U.S. patent application number 15/887848 was filed with the patent office on 2018-11-15 for deposition of licoo2.
This patent application is currently assigned to DEMARAY, LLC. The applicant listed for this patent is DEMARAY, LLC. Invention is credited to R. Ernest Demaray, Hongmei Zhang.
Application Number | 20180331349 15/887848 |
Document ID | / |
Family ID | 36578644 |
Filed Date | 2018-11-15 |
United States Patent
Application |
20180331349 |
Kind Code |
A1 |
Zhang; Hongmei ; et
al. |
November 15, 2018 |
DEPOSITION OF LiCoO2
Abstract
In accordance with the present invention, deposition of
LiCoO.sub.2 layers in a pulsed-dc physical vapor deposition process
is presented. Such a deposition can provide a low-temperature, high
deposition rate deposition of a crystalline layer of LiCoO.sub.2
with a desired <101> or <003> orientation. Some
embodiments of the deposition address the need for high rate
deposition of LiCoO.sub.2 films, which can be utilized as the
cathode layer in a solid state rechargeable Li battery, Embodiments
of the process according to the present invention can eliminate the
high temperature (>700.degree. C.) anneal step that is
conventionally needed to crystallize the LiCoO.sub.2 layer.
Inventors: |
Zhang; Hongmei; (San Jose,
CA) ; Demaray; R. Ernest; (Portola Valley,
CA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
DEMARAY, LLC |
Portola Valley |
CA |
US |
|
|
Assignee: |
DEMARAY, LLC
PORTOLA VALLEY
CA
|
Family ID: |
36578644 |
Appl. No.: |
15/887848 |
Filed: |
February 2, 2018 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
14136842 |
Dec 20, 2013 |
9887414 |
|
|
15887848 |
|
|
|
|
11297057 |
Dec 7, 2005 |
8636876 |
|
|
14136842 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
H01M 4/661 20130101;
H01M 10/052 20130101; H01M 4/0428 20130101; Y10T 29/49115 20150115;
H01M 4/131 20130101; H01M 4/0423 20130101; H01M 10/0585 20130101;
H01M 6/185 20130101; C23C 14/08 20130101; H01M 4/0471 20130101;
H01M 4/66 20130101; H01M 4/525 20130101; H01M 10/0562 20130101;
H01M 4/667 20130101; H01M 2300/0071 20130101; H01M 6/188 20130101;
C23C 14/35 20130101; H01M 2004/028 20130101; H01M 2300/002
20130101; H01M 4/1391 20130101; Y02E 60/10 20130101; C23C 14/5806
20130101; H01M 4/0426 20130101; H01M 6/46 20130101 |
International
Class: |
H01M 4/04 20060101
H01M004/04; H01M 4/66 20060101 H01M004/66; C23C 14/08 20060101
C23C014/08; C23C 14/35 20060101 C23C014/35; C23C 14/58 20060101
C23C014/58; H01M 10/0585 20100101 H01M010/0585; H01M 10/0562
20100101 H01M010/0562; H01M 10/052 20100101 H01M010/052; H01M 6/46
20060101 H01M006/46; H01M 6/18 20060101 H01M006/18; H01M 4/525
20100101 H01M004/525; H01M 4/1391 20100101 H01M004/1391; H01M 4/131
20100101 H01M004/131 |
Claims
1-46. (canceled)
47. A method of making a battery, comprising: depositing a first
conducting layer over a substrate; depositing a first crystalline
LiCoO.sub.2 layer over the first conducting layer by applying
pulsed DC power to a densified conductive ceramic LiCoO.sub.2
sputter target that includes at least one dopant of Ni, Si, or Nb,
the deposited first crystalline LiCoO.sub.2 layer having a columnar
structure; depositing a first LiPON (Li.sub.xPO.sub.yN.sub.z) layer
over the first crystalline LiCoO.sub.2 layer; depositing a first
anode layer over the first LiPON (Li.sub.xPO.sub.yN.sub.z) layer;
and depositing a second conducting layer over the first anode
layer.
48. The method of claim 47, further comprising: depositing a
stacked battery over the second conducting layer in a parallel
arrangement, wherein the parallel arrangement includes: depositing
a second anode layer over the second conducting layer; depositing a
second LiPON (Li.sub.xPO.sub.yN.sub.z) layer over the second anode
layer; and depositing a second crystalline LiCoO.sub.2 layer over
the second LiPON (Li.sub.xPO.sub.yN.sub.z) layer.
49. The method of claim 47, further comprising: depositing a
stacked battery over the second conducting layer in a series
arrangement, wherein the series arrangement includes: depositing a
second crystalline LiCoO.sub.2 layer over the second conducting
layer; depositing a second LiPON (Li.sub.xPO.sub.yN.sub.z) layer
over the second crystalline LiCoO.sub.2 layer; and depositing a
second anode layer over the second LiPON (Li.sub.xPO.sub.yN.sub.z)
layer.
50. The method of claim 47, further comprising: preheating the
substrate to a temperature of about 200.degree.C.
51. The method of claim 47, further comprising: depositing a
lift-off layer between the substrate and the bottom conducting
layer, the lift-off layer including one or more materials selecting
from the group consisting of polyimide, CaF.sub.2, and carbon; and
lifting off the battery from the substrate using one or more
processes selected from the group consisting of applying oxidation,
heat, light, and a combination thereof to the lift-off layer.
52. The method of claim 47, wherein depositing the crystalline
LiCoO.sub.2 layer includes: flowing a gaseous mixture including
argon and oxygen through a chamber for depositing the crystalline
LiCoO.sub.2; applying the pulsed DC power to the densified
conductive ceramic LiCoO.sub.2 sputter target; applying an RF bias
power to the substrate; filtering the RF bias power with a
narrow-band rejection filter from coupling into the pulsed DC
power; and depositing the crystalline LiCoO.sub.2 layer having the
columnar structure, wherein the densified conductive ceramic
LiCoO.sub.2 sputter target has a resistivity in a range from about
3 k.OMEGA, to about 10 k.OMEGA.
53-56. (canceled)
Description
RELATED APPLICATION
[0001] The present application claims priority to Provisional
Application No. 60/651,363, filed on Feb. 8, 2005, by Hongmei Zhang
and Richard E. Demaray, and to Provisional Application No.
60/634,818, filed on Dec. 8, 2004, by the same inventors, each of
which is herein incorporated by reference in its entirety.
BACKGROUND
1. Field of the Invention
[0002] The present invention is related to thin-film solid-state
batteries and, in particular, the deposition of LiCoO.sub.2 films
and layers for battery manufacture.
2. Discussion of Related Art
[0003] Solid-state thin-film batteries are typically formed by
stacking thin films on a substrate in such a way that the films
cooperate to generate a voltage. The thin films typically include
current collectors, a cathode, an anode, and an electrolyte. The
thin films can be deposited utilizing a number of deposition
processes, including sputtering and electroplating. Substrates
suitable for this application have conventionally been high
temperature materials capable of withstanding at least one high
temperature anneal process to at least 700.degree. C. for up to
about 2 hours in air so as to crystallize the LiCoO.sub.2 film.
Such a substrate can be any suitable material with appropriate
structural and material properties, for example a semiconductor
wafer, metallic sheet (e.g., titanium or zirconium), ceramic such
as alumina, or other material capable of withstanding subsequent
high temperature processing in the presence of the LiCoO.sub.2,
which can experience significant interfacial reactions with most
materials utilized in a battery during these temperature
cycles.
[0004] Other lithium containing mixed metal, oxides besides
LiCoO.sub.2, including Ni, Nb, Mn, V, and sometimes also Co, but
including other transition metal oxides, have been evaluated as
crystalline energy storage cathode materials. Typically, the
cathode material is deposited in amorphous form and then the
material is heated in an anneal process to form the crystalline
material. In LiCoO.sub.2, for example, an anneal at or above
700.degree. C. transforms the deposited amorphous film to a
crystalline form. Such a high temperature anneal, however, severely
limits the materials that can be utilized as the substrate, induces
destructive reaction with the lithium containing cathode material
and often requires the use of expensive noble metals such as gold.
Such high thermal budget processes (i.e., high temperatures for
extended periods of time) are incompatible with semiconductor or
MEM device processing and limit the choice of substrate materials,
increase the cost, and dec the yield of such batteries.
[0005] It is known that crystallization of amorphous LiCoO.sub.2 on
precious metals can he achieved. An example of this crystallization
is discussed in Kim et al., where a conventional furnace anneal at
700.degree. C. for 20 minutes of an amorphous layer of LiCoO.sub.2
on a precious metal achieves crystallization of the LiCoO.sub.2
material, as shown by x-ray diffraction data. Kim, HanKi and Yoon,
Young Soo, "Characteristics of rapid-thermal-annealed LiCoO.sub.2,
cathode film for an all-solid-state thin film microbattery," J.
Vac. Sci. Techn. A 22(4), July/August 2004. In Kim et al., the
LiCoO.sub.2 film was deposited on a platinum film that was
deposited on a high-temperature MgO/Si substrate. In Kim et al, it
was shown that such a crystalline film is capable of constituting
the Li+ ion containing cathode layer of a functional all
solid-state Li+ ion battery.
[0006] There are many references that disclose an son beam assisted
process that can provide a LiCoO.sub.2 film that demonstrates some
observable crystalline composition by low angle x-ray diffraction
(XRD). Some examples of these are found in U.S. patent application
Ser. No. 09/815,983 (Publication No. US 2002/001747), Ser. No.
09/815,621 (Publication No. US 2001/0032666), and Ser. No.
09/815,919 (Publication No. US 2002/0001746). These references
disclose the use of a second front side ion beam or other ion
source side-by-side with a deposition source so as to obtain a
region of overlap of the flux of ions with the flux of LiCoO2 vapor
at the substrate surface. None of these references disclose film
temperature data or other temperature data of the film during
deposition to support an assertion of low temperature
processing.
[0007] It is very difficult to form a uniform deposition either by
sputtering a material layer or by bombardment with an ion flux.
Utilization of two uniform simultaneous distributions from two
sources that do not occupy the same position and extent with
respect to the substrate enormously increases the difficulties
involved in achieving a uniform material deposition. These
references do not disclose a uniform materials deposition, which is
required for reliable production of thin-film batteries. A well
understood specification for material uniformity for useful battery
products is that a 5% one-sigma material uniformity is standard in
thin film manufacturing. About 86% of the films with this
uniformity will be found acceptable for battery production.
[0008] It is even more difficult to scale a substrate to
manufacturing scale, such as 200 mm or 300 mm. Indeed, in the
references discussed above that utilize both a sputtering
deposition and an ion beam deposition, only small area targets and
small area substrates are disclosed. These references disclose a
single feasibility result. No method for achieving a uniform
distribution from two separate front side sources has been
disclosed in these references.
[0009] Further, conventional materials and production processes can
limit the energy density capacity of the batteries produced,
causing a need for more batteries occupying more volume. It is
specifically desirable to produce batteries that have large amounts
of stored energy per unit volume in order to provide batteries of
low weight and low volume.
[0010] Therefore, there is a need for a low temperature process for
depositing crystalline material, for example LiCoO.sub.2 material,
onto a substrate. In particular, there is a need for processes that
allow production of cathodic lithium films for a battery structure
with a low enough thermal budget to allow production of functional
structures on low temperature materials such as stainless steel,
aluminum, or copper foil.
SUMMARY
[0011] In accordance with the present invention, deposition of
LiCoO.sub.2 layers in a pulsed-dc physical vapor deposition process
is presented, Such a deposition can provide a low-temperature, high
deposition rate deposition of a crystalline layer of LiCoO.sub.2
with a desired <101> orientation. Some embodiments of the
deposition address the need for high rate deposition of LoCoO.sub.2
films, which can be utilized as the cathode layer in a solid state
rechargeable Li battery. Embodiments of the process according to
the present invention can eliminate the high temperature
(>700.degree. C.) anneal step that is conventionally needed to
crystallize the LiCoO.sub.2 layer.
[0012] A method of depositing a LoCiO.sub.2 layer according to some
embodiments of the present invention includes placing a substrate
in a reactor; flowing a gaseous mixture including argon and oxygen
through the reactor; and applying pulsed-DC power to a target
formed of LiCoO.sub.2 positioned opposite the substrate. In some
embodiments, a LiCoO.sub.2 layer is formed on the substrate,
Further, in some embodiments the LiCoO.sub.2 layer is a crystalline
layer of orientation <101>.
[0013] In some embodiments, a stacked battery structure cart be
formed. The stacked battery structure includes one or more battery
stacks deposited on a thin substrate, wherein each battery stack
includes; a conducting layer, a crystalline LiCoO.sub.2 layer
deposited over the conducting layer, a LiPON layer deposited over
the LiCoO.sub.2 layer; and an anode deposited over the LiPON layer.
A top conducting layer can be deposited over the one or more
battery stacks.
[0014] In some embodiments, a battery structure can be formed in a
cluster tool. A method of producing a battery in a cluster tool
includes loading a substrate into a cluster tool; depositing a
conducting layer over the substrate in a first chamber of the
cluster tool; depositing a crystalline LiCoO.sub.2 layer over the
conducting layer in a second chamber of the cluster tool;
depositing a LiPON layer over the LiCoO.sub.2 layer in a third
chamber of the duster tool; depositing an anode layer over the
LiCoO.sub.2 layer in a fourth chamber; and depositing a second
conducting layer over the LiPON layer in a fifth chamber of the
cluster tool.
[0015] A fixture for holding a thin substrate can include a top
portion and a bottom portion, wherein the thin substrate is held
when the top portion is attached to the bottom portion.
[0016] These and other embodiments of the invention, are further
discussed below with reference to the following figures. It is to
be understood that both the foregoing general description and the
following detailed description are exemplary and explanatory only
and are not restrictive of the invention, as claimed. Further,
specific explanations or theories regarding the deposition or
performance of certain layers during deposition processes or in the
performance of devices incorporating those layers are presented for
explanation only and are not to be considered limiting with respect
to the scope of the present disclosure or the claims.
BRIEF DESCRIPTION OF THE DRAWINGS
[0017] FIGS. 1A and 1B illustrate a pulsed-DC biased reactive
deposition apparatus that can be utilized in the methods of
depositing according to the present invention.
[0018] FIG. 2 shows an example of a target that can be utilized in
the reactor illustrated in FIGS. 1A and 1B.
[0019] FIG. 3 illustrates a thin-film battery design according to
some embodiments of the present invention.
[0020] FIGS. 4A and 4B show an x-ray diffraction analysis of and an
SEM photograph of a LiCoO.sub.2 film deposited according to
embodiments of the present invention.
[0021] FIGS. 5A through 5E show SEM photographs of LiCoO.sub.2
films according to some embodiments of the present invention.
[0022] FIG. 6A illustrates a layer of LiCoO.sub.2 deposited
according to some embodiments of the present invention on a thin
substrate.
[0023] FIG. 6B illustrates a layer of LiCoOi deposited according to
some embodiments of the present invention over a conducting layer
on a thin substrate.
[0024] FIGS. 7A, 7B, 7C, and 7D illustrate a thin substrate mount
and mask arrangement that can be utilized in the deposition of
LiCoO.sub.2 layers deposited according to some embodiments of the
present invention.
[0025] FIG. 8 illustrates a cluster tool that can be utilized to
form batteries with LiCoO.sub.2 layers deposited according to some
embodiments of the present invention.
[0026] FIGS. 9A and 9B illustrate examples of stacked batter
structures with LiCoO.sub.2 layers deposited according to some
embodiments of the present invention.
[0027] FIGS. 10A through 10D illustrate deposition and anneal steps
for LiCoO.sub.2 deposited over an iridium layer on a silicon
wafer.
[0028] FIGS. 11A through 11D illustrate a single layer battery
formed over an iridium layer according to some embodiments of the
present invention.
[0029] FIG. 12 illustrates battery performance utilizing films
deposited according to some embodiments of the present
invention.
[0030] In the figures, elements having the same designation have
the same or similar functions.
DETAILED DESCRIPTION
[0031] In accordance with embodiments of the present invention,
LiCoO.sub.2 films are deposited on a substrate by a pulsed-dc
physical vapor deposition (PVD) process. In contrast to, for
example, Kim et al., LiCoO.sub.2 films according to some
embodiments of the present Invention provide a crystalline
LiCoO.sub.2 film as deposited on a substrate at a substrate
temperature as low as about 220.degree. C. during deposition,
without the use of a metallic nucleation or barrier underlying
film. The as-deposited crystalline LiCoO.sub.2 films can be easily
ripened to very high crystalline condition by anneal. In addition,
the as deposited crystalline films, when positioned on a noble
metal film can be annealed at much further reduced temperatures,
for example as low as 400 to 500.degree. C. instead of 700.degree.
C., providing for deposition, annealing, and production of solid
state batteries on lower temperature substrates.
[0032] In the present application, a single, extended source is
described which has been scaled to 400 mm.times.500 mm for
production achieving a high LiCoO.sub.2 uniformity at a deposition
rate of 1.2 microns thickness an hour over an area of 2000
cm.sup.2, without the need for secondary front side ion source or
ion assistance.
[0033] In one example process, a LiCoO.sub.2 film was deposited
utilizing a conductive ceramic LiCoO.sub.2 target as described
herein, with pulsed-dc power of 4 kW, no bias, with 60 sccm Ar and
20 sccm O.sub.2 gas flows. A 3000 Angstrom layer of crystalline
LiCoO.sub.2 was deposited on a substrate area of 400.times.500
mm.
[0034] On other depositions utilizing this process, a temperature
measurement of the substrate during deposition showed that the
substrate remained at less than 224.degree. C. Temperature
measurements were performed utilizing a temperature sticker
purchased from Omega Engineering, Stamford, Conn. (Model no.
TL-F-390, active from 199-224.degree. C.).
[0035] Moreover, in some embodiments, films deposited according to
the present invention can have a deposition rate of from about 10
to about 30 times higher than processes in conventional films.
Deposition thicknesses and times of deposition for films deposited
according to the present invention are illustrated in Table I.
Furthermore, films according to the present invention can be
deposited on wide area substrates having a surface area from 10 to
50 times the surface area of prior sputtering processes, resulting
in much higher productivity and much lower cost of manufacture,
thereby providing high-volume, low-cost batteries.
[0036] Further, conventional deposition processes without ion
sources are capable of depositing amorphous LiCoO.sub.2 layers, but
do not deposit crystalline LiCoO.sub.2 layers. Surprisingly,
depositions according to some embodiment of the present invention,
deposit a LiCoO.sub.2 layer with substantial crystallinity readily
measured by x-ray diffraction techniques. In some embodiments, the
crystallinity of the as-deposited LiCoO.sub.2 layers is sufficient
to be utilized in a battery structure with no further thermal
processing. In some embodiments, crystallinity of the as-deposited
LiCoO.sub.2 layers are improved by thermal processes with low
thermal budgets, which can be compatible with films deposited on
low-temperature substrates.
[0037] Further, as-deposited the stoichiometry of some LiCoO.sub.2
layers deposited according to some embodiments of the present
invention shows that this layer is sufficient for utilization in a
battery. With the demonstrated ability to deposit a LiCoO.sub.2
film with crystalllnity and with sufficient stoichiometry, a
battery utilizing as-deposited LiCoO.sub.2 films can be produced.
Heat treating the LiCoO.sub.2 layers may improve the crystallinity
and lower the impedance.
[0038] In some embodiments, a crystalline layer of LiCoO.sub.2 with
a <101> or <003> crystalline orientation is deposited
directly on the substrate. Deposition of crystalline material can
eliminate or lessen the need of a subsequent high temperature
anneal or precious-metal layers to crystallize and orient the film.
Removing the high temperature anneal allows for formation of
battery structures on light-weight and low temperature substrates
such as stainless steel foil, copper foil, aluminum foil, and
plastic sheet, reducing both the weight and the cost of batteries
while retaining the energy density storage capabilities of Li-based
batteries. In some embodiments, a crystalline LiCoO.sub.2 layer can
be deposited on a precious metal layer, such as iridium, resulting
in a further significant lowering of the ripening thermal budget
required to improve crystallinity.
[0039] Deposition of materials by pulsed-DC biased reactive ion
deposition is described in U.S. patent application Ser. No.
10/101,863, entitled "Biased Pulse DC Reactive Sputtering of Oxide
Films," to Hongmei Zhang, et al., filed on Mar. 16, 2002.
Preparation of targets is described in U.S. patent application Ser.
No. 10/101,341, entitled "Rare-Earth Pre-Alloyed PVD Targets for
Dielectric Planar Applications," to Vassiliki Milonopoulou, et al.,
filed on Mar. 16, 2002, U.S. patent application Ser. No. 10/101,863
and U.S. patent application Ser. No. 10/101,341 are each assigned
to the same assignee as is the present disclosure and each is
incorporated herein in their entirety. Deposition of oxide
materials has also been described in U.S. Pat. No. 6,506,289, which
is also herein incorporated by reference in its entirety.
Transparent oxide films can be deposited utilizing processes
similar to those specifically described in U.S. Pat. No. 6,506,289
and U.S. application Ser. No. 10/101,863.
[0040] FIG. 1A shows a schematic of a reactor apparatus 10 for
sputtering material from a target 12 according to the present
invention. In some embodiments, apparatus 10 may, for example, be
adapted from an AKT-1600 PVD (400.times.500 mm substrate size)
system from Applied Komatsu or an AKT-4300 (600.times.720 mm
substrate size) system from Applied Komatsu, Santa Clara, Calif.,
The AKT-1600 reactor, for example, has three deposition chambers
connected by a vacuum transport chamber. These AKT reactors can be
modified such that pulsed DC power is supplied to the target and RF
power is supplied to the substrate during deposition of a material
film.
[0041] Apparatus 10 includes target 12 which is electrically
coupled through a filter 15 to a pulsed DC power supply 14. In some
embodiments, target 12 is a wide area sputter source target, which
provides material to be deposited on a substrate 16. Substrate 16
is positioned parallel to and opposite target 12. Target 12
functions as a cathode when power is applied to it from the pulsed
DC power supply 14 and is equivalently termed a cathode.
Application of power to target 12 creates a plasma 53. Substrate 16
is capacitively coupled to an electrode 17 through an insulator 54.
Electrode 17 can be coupled to an RF power supply 18. A magnet 20
is scanned across the top of target 12.
[0042] For pulsed reactive dc magnetron sputtering, as performed by
apparatus 10, the polarity of the power supplied to target 12 by
power supply 14 oscillates between negative and positive
potentials. During the positive period, the insulating layer of the
surface of target 12 is discharged and arcing is prevented. To
obtain arc free deposition, the poising frequency exceeds a
critical frequency that can depend on target material, cathode
current and reverse time. High quality oxide films can be made
using reactive pulse DC magnetron sputtering as shown in apparatus
10.
[0043] Pulsed DC power supply 14 can be any pulsed DC power supply,
for example an AE Pinnacle plus 10K by Advanced Energy, Inc. With
this DC power supply, up to 10 kW of pulsed DC power can be
supplied at a frequency of between 0 and 350 kHz. The reverse
voltage can be 10% of the negative target voltage. Utilization of
other power supplies can lead to different power characteristics,
frequency characteristics, and reverse voltage percentages. The
reverse time on this embodiment of power supply 14 can be adjusted
between 0 and 5 .mu.s.
[0044] Filter 15 prevents the bias power from power supply 18 from
coupling into pulsed DC power supply 14. In some embodiments, power
supply 18 can be a 2 MHz RF power supply, for example a Nova-25
power supply made by ENI, Colorado Springs, Colo.
[0045] In some embodiments, filter 15 can be a 2 MHz sinusoidal
band rejection filter. In some embodiments, the band width of the
filter can be approximately 100 kHz. Filter 15, therefore, prevents
the 2 MHz power from the bias to substrate 16 from damaging power
supply 14 and allow passage of the pulsed-dc power and
frequency.
[0046] Pulsed DC deposited films are net fully dense and may have
columnar structures. Columnar structures can be detrimental to thin
film applications such as barrier films and dielectric films, where
high density is important, due to the boundaries between the
columns. The columns act to lower the dielectric strength of the
material, but may provide diffusion paths for transport or
diffusion of electrical current, ionic current, gas, or other
chemical agents such as water. In the case of a solid state
battery, a columnar structure containing crystallinity as derived
from processes according to the present invention is beneficial for
battery performance because it allows better Li transport through
the boundaries of the material.
[0047] In the deposition system, target 12 can have an. active size
of about 675.7.times.582.48 mm by 4 to 8 mm in order to deposit
films on substrate 16 that have dimension about 400.times.500 mm.
The temperature of substrate 16 can be adjusted to between
-50.degree. C. and 500.degree. C. The distance between target 12
and substrate 16 can be between about 3 and about 9 cm (in some
embodiments, between 4.8 and 6 cm are used). Process gas can be
inserted into the chamber of apparatus 10 at a rate up to about 200
sccm while the pressure in the chamber of apparatus 10 can be held
at between about 0.7 and 6 milliTorr. Magnet 20 provides a magnetic
field of strength between about 400 and about 600 Gauss directed in
the plane of target 12 and is moved across target 12 at a rate of
less than about 20-30 sec/scan. In some embodiments utilizing the
AKT reactor, magnet 20 can be a race-track shaped magnet with
dimensions about 150 mm by 600 mm.
[0048] FIG. 2 illustrates an example of target 12. A film deposited
on a substrate positioned on carrier sheet 17 directly opposed to
region 52 of target 12 has good thickness uniformity. Region 52 is
the region shown in FIG. 1B that is exposed to a uniform plasma
condition. In some implementations, carrier 17 can be coextensive
with region 52. Region 24 shown in FIG. 2 indicates the area below
which both physically and chemically uniform deposition can be
achieved, for example where physical and chemical uniformity
provide refractive index uniformity, oxide film uniformity, or
metallic film uniformity. FIG. 2 indicates region 52 of target 12
that provides thickness uniformity, which is, in general, larger
than region 24 of target 12 providing thickness and chemical
uniformity to the deposited film. In optimized processes, however,
regions 52 and 24 may be coextensive.
[0049] In some embodiments, magnet 20 extends beyond area 52 in one
direction, for example the Y direction in FIG. 2, so that scanning
is necessary in only one direction, for example the X direction, to
provide a time averaged uniform magnetic field. As shown in FIGS.
1A and 1B, magnet 20 can be scanned over the entire extent of
target 12, which is larger than region 52 of uniform sputter
erosion. Magnet 20 is moved in a plane parallel to the plane of
target 12.
[0050] The combination of a uniform target 12 with a target area 52
larger than the area of substrate 16 can provide films of highly
uniform thickness. Further, the material properties of the film
deposited can be highly uniform. The conditions of sputtering at
the target surface, such as the uniformity of erosion, the average
temperature of the plasma at the target surface, and the
equilibration of the target surface with the gas phase ambient of
the process are uniform over a region which is greater than or
equal to the region to be coated with a uniform film thickness. In
addition, the region of uniform film thickness is greater than or
equal to the region of the film which is to have highly uniform,
electrical, mechanical, or optical properties such as index of
refraction, stoichiometry, density, transmission, or
absorptivity.
[0051] Target 12 can be formed of any materials that provide the
correct stoichiometry for LiCoO.sub.2 deposition. Typical ceramic
target materials include oxides of Li and Co as well as metallic Li
and Co additions and dopants such as Ni, Si, Nb, or other suitable
metal oxide additions. In the present disclosure, target 12 can be
formed from LiCoO.sub.2 for deposition of LiCoO.sub.2 film.
[0052] In some embodiments of the invention, material tiles are
formed. These tiles can be mounted on a backing plate to form a
target for apparatus 10. A wide area sputter cathode target can be
formed from a close packed array of smaller tiles. Target 12,
therefore, may include any number of tiles, for example between 2
and 60 individual tiles. Tiles can be finished to a size so as to
provide a margin of edge-wise non-contact, tile to tile, less than
about 0.010'' to about 0.020'' or less than half a millimeter so as
to eliminate plasma processes that may occur between adjacent ones
of tiles 30. The distance between tiles of target 12 and the dark
space anode or ground shield 19 in FIG. 1B can be somewhat larger
so as to provide ion contact assembly or to provide for thermal
expansion tolerance during process chamber conditioning or
operation.
[0053] As shown in FIG. 1B, a uniform plasma condition can be
created in the region between target 12 and substrate 16 in a
region overlying substrate 16. A plasma 53 can be created in region
51, which extends under the entire target 12. A central region 32
of target 12 can experience a condition of uniform sputter erosion.
As discussed further herein, a layer deposited on a substrate
placed anywhere below central region 52 can then be uniform in
thickness and other properties (i.e., dielectric, optical index, or
material concentrations). In some embodiments, target 12 is
substantially planar in order to provide uniformity in the film
deposited on substrate 16. In practice, planarity of target 12 can
mean that all portions of the target surface in region 52 are
within a few millimeters of a planar surface, and can be typically
within 0.5 mm of a planar surface.
[0054] FIG. 3 shows a battery structure with a LiCoO.sub.2 layer
deposited according to some embodiments of the present invention.
As shown in FIG. 3, a metallic current collection layer 302 is
deposited on a substrate 301. In some embodiments, current
collection layer 302 can be patterned in various ways before
deposition of a LiCoO.sub.2 layer 303. Also according to some
embodiments, LiCoO.sub.2 layer 303 can be a deposited crystalline
layer. In some embodiments of the invention, layer 303 is
crystalline without the necessity of a crystallizing heat
treatment. Therefore, substrate 301 can be a silicon wafer,
titanium metal, alumina, or other conventional high temperature
substrate, but may also be a low temperature material such as
plastic, glass, or other material which could be susceptible to
damage from the high temperature crystallizing heat treatment. This
feature can have the great advantage of decreasing the expense and
weight of battery structures formed by the present invention. The
low temperature deposition of the LiCoO.sub.2 allows for successive
depositions of battery layers, one upon another. Such a process
would have the advantage that successive layers of battery
structure would be obtained in a stacked condition without the
inclusion of a substrate layer. The stacked layered battery would
provide higher specific energy density as well as low impedance
operation for charging and discharging.
[0055] In some embodiments, an oxide layer can be deposited on
substrate 301. For example, a silicon oxide layer can be deposited
on a silicon wafer. Other layers can be formed between conducting
layer 302 and substrate 301.
[0056] As further shown in FIG. 3, a LiPON layer 304
(Li.sub.xPO.sub.yN.sub.2z) is deposited over LiCoO.sub.2 layer 303.
LiPON layer 304 is the electrolyte for battery 300 while
LiCoO.sub.2 layer 303 acts as the cathode. A metallic conducting
layer 305 can be deposited over the LiPON layer 304 in order to
complete the battery. Metallic conducting layer 305 can include
lithium adjacent to LiPON layer 304.
[0057] An anode 305 is deposited over LiPON layer 304. Anode 305
can be, for example an evaporated lithium metal. Other materials
such as, for example, nickel can also be utilized. A current
collector 306, which is a conducting material, is then deposited
over al least a portion of anode 305.
[0058] A Li based thin film battery operates by transport of Li
ions in the direction from current collector 306 to current
collector 302 in order to hold the voltage between current
collector 306 and current collector 302 at a constant voltage. The
ability for battery structure 300 to supply steady current, then,
depends on the ability of Li ions to diffuse through LiPON layer
304 and LiCoO.sub.2 layer 303. Li transport through bulk cathode
LiCoO.sub.2 layer 303 in a thin film battery occurs by the way of
grains or grain boundaries. Without being restricted in this
disclosure to any particular theory of transport, it is believed
that the grains with their planes parallel to substrate 302 will
block the flow of Li ions while grains oriented with planes
perpendicular to substrate 301 (i.e., oriented parallel to the
direction of Li ion flow) facilitate the Li diffusion. Therefore,
in order to provide a high-current battery structure, LiCoO.sub.2
layer 303 should include crystals oriented in the <101>
direction or <003> direction.
[0059] In accordance with the present invention, LiCoO.sub.2 films
can be deposited on substrate 302 with a pulsed-DC biased PVD
system as was described above. In addition, an AKT 1600 PVD system
can be modified to provide an RF bias and an Advanced Energy
Pinnacle plus 10K pulsed DC power supply can be utilized to provide
power to a target. The pulsing frequency of the power supply can
vary from about 0 to about 350 KHz. The power output of the power
supply is between 0 and about 10 kW. A target of densified
LiCoO.sub.2 tiles having a resistivity in the range of about 3 to
about 10 k.OMEGA. can he utilized with dc-sputtering.
[0060] In some embodiments, LiCoO.sub.2 films are deposited on Si
wafers. Gas flows containing Oxygen and Argon can be utilized. In
some embodiments, the Oxygen to Argon ratio ranges from 0 to about
50% with a total gas flow of about 80 sccm. The pulsing frequency
ranges from about 200 kHz to about 300 kHz during deposition. RF
bias can also be applied to the substrate. In many trials, the
deposition rates vary from about 2 Angstrom/(kW sec) to about 1
Angstrom/(kW sec) depending on the O.sub.2/Ar ratio as well as
substrate bias.
[0061] Table I illustrates some example depositions of LiCoO.sub.2
according to the present invention. XRD (x-Ray Diffraction) results
taken on the resulting thin films illustrate that films deposited
according to the present invention are crystalline films, often
with highly textured grain sizes as large as about 150 nm. The
dominant crystal orientation appears to be sensitive to the
O.sub.2/Ar ratio. For certain O.sub.2/Ar ratios (.about.10%),
as-deposited films exhibit a preferred orientation in the <101
> direction or the <003> direction with poorly developed
<003> planes.
[0062] FIGS. 4A and 4B illustrate an XRD Analysis and SEM cross
section, respectively, of the LiCoO.sub.2 film deposited as Example
15 in Table I. Such a LiCoO.sub.2 film was deposited on Si wafer
with 2 kW of target power, a frequency of 300 kHz, with 60 sccm Ar
and 20 sccm of O.sub.2 for a substrate with an initial temperature
of about 30.degree. C. As shown in the XRD analysis of FIG. 4A, a
strong <101> peak is indicated showing a strong orientation
of LiCoO.sub.2 crystals in the desired <101> crystallographic
direction. The SEM cross section shown in FIG. 4B further shows the
columnar structure of the film having the <101> direction and
the grain boundaries of the resulting LiCoO.sub.2 crystals.
[0063] FIGS. 5A through 5E show SEM cross sections of further
example depositions of LiCoO.sub.2 crystals according to the
present invention. In each of the examples, deposition of the
LiCoO.sub.2 film was performed on a Si wafer with target power of
about 2 kW and frequency of about 250 kHz. The LiCoO.sub.2 film
shown in FIG. 5A corresponds to the example deposition Example 1 in
Table I. In the deposition of the LiCoO.sub.2 film shown in FIG.
5A, no bias power was utilized with an argon flow rate of about 80
sccm and an oxygen flow rate of about 0 sccm. A deposition rate of
about 1.45 .mu.m/hr was achieved over the full substrate area of
400.times.500 mm. Further, as is indicated in the cross section
shown in FIG. 5A, a <101> orientation of the LiCoO.sub.2 was
achieved.
[0064] The rate of deposition of the LiCoO.sub.2 layer shown in
FIG. 5A is very high, likely due to the relatively high
conductivity or low resistivity of the ceramic LiCoO.sub.2 oxide
sputter target. A target resistance of 10 kOhms was measured by
means of an Ohm meter over a distance of about 4 cm on the surface
of target 12. This high rate allows the manufacture of the 3 micron
or thicker LiCoO.sub.2 layer required for the battery at high rate
over a wide area in short times, resulting in very high
productivity and very low cost. Target resistance on the order of
about 500 k.OMEGA. over the same distance by the same measurement
technique or higher would not allow for such a high sputter
efficiency or high rate of deposition at such a low target power.
The resistance of conventional target materials can be unmeasurably
high. A resistance of 100 k.OMEGA. over about 4 cm of surface will
result in high sputter efficiency and high rate of deposition.
Further, because deposition rates typically scale nearly linearly
with target power, a deposition at 6 kW will yield a deposition
rate of approximately 3 .mu.m/hr, which is a very desirable rate of
deposition for manufacturability of Li-based thin-film solid-state
batteries on a surface area of 400.times.500 mm.sup.2.
[0065] The LiCoO.sub.2 layer shown in FIG. 5B is deposited under
the conditions listed as Example 7 in Table I. Again, no bias was
utilized in the deposition. An argon flow rate of about 72 sccm and
an oxygen flow rate of about 8 sccm was utilized. The deposition
rate was significantly reduced to about 0.85 .mu.m/hr. Further,
although a <101> crystallinity cart be discerned, that
<101> crystallinity is not as pronounced as that exhibited in
the deposition of the film shown in FIG. 5A.
[0066] The LiCoO.sub.2 film shown in FIG. 5C was deposited
according to Example 3 in Table I. In this deposition, 100 W of
bias power is applied to the substrate. Further, an argon flow rate
of 72 sccm, and an oxygen flow rate of 8 sccm was utilized. The
deposition rate was about 0.67 .mu.m/hr. Therefore, the application
of bias in comparison with the LiCoO.sub.2 film shown in FIG. 5B
further reduced the deposition rate (from 0.85 .mu.m/hr of the
example shown in FIG. 5B to 0.67 .mu.m/hr of the example shown in
FIG. 5C). Further, the desired <101> directionality of formed
crystals appears to be further degraded.
[0067] The LiCoO.sub.2 film shown in FIG. 5D corresponds to Example
4 in Table I. In this deposition, the Ar/O.sub.2 ratio was
increased. As is shown in FIG. 5D, increasing the Ar/O.sub.2 ratio
improves crystallinity. With respect to the example illustrated in
FIG. 5C, the deposition illustrated in FIG. 5D was performed with
an argon flow of about 76 sccm and an oxygen flow of about 4 sccm
as well as retaining the 100 W bias to the substrate. The
LiCoO.sub.2 deposition rate was improved to 0.79 .mu.m/hr from a
rate of 0.67 .mu.m/hr illustrated in FIG. 5C.
[0068] In the example deposition illustrated in FIG. 5B
corresponding to Example 5 in Table I. The substrate temperature
was set at about 200.degree. C. while the bias power remained at
about 100 W. The argon flow rate was set at about 76 sccm and the
oxygen flow rate was set at about 4 sccm. The resulting deposition
rate for the LiCoO.sub.2 layer was about 0.74 .mu.m/hr.
[0069] In Example 6 of Table I, the argon flow rate was set at
about 74 sccm and the oxygen flow rata wag set at about 6 sccm,
resulting in a LiCoO.sub.2 deposition rate of about 0.67 .mu.m/hr.
Therefore, increasing both argon and oxygen flow rate over the
deposition illustrated in FIG. 5E resulted in a lower deposition
rate.
[0070] The data show clearly that an as-deposited crystalline film
of LiCoO.sub.2 can be obtained under several of the process
conditions, as shown in Table II. In particular, very high rates of
deposition with low power are obtained along with the oriented
crystalline structure for the process.conditions according to
embodiments of the present invention.
[0071] FIG. 6A illustrates a layer of LiCoO.sub.2 602 deposited on
a thin substrate 601 according to some embodiments of the present
invention. Higher lithium-ion mobilities can be achieved utilizing
crystalline LiCoO.sub.2 cathode films 602 deposited on a thin
substrate 601 that has thickness comparable to that of the battery
stack itself, rather than a thickness many or tens of times that of
the battery stack. Such a film can lead to faster charging and
discharging rates. Substrate 601 can be formed of a thin metallic
sheet (e.g., aluminum, titanium, stainless steel, or other suitable
thin metallic sheets can be formed of a polymer or plastic
material, or may be formed of a ceramic or glass material. As sho
wn in FIG. 6B, if substrate 601 is an insulating material, a
conducting layer 603 can be deposited between substrate 601 and
LiCoO.sub.2 layer 602.
[0072] Depositing materials on a thin substrate involves holding
and positioning the substrate during deposition. FIGS. 7A, 7B, 7C,
and 7D illustrate a reusable fixture 700 for holding a thin film
substrate. As shown in FIG. 7A, reusable fixture 700 includes a top
portion 701 and a bottom portion 702 that snap together, Thin
substrate 601 is positioned between top portion 701 and bottom
portion 702. As shown in FIG. 7B, top portion 701 and bottom,
portion 702 are such that substrate 601 is brought into tension and
subsequently clamped as top portion 701 is closed into bottom
portion 702. Substrate 601 can be easily held by fixture 700 so
that substrate 601 can be handled and positioned. In some
embodiments, the corners of substrate 601, areas 703, are removed
so that substrate 601 is more easily stretched by avoiding
"wrap-around" corner clamping effects when top portion 701 is
closed into bottom portion 702.
[0073] As shown in FIG. 7C, a mask 712 can be attached to fixture
700. In some embodiments, fixture 700 includes guides in order to
align fixture 700 with respect to mask 712. In some embodiments,
mask 712 may be attached to fixture 700 and travel with fixture
700. Mask 712 can be positioned at any desired height above
substrate 601 in fixture 700. Therefore, mask 712 can function as
either a contact or proximity mask. In some embodiments, mask 712
is formed of another thin substrate mounted in a fixture similar to
fixture 700.
[0074] As shown in FIGS. 7C and 7D, fixture 700 and mask 712 can be
positioned relative to mount 710. Mount 710, for example, can be a
susceptor, mount, or an electrostatic chuck of a processing chamber
such as that shown in FIGS. 1A and 1B. Fixture 700 and mask 712 can
have features that allow for ready alignment with respect to each
other and with respect. to mount 710. In some embodiments, mask 712
is resident in fee processing chamber and aligned with fixture 700
during positioning of fixture 700 on mount 710, as shown in FIG.
7D.
[0075] Utilizing fixture 700 as shown in FIGS. 7A, 7B, 7C, and 7D
allows processing of a thin film substrate in a processing chamber.
In some embodiments, thin film substrates can be about 10 .mu.m or
more. Further, thin film substrate 601, once mounted within fixture
700, can be handled and moved from process chamber to process
chamber. Therefore, a multiprocessor chamber system can be utilized
to form stacks of layers, including one or more layers of
LiCoO.sub.2 deposited according to embodiments of the present
invention.
[0076] FIG. 8 illustrates a cluster tool 800 for processing thin
film substrates. Cluster tool 800 can, for example, include load
lock 802 and load lock 803, through which mounted thin film
substrate 601 is loaded and a resultant device is removed from
cluster tool 800. Chambers 804, 805, 806, 807, and 808 are
processing chambers for depositions of materials, heat treatments,
etching, or other processes. One or more of chambers 804, 805, 806,
807, and 808 can be a pulsed-DC PVD chamber such as that discussed
above with respect to FIGS. 1A and 1B and within which a
LiCoO.sub.2 film deposited according to embodiments of the present
invention may be deposited.
[0077] Processing chambers 804, 805, 806, 807, and 808 as well as
load locks 802 and 803 are coupled by transfer chamber 801.
Transfer chamber 801 includes substrate transfer robotics to
shuttle individual wafers between processing chambers 804, 805,
806, 807, and 808 and load locks 802 and 803.
[0078] In production of a conventional thin-film battery, ceramic
substrates are loaded into load lock 803. A thin metallic layer can
be deposited in chamber 804, followed by a LiCoO.sub.2 deposition
performed in chamber 805. The substrate is then removed through
load lock 803 for an in-air heat treatment external to cluster tool
800. The treated wafer is then reloaded into cluster tool 800
through load lock 802. A LiPON layer can be deposited in chamber
806. The wafer is then again removed from cluster cool 800 for
deposition of the lithium anode layer, or sometimes chamber 807 can
be adapted to deposition of the lithium anode layer. A second
metallic layer is deposited in chamber 808 to form a charge
collector and anode collector. The finished battery structure is
then off-loaded from cluster tool 800 in load lock 802. Wafers are
shuttled from chamber to chamber by robotics in transfer chamber
801.
[0079] A battery structure produced according to the present
invention could utilize thin film substrates loaded in a fixture
such as fixture 700. Fixture 700 is then loaded into load lock 803.
Chamber 804 may still include deposition of a conducting layer.
Chamber 805 then includes deposition of a LiCoO.sub.2 layer
according to embodiments of the present invention. A LiPON layer
can then be deposited in chamber 806. Chamber 807 may still be
adapted to deposition of a lithium rich material such as lithium
metal and chamber 808 can be utilized for deposition of the
conducting layer of the current collector. In this process, no heat
treatment is utilized to crystallize the LiCoO.sub.2 layer.
[0080] Another advantage of a thin film battery process is the
ability to stack battery structures. In other words, substrates
loaded into cluster tool 800 may traverse process chambers 804,
805, 806, 807, and 808 multiple times in order to produce multiply
stacked battery structures. FIGS. 9A and 9B illustrate such battery
structures.
[0081] FIG. 9A illustrates a parallel coupled stacking. As shown in
FIG. 9A, a substrate 601, which for example can be a plastic
substrate, is loaded into load lock 803. A conducting layer 603,
for example about 2 .mu.m of aluminum, copper, iridium or other
material, acts as a bottom current collector. Conducting layer 603,
for example, can be deposited in chamber 804. A LiCoO.sub.2 layer
602 is then deposited on conducting layer 603. LiCoO.sub.2 layer
602 can be about 3-10 .mu.m and can be deposited in chamber 805
according to embodiments of the present invention. The wafer can
then be moved to chamber 806 where a LiPON layer 901 of thickness
of about 0.5 to about 2 .mu.m can be deposited. In chamber 807, an
anode layer 902, for example a lithium metal layer of up to about
10 .mu.m, can then be deposited in chamber 807. A second conducting
layer 903 can then be deposited over anode layer 902. A second
battery stack can then be deposited over the first battery stack
formed by metal layer 603, LiCoO.sub.2 layer 602, LiPON layer 901,
lithium layer 902, and current collection conduction layer 903.
Over current collection conducting layer 903, another lithium layer
902 is formed. Another LiPON layer 901 is formed over lithium layer
902. Another LiCoO2 layer 602 is formed over LiPON layer 901 and
finally another metal layer 603 is formed over LiCoO2 layer 602. In
some embodiments, further stackings can be formed. In some
embodiments, metal layers 603 and 903 differ in the mask utilized
in deposition so that tabs are formed for electrical coupling of
layers.
[0082] As discussed above, any number of individual battery stacks
can be formed such that parallel battery formations are formed.
Such a parallel arrangement of battery stacking structure can be
indicated as Current collector/LiCoO2/LiPON/Anode/current
collector/Anode/LiPON/LiCoO2/current collector/LiCoO2 . . .
/current collector. FIG. 9B illustrates an alternative stacking
corresponding to the battery structure current
collector/LiCoO2/LiPON/anode/current
collector/LiCoO2/LiPON/ansode/current collector . . . /current
collector. In this case, a series arrangement battery stacking
structure is formed because the individual battery stacks share
anodes.
[0083] To form the structures shown in FIGS. 9A and 9B, substrates
are rotated again through the chambers of cluster tool 800 in order
to deposit the multiple sets of batteries. In general, a stack of
any number of batteries can be deposited in this fashion.
[0084] In some embodiments, stoichiometric LiCoO.sub.2 can be
deposited or iridium. FIGS. 10A through 10D illustrate an anneal
procedure for Li--Co deposition over an iridium layer that has been
deposited on a Si wafer. The LiCoO.sub.2 deposition was
accomplished as discussed above with a target power of 2 kW, no
bias power, reverse time of 1.6 .mu.s, a pulsing frequency of 300
kHz, with 60 sccm Ar flow and 20 sccm of O.sub.2 flow, with no
pre-heat for 7200 sec. As a result, a layer of LiCoO.sub.2 of about
1.51 .mu.m was deposited.
[0085] FIGS. 10A through 10D show XRD analysis of both as-deposited
and annealed layers of LiCoO.sub.2 deposited as discussed above.
The XRD analysis of the as-deposited layer demonstrates a shallow
peak at 2.theta.=18.85.degree. denoting a <003> orientation
of crystalline LiCoO.sub.2, a sharper peak at about
2.theta.=38.07.degree. corresponding with the desired <101>
crystallographic direction, and a peak at 2.theta.=40.57.degree.
corresponding to the <111 > direction of iridium. However,
the position of the <101 > LiCoO.sub.2 peak indicates that
the <101> LiCoO.sub.2 peak is nonstoichiometric LiCoO.sub.2.
In order to be useful as a battery layer, stoichiometric
LiCoO.sub.2 provides for the best Li transport. One of ordinary
skill in the art will notice that careful adjustment of deposition
parameters can provide stoichiometric LiCoO.sub.2 of desired
orientation.
[0086] FIG. 10B shows an XRD analysis of the sample shown in FIG.
10A after a 300.degree. C. anneal in air for 2 hours. As shown in
FIG. 10B, the XRD peak corresponding to <003> LiCoO.sub.2
grows, indicating crystallization of LiCoO.sub.2 into the
<003> direction. Further, the <101> peak of LiCoO.sub.2
shifts slightly to 2.theta.=38.53.degree., indicating a more
stoichiometric crystallization of the <101> LiCoO.sub.2.
However, file crystalline LiCoO.sub.2 is still not stoichiometric
after this anneal. One of ordinary skill in the art will notice
that longer anneals and/or further adjustment of the deposited
stoichiometry may result in usefully oriented stoichiometric
LiCoO.sub.2 layers with anneal temperatures at 300.degree. C. or
less. Consequently, low temperature materials such as polymers,
glass, or metal may be utilized as the substrate.
[0087] FIG. 10C illustrates an XRD analysis from the sample after a
subsequent 500.degree. C. anneal in air for 2 hours. As shown in
FIG. 10C, more of the LiCoO.sub.2 erystaliaes into the <003>
layer. Further, the <101> LiCoO.sub.2 peak shifts again to
2.theta.=39.08.degree., indicating crystallization of a <012>
layer of LiCoO.sub.2. In this case, the <012> LiCoO.sub.2
cyrstal is stoichiometric and therefore allows for efficient Li
transport. One of ordinary skill in the art will notice that longer
anneals and/or further adjustment of the deposited stoichiometry
may result in usefully oriented stoichiometric LiCoO.sub.2 layers
with anneal temperatures at500.degree. C. or less. Consequently,
low temperature materials such as polymers, glass, or metal may be
utilized as the substrate.
[0088] FIG. 10D illustrates an XRD analsysis of the sample after a
subsequent anneal of 700.degree. C in air for 2 hours. As shown in
FIG. 10D, the <003> LiCoO.sub.2 peak disappears, but the
<012> LiCoO.sub.2 peak remains relatively the same as that
shown in the 500.degree. anneal illustrated in FIG. 10C.
[0089] FIGS. 10A through 10D demonstrate deposition of <101>
LiCoO.sub.2 at law temperature over an iridium layer. Subsequent
anneals to 500.degree. C. may be desired to change the
stoichiometry of the <101 > LiCoO.sub.2 layer, but anneals to
700.degree. C. do not appear to be necessary. With anneal
temperatures less than 500.degree. C., depositions of a LiCoO.sub.2
layer over a conducting iridium layer can be accomplished on glass,
aluminum foil, plastic, or other low temperature substrate
material. Anneal temperatures of less than 500.degree. C. but
greater than 300.degree. C. or lengthening the time of lower
temperature anneals may also result in desired orientations of
stoichiometric crystalline LiCoO.sub.2.
[0090] FIGS. 11A through 11D illustrate formation of a single-layer
battery according to some embodiments of the present invention. As
shown in FIG. 11A, a lift-off layer 1102 can be deposited on a
substrate 1101. Further, an iridium layer 1103 can be deposited
over lift-off layer 1102. In some embodiments, substrate 1101 can
be plastic, glass, Al foil, Si wafer, or any other material.
Lift-off layer 1102 can be any lift off layer and can be a polymer
layer such as polyimide, an inorganic layer such as CaF.sub.2 or
carbon, or an adhesive layer that loses its adhesion as a result
of, for example, oxidation, heat, or light. Lift-off layers are
well known, Iridium layer 1103 can be from about 500 .ANG. or
more.
[0091] As shown in FIG. 11B, a LiCoO.sub.2 layer is deposited over
iridium layer 1103 as was discussed above. In some embodiments, an
anneal can be performed at this step. In some embodiments, further
layers of the battery may be deposited before an anneal step is
performed. In some embodiments, a stoichiometric LiCoO.sub.2 layer
of a useful crystalline orientation may result in the as-deposited
LiCoO.sub.2 with no further anneals necessary.
[0092] FIG. 11C illustrates deposition of a LiPON layer 1105 over
the LiCoO.sub.2 layer, deposition of a Li layer 1106 over LiPON
layer 1105, and deposition of an electrode layer 1107 over Li layer
1106. In some embodiments, an anneal step of up to 500.degree. C.
as discussed above may be performed here.
[0093] As shown in FIG. 11D, the resulting single-layer battery
formed from iridium layer 1103, LiCoO.sub.2 layer 1104, LiPON layer
1105, Li layer 1106, and electrode layer 1107 can be "lifted off"
from substrate 1101. Such a single-layer battery can be a
free-standing battery of thickness about 5 .mu.m or greater. Such a
battery, without the requirement of a substrate 1101, is well known
to have the potential of energy storage of greater than about 1
kW-hr/liter.
[0094] As an alternative to a lift-off process as described in
FIGS. 11A through 11D, a substrate may be removed during
anneal.leaving a single-layer battery. Further, in some
embodiments, substrate 1101 can be removed by a solvent, etching,
or a photo process. Further, single-layer batteries may be combined
or stacked in any fashion to provide a device of greater energy
storage at a particular voltage.
[0095] FIG. 12 illustrates performance of a battery structure such
as that shown in FIGS. 9A and 9B with a LiCoO.sub.2 film deposited
according to the present invention. The film was annealed at 700 C
for a 2 hour period and characterized by Oakridge Microenergy,
Inc., of Oakridge, Tenn.
[0096] One skilled in the art will recognize variations and
modifications of the examples specifically discussed in this
disclosure. These variations and modifications are intended to be
within the scope and spirit of this disclosure. As such, the scope
is limited only by the following claims.
TABLE-US-00001 TABLE I Initial Substrate Temperature (temperature
Target Bias Reverse during Deposition Film Example Power Power Time
Frequency ar O2 deposit) Time Thickness # (kW) (W) (.mu.s) (kHz)
(sccm) (sccm) (.degree. C.) (sec) (.mu.m) 1 2 0 1.6 250 80 0 30
10000 3.9 2 2 0 250 72 8 30 7200 1.7 3 2 100 250 72 8 30 7200 1.34
4 2 100 250 76 4 30 7200 1.57 5 2 100 250 76 4 200 7200 1.3 6 2 100
250 74 6 200 7200 1.3 7 2 0 300 72 8 30 7200 1.58 8 2 0 300 74 6 30
7200 9 2 100 300 74 6 30 7200 10 2 100 300 72 8 30 7200 11 2 100
300 70 10 30 7200 12 2 0 300 70 10 30 7200 13 2 0 300 72 8 30 7200
1.58 14 2 0 300 74 6 30 7200 15 2 0 300 60 20 30 7200 16 2 0 300 50
30 30 7200 17 2 200 300 60 20 30 7200 18 2 50 300 60 20 30 7200 19
2 0 300 70 10 30 7200 20 2 0 300 65 15 30 7200 21 3 0 300 65 15 30
7200 22 2 0 1.6 250 60 20 30 7200 23 3 0 1.6 250 60 20 30 7200 24 2
0 1.6 250 60 20 30 (NPH) 7200 25 2 0 1.6 250 60 20 10 min heat 7200
30 min coc 26 2 0 1.6 250 60 20 no preheat 9000 27 2 0 300 60 20 no
preheat 7200 28 2 0 300 60 20 15 min heat, 7200 10 min 29 2 0 250
60 20 no preheat 30 2 0 250 60 20 10 min, 10 min
TABLE-US-00002 TABLE II Example d.sub.101 crystallite # Phase
Lattice Texture [.ANG.] 2.theta. [.degree.] size [.ANG.] 15
LiCoO.sub.2 rhombohedral strong 2.376 37.83 ~1300 [101] (1) 16
LiCoO.sub.2 Rhombohedral strong 2.375 37.85 ~750 [101] (1) 17 Co
cubic random -- -- <50 18 Co cubic random -- -- <50 19
LiCoO.sub.2 rhombohedral strong 2.370 37.93 ~1400 [101] (1) 20
LiCoO.sub.2 rhombohedral strong 2.372 37.90 ~1500 [101] (1) 21
LiCoO.sub.2 rhombohedral strong 2.370 37.92 ~1700 [101] (1) PDF
LiCoO.sub.2 Rhombohedral random 1.408 37.31 -- (1)
* * * * *