U.S. patent application number 16/218885 was filed with the patent office on 2020-01-23 for cmas resistant thermal barrier coatings.
The applicant listed for this patent is General Electric Company. Invention is credited to Larry Steven Rosenzweig, James Anthony Ruud, Shankar Sivaramakrishnan.
Application Number | 20200024718 16/218885 |
Document ID | / |
Family ID | 53367706 |
Filed Date | 2020-01-23 |
United States Patent
Application |
20200024718 |
Kind Code |
A1 |
Rosenzweig; Larry Steven ;
et al. |
January 23, 2020 |
CMAS RESISTANT THERMAL BARRIER COATINGS
Abstract
The present application provides Calcia-Magnesia-Alumina-Silica
(CMAS) (or molten silicate) resistant thermal barrier coatings
(IBC). The coatings include elongate growth domains of
non-equiaxed, randomly arranged overlapping grains or splats. The
elongate growth domains include overlapping individual, randomly
distributed splats of tough and soft phases. In some embodiments,
the elongate growth domains are formed via air plasma spray. In
some embodiments, the tough phases are at least partially
stabilized zirconia and/or hafnia compositions, and the soft phases
are CMAS (or molten silicate) reactive or resistant compositions.
Within each elongate growth domain, the mixture of the tough and
soft phases act together to limit penetration of CMAS and also
provide sufficient domain toughness to minimize cracking forces
produced during crystallization of infiltrated CMAS. The soft
phases may react with the CMAS and increase its melting point,
increase its viscosity, and reduce the destabilization of the tough
phases.
Inventors: |
Rosenzweig; Larry Steven;
(Clifton Park, NY) ; Ruud; James Anthony; (Delmar,
NY) ; Sivaramakrishnan; Shankar; (Niskayuna,
NY) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
General Electric Company |
Schenectady |
NY |
US |
|
|
Family ID: |
53367706 |
Appl. No.: |
16/218885 |
Filed: |
December 13, 2018 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
14107225 |
Dec 16, 2013 |
10179945 |
|
|
16218885 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
Y02T 50/60 20130101;
C23C 4/134 20160101; F01D 5/288 20130101; C23C 4/067 20160101; Y10T
428/24802 20150115 |
International
Class: |
C23C 4/067 20060101
C23C004/067; F01D 5/28 20060101 F01D005/28; C23C 4/134 20060101
C23C004/134 |
Claims
1.-19. (canceled)
20. A method of forming a thermal barrier coating on a substrate,
the method comprising: obtaining a substrate; obtaining a feedstock
consisting of about micron or sub-micron ceramic particles of tough
and soft phases suspended in a liquid agent, wherein the tough
phases are at least one of partially stabilized zirconia
compositions and partially stabilized hafnia compositions, and the
soft phases are at least one of CMAS reactive compositions and CMAS
resistant compositions; and utilizing an air plasma spray apparatus
to heat and deposit the tough and soft phases of the feedstock on
the substrate in randomly distributed overlapping splats that form
a plurality of elongate material growth domains of at least about
75% density defined between domain boundaries.
21. The method of claim 20, wherein at least about 75% of the
splats of the domains include a width to length aspect ratio of
greater than or equal to about 3:1 and a substantially isotropic
crystallographic orientation.
22. The method of claim 21, wherein the widths of the splats are
oriented within the range of about 45 degrees to about 90 degrees
with respect to the direction in which the tough and soft phases
are deposited on the substrate from the air plasma spray
apparatus.
23. The method of claim 20, wherein the tough phases are stabilized
by at least one of yttria, magnesia, calcia, ceria, lanthana,
neodymia, europia, gadolinia, erbia, dysprosia, ytterbia, scandia,
samaria and lutetia, and wherein the soft phases are molten
silicate resistant compositions.
24. The method of claim 20, wherein the feedstock is a mixture of
the tough and soft phase, and wherein utilizing an air plasma spray
apparatus to heat and deposit the tough and soft phases of the
feedstock on the substrate includes introducing the mixture into a
plasma plume of the air plasma spray apparatus.
25. The method of claim 20, wherein the feedstock includes a first
distinct feedstock including the tough phases and a second distinct
feedstock including the soft phases, and wherein utilizing an air
plasma spray apparatus to heat and deposit the tough and soft
phases of the feedstock on the substrate includes introducing the
first and second feedstocks into a plasma plume of the air plasma
spray apparatus at the same time.
Description
BACKGROUND
[0001] The present disclosure generally relates to configurations,
components, assemblies and related methods of thermal barrier
coatings, and in particular nanocomposite thermal barrier coatings
with tough and soft or reactive phases in a strain tolerant
microstructure.
[0002] Gas turbines are of prime importance in a range of
industrial sectors, particularly for power generation and for
propulsion of aircraft, marine craft, etc. The design of modern gas
turbines is driven by the demand for higher turbine efficiency. It
is widely recognized that turbine efficiency can be increased by
operating the turbine at higher temperatures. In order to assure a
satisfactory life span at these higher temperatures, thermal
barrier coatings (hereinafter referred to as "TBCs") are applied to
airfoils and combustion components, for example, of the turbine
using various techniques. Ceramic thermal barrier coatings within
such turbines represent the predominant area of their development,
playing increasingly key roles in providing protection against
over-heating and oxidation of metallic components.
[0003] A key concern for turbines utilized in both power generation
and propulsion applications is with harmful effects of ingested
species or particulate, often referred to as "dust," which can
adhere to TBCs and damage them. Ingested dust melts during use of
the turbine and typically forms a composition of molten dust
referred to as "CMAS" (Calcia-Magnesia-Alumina-Silica). Calcia,
magnesia, alumina and silica are the main ingredients of what is
typically regarded as a family of particulate matter referred to as
CMAS. However, other species of materials which may be referred to
by the "CMAS" classification include volcanic ash, salt, and
sulfur. Ingested CMAS induce degradation in both unprotected
metallic alloys and ceramic coatings, such as TBCs. For example, a
chief mode of failure of ceramic layers, and particularly TBCs, due
to CMAS ingestion is loss of TBC compliance. Typically, the molten
CMAS penetrates and fills the pores of the TBC structure. The
penetrated CMAS then solidifies within the pores as the TBC cools.
As another example, CMAS ingestion can damage ceramic layers, and
particularly TBCs, by promoting sintering and thereby making them
prone to spallation. Such degradation commonly arises when ingested
particulate adheres to the coating and either creates a CMAS-rich
outer layer or leads to diffusion into the coating of these oxides
along internal grain boundaries, free surfaces (e.g., pores) or
open defects. These oxides do not readily dissolve in the zirconia
lattice, but tend to form vitreous phases, where they can
accelerate sintering (particularly if significant levels of
"liquid" phases are created).
[0004] One TBC category in industrial use is yttria-stabilized
zirconia (YSZ) based TBCs, such as 7YSZ which offers chemical
stability, low thermal conductivity and relatively high thermal
expansivity that reduces coating-substrate thermal mismatch strains
during heating and cooling. Air plasma spraying (APS) is widely
used to produce such YSZ-based coatings. Unfortunately,
conventional YSZ-based thermal barrier coatings deposited via APS
have been shown to not include sufficient resistance to spallation
when CMAS is ingested from the environment. as discussed above.
Electron-beam physical vapor deposition (EBPVD) of YSZ-based TBCs
has shown better spallation resistance against CMAS ingestion than
APS applied coatings. However, although PVD coatings also provide
attractive strain tolerance properties they tend to be relatively
expensive and applicable to only relatively small components when
compared with APS as the PVD processes requires a vacuum chamber
and supporting equipment. Another newer technique to combat
spallation resulting from CMAS ingestion involves TBC compositions
with higher rare earth contents as compared to prior TBCs. These
high rare earth TBCs are designed to react with ingested CMAS,
and/or resist reactions with CMAS (or molten silicate), and thereby
limit its penetration. These high rare earth TBCs, however, have
much lower fracture toughness than conventional YSZ-based thermal
barrier coatings, such as 7YSZ, and are thereby prone to
thermo-mechanical stresses during engine operation.
[0005] As a result, a need exists for thermal barrier coatings and
related methods that are resistant to CMAS ingestion (i.e.,
spallation resistant), include high strain tolerance, are scalable
(i.e., compatible with large components), and are relatively
inexpensive as compared with prior art thermal barrier
coatings.
BRIEF DESCRIPTION
[0006] In one aspect, thermal barrier coatings are disclosed. The
coatings include a plurality of elongate material growth domains
defined between domain boundaries. The domains have an intra-domain
density of at least about 75%. The domains include individual,
randomly distributed splats of tough and soft phases stacked
throughout the growth domains. The tough phases are at least one of
partially stabilized zirconia compositions and partially stabilized
hafnia compositions, and the soft phases are at least one of CMAS
reactive compositions and CMAS resistant compositions.
[0007] In another aspect, articles for use at elevated temperatures
are disclosed. The articles include a substrate and a thermal
barrier coating disposed on the substrate. The coating includes a
plurality of elongate material growth domains of at least about 75%
density defined between domain boundaries. The coating also
includes individual, randomly distributed first and second splats.
The first splats are at least one of partially stabilized zirconia
compositions and partially stabilized hafnia compositions, and the
second plats are at least one of CMAS reactive compositions and
CMAS resistant compositions.
[0008] In another aspect, methods of forming a thermal barrier
coating on a substrate are disclosed. The method includes obtaining
a substrate and obtaining a feedstock. The feedstock includes about
micron or sub-micron ceramic particles of tough and soft phases
suspended in a liquid agent. The tough phases are at least one of
partially stabilized zirconia compositions and partially stabilized
hafnia compositions, and the soft phases are at least one of CMAS
reactive compositions and CMAS resistant compositions. The methods
also include utilizing an air plasma spray apparatus to heat and
deposit the tough and soft phases of the feedstock on the substrate
in randomly distributed overlapping splats that form a plurality of
elongate material growth domains of at least about 75% density
defined between domain boundaries.
[0009] These and other objects, features and advantages of this
disclosure will become apparent from the following detailed
description of the various aspects of the disclosure taken in
conjunction with the accompanying drawings.
DRAWINGS
[0010] FIGS. 1A and 1B are yttrium aluminum garnet (YAG)
back-scatter detector (BSE) images showing the cross-section of
elongate growth domains of an exemplary embodiment of an air plasma
sprayed thermal barrier coating (TBC) according to the present
disclosure;
[0011] FIGS. 2A-2C are YAG BSE images showing the cross-section of
interior structure of an elongate growth domain of the exemplary
air plasma sprayed TBC of FIGS. 1A and 1B according to the present
disclosure;
[0012] FIGS. 3A and 3B are YAG BSE images showing the cross-section
of a boundary between two elongate growth domains of the exemplary
air plasma sprayed TBC of FIGS. 1A and 1B according to the present
disclosure; and
[0013] FIG. 4 is a diagram illustrating an exemplary method of
forming an air plasma sprayed TBC according to the present
disclosure on a substrate.
DETAILED DESCRIPTION
[0014] Each embodiment presented below facilitates the explanation
of certain aspects of the disclosure, and should not be interpreted
as limiting the scope of the disclosure. Moreover, approximating
language, as used herein throughout the specification and claims,
may be applied to modify any quantitative representation that could
permissibly vary without resulting in a change in the basic
function to which it is related. Accordingly, a value modified by a
term or terms, such as "about," is not limited to the precise value
specified. In some instances, the approximating language may
correspond to the precision of an instrument for measuring the
value. When introducing elements of various embodiments, the
articles "a," "an," "the," and "said" are intended to mean that
there are one or more of the elements. The terms "comprising,"
"including," and "having" are intended to be inclusive and mean
that there may be additional elements other than the listed
elements. As used herein, the terms "may" and "may be" indicate a
possibility of an occurrence within a set of circumstances: a
possession of a specified property, characteristic or function;
and/or qualify another verb by expressing one or more of an
ability, capability, or possibility associated with the qualified
verb. Accordingly, usage of "may" and "may be" indicates that a
modified term is apparently appropriate, capable, or suitable for
an indicated capacity, function, or usage, while taking into
account that in some circumstances, the modified term may sometimes
not be appropriate, capable, or suitable. Any examples of operating
parameters are not exclusive of other parameters of the disclosed
embodiments. Components, aspects, features, configurations,
arrangements, uses and the like described, illustrated or otherwise
disclosed herein with respect to any particular embodiment may
similarly be applied to any other embodiment disclosed herein.
[0015] As discussed above, conventional air plasma sprayed (APS)
thermal barrier coatings (TBC) have limited spallation resistance
against CMAS ingestion in modern turbines. This disclosure provides
TBCs with a thereto-mechanically compliant composite microstructure
with enhanced chemical resistance utilizing air plasma spray
methods and suspension feedstocks consisting of dispersed micron or
sub-micron ceramic particles. In some embodiments, the suspension
feedstock includes one or more partially stabilized zirconia
composition and/or partially stabilized hafnia composition (or
"tough" phase) and one or more CMAS (or molten silicate) reactive
or resistant composition (or "soft" phase). In some embodiments,
the partially stabilized zirconia and/or hafnia composition (or
"soft" phase) is a zirconia and/or hafnia composition that includes
a sufficient amount stabilizer oxides to form and retain a
metastable t' tetragonal (t-prime) phase structure during
deposition and turbine service exposures, but not an amount that
produces a fully stabilized cubic phase structure. In some
embodiments, without stabilizer additions, zirconia and hafnia
compositions have a monoclinic structure at room temperature and do
not have sufficient thermal or mechanical properties to function as
a TBC in high temperature applications. The amount of stabilizer is
that is required or needed to produce a partially stabilized or
fully stabilized structure (e.g., zirconia or hafnia) is dependent
upon, for example, the type of stabilizer. In some embodiments,
while partially stabilized zirconia and hafnia compositions have
desirable thermal and mechanical properties for high-temperature
TBC applications, their thermal and mechanical properties may vary
depending upon stabilizer composition(s) and quantity, for example.
Fully stabilized zirconia or hafnia compositions, or cubic
structures, while generally have adequate thermal properties, they
may generally lack sufficient mechanical toughness for most
high-temperature TBC applications.
[0016] In some embodiments, the coatings of the present invention
may owe their microstructure at least in part to the processing
used in their fabrication. APS, which, as discussed above, provides
certain economic and manufacturing advantages over processes which
require the use of vacuum equipment, such as PVD or vacuum plasma
spray deposition. In particular, the process uses a feedstock
comprising fine particles suspended in a liquid agent (e.g.,
alcohol, water or mixtures of water and alcohol) that is fed to a
plasma spray torch in a controlled manner and injected into the
plasma plume for deposition onto a substrate. The feedstock may
include two or more individual liquid feedstocks that are fed
directly into the plasma plume. The two or more feedstocks may be
pre-mixed and the mixture fed into the plasma plume, or the two or
more feedstocks may be separate and distinct feedstocks which are
individually fed into the plasma plume (thereby "mixed" in the
plasma plume and/or as they are applied to the substrate). In these
ways, the fine particles of the feedstock are melted individually
and thrown or otherwise directed to, and thereby on, a substrate.
The particles may have a median diameter typically, but not
necessarily, equal to or less than about 0.5 micrometers. Those
skilled in the art will appreciate that many different processing
parameters are available for adjustment in a given air plasma spray
(APS) process, and that various combinations of these parameters
may result in coatings with different structures and
properties.
[0017] In some embodiments, the substrate or article 16 to which
the coating 10 is applied, as shown in FIG. 1A, may be any suitable
support material, but in particular embodiments comprises a high
temperature alloy, such as a nickel-based or cobalt-based
superalloy. In some embodiments, the substrate 16 may be a
component of a gas turbine assembly, including, for instance, a gas
turbine assembly for power generation or for propulsion. Exemplary
components of turbines may include blades, stator vanes, and
combustion components. In some embodiments, the substrate 16
further comprises a bondcoat disposed between coating 10 and the
substrate 16. Bondcoats, such as MCrAlY or aluminide coatings, may
be utilized to provide oxidation resistance to the substrate 16
and/or to enhance adhesion of the ceramic TBC(s) 10.
[0018] In one embodiment, as depicted in the YAG BSE images of
FIGS. 1A and 1B of the cross-section of an exemplary embodiment of
an exemplary air plasma sprayed coating 10, the exemplary coating
10 comprises a plurality of elongate material growth domains 12, as
described in U.S. Patent Application Publication No. 2009/0280298
to Rosenzweig et al., which is incorporated herein in its entirety.
As used herein, the term "elongate" refers to a structure having an
aspect ratio of greater than 1. The exemplary growth domains 12 are
generally vertically oriented, such that their longest axes extend
in a direction at least generally away from the interface 18 and
substrate 16 to which the coating is applied, as shown in FIGS. 1A
and 1B.
[0019] As also shown in FIGS. 1A and 1B, and additionally in FIGS.
3A and 3B, in some embodiments as the coating material is deposited
to form the coating 10 the material accumulates in exemplary
domains 12 defined as regions of comparatively high density
separated by exemplary domain boundaries 14 of comparatively
substantially low (though not necessarily zero) density. In some
embodiments, the domain boundaries 14 may include a coating 10
material density of less than about 25%, or less than about 10%, or
less than about 5%. The domain boundaries 14 may, in some
embodiments, extend for a length equal to at least about 50% of the
coating thickness of the coating 10, and at least about 75% of the
thickness in some embodiments. Generally, the strain tolerance of
exemplary coating 10 is enhanced by the presence of relatively
long, well-defined boundaries 14.
[0020] In some embodiments, the density of material contained
within domains 12 (e.g., tough and soft phases), also referred to
herein as "intra-domain density," is at least about 75% of
theoretical density, as shown in FIGS. 2A-2C. In some embodiments,
this density is even higher, such as greater than 85% and, in
certain embodiments greater than 95%. A high intra-domain density
may provide desirable resistance to erosion and may enhance
cohesive strength of the exemplary coating 10.
[0021] As discussed above, the presence of domain boundaries 14
(see FIGS. 1A, 1B, 3A and 3B) may provide desirable compliance and
strain tolerance properties for exemplary coating 10. For example,
a coating with narrower domains may have a greater density of
domain boundaries. In some embodiments, the width of the domains 12
can be in the range from about 5 micrometers to about 350
micrometers. In some embodiments, the width of the domains 12 can
be in the range from about 20 micrometers to about 100 micrometers.
In some embodiments, the width of the domains 12 can be in the
range from about 30 micrometers to about 90 micrometers. In some
embodiments, the width of the domains 12 can be in the range from
about 40 micrometers to about 80 micrometers. In some embodiments,
the width of the domains 12 can be in the range from about 100
micrometers to about 350 micrometers. Domain width as used herein
may be measured based on the average number of boundaries 14
respectively intercepted by lines of known length drawn along a
cross section of the coating 10 at 33% of the coating thickness and
at 67% of the coating thickness; mean domain width is simply the
known length divided by the number of intercepted boundaries 14. In
certain embodiments, at least about 50% by volume of the coating 10
contains domains 12; thus it is not necessary that the entire
coating 10 comprise the microstructure described herein. In some
embodiments, however, the advantages provided by this unique
structure are such that substantially all of the coating 10
comprises the described microstructure.
[0022] In some embodiments the exemplary domains 12 of the coating
10 may be formed by the deposition mechanism of the coating 10,
such as substantially by accumulation of pre-condensed matter at a
growth surface. In such an embodiment, "pre-condensed matter"
refers to solid and/or liquid phases or matter that impinges upon a
growth surface (e.g., the substrate 16 and or already deposited
phases), rather than matter that condenses at the growth surface
from the vapor phase. For example, exemplary domains 12 may
comprise a plurality of at least partially melted and solidified
particles (meaning the particles were at least partially liquid
before impinging the surface and finally fully solidifying), which
are often (though not always) discernable as "prior particles" in
the microstructure of coating 10 via microscopy techniques, as
shown in the cross-sectional YAG BSE images of the exemplary
domains 12 of the coating 10 in FIGS. 2B, 2C and 3B, In certain
embodiments, at least 50% of the material present in the domains 12
comprises at least partially melted and solidified particles. In
some embodiments at least about 80% of the material present in the
domains 12 comprises at least partially melted and/or solidified
particles. In some embodiments substantially all of the material in
domains 12 is made of at least partially melted and solidified
particles.
[0023] In some embodiments, the exemplary domains 12 generally lack
substantial crystallographic texture, in stark contrast to coatings
deposited via a vapor deposition mechanism. Instead, in some
embodiments the exemplary domains 12 typically have a substantially
isotropic crystallographic orientation. In this context, a
"substantially isotropic crystallographic orientation" means that
the material in question has a texture coefficient in the range
from about 0.75 to about 1.25, as that coefficient is defined in D.
S. Rickerby, A. M. Jones and B. A. Bellamy, Surface and Coatings
Technology, 37, 111-137 (1989).
[0024] In contrast to dense vertically cracked coatings and other
coatings including growth domains (e.g., the coatings of the '298
patent publication discussed above), exemplary coatings 10 of the
present disclosure are generally characterized by growth domains 12
that include randomly arranged or distributed grains or splats
(discussed further below) which substantially lack an equiaxed
morphology (or substantially include "non-equiaxed" grains) with
the presence of distinct lamellar features. "Non-equiaxed" (or lack
of an equiaxed grain or splat morphology) being defined herein as
grains or splats having a median aspect ratio (width/length)
greater than or equal to about 3:1, and "randomly arranged" or
"randomly distributed" stacked splats being defined herein as the
general randomness of the overlapping and/or positioning of grains
or splats relative to one another. In some embodiments, the stacked
individual distinct grains or splats of tough and soft phases may
each include or define a median aspect ratio (width/length) greater
than or equal to about 5:1. Although the overlapping and/or
positioning of the grains or lamellar splats may be substantially
random, the long axes (e.g., width) of the grains or lamellar
splats of the exemplary coatings 10 disclosed herein may be
generally oriented within about 45 degrees to perpendicular (i.e.,
90 degrees) with respect to the direction in which they are applied
to, or deposited on, a substrate (e.g., the direction of a torch
spray plume, such as a plasma plume when applied via APS), stacked
or overlapped on the substrate and each other, and/or the thickness
of the as-applied coating 10. In some embodiments, the domains may
include at least about 75% non-equiaxed grains or lamellar splats,
preferably at least about 85% non-equiaxed grains or lamellar
splats, and more preferably at least about 95% non-equiaxed grains
or lamellar splats.
[0025] The suspension feedstock utilized in an APS process to form
the exemplary coatings 10 of the present disclosure may include one
or more partially stabilized zirconia tough phase and/or one or
more partially stabilized hafnia tough phase, and one or more CMAS
(or molten silicate) reactive or resistant soft phase. During the
APS process, the tough and soft phases form at least partially
melted, and eventually solidified, particles of the domains 12 (see
FIGS. 2B, 2C and 3B). In some embodiments, the feedstock utilized
by the APS process to form the domains 12 of tough and soft phases
may be a mixture of the tough and soft phases that is fed into the
torch plume of the APS process, such as a plasma plume. In some
other embodiments, the feedstock utilized by the APS process to
form the growth domains 12 of tough and soft phases may be two or
more separate and distinct individual feedstocks that each include
only one of the tough and soft phases (as opposed to a mixture of
tough and soft phases). In some such embodiments, the individual
tough and soft phase feedstocks may be separately directed into the
torch plume of the APS process at about the same time to form the
growth domains 12.
[0026] As shown in FIGS. 2B and 2C, for example, each elongate
growth domain 12 may include individual, randomly distributed and
overlapped splats 20, 30 that are stacked throughout the growth
domains 12 (i.e., are stacked or overlapped to form the thickness
of the domains 12 and coating 10). Further, the growth domains 12
may include voids or gaps 40 interspersed with the randomly
distributed splats 20, 30. In some embodiments the randomly
distributed splats 20, 30 are formed by melted, or partially
melted, tough 20 and soft 30 phases as they impact tough 20 and
soft phases 30 that have already been deposited on the substrate
16. As shown in FIGS. 2B and 2C for example, the splats 20, 30 may
be substantially thin and wide after impacting the substrate 16 and
or a previously applied splat 20, 30, and may or may not be
connected to one or more other splat 20, 30 of the same type. In
this way, the splats 20, 30 correspond to the tough and soft phases
of the domains 12 of the coating 10 (and the feedstock utilized to
form the coating 10) and are randomly overlapped as they are
applied to the substrate 16 and previously applied or formed splats
20, 30. In some embodiments, the stacked, randomly distributed
splats of the tough 20 and soft 30 phases of the exemplary coating
10 form elongate growth domains 12 within the range of about 5
microns to about 150 microns in thickness measured from the
interface 18 of the domains 12 with the substrate 16.
[0027] In some embodiments the exemplary coating 10 includes an
overall microstructure of predominantly elongated growth domains of
non-equiaxed grains which provides advantageous strain tolerance.
In some embodiments within each elongate growth domain 12 of the
exemplary coating 10, the mixture of tough phases 20 and CMAS (or
molten silicate) reactive or resistant soft phases 30 act together
to limit penetration of CMAS into the coating 10 during use.
Further, in some such embodiments the tough phases 20 and CMAS (or
molten silicate) reactive or resistant soft phases 30 act together
to provide sufficient domain toughness to minimize cracking forces
produced during crystallization of any infiltrated CMAS into the
elongate growth domain boundaries 14 or any open defect with the
coating 10 microstructure. In some embodiment, the CMAS (or molten
silicate) reactive or resistant soft phases 30 are effective in
reacting with or effecting any infiltrated CMAS to increase its
melting point, increase its viscosity, reduce overall CMAS
infiltration, and reduce the destabilization of the tough phases 20
of the coating 10.
[0028] In this way, the exemplary coatings 10 of the present
disclosure provide tough phases 20 within an elongate growth domain
12 structure that provides the necessary toughness to withstand
thermo mechanical stresses during use, such as use in a turbine.
Inter-dispersion of the soft or reactive phases 30 of the exemplary
coatings 10 provide chemical reaction with infiltrated CMAS, such
as CMAS deposited on or in the coating 10. As a result, the overall
microstructure (elongate growth domains 12, as discussed above)
along with the mixed chemical composition of tough 20 and soft 30
phases functionally provides superior resistance to spallation
damage caused by the deposition and melting of CMAS on substrates
or components 16 coated with the thermal barrier coating 10.
[0029] In some embodiments, the tough phase 20 of the suspension
feedstock for the APS process utilized to form the exemplary
coating 10, and thereby the tough phase splats 20 of the elongate
growth domains 12 of the formed thermal barrier coating 10,
(collectively referred to herein as the tough phase 20 of the
coating 10) is formed of at least one of partially stabilized
zirconia and partially stabilized hafnia. In some such embodiments,
the zirconia-based or hafnia-based tough phases 20 of the coating
10 are stabilized by at least one of yttria, magnesia, calcia,
ceria, lanthana, neodymia, europia, gadolinia, erbia, dysprosia,
ytterbia, scandia, samaria, and lutetia. In some embodiments, the
stabilizer of the zirconia-based and/or hafnia-based tough phase of
the coating 10 may be incorporated individually or in combination
depending upon the desired properties. In some embodiments, the
tough phase 20 of the exemplary coating 10 is 7YSZ.
[0030] In some embodiments, the suspension feedstock for the APS
process utilized to form the exemplary coating 10, and thereby the
formed thermal barrier coating 10, includes more of the tough phase
20 than the soft phase 30. In some embodiments, the coating 10
includes at least about 25 wt % tough phase 20, and preferable at
least about 50 wt % tough phase 20, and more particularly at least
about 75 wt % tough phase 20. In some embodiments, the exemplary
coating 10 includes about 54 wt % tough phase 20 and about 46% soft
phase 30.
[0031] In some embodiments, the CMAS (or molten silicate) reactive
or resistant soft phase 30 of the suspension feedstock for the APS
process utilized to form the exemplary coating 10, and thereby the
soft phase splats 30 of the elongate growth domains 12 of the
formed thermal barrier coating 10, (collectively referred to herein
as the tough phase 30 of the coating 10) is formed of at least one
oxide that reacts with or otherwise effects the properties of CMAS.
In some such embodiments, the CMAS (or molten silicate) reactive or
resistant soft phase 30 of the coating 10 is one or more of various
oxides such as hafnia, yttria, ytterbia, zirconia, lanthana, ceria,
and alumina. In some embodiments, the soft phase 30 of the
exemplary coating 10 is Y2O3.
[0032] In some embodiments of the coating 10, the CMAS (or molten
silicate) reactive or resistant soft phase 30 thereof is at least
one molten silicate resistant material. In some such embodiments,
the soft phase 30 of the exemplary coating 10 includes at least one
material selected from the group consisting of zirconia, hafnia,
and titanic stabilized with a rare earth material which comprises
at least one oxide selected from the group consisting of calcium,
magnesium, lanthanum, cerium, praseodymium, neodymium, promethium,
samarium, europium, gadolinium, terbium, dysprosium, holmium,
erbium, thulium, ytterbium, yttrium lutetium, scandium, indium, and
mixtures thereof. In some such embodiments, the soft phase 30 of
the exemplary coating 10 includes at least one oxide of a material
selected from the group consisting of aluminum, calcium, magnesium,
silicon, tantalum, titanium, cerium, praseodymium, neodymium,
promethium, samarium, europium, terbium, dysprosium, holmium,
erbium, thulium, yttrium, ytterbium, lutetium, scandium, indium,
hafnium, gadolinium and mixtures thereof. In some such embodiments,
the soft phase 30 of the exemplary coating 10 includes at least one
sodium containing compound selected from the group consisting of
sodium oxide, sodium silicate, sodium titanate, and mixtures
thereof.
[0033] In some such embodiments, the soft phase 30 of the exemplary
coating 10 includes at least one garnet having the formula
A.sub.3B.sub.3X.sub.3O.sub.12 where A comprises at least one of the
metals selected from the group consisting of Ca.sup.+2, Gd.sup.+3,
In.sup.+3, Mg.sup.+2, Na.sup.+, K.sup.+, Fe.sup.+2, La.sup.+2,
Ce.sup.+2, Pr.sup.+2, Nd.sup.+2, Pm.sup.+2, Sm.sup.+2, Eu.sup.+2,
Gd.sup.+2, Tb.sup.+2, Dy.sup.+2, Ho.sup.+2, Er.sup.+2, Tm.sup.+2,
Yb.sup.+2, Lu.sup.+2, Sc.sup.+2, Y.sup.+2, Ti.sup.+2Zr.sup.+2,
Hf.sup.+2, V.sup.+2, Ta.sup.+2, Cr.sup.+2, W.sup.+2, Mn.sup.+2,
Tc.sup.+2, Re.sup.+2, Fe.sup.+2, Os.sup.+2, Co.sup.+2, Ir.sup.+2,
Ni.sup.+2, Zn.sup.+2, and Cd.sup.+2; where B comprises at least one
of the metals selected from the group consisting of Zr.sup.+4,
Hf.sup.+4, Gd.sup.+3, Al+3, Fe.sup.+3, La.sup.+2, Ce.sup.+2,
Pr.sup.+2, Nd.sup.+2, Pm.sup.+2, Sm.sup.+2, Eu.sup.+2, Gd.sup.+2,
Tb.sup.+2, Dy.sup.+2, Ho.sup.+2, Er.sup.+2, Tm.sup.+2, Yb.sup.+2,
Lu.sup.+2, In.sup.+3, Sc.sup.+2, Y.sup.+2, Cr.sup.+3, Sc.sup.+3,
Y.sup.+3, V.sup.+3, Nb.sup.+3, Cr.sup.+3, Mo.sup.+3, W.sup.+3,
Mn.sup.+3, Fe.sup.+3, Ru.sup.+3, Co.sup.+3, Rh.sup.+3, Ir.sup.+3,
Ni.sup.+3, and Au.sup.+3; where X comprises at least one of the
metals selected from the group consisting of Si.sup.4+, Ti.sup.+4,
Al.sup.+3, Fe.sup.+3, Cr.sup.+3, Sc.sup.+3, Y.sup.+3, V.sup.+3,
Nb.sup.+3, Cr.sup.+3, Mo.sup.+3, W.sup.+3, Mn.sup.+3, Fe.sup.+3,
Ru.sup.+3, Co.sup.+3, Rh.sup.+3, Ir.sup.+3, Ni.sup.+3, and
Au.sup.+3; and where O is oxygen.
[0034] In some such embodiments, the soft phase 30 of the exemplary
coating 10 includes an oxyapatite having the formula
A.sub.4B.sub.6X.sub.6O.sub.26 where A comprises at least one of the
metals selected from the group consisting of is Ca.sup.+2,
Mg.sup.+2, Fe.sup.+2, Na.sup.+, K.sup.+, Gd.sup.+3, Zr.sup.+4,
Hf.sup.+4, Y.sup.+2, Sc.sup.+2, Sc.sup.+3, In+3, La.sup.+2,
Ce.sup.+2, Pr.sup.+2, Nd.sup.+2, Pm.sup.+2, Sm.sup.+2, Eu.sup.+2,
Gd.sup.+2, Tb.sup.+2, Dy.sup.+2, Ho.sup.+2, Er.sup.+2, Tm.sup.+2,
Yb.sup.+2, Lu.sup.+2, Sc.sup.+2, Y.sup.+2, Ti.sup.+2, Zr.sup.+2,
Hf.sup.+2, V.sup.+2, Ta.sup.+2, Cr.sup.+2, W.sup.+2, Mn.sup.+2,
Tc.sup.+2, Re.sup.+2, Fe.sup.+2, Os.sup.+2, Co.sup.+2, Ir.sup.+2,
Ni.sup.+2, Zn.sup.+2, and Cd.sup.+2; where B comprises at least one
of the metals selected from the group consisting of Gd.sup.+3,
Y.sup.+2, Sc.sup.+2, In.sup.+3, Zr.sup.+4, Hf.sup.+4, Cr.sup.+3,
Sc.sup.+3, Y.sup.+3, V.sup.+3, Nb.sup.+3, Cr.sup.+3, Mo.sup.+3,
W.sup.+3, Mn.sup.+3, Fe.sup.+3, Ru.sup.+3, Co.sup.+3, Rh.sup.+3,
Ir.sup.+3, Ni.sup.+3, and Au.sup.+3; where X comprises at least one
of the metals selected from the group consisting of Si.sup.+4,
Ti.sup.+4, Al.sup.+4, Cr.sup.+3, Sc.sup.+3, Y.sup.+3, V.sup.+3,
Nb.sup.+3, Cr.sup.+3, Mo.sup.+3, W.sup.+3, Mn.sup.+3, Fe.sup.+3,
Ru.sup.+3, Co.sup.+3, Rh.sup.+3, Ir.sup.+3, Ni.sup.+3, and
Au.sup.+3, and where O is oxygen.
[0035] In some such embodiments, the soft phase 30 of the exemplary
coating 10 includes a titanate mixed with at least one oxide
comprising at least one oxide of a material selected from the group
consisting of lanthanum, cerium, praseodymium, neodymium,
promethium, samarium, europium, gadolinium, terbium, dysprosium,
holmium, erbium, thulium, ytterbium, lutetium, scandium, indium,
yttrium, and mixtures thereof. In some such embodiments, the soft
phase 30 of the exemplary coating 10 includes a metal carbide from
the group consisting of silicon carbide, tantalum carbide, titanium
carbide, tungsten carbide, silicon oxycarbide, and mixtures
thereof. In some such embodiments, the soft phase 30 of the
exemplary coating 10 includes is a metal nitride from the group
consisting of silicon nitride, zirconium nitride, tantalum nitride,
boron nitride, and mixtures thereof.
[0036] In some such embodiments, the soft phase 30 of the exemplary
coating 10 includes a metal silicide from the group consisting of
chromium silicide, molybdenum silicide, tantalum silicide, titanium
silicide, tungsten silicide, zirconium silicide, and mixtures
thereof. In some such embodiments, the soft phase 30 of the
exemplary coating 10 includes 3-70 mol % gadolinia, balance hafnia.
In some such embodiments, the soft phase 30 of the exemplary
coating 10 includes gadolinia and zirconia and has a cubic crystal
structure. In some such embodiments, the soft phase 30 of the
exemplary coating 10 includes a material with a cubic pyrochlore
structure.
[0037] FIG. 4 illustrates exemplary methods of forming a TBC of the
present disclosure on a substrate. The exemplary methods are
referenced generally by reference numeral 110. As shown in FIG. 4,
the exemplary methods 110 of forming a TBC, such as the coating 10
discussed above, include obtaining 112 a substrate to coat with the
TBC Obtaining 112 the substrate may include forming the substrate
or obtain a pre-made substrate. The substrate may be any material
or combinations of materials. In some embodiments, the substrate
may be a metallic substrate. In some embodiments, obtaining 112 the
substrate may include forming or obtaining a bondcoat on an upper
surface of the substrate.
[0038] As shown in FIG. 4, the exemplary methods 110 of forming a
TBC on a substrate include obtaining 114/116 a feedstock of tough
and soft phases. In some embodiments, obtaining 114/116 one or more
feedstock of tough and soft phases may include obtaining or forming
one or more feedstock that includes tough and/or soft phases
suspended in a liquid agent. The suspension(s) may include of about
micron or sub-micron ceramic particles. As discussed above, the
tough phases may be at least one of partially stabilized zirconia
compositions and partially stabilized hafnia compositions. In some
embodiments, the tough phases may be stabilized by at least one of
yttria, magnesia, calcic, ceria, lanthana, neodymia, europia,
gadolinia, erbia, dysprosia, ytterbia, scandia, samaria and
lutetia. As also discussed above, the soft phases may be at least
one of CMAS reactive compositions and CMAS resistant compositions.
In some embodiments, the soft phases may be molten silicate
resistant compositions.
[0039] In some embodiments, as shown in FIG. 4, obtaining 114/116 a
feedstock of tough and soft phases may include obtaining or forming
114 a feedstock including a mixture of the tough and soft phase. In
some embodiments, as also shown in FIG. 4, obtaining 114/116 a
feedstock of tough and soft phases may include obtaining or forming
116 a first distinct feedstock including the tough phases and a
second distinct feedstock including the soft phases.
[0040] The exemplary methods 110 of forming a TBC on a substrate
may include utilizing 118 an air plasma spray apparatus to heat and
deposit the tough and soft phases of the feedstock or feedstocks on
the substrate (e.g., on an upper surface of the substrate or a
bondcoat on the substrate), as shown in FIG. 4. In some
embodiments, utilizing 118 an air plasma spray apparatus to heat
and deposit the tough and soft phases of the feedstock or
feedstocks on the substrate in randomly distributed overlapping
splats of the tough and soft phases that form a plurality of
elongate growth domains between domain boundaries. In some such
embodiments, the elongate material growth domains include at least
about 75% density defined between the domain boundaries. In some
embodiments, at least about 75% of the splats of the elongate
growth domains include a width to length aspect ratio of greater
than or equal to about 3:1 and a substantially isotropic
crystallographic orientation. In some embodiments, the widths of
the splats are oriented within the range of about 45 degrees to
about 90 degrees with respect to the direction in which the tough
and soft phases are deposited on the substrate from the air plasma
spray apparatus.
[0041] In some embodiments, utilizing 18 an air plasma spray
apparatus to heat and deposit the tough and soft phases of a
feedstock on the substrate includes introducing a feedstock of a
mixture of the tough and soft phases into a plasma plume of the air
plasma spray apparatus. In some other embodiments, utilizing 18 an
air plasma spray apparatus to heat and deposit the tough and soft
phases of feedstocks on the substrate includes introducing the
individual first and second feedstocks into a plasma plume of the
air plasma spray apparatus at about the same time.
[0042] As shown in FIG. 4, after the utilizing 118 an air plasma
spray apparatus to heat and deposit the tough and soft phases of
the feedstock or feedstocks on the substrate, the exemplary methods
110 of forming a TBC on a substrate may include allowing 120 the
deposited molten or semi-molten splats of elongate growth domains
to cool and solidify to form a TBC on the substrate.
[0043] The following examples are illustrative of the exemplary
TBCs, and the exemplary methods of forming the exemplary TBCs,
disclosed herein.
EXAMPLE 1
[0044] Nanocomposite thermal barrier coatings with tough and soft
phases in a strain tolerant microstructure, as disclosed herein,
were foiled on metallic substrates. The metallic substrates were
Rene N5 alloy substrates that included about 150 microns of NiCrAlY
bondcoat. The bondcoat was applied to the substrates utilizing an
air plasma spray process that produced a surface roughness of about
10 micron Ra. A first thermal barrier layer of about an 8 weight
percent Y2O3 and about 92 weight percent ZrO2 composition was
deposited to a thickness of about 180 microns onto the bondcoated
surface. The 8YSZ had a D50 particle size of about 0.6 microns that
was suspended in ethanol at about 20 wt % solids using
polyethyleneimine as a dispersant (at about 0.2 wt % of the
solids).
[0045] An air plasma torch was utilized to form a first 8YSZ TBC
layer from the 8YSZ suspension on the substrates. In particular,
the 8YSZ suspension was injected into a plasma torch through the
center tube of a tube-in-tube atomizing injector with a nitrogen
atomizing gas sent through the outer tube. An about 3/8 inch
diameter nozzle was used at the end of the plasma torch. The 8YSZ
suspension was pumped to the injector at a feedrate of about 24
ml/min. The plasma torch was rastered across the substrate at about
600 mm/sec with stripe spacing interval of 4 mm. The spray distance
between the torch nozzle and the substrate was about maintained at
about 75 mm. The plasma conditions used included about 300 slpm
total gas flow with about 30% nitrogen, about 10% hydrogen, and
about 60% argon flow ratios. A current of about 180 A was used for
each of the three electrodes, resulting in a total gun power of
about 100 kW.
[0046] A second TBC layer according to the present discourse was
made over the top of the first SYSZ TBC layer by mixing two
separate suspensions in a 1:1 ratio by weight. One suspension was
the suspension used to form the first 8YSZ TBC layer as described
above. The second suspension was 20 percent by weight of
Y.sub.2O.sub.3 particles in ethanol with a D50 particle size of
about 0.5 microns. The two suspensions were mixed together before
injection into the plasma torch described above with respect to the
first TBC layer. The second TBC layer was deposited using the same
plasma conditions as used for the underlying first 8YSZ TBC layer,
except that the spray distance was maintained at about 90 mm to
produce the desired growth domain microstructure.
EXAMPLE 2
[0047] A Hastelloy X substrate with the same NiCrAlY bondcoat as
described above in EXAMPLE 1 was over-coated with a first 8YSZ TBC
layer of about 500 microns (e.g., as described above). A topcoat of
a composite second TBC layer of about 180 micron thickness was
applied onto the first 8YSZ TBC layer. The composite TBC was
produced by injecting a solution made by mixing, at a 4:1 ratio by
weight, first and second ethanol based suspensions. The first
suspension included about 20 weight percent of 8YSZ with a D50
particle size of about 0.6 micron particles, and the second
suspension included 20 weight percent hafnium oxide, HfO.sub.2,
with a D50 particle size of about 0.35 microns. The same plasma
torch configuration as described above in EXAMPLE 1 was used with
plasma conditions of about 300 slpm total gas flow, with about 10%
nitrogen, about 15% hydrogen, and about 75% argon flow ratios. A
current of about 200 A was used for each of the three electrodes,
resulting in a total gun power of about 97 kW. A spray distance of
about 75 mm and suspension feedrate of 24 ml/min was utilized for
both the first and second TBC layers.
[0048] It is to be understood that the above description is
intended to be illustrative, and not restrictive. Numerous changes
and modifications may be made herein by one of ordinary skill in
the art without departing from the general spirit and scope of the
invention as defined by the following claims and the equivalents
thereof. For example, the above-described embodiments (and/or
aspects thereof) may be used in combination with each other. In
addition, many modifications may be made to adapt a particular
situation or material to the teachings of the various embodiments
without departing from their scope. While the dimensions and types
of materials described herein are intended to define the parameters
of the various embodiments, they are by no means limiting and are
merely exemplary. Many other embodiments will be apparent to those
of skill in the art upon reviewing the above description. The scope
of the various embodiments should, therefore, be determined with
reference to the appended claims, along with the full scope of
equivalents to which such claims are entitled. In the appended
claims, the terms "including" and "in which" are used as the
plain-English equivalents of the respective terms "comprising" and
"wherein." Moreover, in the following claims, the terms "first,"
"second," and "third," etc. are used merely as labels, and are not
intended to impose numerical requirements on their objects. Also,
the term "operably" in conjunction with terms such as coupled,
connected, joined, sealed or the like is used herein to refer to
both connections resulting from separate, distinct components being
directly or indirectly coupled and components being integrally
formed (i.e., one-piece, integral or monolithic). Further, the
limitations of the following claims are not written in
means-plus-function format and are not intended to be interpreted
based on 35 U.S.C. .sctn. 112, sixth paragraph, unless and until
such claim limitations expressly use the phrase "means for"
followed by a statement of function void of further structure. It
is to be understood that not necessarily all such objects or
advantages described above may be achieved in accordance with any
particular embodiment. Thus, for example, those skilled in the art
will recognize that the systems and techniques described herein may
be embodied or carried out in a manner that achieves or optimizes
one advantage or group of advantages as taught herein without
necessarily achieving other objects or advantages as may be taught
or suggested herein.
[0049] While the invention has been described in detail in
connection with only a limited number of embodiments, it should be
readily understood that the invention is not limited to such
disclosed embodiments. Rather, the invention can be modified to
incorporate any number of variations, alterations, substitutions or
equivalent arrangements not heretofore described, but which are
commensurate with the spirit and scope of the invention.
Additionally, while various embodiments of the invention have been
described, it is to be understood that aspects of the disclosure
may include only some of the described embodiments. Accordingly,
the invention is not to be seen as limited by the foregoing
description, but is only limited by the scope of the appended
claims.
[0050] This written description uses examples to disclose the
invention, including the best mode, and also to enable any person
skilled in the art to practice the invention, including making and
using any devices or systems and performing any incorporated
methods. The patentable scope of the invention is defined by the
claims, and may include other examples that occur to those skilled
in the art. Such other examples are intended to be within the scope
of the claims if they have structural elements that do not differ
from the literal language of the claims, or if they include
equivalent structural elements with insubstantial differences from
the literal language of the claims.
* * * * *