U.S. patent application number 16/250337 was filed with the patent office on 2019-05-23 for use of a wax-modified, air rectified asphalt in built up roofing asphalt compositions.
The applicant listed for this patent is Owens Corning Intellectual Capital, LLC. Invention is credited to David C. Trumbore.
Application Number | 20190153228 16/250337 |
Document ID | / |
Family ID | 55971276 |
Filed Date | 2019-05-23 |
![](/patent/app/20190153228/US20190153228A1-20190523-D00001.png)
United States Patent
Application |
20190153228 |
Kind Code |
A1 |
Trumbore; David C. |
May 23, 2019 |
USE OF A WAX-MODIFIED, AIR RECTIFIED ASPHALT IN BUILT UP ROOFING
ASPHALT COMPOSITIONS
Abstract
A composition and method for making a heat stable, low
application temperature Built Up Roofing Asphalt (BURA) is
provided. The composition comprises a wax-modified, air rectified
asphalt conforming to Type 3 BURA and, in some embodiments, Type 4
BURA specifications.
Inventors: |
Trumbore; David C.;
(Chicago, IL) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Owens Corning Intellectual Capital, LLC |
Toledo |
OH |
US |
|
|
Family ID: |
55971276 |
Appl. No.: |
16/250337 |
Filed: |
January 17, 2019 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
14944374 |
Nov 18, 2015 |
10189994 |
|
|
16250337 |
|
|
|
|
62082683 |
Nov 21, 2014 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C08L 91/06 20130101;
E04D 11/02 20130101; C08L 2555/64 20130101; C08L 2555/72 20130101;
C08L 95/00 20130101; C08L 2201/08 20130101; E04D 7/00 20130101;
C08L 95/00 20130101; C08L 91/06 20130101 |
International
Class: |
C08L 95/00 20060101
C08L095/00; C08L 91/06 20060101 C08L091/06; E04D 11/02 20060101
E04D011/02 |
Claims
1-13. (canceled)
14. An asphalt composition comprising: an air rectified asphalt
blown to a first softening point from about 140.degree. F. to about
175.degree. F.; and a wax additive, wherein the additive has a melt
point higher than about 100.degree. C.; wherein the asphalt
composition has a penetration at 25.degree. C. of 12 dmm to 35
dmm.
15. The asphalt composition of claim 14, wherein the asphalt
composition has an equiviscous temperature (EVT) of from about
340.degree. F. to about 390.degree. F. for mopping applications and
from about 380.degree. F. to about 430.degree. F. for mechanical
applications.
16. The asphalt composition of claim 14, wherein the air rectified
asphalt is blown to a first softening point that is at least about
145.degree. F.
17. The asphalt composition of claim 14, wherein the air rectified
asphalt is blown to a first softening point from about 145.degree.
F. to about 165.degree. F.
18. The asphalt composition of claim 14, wherein the air rectified
asphalt is blown to a first softening point that is at least about
156.degree. F.
19. The asphalt composition of claim 14, wherein the air rectified
asphalt is blown to a first softening point of about 164.degree.
F.
20. The asphalt composition of claim 14, wherein the wax additive
comprises from about 1.5% to about 4.5% based on the weight of the
total asphalt composition.
21. The asphalt composition of claim 14, wherein the wax additive
comprises one or more of a functionalized wax, a synthetic wax, or
a naturally occurring wax.
22. The asphalt composition of claim 14, wherein the wax additive
comprises a synthetic wax selected from ethylene bis-stearamide wax
(EBS), Fischer-Tropsch wax (FT), oxidized Fischer-Tropsch wax
(FTO), polyolefin wax, polyethylene wax (PE), oxidized polyethylene
wax (PEO), polypropylene wax, polypropylene/polyethylene wax,
alcohol wax, silicone wax, petroleum wax, microcrystalline wax, or
paraffin.
23. The asphalt composition of claim 22, wherein the wax additive
comprises one or more of a Fischer-Tropsch wax, a polyethylene wax,
and an ethylene bis-stearamide wax.
24. The asphalt composition of claim 14, wherein the wax additive
comprises a functionalized wax selected from amine waxes, amide
waxes, ester waxes, carboxylic acid waxes, and microcrystalline
waxes.
25. The asphalt composition of claim 14, wherein the wax additive
comprises a naturally occurring wax derived from a plant, animal or
mineral.
26. The asphalt composition of claim 25, wherein the naturally
occurring wax is selected from candelilla wax, carnauba wax, rice
wax, Japan wax, jojoba oil, beeswax, lanolin whale wax, montan wax,
ozokerite and ceresin.
27. The asphalt composition of claim 14, wherein the asphalt
composition has a minimum solubility in trichloroethylene of
99%.
28. The asphalt composition of claim 14, wherein the asphalt
composition has a penetration at 25.degree. C. of 15 dmm to 35
dmm.
29. The asphalt composition of claim 14, wherein the asphalt
composition has a penetration at 25.degree. C. of 12 dmm to 25
dmm.
30. An asphalt composition comprising: an air rectified asphalt;
and a wax additive, wherein the additive has a melt point higher
than about 100.degree. C.; wherein the asphalt composition has an
equiviscous temperature (EVT) of from about 340.degree. F. to about
390.degree. F. for mopping applications and from about 380.degree.
F. to about 430.degree. F. for mechanical applications.
31. The asphalt composition of claim 30, wherein the air rectified
asphalt is blown to a first softening point from about 140.degree.
F. to about 175.degree. F.
32. The asphalt composition of claim 30, wherein the air rectified
asphalt does not include a blowing catalyst.
33. The asphalt composition of claim 30, wherein the asphalt
composition has a penetration at 25.degree. C. of 12 dmm to 35 dmm.
Description
RELATED APPLICATIONS
[0001] This application is a continuation of U.S. Non-Provisional
application Ser. No. 14/944,374, filed on Nov. 18, 2015, which
claims priority from U.S. Provisional Application No. 62/082,683,
filed on Nov. 21, 2014, the entire disclosures of which are
incorporated herein by reference.
FIELD OF THE DISCLOSURE
[0002] The present disclosure relates generally to asphalt roofing
products, including asphalt for Built Up Roofing Asphalt (BURA)
compositions. Particularly, the present disclosure relates to
methods and compositions for producing a wax-modified, air
rectified asphalt that meets the ASTM specifications for Type 3
BURA and, in some embodiments, Type 4 BURA. The wax-modified, air
rectified asphalt disclosed herein may be applied at lower
temperatures than conventional BURA compositions.
BACKGROUND
[0003] The Equiviscous Temperature (EVT) signifies the temperature
needed to achieve the proper viscosity for proper application in
the field. In order to achieve this temperature at application, the
asphalt must be heated to an elevated temperature in a kettle prior
to transport to a rooftop. It is desirable to minimize both the
kettle temperature and the EVT to the extent possible, while still
maintaining the desired heat stability, viscosity, and ductility
for a BURA composition.
SUMMARY
[0004] Various exemplary embodiments of the present invention are
directed to a heat stable, low application temperature, built-up
roofing asphalt (BURA).
[0005] In some exemplary embodiments, a BURA composition is
disclosed. The BURA composition includes an air rectified asphalt
and a wax additive. The BURA composition has an equiviscous
temperature (EVT) of from about 340.degree. F. to about 390.degree.
F. for mopping applications and from about 380.degree. F. to about
430.degree. F. for mechanical applications. This is between about
50.degree. F. and 83.degree. F. lower than conventional BURA
application temperatures.
BRIEF DESCRIPTION OF THE DRAWINGS
[0006] The advantages of this invention will be apparent upon
consideration of the following detailed disclosure of the
invention, especially when taken in conjunction with the
accompanying drawings wherein:
[0007] FIG. 1 is a graph depicting a Penetration Index of less than
2, based on the definition provided by the Eurobitume Technical
Committee Task Force in 2011.
DETAILED DESCRIPTION OF THE DISCLOSURE
[0008] Numerical ranges as used herein are intended to include
every number and subset of numbers within that range, whether
specifically disclosed or not. Further, these numerical ranges
should be construed as providing support for a claim directed to
any number or subset of numbers in that range. For example, a
disclosure of from 1 to 10 should be construed as supporting a
range of from 2 to 8, from 3 to 7, from 5 to 6, from 1 to 9, from
3.6 to 4.6, from 3.5 to 9.9, and so forth.
[0009] All references to singular characteristics or limitations of
the present disclosure shall include the corresponding plural
characteristic or limitation, and vice versa, unless otherwise
specified or clearly implied to the contrary by the context in
which the reference is made.
[0010] Unless defined otherwise, all technical and scientific terms
used herein have the same meaning as commonly understood by one of
ordinary skill in the art to which the invention belongs. Although
any methods and materials similar or equivalent to those described
herein can be used in the practice or testing of the present
invention, the preferred methods and materials are described
herein. All references cited herein, including published or
corresponding U.S. or foreign patent applications, issued U.S. or
foreign patents, or any other references, are each incorporated by
reference in their entireties, including all data, tables, figures,
and text presented in the cited references. In the drawings, the
thickness of the lines, layers, and regions may be exaggerated for
clarity. It is to be noted that like numbers found throughout the
figures denote like elements.
[0011] A heat stable, low application temperature, built-up roofing
asphalt (BURA) composition is described in detail herein. In some
exemplary embodiments, the inventive composition includes an air
rectified asphalt and a wax additive to meet the ASTM D 312
specifications for Type 3 BURA, and in some embodiments, Type 4
BURA. Further, the application temperature of the BURA composition
disclosed herein is about 50.degree. F. and 83.degree. F. lower
than conventional BURA application temperatures.
[0012] U.S. Pat. No. 4,554,023, incorporated herein by reference in
its entirety, discloses the use of a bis-stearoylamide additive to
reduce the viscosity of an asphalt to a viscosity desired for an
ultimate blend. BURA compositions in accordance with this present
invention may include any combination or sub combination of the
features disclosed by the present application and U.S. Pat. No.
4,554,023.
[0013] U.S. Pat. Nos. 7,857,904, 7,951,239, 7,951,240, and
8,753,442 each disclose a method for producing coating asphalts.
U.S. Pat. Nos. 7,857,904, 7,951,239, 7,951,240, and 8,753,442 are
each incorporated herein by reference in their entirety. The
methods include partially air blowing the paving grade asphalt
feedstock to lower its penetration value and raise its softening
point. A wax is then added to the partially blown asphalt to
further raise its softening point to a point that is within the
desired range for coating asphalt. This process additionally
incorporates a blowing catalyst, such as phosphoric acid, to
further soften the asphalt. BURA compositions in accordance with
this present invention may include any combination or sub
combination of the features disclosed by the present application
and U.S. Pat. Nos. 7,857,904, 7,951,239, 7,951,240, and
8,753,442.
[0014] U.S. Patent Application Ser. No. 61/953,413, incorporated
herein by reference in its entirety, discloses methods and
compositions for producing BURA and coating asphalt compositions
from non-coating grade asphalts, such as paving-grade asphalts. The
built up roofing asphalt composition incorporates an ester
additive, such as a vegetable oil, fat, or plasticizer to over
blown paving asphalt. BURA compositions in accordance with this
present invention may include any combination or sub combination of
the features disclosed by the present application and U.S. Patent
Application Ser. No. 61/953,413.
Definitions
[0015] As used herein, unless otherwise specified, the term
"asphalt" is meant to include asphalts produced from petroleum
refining, including residua from atmospheric distillation, from
vacuum distillation, from solvent de-asphalting units, and from
recycled asphalt or petroleum product streams, such as re-refined
motor oil bottoms. Mixtures of different asphalts may also be used.
The general inventive concepts may also be used with natural
bitumen, such as the products extracted from the oil sands in
Alberta or asphalts derived from oil sands by various refinery
processes.
[0016] As used herein, unless otherwise specified, the term "BURA"
means asphalt that is suitable for use as built up roofing asphalt
according to the four types defined by ASTM D 312, displayed below
in Table 1.
TABLE-US-00001 TABLE 1 Four Types of BURA According to ASTM D 312
TYPE 1 TYPE 2 TYPE 3 TYPE 4 Property Min Max Min Max Min Max Min
Max Softening point 57 66 70 80 85 96 99 107 .degree. C. (.degree.
F.) (135) (151) (158) (176) (185) (205) (210) (225) Flash Point,
260 -- 260 -- 260 -- 260 -- .degree. C. (.degree. F.) (500) (500)
(500) (500) Penetration Units: (dmm) At 0.degree. C. 3 6 6 6
(32.degree. F.) At 25.degree. C. 18 60 18 40 15 35 12 25
(77.degree. F.) At 46.degree. C. 90 180 -- 100 -- 90 -- 75
(115.degree. F.) Ductility at 10.0 -- 3.0 -- 2.5 -- 1.5 --
25.degree. C. Solubility in 99 -- 99 -- 99 -- 99 -- trichloro-
ethylene %
[0017] The general inventive concepts herein relate to an asphalt
composition that meets the properties listed in Table 1 for
classification as Type 3 BURA, and in some embodiments, Type 4
BURA.
[0018] The properties of the disclosed asphalt compositions may be
measured by any suitable test known and accepted in the art. In the
description provided herein, the asphalt properties are measured as
follows: softening point or "SP" by ASTM D36; penetration or "pen"
by ASTM D5 run at 25.degree. C.; melt viscosity or "visc" by ASTM
D4402; durability by ASTM D4798; flashpoint by ASTM D92; stain
index by ASTM D2746; and stability by ASTM D3791 modified to run at
oven temperature of 260.degree. C. for up to 5 days or similar test
procedure.
[0019] Any suitable asphalt(s) may be used in accordance with the
BURA compositions disclosed herein. For example, paving asphalts
which meet the PG64-22 specifications (AASHTO M320) may be used,
especially those meeting or exceeding the first number, 64, which
is the average seven day maximum pavement temperature performance
test and is based on rheological properties such as dynamic shear.
Paving asphalts were traditionally graded by viscosity, and a
common asphalt that is similar to the PG64-22 grade and usable in
this method is the AC20 grade (ASTM D3381). Other examples of
paving asphalts that may be suitable include PG67-22, PG-70-22,
PG58-22, PG70-16, PG70-10, PG67-10, pen grade 40-50, pen grade
60-70, pen grade 85-100, pen grade 120-150, AR4000, AR8000, and
AC30 grade. Additionally softer asphalts, commonly called roofers
flux, as well as harder asphalts from solvent deasphalting
processes can both be used in blends or with various paving
asphalts to achieve the desired BURA product.
Method of Making the Air Rectified, Wax-Modified BURA
[0020] The present disclosure is directed to a heat stable BURA
composition. In some exemplary embodiments, the inventive
composition includes an air rectified asphalt and a wax additive to
meet the ASTM D 312 specifications for Type 3 BURA and, in some
embodiments, Type 4 BURA.
[0021] As described in detail hereafter, the general inventive
concepts encompass the use of air rectified, as opposed to more
fully oxidized, asphalt in a BURA composition. Eurobitume has
defined air rectified asphalt by a Penetration Index threshold, and
this definition has generally been adopted in the field. The
Penetration Index (PI) is calculated based on the softening point
and penetration of the asphalt. FIG. 1 shows the combination of
softening point and penetration that meets the Eurobitume
distinction for air rectified asphalt. Combinations of softening
point and penetration that lie below the curve in FIG. 1 give PI's
of less than 2, and thus meet the standard for air rectified
asphalts. In contrast, combinations above the line give PI's of
greater than 2, and are defined as more fully oxidized
asphalts.
[0022] A conventional air blowing process involves the oxidation of
an asphalt composition by bubbling or blowing oxygen-containing gas
(for example, air, oxygen or an oxygen-inert gas mixture) through
molten asphalt at an elevated temperature for a particular
processing time, such as from about 1 hour to about 12 hours. The
processing time depends on various factors, such as the type of
asphalt feedstock used, the processing temperature, the air flow
rate, the design of the process equipment, and the desired
characteristics of the BURA composition to be produced. The process
involves loading the asphalt feedstock into a converter (oxidizer)
at any suitable temperature, for example, a temperature of from
about 200.degree. C. to about 230.degree. C. Thereafter, the gas is
bubbled or blown through the molten asphalt. The reaction produced
by the blowing is exothermic and raises the temperature of the
asphalt to any suitable blowing temperature, for example, a
temperature of from about 250.degree. C. about 265.degree. C. The
maximum temperature is usually controlled by a water-cooled jacket.
In some exemplary embodiments, the process is carried out at
ambient pressure, although it can also be carried out at elevated
pressure. In some exemplary embodiments, the process is carried out
in batches, although it can also be carried out continuously.
[0023] Thus, whereas oxidized asphalts are produced over a wide
range of softening points and penetrations, air rectified asphalts
are blown for a shorter time than higher softening point products,
and are often referred to as "partially blown" or "semi-blown."
[0024] The "target softening point range" is the range that meets
the ASTM specification for the BURA composition. For example, for
Type 3 BURA, the target softening point range is from 185.degree.
F. to 205.degree. F. based on the ASTM D312 specification. The
intermediate or first softening point that results from the partial
blowing step to produce an air rectified asphalt is lower than the
target softening point range. For example, the first softening
point may be within a range of from about 140.degree. F. to about
175.degree. F., depending on the particular grade of asphalt used
and depending on whether or not a catalyst is used during blowing.
In some exemplary embodiments, the first softening point is within
a range of from about 145.degree. F. to about 165.degree. F. In
some embodiments the first softening point is about 164.degree. F.
In some exemplary embodiments, the first softening point is about
156.degree. F. In some exemplary embodiments, the first softening
point is about 145.degree. F.
[0025] In some exemplary embodiments, a blowing catalyst may be
added to the asphalt before or during the partial blowing process.
Several catalysts may be suitable for use in the air blowing
process to either speed up the reaction or to create a final
product with a higher penetration. If an optional blowing catalyst
is used, any type of blowing catalyst or mixture of blowing
catalysts may be used. Common catalysts include ferric chloride and
phosphoric acid
[0026] The blowing process generates flue gases, which generally
may contain hydrogen sulfide, sulfur oxides (SOX), organosulfur
compounds, hydrocarbons, nitrogen oxides (NOX), carbon monoxide,
and water. When ferric chloride is used as a catalyst, the flue
gases may also contain hydrogen chloride. Prior to release into the
atmosphere, the flue gases are typically passed through a
water-sealed knockout tank and then subjected to an incineration
process to control the emissions of volatile organic compounds
(VOC's). In that process, the sulfur compounds are oxidized to form
sulfur oxides, and the carbon monoxide is oxidized to carbon
dioxide. The energy used to incinerate these fumes and the
emissions that remain after incineration both increase as the
processing time increases.
[0027] In accordance with the process described herein, a wax is
added to the first softening point product. By adding a wax, the
softening point is increased to the target softening point range
while maintaining a penetration within the desired range. In other
embodiments, the wax addition may lower or raise the penetration as
it increases the softening point. In the case of a wax addition
that lowers the penetration, the partial blowing step of the method
would be stopped at a higher penetration value and hence lower
softening point value. In that case, the wax addition step further
lowers the penetration to a second penetration that is within the
target penetration range. In one embodiment, the asphalt may be
further blown after the wax addition and/or other additives may be
added, provided the asphalt maintains the requirements of an "air
rectified" asphalt.
[0028] Any type of wax, or a mixture of one or more different waxes
capable of functioning as described herein, may be used in the
present method. In some exemplary embodiments, the wax has a high
congealing point or a high drop melt point of at least about
75.degree. C., including at least about 90.degree. C., and
including at least about 100.degree. C. When referring to wax
testing, the term "melt point" is used to refer broadly to either
congealing point or drop melt point, which are defined by ASTM D
938 in the case of congealing point and ASTM D 3954 in the case of
drop melt point. Wax may also be characterized by penetration or
hardness (ASTM D5 or ASTM D1321), density (ASTM D1505), viscosity
(ASTM D4402 or ASTM D88), or acid value (ASTM D1386).
[0029] In accordance with the general inventive concepts, the wax
may be a functionalized wax, a synthetic wax, or a naturally
occurring wax. Further, the wax may be oxidized or non-oxidized.
Some examples of synthetic waxes that may be suitable include
ethylene bis-stearamide wax (EBS), Fischer-Tropsch wax (FT),
oxidized Fischer-Tropsch wax (FTO), polyolefin waxes such as
polyethylene wax (PE), oxidized polyethylene wax (PEO),
polypropylene wax, polypropylene/polyethylene wax, alcohol wax,
silicone wax, petroleum waxes such as microcrystalline wax or
paraffin, and other synthetic waxes. Some examples of
functionalized waxes include amine waxes, amide waxes, ester waxes,
carboxylic acid waxes, and microcrystalline waxes.
[0030] Exemplary naturally occurring waxes may be those derived
from a plant, animal or mineral. Examples of natural waxes include
plant waxes such as candelilla wax, carnauba wax, rice wax, Japan
wax and jojoba oil, animal waxes such as beeswax, lanolin and whale
wax, and mineral waxes such as montan wax, ozokerite and
ceresin.
[0031] Certain types of waxes may be particularly effective for use
with the BURA compositions disclosed herein. In some embodiments,
the wax is a Fischer-Tropsch wax with a melt point of greater than
100.degree. C., and a hardness at 25.degree. C. of 1 dmm or less.
In other embodiments, the wax is a polyethylene wax with a melt
point of greater than 100.degree. C. up to about 120.degree. C., a
hardness at 25.degree. C. up to about to 4 dmm, a density of from
about 0.91 to about 0.95 gm/cc, a viscosity of about 20 to about
450 cps at 140.degree. C., and a nil acid number. In other
embodiments, the wax is an oxidized polyethylene wax with melt
point of about 135 to about 140.degree. C., a hardness at
25.degree. C. of <0.5 dmm, a viscosity of about 3600 to about
4500 at 150.degree. C., and acid number of 30. In other
embodiments, the wax is an ethylene bis-stearamide wax with a melt
point of about 135.degree. C. to about 145.degree. C. and an acid
number of 8.
[0032] Further, any suitable mixtures of different waxes may also
be used. For example, the wax may include a blend of a
Fischer-Tropsch wax and a polyethylene wax.
[0033] In accordance with the general inventive concepts, the wax
may be added in any suitable amount. In some exemplary embodiments,
the wax is added in an amount from about 1% to about 5% by weight,
including from about 1.5% to about 4.5% by weight, including from
about 2.5% to about 3.5% by weight of the BURA composition.
Properties of the Air Rectified, Wax-Modified BURA Composition
[0034] In some exemplary embodiments, the air rectified,
wax-modified asphalt provides the inventive BURA composition a
resistance to a phenomenon known as "dropback." Dropback is a
phenomenon that occurs when asphalt is exposed to high temperatures
for a prolonged period of time. In general, the higher the
temperature, or the longer the asphalt is exposed to heat, the
lower the softening point and higher the penetration value may
become. However, even after being exposed to heat (about
500.degree. F.) for 5 hours, 24 hours, or more, the inventive BURA
composition does not exhibit a significant change in softening
point or penetration level. In some exemplary embodiments, the BURA
compositions average a loss of about 1.degree. F. softening point
after 5 hours at 500.degree. F. and a gain of about 1.degree. F.
softening point after 24 hours at 500.degree. F.
[0035] As discussed throughout the present disclosure, the
inventive concepts relate to a BURA composition comprising air
rectified, as opposed to more fully oxidized, asphalt. The
Equiviscous Temperature (EVT) is used to determine the temperature
to which the asphalt needs to be heated in order to achieve proper
application. The EVT is evaluated based on ASTM D 4402 standards.
For mopping application, a temperature is needed that achieves an
asphalt viscosity of 125 cps. For mechanical application, a
temperature is needed that achieves an asphalt viscosity of 75 cps.
The BURA composition disclosed herein has an application
temperature that is between about 50.degree. F. and 83.degree. F.
lower than typical conventional BURA application temperatures. In
some exemplary embodiments, the BURA composition has an equiviscous
temperature (EVT) of from about 340.degree. F. to about 390.degree.
F. for mopping applications and from about 380.degree. F. to about
430.degree. F. for mechanical applications. In some exemplary
embodiments, the BURA composition disclosed herein provides an
average decrease in EVT of about 59.degree. F. for mopping and
about 45.degree. F. for mechanical applications compared to typical
conventional BURA compositions. In some exemplary embodiments, the
BURA composition disclosed herein provides an average decrease in
EVT of about 67.degree. F. for mopping and about 83.degree. F. for
mechanical applications compared to conventional BURA
compositions.
[0036] The general inventive concepts have been described above
both generically and with regard to various exemplary embodiments.
Although the general inventive concepts have been set forth in what
is believed to be exemplary illustrative embodiments, a wide
variety of alternatives known to those of skill in the art can be
selected within the generic disclosure. The general inventive
concepts are not otherwise limited, except for the recitation of
the claims set forth below.
[0037] As used in the description of the invention and the appended
claims, the singular forms "a," "an," and "the" are intended to
include the plural forms as well, unless the context clearly
indicates otherwise. To the extent that the term "includes" or
"including" is used in the specification or the claims, it is
intended to be inclusive in a manner similar to the term
"comprising" as that term is interpreted when employed as a
transitional word in a claim. Furthermore, to the extent that the
term "or" is employed (e.g., A or B) it is intended to mean "A or B
or both." When the applicants intend to indicate "only A or B but
not both" then the term "only A or B but not both" will be
employed. Thus, use of the term "or" herein is the inclusive, and
not the exclusive use. Also, to the extent that the terms "in" or
"into" are used in the specification or the claims, it is intended
to additionally mean "on" or "onto." Furthermore, to the extent the
term "connect" is used in the specification or claims, it is
intended to mean not only "directly connected to," but also
"indirectly connected to" such as connected through another
component or components.
[0038] Unless otherwise indicated herein, all sub-embodiments and
optional embodiments are respective sub-embodiments and optional
embodiments to all embodiments described herein. While the present
application has been illustrated by the description of embodiments
thereof, and while the embodiments have been described in
considerable detail, it is not the intention of the applicants to
restrict or in any way limit the scope of the appended claims to
such detail. Additional advantages and modifications will readily
appear to those skilled in the art. Therefore, the application, in
its broader aspects, is not limited to the specific details, the
representative process, and illustrative examples shown and
described. Accordingly, departures may be made from such details
without departing from the spirit or scope of the applicant's
general disclosure herein.
* * * * *