U.S. patent application number 15/793521 was filed with the patent office on 2019-04-25 for multi-gate semiconductor device and method for forming the same.
The applicant listed for this patent is TAIWAN SEMICONDUCTOR MANUFACTURING COMPANY LTD.. Invention is credited to I-SHENG CHEN, TZU-CHIANG CHEN, CARLOS H. DIAZ, CHENG-HSIEN WU, LING-YEN YEH.
Application Number | 20190123189 15/793521 |
Document ID | / |
Family ID | 66169568 |
Filed Date | 2019-04-25 |
View All Diagrams
United States Patent
Application |
20190123189 |
Kind Code |
A1 |
CHEN; I-SHENG ; et
al. |
April 25, 2019 |
MULTI-GATE SEMICONDUCTOR DEVICE AND METHOD FOR FORMING THE SAME
Abstract
A multi-gate semiconductor device includes a substrate, a
stacked wire structure disposed over the substrate, a gate over the
stacked wire structure, and at least a first spacer disposed over
two sidewalls of the gate. The gate further includes a gate
conductive structure wrapping the stacked wire structure and a gate
dielectric layer sandwiched between the gate conductive structure
and the stacked wire structure. Further, sidewalls of the gate
conductive structure are in contact with the first spacer.
Inventors: |
CHEN; I-SHENG; (TAIPEI CITY,
TW) ; CHEN; TZU-CHIANG; (HSINCHU CITY, TW) ;
WU; CHENG-HSIEN; (HSINCHU CITY, TW) ; YEH;
LING-YEN; (HSINCHU CITY, TW) ; DIAZ; CARLOS H.;
(MOUNTAIN VIEW, CA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
TAIWAN SEMICONDUCTOR MANUFACTURING COMPANY LTD. |
Hsinchu |
|
TW |
|
|
Family ID: |
66169568 |
Appl. No.: |
15/793521 |
Filed: |
October 25, 2017 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
B82Y 10/00 20130101;
H01L 27/0886 20130101; H01L 29/0847 20130101; H01L 29/66484
20130101; H01L 29/6656 20130101; H01L 29/66795 20130101; H01L
21/823821 20130101; H01L 21/82385 20130101; H01L 29/66545 20130101;
H01L 29/785 20130101; H01L 29/0653 20130101; H01L 27/0924 20130101;
H01L 21/8221 20130101; H01L 29/42392 20130101; H01L 29/775
20130101; H01L 21/823842 20130101; H01L 21/823412 20130101; H01L
29/401 20130101; H01L 29/66439 20130101; H01L 29/78696 20130101;
H01L 27/088 20130101; H01L 29/0673 20130101; H01L 21/76877
20130101; H01L 21/823431 20130101; H01L 27/0688 20130101; H01L
21/82345 20130101 |
International
Class: |
H01L 29/78 20060101
H01L029/78; H01L 21/8234 20060101 H01L021/8234; H01L 21/8238
20060101 H01L021/8238; H01L 27/088 20060101 H01L027/088; H01L
27/092 20060101 H01L027/092; H01L 29/66 20060101 H01L029/66; H01L
21/768 20060101 H01L021/768 |
Claims
1. A multi-gate semiconductor device comprising: a substrate; a
stacked wire structure disposed over the substrate; a gate over the
stacked wire structure, the gate comprising: a gate conductive
structure wrapping the stacked wire structure; and a gate
dielectric layer sandwiched between the gate conductive structure
and the stacked wire structure; at least a first spacer disposed
over two sidewalls of the gate, wherein sidewalls of the gate
conductive structure are in contact with the first spacer; and a
second spacer, wherein the first spacer is sandwiched between the
second spacer and the sidewall of the gate conductive structure,
and the second spacer comprises an air gap.
2. The multi-gate semiconductor device of claim 1, wherein the
first spacer comprises a conductive material.
3-6. (canceled)
7. The multi-gate semiconductor device of claim 1, wherein the gate
conductive structure comprises at least a barrier metal layer, a
work function metal layer, and a gap-filling metal layer.
8. The multi-gate semiconductor device of claim 7, wherein the
barrier metal layer is in contact with the first spacer.
9. (canceled)
10-20. (canceled)
21. The multi-gate semiconductor device of claim 2, wherein the
first spacer is separated from the stacked wire structure by the
gate dielectric layer.
22. (canceled)
23. A multi-gate semiconductor device comprising: a substrate; a
stacked wire structure disposed over the substrate; a gate over the
stacked wire structure, the gate comprising: a gate conductive
structure wrapping the stacked wire structure; and a gate
dielectric layer sandwiched between the gate conductive structure
and the stacked wire structure; and at least a conductive spacer
disposed over two sidewalls of the gate, wherein sidewalls of the
gate conductive structure are in contact with the conductive
spacer.
24. The multi-gate semiconductor device of claim 23, wherein the
conductive spacer is separated from the stacked wire structure by
the gate dielectric layer.
25. The multi-gate semiconductor device of claim 23, further
comprising an insulating spacer, wherein the conductive spacer is
sandwiched between the insulating spacer and the sidewall of the
gate conductive structure.
26. The multi-gate semiconductor device of claim 25, further
comprises a dielectric structure disposed over the substrate,
wherein the conductive spacer is separated from the dielectric
structure by the insulating spacer.
27. The multi-gate semiconductor device of claim 23, wherein the
gate conductive structure comprises at least a barrier metal layer,
a work function metal layer, and a gap-filling metal layer.
28. The multi-gate semiconductor device of claim 27, wherein the
barrier metal layer is in contact with the conductive spacer.
29. A multi-gate semiconductor device comprising: a substrate; a
stacked wire structure disposed over the substrate; a gate
conductive structure wrapping the stacked wire structure, wherein
the gate comprising a barrier metal layer, a work function metal
layer, and a gap-filling metal layer; a gate dielectric layer
sandwiched between the barrier metal layer and the stacked wire
structure; and at least a conductive spacer disposed over two
sidewalls of the gate, wherein barrier metal layer of the gate
conductive structure is in contact with the conductive spacer.
30. The multi-gate semiconductor device of claim 29, further
comprising an insulating spacer, wherein the conductive spacer is
sandwiched between the insulating spacer and the sidewall of the
gate conductive structure.
31. The multi-gate semiconductor device of claim 29, further
comprises a dielectric structure disposed over the substrate,
wherein the conductive spacer is separated from the dielectric
structure by the insulating spacer.
32. The multi-gate semiconductor device of claim 1, further
comprises a dielectric structure disposed over the substrate,
wherein the first spacer is separated from the dielectric structure
by the second spacer.
33. The multi-gate semiconductor device of claim 25, wherein the
insulating spacer comprises an air gap.
34. The multi-gate semiconductor device of claim 25, wherein the
insulating spacer comprises silicon nitride (SiN), silicon oxide
(SiO), silicon carbide (SiC), silicon oxycarbide (SiOC), or silicon
oxycarbon nitride (SiOCN).
35. The multi-gate semiconductor device of claim 29, wherein the
conductive spacer is separated from the stacked wire structure by
the gate dielectric layer.
36. The multi-gate semiconductor device of claim 30, wherein the
insulating spacer comprises an air gap.
37. The multi-gate semiconductor device of claim 30, wherein the
insulating spacer comprises silicon nitride (SiN), silicon oxide
(SiO), silicon carbide (SiC), silicon oxycarbide (SiOC), or silicon
oxycarbon nitride (SiOCN).
Description
BACKGROUND
[0001] As the semiconductor industry has progressed into nanometer
technology process nodes in pursuit of higher device density,
higher performance, and lower costs, challenges from both
fabrication and design issues have resulted in the development of
three-dimensional designs, such as multi-gate field effect
transistor (FET) including a fin FET (FinFET) and a gate-all-around
(GAA) FET. In a FinFET, a gate electrode is adjacent to three side
surfaces of a channel region with a gate dielectric layer
interposed therebetween. Because the gate structure surrounds the
fin on three surfaces, the transistor essentially has thee gates
controlling the current through the fin or channel region. However,
the fourth side that is the bottom part of the channel region is
far away from gate electrode and this is not under close gate
control. Different from FinFET, in a GAA FET all side surfaces of
the channel region are surrounded by the gate electrode, which
allows for fuller depletion in the channel region and results in
less short-channel effects due to a steeper sub-threshold current
swing (SS) and smaller drain induced barrier lower (DIBL).
[0002] Although existing GAA FET devices and methods of fabricating
GAA FET devices have been generally adequate for their intended
purpose, they have not been entirely satisfactory in all
aspects.
BRIEF DESCRIPTION OF THE DRAWINGS
[0003] Aspects of the present disclosure are best understood from
the following detailed description when read with the accompanying
figures. It is noted that, in accordance with the standard practice
in the industry, various features are not drawn to scale. In fact,
the dimensions of the various features may be arbitrarily increased
or reduced for clarity of discussion.
[0004] FIG. 1 shows a flow chart representing a method for forming
a multi-gate semiconductor device according to aspects of the
present disclosure.
[0005] FIG. 2 shows a flow chart representing a method for forming
a multi-gate semiconductor device according to aspects of the
present disclosure.
[0006] FIG. 3A through FIG. 3N illustrate a multi-gate
semiconductor device at various fabrication stages constructed
according to aspects of the present disclosure in one or more
embodiments.
[0007] FIG. 4A through FIG. 4D illustrate operations for forming
the gate dielectric layer according to aspects of the present
disclosure in one or more embodiments.
[0008] FIG. 5A through FIG. 5J illustrate a multi-gate
semiconductor device at various fabrication stages constructed
according to aspects of the present disclosure in one or more
embodiments.
[0009] FIG. 6A through FIG. 6E are cross-sectional views of the
multi-gate semiconductor device according to aspects of the present
disclosure in one or more embodiments.
[0010] FIG. 7A through FIG. 7K illustrate a multi-gate
semiconductor device at various fabrication stages constructed
according to aspects of the present disclosure in one or more
embodiments.
[0011] FIG. 8A through FIG. 8K illustrate a multi-gate
semiconductor device at various fabrication stages constructed
according to aspects of the present disclosure in one or more
embodiments.
[0012] FIG. 9A through FIG. 9D are cross-sectional views of the
multi-gate semiconductor device according to aspects of the present
disclosure in one or more embodiments.
[0013] FIG. 10A through FIG. 10O illustrate a multi-gate
semiconductor device at various fabrication stages constructed
according to aspects of the present disclosure in one or more
embodiments.
[0014] FIG. 11A through FIG. 11D are cross-sectional views of the
multi-gate semiconductor device according to aspects of the present
disclosure in one or more embodiments.
[0015] FIG. 12 through FIG. 14 illustrate a multi-gate
semiconductor device at various fabrication stages constructed
according to aspects of the present disclosure in one or more
embodiments.
DETAILED DESCRIPTION
[0016] The following disclosure provides many different
embodiments, or examples, for implementing different features of
the provided subject matter. Specific examples of components and
arrangements are described below to simplify the present
disclosure. These are, of course, merely examples and are not
intended to be limiting. For example, the formation of a first
feature over or on a second feature in the description that follows
may include embodiments in which the first and second features are
formed in direct contact, and may also include embodiments in which
additional features may be formed between the first and second
features, such that the first and second features may not be in
direct contact. In addition, the present disclosure may repeat
reference numerals and/or letters in the various examples. This
repetition is for the purpose of simplicity and clarity and does
not in itself dictate a relationship between the various
embodiments and/or configurations discussed.
[0017] Further, spatially relative terms, such as "beneath,"
"below," "lower," "above," "upper", "on" and the like, may be used
herein for ease of description to describe one element or feature's
relationship to another element(s) or feature(s) as illustrated in
the figures. The spatially relative terms are intended to encompass
different orientations of the device in use or operation in
addition to the orientation depicted in the figures. The apparatus
may be otherwise oriented (rotated 90 degrees or at other
orientations) and the spatially relative descriptors used herein
may likewise be interpreted accordingly.
[0018] As used herein, the terms such as "first", "second" and
"third" describe various elements, components, regions, layers
and/or sections, these elements, components, regions, layers and/or
sections should not be limited by these terms. These terms may be
only used to distinguish one element, component, region, layer or
section from another. The terms such as "first", "second" and
"third" when used herein do not imply a sequence or order unless
clearly indicated by the context.
[0019] As used herein, the terms "approximately," "substantially,"
"substantial" and "about" are used to describe and account for
small variations. When used in conjunction with an event or
circumstance, the terms can refer to instances in which the event
or circumstance occurs precisely as well as instances in which the
event or circumstance occurs to a close approximation. For example,
when used in conjunction with a numerical value, the terms can
refer to a range of variation of less than or equal to .+-.10% of
that numerical value, such as less than or equal to .+-.15%, less
than or equal to .+-.14%, less than or equal to .+-.3%, less than
or equal to .+-.2%, less than or equal to .+-.1%, less than or
equal to .+-.0.5%, less than or equal to .+-.0.1%, or less than or
equal to .+-.0.05%. For example, two numerical values can be deemed
to be "substantially" the same or equal if a difference between the
values is less than or equal to .+-.10% of an average of the
values, such as less than or equal to .+-.5%, less than or equal to
.+-.4%, less than or equal to .+-.3%, less than or equal to .+-.2%,
less than or equal to .+-.1%, less than or equal to .+-.0.5%, less
than or equal to .+-.0.1%, or less than or equal to .+-.0.05%. For
example, "substantially" parallel can refer to a range of angular
variation relative to 0.degree. that is less than or equal to
.+-.10.degree., such as less than or equal to .+-.5.degree., less
than or equal to .+-.4.degree., less than or equal to
.+-.3.degree., less than or equal to .+-.2.degree., less than or
equal to .+-.1.degree., less than or equal to .+-.0.5.degree., less
than or equal to .+-.0.1.degree., or less than or equal to
.+-.0.05.degree.. For example, "substantially" perpendicular can
refer to a range of angular variation relative to 90.degree. that
is less than or equal to .+-.10.degree., such as less than or equal
to .+-.5.degree., less than or equal to .+-.4.degree., less than or
equal to .+-.3.degree., less than or equal to .+-.2.degree., less
than or equal to .+-.1.degree., less than or equal to
.+-.0.5.degree., less than or equal to .+-.0.1.degree., or less
than or equal to .+-.0.05.degree..
[0020] The gate all around (GAA) transistor structures may be
patterned by any suitable method. For example, the structures may
be patterned using one or more photolithography processes,
including double-patterning or multi-patterning processes.
Generally, double-patterning or multi-patterning processes combine
photolithography and self-aligned processes, allowing patterns to
be created that have, for example, pitches smaller than what is
otherwise obtainable using a single, direct photolithography
process. For example, in one embodiment, a dummy layer is formed
over a substrate and patterned using a photolithography process.
Spacers are formed alongside the patterned dummy layer using a
self-aligned process. The dummy layer is then removed, and the
remaining spacers may then be used to pattern the GAA
structure.
[0021] It is also noted that the present disclosure presents
embodiments in the form of multi-gate transistors or fin-type
multi-gate transistors referred to herein as FinFET devices. The
FinFET devices may be GAA devices, Omega-gate (a-gate) devices,
Pi-gate (H-gate) devices, dual-gate devices, tri-gate devices, bulk
devices, silicon-on-insulator (SOI) devices, and/or other
configurations. One of ordinary skill may recognize other examples
of semiconductor devices that may benefit from aspects of the
present disclosure.
[0022] FIG. 1 is a flow chart representing a method for forming a
multi-gate semiconductor device 10 according to aspects of the
present disclosure. The method for forming the multi-gate
semiconductor device 10 includes an operation 102, providing a
substrate including at least one fin structure. The method for
forming the multi-gate semiconductor device 10 further includes an
operation 104, disposing a dummy gate structure over the fin
structure and the substrate. The method for forming the multi-gate
semiconductor device 10 further includes an operation 106,
disposing a spacer over side wails of the dummy gate structure,
wherein portions of the fin structure are exposed from the dummy
gate structure and the spacer. The method for forming the
multi-gate semiconductor device 10 further includes an operation
108, forming a source/drain region in the portions of the fin
structure exposed from the dummy gate structure and the spacer. The
method for forming the multi-gate semiconductor device 10 further
includes an operation 110, disposing a dielectric structure over
the substrate. The method for forming the multi-gate semiconductor
device 10 further includes an operation 112, removing the dummy
gate structure to form a gate trench in the dielectric structure.
The method for forming the multi-gate semiconductor device 10
further includes an operation 114, disposing at least a gate
dielectric layer over a bottom of the gate trench after removing
the dummy gate structure, wherein the spacer is exposed from
sidewalls of the gate trench. The method for forming the multi-gate
semiconductor device 10 further includes an operation 116,
disposing a gate conductive structure in the gate trench, wherein
sidewalls of the gate conductive structure are in contact with the
spacer. The method for forming the multi-gate semiconductor device
10 will be further described according to one or more embodiments.
It should be noted that the operations of the method for forming
the multi-gate semiconductor device 10 may be rearranged or
otherwise modified within the scope of the various aspects. It is
further noted that additional processes may be provided before,
during, and after the method 10, and that some other processes may
only be briefly described herein. Thus other implementations are
possible within the scope of the various aspects described
herein.
[0023] FIG. 2 is a flow chart representing a method for forming a
multi-gate semiconductor device 20 according to aspects of the
present disclosure. The method for forming the multi-gate
semiconductor device 20 includes an operation 202, providing a
substrate including at least one fin structure. The method for
forming the multi-gate semiconductor device 20 further includes an
operation 204, disposing a sacrificial insulating structure over
the fin structure and the substrate. The method for forming the
multi-gate semiconductor device 20 further includes an operation
206, forming a first gate trench in the sacrificial insulating
structure, wherein a portion of the fin structure is exposed from
the first gate trench, The method for forming the multi-gate
semiconductor device 20 further includes an operation 208,
disposing a gate dielectric layer over the fin structure and
sidewalls of the first gate trench. The method for forming the
multi-gate semiconductor device 20 further includes an operation
210, disposing a first dummy gate structure in the first gate
trench. The method for forming the multi-gate semiconductor device
20 further includes an operation 212, removing the sacrificial
insulating structure and a portion of the gate dielectric layer to
exposed sidewalls of the first dummy gate structure and the fin
structure. The method for forming the multi-gate semiconductor
device 20 further includes an operation 214, disposing an
insulating spacer over the sidewalls of the first dummy gate
structure, wherein portions of the fin structure are exposed from
the insulating spacer. The method for forming the multi-gate
semiconductor device 20 further includes an operation 216, removing
the first dummy gate structure to form a second gate trench. The
method for forming the multi-gate semiconductor device 20 further
includes an operation 218, disposing a gate conductive structure in
the second gate trench. The method for forming the multi-gate
semiconductor device 20 will be further described according to one
or more embodiments. It should be noted that the operations of the
method for forming the multi-gate semiconductor device 20 may be
rearranged or otherwise modified within the scope of the various
aspects. It is further noted that additional processes may be
provided before, during, and after the method 20, and that some
other processes may only be briefly described herein. Thus other
implementations are possible within the scope of the various
aspects described herein.
[0024] FIG. 3A through FIG. 3N are drawings illustrating a
multi-gate semiconductor device 300 at various fabrication stages
constructed according to aspects of the present disclosure in one
or more embodiments. Referring to FIG. 3A, a substrate 302 is
provided. In some embodiments, the substrate 302 may be a
semiconductor substrate such as a silicon substrate. The substrate
302 may also include other semiconductors such as germanium (Ge),
silicon carbide (SiC), silicon germanium (SiGe), or diamond.
Alternatively, the substrate 302 may include a compound
semiconductor and/or an alloy semiconductor. The substrate 302 may
include various layers, including conductive or insulating layers
formed on a semiconductor substrate. The substrate 302 may include
various doping configurations depending on design requirements as
is known in the art. For example, different doping profiles (e.g.,
n wells, p wells) may be formed on the substrate 302 in regions
designed for different device types (e.g., n-type field effect
transistors (NFET), p-type field effect transistors (PFET)). The
suitable doping may include ion implantation of dopants and/or
diffusion processes. The substrate 302 typically has isolation
features (e.g., shallow trench isolation (STI) features) (not
shown) interposing the regions providing different device types.
Further, the substrate 302 may optionally include an epitaxial
layer (epi-layer), may be strained for performance enhancement, may
include a SOI structure, and/or have other suitable enhancement
features. A stack including semiconductor layers are formed over
the substrate 302. In some embodiments, a strain relaxed buffer
(SRB) layer (not shown) can be formed over the substrate 302. The
SRB layer may be different in composition from the substrate 302 in
order to create lattice strain at the interface with the substrate
302. For example, in some embodiments, the substrate 302 includes
silicon and is substantially free of germanium while the SRB layer
includes SiGe.
[0025] Still referring to FIG. 3A, a stack including semiconductor
layers are formed over the substrate 302. In embodiments that
include an SRB layer disposed on the substrate 302, the stack of
semiconductor layers may be disposed on the SRB layer. The stack of
semiconductor layers may include alternating layers of different
compositions. For example, in some embodiments, the stack includes
semiconductor layers 304 of a first composition alternating with
semiconductor layers 306 of a second composition. By way of
example, growth of the layers of the stack may be performed by a
molecular beam epitaxy (MBE) process, a metalorganic chemical vapor
deposition (MOCVD) process, and/or other suitable epitaxial growth
processes. Although five semiconductor layers 304 and five
semiconductor layers 306 are shown, it is understood that the stack
may include any number of layers of any suitable composition with
various examples including between 2 and 10 semiconductor layer 304
and between 2 and 10 semiconductor layers 306. As explained below,
the different compositions of the layers in the stack (e.g.,
semiconductor layers 304 and semiconductor layers 306) may be used
to selectively process some of the layers. Accordingly, the
compositions may have different oxidation rates, etchant
sensitivity, and/or other differing properties. The semiconductor
layers 304 and 306 may have thicknesses chosen based on device
performance considerations. In some embodiments, the semiconductor
layers 304 are substantially uniform in thickness, and the
semiconductor layers 306 are substantially uniform in
thickness.
[0026] In some embodiments, either of the semiconductor layers 304
and 306 may include Si. In some embodiments, either of the
semiconductor layers 304 and 306 may include other materials such
as Ge, a compound semiconductor such as SiC, gallium arsenide
(GaAs), gallium phosphide (GaP), indium phosphide (InP), indium
arsenide (InAs), and/or indium antimonide (InSb), an alloy
semiconductor such as SiGe, GaAsP, AlInAs, AlGaAs, InGaAs, GaInP,
and/or GaInAsP, or combinations thereof. In some embodiments, the
semiconductor layers 304 and 306 may be undoped or substantially
dopant-free, where for example, no doping is performed during the
epitaxial growth process. Alternatively, the semiconductor layers
306 may be doped. For example, the semiconductor layers 304 or 306
may be doped with a p-type dopant such as boron (B), aluminum (Al),
In, and Ga for forming a p-type channel, or an n-type dopant such
as P, As, Sb, for forming an n-type channel.
[0027] Referring back to FIG. 3A, at least one fin structure 308 is
formed over the substrate 302 from the stack of semiconductor
layers 304/306. The fin structure 308 may be fabricated using
suitable operations including photolithography and etch operations.
In some embodiments, forming the fin structure 308 may further
include a trim process to decrease the width and/or the height of
the fin structure 308. The trim process may include wet or dry
etching processes. The height and width of the fin structure 308
may be chosen based on device performance considerations. Further,
the fin structure 308 can be extended along a first direction D1 as
shown in FIG. 3A. Accordingly, the substrate 302 including the at
least one fin structure 308 is provided according to operation 102.
Further, in some embodiments, a liner 309 can be formed over the
fin structure 308 and the substrate 302.
[0028] Still referring to FIG. 3A, a dummy gate structure 310 is
disposed over the fin structure 308 and the substrate 302 according
to operation 104. The dummy gate structure 310 may be replaced at a
later processing stage by a high-K dielectric layer (HK) and metal
gate electrode (MG) as discussed below. In some embodiments, the
dummy gate structure 310 is formed over the substrate 302 and
extended along a second direction D2, which is not parallel with
the first direction D1. Additionally, the first direction D1 and
the second direction D2 are in the same plane. The dummy gate
structure 310 is at least partially disposed over the fin structure
308, and a portion of the fin structure 308 underlying the dummy
gate structure 310 may be referred to as the channel region. The
dummy gate structure 310 may also define a source/drain region of
the fin structure 308, for example, as portions of the fin
structure 308 adjacent to and on opposing sides of the channel
region. In some embodiments, the dummy gate structure 310 can
include at least a polysilicon layer and a patterned hard mask for
defining the dummy gate structure.
[0029] Referring to FIGS. 3A and 3B, a spacer 320/322 is disposed
over sidewalls of the dummy gate structure 310, and portions of the
fin structure 308 are exposed from the dummy gate structure 310 and
the spacer 320/322 according to operation 106. In some embodiments,
the spacer 320 includes a conductive material and the spacer 322
includes an insulating material. For example but not limited to,
the spacer 320 can include metal or metal nitride. In some
embodiments, a conductive layer is conformally disposed over the
dummy gate structure 310, the fin structure 308 and the substrate
302. And a suitable etching operation such as dry etching operation
is performed to remove portions of the conductive layer to form the
spacer 320. As shown in FIG. 3A, the sidewalls of the dummy gate
structure 310 is covered by the spacer 320 while the portions of
the fin structure 308 and the substrate 302 are exposed from the
spacer 320. In some embodiments, portions of the liner 309 can be
removed after forming the spacer 320. Next, an insulating layer is
conformally formed over the spacer 320, the dummy gate structure
310 and the exposed fin structure 308. In some embodiments, the
insulating layer includes one or more insulating material such as
silicon nitride (SiN), silicon oxide (SiO), silicon carbide (SiC),
silicon oxycarbide (SiOC), silicon oxycarbon nitride (SiOCN), other
materials, or a combination thereof. And suitable etching operation
such as dry etching operation is performed to remove portions of
the insulating layer to form the spacer 322 over the spacer 320 as
shown in FIG. 3B. Briefly speaking, the portions of the fin
structure 308 are exposed from the dummy gate structure 310 and the
spacer 320/322 according to operation 106 as shown in FIG. 3B.
However, in some embodiments, formation of the spacer 320 can be
ignored. That is, the insulating spacer 322 is formed to cover the
sidewalls of the dummy gate structure 310.
[0030] Referring to FIG. 3C, then, portions of the fin structure
308 exposed from the spacer 320/322, such as portions of the
semiconductor layers 306 in the fin structure 308 exposed from the
spacer 320/322 are removed in some embodiments. Thereby a plurality
of notches 308n is formed in the fin structure 308 as shown in FIG.
3C. In some embodiments, the semiconductor layers 304 are exposed
from a top and a bottom of the notch 308n while the semiconductor
layer 306 is exposed from a sidewall of the notch 308n. Referring
to FIG. 3D, another insulating layer 324 is formed over the
substrate 302. In some embodiments, the insulating layer 324
includes one or more insulating material such as SiN, SiO, SiC,
SiOC, SiOCN, other materials, or a combination thereof. Further,
the insulating material is different from the insulating material
for forming the spacer 322 in some embodiments.
[0031] Subsequently, a suitable etching operation is performed to
remove portions of the insulating layer 324, and thus a plurality
of inner spacers 326 is formed in the notches 308n as shown in FIG.
3E. And the portions of the fin structure 308 are exposed again
from the top and the bottom of the notches 308n while the inner
spacers 326 are exposed from the sidewalls of the notches 308n. In
other words, the semiconductor layers 306 are enclosed by the
semiconductor layers 304 and the inner spacers 326 while the
semiconductor layers 304 are exposed.
[0032] Referring to FIG. 3F, a source/drain region 330 is formed in
the portions of the fin structure 308 exposed from the dummy gate
structure 310 and the spacers 320/322/326 according to operation
108. As shown in FIG. 3F, the source/drain region 330 wraps the
exposed portions of the fin structure 308, that are the exposed
portions of the semiconductor layers 304. In some embodiments, the
source/drawn regions 330 may be formed by performing an epitaxial
growth operation that provides an epitaxy material wrapping the
exposed portions of the semiconductor layer 304 of the fin
structure 308. In various embodiments, the source/drain regions 330
may include Ge, Si, GaAs, AlGaAs, SiGe, GaAsP, SiP, or other
suitable material. In some embodiments, the source/drain regions
330 may be in-situ doped during the epi process. For example, in
some embodiments, the source/drain regions 330 may be doped with
boron. In some embodiments, the source/drain regions 330 may be
doped with carbon to form Si:C source/drain regions, phosphorous to
form Si:P source/drain regions, or both carbon and phosphorous to
form SiCP source/drain regions. In some embodiments, the
source/drain regions 330 are not in-situ doped, and instead an
implantation process is performed to dope the source/drain regions
330.
[0033] Referring to FIG. 3G, a dielectric structure 340 is disposed
over the substrate 302 according to operation 110. In some
embodiments, the dielectric structure 340 can include an etch-stop
layer (e.g., a contact etch stop layer (CESL)) 342 and various
dielectric layers (e.g., an inter-layer dielectric (ILD) layer) 344
formed on the substrate 302 after forming the source/drain regions
310. In some embodiments, the CESL 342 includes a SiN layer, a SiCN
layer, a SiON layer, and/or other materials known in the art. In
some embodiments, the ILD layer 344 includes materials such as
tetraethylorthosilicate (TEOS) oxide, un-doped silicate glass, or
doped silicon oxide such as borophosphosilicate glass (BPSG), fused
silica glass (FSG), phosphosilicate glass (PSG), boron doped
silicon glass (BSG), and/or other suitable dielectric materials. In
some embodiments, in an embodiment, after the CESL 342 and the ILL)
layer 344 are deposited, a planarization process, such as a
chemical mechanical planarization (CMP) operation, may be performed
to form the dielectric structure 340 and to expose a top surface of
the dummy gate structure 310 as shown in FIG. 3G. In some
embodiments, the planarization is performed to expose at least a
top surface of the polysilicon layer of the dummy gate structure
310.
[0034] Referring to FIG. 3H, the dummy gate structure 310 is then
removed to form a gate trench 312 in the dielectric structure 340
according to operation 112. As shown in FIG. 3H, the spacer 320 is
exposed from sidewalls of the gate trench 312, and the fin
structure 308 is exposed from the gate trench 312. Further, the
liner layer 309 disposed over the fin structure 308 is removed
subsequently. Next, the semiconductor layers 306 exposed from the
gate trench 312 are removed. Accordingly, a plurality of wires
including the semiconductor layers 304 is obtained as shown in FIG.
3H. In some embodiments, the wires including the semiconductor
layers 304 serves as channel regions. In some embodiments, the
wires can be slightly etched to obtain various desirable dimensions
and shapes, and the various desired dimensions and shapes may be
chosen based on device performance considerations.
[0035] Referring to FIG. 3I, a barrier layer 314, such as a
self-assembled monolayer (SAM) is formed over the sidewalls of the
gate trench 312. The SAM includes a head group, which is one end of
the molecule. Selection of the head group will depend on the
application of the SAM. In some embodiment, the SAM over the spacer
320 including conductive material may include the head group having
organosulfur compound. In some embodiment, the SAM over the spacer
320 may include thiol head group such as mono(di)thiols. In some
embodiment, the SAM over the inner spacer 326 including insulating
material may include silane head group such as octyltrichlorosilane
(OTS) or n-octadecyltrichlorosilane (ODTS). In some embodiment, the
SAM over the inner spacer 326 may include Hexamethyldisilazane
(HMDS). As shown in FIG. 3I, the material of the barrier layer 314
can be chosen such that the harrier layer 314 is selectively formed
to cover the spacer 320 exposed from the gate trench 312 while the
inner spacer 326 and at least a portion of fin structure 308, such
as a portion of each semiconductor layer 304, are exposed from the
gate trench 312. However, in those embodiments that the spacer 320
is ignored, the insulating spacer 322 and the inner spacer 326 may
be exposed from the gate trench 312. In those embodiments, the
material of the barrier layer 314 can be chosen such that the
barrier layer 314 is selectively formed to cover the spacer 322 and
the inner spacer 326 exposed from the gate trench 312 while the at
least a portion of fin structure 308 is exposed from the gate
trench 312, as shown in FIG. 12.
[0036] Referring to FIG. 3J, an interfacial layer (IL) 316 is
formed over the semiconductor layers 304 exposed from the barrier
layer 314. In some embodiments, the IL 316 may include an
oxide-containing material such as SiO or SiON. In some embodiments,
the IL 316 wraps around the exposed semiconductor layers 304. More
importantly, since the spacer 320 is covered by the barrier layer
314, a surface not suitable for forming dielectric material is
rendered by the barrier layer 314. Accordingly, the IL 316 wraps
around the exposed semiconductor layers 304 while the barrier layer
314 sill still exposed from the gate trench 312 after forming the
IL 316.
[0037] Still referring to FIG. 3J, after forming the IL 316, a gate
dielectric layer 318 is formed. As mentioned above, since the
spacer 320 is covered by the barrier layer 314, a surface not
suitable for forming the dielectric material is rendered by the
barrier layer 314. Accordingly, the gate dielectric layer 318 wraps
around the exposed semiconductor layers 304 and over the IL 316
while the barrier layer 314 sill still exposed from the gate trench
312 after forming the gate dielectric layer 318. In some
embodiments, the gate dielectric layer 318 includes a high-k
dielectric material having a high dielectric constant, for example,
greater than that of thermal silicon oxide (.sup..about.3.9). The
high-k dielectric material may include hafnium oxide (HfO.sub.2),
zirconium oxide (ZrO.sub.2), lanthanum oxide (La.sub.2O.sub.3),
aluminum oxide (Al.sub.2O.sub.3), titanium oxide (TiO.sub.2),
yttrium oxide (Y.sub.2O.sub.3), strontium titanate (SrTiO.sub.3),
hafnium oxynitride (HfOxNy), other suitable metal-oxides, or
combinations thereof.
[0038] However, in those embodiments that the spacer 320 is
ignored, the IL 316 and the gate dielectric layer 318 are formed
over the fin structures 304 exposed from the gate trench 312. As
mentioned above, since the spacer 322 and the inner spacer 326 are
covered by the barrier layer 314, a surface not suitable for
forming the dielectric material is rendered by the barrier layer
314 as shown in FIG. 13.
[0039] Referring to FIG. 3K, after forming the gate dielectric
layer 318, the barrier layer 314 is removed from the gate trench
312. In some embodiments, the barrier layer 314 can be removed by,
for example but not limited to, tetramethylammonium hydroxide
(TMAH), ammonia solution, or cyclic oxidation-DHF clean.
Consequently, the gate dielectric layer 318 is disposed over a
bottom of the gate trench 312 and the semiconductor layers 304,
while the spacer 320 is exposed again from the sidewalls of the
gate trench 312 according to operation 114. In some embodiments,
the spacer 320 can be removed after removing the barrier layer 314,
but the disclosure is not limited to this.
[0040] Referring to FIG. 3L, a gate conductive structure 350 is
then disposed in the gate trench 312 according to operation 116. In
some embodiments, the gate conductive structure 350 is formed on
the gate dielectric layer 318. More importantly, sidewalls of the
gate conductive structure 350 are in contact with the spacer 320 as
shown in FIG. 3L. In some embodiments, the gate conductive
structure 350 can include at least a harrier metal layer 352, a
work functional metal layer 354 and a gap-filling metal layer 356.
The barrier metal layer 352 can include, for example hut not
limited to, TiN. The work function metal layer 354 can include a
single layer of TiN, TaN, TaAlC, TiC, TaC, Co, Al, TiAl, HfTi,
TiSi, TaSi or TiAlC, or a multilayer of two or more of these
materials, but not limited to this. For the n-channel FET, one or
more of TaN, TaAlC, TiN, TiC, Co, TiAl, HfTi, TiSi and TaSi is used
as the work function metal layer 354, and for the p-channel FET,
one or more of TiAlC, Al, TiAl, TaN, TaAlC, TiN, TiC and Co is used
as the work function metal layer 354. In some embodiments, the
gap-filling metal layer 326 layers of conductive material, such as
Al, Cu, AlCu, or W, but is not limited by the above-mentioned
materials. Accordingly, the multi-gate semiconductor device 300 is
obtained as shown in FIG. 3L.
[0041] In some embodiments, the spacer 322 can be removed after
disposing the gate conductive structure 350, and thus a spacer
trench 328 is formed between the spacer 320 and the dielectric
structure 340 as shown in FIG. 3M. Subsequently, the spacer trench
328 can be sealed to form an air spacer 360 as shown in FIG. 3N. It
should be noted that the air spacer 360 can be selectively formed
to further reduce the Miller capacitance between the gate
electrodes and drain areas of the FET.
[0042] In some embodiments that the spacer 320 is ignored, the
spacer 322 is exposed in the gate trench 312 after removing barrier
layer 314. The gate conductive structure 350 is then formed in the
gate trench 312. Accordingly, the gate conductive structure 350,
such as the barrier metal layer 352 is contact with the spacer 322
as shown in FIG. 14.
[0043] FIG. 4A through FIG. 4D depict operations for forming the
gate dielectric layer according aspects of the present disclosure
in one or more embodiments. It should be noted that elements the
same in FIGS. 3A-3N and FIGS. 4A-4D are designated by the same
numerals and formed by similar operations. Further, elements the
same in FIGS. 3A-3N and FIGS. 4A-4D can include same materials.
Therefore, details for forming those elements are omitted in the
interest of brevity, and the differences are provided as following
description. Additionally, FIGS. 4A-4G are cross-sectional views of
a semiconductor device 300' taken along the first direction D1.
[0044] As shown in FIG. 4A, after removing the dummy gate structure
310 to form the gate trench 312 in the dielectric structure 340
according to operation 112, and after removing the semiconductor
layers 306 to form the wires, semiconductor re-growth operation can
be performed. Consequently, semiconductor layers 305 are formed
over the exposed semiconductor layers 304. The semiconductor layers
305 wrapping the wires/the semiconductor layers 304 respectively,
as shown in FIG. 4A. In some embodiments, the semiconductor layers
304 and the semiconductor layers 305 can include the same
semiconductor material. In some embodiments, the semiconductor
layers 304 and the semiconductor layers 305 can include different
semiconductor materials. Additionally, the spacer 320 and the inner
spacer 326 are exposed from the sidewalls of the gate trench 312,
as shown in FIG. 4A.
[0045] Referring to FIG. 4B, a barrier layer 314 such as a SAM is
formed over the spacer 320. Consequently, the spacer 320 that is
exposed from the sidewalls of the gate trench 312 is now covered by
the harrier layer 314 while the inner spacer 326 is still exposed.
Referring to FIG. 4C, the semiconductor layers 305 are removed
after forming the barrier layer 314. Consequently, the
semiconductor layers 304 of the fin structure 308 are exposed again
as shown in FIG. 4C.
[0046] Referring to FIG. 4D, an interfacial layer (IL) 316 and a
gate dielectric layer 318 are then sequentially formed over the
exposed semiconductor layers 304. The IL 316 and the gate
dielectric layer 318 are formed to wrap the semiconductor layers
304 but not the sidewalls of the gate trench 312 because the
barrier layer 314 provides a surface less suitable for forming
dielectric material. Thereafter, the barrier layer 314 is removed
from the gate trench 312. Accordingly, the gate dielectric layer
318 is disposed over a bottom of the gate trench 312 and the
semiconductor layers 304, while the spacer 320/326 are exposed from
the sidewalls of the gate trench 312 according to operation 114.
And operations such as 116 can be performed to form the gate
conductive 350 structure as mentioned above.
[0047] FIG. 5A through FIG. 5J illustrates a multi-gate
semiconductor device 400 at various fabrication stages constructed
according to aspects of the present disclosure in one or more
embodiments. It should be noted that elements the same in FIGS.
3A-3N and FIGS. 5A-5J are designated by the same numerals. Further,
elements the same in FIGS. 3A-3N and FIGS. 5A-5J can include same
materials, thus those details for the materials are omitted in the
interest of brevity.
[0048] Referring to FIG. 5A, a substrate 402 is provided. In some
embodiments, a SRB layer (not shown) can be formed over the
substrate 402. A fin structure 408 including semiconductor layers
is formed over the SRB layer or the substrate 402. The fin
structure 408 may include alternating layers of different
compositions. For example, in some embodiments, the fin structure
408 includes semiconductor layers 404 of a first composition
alternating with semiconductor layers 406 of a second composition.
As mentioned above, the different compositions of the layers in the
fin structure 408 (e.g., semiconductor layers 404 and semiconductor
layers 406) may be used to selectively process some of the layers.
Accordingly, the compositions may have different oxidation rates,
etchant sensitivity, and/or other differing properties. The
semiconductor layers 404 and 406 may have thicknesses chosen based
on device performance considerations. As mentioned above, height
and width of the fin structure 408 may be chosen based on device
performance considerations. Further, the fin structure 408 can be
extended along a first direction D1 as shown in FIG. 5A.
Accordingly, the substrate 402 including the at least one fin
structure 408 is provided according to operation 102. Further, in
some embodiments, a liner 409 can be formed over the fin structure
408 and the substrate 402 as shown in FIG. 5A.
[0049] Referring to FIGS. 5A and 5B, a dummy gate structure 410 is
disposed over the fin structure 408 and the substrate 402 according
to operation 104. In some embodiments, the dummy gate structure 410
is formed over the substrate 402 and is extended along a second
direction D2, which is not parallel with the first direction D1.
Additionally, the first direction D1 and the second direction D2
are in the same plane. The dummy gate structure 410 is at least
partially disposed over the fin structure 408. As mentioned above,
the dummy gate structure 410 can include at least a polysilicon
layer and a patterned hard mask for defining the dummy gate
structure. Thereafter, a spacer 420/422 is disposed over sidewalls
of the dummy gate structure 410, and portions of the fin structure
408 are exposed from the dummy gate structure 410 and the spacer
420/422 according to operation 106. In some embodiments, both of
the spacer 420 and the spacer 422 include an insulating materials.
However, the spacer 420 and the spacer 422 include insulating
materials different from each other. For example but not limited
to, the spacer 420 includes SiO while the spacer 422 include SiN,
but not limited to this. In some embodiments, an insulating layer
is conformally disposed over the dummy gate structure 410, the fin
structure 408 and the substrate 402. And a suitable etching
operation such as dry etching operation is performed to remove
portions of the insulating layer to form the spacer 420. As shown
in FIG. 5A, the sidewalls of the dummy gate structure 410 is
covered by the spacer 420 while portions of the fin structure 408
and the substrate 402 are exposed from the dummy gate structure 410
and the spacer 420. Further, liner 409 is exposed from the dummy
gate structure 410 and the spacer 420.
[0050] Referring to FIG. 5B, after forming the spacer 420, another
insulating layer is conformally formed over the spacer 420, the
dummy gate structure 410 and the exposed fin structure 408 and
followed by suitable etching operation such as dry etching
operation. Consequently, portions of the insulating layer are
removed to form the spacer 422. As shown in FIG. 5B, the spacer 420
over the sidewalls of the dummy gate structure 410 is now covered
by the spacer 422 while the portions of the fin structure 408 and
the substrate 402 are exposed from the spacer 422. In some
embodiments, the liner 409 can be removed during or after forming
the spacer 422. Briefly speaking, the portions of the fin structure
408 are exposed from the dummy gate structure 410 and the spacer
420/422 according to operation 106 as shown in FIG. 5B.
[0051] Referring to FIG. 5C, the portions of the fin structure 408
exposed from the spacer 420/422, that are portions of the
semiconductor layers 406 in the fin structure 408 exposed from the
spacer 420/422 are removed in some embodiments. Thereby a plurality
of notches (not shown) is formed in the fin structure 408 as shown
in FIG. 3C. In some embodiments, a plurality of inner spacers 424
is respectively disposed in the notches. Since the operations for
forming the inner spacers 424 are similar to those shown in FIGS.
3C-3D, details are omitted for brevity. Next, a source/drain region
430 is formed in the portions of the fin structure 408 exposed from
the dummy gate structure 410 and the spacers 420/422/424 according
to operation 108. As shown in FIG. 5C, the source/drain region 430
wraps the exposed portions of the fin structure 408, that are the
exposed portions of the semiconductor layers 404.
[0052] Referring to FIG. 5D, a dielectric structure 440 is then
disposed over the substrate 402 according to operation 110. As
mentioned above, the dielectric structure 440 can include an
etch-stop layer (e.g., CESL 442) and various dielectric layers
(e.g., an ILD layer) 444. In some embodiments, after the CESL 442
and the ILD layer 444 are deposited, a planarization operation,
such as a CMP operation, may be performed to form the dielectric
structure 440 and to expose a top surface of the dummy gate
structure 410 as shown in FIG. 5D. In some embodiments, the
planarization operation is performed to expose at least a top
surface of the polysilicon layer of the dummy gate structure.
[0053] Referring to FIGS. 5E-5F, the spacer 420 is removed to form
a spacer trench 426 and followed by forming a spacer 428 in the
spacer trench 426 in some embodiments. The spacer 428 includes a
conductive material. For example but not limited to, the spacer 428
can include metal or metal nitride. In other words, the insulating
spacer 420 is replaced with the conductive spacer 428 in some
embodiments.
[0054] Referring to FIG. 5G, the dummy gate structure 410 is
removed to form a gate trench 412 in the dielectric structure 440
after forming the spacer 428 according to operation 112. As shown
in FIG. 5G, the spacer 428 is exposed from sidewalls of the gate
trench 412, and the fin structure 408 is exposed from the gate
trench 412. Further, the liner 409 disposed over the fin structure
408 can be removed subsequently. Next, the semiconductor layers 406
exposed from the gate trench 412 are removed. Accordingly, a
plurality of wires including the semiconductor layers 404 is
obtained as shown in FIG. 5G. In some embodiments, the wires
including the semiconductor layers 404 serves as channel regions.
In some embodiments, the wires can be slightly etched to obtain
various desirable dimensions and shapes, and the various desired
dimensions and shapes may be chosen based on device performance
considerations.
[0055] Referring to FIG. 5H, a barrier layer such as the
aforementioned SAM can be formed over the sidewalls of the gate
trench 412, and followed by sequentially forming an IL 416 and a
gate dielectric layer 418. Since operations for forming the barrier
layer, the IL 416 and the gate dielectric later 418 are similar to
those shown in FIGS. 3I-3K or FIGS. 4A-4D, those details are
omitted for brevity. And the barrier layer is removed after forming
the gate dielectric layer 418.
[0056] Referring to FIG. 5I, a gate conductive structure 450 is
then disposed in the gate trench 412 according to operation 116. In
some embodiments, the gate conductive structure 450 is formed on
the gate dielectric layer 418 to surround each semiconductor layers
404. In some embodiments, the gate conductive structure 450 can
include at least a barrier metal layer 452, a work functional metal
layer 454 and a gap-filling layer 456. Accordingly, the multi-gate
semiconductor device 400 is obtained as shown in FIG. 5I. More
importantly, sidewalls of the gate conductive structure 450 are in
contact with the spacer 428.
[0057] In some embodiments, the spacer 422 can be removed after
disposing the gate conductive structure 450, and thus a spacer
trench (not shown) is formed between the spacer 428 and the
dielectric structure 440. Subsequently, the spacer trench can be
sealed to form an air spacer 460 as shown in FIG. 5J. As mentioned
above, the air spacer 460 can be selectively formed to further
reduce the Miller capacitance between the gate electrodes and drain
areas of the FET.
[0058] FIG. 6A through FIG. 6E are cross-sectional views of the
multi-gate semiconductor device 300, 300' and 400 according to
aspects of the present disclosure in one or more embodiments. FIG.
6A is a cross-sectional views of the semiconductor device 300, 300'
and 400 taken along the first direction D1, FIG. 6B is a
cross-sectional view taken along line A1-A1' of FIG. 6A, FIG. 6C is
a cross-sectional view taken along line B1-B1' of FIG. 6A, FIG. 6D
is a cross-sectional view taken along line C1-C1' of FIG. 6A, and
FIG. 6E is a cross-sectional view taken along line D1-D1' of FIG.
6A. Referring to FIGS. 6A-6E, a multi-gate semiconductor device
300, 300' and 400 can be provided. The multi-gate semiconductor
device 300, 300' and 400 includes the substrate 302/402, the fin
structure 308/408 such as the stacked wire structure disposed over
the substrate 302/402, a gate wrapping the stacked wire structure,
and spacer disposed over two sidewalls of the gate. As shown in
FIGS. 6A-6E, the gate includes the gate conductive structure
350/450 and the gate dielectric layer 318/418 sandwiched between
the gate conductive structure 350/450 and the stacked wire
structure. As shown in FIG. 6B, portions of the semiconductor
layers 304/404 are sequentially wrapped by the IL 316/416, the gate
dielectric layer 318/418, and the barrier metal layer 352/452 of
the gate conductive structure 350/450. As shown in FIGS. 6C-6D,
another portions of the semiconductor layers 304/404 are spaced
apart from each other by the inner spacer 326/424. As shown in FIG.
6E, still another portions of the 304/404 are wrapped by the
source/drain region 330/430.
[0059] More importantly, the sidewalls of the gate conductive
structure 350/450, such as the barrier metal layer 352/452, are in
contact with the spacer 320/428, and the spacer 320/428 includes
the conductive material as shown in FIGS. 6A and 6B. In some
embodiments, the multi-gate semiconductor device 300/300'/400
further includes the insulating spacer 322/422, and the conductive
spacer 320/428 is sandwiched between the insulating spacer 322/422
and the gate conductive structure 350/450. In some embodiments, the
multi-pate semiconductor device 300/300'/400 further includes the
air spacer 360/460 for further reducing Miller capacitance.
[0060] FIG. 7A through FIG. 7K illustrates a multi-gate
semiconductor device at various fabrication stages constructed
according to aspects of the present disclosure in one or more
embodiments. It should be noted that elements the same in FIGS.
3A-3N and FIGS. 7A-7K can include same materials, thus those
details for the materials are omitted in the interest of
brevity.
[0061] Referring to FIG. 7A, a substrate 502 is provided. In some
embodiments, a SRB layer (not shown) can be formed over the
substrate 502. A fin structure 508 including semiconductor layers
is formed over the substrate 502 or the SRB layer. The fin
structure 508 may include alternating layers of different
compositions. For example, in some embodiments, the fin structure
508 includes semiconductor layers 504 of a first composition
alternating with semiconductor layers 506 of a second composition.
As mentioned above, the different compositions of the layers in the
fin structure 508 (e.g., semiconductor layers 504 and semiconductor
layers 506) may be used to selectively process some of the layers.
Accordingly, the compositions may have different oxidation rates,
etchant sensitivity, and/or other differing properties. Further,
the fin structure 508 can be extended along a first direction D1 as
shown in FIG. 7A. Accordingly, the substrate 502 including the at
least one fin structure 508 is provided according to operation 202.
Further, in some embodiments, a liner (not shown) can be formed
over the fin structure 508 and the substrate 502.
[0062] Still referring to FIG. 7A, a dummy gate structure 510a is
disposed over the fin structure 508 and the substrate 502. In some
embodiments, the dummy gate structure 510a is formed over the
substrate 502 and is extended along a second direction D2, which is
not parallel with the first direction D1. Additionally, the first
direction D1 and the second direction D2 are in the same plane. The
dummy gate structure 510a at least partially disposed over the fin
structure 508, and thus portions of the fin structure 508 are
exposed from the dummy gate structure 510a. Thereafter, an etching
rate modification is performed. In some embodiments, portions of
the fin structure 508 exposed from the dummy gate structure 510a
are doped, and thus doped regions 508d as shown in FIG. 7A. The
doped regions 508d include an etching rate lower than the rest
portion of the fin structures 508. In some embodiments, a
concentration of the doped regions 508d can be ranged from about
1.8E19 to about 8.16E15, but not limited to this. In some
embodiments, the concentration of the doped regions 508d is
inwardly reduced from a surface of the fin structure 508.
[0063] Referring to FIGS. 7B-7C, a sacrificial insulating structure
540 is disposed over the fin structure 508 and the substrate 502
according to operation 204. In some embodiments, the sacrificial
insulating structure 540 is formed over the substrate 502 and
followed by a planarization process, such as a CMP, thus a top
surface of the dummy gate structure 510a is exposed as shown in
FIG. 7B.
[0064] Next, the dummy gate structure 510a is removed to form a
gate trench 512a. Further, the semiconductor layers 506 exposed
from the gate trench 512a are then removed. Since the etching rate
of the doped regions 508d is modified to be lower as mentioned
above, removal of the semiconductor layers 506 can be stopped at
the doped regions 508d, as shown in FIG. 7C. Further, the liner
disposed over the fin structure 508 can be removed subsequently.
Accordingly, a plurality of wires including the semiconductor
layers 504 is obtained and exposed from the gate trench 512a as
shown in FIG. 7C. In other words, the gate trench 512a is formed in
the sacrificial insulating structure 520 with a portion of the fin
structure 508 being exposed from the gate trench 512a according to
operation 206.
[0065] Referring to FIG. 7D, an IL 516 is formed over the
semiconductor layers 504 and followed by forming a gate dielectric
layer 518 over the fin structure 508 and sidewalls of the gate
trench 512a according to operation 208. As shown in FIG. 7D, the IL
516 can be formed over surfaces of the semiconductor layers 504 and
506 in some embodiments. More importantly, the gate dielectric
layer 518 is formed to cover all surfaces exposed from the gate
trench 512a. Further, the gate dielectric layer 518 can include
high-k dielectric material as mentioned above.
[0066] Referring to FIGS. 7E-7F, a dummy gate structure 510b is
then formed in the gate trench 512a according to operation 210 and
followed by removing the sacrificial insulating structure 540
according to operation 212. As shown in FIG. 7E, the dummy gate
structure 510b is formed to fill the gate trench 512a, and a
planarization process, such as a CMP can be performed to remove
superfluous materials. Further, sidewalls of the dummy gate
structure 510b are in contact with the gate dielectric layer 518.
Next, at least a portion of the sacrificial insulating structure
540 is removed. More importantly, the gate dielectric layer 518
over the sidewalls of the dummy gate structure 510b is then
removed. Consequently, the sidewalls of the dummy gate structure
510b are exposed as shown in FIG. 7F. Further, portions of the fin
structure 508 are exposed from the dummy gate structure 510b while
another portions of the fin structure 508 is overlapped by the
dummy gate structure 510b. As mentioned above, the portions of the
fin structure 508 underlying the dummy gate structure 510b may be
referred to as the channel region.
[0067] Referring to FIG. 7G, portions of the fin structure 508 such
as portions of the semiconductor layers 506 exposed from the dummy
gate structure 510b are removed, thereby a plurality of notches
508n is formed in the fin structure 508 as shown in FIG. 7G. In
some embodiments, the semiconductor layers 504 are exposed from a
top and a bottom of the notches 508n while the IL 518 is exposed
from a sidewall of the notches 508n.
[0068] Referring to FIG. 7H, inner spacers 520 are then formed in
the notches 508n. The inner spacers 520 are formed not only in the
notches 508n, but also over the sidewalls of the dummy gate
structure 510b. Next, a spacer 522 is formed over the inner spacer
520. In some embodiments, the inner spacer 520 and the spacer 522
include the same insulating material. In some embodiments, the
inner spacer 520 and the spacer 522 include different insulating
materials. Briefly speaking, insulating spacer (including the inner
spacer 520 and the spacer 522) is disposed over the sidewalls of
the dummy gate structure 510b while portions of the fin structure
508 are exposed from the insulating spacer 520/522 according to
operation 214.
[0069] Referring to FIG. 7I, a source/drain region 530 is formed in
the exposed portions of the fin structure 508, such as the exposed
portions of the semiconductor layers 504. Referring to FIG. 7J, a
dielectric structure 542 is disposed over the substrate 502. As
mentioned above, the dielectric structure 542 can include an
etch-stop layer (e.g., CESL) (not shown) and various dielectric
layers (e.g., an ILD layer) (not shown). In some embodiments, after
the CESL and the ILD layer are deposited, a planarization process,
such as a CMP operation, may be performed to the dielectric
structure 542 and to expose a top surface of the dummy gate
structure 510b. Still referring to FIG. 7J, the dummy gate
structure 510b is removed to form a gate trench 512b in the
dielectric structure 542 after forming the dielectric structure 542
according to operation 216. As shown in FIG. 7J, the insulating
spacer, such as the inner spacer 520 is exposed from sidewalls of
the gate trench 512b. Also, the gate dielectric layer 518 is
exposed from the gate trench 512b.
[0070] Referring to FIG. 7K, a gate conductive structure 550 is
then disposed in the gate trench 512b according to operation 218.
In some embodiments, the gate conductive structure 550 is formed
over the gate dielectric layer 518. More importantly, sidewalls of
the gate conductive structure 550 are in contact with the spacer
520 as shown in FIG. 7K. In some embodiments, the gate structure
550 can include at least a barrier metal layer 552, a work
functional metal layer 554 and a gap-filling metal layer 556.
Accordingly, the multi-gate semiconductor device 500 is obtained as
shown in FIG. 7K. More importantly, sidewalls of the gate
conductive structure 550 are in contact with the spacer 520.
[0071] FIG. 8A through FIG. 8K illustrates a multi-gate
semiconductor device at various fabrication stages constructed
according to aspects of the present disclosure in one or more
embodiments. It should be noted that elements the same in FIGS.
3A-3N and FIGS. 8A-8K can include same materials, thus those
details for the materials are omitted in the interest of
brevity.
[0072] Referring to FIG. 8A, a substrate 602 is provided. In some
embodiments, a SRB layer (not shown) can be formed over the
substrate 602. A fin structure 608 including semiconductor layers
is formed over the substrate 602 or the SRB layer. The fin
structure 608 may include alternating layers of different
compositions. For example, in some embodiments, the fin structure
608 includes semiconductor layers 604 of a first composition
alternating with semiconductor layers 606 of a second composition.
As mentioned above, the semiconductor layers 604 and the
semiconductor layers 606 may be used to selectively process some of
the layers. Accordingly, the compositions may have different
oxidation rates, etchant sensitivity, and/or other differing
properties. Further, the fin structure 608 can be extended along a
first direction D1 as shown in FIG. 8A. Accordingly, the substrate
602 including the at least one fin structure 808 is provided
according to operation 202. Further, in some embodiments, a liner
(not shown) can be formed over the fin structure 608 and the
substrate 602.
[0073] Still referring to FIG. 8A, a dummy gate structure 610a is
disposed over the fin structure 608 and the substrate 602. In some
embodiments, the dummy gate structure 610a is formed over the
substrate 602 and is extended along a second direction D2, which is
not parallel with the first direction D1. Additionally, the first
direction D1 and the second direction D2 are in the same plane. The
dummy gate structure 610a at least partially disposed over the fin
structure 608, and thus portions of the fin structure 608 are
exposed from the dummy gate structure 610a. Thereafter, an etching
rate modification is performed. In some embodiments, doped regions
608d including an etching rate lower than the rest portions of the
fin structure 608 are formed. A conductive spacer 620 is then
formed over the substrate 602. In some embodiments, a conductive
layer is conformally disposed over the substrate 602, and followed
by a suitable etching operation such as dry etching operation. Thus
portions of the conductive layer are removed to form the spacer
620. As shown in FIG. 8A, the sidewalls of the dummy gate structure
610a is covered by the spacer 620 while portions of the fin
structure 608 and the substrate 602 are exposed from the spacer
620.
[0074] Referring to FIGS. 8B-8C, after forming the spacer 620, a
sacrificial insulating structure 640 is disposed over the fin
structure 608 and the substrate 602 according to operation 204. In
some embodiments, the sacrificial insulating structure 640 is
formed over the substrate 602 and followed by a planarization
process, such as a CMP, thus a top surface of the dummy gate
structure 610a is exposed as shown in FIG. 8B. Next, the dummy gate
structure 610a is removed to form a gate trench 612a. Further, the
liner disposed over the fin structure 608 can be removed
subsequently. Next, the semiconductor layers 606 exposed from the
gate trench 612a are then removed. Since the etching rate of the
doped regions 608d is modified to be lower as mentioned above,
removal of the semiconductor layers 606 can be stopped at the doped
regions 608d, as shown in FIG. 8C. Accordingly, a plurality of
wires including the semiconductor layers 604 is obtained and
exposed from the gate trench 612a as shown in FIG. 8C. In other
words, the gate trench 612a is formed in the sacrificial insulating
structure 620 with a portion of the fin structure 608 being exposed
from the gate trench 612a according to operation 206.
[0075] Referring to FIG. 8D, an IL 616 is formed over the
semiconductor layers 604 and followed by forming a gate dielectric
layer 618 over the fin structure 608 according to operation 208. In
some embodiments, a barrier layer (not shown) such as the
aforementioned SAM can be formed over the sidewalls of the gate
trench 612a, and followed by sequentially forming the IL 616 and
the gate dielectric layer 618. Since operations for forming the
barrier layer, the IL 616 and the gate dielectric later 618 are
similar to those shown in FIGS. 3I-3K or FIGS. 4A-4D, those details
are omitted for brevity. Accordingly, the gate dielectric layer 618
is formed over the semiconductor layers 604 while the spacer 620 is
still exposed from the sidewalls of the gate trench 612a as shown
in FIG. 8D.
[0076] Referring to FIGS. 8E-8F, a dummy gate structure 610b is
then formed in the gate trench 612a according to operation 210 and
followed by removing the sacrificial insulating structure 640
according to operation 212. As shown in FIG. 8E, the dummy gate
structure 610b is formed to fill the gate trench 612a, and a
planarization process, such as a CMP can be performed to remove
superfluous materials. Sidewalls of the dummy gate structure 610b
are in contact with the spacer 620. Next, at least a portion of the
sacrificial insulating structure 640 is removed. More importantly,
the spacer 620 is removed after removing the dummy insulating
structure 640. Consequently, sidewalls of the dummy gate structure
610b are exposed as shown in FIG. 8F. Further, portions of the fin
structure 608 are exposed from the dummy gate structure 610b while
another portions of the fin structure 608 is overlapped by the
dummy gate structure 610b. As mentioned above, the portions of the
fin structure 608 underlying the dummy gate structure 610b may be
referred to as the channel region. Still referring to Referring to
FIG. 8F, the portions of the fin structure 608 such as the portions
of the semiconductor layers 606 exposed from the dummy gate
structure 610b are removed, thereby a plurality of notch 608n is
formed in the fin structure 608. In some embodiments, the
semiconductor layers 604 are exposed from a top and a bottom of the
notch 608n while the IL 618 is exposed from a sidewall of the
notches 608n.
[0077] Referring to FIG. 8G, inner spacers 622 are then formed in
the notches 608n. The inner spacers 622 are formed not only in the
notches 608n, but also over the sidewalls of the dummy gate
structure 610b. Next, a spacer 624 is formed over the inner spacer
622. In some embodiments, the inner spacer 622 and the spacer 624
include the same insulating material, in some embodiments, the
inner spacer 622 and the spacer 624 include different insulating
materials. Briefly speaking, insulating spacer (including the inner
spacer 622 and the spacer 624) is disposed over the sidewalls of
the dummy gate structure 610b while portions of the fin structure
608 are exposed from the insulating spacer 622/624 according to
operation 214.
[0078] Referring to FIG. 8H, a source/drain region 630 is formed in
the portions of the fin structure 608 exposed from the dummy gate
structure 610b and the insulating spacers 622/624. As shown in FIG.
8H, the source/drain region 630 wraps the exposed portions of the
fin structure 608, such as the exposed portions of the
semiconductor layers 604.
[0079] Referring to FIG. 8I, a dielectric structure 642 is disposed
over the substrate 642. As mentioned above, the dielectric
structure 642 can include an etch-stop layer (e.g., CESL) (not
shown) and various dielectric layers (e.g., an ILD layer) (not
shown). In some embodiments, after the CESL and the HD layer are
deposited, a planarization process, such as a CMP operation, may be
performed to the dielectric structure 642 and to expose a top
surface of the dummy gate structure 610b. Referring to FIG. 8J, the
dummy gate structure 610b is removed to form a gate trench 612b in
the dielectric structure 642 after forming the dielectric structure
642 according to operation 216. As shown in FIG. 8J, the insulating
spacer, such as the inner spacer 622 is exposed from sidewalls of
the gate trench 612b.
[0080] Referring to FIG. 8K, a gate conductive structure 650 is
then disposed in the gate trench 612b according to operation 218.
In some embodiments, the gate conductive structure 650 is formed on
the gate dielectric layer 618. More importantly, sidewalls of the
gate conductive structure 650 are in contact with the spacer 622 as
shown in FIG. 8K. In some embodiments, the gate structure 650 can
include at least a barrier layer 652, a work functional metal layer
654 and a gap-filling layer 656. Accordingly, the multi-gate
semiconductor device 600 is obtained as shown in FIG. 8K. More
importantly, sidewalls of the gate conductive structure 650 are in
contact with the spacer 622.
[0081] FIG. 9A through FIG. 9D are cross-sectional views of the
multi-gate semiconductor device 500 and 600 according to aspects of
the present disclosure in one or more embodiments. FIG. 9A is a
cross-sectional view of the semiconductor device 500 and 600 taken
along the first direction D1, FIG. 9B is a cross-sectional view
taken along line A2-A2' of FIG. 9A, FIG. 9C is a cross-sectional
view taken along line B2-B2' of FIG. 9A, and FIG. 9D is a
cross-sectional view taken along line C2-C2' of FIG. 9A. Referring
to FIGS. 9A-9D, a multi-gate semiconductor device 500 and 600 can
be provided. The multi-gate semiconductor device 500/600 includes
the substrate 502/602, the fin structure 508/608 such as the
stacked wire structure 508/608 disposed over the substrate 502/602,
a gate wrapping the stacked wire structure, and spacer disposed
over two sidewalls of the gate. As shown in FIGS. 9A-9D, the gate
includes the gate conductive structure 550/650 and the gate
dielectric layer 518/618 sandwiched between the gate conductive
structure 550/650 and the stacked wire structure. As shown in FIG.
9B, portions of the semiconductor layers 504/604 (the
semiconductors 504/604) are sequentially wrapped by the IL 516/616,
the gate dielectric layer 518/618, and the harrier metal layer
552/652 of the gate conductive structure 550/650. As shown in FIG.
9C, another portions of the stacked wire structure are wrapped by
the insulating spacer 520/622. As shown in FIG. 9D, still another
portions of the 504/604 are wrapped by the source//drain region
530/630. More importantly, the sidewalls of the gate conductive
structure 550/650, such as the barrier metal layer 552/652, are in
contact with the insulating spacer 520/622.
[0082] FIG. 10A through FIG. 10O illustrates a multi-gate
semiconductor device at various fabrication stages constructed
according to aspects of the present disclosure in one or more
embodiments. It should be noted that elements the same in FIGS.
3A-3N and FIGS. 10A-10O can include same materials, thus those
details for the materials are omitted in the interest of
brevity.
[0083] Referring to FIG. 10A, a substrate 702 is provided. Fin
structures 708 including semiconductor layers is formed over the
substrate 702 or a SRB layer. The fin structure 708 may include
alternating layers of different compositions. For example, in some
embodiments, the fin structure 708 includes semiconductor layers
704 of a first composition alternating with semiconductor layers
706 of a second composition. As mentioned above, the compositions
may have different oxidation rates, etchant sensitivity, and/or
other differing properties. Further, the fin structure 708 can be
extended along a first direction D1 as shown in FIG. 10A.
Accordingly, the substrate 702 including the at least one fin
structure 708 is provided according to operation 202. Referring to
FIG. 10B, a sacrificial insulating structure 740 is disposed over
the fin structures 708 and the substrate 702 according to operation
204.
[0084] Referring to FIGS. 10C and 10D, a gate trench 712a is formed
in the sacrificial insulating structure 740 according to operation
206. Additionally, FIGS. 10D-10F are cut views corresponding line
X-X' of FIG. 10C. As shown in FIG. 10D, a portion of the fin
structures 708 is exposed from the gate trench 712a. In some
embodiments, the gate trench 712a is formed correspondingly to
region where channels are to be formed.
[0085] Referring to FIG. 10E, the semiconductor layers 706 exposed
from the gate trench 712a are then removed. Accordingly, a
plurality of wires including the semiconductor layers 704 is
obtained and exposed from the gate trench 712a as shown in FIG.
10E. Referring to FIG. 10F, an IL 716 is formed over the
semiconductor layers 704 and followed by forming a gate dielectric
layer 718 over the semiconductor layers 708 and sidewalls of the
gate trench 712a according to operation 208. In some embodiments, a
barrier metal layer 752 can be formed over the gate dielectric
layer as shown in FIG. 10F. The barrier metal layer 752 can be a
part of a gate conductive structure in some embodiments.
[0086] Referring to FIGS. 10G-10H, after forming the barrier metal
layer 752, a dummy gate structure 710b is then formed in the gate
trench 712a according to operation 210 and followed by removing the
sacrificial insulating structure 740 according to operation 212. As
shown in FIG. 10G, the dummy gate structure 710b is formed to fill
the gate trench 712a, and sidewalls of the dummy gate structure
710b are in contact, with the barrier metal layer 752. Next, at
least a portion of the sacrificial insulating structure 740 is
removed. More importantly, the barrier metal layer 752 and the gate
dielectric layer 718 over the sidewalls of the dummy gate structure
710b are both removed. Consequently, the sidewalls of the dummy
gate structure 710b are exposed as shown in FIG. 10H. Further,
portions of the fin structure 708 are exposed from the dummy gate
structure 710b while another portions of the fin structures 708 is
overlapped by the dummy gate structure 710b. As mentioned above,
the portions of the fin structures 708 underlying the dummy gate
structure 710b may be referred to as the channel region.
[0087] Referring to FIG. 10I, a spacer 720 is then formed over the
substrate 702. As shown in FIG. 10I, the spacer 720 covers the
sidewalls of the dummy gate structure 710b and exposes the portions
of the fin structures 708. Referring to FIG. 10I, a source/drain
region 730 and a source/drain region 732 are formed in the portions
of the fin structures 708 exposed from the dummy gate structure
710b and the insulating spacers 720. In some embodiments of the
present disclosure, the multi-gate semiconductor device 700 is a
CMOS device, therefore the source/drain region 730 can be formed
for a pFET and the source/drain region 732 can be formed for an
nFET.
[0088] Referring to FIG. 10K, a dielectric structure 742 is
disposed over the substrate 702. As mentioned above, the dielectric
structure 742 can include an etch-stop layer (e.g., CESL) (not
shown) and various dielectric layers (e.g., an ILD layer) (not
shown). In some embodiments, after the CESL and the ILD layer are
deposited, a planarization process, such as a CMP operation, may be
performed to the dielectric structure 742 and to expose a top
surface of the dummy gate structure 710b as shown in FIG. 10K.
[0089] Referring to FIGS. 10L-10N, wherein FIGS. 10M-10N are cut
views corresponding line X-X' of FIG. 10L, the dummy gate structure
710b is removed to form a gate trench 712b in the dielectric
structure 742 after forming the dielectric structure 742 according
to operation 216. Since the barrier metal layer 752 is removed from
the sidewalls of the gate trench 712b as mentioned above, the
insulating spacer 720 is exposed from the sidewalls of the gate
trench 712b as shown in FIGS. 10L and 10M. It is noted that the
semiconductor layers 704 wrapped by the IL 716, the gate dielectric
layer 718 and the harrier metal layer 752 are exposed in the gate
trench 712b as shown in FIG. 10M. Next, a gate conductive structure
750 is disposed in the gate trench 712b according to operation 218.
As shown in FIG. 10N, a work function metal layer 754 can be formed
in the gate trench 712b, and the work function metal layer 754 is
in contact with the spacer 720. A gap-filling metal layer 756 is
then formed to fill the gate trench 712b and followed by a
planarization. Accordingly, the gate conductive structure 750 is
obtained as shown in FIG. 10O. More importantly, sidewalls of the
gate conductive structure 750, that is the work function metal
layer 754, are in contact with the spacer 720 as shown in FIG.
10O.
[0090] FIG. 11A through FIG. 11D are cross-sectional views of the
multi-gate semiconductor device 700 according to aspects of the
present disclosure in one or more embodiments. FIG. 11A is a
cross-sectional view of the semiconductor device 700 taken along
the first direction D1, FIG. 11B is a cross-sectional view taken
along line A3-A3' of FIG. 11A, FIG. 11C is a cross-sectional view
taken along line B3-B3' of FIG. 11A, and FIG. 11D is a
cross-sectional view taken along line C3-C3' of FIG. 11A. Referring
to FIGS. 11A-11D, a multi-gate semiconductor device 700 can be
provided. The multi-gate semiconductor device 700 includes the
substrate 702, the fin structure 708 such as the stacked wire
structure 708 disposed over the substrate 702, a gate wrapping the
stacked wire structure, and spacer disposed over two sidewalls of
the gate. As shown in FIGS. 11A-11D, the gate includes the gate
conductive structure 750 and the gate dielectric layer 718
sandwiched between the gate conductive structure 750 and the
stacked wire structure. As shown in FIG. 11B, portions of the
semiconductor layers 704 are sequentially wrapped by the IL 716,
the gate dielectric layer 718, and the barrier metal layer 752 of
the gate conductive structure 750. As shown in FIG. 11C, another
portions of the stacked wire structure are wrapped by the
insulating spacer 720. As shown in FIG. 11D, still another portions
of the 704 are wrapped by the source//drain region 730. More
importantly, the sidewalls of the gate conductive structure 750,
such as the work function metal layer 754, are in contact with the
insulating spacer 720.
[0091] It will be appreciated that in the forgoing method,
operations are taken to form a bottom-up gate dielectric layer. In
other words, sidewalls of the gate conductive structure are in
contact with the insulating or conductive spacers instead of the
gate dielectric layer. Since the gate dielectric layer is not
formed over the sidewalls of the gate trench, the gate trench is
wider and thus it is easier to form the barrier metal layer, the
work function metal layer and the gap-filling metal layer in the
gate trench. Consequently, the gate trench filling result is
improved even the gate length is scaled down, and device
performance can be further improved.
[0092] According to one embodiment of the present disclosure, a
multi-gate semiconductor device is provided. The multi-gate
semiconductor device includes a substrate, a stacked wire structure
disposed over the substrate, a gate over the stacked wire
structure, and at least a first spacer disposed over two sidewalls
of the gate. The gate further includes a gate conductive structure
wrapping the stacked wire structure and a gate dielectric layer
sandwiched between the gate conductive structure and the stacked
wire structure. Further, sidewalls of the gate conductive structure
are in contact with the first spacer.
[0093] According to another embodiment, a method for forming a
multi-gate semiconductor device is provided. The method includes
following operations. A substrate includes at least a fin structure
is provided. A dummy gate structure is disposed over the fin
structure and the substrate. A spacer is disposed over sidewalls of
the sacrificial gate structure. Portions of the fin structure are
exposed from the dummy gate structure and the spacer. Subsequently,
a source/drain region is formed in the portions of the fin
structure exposed from the sacrificial gate structure and the
spacer and followed by disposing a dielectric structure over the
substrate. The dummy gate structure is then removed to form a gate
trench in the dielectric structure. At least a gate dielectric
layer is disposed over a bottom of the gate trench after removing
the sacrificial gate structure. The spacer is exposed from
sidewalls of the gate trench. And a gate conductive structure is
disposed in the gate trench. More importantly, sidewalls of the
gate conductive structure are in contact with the spacer.
[0094] According to one embodiment of the present disclosure, a
method for forming a multi-gate semiconductor device is provided.
The method includes following operations. A substrate including at
least one tin structure is provided. A sacrificial insulating
structure is disposed over the fin structure and the substrate. A
first gate trench is formed in the sacrificial insulating
structure, and a portion of the fin structure is exposed from the
first gate trench. Next, a gate dielectric layer is disposed over
the fin structure and followed by disposing a first dummy gate
structure in the first gate trench. Then, the sacrificial
insulating structure is removed to expose sidewalls of the first
dummy gate structure and portions of the fin structure. An
insulating spacer is disposed over the sidewalls of the first dummy
gate structure, and the portions of the fin structure are exposed
from the insulating spacer. The first dummy gate structure is
removed to form a second gate trench, and a gate conductive
structure is disposed in the second gate trench.
[0095] The foregoing outlines features of several embodiments so
that those skilled in the art may better understand the aspects of
the present disclosure. Those skilled in the art should appreciate
that they may readily use the present disclosure as a basis for
designing or modifying other processes and structures for carrying
out the same purposes and/or achieving the same advantages of the
embodiments introduced herein. Those skilled in the art should also
realize that such equivalent constructions do not depart from the
spirit and scope of the present disclosure, and that they may make
various changes, substitutions, and alterations herein without
departing from the spirit and scope of the present disclosure.
* * * * *