U.S. patent application number 16/302404 was filed with the patent office on 2019-09-12 for polyacetal resin composition and method for producing the same.
This patent application is currently assigned to MITSUBISHI GAS CHEMICAL COMPANY, INC.. The applicant listed for this patent is MITSUBISHI GAS CHEMICAL COMPANY, INC.. Invention is credited to Daisuke SUNAGA.
Application Number | 20190276659 16/302404 |
Document ID | / |
Family ID | 60325958 |
Filed Date | 2019-09-12 |
![](/patent/app/20190276659/US20190276659A1-20190912-P00001.png)
![](/patent/app/20190276659/US20190276659A1-20190912-P00002.png)
United States Patent
Application |
20190276659 |
Kind Code |
A1 |
SUNAGA; Daisuke |
September 12, 2019 |
POLYACETAL RESIN COMPOSITION AND METHOD FOR PRODUCING THE SAME
Abstract
The purpose of the present invention is to provide: a polyacetal
resin composition which is excellent in terms of impact resistance,
thermal stability, and releasability; and a process for producing
the polyacetal resin composition. The polyacetal resin composition
comprises 100 parts by mass of a polyacetal resin (A) in which the
molecular chain has neither a crosslink nor a branch therein,
0.01-10.0 parts by mass of an antioxidant (B), 0.01-5.0 parts by
mass of a nitrogenous compound (C), and 0.05-1.0 parts by mass of a
fatty acid amide (D), and has a melt index, as measured in
accordance with ISO 1133, of 0.5-1.5 g/10 min. A process for
producing the polyacetal resin compositions is also provided.
Inventors: |
SUNAGA; Daisuke; (Mie,
JP) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
MITSUBISHI GAS CHEMICAL COMPANY, INC. |
Tokyo |
|
JP |
|
|
Assignee: |
MITSUBISHI GAS CHEMICAL COMPANY,
INC.
Tokyo
JP
|
Family ID: |
60325958 |
Appl. No.: |
16/302404 |
Filed: |
May 19, 2017 |
PCT Filed: |
May 19, 2017 |
PCT NO: |
PCT/JP2017/018762 |
371 Date: |
November 16, 2018 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C08K 5/13 20130101; C08L
59/00 20130101; C08K 5/34922 20130101; C08L 59/00 20130101; C08L
59/00 20130101; C08K 5/134 20130101; C08L 59/00 20130101; C08K
5/3492 20130101; C08K 5/16 20130101; C08K 5/005 20130101; C08K 5/16
20130101; C08L 59/00 20130101; C08K 5/13 20130101; C08K 5/34922
20130101; C08K 5/20 20130101; C08K 5/005 20130101; C08L 59/00
20130101; C08K 5/20 20130101 |
International
Class: |
C08L 59/00 20060101
C08L059/00; C08K 5/00 20060101 C08K005/00; C08K 5/20 20060101
C08K005/20; C08K 5/134 20060101 C08K005/134; C08K 5/3492 20060101
C08K005/3492 |
Foreign Application Data
Date |
Code |
Application Number |
May 19, 2016 |
JP |
2016-100827 |
Claims
1. A polyacetal resin composition comprising 100 parts by mass of a
polyacetal resin (A) having a molecular chain with neither
crosslinks nor branches, 0.01 to 10.0 parts by mass of an
antioxidant (B), 0.01 to 5.0 parts by mass of a nitrogen-containing
compound (C) and 0.05 to 1.0 part by mass of a fatty acid amide
(D), wherein the polyacetal resin composition has a melt index of
0.5 to 1.5 g/10 minutes as measured in accordance with ISO
1133.
2. The polyacetal resin composition according to claim 1, which has
a Charpy impact value of not less than 10 kJ as measured in
accordance with ISO 194.
3. The polyacetal resin composition according to claim 1, wherein
the antioxidant (B) is a hindered phenol-based antioxidant.
4. The polyacetal resin composition according to claim 1, wherein
the antioxidant (B) is triethylene
glycol-bis-3-(3-t-butyl-4-hydroxy-5-methylphenyl) propionate.
5. The polyacetal resin composition according to claim 1, wherein
the nitrogen-containing compound (C) is an amino-substituted
triazine compound.
6. The polyacetal resin composition according to claim 1, wherein
the nitrogen-containing compound (C) is melamine.
7. The polyacetal resin composition according to claim 1, wherein
the fatty acid amide (D) is hexamethylenebisstearamide or
ethylenebisstearamide.
8. The polyacetal resin composition according to claim 1, wherein
the fatty acid amide (D) is ethylenebisstearamide.
9. A method for producing a polyacetal resin composition according
to claim 1, comprising melt kneading 100 parts by mass of a
polyacetal resin (A) having a molecular chain with neither
crosslinks nor branches, 0.01 to 10.0 parts by mass of an
antioxidant (B), 0.01 to 5.0 parts by mass of a nitrogen-containing
compound (C) and 0.05 to 1.0 part by mass of a fatty acid amide (D)
at a temperature controlled within the range of not less than
250.degree. C. and not more than 270.degree. C.
10. The production method according to claim 9, wherein the melt
kneading is performed for not less than 1 minute and not more than
5 minutes.
11. A molded body comprising the polyacetal resin composition
according to claim 1.
12. A part, which is a cut molded body according to claim 11.
13. The polyacetal resin composition according to claim 2, wherein
the antioxidant (B) is a hindered phenol-based antioxidant.
14. The polyacetal resin composition according to claim 2, wherein
the antioxidant (B) is triethylene
glycol-bis-3-(3-t-butyl-4-hydroxy-5-methylphenyl) propionate.
15. The polyacetal resin composition according to claim 2, wherein
the nitrogen-containing compound (C) is an amino-substituted
triazine compound.
16. The polyacetal resin composition according to claim 2, wherein
the nitrogen-containing compound (C) is melamine.
17. The polyacetal resin composition according to claim 2, wherein
the fatty acid amide (D) is hexamethylenebisstearamide or
ethylenebisstearamide.
18. The polyacetal resin composition according to claim 2, wherein
the fatty acid amide (D) is ethylenebisstearamide.
19. A molded body comprising the polyacetal resin composition
according to claim 2.
20. The polyacetal resin composition according to claim 3, wherein
the antioxidant (B) is triethylene
glycol-bis-3-(3-t-butyl-4-hydroxy-5-methylphenyl) propionate.
Description
TECHNICAL FIELD
[0001] The present invention relates to a polyacetal resin
composition and a method for producing such compositions.
BACKGROUND ART
[0002] Polyacetal resins, which have well-balanced properties such
as mechanical properties, thermal properties, electrical
properties, sliding properties and molding properties, are used
widely as structural materials and mechanism parts such as
electrical devices, automobile parts and precision machine parts.
One of the performances often required in these applications is an
improvement in toughness indicated by impact resistance or tensile
elongation. Further, polyacetal resins are easy to mold and are
therefore used in the production of complex-shaped molded articles
by, for example, injection molding. Thus, enhanced thermal
stability and releasability in the molding process are sometimes
required.
[0003] A known approach to improving toughness is to add
thermoplastic polyurethanes or elastomers to polyacetal resins. On
the other hand, techniques have been reported which impart high
toughness to polyacetal resins without use of modifiers such as
elastomers. Specifically, a molding material has been reported
which includes a linear polyoxymethylene copolymer and a
conventional additive and has a melt flow index (MFI, 190.degree.
C., 2.16 kg load) of not more than 0.8 g/10 minutes (see, for
example, Patent Literature 1). It has been also reported that a
polyoxymethylene copolymer resin which has a melt flow index of 0.1
to 2.0 g/10 minutes and has a substantially linear molecular
structure, or a composition of such a resin, exhibits an enhanced
melt tension, and an extrusion molded article obtained using such a
material attains excellent mechanical properties and cutting
processability (see, for example, Patent Literature 2). Further, a
polyacetal molded body for cutting processing that exhibits
outstanding machinability has been reported, wherein the polyacetal
molded body is obtained by molding a polyacetal resin composition
including 100 parts by weight of a polyacetal copolymer obtained by
polymerizing trioxane with 0.1 to 10 wt % of cyclic ether and/or
cyclic formal as a comonomer and 0.1 to 3 wt % of diglycidyl
compound, 0.01 to 5 parts by weight of one, or two or more kinds of
compounds selected from nitrogen-containing compounds, fatty acid
ester compounds and metal-containing compounds, and 0.01 to 5.0
parts by weight of a hindered phenol-based compound, wherein the
polyacetal resin composition has a melt index of 0.01 to 5.0 g/10
minutes (see, for example Patent Literature 3).
CITATION LIST
Patent Literature
[0004] Patent Literature 1: Japanese Patent Application Kokai
Publication No. H6-199972
[0005] Patent Literature 2: Japanese Patent Application Kokai
Publication No. H5-301271
[0006] Patent Literature 3: Japanese Patent Application Kokai
Publication No. H5-156118
SUMMARY OF INVENTION
Technical Problem
[0007] Patent Literatures 1 and 2 disclose that the impact
resistance or melt tension of the polyacetal resins is enhanced,
but are silent with respect to thermal stability or releasability.
Reproduction of the polymerization of trioxane and dioxolane in the
presence of tungstophosphoric acid in accordance with Examples of
Patent Literature 1 resulted in a polyacetal resin which showed
significantly poor thermal stability. Patent Literature 3 discloses
that the polyacetal resin composition has excellent machinability
and keeps excellent properties such as mechanical strength and
toughness in a well-balanced manner, but this literature does not
mention thermal stability or releasability. The composition of
Patent Literature 3 has been found to have low toughness indicated
by Charpy impact value due to the fact that it includes a
polyacetal resin with a crosslinked structure. Further, it has been
found that the use of a fatty acid ester in a polyacetal resin
composition leads to easy occurrence of slippage in the extrusion
step, and the use of a metal-containing compound such as calcium
stearate causes significant yellowing and a decrease in thermal
stability. As discussed above, the conventional techniques do not
explicitly describe an approach to improving releasability, and
thus there is need of further improvements for the injection
molding applications. Further, the conventional techniques are not
satisfactory in terms of thermal stability required for injection
molding.
[0008] It is therefore an object of the invention to provide a
polyacetal resin composition having excellent impact resistance,
thermal stability and releasability, and a method for producing
such compositions.
Solution to Problem
[0009] The present inventors have conducted extensive studies
directed to achieving the above object, and have found that
outstanding impact resistance, thermal stability and releasability
are attained by a polyacetal resin composition which includes a
polyacetal resin (A) having a molecular chain with neither
crosslinks nor branches, an antioxidant (B), a nitrogen-containing
compound (C) and a fatty acid amide (D) and which has a melt index
in the specific range as measured in accordance with ISO 1133. The
present invention has been completed based on the finding.
[0010] Aspects of the present invention reside in the
following.
[0011] [1] A polyacetal resin composition comprising 100 parts by
mass of a polyacetal resin (A) having a molecular chain with
neither crosslinks nor branches, 0.01 to 10.0 parts by mass of an
antioxidant (B), 0.01 to 5.0 parts by mass of a nitrogen-containing
compound (C) and 0.05 to 1.0 part by mass of a fatty acid amide
(D), wherein the polyacetal resin composition has a melt index of
0.5 to 1.5 g/10 minutes as measured in accordance with ISO
1133.
[0012] [2] The polyacetal resin composition according to [1], which
has a Charpy impact value of not less than 10 kJ as measured in
accordance with ISO 194.
[0013] [3] The polyacetal resin composition according to [1] or
[2], wherein the antioxidant (B) is a hindered phenol-based
antioxidant.
[0014] [4] The polyacetal resin composition according to any one of
[1] to [3], wherein the antioxidant (B) is triethylene
glycol-bis-3-(3-t-butyl-4-hydroxy-5-methylphenyl) propionate.
[0015] [5] The polyacetal resin composition according to any one of
[1] to [4], wherein the nitrogen-containing compound (C) is an
amino-substituted triazine compound.
[0016] [6] The polyacetal resin composition according to any one of
[1] to [5], wherein the nitrogen-containing compound (C) is
melamine.
[0017] [7] The polyacetal resin composition according to any one of
[1] to [6], wherein the fatty acid amide (D) is
hexamethylenebisstearamide or ethylenebisstearamide.
[0018] [8] The polyacetal resin composition according to any one of
[1] to [6], wherein the fatty acid amide (D) is
ethylenebisstearamide.
[0019] [9] A method for producing a polyacetal resin composition
according to [1], comprising melt kneading 100 parts by mass of a
polyacetal resin (A) having a molecular chain with neither
crosslinks nor branches, 0.01 to 10.0 parts by mass of an
antioxidant (B), 0.01 to 5.0 parts by mass of a nitrogen-containing
compound (C) and 0.05 to 1.0 part by mass of a fatty acid amide (D)
at a temperature controlled within the range of not less than
250.degree. C. and not more than 270.degree. C.
[0020] [10] The production method according to [9], wherein the
melt kneading is performed for not less than 1 minute and not more
than 5 minutes.
[0021] [11] A molded body comprising the polyacetal resin
composition according to any one of [1] to [8].
[0022] [12] A part, which is a cut molded body according to
[11].
Advantageous Effects of Invention
[0023] The polyacetal resin compositions of the present invention
have outstanding impact resistance and thus can be used widely as
structural materials and mechanism parts such as electrical
devices, automobile parts and precision machine parts. Further, the
polyacetal resin compositions of the invention have excellent
thermal stability and releasability and thus can be suitably used
not only for extrusion molding but also for injection molding.
DESCRIPTION OF EMBODIMENTS
[0024] The present invention will be described hereinbelow.
Polyacetal Resins (A)
[0025] The polyacetal resin (A) of the invention is a polymer
having an acetal structure: --O--CRH-- (wherein R is a hydrogen
atom or an organic group) as a repeating unit. The polymer usually
has an acetal structure in which R is a hydrogen atom, that is, an
oxymethylene group (--OCH.sub.2--) as the main structural unit. The
polyacetal resin (A) used in the invention may be a copolymer (a
block copolymer), a terpolymer or the like which contains one or
more kinds of repeating structural units other than the
oxymethylene groups, but the polyacetal resin (A) has a molecular
chain with neither crosslinks nor branches. Here, the phrase "have
a molecular chain with neither crosslinks nor branches" means that
the resin has no structural units derived from a monomer capable of
forming branches or crosslinks such as, for example, a glycidyl
ether compound. That is, the polyacetal resin (A) of the invention
is substantially linear. Examples of the structural units other
than the oxymethylene groups include C.sub.2-10 optionally branched
oxyalkylene groups such as oxyethylene groups
(--OCH.sub.2CH.sub.2-- or --OCH(CH.sub.3)--), oxypropylene groups
(--OCH.sub.2CH.sub.2CH.sub.2--, --OCH(CH.sub.3)CH.sub.2-- or
--OCH.sub.2CH(CH.sub.3)--), and oxybutylene groups
(--OCH.sub.2CH.sub.2CH.sub.2CH.sub.2--,
--OCH(CH.sub.3)CH.sub.2CH.sub.2--,
--OCH.sub.2CH(CH.sub.3)CH.sub.2--,
--OCH.sub.2CH.sub.2CH(CH.sub.3)--, --OCH(C.sub.2H.sub.5)CH.sub.2--
or --OCH.sub.2CH(C.sub.2H.sub.5)--). In particular, C.sub.2-4
optionally branched oxyalkylene groups are preferable, and the
oxyethylene group (--OCH.sub.2CH.sub.2--) is particularly
preferable. The content of the structural units other than the
oxymethylene groups (for example, the oxyalkylene groups) is not
particularly limited, but is preferably not less than 0.1 mass % in
the polyacetal resin, more preferably not more than 25.0 mass %,
and still more preferably not less than 0.5 mass % and not more
than 20.0 mass %.
[0026] The polyacetal resin (A) of the invention may be produced by
any conventional and known method appropriately without limitation.
For example, a polyacetal resin (A) having an oxymethylene group
and a C.sub.2-4 oxyalkylene group as structural units may be
produced by copolymerizing a cyclic acetal of oxymethylene groups
such as formaldehyde trimer (trioxane) or tetramer (tetraoxane)
with a cyclic acetal containing a C.sub.2-4 oxyalkylene group such
as ethylene oxide, 1,3-dioxolane, 1,3,6-trioxocane or
1,3-dioxepane. In particular, the polyacetal resin (A) used in the
invention is preferably a copolymer of a cyclic acetal such as
trioxane or tetraoxane with ethylene oxide or 1,3-dioxolane. A
copolymer of trioxane and 1,3-dioxolane is particularly
preferable.
[0027] For example, the polyacetal resin (A) of the invention may
be obtained by the bulk polymerization of a cyclic acetal of
oxymethylene groups with a cyclic acetal containing a C.sub.2-4
oxyalkylene group as a comonomer in the presence of a
polymerization catalyst. To deactivate the polymerization catalyst
and the polymerization growth ends, a reaction terminator may be
used as required. A molecular weight modifier may be used as
required in order to control the molecular weight of the polyacetal
resin (A). The types and amounts of the polymerization catalyst,
reaction terminator and molecular weight modifier which may be used
in the production of the polyacetal resin (A) of the invention are
not particularly limited as long as the advantageous effects of the
invention are not impaired. Any known polymerization catalysts,
reaction terminators and molecular weight modifiers may be used
appropriately.
[0028] Examples of the polymerization catalysts include, although
not particularly limited thereto, Lewis acids such as boron
trifluoride, tin tetrachloride, titanium tetrachloride, phosphorus
pentachloride, phosphorus pentafluoride, arsenic pentafluoride and
antimony pentafluoride, as well as complex compounds or salt
compounds of these Lewis acids. Examples further include protonic
acids such as trifluoromethanesulfonic acid and perchloric acid;
esters of protonic acids such as esters of trifluoromethanesulfonic
acid or perchloric acid with a lower aliphatic alcohol; and
anhydrides of protonic acids such as mixed anhydrides of
trifluoromethanesulfonic acid or perchloric acid with other lower
aliphatic carboxylic acid. Examples further include triethyloxonium
hexafluorophosphate, triphenylmethyl hexafluoroarsenate and acetyl
hexafluoroborate. In particular, compounds including boron
trifluoride are preferable, and boron trifluoride diethyl etherate
and boron trifluoride dibutyl etherate which are coordination
complexes with ethers are particularly preferable.
[0029] The polymerization catalyst may be used in any amount
without limitation. The amount is usually 1.0.times.10.sup.-8 to
2.0.times.10.sup.-3 mol per 1 mol of the total of the cyclic acetal
of oxymethylene groups and comonomers, and is preferably in the
range of 5.0.times.10.sup.-8 to 8.0.times.10.sup.-4 mol, and
particularly preferably in the range of 5.0.times.10.sup.-8 to
1.0.times.10.sup.-4 mol.
[0030] Examples of the reaction terminators include, although not
particularly limited thereto, trivalent organic phosphorus
compounds, amine compounds, and alkali metal or alkaline earth
metal hydroxides. The reaction terminators may be used singly, or
two or more may be used in combination. In particular, trivalent
organic phosphorus compounds, tertiary amines and hindered amines
are preferable.
[0031] The reaction terminator may be used in any amount without
limitation as long as the amount is sufficient to deactivate the
polymerization catalyst. The amount is usually in the range of
1.0.times.10.sup.-1 to 1.0.times.10.sup.1 in molar ratio relative
to the polymerization catalyst.
[0032] Examples of the molecular weight modifiers include, although
not particularly limited thereto, methylal, methoxymethylal,
dimethoxymethylal, trimethoxymethylal and oxymethylene di-n-butyl
ether, with methylal being particularly preferable. The amount in
which the molecular weight modifier is used is determined
appropriately in accordance with the target molecular weight.
Usually, the amount is controlled in the range of 0 to 0.1 mass %
relative to all the monomers.
[0033] The polyacetal resin (A) of the invention preferably has a
melt index (MI, 190.degree. C., 2.16 kg load) of 0.5 to 1.5 g/10
minutes as measured in accordance with ISO 1133.
[0034] Antioxidants (B)
[0035] The antioxidant (B) added to the polyacetal resin
composition of the invention is not particularly limited as long as
it has an antioxidant action on the polyacetal resin. Examples
thereof include phenol-based antioxidants and phosphorus-based
antioxidants. Of these, phenol-based antioxidants are preferable,
and hindered phenol-based antioxidants are particularly preferable.
The antioxidants may be used singly, or two or more may be used in
combination.
[0036] The hindered phenol-based antioxidants are not particularly
limited as long as they are the hindered phenol compounds which
have an antioxidant action on the polyacetal resins. Examples
thereof include 2,2'-methylene-bis(4-methyl-6-t-butylphenol),
4,4'-methylene-bis(2,6-di-t-butylphenol),
1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene,
3,5-di-t-butyl-4-hydroxybenzyldimethylamine,
distearyl-3,5-di-t-butyl-4-hydroxybenzyl phosphonate,
diethyl-3,5-di-t-butyl-4-hydroxybenzyl phosphonate,
2,6,7-trioxa-1-phospha-bicyclo[2.2.2]oct-4-yl-methyl-3,5-di-t-butyl-4-hyd-
roxyhydrocinnamate,
3,5-di-t-butyl-4-hydroxyphenyl-3,5-distearyl-thiotriazylamine,
2-(2-hydroxy-3,5-di-t-butylphenyl)-5-chlorobenzotriazole,
2,6-di-t-butyl-4-hydroxymethylphenol,
2,4-bis-(n-octylthio)-6-(4-hydroxy-3,5-di-t-butylanilino)-1,3,5-triazine,
N,N'-hexamethylenebis(3,5-di-t-butyl-4-hydroxy-hydrocinnamamide),
octadecyl-3-(3,5-di-t-butyl-4-hydroxyphenyl) propionate,
1,6-hexanediol-bis[3-(3,5-di-t-butyl-4-hydroxyphenyl) propionate],
pentaerythritol-tetrakis[3-(3,5-di-t-butyl-4-hydroxyphenyl)
propionate], triethylene
glycol-bis[3-(3,5-dimethyl-4-hydroxyphenyl) propionate],
triethylene glycol-bis[3-(3-t-butyl-5-methyl-4-hydroxyphenyl)
propionate], triethylene
glycol-bis[3-(3,5-di-t-butyl-4-hydroxyphenyl) propionate], and
2,2'-thiodiethyl-bis[3-(3,5-di-t-butyl-4-hydroxyphenyl)
propionate]. The hindered phenol compounds may be used singly, or
two or more may be used in combination.
[0037] Of these,
1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene,
pentaerythritol-tetrakis[3-(3,5-di-t-butyl-4-hydroxyphenyl)
propionate], and triethylene
glycol-bis[3-(3-t-butyl-5-methyl-4-hydroxyphenyl) propionate] are
preferable, and triethylene
glycol-bis[3-(3-t-butyl-5-methyl-4-hydroxyphenyl) propionate] is
particularly preferable.
[0038] The ratio of the antioxidant (B) is 0.01 to 10.0 parts by
mass relative to 100 parts by mass of the polyacetal resin (A), and
is preferably 0.05 to 5.0 parts by mass, and particularly
preferably 0.1 to 1.0 part by mass. When the ratio of the
antioxidant (B) is 0.01 part by mass or above, the desired thermal
stability is obtained.
[0039] Nitrogen-Containing Compounds (C)
[0040] Examples of the nitrogen-containing compounds (C) added to
the polyacetal resin composition of the invention include, although
not particularly limited thereto, polyamide resins, dicarboxylic
acid hydrazides and amino-substituted triazine compounds. Of these,
amino-substituted triazine compounds are preferable. The
nitrogen-containing compounds may be used singly, or two or more
may be used in combination.
[0041] Examples of the amino-substituted triazine compounds
include, although not particularly limited thereto, guanamine,
melamine, N-butylmelamine, N-phenylmelamine, N,N-diphenylmelamine,
N,N-diallylmelamine, N,N',N''-triphenylmelamine, methylolmelamines
such as N,N',N''-trimethylolmelamine, alkylated melamines such as
hexamethoxymethylmelamine, benzoguanamine,
2,4-diamino-6-methyl-sym-triazine,
2,4-diamino-6-butyl-sym-triazine,
2,4-diamino-6-benzyloxy-sym-triazine,
2,4-diamino-6-butoxy-sym-triazine,
2,4-diamino-6-cyclohexyl-sym-triazine,
2,4-diamino-6-chloro-sym-triazine,
2,4-diamino-6-mercapto-sym-triazine, and ammeline
(4,6-diamino-2-hydroxy-1,3,5-triazine). Of these, melamine,
methylolmelamine, alkylated melamines and benzoguanamine are
preferable, and melamine is particularly preferable.
[0042] The ratio of the nitrogen-containing compound (C) is 0.01 to
5.0 parts by mass relative to 100 parts by mass of the polyacetal
resin (A), and is preferably 0.03 to 3.0 parts by mass, and
particularly preferably 0.05 to 1.0 part by mass. When the ratio of
the nitrogen-containing compound (C) is in the above range, the
desired thermal stability is obtained, and the polyacetal resin
composition attains a low melt index (MI) and good impact
resistance (a Charpy impact value). Further, good tensile
elongation at break is obtained.
[0043] Fatty Acid Amides (D)
[0044] Examples of the fatty acid amides (D) added to the
polyacetal resin composition of the invention include, although not
particularly limited thereto, saturated fatty acid amides,
unsaturated fatty acid amides, saturated fatty acid bisamides and
unsaturated fatty acid bisamides. Of these, saturated fatty acid
bisamides are preferable. The fatty acid amides may be used singly,
or two or more may be used in combination.
[0045] The saturated fatty acid amides or unsaturated fatty acid
amides are, for example, amides of saturated or unsaturated fatty
acids having 10 to 22 carbon atoms, such as lauramide, palmitamide,
stearamide, oleamide and erucamide. The saturated fatty acid
bisamides or unsaturated fatty acid bisamides are, for example,
reaction products of a C.sub.1-6 alkylene diamine with a
C.sub.10-22 saturated or unsaturated fatty acid, such as
ethylenebiscapramide, ethylenebislauramide, ethylenebisstearamide,
ethylenebishydroxystearamide, ethylenebisbehenamide,
hexamethylenebisstearamide, hexamethylenebisbehenamide,
hexamethylenebishydroxystearamide, ethylenebisoleamide,
ethylenebiserucamide and hexamethylenebisoleamide. Of these,
reaction products of a C.sub.2-6 alkylene diamine with a
C.sub.10-22 saturated fatty acid are preferable,
hexamethylenebisstearamide and ethylenebisstearamide are more
preferable, and ethylenebisstearamide is particularly
preferable.
[0046] The ratio of the fatty acid amide (D) is 0.05 to 1.0 part by
mass relative to 100 parts by mass of the polyacetal resin (A), and
is preferably 0.05 to 0.5 part by mass, and particularly preferably
0.1 to 0.5 part by mass. When the ratio of the fatty acid amide (D)
is 0.05 part by mass or above, the desired releasability is
obtained. When the ratio of the fatty acid amide (D) is 1.0 part by
mass or less, the polyacetal resin composition attains good impact
resistance.
[0047] Additional Components
[0048] Where necessary, the polyacetal resin composition of the
invention may appropriately contain, in addition to the components
described hereinabove, additional components such as a variety of
additives including stabilizers, nucleating agents, fillers,
pigments, lubricants, plasticizers, antistatic agents, UV
absorbers, flame retardants and auxiliary flame retardants, other
resins and elastomers while still achieving the advantageous
effects of the invention.
[0049] <Methods for Producing Polyacetal Resin
Compositions>
[0050] A method for producing a polyacetal resin composition of the
present invention comprises melt kneading 100 parts by mass of a
polyacetal resin (A) having a molecular chain with neither
crosslinks nor branches, 0.01 to 10.0 parts by mass of an
antioxidant (B), 0.01 to 5.0 parts by mass of a nitrogen-containing
compound (C) and 0.05 to 1.0 part by mass of a fatty acid amide (D)
at a temperature controlled within the range of not less than
250.degree. C. and not more than 270.degree. C. The polyacetal
resin (A), the antioxidant (B), the nitrogen-containing compound
(C) and the fatty acid amide (D) are as described hereinabove. In
the production of the polyacetal resin composition, where
necessary, the composition may contain the aforementioned
additional components in addition to the polyacetal resin (A)
having a molecular chain with neither crosslinks nor branches, the
antioxidant (B), the nitrogen-containing compound (C) and the fatty
acid amide (D).
[0051] The polyacetal resin composition of the invention may be
produced by mixing the polyacetal resin (A) having a molecular
chain with neither crosslinks nor branches, the antioxidant (B),
the nitrogen-containing compound (C), the fatty acid amide (D) and
optionally the additional components in any order, and melt
kneading the mixture.
[0052] The apparatuses used in the production of the polyacetal
resin compositions are not particularly limited, and mixers,
kneaders and the like which are conventionally used for the
production of resin compositions of this class, may be used.
[0053] The melt kneading is performed while controlling the
temperature of the polyacetal resin composition inside the kneader
within the range of not less than 250.degree. C. and not more than
270.degree. C. More specifically, the melt kneading is particularly
preferably performed while controlling the temperature of the
apparatus (for example, the jacket temperature) or kneading
conditions (for example, the rotational speed of the screw) so that
the resin temperature at the exit of the kneader is within the
range of not less than 250.degree. C. and not more than 270.degree.
C. By controlling the temperature of the polyacetal resin
composition inside the kneader in the above range, the melt index
of the resultant polyacetal resin composition is brought to the
range of 0.5 to 1.5 g/10 minutes as measured in accordance with ISO
1133, and the composition tends to attain excellent impact
resistance and also tends to show excellent thermal stability. The
melt kneading is preferably performed for not less than 1 minute
and not more than 5 minutes. Controlling the melt kneading time in
this range brings the melt index of the resultant polyacetal resin
composition to the range of 0.5 to 1.5 g/10 minutes as measured in
accordance with ISO 1133, and the composition tends to attain
excellent impact resistance. In general, the melt kneading of a
polyacetal resin composition is carried out at a jacket temperature
of 200.degree. C. to 250.degree. C. In this case, the temperature
of the polyacetal resin composition inside the kneader becomes far
higher than the jacket temperature due to the friction within the
molten polyacetal resin composition. In some cases, the temperature
of the resin composition (for example, the resin temperature at the
exit) exceeds 270.degree. C.
[0054] Specifically, the polyacetal resin composition is produced,
for example, in such a manner that predetermined amounts of the
antioxidant (B), the nitrogen-containing compound (C) and the fatty
acid amide (D) are added simultaneously or in any order to the
polyacetal resin (A) having a molecular chain with neither
crosslinks nor branches, the addition being optionally accompanied
by the addition of the additional components, and all the
components are mixed together with a device such as a tumbler-type
blender. Next, the obtained mixture can be melt kneaded in a
twin-screw extruder equipped with a devolatilizing vent so that the
temperature of the polyacetal resin composition inside the kneader
is within the range of not less than 250.degree. C. and not more
than 270.degree. C., and the melt can be extruded into a form of a
strand, which is then pelletized to give the polyacetal resin
composition having the desired formulation.
[0055] Polyacetal Resin Compositions and Molded Bodies
[0056] The polyacetal resin composition of the invention obtained
as described above has a melt index (MI, 190.degree. C., 2.16 kg
load) in the range of 0.5 to 1.5 g/10 minutes as measured in
accordance with ISO 1133. This range of melt index ensures that the
resin composition exhibits excellent impact resistance (a Charpy
impact value). The polyacetal resin composition of the invention
preferably has a Charpy impact value of not less than 10 kJ as
measured in accordance with ISO 194. When the Charpy impact value
is 10 kJ or above, the polyacetal resin composition may be suitably
used for impact resistant parts such as gear parts subjected to
high torque.
[0057] The polyacetal resin composition of the invention may be
molded in accordance with known polyacetal resin molding methods.
For example, the resin composition melt kneaded in an extruder may
be directly molded, without being pelletized, into an injection
molded article, a blow molded article, an extrusion molded article
or the like. Examples of the molded bodies made of the polyacetal
resin composition of the invention include, but are not limited to,
pellets, round bars, thick plates, sheets, tubes, and cylindrical
or tetragonal containers. The molded bodies of the invention may be
used in applications where polyacetal resin compositions have been
conventionally used, such as various parts of machinery, electrical
devices, automobiles, construction materials and the like. The
molded bodies may be further worked, for example, cut into
industrial parts for use in various fields, in particular,
high-grade parts requiring reliability such as electrical or
electronical parts and automobile parts.
EXAMPLES
[0058] Hereinbelow, embodiments and advantageous effects of the
present invention will be described in detail by presenting
Examples and Comparative Examples. However, it should not be
construed that the scope of the present invention is limited to
such Examples.
[0059] Polyacetal resin compositions obtained in Examples and
Comparative Examples were evaluated by the following methods.
Melt Index (MI)
[0060] The measurement was performed at 190.degree. C. and 2.16 kg
load in accordance with ISO 1133.
[0061] Tensile Elongation at Break
[0062] Test piece molding: Pellets of a polyacetal resin
composition obtained in an Example or a Comparative Example were
predried at 80.degree. C. for 3 hours, and were thereafter molded
into a test piece in accordance with the procedures described in
ISO 294-1. The molded test piece was conditioned in a chamber at a
temperature of 23.+-.2.degree. C. and a relative humidity of
50.+-.5% for at least 48 hours, and was thereafter subjected to a
tensile test.
[0063] Tensile characteristics test: The tensile elongation at
break (the distance between gauge lines) was measured in accordance
with the procedures described in ISO 527-1 and ISO 527-2 at a
measurement temperature of 23.degree. C., an initial distance
between the gauge lines of 50 mm and a tension rate of 50
mm/minute.
[0064] The larger the value of tensile elongation at break, the
higher the toughness.
[0065] Charpy Impact Value
[0066] Each of polyacetal resin compositions obtained in Examples
and Comparative Examples was molded into a dumbbell-shaped molded
piece in accordance with ISO 527 with an injection molding machine
having a mold clamping force of 90 tons. The molded piece obtained
was worked in accordance with ISO 194 and tested for a Charpy
impact value.
[0067] Residence Thermal Stability
[0068] A polyacetal resin composition obtained in an Example or a
Comparative Example was molded into a 75.times.50.times.5 mm
plate-shaped molded piece with an injection molding machine having
a mold clamping force of 70 tons. During this process, the
composition was retained in a cylinder set at 200.degree. C. and
was molded every 12 minutes. The residence time (minutes) when the
occurrence of silver streaks (a phenomenon that gas outflow marks
is observed in a radial appearance on the surface of the molded
piece) was first observed on the surface of the molded piece, was
measured.
[0069] Releasability Evaluation: Mold Release Resistance
[0070] Releasability was evaluated in the following manner.
Containers in the form of a 30.times.50.times.30 mm box having a
central rib (box-shaped molded containers) were continuously molded
automatically with an injection molding machine PS40 manufactured
by NISSEI PLASTIC INDUSTRIAL CO., LTD. The pressure applied to the
ejector pin in demolding the box-shaped molded container was
measured with a pin-type pressure sensor. The composition was
continuously molded in 30 shots. The average of the values of
pressure applied to the ejector pin in the 11th to 30th shots was
obtained as the mold release resistance (unit: MPa) of each sample
of Examples and Comparative Examples.
[0071] Polyacetal resins used in Examples and Comparative Examples
were produced as described below.
Production of Polyacetal Resin (A-1)
[0072] A polyacetal resin (A-1) used in Examples and Comparative
Examples was produced as follows. A twin-screw continuous
polymerizer that had been equipped with a jacket set at 65.degree.
C. and a self-cleaning paddle was continuously supplied with 100
parts by mass of trioxane, 4 parts by mass of 1,3-dioxolane and a
benzene solution containing 0.025 mmol of boron trifluoride diethyl
etherate as a polymerization catalyst per 1 mol of all the monomers
(trioxane and 1,3-dioxolane). The polymerization was performed
continuously so that the residence time for the raw materials in
the polymerizer would be 20 minutes.
[0073] To the obtained polymerization reaction product was added a
benzene solution containing triphenylphosphine in a molar amount
two times that of boron trifluoride diethyl etherate used as a
polymerization catalyst. After the polymerization catalyst had been
deactivated, the polymer was triturated. A polyacetal resin (A-1)
was thus obtained. The yield of the polyacetal resin (A-1) was 95%,
and the melt index (MI) was 0.6 g/10 minutes.
[0074] Production of Polyacetal Resin (A-2)
[0075] A polyacetal resin (A-2) used in Comparative Examples was
produced as follows. A twin-screw continuous polymerizer that had
been equipped with a jacket set at 65.degree. C. and a
self-cleaning paddle was continuously supplied with 100 parts by
mass of trioxane, 4 parts by mass of 1,3-dioxolane and a benzene
solution containing 0.030 mmol of boron trifluoride diethyl
etherate as a polymerization catalyst per 1 mol of all the monomers
(trioxane and 1,3-dioxolane). The polymerization was performed
continuously so that the residence time for the raw materials in
the polymerizer would be 20 minutes.
[0076] To the obtained polymerization reaction product was added a
benzene solution containing triphenylphosphine in a molar amount
two times that of boron trifluoride diethyl etherate used as a
polymerization catalyst. After the polymerization catalyst had been
deactivated, the polymer was triturated. A polyacetal resin (A-2)
was thus obtained. The yield of the polyacetal resin (A-2) was 95%,
and the melt index (MI) was 2.5 g/10 minutes.
[0077] Production of Polyacetal Resin (A-3)
[0078] A polyacetal resin (A-3) used in Comparative Examples was
produced as follows. A twin-screw continuous polymerizer that had
been equipped with a jacket set at 65.degree. C. and a
self-cleaning paddle was continuously supplied with 100 parts by
mass of trioxane, 4 parts by mass of 1,3-dioxolane, 0.7 part by
mass of 1,4-butanediol diglycidyl ether, and a benzene solution
containing 0.025 mmol of boron trifluoride diethyl etherate as a
polymerization catalyst per 1 mol of all the monomers (trioxane,
1,3-dioxolane, and 1,4-butanediol diglycidyl ether). The
polymerization was performed continuously so that the residence
time for the raw materials in the polymerizer would be 20
minutes.
[0079] To the obtained polymerization reaction product was added a
benzene solution containing triphenylphosphine in a molar amount
two times that of boron trifluoride diethyl etherate used as a
polymerization catalyst. After the polymerization catalyst had been
deactivated, the polymer was triturated. A polyacetal resin (A-3)
was thus obtained. The yield of the polyacetal resin (A-3) was 95%,
and the melt index (MI) was 0.6 g/10 minutes.
[0080] Other components used in polyacetal resin compositions of
Examples and Comparative Examples are described below.
Antioxidant (B)
[0081] Triethylene
glycol-bis-3-(3-t-butyl-4-hydroxy-5-methylphenyl) propionate
(Irganox (registered trademark) 245 manufactured by BASF
Corporation)
Nitrogen-Containing Compound (C)
[0082] Melamine (manufactured by Mitsui Chemicals, Inc.)
Fatty Acid Amide (D-1)
[0083] Ethylenebisstearamide (manufactured by Kao Corporation)
Fatty Acid Amide (D-2)
[0084] Hexamethylenebisstearamide (manufactured by CHEMICAL LAND
21)
<Fatty Acid Metal Salt (E)>
[0085] Calcium stearate (CALCIUM STEARATE S manufactured by NOF
CORPORATION)
[0086] Polyacetal resin compositions of Examples and Comparative
Examples were produced as described below.
Example 1
[0087] A polyacetal resin composition of Example 1 was obtained as
follows. To 100 parts by mass of the polyacetal resin (A-1)
obtained by the aforementioned method were added 0.3 part by mass
of Irganox (registered trademark) 245, 0.1 part by mass of melamine
and 0.15 part by mass of ethylenebisstearamide. The mixture was
continuously extruded from a twin-screw extruder while performing
devolatilization under a cylinder temperature of 200.degree. C. and
a reduced pressure of 21.3 kPa. Pellets of a polyacetal resin
composition were thus obtained. The resin temperature was actually
measured at the extruder die exit using a thermocouple thermometer,
and was controlled by manipulating the rotational speed of the
extruder screw. The residence time for the resin composition was 3
minutes.
[0088] The obtained pellets were subjected to the measurements of
tensile elongation at break, Charpy impact value, residence thermal
stability and mold release resistance by the aforementioned
methods. The results are described in Table 1.
Examples 2 to 7, and Comparative Examples 1 and 4 to 7
[0089] With a formulation and a resin temperature at the extruder
exit described in Table 1, the antioxidant (B), the
nitrogen-containing compound (C), and the fatty acid amide (D-1) or
(D-2) were added to the polyacetal resin (A-1), (A-2) or (A-3)
obtained by the aforementioned method, and the mixture was
continuously extruded from a twin-screw extruder while performing
devolatilization under a cylinder temperature of 200.degree. C. and
a reduced pressure of 21.3 kPa. Pellets of a polyacetal resin
composition were thus obtained, respectively. The resin temperature
was actually measured at the extruder die exit using a thermocouple
thermometer, and was controlled by manipulating the rotational
speed of the extruder screw. The residence time for the resin
composition was 3 minutes.
[0090] The obtained pellets were subjected to the measurements of
tensile elongation at break, Charpy impact value, residence thermal
stability and mold release resistance by the aforementioned
methods. The results are described in Table 1.
Comparative Example 2
[0091] Pellets of a polyacetal resin composition were obtained in
the same manner as in Example 1, except that the fatty acid amide
(D) was replaced by calcium stearate as the fatty acid metal salt
(E). The resin temperature was actually measured at the extruder
die exit using a thermocouple thermometer, and was controlled by
manipulating the rotational speed of the extruder screw. The
residence time for the resin composition was 3 minutes. The
obtained pellets were subjected to the measurements of tensile
elongation at break, Charpy impact value, residence thermal
stability and mold release resistance by the aforementioned
methods. The results are described in Table 1.
Comparative Example 3
[0092] Pellets of a polyacetal resin composition were obtained in
the same manner as in Example 1, except that the fatty acid amide
(D) was not added. The resin temperature was actually measured near
the extruder die exit using a thermocouple thermometer, and was
controlled by manipulating the rotational speed of the extruder
screw. The residence time for the resin composition was 3 minutes.
The obtained pellets were subjected to the measurements of tensile
elongation at break, Charpy impact value, residence thermal
stability and mold release resistance by the aforementioned
methods. The results are described in Tables 1 and 2.
TABLE-US-00001 TABLE 1 Unit Example 1 Example 2 Example 3 Example 4
Example 5 Example 6 Example 7 Polyacetal resin (A-1) phr 100 100
100 100 100 100 100 Polyacetal resin (A-2) phr Polyacetal resin
(A-3) phr Antioxidant(B) phr 0.3 0.3 0.3 0.3 0.3 0.3 0.3
Nitrogen-containing phr 0.1 0.1 0.1 0.1 0.1 0.1 0.1 compound(C)
Fatty acid amide(D-1) phr 0.15 0.3 0.15 0.15 0.5 0.9 Fatty acid
amide(D-2) phr 0.15 Fatty acid metal salt(E) phr Resin temperature
at .degree. C. 250 257 260 268 260 260 266 extruder exit MI of
Resin composition g/10 0.8 0.8 1.2 0.8 0.8 0.8 0.9 (MI of pellets)
minutes Tensile elongation at % 45.9 46.1 46.7 44.9 45.0 40.5 43.2
break Charpy impact value kJ 13.5 13.5 13.5 13.0 12.5 12.0 10.5
Residence of thermal minutes 72 72 72 72 72 72 72 stability
(200.degree. C.) Mold release resistance MPa 3.2 3.4 3.3 3.3 3.4
3.8 4.3 A-1: a linear polyacetal resin (MI of the resin: 0.6 g/10
minutes) A-2: a linear polyacetal resin (MI of the resin: 2.5 g/10
minutes) A-3: a crosslinked polyacetal resin B: triethylene
glycol-bis|3-(3-t-butyl-4-hydroxy-5-methylphenyl) propionate| C:
melamine D-1: ethylenebisstearamide D-2: hexamethylenebisstearamide
E: calcium stearate
TABLE-US-00002 TABLE 2 Comparative Comparative Comparative
Comparative Comparative Comparative Comparative Unit Example 1
Example 2 Example 3 Example 4 Example 5 Example 6 Example 7
Polyacetal resin (A-1) phr 100 100 100 100 Polyacetal resin (A-2)
phr 100 100 Polyacetal resin (A-3) phr 100 Antioxidant(B) phr 0.3
0.3 0.3 0.3 0.3 0.3 0.3 Nitrogen-containing phr 0.001 0.1 0.1 0.1
0.1 0.1 0.1 compound(C) Fatty acid amide(D-1) phr 0.15 0.15 0.15
0.9 0.15 Fatty acid amide(D-2) phr Fatty acid metal salt(E) phr
0.15 Resin temperature at .degree. C. 260 264 260 285 260 260 260
extruder exit MI of Resin composition g/10 1.6 1.0 0.8 2.5 2.7 2.7
0.8 (MI of pellets) minutes Tensile elongation at % 32.6 37.6 43.5
34.3 34.0 30.5 34.3 break Charpy impact value kJ 9.0 13.0 13.0 8.3
8.0 7.5 9.9 Residence of thermal minutes 36 12 72 36 72 72 36
stability (200.degree. C.) Mold release resistance MPa 3.6 4.8 6.5
4.0 3.7 4.1 4.0 A-1: a linear polyacetal resin (MI of the resin:
0.6 g/10 minutes) A-2: a linear polyacetal resin (MI of the resin:
2.5 g/10 minutes) A-3: a crosslinked polyacetal resin B:
triethylene glycol-bis[3-(3-t-butyl-4-hydroxy-5-methylphenyl)
propionate] C: melamine D-1: ethylenebisstearamide D-2:
hexamethylenebisstearamide E: calcium stearate
INDUSTRIAL APPLICABILITY
[0093] The polyacetal resin compositions of the present invention
have outstanding impact resistance and thus can be used widely as
structural materials and mechanism parts such as electrical
devices, automobile parts and precision machine parts. Further, the
polyacetal resin compositions of the invention have excellent
thermal stability and releasability and thus can be suitably used
not only for extrusion molding but also for injection molding.
* * * * *