U.S. patent application number 16/235724 was filed with the patent office on 2020-06-25 for system for introducing dopant into a melt of semiconductor or solar-grade material.
The applicant listed for this patent is GlobalWafers Co., Ltd. Invention is credited to Marco D'Angella, Mauro Dioda, Stephan Haringer.
Application Number | 20200199772 16/235724 |
Document ID | / |
Family ID | 55637400 |
Filed Date | 2020-06-25 |
![](/patent/app/20200199772/US20200199772A9-20200625-D00000.png)
![](/patent/app/20200199772/US20200199772A9-20200625-D00001.png)
![](/patent/app/20200199772/US20200199772A9-20200625-D00002.png)
![](/patent/app/20200199772/US20200199772A9-20200625-D00003.png)
![](/patent/app/20200199772/US20200199772A9-20200625-D00004.png)
United States Patent
Application |
20200199772 |
Kind Code |
A9 |
Haringer; Stephan ; et
al. |
June 25, 2020 |
SYSTEM FOR INTRODUCING DOPANT INTO A MELT OF SEMICONDUCTOR OR
SOLAR-GRADE MATERIAL
Abstract
A method of growing a doped monocrystalline ingot using a
crystal growing system is provided. The crystal growing system
includes a growth chamber, a dopant feeding device, and a feed
tube. The method includes preparing a melt of semiconductor or
solar-grade material in a crucible disposed within the growth
chamber, introducing a solid dopant into the feed tube with the
dopant feeding device, melting the solid dopant within the feed
tube to a form a liquid dopant, introducing the liquid dopant into
the melt below a surface of the melt, and growing a monocrystalline
ingot from the melt by contacting the melt with a seed crystal and
pulling the seed crystal away from the melt.
Inventors: |
Haringer; Stephan;
(Kastelbell -Tschars, IT) ; D'Angella; Marco;
(Merano, IT) ; Dioda; Mauro; (Bolzano,
IT) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
GlobalWafers Co., Ltd |
Hsinchu |
|
TW |
|
|
Prior
Publication: |
|
Document Identifier |
Publication Date |
|
US 20190136406 A1 |
May 9, 2019 |
|
|
Family ID: |
55637400 |
Appl. No.: |
16/235724 |
Filed: |
December 28, 2018 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
15556865 |
Sep 8, 2017 |
10443148 |
|
|
PCT/IB2016/051357 |
Mar 10, 2016 |
|
|
|
16235724 |
|
|
|
|
62130692 |
Mar 10, 2015 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C30B 15/04 20130101;
C30B 29/06 20130101 |
International
Class: |
C30B 15/04 20060101
C30B015/04; C30B 29/06 20060101 C30B029/06 |
Claims
1-18. (canceled)
19. A system for growing a single crystal ingot from a melt of
semiconductor or solar-grade material, the system comprising: a
housing defining a crystal growth chamber; a crucible disposed
within the growth chamber for holding a melt of semiconductor or
solar-grade material; a dopant feeding device configured to
dispense solid dopant; and a feed tube configured to receive solid
dopant from the dopant feeding device and dispense liquid dopant
into the melt, the feed tube defining a dopant outlet and including
a restrictor nozzle configured to inhibit solid dopant from passing
through the dopant outlet and to allow liquid dopant to pass
through the dopant outlet.
20. The system of claim 19, wherein at least a portion of the feed
tube is moveable from a retracted position to an extended position
in which the dopant outlet is positioned below a surface of the
melt.
21. The system of claim 19, wherein the housing has a feed port
defined therein for introducing dopant into the growth chamber, the
feed tube extending through the feed port.
22. The system of claim 19, wherein the feed tube includes a
sidewall defining a dopant passage, the restrictor nozzle including
a conical portion extending radially inward from the sidewall to
the dopant outlet.
23. The system of claim 22, wherein the conical portion extends
radially inward from the sidewall at an angle of between about
20.degree. and about 30.degree..
24. The system of claim 19, wherein the dopant outlet has a
diameter of between about 1 millimeter and about 4 millimeters.
25. The system of claim 19, wherein the feed tube includes an outer
feed tube and an inner feed tube at least partially disposed within
the outer feed tube, the outer feed tube including the restrictor
nozzle.
26. The system of claim 25, wherein the outer feed tube is
configured to move relative to the inner feed tube between a
retracted position and an extended position is which the dopant
outlet is positioned below a surface of the melt.
27. The system of claim 19, wherein the feed tube is made of
quartz.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application claim priority to U.S. Provisional Patent
Application Ser. No. 62/130,692, filed Mar. 10, 2015, the
disclosure of which is hereby incorporated by reference in its
entirety.
FIELD
[0002] The field relates generally to preparation of single
crystals of semiconductor or solar-grade material and, more
specifically, to a liquid doping system for controlled doping of a
melt of semiconductor or solar-grade material.
BACKGROUND
[0003] Single crystal material, which is the starting material for
fabricating many electronic components such as semiconductor
devices and solar cells, is commonly prepared using the Czochralski
("CZ") method. Briefly, the Czochralski method involves melting
polycrystalline source material, such as polycrystalline silicon
("polysilicon"), in a crucible to form a silicon melt and then
pulling a single-crystal ingot from the melt.
[0004] During the process, dopants are added to the molten source
material to modify the base resistivity of the resulting
monocrystalline structure. Dopants are often added to the molten
source material in solid form, at least for p-type and n-type
silicon. However, the use of solid dopants presents several
drawbacks.
[0005] One drawback is a thermal shock resulting from the
temperature difference between solid dopants and the molten source
material. This thermal shock causes the molten source material to
solidify underneath the solid dopant granules, creating "floating
boats". Additionally, quartz particles can form during the
formation of the floating boats. These quartz particles may remain
in the molten source material long after the floating boats have
melted, resulting in crystal defects or loss of crystal
structure.
[0006] A further drawback resulting from the addition of solid
dopants to the molten source material is contamination of the
monocrystalline growing assembly. The impact of solid dopants on
the surface of the molten source material causes the molten source
material to splash out of the crucible and onto various components
of the monocrystalline growing assembly, which may result in
crystal defects or damage to components in the assembly.
[0007] Yet another drawback to using solid dopants is that many
have relatively high evaporation rates, such as indium or antimony.
Placing these dopants directly into the crucible with the
semiconductor or other solar-grade material prior to melting causes
the dopant to evaporate during the heating of the semiconductor or
solar-grade material. Additional dopant must be added to compensate
for the lost dopant, often in significant quantities, resulting in
an inefficient use of the dopant. Additionally, the evaporated
dopant condenses on various components of the growing assembly,
resulting in contamination of the assembly. Moreover, when low
temperature or volatile dopants are added to a melt, they often
remain on the surface of the melt even after the dopants are
melted. As a result, there is often a continuous liquid-gas
interface through which the dopant can readily evaporate.
[0008] Accordingly, a need exists for more satisfactory systems and
methods for introducing dopants into a melt of semiconductor or
solar-grade material.
[0009] This Background section is intended to introduce the reader
to various aspects of art that may be related to various aspects of
the present disclosure, which are described and/or claimed below.
This discussion is believed to be helpful in providing the reader
with background information to facilitate a better understanding of
the various aspects of the present disclosure. Accordingly, it
should be understood that these statements are to be read in this
light, and not as admissions of prior art.
BRIEF SUMMARY
[0010] In one aspect, a method of growing a doped monocrystalline
ingot using a crystal growing system is provided. The crystal
growing system includes a growth chamber, a dopant feeding device,
and a feed tube. The method includes preparing a melt of
semiconductor or solar-grade material in a crucible disposed within
the growth chamber, introducing a solid dopant into the feed tube
with the dopant feeding device, melting the solid dopant within the
feed tube to a form a liquid dopant, introducing the liquid dopant
into the melt below a surface of the melt, and growing a
monocrystalline ingot from the melt by contacting the melt with a
seed crystal and pulling the seed crystal away from the melt.
[0011] In another aspect, a method of introducing a dopant into a
melt of semiconductor or solar-grade material using a feed tube and
a dopant feeding device is provided. The method includes
introducing a solid dopant into the feed tube with the dopant
feeding device, melting the solid dopant within the feed tube to a
form a liquid dopant, and introducing the liquid dopant into the
melt below a surface of the melt.
[0012] In yet another aspect, a system for growing a single crystal
ingot from a melt of semiconductor or solar-grade material is
provided. The system includes a housing defining a crystal growth
chamber, a crucible disposed within the growth chamber for holding
a melt of semiconductor or solar-grade material, a dopant feeding
device configured to dispense solid dopant, and a feed tube. The
feed tube is configured to receive solid dopant from the dopant
feeding device and dispense liquid dopant into the melt. The feed
tube defines a dopant outlet, and includes a restrictor nozzle
configured to inhibit solid dopant from passing through the dopant
outlet and to allow liquid dopant to pass through the dopant
outlet.
[0013] Various refinements exist of the features noted in relation
to the above-mentioned aspects. Further features may also be
incorporated in the above-mentioned aspects as well. These
refinements and additional features may exist individually or in
any combination. For instance, various features discussed below in
relation to any of the illustrated embodiments may be incorporated
into any of the above-described aspects, alone or in any
combination.
BRIEF DESCRIPTION OF THE DRAWINGS
[0014] FIG. 1 is a cross-section of a crystal growing system
including an example doping system for introducing liquid dopant
into a melt;
[0015] FIG. 2 is a cross-section of a dopant feeding device
suitable for use with the doping system of FIG. 1;
[0016] FIG. 3 is an enlarged cross-sectional view of a feed tube of
the doping system of FIG. 1; and
[0017] FIG. 4 is a flow chart of an example method of growing a
doped monocrystalline ingot using the crystal growing system of
FIG. 1.
[0018] Corresponding reference characters indicate corresponding
parts throughout the several views of the drawings.
DETAILED DESCRIPTION
[0019] Referring to FIG. 1, a crystal growing system is shown
schematically and is indicated generally at 100 in FIG. 1. The
crystal growing system 100 is used to produce monocrystalline
(i.e., single crystal) ingots of semiconductor or solar-grade
material (e.g., silicon) by the Czochralski (CZ) method. Although
the crystal growing system 100 is described herein with reference
to a batch or recharge CZ method, the crystal growing system 100
may also be used to grow monocrystalline ingots by a continuous CZ
method.
[0020] The illustrated crystal growing system 100 generally
includes a housing 102 defining a growth chamber 104 and an ingot
removal chamber 106 connected to and positioned above the growth
chamber 104. A crucible 108 containing a melt 110 of semiconductor
or solar-grade material (e.g., silicon) is positioned within the
growth chamber 104, and one or more heating elements 112 are
positioned proximate the crucible 108 for supplying thermal energy
to the system 100. The crystal growing system 100 also includes an
automatic doping system 114 connected to the housing 102 for
introducing dopant into the melt 110.
[0021] The housing 102 includes a lower portion 116, an upper dome
118 connected to the lower portion 116, and an elongate tubular
portion 120 extending generally upward from the upper dome 118. In
the illustrated embodiment, the growth chamber 104 is defined by
the lower portion 116 and the upper dome 118, and the ingot removal
chamber 106 is generally defined by the elongate tubular portion
120. The upper dome 118 includes a central annular opening 122
providing communication between the growth chamber 104 and the
removal chamber 106, and a feed port 124 (broadly, an opening)
through which dopants may be introduced into the melt 110. In the
illustrated embodiment, the feed port 124 is defined along the
upper dome 118, although the feed port 124 may be located along any
suitable portion of the housing 102 that enables the doping system
114 to function as described herein.
[0022] The housing 102 may be made of stainless steel or other
suitable materials. In some embodiments, one or more of the lower
portion 116, the upper dome 118, and the tubular portion 120 may
include water-cooled stainless steel walls.
[0023] The crucible 108 is positioned within the growth chamber 104
and beneath the removal chamber 106 such that an ingot grown from
the melt 110 can be pulled by a crystal pulling mechanism 126
through the central opening 122 in the upper dome 118 and into the
removal chamber 106. The crucible 108 may be supported within the
growth chamber 104 by a susceptor (not shown) and a rotatable shaft
(not shown) configured to rotate the crucible 108 during growth of
a crystal ingot.
[0024] The crucible 108 may be made of, for example, quartz or any
other suitable material that enables the crystal growing system 100
to function as described herein. Further, the crucible 108 may have
any suitable size that enables the crystal growing system 100 to
function as described herein. In some embodiments, the crucible 108
has a diameter of between about 16 inches and about 32 inches, more
suitably between about 20 inches and about 28 inches, and even more
suitably between about 20 inches and about 24 inches. In other
embodiments, the crucible 108 may have a diameter less than about
16 inches or greater than about 32 inches.
[0025] The doping system 114 generally includes a dopant feeding
device 128 and a feed tube 130. The dopant feeding device 128 is
secured to the housing 102, and is positioned outside of the growth
chamber 104. The feed tube 130 is positioned proximate an outlet of
the dopant feeding device 128, and extends through the feed port
124 of the housing 102 and into the growth chamber 104. The dopant
feeding device 128 is configured to dispense solid dopant into the
feed tube 130, and the feed tube 130 is configured to retain solid
dopant therein until the dopant is melted, and to introduce liquid
dopant into the melt 110.
[0026] FIG. 2 is a cross section of an example dopant feeding
device 200 suitable for use with the doping system 114 of FIG. 1.
The example dopant feeding device 200 is configured to dispense
metered quantities of solid dopant through an outlet 202 defined at
the lowermost point of the dopant feeding device 200. The dopant
feeding device 200 generally includes a fill assembly 204, a hopper
206, and a double valve system 208.
[0027] The fill assembly 204 includes a fill port 210 and a feed
tube 212 connected to the fill port 210 and extending from the fill
port 210 into the hopper 206. To load dopant into the dopant
feeding device 200, dopant is fed into the fill port 210 and is
funneled down into the feed tube 212 and into the hopper 206.
[0028] The hopper 206 includes a dopant container 214 for storing
dopant, and a dopant funnel 216 connected to a lower opening 218 of
the dopant container 214. Dopant fed into the fill port 210 is
directed into the dopant container 214 by the feed tube 212. Dopant
is stored in the dopant container 214, and is released in metered
quantities into the dopant funnel 216 using the double valve system
208.
[0029] The double valve system 208 includes a lower valve 220 and
an upper valve 222. The lower valve 220 and the upper valve 222 are
both operably connected to a pneumatic actuator 224. A fill chamber
226 is defined between the upper valve 222 and the dopant container
214. The volume of the chamber 226 defines the dopant charge or the
amount of dopant released by the dopant feeding device 200 in a
single discharge. The pneumatic actuator 224 is configured to
vertically reciprocate the lower valve 220 and the upper valve 222
to release metered quantities of dopant from the chamber 226 into
the dopant funnel 216 through the lower opening 218 of the dopant
container 214. Dopant released into the dopant funnel 216 is
dispensed from the dopant feeding device 200 into the feed tube 212
through the outlet 202 defined at the lowermost point of dopant
feeding device 200).
[0030] The dopant feeding device 200 is described in greater detail
in International Patent Application No. PCT/IT2013/000161, which is
hereby incorporated by reference in its entirety.
[0031] Referring again to FIG. 1, the feed tube 130 includes a
first end 132, a second end 134 distal from the first end 132, and
an annular sidewall 136 extending along a longitudinal axis of the
feed tube 130 from the first end 132 to second end 134. The feed
tube 130 has a dopant inlet 138 defined at the first end 132, a
dopant outlet 140 (also shown in FIG. 3) defined at the second end
134, and a dopant passage 142 defined therein extending from the
dopant inlet 138 to the dopant outlet 140. Solid dopant dispensed
from the dopant feeding device 128 is received in the feed tube 130
at the dopant inlet 138, and falls through the dopant passage 142
towards the dopant outlet 140 where the solid dopant is retained
until it is melted and released into the melt 110.
[0032] In the example embodiment, the feed tube 130 is a telescopic
feed tube, including a fixed, inner feed tube 144 and moveable,
outer feed tube 146. The inner feed tube 144 is secured in a fixed
relationship to one or both of the housing 102 and the dopant
feeding device 128, and the outer feed tube 146 is configured to
move relative to the inner feed tube 144. The inner feed tube 144
and the outer feed tube 146 are concentrically arranged about a
common longitudinal axis, and the outer feed tube 146 is configured
to move along the longitudinal axis between an extended position
(shown in FIG. 1) and a retracted position (not shown in FIG. 1).
The inner feed tube 144 defines the first end 132 and the dopant
inlet 138 of the feed tube 130, and the outer feed tube 146 defines
the second end 134 and the dopant outlet 140 of the feed tube
130.
[0033] The components of the feed tube 130 (e.g., the inner feed
tube 144 and the outer feed tube 146) are suitably made of
refractory materials that remain substantially chemically inert at
elevated temperatures. Suitable materials from which the components
of the feed tube 130 may be made of include, for example and
without limitation, quartz.
[0034] In the example embodiment, the outer feed tube 146 is
operatively connected to a linear slide mechanism 148 configured to
move the outer feed tube 146 between the extended position (shown
in FIG. 1) and the retracted position (not shown in FIG. 1). In
some embodiments, the linear slide mechanism 148 is configured to
retract the outer feed tube 146 entirely out of the growth chamber
104 when the outer feed tube 146 is in the retracted position. In
other embodiments, at least a portion of the outer feed tube 146 is
positioned within the growth chamber 104 when the outer feed tube
146 is in the retracted position. The linear slide mechanism 148
may include any suitable device or combination of devices that
enable the doping system 114 to function as described herein
including, for example and without limitation, tracks, rails,
rollers, bearing mechanisms, actuators, and combinations
thereof.
[0035] In the example embodiment, the linear slide mechanism 148
includes a rail 150, coupling members 152 slidably connected to the
rail 150 and attached to the outer feed tube 146, and an actuator
(not shown) operably connected to one or both of the outer feed
tube 146 and the coupling members 152. The actuator of the linear
slide mechanism 148 is configured to move the coupling members 152
along the rail 150, and move the outer feed tube 146 between the
extended and retracted positions. In other suitable embodiments,
linear actuating devices other than a linear slide mechanism may be
used to move the outer feed tube 146 between the extended and
retracted positions.
[0036] FIG. 3 is an enlarged cross-sectional view of the feed tube
130, specifically, the outer feed tube 146. When the outer feed
tube 146 is in the extended position, as shown in FIG. 3, the
dopant outlet 140 is submerged at a depth 302 below a surface 304
of the melt 110. The outer feed tube 146 includes a restrictor
nozzle 306 at the second end 134 of the feed tube 130 configured to
inhibit solid dopant 308 from passing through the dopant outlet 140
and to allow liquid dopant to pass through the dopant outlet
140.
[0037] The restrictor nozzle 306 includes a conical portion 310
extending radially inward from the annular sidewall 136 to the
dopant outlet 140 at an angle 312, and defines a diameter 314 of
the dopant outlet 140 sized to inhibit solid dopant 308 from
passing therethrough. The dopant outlet 140 may have any suitable
diameter 314 that enables the doping system 114 to function as
described herein, and may vary depending on the type of solid
dopant 308 used to dope the melt 110. In some embodiments, for
example, the dopant outlet 140 has a diameter of between about 1
millimeter (mm) and about 4 mm, and is configured to receive solid
dopant 308 having an average particle size of between about 2 mm
and about 5 mm.
[0038] In some embodiments, the angle 312 at which the conical
portion 310 of the restrictor nozzle 306 extends inward from the
sidewall 136 is between about 15.degree. and about 35.degree. and,
more suitably, between about 20.degree. and about 30.degree.. In
the illustrated embodiment, the conical portion 310 extends inward
from the sidewall 136 at an angle of about 25.degree.. Moreover, in
the illustrated embodiment, the conical portion 310 of the
restrictor nozzle 306 extends inward from the sidewall 136 at an
angle 312 such that, when the feed tube 130 is in the extended
position, the conical portion 310 and the reminder of the
restrictor nozzle 306 are generally oriented at the same angle with
respect to the surface of the melt 110, as shown in FIG. 3.
[0039] Solid dopant 308 introduced into the feed tube 130 is
retained within the dopant passage 142 by the restrictor nozzle 306
at the second end 134 of the feed tube 130 until the solid dopant
308 is melted by heat from the melt 110 and/or the heating elements
112. As the solid dopant melts and forms liquid dopant, the liquid
dopant flows out of the feed tube 130 through the dopant outlet 140
and into the melt 110. The shape and orientation of restrictor
nozzle 306 and, in particular, the angle 312 at which conical
portion 310 extends from the sidewall 136 facilitate dispensing all
liquid dopant from within the feed tube 130.
[0040] In the example embodiment, the restrictor nozzle 306 is also
configured to inhibit liquid melt material from flowing upward into
the feed tube 130 through the dopant outlet 140, which can damage
or impair operability of the feed tube 130 (e.g., by clogging the
dopant outlet 140). In particular, the restrictor nozzle 306 is
sized and shaped, and made of suitable materials so that the
interfacial surface energy between the melt 110 and the restrictor
nozzle 306 and the surface tension of the melt 110 inhibits melt
material from flowing upward into the feed tube 130 through the
dopant outlet 140. In the example embodiment, the outer feed tube
146 is suitably made of quartz, and has a dopant outlet 140 with a
diameter in the range of between about 1 mm and about 4 mm. The
outer feed tube 146 is suitable for introducing liquid dopant into
the melt 110 at a depth 302 up to about 5 mm. In other embodiments,
the outer feed tube 146 may be made of materials other than quartz,
such as other refractory materials that remain inert at elevated
temperatures, and have a dopant outlet with a diameter less than
about 1 mm or greater than about 4 mm.
[0041] In use, the crystal growing system 100 is used to grow doped
monocrystalline ingots, such as antimony-doped single crystal
silicon ingots, from the melt 110. More specifically, the melt 110
is prepared in the crucible 108 by charging the crucible 108 with
feedstock material, such as chunk polycrystalline silicon. The
feedstock material is melted in the crucible 108 using heating
elements 112 to form the melt 110 of semiconductor or solar grade
material. Dopants are added the melt 110 using the automatic doping
system 114 by dispensing solid dopant from the dopant feeding
device 128 into the feed tube 130, melting the solid dopant within
the feed tube 130 to form liquid dopant, and introducing the liquid
dopant into the melt 110 through the dopant outlet 140 at a depth
below the surface of the melt 110. When a desired amount of dopant
has been added to the melt 110, a monocrystalline ingot is grown
from the melt 110 by contacting the melt 110 with a seed crystal
(not shown) to initiate crystal growth, and subsequently pulling
the seed crystal away from the melt to grow the monocrystalline
ingot.
[0042] FIG. 4 is a flow chart of an example method 400 of growing a
doped monocrystalline ingot using the crystal growing system 100
described above with reference to FIGS. 1-3. The method 400
generally includes preparing 410 a melt of semiconductor or
solar-grade material in the crucible 108 disposed within the growth
chamber 104, introducing 420 a solid dopant into the feed tube 130
with the dopant feeding device 128, melting 430 the solid dopant
within the feed tube 130 to a form a liquid dopant, introducing 440
the liquid dopant into the melt 110 below the surface 304 of the
melt 110, and growing 450 a doped monocrystalline ingot from the
melt by contacting the melt with a seed crystal and pulling the
seed crystal away from the melt.
[0043] The melt 110 may be prepared, for example, by charging the
crucible 108 with solid feedstock material and melting the
feedstock material with heating elements 112. The semiconductor or
solar-grade material used to prepare the melt 110 may include, for
example and without limitation, silicon.
[0044] The doping system 114 and the method 400 are particularly
suitable for use with dopants having a relatively low melting
temperature relative to the melting temperature of the
semiconductor or solar-grade material used to prepare the melt 110.
In some embodiments, for example, the dopant used to dope the melt
110 has a melting temperature less than the melting temperature of
the semiconductor or solar-grade material used to prepare the melt.
In some particular embodiments, such as when silicon is used to
prepare the melt, the dopant used to dope the melt is selected from
the group consisting of aluminum, gallium, indium, thallium, and
antimony, although any suitable n-type or p-type dopant may be used
with the doping system 114 and the method 400.
[0045] In some embodiments, the method 400 further includes
positioning the dopant outlet 140 of the feed tube 130 at a depth
302 below the surface 304 of the melt 110. In some embodiments, for
example, all or part of the feed tube used to carry out the method
400 is moveable between an extended position, in which the feed
tube is positioned within the growth chamber 104 and the dopant
outlet is positioned below the surface of the melt 110, and a
retracted position, in which the feed tube is removed from the
growth chamber 104. The dopant outlet may be positioned at any
suitable depth below the surface of the melt that enables the
doping system 114 to function as described herein. In some
embodiments, for example, the dopant outlet is positioned at a
depth of at least about 1 cm below the surface of the melt and,
more suitably, at a depth of between about 1 cm and about 5 cm
below the surface of the melt.
[0046] In some embodiments, solid dopant is introduced into the
feed tube while the feed tube is in the extended position and is
positioned within the growth chamber. In other embodiments, solid
dopant is introduced into the feed tube while the feed tube is in
the retracted position and removed from the growth chamber, and the
feed tube is subsequently moved to the extended position such that
solid dopant within the feed tube can be melted by heat from the
melt.
[0047] In some embodiments, introducing 420 a solid dopant into the
feed tube includes introducing multiple charges of solid dopant
into the feed tube without removing the feed tube from growth
chamber. For example, introducing 420 a solid dopant into the feed
tube may include introducing a first charge of solid dopant into
the feed tube and, after the first charge of solid dopant is melted
and introduced into the melt, introducing a second charge of solid
dopant into the feed tube without removing the feed tube from the
growth chamber.
[0048] In some embodiments, introducing 440 the liquid dopant into
the melt includes introducing the liquid dopant into the melt while
the monocrystalline ingot is being grown. In some embodiments, for
example, the feed tube 130 is held in the extended position after
crystal growth is initiated, and liquid dopant is intermittently or
continuously introduced into the melt 110 while the monocrystalline
ingot is grown. Thus, the method 400 can be used to dope a melt in
a batch CZ process or in a continuous CZ process.
[0049] Embodiments of the doping systems and methods described
herein provide several advantages over known doping systems and
methods. For example, the doping systems and methods described
herein introduce dopants in liquid form below a surface of a melt
of semiconductor or solar-grade material. By introducing dopants in
liquid form, the doping systems and methods of the present
application facilitate inhibiting thermal shock and freezing of
melt material, which can result in loss of crystal structure of a
growing monocrystalline ingot. Moreover, by introducing dopants as
a liquid below the surface of a melt, the doping systems and
methods of the present application facilitate reducing evaporation
of elemental dopant and dopant compounds (e.g., dopant oxide
species) that might otherwise deposit on view ports on a crystal
growing system and inhibit an operator's ability to monitor a
crystal growing operation. In addition, introducing dopants as a
liquid below the surface of a melt inhibits splashing of the melt,
which might otherwise cause crystal defects or damage to components
of the crystal growing system.
[0050] The doping systems and methods of the present application
thus facilitate doping semiconductor or solar-grade melts with low
temperature dopants, such as aluminum, gallium, indium, thallium,
and antimony, while alleviating many of the problems associated
with using low temperature dopants to dope semiconductor or
solar-grade melts.
[0051] When introducing elements of the present invention or the
embodiment(s) thereof, the articles "a", "an", "the" and "said" are
intended to mean that there are one or more of the elements. The
terms "comprising", "including" and "having" are intended to be
inclusive and mean that there may be additional elements other than
the listed elements.
[0052] As various changes could be made in the above constructions
and methods without departing from the scope of the invention, it
is intended that all matter contained in the above description and
shown in the accompanying drawings shall be interpreted as
illustrative and not in a limiting sense.
* * * * *