U.S. patent application number 16/511803 was filed with the patent office on 2021-01-21 for method for forming a semiconductor device.
This patent application is currently assigned to TAIWAN SEMICONDUCTOR MANUFACTURING CO., LTD.. The applicant listed for this patent is TAIWAN SEMICONDUCTOR MANUFACTURING CO., LTD.. Invention is credited to Chia-Yun CHEN, Po-Zen CHEN, Keng-Ying LIAO, Chin-Yu LIN, Huai-Jen TUNG, Ta-Cheng WEI, Su-Yu YEH.
Application Number | 20210020669 16/511803 |
Document ID | / |
Family ID | 1000005313111 |
Filed Date | 2021-01-21 |
![](/patent/app/20210020669/US20210020669A1-20210121-D00000.png)
![](/patent/app/20210020669/US20210020669A1-20210121-D00001.png)
![](/patent/app/20210020669/US20210020669A1-20210121-D00002.png)
![](/patent/app/20210020669/US20210020669A1-20210121-D00003.png)
![](/patent/app/20210020669/US20210020669A1-20210121-D00004.png)
![](/patent/app/20210020669/US20210020669A1-20210121-D00005.png)
![](/patent/app/20210020669/US20210020669A1-20210121-D00006.png)
![](/patent/app/20210020669/US20210020669A1-20210121-D00007.png)
![](/patent/app/20210020669/US20210020669A1-20210121-D00008.png)
![](/patent/app/20210020669/US20210020669A1-20210121-D00009.png)
![](/patent/app/20210020669/US20210020669A1-20210121-D00010.png)
View All Diagrams
United States Patent
Application |
20210020669 |
Kind Code |
A1 |
LIN; Chin-Yu ; et
al. |
January 21, 2021 |
METHOD FOR FORMING A SEMICONDUCTOR DEVICE
Abstract
A method for fabricating a semiconductor device is provided. The
method includes forming a metal catalyst layer on an etching area
of the semiconductor substrate; performing a wet etch process to
the semiconductor substrate to etch the etching area of the
semiconductor substrate under the metal catalyst layer, thereby
forming a trench in the semiconductor substrate; and removing the
metal catalyst layer from the semiconductor substrate after
performing the wet etch process.
Inventors: |
LIN; Chin-Yu; (Taichung
City, TW) ; LIAO; Keng-Ying; (Tainan City, TW)
; TUNG; Huai-Jen; (Tainan City, TW) ; CHEN;
Po-Zen; (Tainan City, TW) ; YEH; Su-Yu;
(Tainan City, TW) ; CHEN; Chia-Yun; (Taipei City,
TW) ; WEI; Ta-Cheng; (Tainan City, TW) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
TAIWAN SEMICONDUCTOR MANUFACTURING CO., LTD. |
Hsinchu |
|
TW |
|
|
Assignee: |
TAIWAN SEMICONDUCTOR MANUFACTURING
CO., LTD.
Hsinchu
TW
|
Family ID: |
1000005313111 |
Appl. No.: |
16/511803 |
Filed: |
July 15, 2019 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
H01L 27/14683 20130101;
H01L 31/1804 20130101; H01L 21/76895 20130101; H01L 21/30604
20130101; H01L 27/1463 20130101; H01L 21/31053 20130101; H01L
21/76224 20130101 |
International
Class: |
H01L 27/146 20060101
H01L027/146; H01L 21/306 20060101 H01L021/306; H01L 21/762 20060101
H01L021/762; H01L 21/3105 20060101 H01L021/3105; H01L 21/768
20060101 H01L021/768; H01L 31/18 20060101 H01L031/18 |
Claims
1. A method for fabricating a semiconductor device, comprising:
forming a patterned mask layer on a semiconductor substrate,
wherein the patterned mask layer exposes an etching area of the
semiconductor substrate; depositing a metal catalyst material on
the etching area and the patterned mask layer; removing the
patterned mask layer and a portion of the metal catalyst material
on the patterned mask layer to form a metal catalyst layer on the
etching area of the semiconductor substrate; performing a wet etch
process to the semiconductor substrate to etch the etching area of
the semiconductor substrate under the metal catalyst layer, thereby
forming a trench in the semiconductor substrate; and removing the
metal catalyst layer from the semiconductor substrate after
performing the wet etch process.
2. The method of claim 1, further comprising: forming an isolation
feature in the trench after removing the metal catalyst layer from
the semiconductor substrate.
3. The method of claim 2, wherein forming the isolation feature in
the trench comprises: overfilling the trench with a dielectric
material; and planarizing the dielectric material to remove a
portion of the dielectric material outside the trench.
4-5. (canceled)
6. The method of claim 1, wherein performing the wet etch process
comprises immersing the semiconductor substrate in an etching
solution.
7. The method of claim 1, further comprising: forming an
interconnect layer on a first side of the semiconductor substrate
prior to depositing the metal catalyst material, wherein depositing
the metal catalyst material is performed such that the metal
catalyst material is on a second side of the semiconductor
substrate opposite to the first side of the semiconductor
substrate.
8. The method of claim 1, further comprising: forming an
interconnect layer on a first side of the semiconductor substrate,
wherein depositing the metal catalyst material is performed such
that the metal catalyst material is on the first side of the
semiconductor substrate.
9. A method for fabricating a semiconductor device, comprising:
forming a plurality of photosensitive regions in a semiconductor
substrate; forming an interconnect layer on a front-side of the
semiconductor substrate after forming the photosensitive regions;
forming a metal catalyst layer on a back-side of the semiconductor
substrate after forming the photosensitive regions and forming the
interconnect layer; etching a portion of the semiconductor
substrate under the metal catalyst layer, thereby forming a trench
on the back-side of the semiconductor substrate; and forming an
isolation feature in the trench on the back-side of the
semiconductor substrate.
10. The method of claim 9, wherein forming the photosensitive
regions comprises performing an implantation process to the
front-side of the semiconductor substrate.
11. The method of claim 9, wherein forming the isolation feature is
performed such that the isolation feature is between adjacent two
of the photosensitive regions.
12. The method of claim 9, wherein forming the isolation feature is
performed such that the isolation feature has a vertical sidewall
with respect to the back-side of the semiconductor substrate.
13. The method of claim 9, wherein forming the metal catalyst layer
is performed such that the metal catalyst layer has a plurality of
openings to expose the back-side of the semiconductor
substrate.
14. The method of claim 9, further comprising: removing the metal
catalyst layer from the semiconductor substrate prior to forming
the isolation feature.
15. A method for fabricating a semiconductor device, comprising:
forming a patterned mask layer on a front-side of a semiconductor
substrate; depositing a metal catalyst material on the patterned
mask layer on the front-side of a semiconductor substrate; removing
the patterned mask layer and a portion of the metal catalyst
material on the patterned mask layer to form a metal catalyst layer
on the front-side of the semiconductor substrate; etching a portion
of the semiconductor substrate under the metal catalyst layer,
thereby forming a trench on the front-side of the semiconductor
substrate; forming an isolation feature in the trench on the
front-side of the semiconductor substrate; and forming a plurality
of photosensitive regions in the semiconductor substrate after
forming the isolation feature.
16. The method of claim 15, wherein forming the photosensitive
regions comprises performing an implantation process to the
front-side of the semiconductor substrate.
17. The method of claim 15, wherein forming the photosensitive
regions is performed such that the isolation feature is between
adjacent two of the photosensitive regions.
18. The method of claim 15, wherein forming the isolation feature
is performed such that the isolation feature has a vertical
sidewall with respect to the front-side of the semiconductor
substrate.
19. The method of claim 15, wherein removing the patterned mask
layer and a portion of the metal catalyst material on the patterned
mask layer is performed such that the metal catalyst layer has a
plurality of openings to expose the front-side of the semiconductor
substrate.
20. The method of claim 15, further comprising: removing the metal
catalyst layer from the semiconductor substrate prior to forming
the isolation feature.
21. The method of claim 15, further comprising: forming an
interconnect layer on the front-side of the semiconductor substrate
after forming the photosensitive regions.
22. The method of claim 1, wherein the wet etch process is
performed such that the metal catalyst layer is in the trench, and
removing the metal catalyst layer from the semiconductor substrate
is performed such that the metal catalyst layer is removed from the
trench.
Description
BACKGROUND
[0001] Integrated circuits (IC) with image sensors are used in a
wide range of modern day electronic devices. In recent years,
complementary metal-oxide semiconductor (CMOS) image sensors have
begun to see widespread use, largely replacing charge-coupled
devices (CCD) image sensors. Compared to CCD image sensors, CMOS
image sensors are increasingly favored due to low power
consumption, a small size, fast data processing, a direct output of
data, and low manufacturing cost. Some types of CMOS image sensors
include front-side illuminated (FSI) image sensors and back-side
illuminated (BSI) image sensors.
BRIEF DESCRIPTION OF THE DRAWINGS
[0002] Aspects of the present disclosure are best understood from
the following detailed description when read with the accompanying
figures. It is noted that, in accordance with the standard practice
in the industry, various features are not drawn to scale. In fact,
the dimensions of the various features may be arbitrarily increased
or reduced for clarity of discussion.
[0003] FIGS. 1-11 illustrate a method of fabricating an image
sensor according to various embodiments of the present
disclosure.
[0004] FIGS. 12-18 are cross-sectional views of an image sensor at
various intermediate stages of fabricating the image sensor
according to various embodiments of the present disclosure.
[0005] FIG. 19 is a cross-sectional view of an image sensor device
according to some embodiments of the present disclosure.
DETAILED DESCRIPTION
[0006] The following disclosure provides many different
embodiments, or examples, for implementing different features of
the provided subject matter. Specific examples of components and
arrangements are described below to simplify the present
disclosure. These are, of course, merely examples and are not
intended to be limiting. For example, the formation of a first
feature over or on a second feature in the description that follows
may include embodiments in which the first and second features are
formed in direct contact, and may also include embodiments in which
additional features may be formed between the first and second
features, such that the first and second features may not be in
direct contact. In addition, the present disclosure may repeat
reference numerals and/or letters in the various examples. This
repetition is for the purpose of simplicity and clarity and does
not in itself dictate a relationship between the various
embodiments and/or configurations discussed.
[0007] Further, spatially relative terms, such as "beneath,"
"below," "lower," "above," "upper" and the like, may be used herein
for ease of description to describe one element or feature's
relationship to another element(s) or feature(s) as illustrated in
the figures. The spatially relative terms are intended to encompass
different orientations of the device in use or operation in
addition to the orientation depicted in the figures. The apparatus
may be otherwise oriented (rotated 90 degrees or at other
orientations) and the spatially relative descriptors used herein
may likewise be interpreted accordingly.
[0008] In the present embodiments, a method for forming a trench
with vertical sidewalls is provided. The trench may have a high
aspect ratio. The trench may be filled with dielectric materials,
thereby forming an isolation structure, such as a deep trench
isolation (DTI) structure or a shallow trench isolation (STI) for
an image sensor integrated chip. Although the isotation structure
in the present embodiments are illustrated within a BSI image
sensor, it will be appreciated that the disclosed isotation
structure may also be used with front-side image (FSI) image
sensors. Furthermore, the method for forming the trench with
vertical sidewalls and a high aspect ratio and forming the
isolation structure in the trench may be used in other process, not
limited the process of fabricating an image sensor.
[0009] FIGS. 1-11 illustrate a method of fabricating an image
sensor according to various embodiments of the present disclosure.
FIG. 1 illustrates a substrate 110 with its back-side 110b bonded
to a support substrate 900. The substrate 110 may be any type of
semiconductor body (e.g., silicon, SiGe, semiconductor-on-insulator
(SOI), etc.), as well as any other type of semiconductor and/or
epitaxial layers, associated therewith. For example, in some
embodiments, the substrate 110 may include a base substrate and an
epitaxial layer. In some embodiments, the substrate 110 may include
a silicon substrate. In some embodiments, the substrate 110 may be
thinned by etching and/or mechanical grinding a front-side 110f of
the substrate 110 after bonding to the support substrate 900.
Thinning the substrate 110 allows for radiation to pass more easily
to a photosensitive region subsequently formed within the substrate
110.
[0010] Reference is made to FIG. 2. One or more isolation features
120 may be formed within the front-side 110f of the substrate 110.
The isolation features 120 include shallow trench isolation (STI)
structures and/or local oxidation of silicon (LOCOS) structures. In
some embodiments, the isolation features 120 are formed by
patterning the front-side 110f of the substrate 110 to form
trenches in the substrate 110 and filling a dielectric material
into the trenches. The dielectric material may include silicon
oxide, silicon nitride, silicon oxynitride, a low-k material, or
another suitable dielectric material. A chemical mechanical
polishing (CMP) process may be performed to planarize the surface
of the dielectric material filling the trenches. In some
embodiments, dopants in p-type or n-type are implanted into the
substrate 110 prior to the formation of the isolation features 120,
such that the isolation features 120 may each be surrounded by a
doped layer.
[0011] Reference is made to FIG. 3. Plural photosensitive regions
SE are formed within pixel regions 112-114 of the substrate 110,
respectively, in which each pixel regions 112-114 is between two
adjacent isolation features 120. In some embodiments, the
photosensitive region SE may include photodiodes formed by
implanting or diffusing one or more dopant species into a
front-side 110f of the substrate 110. For example, the
photosensitive regions SE are doped with a doping polarity opposite
from that of the substrate 110. The photosensitive regions SE are
formed adjacent to or near the front-side 110f of the substrate
110. The photosensitive regions SE are operable to sense incident
radiation that enters the pixel region from the back-side 110b. The
incident radiation may be visual light. Alternatively, the incident
radiation may be infrared (IR), far infrared (FIR), ultraviolet
(UV), X-ray, microwave, other suitable types of radiation, or a
combination thereof.
[0012] One or more transistor gate structures 130 are formed along
the front-side 110f of the substrate 110 within the pixel regions
112-114. In various embodiments, the one or more transistor gate
structures 130 may correspond to a transfer transistor, a
source-follower transistor, a row select transistor, and/or a reset
transistor. In some embodiments, the one or more transistor gate
structures 130 may be formed by depositing a gate dielectric film
and a gate electrode film on the front-side 110f of the substrate
110. The gate dielectric film and the gate electrode film are
subsequently patterned to form a gate dielectric layer 132 and a
gate electrode 134. Sidewall spacers 136 may be formed on the outer
sidewalls of the gate electrode 134. In some embodiments, the
sidewall spacers 136 may be formed by depositing a spacer layer
(e.g., a nitride, an oxide, etc.) onto the front-side 110f of the
substrate 110 and selectively etching the spacer layer to form the
sidewall spacers 136. In some embodiments, source/drain regions are
formed, by ion implantation or epitaxially growth, on two opposing
sides of each of the gate structures 130.
[0013] Reference is made to FIG. 4. Plural conductive interconnect
layers 150 are formed within a dielectric structure 140 formed
along the front-side 110f of the substrate 110. The dielectric
structure 140 includes plural stacked ILD layers, while the plural
conductive interconnect layers 150 include alternating layers of
conductive wires and vias. In some embodiments, one or more of the
plural conductive interconnect layers 150 may be formed using a
damascene process (e.g., a single damascene process or a dual
damascene process). The damascene process is performed by forming
an ILD layer over the front-side 110f of the substrate 110, etching
the ILD layer to form a via hole and/or a metal trench, and filling
the via hole and/or metal trench with a conductive material. In
some embodiments, the ILD layer may be deposited by a physical
vapor deposition technique (e.g., physical vapor deposition (PVD),
chemical vapor deposition (CVD), plasma enhanced CVD (PE-CVD),
atomic layer deposition (ALD), etc.) and the conductive material
may be formed using a deposition process and/or a plating process
(e.g., electroplating, electro-less plating, etc.). In various
embodiments, the plural conductive interconnect layers 150 may
include tungsten, copper, or aluminum copper, for example.
[0014] In some embodiments, the support substrate 900 may be
removed from the back-side 110b of the substrate 110 after forming
the dielectric structure 140 and the conductive interconnect layers
150 along the front-side 110f of the substrate 110. Subsequently,
isolation features 160 (referring to FIGS. 10A and 10B) are to be
formed from the back-side 110b of the substrate 110. The isolation
features 160 (referring to FIGS. 10A and 10B) may be formed by
patterning the back-side 110b of the substrate 110 to form plural
trenches and filling the trenches with dielectric materials. In
some cases where the trenches are formed by plasma dry etch
process, the plasma may destroy the lattice of the substrate and
thereby lower the absorbance of the substrate, which will result in
poor detection performance of the image sensor subsequently formed.
In the present embodiments, FIGS. 5A-9 shows a method for forming
the trenches by a wet etch process without using plasma, such that
lattice of the substrate would not be damaged by the plasma, and
the detection performance of the image sensor may not be
impaired.
[0015] Reference is made to FIGS. 5A and 5B. FIG. 5B is a
cross-sectional view taken along line 5B-5B of FIG. 5A. The
substrate 110 is first flipped about the horizontal axis, and the
support substrate 900 is removed. A patterned mask PM1 is formed
along the back-side 110b of the substrate 110. The patterned mask
PM1 includes sidewalls defining openings O1 along the back-side
110b of the substrate 110.
[0016] The patterned mask PM1 may include a mask layer PM11, an
anti-reflective coating (ARC) layer PM12, and a photoresist layer
PM13 on the back-side 110b of the substrate 110. The mask layer
PM11 may include one or more oxide (e.g., silicon oxide) and/or
nitride (e.g., silicon nitride) layers. The mask layer PM11 may be
blanket deposited over substrate 110 using any suitable deposition
process, such as, atomic layer deposition (ALD), chemical vapor
deposition (CVD), high density plasma CVD (HDP-CVD), physical vapor
deposition (PVD), thermal oxidation, thermal nitridation, and the
like. The mask layer PM11 may also act as an etch stop layer for
etching the ARC layer PM12.
[0017] The ARC layer PM12 and the photoresist layer PM3 may be
blanket deposited over the mask layer 105. The ARC layer PM12 may
reduce a reflection from underlying layers during photolithography.
In some embodiments, the ARC layer PM12 may be formed using similar
materials and methods as those mentioned regarding the mask layer
PM11, and the materials and methods of the ARC layer PM12 are not
repeated herein. In some embodiments, the mask layer PM11 may be
formed of silicon oxide and the ARC layer PM12 may be formed of
silicon nitride.
[0018] In some embodiments, the photoresist layer PM13 may be
patterned to include openings by exposing the photoresist layer
PM13 to light (e.g., ultraviolet light) using a reticle. Exposed or
unexposed portions of the photoresist layer PM13 may then be
removed by development depending on whether a positive or negative
resist is used to form the openings in the photoresist layer PM13.
The openings in the photoresist layer PM13 may be aligned with an
area of substrate 110 disposed between adjacent pixel regions
112-114. The pattern of the photoresist layer PM13 (e.g., the
openings) is then transferred to the ARC layer PM12 and the mask
layer PM11 using a suitable etching process. To specific, the
photoresist layer PM13 is used as an etch mask to etch the
underlying ARC layer PM12 and the mask layer PM11.
[0019] Accordingly, openings are formed in the ARC layer PM12 and
the mask layer PM11, such that the patterned mask PM1 has the
openings O1 to expose areas of the back-side 110b of the substrate
110 that is to be etched in subsequent process. The exposed areas
of the back-side 110b of the substrate 110 may also be referred to
as etching areas in this context. In some embodiments, each pixel
regions 112 and 114 is between adjacent etching areas exposed by
the patterned mask PM1.
[0020] In some alternative embodiments, the patterned mask PM1 may
be formed by depositing a layer of photosensitive material (e.g., a
positive or negative photoresist) along the back-side 110b of the
substrate 110. The layer of photosensitive material is selectively
exposed to electromagnetic radiation according to a photomask. The
electromagnetic radiation modifies a solubility of exposed regions
within the photosensitive material to define soluble regions. The
photosensitive material is subsequently developed to define the
openings O1 within the photosensitive material by removing the
soluble regions.
[0021] Reference is made to FIG. 6. A metal catalyst layer 310 is
blanketly deposited over the patterned mask PM1 and the exposed
areas of the substrate 110. The metal catalyst layer 310 may
include one or more metal having a catalytic effect for etching the
substrate 110, which will be illustrated later. For example, the
metal catalyst layer 310 may include group-B metals, such as gold
(Au), silver (Ag), copper (Cu), platinum (Pt), iron (Fe), manganese
(Mn), cobalt (Co), or other metal elements capable of being a
mediator of the redox reaction (described below). The metal
catalyst layer 310 may be deposited by, atomic layer deposition
(ALD), chemical vapor deposition (CVD), high density plasma CVD
(HDP-CVD), physical vapor deposition (PVD), sputtering, and the
like. The metal catalyst layer 310 may be a composite structure
having two or more metal layers made of different materials. For
example, the metal catalyst layer 310 has a first metal layer and a
second metal layer overlaying the first metal layer, in which the
first and second metal layer are different and made of
aforementioned group-B metals. In some embodiments, the first metal
layer is Ag, and the second metal layer is Pt or Au. In some other
embodiments, the first metal layer is Au, and the second metal
layer is Pt or Ag.
[0022] In some embodiments, a thickness of the metal catalyst layer
310 may range from about 1 nanometer to about 500 nanometers, for
example, from about 10 nanometers to about 50 nanometers. Through
the configuration, the metal catalyst layer 310 may serve as a
catalyst for etching the substrate 110, and the metal catalyst
layer 310 is uniform enough to provide desired etched profile in
subsequent process. If the thickness of the metal catalyst layer
310 is greater than about 500 nanometers, the metal catalyst layer
310 may peel off. If the thickness of the metal catalyst layer 310
is less than about 1 nanometer, the metal catalyst layer 310 may be
uneven, which will result in uneven etched profile in subsequent
process.
[0023] Reference is made to FIGS. 7A and 7B. FIG. 7B is a
cross-sectional view taken along line 7B-7B of FIG. 7A. The
patterned mask PM1 (referring to FIG. 6) is removed from the
substrate 110, and a portion of the metal catalyst layer 310 over
the patterned mask PM1 (referring to FIG. 6) is also removed from
the substrate. The removal may include a stripped off process. An
amount of each of the patterned portions of the photoresist layer
is removed by a wet etch process. For example, a strip solvent may
be applied by immersion or spray onto the substrate 110 to remove
the patterned mask PM1 from the substrate 110. The strip solvent
may be may include propylene glycol methyl ether (PGME), propylene
glycol methyl ether acetate (PGMEA), the like, and the combination
thereof. After stripping the patterned mask PM1, another portion of
the metal catalyst layer 310 remains on the back-side 110b of the
substrate 110 and is referred to as a metal catalyst layer 310'
hereinafter. As shown in the figure, the metal catalyst layer 310'
may have plural openings 3100 to expose the back-side 110b of the
semiconductor substrate 110.
[0024] Reference is made to FIG. 8. A wet etching process is
performed to the substrate 110 to etch a portion of the substrate
110 under the metal catalyst layer 310', such that trenches 110T
are formed on the back-side 110b of the substrate 110. The wet
etching process is performed by exposing the back-side 110b of the
substrate 110 to one or more etchants with the metal catalyst layer
310' in place. For example, the substrate 110 is immersed in an
etching solution containing the one or more etchants, such that the
etching solution reaches the metal catalyst layer 310' and a
portion of the semiconductor substrate not covered by the metal
catalyst layer 310'. The one or more etchants react with the metal
catalyst layer 310' and remove parts of the substrate 110 below the
metal catalyst layer 310'. The etchants do not react with the
portion of the semiconductor substrate not covered by the metal
catalyst layer 310'. Therefore, the wet etching process forms
plural trenches 110T, which will subsequently accommodate DTI
structures. The trenches 110T has vertical sidewalls S1, which may
have a right angle with respect to the back-side 110b of the
substrate. For example, an angle between the vertical sidewalls S1
and the back-side 110b can be in a range of about 80 degrees to
about 100 degrees, for example, about 90 degrees.
[0025] In some cases, BOSCH process, which includes cycle steps of
deposition, clean, and etch, can be used to form trenches. However,
the trenches formed by the BOSCH process may have balling profile,
striation shapes, and scallop sidewalls, which would result in
defect in subsequently deposition process. In some embodiments,
compared with trenches formed by BOSCH process the wet etch process
may form the trenches 110T with flat vertical sidewalls S1, such
that subsequently deposition process may have less defect. Through
the configuration, the DTI structures subsequently formed in the
trenches 110T will have vertical sidewalls, which in turn will
enlarge areas of the pixel regions of the image sensor.
[0026] In some embodiments where the semiconductor substrate 110 is
silicon, the etching solution can be an aqueous solution of
hydrofluoric acid (e.g., hydrogen fluoride (HF)) and an oxidative
agent like hydrogen peroxide (H.sub.2O.sub.2) or HNO.sub.3. Hole
injection takes place during the wet etch process such that the
etching solution can be infiltrated to the surface of the silicon
substrate 110. The oxidative agent like H.sub.2O.sub.2 or HNO.sub.3
is utilized to oxidize the silicon to form silicon dioxide
underneath the silver, and then the hydrofluoric acid is utilized
to etch the silicon dioxide, thereby etching down. Through the
configuration, the silicon substrate 110 is partially etched down
through a redox reaction with the catalyst of the metal catalyst
layer 310' (e.g., silver) at the area on which the silver is
located, and the area uncovered by the metal catalyst layer 310'
(e.g., silver) is not etched down.
[0027] To be specific, the oxidative agent (e.g., H.sub.2O.sub.2 or
HNO.sub.3), in the etching solution oxidizes the surface of the
substrate 110 which contacts the metal catalyst layer 310' (i.e.,
the surface of the substrate 110 under the metal catalyst layer
310') to form silicon oxide by the metal catalyst layer 310'. And
then, HF in the etching solution etches the silicon oxide on the
substrate 110. When the silicon oxide is completely etched, the
metal catalyst layer 310' follows down to contact the newly exposed
surface of the substrate 110 and foregoing reactions (or steps) are
repeated to etch the newly exposed surface of the substrate 110.
The surface of the substrate 110 contacting the bottom of the metal
catalyst layer 310' is etched continuously by repeating foregoing
reactions (or steps) because only the bottom of the metal catalyst
layer 310' contacts the surface of the substrate 110. Therefore, a
vertical etching is created on substrate 110, such that the
trenches 110T are formed.
[0028] In some embodiments, the redox reaction may be expressed as
M.sup.x++xe.sup.-.fwdarw.M at cathode, and
Si+6F.sup.-.fwdarw.SiF.sub.6.sup.2-+x4e.sup.- at anode, in which x
is an positive integer, and M is the metal element of the metal
catalyst layer 310', such that the overall redox reaction may be
expressed as 4M.sup.x++xSi+6xF.sup.-.fwdarw.4M+xSiF.sub.6.sup.2-.
The metal ions M.sup.x+ is provided by a reaction between the metal
element of the metal catalyst layer 310' and the etching solution
(e.g., the solution including HF and HNO.sub.3/H.sub.2O.sub.2).
Through the configuration, the Si substrate 110 is etched while the
metal catalyst layer 310' remains substantially intact. For
example, the metal catalyst layer 310' may have substantially the
same thickness before and after the wet etch process.
[0029] In some embodiments, HF in the etching solution is designed
to have a concentration ranging from about 2.0 M to about 7.7 M,
for example, ranging from about 3.4 M to about 5.8 M. If the
concentration of HF in the etching solution is less than 2.0 M, the
redox reaction may not happen. If the concentration of HF in the
etching solution is greater than 7.7 M, the metal catalyst layer
310 may be partially etched or peel off, which may result in
undesired profile (e.g., uneven bottom surface) of the trench 110T.
In some other embodiments, the etching solution may not include HF,
but includes other suitable etchants (e.g., acids) for etching the
silicon oxide on the substrate 110.
[0030] In some embodiments where the oxidative agent is
H.sub.2O.sub.2, H.sub.2O.sub.2 in the etching solution is designed
to have a concentration ranging from about 0.2 M to about 3.4 M,
for example, ranging from about 0.4 M to about 1.2 M. If the
concentration of H.sub.2O.sub.2 in the etching solution is less
than 0.2 M, the rate to etch the silicon under the metal catalyst
layer 310 may be too slow, which may unnecessarily lengthen
throughput times of products. If the concentration of
H.sub.2O.sub.2 in the etching solution is greater than 3.4 M, pores
may be formed on sidewalls of the trench 110T, which will result in
undesired profile (e.g., uneven sidewalls) of the trench 110T.
[0031] Depending on the requirements of DTI structures of image
sensor devices, the substrate 110 may be immersed in the etching
solution for an immerse time of about 1 minute to about 4 hours,
for example, about 5 minutes to about 20 minutes. If the immerse
time is less than 1 minute, the depth of the trench may not be
enough. If the immerse time is greater than 4 hours, the substrate
110 may be etch through, and the device may be damaged. The
trenches 110T may have a high aspect ratio greater than about 10,
for example, ranging from about 10 to about 250. In some further
embodiments, the aspect ratio of the trenches 110T may greater than
about 200 or 300. Through the configuration, the DTI structures in
the substrate get deeper and is applicable to image sensors
detecting long wavelength light (e.g. infrared light or far
infrared light) or multi-wavelength light.
[0032] Reference is made to FIG. 9. The metal catalyst layer 310'
is removed from the trenches 110T. For example, the metal catalyst
layer 310' may be rinsed and washed away from the silicon substrate
110 by using a suitable solution, which removes the metal catalyst
layer 310' while remaining the substrate 110 intact. For example,
the metal-rinsing solution may etch the metal catalyst layer 310',
in which the metal-rinsing solution is selected such that the
metal-rinsing solution has a higher etch rate to the metal catalyst
layer 310' than that to the substrate 110. For example, in some
embodiments where the substrate 110 is silicon, the metal-rinsing
solution used herein may be aqua regia, which is a mixture of
nitric acid and hydrochloric acid in a molar ratio of 1:3. In some
embodiments, the substrate 110 may be immersed in the metal-rinsing
solution for about 0.1 minutes to about 10 minutes. If the
substrate 110 is immersed in the metal-rinsing solution for less
than 0.1 minutes, residues of the metal catalyst layer 310' may
remain on the substrate 110. If the substrate 110 is immersed in
the metal-rinsing solution for more than 10 minutes, the device may
be damaged. In some other embodiments, the metal-rinsing solution
may nitric acid.
[0033] Reference is made to FIGS. 10A and 10B. FIG. 10B is a
cross-sectional view taken along line 10B-10B of FIG. 10A.
Isolation features 160 are formed in the trenches 110T. In some
embodiments, the isolation features 160 may be referred to as DTI
structures. In various embodiments, the isolation features 160 may
include an oxide, such as silicon oxide, TEOS, etc. For example,
the trenches 110T is overfilled with a dielectric material, and
then a planarization process such as CMP is performed to remove a
portion of the dielectric material out of the trenches 110T. Any
suitable deposition technique, such as chemical vapor deposition
(CVD), can be used to form the dielectric material. The isolation
features 160 may have vertical sidewalls 160S correspond to the
vertical sidewalls S1 of the trenches 110T. For example, an angle
between the vertical sidewalls 160S and the back-side 110b can be
in a range of about 80 degrees to about 100 degrees, for example,
in a range of about 89 degrees to about 91 degrees.
[0034] In some embodiments, the isolation features 160 may each be
surrounded by a doped layer. Prior to the formation of the
isolation features 160, a doped layer may be formed conformally
over the trenches 110T. The doped layer is lined inside the
trenches 110T following a contour of trenches 110T and over the
substrate 110. In some embodiments, the doped layer is formed by an
ion implantation process that implants dopant in p-type or n-type
into the substrate 110. In various embodiments, the doped layer is
formed by a multi-process implantation or different implantation
process to form suitable doping profiles within doped layer. In
some other embodiments, the doped layer may be omitted.
[0035] Reference is made to FIG. 11. A dielectric planarization
structure 180 is formed over the isolation features 160 and the
substrate 110, and then plural color filters 192-194 are formed
over the dielectric planarization structure 180. In some
embodiments, the color filters 192-194 may be formed within
openings in a grid structure 200 overlying the dielectric
planarization structure 180. In some embodiments, plural color
filters 192-194 may be formed by forming a color filter layer and
patterning the color filter layer. The color filter layer is formed
of a material that allows for the transmission of radiation (e.g.,
light) having a specific range of wavelength, while blocking light
of wavelengths outside of the specified range. Plural micro-lenses
210 are formed over the color filters 192-194 for collecting
photons into pixels. The grid structure 200 may be positioned
between adjacent color filters to prevent cross contamination of
photons in adjacent pixels. The impinging photons are therefore
entering the image sensing device through the back-side 110b. At
the presence of high aspect ratio DTI features 160, the photons
entering one of the photosensitive regions SE are barred from
travelling to the adjacent photosensitive regions SE, and thus
cross contamination of the incoming signal can be reduced.
[0036] Although the method illustrated in FIG. 5A-9 is used for
forming the trenches accommodating DTI structures, it should not
limit the scope of the present disclosure. In some embodiments, the
method may also be applicable to form a trench accommodating STI
structures, which is illustrated in FIGS. 12-18 below.
[0037] FIGS. 12-18 are cross-sectional views of an image sensor at
various intermediate stages of fabricating the image sensor.
Referring to FIG. 12, a patterned mask PM2 is formed along the
front-side 110f of the substrate 110. The patterned mask PM2
includes sidewalls defining openings O2 along the front-side 110f
of the substrate 110, in which the openings O2 expose areas of the
front-side 110f of the substrate 110 that is to be etched in
subsequent process. The exposed areas of the front-side 110f of the
substrate 110 may also be referred to as etching areas in this
context. In some embodiments, the etching areas exposed by the
patterned mask PM2 are not overlapping with the photosensitive
regions subsequently formed. The patterned mask PM2 may include a
mask layer PM21, an anti-reflective coating (ARC) layer PM22, and a
photoresist layer PM23 on the front-side 110f of the substrate 110.
The detail configuration of the patterned mask PM2 may be similar
to the patterned mask PM1 in FIG. 5B, and not repeated herein.
[0038] A metal catalyst layer 320 is blanketly deposited over the
patterned mask PM2 and the exposed areas of the substrate 110. The
metal catalyst layer 320 may include one or more metal having a
catalytic effect for etching the substrate 110. For example, the
metal catalyst layer 320 may include group-B metals, such as gold
(Au), silver (Ag), copper (Cu), platinum (Pt), iron (Fe), manganese
(Mn), cobalt (Co), or other metal elements capable of being a
mediator of the redox reaction. The detail configuration of the
metal catalyst layer 320 may be similar to the metal catalyst layer
310 in FIG. 6, and not repeated herein.
[0039] Reference is made to FIG. 13. The patterned mask PM2
(referring to FIG. 13) is removed from the substrate 110, and a
portion of the metal catalyst layer 320 over the patterned mask PM2
(referring to FIG. 13) is also removed from the substrate. The
removal may include a stripped off process. After stripping the
patterned mask PM2, another portion of the metal catalyst layer 320
remains on the front-side 110f of the substrate 110 and is referred
to as a metal catalyst layer 320' hereinafter. As shown in the
figure, the metal catalyst layer 320' may have plural openings 3200
to expose the front-side 110f of the semiconductor substrate 110.
Other details of the removing the patterned mask PM2 may be similar
to those illustrated with FIGS. 7A and 7B, and not repeated
herein.
[0040] Reference is made to FIG. 14. A wet etching process is
performed to the substrate 110 to etch a portion of the substrate
110 under the metal catalyst layer 320', such that trenches 110T'
are formed on the front-side 110f of the substrate 110. The wet
etching process is performed by exposing the front-side 110f of the
substrate 110 to one or more etchants with the metal catalyst layer
320' in place. For example, the substrate 110 is immersed in an
etching solution containing the one or more etchants. The one or
more etchants react with the metal catalyst layer 320' and remove
parts of the substrate 110 below the metal catalyst layer 320',
thereby forming plural trenches 110T', which will subsequently
accommodate STI structures. For example, the etching solution can
be an aqueous solution of hydrogen fluoride (HF) and an oxidative
agent like hydrogen peroxide (H.sub.2O.sub.2) or HNO.sub.3. The
trenches 110T' may have vertical sidewalls S2, which have a right
angle with respect to the front-side 110f of the substrate. For
example, an angle between the vertical sidewalls S2 and the
front-side 110f can be in a range of about 80 degrees to about 100
degrees, for example, in a range of about 89 degrees to about 91
degrees. Through the configuration, the STI structure will have
vertical sidewalls, which in turn will enlarge areas of the pixel
regions of the image sensor. The detail configuration of the wet
etching process may be similar to those illustrated with FIG. 8,
and not repeated herein.
[0041] Reference is made to FIG. 15. The metal catalyst layer 320'
is removed from the trenches 110T'. For example, the metal catalyst
layer 320' may be rinsed and washed away from the silicon substrate
110 by using a suitable solution, which removes the metal catalyst
layer 320' while remaining the substrate 110 intact. The detail
configuration of removing the metal catalyst layer 320' may be
similar to those illustrated with FIG. 9, and not repeated
herein.
[0042] Reference is made to FIG. 16. Isolation features 120 are
formed in the trenches 110T'. In some embodiments, the isolation
features 120 may be referred to as STI structures. In various
embodiments, the isolation features 120 may include an oxide, such
as silicon oxide, TEOS, silicon nitride, silicon oxynitride, a
low-k material, or other suitable dielectric materials. For
example, the trenches 110T' is overfilled with a dielectric
material, and then a planarization process such as CMP is performed
to remove a portion of the dielectric material out of the trenches
110T'. Any suitable deposition technique, such as chemical vapor
deposition (CVD), can be used to form the dielectric material. The
isolation features 120 may have vertical sidewalls 120S correspond
to the vertical sidewalls S2 of the trenches 110T'. For example, an
angle between the vertical sidewalls 120S and the front-side 110f
can be in a range of about 80 degrees to about 100 degrees, for
example, in a range of about 89 degrees to about 91 degrees.
[0043] Reference is made to FIG. 17. Plural photosensitive regions
SE are formed within pixel regions 112-114 of the substrate 110,
respectively, in which each pixel regions 112-114 is between two
adjacent isolation features 120. Subsequently, one or more
transistor gate structures 130 are formed along the front-side 110f
of the substrate 110 within the pixel regions 112-114, and then
plural conductive interconnect layers 150 are formed within a
dielectric structure 140 formed along the front-side 110f of the
substrate 110. The detail configuration of the formation of the
transistor gate structures 130, the dielectric structure 140, and
the conductive interconnect layers 150 may be similar to those
illustrated with FIGS. 3 and 4, and not repeated herein.
[0044] Reference is made to FIG. 18. The substrate 110 is first
flipped about the horizontal axis, and the support substrate 900
(referring to FIG. 16) is removed. Subsequently, DTI features 160
are formed on the back-side 110b of the substrate 110. Then, a
dielectric planarization structure 180, color filters 192-194, and
micro-lenses 210 are formed on the back-side 110b of the substrate
110 in a sequence. Other detail configuration of the DTI features
160, dielectric planarization structure 180, color filters 192-194,
and micro-lenses 210 are illustrated previously, and not repeated
herein.
[0045] FIG. 19 is a cross-sectional view of an image sensor device
100 according to some embodiments of the present disclosure. The
image sensor device 100 include a pixel array area AA, a periphery
area PA, a bonding pad area BA (also referred to as an E-pad
region), and a scribe line area SA. The dashed lines in FIG. 19
designate the approximate boundaries between the areas AA, PA, BA,
and SA. It is understood that these areas AA, PA, BA, and SA extend
vertically above and below the substrate 110. The pixel array area
AA contains arrays of radiation-sensing pixels. Each pixel may
include a radiation-sensing device (e.g., photosensitive regions SE
and transistors coupled to the photosensitive regions SE) that can
sense or detect radiation having specific wavelengths, which may
correspond to lights of different colors. The DTI features 160 or
STI features 120 defines the pixel regions 112-114 accommodating
the radiation-sensing pixels. The periphery area PA may include
other devices PD that need to be kept optically dark. For example,
the devices PD may be a digital device, such as an
application-specific integrated circuit (ASIC) device or a
system-on-chip (SOC) device. The other devices PD may be a
reference pixel that is used to establish a baseline of an
intensity of light for the image sensor device 100. The bonding pad
area BA may include one or more conductive bonding pads or E-pads
CP, through which electrical connections between the image sensor
device 100 and outside devices may be established. For example, a
bonding wire BW is attached to the conductive bonding pad CP
through the bonding ball BB. The scribe line area SA may be the
region that separates one semiconductor die that includes the
bonding pad area BA, the periphery area PA, and the pixel array
area AA from an adjacent semiconductor die (not illustrated). The
scribe line area SA is cut in a later fabrication process to
separate adjacent dies before the dies are packaged and sold as
integrated circuit chips. The scribe line area SA is cut in such a
way that the semiconductor devices in each die are not damaged.
[0046] Based on the above discussions, it can be seen that the
present disclosure offers advantages. It is understood, however,
that other embodiments may offer additional advantages, and not all
advantages are necessarily disclosed herein, and that no particular
advantage is required for all embodiments. One advantage is that
the wet etching process with metal catalyst forms trenches in a
substrate without using plasma, such that lattice of the substrate
would not be damaged by the plasma. Another advantage is that the
trenches are formed with high aspect ratio, such that the isolation
features (e.g., DTI structure) in the substrate may get deeper and
applicable to image sensors detecting long wavelength light (e.g.
infrared light or far infrared light) or multi-wavelength light.
Still another advantage is that the wet etching process with metal
catalyst result in the isolation features (e.g., DTI or STI
structures) having vertical sidewalls, which in turn will enlarge
areas of the pixel regions of the image sensor.
[0047] In some embodiments, a method for fabricating a
semiconductor device is provided. The method includes forming a
metal catalyst layer on an etching area of the semiconductor
substrate; performing a wet etch process to the semiconductor
substrate to etch the etching area of the semiconductor substrate
under the metal catalyst layer, thereby forming a trench in the
semiconductor substrate; and removing the metal catalyst layer from
the semiconductor substrate after performing the wet etch
process.
[0048] In some embodiments, a method for fabricating a
semiconductor device is provided. The method includes forming a
plurality of photosensitive regions in the semiconductor substrate;
forming a metal catalyst layer on a back-side of a semiconductor
substrate after forming the photosensitive regions; etching a
portion of the semiconductor substrate under the metal catalyst
layer, thereby forming a trench on the back-side of the
semiconductor substrate; and forming an isolation feature in the
trench on the back-side of the semiconductor substrate.
[0049] In some embodiments, a method for fabricating a
semiconductor device is provided. The method includes forming a
metal catalyst layer on a front-side of a semiconductor substrate;
etching a portion of the semiconductor substrate under the metal
catalyst layer, thereby forming a trench on the front-side of the
semiconductor substrate; forming an isolation feature in the trench
on the front-side of the semiconductor substrate; and forming a
plurality of photosensitive regions in the semiconductor substrate
after forming the isolation feature.
[0050] The foregoing outlines features of several embodiments so
that those skilled in the art may better understand the aspects of
the present disclosure. Those skilled in the art should appreciate
that they may readily use the present disclosure as a basis for
designing or modifying other processes and structures for carrying
out the same purposes and/or achieving the same advantages of the
embodiments introduced herein. Those skilled in the art should also
realize that such equivalent constructions do not depart from the
spirit and scope of the present disclosure, and that they may make
various changes, substitutions, and alterations herein without
departing from the spirit and scope of the present disclosure.
* * * * *