U.S. patent application number 16/777394 was filed with the patent office on 2020-05-28 for flexible container with fitment and process for producing same.
The applicant listed for this patent is Dow Global Technologies LLC. Invention is credited to Marcos Pini Franca, Bruno Rufato Pereira, Kenneth R. Wilkes.
Application Number | 20200165015 16/777394 |
Document ID | / |
Family ID | 53765558 |
Filed Date | 2020-05-28 |
![](/patent/app/20200165015/US20200165015A1-20200528-D00000.png)
![](/patent/app/20200165015/US20200165015A1-20200528-D00001.png)
![](/patent/app/20200165015/US20200165015A1-20200528-D00002.png)
![](/patent/app/20200165015/US20200165015A1-20200528-D00003.png)
![](/patent/app/20200165015/US20200165015A1-20200528-D00004.png)
![](/patent/app/20200165015/US20200165015A1-20200528-D00005.png)
![](/patent/app/20200165015/US20200165015A1-20200528-D00006.png)
![](/patent/app/20200165015/US20200165015A1-20200528-D00007.png)
![](/patent/app/20200165015/US20200165015A1-20200528-D00008.png)
![](/patent/app/20200165015/US20200165015A1-20200528-D00009.png)
![](/patent/app/20200165015/US20200165015A1-20200528-D00010.png)
United States Patent
Application |
20200165015 |
Kind Code |
A1 |
Pereira; Bruno Rufato ; et
al. |
May 28, 2020 |
FLEXIBLE CONTAINER WITH FITMENT AND PROCESS FOR PRODUCING SAME
Abstract
A flexible container is provided. The flexible container
includes four panels. The four panels form (i) a body portion; (ii)
a neck portion, and a flare portion that extends from the neck
portion; (iii) a tapered transition portion between the body
portion and the neck portion; and (iv) the neck portion has a
reduced width. The flare portion has an expanded end. The width of
the flare portion gradually increases from the neck portion to the
expanded end.
Inventors: |
Pereira; Bruno Rufato;
(Houston, TX) ; Franca; Marcos Pini; (Sao Paulo
City, BR) ; Wilkes; Kenneth R.; (Asheville,
NC) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Dow Global Technologies LLC |
Midland |
MI |
US |
|
|
Family ID: |
53765558 |
Appl. No.: |
16/777394 |
Filed: |
January 30, 2020 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
14800312 |
Jul 15, 2015 |
10589882 |
|
|
16777394 |
|
|
|
|
62025288 |
Jul 16, 2014 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
B29K 2023/0633 20130101;
B29K 2023/06 20130101; B29K 2023/065 20130101; B29K 2023/12
20130101; B29K 2077/00 20130101; B29C 65/02 20130101; B29C 65/749
20130101; B29C 66/71 20130101; B29C 66/81423 20130101; B31B 2170/20
20170801; B65D 2575/586 20130101; B31B 70/642 20170801; B29C
66/83221 20130101; B65D 75/563 20130101; B29C 66/53242 20130101;
B65B 3/02 20130101; B31B 70/66 20170801; B29C 66/5344 20130101;
B65B 61/186 20130101; B29C 66/63 20130101; B65D 75/5866 20130101;
B29C 66/71 20130101; B29C 65/74 20130101; B31B 2160/20 20170801;
B29C 66/71 20130101; B65B 43/08 20130101; B29C 66/71 20130101; B29C
66/53246 20130101; B29C 66/1122 20130101; B65B 61/005 20130101;
B31B 70/872 20170801; B65B 3/045 20130101; B65B 3/027 20130101;
B29C 66/81431 20130101; B31B 70/74 20170801; B31B 70/844 20170801;
B29C 66/71 20130101; B31B 2150/00 20170801; B29L 2031/7128
20130101; B65D 75/5805 20130101; B31B 70/874 20170801; B65D 75/5883
20130101; B29C 66/53262 20130101; B29C 66/71 20130101; B29C
66/73921 20130101; B65B 61/188 20130101; B65B 7/02 20130101; B65D
75/5811 20130101 |
International
Class: |
B65B 3/02 20060101
B65B003/02; B29C 65/00 20060101 B29C065/00; B29C 65/02 20060101
B29C065/02; B31B 70/84 20060101 B31B070/84; B31B 70/74 20060101
B31B070/74; B65D 75/58 20060101 B65D075/58; B65B 61/18 20060101
B65B061/18; B65B 61/00 20060101 B65B061/00; B65B 7/02 20060101
B65B007/02 |
Claims
1-11. (canceled)
12. A process comprising: A) providing a flexible container with
four panels, the four panels forming (i) a body portion, (ii) a
neck portion, (iii) a tapered transition portion between the body
portion and the neck portion, (iv) the neck portion having a
reduced width, (B) adding, through the neck portion, a flowable
substance into the container interior; and (C) sealing the neck
portion.
13. The process of claim 12 comprising heat sealing the neck
portion.
14. The process of claim 11 wherein the flexible container
comprises a flare portion having an expanded end, the width of the
flare portion gradually increases from the neck portion to the
flare portion expanded end; and sealing the flare portion.
15. The flexible container of claim 11 comprising opening the seal
and re-sealing the seal.
Description
BACKGROUND
[0001] The present disclosure is directed to a flexible container
for dispensing a flowable material and a process for producing the
flexible container.
[0002] Known are flexible containers with a gusseted body section.
These gusseted flexible containers are currently produced using
flexible films which are folded to form gussets and heat sealed in
a perimeter shape. The gusseted body section opens to form a
flexible container with a square cross section or a rectangular
cross section. The gussets are terminated at the bottom of the
container to form a substantially flat base, providing stability
when the container is partially or wholly filled. The gussets are
also terminated at the top of the container to form an open neck
for receiving a rigid fitment and closure.
[0003] Conventional procedures for fabricating gusseted flexible
containers with a rigid fitment have shortcomings. One conventional
approach only partially heat seals the flexible
container--requiring the bottom of the container to remain unsealed
or otherwise open. The rigid fitment is subsequently inserted
through the open bottom of the container and into the neck. Once
the fitment is placed into the neck, the heat seal process
continues, with a heat seal formed to close the previously-open
container bottom. This approach is inefficient as it interrupts the
perimeter heat seal procedure and requires two steps to form the
container.
[0004] Another conventional approach requires the rigid fitment to
be manually installed, upside down, into the neck opening. The
fitment is then rotated by hand inside of the flexible container
and pushed into place, aligning the fitment with the neck opening
to allow proper sealing between the flexible container film
structure and the fitment. The fitment is subsequently clamp heat
sealed to the neck. This approach is cumbersome, labor intensive
and time consuming.
[0005] A need exists for a process of producing a gusseted flexible
container which increases production efficiencies such as shortened
production time, reduction of manual tasks via automation, and a
streamlining of production steps.
[0006] A need further exists for a process of producing a gusseted
flexible container with a fitment having improved impact
strength.
[0007] A need further exists for a gusseted flexible container
having a fitment with improved impact resistance and/or a
thin-walled fitment.
SUMMARY
[0008] The present disclosure provides a process for producing a
flexible container and the resultant flexible container.
[0009] In an embodiment, a process for producing a flexible
container is provided and includes (A) providing a flexible
container with four panels. The four panels form (i) a body
portion, (ii) a neck portion, and a flare portion that extends from
the neck portion, (iii) a tapered transition portion between the
body portion and the neck portion. (iv) The neck portion has a
reduced width, and the flare portion has an expanded end. The width
of the flare portion gradually increases from the neck portion to
the expanded end of the flare portion. The process includes (B)
inserting a fitment into the flare portion from the expanded
end.
[0010] The present disclosure provides another process. In an
embodiment, a process for producing a flexible container is
provided and includes (A) providing a flexible container with four
panels, the four panels forming (i) a body portion, (ii) a neck
portion, (iii) a tapered transition portion between the body
portion and the neck portion, and (iv) the neck portion has a
reduced width. The process includes (B) adding, through the neck
portion, a flowable substance into the container interior; and (C)
sealing the neck portion.
BRIEF DESCRIPTION OF THE DRAWINGS
[0011] FIG. 1 is a front elevation view of a flexible container in
a collapsed configuration in accordance with an embodiment of the
present disclosure.
[0012] FIG. 2 is an exploded side elevation view of a panel
sandwich.
[0013] FIG. 3 is a perspective view of the flexible container of
FIG. 1 in an expanded configuration and in accordance with an
embodiment of the present disclosure.
[0014] FIG. 4 is a bottom plan view of the expanded flexible
container of FIG. 3 in accordance with an embodiment of the present
disclosure.
[0015] FIG. 5 is a top plan view of the flexible container of FIG.
3.
[0016] FIG. 6 is an enlarged view of area 6 of FIG. 1
[0017] FIG. 7 is a perspective view of a mandrel and a fitment in
accordance with an embodiment of the present disclosure.
[0018] FIG. 8 is a perspective view of a mandrel supporting a
fitment in accordance with an embodiment of the present
disclosure.
[0019] FIG. 9 is a perspective view of a fitment being inserted
into the expanded end of the flare portion in accordance with an
embodiment of the present disclosure.
[0020] FIG. 10 is a perspective view of a fitment being inserted
into the expanded end of the flare portion in accordance with an
embodiment of the present disclosure.
[0021] FIG. 11 is a perspective view of a fitment being inserted
into the neck portion in accordance with an embodiment of the
present disclosure.
[0022] FIG. 12 is a perspective view of the fitment being sealed to
the neck portion in accordance with an embodiment of the present
disclosure.
[0023] FIG. 13 is a perspective view of the fitment being sealed to
the neck portion in accordance with an embodiment of the present
disclosure.
[0024] FIGS. 14-15 are perspective views of a scoring device in
accordance with an embodiment of the present disclosure.
[0025] FIG. 16 is a perspective view of an excess flare portion in
accordance with an embodiment of the present disclosure.
[0026] FIG. 17 is a perspective view of a flexible container with a
fitment in accordance with an embodiment of the present
disclosure.
[0027] FIG. 18 is a perspective view of a flexible container with a
neck seal in accordance with an embodiment of the present
disclosure.
[0028] FIG. 19 is a perspective view of a flexible container with a
flare seal in accordance with an embodiment of the present
disclosure.
DETAILED DESCRIPTION
[0029] The present disclosure provides a process and a flexible
container produced from the process. In an embodiment, the process
includes (A) providing a flexible container with four panels. The
four panels form (i) a body portion; (ii) a neck portion, and a
flare portion that extends from the neck portion; (iii) a tapered
transition portion between the body portion and the neck portion;
and (iv) the neck portion has a reduced width, the flare portion
has an expanded end; and the width of the flare portion gradually
increases from the neck portion to the flare expanded end (i.e.,
the expanded end of the flare portion). The process includes (B)
inserting a fitment into the flare portion from the expanded
end.
[0030] 1. Flexible Container
[0031] The process includes providing a flexible container 10.
Flexible container 10 has a collapsed configuration (as shown in
FIG. 1) and has an expanded configuration (shown in FIGS. 3, 4, 5).
FIG. 1 shows the flexible container 10 having a bottom section I, a
body section II, a tapered transition section III, a neck section
IV, and a flare section V. In the expanded configuration, the
bottom section I forms a bottom segment 26. The body section II
forms a body portion. The tapered transition section III forms a
tapered transition portion. The neck section IV forms a neck
portion. The flare section V forms a flare portion.
[0032] The flexible container 10 is made from four panels. During
the fabrication process, the panels are formed when one or more
webs of film material are sealed together. While the webs may be
separate pieces of film material, it will be appreciated that any
number of the seams between the webs could be "pre-made," as by
folding one or more of the source webs to create the effect of a
seam or seams. For example, if it were desired to fabricate the
present flexible container from two webs instead of four, the
bottom left center, and right center webs could be a single folded
web, instead of three separate webs. Similarly, one, two, or more
webs may be used to produce each respective panel (i.e., a
bag-in-a-bag configuration or a bladder configuration).
[0033] FIG. 2 shows the relative positions of the four webs as they
form four panels (in a "one up" configuration) as they pass through
the fabrication process. For clarity, the webs are shown as four
individual panels, the panels separated and the heat seals not
made. The constituent webs form first gusset panel 18, second
gusset panel 20, front panel 22 and rear panel 24. The panels 18-24
are a multilayer film as discussed in detail below. The gusset fold
lines 60 and 62 are shown in FIGS. 1 and 2.
[0034] As shown in FIG. 2, the folded gusset panels 18, 20 are
placed between the rear panel 24 and the front panel 22 to form a
"panel sandwich." The gusset panel 18 opposes the gusset panel 20.
The edges of the panels 18-24 are configured, or otherwise
arranged, to form a common periphery 11 as shown in FIG. 1. The
flexible multilayer film of each panel web is configured so that
the heat seal layers face each other. The common periphery 11
includes the bottom seal area including the bottom end of each
panel.
[0035] When the container 10 is in the collapsed configuration, the
flexible container is in a flattened, or in an otherwise evacuated
state. The gusset panels 18, 20 fold inwardly (dotted gusset fold
lines 60, 62 of FIG. 1) and are sandwiched by the front panel 22
and the rear panel 24.
[0036] FIGS. 3-5 show flexible container 10 in the expanded
configuration. The flexible container 10 has four panels, a front
panel 22, a back panel 24, a first gusset panel 18 and a second
gusset panel 20. The four panels 18, 20, 22, and 24 form the body
section II and extend toward a top end 44 and extend toward a
bottom end 46 of the container 10. Sections III, IV, and V
(respective tapered transition section, neck section, and flare
section) form a top segment 28. Section I (bottom section) forms a
bottom segment 26.
[0037] The four panels 18, 20, 22 and 24 can each be composed of a
separate web of film material. The composition and structure for
each web of film material can be the same or different.
Alternatively, one web of film material may also be used to make
all four panels and the top and bottom segments. In a further
embodiment, two or more webs can be used to make each panel.
[0038] In an embodiment, four webs of film material are provided,
one web of film for each respective panel 18, 20, 22, and 24. The
process includes sealing edges of each film to the adjacent web of
film to form peripheral seals 41 (FIGS. 1, 3, 4, 5). The peripheral
tapered seals 40a-40d are located on the bottom segment 26 of the
container as shown in FIG. 4. The peripheral seals 41 are located
on the side edges of the container 10. Consequently the process
includes forming a closed bottom section I, a closed body section
II, and a closed tapered transition section III.
[0039] To form the top segment 28 and the bottom segment 26, the
four webs of film converge together at the respective end and are
sealed together. For instance, the top segment 28 can be defined by
extensions of the panels sealed together at the tapered transition
section III, the neck section IV, and the flare section V. The top
end 44 includes four top panels 28a-28d (FIG. 5) of film that
define the top segment 28. The bottom segment 26 can be defined by
extensions of the panels sealed together at the bottom section I.
The bottom segment 26 can also have four bottom panels 26a-26d of
film sealed together and can also be defined by extensions of the
panels at the opposite end 46 as shown in FIG. 4.
[0040] The neck portion can extend from the transition portion.
Alternatively, the neck portion can extend from one of the four
panels of the body portion, or from a corner of the body
portion.
[0041] In an embodiment, the neck 30 is positioned at a midpoint of
the top segment 28. The neck 30 may (or may not) be sized smaller
than a width of the body section III, such that the neck 30 can
have an area that is less than a total area of the top segment 28.
The location of the neck 30 can be anywhere on the top segment 28
of the container 10.
[0042] In an embodiment, the neck is formed from two or more
panels. In a further embodiment, the neck 30 is formed from four
panels.
[0043] Although FIGS. 1 and 3 show the flexible container 10 with a
top handle 12 and a bottom handle 14, it is understood the flexible
container may be fabricated without handles or with only one
handle. When the flexible container has a top handle, the neck is
preferably located on the top segment between the handle legs to
facilitate easy pouring.
[0044] In an embodiment, the neck 30 is located in the top segment
28 and is centered between the legs 13 of the top handle 12.
[0045] The four panels of film that form the flexible container 10
extend from the body section II (forming body portion 47), to the
tapered transition section III (forming tapered transition portion
48), to form a neck portion 30 (in the neck section IV) and a flare
portion 50 (in the flare section V). The four panels of film also
extend from the body section II to the bottom section I (forming
bottom portion 49). When the flexible container 10 is in the
collapsed configuration (FIG. 1), the neck portion 30 has a width
that is less than the width of the tapered transition section III,
includes the neck portion has a "reduced width." The flare portion
50 extends from the neck portion 30. FIGS. 1 and 3 show the flare
portion 50 and the neck portion 30 form an access opening into the
flexible container interior. As shown in FIGS. 1, 3 and 5, the
flare portion 50 has an expanded end 51 and the width of the flare
portion 50 gradually increases from the neck portion 30 to the
expanded end 51. The flare sides 52 extend outwardly toward the
handle legs 13, 15 when moving from the neck portion 30 to the
expanded end 51. The panels are sealed together to form a closed
bottom section, a closed body section, and a closed tapered
transition section. Nonlimiting examples of suitable heating
procedures include heat sealing and/or ultrasonic sealing. When the
container 10 is in the expanded configuration, the expanded end 51
of the flare portion 50 is open or is otherwise unsealed. When the
flexible container 10 is in the collapsed configuration, the
expanded end 51 is unsealed and is openable. The open expanded end
51 permits access to the container interior through the flare
portion 50 and the neck portion 30 as shown in FIGS. 3 and 5.
[0046] The expanded end 51 has a width G having a length that is
greater than a width F of the neck portion 30, as shown in FIG. 1.
In an embodiment, the length of width G (in millimeters, mm) is
from 1.1, or 1.2, or 1.5, or 2.0, or 3.0, or 4.0 to 5.0, or 6.0, or
7.0, or 8.0 times greater than the length of width F.
[0047] When the flexible container 10 is in the expanded
configuration (as shown in FIG. 3), the flare portion 50 defines a
frustoconical-shaped inner volume whereby the diameter of the flare
portion 50 increases gradually when moving from the neck portion 30
to the expanded end 51.
[0048] As shown in FIGS. 1, 3-4, the flexible bottom handle 14 can
be positioned at a bottom end 46 of the container 10 such that the
bottom handle 14 is an extension of the bottom segment 26.
[0049] Each panel includes a respective bottom face. FIG. 4 shows
four triangle-shaped bottom faces 26a-26d, each bottom face being
an extension of a respective film panel. The bottom faces 26a-26d
make up the bottom segment 26. The four panels 26a-26d come
together at a midpoint of the bottom segment 26. The bottom faces
26a-26d are sealed together, such as by using a heat-sealing
technology, to form the bottom handle 14. For instance, a weld can
be made to form the bottom handle 14, and to seal the edges of the
bottom segment 26 together. Nonlimiting examples of suitable
heat-sealing technologies include hot bar sealing, hot die sealing,
impulse sealing, high frequency sealing, or ultrasonic sealing
methods.
[0050] FIG. 4 shows bottom segment 26. Each panel 18, 20, 22, 24
has a respective bottom face 26a-26d that is present in the bottom
segment 26. Each bottom face is bordered by two opposing peripheral
tapered seals 40a-40d. Each peripheral tapered seal 40a-40d extends
from a respective peripheral seal 41. The peripheral tapered seals
for the front panel 22 and the rear panel 24 have an inner edge
29a-29d (FIG. 4) and an outer edge 31 (FIG. 6). The peripheral
tapered seals 40a-40d converge at a bottom seal area 33 (FIG. 1,
FIG. 4, FIG. 6).
[0051] The front panel bottom face 26a includes a first line A
defined by the inner edge 29a of the first peripheral tapered seal
40a and a second line B defined by the inner edge 29b of the second
peripheral tapered seal 40b. The first line A intersects the second
line B at an apex point 35a in the bottom seal area 33. The front
panel bottom face 26a has a bottom distalmost inner seal point 37a
("BDISP 37a"). The BDISP 37a is located on the inner edge.
[0052] The apex point 35a is separated from the BDISP 37a by a
distance S from 0 millimeter (mm) to less than 8.0 mm.
[0053] In an embodiment, the rear panel bottom face 26c includes an
apex point similar to the apex point on the front panel bottom
face. The rear panel bottom face 26c includes a first line C
defined by the inner edge of the 29c first peripheral tapered seal
40c and a second line D defined by the inner edge 29d of the second
peripheral tapered seal 40d. The first line C intersects the second
line D at an apex point 35c in the bottom seal area 33. The rear
panel bottom face 26c has a bottom distalmost inner seal point 37c
("BDISP 37c"). The BDISP 37c is located on the inner edge. The apex
point 35c is separated from the BDISP 37c by a distance T from 0
millimeter (mm) to less than 8.0 mm.
[0054] It is understood the following description to the front
panel bottom face applies equally to the rear panel bottom face,
with reference numerals to the rear panel bottom face shown in
adjacent closed parentheses.
[0055] In an embodiment, the BDISP 37a (37c) is located where the
inner edges 29a (29c) and 29b (29d) intersect. The distance between
the BDISP 37a (37c) and the apex point 35a (35c) is 0 mm.
[0056] In an embodiment, the inner seal edge diverges from the
inner edges 29a, 29b (29c, 29d), to form an inner seal arc 39a
(front panel) and inner seal arc 39c (rear panel) as shown in FIGS.
4 and 8. The BDISP 37a (37c) is located on the inner seal arc 39a
(39c). The apex point 35a (apex point 35c) is separated from the
BDISP 37a (BDISP 37c) by the distance S (distance T) which is from
greater than 0 mm, or 1.0 mm, or 2.0 mm, or 2.6 mm, or 3.0 mm, or
3.5 mm, or 3.9 mm, to 4.0 mm, or 4.5 mm, or 5.0 mm, or 5.2 mm, or
5.3 mm, or 5.5 mm, or 6.0 mm, or 6.5 mm, or 7.0 mm, or 7.5 mm, or
7.9 mm.
[0057] In an embodiment, apex point 35a (35c) is separated from the
BDISP 37a (37c) by the distance S (distance T) which is from
greater than 0 mm to less than 6.0 mm.
[0058] In an embodiment, the distance from S (distance T) from the
apex point 35a (35c) to the BDISP 37a (37c) is from greater than 0
mm, or 0.5 mm or 1.0 mm, or 2.0 mm to 4.0 mm or 5.0 mm or less than
5.5 mm.
[0059] In an embodiment, apex point 35a (apex point 35c) is
separated from the BDISP 37a (BDISP 37c) by the distance S
(distance T) which is from 3.0 mm, or 3.5 mm, or 3.9 mm, to 4.0 mm,
or 4.5 mm, or 5.0 mm, or 5.2 mm, or 5.3 mm, or 5.5 mm.
[0060] In an embodiment, the distal inner seal arc 39a (39c) has a
radius of curvature from 0 mm, or greater than 0 mm, or 1.0 mm to
19.0 mm, or 20.0 mm.
[0061] In an embodiment, each peripheral tapered seal 40a-40d
(outside edge) and an extended line from respective peripheral seal
41 (outside edge) form an angle G as shown in FIG. 1. The angle G
is from 40.degree. or 42.degree., or 44.degree., or 45.degree. to
46.degree., or 48, or 50.degree.. In an embodiment, angle G is
45.degree..
[0062] The bottom segment 26 includes a pair of gussets 54 and 56
formed thereat, which are essentially extensions of the bottom
faces 26a-26d. The gussets 54 and 56 can facilitate the ability of
the flexible container 10 to stand upright. These gussets 54 and 56
are formed from excess material from each bottom face 26a-26d that
are joined together to form the gussets 54 and 56. The triangular
portions of the gussets 54 and 56 comprise two adjacent bottom
segment panels sealed together and extending into its respective
gusset. For example, adjacent bottom faces 26a and 26d extend
beyond the plane of their bottom surface along an intersecting edge
and are sealed together to form one side of a first gusset 54.
Similarly, adjacent bottom faces 26c and 26d extend beyond the
plane of their bottom surface along an intersecting edge and are
sealed together to form the other side of the first gusset 54.
Likewise, a second gusset 56 is similarly formed from adjacent
bottom faces 26a-26b and 26b-26c. The gussets 54 and 56 can contact
a portion of the bottom segment 26, where the gusset portions
gussets 54 and 56 can contact bottom faces 26b and 26d covering
them, while bottom segment panels 26a and 26c remain exposed at the
bottom end 46.
[0063] As shown in FIGS. 3-4, the gussets 54 and 56 of the flexible
container 10 can further extend into the bottom handle 14. In the
aspect where the gussets 54 and 56 are positioned adjacent bottom
segment panels 26b and 26d, the bottom handle 14 can also extend
across bottom faces 26b and 26d, extending between the pair of
panels 18 and 20. The bottom handle 14 can be positioned along a
center portion or midpoint of the bottom segment 26 between the
front panel 22 and the rear panel 24.
[0064] The top handle 12 and the bottom handle 14 can comprise up
to four plys of film sealed together for a four panel container 10.
When more than four panels are used to make the container, the
handles can include the same number of panels used to produce the
container. Any portion of the handles 12, 14 where all four plys
are not completely sealed together by the heat-sealing method, can
be adhered together in any appropriate manner, such as by a tack
seal to form a fully-sealed multilayer handle. Alternatively, the
top handle can be made from as few as a single ply of film from one
panel only or can be made from only two plies of film from two
panels. The handles 12, 14 can have any suitable shape and
generally will take the shape of the film end. For example,
typically the web of film has a rectangular shape when unwound,
such that its ends have a straight edge. Therefore, the handles 12,
14 would also have a rectangular shape.
[0065] Additionally, the bottom handle 14 can contain a handle
opening 16 or cutout section therein sized to fit a user's hand, as
can be seen in FIG. 1. The handle opening 16 can be any shape that
is convenient to fit the hand and, in one aspect, the handle
opening 16 can have a generally oval shape. In another aspect, the
handle opening 16 can have a generally rectangular shape.
Additionally, the handle opening 16 of the bottom handle 14 can
also have a flap 38 that comprises the cut material that forms the
handle opening 16. To define the handle opening 16, the handle 14
can have a section that is cut out of the multilayer handle 14
along three sides or portions while remaining attached at a fourth
side or lower portion. This provides a flap of material 38 that can
be pushed through the opening 16 by the user and folded over an
edge of the handle opening 16 to provide a relatively smooth
gripping surface at an edge that contacts the user's hand. If the
flap of material were completely cut out, this would leave an
exposed fourth side or lower edge that could be relatively sharp
and could possibly cut or scratch the hand when placed there.
[0066] Furthermore, a portion of the bottom handle 14 attached to
the bottom segment 26 can contain a dead machine fold 42 or a score
line that provides for the handle 14 to consistently fold in the
same direction, as illustrated in FIG. 3. The machine fold 42 can
comprise a fold line that permits folding in a first direction
toward the front side panel 22 and restricts folding in a second
direction toward the rear panel 24. The term "restricts" as used
throughout this application can mean that it is easier to move in
one direction, or the first direction, than in an opposite
direction, such as the second direction. The machine fold 42 can
cause the handle 14 to consistently fold in the first direction
because it can be thought of as providing a generally permanent
fold line in the handle that is predisposed to fold in the first
direction X, rather than in the second direction Y. This machine
fold 42 of the bottom handle 14 can serve multiple purposes, one
being that when a user is transferring the product from the
container 10 they can grasp the bottom handle 14 and it will easily
bend in the first direction X to assist in pouring. Secondly, when
the flexible container 10 is stored in an upright position, the
machine fold 42 in the bottom handle 14 encourages the handle 14 to
fold in the first direction X along the machine fold 42, such that
the bottom handle 14 can fold underneath the container 10 adjacent
one of the bottom segment panels 26a, as shown in FIG. 4. The
weight of the product can also apply a force to the bottom handle
14, such that the weight of the product can further press on the
handle 14 and maintain the handle 14 in the folded position in the
first direction X. As will be discussed herein, the top handle 12
can also contain a similar machine fold that also allows it to fold
consistently in the same first direction X as the bottom handle
14.
[0067] Additionally, as the flexible container 10 is evacuated and
less product remains, the bottom handle 14 can continue to provide
support to help the flexible container 10 to remain standing
upright unsupported and without tipping over. Because the bottom
handle 14 is sealed generally along its entire length extending
between the pair of gusset panels 18 and 20, it can help to keep
the gussets 54 and 56 (FIG. 1, FIG. 3) together and continue to
provide support to stand the container 10 upright even as the
container 10 is emptied.
[0068] As seen in FIGS. 1, 3, and 5, the top handle 12 can extend
from the top segment 28 and, in particular, can extend from the
four panels 28a-28d that make up the top segment 28. The four
panels 28a-28d of film that extend into the top handle 12 are all
sealed together to form a multi-layer top handle 12. The top handle
12 can have a U-shape and, in particular, an upside down U-shape
with a horizontal upper handle portion 12a having two pairs of
spaced legs 13 and 15 extending therefrom. The pair of legs 13 and
15 extend from the top segment 28, adjacent the neck portion
30.
[0069] A portion of the top handle 12 can extend above the neck
portion 30 and above the top segment 28 when the handle 12 is
extended in a position perpendicular to the top segment 28 and, in
particular, the entire upper handle portion 12a can be above the
flare portion 50 and the top segment 28. The two pairs of legs 13
and 15 along with the upper handle portion 12a together make up the
handle 12 surrounding a handle opening that allows a user to place
their hand therethrough and grasp the upper handle portion 12a of
the handle 12.
[0070] As with the bottom handle 14, the top handle 12 also can
have a dead machine fold that permits folding in a first direction
toward the front side panel 22 and restricts folding in a second
direction toward the rear side panel 24. The machine fold can be
located in each of the pair of legs 13, 15 at a location where the
seal begins. The handle 12 can be adhered together, such as with a
tack adhesive, for example. The machine fold in the handle 12 can
allow for the handle 12 to be inclined to fold or bend consistently
in the same first direction X as the bottom handle 14, rather than
in the second direction Y. As shown in FIGS. 1, 3, and 5, the
handle 12 can likewise contain a flap portion 36, that folds
upwards toward the upper handle portion 12a of the handle 12 to
create a smooth gripping surface of the handle 12, as with the
bottom handle 14, such that the handle material is not sharp and
can protect the user's hand from getting cut on any sharp edges of
the handle 12.
[0071] In an embodiment, either top handle 12 or bottom handle 14
can be "a punch-out handle," that is, a handle formed by a process
the cuts out or "punches" film material from the flexile container,
thereby removing film material from the flexible container. The
punch-out handle does not have, or is otherwise void of, flap
portion 36 (for top handle 12) and/or flap portion 38 (for bottom
handle 14).
[0072] In an embodiment, a grip member can be attached to either
the top handle 12 or the bottom handle 14. The grip member can be
placed around top handle 12 and/or bottom handle 14. Grip member
can also be molded into the flexible container. The grip member can
be adhesively attached to any portion of the flexible container.
The grip member provides additional comfort to the user when
carrying, or otherwise using, the flexible container. The grip
member provides additional reinforcement to the flexible container.
In a further embodiment, the grip member can be removed from the
flexible container 10 after use and be re-used with another
flexible container.
[0073] When the container 10 is in a rest position, such as when it
is standing upright on its bottom segment 26, as shown in FIG. 3,
the bottom handle 14 can be folded underneath the container 10
along the bottom machine fold 42 in the first direction X, so that
it is parallel to the bottom segment 26 and adjacent bottom panel
26a, and the top handle 12 will automatically fold along Its
machine fold in the same first direction X, with a front surface of
the handle 12 parallel to a top section or panel 28a of the top
segment 28. The top handle 12 folds in the first direction X,
rather than extending straight up, perpendicular to the top segment
28, because of the machine fold. Both handles 12 and 14 are
inclined to fold in the same direction X, such that upon
dispensing, the handles can fold the same direction, relatively
parallel to its respective end panel or end segment, to make
dispensing easier and more controlled. Therefore, in a rest
position, the handles 12 and 14 are both folded generally parallel
to one another. Additionally, the container 10 can stand upright
even with the bottom handle 14 positioned underneath the upright
container 10.
[0074] The material of construction of the flexible container 10
can comprise food-grade plastic. For instance, nylon,
polypropylene, polyethylene such as high density polyethylene
(HDPE) and/or low density polyethylene (LDPE) may be used as
discussed later. The film of the plastic container 10 can have a
thickness and barrier properties that is adequate to maintain
product and package integrity during manufacturing, distribution,
product shelf life and customer usage.
[0075] In an embodiment, the flexible multilayer film has a
thickness from 100 micrometers, or 200 micrometers, or 250
micrometers to 300 micrometers, or 350 micrometers, or 400
micrometers. In an embodiment, the film material provides the
appropriate atmosphere within the flexible container 10 to maintain
the product shelf life of at least about 180 days. Such films can
comprise an oxygen barrier film, such as a film having a low oxygen
transmission rate (OTR) from greater than 0 to 0.4
cc/m.sup.2/atm/24 hrs at 23.degree. C. and 80% relative humidity
(RH). Additionally, the flexible multilayer film can also comprise
a water vapor barrier film, such as a film having a low water vapor
transmission rate (WVTR) from greater than 0 to 15 g/m.sup.2/24 hrs
at 38.degree. C. and 90% RH. Moreover, it may be desirable to use
materials of construction having oil and/or chemical resistance
particularly in the seal layer, but not limited to just the seal
layer. The flexible multilayer film can be either printable or
compatible to receive a pressure sensitive label or other type of
label for displaying of indicia on the flexible container 10.
[0076] In an embodiment the film can also be made of non-food grade
resins for producing containers for materials other than food.
[0077] In an embodiment, each panel is made from a flexible
multilayer film having at least one, or at least two, or at least
three layers. The flexible multilayer film is resilient, flexible,
deformable, and pliable. The structure and composition of the
flexible multilayer film for each panel may be the same or
different. For example, each of the four panels can be made from a
separate web, each web having a unique structure and/or unique
composition, finish, or print. Alternatively, each of the four
panels can be the same structure and the same composition.
[0078] In an embodiment, each panel 18, 20, 22, 24 is a flexible
multilayer film having the same structure and the same
composition.
[0079] The flexible multilayer film may be (i) a coextruded
multilayer structure or (ii) a laminate, or (iii) a combination of
(i) and (ii). In an embodiment, the flexible multilayer film has at
least three layers: a seal layer, an outer layer, and a tie layer
between. The tie layer adjoins the seal layer to the outer layer.
The flexible multilayer film may include one or more optional inner
layers disposed between the seal layer and the outer layer.
[0080] In an embodiment, the flexible multilayer film is a
coextruded film having at least two, or three, or four, or five, or
six, or seven to eight, or nine, or 10, or 11, or more layers. Some
methods, for example, used to construct films are by cast
co-extrusion or blown co-extrusion methods, adhesive lamination,
extrusion lamination, thermal lamination, and coatings such as
vapor deposition. Combinations of these methods are also possible.
Film layers can comprise, in addition to the polymeric materials,
additives such as stabilizers, slip additives, antiblocking
additives, process aids, clarifiers, nucleators, pigments or
colorants, fillers and reinforcing agents, and the like as commonly
used in the packaging industry. It is particularly useful to choose
additives and polymeric materials that have suitable organoleptic
and or optical properties.
[0081] In another embodiment, the flexible multilayer film can
comprise a bladder wherein two or more films that are adhered in
such a manner as to allow some delamination of one or more plies to
occur during a significant impact such that the inside film
maintains integrity and continues to hold contents of the
container.
[0082] Nonlimiting examples of suitable polymeric materials for the
seal layer include olefin-based polymer (including any
ethylene/C.sub.3-C.sub.10 .alpha.-olefin copolymers linear or
branched), propylene-based polymer (including plastomer and
elastomer, random propylene copolymer, propylene homopolymer, and
propylene impact copolymer), ethylene-based polymer (including
plastomer and elastomer, high density polyethylene ("HDPE"), low
density polyethylene ("LDPE"), linear low density polyethylene
("LLDPE"), medium density polyethylene ("MDPE"), ethylene-acrylic
acid or ethylene-methacrylic acid and their ionomers with zinc,
sodium, lithium, potassium, magnesium salts, ethylene vinyl acetate
copolymers and blends thereof.
[0083] Nonlimiting examples of suitable polymeric material for the
outer layer include those used to make biaxially or monoaxially
oriented films for lamination as well as coextruded films. Some
nonlimiting polymeric material examples are biaxially oriented
polyethylene terephthalate (OPET), monoaxially oriented nylon
(MON), biaxially oriented nylon (BON), and biaxially oriented
polypropylene (BOPP). Other polymeric materials useful in
constructing film layers for structural benefit are polypropylenes
(such as propylene homopolymer, random propylene copolymer,
propylene impact copolymer, thermoplastic polypropylene (TPO) and
the like, propylene-based plastomers (e.g., VERSIFY.TM. or
VISTAMAX.TM.)), polyamides (such as Nylon 6, Nylon 6,6, Nylon 6,66,
Nylon 6,12, Nylon 12 etc.), polyethylene norbornene, cyclic olefin
copolymers, polyacrylonitrile, polyesters, copolyesters (such as
PETG), cellulose esters, polyethylene and copolymers of ethylene
(e.g., LLDPE based on ethylene octene copolymer such as DOWLEX.TM.,
blends thereof, and multilayer combinations thereof.
[0084] Nonlimiting examples of suitable polymeric materials for tie
layer include functionalized ethylene-based polymers such as
ethylene-vinyl acetate ("EVA"), polymers with maleic
anhydride-grafted to polyolefins such as any polyethylene,
ethylene-copolymers, or polypropylene, and ethylene acrylate
copolymers such an ethylene methyl acrylate ("EMA"), glycidyl
containing ethylene copolymers, propylene and ethylene based olefin
block copolymers INFUSE.TM. Olefin Block Copolymers available for
the Dow Chemical Company and INTUNE.TM. (PP-based Olefin Block
Copolymers available from The Dow Chemical Company, and blends
thereof.
[0085] The flexible multilayer film may include additional layers
which may contribute to the structural integrity or provide
specific properties. The additional layers may be added by direct
means or by using appropriate tie layers to the adjacent polymer
layers. Polymers which may provide additional mechanical
performance such as stiffness or opacity, as well polymers which
may offer gas barrier properties or chemical resistance can be
added to the structure.
[0086] Nonlimiting examples of suitable material for the optional
barrier layer include copolymers of vinylidene chloride and methyl
acrylate, methyl methacrylate or vinyl chloride (e.g., SARAN resins
available from The Dow Chemical Company); vinylethylene vinyl
alcohol (EVOH), metal foil (such as aluminum foil). Alternatively,
modified polymeric films such as vapor deposited aluminum or
silicon oxide on such films as BON, OPET, or OPP, can be used to
obtain barrier properties when used in laminate multilayer
film.
[0087] In an embodiment, the flexible multilayer film includes a
seal layer selected from LLDPE (sold under the trade name
DOWLEX.TM. (The Dow Chemical Company)), single-site LLDPE
substantially linear, or linear ethylene alpha-olefin copolymers,
including polymers sold under the trade name AFFINITY.TM. or
ELITE.TM. (The Dow Chemical Company) for example, propylene-based
plastomers or elastomers such as VERSIFY.TM. (The Dow Chemical
Company), and blends thereof. An optional tie layer is selected
from either ethylene-based olefin block copolymer PE-OBC (sold as
INFUSE.TM.) or propylene-based olefin block copolymer PP-OBC (sold
as INTUNE.TM.). The outer layer includes greater than 50 wt % of
resin(s) having a melting point, Tm, that is from 25.degree. C., to
30.degree. C., or 40.degree. C. or higher than the melting point of
the polymer in the seal layer wherein the outer layer polymer is
selected from resins such as VERSIFY or VISTAMAX, ELITE.TM., HDPE
or a propylene-based polymer such as propylene homopolymer,
propylene impact copolymer or TPO.
[0088] In an embodiment, the flexible multilayer film is
co-extruded.
[0089] In an embodiment, flexible multilayer film includes a seal
layer selected from LLDPE (sold under the trade name DOWLEX.TM.
(The Dow Chemical Company)), single-site LLDPE (substantially
linear, or linear, olefin polymers, including polymers sold under
the trade name AFFINITY.TM. or ELITE.TM. (The Dow Chemical Company)
for example, propylene-based plastomers or elastomers such as
VERSIFY.TM. (The Dow Chemical Company), and blends thereof. The
flexible multilayer film also includes an outer layer that is a
polyamide.
[0090] In an embodiment, the flexible multilayer film is a
coextruded film and includes:
[0091] (i) a seal layer composed of an olefin-based polymer having
a first melt temperature less than 105.degree. C., (Tm1); and
[0092] (ii) an outer layer composed of a polymeric material having
a second melt temperature, (Tm2),
[0093] wherein Tm2-Tm1>40.degree. C.
[0094] The term "Tm2-Tm1" is the difference between the melt
temperature of the polymer in the outer layer and the melt
temperature of the polymer in the seal layer, and is also referred
to as ".DELTA.Tm." In an embodiment, the .DELTA.Tm is from
41.degree. C., or 50.degree. C., or 75.degree. C., or 100.degree.
C., to 125.degree. C., or 150.degree. C., or 175.degree. C., or
200.degree. C.
[0095] In an embodiment, the flexible multilayer film is a
coextruded film, the seal layer is composed of an ethylene-based
polymer, such as a linear or a substantially linear polymer, or a
single-site catalyzed linear or substantially linear polymer of
ethylene and an alpha-olefin monomer such as 1-butene, 1-hexene or
1-octene, having a Tm from 55.degree. C. to 115.degree. C. and a
density from 0.865 to 0.925 g/cm.sup.3, or from 0.875 to 0.910
g/cm.sup.3, or from 0.888 to 0.900 g/cm.sup.3 and the outer layer
is composed of a polyamide having a Tm from 170.degree. C. to
270.degree. C.
[0096] In an embodiment, the flexible multilayer film is a
coextruded film having at least five layers, the coextruded film
having a seal layer composed of an ethylene-based polymer, such as
a linear or substantially linear polymer, or a single-site
catalyzed linear or substantially linear polymer of ethylene and an
alpha-olefin comonomer such as 1-butene, 1-hexene or 1-octene, the
ethylene-based polymer having a Tm from 55.degree. C. to
115.degree. C. and density from 0.865 to 0.925 g/cm.sup.3, or from
0.875 to 0.910 g/cm.sup.3, or from 0.888 to 0.900 g/cm.sup.3 and an
outermost layer composed of a polyamide having a Tm from
170.degree. C. to 270.degree. C.
[0097] In an embodiment, the flexible multilayer film is a
coextruded film having at least seven layers. The seal layer is
composed of an ethylene-based polymer, such as a linear or
substantially linear polymer, or a single-site catalyzed linear or
substantially linear polymer of ethylene and an alpha-olefin
comonomer such as 1-butene, 1-hexene or 1-octene, the
ethylene-based polymer having a Tm from 55.degree. C. to
115.degree. C. and density from 0.865 to 0.925 g/cm.sup.3, or from
0.875 to 0.910 g/cm.sup.3, or from 0.888 to 0.900 g/cm.sup.3. The
outer layer is a polyamide having a Tm from 170.degree. C. to
270.degree. C.
[0098] In an embodiment, the flexible multilayer film includes a
seal layer composed of an ethylene-based polymer, or a linear or
substantially linear polymer, or a single-site catalyzed linear or
substantially linear polymer of ethylene and an alpha-olefin
monomer such as 1-butene, 1-hexene or 1-octene, having a heat seal
initiation temperature (HSIT) from 65.degree. C. to less than
125.degree. C. Applicant discovered that the seal layer with an
ethylene-based polymer with a HSIT from 65.degree. C. to less than
125.degree. C. advantageously enables the formation of secure seals
and secure sealed edges around the complex perimeter of the
flexible container. The ethylene-based polymer with HSIT from
65.degree. C. to less than 125.degree. C. is a robust sealant which
also allows for better sealing to the rigid fitment which is prone
to failure. The ethylene-based polymer with HSIT from 65.degree. C.
to 125.degree. C. enables lower heat sealing pressure/temperature
during container fabrication. Lower heat seal pressure/temperature
results in lower stress at the fold points of the gusset, and lower
stress at the union of the films in the top segment and in the
bottom segment. This improves film integrity by reducing wrinkling
during the container fabrication. Reducing stresses at the folds
and seams improves the finished container mechanical performance.
The low HSIT ethylene-based polymer seals at a temperature below
what would cause the outer layer to be compromised.
[0099] In an embodiment, the flexible multilayer film is a
coextruded five layer film, or a coextruded seven layer film having
at least two layers containing an ethylene-based polymer. The
ethylene-based polymer may be the same or different in each
layer.
[0100] In an embodiment, the flexible multilayer film is a
coextruded five layer, or a coextruded seven layer film having at
least two layers containing a polyamide polymer.
[0101] In an embodiment, the flexible multilayer film is a
seven-layer coextruded film with a seal layer composed of an
ethylene-based polymer, or a linear or substantially linear
polymer, or a single-site catalyzed linear or substantially linear
polymer of ethylene and an alpha-olefin monomer such as 1-butene,
1-hexene or 1-octene, having a Tm from 90.degree. C. to 104.degree.
C. The outer layer is a polyamide having a Tm from 170.degree. C.
to 270.degree. C. The film has a .DELTA.Tm from 40.degree. C. to
200.degree. C. The film has an inner layer (first inner layer)
composed of a second ethylene-based polymer, different than the
ethylene-based polymer in the seal layer. The film has an inner
layer (second inner layer) composed of a polyamide the same or
different to the polyamide in the outer layer. The seven layer film
has a thickness from 100 micrometers to 250 micrometers.
[0102] FIG. 6 shows an enlarged view of the bottom seal area 33
(area 6) of FIG. 1 and the front panel 26a. The fold lines 60 and
62 of respective gusset panels 18, 20 are separated by a distance U
that is from 0 mm, or greater than 0 mm, or 0.5 mm, or 1.0 mm, or
2.0 mm, or 3.0 mm, or 4.0 mm, or 5.0 mm to 12.0 mm, or greater than
60.0 mm (for larger containers, for example). In an embodiment,
distance U is from greater than 0 mm to less than 6.0 mm. FIG. 6
shows line A (defined by inner edge 29a) intersecting line B
(defined by inner edge 29b) at apex point 35a. BDISP 37a is on the
distal inner seal arc 39a. Apex point 35a is separated from BDISP
37a by S having a length from greater than 0 mm or 1.0 mm, or 2.0
mm, or 2.6 mm, or 3.0 mm, or 3.5 mm, or 3.9 mm to 4.0 mm, or 4.5
mm, or 5.0 mm, or 5.2 mm, or 5.5 mm, or 6.0 mm, or 6.5 mm, or 7.0
mm, or 7.5 mm, or 7.9 mm.
[0103] In FIG. 6, an overseal 64 is formed where the four
peripheral tapered seals 40a-40d converge in the bottom seal area.
The overseal 64 includes 4-ply portions 66, where a portion of each
panel is heat sealed to a portion of every other panel. Each panel
represents 1-ply in the 4-ply heat seal. The overseal 64 also
includes a 2-ply portion 68 where two panels (front panel and rear
panel) are sealed together. Consequently, the "overseal," as used
herein, is the area where the peripheral tapered seals converge
that is subjected to a subsequent heat seal operation (and
subjected to at least two heat seal operations altogether). The
overseal is located in the peripheral tapered seals and does not
extend into the chamber of the flexible container 10.
[0104] In an embodiment, the apex point 35a is located above the
overseal 64. The apex point 35a is separated from, and does not
contact the overseal 64. The BDISP 37a is located above the
overseal 64. The BDISP 37a is separated from and does not contact
the overseal 64.
[0105] In an embodiment, the apex point 35a is located between the
BDISP 37a and the overseal 64, wherein the overseal 64 does not
contact the apex point 35a and the overseal 64 does not contact the
BDISP 37a.
[0106] The distance between the apex point 35a to the top edge of
the overseal 64 is defined as distance W shown in FIG. 6. In an
embodiment, the distance W has a length from 0 mm, or greater than
0 mm, or 2.0 mm, or 4.0 mm to 6.0 mm, or 8.0 mm, or 10.0 mm or 15.0
mm.
[0107] When more than four webs are used to produce the container,
the portion 68 of the overseal 64 may be a 4-ply, or a 6-ply, or an
8-ply portion.
[0108] In an embodiment, the flexible container 10 has a vertical
drop test pass rate from 90%, or 95% to 100%. The vertical drop
test is conducted as follows. The container is filled with tap
water to its nominal capacity, conditioned at 25.degree. C. for at
least 3 hours, held in upright position from its upper handle at
1.5 m height (from the base or side of the container to the
ground), and released to a free fall drop onto a concrete slab
floor. If any leak is detected immediately after the drop, the test
is recorded as a failure. A minimum of twenty flexible containers
are tested. A percentage for pass/fail containers is then
calculated.
[0109] In an embodiment, the flexible container 10 has a side drop
pass rate from 90%, or 95% to 100%. This side drop test is
conducted as follows. The container is filled with tap water to its
nominal capacity, conditioned at 25.degree. C. for at least 3
hours, held in upright position from its upper handle. The flexible
container is released on its side from a 1.5 m height to a free
fall drop onto a concrete slab floor. If any leak is detected
immediately after the drop, the test is recorded as failure. A
minimum of twenty flexible containers are tested. A percentage for
pass/fail containers is then calculated.
[0110] In an embodiment, the flexible container 10 passes the
stand-up test where the package is filled with water at ambient
temperature and placed on a flat surface for seven days and it
should remain in the same position, with unaltered shape or
position.
[0111] In an embodiment, the flexible container 10 has a volume
from 0.050 liters (L), or 0.1 L, or 0.15 L, or 0.2 L, or 0.25
liters (L), or 0.5 L, or 0.75 L, or 1.0 L, or 1.5 L, or 2.5 L, or 3
L, or 3.5 L, or 4.0 L, or 4.5 L, or 5.0 L to 6.0 L, or 7.0 L, or
8.0 L, or 9.0 L, or 10.0 L, or 20 L, or 30 L.
[0112] The flexible container 10 can be used to store any number of
flowable substances therein. In particular, a flowable food product
can be stored within the flexible container 10. In one aspect,
flowable food products such as salad dressings, sauces, dairy
products, mayonnaise, mustard, ketchup, other condiments, beverages
such as water, juice, milk, or syrup, carbonated beverages, beer,
wine, animal feed, pet feed, and the like can be stored inside of
the flexible container 10.
[0113] The flexible container 10 is suitable for storage of other
flowable substances including, but not limited to, oil, paint,
grease, chemicals, suspensions of solids in liquid, and solid
particulate matter (powders, grains, granular solids).
[0114] The flexible container 10 is suitable for storage of
flowable substances with higher viscosity and requiring application
of a squeezing force to the container in order to discharge.
Nonlimiting examples of such squeezable and flowable substances
include grease, butter, margarine, soap, shampoo, animal feed,
sauces, and baby food.
[0115] 2. Fitment
[0116] The present process includes inserting a fitment into the
flare portion 50 from the expanded end 51. As shown in FIGS. 7-17,
the fitment 70 includes a base 72 and a closure 74. Although the
base 72 has a circular cross-sectional shape, it is understood that
the base 72 can have other cross-sectional shapes such as a
polygonal cross-sectional shape, for example. The base 72 with
circular cross-sectional shape is distinct from fitments with
canoe-shaped bases used for conventional two-panel flexible
pouches.
[0117] In an embodiment, the outer surface of the base 72 has
surface texture. The surface texture can include embossment 73, and
a plurality of radial ridges to promote sealing to the inner
surface of the neck portion 30 as will be discussed below.
[0118] In an embodiment, the fitment 70 excludes fitments with
oval, wing-shaped, eye-shaped, or canoe-shaped bases.
[0119] Although FIGS. 7-17 show a screw-on type closure (for use
with a mated screw-on cap), it is understood that the fitment 70
may embody other closure systems. Nonlimiting examples of suitable
fitments and closures, include, screw cap, flip-top cap, snap cap,
liquid or beverage dispensing fitments (stop-cock or thumb
plunger), Colder fitment connector, tamper evident pour spout,
vertical twist cap, horizontal twist cap, aseptic cap, vitop press,
press tap, push on tap, lever cap, conro fitment connector, and
other types of removable (and optionally reclosable) closures. The
closure and/or fitment may or may not include a gasket.
[0120] In an embodiment, the closure 74 is watertight. In a further
embodiment, the closure 74 provides a hermetic seal to the
container 10.
[0121] In an embodiment, the fitment 70 can be made of a rigid
construction and can be formed of any appropriate plastic, such as
high density polyethylene (HDPE), low density polyethylene (LDPE),
polypropylene (PP), and combinations thereof. The location of the
neck portion 30 can be anywhere on the top segment 28 of the
container 10. In an embodiment the neck portion 30 is located at
the center or midpoint of the top segment 28.
[0122] In an embodiment, the fitment is made by co-injection of a
two-component structure A/B wherein A is an inside material having
a melting point, Tm, greater than the Tm of an outside material B
(seal side). In another embodiment, the materials A and B are
different types of materials, where an optional tie layer C adheres
material A to material B. In a further embodiment, the outside
material B has a low coefficient of friction (COF) to facilitate
fitment insertion into the neck portion 30.
[0123] In an embodiment, the fitment 70 includes a polymeric
composition having an Izod impact resistance from greater than 50
Joules (J)/meter (m), or 100 J/m, or 150 J/m, or 200 J/m, or 250
J/m to 300 J/m, or 350 J/m, or 400 J/m, or 450 J/m, or 500 J/m.
Izod impact resistance is measured in accordance with ASTM D 256.
In a further embodiment, the fitment includes a polyolefin having
an Izod impact resistance from greater than 50 J/m, or 100 J/m, or
150 J/m, or 200 J/m, or 250 J/m to 300 J/m, or 350 J/m, or 400 J/m,
or 450 J/m, or 500 J/m.
[0124] In an embodiment, the fitment 70 includes a polymeric
composition containing a polyolefin with a melt temperature (Tm)
greater than or equal to the melt temperature of the polyolefin
present in the seal layer of the multilayer film used to make the
panels. When clamp heat sealing is utilized to form the seal
between the base 72 and the neck portion 30, a nonlimiting example
includes a fitment 70 composed of a HDPE having a Tm of 125.degree.
C. and the seal layer for the container 10 contains an LDPE with a
Tm of 105.degree. C. Another nonlimiting example is a fitment 70
composed of LLDPE with Tm of 120.degree. C., and the container 10
has a seal layer containing an ethylene/.alpha.-olefin copolymer
(AFFINITY.TM. PL 1140G) with a Tm 96.degree. C.
[0125] In an embodiment, the process includes supporting the
fitment 70 on a mandrel 80, and subsequently inserting the fitment
70 first into the expanded end 51, then into the flare portion 50,
and then into the neck portion 30. A plurality of fitments may be
fed sequentially to the mandrel 80 by an automated feed system as
shown in FIGS. 7-8. FIG. 7 shows the mandrel 80 moving into
position to receive and support one of a plurality of fitments 70.
Although FIG. 7 shows the mandrel 80 having a length similar to the
length of the closure 74, it is understood that the mandrel 80 can
have a length the same as, or substantially the same as, or greater
than, the length of the fitment 70. In other words, the mandrel 80
can partially support, or fully support, the fitment 70, the base
72, the closure 74, and any combination thereof.
[0126] FIG. 8 shows the fitment 70 supported on the mandrel 80. The
outer diameter of the mandrel 80 is mated to the inner diameter of
the fitment 70 such that the fitment 70 fits, snugly fits, or
friction fits on the mandrel 80. In other words, the mandrel 80 is
configured to fit into/through the closure 74, or into/through both
the closure 74 and the base 72.
[0127] In an embodiment, the mandrel 80 is a component of an
automated system, the mandrel a component of a movable arm as shown
in FIGS. 7-16.
[0128] FIG. 9 shows the fitment 70 (supported by the mandrel 80)
approaching the expanded end 51 of the flare portion 50. FIG. 10
shows the fitment 70 (supported by the mandrel 80) entering
through, or otherwise inserting into, the expanded end 51 and into
the flare portion 50. In FIG. 11, the fitment 70 (supported by the
mandrel 80) continues to move, and continues to enter into, or
continues to insert into, the neck portion 30. In an embodiment,
the outer diameter of the base 72 is the same as, or slightly less
than, the inner diameter of the neck portion 30 such that the base
72 snugly fits, or otherwise friction fits, into the neck portion
30.
[0129] Although FIGS. 7-11 show the mandrel 80 (with fitment 70)
moving toward the flexible container 10, it is understood that the
flexible container 10 may be moved toward the mandrel 80
(supporting the fitment 70), the mandrel 80 being stationary, or
intermittently stationary and intermittently movable, during the
insertion process. Alternatively, the process may entail a system
whereby the flexible container 10 and the mandrel 80 each is
movable with respect to the other, such that the flexible container
10 and the fitment 70 (supported by the mandrel 80) can each be
moved toward and away from the other in order to insert the fitment
70 into the expanded end 51, through the flare portion 50, and into
the neck portion 30.
[0130] In an embodiment, the process includes adjoining the fitment
70 to the neck portion 30. As shown in FIG. 11, the base 72 of the
fitment 70 is inserted into the neck portion 30, with the outer
surface of the base 72 adjoined to the inner surface of the base 72
by way of friction fit, compression fit, an adhesive composition,
and combinations thereof.
[0131] With the base 72 located in the neck portion 30, an
embodiment of the process includes heat sealing the base 72 of the
fitment 70 to the neck portion 30. The heat sealing procedure
utilizes opposing heat seal clamps 90, 92 as shown in FIGS. 12-13.
The heat seal clamps are heated to a temperature greater than or
equal to the melt temperature (Tm) of the seal layer of the
multilayer film and less than the melt temperature of the fitment
70. The heat seal clamps 90, 92 compress the seal layer of the
multilayer film against the outer surface of the base 72 for a
duration from 0.1 seconds, or 0.5 seconds, or 1.0 second, or 2.0
seconds, or 3.0 seconds, or 4.0 seconds, or 5.0 seconds to 6.0
seconds, or 7.0 seconds, or 8.0 seconds, or 9.0 seconds or 10
seconds. The mandrel 80 supports the fitment 70 during the contact
and compression between the heat seal clamps 90, 92 and the neck
portion 30. In an embodiment, the process includes supporting the
base 72 with the mandrel 80 during the seal process. The seal
process can be clamp heat seal or ultrasonic seal. Support of the
fitment 70 by the mandrel 80 advantageously avoids deformation of
the fitment 70 (and the base 72 and the closure 74) during the heat
seal procedure.
[0132] In an embodiment, the process includes ultrasonic sealing
the base 72 of the fitment 70 to the neck portion 30. Ultrasonic
sealing entails directing ultrasonic vibration to the interface
between the base 72 and the neck portion 30 while pressure is
applied. The ultrasonic energy melts a portion of the interface to
create a seal between the base 72 and the neck portion 30. In an
embodiment, the process includes ultrasonically sealing a base 72
composed of ethylene/.alpha.-olefin copolymer such as ELITE.TM.
(4.0 MI and 122.degree. C. Tm) to a neck portion 30 having seal
layer composed of ethylene/.alpha.-olefin copolymer ELITE.TM. 5400G
(1.0 MI, 122.degree. C. Tm) and/or ethylene/.alpha.-olefin
copolymer AFFINITY.TM. PL 1880G (1.0 MI, 99.degree. C. Tm).
[0133] Since ultrasonic sealing heats only the seal layer, the Tm
of the seal layer can be from 10.degree. C. to 5.degree. C. less
than the Tm of the fitment. In an embodiment, the process includes
ultrasonically sealing a fitment 70 composed of an
ethylene/.alpha.-olefin copolymer (such as AFFINITY.TM. PL 1880G)
having a Tm of 99.degree. C. to a neck portion 30 having a seal
layer composed of an LDPE with a Tm of 105.degree. C.
[0134] In an embodiment, the process includes rotating the flexible
container 90.degree. or from 80.degree. to 100.degree., with
respect to the heat seal clamps and repeating the heat sealing
procedure described above. FIG. 12 shows the first heat seal
sequence and FIG. 13 shows the second heat seal sequence with the
flexible container 10 rotated 90.degree.. Heat seal clamps 90, 92
move in opposing directions and toward each other to compress heat
seal the neck portion 30 onto the base 72.
[0135] In an embodiment, the process includes forming a watertight
seal between the base 72 and the neck portion 30.
[0136] In an embodiment, the process includes forming a watertight
and airtight seal between the base 72 and the neck portion 30.
[0137] As shown in FIG. 14, the heat seal formed between the neck
portion 30 and the base 72 defines an excess flare portion 96.
Thus, an embodiment of the present process includes forming, with
the adjoining, an excess flare portion.
[0138] In an embodiment, the process includes removing the excess
flare portion 96 from the flexible container 10. FIGS. 14-16 show a
score device 100 placed into contact with the neck portion 30 of
the flexible container 10. A blade portion 102 of the score device
100 contacts the neck portion 30 as the flexible container 10 is
rotated to score, cut, or otherwise disconnect the excess flange
portion 96 from the neck portion 30. The mandrel 80 is then moved
away from the fitment 70 (or vice versa) and the excess score
portion 96 is removed from the flexible container 10. The excess
flare portion 96 may be recycled or discarded.
[0139] In an embodiment, the process includes inserting the fitment
through the flare portion. The mandrel enters the neck portion such
that the fitment base enters the container interior. The mandrel
may extend to such a length that the entire fitment (base and top)
may be inserted, or otherwise enter, the container interior. The
process includes contacting the score device with the neck portion
and supporting the neck portion with the mandrel during the
contacting. The process includes rotating the neck portion (or
rotating the score device) to cut excess flare portion from the
neck portion. In this way, the mandrel supports the neck during
scoring, thereby avoiding cuts to the fitment. The process includes
removing the excess flare portion from the neck portion. Once the
excess flare portion is removed, the process includes retracting,
with the mandrel, the fitment into the neck portion and sealing the
fitment base to the neck portion.
[0140] FIG. 17 shows the completed flexible container 10 having the
fitment 70 inserted thereon. A flowable substance is located in the
container interior. The flexible container 10 is a stand-up
container (otherwise known as a stand-up pouch or SUP).
[0141] In an embodiment, a flowable substance can be added to the
flexible container 10 either before or after the fitment 70 is
inserted into the flare portion 50. The flowable substance can be
any flowable substance (particulate or liquid) as previously
disclosed above. In one embodiment, the process includes inserting
a flowable substance through the fitment 70 that is previously
adjoined to the neck portion 30.
[0142] In another embodiment, the process includes adding a
flowable substance to the flexible container interior before the
fitment 70 is inserted into the expanded end 51. The process
includes adding the flowable substance through the expanded end 51,
through the flare portion 50, through the neck portion 30, and into
the container interior. After flowable substance is added to the
container interior, the fitment 70 can be inserted into the
expanded end 51, into the flare portion 50, and adjoined to the
neck portion 30 as previously discussed above.
[0143] In an embodiment, a carry member is attached to the fitment.
The carry member can be attached to fit around a portion of, or
all, the outer circumference of the fitment by way of one, some, or
all of the following: friction fit, compression fit, and snap-on
fit. The carry member is advantageous when the flexible container
does not include handles. The carry member can also be used to
dispense the contents from the flexible container.
[0144] 3. Sealed Container No Fitment
[0145] The present disclosure provides another process. In an
embodiment, the process includes (A) providing a flexible container
with four panels. The four panels form (i) a body portion, (ii) a
neck portion, (iii) a tapered transition portion between the body
portion and the neck portion, and (iv) the neck portion has a
reduced width. The process includes (B) adding, through the neck, a
flowable substance into the container interior; and (C) sealing the
neck portion.
[0146] The flexible container can be any flexible container as
described above. However, in this embodiment, the flexible
container lacks a fitment (i.e., lacks fitment 70) and the flare
portion is optional.
[0147] In an embodiment, the flexible container does not include,
or is otherwise void of, a flare portion as shown in FIG. 18. The
process includes sealing the neck portion 30 and forming a neck
seal 150. The neck seal 150 can be a heat seal, an adhesive seal,
and a combination thereof.
[0148] In an embodiment, the neck seal 150 is a heat seal.
[0149] The neck seal 150 may include notches 152 (or cut-outs),
and/or a perforation 154 to promote actuation of, or opening, the
neck seal 150. Actuation of the neck seal 150 may be performed by
hand (tear seal) or by way of scissors, blade or other sharp
object.
[0150] In an embodiment, the flexible container 10 includes the
flare portion 50 as shown in FIG. 19. The flare portion 50 has an
expanded end 51, and the width of the flare portion gradually
increases from the neck portion to the flare expanded end, as
previously disclosed herein. The process includes adding a flowable
substance through the expanded end 51, through the flare portion
50, through the neck portion 30, and into the container interior.
With the flowable substance in the container interior, the process
includes sealing the flare portion 50 to form a flare seal 160 as
shown in FIG. 19. The flare portion 50 can be sealed at the
expanded end 51, below the expanded end 51, and combinations
thereof. It is understood that when the flexible container includes
the flare portion, the flare seal replaces, or otherwise
substitutes, the neck seal.
[0151] The flare seal 160 can include notches 162 and/or a
perforation 164 to promote actuation of the flange seal as
disclosed above with respect to the neck seal.
[0152] The flexible container with the neck seal or the flare seal
can be a single use container or a re-sealable container. In an
embodiment, the flexible container is a single use container and
the process includes adding a flowable substance through either the
neck portion 30 (or through the flare portion 50) and into the
container interior. With the flowable substance in the container
interior, the process includes forming a notched seal (also known
as a tear seal) in either the neck portion 30 (notches 152, FIG.
18), or in the flare portion 50 (notches 162, FIG. 19). When the
notched seal is actuated, access to the container interior is
provided and the flowable substance is dispensed through the neck
portion 30 (or the flare portion 50).
[0153] In an embodiment, either the neck seal 150 or the flare seal
160 can be a re-sealable seal. The process includes adding a
flowable substance through the neck 30 (or through the expanded end
51, through the flare portion 50, through the neck portion 30), and
into the container interior. With the flowable substance in the
container interior, the process includes forming a re-sealable seal
in either the neck portion 30 or in the flare portion 50.
[0154] FIG. 18 shows an interlocking rib structure 156 that is a
re-seal structure such as a Zip-loc-type re-seal structure, for
example. Other nonlimiting examples of suitable re-sealable seals
include a peelable seal, a flap seal, an adhesive seal (such as a
pressure sensitive adhesive seal, a zipper seal, hook and loop
re-seal structure (Velcro-type seal), and any combination
thereof.
[0155] In an embodiment, either the neck seal 150 or the flare seal
160 includes a microcapillary strip. With actuation of seal
150/160, the microcapillary strip provides controlled spray
delivery of the container contents.
[0156] In an embodiment, either the neck seal 150 or the flare seal
160 may include a closure. The closure covers the exposed opening
of the neck seal or flare seal after the seal has been actuated.
Nonlimiting examples of suitable closures include a Ziploc-type
closure, hook and loop material (i.e., Velcro), an adhesive strip
(such as packaging tape, for example), and flexible material
hingedly attached to the flexible pouch for placement over the
opened seal.
[0157] The present process may comprise two or more embodiments
disclosed herein.
Definitions
[0158] The numerical ranges disclosed herein include all values
from, and including, the lower value and the upper value. For
ranges containing explicit values (e.g., 1 or 2, or 3 to 5, or 6,
or 7) any subrange between any two explicit values is included
(e.g., 1 to 2; 2 to 6; 5 to 7; 3 to 7; 5 to 6; etc.).
[0159] Unless stated to the contrary, implicit from the context, or
customary in the art, all parts and percents are based on weight,
and all test methods are current as of the filing date of this
disclosure.
[0160] The term "composition," as used herein, refers to a mixture
of materials which comprise the composition, as well as reaction
products and decomposition products formed from the materials of
the composition.
[0161] The terms "comprising," "including," "having," and their
derivatives, are not intended to exclude the presence of any
additional component, step or procedure, whether or not the same is
specifically disclosed. In order to avoid any doubt, all
compositions claimed through use of the term "comprising" may
include any additional additive, adjuvant, or compound, whether
polymeric or otherwise, unless stated to the contrary. In contrast,
the term, "consisting essentially of" excludes from the scope of
any succeeding recitation any other component, step or procedure,
excepting those that are not essential to operability. The term
"consisting of" excludes any component, step or procedure not
specifically delineated or listed.
[0162] Dart drop test is measured in accordance with ASTM D 1709
with results reported in grams, g.
[0163] Density is measured in accordance with ASTM D 792 with
results reported as grams per cubic centimeter, or g/cm.sup.3.
[0164] Elmendorf tear, machine direction, MD, cross direction CD,
is measured in accordance with ASTM D 1922, with results reported
in grams, g.
[0165] An "ethylene-based polymer," as used herein is a polymer
that contains more than 50 mole percent polymerized ethylene
monomer (based on the total amount of polymerizable monomers) and,
optionally, may contain at least one comonomer.
[0166] Flexural modulus (2%) is measured in accordance with ASTM D
790 with results reported in megaPascals, MPa.
[0167] The term "heat seal initiation temperature," is minimum
sealing temperature required to form a seal of significant
strength, in this case, 2 lb/in (8.8N/25.4 mm). The seal is
performed in a Topwave HT tester with 0.5 seconds dwell time at 2.7
bar (40 psi) seal bar pressure. The sealed specimen is tested in an
Instron Tensiomer at 10 in/min (4.2 mm/sec or 250 mm/min).
[0168] Izod impact resistance is measured at 25.degree. C. and in
accordance with ASTM D 256 with results reported in Joules per
meter, J/m.
[0169] Melt flow rate (MFR) is measured in accordance with ASTM D
1238, Condition 280.degree. C./2.16 kg (g/10 minutes).
[0170] Melt index (MI) is measured in accordance with ASTM D 1238,
Condition 190.degree. C./2.16 kg (g/10 minutes).
[0171] Secant modulus (2%), MD and CD, is measured in accordance
with ASTM D 882 with results reported as megaPascals, or MPa.
[0172] Strain at tensile strength, MD and CD, is measured in
accordance with ASTM D 882 with results reported as percent, %.
[0173] Tensile elongation to break is measured in accordance with
ASTM D 638 with results reported in percent, %.
[0174] Tensile strength, MD and CD, is measured in accordance with
ASTM D 882 with results reported as megaPascals, or MPa.
[0175] Tensile strength to yield is measured in accordance with
ASTM D 638 results reported in megaPascals, MPa.
[0176] Tm or "melting point" as used herein (also referred to as a
melting peak in reference to the shape of the plotted DSC curve) is
typically measured by the DSC (Differential Scanning calorimetry)
technique for measuring the melting points or peaks of polyolefins
as described in U.S. Pat. No. 5,783,638. It should be noted that
many blends comprising two or more polyolefins will have more than
one melting point or peak, many individual polyolefins will
comprise only one melting point or peak.
[0177] An "olefin-based polymer," as used herein is a polymer that
contains more than 50 mole percent polymerized olefin monomer
(based on total amount of polymerizable monomers), and optionally,
may contain at least one comonomer. Nonlimiting examples of
olefin-based polymer include ethylene-based polymer and
propylene-based polymer.
[0178] A "polymer" is a compound prepared by polymerizing monomers,
whether of the same or a different type, that in polymerized form
provide the multiple and/or repeating "units" or "mer units" that
make up a polymer. The generic term polymer thus embraces the term
homopolymer, usually employed to refer to polymers prepared from
only one type of monomer, and the term copolymer, usually employed
to refer to polymers prepared from at least two types of monomers.
It also embraces all forms of copolymer, e.g., random, block, etc.
The terms "ethylene/.alpha.-olefin polymer" and
"propylene/.alpha.-olefin polymer" are indicative of copolymer as
described above prepared from polymerizing ethylene or propylene
respectively and one or more additional, polymerizable
.alpha.-olefin monomer. It is noted that although a polymer is
often referred to as being "made of" one or more specified
monomers, "based on" a specified monomer or monomer type,
"containing" a specified monomer content, or the like, in this
context the term "monomer" is understood to be referring to the
polymerized remnant of the specified monomer and not to the
unpolymerized species. In general, polymers herein are referred to
has being based on "units" that are the polymerized form of a
corresponding monomer.
[0179] A "propylene-based polymer" is a polymer that contains more
than 50 mole percent polymerized propylene monomer (based on the
total amount of polymerizable monomers) and, optionally, may
contain at least one comonomer.
[0180] Some embodiments of the present disclosure will now be
described in detail in the following Examples.
EXAMPLES
[0181] 1. Materials
[0182] Four panel flexible containers having a neck and a body as
shown in FIGS. 1-6 are formed using the seven-layer film provided
in Table 1. The containers used in the present examples and in the
comparative samples (CS) are produced with a volume of 3.875 L
using a 150 micrometer (.mu.m) seven-layer film ISO X7-7135C-1TC
produced by ISO Poly Films (Gray Court, S.C.) as shown in Table
1.
TABLE-US-00001 TABLE 1 Composition of 7-layer coextruded flexible
multilayer film % Thick- Weight Den- Overall Description ness %
Layer sity ULTRA- Nylon 6/66 viscosity 13.0% 15.3% 1 1.12 MID
number 195 cm.sup.3/g C33L01 (ISO 307 @ 0.5% in 96%
H.sub.2SO.sub.4), melting point 196.degree. C. (ISO 3146) AMPLIFY
Maleic anhydride 12.0% 11.6% 2 0.922 TY1352 grafted polyethylene
0.922 g/cm.sup.3; 1.0 MI @ 2.16 Kg 190.degree. C. ELITE
Polyethylene density 20.0% 19.2% 3 0.916 5400G 0.916 g/cm.sup.3;
1.0 MI @ 2.16 Kg 190.degree. C. AMPLIFY Maleic anhydride 12.0%
11.6% 4 0.922 TY1352 grafted polyethylene 0.922 g/cm.sup.3; 1.0 MI
@ 2.16 Kg 190.degree. C. ULTRA- Nylon 6/66 viscosity 6.0% 7.0% 5
1.12 MID number 195 cm.sup.3/g C33L01 (ISO 307 @ 0.5% in 96%
H.sub.2SO.sub.4), melting point 196.degree. C. (ISO 3146) AMPLIFY
Maleic anhydride 12.0% 11.6% 6 0.922 TY1352 grafted polyethylene
0.922 g/cm.sup.3; 1.0 MI @ 2.16 Kg 190.degree. C. AFFINITY Ethylene
alpha-olefin 23.6% 22.3% 7* 0.899 PF1146G copolymer 0.899
g/cm.sup.3; 1.0 MI @ 2.16 Kg 190.degree. C. AMPACET Slip
masterbatch 1.0% 1.0% 7* 0.92 10090 (S) available from Ampacet
Corp. AMPACET Antiblock masterbatch 0.4% 0.4% 7* 1.05 10063 (AB)
available from Ampacet Corp. Total 100.0% 100.0% *layer 7 is a
3-component blend, layer 7 is the heat seal layer (or seal
layer)
TABLE-US-00002 TABLE 2 Film Properties for ISO X7-7135C-1TC
Property Method Units Value Dart Drop test ASTM D1709 g 1500 2%
Secant Modulus, ASTM D882 MPa 172 +/12 machine direction (MD) 2%
Secant Modulus, ASTM D882 MPa 180 +/- 15 cross direction (CD) Film
Thickness ASTM D6988 Micro- 152 +/- 2 meters Elmendorf ASTM D1922 g
5553 +/- 692 Tear, MD Elmendorf ASTM D1922 g 5471 +/- 979 Tear, CD
Tensile ASTM D882 MPa 31.2 +/- 0.7 Strength MD Strain at Tensile
ASTM D882 % 434 +/- 12 Strength MD Tensile ASTM D882 MPa 31.0 +/-
1.3 Strength CD Strain at tensile ASTM D882 % 468 +/- 9 Strength
CD
[0183] The flexible containers are fabricated under the heat seal
conditions provided in Table 3 below using fabrication equipment by
KRW Machinery Inc. (Weaverville, N.C.). All seals in the flexible
containers are made with one strike.
TABLE-US-00003 TABLE 3 Heat Seal Conditions for 0.15 mm Films (Web
Sandwich of 0.6 mm, 4 ply) Seal Bar Overseal Temp- Platen Dwell
protrusion erature, Pressure, Time, height, Seal Bar Seals .degree.
C. J/cm.sup.2 sec mm Dimensions Peri- 143 258 0.75 0 10 mm .times.
pheral perimeter for 3.875 L Over- 182 258 0.75 0.30 3.2 mm .times.
25.4 seal mm (overseal bar, centered about the apex point, W = 3.5
mm)
[0184] The flexible containers have the container geometry as
described herein. In particular, each flexible container tested has
the bottom geometry as shown in FIG. 4 and an oversea) shown in
FIG. 6. The distance between the apex point and BDISP (i.e.,
distance S) is approximately 4 mm.
[0185] Table 4 provides nonlimiting examples of materials suitable
to produce a fitment that can be used in the present process. In an
embodiment, the fitment is composed of a material having an Izod
impact resistance from greater than 50 J/m to 500 J/m and shown in
Table 4 below.
TABLE-US-00004 TABLE 4 Fitment Material Performance Flexural
Tensile Tensile Modulus Izod Impact Strength Elongation 2%
Resistance to Yield to Break Secant 25.degree. C. Material Product
density MI (MPa) (%) (MPa) (J/m) Tm (.degree. C.) High Density Dow
HDPE 8262B 0.960 8 29 670 1110 15** 140 Polyethylene High Density
Dow DMDA 8920 0.954 20 28.3 250 1150 21** 130 Polyethylene Low
Density LDPE 9931 (Dow) 0.923 25 10.3 40 317 420 110 Polyethylene
Linear Low Density Dow DNDA 8320 0.924 20 11.7 60 386 -- 123
polyethylene Linear Low Density LLDPE DOWLEX .TM. 0.919 6 8.1 560
328 430 124 polyethylene 2535 Enhanced ELITE .TM. 5230G 0.916 4 9
539 -- -- 122 polyethylene Polypropylene Braskem PP 5E16S 0.910
.sup. 40.sup.+ 32 7 1351* 27** ~165 Homopolymer hPP Polypropylene
A. Shulman 0.900 .sup. 5.sup.+ 20.7 >50 850* 530 ~135 Impact
Copolymer Polypropylene 1188-01 *1% secant modulus .sup.+MFR
**comparative sample
[0186] Comparative Sample 1 (CS1)
[0187] A 3.875 L container blank made at the above conditions of
film ISO X7-7135C-1TC and sealed as in Table 3 having no flare
portion (fully formed container but has not had fitment yet
attached) such that the neck is uniform in diameter. An HDPE
fitment (70) of design shown in FIGS. 7-17 with 38 mm outer
diameter (OD) at threads and 41 mm OD with 1.6 mm wall thickness at
base is inserted into the top of the fully formed blank without any
flare portion. Insertion of the fitment into the top of the neck
results in frequent fold over of the neck film requiring manual
unfolding of the film and resulting in slower speeds of
manufacture. Failure to properly seat the film onto the fitment
prior to sealing can also result in sealing failures at or near
locations where the film is folded over by the insertion process.
10 production runs under these parameters are performed and the
times for each production phase are averaged as shown in Table
5.
Example 1
[0188] A 3.875 L container blank made at the above conditions of
film ISO X7-7135C-1TC and sealed as in Table 3 but having a flare
portion such that top opening is a greater diameter than the neck
diameter. An HDPE fitment 70 of design shown in FIGS. 7-17 with 38
mm OD at threads and 41 mm OD with 1.6 mm wall thickness at base is
inserted directly into the top opening of the flare portion and
into the neck without folds of the film of the neck allowing easy
placement of the fitment into the neck and good sealing of the film
of the neck to the fitment. 10 production runs under these
parameters are performed and the times for each production phase
are averaged as shown in Table 5.
Example 2
[0189] A 3.875 L container blank made at the above conditions of
film ISO X7-7135C-1TC and sealed as in Table 3 but having a flare
portion such that top opening is a greater diameter than the neck
diameter. An HDPE fitment 70 of design shown in FIGS. 7-17 with 38
mm OD at threads and 41 mm OD with 1.6 mm wall thickness at base is
inserted directly into the top opening of the flare portion and
into the neck without folds of the film of the neck allowing easy
placement of the fitment into the neck and good sealing of the film
of the neck to the fitment. The flare portion is hand trimmed at
the bottom of the flare portion with blade against film on fitment
(as in FIGS. 7-16, but by hand). The flare portion is then removed
from the container. 10 production runs under these parameters are
performed and the times for each production phase are averaged as
shown in Table 5.
Example 3
[0190] A 3.875 L container blank made at the above conditions of
film listed in Table 1 above has no fitment but having a flare
portion such that top opening is a greater diameter than the neck
diameter. An HDPE fitment 70 of design shown in FIGS. 7-17 with 38
mm outer diameter (OD) at threads and 41 mm OD with 1.6 mm wall
thickness at base is inserted into the top opening, through the
flare portion but deeper and past the neck to allow the base of the
flare portion to be supported only by the mandrel. The film is then
trimmed at the base of the flare portion on the mandrel support and
the fitment is then pulled back into the neck in position for
sealing. The heat seal is made between the neck portion and the
fitment base. The mandrel is then retracted from the sealed fitment
and the excess flare portion removed. 10 production runs under
these parameters are performed and the times for each production
phase are averaged as shown in Table 5.
[0191] Table 5 shows the production steps from fitment insertion to
heat sealing. These steps constitute the total time to build a
flexible container with fitment, i.e., the "Total Build Time."
Total Build Time is reported in seconds. The values in Table 5 are
an average of 10 production runs under the stated parameters for
each sample.
TABLE-US-00005 TABLE 5 Build time for containers with fitments by
hand 2.sup.nd seal Insertion 1.sup.st Seal, (90 deg), Total
description Insert Trim sec sec seal Total Build (average of 10
time, time, Position 177.degree. C./4.4 177.degree. C./4.4 time,
Time Example builds) sec sec time, sec bar bar sec (sec) CS 1 Base
inserted 60 NA 4 4 2 6 70 into neck by hand and sealed Ex 1 Base
inserted 7 NA 4 4 2 6 17 into flare top/neck by hand and sealed Ex
2 Base insert into 7 20 4 4 2 6 37 flare top/neck, trimmed on
fitment by hand and sealed Ex 3 Base insert into 7 14 4 4 2 6 31
flare top past neck, trimmed on mandrel by hand, pulled back into
neck and sealed
[0192] Examples 1-3 each have a Total Build Time that is less than
the Total Build Time for Comparative Sample 1. Table 5 shows that
provision of the flare portion reduces production time (i.e.,
reduces Total Build Time) and improves production efficiency.
[0193] Comparative Sample 2 (CS2) and Examples 4-5
[0194] Containers are made as in the process described in Example 1
but using an alternate 38 mm fitment material having 1.6 mm wall
thickness. The examples in Table 6 show a fitment consisting of
different materials can be successfully installed. In an
embodiment, the fitments have Izod impact strengths by ASTM D256
from greater than 50 J/m to 500 J/m. Table 6 also shows seals that
have both strength and hermeticity can be achieved as shown by
successful burst and hang tests, respectively.
TABLE-US-00006 TABLE 6 Examples of containers made with fitments of
different materials Seal conditions (Temperature, Ex- seal time,
Burst Hang ample Material Product pressure) test test CS2 High DMDA
8920 177.degree. C., 4 sec Pass Pass (comp- Density 1.sup.st seal,
rotate arative) Poly- 90 deg, 2 sec ethylene seal 2.sup.nd seal,
4.4 bar Ex 4 High DMDA 177.degree. C., 4 sec Pass Pass Density 8920
+ 20% 1.sup.st seal, rotate Poly- ENGAGE .TM. 90 deg, 2 sec
ethylene 8200 seal 2.sup.nd seal, with 4.4 bar modifier Ex 5 Linear
DNDA 8320 177.degree. C., 4 sec Pass Pass Low 1.sup.st seal, rotate
Density- 90 deg, 2 sec poly seal 2.sup.nd seal, ethylene 4.4
bar
[0195] Burst Test Procedure
[0196] Process: [0197] 1.) All flexible containers are
numbered/tagged with testing number, identifying film #, and
production set points (if necessary) [0198] 2.) All flexible
containers are pre-inflated via manual inflation or compressed air.
[0199] 3.) Caps are applied tightly. [0200] 4.) Flexible containers
are placed inside the vacuum pressure chamber and lid is closed.
[0201] 5.) Vacuum pressure is applied via vacuum pump. Pressure
should be applied slowly as flexible container continues to
inflate. [0202] 6.) Units of vacuum are recorded in (inHg).
Exceptional results are 18 (inHG) held for 60 seconds. Passing is
12 (inHg). [0203] 7.) Any weak areas of seal will be exposed as
leaks during the testing time period. Bubbles should be looked for
and can indicate a weak area of the flexible container. [0204] 8.)
The flexible container is filled completely with air and the
closure on the fitment is tightened. Then the flexible container is
completely submerged in a water bath. The chamber over the water is
then evacuated to create a vacuum. A "pass" score for the burst
test is when there are no bubbles visually observed in the water
bath after 30 seconds at 40 kilopascals of vacuum.
[0205] Gravity Hang Test Procedure
[0206] Process: [0207] 1.) All flexible containers are
numbered/tagged with testing number, identifying film #, and
production set points (if necessary) [0208] 2.) All flexible
containers are filled with room temp water to recommended fill
height. [0209] 3.) 3 drops of Methylene Blue die and 3 drops of
surfactant (soap) are added to each flexible container and
agitated. [0210] 4.) Closures are applied tightly to the fitment.
[0211] 5.) Flexible containers are then hung both neck side down
and neck side up to test the strength of both the neck seal and the
caulk seal areas. [0212] 6.) Flexible containers are left hanging
for 48 hours. [0213] 7.) Any weak areas of seal will be exposed as
leaks during the testing time period. [0214] 8.) A "pass" score for
the hang test is hanging the flexible container for 48 hours
without a leak detected. Leaks are detected by visual
identification of white paper below the flexible container to show
any drops that have fallen. The water solution added to the
flexible container contains a blue vegetable dye for aiding visual
detection of the leak. The water solution also contains a drop or
two of soap (Dawn dish soap) where the soap surfactant helps allow
water to penetrate any gaps in seal that might be present.
[0215] Wall thickness is thickness (in mm) of the fitment base.
[0216] For example, the stiffness factor of HDPE 8262B at 1 mm wall
thickness (1.1), is equivalent to the stiffness factor (1.1) of
LLDPE Dowlex 2535 or LDPE 9931 at a wall thickness of 1.5 mm. For a
lower modulus material such as ENGAGE 8401, a wall thickness of 3.3
mm would be required to obtain a stiffness factor of 1.1.
[0217] Applicant discovered that utilization of the present process
(mandrel support of fitment and subsequent fitment insertion into
neck portion via expanded end and flare portion) advantageously
enables "thin-walling," or the reduction of the wall thickness for
the fitment base, permitting the use of thinner walled fitments as
well as the opportunity to use different materials for the
fitments.
[0218] For example, the wall thickness of the fitment base used in
conventional four-sided flexible containers is about 2.0 mm. The
present process advantageously enables "thin-walling," or the
reduction of the wall thickness for the base of the fitment.
Applicant unexpectedly found that the present process enables the
production of a four-panel flexible container with a fitment having
a base wall thickness from 0.15 mm, or 0.2 mm, or 0.3 mm, or 0.5
mm, or 0.7 mm, or 0.9 mm, or 1.0 mm to 1.1 mm, or 1.3 mm, or 1.5
mm, or 1.7 mm, or 1.9 mm.
[0219] It is specifically intended that the present disclosure not
be limited to the embodiments and illustrations contained herein,
but include modified forms of those embodiments including portions
of the embodiments and combinations of elements of different
embodiments as come with the scope of the following claims.
* * * * *