U.S. patent application number 16/592133 was filed with the patent office on 2020-01-30 for overflow downdraw glass tube forming apparatus.
The applicant listed for this patent is CORNING INCORPORATED. Invention is credited to Paul D. Albee, Antoine Gaston Denis Bisson, Olus Naili Boratav, Patrick Joseph Cimo, Glen Bennett Cook, Frank Coppola, Michael Thomas Gallagher, Laurent Joubaud, Irene Mona Peterson, Richard Curwood Peterson, George Clinton Shay, Nicholas Ryan Wheeler.
Application Number | 20200031703 16/592133 |
Document ID | / |
Family ID | 54197053 |
Filed Date | 2020-01-30 |
![](/patent/app/20200031703/US20200031703A1-20200130-D00000.png)
![](/patent/app/20200031703/US20200031703A1-20200130-D00001.png)
![](/patent/app/20200031703/US20200031703A1-20200130-D00002.png)
![](/patent/app/20200031703/US20200031703A1-20200130-D00003.png)
![](/patent/app/20200031703/US20200031703A1-20200130-D00004.png)
![](/patent/app/20200031703/US20200031703A1-20200130-D00005.png)
![](/patent/app/20200031703/US20200031703A1-20200130-D00006.png)
![](/patent/app/20200031703/US20200031703A1-20200130-D00007.png)
![](/patent/app/20200031703/US20200031703A1-20200130-D00008.png)
![](/patent/app/20200031703/US20200031703A1-20200130-D00009.png)
![](/patent/app/20200031703/US20200031703A1-20200130-D00010.png)
View All Diagrams
United States Patent
Application |
20200031703 |
Kind Code |
A1 |
Albee; Paul D. ; et
al. |
January 30, 2020 |
OVERFLOW DOWNDRAW GLASS TUBE FORMING APPARATUS
Abstract
An apparatus for forming glass tubing is described. The
apparatus for forming glass tubing comprises an endless former with
an outer surface and an inner passage defining an inner surface.
The apparatus for forming glass tubing further comprises two
chambers from which molten glass may flow. One chamber flows molten
glass to the outer surface of the endless former and another
chamber flows molten glass to the inner surface of the endless
former. The two flows of molten glass meet at the bottom of the
former to form glass tubing.
Inventors: |
Albee; Paul D.; (Bradford,
VT) ; Bisson; Antoine Gaston Denis; (Bois le Roi,
FR) ; Boratav; Olus Naili; (Ithaca, NY) ;
Cimo; Patrick Joseph; (Corning, NY) ; Cook; Glen
Bennett; (Elmira, NY) ; Coppola; Frank;
(Horseheads, NY) ; Gallagher; Michael Thomas;
(Painted Post, NY) ; Joubaud; Laurent; (Paris,
FR) ; Peterson; Irene Mona; (Elmira Heights, NY)
; Peterson; Richard Curwood; (Elmira Heights, NY)
; Shay; George Clinton; (Hardy, VA) ; Wheeler;
Nicholas Ryan; (Corning, NY) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
CORNING INCORPORATED |
Corning |
NY |
US |
|
|
Family ID: |
54197053 |
Appl. No.: |
16/592133 |
Filed: |
October 3, 2019 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
15508160 |
Mar 2, 2017 |
10472269 |
|
|
PCT/US15/48282 |
Sep 3, 2015 |
|
|
|
16592133 |
|
|
|
|
62045114 |
Sep 3, 2014 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C03B 17/04 20130101;
C03B 17/025 20130101; C03B 17/02 20130101 |
International
Class: |
C03B 17/02 20060101
C03B017/02; C03B 17/04 20060101 C03B017/04 |
Claims
1. An apparatus for forming glass tubing comprising: an endless
former, a first molten glass hold, and a second molten glass hold,
wherein the endless former is positioned substantially vertically
and comprises an upper portion, an outer surface, and a first inner
passage with a first inner surface, the upper portion of the
endless former comprises an extension configured to be fixed in
order to fix the endless former in a substantially vertical
position; wherein the first molten glass hold comprises a first
floor, the first floor comprises a first opening configured for
positioning of the endless former; the first molten glass hold is
positioned so that the first floor is spaced below the extension of
the endless former and the endless former is positioned within the
opening in the first floor defining a glass flow gap between the
endless former and the first floor of the first molten glass hold;
the first floor is configured to permit the flow of molten glass
toward the endless former such that molten glass may pass through
the glass flow gap and down along the outer surface of the endless
former; and wherein the second molten glass hold comprises a second
floor spaced above the first floor and above the extension of the
endless former, the second floor comprises a second opening and a
first neck extending downwardly from the second opening; the first
neck comprises a second inner passage with a second inner surface;
the second floor is configured to permit the flow of molten glass
toward the second opening such that the molten glass may flow into
the second opening and down along the second inner surface of the
first neck; the second molten glass hold is positioned such that
the molten glass flowing into the second opening and the down along
the second inner surface of the first neck will flow down along the
first inner surface of the endless former to meet the molten glass
flowing down along the outer surface of the endless former to form
glass tubing.
2. The apparatus for forming glass tubing of claim 1, wherein the
first molten glass hold is fixed separately from the endless former
to permit adjustment of the first molten glass hold relative to the
endless former; and the second molten glass hold is fixed
separately from the endless former to permit adjustment of the
second molten glass hold relative to the endless former.
3. The apparatus for forming glass tubing of claim 1, wherein the
endless former has a lower portion, the lower portion includes a
bottom and a wedge-shaped portion such that the outer surface and
first inner surface form a taper and meet at the bottom of the
lower portion.
4. The apparatus for forming glass tubing of claim 1, wherein the
first floor includes a first endless upward extension adjacent the
first opening, the first endless upward extension is configured to
impede the flow of molten glass and to cause the molten glass to
flow over the first endless upper extension before passing into the
glass flow gap.
5. The apparatus for forming glass tubing of claim 1, wherein the
second floor includes a second endless upward extension adjacent
the second opening, the second endless upward extension configured
to impede the flow of molten glass and to cause the molten glass to
flow over the second endless upper extension before passing into
the second inner passage of the first neck to flow down along the
second inner surface of the first neck and the first inner surface
of the endless former.
6. The apparatus for forming glass tubing of claim 1, wherein the
first floor includes a first means for regulating the flow of
molten glass and the second floor includes a second means for
regulating the flow of molten glass.
7. The apparatus for forming glass tubing of claim 6, wherein the
first means for regulating flow of molten glass comprises the first
floor having a first endless upward extension adjacent the first
opening, the first endless upward extension is configured to impede
the flow of molten glass and to cause the molten glass to flow over
the first endless upper extension before passing into the glass
flow gap, the first endless upward extension of the first floor
includes a non-uniform height configured to impede the flow of
molten glass to a greater extent from one direction relative to the
flow of molten glass from a different direction; and the second
means for regulating flow of molten glass comprises the second
floor having a second endless upward extension adjacent the second
opening, the second endless upward extension is configured to
impede the flow of molten glass and to require the molten glass to
flow over the second endless upper extension before passing into
the second opening, the second endless upward extension of the
second floor includes a non-uniform height configured to impede the
flow of molten glass to a greater extent from one direction
relative to the flow of molten glass from a different
direction.
8. The apparatus for forming glass tubing of claim 1, further
comprising a third molten glass hold, the third molten glass hold
comprises a third floor spaced above the second floor of the second
molten glass hold; the third floor comprises a third opening and a
second neck extending downwardly from the third opening; the second
neck has a third inner passage with a third inner surface; the
third floor is configured to permit the flow of molten glass toward
the third opening such that molten glass may flow into the third
opening and down along the third inner surface of the second neck;
the third molten glass hold is positioned such that the molten
glass flowing into the third opening and down along the third inner
surface of the second neck will flow down along the second inner
surface of the first neck, down along the first inner surface of
the endless former to meet the molten glass flowing down along the
outer surface of the endless former to form glass tubing.
9. The apparatus for forming glass tubing of claim 1 wherein the
third opening and the second neck of the third molten glass hold
are aligned substantially axially with the first inner passage of
the endless former and the second opening and first neck of the
second floor.
Description
[0001] This application is a divisional of U.S. patent application
Ser. No. 15/508,160 filed Mar. 2, 2017, which claims the benefit of
priority under 35 U.S.C. .sctn. 365 of International Patent
Application Serial No. PCT/US15/48282 filed on Sep. 3, 2015,
designating the United States of America the content of which is
relied upon and incorporated herein by reference in its entirety.
International Patent Application Serial No. PCT/US15/48282 claims
the benefit of priority under 35 U.S.C. .sctn. 119 of U.S.
Provisional Application Ser. No. 62/045,114, filed on Sep. 3, 2014,
the content of each are relied upon and incorporated herein by
reference in their entirety.
BACKGROUND OF THE INVENTION
[0002] The present disclosure relates generally to the manufacture
of fused glass tubing, and, more particularly, to fused glass
tubing formed from an overflow process.
[0003] During glass forming, when surfaces are touched by tooling,
as is typical in current fabrication methods, the surface becomes
damaged. When viewed by the unaided eye, these damages are visible
as optical distortions. Additionally, these defects are easily
viewed as dark lines when observed via Xenon shadowgraph. Damaged
surfaces are undesirable for applications which require the highest
optical quality, similar to that which is achieved with
fusion-formed glass. In addition, defects caused by tooling can
decrease the strength and reliability of a tube.
BRIEF SUMMARY OF THE INVENTION
[0004] One embodiment of the present disclosure is an apparatus for
forming glass tubing that includes an endless former with an
outside surface and an inside surface. The former is "endless"
because it comprises a ring or other closed circuit structure with
no beginning or end. Molten glass may flow along both the outside
and inside surfaces to meet at the bottom of the glass former to
form fused glass tubing. The apparatus includes at least two
sources that supply the molten glass for flowing over the outside
and inside surfaces.
[0005] In another embodiment of the present disclosure, the
apparatus for forming glass tubing may include a third source that
supplies the molten glass. In such an embodiment, two different
layers of molten glass may flow along the inside wall of the former
to meet with a third layer flowing along the outside wall of the
former to form three-layer fused glass tubing.
[0006] In another embodiment of the present disclosure, the
apparatus for forming glass tubing may include more than two
sources that supply molten glass to the former. An example
embodiment under this aspect could comprise a third source that
supplies the molten glass. In such an embodiment, two different
layers of molten glass may flow along the outside wall of the
former to meet with a third layer flowing along the inside wall of
the former to form three-layer fused glass tubing. Alternatively,
in such an embodiment, two layers of molten glass may flow along
the inside wall of the former and meet a third layer flowing along
the outside wall of the former to form a three-layer fused glass
structure. In fact, the apparatuses and processes described herein
could be generalize to n sources that supply molten glass to the
exterior of the former and provide n layers of molten glass flowing
on the exterior of the former and m sources that supply molten
glass to the interior of the former and provide m layers of molten
glass flowing on the interior of the former to form an n+m layered
glass structure at the bottom of the former.
[0007] Additional features and advantages will be set forth in the
detailed description which follows, and in part will be readily
apparent to those skilled in the art from that description or
recognized by practicing the embodiments as described herein,
including the detailed description which follows, the claims, as
well as the appended drawings.
[0008] It is to be understood that both the foregoing general
description and the following detailed description are merely
exemplary, and are intended to provide an overview or framework to
understanding the nature and character of the claims. The
accompanying drawings are included to provide a further
understanding, and are incorporated in and constitute a part of
this specification. The drawings illustrate one or more
embodiment(s), and together with the description serve to explain
principles and operation of the various embodiments.
BRIEF DESCRIPTION OF SEVERAL VIEWS OF THE DRAWINGS
[0009] FIG. 1 is an elevated cross-sectional side view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure.
[0010] FIG. 2 is an elevated view of a former for use in one
embodiment of the present disclosure.
[0011] FIG. 3 is a perspective view of a portion of a retention
ring for use in one embodiment of the present disclosure.
[0012] FIG. 4 is an elevated cross-sectional side view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure.
[0013] FIG. 5 is an elevated cross-sectional side view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure.
[0014] FIG. 6 is an elevated cross-sectional top view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure.
[0015] FIG. 7 is an elevated cross-sectional side view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure.
[0016] FIG. 8 is an elevated cross-sectional side view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure.
[0017] FIG. 9 is an elevated cross-sectional side view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure.
[0018] FIG. 10 is an elevated cross-sectional side view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure.
[0019] FIG. 11 is an elevated cross-sectional side view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure.
[0020] FIG. 12 is an elevated cross-sectional side view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure.
[0021] FIG. 13 is an elevated cross-sectional side view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure.
DETAILED DESCRIPTION OF THE INVENTION
[0022] Reference will now be made in detail to embodiments of the
present disclosure, examples of which are illustrated in the
accompanying drawings. Whenever possible, the same reference
numerals will be used throughout the drawings to refer to the same
or like parts.
[0023] FIG. 1 is an elevated cross-sectional side view of one
embodiment of a fused glass tube forming apparatus of the present
disclosure. The apparatus for forming glass tubing 10 includes an
endless former 12 and a molten glass hold 14. The endless former 12
is referred to as endless because it comprises a closed circuit,
such as a circular ring, but may also be of a different shape, such
as rectangular or square. As will be evident from the disclosure
below, the shape of the endless former 12 generally defines the
shape of the resulting fused glass tube made by the apparatus for
forming glass tubing 10.
[0024] The endless former 12 has a lower portion 16, a middle
portion 18 and an upper portion 20. The endless former 12 also has
an outer surface 22 and an inner passage 24 that defines an inner
surface 26. As depicted in FIG. 1, the lower portion 16 of the
endless former is generally wedge-shaped with both the outer
surface 22 and the inner surface 26 sloped toward each other to
define a taper with a bottom 27. The taper of the lower portion 16
is not limited to the configuration depicted in FIG. 1. For
example, the wedge of the lower portion 16 could result from the
outer surface 22 alone sloping toward the inner surface 26, or the
inner surface 26 alone sloping toward the outer surface 22. As
explained in further detain below, the shape and dimensions of the
wedge-shaped portion may vary depending on the glass composition to
be formed or other considerations, such as tube thickness, tube
shape, thermal constraints and environmental conditions.
[0025] The outer surface 22 of the endless former 12 provides a
surface along which molten glass may flow to the bottom 27.
Similarly, the inner surface 26 provides a surface along which
molten glass may flow towards the bottom 27. The flowing molten
glass along the outer surface 22 and along the inner surface 26
will meet at the bottom 27 thereby forming fused glass tubing. As
already mentioned, the cross section of the fused glass tubing
formed by the endless former 12 will depend on the shape of the
endless former 12.
[0026] The molten glass hold 14 has a lower chamber 28 and an upper
chamber 30.
[0027] The lower chamber 28 has a lower chamber floor 31 with an
opening 32. The opening 32 is configured to allow positioning of
the endless former 12. The arrangement of the endless former 12
positioned in the opening 32 of the floor 31 defines a glass flow
gap 33. The lower chamber 28 also includes a side wall 34 and a
ceiling 36. Molten glass may be fed to the lower chamber 28 through
the molten glass feed 44. The floor 31 of the lower chamber 28 is
configured to promote flow of the molten glass from the molten
glass feed 44 to the glass flow gap 33 such that the molten glass
will flow evenly through the glass flow gap 33. As will be
described in more detail below, the lower chamber 28 may be
provided with any number of means for regulating the flow of molten
glass to promote proper and even flow.
[0028] The upper chamber 30 of the molten glass hold 14 is of a
construction similar to that of the lower chamber 28. The upper
chamber 30 has a floor 38, a side wall 40 and a ceiling 42. The
floor 38 of the upper chamber 30 includes an opening 43 to
accommodate the upper portion 20 of the endless former 12. The
endless former 12 may be positioned within the opening 43 such that
the upper portion 20 extends above the floor 38 of the upper
chamber 30. The upper portion may be provided with an indent 74 so
that a retention ring 70 with a foot 72 may fix the endless former
in position within the opening 43 of the upper chamber floor 38 and
within the opening 32 of the lower chamber floor 31.
[0029] Molten glass may flow into the upper chamber 30 through the
molten glass feed 48. The floor 38 of the upper chamber 30 is
configured to promote even flow of the molten glass towards the
opening 43 in the floor 38 and the retention ring 70. In the
configuration shown in FIG. 1 the molten glass will flow from the
molten glass feed 48 into the upper chamber 30 towards the
retention ring 70. The retention ring 70 will serve as a dam
regulating the flow of molten glass such that the molten glass must
rise to the level of the height of the retention ring 70 before the
molten glass may flow over the retainer ring and into the inner
passage 24 of the endless former 12.
[0030] The molten glass may then flow down along the inner surface
26 towards the bottom 27 of endless former 12. The film
(alternatively described as a layer or coating) of molten glass
flowing down along the inner surface 26 of the endless former will
meet and fuse with the flow of molten glass from the lower chamber
28 and flowing down the outer surface 22 of the endless former 12.
The flow of molten glass flowing on the inner surface 26 will
provide the inner surface of the fused glass tubing while the
molten glass flowing downwardly on the outer surface 22 will
provide the outer surface of the fused glass tubing. The resulting
fused glass tubing will have pristine inner and outer surfaces as a
result of being formed free from contact with any surfaces, tools,
or other devices.
[0031] A vent 46 may be connected to the lower chamber 28 and a
vent 50 may be connected to the upper chamber 30 to vent gases when
molten glass flows into the lower chamber 28 and upper chamber 30,
respectively.
[0032] As shown in FIG. 1, the molten glass hold 14 comprises a
number of insulating components to prevent unwanted cooling of the
molten glass. The molten glass hold may include ceramic bricks 52,
54, as well as ceramic boards 56, 58, 60, 62, 64, 66. These
insulating components are standard in the industry and any
combination of insulating components is contemplated in the present
disclosure.
[0033] The floor 31, the side wall 34 and the ceiling 36 of the
lower chamber 28 and the floor 38 side wall 40 and ceiling 42 of
the upper chamber 30 should be made of materials typically used in
the production of glass, for example, platinum or ceramic, e.g.,
zircon or silicon nitride. Similarly, the retention ring 70 and the
endless former 12 should be made of materials typically used in
molten glass applications, for example, platinum or ceramic e.g.,
zircon or silicon nitride (see, e.g., U.S. Pat. Nos. 3,338,696,
3,437,470, 3,682,609, and 8,028,544, all of which are herein
incorporated by reference in their entireties). The lower chamber
28 and upper chamber 30 may be heated by any means known in the
art, such as convection, conduction, radiation, or advection. For
example, the lower chamber 28 and upper chamber 30 may be heated
via heating wire or coil 68, optionally made of platinum.
[0034] FIG. 1 shows lower chamber 28 capable of being heated on all
sides with heating wire or coil 68 along the entire floor 31, side
wall 34, and ceiling 36. Similarly, the upper chamber 30 is lined
with heating wire or coil 68 along the entire length of the floor
38, side wall 40 and ceiling 42. The heating generated by the
heating wire or coil 68 may be regulated from one area of the lower
chamber 28 to another creating heat gradients which may also assist
in regulating the flow of the molten glass through the chamber 28
to the glass flow gap 33. Similarly, a heating wire or coil 68 may
be regulated from one area to another in the upper chamber 30
creating heat gradients in the upper chamber 30 and regulating the
flow of molten glass through that chamber 30 as well.
[0035] The ceiling 42 of the upper chamber 30 may be provided with
an opening 77 to accommodate a plunger 78 comprises a rod 79 and a
bell 80. The rod 79 is vertically adjustable such that the bell 80
may be lowered into the inner passage 24 of the endless former 12
at the upper portion 20 to regulate flow of molten glass into the
inner passage 24 of the endless former 12.
[0036] FIG. 2 is an elevated view of a former for use in one
embodiment of the present disclosure. The former 12 as shown in
FIG. 2 corresponds to the embodiment shown in FIG. 1. Specifically,
the former 12 includes an indent 74, which cooperates with the
retention ring 70 (FIG. 1) to fix the former 12 within the
apparatus for forming glass tubing 10.
[0037] FIG. 3 is a perspective view of a portion of the retention
ring 70. The retention ring 70 includes the foot 72 and an upper
extension 82. The foot 72 is configured to engage the indent 74 of
the former 12 (FIG. 2). When the former 12 is positioned within the
apparatus for forming glass tubing 10 with the foot 72 of the ring
70 engaging the indent 74, the former 12 is fixed in place within
the apparatus 10, as shown in FIG. 1.
[0038] FIG. 4 is an elevated cross-sectional view of one embodiment
of the present disclosure. The apparatus for forming glass tubing
10 shown in FIG. 4 is the same apparatus shown in FIG. 1 with a
ring 76 placed in the opening 32 of the floor 31 of the lower
chamber 28. The ring 76 is conventionally made of platinum but may
be made of any material conventionally used in processing molten
glass. The ring 76 will serve as a dam regulating the flow of
molten glass such that the molten glass must rise to the level of
the height of the ring 76 before the molten glass may flow over the
ring 76 and into the glass flow gap 33.
[0039] FIG. 5 is an elevated cross-sectional view of one embodiment
of the present disclosure. The apparatus for forming glass tubing
10 shown in FIG. 5 is the same apparatus shown in FIG. 1 with a
contoured dam 84 placed adjacent the retention ring 70 in the upper
chamber 30. The contoured dam 84 includes an increased height H1
and a decreased height H2. The contoured dam 84 is designed with
the depicted height variation in order to regulate the flow of
molten glass from the glass inlet 48 to the opening 43 in the floor
38. The flow of molten glass from the glass feed 48 may require
regulation through means such as the contoured dam 84 in order to
ensure proper and even flow into the inner passage 24 of the former
12. The increased height H1 is adjacent to the glass feed 48 to
account for the greater volume of molten glass present on the feed
side of the upper chamber 30. The shape of the upper surface of the
contoured dam 84 in transitioning from height H1 to height H2 is
determined by the desired flow properties, and may take on a linear
or nonlinear shape when viewed in elevated cross-section (i.e., as
shown in FIG. 5).
[0040] The apparatus 10 of FIG. 5 also differs from FIG. 1 in that
it includes a second contoured dam 86 at the opening 32 of the
lower chamber 28 similar to the contoured dam 84 of the upper
chamber 30, the contoured dam 86 of the lower chamber 28 includes a
varying height in order to regulate the flow of molten glass from
the glass feed 44 to the opening 32. Such a contoured dam 86 may be
required to regulate the flow of molten glass from the feed 44 to
the opening 32 in order to ensure even flow of the molten glass
through the opening 32 onto the outer surface 22 of the former 12.
As in the case of contoured dam 84, the shape of the upper surface
of the contoured dam 86 is determined by the desired flow
properties, and may take on a linear or nonlinear shape when viewed
in elevated cross-section (i.e., as shown in FIG. 5).
[0041] FIG. 6 is an elevated cross-sectional top view of one
embodiment of the present disclosure. The cross sectional view
shown in FIG. 6 is through the upper chamber 30. The general
construction of an acceptable side wall for the apparatus 10 is
shown including the ceramic board 66, the ceramic board 58, and the
stainless steel casing 69. Also shown are the glass feed 44 for the
lower chamber and the glass feed 48 for the upper chamber. The
ceramic brick 54 shown in FIG. 1 is not shown in order to show the
complete floor 38.
[0042] The floor 38 of the upper chamber 30 may include a bowl 88
(not shown in FIG. 1), which may be further utilized to regulate
the flow of molten glass from glass feed 48 to the retention ring
70 and the former 12. The floor 38 including the bowl 88 may be
made of ceramic. Alternatively, the bowl 88 may be separately made
of platinum. If the bowl 88 is made of platinum, the bowl 88 may be
heated to further regulate the flow of molten glass from the glass
feed 48 to the retainer ring 70.
[0043] The embodiments of FIGS. 7-13 are simplified versions of the
embodiments of FIG. 1-6. As is readily apparent, many of the
features and details described in connection with FIGS. 1-6 are
equally applicable to the embodiments of FIGS. 7-13.
[0044] FIG. 7 is an elevated cross-sectional view of one embodiment
of the present disclosure. The apparatus for forming glass tubing
100 is shown in a simplified version and includes an endless former
102 and a molten glass hold 104. The molten glass hold 104 has a
lower chamber 106 and an upper chamber 108. The lower chamber 106
has a floor 110, a side wall 112 and a glass feed 114. The upper
chamber 108 has a floor 116, a side wall 118, and a glass feed
120.
[0045] FIG. 7 shows a variation on the manner in which the former
102 is fixed in place. The floor 116 of the upper chamber 108
includes a recess 122. The recess is configured to accommodate a
retention ring 124 that includes a foot 126. The foot 126 engages
an indent 128 in the former 102.
[0046] FIG. 8 is an elevated cross-sectional side view of one
embodiment of the present disclosure. FIG. 8 is similar to the
embodiment of FIG. 7 except that the floor 110 of the lower chamber
106 is provided with a dam 130 and the floor 116 of the upper
chamber 108 is provided with a dam 132. The dam 130 in the lower
chamber 106 regulates the flow of molten glass from the glass feed
114 to effect a more uniform flow of glass into the glass flow gap
115 defined between the floor 110 of the lower chamber 106 and the
former 102. Similarly, the dam 132 regulates the flow of molten
glass from the glass feed 120 to effect a more uniform flow of
glass over the dam 132 and into the inner passage 133 of the former
102.
[0047] FIG. 9 is an elevated cross-sectional side view of one
embodiment of the present disclosure. FIG. 9 shows the floor 110 of
the lower chamber 106 with a contoured dam 134. The contoured dam
provides additional regulation of the flow of molten glass from the
glass feed 114 to the glass flow gap 115. The contoured dam 134 has
a greater height adjacent the glass feed 115 to account for the
greater volume of molten glass adjacent the glass feed 114. The
contoured dam 134 is designed to provide a more even flow from the
second chamber 106 into the glass flow gap 115. The increased
height adjacent to the glass feed 114 accounts for the greater
volume of molten glass present on the feed side of the lower
chamber 106.
[0048] The contoured dam 136 similarly regulates the flow of glass
in the upper chamber 108 from the glass feed 120 to the inner
passage 133 of the former 102. The increased height adjacent to the
glass feed 120 accounts for the greater volume of molten glass
present on the feed side of the upper chamber 108.
[0049] FIG. 10 is an elevated cross-sectional side view of one
embodiment of the present disclosure. FIG. 10 shows an alternative
embodiment for the former 102. The former 102 includes a wide wedge
portion 138. The wide wedge portion 138 is designed to increase the
outer surface 139 of the former 102. It is known that flowing
molten glass requires time to heal after the glass surface has been
in contact with tooling or other surfaces. As shown in the
apparatus of FIG. 10, molten glass flowing from the lower chamber
106 will be in contact with the floor 110 and also with the outer
boundary 137 of the glass flow gap 115. The outer surface of the
glass tubing formed by the apparatus for forming glass tubing 100
will potentially have been in direct contact with the floor 110 of
the lower chamber 106 as well as the outside boundary 137 of the
glass flow gap 115. In order to form glass tubing with a pristine
outer surface, the outer surface of the molten glass flowing along
the outer surface 139 of the former 102 must be provided sufficient
time to heal. The widened wedge portion of the former 102 is
intended to provide that healing time to the outer surface of the
flowing molten glass. The time required for the outer surface of
the flowing molten glass to heal will vary depending on the type of
glass that is being used, including its viscosity and surface
tension. Accordingly, different glasses will require different
healing times, including different distances to travel along the
outer surface 139 of the former 102.
[0050] FIG. 11 is an elevated cross-sectional side view of one
embodiment of the present disclosure. FIG. 11 shows a former 102
with a long wedge portion 140. The long wedge portion 140 increases
the outer surface 142 to provide sufficient healing time to the
molten glass flowing along the outer surface 142. Similarly, the
long wedge portion increases the inner surface 144 to provide
sufficient healing time to the molten glass flowing along the inner
surface 144. As a result of increasing the length traveled along
the outer surface 142 and the inner surface 144 the former 102 with
its long wedge portion 140 increases the time for both molten glass
flows to heal and thus result in a fused glass tube having pristine
inner and outer surfaces.
[0051] FIG. 12 is an elevated cross-sectional side view of one
embodiment of the present disclosure. The apparatus for forming
glass tubing 145 is similar to that of FIG. 7 and includes a lower
chamber 106 and an upper chamber 108. The lower chamber 106 and the
upper chamber 108 are as described above in connection with FIG. 7
through 11. The former 102 is as described in connection with FIGS.
7 through 11. In addition, the apparatus for forming glass tubing
145 includes a middle chamber 146. The middle chamber 146 has a
floor 147, a side wall 148 and a glass feed 149. The floor 147
includes an opening 141. The opening 141 is configured to
accommodate the former 102. Molten glass may flow from the glass
feed 149 toward the opening 141. Any of the means already described
for regulating the flow of the molten glass may be used with the
middle chamber 146.
[0052] The molten glass from the middle chamber 146 will flow down
along the outer surface 143 of the former 102. Molten glass from
the lower chamber 106 may also flow onto the outer surface 143 as a
layer over the layer of molten glass from the middle chamber.
Molten glass from the upper chamber 108 may flow down along the
inner surface 135 of the former 102. The resulting tubing will have
three layers with the outside layer formed from the molten glass
from the lower chamber 106, the middle layer formed from the molten
glass from the middle chamber 146, and the inner layer formed from
the molten glass from the upper chamber 108.
[0053] FIG. 13 is an elevated cross-sectional side view of one
embodiment of the present disclosure. The apparatus for forming
glass tubing 150 includes an endless former 152, a bottom molten
glass hold 154, a middle molten glass hold 156, and an upper molten
glass hold 158. The former includes an upper portion 160, an outer
surface 162, a lower portion 164, and inner passage 166 with an
inner surface 168, and an extension 170. The extension includes a
bowl 172. The extension 170 is designed to be fixed so that the
position of the former 152 is static.
[0054] The bottom molten glass hold 154 includes an insulating
floor 174 with an opening 175 in the floor 174, and an insulating
wall 176. The floor may also include a dam 178. The bottom molten
glass hold 154 includes a glass feed 180. Molten glass may be fed
into the bottom molten glass hold 154 through the glass feed 180
such that the molten glass will flow towards the opening 175. The
dam 178 serves to regulate the flow of the molten glass into the
glass flow gap 182 defined by the second floor 174 and the outer
surface 162 of the former 152.
[0055] The middle molten glass hold 156 includes an insulating
floor 184 that includes a dam 186 and an opening 188, an insulating
wall 190, and a molten glass feed 192. The middle molten glass hold
156 may include a neck 194 extending down from the bottom of the
floor 184 at the floor opening 188. The opening defines an inner
passage 196 with an inner surface 198. The inner surface 198 may
include a frustoconical portion 200 at its upper extent.
[0056] Molten glass may be fed into the middle molten glass hold
156 through the glass feed 192. The molten glass may flow towards
the dam 186. The molten glass may flow over the dam 186 and into
the opening 188 so that it flows along the inner surface 198 of the
inner passage 196. The molten glass will flow down along the inner
surface 198 of the neck 194 until it is free of the neck and flows
down into the bowl 172 of the endless former 152. The glass flow
from the middle molten glass hold 156 will then continue to flow
down along the inner surface 168 of the endless former 152.
[0057] The upper molten glass hold 158 includes an insulated floor
202 with a dam 204 and an opening 206, an insulating wall 208, and
a molten glass feed 210. The upper molten glass hold 158 may also
include a neck 212. The opening 206 of the upper molten glass hold
158 defines an inner passage 214 with an inner surface 216. Molten
glass may be fed into the upper molten glass hold 158 through the
glass feed 210 with the glass flowing towards the dam 204, over the
dam 204, into the opening 206 and down along the inner surface 216.
When the molten glass flow is free of the inner surface 216, it may
flow into the opening 188 of the middle molten glass hold.
Preferably, the molten glass flowing from the upper molten glass
hold 158 will flow onto the molten glass flowing from the middle
molten glass hold 156. The neck 216 of the upper molten glass hold
158 should have an inner diameter that is greater than the inner
diameter of the neck 194 of the middle molten glass hold 156, as
shown in FIG. 13. In such an arrangement, the molten glass flowing
from the upper molten glass hold 158 will flow onto the molten
glass flowing from the middle molten glass hold 156 at the
frustoconical portion 200 of the opening 188 of the middle molten
glass hold. As is evident, any configuration for the opening 188
and the neck 194 of the middle molten glass hold 156 that results
in the molten glass flow from the upper molten glass hold 158 being
layered onto the molten glass flowing from the middle molten glass
hold 156 is acceptable. For example, the entire inner passage 196
may be defined by angled walls such as present in the frustoconical
portion 200.
[0058] The bottom molten glass hold 154 may be mounted separately
from the endless former 152 such that it may be horizontally
adjusted relative to the endless former 152. In this way the flow
of molten glass from the glass feed 180 towards the glass flow gap
182 may be regulated to provide the desired flow through the glass
flow gap 182 and onto the outer surface 164 of the endless former
152.
[0059] Similarly, the middle molten glass hold 156 may be mounted
separately from the endless former 152 and the bottom molten glass
hold 154 so that it too can be adjusted horizontally relative to
the endless former 152 and the bottom molten glass hold 154. Upper
molten glass hold 158 may also be separately mounted such that it
can be adjusted horizontally relative to each of the endless former
152, the bottom molten glass hold 154, and the middle molten glass
hold 156.
[0060] The designs shown in FIGS. 12 and 13 can be expanded beyond
three layers. By the inclusion of additional holds, the apparatuses
shown can be used to form glass structures having 4 or more layers.
In another embodiment the apparatus for forming glass tubing may
include more than two sources that supply molten glass to the
former. In fact, the apparatuses described herein, for example, by
generalizing the design shown in FIG. 12, could be used as n
sources that supply molten glass to the exterior of the former and
provide n layers of molten glass flowing on the exterior of the
former. Similarly, it is possible to generalize the design in FIG.
13 to provide m sources that supply molten glass to the interior of
the former and provide m layers of molten glass flowing on the
interior of the former. The resulting glass structure at the bottom
of the former 27 is a multilayered product formed of n+m
layers.
[0061] The apparatus for forming glass tubing 150 may be altered in
numerous ways as described above in connection with FIGS. 7 through
11 to include contoured dams and different shaped formers. As
already noted, many of the features of other embodiments are
equally applicable to the apparatus for forming glass tubing
150.
[0062] In the above embodiments, a number of means for regulating
the flow of molten glass have been described. Those means include
dams, including extensions, over which molten glass must flow,
contoured dams and extensions designed to account for the greater
volume of molten glass present on one side of the chamber,
contouring the floor, such as with a bowl, of a hold or chamber,
temperature regulation of the chamber or floor to create a
temperature gradient in the chamber or floor, and tilting or
horizontally adjusting the floor. Each of these means for
regulating the flow of molten glass may be used separately or
together to adjust the flow of molten glass to the desired
effect.
[0063] It will be apparent to those skilled in the art that various
modifications and variations can be made without departing from the
spirit and scope of the invention, which is defined by the appended
claims. The appended claims make reference to specific structures
and may reference structures with an ordinal prefix. The presence
of an ordinal prefix should not be understood to require structures
with all prior ordinal prefixes. For example, if a claim refers to
a third dam, it should not be understood that the claim will also
require a second dam. This reference within claims is made to avoid
confusion between separately dependent claims.
* * * * *