U.S. patent application number 16/554639 was filed with the patent office on 2019-12-19 for method and apparatus for removing paint on metallic components.
The applicant listed for this patent is IBC Materials & Technologies, Inc.. Invention is credited to Solomon Berman, Daesung Chong, Ashok Ramaswamy.
Application Number | 20190382913 16/554639 |
Document ID | / |
Family ID | 67769985 |
Filed Date | 2019-12-19 |
United States Patent
Application |
20190382913 |
Kind Code |
A1 |
Berman; Solomon ; et
al. |
December 19, 2019 |
METHOD AND APPARATUS FOR REMOVING PAINT ON METALLIC COMPONENTS
Abstract
An apparatus for removing paint from a metallic component. The
apparatus includes an electrolytic cell in which the metallic
component is an anode, and a DC power supply capable of producing a
plasma causing the paint from the metallic component to
disintegrate. A method of depainting a metallic component includes
providing an electrolytic cell with the metallic component to be
depainted acting as an anode. A DC power supply connected to the
cathode and anode is activated to produce a plasma causing the
paint from the metallic component to disintegrate. Another method
of method of depainting a metallic component includes providing an
aqueous solution of sodium hydrogen carbonate, sodium citrate, and
potassium oxalate as an electrolyte, a cathode and a pained
metallic component as an anode. A DC power supply connected to the
cathode and anode produces a plasma causing the paint from the
painted metallic component to disintegrate.
Inventors: |
Berman; Solomon; (Carmel,
IN) ; Chong; Daesung; (Yorktown, IN) ;
Ramaswamy; Ashok; (Indianapolis, IN) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
IBC Materials & Technologies, Inc. |
Lebanon |
IN |
US |
|
|
Family ID: |
67769985 |
Appl. No.: |
16/554639 |
Filed: |
August 29, 2019 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
15490429 |
Apr 18, 2017 |
10400350 |
|
|
16554639 |
|
|
|
|
62325282 |
Apr 20, 2016 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C25F 5/00 20130101; C23G
5/00 20130101; H01J 37/32321 20130101; H01J 2237/334 20130101; C23F
4/00 20130101 |
International
Class: |
C25F 5/00 20060101
C25F005/00; H01J 37/32 20060101 H01J037/32; C23F 4/00 20060101
C23F004/00 |
Claims
1. An apparatus for removing paint from a painted metallic
component comprising: a tank containing a liquid electrolyte; a
cathode immersed in the liquid electrolyte; a painted metallic
component to be depainted acting as anode and immersed in the
liquid electrolyte, the painted metallic component comprising a
primer and one or more layers of paint on a surface thereof; a DC
power supply or a pulsed DC power supply connected to the anode and
cathode to form an electrolytic cell and produce a plasma near the
painted metallic component; and means for activating the DC power
supply to produce the plasma and selecting a voltage for the
electrolytic cell formed by the cathode, the anode, and the liquid
electrolyte and a duration of the plasma that results in the
disintegration of the primer and paint of the one or more layers of
paint from the painted metallic component into pieces that fall
into the liquid electrolyte, thereby resulting in a depainted
metallic component.
2. The apparatus of claim 1, wherein the liquid electrolyte is an
aqueous solution of at least one salt.
3. The apparatus of claim 2, wherein the at least one salt is one
of an ammonium salt, a sodium salt or a potassium salt.
4. The apparatus of claim 2, wherein the at least one salt is two
salts.
5. The apparatus of claim 4, wherein the two salts are an ammonium
salt and a potassium salt.
6. The apparatus of claim 4, wherein the two salts are an ammonium
salt and a sodium salt.
7. The apparatus of claim 4, wherein the two salts are a sodium
salt and a potassium salt.
8. The apparatus of claim 1, wherein the cathode is made of
stainless steel SS 316.
9. The apparatus of claim 3, wherein the painted metallic component
comprises an aluminum alloy.
10. The apparatus of claim 9, wherein the aluminum alloy is Al 7075
or Al 2014.
11. The apparatus of claim 1, wherein the DC power supply is
capable of producing 1000 volts.
12. The apparatus of claim 1, further comprising a draining and
filtration system for the liquid electrolyte capable of capturing
the pieces falling into the liquid electrolyte.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] The present U.S. patent application is a divisional of U.S.
patent application Ser. No. 15/490,429 filed Apr. 18, 2017 which is
related to and claims the priority benefit of U.S. Provisional
Patent Application Ser. No. 62/325,282, filed Apr. 20, 2016. The
contents of both these applications are hereby incorporated by
reference in their entirety into the present disclosure.
TECHNICAL FIELD
[0002] The present disclosure generally relates to methods of paint
removal on metallic components, such as, but not limited to,
structural components used in, but not limited to, aircrafts.
BACKGROUND
[0003] This section introduces aspects that may help facilitate a
better understanding of the disclosure. Accordingly, these
statements are to be read in this light and are not to be
understood as admissions about what is or is not prior art.
[0004] There are many situations wherein paint on a metallic
component is desired to be removed. For purposes of this
disclosure, a component is meant to be a structural component or a
physical component of a mechanical system or an implement providing
a utility. Those of skill in the art will recognize that the
methods and apparatus of this disclosure will apply to a broad
range of metallic components. Such situations, namely where paint
on a metallic component has to be removed, include but are not
limited to inspection of components where the paint can interfere
with the inspection process or techniques, and removing defective
or degrading paint in order to put on fresh paint. Further, in some
situations, where multiple layers of paint or other substances
exist, one or more of these layers may have to be removed. Methods
of such paint removal to date include blasting by plastic media and
chemical processes. These methods typically require specialized
equipment, are expensive and/or are not environmentally
friendly.
[0005] It is desirable to have environmentally friendly,
cost-effective techniques that remove layers of paint and other
substances on metallic components or other objects completely or
selectively.
SUMMARY
[0006] An apparatus for removing paint from a metallic component is
disclosed. The apparatus includes a tank containing a liquid
electrolyte, a cathode immersed in the liquid electrolyte, a
painted metallic component acting as an anode immersed in the
liquid electrolyte, and a DC power supply connected to the anodes
and cathodes to form an electrolytic cell, the electrolytic cell
being capable of producing a plasma near the painted component,
such that the paint from the painted metallic component
disintegrates into pieces falling into the liquid electrolyte,
thereby resulting in a depainted metallic component.
[0007] A method of depainting a metallic component is disclosed.
The method includes providing a tank containing a liquid
electrolyte and a cathode immersed in the liquid electrolyte. A
metallic component to be depainted is immersed into the liquid
electrolyte to act as an anode. A DC power supply is connected to
the anode and cathode to form an electrolytic cell capable of
producing a plasma near the painted metallic component. The DC
power supply is activated to produce a plasma near the painted
metallic component for a duration such that the paint from the
painted metallic component disintegrates into pieces falling into
the liquid electrolyte, thereby resulting in a depainted metallic
component.
[0008] Another method of depainting a metallic component is
disclosed. The method includes providing a tank containing an
aqueous solution of sodium hydrogen carbonate, sodium citrate and
potassium oxalate. The aqueous solution acts as a liquid
electrolyte. The tank also contains a cathode made of 316 SS
immersed in the liquid electrolyte. A painted metallic component is
immersed into the liquid electrolyte to act as an anode. A DC or
pulsed DC power supply capable of producing over 200 volts is
connected to the anode and cathode to form an electrolytic cell
capable of producing a plasma near the painted metallic component.
The DC power supply is activated to produce a plasma near the
painted metallic component for about 5 minutes such that the paint
from the painted metallic component disintegrates into pieces
falling into the liquid electrolyte, thereby resulting in a
depainted metallic component.
BRIEF DESCRIPTION OF DRAWINGS
[0009] While some of the figures shown herein may have been
generated from scaled drawings or from photographs that are
scalable, it is understood that such relative scaling within a
figure are by way of example, and are not to be construed as
limiting.
[0010] FIG. 1 is a schematic representation of one embodiment of
apparatus that can be used for depainting according to this
disclosure.
[0011] FIGS. 2 A and 2B show images of a metallic component made of
Al 7075 alloy before and after paint removal, respectively.
[0012] FIG. 3A represents a cross-sectional image of a part made of
Al 7075 alloy having an anodized layer with a painted surface.
[0013] FIG. 3B shows the part in FIG. 3A after the paint layers
have been removed utilizing the process and apparatus of this
disclosure.
[0014] FIG. 4 is an SEM image of a painted surface prior to PEDP
treatment.
[0015] FIG. 5 is an SEM image of the surface of FIG. 4 after
subjecting to PEDP treatment.
[0016] FIG. 6 shows representative areas of primer and paint
removed from the metallic component.
DETAILED DESCRIPTION
[0017] For the purposes of promoting an understanding of the
principles of the disclosure, reference will now be made to the
embodiments illustrated in the drawings and specific language will
be used to describe the same. It will nevertheless be understood
that no limitation of the scope of the disclosure is thereby
intended, such alterations and further modifications in the
illustrated device, and such further applications of the principles
of the disclosure as illustrated therein being contemplated as
would normally occur to one skilled in the art to which the
disclosure relates.
[0018] FIG. 1 is a schematic representation of one embodiment of an
apparatus 100 according to this disclosure for use in depainting a
metallic component. In this disclosure, the word "depainting" is
used to mean removing paint from a metallic component or its
surface. An entire layer may or may not be removed as a single
entity. In many instances, a layer of paint or a primer used in the
painting process disintegrates into pieces. The apparatus 100
comprises an electrolytic cell, as described below. Referring to
FIG. 1, 101 represents a tank comprising a liquid electrolyte 102.
A non-limiting example of electrolyte 102 is an aqueous solution
with a pH in the range of 5-9. Examples of electrolytes suitable
for purposes of this disclosure include, but are not limited to
aqueous solution of ammonium salts or potassium salts or sodium
salts. Salts suitable for this purpose include, but not limited to
ammonium chloride, ammonium fluoride, ammonium sulfate, ammonium
citrate, ammonium hydrogen carbonate, ammonium carbonate, ammonium
oxalate, ammonium formate, ammonium acetate, ammonium nitrate,
sodium chloride, sodium fluoride, sodium sulfate, sodium phosphate,
sodium hydrogen carbonate, sodium carbonate, sodium oxalate, sodium
formate, sodium acetate, sodium nitrate, potassium chloride,
potassium fluoride, potassium sulfate, potassium phosphate,
potassium hydrogen carbonate, potassium carbonate, potassium
oxalate, potassium formate, potassium acetate, and potassium
nitrate. It should be noted that the aqueous solution used as the
electrolyte can contain more than one salt, such as two, three or
more salts. In FIG. 1, 103 represents a metallic component (or
part) comprising a layer or layers of paint which is desired to be
removed and forms an anode. In FIG. 1, 104 is a cathode. As a
non-limiting example, cathode 104 can be made of stainless steel, a
non-limiting example of which is, SS 316. SS 316 is a designation
of stainless steel known to those skilled in the art. As a
non-limiting example, 103 can be a component made of aluminum or
its alloys. In this example, 103 can further contain an anodized
layer with a paint layer on top of the anodized layer. Referring
again to FIG. 1, 105 represents a DC or pulsed DC power supply
suitably connected to the electrodes (anodes and cathode) so as to
form an electrolytic cell. It should be noted that the methods an
apparatuses of this disclosure can utilize DC or pulsed DC.
Voltages indicated would refer to peak voltage when pulsed DC is
employed.
[0019] In operation, a DC or pulsed DC voltage is applied to an
electrolytic cell as shown in FIG. 1. Referring again to FIG. 1,
under the action of this voltage, a plasma (not shown) is created
in the vicinity of the part 103 containing a painted section or
surface. The plasma so created acts to affect the integrity of
adhesion of paint to the metallic component 103 or the adhesion of
paint to a layer of another material (such as an anodized layer)
which is part of the metallic component 103, in such a way that the
paint loses adhesion and disintegrates and falls into the
electrolyte as particles or agglomerates of particles of chunks of
particles. In practice, the paint layer or layers also contain a
primer material which is applied to a surface prior to painting.
The primer material also disintegrates in this paint removal
process of this disclosure and can be removed by filtration of the
electrolyte containing the removed paint and/or removed primer.
[0020] It should be noted that while one anode (the metallic
component) and one cathode are shown, it is possible to utilize
counter electrodes, thus having more than two electrodes in the
electrolytic cell of FIG. 1. The methodology of employing counter
electrodes is known to those skilled in the art.
[0021] It should be further noted that the apparatus shown in FIG.
1 can be enhanced or modified by including a draining, and
filtration system for the electrolyte, so that the pieces of the
disintegrated paint and primer can be captured.
[0022] The degree of disintegration of the primer and paint depends
on the strength of the plasma, which in turn depends on the voltage
applied to the electrolytic cell, the current density of the anode
and the duration of the plasma created. FIGS. 2A and 2B show images
of a component made of Al 7075 alloy (known to those skilled in the
art) before and after paint removal, respectively. The duration of
plasma to achieve the surface shown in FIG. 2B is approximately 5
minutes utilizing an aqueous electrolyte solution with pH in the
range of 5-9 and applying a voltage over 200 Volts. The strength of
a plasma is related to applied voltage and the current density
created on the anode. In the experiments leading to this
disclosure, the current density on the anode varied between 0.18 to
0.24 Amperes/square centimeter. It should be noted that shorter and
longer times are possible depending on the thickness of the painted
layers, composition of the paint and primer, for the duration of
the plasma to achieve acceptable results. In this disclosure, the
above described depainting process will be referred to as Plasma
Electrolytic Depainting Process (PEDP), and the depainting method
as s PEDP treatment.
[0023] FIG. 3A represents a cross-sectional optical microscopy
image of a part made of Al 7075 having an anodized layer with a
painted surface. In FIG. 3A, it can be seen that there is layer of
epoxy and polyurethane-based painted layers adherent to and on top
of an anodized layer which is on top and adherent to the base
metal. FIG. 3B shows a cross-sectional optical microscopy image of
a structure similar to the one in FIG. 3A, but after a depainting
or PEPD treatment is completed, showing that the paint layers have
been removed utilizing the process and apparatus of this disclosure
as described above. In both the figures, namely FIGS. 3A and 3B,
the layer marked resin represents the mounting compound used in the
preparation of the optical microscopy samples in producing the
images, as is generally understood by those skilled in the art.
[0024] FIG. 4 is a Scanning Electron Microscope (SEM) image of a
painted surface of a component made of Al 7075 alloy prior to PEDP
treatment showing high level of metal oxides (through Energy
Dispersive Spectroscopy (EDS) analysis), in part of the aluminum
alloy substrate captured in FIG. 4. X-ray Diffraction pattern
analysis of painted parts before PEDP treatment detected the
presence of many elements and compounds contained in the paint and
primer, as well as aluminum from Al 7075 alloy. The surface after
the PEDP treatment can be called depainted surface. FIG. 5 is an
SEM image of the surface of FIG. 4 after subjecting to PEDP
treatment. In other words FIG. 5 is an SEM image of depainted
surface of Al 7075 alloy. It should be noted that in FIG. 5, the
paint layer has been removed exposing the anodized layer on which
the original paint was adhering, showing that integrity of the
anodized layer has been preserved. EDS analysis of the depainted
surface confirmed that the exposed layer of the depainted part is
anodized layer.
[0025] FIG. 6 is an image of pieces of the primer and paint removed
from the part made of Al 7075 shown FIG. 2A. In FIG. 6,
representative pieces of primer and paint removed from the metallic
component by the PEDP treatment of this disclosure are marked.
These pieces are obtained by filtration of the electrolyte used in
the PEDP treatment after the PEDP treatment of the metallic
component is completed.
[0026] It should be noted that, for a given size of the metallic
component and its composition, by proper selection of the
combination of voltage for electrolytic cell of this disclosure and
the plasma duration in the PEDP treatment. In particular, by a
proper combination of the electrolytic cell voltage and plasma
duration, paint layers can be removed selectively, without damaging
the integrity of the anodized layer prevailing in, for example, the
Al 7075 alloy, and adhesion of the anodized layer to the base
alloy.
[0027] The PEDP treatment of this disclosure can be useful in
achieving depainting of metallic components used in many
industries. A non-limiting example is aerospace industry.
[0028] Based on the above detailed description, it is an objective
of this disclosure to describe an apparatus for removing paint from
a metallic component. The apparatus includes a tank containing a
liquid electrolyte, a cathode immersed in the liquid electrolyte, a
painted metallic component acting as an anode immersed in the
liquid electrolyte, and a DC or pulsed DC power supply connected to
the anode and cathode to form an electrolytic cell, wherein the
electrolytic cell capable of producing a plasma near the painted
metallic component, such that the paint from the metallic component
disintegrates into pieces falling into the liquid electrolyte,
thereby resulting in a depainted metallic component. In some
embodiments of the apparatus of this disclosure, the liquid
electrolyte is an aqueous solution of a salt. Salts suitable for
this purpose include but not limited to ammonium salts, sodium
salts, and potassium salts. Non-limiting examples of ammonium salts
are: ammonium chloride, ammonium fluoride, ammonium sulfate,
ammonium citrate, ammonium hydrogen carbonate, ammonium carbonate,
ammonium oxalate, ammonium formate, ammonium acetate, and ammonium
nitrate. Non-limiting examples of sodium salts suitable for the
apparatus of this disclosure are sodium chloride, sodium fluoride,
sodium sulfate, sodium phosphate, sodium hydrogen carbonate, sodium
carbonate, sodium oxalate, sodium formate, sodium acetate, and
sodium nitrate. Non-limiting examples of potassium salts suitable
for the apparatus of this disclosure are potassium chloride,
potassium fluoride, potassium sulfate, potassium phosphate,
potassium hydrogen carbonate, potassium carbonate, potassium
oxalate, potassium formate, potassium acetate, and potassium
nitrate. In some embodiments of the apparatus, more than one salt
can be used. A non-limiting example of using more than one salt can
include usage of an ammonium salt, a sodium salt and a potassium
salt or combinations thereof. Materials suitable for a cathode of
this apparatus include, but not limited to stainless steel, such
as, but not limited to SS316. In some embodiments of the apparatus,
the metallic component which is depainted can be made of an alloy.
In some embodiments, the alloy can be an aluminum alloy, such as,
but not limited to Al 7075. In some embodiments of the apparatus,
the DC or pulsed DC power supply is capable of producing 1000
Volts. In some embodiments of the apparatus, a draining and
filtration system for the liquid electrolyte, capable of capturing
the pieces falling into the liquid electrolyte, can be
incorporated.
[0029] It is another objective of this disclosure to describe a
method of depainting a metallic component. The method includes
providing a tank containing a liquid electrolyte and a cathode
immersed in the liquid electrolyte, immersing a metallic component
to be depainted into the liquid electrolyte to act as an anode,
providing a DC power supply connected to the anodes and cathode to
form an electrolytic cell capable of producing a plasma near the
painted metallic component, and activating the DC power supply to
produce a plasma near the painted metallic component for a duration
such that the paint from the metallic component disintegrates into
pieces falling into the liquid electrolyte, thereby resulting in a
depainted metallic component. In some embodiments of the method, of
this disclosure, the liquid electrolyte is an aqueous solution of a
salt. Salts suitable for this purpose include but not limited to
ammonium salts, sodium salts, and potassium salts. Non-limiting
examples of ammonium salts are: ammonium chloride, ammonium
fluoride, ammonium sulfate, ammonium citrate, ammonium hydrogen
carbonate, ammonium carbonate, ammonium oxalate, ammonium formate,
ammonium acetate, and ammonium nitrate. Non-limiting examples of
sodium salts suitable for the apparatus of this disclosure are
sodium chloride, sodium fluoride, sodium sulfate, sodium phosphate,
sodium hydrogen carbonate, sodium carbonate, sodium oxalate, sodium
formate, sodium acetate, and sodium nitrate. Non-limiting examples
of potassium salts suitable for the apparatus of this disclosure
are potassium chloride, potassium fluoride, potassium sulfate,
potassium phosphate, potassium hydrogen carbonate, potassium
carbonate, potassium oxalate, potassium formate, potassium acetate,
and potassium nitrate. In some embodiments of the apparatus, more
than one salt can be used. A non-limiting example of using more
than one salt can include use of an ammonium salt, a sodium salt
and a potassium salt or combinations thereof. Materials suitable
for a cathode of this method include, but not limited to stainless
steel, such as, but not limited to SS316. In some embodiments of
the method, the metallic component which is depainted can be made
of an alloy. In some embodiments, the alloy can be an aluminum
alloy, such as, but not limited to Al 7075. In some embodiments of
the method, the DC or pulsed DC power supply is capable of
producing 1000 Volts. In some embodiments of the apparatus, a
draining and filtration system for the liquid electrolyte, capable
of capturing the pieces falling into the liquid electrolyte, can be
incorporated. In some embodiments of the method, the metallic
component is an aircraft component. In some preferred embodiments,
the metallic component is or part of an aircraft wheel. In some
embodiments, the wheel comprises an aluminum alloy, such as but not
limited to Al 7075. In some embodiments of the method, the duration
of activating the DC power supply is in the range of 1-30
minutes.
[0030] In some embodiments of the method of this disclosure, the
method of depainting a metallic component includes providing a tank
containing an aqueous solution of sodium hydrogen carbonate in the
range of, 2-28%, sodium citrate <9%, and potassium oxalate
<12%, as a liquid electrolyte with a pH of 8, and 316 SS as
cathode immersed in the liquid electrolyte, immersing a metallic
component made of an aluminum alloy, such as but not limited to Al
7075 or Al 2014, to be depainted into the liquid electrolyte to act
as an anode, providing a DC power supply connected to the anodes
and cathode to form an electrolytic cell capable of producing a
plasma near the painted metallic component, and activating the DC
power supply producing a voltage of more than 200 volts to produce
a plasma near the painted metallic component for a duration in the
range of 1-30 minutes such that the paint from the painted metallic
component disintegrates into pieces falling into the liquid
electrolyte, thereby resulting in a depainted metallic
component.
[0031] The scope of this disclosure is not limited to aluminum and
its alloys as the materials from which depainting is achieved.
Components made of other materials such as titanium alloys, nickel
alloys and steel alloys are also suitable for depainting by the
PEDP treatment described of this disclosure. Further, the power
supply can be configured to provide DC or pulsed DC voltages up to
1000 Volts nominal but can be smaller or greater than 1000 volts as
required for the operation. The pH of the electrolyte can vary in
the range of 3-12. Further, it should be stressed that, while
several embodiments described in this disclosure make reference to
DC power supply, it is an objective of this disclosure to assert
that pulsed DC supply can be employed in place of DC power supply
in all the embodiments of this disclosure.
[0032] It should be recognized that the methods and apparatus of
this disclosure are applicable to a variety of metallic components
in a variety of applications and industry. A non-limiting example
of an industry is the aircraft industry wherein many metallic
components such as, but not limited to aircraft wheels, require
depainting. Similarly many equipments including but not limited to
military equipment such as, but not limited to weapons systems,
have metallic components that need depainting. In all the
applications, the methods and apparatus of this disclosure are
applicable to a variety of metals and alloys. That is, the metallic
components to be depainted, in aircraft or other industries, can be
made of aluminum, steel, titanium or other metals and alloys.
[0033] In some situations, such as for inspection of high stress
areas for cracks, it may be required that paint be removed from a
metallic component only in selected areas. Such selective
depainting can be achieved by suitably masking the anode (masking
methods are known to those skilled in the art) thereby preventing
the masked areas from the effects of plasma and hence the
depainting.
[0034] While the invention has been described in terms of specific
embodiments, including particular configurations, it is apparent
that other forms could be adopted by one skilled in the art.
Accordingly, it should be understood that the invention is not
limited to the specific disclosed embodiments. Other
implementations are possible. Therefore, the scope of the invention
is to be limited only by the following claims.
* * * * *