was evaluated as allowable (having
excellent fingerprint wiping performance).
(Adhesiveness)
[0241] Adhesiveness was determined by the following method. The
surface (surface opposite to the substrate) of the polymer layer of
the antifouling film of each example/comparative example was cut
with a utility knife so as to have a grid pattern of 11 vertical
linear cuts and 11 horizontal linear cuts at an interval of 1 mm,
whereby 100 squares (1-mm squares) were marked on the surface.
Then, a polyester pressure-sensitive adhesive tape "No. 31B"
available from Nitto Denko Corporation was attached to the squares
with pressure. The pressure-sensitive adhesive tape was peeled at a
speed of 100 mm/s in the direction of 90.degree. with respect to
the surfaces of the squares. The peeled state of the polymer layer
on the substrate was visually observed. The number "M" (unit:
piece) of squares of the polymer layer remaining on the substrate
was counted. Evaluation criteria were as follows.
[0242] Good: M=100
[0243] Fair: M=95 to 99
[0244] Poor: M=0 to 94
[0245] The case of good or fair was evaluated as allowable (having
excellent adhesiveness).
(Rubbing Resistance)
[0246] Rubbing resistance was evaluated in view of smoothness and
steel wool resistance.
[0247] Smoothness was evaluated from the coefficient of dynamic
friction of the surface of the antifouling film of each
example/comparative example. Specifically, the antifouling film of
each example/comparative example was fixed on a stage of a surface
property tester "Heidon.RTM.-14FW" available from Shinto Scientific
Co., Ltd. and the horizontal state was confirmed. The surface
(surface opposite to the substrate) of the polymer layer of the
antifouling film of each example/comparative example was rubbed for
a 20-mm distance with a probe placed on the surface with a load of
400 g. Then, a stable part of the obtained chart was extracted and
the coefficient of dynamic friction was calculated.
[0248] Steel wool resistance was evaluated by the following method.
The surface (surface opposite to the substrate) of the polymer
layer of the antifouling film of each example/comparative example
was rubbed with a steel wool "#0000" available from Nihon Steel
Wool Co., Ltd. with a load of 400 g. The surface (surface opposite
to the substrate) of the polymer layer of the antifouling film of
each example/comparative example was visually observed at an
illuminance of 100 lx (under a fluorescent lamp) and the number "N"
of scratches was counted. The steel wool rubbing was performed with
a surface property tester "Heidon-14FW" available from Shinto
Scientific Co., Ltd. as a tester at a stroke width of 30 mm and a
speed of 100 mm/s, and the surface was reciprocally rubbed 10
times. Evaluation criteria were as follows.
[0249] Excellent: N=0
[0250] Good: N=1 to 3
[0251] Fair: N=4 to 10
[0252] Poor: N=11 to 20
[0253] Bad: N.gtoreq.21
[0254] The case of excellent, good, or fair was evaluated as
allowable (having excellent steel wool resistance).
(Reliability)
[0255] Reliability was evaluated from the bleed out state of the
antifouling film of each example/comparative example. Specifically,
the antifouling film of each example/comparative example was
subjected to a high temperature/high humidity test at a temperature
of 60.degree. C., a humidity of 95%, and leaving time of 1000
hours. The polymer layer of the antifouling film of each
example/comparative example was visually observed at an illuminance
of 100 lx (under a fluorescent lamp) for confirming the state of
white turbidity. Through the visual observation, a polymer layer
without white turbidity was determined to have no bleed out and
evaluated as having good reliability. In contrast, a polymer layer
with white turbidity was determined to have bleed out and evaluated
as having poor reliability. When evaluation through the visual
observation was difficult, the reliability was evaluated from
presence or absence of difference between superimposed specular
reflection spectra of light incident at an angle of 5.degree.
measured before and after the high temperature/high humidity test.
Specifically, the reflectances of the spectra were compared before
and after the high temperature/high humidity test. The case with
absence of difference between the reflectances was evaluated as
having good reliability while the case with presence of difference
between the reflectances (in the case where the reflectance
entirely increased after the high temperature/high humidity test)
was evaluated as having poor reliability. A specular reflection
spectrum of light incident at an angle of 5.degree. was measured as
follows. A black acrylic plate was attached to the antifouling film
of each example/comparative example on the surface opposite to the
polymer layer of the substrate. The surface (surface opposite to
the substrate) of the polymer layer of the antifouling film of each
example/comparative example was irradiated using a light source
from an azimuth at a polar angle of 5.degree.. Then, the specular
reflection spectrum in a wavelength range from 380 to 780 nm was
measured with a spectrophotometer "UV-3100PC" available from
Shimadzu Corporation.
TABLE-US-00014 TABLE 14 Example 1 Example 2 Example 3 Example 4
Example 5 Polymerizable composition R1 R2 R3 R4 R5 Transparency of
polymerizable composition Good Good Good Good Good Antifouling
Water Contact angle of water 155 153 156 157 157 performance
repellency (.degree.) Oil Contact angle of hexadecane 85 84 86 85
86 repellency (.degree.) Fingerprints wiping performance Good Good
Good Good Good Adhesiveness Good Good Good Good Good Rubbing
Smoothness Coefficient of dynamic friction 1.2 1.3 1.2 1.2 1.4
resistance Steel wool resistance Excellent Fair Good Excellent Fair
Reliability Good Good Good Good Good
TABLE-US-00015 TABLE 15 Example 6 Example 7 Example 8 Example 9
Example 10 Polymerizable composition R6 R7 R8 R9 R10 Transparency
of polymerizable composition Good Good Good Good Good Antifouling
Water Contact angle of water 159 154 159 155 156 performance
repellency (.degree.) Oil Contact angle of hexadecane 88 83 89 84
87 repellency (.degree.) Fingerprints wiping performance Good Good
Good Good Good Adhesiveness Good Good Good Fair Good Rubbing
Smoothness Coefficient of dynamic friction 1.1 1.5 1.1 1.5 1.3
resistance Steel wool resistance Fair Fair Good Excellent Excellent
Reliability Good Good Good Good Good
TABLE-US-00016 TABLE 16 Example 11 Example 12 Example 13 Example 14
Example 15 Polymerizable composition R11 R12 R13 R14 R15
Transparency of polymerizable composition Fair Good Good Good Fair
Antifouling Water Contact angle of water 154 153 141 134 160
performance repellency (.degree.) Oil Contact angle of hexadecane
80 83 65 38 90 repellency (.degree.) Fingerprints wiping
performance Good Good Fair Fair Good Adhesiveness Fair Good Good
Good Good Rubbing Smoothness Coefficient of dynamic friction 1.5
1.4 1.8 1.9 0.9 resistance Steel wool resistance Excellent Fair
Good Fair Fair Reliability Good Good Good Good Good
TABLE-US-00017 TABLE 17 Comparative Comparative Comparative
Comparative Comparative Example 1 Example 2 Example 3 Example 4
Example 5 Polymerizable composition R16 R17 R18 R19 R20
Transparency of polymerizable composition Good Good Good Good Good
Antifouling Water Contact angle of water 154 155 153 155 150
performance repellency (.degree.) Oil Contact angle of hexadecane
84 86 85 87 78 repellency (.degree.) Fingerprints wiping
performance Good Good Good Good Good Adhesiveness Good Good Good
Fair Good Rubbing Smoothness Coefficient of dynamic friction 1.4
1.5 1.6 1.2 1.7 resistance Steel wool resistance Poor Poor Poor
Poor Poor Reliability Good Good Good Good Good
TABLE-US-00018 TABLE 18 Comparative Comparative Comparative
Comparative Comparative Example 6 Example 7 Example 8 Example 9
Example 10 Polymerizable composition R21 R22 R23 R24 R25
Transparency of polymerizable composition Good Good Good Good Good
Antifouling Water Contact angle of water 155 156 154 155 158
performance repellency (.degree.) Oil Contact angle of hexadecane
84 82 80 82 85 repellency (.degree.) Fingerprints wiping
performance Good Good Good Good Good Adhesiveness Good Good Good
Good Fair Rubbing Smoothness Coefficient of dynamic friction 1.4
1.5 1.6 1.7 1.3 resistance Steel wool resistance Poor Poor Poor
Poor Bad Reliability Good Good Good Good Good
TABLE-US-00019 TABLE 19 Comparative Comparative Comparative
Comparative Comparative Example 11 Example 12 Example 13 Example 14
Example 15 Polymerizable composition R26 R27 R28 R29 R30
Transparency of polymerizable composition Poor Fair Good Poor Good
Antifouling Water Contact angle of water 124 140 153 98 18
performance repellency (.degree.) Oil Contact angle of hexadecane
24 58 87 21 8 repellency (.degree.) Fingerprints wiping performance
Poor Good Good Poor Poor Adhesiveness Poor Poor Good Good Good
Rubbing Smoothness Coefficient of dynamic friction 1.3 1.8 1.3 2.4
3.3 resistance Steel wool resistance Poor Good Poor Poor Bad
Reliability Good Good Good Poor Good
TABLE-US-00020 TABLE 20 Comparative Comparative Comparative
Comparative Comparative Example 16 Example 17 Example 18 Example 19
Example 20 Polymerizable composition R31 R32 R33 R34 R35
Transparency of polymerizable composition Fair Good Poor Poor Poor
Antifouling Water Contact angle of water 160 80 27 25 29
performance repellency (.degree.) Oil Contact angle of hexadecane
92 18 13 15 14 repellency (.degree.) Fingerprints wiping
performance Good Poor Poor Poor Poor Adhesiveness Good Good Good
Good Good Rubbing Smoothness Coefficient of dynamic friction 0.8
1.1 3.0 2.8 2.8 resistance Steel wool resistance Poor Excellent Bad
Bad Bad Reliability Poor Good Poor Poor Poor
TABLE-US-00021 TABLE 21 Comparative Comparative Comparative Example
21 Example 22 Example 23 Polymerizable composition R36 R37 R38
Transparency of polymerizable composition Good Good Good
Antifouling Water Contact angle of water 104 114 117 performance
repellency (.degree.) Oil Contact angle of hexadecane 33 37 36
repellency (.degree.) Fingerprints wiping performance Fair Fair
Fair Adhesiveness Good Good Good Rubbing Smoothness Coefficient of
dynamic friction 2.5 2.6 2.5 resistance Steel wool resistance Poor
Poor Poor Reliability Good Good Good
[0256] As shown in Tables 14 to 16, the films of Examples 1 to 15
were each excellent in all of antifouling performance,
adhesiveness, rubbing resistance, and reliability. Meanwhile, as
shown in Tables 17 to 21, the films of Comparative Examples 1 to 23
were each insufficient in at least one selected from the group
consisting of antifouling performance, adhesiveness, rubbing
resistance, and reliability.
[0257] The film of Comparative Example 1, which contained the
urethane acrylate A5 containing less than six functional groups in
the polymerizable composition R16, had insufficient rubbing
resistance (steel wool resistance).
[0258] The film of Comparative Example 2, which contained the
urethane acrylate A6 containing less than six functional groups in
the polymerizable composition R17, had insufficient rubbing
resistance (steel wool resistance).
[0259] The film of Comparative Example 3, which contained the
urethane acrylate A7 containing less than six functional groups in
the polymerizable composition R18, had insufficient rubbing
resistance (steel wool resistance).
[0260] The film of Comparative Example 4, which contained, in the
polymerizable composition R19, less than 15 wt % of the proportion
of a urethane acrylate component derived from the urethane acrylate
A1 in terms of active constituents, had insufficient rubbing
resistance (steel wool resistance).
[0261] The film of Comparative Example 5, which contained, in the
polymerizable composition R20, more than 40 wt % of the proportion
of the urethane acrylate A3 in terms of active constituents and
less than 35 wt % of the proportion of the multifunctional acrylate
B3 in terms of active constituents, had insufficient rubbing
resistance (steel wool resistance).
[0262] The film of Comparative Example 6, which contained the
multifunctional acrylate B4 containing less than four functional
groups in the polymerizable composition R21, had insufficient
rubbing resistance (steel wool resistance).
[0263] The film of Comparative Example 7, which contained the
multifunctional acrylate B5 containing less than four functional
groups in the polymerizable composition R22, had insufficient
rubbing resistance (steel wool resistance).
[0264] The film of Comparative Example 8, which contained the
multifunctional acrylate B6 containing less than four functional
groups in the polymerizable composition R23, had insufficient
rubbing resistance (steel wool resistance).
[0265] The film of Comparative Example 9, which contained the
multifunctional acrylate B7 containing less than three ethylene
oxide groups for each functional group in the polymerizable
composition R24, had insufficient rubbing resistance (steel wool
resistance).
[0266] The film of Comparative Example 10, which contained, in the
polymerizable composition R25, less than 15 wt % of the proportion
of the urethane acrylate A3 in terms of active constituents and
more than 60 wt % of the proportion of the multifunctional acrylate
B3 in terms of active constituents, had insufficient rubbing
resistance (steel wool resistance).
[0267] The film of Comparative Example 11, which contained the
monofunctional acrylate C4 with an ethylene oxide group in the
polymerizable composition R26 and thereby had a low compatibility
with other components, had insufficient transparency of the
polymerizable composition R26. The antifouling performance,
adhesiveness, and rubbing resistance (steel wool resistance) were
also insufficient.
[0268] The film of Comparative Example 12, which contained, in the
polymerizable composition R27, less than 15 wt % of the proportion
of the monofunctional acrylate C3 in terms of active constituents,
had insufficient adhesiveness.
[0269] The film of Comparative Example 13, which contained, in the
polymerizable composition R28, more than 30 wt % of the proportion
of the monofunctional acrylate C3 in terms of active constituents,
had insufficient rubbing resistance (steel wool resistance).
[0270] The film of Comparative Example 14, which had more than 50
wt % of the fluorine atom concentration in the release agent D3 in
the polymerizable composition R29 and thereby had a low
compatibility with other components, had insufficient transparency
of the polymerizable composition R29. The antifouling performance,
rubbing resistance, and reliability were also insufficient.
[0271] The film of Comparative Example 15, which contained no
fluorine release agent (Component D) in the polymerizable
composition R30, had insufficient antifouling performance and
insufficient rubbing resistance.
[0272] The film in Comparative Example 16, which contained, in the
polymerizable composition R31, more than 10 wt % of the proportion
of the release agent D1 in terms of active constituents, had
insufficient rubbing resistance (steel wool resistance) and
insufficient reliability.
[0273] The film of Comparative Example 17, which contained a
silicon-based release agent with no perfluoropolyether group as the
release agent D4 in the polymerizable composition R32, had
insufficient antifouling performance.
[0274] The film of Comparative Example 18, which contained a
silicon-based release agent with no perfluoropolyether group as the
release agent D5 in the polymerizable composition R33, was
insufficient in antifouling performance, rubbing resistance, and
reliability. The transparency of the polymerizable composition R33
was also insufficient.
[0275] The film of Comparative Example 19, which contained a
silicon-based release agent with no perfluoropolyether group as the
release agent D6 in the polymerizable composition R34, was
insufficient in antifouling performance, rubbing resistance, and
reliability. The transparency of the polymerizable composition R34
was also insufficient.
[0276] The film of Comparative Example 20, which contained a
silicon-based release agent with no perfluoropolyether group as the
release agent D7 in the polymerizable composition R35, was
insufficient in antifouling performance, rubbing resistance, and
reliability. The transparency of the polymerizable composition R35
was also insufficient.
[0277] The film of Comparative Example 21, which contained a
fluorine release agent with no perfluoropolyether group as the
release agent D8 in the polymerizable composition R36, was
insufficient in antifouling performance (water repellency) and
rubbing resistance.
[0278] The film of Comparative Example 22, which contained a
fluorine release agent with no perfluoropolyether group as the
release agent D9 in the polymerizable composition R37, was
insufficient in antifouling performance (water repellency) and
rubbing resistance.
[0279] The film of Comparative Example 23, which contained a
fluorine release agent with no perfluoropolyether group as the
release agent D10 in the polymerizable composition R38, was
insufficient in antifouling performance (water repellency) and
rubbing resistance.
[Additional Remarks]
[0280] An aspect of the present invention may be an antifouling
film including: a substrate, and a polymer layer disposed on a
surface of the substrate and including on a surface thereof an
uneven structure provided with multiple projections at a pitch not
longer than a wavelength of visible light, the polymer layer being
a cured product of a polymerizable composition, the polymerizable
composition containing, in terms of active constituents, 15 to 40
wt % of an urethane acrylate containing six or more functional
groups, 35 to 60 wt % of a multifunctional acrylate containing four
or more functional groups and 3 to 15 ethylene oxide groups for
each functional group, 15 to 30 wt % of a monofunctional acrylate
with no ethylene oxide group, 0.5 to 10 wt % of a fluorine release
agent containing a perfluoropolyether group and having a fluorine
atom concentration of 50 wt % or lower, and 0.5 to 5 wt % of a
polymerization initiator. This achieves an antifouling film
excellent in all of antifouling performance, adhesiveness, rubbing
resistance, and reliability.
[0281] The polymer layer may include a surface having a coefficient
of dynamic friction of 2.0 or lower. This achieves favorably
improved rubbing resistance.
[0282] The polymer layer may include a surface having a contact
angle of water of 130.degree. or greater and a contact angle of
hexadecane of 30.degree. or greater. This achieves favorably
improved antifouling performance.
[0283] The monofunctional acrylate may include one or both of
N-acryloyl morpholine and N,N-dimethyl acrylamide. This can reduce
the viscosity of the monofunctional acrylate and more improve the
compatibility with the urethane acrylate, the multifunctional
acrylate, and the fluorine release agent. Furthermore, when the
substrate is a triacetyl cellulose film, the adhesiveness is more
improved.
[0284] The polymer layer may have a thickness of 5.0 .mu.m or more
and 20.0 .mu.m or less. This allows fluorine atoms in the fluorine
release agent to be distributed on a surface (surface opposite to
the substrate) of the polymer layer at a higher concentration.
[0285] The multiple projections may have an average pitch of 100 nm
or longer and 400 nm or shorter. This sufficiently prevents
occurrence of optical phenomena such as moire and iridescence.
[0286] The multiple projections may have an average height of 50 nm
or higher and 600 nm or lower. This can satisfy preferred average
aspect ratio of the multiple projections.
[0287] The multiple projections may have an average aspect ratio of
0.8 or more and 1.5 or less. This sufficiently prevents occurrence
of optical phenomena such as moire and iridescence and can achieve
excellent antireflective performance. This also sufficiently
prevents occurrence of sticking and deterioration in transforming
performance in formation of the uneven structure due to
deterioration in processability of the uneven structure.
REFERENCE SIGNS LIST
[0288] 1: Antifouling film [0289] 2: Substrate [0290] 3: Polymer
layer [0291] 4: Projection [0292] 5: Polymerizable composition
[0293] 6: Die [0294] P: Pitch [0295] T: Thickness of polymer
layer
* * * * *