U.S. patent application number 16/438160 was filed with the patent office on 2019-09-26 for personal watercraft fabrication using thermoforming.
The applicant listed for this patent is Free Form Factory, Inc.. Invention is credited to Jordan Darling.
Application Number | 20190291334 16/438160 |
Document ID | / |
Family ID | 58719938 |
Filed Date | 2019-09-26 |
![](/patent/app/20190291334/US20190291334A1-20190926-D00000.png)
![](/patent/app/20190291334/US20190291334A1-20190926-D00001.png)
![](/patent/app/20190291334/US20190291334A1-20190926-D00002.png)
![](/patent/app/20190291334/US20190291334A1-20190926-D00003.png)
![](/patent/app/20190291334/US20190291334A1-20190926-D00004.png)
![](/patent/app/20190291334/US20190291334A1-20190926-D00005.png)
![](/patent/app/20190291334/US20190291334A1-20190926-D00006.png)
![](/patent/app/20190291334/US20190291334A1-20190926-D00007.png)
![](/patent/app/20190291334/US20190291334A1-20190926-D00008.png)
![](/patent/app/20190291334/US20190291334A1-20190926-D00009.png)
United States Patent
Application |
20190291334 |
Kind Code |
A1 |
Darling; Jordan |
September 26, 2019 |
PERSONAL WATERCRAFT FABRICATION USING THERMOFORMING
Abstract
Personal watercraft and personal watercraft fabrication using a
thermoforming process are described. The personal watercraft
manufacturing process includes a set of molds, thermoforming
equipment, and thermal formable materials. The process greatly
reduces manufacturing costs, decreases manufacturing time,
increases part consistency and tolerances, offers better
performance characteristics and durability and results in less
environmentally harmful deposits and waste.
Inventors: |
Darling; Jordan; (Mesa,
AZ) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Free Form Factory, Inc. |
Phoenix |
AZ |
US |
|
|
Family ID: |
58719938 |
Appl. No.: |
16/438160 |
Filed: |
June 11, 2019 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
14949881 |
Nov 24, 2015 |
|
|
|
16438160 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
B29K 2105/256 20130101;
B29C 51/421 20130101; B63B 5/24 20130101; B63B 34/10 20200201; B29C
51/266 20130101; B29L 2031/3067 20130101; B63B 73/00 20200101; B29C
51/10 20130101; B29L 2031/307 20130101 |
International
Class: |
B29C 51/10 20060101
B29C051/10; B29C 51/26 20060101 B29C051/26; B63B 5/24 20060101
B63B005/24; B63B 9/06 20060101 B63B009/06; B29C 51/42 20060101
B29C051/42 |
Claims
1. A method of forming a jet-pump powered personal watercraft, the
method comprising: producing a top deck mold for a first component
of the personal watercraft, the top deck mold including a feature
for assimilation into the first component, the feature comprising
at least one of a foot tray feature, a bulkhead/firewall feature, a
gunwales feature, and an engine bay opening feature, wherein the
top deck mold further comprises a first bond rail feature; drawing
a heated first thermoplastic material into or over the top deck
mold using a vacuum to form the first component; extracting the
first component from the top deck mold; producing a bottom hull
mold for a second component of the personal watercraft, the bottom
hull mold including a convex groove feature running longitudinally
along the bottom hull mold and parallel to a center line of the
bottom hull mold, and a second bond rail feature having a shape
complementary of the first bond rail; drawing a heated second
thermoplastic material into or over the bottom hull mold using a
vacuum to produce the second component; and extracting the second
component from the bottom hull mold.
2. The method of claim 1, wherein the top deck mold comprises a
foot tray feature, a bulkhead/firewall feature, a gunwales feature,
and an engine bay opening feature.
3. The method of claim 1, wherein the bottom hull mold further
comprises a mid-rocker feature and a pump cavity feature.
4. The method of claim 1, further comprising trimming excess
material from the first component and trimming excess material from
the second component.
5. The method of claim 1, further comprising coupling the first
bond rail of the first component to the second bond rail of the
second component to form the personal watercraft.
6. The method of claim 1 wherein at least one of the first
thermoplastic material and the second thermoplastic material
comprise a non-volatile organic compound (VOC) material.
7. The method of claim 2, further comprising producing a hood mold
having a shape configured to engage with the engine bay opening
feature of the first component.
8. The method of claim 3, further comprising producing a plate
covering mold having a shape configured to engage with the pump
cavity feature of the second component.
9. The method of claim 7, further comprising: drawing a heated
third thermoplastic material into or over the hood mold using a
vacuum to form a hood; extracting the hood from the hood mold; and
coupling the hood to the first component proximate the engine bay
opening.
10. The method of claim 8, further comprising: drawing a heated
fourth thermoplastic material into or over a plate covering mold
using a vacuum to form a plate covering; extracting the plate
covering from the plate covering mold; and coupling the plate
covering to the second component proximate the pump cavity.
11. A method of forming a jet-pump powered personal watercraft, the
method comprising: drawing a heated first thermoplastic material
into or over a top deck mold using a vacuum to form a top deck,
wherein the top deck mold includes a first bond rail a foot tray
feature, a bulkhead/firewall feature, a gunwales feature, and an
engine bay opening feature; extracting the top deck from the top
deck mold; drawing a heated second thermoplastic material into or
over the bottom hull mold using a vacuum to produce a bottom hull,
wherein the bottom hull mold includes a convex groove feature
running longitudinally along the bottom hull mold and parallel to a
center line of the bottom hull mold, a second bond rail feature
having a shape complementary of the first bond rail, and a pump
cavity feature; extracting the bottom hull from the bottom hull
mold; drawing a heated third thermoplastic material into or over a
hood mold using a vacuum to form a hood; extracting the hood from
the hood mold; drawing a heated fourth thermoplastic material into
or over a plate covering mold using a vacuum to form a plate
covering; extracting the plate covering from the plate covering
mold; coupling the first bond rail of the top deck to the second
bond rail of the bottom hull; coupling the plate covering to the
second component proximate a pump cavity of the bottom hull; and
coupling the hood to the first component proximate an engine bay
opening of the top deck.
12. The method of claim 11, wherein the bottom hull mold further
comprises a mid-rocker feature.
13. The method of claim 11, further comprising trimming excess
material from the top deck and trimming excess material from the
bottom hull.
14. The method of claim 11, wherein at least one of the first
thermoplastic material and the second thermoplastic material
comprise a non-volatile organic compound (VOC) material.
15. A bottom hull and top deck for a jet-pump powered personal
watercraft, comprising: the top deck formed from a first
thermoplastic material, wherein the top deck comprises a foot tray
feature, a bulkhead/firewall feature, a gunwales feature, an engine
bay opening feature, and a first bond rail feature; and the bottom
hull formed from a second thermoplastic material and coupled to the
top deck, wherein the bottom hull comprises a concave groove
feature running longitudinally along the bottom hull and parallel
to a center line of the bottom hull, and a second bond rail feature
having a shape complementary of the first bond rail feature.
16. The bottom hull and top deck of claim 15, wherein the first
bond rail feature is coupled to the second bond rail feature.
17. The bottom hull and top deck of claim 15, wherein the first
thermoplastic material and the second thermoplastic material are
the same material.
18. The bottom hull and top deck of claim 15, wherein the first
thermoplastic material and the second thermoplastic material do not
contain volatile organic compound (VOC) material.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is a continuation of co-pending U.S. patent
application Ser. No. 14/949,881 filed Nov. 24, 2015, now U.S.
Patent Application Publication 2017-0144359 entitled "PERSONAL
WATERCRAFT FABRICATION USING THERMOFORMING." The disclosures of all
the foregoing applications are incorporated herein by reference in
their entireties, including but not limited to those portions that
specifically appear hereinafter, but except for any subject matter
disclaimers or disavowals, and except to the extent that the
incorporated material is inconsistent with the express disclosure
herein, in which case the language in this disclosure shall
control.
TECHNICAL FIELD
[0002] The present disclosure generally relates to watercraft,
watercraft fabrication, and generally to the use of a thermoforming
process to fabricate components. More specifically, the present
disclosure relates to personal watercraft fabrication using
thermoforming.
COPYRIGHT
[0003] A portion of the disclosure of this patent document contains
material that is subject to copyright protection. The copyright
owner has no objection to the facsimile reproduction of the patent
document or the patent disclosure, as it appears in the Patent and
Trademark Office patent files or records, but otherwise reserves
all copyright rights whatsoever. The following notice applies to
the disclosure and data as described below and in the drawings that
form a part of this document: Copyright 2014-2015 Free Form Factory
Inc., All Rights Reserved.
RELATED ART
[0004] Watercraft, including jetskis, are a common mode of
transportation on the water. However, conventional watercraft have
physical and structural boundaries that are being pushed by
enthusiasts every day. In many cases, the advancement of watercraft
engines is outpacing the design and manufacturing of the hulls. The
hulls on conventional watercraft are still manufactured using
costly, time-consuming, and environmentally detrimental processes.
There is a need for a stronger, easier to manufacture, and
environmentally-conscious manufacturing process for personal
watercraft hull, deck, and covering components to accommodate this
rapidly advancing industry.
[0005] Personal watercraft are currently manufactured using the
process of fiberglass lay-up. This process is used to fabricate
standard sport boat types of watercraft hulls in a closed mold
resin transfer molding (RTM) process or a vacuum molding process.
In a RTM process, a two-piece mold consists of a female dye
(cavity) and a male dye (core) used in the process. A composite
mixture of resin, reinforcement, filler, and additives is placed
between the two matched molds, which are then closed under pressure
to cure the composite into a solid reinforced plastic part. The
fiberglass manufacturing process is labor-intensive,
time-consuming, and releases volatile organic compounds (VOC) that
may be toxic to those manufacturing it. Additionally, the
fiberglass fabrication process imposes limitations on the
performance, durability, and consistency in the manufacturing of
watercraft parts.
[0006] For example, U.S. Pat. No. 2,617,126 to Nebesar demonstrates
the use of impregnated fiberglass to create a solid one-piece hull.
In FIG. 1 of Nebesar, a laborer is depicted in the beginning of the
lay-up process wearing a respirator. This is indicative of the
hazardous airborne chemicals that are emitted during this
manufacturing method. Also indicated are multiple steps and complex
jigs required to execute this hull manufacturing method. This
similar method, and its downfalls, are demonstrated in U.S. Pat.
No. 5,433,165 to McGuiness. These similar processes and their flaws
are typical when the manufacturing process uses hand labor that
requires multiple layers of fiberglass material and resins joined
together. The conventional process of constructing each boat hull
and deck is time-consuming and labor-intensive, thereby adding to
the overall cost of construction. Additionally, there are
environmental issues with the construction of fiberglass boats in
the creation of volatile organic compounds.
[0007] U.S. Pat. No. 8,701,585 to Seaman describes watercraft, such
as a boat, that is molded in two sections, such as the boat deck
and the boat hull, using a polyuria composition and polyurethane
foam and chopped glass fibers. The result is a monolithic structure
that can allegedly be manufactured quickly in a closed molding
process that does not create volatile organic compounds. However,
the described manufacturing process is very expensive and requires
skilled labor. There are variables in each lay-up, such as the
expansion rate of the foam compound, which must be determined and
that add to the complexity of this process. In addition, the
compound typically requires an embedded metal frame and a
UV-protection coating in order to make it last in the typical use
conditions. All of this conventional process is complex,
inconsistent, requires skilled labor, and yields a product that
will eventually fail structurally over time and produce
un-recyclable waste.
SUMMARY
[0008] In various example embodiments shown and described herein, a
method of manufacturing objects, such as personal watercraft hulls,
decks, hoods, and covering components by thermoforming sheets of
thermoplastic material is disclosed. In an example embodiment,
sheets of thermoplastic material are heated and a thermoforming
step is performed in which the heated sheets are manipulated
plastically inside or outside of a mold using heat and vacuum
and/or air pressure. In various example embodiments, the disclosed
process is directed to an application of forming polymers and other
especially thermo-reactive plastics using rapid changes in
temperature that correlate to the properties of the given material.
As described in more detail herein, the material is formed to a
molded surface and cured/cooled down. In an example embodiment, the
process is used in the fabrication of personal watercraft,
including, but not limited to, personal watercraft hulls, decks,
hoods, and covering components. The various embodiments described
herein include a variety of products and methods for a variety of
watercraft, including both sit down watercraft, stand up
watercraft, jetskis, and the like.
[0009] Manufacturing personal watercraft hulls, decks, hoods, and
covering components comprises the use of molds, male or female, to
which the thermoset plastic or other thermoplastic material will
form, thereby creating the desired components. The formed sheets of
thermoplastic material can then be trimmed to the specified part
for final assembly. This process greatly reduces manufacturing
costs, decreases manufacturing time, increases part consistency,
offers better performance characteristics and durability, and
results in less environmentally harmful deposits and waste.
[0010] An objective of the various example embodiments is to
provide a means of manufacturing personal watercraft hulls, decks,
hoods, and covering components so that they are more durable and
rigid, easier to manufacture, quicker to manufacture, and result in
less environmentally harmful waste. In various example embodiments,
a thermoforming manufacturing process is used to fabricate personal
watercraft hulls, decks, hoods, and covering components.
[0011] In an example embodiment, a personal watercraft hull, deck,
hood, and covering components will resist higher impacts, because
of the method of thermoform manufacturing as disclosed herein.
[0012] In an example embodiment, a personal watercraft hull, deck,
hood, and covering components will have decreased manufacturing
times, because of the method of thermoform manufacturing as
disclosed herein.
[0013] In an example embodiment, a personal watercraft hull, deck,
hood, and covering components will have increased consistency per
part, because of the method of thermoform manufacturing as
disclosed herein.
[0014] In an example embodiment, a personal watercraft hull, deck,
hood, and covering components will be environmentally friendly and
recyclable, because of the method of thermoform manufacturing as
disclosed herein.
[0015] Other features and advantages of the example embodiments
will become apparent from the following detailed description taken
in conjunction with the accompanying drawings which illustrate, by
way of example, the principles of the example embodiments.
BRIEF DESCRIPTION OF THE DRAWINGS
[0016] For a better understanding of the example embodiments,
reference should be made to the following detailed description
disclosed in conjunction with the accompanying drawings, in
which:
[0017] FIG. 1 is a top view of a personal watercraft thermoforming
bottom hull mold;
[0018] FIG. 2 is a perspective view of a personal watercraft
thermoforming bottom hull mold;
[0019] FIG. 3 is a top view of a personal watercraft thermoforming
top deck mold;
[0020] FIG. 4 is a perspective view of a personal watercraft
thermoforming top deck mold;
[0021] FIG. 5 is a top view of a personal watercraft thermoforming
hood and covering component family mold;
[0022] FIG. 6 is a perspective view of a personal watercraft
thermoforming hood and covering component family mold;
[0023] FIG. 7 is a top view of the result of thermoform
manufacturing a bottom hull according to an example embodiment;
[0024] FIG. 8 is a perspective view of the result of thermoform
manufacturing a bottom hull according to an example embodiment;
[0025] FIG. 9 is a top view of the result of thermoform
manufacturing a top deck according to an example embodiment;
[0026] FIG. 10 is a perspective view of the result of thermoform
manufacturing a top deck according to an example embodiment;
[0027] FIG. 11 is a top view of the result of thermoform
manufacturing a hood and covering components according to an
example embodiment;
[0028] FIG. 12 is a perspective view of the result of thermoform
manufacturing a hood and covering components according to an
example embodiment;
[0029] FIG. 13 is a perspective view of the assembled hull, top
deck, and hood manufactured by the method of thermoform
manufacturing according to an example embodiment;
[0030] FIG. 14 is a top view of the assembled hull, top deck, and
hood manufactured by the method of thermoform manufacturing
according to an example embodiment;
[0031] FIG. 15 is a side view of the assembled hull, top deck, and
hood manufactured by the method of thermoform manufacturing
according to an example embodiment;
[0032] FIG. 16 is a bottom view of the assembled hull, top deck,
and hood manufactured by the method of thermoform manufacturing
according to an example embodiment; and
[0033] FIG. 17 is a flowchart illustrating one method of personal
watercraft hull, deck, hood, and covering component manufacturing
by the method of thermoform manufacturing according to an example
embodiment.
DETAILED DESCRIPTION
[0034] Reference will now be made in detail to the example
embodiments illustrated in the accompanying drawings. Wherever
possible, the same reference numbers will be used throughout the
drawings to refer to the same or like parts. Personal watercraft
and personal watercraft fabrication using a thermoforming process
are described herein.
[0035] FIG. 1 is a top view of a personal watercraft thermoforming
bottom hull mold. FIG. 2 is a perspective view of a personal
watercraft thermoforming bottom hull mold. As shown in FIGS. 1 and
2, a mold can be used to fabricate a watercraft bottom deck/hull
(e.g., the bottom section of the watercraft) using a thermoforming
process. In an example embodiment, the illustrated mold includes a
first feature 1A used to form a mid-rocker 1 in the fabricated
bottom hull (e.g., see FIGS. 7, 8, and 15). The mid-rocker 1 is
produced by a low, generally flat recessed feature 1A in the mold
running longitudinally at the centerline 10 from the bow to a pump
intake feature aft of the point amidships. On the exterior side of
the fabricated bottom hull, the mid-rocker 1 is a generally flat
raised area in the hull running longitudinally at the centerline 10
and parallel with the centerline 10. The mid-rocker 1 provides lift
in the center of the bottom deck/hull by slowing down the flow of
water, thereby giving the hull a unique aquatic handling
characteristic.
[0036] Referring still to FIGS. 1 and 2 in the example embodiment,
the illustrated bottom hull mold includes second features 2A used
to form chines 2 in the fabricated bottom hull (e.g., see FIGS. 7,
8, and 15). The chines 2 are produced by convex, raised features 2A
in the mold running longitudinally both port and starboard of the
centerline and parallel with the centerline 10. On the exterior
side of the fabricated bottom hull, the chines 2 are concave
grooves in the hull running longitudinally on either side of the
centerline 10 and parallel with the centerline 10. The chines 2
provide a means of carving and turning and improve the aquatic
handling of the watercraft. On the interior side of the fabricated
bottom hull, the valley of the chines 2 are designed to accommodate
an internal structure that provides rigidity and eliminates
unwanted flex of the hull.
[0037] Referring still to FIGS. 1 and 2 in the example embodiment,
the illustrated bottom hull mold includes a third feature 9A used
to form a pump cavity/pump tunnel 9 in the fabricated bottom hull
(e.g., see FIGS. 7 and 8). The pump cavity/pump tunnel 9 is
produced by a convex, rounded feature 9A in the aft portion of the
mold to produce a cavity or tunnel 9 in the fabricated bottom hull.
The pump cavity/pump tunnel 9 is provided in the fabricated bottom
hull to accommodate the intake of water into a jet pump.
[0038] Given the bottom hull mold as illustrated in FIGS. 1 and 2
and described above, the fabricated bottom hull can be produced
with this mold using a thermoforming process instead of a
conventional fiberglass/resin process. In an example embodiment,
one or more sheets of thermoplastic material can be heated in
conventional ways, such as by insertion into a heating unit or
heater. The thermoplastic material can be any of a variety of
standard polymers, thermo-reactive plastics, and other
thermoplastic materials. The heated thermoplastic sheets can be
manipulated plastically in or outside of the mold using heat and
vacuum and/or air pressure. Desired temperature levels and
corresponding pliability levels can be achieved. Especially
thermo-reactive plastics can accommodate rapid changes in
temperature that correlate to the properties of the given material.
After the thermoplastic sheet is heated to a desired temperature,
the heated thermoplastic sheet can be draped over the mold, such as
the bottom hull mold described above. Positive or negative air
pressure or a vacuum can be used to draw the heated thermoplastic
sheet into the mold and into contact with the various features of
the mold as described above. By virtue of the geometry and
configuration of the mold features and the pliability of the
thermoplastic sheet controlled by the temperature and properties of
the material, the heated thermoplastic sheet is drawn into the mold
in a manner that minimizes or eliminates air pockets between the
heated thermoplastic sheet and the outer surface of the mold. Once
the heated thermoplastic sheet has completely enveloped the mold
and assimilated the features of the mold, the thermoplastic sheet
can be allowed to cool. After the thermoplastic sheet has cooled,
the material hardens in the shape of the features on the mold and
becomes a fabricated part. In the case of the use of the bottom
hull mold as described above, the fabricated part becomes the
fabricated bottom hull. At this point, the fabricated part can be
extracted from the mold. Any excess material can be trimmed from
the fabricated part. The fabricated part is now ready to be coupled
with other fabricated parts to produce the final assembly. As a
result, a variety of parts can be fabricated using the
thermoforming process described herein.
[0039] FIG. 3 is a top view of a personal watercraft thermoforming
top deck mold. FIG. 4 is a perspective view of a personal
watercraft thermoforming top deck mold. As shown in FIGS. 3 and 4,
a mold can be used to fabricate a watercraft top deck using the
thermoforming process described above. In an example embodiment,
the illustrated mold includes a first feature 3A used to form a
foot tray/trays 3 in the fabricated top deck (e.g., see FIGS. 9 and
10). The foot tray/trays 3 are produced by a raised, generally flat
feature 3A in the mold at the aft end of the watercraft mold. On
the exterior side of the fabricated top deck, the foot tray/trays 3
are a generally flat lowered area in the top deck at the aft end of
a stand up watercraft and on either side of a sit down watercraft.
The foot tray/trays 3 provide a place for the rider or riders to
stand/place their feet in the finished watercraft assembly. In an
example embodiment, a vertical wall, also known as a
bulkhead/firewall, can be fabricated under the front edge of the
foot tray/trays 3, in between the top deck and bottom hull
components. This bulkhead/firewall can also be thermoformed,
thereby providing a tight tolerance and a repeatable precision
part. The bulkhead/firewall provides a means of mounting drivetrain
couples and plumbing inside the fabricated watercraft.
[0040] Referring still to FIGS. 3 and 4 in the example embodiment,
the illustrated top deck mold includes second features 4A used to
form gunwales 4 in the fabricated top deck (e.g., see FIGS. 9 and
10). The gunwales 4 are produced by generally rectangular, lowered
features 4A at the aft end of the watercraft mold. On the exterior
side of the fabricated top deck, the gunwales 4 are generally
rectangular, raised short walls. The gunwales 4 are provided to
prevent the rider/rider's feet from sliding off the side of the
foot tray/trays 3.
[0041] Referring still to FIGS. 3 and 4 in the example embodiment,
the illustrated top deck mold includes a third feature 5A used to
form an engine bay opening 5 in the fabricated top deck (e.g., see
FIGS. 9 and 10). The engine bay opening 5 is produced by generally
rectangular, lowered feature 5A at the center of the watercraft
mold. On the exterior side of the fabricated top deck, the engine
bay opening 5 is a generally rectangular, raised area in the top
deck. The engine bay opening 5 is produced to provide an entry
point into the engine bay of the watercraft.
[0042] Referring again to FIGS. 1 through 4 in the example
embodiment, the illustrated bottom hull mold and top deck mold
include a fourth feature 6A used to form bond rails 6 for both the
top deck and hull/bottom deck on the fabricated watercraft (e.g.,
see FIG. 13). The bond rails 6 provide a means of mounting or
bonding the thermoform-fabricated top deck to the
thermoform-fabricated bottom hull/deck. In an example embodiment,
the bond rails 6 are produced with a unique curvature downward,
built into the hull (not an aftermarket add on) and providing the
rider with additional handling performance. In particular, the
downward curvature of the bond rails 6 act as a fin when the rider
leans into a turn. The enlarged curved bond rails 6 prevent the
watercraft from submerging on landings and washing the rider out of
the foot tray 3. Because of the precision manufacturing enabled by
the thermoforming process described herein, the top deck and bottom
hull can be fabricated with tight tolerances, allowing for a
sealable joint between the top and bottom deck. The bond rail 6 in
the nose/bow of the watercraft is configured to be flat and short.
This configuration allows for easy entry of the watercraft into the
water, when entering the water bow first. A longer bond rail in the
nose/bow of the watercraft would increase the shock/force when
entering the water.
[0043] FIG. 5 is a top view of a personal watercraft thermoforming
hood and covering component family mold. FIG. 6 is a perspective
view of a personal watercraft thermoforming hood and covering
component family mold. As shown in FIGS. 5 and 6, molds can be used
to fabricate a watercraft hood and covering component using the
thermoforming process described above. In an example embodiment,
the illustrated mold includes a first feature 7A used to form a
hood/engine covering 7 for the fabricated watercraft (e.g., see
FIGS. 11 and 12). The hood/engine covering 7 is produced by a
recessed feature 7A in the mold. On the exterior side of the
fabricated hood/engine covering 7, the hood/engine covering 7 is a
rounded, generally rectangular component. The hood/engine covering
7 provides a hood, which can be placed on top of the engine bay
opening 5 and mounted to the top deck. The hood/engine covering 7
prevents water from entering the watercraft engine bay.
[0044] Referring still to FIGS. 5 and 6 in the example embodiment,
the illustrated thermoforming hood and covering component family
mold includes a second feature 8A used to form a ride/pump plate
covering 8 (e.g., see FIGS. 11 and 12). The ride/pump plate
covering 8 is produced by generally rectangular, raised feature 8A
in the watercraft mold. On the exterior side of the fabricated
ride/pump plate covering 8, the ride/pump plate covering 8 is a
generally rectangular component. The ride/pump plate covering 8 is
produced to cover and protect the jet pump on the bottom deck/hull
of the watercraft.
[0045] As shown in FIGS. 1 through 6, thermoforming molds can be
provided to fabricate watercraft components using the thermoforming
process described above. The thermoforming process of the example
embodiments provides a fabrication method that produces durable and
precise components, is cost effective, and provides a green
alternative to conventional fiberglass manufacturing of personal
watercraft (PWC) hulls and components. The thermoforming process of
the example embodiments provides a green alternative; because, the
process uses zero VOC (volatile organic compound) emitting
materials, produces recyclable components, uses less manufacturing
steps, takes less time, and produces less waste.
[0046] FIG. 7 is a top view of the result of thermoform
manufacturing a bottom hull according to an example embodiment.
FIG. 8 is a perspective view of the result of thermoform
manufacturing a bottom hull according to an example embodiment. As
described above, the thermoformed bottom hull can be fabricated
using the mold described above with the integrated features
assimilated from the mold. By virtue of the thermoforming process,
the fabricated bottom hull is durable and precisely
manufactured.
[0047] FIG. 9 is a top view of the result of thermoform
manufacturing a top deck according to an example embodiment. FIG.
10 is a perspective view of the result of thermoform manufacturing
a top deck according to an example embodiment. As described above,
the thermoformed top deck can be fabricated using the mold
described above with the integrated features assimilated from the
mold.
[0048] FIG. 11 is a top view of the result of thermoform
manufacturing a hood and covering components according to an
example embodiment. FIG. 12 is a perspective view of the result of
thermoform manufacturing a hood and covering components according
to an example embodiment. As described above, the thermoformed hood
and covering components can be fabricated using the mold described
above with the integrated features assimilated from the mold.
[0049] FIG. 13 is a perspective view of the assembled hull, top
deck, and hood manufactured by the method of thermoform
manufacturing according to an example embodiment. FIG. 14 is a top
view of the assembled hull, top deck, and hood manufactured by the
method of thermoform manufacturing according to an example
embodiment. FIG. 15 is a side view of the assembled hull, top deck,
and hood manufactured by the method of thermoform manufacturing
according to an example embodiment. FIG. 16 is a bottom view of the
assembled hull, top deck, and hood manufactured by the method of
thermoform manufacturing according to an example embodiment.
[0050] Once each of the watercraft components is fabricated using
the thermoforming process described above, the components can be
assembled into a completed watercraft. The top deck can be coupled
to the bottom hull at the bond rails 6 as described above. A
conventional epoxy, acrylic, bonding agent, rivets, screws, or
other attachment mechanisms can be used to secure the top deck and
bottom hull components together. The hood and covering component
and the ride/pump plate covering can be similarly attached. As a
result, a complete watercraft assembly can be fabricated using the
thermoforming process as described herein.
[0051] Referring now to FIG. 17, a flow chart illustrates an
example embodiment of a method 900 as described herein. The method
900 of an example embodiment includes: producing a mold for a
component of a personal watercraft, the mold including features for
assimilation into the component (method block 902); inserting
thermoplastic material into a heater (method block 904); draping
the heated thermoplastic material over the mold (method block 906);
drawing the heated thermoplastic material into or over the mold
using a vacuum, the heated thermoplastic material assimilating the
features of the mold to produce the component (method block 908);
allowing the component to cool (method block 910); extracting the
component from the mold (method block 912); and trimming excess
material from the component (method block 914).
[0052] The Abstract of the Disclosure is provided to allow the
reader to quickly ascertain the nature of the technical disclosure.
It is submitted with the understanding that it will not be used to
interpret or limit the scope or meaning of the claims. In addition,
in the foregoing Detailed Description, it can be seen that various
features are grouped together in a single embodiment for the
purpose of streamlining the disclosure. This method of disclosure
is not to be interpreted as reflecting an intention that the
claimed embodiments require more features than are expressly
recited in each claim. Rather, as the following claims reflect,
inventive subject matter lies in less than all features of a single
disclosed embodiment. Thus, the following claims are hereby
incorporated into the Detailed Description, with each claim
standing on its own as a separate embodiment.
* * * * *