U.S. patent application number 15/772418 was filed with the patent office on 2019-01-03 for metal powder atomization manufacturing processes.
The applicant listed for this patent is AP&C ADVANCED POWDERS & COATINGS INC.. Invention is credited to Matthieu BALMAYER, Frederic LAROUCHE, Frederic MARION.
Application Number | 20190001416 15/772418 |
Document ID | / |
Family ID | 58629652 |
Filed Date | 2019-01-03 |
![](/patent/app/20190001416/US20190001416A1-20190103-D00000.png)
![](/patent/app/20190001416/US20190001416A1-20190103-D00001.png)
![](/patent/app/20190001416/US20190001416A1-20190103-D00002.png)
![](/patent/app/20190001416/US20190001416A1-20190103-D00003.png)
![](/patent/app/20190001416/US20190001416A1-20190103-D00004.png)
![](/patent/app/20190001416/US20190001416A1-20190103-D00005.png)
![](/patent/app/20190001416/US20190001416A1-20190103-D00006.png)
![](/patent/app/20190001416/US20190001416A1-20190103-D00007.png)
United States Patent
Application |
20190001416 |
Kind Code |
A1 |
LAROUCHE; Frederic ; et
al. |
January 3, 2019 |
METAL POWDER ATOMIZATION MANUFACTURING PROCESSES
Abstract
There are provided reactive metal powder atomization
manufacturing processes. For example, such processes include
providing a heated metal source and contact the heated metal source
with at least one additive gas while carrying out the atomization
process. Such processes provide raw reactive metal powder having
improved flowability. The at least one additive gas can be mixed
together with an atomization gas to obtain an atomization mixture,
and the heated metal source can be contacted with the atomization
mixture while carrying out the atomization process. Reactive metal
powder spheroidization manufacturing processes are also
provided.
Inventors: |
LAROUCHE; Frederic; (Ile
Bizard, CA) ; MARION; Frederic; (Montreal, CA)
; BALMAYER; Matthieu; (Montreal, CA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
AP&C ADVANCED POWDERS & COATINGS INC. |
Boisbriand |
|
CA |
|
|
Family ID: |
58629652 |
Appl. No.: |
15/772418 |
Filed: |
October 27, 2016 |
PCT Filed: |
October 27, 2016 |
PCT NO: |
PCT/CA2016/051240 |
371 Date: |
April 30, 2018 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
62247794 |
Oct 29, 2015 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
B22F 2999/00 20130101;
B22F 1/02 20130101; B22F 9/04 20130101; C22C 1/0408 20130101; B22F
2202/13 20130101; B22F 9/14 20130101; B22F 2009/0828 20130101; C22C
1/0416 20130101; B22F 1/0014 20130101; B22F 2201/02 20130101; B01J
2/02 20130101; B22F 2201/04 20130101; B22F 2201/03 20130101; C22C
1/0458 20130101; B22F 2201/50 20130101; B22F 2998/10 20130101; B22F
1/0081 20130101; B22F 2009/0848 20130101; B22F 9/082 20130101; B22F
2009/0824 20130101; B22F 2999/00 20130101; B22F 9/082 20130101;
B22F 2202/13 20130101; B22F 2999/00 20130101; B22F 9/082 20130101;
B22F 2201/10 20130101; B22F 2201/11 20130101; B22F 2201/12
20130101; B22F 2201/013 20130101; B22F 2201/016 20130101; B22F
2201/02 20130101; B22F 2201/03 20130101; B22F 2201/04 20130101;
B22F 2201/05 20130101; B22F 2201/50 20130101; B22F 2999/00
20130101; B22F 9/04 20130101; B22F 2202/13 20130101; B22F 2201/10
20130101; B22F 2201/11 20130101; B22F 2201/12 20130101; B22F
2201/013 20130101; B22F 2201/016 20130101; B22F 2201/02 20130101;
B22F 2201/03 20130101; B22F 2201/04 20130101; B22F 2201/05
20130101; B22F 2201/50 20130101; B22F 2999/00 20130101; B22F 9/14
20130101; B22F 2202/13 20130101; B22F 2201/10 20130101; B22F
2201/11 20130101; B22F 2201/12 20130101; B22F 2201/013 20130101;
B22F 2201/016 20130101; B22F 2201/02 20130101; B22F 2201/03
20130101; B22F 2201/04 20130101; B22F 2201/05 20130101; B22F
2201/50 20130101 |
International
Class: |
B22F 9/08 20060101
B22F009/08; B22F 9/04 20060101 B22F009/04; B22F 9/14 20060101
B22F009/14; B22F 1/00 20060101 B22F001/00; B22F 1/02 20060101
B22F001/02 |
Claims
1. A reactive metal powder atomization manufacturing process
comprising: atomizing a heated reactive metal source to produce a
raw reactive metal powder; contacting said heated reactive metal
source with an atomization mixture comprising at least one
atomizing gas and at least one additive gas that is present at a
concentration of less than 1000 ppm in said atomization mixture
while atomizing said heated reactive metal source; and forming,
with said at least one additive gas, a surface layer on said raw
reactive metal powder, said raw reactive metal powder with said
surface layer thereon, comprises less than 1000 ppm of at least one
element from said at least one additive gas, wherein said surface
layer comprises a first layer and a second layer, said first layer
comprising atoms of said heated reactive metal source with atoms
and/or molecules of said at least one additive gas, said first
layer being a depletion layer deeper and thicker than said second
layer, said second layer being a native oxide layer, and wherein a
particle size distribution of about 10 to about 53 .mu.m of said
raw reactive metal powder with said surface layer thereon, has a
flowability less than 40 s, measured according to ASTM B213.
2. The process of claim 1, wherein said raw reactive metal powder
with said surface layer thereon has a particle size distribution of
about 10 to about 45 .mu.m having a flowability less than 40 s,
measured according to ASTM B213.
3. The process of claim 1, wherein said raw reactive metal powder
with said surface layer thereon has a particle size distribution of
about 15 to about 45 .mu.m having a flowability less than 40 s,
measured according to ASTM B213.
4. The process of claim 1, wherein said raw reactive metal powder
with said surface layer thereon has a particle size distribution of
about 15 to about 53 .mu.m having a flowability less than 40 s,
measured according to ASTM B213.
5. The process of claim 1, wherein said raw reactive metal powder
with said surface layer thereon comprises a particle size
distribution of about 25 to about 45 .mu.m having a flowability
less than 40 s, measured according to ASTM B213.
6. The process of claim 1, wherein said raw reactive metal powder
with said surface layer thereon comprises a particle size
distribution of about 25 to about 53 .mu.m having a flowability
less than 40 s, measured according to ASTM B213.
7. The process of claim 1, wherein the raw reactive metal powder
with said surface layer thereon further comprises a particle size
distribution of about 45 to about 75 .mu.m having a flowability
less than 28 s, measured according to ASTM B213.
8. (canceled)
9. The process of claim 0, wherein said raw reactive metal powder
with said surface layer thereon comprises a particle size
distribution of about 10 to about 53 .mu.m having a flowability
less than 36 s, measured according to ASTM B213.
10. (canceled)
11. The process of claim 0, wherein said raw reactive metal powder
with said surface layer thereon comprises a particle size
distribution of about 10 to about 53 .mu.m having a flowability
less than 30 s, measured according to ASTM B213.
12. The process of claim 0, wherein said raw reactive metal powder
with said surface layer thereon comprises a particle size
distribution of about 10 to about 53 .mu.m having a flowability
less than 28 s, measured according to ASTM B213.
13-31. (canceled)
32. The process of claim 0, wherein said raw reactive metal powder
with said surface layer thereon further comprises a particle size
distribution of about 45 to about 75 .mu.m having a flowability
less than 26 s, measured according to ASTM B213.
33-35. (canceled)
36. The process of claim 0, wherein said raw reactive metal powder
with said surface layer thereon further comprises a particle size
distribution of about 45 to about 106 .mu.m having a flowability
less than 26 s, measured according to ASTM B213.
37-41. (canceled)
42. The process of claim 1, wherein said heated reactive metal
source is contacted with said at least one additive gas at
substantially the same time as contact with an atomizing gas.
43. (canceled)
44. The process of claim 1, wherein said atomizing gas and said at
least one additive gas are mixed together prior to contact with
said heated reactive metal source.
45. The process of claim 1, wherein said first layer has a
substantially positive charge and said second layer has a
substantially negative charge, and wherein said first layer and
said second layer have a combined charge that is substantially
neutral.
46. (canceled)
47. The process of claim 1, further comprising: sieving said raw
reactive metal powder with said surface layer thereon after
atomizing said heated reactive metal source to separate said raw
reactive metal powder with said surface layer thereon by particle
size distributions; and after said sieving, separately stirring
said separated raw reactive metal powder with said surface layer
thereon in water.
48-49. (canceled)
50. The process of claim 1, wherein said surface layer thereon
comprises less than about 500 ppm of said at least one element from
said at least one additive gas.
51. (canceled)
52. The process of claim 1, wherein said surface layer thereon
comprises less than about 200 ppm of said at least one element from
said at least one additive gas.
53. (canceled)
54. The process of claim 1, wherein said surface layer thereon
comprises less than about 100 ppm of said at least one element from
said at least one additive gas.
55. The process of claim 1, wherein said surface layer thereon has
an added content of an electronegative element from said at least
one additive gas of less than about 500 ppm.
56-58. (canceled)
59. The process of claim 1, wherein said surface layer thereon has
an added content of an electronegative element from said at least
one additive gas of less than about 100 ppm.
60. A reactive metal powder atomization manufacturing process
comprising: mixing together an atomizing gas and at least one
additive gas to obtain an atomization mixture; contacting a heated
reactive metal source with said atomization mixture while atomizing
said heated reactive metal source to produce a raw reactive metal
powder having a surface layer thereon; sieving said raw reactive
metal powder with said surface layer thereon to obtain a powder
having a predetermined particle size; and contacting said powder
having said predetermined particle size with water.
61-64. (canceled)
65. The process of claim 60, wherein said surface layer comprises a
first layer and a second layer, said first layer comprising atoms
of said heated reactive metal source with atoms and/or molecules of
said at least one additive gas, said first layer being a depletion
layer deeper and thicker than said second layer, said second layer
being a native oxide layer.
66. The process of claim 65, wherein said first layer has a
substantially positive charge and said second layer has a
substantially negative charge, and wherein said first layer and
said second layer have a combined charge that is substantially
neutral.
67-78. (canceled)
79. The process of claim 60, wherein said surface layer thereon has
an added content of an electronegative element from said at least
one additive gas of less 100 ppm.
80. The process of claim 60, wherein said predetermined particle
size comprises a particle size distribution chosen from 10-45
.mu.m, 15-45 .mu.m, 10-53 .mu.m, 15-53 .mu.m, and 25-45 .mu.m.
81. A reactive metal powder spheroidization manufacturing process
comprising: contacting a reactive metal powder source with a
spheroidization process gas mixture that comprises at least one
spheroidization process gas and at least one additive gas that is
present at a concentration of less than 1000 ppm in said
spheroidization process gas mixture while spheroidizing said
reactive metal powder source to produce a raw reactive metal
powder; and forming, with said at least one additive gas, a surface
layer on said raw reactive metal powder, said raw reactive metal
powder with said surface layer thereon comprises less than 1000 ppm
of at least one element from said at least one additive gas,
wherein said surface layer comprises a first layer and a second
layer, said first layer comprising atoms of said heated reactive
metal source with atoms and/or molecules of said at least one
additive gas, said first layer being a depletion layer deeper and
thicker than said second layer, said second layer being a native
oxide layer, and wherein a particle size distribution of about 10
to about 53 .mu.m of said raw reactive metal powder with said
surface layer thereon has a flowability less than 40 s, measured
according to ASTM B213.
82. The process of claim 81, wherein said raw reactive metal powder
with said surface layer thereon comprises a particle size
distribution of about 10 to about 45 .mu.m having a flowability
less than 40 s, measured according to ASTM B213.
83. The process of claim 81, wherein said raw reactive metal powder
with said surface layer thereon comprises a particle size
distribution of about 15 to about 45 .mu.m having a flowability
less than 40 s, measured according to ASTM B213.
84. The process of claim 81, wherein said raw reactive metal powder
with said surface layer thereon comprises a particle size
distribution of about 15 to about 53 .mu.m having a flowability
less than 40 s, measured according to ASTM B213.
85. The process of claim 81, wherein said raw reactive metal powder
with said surface layer thereon comprises a particle size
distribution of about 25 to about 45 .mu.m having a flowability
less than 40 s, measured according to ASTM B213.
86. The process of claim 81, wherein said raw reactive metal powder
with said surface layer thereon comprises a particle size
distribution of about 25 to about 53 .mu.m having a flowability
less than 40 s, measured according to ASTM B213.
87. (canceled)
88. The process of claim 81, wherein said raw reactive metal powder
with said surface layer thereon further comprises particle size
distribution of about 45 to about 106 .mu.m having a flowability
less than 28 s, measured according to ASTM B213.
89. A reactive metal powder spheroidization manufacturing process
comprising: mixing together a spheroidization process gas and at
least one additive gas to obtain a spheroidization process gas
mixture; contacting a reactive metal powder source with said
spheroidization process gas mixture while spheroidizing said
reactive metal powder source to produce a raw reactive metal powder
having a surface layer thereon; sieving said raw reactive metal
powder with said surface layer thereon to obtain a powder having
predetermined particle size; and contacting said powder having said
predetermined particle size with water.
90. (canceled)
91. The process of claim 1, wherein said at least one additive gas
is an oxygen-containing gas.
92. The process of claim 1, wherein said at least one additive gas
is an oxygen-containing gas chosen from O.sub.2, CO.sub.2, CO,
NO.sub.2, air, water vapor and mixtures thereof.
93. The process of claim 1, wherein said at least one additive gas
is a halogen-containing gas.
94. (canceled)
95. The process of claim 1, wherein said at least one additive gas
is a hydrogen-containing gas.
96. The process of claim 1, wherein said at least one additive gas
is a sulfur-containing gas.
97. The process of claim 1, wherein said at least one additive gas
is a nitrogen-containing gas.
98. (canceled)
99. The process of claim 1, wherein said raw reactive metal powder
with said surface layer thereon comprises at least one of titanium,
zirconium, magnesium, and aluminum.
100. The process of claim 1, wherein said raw reactive metal powder
with said surface layer thereon is a metal powder comprising at
least one member chosen from one of titanium, titanium alloys,
zirconium, zirconium alloys, magnesium, magnesium alloys, aluminum
and aluminum alloys.
101. The process of claim 1, wherein said raw reactive metal powder
with said surface layer thereon comprises titanium.
102. The process of claim 1, wherein said raw reactive metal powder
comprises a titanium alloy.
103-110. (canceled)
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] The present application claims priority to U.S. 62/247,794
filed on Oct. 29, 2015, which is hereby incorporated by reference
in its entirety.
FIELD OF THE DISCLOSURE
[0002] The present disclosure relates to the field of production of
spheroidal powders such as reactive metal powders. More
particularly, it relates to methods and apparatuses for preparing
reactive metal powders by having improved flowability.
BACKGROUND OF THE DISCLOSURE
[0003] Typically, the desired features of high quality reactive
metal powders will be a combination of high sphericity, density,
purity, flowability and low amount of gas entrapped porosities.
Fine powders are useful for applications such as 3D printing,
powder injection molding, hot isostatic pressing and coatings. Such
fine powders are used in aerospace, biomedical and industrial
fields of applications.
[0004] A powder having poor flowability may tend to form
agglomerates having lower density and higher surface area. These
agglomerates can be detrimental when used in applications that
require of fine reactive metal powders. Furthermore, reactive
powder with poor flowability can cause pipes clogging and/or stick
on the walls of an atomization chamber of an atomizing apparatus or
on the walls of conveying tubes. Moreover, powders in the form of
agglomerates are more difficult to sieve when separating powder
into different size distributions. Manipulation of powder in the
form of agglomerates also increases the safety risks as higher
surface area translates into higher reactivity.
[0005] By contrast, metal powders having improved flowability are
desirable for various reasons. For example, they can be used more
easily in powder metallurgy processes as additive manufacturing and
coatings.
SUMMARY
[0006] It would thus be highly desirable to be provided with a
device, system or method that would at least partially address the
poor flowability of reactive metal powder related to static
electricity sensitivity. A high flowability powder usually
translates in a higher apparent density and it can be spread more
easily in order to produce an uniform layer of powder.
[0007] According to one aspect, there is provided a reactive metal
powder atomization manufacturing process comprising:
[0008] providing a heated metal source; and
[0009] contacting said heated metal source with at least one
additive gas while carrying out said atomization process.
[0010] According to another aspect, there is provided a reactive
metal powder atomization manufacturing process comprising:
[0011] providing a heated metal source; and
[0012] contacting said heated metal source with at least one
additive gas while carrying out said atomization process, thereby
obtaining a raw reactive metal powder comprising
particle size distribution of about 10 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 10 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 15 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 15 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 25 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 25 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 45 to about 75 .mu.m having a
flowability less than 28 s, measured according to ASTM B213;
particle size distribution of about 45 to about 106 .mu.m having a
flowability less than 28 s, measured according to ASTM B213;
particle size distribution of about 45 to about 150 .mu.m having a
flowability less than 28 s, measured according to ASTM B213; and/or
particle size distribution of about 45 to about 180 .mu.m having a
flowability less than 28 s, measured according to ASTM B213.
[0013] According to another aspect, there is provided a reactive
metal powder atomization manufacturing process comprising:
[0014] providing a heated metal source;
[0015] mixing together an atomization gas and at least one additive
gas to obtain an atomization mixture;
[0016] contacting said heated metal source with said atomization
mixture while carrying out said atomization process.
[0017] According to another aspect, there is provided a reactive
metal powder atomization manufacturing process comprising:
[0018] providing a heated metal source;
[0019] mixing together an atomization gas and at least one additive
gas to obtain an atomization mixture;
[0020] contacting said heated metal source with said atomization
mixture while carrying out said atomization process, thereby
obtaining a raw reactive metal powder comprising
particle size distribution of about 10 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 10 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 15 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 15 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 25 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 25 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 45 to about 75 .mu.m having a
flowability less than 28 s, measured according to ASTM B213;
particle size distribution of about 45 to about 106 .mu.m having a
flowability less than 28 s, measured according to ASTM B213;
particle size distribution of about 45 to about 150 .mu.m having a
flowability less than 28 s, measured according to ASTM B213; and/or
particle size distribution of about 45 to about 180 .mu.m having a
flowability less than 28 s, measured according to ASTM B213.
[0021] According to another aspect, there is provided a metal
powder atomization manufacturing process comprising:
[0022] providing a heated metal source; and
[0023] contacting said heated metal source with at least one
additive gas while carrying out said atomization process under
conditions sufficient to produce a reactive metal powder having an
added content of each electronegative atom and/or molecule from the
additive gas of less than 1000 ppm.
[0024] According to another aspect, there is provided a metal
powder atomization manufacturing process comprising:
[0025] providing a heated metal source;
[0026] mixing together an atomization gas and at least one additive
gas to obtain an atomization mixture; and
[0027] contacting said heated metal source with said atomization
mixture while carrying out said atomization process under
conditions sufficient to produce a raw reactive metal powder having
an added content of electronegative atoms and/or molecules from the
additive gas of less than 1000 ppm.
[0028] According to another aspect, there is provided a metal
powder atomization manufacturing process comprising:
[0029] providing a heated metal source;
[0030] mixing together an atomization gas and at least one additive
gas to obtain an atomization mixture;
[0031] contacting said heated metal source with said atomization
mixture while carrying out said atomization process, thereby
obtaining a raw metal powder;
[0032] sieving said raw reactive metal powder to obtain a powder
having predetermined particle size; and
[0033] contacting said powder having said predetermined particle
size with water.
[0034] According to another aspect, there is provided a reactive
metal powder spheroidization manufacturing process comprising:
[0035] providing a reactive metal powder source; and
[0036] contacting said reactive metal powder source with at least
one additive gas while carrying out said spheroidization
process.
[0037] According to another aspect, there is provided a reactive
metal powder spheroidization manufacturing process comprising:
[0038] providing a reactive metal powder source; and
[0039] contacting said reactive metal powder source with at least
one additive gas while carrying out said spheroidization process,
thereby obtaining a raw reactive metal powder comprising
particle size distribution of about 10 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 10 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 15 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 15 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 25 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 25 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 45 to about 75 .mu.m having a
flowability less than 28 s, measured according to ASTM B213;
particle size distribution of about 45 to about 106 .mu.m having a
flowability less than 28 s, measured according to ASTM B213;
particle size distribution of about 45 to about 150 .mu.m having a
flowability less than 28 s, measured according to ASTM B213; and/or
particle size distribution of about 45 to about 180 .mu.m having a
flowability less than 28 s, measured according to ASTM B213.
[0040] According to another aspect, there is provided a reactive
metal powder spheroidization manufacturing process comprising:
[0041] providing a reactive metal powder source;
[0042] mixing together a spheroidization process gas and at least
one additive gas to obtain a spheroidization process gas
mixture;
[0043] contacting said reactive metal powder source with said
spheroidization process gas mixture while carrying out said
spheroidization process,
[0044] According to another aspect, there is provided a reactive
metal powder spheroidization manufacturing process comprising:
[0045] providing a reactive metal powder source;
[0046] mixing together a spheroidization process gas and at least
one additive gas to obtain a spheroidization process gas
mixture;
[0047] contacting said reactive metal powder source with said
spheroidization process gas mixture while carrying out said
spheroidization process, thereby obtaining a raw reactive metal
powder comprising
particle size distribution of about 10 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 10 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 15 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 15 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 25 to about 45 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 25 to about 53 .mu.m having a
flowability less than 40 s, measured according to ASTM B213;
particle size distribution of about 45 to about 75 .mu.m having a
flowability less than 28 s, measured according to ASTM B213;
particle size distribution of about 45 to about 106 .mu.m having a
flowability less than 28 s, measured according to ASTM B213;
particle size distribution of about 45 to about 150 .mu.m having a
flowability less than 28 s, measured according to ASTM B213; and/or
particle size distribution of about 45 to about 180 .mu.m having a
flowability less than 28 s, measured according to ASTM B213.
[0048] According to another aspect, there is provided a reactive
metal powder spheroidization manufacturing process comprising:
[0049] providing a reactive metal powder source; and
[0050] contacting said reactive metal source with at least one
additive gas while carrying out said spheroidization process under
conditions sufficient to produce a raw reactive metal powder having
an added content of each electronegative atom and/or molecule from
the additive gas of less than 1000 ppm.
[0051] According to another aspect, there is provided a reactive
metal powder spheroidization manufacturing process comprising:
[0052] providing a reactive metal powder source;
[0053] mixing together a spheroidization process gas and at least
one additive gas to obtain a spheroidization process gas
mixture;
[0054] contacting said reactive metal powder source with said
spheroidization process gas mixture while carrying out said
spheroidization process under conditions sufficient to produce a
raw reactive metal powder having an added content of
electronegative atoms and/or molecules from the additive gas of
less than 1000 ppm.
[0055] According to another aspect, there is provided a metal
powder spheroidization manufacturing process comprising:
[0056] providing a reactive metal powder source;
[0057] mixing together spheroidization process gas and at least one
additive gas to obtain a spheroidization process gas mixture;
[0058] contacting said reactive metal powder source with said
spheroidization process gas mixture while carrying out said
atomization process, thereby obtaining a raw metal powder;
[0059] sieving said raw reactive metal powder to obtain a powder
having predetermined particle size;
[0060] contacting said powder having said predetermined particle
size with water.
[0061] According to another example, there is provided a process
for preparing a reactive metal powder mixture comprising mixing
together a reactive metal powder obtained by a process as defined
in the present disclosure, with a reactive metal powder obtained by
a process different than those recited in the present
disclosure.
[0062] According to another example, there is provided a process
for preparing a reactive metal powder mixture comprising mixing
together a reactive metal powder obtained by a process as defined
in the present disclosure, with a reactive metal powder obtained by
a process different than those recited in the present
disclosure.
[0063] According to another example, there is provided a process
for preparing a reactive metal powder mixture comprising mixing
together a reactive metal powder obtained by a metal powder
atomization manufacturing process as defined in the present
disclosure, with a reactive metal powder obtained by a metal powder
spheroidization manufacturing process as defined in the present
disclosure.
[0064] According to another example, there is provided a reactive
metal powder obtained by a process as defined in the present
disclosure.
[0065] The present disclosure refers to methods, processes, systems
and apparatuses that enable the production of reactive metal powder
that exhibits a high flowability. The effect can be observed for
various particle size distributions including for fine particle
size distributions which would not even flow in a Hall flowmeter
without the treatment described. One advantage of current method is
that it does not add foreign particles in the powder. It is only a
surface treatment that causes the improvement.
[0066] It was observed that the various technologies described in
the present disclosure help to reduce the static electricity
sensitivity of the powder which is resulting in improved
flowability behavior of the powder.
DRAWINGS
[0067] The following drawings represent non-limitative examples in
which:
[0068] FIG. 1 is a cross-sectional view of an example atomizing
system;
[0069] FIG. 2 is a schematic diagram of a particle of reactive
metal powder formed according to an atomization process in which
the heated metal source is not contacted with an additive gas;
[0070] FIG. 3 is a schematic diagram of a particle of reactive
metal powder formed according to an atomization process in which
the heated metal source is contacted with an additive gas
[0071] FIG. 4 illustrates a schematic diagram of a particle having
a radius R and a plurality of particles each having a radius r
formed from the same mass of material;
[0072] FIG. 5 illustrates a TOF-SIMS signature for a particle
obtained from various testings;
[0073] FIG. 6 is a photograph of a batch of metal powder formed
according to an atomization process that does not include the step
of contacting with an additive gas; and
[0074] FIG. 7 is a photograph of a batch of metal powder formed
according to an atomization process in which the metal source has
been contacted with an additive gas.
DESCRIPTION OF VARIOUS EMBODIMENTS
[0075] The following examples are presented in a non-limiting
manner.
[0076] The word "a" or "an" when used in conjunction with the term
"comprising" in the claims and/or the specification may mean "one",
but it is also consistent with the meaning of "one or more", "at
least one", and "one or more than one" unless the content clearly
dictates otherwise. Similarly, the word "another" may mean at least
a second or more unless the content clearly dictates otherwise.
[0077] As used in this specification and claim(s), the words
"comprising" (and any form of comprising, such as "comprise" and
"comprises"), "having" (and any form of having, such as "have" and
"has"), "including" (and any form of including, such as "include"
and "includes") or "containing" (and any form of containing, such
as "contain" and "contains"), are inclusive or open-ended and do
not exclude additional, unrecited elements or process steps.
[0078] The expression "atomization zone" as used herein, when
referring to a method, apparatus or system for preparing a metal
powder, refers to a zone in which the material is atomized into
droplets of the material. The person skilled in the art would
understand that the dimensions of the atomization zone will vary
according to various parameters such as temperature of the
atomizing means, velocity of the atomizing means, material in the
atomizing means, power of the atomizing means, temperature of the
material before entering in the atomization zone, nature of the
material, dimensions of the material, electrical resistivity of the
material, etc.
[0079] The expression "heat zone of an atomizer" as used herein
refers to a zone where the powder is sufficiently hot to react with
the electronegative atoms of the additive gas in order to generate
a depletion layer, as discussed in the present disclosure.
[0080] The expression "metal powder has a X-Y .mu.m particle size
distribution means it has less than 5% wt. of particle above Y
.mu.m size with the latter value measured according to ASTM B214
standard. It also means it has less than 6% wt. of particle below X
.mu.m size (d6.gtoreq.X .mu.m) with the latter value measured
according to ASTM B822 standard.
[0081] The expression "metal powder having a 15-45 .mu.m particle
size means it has less than 5% wt. of particle above 45 .mu.m
(measured according to ASTM B214 standard) and less than 6% wt. of
particle below 15 .mu.m (measured according to ASTM B822
standard).
[0082] The expression "Gas to Metal ratio" as used herein refers to
the ratio of mass per unit of time (kg/s) of gas injected on the
mass feedrate (kg/s) of the metal source provided in the
atomization zone.
[0083] The expression "reactive metal powder" as used herein refers
to a metal powder that cannot be efficiently prepared via the
classical gas atomization process in which close-coupled nozzle is
used. For example, such a reactive metal powder can be a powder
comprising at least one member chosen from titanium, titanium
alloys, zirconium, zirconium alloys, magnesium, magnesium alloys,
aluminum and aluminum alloys.
[0084] The term "raw reactive metal powder" as used herein refers
to a reactive metal powder obtained directly from an atomization
process without any post processing steps such as sieving or
classification techniques.
[0085] It was observed that reactive metal powder having fine
particle sizes, such within a size distributions below 106 .mu.m,
possess more surface area and stronger surface interactions. These
result in poorer flowability behavior than coarser powders. The
flowability of a powder depends on one or more of various factors,
such as particle shape, particle size distribution, surface
smoothness, moisture level, satellite content and presence of
static electricity. The flowability of a powder is thus a complex
macroscopic characteristic resulting from the balance between
adhesion and gravity forces on powder particles.
[0086] For example, particle size distribution can be:
of about 10 to about 53 .mu.m having a flowability less than 40 s,
measured according to ASTM B213; of about 10 to about 45 .mu.m
having a flowability less than 40 s, measured according to ASTM
B213; of about 15 to about 45 .mu.m having a flowability less than
40 s, measured according to ASTM B213; of about 15 to about 53
.mu.m having a flowability less than 40 s, measured according to
ASTM B213; of about 25 to about 45 .mu.m having a flowability less
than 40 s, measured according to ASTM B213; of about 25 to about 53
.mu.m having a flowability less than 40 s, measured according to
ASTM B213; of about 45 to about 75 .mu.m having a flowability less
than 28 s, measured according to ASTM B213; of about 45 to about
106 .mu.m having a flowability less than 28 s, measured according
to ASTM B213; of about 45 to about 150 .mu.m having a flowability
less than 28 s, measured according to ASTM B213; and/or of about 45
to about 180 .mu.m having a flowability less than 28 s, measured
according to ASTM B213.
[0087] For example, particle size distribution can be of about 10
to about 53 .mu.m having a flowability less than 36 s, measured
according to ASTM B213.
[0088] For example, particle size distribution can be of about 10
to about 53 .mu.m having a flowability less than 32 s, measured
according to ASTM B213.
[0089] For example, particle size distribution can be of about 10
to about 53 .mu.m having a flowability less than 30 s, measured
according to ASTM B213.
[0090] For example, particle size distribution can be of about 10
to about 53 .mu.m having a flowability less than 28 s, measured
according to ASTM B213.
[0091] For example, particle size distribution can be of about 10
to about 45 .mu.m having a flowability less than 36 s, measured
according to ASTM B213.
[0092] For example, particle size distribution can be of about 10
to about 45 .mu.m having a flowability less than 32 s, measured
according to ASTM B213.
[0093] For example, particle size distribution can be of about 10
to about 45 .mu.m having a flowability less than 30 s, measured
according to ASTM B213.
[0094] For example, particle size distribution can be of about 10
to about 45 .mu.m having a flowability less than 28 s, measured
according to ASTM B213.
[0095] For example, particle size distribution can be of about 15
to about 45 .mu.m having a flowability less than 36 s, measured
according to ASTM B213.
[0096] For example, particle size distribution can be of about 15
to about 45 .mu.m having a flowability less than 32 s, measured
according to ASTM B213.
[0097] For example, particle size distribution can be of about 15
to about 45 .mu.m having a flowability less than 30 s, measured
according to ASTM B213.
[0098] For example, particle size distribution can be of about 15
to about 45 .mu.m having a flowability less than 28 s, measured
according to ASTM B213.
[0099] For example, particle size distribution can be of about 15
to about 53 .mu.m having a flowability less than 36 s, measured
according to ASTM B213.
[0100] For example, particle size distribution can be of about 15
to about 53 .mu.m having a flowability less than 32 s, measured
according to ASTM B213.
[0101] For example, particle size distribution can be of about 15
to about 53 .mu.m having a flowability less than 30 s, measured
according to ASTM B213.
[0102] For example, particle size distribution can be of about 15
to about 53 .mu.m having a flowability less than 28 s, measured
according to ASTM B213.
[0103] For example, the raw reactive metal powder comprises a
particle size distribution of about 25 to about 45 .mu.m having a
flowability less than 36 s, measured according to ASTM B213.
[0104] For example, the raw reactive metal powder comprises a raw
reactive metal powder comprises a particle size distribution of
about 25 to about 45 .mu.m having a flowability less than 32 s,
measured according to ASTM B213.
[0105] For example, the raw reactive metal powder comprises a raw
reactive metal powder comprises a particle size distribution of
about 25 to about 45 .mu.m having a flowability less than 30 s,
measured according to ASTM B213.
[0106] For example, the raw reactive metal powder comprises a
particle size distribution of about 25 to about 45 .mu.m having a
flowability less than 25 s, measured according to ASTM B213.
[0107] For example, the raw reactive metal powder comprises a
particle size distribution of about 25 to about 53 .mu.m having a
flowability less than 36 s, measured according to ASTM B213.
[0108] For example, the raw reactive metal powder comprises a
particle size distribution of about 25 to about 53 .mu.m having a
flowability less than 32 s, measured according to ASTM B213.
[0109] For example, the raw reactive metal powder comprises a
particle size distribution of about 25 to about 53 .mu.m having a
flowability less than 30 s, measured according to ASTM B213.
[0110] For example, the raw reactive metal powder comprises a
particle size distribution of about 25 to about 53 .mu.m having a
flowability less than 25 s, measured according to ASTM B213.
[0111] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 75 .mu.m having a
flowability less than 26 s, measured according to ASTM B213.
[0112] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 75 .mu.m having a
flowability less than 25 s, measured according to ASTM B213.
[0113] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 75 .mu.m having a
flowability less than 24 s, measured according to ASTM B213.
[0114] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 75 .mu.m having a
flowability less than 23 s, measured according to ASTM B213.
[0115] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 106 .mu.m having a
flowability less than 26 s, measured according to ASTM B213.
[0116] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 106 .mu.m having a
flowability less than 25 s, measured according to ASTM B213.
[0117] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 106 .mu.m having a
flowability less than 24 s, measured according to ASTM B213.
[0118] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 106 .mu.m having a
flowability less than 23 s, measured according to ASTM B213.
[0119] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 150 .mu.m having a
flowability less than 26 s, measured according to ASTM B213.
[0120] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 150 .mu.m having a
flowability less than 25 s, measured according to ASTM B213.
[0121] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 150 .mu.m having a
flowability less than 24 s, measured according to ASTM B213.
[0122] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 150 .mu.m having a
flowability less than 23 s, measured according to ASTM B213.
[0123] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 180 .mu.m having a
flowability less than 26 s, measured according to ASTM B213.
[0124] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 180 .mu.m having a
flowability less than 25 s, measured according to ASTM B213.
[0125] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 180 .mu.m having a
flowability less than 24 s, measured according to ASTM B213.
[0126] For example, the raw reactive metal powder comprises a
particle size distribution of about 45 to about 180 .mu.m having a
flowability less than 23 s, measured according to ASTM B213.
[0127] For example, the heated metal source is contacted with said
at least one additive gas in an atomizing zone of an atomizer.
[0128] For example, the heated metal source is contacted with said
at least one additive gas within a heat zone of an atomizer.
[0129] For example, the heated metal source is contacted with said
at least one additive gas at substantially the same time as contact
with an atomizing gas.
[0130] For example, the atomizing gas is an inert gas.
[0131] For example, the atomizing gas and the additive gas are
mixed together prior to contact with the heated metal source.
[0132] For example, the contacting with the additive gas causes
formation of a first layer and a second layer on the surface of the
raw metal particles, said first layer comprising atoms of said
heated metal with atoms and/or molecules of said additive gas, said
first layer being a depletion layer deeper and thicker than a
native oxide layer, said second layer being a native oxide
layer.
[0133] For example, the first layer has a substantially positive
charge and the second layer has a substantially negative charge,
and wherein the first layer and the second layer have a combined
charge that is substantially neutral.
[0134] For example, the process further comprises: [0135] sieving
the raw reactive metal powder after atomizing of the heated metal
source to separate the raw reactive metal powder by particle size
distributions.
[0136] For example, the process further comprises: [0137] after
sieving, separately stirring the separated raw material powder in
water.
[0138] For example, the water is distilled water or demineralized
water.
[0139] For example, the flowability of the reactive metal powder is
measured on the dried sieved metal powder after having been
stirred.
[0140] For example, the reactive metal powder has an added content
of each electronegative atom and/or molecule from the additive gas
of less than 1000 ppm.
[0141] For example, the reactive metal powder has an added content
of each of said electronegative atom and/or molecule from the
additive gas of less than 500 ppm.
[0142] For example, the reactive metal powder has an added content
of each of said electronegative atom and/or molecule from the
additive gas of less than 250 ppm.
[0143] For example, the reactive metal powder has an added content
of each of said electronegative atom and/or molecule from the
additive gas of less than 200 ppm.
[0144] For example, the reactive metal powder has an added content
of each of said electronegative atom and/or molecule from the
additive gas of less than 150 ppm.
[0145] For example, the reactive metal powder has an added content
of each of said electronegative atom and/or molecule from the
additive gas of less than 100 ppm.
[0146] For example, the predetermined particle size is comprising
any particle size distributions of about 10-53 .mu.m such as 10-45
.mu.m, 15-45 .mu.m, 10-53 .mu.m, 15-53 .mu.m, and/or 25-45
.mu.m.
[0147] For example, the at least one additive gas is an
oxygen-containing gas.
[0148] For example, the at least one additive gas is an
oxygen-containing gas chosen from O.sub.2, CO.sub.2, CO, NO.sub.2,
air, water vapor and mixtures thereof.
[0149] For example, the at least one additive gas is a
halogen-containing gas.
[0150] For example, the halogen is F, Cl, Br or I.
[0151] For example, the at least one additive gas is a
hydrogen-containing gas.
[0152] For example, the at least one additive gas is a
sulfur-containing gas.
[0153] For example, the at least one additive gas is a
nitrogen-containing gas.
[0154] For example, the at least one additive gas is chosen from
O.sub.2, H.sub.2O, CO, CO.sub.2, NO.sub.2, N.sub.2, NO.sub.3,
Cl.sub.2, SO.sub.2, SO.sub.3, and mixtures thereof.
[0155] For example, the reactive metal powder comprises at least
one of titanium, zirconium, magnesium, and aluminum.
[0156] For example, the reactive metal powder is a metal powder
comprising at least one member chosen from one of titanium,
titanium alloys, zirconium, zirconium alloys, magnesium, magnesium
alloys, aluminum and aluminum alloys.
[0157] For example, the reactive metal powder comprises
titanium.
[0158] For example, the reactive metal powder comprises a titanium
alloy.
[0159] For example, the reactive metal powder comprises
zirconium.
[0160] For example, the reactive metal powder comprises a zirconium
alloy.
[0161] For example, the reactive metal powder is a metal powder
comprising at least one member chosen from one of titanium and
titanium alloys.
[0162] For example, the process is carried out by means of at least
one plasma torch.
[0163] For example, the process is carried out by means of at least
one plasma torch.
[0164] For example, the at least one plasma torch is a radio
frequency (RF) plasma torch.
[0165] For example, the least one plasma torch is a direct current
(DC) plasma torch.
[0166] For example, the least one plasma torch is a microwave (MW)
plasma torch.
[0167] Referring now to FIG. 1, therein illustrated is a
cross-section of an example of atomizing system 2'. The atomizing
system 2' includes a receptacle 8 that receives feed of a metal
source 16 from an upstream system. For example, the feed of metal
source 16 is provided as a melted stream, but it may be provided as
a metal rod or wire as well. The metal source may be heated
according to various techniques.
[0168] The heated metal source 16 is fed, through an outlet 24,
into an atomization zone 32, which is immediately contacted with an
atomizing fluid from an atomizing source 40. Contact of the heated
metal source 16 by the atomizing fluid causes raw reactive metal
powder 64 to be formed, which is then exited from the atomization
zone 32. For example, the atomizing fluid may be an atomizing gas.
For example, the atomizing gas may be an inert gas.
[0169] For example, the inert gas can be chosen from Ar and/or
He.
[0170] It will be understood that while an atomizing system 2'
having atomizing plasma torches 40, methods and apparatus described
herein for forming reactive metal powder having improved
flowability may be applied to other types of spherical powder
production system, such as skull melting gas atomization process,
electrode induction melting gas atomization process (EIGA process),
plasma rotating electrode process, plasma (RF, DC, MW)
spheroidization process, etc.
[0171] According to the illustrated example, the plasma source 40
includes at least one plasma torch. At least one discrete nozzle 48
of the at least one plasma torch 40 is centered upon the metal
source feed. For example, the cross-section of the nozzle 48 may be
tapered towards the metal source feed so as to focus the plasma
that contacts the metal source feed. As described elsewhere herein,
the nozzle 48 may be positioned so that the apex of the plasma jet
contacts the metal source fed from the receptacle 8. The contacting
of the metal source feed by the plasma from the at least one plasma
source 40 causes the metal source to be atomized.
[0172] Where a plurality of plasma torches are provided, the
nozzles of the torches are discrete nozzles 48 of the plasma
torches that are oriented towards the metal source from the
receptacle 8. For example, the discrete nozzles 48 are positioned
so that the apexes of the plasma jet outputted therefrom contacts
the metal source from the receptacle 8.
[0173] According to various exemplary embodiments for preparing
spheroidal powders, the heated metal source is contact with at
least one additive gas while carrying out the atomization
process.
[0174] The additive gas can be any gas comprising electronegative
atom or molecule. The additive gas may include fluorine, chlorine,
iodine, bromide, hydrogen-based, nitrogen-based and carbon-based
compounds.
[0175] The additive gas may be an oxygen-containing gas. The
expression "oxygen-containing gas" as used herein refers to a gas
that contains at least one atom of oxygen. For example, such a gas
may be O.sub.2, CO.sub.2, CO, NO.sub.2, air, water vapor, ozone,
etc.
[0176] According to various exemplary embodiments, the additive gas
contacts the heated metal source 16 within the atomization zone 32
of an atomizer. This atomization zone 32 is a high heat zone of the
atomizer. Accordingly, the heated metal source 16 may be contacted
by the atomization gas and the additive gas at substantially the
same time within the atomization zone 32.
[0177] The reaction between the metal particles produced from the
atomization of the heated metal source and the additive gas can
take place as long as the metal particles are sufficiently hot to
allow the electronegative atoms and/or molecules to diffuse several
tens of nanometers into the surface layer.
[0178] It will be understood that according to various exemplary
embodiments described herein, the additive gas contacts the heated
metal source during the atomization process in addition to the
contacting of the heated metal source with the atomizing fluid.
[0179] It will be further understood that according to existing
atomization processes, some additive gas may be inherently
introduced into the atomizing fluid, such as through contamination,
latent impurities, or leaks. For example, the introduced additive
gas may include air or oxygen.
[0180] However, according to various exemplary embodiments
described herein for producing spheroidal powders, the additive gas
for contacting the heated metal source is deliberately provided in
addition to any additive gas that could be inherently introduced
during the atomization process.
[0181] According to various exemplary embodiments, a first set of
nozzles projects the atomizing fluid into the atomization zone 32
to contact the heated metal source 16 and a second set of nozzles
injects the additive gas into the atomization zone 32 to contact
the heated metal source 16. Another alternative is that the second
set of nozzles can mix the additive gas in a compatible fluid with
the atomizing fluid prior to inject into the atomization zone 32.
For example, the atomizing fluid and the additive gas contact the
heated metal source 16 at substantially the same time or slightly
after. For example, it is possible to mix the additive gas to
dilute such additive gas and avoid too large local concentration
that could result in an adverse or undesired reaction.
[0182] According to various alternative exemplary embodiments, the
atomizing fluid is an atomizing gas, which is mixed with the at
least one additive gas to form an atomization mixture. For example,
the atomizing gas and the additive gas are mixed together prior to
contact with the heated metal source. The atomizing gas and the
additive gas may be mixed together within a gas storage tank or a
pipe upstream of the contacting with the heated metal source. For
example, the additive gas may be injected into a tank of atomizing
gas. The injected additive gas is in addition to any additive gas
inherently present into the atomizing gas.
[0183] The amount of additive gas contacting the heated metal
source may be controlled based on desired end properties of the
reactive metal powders to be formed from the atomization
process.
[0184] For example, the additive gas contained within the formed
reactive metal powder may be viewed as a contaminant of the metal
powder. Accordingly, the amount of additive gas contacting the
heated metal source is controlled so that the amount of atoms
and/or molecules of the additive gas contained within the reactive
metal powder is maintained within certain limits.
[0185] For example, the chemical composition limit within reactive
metal powder may be prescribed by appropriate standards, such as
the composition in table 1 of AMS 4998, ASTM F3001, ASTM F2924,
ASTM B348, ASTM B350 and in table 3 of ASTM B550. Accordingly, the
amount of additive gas contacting the heated metal source is
controlled based on the composition of the additive gas and the
limit or limits prescribed by standard for the one or more atoms
and/or molecules composing the additive gas.
[0186] For example, where the additive gas contains oxygen and the
reactive metal powder to be formed is titanium alloy powder, the
amount of additive gas contacting the heated metal source is
controlled so that the amount of oxygen within the formed reactive
metal powder is below 1800 ppm according to the AMS 4998 standard
and is below 1300 ppm according to ASTM F3001.
[0187] For example, where the additive gas contains carbon and the
reactive metal powder to be formed is titanium alloy powder, the
amount of additive gas contacting the heated metal source is
controlled so that the amount of carbon within the formed reactive
metal powder is below 1000 ppm according to the AMS 4998 standard
and is below 800 ppm according to ASTM F3001.
[0188] For example, where the additive gas contains hydrogen and
the reactive metal powder to be formed is titanium alloy powder,
the amount of additive gas contacting the heated metal source is
controlled so that the amount of hydrogen within the formed
reactive metal powder is below 120 ppm according to the AMS 4998
standard and ASTM F3001.
[0189] For example, where the additive gas contains nitrogen and
the reactive metal powder to be formed is titanium alloy powder,
the amount of additive gas contacting the heated metal source is
controlled so that the amount of nitrogen within the formed
reactive metal powder is below about 400 ppm according to the AMS
4998 standard and is below 500 ppm according to ASTM F3001.
[0190] For example, where the additive gas contains chlorine and
the reactive metal powder to be formed is titanium metal powder,
the amount of additive gas contacting the heated metal source is
controlled so that the amount of chlorine within the formed
reactive metal powder is below about 1000 ppm according to the ASTM
F3001 standard.
[0191] For example, the amount of additive gas contacting the
heated metal source may be controlled by controlling the quantity
of additive gas injected into the atomization gas when forming the
atomization mixture. For example, the amount of additive gas
injected may be controlled to achieve one or more desired ranges of
ratios of atomization gas to additive gas within the formed
atomization mixture.
[0192] For reactive metal powders formed without the addition of an
additive gas, it was observed that reactive metal powders having
various different particle size distributions and that had
undergone sieving and blending steps did not always flow
sufficiently to allow measurement of their flowability in a Hall
flowmeter (see FIG. 1 of ASTM B213). For example, reactive metal
powder falling within particle size distributions between 10-53
.mu.m did not flow in a Hall flowmeter according to ASTM B213.
[0193] Without being bound by the theory, one important factor for
causing the poor flowability of reactive metal powder is its
sensitivity to static electricity. The sieving, blending and
manipulation steps may cause particles of the reactive metal powder
to collide with one another, thereby increasing the level of static
electricity. This static electricity further creates cohesion
forces between particles, which causes the reactive metal powder to
flow poorly.
[0194] The raw reactive metal powder formed from atomizing the
heated metal source by contacting the heated metal source with the
atomization gas and the additive gas is further collected. The
collected raw reactive metal powder contains a mixture of metal
particles of various sizes. The raw reactive metal powder is
further sieved so as to separate the raw reactive metal powder into
different size distributions, such as 10-45 .mu.m, 15-45 .mu.m,
10-53 .mu.m, 15-53 .mu.m, and/or 25-45 .mu.m.
[0195] After sieving, each particle size distribution of metal
powder is separately stirred in distilled water or demineralized
water. The stirring may help to remove electrostatic charges
accumulated on the surface of the particles of the metal
powder.
[0196] After sieving, each particle size distributions of metal
powder is separately left to dry.
[0197] It was observed that reactive metal powders formed according
to various exemplary atomization methods described herein in which
the heated metal source is contacted with the additive gas
exhibited substantially higher flowability than reactive metal
powders formed from an atomization methods without the contact of
the additive gas. This difference in flowability between metal
powders formed according to the different methods can mostly be
sized in metal powders having the size distributions of 10-45
.mu.m, 15-45 .mu.m, 10-53 .mu.m, 15-53 .mu.m and/or 25-45 .mu.m or
similar particle size distributions. However, it will be understood
that metal powders in other size distributions may also exhibit
slight increase in flowability when formed according to methods
that include contact of the heated metal source with the additive
gas.
[0198] It is well known that titanium forms a native surface oxide
layer once exposed to air. This layer is typically about 3-5 nm and
is composed essentially of titanium oxides (S. Axelsson, 2012, p.
37). The native oxide acts as a passivation layer and reduces the
reactivity. This native layer has a strong affinity with water
vapour (hydrophilic) and possesses hydroxyl group at the surface
(Tanaka et al., 2008, p. 1; Lu et al., 2000, p. 1).
[0199] Without being bound by the theory, from contact of the
heated metal source with the additive gas during atomization, atoms
and/or molecules of the additive gas react with particles of the
reactive metal powder as these particles are being formed.
Accordingly, a first layer formed of a compound of the heated metal
with the additive gas and that is depleting through the thickness
is formed on the outer surface of the particles of the reactive
metal particle. This layer is thicker and deeper in the surface and
is located below the native oxide layer. For example, the compound
of the heated metal with the additive gas in the depleted layer is
metal oxide, nitride, carbide or halide. Since the atoms of the
additive gas are depleting through the thickness of the surface
layer, it forms a non stoichiometric compound with the metal. Such
compound causes this first layer to have a substantially positive
charge.
[0200] This first layer can only be formed at high temperature
since the electronegative atoms and/or molecules need to have
enough energy to diffuse much more into the surface layer than in a
native oxide layer.
[0201] A second layer being a native oxide layer is further formed
on the surface of the particles of the reactive metal powder. The
hydroxyl group formed at the surface causes the second layer to
have a substantially negative charge.
[0202] The first layer having a substantially positive charge and
the second layer having a substantially negative charge form
together an electric double layer. The combined charge of the
double layer has a substantially neutral charge (i.e. net charge
tending to zero). This neutral charge on the surface of the
particles of the reactive metal powder may contribute to the
improved flowability of the reactive metal powder formed according
to exemplary methods and apparatuses described herein. For example,
whereas a net charge on a particle, such as one formed according to
traditional atomization methods, will favor polarization of the
particle and increase the interaction with other particles, a
weakly charged particle will have little electric interaction with
other particles. This decreased interaction may lead to superior
flowability.
[0203] FIG. 2 illustrates a schematic diagram of a particle 100 of
reactive metal powder formed according to an atomization processes
in which the heated metal source 16 is not contacted with the
additive gas. The formed particle 100 generally includes a particle
body 108 (for example a Ti-6Al-4V particle) and a surface native
oxide layer 116. The surface native oxide layer 116 has a generally
negative charge, which gives the formed particle 100 a net non-zero
charge (i.e for particle 108, Q.sub.net.noteq.0). Such negative
charge gives a greater ability to polarize. The particle 108 also
comprises hydroxyl groups at the surface 116.
[0204] FIG. 3 illustrates a schematic diagram of a particle 140 of
reactive metal powder formed according to exemplary atomization
methods described herein in which the heated metal source 16 is
contacted with an additive gas. A first layer 148 (or layer 1) is
formed on the outer surface of the particle body 156 (for example a
Ti-6Al-4V particle). It results from the compounding of the heated
metal with the electronegative atoms and/or molecules that are
depleting through the thickness. A second layer 164 (or layer 2)
being a native oxide layer is further formed on the surface of the
particle body 156. As described elsewhere herein, the first layer
148 and the second layer 164 have a combined charge that is
substantially neutral, thereby causing the formed particle 140 to
have a substantially net zero charge (Q.sub.net.apprxeq.0) and a
lower ability to polarize.
[0205] Following the theory that the electronegative atoms and/or
molecules from the additive gas become a surface additive on the
particles of the raw metal powder formed, the amount of additive
gas injected with the atomization gas to form an atomization
mixture may be controlled as it varies quasi linearly with the
production rate of metal powder having a predetermined particle
size distribution. The amount of additive gas needed to form the
layer 1 is related to the total surface area of the metal particles
which depends of the production rate and particle size
distributions (see FIG. 4). The concentration of the additive gas
and the thermal conditions of the metal particles will determine
the depleting layer depth of the layer 1.
[0206] Further following the theory that the electronegative atoms
and/or molecules from the additive gas become a surface additive on
particles of the raw metal powder formed, the amount of additive
gas injected with the atomization gas to form an atomization
mixture may be controlled as it varies with the total area of the
particles of the metal powder formed as shown in FIG. 4.
[0207] Further following the theory that the electronegative atoms
and/or molecules from the additive gas become a surface additive on
particles of the raw metal powder formed, the amount of additive
gas injected with the atomization gas to form an atomization
mixture may be controlled as it varies with the temperature of the
surface of the particles of the raw metal powder formed. The
reaction rate .PHI. of such chemical reaction of activation energy
E generally follows an Arhenius relation with the temperature
T:
.PHI..varies.eE/kT
The injection of the additive gas at high temperature is thus more
efficient and requires less additive gas concentration to generate
the ideal depletion depth and form the layer 1.
[0208] FIG. 4 illustrates a schematic diagram of a particle 180
having a radius R and a depletion depth of .delta. at the surface
of the particle 188. The total surface area of the particle is
S.sub.1=4.pi.R.sup.2.
[0209] FIG. 4 further illustrates a schematic diagram of a
plurality of particles (n particles) 200 of the same size having
the same total mass as the mass of the particle 180. The particles
200 are smaller in size than particle 180 but they have a larger
surface area in total than particle 180. each particle 200 having a
radius r and the total number of particles being n=R.sup.3/r.sup.3.
The combined surface area of the particles 200 is
S.sub.2=n4.pi.r.sup.2=R/rS.sub.1. It increases linearly with
decreasing radius of particles.
[0210] The amount of surface additive added is thus a function of
the total surface area as the volume that will be treated is the
product of the total surface area by the depletion depth.
[0211] For example, the obtained metal powders can have less than
about 100 150, 200, 300, 500, 1000 or 1500 ppm of an
electronegative atom and/or molecule (for example an
electronegative atom and/or molecule element that is comprised
within the additive gas used to produce the powder).
Experiment 1
[0212] Four different lots of powder were produced by plasma
atomization under the same experimental conditions except for the
composition of the atomization mixture contacting the heated metal
source.
[0213] The atomizing gas is high purity argon (>99.997%).
[0214] In Tests 1 and 2, only the atomizing gas was used to contact
the heated metal source during the atomization process.
[0215] In Test 3, air was injected to the high purity argon to form
an atomization mixture of 80 ppm of air with argon. Heated metal
was contacted with the atomization mixture during the atomization
process.
[0216] In Test 4, O.sub.2 was injected to the high purity argon to
form an atomization mixture of 50 ppm of O.sub.2 with argon. Heated
metal was contacted with this second atomization mixture during the
atomization process.
[0217] After contacting with the atomizing gas (Test 1 and 2) or
the atomization mixture (Test 3 and 4), formed raw reactive metal
powder is sieved to isolate the 15-45 .mu.m particle size
distributions.
[0218] The sieved powder is then mixed to ensure homogeneity.
[0219] The powder was further stirred in distilled water or
demineralized water to remove static electricity charges
accumulated during previous steps.
[0220] The powder was dried in air at 80.degree. C. for 12 h.
[0221] FIG. 5 is a graph illustrating the oxygen profile comparison
between different samples by TOF-SIMS. The TOF-SIMS signature of
powder is obtained for Test 1 to 4. The presence of a depletion
layer can be associated with the high flowability powders as can be
seen in Table 1.
[0222] The TOF-SIMS signature of a fine powder that has been
treated can be clearly seen from the FIG. 5. A tail in the oxygen
content enters deeper in the surface layer. It is critical to
obtain this depletion layer with a certain critical depth in order
to get the improved flowability behavior. The TOF-SIMS results
suggest that the depletion layer has a depth of the order of 100
nm. The depth can be estimated by calibrating the sputtering rate
of the ion beam obtained on a Ti-6Al-4V bulk part with a
profilometer. The sputtering rate depends of the ion beam intensity
and of the type of material. The calibration is done prior to
measurements and the ion beam energy is very stable.
TABLE-US-00001 TABLE 1 Test 1 to 4 description with flowability and
apparent density measured on a 15-45 .mu.m particle size
distribution Visual compaction Additive gas Apparent in the
collection Concentration Flowability density bucket after Lot #
(ppm) (s) (g/cm.sup.3) atomization Test 1 0 NF NA bad Test 2 0 NF
NA bad Test 3 80 ppm air 27.3 2.51 good Test 4 50 ppm O2 27 2.50
good Per ASTM Per ASTM B213 B212
TABLE-US-00002 TABLE 2 Powder chemical composition of Test 1 to 4
on a 15-45 .mu.m particle size distribution Chemical Composition
(wt. %) Lot # O N H C Fe Al V Ti Test 1 0.102 0.007 0.0043 0.008
0.13 6.35 3.94 88.94 Test 2 0.094 0.01 0.0022 0.016 0.21 6.37 3.91
88.85 Test 3 0.084 0.025 0.0016 0.01 0.21 6.39 3.87 88.87 Test 4
0.112 0.005 0.0084 0.011 0.13 6.33 3.82 89.03 Per ASTM E1409 Per
ASTM E1447 Per ASTM E1941 Per ASTM E2371
TABLE-US-00003 TABLE 3 Particle size distributions of Test 1 to 4
on a 15-45 .mu.m particle size distribution Particle size
distribution (wt. %) Lot # >53 >45 .ltoreq.45 > 25 <25
Total D10 D50 D90 Test 1 0 2.2 80.6 17.2 100 20.9 33.0 43.6 Test 2
0.5 1.5 72.2 25.8 100 21.4 33.3 44.7 Test 3 0.1 2.2 71.9 25.8 100
22.5 33.7 44.3 Test 4 0 3.0 69.0 28.0 100.0 22.6 34.1 45.5 Per ASTM
B214 Per ASTM B822
[0223] It was determined from statistical data analysis of many
batches that the injection of air (Test 3) adds about 100-150 ppm
of nitrogen and about 50 ppm of oxygen to the powder. The injection
of air improved flowability of the formed reactive metal
powder.
[0224] It was further determined from statistical data analysis
that injection of only O.sub.2 (Test 4) adds about 150-200 ppm of
oxygen and no nitrogen.
[0225] Additional successful tests on the flowability of 15-45
.mu.m particle size distribution have been carried by injecting
water vapor. Improvement of flowability of 15-45 .mu.m particle
size distribution was also observed.
[0226] The treatment performed maintains a satisfying chemical
composition according to the composition of standard ASTM B348,
ASTM F2924 and ASTM F3001. It would have also complied with those
of AMS 4998 if the oxygen of the raw material would have been
slightly higher.
[0227] FIG. 6 is a photograph of a batch of about 100 kg of metal
powder formed according to an atomization process that does not
include contacting with the additive gas. Due to agglomerates, 90%
of the collecting bucket is filled and the visual compaction is
bad.
[0228] FIG. 7 is a photograph of a batch of about 100 kg of metal
powder formed according to an atomization process in which the
metal source is contacted with the additive gas. Due to improved
flowability and lower surface interactions between particles, 20%
of the collecting bucket is filled for the same amount of material
as used during the run of FIG. 6 and the visual compaction is
good.
[0229] Tests similar to Test 3 and 4 have been carried by
intermittently injecting the additive gas. It was found that the
treatment was still effective while having the advantage of adding
less impurity to the final product.
[0230] Similarly, we showed that a mixture of up to 30% of powder
with good flowability can be blended with 70% of powder that did
not flow in Hall flowmeter and the resulting powder was still
flowing even if not as well as the starting powder.
Experiment 2
[0231] Heat treatment was performed a posteriori on already-formed
metal powder that was formed from a process in which additive gas
was not used.
[0232] More specifically, the already-formed metal powder was
heated in air atmosphere at about 250.degree. C. for 12 hours. It
was expected that this heating would cause addition of oxygen to
surface of particles of the raw metal powder and increase the
thickness of the native oxide layer.
[0233] It was observed that oxidation/nitridation a posteriori did
not produce a similar result to that of contacting the additive gas
in the atomization zone of an atomization process. The improvement
of the flowability of the metal powder was not observed.
[0234] It seems that a posteriori heating of already-formed metal
powder will only thicker the native oxide layer and did not have
the ability to provide a sufficient deep and depletion
oxide/nitride layer on the particle. The thicker oxide layer will
also remain quasi stoichiometric and will not be able to provide
the positively charged layer 1 which is provided by the depletion
layer.
[0235] Without being bound to the theory, the high temperature
involved during the atomization and the low concentration of
additive gas enable the oxidation/nitridation reaction that forms
the depletion oxide/nitride layer when the metal source is
contacted with the additive gas.
[0236] Embodiments of paragraphs [0027] to [00192] of the present
disclosure are presented in such a manner in the present disclosure
so as to demonstrate that every combination of embodiments, when
applicable can be made. These embodiments have thus been presented
in the description in a manner equivalent to making dependent
claims for all the embodiments that depend upon any of the
preceding claims (covering the previously presented embodiments),
thereby demonstrating that they can be combined together in all
possible manners. For example, all the possible combination, when
applicable, between the embodiments of paragraphs [0027] to [00192]
and the processes of paragraphs [0006] to [0026] are hereby covered
by the present disclosure.
[0237] It will be appreciated that, for simplicity and clarity of
illustration, where considered appropriate, reference numerals may
be repeated among the figures to indicate corresponding or
analogous elements or steps. In addition, numerous specific details
are set forth in order to provide a thorough understanding of the
exemplary embodiments described herein. However, it will be
understood by those of ordinary skill in the art that the
embodiments described herein may be practiced without these
specific details. In other instances, well-known methods,
procedures and components have not been described in detail so as
not to obscure the embodiments described herein. Furthermore, this
description is not to be considered as limiting the scope of the
embodiments described herein in any way but rather as merely
describing the implementation of the various embodiments described
herein.
* * * * *