U.S. patent application number 17/078236 was filed with the patent office on 2021-02-11 for electrochemical cell.
The applicant listed for this patent is EaglePicher Technologies, LLC. Invention is credited to David Timothy Andrew Darch, Mario Destephen, Umamaheswari Janakiraman, Jason A. Mudge, Ernest Ndzebet, Dong Zhang.
Application Number | 20210043888 17/078236 |
Document ID | / |
Family ID | 1000005168789 |
Filed Date | 2021-02-11 |
![](/patent/app/20210043888/US20210043888A1-20210211-D00000.png)
![](/patent/app/20210043888/US20210043888A1-20210211-D00001.png)
![](/patent/app/20210043888/US20210043888A1-20210211-D00002.png)
![](/patent/app/20210043888/US20210043888A1-20210211-D00003.png)
![](/patent/app/20210043888/US20210043888A1-20210211-D00004.png)
![](/patent/app/20210043888/US20210043888A1-20210211-D00005.png)
![](/patent/app/20210043888/US20210043888A1-20210211-D00006.png)
![](/patent/app/20210043888/US20210043888A1-20210211-D00007.png)
![](/patent/app/20210043888/US20210043888A1-20210211-D00008.png)
![](/patent/app/20210043888/US20210043888A1-20210211-D00009.png)
![](/patent/app/20210043888/US20210043888A1-20210211-D00010.png)
United States Patent
Application |
20210043888 |
Kind Code |
A1 |
Zhang; Dong ; et
al. |
February 11, 2021 |
ELECTROCHEMICAL CELL
Abstract
An electrochemical cell that converts chemical energy to
electrical energy includes a cathode with an active material of
fluorinated carbon on a perforated metal cathode current collector,
a lithium anode on a perforated metal anode current collector, a
stepped header, a stable electrolyte, and a separator. In various
embodiments, an anode current collector design, a cathode current
collector design, a stepped header design, a cathode formulation,
an electrolyte formulation, a separator, and a battery
incorporating the electrochemical cell are provided.
Inventors: |
Zhang; Dong; (Webb City,
MO) ; Mudge; Jason A.; (Joplin, MO) ; Darch;
David Timothy Andrew; (Neosho, MO) ; Destephen;
Mario; (Joplin, MO) ; Ndzebet; Ernest; (Carl
Junction, MO) ; Janakiraman; Umamaheswari; (Webb
City, MO) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
EaglePicher Technologies, LLC |
St. Louis |
MO |
US |
|
|
Family ID: |
1000005168789 |
Appl. No.: |
17/078236 |
Filed: |
October 23, 2020 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
15924158 |
Mar 16, 2018 |
|
|
|
17078236 |
|
|
|
|
62472522 |
Mar 16, 2017 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
H01M 50/147 20210101;
H01M 2220/30 20130101; H01M 4/5835 20130101; H01M 2004/027
20130101; H01M 4/667 20130101; H01M 50/636 20210101; H01M 50/183
20210101; H01M 4/382 20130101; H01M 4/80 20130101; H01M 6/16
20130101; H01M 2004/028 20130101; H01M 4/623 20130101; H01M 4/663
20130101; H01M 50/172 20210101; H01M 2300/0037 20130101; H01M 6/166
20130101; H01M 4/364 20130101; H01M 4/625 20130101; H01M 4/06
20130101 |
International
Class: |
H01M 2/04 20060101
H01M002/04; H01M 2/08 20060101 H01M002/08; H01M 4/80 20060101
H01M004/80; H01M 4/583 20060101 H01M004/583; H01M 4/62 20060101
H01M004/62; H01M 6/16 20060101 H01M006/16; H01M 4/38 20060101
H01M004/38; H01M 4/36 20060101 H01M004/36; H01M 4/06 20060101
H01M004/06; H01M 2/06 20060101 H01M002/06; H01M 2/36 20060101
H01M002/36 |
Claims
1. An electrolyte for an electrochemical cell, comprising: a
lithium salt; a first solvent; and a second solvent, wherein the
first solvent is 1,2-dimethoxyethane, and wherein the second
solvent is .gamma.-butyrolactone.
2. The electrolyte of claim 1, wherein a weight ratio of the first
solvent to the second solvent is 0.5 to 1.3.
3. The electrolyte of claim 1, wherein a weight ratio of the first
solvent to the second solvent is 1:1.
4. The electrolyte of claim 1, wherein a concentration of the
lithium salt is 0.8 moles per liter to 1.1 moles per liter, based
on a total volume of the first solvent and the second solvent.
5. The electrolyte of claim 1, wherein the lithium salt comprises
LiBF.sub.4, LiAsF.sub.6, LiSbF.sub.6, or LiClO.sub.4, or a
combination thereof.
6. The electrolyte of claim 1, wherein the lithium salt is
LiBF.sub.4, the concentration of the LiBF.sub.4 in the electrolyte
is 1 mole per liter, based on a total volume of the first solvent
and the second solvent, the first solvent is 1,2-dimethoxyethane,
and the second solvent is .gamma.-butyrolactone.
7. An electrochemical cell comprising: a cathode comprising a
cathode composition disposed on a cathode current collector,
wherein the cathode composition comprises a cathode active
material, a conductive carbon filler, and a binder; an anode; and
an electrolyte, wherein the electrolyte comprises comprising a
lithium salt; a first solvent; and a second solvent, wherein the
cathode active material is fluorinated carbon, the conductive
carbon filler is carbon black, the binder is a fluorinated polymer,
and a weight ratio of the cathode active material to the conductive
carbon filler to the binder is 90:6:4, wherein a weight ratio of an
amount of the electrolyte to an amount of the cathode active
material is 0.7 to 1.1, and wherein the electrochemical cell has a
swelling percentage of less than or equal to 2 percent.
8. The electrochemical cell of claim 7, wherein the weight ratio of
the amount of the electrolyte to the amount of the cathode active
material is 0.93.
9. The electrochemical cell of claim 7, wherein a concentration of
the lithium salt in the electrolyte is 0.8 moles per liter to 1.1
moles per liter, based on a total volume of the first solvent and
the second solvent.
10. The electrochemical cell of claim 7, wherein the first solvent
comprises 1,2-dimethoxyethane, 1,2-diethoxyethane,
1-ethoxy,2-methoxyethane, ethyl methyl carbonate, methyl propyl
carbonate, ethyl propyl carbonate, diethyl carbonate, or a
combination thereof, and the second solvent comprises propylene
carbonate, ethylene carbonate, .gamma.-butyrolactone,
N-methyl-pyrrolidinone, or a combination thereof.
11. The electrochemical cell of claim 7, wherein the first solvent
is 1,2-dimethoxyethane and the second solvent is
.gamma.-butyrolactone.
12. The electrochemical cell of claim 7, wherein a weight ratio of
the first solvent to the second solvent is 0.5 to 1.3.
13. The electrochemical cell of claim 7, wherein a weight ratio of
the first solvent to the second solvent is 1:1.
14. The electrochemical cell of claim 7, wherein the lithium salt
comprises LiBF.sub.4, LiAsF.sub.6, LiSbF.sub.6, or LiClO.sub.4, or
a combination thereof.
15. The electrochemical cell of claim 7, wherein the lithium salt
is LiBF.sub.4, the concentration of the LiBF.sub.4 in the
electrolyte is 1 mole per liter, based on a total volume of the
first solvent and the second solvent, the first solvent is
1,2-dimethoxyethane, and the second solvent is
.gamma.-butyrolactone.
16. The electrochemical cell of claim 15, wherein the anode
comprises a lithium metal foil.
17. An implantable device comprising the electrochemical cell of
claim 1.
18. A method of manufacturing the electrochemical cell of claim 12,
the method comprising: providing the cathode; providing the anode,
wherein the anode comprises a lithium metal foil; and disposing the
electrolyte between the anode and the cathode.
19. The method of claim 18, wherein the ratio of the amount of the
electrolyte to the amount of the cathode active material is
0.93.
20. The method of claim 18, wherein the lithium salt is LiBF.sub.4,
the concentration of the LiBF.sub.4 in the electrolyte is 1 mole
per liter based on a total volume of the first solvent and the
second solvent, the first solvent is 1,2-dimethoxyethane, and the
second solvent is .gamma.-butyrolactone.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] The present application is a continuation of U.S.
application Ser. No. 15/924,158, filed on Mar. 16, 2018, which
claims priority to U.S. provisional application No. 62/472,522,
filed on Mar. 16, 2017 under 35 U.S.C. 119(e), the contents of
which are hereby incorporated by reference in their entirety.
BACKGROUND
[0002] The present inventions relate generally to the field of
electrochemical cells. More particularly, the present inventions
relate to lithium/fluorinated carbon (Li/CF.sub.x) electrochemical
cells for use in implantable medical devices.
[0003] Li/CF.sub.x electrochemical cells are known to be used in
multitude of devices including implantable medical devices. These
electrochemical cells are known to swell during discharge. However,
in the design of a medical device, more particularly an implantable
medical device, the swelling may need to be controlled. The control
on swelling may be needed to ensure that enough space is reserved
for the cell volume change in order to prevent damage to the device
circuitry. Consequently, the more swelling the cell experiences,
the more void space may be needed to be reserved in the device,
leading to greater total device volume. The swelling may result in
capacity loss due to lack of electrolyte in contact with some solid
particles (that is, loss of interface between solids and
electrolyte).
[0004] In the art there are references to the minimization or
elimination of swelling in Li/CF.sub.x cells discharged under high
rate applications. When CF.sub.x materials are synthesized from
fibrous carbonaceous materials, in comparison to petroleum coke,
cell swelling may be greatly reduced, and in some cases eliminated.
It is believed that the Li/CF.sub.x cell is known to produce a
cathode swelling that may result in mechanical deformation of the
cell. References in the art report the cathode swelling as a
function of discharge depth, rate, and temperature. A mechanism in
which the discharge product is LiF deposited on the internal
surfaces of the carbon layers left behind after electrochemical
reduction with this deposition leading directly to the measured
cathode swelling is also proposed in the art.
[0005] In view of the foregoing, it is clear that these traditional
techniques are not perfect and leave room for more optimal
approaches. Particularly, in the field of implantable medical
devices, a smaller total device volume may be desired and hence it
may be desirable to minimize the extent of swelling in Li/CF.sub.x
electrochemical cells.
SUMMARY
[0006] In one embodiment, the present invention describes an
electrochemical cell that converts chemical energy to electrical
energy. Particularly, the invention pertains to an electrochemical
cell having a cathode with an active material of fluorinated carbon
on a perforated metal cathode current collector, a lithium anode on
a perforated metal anode current collector, a stepped header, a
stable electrolyte, and a separator. In various embodiments, the
invention provides an anode current collector design, a cathode
current collector design, a stepped header design, a cathode
formulation, an electrolyte formulation, a separator, and a battery
incorporating the electrochemical cell.
[0007] In one embodiment, the swelling of the cell after discharge
to zero volt is less than or equal to about 2 percent.
BRIEF DESCRIPTION OF THE DRAWINGS
[0008] The present invention is illustrated by way of example, and
not by way of limitation, in the figures of the accompanying
drawings and in which like reference numerals refer to similar
elements and in which:
[0009] FIG. 1 illustrates a perspective view of a finished
electrochemical cell, in accordance with an embodiment of the
present invention;
[0010] FIG. 2 illustrates an exploded view of an electrochemical
cell, in accordance with an embodiment of the present
invention;
[0011] FIG. 3 illustrates a cross-sectional view of an
electrochemical cell, in accordance with an embodiment of the
present invention;
[0012] FIG. 4 illustrates a cathode current collector of an
electrochemical cell, in accordance with an embodiment of the
present invention;
[0013] FIG. 5 illustrates an anode current collector of an
electrochemical cell, in accordance with an embodiment of the
present invention;
[0014] FIG. 6 illustrates an exploded view of an anode including an
anode current collector and two lithium foils of an electrochemical
cell, in accordance with an embodiment of the present
invention;
[0015] FIG. 7 illustrates a stepped header of an electrochemical
cell, in accordance with an embodiment of the present
invention;
[0016] FIG. 8 is a graph illustrating a discharge curve of an
Li/CF.sub.x electrochemical cell, constructed in accordance with
embodiments of the present invention;
[0017] FIG. 9 is a graph illustrating deep discharge of an
Li/CF.sub.x an electrochemical cell, constructed in accordance with
embodiments of the present invention; and
[0018] FIG. 10 is a graph illustrating a degree of swelling of
twenty-four Li/CF.sub.x electrochemical cells, constructed in
accordance with embodiments of the present invention.
[0019] Unless otherwise indicated illustrations in the figures are
not necessarily drawn to scale.
DETAILED DESCRIPTION
[0020] The present invention is best understood by reference to the
detailed figures and description set forth herein.
[0021] Embodiments of the invention include a primary lithium-based
electrochemical cell. It may be appreciated that those skilled in
the art will, in light of the teachings of the present invention,
understand that the term "primary" denotes a non-rechargeable
electrochemical cell, in contrast to the term "secondary" which
denotes a rechargeable electrochemical cell. As used herein, a
battery, may consist of one or more of the primary electrochemical
cells. Typically, primary lithium batteries are those having
metallic lithium anode, pairing with various cathodes, including
Li/CF.sub.x, Li/MnO.sub.2, Li/SVO, and Li/Hybrid, where Hybrid is a
mixture of CF.sub.x, and/or MnO.sub.2, and/or SVO.
[0022] During the discharge of such a battery, the oxidation of the
lithium metal to lithium ions takes place at the anode according to
the following reaction:
Li.fwdarw.Li.sup.++e
[0023] The reduction of the oxidizing substance occurs at the
cathode. In the case where the oxidizing agent is CF.sub.x, the
reduction reaction is as follows:
CF.sub.x+e+xLi.sup.+.fwdarw.C+xLiF
[0024] During discharge, the oxidation of the lithium metal to
lithium ions occurs at the anode, and the lithium ions leave anode
surface and migrate into the porous cathode. At the cathode during
discharge, the insertion of lithium into CF.sub.x takes place,
producing insoluble lithium fluoride and graphite (an electronic
conductor).
[0025] For example, a theoretical calculation on electrode
dimension change during discharge may be done in the following
manner. Carbon monofluoride (CF.sub.x) is used as the cathode
active material for the present inventions. The overall discharge
reaction in a Li/CF.sub.x cell is shown in the following equation
I.
xLi+CF.sub.x.fwdarw.C+xLiF (Equation 1)
[0026] Table 1 provided below shows the data for volume expansion
for the cathode, in an exemplary embodiment. Based on the data in
Table 1, for the discharge reaction given in equation (1) with the
molar volume of CF.sub.1.0 at 11.2 cubic centimeter per mole (2.8
grams per cubic centimeter), LiF at 9.8 centimeter per mole (2.65
grams per cubic centimeter), and C at 6.0 centimeter per mole (2.0
grams per cubic centimeter), the volume expansion for the cathode
may be calculated to about 41 percent for a complete discharge. On
the other hand, the Li anode will be completely dissolved by anodic
reaction, as shown in Table 1, and the volume expansion of anode is
about -100 percent (minus 100 percent). Based on the molar volume
of each species in equation (1), if one combines the volume changes
on both cathode side and anode side, the net expansion for the
whole cell (as provided in Table 1) is about -34.7 percent (minus
34.7 percent), assuming the capacity ratio of anode to cathode is
1:1.
TABLE-US-00001 TABLE 1 Theoretical calculation for cell dimension
change during discharge Molar Density Volume Volume Reaction
Species (g/cm.sup.3) (cm.sup.3/mole) Expansion* Cathode CF.sub.1.0
2.8 11.2 41% CF.sub.1.0 .fwdarw. C + LiF C 2.0 6.0 (6.0 + 9.8 -
11.2)/11.2 LiF 2.65 9.8 Anode Li 0.534 13.0 -100% Li .fwdarw.
Li.sup.+ Cell NA NA NA -34.7% CF.sub.1.0 + Li .fwdarw. C + (6.0 +
9.8 - 11.2 - LiF 13.0)/(11.2 + 13.0) *Assuming the capacity ratio
of anode to cathode is 1:1
[0027] One skilled in the art may appreciate that the above
calculation takes into account only the active materials in the
electrochemical cell. It does not consider change in the volume of
cathode binder and cathode conductive filler and change in the gap
between CF.sub.x particles and carbon particles. However, the
negative volume change in the solid phase may create more void
space between solid particles. Therefore, while discharge proceeds
there may be a tendency of lack of electrolyte between the solids
because the electrolyte volume is fixed and is equal to the initial
value at undischarged state if the side reaction for electrolyte
during the discharge is negligible. The above descriptions about
change in the volume of reactants and products imply that the
electrochemical reaction itself may not be the cause of the
swelling of a Li/CF.sub.x cell. Instead, it is the electrochemical
reaction that may lead to a shrinking of a Li/CF.sub.x cell.
Accordingly, in various embodiments, if the factors, such as
selection of cathode active material, optimized cathode and anode
design, optimized value of electrolyte amount, are appropriately
determined, the cell swelling may be minimized.
[0028] Embodiments of the invention are described below with
reference to the Figures, experimental, and detailed description.
However, those skilled in the art will readily appreciate that the
detailed description given herein with respect to these figures and
experimental is for explanatory purposes as the invention extends
beyond these limited embodiments.
[0029] The singular forms "a", "an" and "the" include plural
referents unless the context clearly dictates otherwise.
[0030] The term "optional" or "optionally" means that the
subsequently described event or circumstance may or may not occur,
and that the description includes instances where the event occurs
and instances where it does not.
[0031] In one embodiment is provided, an electrochemical cell. The
electrochemical cell includes a cathode, an anode, a header, and an
electrolyte. The cathode includes a cathode formulation. The
cathode formulation includes a cathode active material, a
conductive carbon filler, and a binder. The cathode formulation is
disposed on a cathode current collector. The anode comprises at
least two lithium metal foils disposed on an anode current
collector. The header includes a stepped header. The header
includes at least two steps, wherein the first step is to fulfill
the ball seal requirements, and the second step is to fulfill the
glass sealing requirements. The electrolyte comprises a lithium
salt in a mixed solvent. The ratio of an amount of electrolyte to
an amount of cathode active material is about 0.7 to about 1.1. The
cell has a swelling percentage of less than or equal to about 2
percent.
[0032] Referring to FIG. 1, a perspective view 100 of a finished
electrochemical cell is illustrated, in accordance with an
embodiment of the present invention. The electrochemical cell
includes an outer casing 110, and a header 112. The header 112
includes a vent location 118, and pins 114 and 116 for external
connection. Internally the pin 114 is connected to the cathode
current collector (not shown in figure) and the pin 116 is
connected to the anode current collector (not shown in figure).
[0033] In one embodiment, the cathode includes a cathode current
collector. It may be appreciated that those skilled in the art
will, in light of the teachings of the present invention, that the
cathode current collector may include any suitable material known
to be used in the art as a cathode current collector. Suitable
materials may include, but are not limited to, stainless steel,
aluminum, and titanium. In an exemplary embodiment, the material
used for the cathode current collector is stainless steel, such as,
for example, SS316, SS316L, SS304.
[0034] In one embodiment, the cathode current collector is
perforated. In an exemplary embodiment, the perforation consists of
large circles and small circles in order to maximize the void area
while maintaining the current collector strength. The maximized
void area is beneficial for enhancing the adhesion between the two
halves of the cathode pellet sandwiching the current collector. The
ratio of number of large circles to small circles is about 4:3.
Alternatively, the void area can take other shapes, such as square,
diamond, rectangular, and triangle. In one embodiment, the diameter
for the large circles may be in a range of about 3.0 millimeter
(mm) to about 2.0 mm. In another embodiment, the diameter for the
large circles may be in a range of about 2.8 mm to about 2.2 mm. In
yet another embodiment, the average diameter for the large circles
may be in a range of about 2.6 mm to about 2.3 mm. In one
embodiment, the average diameter for the large circles is about 2.4
mm. In one embodiment, the diameter for the small circles may be in
a range of about 1.4 mm to about 2.5 mm. In another embodiment, the
diameter for the small circles may be in a range of about 1.6 mm to
about 2.3 mm. In yet another embodiment, the average diameter for
the small circles may be in a range of about 1.8 mm to about 2.1
mm. In one embodiment, the average diameter for the small circles
is about 1.9 mm.
[0035] As shown herein below with reference to FIG. 4, in one
embodiment, the ratio of perforated area to the whole cathode
current collector (excluding the tabbing area) may be in a range of
about 0.40 to about 0.80 In another embodiment, the ratio of
perforated area to the whole cathode current collector (excluding
the tabbing area) may be in a range of about 0.50 to about 0.70 In
yet another embodiment, the ratio of perforated area to the whole
cathode current collector (excluding the tabbing area) may be in a
range of about 0.55 to about 0.65 In one embodiment, the ratio of a
perforated area to a whole area of cathode current collector
(excluding the tabbing area) is about 0.60.
[0036] In one embodiment, the cathode current collector has a
thickness. In one embodiment, the thickness of the cathode current
collector may be in a range of about 0.002 mm to about 0.010 mm. In
another embodiment, the thickness of the cathode current collector
may be in a range of about 0.040 mm to about 0.090 mm. In yet
another embodiment, the thickness of the cathode current collector
may be in a range of about 0.060 mm to about 0.080 mm. In one
embodiment, the thickness of the cathode current collector is about
0.075 mm.
[0037] In one embodiment, the cathode formulation comprises a
cathode active material, at least one conductive carbon filler, and
a binder. In one embodiment, the cathode active material employed
in the cathode formulation includes electrochemically active
fluorinated carbon, i.e., CF.sub.x. In one embodiment, the CF.sub.x
material may be blended with the binder and the conductive carbon
to form a pellet. The pellet may then be disposed onto the cathode
current collector, i.e., the pellet may be pressed onto the cathode
current collector. In one embodiment, the conductive carbon filler
may include carbon black.
[0038] Accordingly, in one embodiment, the cathode active material
comprises fluorinated carbons represented by the formula CF.sub.x,
wherein x is a number between 0.1 and 2.0. The atomic weight of
fluorine is 18.998 and the atomic weight of carbon is 12.011. The
fluorination level of a given CF.sub.x material may be expressed as
a percentage that represents the atomic weight contribution of the
fluorine (18.998.times.) divided by the sum of the atomic weight
contribution of the fluorine (18.998.times.) and the atomic weight
contribution of the carbon (12.011). Thus, for C.sub.1F.sub.1
stoichiometry, the fluorination level would be
18.998/(18.998+12.011)=61.3 percent.
[0039] CF.sub.x is conventionally prepared from the reaction of
fluorine gas with a crystalline or amorphous carbon. Graphite is an
example of a crystalline form of carbon, while petroleum coke, coal
coke, carbon black and activated carbon are examples of amorphous
carbon. The reaction between fluorine and carbon is usually carried
out at temperatures ranging from 300 degrees Celsius to 650 degrees
Celsius in a controlled pressure environment. A variety of CF.sub.x
materials are available from commercial sources, including
materials derived from the fluorination of petroleum coke, carbon
black and graphite.
[0040] Suitable examples of fluorinated carbons that may be used in
forming a cathode as disclosed herein include, but are not limited
to, fluorinated carbons that are based on different carbonaceous
starting materials. For example, a cathode in accordance with the
invention can be formed by a fluorinated petroleum coke. The
fluorinated petroleum coke for use in the present invention is
preferably fully fluorinated to a fluorination level of
approximately 58 to 65 percent, with x value between 0.9 to 1.2.
However, other fluorination levels could potentially also be used.
Advantages of using petroleum coke based CF.sub.x material is that
it is thermally stable in contact with electrolyte in a wide
temperature range of about -40 degrees Celsius to about 70 degrees
Celsius. The petroleum coke based CF.sub.x material is also found
to be chemically stable in contact with electrolyte, leading to
minimal or no side reactions that may generate gas species causing
cell swelling. Suitable examples of the CF.sub.x material include
but are not limited to Carbofluor.RTM. 1000 from Advanced Research
Chemicals (Catoosa Okla.).
[0041] In one embodiment, as mentioned hereinabove, cathodes may
include the usual non-electrochemically active materials, such as
conductive fillers and a binder. In one embodiment, the conductive
filler is carbon black, although graphite or mixtures of carbon
black and graphite may also be used. In one embodiment, the
conductive carbon filler used in the cathode formulation is also
thermally and chemically stable. Suitable examples of the
conductive carbon filler include, but are not limited to, Super
P.RTM.-Li from TIMCAL. Metals such as nickel, aluminum, titanium
and stainless steel in powder form may likewise be used. Suitable
examples of binder include but is not limited to an aqueous
dispersion of a fluorinated resin material, such as a
polytetrafluoroethylene (PTFE) or polyvinylidene fluoride (PVDF).
In one embodiment, the binding material is inert PTFE emulsion. It
may be appreciated that those skilled in the art will, in light of
the teachings of the present invention, that any suitable mixing
ratio of the fluorinated carbon, the conductive filler, and the
binder may be used. In an exemplary embodiment, the cathode may
include, by weight, 90 percent of the fluorinated carbon material,
6.0 percent conductive filler and 4.0 percent binder.
[0042] During fabrication of the CF.sub.x cathode, the fluorinated
carbon material, which comes in powder form, is blended with the
conductive filler. The CF.sub.x and conductive filler are then
combined with the binder by a wet process. The wetted cathode
mixture is intimately blended, filtered and dried, then pressed
into a cathode current collector as illustrated in FIG. 4. The
current collector will assist in forming electrical conducting path
between cathode and cell positive terminal and promote uniform
utilization of the cathode material during discharge.
[0043] In one embodiment, the cathode current collector may be
coated with conductive carbon. The coating is done before pressing
pellet. The conductive carbon coating may help to promote adhesion
between the pellet (cathode formulation) and the cathode current
collector, and to enhance the continuity of electrical conduction
between the cathode current collector and the pellet. In one
embodiment, the conductive carbon material may include, but not be
limited to, graphite with a thermoplastic binder. In one
embodiment, the conductive carbon coating on the cathode current
collector may be obtained by application of a coating material such
as commercially available Dag.RTM. EB-012 by Acheson Colloids
Company. on the cathode current collector surface. Advantages of
using the conductive coating includes reduction of cathode
swelling. In one embodiment, the conductive carbon coating has a
thickness. In one embodiment, the thickness of the conductive
carbon coating may be in a range of about 0.040 . . . millimeter
(mm) to about 0.0120 mm. In another embodiment, the thickness of
the conductive carbon coating may be in a range of about 0.050
millimeter (mm) to about 0.100 mm. In yet another embodiment, the
thickness of the conductive carbon coating may be in a range of
about 0.060 millimeter (mm) to about 0.090 mm. In one embodiment,
the thickness of the conductive carbon coating is about 0.080
mm.
[0044] In various embodiments, advantages of using a perforated
cathode current collector include improved pellet cohesion around
the edges of the perforations. Further the alignment tab, as
described in FIG. 4, features a partially etched cut line which
facilitates consistent pellet pressing while minimizing final tab
length and interference with the tab to the header weld.
[0045] In one embodiment, the anode includes at least one lithium
foil disposed on an anode current collector. It may be appreciated
that those skilled in the art will, in light of the teachings of
the present invention, that the anode current collector may include
any suitable material known to be used in the art as an anode
current collector. Suitable materials may include, but are not
limited to, stainless steel, and copper. In an exemplary
embodiment, the material used for the anode current collector is
stainless steel, such as SS316, SS316L and SS304, as it has a high
strength, high stability toward lithium metal and electrolyte, and
good electric conductivity. In one embodiment, the anode current
collector may include a perforated metal, an expanded metal, a
grid, or a metallic fabric.
[0046] In one embodiment, the perforation consists of a diamond
shape, a circle, an oval, a rectangle, a star, a triangle, and
combinations thereof. In one embodiment, the average size of the
perforation may be in a range of about 0.10 mm to about 0.20 mm. In
another embodiment, the average size of the perforation may be in a
range of about 0.12 mm to about 0.18 mm. In yet another embodiment,
the average size of the perforation may be in a range of about 0.13
mm to about 0.17 mm. In one embodiment, the average size of the
perforation is about 0.15 mm.
[0047] As shown herein below with reference to FIG. 5, in one
embodiment, the percentage of perforated area to the whole anode
current collector (excluding the tabbing area) may be in a range of
about 30 percent to about 90 percent. In another embodiment, the
percentage of perforated area to the whole anode current collector
(excluding the tabbing area) may be in a range of about 40 percent
to about 80 percent. In yet another embodiment, the percentage of
perforated area to the whole anode current collector (excluding the
tabbing area) may be in a range of about 50 percent to about 70
percent. In one embodiment, the percentage of a perforated area to
a whole area of anode current collector (excluding the tabbing
area) is about 60 percent. The advantage of the anode current
collector is that, it may allow uniform utilization of lithium
foils during discharge. At the same time, the perforated anode
current collector may take up only a little amount of volume inside
the cell, allowing maximization of the amount of electrochemically
active components in the cell to generate high energy density.
[0048] In one embodiment, the total surface area of the anode
current collector excluding the central folding and tabbing area is
equal to or a little smaller than the area of the lithium foils. In
one embodiment, the ratio of the surface area of the current
collector (excluding the central folding and tabbing area) to the
area of the lithium foils may be in a range of about 70 percent to
about 100 percent. In another embodiment, the ratio of the surface
area of the current collector (excluding the central folding and
tabbing area) to the area of the lithium foils may be in a range of
about 80 percent to about 100 percent. In yet another embodiment,
the ratio of the surface area of the current collector (excluding
the central folding and tabbing area) to the area of the lithium
foils may be in a range of about 90 percent to about 100 percent.
In one embodiment, the anode current collector has a thickness.
[0049] In one embodiment, the thickness of the anode current
collector may be in a range of about 0.010 mm to about 0.100 mm. In
another embodiment, the thickness of the anode current collector
may be in a range of about 0.020 mm to about 0.070 mm. In yet
another embodiment, the thickness of the anode current collector
may be in a range of about 0.040 mm to about 0.060 mm. In one
embodiment, the thickness of the anode current collector is about
0.050 mm.
[0050] Referring to FIG. 2, an exploded view 200 of an
electrochemical cell is illustrated, in accordance with an
embodiment of the present invention. The view 200 shows a cell
container or casing 210 and a blow-up portion (Detail A 212) of
header 214. The detail A 212 shows the header 214 to include an
opening 217 for receiving a ball seal 218 which may then be sealed
with a fill port cover 216, openings 224 and 226 for connecting a
tab portion 229 of a cathode current collector 228 and a tab
portion 239 of an anode current collector 238 to pin extenders 220
and 222 respectively. In one embodiment, the pin extenders 220 and
22 may be gold plated. The opening 217 may function as a vent in
the cell. The view 200 also shows a cathode current collector 228,
more particularly the tab portion 229 of the cathode current
collector 228, encased in the cathode formulation in the form of a
cathode pellet 230, a cathode separator pouch 232 encasing the
cathode current collector 228 and the cathode pellet 230, two
lithium foils 234, 236, an anode current collector 238 with the tab
portion 239, an anode separator pouch 240, and an insulator pouch
242 that contains and insulates all the parts of the cell from the
outer casing 210. The negative current output terminal i.e., pin
extender 222 of the cell may be connected to the negative terminal
pin, then connected to anode current collector tab portion 239.
[0051] Referring to FIG. 4, a cathode current collector of an
electrochemical cell is illustrated, in accordance with an
embodiment of the present invention. As shown in FIG. 4, the
cathode current collector 400 includes a perforated stainless-steel
plate that includes large circles 410 and small circles 412. As
mentioned herein above, in one exemplary embodiment, the average
diameter for the large circles is about 2.4 mm, the average
diameter of the small circles is about 1.9 mm and the ratio of
perforated area 410, 412 to the whole collector 414 (excluding the
tabbing area 416) is 0.6.
[0052] Referring to FIG. 5, an anode current collector of an
electrochemical cell is illustrated, in accordance with an
embodiment of the present invention. As shown in FIG. 5, the anode
current collector 500 includes central portion 514 having two side
perforated side portions 510, 512, and a tab portion 516 connected
to one of the side portions. The anode current collector 500, in an
exemplary embodiment is folded along the central alignment feature
514 along central axis 518 to form a book like structure shown in
view 520. In one embodiment, the alignment feature 514 in the
center of the anode current collector, may facilitate proper anode
to anode current collector alignment and anode current collector
folding, which are key steps in the cell construction. As described
with reference to FIG. 3 hereinbelow, the anode current collector
(anode) and the cathode current collector (cathode) in the cell are
assembled in a manner such that the anode current collector
sandwiches the cathode current collector. The two holes in the
center of the anode current collector will allow the anode current
collector to sit on a fixture stationary, and lithium foils can be
pressed properly onto the anode current collector. Also, the two
holes void of materials allow for easy folding of the anode current
collector to form proper geometry sandwiching the cathode to fit
into the cell case.
[0053] Referring to FIG. 6, an exploded view of an anode including
an anode current collector and two lithium foils of an
electrochemical cell is illustrated, in accordance with an
embodiment of the present invention. As shown in FIG. 6, lithium
foils 612, 614 are then disposed onto the folded anode current
collector 610 with sides 510, 512, the central alignment feature
514. In one embodiment, the lithium foils are pressed on to the
perforated surface of the anode current collector. Likewise, other
techniques now know by those skilled in the art, or later
developed, may be applied to dispose the lithium foil on to current
collector.
[0054] In one embodiment, the electrochemical cell disclosed herein
includes a stepped header design. In one embodiment, stepped header
design consists of two or more steps in the header body profile.
Referring to FIG. 7 is illustrated a stepped header of an
electrochemical cell, in accordance with an embodiment of the
present invention. As shown in view 700 in FIG. 7, the lower
portion 710 of the header includes a first step 712, and a second
step 714. The optimized stepped header design of the header may
allow for increased or maximum internal cell volume. In one
exemplary embodiment, the first step 712 may be designed around
ball seal requirements and the second step 714 may be designed
around glass-to-metal seal requirements. The first step 712 should
have sufficient thickness so that the contact area of ball to
header is adequate to hold the ball in place. The ball can be as
small as possible so that the thickness of this step of header can
be smaller than the thickness of the second step, thus yielding
more cell internal volume. The first step includes an opening 716
which may be designed to receive the ball seal 218 and the fill
port cover 216, described hereinabove, with reference to FIG. 2.
The second step 714 step should have sufficient thickness so that
the glass in the glass-to-metal seal can have sufficient thickness
to form a hermetic seal. The second step 716 includes terminal pins
718 and 720 for connecting the tab portion 229 of the cathode
current collector 228 and the tab portion 239 of the anode current
collector 240 to pin extenders 220 and 222 respectively, as
described hereinabove with reference to FIG. 2.
[0055] In one embodiment, the thickness of the first step may be in
a range of about 0.7 mm to about 1.5 mm. In another embodiment, the
thickness of the first step may be in a range of about 0.8 mm to
about 1.4 mm. In yet another embodiment, the thickness of the first
step may be in a range of about 0.9 mm to about 1.3 mm. In one
embodiment, the first step of the header may have a thickness of
about 1.1 mm. In one embodiment, the thickness of the second step
may be in a range of about 1.1 mm to about 1.9 mm. In another
embodiment, the thickness of the second step may be in a range of
about 1.2 mm to about 1.8 mm. In yet another embodiment, the
thickness of the second step may be in a range of about 1.3 mm to
about 1.7 mm. In one embodiment, the second step of the header may
have a thickness of about 1.5 mm.
[0056] Advantages of the stepped header design include an increased
internal volume of the electrochemical cell, the utilization of
which allows the cell to achieve electrolyte volume and void volume
goals. It may be appreciated that those skilled in the art will, in
light of the teachings of the present invention, that a proper
selection of the amount of electrolyte and void volume may
positively impact the cell energy density and the cell swelling. A
sufficient amount of electrolyte is necessary for the cell to
deliver desirable energy. But over fill of electrolyte in the cell
may increase the risk of cell swelling because there will be less
void volume that can be used for holding gas species formed as a
result of side reactions in the cell. In one embodiment, the amount
of electrolyte filled in a cell may be in a range of about 38
percentage to about 46 percentage based on the total internal
volume of the cell. In another embodiment, the amount of
electrolyte filled in a cell may be in a range of about 40
percentage to about 44 percentage based on the total internal
volume of the cell. In yet another embodiment, the amount of
electrolyte filled in a cell may be in a range of about 41
percentage to about 43 percentage based on the total internal
volume of the cell. In one embodiment, the amount of electrolyte
filled in a cell is about 42 percentage based on the total internal
volume of the cell.
[0057] In one embodiment, the amount of void volume in a cell may
be in a range of about 3 percentage to about 9 percentage based on
the total internal volume of the cell. In another embodiment, the
amount of void volume in a cell may be in a range of about 4
percentage to about 8 percentage based on the total internal volume
of the cell. In yet another embodiment, the amount of void volume
in a cell may be in a range of about 5 percentage to about 7
percentage based on the total internal volume of the cell. In one
embodiment, the amount of void volume in a cell is about 6 based on
the total internal volume of the cell.
[0058] In one embodiment, the ratio of the electrolyte volume to
the void volume in a newly manufactured cell may be in a range of
about 4.0 to about 10.0 based on the total volume of the cell. In
another embodiment, the ratio of the electrolyte volume to the void
volume in a newly manufactured cell may be in a range of about 5.0
to about 9.0 based on the total volume of the cell. In yet another
embodiment, the ratio of the electrolyte volume to the void volume
in a newly manufactured cell may be in a range of about 6.0 to
about 8.0 based on the total volume of the cell. In one embodiment,
the ratio of the electrolyte volume to the void volume in a newly
manufactured cell may be about 7.0 based on the total volume of the
cell.
[0059] In one embodiment, the electrolyte formulation includes a
lithium salt in a mixed solvent. The electrolyte provides an ionic
source serving as electrical conducting carrier between the cathode
and the anode during cell discharge. Suitable lithium salts may
include, but are not limited to, LiBF.sub.4, LiAsF.sub.6,
LiSbF.sub.6, or LiClO.sub.4, or a combination of two or more of
these salts. In one embodiment, the solvent may include a mixture
of two compounds. One compound having a low viscosity and the other
compound having a high permittivity. Suitable examples of solvents
having a low viscosity include, but are not limited to,
1,2-dimethoxyethane (DME), 1,2-diethoxyethane (DEE),
1-ethoxy,2-methoxyethane (EME), ethyl methyl carbonate, methyl
propyl carbonate, ethyl propyl carbonate, and diethyl carbonate.
Suitable examples of solvents having a high permittivity include,
but are not limited to, propylene carbonate (PC), ethylene
carbonate (EC), .gamma.-butyrolactone (GBL), and
N-methyl-pyrrolidinone (NMP). In one embodiment, the lithium salt
is LiBF.sub.4, and the mixed solvent is composed of
1,2-dimethoxyethane (DME) and .gamma.-butyrolactone (GBL). It may
be appreciated that those skilled in the art will, in light of the
teachings of the present invention, that the selected electrolyte
may have a good electrical conductivity and chemical stability when
in contact with both lithium anode and CF.sub.x cathode, thus
aiding in elimination or minimizing of cell swelling.
[0060] In one embodiment, the electrolyte amount may be determined
by the ratio of electrolyte amount to the amount of fluorinated
carbon (CF.sub.x). To maximize the energy density,
as-much-as-possible electrochemical active materials should be
filled into a cell. At the same time, each bit of the cathode
active material should be in contact with the electrolyte, in order
for each part of cathode to be active in contributing to discharge
capacity. It may be appreciated that those skilled in the art will,
in light of the teachings of the present invention, that adequate
amount of electrolyte is needed to achieve high energy density.
However, more than sufficient amount of electrolyte may cause lack
of void volume in the cell, thus leading to cell swelling. It may
be appreciated that those skilled in the art will, in light of the
teachings of the present invention, that the ratio of electrolyte
amount to the amount of fluorinated carbon (CF.sub.x) should be
properly determined. In one embodiment, the ratio of electrolyte
amount to the amount of fluorinated carbon (CF.sub.x) is in a range
of about 0.7 to about 1.1. In another embodiment, the ratio of
electrolyte amount to the amount of fluorinated carbon (CF.sub.x)
is in a range of about 0.8 to about 1.0. In yet another embodiment,
the ratio of electrolyte amount to the amount of fluorinated carbon
(CF.sub.x) is in a range of about 0.9 to about 1.05. In one
embodiment, the ratio of electrolyte amount to the amount of
fluorinated carbon (CF.sub.x) is about 0.93.
[0061] In one embodiment, the ratio of solvent one with low
viscosity and the solvent two with high permittivity is, by volume,
in a range of about 0.5 to about 1.5 In another embodiment, the
ratio of solvent one with low viscosity and the solvent two with
high permittivity is in a range of about 0.7 to about 1.3 In yet
another embodiment, the ratio of solvent one with low viscosity and
the solvent two with high permittivity is in a range of about 0.8
to about 1.2 In one embodiment, the ratio of solvent one with low
viscosity and the solvent two with high permittivity is about
1.0.
[0062] In one embodiment, the amount of lithium salt to solvent
mixture is in a range of about 0.8 moles per liter to about 1.2
moles per liter based on a total volume of the solvent. In another
embodiment, the ratio of lithium salt to solvent mixture is in a
range of about 0.9 moles per liter to about 1.1 moles per liter
based on a total volume of the solvent. In yet another embodiment,
the ratio of lithium salt to solvent mixture is in a range of about
0.95 moles per liter to about 1.05 moles per liter based on a total
volume of the solvent. In one embodiment, the ratio of lithium salt
to solvent mixture is about 1.0 moles per liter.
[0063] Referring to FIG. 3, a cross-sectional view of an
electrochemical cell is illustrated, in accordance with an
embodiment of the present invention. In the exemplary embodiment
illustrated in FIG. 3, the view 300 of the electrochemical cell
includes a cell case or battery case 328 which houses a cathode
assembly including a cathode current collector 318 integrated with
a cathode current collector tab 310 and encased in a cathode
separator 312. The cathode pellet 322 is pressed on to the cathode
current collector 318. The cell also includes an anode assembly
including an anode 320 pressed on to the anode current collector
324 and encased in an anode separator 316. The anode assembly
sandwiches the cathode assembly. The anode assembly and the cathode
assembly are then encased in an insulator pouch 326 which is
covered by the cell casing 328. The cell may be closed with a
stepped header 330 which is welded on its circumference with the
cell casing by forming welding rings 332. The header includes a
feed thru pin 334 for connection to device and glass to metal seal
336 to prevent leakage of electrolyte, solvents, etc. . . . . In
the exemplary embodiment illustrated in FIG. 3, the cathode current
collector has a thickness of about 0.075 mm, is made of stainless
steel, has perforations formed of large circles (average diameter
of about 2.4 mm) and small circles (average diameter of about 1.9
mm), cathode pellet 322 is composed of fluorinated carbon
(CF.sub.x), carbon black and binder in a ratio of about 90:6:4,
ratio of perforated area to total area of cathode current collector
is about 0.6 and cathode is coated with a 0.05 mm thick layer of
conductive carbon (not shown in figure). The anode current
collector includes a lithium metal foil 320 pressed on the anode
current collector 324, the anode current collector has a thickness
of 0.05 mm, is made of stainless steel, has diamond shaped
perforations, and ratio of perforated area to total area of anode
current collector is about 0.6. The electrolyte used includes
lithium salt is LiBF.sub.4, and mixed solvent composed of
1,2-dimethoxyethane (DME) and .gamma.-butyrolactone (GBL), and the
ratio of electrolyte amount to the amount of fluorinated carbon
(CF.sub.x) is about 0.93.
[0064] In one embodiment, the separator may be selected from those
commercially available separators. As known to those skilled in the
art, the separator is typically an electrically non-conducting
porous electrolyte-filled membrane, which is sandwiched between and
in contact with the cathode and anode. Its role is to prevent
direct electronic contact between cathode and anode, thus avoiding
a short-circuit between the two electrodes, to allow the flow of
ionic species within the cell. The separator should be chemically
stable while in contact with each of the cathode, anode and
electrolyte. The function and reliability of the separator is
critical for the optimal performance of lithium batteries. The
separator affects the internal cell resistance, discharge rates and
cell stability. The separator material in this invention is
selected based on its stability, porosity, thickness and strength,
to allow good ionic conductivity as well as to maintain stability.
In one embodiment, the separator may have a thickness in a range of
about 0.010 mm to about 0.035 mm. In one embodiment, the separator
may have a porosity of about 40 percent to about 60 percent. In
various embodiments, separator may include one layer of polymer
material, or multi-layer polymer materials. Suitable examples of
separator material may include, but are not limited to, monolayer
polypropylene, or can be tri-layer that consist of two layers of
polypropylene, and sandwiching monolayer of polyethylene. The
stability of the separator contributes to non-swelling of the
lithium battery during deep discharge.
[0065] According to an embodiment of this invention, the case
material (outer casing) for the cell may be made of titanium or
stainless steel. In one embodiment, the case material is titanium,
as titanium allows good compatibility with body fluid while the
battery is implanted into human body.
[0066] EXPERIMENTAL
[0067] Example 1 provides construction details of an anode sample
of an electrochemical cell in accordance with embodiments of the
present invention.
[0068] In Example 1, anode of the electrochemical cell is
constructed using two metallic lithium foils and a perforated
current collector made of stainless steel. The stainless steel
perforated current collector is perforated. FIG. 5 represents a
stainless steel perforated current collector as described in
Example 1. As shown in FIG. 5, in the exemplary embodiment provided
in Example 1, the perforations may consist of diamond shapes. The
stainless steel perforated current collector accordingly has a void
area and a total area. The stainless steel perforated current
collect of Example 1, has a ratio of perforated void area to the
total area of current collector (excluding the central folding and
tabbing area) of about 0.6. The thickness of the stainless steel
perforated current collector is about 0.050 millimeters. The
negative terminal 222 of the electrochemical cell is connected to
the tab portion 516, 239 of the stainless steel perforated anode
current collector.
[0069] Example 2 provides construction details and swelling
characteristics of an Li/CF.sub.x electrochemical cell in
accordance with embodiments of the present invention.
[0070] One Li/CF.sub.x cell was constructed according to preferred
embodiments of the present inventions as described with reference
to FIG. 3 hereinabove. The cell was discharged by a 5-day
accelerated protocol (as in FIG. 8) to 2.0 Volts. For testing of a
medical battery, the test duration of three months to six months is
not unusual. The 5-day protocol allow a faster output of the
testing. The swelling observed for the cell is about 1.0 percent.
As mentioned herein, "swelling" is defined/calculated as the
difference in the cell thickness between the cell in a discharged
state and the cell in an undischarged divided by the thickness of
the cell in the undischarged state. Referring to FIG. 8 is shown a
graph illustrating a discharge of an Li/CF.sub.x an electrochemical
cell, constructed in accordance with embodiments of the present
invention. The graph 800 includes Voltage on Y-Axis 810 and
Discharge capacity in percentage on X-axis 812. The Cell
constructed in Example 2, was discharged from 2.5 V to 2.0 V in a
5-day accelerated protocol and the percentage of discharge capacity
was plotted as curve 814.
[0071] Example 3 provides construction details and swelling
characteristics of two Li/CF.sub.x electrochemical cells in
accordance with embodiments of the present invention.
[0072] Two Li/CF.sub.x cells were constructed according to
preferred embodiments of the present inventions as described with
reference to Example 2 above. The two cells were discharged under a
5-day accelerated protocol. Referring to FIG. 9 is shown a graph
illustrating deep discharge of two Li/CF.sub.x electrochemical
cells, constructed in accordance with embodiments of the present
invention. The graph 900 includes Voltage on Y-Axis 910 and
Discharge capacity on X-axis 912. The Cells constructed in Example
3, were discharged from 2.5 V to 2.0 V in a 5-day accelerated
protocol and the discharge capacity was plotted as curve 914 for
cell 1, and curve 916 for cell 2. After discharge of the two cells
to 0.01V (as shown in FIG. 9), the cell swelling was calculated as
about 0.5 percent for cell 1, and about 1.0 percent for cell 2,
when calculated as described hereinabove in Example 2 in comparison
to the dimensions of undischarged cells.
[0073] Example 4 provides construction details and swelling
characteristics of twenty-four Li/CF.sub.x electrochemical cells in
accordance with embodiments of the present invention.
[0074] Twenty-four Li/CF.sub.x cells were constructed according to
preferred embodiments of the present inventions as described with
reference to Example 2 above. These twenty-four cells were first
discharged to 2.0 Volts by an accelerated protocol and the cell
thickness was measured at this stage. The cells were then
discharged to 0.0 Volts at 250 micro Amperes, and the cell
thickness was measured again. Referring to FIG. 10 is a shown graph
illustrating a degree of swelling of twenty-four Li/CF.sub.x
electrochemical cells, constructed in accordance with embodiments
of the present invention. The graph 1000 includes cell thickness
change in percentage on Y-Axis 1010 and cell group by cell milliamp
hour X-axis 1012. The Cells constructed in Example 4, were
discharged as described herein. FIG. 10 summarizes the swelling
data of the twenty-four cells while the cells were discharged to
2.0 V and further to 0.0 V. The swelling at 2.0 Volts for the 100
percent milliamp hour group is only about 1.5 percent. As observed
in FIG. 10, there is a general trend that the swelling of cell
after discharge to 0.0 Volts is lesser than that after discharge to
2.0 Volts, even some cells shrunk after discharge to 0.0V (see 90
percent milliamp hour group in FIG. 10). This may be attributed to
the fact that the density of the discharge product i.e., carbon and
LiF is greater than the density of the reactants i.e., Li and
CF.sub.x, and thus less volume is needed to hold the solids inside
the container. Further, the internal pressure of the cell is less
than the external air pressure, causing the shrinking of the cell,
and hence a reduction in the cell thickness.
[0075] In one embodiment, the electrochemical cell disclosed herein
includes an electrochemical cell with high specific energy, low
self-discharge rate, and minimal swelling during deep discharge,
particularly for an implantable medical device. For example, the
electrochemical cell may be useful in implantable cardiac monitor
(ICM) devices or other implantable medical products. In various
embodiments, the optimized selection of materials, i.e., the
materials for cathode, electrolyte, separator, current collector,
header, and cell case, and the optimized designs, i.e., the design
of the cathode current collector, design of the anode current
collector, anode to cathode ratio, electrolyte to cathode ratio,
void volume ratio, etc . . . , in the present disclosure may result
in reduced gassing and minimal swelling during deep discharge of
the electrochemical cell.
[0076] All the features disclosed in this specification, including
any accompanying abstract and drawings, may be replaced by
alternative features serving the same, equivalent or similar
purpose, unless expressly stated otherwise. Thus, unless expressly
stated otherwise, each feature disclosed is one example only of a
generic series of equivalent or similar features.
[0077] The foregoing embodiments meet the overall objectives of
this disclosure as summarized above. However, it will be clearly
understood by those skilled in the art that the foregoing
description has been made in terms only of the most preferred
specific embodiments. Therefore, many other changes and
modifications clearly and easily can be made that are also useful
improvements and definitely outside the existing art without
departing from the scope of the present disclosure, indeed which
remain within its very broad overall scope, and which disclosure is
to be defined over the existing art by the appended claims.
* * * * *