U.S. patent application number 16/453111 was filed with the patent office on 2020-12-31 for method for the production of pullulan soft capsules.
The applicant listed for this patent is LEFAN CAPSULE INTERNATIONAL INC. Invention is credited to Xiaosan CAO, Zhongming FANG, Peiyong LIU, Zhidong LU, Fei WANG, Sheng WANG, Xianyu YUN.
Application Number | 20200407763 16/453111 |
Document ID | / |
Family ID | 1000004201839 |
Filed Date | 2020-12-31 |
United States Patent
Application |
20200407763 |
Kind Code |
A1 |
YUN; Xianyu ; et
al. |
December 31, 2020 |
METHOD FOR THE PRODUCTION OF PULLULAN SOFT CAPSULES
Abstract
A method for the production of pullulan soft capsules eliminates
the need to dry pullulan solid product, thereby reducing the
equipment cost and energy consumption. The pullulan raw material
production can be linked directly with the soft capsule production
to provide a unique approach for soft capsule formation. The
purified pullulan fermentation fluid can be directly used in soft
capsule preparation, thus removing the need for a melting process.
On the one hand, the method can decrease material consumption, save
the cost of equipment and labor, reduce production time and
increase productivity. On the other hand, the method can reduce the
fluctuating of raw material quality in the re-melting process and
guarantee a more stable soft capsule production and quality.
Inventors: |
YUN; Xianyu; (Zhenjiang
City, CN) ; WANG; Sheng; (Zhenjiang City, CN)
; FANG; Zhongming; (Zhenjiang City, CN) ; WANG;
Fei; (Zhenjiang City, CN) ; LIU; Peiyong;
(Zhenjiang City, CN) ; CAO; Xiaosan; (Zhenjiang
City, CN) ; LU; Zhidong; (Zhenjiang City,
CN) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
LEFAN CAPSULE INTERNATIONAL INC |
Ontario |
CA |
US |
|
|
Family ID: |
1000004201839 |
Appl. No.: |
16/453111 |
Filed: |
June 26, 2019 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
A61K 9/4883 20130101;
C12P 19/10 20130101 |
International
Class: |
C12P 19/10 20060101
C12P019/10; A61K 9/48 20060101 A61K009/48 |
Claims
1. A method for the production of a pullulan soft capsule,
comprising: fermenting Aureobasidium pullulans cells to produce a
pullulan fermentation liquor; filtering the fermentation liquor;
concentrating the fermentation liquor; transferring the
concentrated fermentation liquor into a gel storage tank having a
temperature control function; pumping the concentrated fermentation
liquor from the gel storage tank into a reaction tank; adding
gelatin and plasticizer to the reaction tank with the concentrated
fermentation liquor, the concentrated fermentation liquor having
pullulan with a molecular weight suitable for the production of the
pullulan soft capsule; and forming the pullulan soft capsule with a
soft capsule making machine, wherein the method lacks drying the
pullulan to form a solid pullulan product.
2-3. (canceled)
4. The method of claim 1, wherein the concentrating the
fermentation liquor is performed to provide a mass fraction of
about 6 percent to about 58 percent by weight.
5. The method of claim 1, wherein the fermentation is performed at
atmospheric pressure and room temperature.
6. The method of claim 1, wherein the step of filtering the
fermentation liquor includes a plate and frame press filter to
remove bacteria.
7. The method of claim 1, wherein the step of filtering the
fermentation liquor includes passing the fermentation liquor
through a resin column for ion exchange.
8. The method of claim 1, where the gel storage tank maintains a
temperature from about 50.degree. C. to about 90.degree. C.
9. The method of claim 1, further comprising adding at least one of
a moisturizing agent and an anti-hygroscopic agent to the reaction
tank.
10. The method of claim 1, wherein the step of forming the pullulan
soft capsule includes: stirring a gel mixture in the reaction tank
until a first dispersion is formed; maintaining the gel mixture at
a temperature of 70-90.degree. C. for 2-8 hours; applying a vacuum
to the gel mixture for 20-40 minutes; cooling the gel mixture to a
temperature at 35-75.degree. C.; and pelleting the gel solution
with the soft capsule making machine to obtain a soft capsule
containing pullulan polysaccharide.
11. A method for the production of a pullulan soft capsule,
comprising: fermenting Aureobasidium pullulans to produce a
pullulan fermentation liquor; filtering the fermentation liquor
through at least one of a plate and frame press filter and an ion
exchange column; concentrating the fermentation liquor;
transferring the concentrated fermentation liquor into a gel
storage tank maintaining a temperature from about 50.degree. C. to
about 90.degree. C.; pumping the concentrated fermentation liquor
from the gel storage tank into a reaction tank; adding a
gelatinizer and a plasticizer to the reaction tank to form a soft
capsule gel liquid, the soft gel capsule liquid having pullulan
with a molecular weight suitable for the production of the pullulan
soft capsule; and forming the pullulan soft capsule with a soft
capsule making machine with the soft capsule gel liquid, wherein
the method lacks drying the pullulan to form a solid pullulan
product.
12. The method of claim 11, wherein the concentrating the
fermentation liquor is performed to provide a mass fraction of
about 6 percent to about 58 percent by weight.
13. The method of claim 11, wherein the fermentation is performed
at atmospheric pressure and room temperature.
14. The method of claim 11, further comprising adding at least one
of a moisturizing agent and an anti-hygroscopic agent to the
reaction tank.
15. A pullulan soft capsule produced by a process comprising:
fermenting Aureobasidium pullulans to produce a pullulan
fermentation liquor; filtering the fermentation liquor;
concentrating the fermentation liquor; transferring the
concentrated fermentation liquor into a gel storage tank having a
temperature control function; pumping the concentrated fermentation
liquor from the gel storage tank into a reaction tank; adding
gelatin and plasticizer to the reaction tank with the concentrated
fermentation liquor; and forming the pullulan soft capsule with a
soft capsule making machine, wherein the process lacks drying the
pullulan to form a solid pullulan product.
16. (canceled)
17. The pullulan soft capsule of claim 15, wherein the
concentrating the fermentation liquor is performed to provide a
mass fraction of about 6 percent to about 58 percent by weight.
18. The pullulan soft capsule of claim 15, wherein the step of
filtering the fermentation liquor includes a plate and frame press
filter to remove bacteria and passing the fermentation liquor
through a resin column for ion exchange.
19. The pullulan soft capsule of claim 15, where the gel storage
tank maintains a temperature from about 50.degree. C. to about
90.degree. C.
Description
BACKGROUND OF THE INVENTION
1. Field of the Invention
[0001] Embodiments of the invention relates generally to capsule
production methods. More particularly, the invention relates to a
method for the production of soft capsules formed from pullulan,
from raw material to final product.
2. Description of Prior Art and Related Information
[0002] The following background information may present examples of
specific aspects of the prior art (e.g., without limitation,
approaches, facts, or common wisdom) that, while expected to be
helpful to further educate the reader as to additional aspects of
the prior art, is not to be construed as limiting the present
invention, or any embodiments thereof, to anything stated or
implied therein or inferred thereupon.
[0003] Pullulan is a polysaccharide polymer of a maltotriose trimer
made up of .alpha.-(1.fwdarw.6)-linked
(1.fwdarw.4)-.alpha.-d-triglucosides, also known as
.alpha.-1,4-.alpha.-1,6-glucan. Three glucose units in maltotriose
are connected by an .alpha.-1,4 glycosidic bond, whereas
consecutive maltotriose units are connected to each other by an
.alpha.-1,6 glycosidic bond. Pullulan is produced from starch by
the fungus Aureobasidium pullulans.
[0004] Pullulan is a natural raw material of vegetable capsules
with excellent film-forming property, water solubility, biological
compatibility, and degradability. However, the production level of
this product is low worldwide. In the production of pullulan, the
drying process has high requirements on equipment and the energy
consumption is large. If the fermentation can't match with the
drying production capacity, it can seriously restrict the pullulan
production capacity, thus finally restrains the application of
pullulan soft capsules.
[0005] Conventionally, pullulan is produced by mesophilic
fermentation of starch syrup by the selected non-toxigenic strain
of Aureobasidium pullulans. The strain is selected by traditional
techniques, i.e. the strain is not the product of genetic
modification using recombinant technologies. The production strain
has a high yield of pullulan, low production of melanin and does
not produce aureobasidin A.
[0006] After completion of the fermentation, the fungal cells are
removed by microfiltration. The cell-free filtrate is
heat-sterilized and treated with activated carbon to remove
pigments and other impurities by adsorption. The decolorized
filtrate is cooled and deionized using cation and anion exchange
resins. The deionized solution is concentrated to a solids content
of about 12%, treated a second time with activated carbon, and
filtered using diatomaceous earth as a filter aid. The filtrate is
concentrated by evaporation to a solids content of about 30% and
dried in a drum dryer. The dried pullulan is pulverized to a
specified particle size and packed in sterilized polyethylene
bags.
[0007] Currently, the raw material of produced pullulan soft
capsules is pullulan dried product, which is the purified
fermentation fluid made in the drying process. A study found that
microwave drying would make the pullulan film distorted, while both
the spray drying and microwave drying would both result in the
browning of the raw pullulan material. Therefore, the drying
process during the preparation of pullulan raw material reduces its
quality and affects the pullulan soft capsules.
[0008] In view of the foregoing, there is a need for alternative
processes for the production of pullulan soft capsules that
addresses the problems outlines above in the conventional methods
of pullulan drying.
SUMMARY OF THE INVENTION
[0009] In some embodiments of the present invention, one aspect is
to reduce the impact of low raw material quality on soft capsule
preparation of pullulan soft capsules by eliminating the separate
drying process, which determines the quality of pullulan formed by
conventional methods.
[0010] In some embodiments of the present invention, another
purpose is to reduce the equipment cost and energy consumption in
the drying process by linking pullulan raw material production with
soft capsule production. At the same time, by process improvements,
the purified pullulan fermentation fluid can be directly used in
soft capsule preparation, thus removing the need for a separate
melting process. On the one hand, these improvements may decrease
material consumption, save the cost of equipment and labor, reduce
production time and increase productivity. On the other hand, these
improvements may reduce the fluctuating of raw material quality in
the re-melting process and guarantee a more stable soft capsule
production and quality.
[0011] Embodiments of the present invention provide a method for
the production of a pullulan soft capsule comprising fermenting
cells to produce a pullulan fermentation liquor; filtering the
fermentation liquor; concentrating the fermentation liquor;
transferring the concentrated fermentation liquor into a gel
storage tank having a temperature control function; pumping the
concentrated fermentation liquor from the gel storage tank into a
reaction tank; adding gelatin and plasticizer to the reaction tank
with the concentrated fermentation liquor; and forming the pullulan
soft capsule with a soft capsule making machine.
[0012] Embodiments of the present invention further provide a
method for the production of a pullulan soft capsule comprising
fermenting Aureobasidium pullulans to produce a pullulan
fermentation liquor; filtering the fermentation liquor through at
least one of a plate and frame press filter and an ion exchange
column; concentrating the fermentation liquor; transferring the
concentrated fermentation liquor into a gel storage tank
maintaining a temperature from about 50.degree. C. to about
90.degree. C.; pumping the concentrated fermentation liquor from
the gel storage tank into a reaction tank; adding a gelatinizer and
a plasticizer to the reaction tank to form a soft capsule gel
liquid; and forming the pullulan soft capsule with a soft capsule
making machine with the soft capsule gel liquid.
[0013] Embodiments of the present invention also provide a pullulan
soft capsule produced by a process comprising fermenting
Aureobasidium pullulans to produce a pullulan fermentation liquor;
filtering the fermentation liquor; concentrating the fermentation
liquor; transferring the concentrated fermentation liquor into a
gel storage tank having a temperature control function; pumping the
concentrated fermentation liquor from the gel storage tank into a
reaction tank; adding gelatin and plasticizer to the reaction tank
with the concentrated fermentation liquor; and forming the pullulan
soft capsule with a soft capsule making machine.
[0014] These and other features, aspects and advantages of the
present invention will become better understood with reference to
the following drawings, description and claims.
BRIEF DESCRIPTION OF THE DRAWINGS
[0015] Some embodiments of the present invention are illustrated as
an example and are not limited by the figures of the accompanying
drawings, in which like references may indicate similar
elements.
[0016] The FIG. illustrates a flow chart schematically showing a
method for the production of pullulan soft capsules according to an
exemplary embodiment of the present invention.
[0017] Unless otherwise indicated illustrations in the figures are
not necessarily drawn to scale.
[0018] The invention and its various embodiments can now be better
understood by turning to the following detailed description wherein
illustrated embodiments are described. It is to be expressly
understood that the illustrated embodiments are set forth as
examples and not by way of limitations on the invention as
ultimately defined in the claims.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS AND BEST MODE OF
INVENTION
[0019] The terminology used herein is for the purpose of describing
particular embodiments only and is not intended to be limiting of
the invention. As used herein, the term "and/or" includes any and
all combinations of one or more of the associated listed items. As
used herein, the singular forms "a," "an," and "the" are intended
to include the plural forms as well as the singular forms, unless
the context clearly indicates otherwise. It will be further
understood that the terms "comprises" and/or "comprising," when
used in this specification, specify the presence of stated
features, steps, operations, elements, and/or components, but do
not preclude the presence or addition of one or more other
features, steps, operations, elements, components, and/or groups
thereof.
[0020] Unless otherwise defined, all terms (including technical and
scientific terms) used herein have the same meaning as commonly
understood by one having ordinary skill in the art to which this
invention belongs. It will be further understood that terms, such
as those defined in commonly used dictionaries, should be
interpreted as having a meaning that is consistent with their
meaning in the context of the relevant art and the present
disclosure and will not be interpreted in an idealized or overly
formal sense unless expressly so defined herein.
[0021] In describing the invention, it will be understood that a
number of techniques and steps are disclosed. Each of these has
individual benefit and each can also be used in conjunction with
one or more, or in some cases all, of the other disclosed
techniques. Accordingly, for the sake of clarity, this description
will refrain from repeating every possible combination of the
individual steps in an unnecessary fashion. Nevertheless, the
specification and claims should be read with the understanding that
such combinations are entirely within the scope of the invention
and the claims.
[0022] In the following description, for purposes of explanation,
numerous specific details are set forth in order to provide a
thorough understanding of the present invention. It will be
evident, however, to one skilled in the art that the present
invention may be practiced without these specific details.
[0023] The present disclosure is to be considered as an
exemplification of the invention and is not intended to limit the
invention to the specific embodiments illustrated by the figures or
description below.
[0024] As is well known to those skilled in the art, many careful
considerations and compromises typically must be made when
designing for the optimal configuration of a commercial
implementation of any system, and in particular, the embodiments of
the present invention. A commercial implementation in accordance
with the spirit and teachings of the present invention may be
configured according to the needs of the particular application,
whereby any aspect(s), feature(s), function(s), result(s),
component(s), approach(es), or step(s) of the teachings related to
any described embodiment of the present invention may be suitably
omitted, included, adapted, mixed and matched, or improved and/or
optimized by those skilled in the art, using their average skills
and known techniques, to achieve the desired implementation that
addresses the needs of the particular application.
[0025] Broadly, embodiments of the present invention provide
methods for the production of pullulan soft capsules that
eliminates the need to dry pullulan solid product, thereby reducing
the equipment cost and energy consumption. The pullulan raw
material production can be linked directly with the soft capsule
production to provide a unique approach for soft capsule formation.
The purified pullulan fermentation fluid can be directly used in
soft capsule preparation, thus removing the need for a melting
process. On the one hand, the method can decrease material
consumption, save the cost of equipment and labor, reduce
production time and increase productivity. On the other hand, the
method can reduce the fluctuating of raw material quality in the
re-melting process and guarantee a more stable soft capsule
production and quality.
[0026] Referring now to the FIG., Aureobasidium pullulans can be
fermented and produced at room temperature and atmospheric
pressure. The fermentation of Aureobasidium pullulans may be
performed by known techniques. Its raw materials include sucrose or
glucose, some of which can be used for the growing consumption of
microbial cells, and the rest can turn into polysaccharose.
[0027] Raw material and water may be placed proportionally into the
seed tank and provided with a sterilization treatment. The
temperature can be controlled at about 26-30.degree. C. Bacteria
can be added to cultivate for 20-22 h, so as to provide sufficient
quantity of liquid for the fermentation tank to produce
bacteria.
[0028] Raw material and nutritive material may be placed
proportionally into the fermentation tank. Purified water may then
be added. After sterilization, the fermentation liquor may then be
added. The temperature is typically controlled at about
26-30.degree. C. The resulting mixture is stirred and cultivated
for about 65-75 h. After that, pullulan fermentation liquor will be
obtained.
[0029] The plate and frame press filter may then be used to filter
and substantially remove the bacteria in the fermentation
liquor.
[0030] The resulting fermentation liquor may be poured into resin
column for ion exchange, so as to substantially remove the small
amount of small protein and salt content therefrom.
[0031] The inlet valve of the filter system can maintain a working
pressure of about 0.5 MPA. During the process, purified water can
be used to backwash the filter system and the liquor may be
concentrated. According to the setting, the mass fraction of the
concentrated liquor can be controlled to about 6-58 (w/w)
percent.
[0032] The concentrated liquor may be transferred into a gel
storage tank, which has a temperature control function, so that the
liquor will be immersed in the tank at about 50-90.degree. C.
[0033] The concentrated liquor can then be pumped into the reaction
tank. Gelatinizers, plasticizers, moisturizing agents and
anti-hygroscopic agents may be added to the reaction tank at
ambient pressure with an agitation speed of about 40-60 r/min.
[0034] The gelatinizer may be various compounds known in the art.
For example, the genatinizer may be gelatin, gellan gum, high acyl
gellan gum, or the like. The gelatin may be obtained from various
sources, such as through a partial hydrolysis of collagen, derived,
for example, from animal bones, skin or connective tissues. In some
embodiments, the gelatinizer may have a gelatin strength (bloom)
between 150 and 200 and a viscosity range from about 25 to 45 milli
poise, for example.
[0035] The plasticizer may be present to make the soft capsule
elastic and pliable. Some of the most common plasticizers include
sorbitol and glycerin.
[0036] The moisturizing agent can be any moisturizing agent known
in the capsule formation arts, including, for example,
methylglycine-proline.
[0037] The anti-hygroscopic agent can be any anti-hygroscopic agent
known in the capsule formation arts, including, for example, one or
combination of stearic acid and lauric acid.
[0038] The resulting mixture can be stirred until a first
dispersion is formed, keeping the gel solution at a temperature of
70-90.degree. C. for 2-8 h and vacuuming for 20-40 min.
[0039] The gel solution can then be cooled to a temperature of
about 35-75.degree. C. The gel solution can be pelleted with a soft
capsule making machine, to obtain a soft capsule formed with
pullulan polysaccharide.
[0040] In some embodiments, the soft capsule making machine can
produce a thin gelatin ribbon that can be used to with an
encapsulation machine to create a soft capsule containing an
appropriate fill material, such as a pharmaceutical preparation.
The soft capsule making machine as described herein may take
various forms, including those that are typically used in the art
to make conventional soft capsules. The specifics for each of these
machines may vary, where the present invention provides a
concentrated pullulan liquor that can be used, with gelatinizers
and plasticizers, for example, to create a desired soft
capsule.
[0041] Many of the above described steps may be performed using
equipment that is known in the art. For example, ion exchange
resins and filtration devices for processing pullulan are known in
the art. Embodiments of the present invention provide a novel
method for the production of pullulan capsules that does not
require a drying or melting step, as is performed in conventional
methods.
[0042] All the features disclosed in this specification, including
any accompanying abstract and drawings, may be replaced by
alternative features serving the same, equivalent or similar
purpose, unless expressly stated otherwise. Thus, unless expressly
stated otherwise, each feature disclosed is one example only of a
generic series of equivalent or similar features.
[0043] Claim elements and steps herein may have been numbered
and/or lettered solely as an aid in readability and understanding.
Any such numbering and lettering in itself is not intended to and
should not be taken to indicate the ordering of elements and/or
steps in the claims.
[0044] Many alterations and modifications may be made by those
having ordinary skill in the art without departing from the spirit
and scope of the invention. Therefore, it must be understood that
the illustrated embodiments have been set forth only for the
purposes of examples and that they should not be taken as limiting
the invention as defined by the following claims. For example,
notwithstanding the fact that the elements of a claim are set forth
below in a certain combination, it must be expressly understood
that the invention includes other combinations of fewer, more or
different ones of the disclosed elements.
[0045] The words used in this specification to describe the
invention and its various embodiments are to be understood not only
in the sense of their commonly defined meanings, but to include by
special definition in this specification the generic structure,
material or acts of which they represent a single species.
[0046] The definitions of the words or elements of the following
claims are, therefore, defined in this specification to not only
include the combination of elements which are literally set forth.
In this sense it is therefore contemplated that an equivalent
substitution of two or more elements may be made for any one of the
elements in the claims below or that a single element may be
substituted for two or more elements in a claim. Although elements
may be described above as acting in certain combinations and even
initially claimed as such, it is to be expressly understood that
one or more elements from a claimed combination can in some cases
be excised from the combination and that the claimed combination
may be directed to a subcombination or variation of a sub
combination.
[0047] Insubstantial changes from the claimed subject matter as
viewed by a person with ordinary skill in the art, now known or
later devised, are expressly contemplated as being equivalently
within the scope of the claims. Therefore, obvious substitutions
now or later known to one with ordinary skill in the art are
defined to be within the scope of the defined elements.
[0048] The claims are thus to be understood to include what is
specifically illustrated and described above, what is conceptually
equivalent, what can be obviously substituted and also what
incorporates the essential idea of the invention.
* * * * *