U.S. patent application number 15/742050 was filed with the patent office on 2019-02-07 for high-reflectivity reflector manufacturing method and high-reflectivity lamp.
This patent application is currently assigned to Shenzhen Thousandshores Technology Co., Ltd.. The applicant listed for this patent is Shenzhen Thousandshores Technology Co., Ltd.. Invention is credited to Ding He, Lei Zhou.
Application Number | 20190041032 15/742050 |
Document ID | / |
Family ID | 65229236 |
Filed Date | 2019-02-07 |
![](/patent/app/20190041032/US20190041032A1-20190207-D00000.png)
![](/patent/app/20190041032/US20190041032A1-20190207-D00001.png)
![](/patent/app/20190041032/US20190041032A1-20190207-D00002.png)
United States Patent
Application |
20190041032 |
Kind Code |
A1 |
He; Ding ; et al. |
February 7, 2019 |
HIGH-REFLECTIVITY REFLECTOR MANUFACTURING METHOD AND
HIGH-REFLECTIVITY LAMP
Abstract
Disclosed are a high-reflectivity reflector manufacturing method
and a high-reflectivity lamp. The high-reflectivity reflector
manufacturing method includes (A) preparing at least one micro
foaming reflection plate processed with an anti-UV process; (B)
performing a preheat process of the micro foaming reflection plate;
(C) performing a heating process of the micro foaming reflection
plate after being processed by the preheat process to soften the
micro foaming reflection plate; (D) performing a hot pressing
process to the softened micro foaming reflection plate to form a
required shape of the reflector; and (E) cooling the reflector to
obtain a high-reflectivity reflector. The present disclosure
significantly improves the light reflectivity up to 95%.about.99%
as well as improving the lamp brightness.
Inventors: |
He; Ding; (Shenzhen,
Guangdong, CN) ; Zhou; Lei; (Shenzhen, Guangdong,
CN) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Shenzhen Thousandshores Technology Co., Ltd. |
Shenzhen, Guangdong |
|
CN |
|
|
Assignee: |
Shenzhen Thousandshores Technology
Co., Ltd.
Shenzhen, Guangdong
CN
Shenzhen Thousandshores Technology Co., Ltd.
Shenzhen, Guangdong
CN
|
Family ID: |
65229236 |
Appl. No.: |
15/742050 |
Filed: |
August 2, 2017 |
PCT Filed: |
August 2, 2017 |
PCT NO: |
PCT/CN2017/095703 |
371 Date: |
January 5, 2018 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
B29C 41/46 20130101;
B29C 41/02 20130101; B29K 2995/003 20130101; B29K 2067/003
20130101; B29L 2031/747 20130101; F21V 7/041 20130101; B29C 51/08
20130101; B29K 2105/0044 20130101; B29C 51/082 20130101; B29K
2105/041 20130101; F21V 7/24 20180201 |
International
Class: |
F21V 7/04 20060101
F21V007/04; B29C 41/02 20060101 B29C041/02; B29C 41/46 20060101
B29C041/46; F21V 7/24 20060101 F21V007/24 |
Claims
1. A high-reflectivity reflector manufacturing method, comprising
the steps of: (A) preparing at least one micro foaming reflection
plate processed with an anti-UV process; (B) performing a preheat
process of the micro foaming reflection plate; (C) performing a
heating process of the micro foaming reflection plate after being
processed by the preheat process to soften the micro foaming
reflection plate; (D) performing a hot pressing process to the
softened micro foaming reflection plate to form a required shape of
the reflector; and (E) cooling the reflector to obtain a
high-reflectivity reflector.
2. The high-reflectivity reflector manufacturing method of claim 1,
wherein the preheat process in Step B has a temperature of
180.about.200.degree. C., and a continuous preheat time of 10
seconds.
3. The high-reflectivity reflector manufacturing method of claim 1,
wherein the heating process in the Step C has a temperature of
230.about.250.degree. C., and a continuous heating time is 5
seconds.
4. The high-reflectivity reflector manufacturing method of claim 1,
wherein the Step D further comprises the step of placing the
softened micro foaming reflection plate into a hot pressing mold
for the hot pressing process to form a required shape of the
reflector, wherein a cavity of the micro foaming reflection plate
is formed inside the hot pressing mold.
5. The high-reflectivity reflector manufacturing method of claim 4,
wherein the Step D further comprises a preheat process to heat the
hot pressing mold to 230.about.250.degree. C.
6. The high-reflectivity reflector manufacturing method of claim 1,
wherein in the anti-UV process of the Step A, an anti-UV agent is
added into a MCPET material to form a synthetic micro foaming
sheet, and the MCPET material and the anti-UV agent have a weight
ratio of 50000:1.
7. The high-reflectivity reflector manufacturing method of claim 1,
wherein the high-reflectivity reflector has a cross-sectional shape
selected from the group consisting of a square shape, a circular
shape, and any other shape, and the reflector has an overall shape
of a cone.
8. A high-reflectivity lamp, comprising a lamp housing with an
accommodating space, a light board installed in the lamp housing,
at least one light emitting source installed on the light board,
and a reflector disposed in the lamp housing and covered onto the
light emitting source, and the reflector being manufactured by the
high-reflectivity reflector manufacturing method of claim 1.
Description
FIELD OF THE INVENTION
[0001] The present disclosure relates to the technical field of
lamps, in particular to a high-reflectivity reflector manufacturing
method and a high-reflectivity lamp.
BACKGROUND OF THE INVENTION
[0002] As the lamp technology advances, there are a wide variety of
lamp products on the market. In general, most lamps come with a
reflector for reflecting the light emitted from a light emitting
source inside the lamp. Although a lamp cover can reflect the light
of the light emitting source, most reflectors used for the lamps
have a reflective material coated onto a PC reflector by
electroplating, so that the reflectivity of the lamp cover becomes
lower, and the overall luminous efficiency of the light emitting
source becomes lower, the brightness of the light outputted from
the lamp becomes weaker, and the user requirements cannot be
met.
[0003] In view of the drawbacks of the prior art, it is necessary
to improve the conventional reflectors.
SUMMARY OF THE INVENTION
[0004] Therefore, it is a primary objective of the present
disclosure to provide a high-reflectivity reflector manufacturing
method to overcome the aforementioned drawbacks of the prior
art.
[0005] To achieve the aforementioned and other objectives, the
present disclosure provides a high-reflectivity reflector
manufacturing method, comprising the following steps A.about.E:
[0006] A. Prepare at least one micro foaming reflection plate
processed with an anti-UV process.
[0007] B. Perform a preheat process of the micro foaming reflection
plate.
[0008] C. Perform a heating process of the micro foaming reflection
plate after being processed by the preheat process to soften the
micro foaming reflection plate.
[0009] D. Perform a hot pressing process to the softened micro
foaming reflection plate to form a required shape of the
reflector.
[0010] E. Cool the reflector to obtain a high-reflectivity
reflector.
[0011] In a specific embodiment, the preheat process in Step B has
a temperature of 180.about.200.degree. C., and a continuous preheat
time of 10 seconds.
[0012] In a specific embodiment, the heating process in the Step C
has a temperature of 230.about.250.degree. C., and a continuous
heating time is 5 seconds.
[0013] In a specific embodiment, the Step D further comprises the
step of placing the softened micro foaming reflection plate into a
hot pressing mold for the hot pressing process to form a required
shape of the reflector, wherein a cavity of the micro foaming
reflection plate is formed inside the hot pressing mold.
[0014] In a specific embodiment, the Step D further comprises a
preheat process to heat the hot pressing mold to
230.about.250.degree. C.
[0015] In a specific embodiment, an anti-UV agent is added into a
MCPET material to form a synthetic micro foaming sheet in the
anti-UV process of the Step A, wherein the MCPET material and the
anti-UV agent have a weight ratio of 50000:1.
[0016] In a specific embodiment, the high-reflectivity reflector
has a cross-sectional shape which is a square shape, a circular
shape, and another other shape, and the reflector has an overall
shape of a cone.
[0017] To achieve the aforementioned and other objectives, the
present disclosure further provides a high-reflectivity lamp
comprising a lamp housing with an accommodating space, a light
board installed in the lamp housing, at least one light emitting
source installed on the light board, and a reflector disposed in
the lamp housing and covered onto the light emitting source, and
the reflector is manufactured according to the aforementioned
high-reflectivity reflector manufacturing method.
[0018] The technical solution of the present disclosure provides a
micro foaming reflection plate processed by an anti-UV process and
preheats the micro foaming reflection plate and then heats and
softens the micro foaming reflection plate, and the micro foaming
reflection plate going through the hot pressing process is formed
into the shape of a reflector, and finally the reflector is formed
after a cooling process. Compared with the prior art, most
conventional reflectors have a reflective material electroplated
onto the reflectors. Therefore, the light cannot be reflected
effectively, and thus resulting in a low light efficiency and a
reflectivity less than 90%. In the present disclosure, a micro
foaming reflection plate processed by an anti-UV process is used
for making a reflector, and the reflectivity will reach up to
95%-99%, and the light efficiency can be improved significantly to
enhance the lamp brightness. In addition, the micro foaming
reflection plate processed by the anti-UV process can improve the
service life of the reflector.
BRIEF DESCRIPTION OF THE DRAWINGS
[0019] The above and other objects, features and advantages of this
disclosure will become apparent from the following detailed
description taken with the accompanying drawings. Only some
embodiments of the present disclosure have been illustrated in the
drawings, but it should be pointed out that many other
modifications are conceivable within the scope of the following
claims.
[0020] FIG. 1 is a flow chart of a high-reflectivity reflector
manufacturing method in accordance with an embodiment of the
present disclosure; and
[0021] FIG. 2 is a schematic view of a high-reflectivity lamp in
accordance with an embodiment of the present disclosure.
DESCRIPTION OF ILLUSTRATED EMBODIMENTS
[0022] It should be understood that the terms used in this
specification and claims such as "first" and "second" are provided
for the purpose of illustrating this disclosure, but not intended
for indicating or implying their relative importance or indicating
the quantity of a specific element. Therefore, the characteristic
with the limitation of the "first" or "second" may indicate or
imply the characteristic of having at least one element. In
addition, the technical solutions of different embodiments may be
combined, but such combination must be able to be implemented by
persons having ordinary skill in the art. Such combination will be
considered to be non-existent if it is contradictory or unable to
be implemented and is not to be covered in the scope of the present
disclosure.
Embodiment 1
[0023] With reference to FIG. 1 for a high-reflectivity reflector
manufacturing method in accordance with an embodiment of the
present disclosure, the high-reflectivity reflector manufacturing
method comprises the following steps A.about.E:
[0024] A. Prepare at least one micro foaming reflection plate
processed with an anti-UV process.
[0025] B. Perform a preheat process of the micro foaming reflection
plate.
[0026] C. Perform a heating process of the micro foaming reflection
plate after being processed by the preheat process to soften the
micro foaming reflection plate.
[0027] D. Perform a hot pressing process to the softened micro
foaming reflection plate to form a required shape of the
reflector.
[0028] E. Cool the reflector to obtain a high-reflectivity
reflector.
[0029] In the Step A of this embodiment, the micro foaming
reflection plate is made of a micro cellular polyethylene
terephthalate (MCPET) material. The micro foaming reflection plate
is a crystallized C with high heat resistance. Since the micro
foaming reflection plate of the present disclosure is processed
with an anti-UV process, a small quantity of anti-UV agent is added
during the manufacture, so that the formed material can last long
and will not be deformed or discolored, and the durability will be
improved. The preheat process of the Step B not just prevents
heating the micro foaming reflection plate to a high temperature
directly and shortens the high-temperature softening time only, but
also facilitates the operation of the micro foaming reflection
plate for an easy fixing and cutting operation. The heating process
of the Step C primarily softens the micro foaming reflection plate
to facilitate the subsequent hot pressing process, and presses the
micro foaming reflection plate into a predetermined shape, and
finally the reflector is cooled to form a high reflectivity
reflector.
[0030] The technical solution of the present disclosure provides a
micro foaming reflection plate processed by an anti-UV process and
preheats the micro foaming reflection plate and then heats and
softens the micro foaming reflection plate, and the micro foaming
reflection plate going through the hot pressing process is formed
into the shape of a reflector, and finally the reflector is formed
after a cooling process. Compared with the prior art, most
conventional reflectors have a reflective material electroplated
onto the reflectors. Therefore, the light cannot be reflected
effectively, and thus resulting in a low light efficiency and a
reflectivity less than 90%. In the present disclosure, a micro
foaming reflection plate processed by an anti-UV process is used
for making a reflector, and the reflectivity will reach up to
95%-99%, and the light efficiency can be improved significantly to
enhance the lamp brightness. In addition, the micro foaming
reflection plate processed by the anti-UV process can improve the
service life of the reflector.
[0031] In a specific embodiment, the preheat process in the Step B
has a temperature of 180-200.degree. C. and a continuous preheat
time of 10 seconds. The aforementioned preheat temperature and
heating time are parameters of an embodiment only. In this
embodiment, the preheat process is taken place at the temperature
of 180-200.degree. C. for 5.about.15 seconds. With the appropriate
temperature and preheat time, the micro foaming reflection plate
can be prevented from being heated directly to a high temperature,
so as to shorten the high-temperature softening time and facilitate
the operation of the micro foaming reflection plate and the fixing
and cutting operation.
[0032] In a specific embodiment, the heating process in the Step C
has a temperature of 230.about.250.degree. C. and a continuous
heating time of 5 seconds. The heating temperature falls within a
range of 230.about.250.degree. C. which may be 230.degree. C.,
240.degree. C., or 250.degree. C., and the continuous heating time
is 5 seconds. Compared with the prior art, the present disclosure
can shorten the heating time and improve the processing
efficiency.
[0033] In a specific embodiment, the Step D further comprises the
step of placing the softened micro foaming reflection plate into a
hot pressing mold for the hot pressing process to form a required
shape of the reflector, wherein a cavity of the micro foaming
reflection plate is formed inside the hot pressing mold. In this
embodiment, a hot pressing mold is provided for shaping, and we can
understand that a desired cavity for molding the micro foaming
reflection plate is formed in the hot pressing mold and used for
performing the hot pressing process of the softened micro foaming
reflection plate, so as to define a specific shape.
[0034] In a specific embodiment, the Step D further comprises a
preheat process to heat the hot pressing mold to
230.about.250.degree. C. During the hot pressing process, it is
necessary to heat the hot pressing mold. To prevent a drop of the
temperature of the micro foaming sheet temperature, the temperature
of the hot pressing mold is maintained within 230.about.250.degree.
C. in order to improve the hot pressing effect.
[0035] In a specific embodiment, in the anti-UV process of the Step
A, a synthetic micro foaming sheet with an anti-UV agent is added
into the MCPET material, wherein the MCPET material and the anti-UV
agent have a weight ratio of 50000:1. In this embodiment, when the
micro foaming sheet with the anti-UV agent is applied to the
high-reflectivity reflector, it can be used for a long time under
the wavelength of 280-320 nm without the issue of discoloring.
[0036] In a specific embodiment, the high-reflectivity reflector
has a cross-sectional shape of a square, a circle, or any other
shape, and the overall shape of the reflector is substantially the
shape of a cone. It is understood that the cross-sectional shape of
the reflector may be any one selected from a square shape, a
circular shape or any other shape, and the overall shape is the
shape of a cone or a cylinder.
Embodiment 2
[0037] With reference to FIG. 2 for a high-reflectivity lamp in
accordance with a embodiment of the present disclosure, the
high-reflectivity lamp comprises a lamp housing 10 with an
accommodating space, a light board installed in the lamp housing,
at least one light emitting source 30 installed on the light board,
and a reflector 20 disposed in the lamp housing and covered onto
the light emitting source, and the reflector 20 is manufactured
according to the aforementioned high-reflectivity reflector
manufacturing method. Since the reflector of the high-reflectivity
lamp of the present disclosure is manufactured according to the
aforementioned high-reflectivity reflector manufacturing method, it
has all advantages and effects of a high-reflectivity
reflector.
[0038] In this embodiment, the reflector of the high-reflectivity
lamp is made of a high-reflectivity material and capable of
improving the light reflection effect of the reflector (when
compared with the surface plating technology of the prior art).
Tests show that the reflection efficiency of the reflector of this
disclosure is over 95%. As to the whole solution, the present
disclosure has the features of a reasonable design, a simple
structure, and a low manufacturing cost, and can prevent the
failure of an effective reflection or the low light utilization
efficiency. In addition, this disclosure may be applied to both
indoor and outdoor lamps to provide a wide scope of
applicability.
[0039] While the disclosure has been described by means of specific
embodiments, numerous modifications and variations could be made
thereto by those skilled in the art without departing from the
scope and spirit of the disclosure set forth in the claims.
* * * * *