U.S. patent application number 15/850738 was filed with the patent office on 2018-11-08 for flame-retardant vanillin-derived cross-linkers.
The applicant listed for this patent is International Business Machines Corporation. Invention is credited to Brandon M. Kobilka, Joseph Kuczynski, Jacob T. Porter, Jason T. Wertz.
Application Number | 20180320079 15/850738 |
Document ID | / |
Family ID | 64014143 |
Filed Date | 2018-11-08 |
United States Patent
Application |
20180320079 |
Kind Code |
A1 |
Kobilka; Brandon M. ; et
al. |
November 8, 2018 |
FLAME-RETARDANT VANILLIN-DERIVED CROSS-LINKERS
Abstract
A flame-retardant vanillin-derived cross-linker, a process for
forming a flame-retardant polymer, and an article of manufacture
comprising a material that contains the flame-retardant
vanillin-derived cross-linker are disclosed. The flame-retardant
vanillin-derived cross-linker can be synthesized from vanillin
obtained from a bio-based source, and can have at least one
phosphoryl or phosphonyl moiety with phenyl, allyl, epoxide,
propylene carbonate, or thioether substituents. The process for
forming the flame-retardant polymer can include reacting a diol
vanillin derivative and a flame-retardant phosphorus-based molecule
to form the flame-retardant vanillin-derived cross-linker, and
binding the flame-retardant vanillin-derived cross-linker to a
polymer. The material in the article of manufacture can be
flame-retardant, and contain flame-retardant vanillin-derived
cross-linkers. Examples of materials that can be in the article of
manufacture can include resins, plastics, adhesives, polymers,
etc.
Inventors: |
Kobilka; Brandon M.;
(Tucson, AZ) ; Kuczynski; Joseph; (North Port,
FL) ; Porter; Jacob T.; (Highland, NY) ;
Wertz; Jason T.; (Pleasant Valley, NY) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
International Business Machines Corporation |
Armonk |
NY |
US |
|
|
Family ID: |
64014143 |
Appl. No.: |
15/850738 |
Filed: |
December 21, 2017 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
15584798 |
May 2, 2017 |
|
|
|
15850738 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C07F 9/12 20130101; C07F
9/1406 20130101; C09K 21/12 20130101; C08K 5/5317 20130101; C09K
21/14 20130101; C12P 7/22 20130101; C07C 15/04 20130101; C07F
9/4015 20130101; C07F 9/65502 20130101; C07F 9/65586 20130101; C08K
5/5313 20130101; C07D 317/12 20130101; C07F 9/145 20130101; C07F
9/4093 20130101; C12P 7/26 20130101; C07F 9/08 20130101; C08K
5/5337 20130101; C07F 9/425 20130101 |
International
Class: |
C09K 21/12 20060101
C09K021/12; C07C 15/04 20060101 C07C015/04; C07D 317/12 20060101
C07D317/12; C08K 5/5337 20060101 C08K005/5337; C08K 5/5317 20060101
C08K005/5317; C12P 7/26 20060101 C12P007/26; C12P 7/22 20060101
C12P007/22; C07F 9/08 20060101 C07F009/08; C08K 5/5313 20060101
C08K005/5313 |
Claims
1. A flame-retardant vanillin-derived cross-linker with a formula
of: ##STR00001## wherein FR is a first phosphorus-based moiety with
a formula selected from a group consisting of moieties with
formulas of: ##STR00002## wherein R is a first substituent selected
from a group consisting of an allyl substituent, an epoxide
substituent, a propylene carbonate substituent, and a thioether
substituent selected from a group consisting of a
hydroxyl-functionalized thioether substituent, an
amino-functionalized thioether substituent, and a carboxylic
acid-functionalized thioether substituent; wherein M is a
flame-retardant substituent selected from a group consisting of
substituents with formulas of: ##STR00003## wherein R is a second
substituent selected from the group consisting of the allyl
substituent, the epoxide substituent, the propylene carbonate
substituent, and the thioether substituent, and wherein the
selection of R depends upon the selection of the first R
substituent, and wherein FR is a second phosphorus-based moiety
selected from the group consisting of moieties with formulas of:
##STR00004## and wherein the flame-retardant vanillin-derived
cross-linker participates in a process of forming a flame-retardant
polymer, the process comprising: forming a diol vanillin derivative
synthesized from vanillin obtained from a biological source,
wherein the diol vanillin derivative is selected from a group
consisting of vanillin derivatives with formulas of: ##STR00005##
forming a phosphorus-based flame-retardant molecule selected from a
group consisting of phosphorus-based flame-retardant molecules with
formulas of: ##STR00006## wherein R is a substituent selected from
a group consisting of an epoxide substituent and an allyl
substituent; chemically reacting the diol vanillin derivative with
the phosphorus-based flame-retardant molecule to form the
flame-retardant vanillin-derived cross-linker; and binding the
flame-retardant vanillin-derived cross-linker to a polymer selected
from a group consisting of polyurethane, an epoxy polymer, a
polyhydroxyurethane, a polycarbonate, a polyester, a polyacrylate,
a polyimide, a polyamide, a polyurea, and a poly(vinyl-ester).
Description
BACKGROUND
[0001] The present disclosure relates to bio-renewable
flame-retardant compounds and, more specifically, flame-retardant
vanillin-derived cross-linkers.
[0002] Bio-based compounds provide a source of renewable materials
for various industrial applications, such as polymers, flame
retardants, cross-linkers, etc. One example of a bio-based compound
that can be used in these applications is vanillin
(4-hydroxy-3-methoxybenzaldehyde). Vanillin is a plant metabolite
and the main component of natural vanilla extract. While vanillin
can be obtained from vanilla extract, or synthesized from
petroleum-based raw materials, a number of biotechnology processes
are also used to produce vanillin. These processes can be
plant-based or microorganism-based, and provide a renewable source
of vanillin on an industrial scale.
SUMMARY
[0003] Various embodiments are directed to flame-retardant
vanillin-derived cross-linkers. The flame-retardant
vanillin-derived cross-linkers can have at least one phosphoryl or
phosphonyl moiety. Each phosphoryl or phosphonyl moiety can have at
least one substituent selected from a group consisting of a phenyl
substituent, an allyl substituent, an epoxide substituent, a
propylene carbonate substituent, and a thioether substituent. The
thioether substituent can be a hydroxyl-functionalized thioether
substituent, an amino-functionalized thioether substituent, or a
carboxylic acid-functionalized thioether substituent. The
flame-retardant vanillin-derived cross-linkers can be synthesized
from vanillin obtained from a bio-based source. Additional
embodiments are directed to forming a flame-retardant polymer. The
polymer can be produced by forming a diol vanillin derivative,
forming a phosphorus-based flame-retardant molecule, and reacting
the diol vanillin derivative and the phosphorus-based
flame-retardant molecule with one another to form a flame-retardant
vanillin-derived cross-linker. The flame-retardant vanillin-derived
cross-linker can then be bound to a polymer, forming the
flame-retardant polymer. The diol vanillin derivative can be a
phenol diol vanillin derivative, a carboxylic acid diol vanillin
derivative, or a benzyl alcohol diol vanillin derivative. The
phosphorus-based flame-retardant molecule can be a phosphate-based
molecule or a phosphonate-based molecule with at least one phenyl
substituent, allyl substituent, epoxide substituent, propylene
carbonate substituent, or thioether substituent. Further
embodiments are directed to an article of manufacture comprising a
material that contains a flame-retardant vanillin-derived
cross-linker. The material can be a resin, plastic, adhesive,
polymer, etc. Examples of polymer materials can include
polyurethane, an epoxy, a polyhydroxyurethane, a polycarbonate, a
polyester, a polyacrylate, a polyimide, a polyamide, a polyurea,
and a poly(vinyl-ester).
BRIEF DESCRIPTION OF THE DRAWINGS
[0004] FIG. 1 is a flow diagram illustrating a process of forming a
flame-retardant polymer with flame-retardant vanillin-derived
cross-linkers, according to embodiments of the present
disclosure.
[0005] FIG. 2A is a chemical reaction diagram illustrating
processes of synthesizing three diol compounds derived from
vanillin, according to embodiments of the present disclosure.
[0006] FIG. 2B is a diagrammatic representation of the molecular
structures of generic phosphorus-based flame-retardant molecules,
according to embodiments of the present disclosure.
[0007] FIG. 3A is a chemical reaction diagram illustrating two
processes of synthesizing a phosphate-based flame-retardant
molecule, according to embodiments of the present disclosure.
[0008] FIG. 3B is a chemical reaction diagram illustrating two
processes of synthesizing a phosphonate-based flame-retardant
molecule, according to embodiments of the present disclosure.
[0009] FIG. 3C is a diagrammatic representation of the molecular
structures of three thiol molecules that are involved in the
synthesis of the flame-retardant vanillin-derived cross-linkers,
according to some embodiments of the present disclosure.
[0010] FIG. 4A is a chemical reaction diagram illustrating a
process of synthesizing a functionalized flame-retardant phenol
vanillin-derived cross-linker, according to some embodiments of the
present disclosure.
[0011] FIG. 4B is a chemical reaction diagram illustrating three
processes of synthesizing thioether-linked flame-retardant phenol
vanillin-derived cross-linkers, according to some embodiments of
the present disclosure.
[0012] FIG. 4C is a chemical reaction diagram illustrating a
process of synthesizing a propylene carbonate-functionalized
flame-retardant phenol vanillin-derived cross-linker, according to
some embodiments of the present disclosure.
[0013] FIG. 4D is a chemical reaction diagram illustrating a
process of synthesizing a functionalized flame-retardant carboxylic
acid vanillin-derived cross-linker, according to some embodiments
of the present disclosure.
[0014] FIG. 4E is a chemical reaction diagram illustrating three
processes of synthesizing thioether-linked flame-retardant
carboxylic acid vanillin-derived cross-linkers, according to some
embodiments of the present disclosure.
[0015] FIG. 4F is a chemical reaction diagram illustrating a
process of synthesizing a propylene carbonate-functionalized
flame-retardant carboxylic acid vanillin-derived cross-linker,
according to some embodiments of the present disclosure.
[0016] FIG. 4G is a chemical reaction diagram illustrating a
process of synthesizing a functionalized flame-retardant benzyl
alcohol vanillin-derived cross-linker, according to some
embodiments of the present disclosure.
[0017] FIG. 4H is a chemical reaction diagram illustrating three
processes of synthesizing thioether-linked flame-retardant benzyl
alcohol vanillin-derived cross-linkers, according to some
embodiments of the present disclosure.
[0018] FIG. 4I is a chemical reaction diagram illustrating a
process of synthesizing a propylene carbonate-functionalized
flame-retardant benzyl alcohol vanillin-derived cross-linker,
according to some embodiments of the present disclosure.
DETAILED DESCRIPTION
[0019] Bio-based compounds are increasingly being used in the
synthesis of substances that previously required petroleum-based
raw materials. One benefit of bio-based compounds is that they are
from renewable resources. Therefore, these compounds have
applications in sustainable, or "green," materials. Sustainable
materials are becoming more and more prevalent, due to the rising
costs of fossil fuels and increasing environmental regulatory
controls. Advances in biotechnology have provided numerous
strategies for efficiently and inexpensively producing bio-based
compounds on an industrial scale. Examples of these strategies
include plant-based or microorganism-based approaches. Plant-based
approaches can involve obtaining a material directly from a plant,
or growing plant tissues or cells that can produce bio-based
compounds from various substrates using their own biosynthetic
pathways. Microorganism-based approaches involve using native or
genetically modified fungi, yeast, or bacteria to produce a desired
compound from a structurally similar substrate.
[0020] Examples of substances that can be produced from bio-based
compounds include polymers, flame retardants, cross-linkers, etc.
In some examples, bio-based polymers and petroleum-based polymers
are blended to form a polymer composite. However, polymers can also
be entirely bio-based, or produced from a combination of bio- and
petroleum-based monomers. Bio-based compounds can also impart
flame-retardant properties to bio- and petroleum-based polymers.
For example, flame-retardant monomers or cross-linkers can be
incorporated into polymers. Additionally, flame-retardant molecules
can be blended or chemically reacted with the polymers.
[0021] Vanillin (4-hydroxy-3-methoxybenzaldehyde) is one example of
a bio-based compound that can have applications as a component of
various polymers, resins, and small molecules. Vanillin is a plant
metabolite and the main component of natural vanilla extract. It
can be obtained from the plant- and microorganism-based bio-sources
discussed above, or synthesized from petroleum-based raw materials.
According to some embodiments of the present disclosure, vanillin
is used as a precursor for flame-retardant cross-linkers. These
flame-retardant vanillin-derived cross-linkers can be incorporated
into to polymers and resins by functional groups on flame-retardant
moieties.
[0022] FIG. 1 is a flow diagram 100 illustrating a process of
forming a flame-retardant polymer with flame-retardant
vanillin-derived cross-linkers 106, according to embodiments of the
present disclosure. Process 100 begins with the formation of a diol
derivative of vanillin. This is illustrated at step 105. A diol is
a molecule with two hydroxyl groups, and diol derivatives of
vanillin are formed when the aldehyde functional group on a
vanillin molecule is replaced by a hydroxyl group or a substituent
that contains a hydroxyl group. The identity of the substituent
with the hydroxyl group is determined by the reaction conditions
under which the diol derivative is produced. Examples of reaction
conditions that can convert vanillin to a diol molecule include
oxidation by sodium percarbonate, oxidation by potassium
permanganate, and reduction by sodium borohydride. The structures
and syntheses of three examples of diol derivatives of vanillin are
discussed in greater detail with regard to FIG. 2A.
[0023] Process 100 continues with the formation of a
phosphorus-based flame-retardant molecule. This is illustrated at
step 110. The phosphorus-based flame-retardant molecule has either
a phosphoryl or phosphonyl moiety (collectively referred to as an
FR group) with an attached R group. Examples of R groups that can
be attached to the FR group include phenyl substituents, epoxide
substituents, allyl substituents, propylene carbonate substituents,
and functionalized thioether substituents, such as
hydroxyl-functionalized thioether substituents,
amino-functionalized thioether substituents, and carboxylic
acid-functionalized thioether substituents. The syntheses and
structures of phosphorus-based flame-retardant molecules are
discussed in greater detail with regard to FIGS. 2B-3B. It should
be noted that the formation of the phosphorus-based flame-retardant
molecule of step 110 is illustrated as occurring after the
formation of the diol vanillin derivative in step 105. However, in
some embodiments, step 110 can occur before step 105.
[0024] The diol derivative of vanillin and the phosphorus-based
flame-retardant molecule are chemically reacted in order to form a
flame-retardant vanillin-derived cross-linker 106. This is
illustrated at step 115. The identity of the M group on the
flame-retardant vanillin-derived cross-linker 106 is determined by
the phosphorus-based flame-retardant molecule and the diol vanillin
derivative used in the reaction. The phosphorus-based
flame-retardant molecules react with hydroxyl groups on the
vanillin derivatives to provide the FR group with the attached R
group. The identities of the FR and R groups on the generic
flame-retardant vanillin-derived cross-linkers 106 can vary.
Examples of FR groups, as well as the syntheses and structures of
flame-retardant vanillin-derived cross-linkers 106 are discussed in
greater detail with regard to FIGS. 4A-4I.
[0025] The flame-retardant vanillin-derived cross-linker 106 formed
in step 115 is chemically reacted with a polymer, forming a bond
between the flame-retardant vanillin-derived cross-linkers 106 and
the polymer. This is illustrated at step 120. The binding of the
flame-retardant vanillin-derived cross-linker 106 to the polymer
forms a flame-retardant polymer. Examples of targeted polymers
include epoxies, polyhydroxyurethanes, polyurethane,
polycarbonates, polyesters, polyacrylates, polyimides, polyamides,
polyureas, poly(vinyl-esters), etc. The materials for these
polymers can come from petroleum- or bio-based sources.
[0026] FIG. 2A is a chemical reaction diagram illustrating
processes 200-1, 200-2, and 200-3 of synthesizing three diol
compounds derived from vanillin, according to embodiments of the
present disclosure. The three diol vanillin derivatives are a
phenol diol derivative 210, a carboxylic acid diol derivative 220,
and a benzyl alcohol diol derivative 230. These vanillin
derivatives are precursors for the flame-retardant vanillin-derived
cross-linkers 106. The syntheses of the flame-retardant
vanillin-derived cross-linkers 106 from the diol vanillin
derivatives are described in greater detail with regard to FIGS.
4A, 4D, and 4G.
[0027] In process 200-1, the phenol diol derivative 210 of vanillin
is produced in an oxidation reaction with sodium percarbonate.
Deionized water is added to a solution of vanillin 205 in
tetrahydrofuran (THF). The resulting vanillin/THF/H.sub.2O solution
is degassed with an inert gas (e.g., argon or nitrogen). While
agitating the mixture, sodium percarbonate (Na.sub.2CO.sub.3.1.5
H.sub.2O.sub.2) is added until pH=3 is reached, thus quenching the
reaction. After quenching the reaction, the THF is evaporated, and
the aqueous phase is extracted with ethyl acetate. The organic
phases are collected, washed with brine, and dried over anhydrous
sodium sulfate (Na.sub.2SO.sub.4). The ethyl acetate is removed
under reduced pressure, yielding the isolated phenol diol
derivative 210.
[0028] In process 200-2, the carboxylic acid diol derivative 220 of
vanillin is produced in an oxidation reaction with potassium
permanganate. Potassium permanganate (KMnO.sub.4) is added to an
acetone/H.sub.2O solution of vanillin 205. The mixture is stirred
for approximately 1.5 hours at room temperature. Sodium bisulfite
(NaHSO.sub.3) in hydrochloric acid (HCl) is added to the resulting
purple mixture until the mixture is colorless. The mixture is
extracted with ethyl acetate, and the organic phases are collected,
washed with brine, and dried over anhydrous magnesium sulfate
(MgSO.sub.4). The ethyl acetate is removed under reduced pressure,
yielding the isolated carboxylic acid diol derivative 220.
[0029] In process 200-3, the benzyl alcohol diol derivative 230 of
vanillin is produced in a reduction reaction with sodium
borohydride. Sodium borohydride (NaBH.sub.4) is added to a solution
of vanillin 205 in anhydrous ether or tetrahydrofuran (THF). The
mixture is stirred at room temperature under an inert gas (e.g.,
argon or nitrogen) for approximately four hours. The mixture is
then concentrated, and purified by column chromatography to give
the benzyl alcohol diol derivative 230 as a colorless oil.
[0030] FIG. 2B is a diagrammatic representation of the molecular
structures 202 of generic phosphorus-based flame-retardant
molecules 240, according to embodiments of the present disclosure.
Each phosphorus-based flame-retardant molecule 240 is either a
phosphate-based flame-retardant molecule 240-1 or a
phosphonate-based flame-retardant molecule 240-2. Herein,
phosphoryl and phosphonyl moieties are replaced by the abbreviation
"FR" in order to simplify illustrations of the molecular
structures. Each phosphorus-based flame-retardant molecule 240 has
a phenyl (Ph) substituent and an R group that can bind to a
resin.
[0031] The identities of the R groups bound to the phosphorus-based
flame-retardant molecules 240 vary, and are discussed in greater
detail with respect to FIGS. 3A, 3B, and 4A-4I Additionally, in
some embodiments, the phenyl group is replaced by another alkyl
substituent (e.g., methyl, ethyl, propyl, isopropyl, etc.). The
syntheses of the phosphorus-based flame-retardant molecules 240 are
discussed with regard to FIGS. 3A and 3B. The phosphorus-based
flame-retardant molecules 240 are reacted with the vanillin diol
derivatives 210, 220, and 230 to form flame-retardant
vanillin-derived cross-linkers 106. These reactions are discussed
in greater detail with regard to FIGS. 4A, 4D, and 4G.
[0032] FIG. 3A is a chemical reaction diagram illustrating two
processes 300-1 and 300-2 of synthesizing the phosphate-based
flame-retardant molecule 240-1, according to embodiments of the
present disclosure. In both processes 300-1 and 300-2, an alcohol
305 is a starting material for the phosphate-based flame-retardant
molecule 240-1. The alcohol 305 has either an allyl R group 307 or
an epoxide R group 308. It should be noted that, though an allyl
group 307 with a single methylene spacer group is illustrated here,
other alcohols with allylic chains of varying lengths (e.g., one to
twelve methylene spacer groups) could be used. Additionally,
alcohols with acrylate substituents are used in some
embodiments.
[0033] In process 300-1, the alcohol 305 is reacted with diphenyl
phosphite and titanium isopropoxide (Ti(O.sup.i(Pr).sub.4) in
benzene to produce a precursor 310 to the phosphate-based
flame-retardant molecule 240-1. In this pseudo-transesterification
reaction, the precursor 310 is formed when a phenyl (Ph)
substituent on diphenyl phosphite is replaced by an allyl 307 or
epoxide 308 R group from the alcohol 305. The precursor 310 is then
reacted with thionyl chloride (SOCl.sub.2) and carbon tetrachloride
(CCl.sub.4) over a range of 0.degree. C. to room temperature (RT),
forming the phosphate-based flame-retardant molecule 240-1.
[0034] In process 300-2, the alcohol 305 is reacted with diphenyl
phosphite in a tetrahydrofuran (THF) solution containing triethyl
amine (Et.sub.3N). This process is carried out over a range of
0.degree. C. to room temperature (RT). A chloride on the phenyl
dichlorophosphate is replaced by the alcohol 305, forming the
phosphate-based flame-retardant molecule 240-1 with an allyl 307 or
epoxide 308 R group.
[0035] FIG. 3B is a chemical reaction diagram illustrating two
processes 300-3 and 300-4 of synthesizing the phosphonate-based
flame-retardant molecule 240-2, according to embodiments of the
present disclosure. In both processes 300-3 and 300-4, an
organochloride 320 is a starting material for the phosphonate-based
flame-retardant molecule 240-2. The organochloride 320 has either
an allyl R group 307 or an epoxide R group 308. It should be noted
that, as in the case of the alcohol 305, other organochlorides with
allylic chains of varying lengths (e.g., one to twelve methylene
spacer groups) could be used. Additionally, organochlorides with
acrylate substituents are used in some embodiments.
[0036] In process 300-3, the organochloride 320 is reacted with
triphenyl phosphite (P(OPh).sub.3). The mixture is heated, either
by refluxing in toluene or microwaving (mw) in ethanol (EtOH),
producing a phosphonyl ester precursor 325 to the phosphonate-based
flame-retardant molecule 240-2. The phosphonyl ester precursor 325
is reacted with phosphorus pentachloride (PCl.sub.5) to form the
phosphonate-based flame-retardant molecule 240-2 with an allyl 307
or epoxide 308 R group.
[0037] In process 300-4, a mixture of the organochloride 320 and
triphenyl phosphite (P(OPh).sub.3) is heated, either by refluxing
in toluene or microwaving (mw) in ethanol (EtOH), forming a
phenylphosphinic acid precursor 327 to the phosphonate-based
flame-retardant molecule 240-2. The reaction is then quenched by
raising the pH of the solution. In this prophetic example, an
ethanol (EtOH)/water (H.sub.2O) solution of sodium hydroxide (NaOH)
is added to the reaction mixture. However, in some embodiments,
bases other than sodium hydroxide, such as potassium hydroxide or
lithium hydroxide, are used to quench the reaction. When the
reaction has been quenched, thionyl chloride (SOCl.sub.2) is added
to the phenylphosphinic acid precursor 327, producing the
phosphonate-based flame-retardant molecule 240-2 with an allyl 307
or epoxide 308 R group.
[0038] FIG. 3C is a diagrammatic representation of the molecular
structures 302 of three thiol molecules that are involved in the
synthesis of the flame-retardant vanillin-derived cross-linkers,
according to some embodiments of the present disclosure. The three
thiol molecules are 2-mercaptoethanol 335, cysteamine hydrochloride
(HCl) 340, and 3-mercaptopropionate 345. Each of these thiols is
involved in the synthesis of a thioether-linked flame-retardant
vanillin derivative. The thiol molecules provide a thioether R
group. Details of the syntheses and structures of the
thioether-linked flame-retardant vanillin derivatives are discussed
in greater detail with regard to FIGS. 4B, 4E, and 4H.
[0039] FIG. 4A is a chemical reaction diagram illustrating a
process 400-1 of synthesizing a functionalized flame-retardant
phenol vanillin-derived cross-linker 406, according to some
embodiments of the present disclosure. In process 400-1, the phenol
diol derivative 210 of vanillin is reacted with a phosphorus-based
flame-retardant molecule 240 and catalytic dimethylaminopyridine
(DMAP) in a dichloromethane (DCM) solution. In some embodiments,
stoichiometric triethylamine is used instead of DMAP. Additionally,
tetrahydrofuran (THF) is used as a solvent in some embodiments.
Stirring this mixture yields the functionalized flame-retardant
phenol vanillin-derived cross-linker 406.
[0040] If process 400-1 is carried out with a phosphorus-based
flame-retardant molecule 240 having an allyl R group 307, the
functionalized flame-retardant phenol vanillin-derived cross-linker
406 will be an allyl-functionalized flame-retardant phenol
vanillin-derived cross-linker 406-1 Likewise, if process 400-1 is
carried out with a phosphorus-based flame-retardant molecule 240
having an epoxide R group 308, the functionalized flame-retardant
phenol vanillin-derived cross-linker 406 will be an
epoxide-substituted flame-retardant phenol vanillin-derived
cross-linker 406-2. If the process is carried out with the
phosphate-based flame-retardant molecule 240-1, the functionalized
flame-retardant phenol vanillin-derived cross-linker 406 will have
a phosphoryl FR group, and, if the reaction is carried out with the
phosphonate-based flame-retardant molecule 240-2, the
functionalized flame-retardant phenol vanillin-derived cross-linker
406 will have a phosphonyl FR group.
[0041] FIG. 4B is a chemical reaction diagram illustrating three
processes 400-2, 400-3, and 400-4 of synthesizing thioether-linked
flame-retardant phenol vanillin-derived cross-linkers, according to
some embodiments of the present disclosure. Each process is a
thiol-ene reaction between the allyl-functionalized flame-retardant
phenol vanillin-derived cross-linker 406-1 and a thiol molecule.
The thiol molecules used in processes 400-2, 400-3, and 400-4 are
2-mercaptoethanol 335, cysteamine HCl 340, and 3-mercaptopropionate
345, respectively. The structures of these thiol molecules are
illustrated in FIG. 3C.
[0042] In process 400-2, the allyl-functionalized flame-retardant
phenol vanillin-derived cross-linker 406-1 is reacted with
2-mercaptoethanol 335 under UV light. The resulting
hydroxyl-functionalized flame-retardant phenol vanillin-derived
cross-linker 411 of vanillin has thioether R.sub.3 groups 412 that
correspond to 2-mercaptoethanol 335. In process 400-3, the
allyl-functionalized flame-retardant phenol vanillin-derived
cross-linker 406-1 is reacted with cysteamine HCl 340 in a pH 9
methanol (MeOH) solution under UV light. The resulting
amino-functionalized flame-retardant phenol vanillin-derived
cross-linker 416 has thioether R.sub.4 groups 417 that correspond
to cysteamine HCl 340. In process 400-4, the allyl-functionalized
flame-retardant phenol vanillin-derived cross-linker 406-1 is
reacted with 3-mercaptopropionate 345 under UV light in a methanol
(MeOH) solution. The resulting carboxylic acid-functionalized
flame-retardant phenol vanillin-derived cross-linker 421 has
thioether R.sub.5 groups 422 that correspond to
3-mercaptopropionate 345.
[0043] FIG. 4C is a chemical reaction diagram illustrating a
process 400-5 of synthesizing a propylene carbonate-functionalized
flame-retardant phenol vanillin-derived cross-linker 426, according
to some embodiments of the present disclosure. The
epoxide-functionalized flame-retardant phenol derivative 406-2 of
vanillin is combined with lithium bromide (LiBr). Carbon dioxide
(CO.sub.2) is added to the mixture, either by injecting into the
headspace of the reaction flask, or by bubbling through the
solution. This step yields the propylene carbonate-functionalized
flame-retardant phenol vanillin-derived cross-linker 426.
[0044] FIG. 4D is a chemical reaction diagram illustrating a
process 400-6 of synthesizing a functionalized flame-retardant
carboxylic acid vanillin-derived cross-linker 431, according to
some embodiments of the present disclosure. The carboxylic acid
diol derivative 220 of vanillin is reacted with a phosphorus-based
flame-retardant molecule 240, as well as magnesium oxide (MgO) and
catalytic dimethylaminopyridine (DMAP). In some embodiments, DMAP
is omitted from the reaction. Stirring this mixture yields the
functionalized flame-retardant carboxylic acid vanillin-derived
cross-linker 431.
[0045] If process 400-6 is carried out with a phosphorus-based
flame-retardant molecule 240 having an allyl R group 307, the
functionalized flame-retardant carboxylic acid vanillin-derived
cross-linker 431 will be an allyl-functionalized flame-retardant
carboxylic acid vanillin-derived cross-linker 431-1. Likewise, if
process 400-6 is carried out with a phosphorus-based
flame-retardant molecule 240 having an epoxide R group 308, the
functionalized flame-retardant carboxylic acid vanillin-derived
cross-linker 431 will be an epoxide-substituted flame-retardant
carboxylic acid vanillin-derived cross-linker 431-2. If the process
is carried out with the phosphate-based flame-retardant molecule
240-1, the functionalized flame-retardant carboxylic acid
vanillin-derived cross-linker 431 will have a phosphoryl FR group,
and, if the reaction is carried out with the phosphonate-based
flame-retardant molecule 240-2, the functionalized flame-retardant
carboxylic acid vanillin-derived cross-linker 431 will have a
phosphonyl FR group.
[0046] FIG. 4E is a chemical reaction diagram illustrating three
processes 400-7, 400-8, and 400-9 of synthesizing thioether-linked
flame-retardant carboxylic acid vanillin-derived cross-linkers,
according to some embodiments of the present disclosure. Each
process is a thiol-ene reaction between the allyl-functionalized
flame-retardant carboxylic acid vanillin-derived cross-linker 431-1
and a thiol molecule. The thiol molecules used in processes 400-7,
400-8, and 400-9 are 2-mercaptoethanol 335, cysteamine HCl 340, and
3-mercaptopropionate 345, respectively. The structures of these
thiol molecules are illustrated in FIG. 3C.
[0047] In process 400-7, the allyl-functionalized flame-retardant
carboxylic acid vanillin-derived cross-linker 431-1 is reacted with
2-mercaptoethanol 335 under UV light. The resulting
hydroxyl-functionalized flame-retardant carboxylic acid
vanillin-derived cross-linker 436 of vanillin has thioether R.sub.3
groups 412 that correspond to 2-mercaptoethanol 335. In process
400-8, the allyl-functionalized flame-retardant carboxylic acid
vanillin-derived cross-linker 431-1 is reacted with cysteamine HCl
340 in a pH 9 methanol (MeOH) solution under UV light. The
resulting amino-functionalized flame-retardant carboxylic acid
vanillin-derived cross-linker 441 has thioether R.sub.4 groups 417
that correspond to cysteamine HCl 340. In process 400-9, the
allyl-functionalized flame-retardant carboxylic acid
vanillin-derived cross-linker 431-1 is reacted with
3-mercaptopropionate 345 under UV light in a methanol (MeOH)
solution. The resulting carboxylic acid-functionalized
flame-retardant carboxylic acid vanillin-derived cross-linker 446
has thioether R.sub.5 groups 422 that correspond to
3-mercaptopropionate 345.
[0048] FIG. 4F is a chemical reaction diagram illustrating a
process 400-10 of synthesizing a propylene carbonate-functionalized
flame-retardant carboxylic acid vanillin-derived cross-linker 451,
according to some embodiments of the present disclosure. The
epoxide-functionalized flame retardant carboxylic acid derivative
431-2 of vanillin is combined with lithium bromide (LiBr). Carbon
dioxide (CO.sub.2) is added to the mixture, either by injecting
into the headspace of the reaction flask, or by bubbling through
the solution. This step yields the propylene
carbonate-functionalized flame-retardant carboxylic acid
vanillin-derived cross-linker 451.
[0049] FIG. 4G is a chemical reaction diagram illustrating a
process 400-11 of synthesizing a functionalized flame-retardant
benzyl alcohol vanillin-derived cross-linker 456, according to some
embodiments of the present disclosure. The benzyl alcohol diol
derivative 230 of vanillin is reacted with a phosphorus-based
flame-retardant molecule 240 and catalytic dimethylaminopyridine
(DMAP) in a dichloromethane (DCM) solution. In some embodiments,
stoichiometric triethylamine is used instead of DMAP. Stirring this
mixture yields the functionalized flame-retardant benzyl alcohol
vanillin-derived cross-linker 456.
[0050] If process 400-11 is carried out with a phosphorus-based
flame-retardant molecule 240 having an allyl R group 307, the
functionalized flame-retardant benzyl alcohol vanillin-derived
cross-linker 456 will be an allyl-functionalized flame-retardant
benzyl alcohol vanillin-derived cross-linker 456-1. Likewise, if
process 400-11 is carried out with a phosphorus-based
flame-retardant molecule 240 having an epoxide R group 308, the
functionalized flame-retardant benzyl alcohol vanillin-derived
cross-linker 456 will be an epoxide-substituted flame-retardant
benzyl alcohol vanillin-derived cross-linker 456-2. If the process
is carried out with the phosphate-based flame-retardant molecule
240-1, the functionalized flame-retardant benzyl alcohol
vanillin-derived cross-linker 456 will have a phosphoryl FR group,
and, if the reaction is carried out with the phosphonate-based
flame-retardant molecule 240-2, the functionalized flame-retardant
benzyl alcohol vanillin-derived cross-linker 456 will have a
phosphonyl FR group.
[0051] FIG. 4H is a chemical reaction diagram illustrating three
processes 400-12, 400-13, and 400-14 of synthesizing
thioether-linked flame-retardant benzyl alcohol vanillin-derived
cross-linkers, according to some embodiments of the present
disclosure. Each process is a thiol-ene reaction between the
allyl-functionalized flame-retardant benzyl alcohol
vanillin-derived cross-linker 456-1 and a thiol molecule. The thiol
molecules used in processes 400-12, 400-13, and 400-14 are
2-mercaptoethanol 335, cysteamine HCl 340, and 3-mercaptopropionate
345, respectively. The structures of these thiol molecules are
illustrated in FIG. 3C.
[0052] In process 400-12, the allyl-functionalized flame-retardant
benzyl alcohol vanillin-derived cross-linker 456-1 is reacted with
2-mercaptoethanol 335 under UV light. The resulting
hydroxyl-functionalized flame-retardant benzyl alcohol
vanillin-derived cross-linker 461 of vanillin has thioether R.sub.3
groups 412 that correspond to 2-mercaptoethanol 335. In process
400-13, the allyl-functionalized flame-retardant benzyl alcohol
vanillin-derived cross-linker 456-1 is reacted with cysteamine HCl
340 in a pH 9 methanol (MeOH) solution under UV light. The
resulting amino-functionalized flame-retardant benzyl alcohol
vanillin-derived cross-linker 466 has thioether R.sub.4 groups 417
that correspond to cysteamine HCl 340. In process 400-14, the
allyl-functionalized flame-retardant carboxylic acid
vanillin-derived cross-linker 456-1 is reacted with
3-mercaptopropionate 345 under UV light in a methanol (MeOH)
solution. The resulting carboxylic acid-functionalized
flame-retardant benzyl alcohol vanillin-derived cross-linker 471
has thioether R.sub.5 groups 422 that correspond to
3-mercaptopropionate 345.
[0053] FIG. 4I is a chemical reaction diagram illustrating a
process 400-15 of synthesizing a propylene carbonate-functionalized
flame-retardant benzyl alcohol vanillin-derived cross-linker 476,
according to some embodiments of the present disclosure. The
epoxide-functionalized flame-retardant benzyl alcohol derivative
456-2 of vanillin is combined with lithium bromide (LiBr). Carbon
dioxide (CO.sub.2) is added to the mixture, either by injecting
into the headspace of the reaction flask, or by bubbling through
the solution. The reaction yields the propylene
carbonate-functionalized flame-retardant benzyl alcohol
vanillin-derived cross-linker 476.
[0054] In some embodiments, the processes of forming substituted
flame-retardant vanillin derivatives illustrated in FIGS. 4A, 4D,
and 4G are carried out with a mixture of both the phosphate-based
240-1 and the phosphonate-based 240-2 flame retardant molecules.
Carrying out processes 400-1, 400-6, and 400-11 with a mixture of
the phosphate-240-1 and phosphonate-based 240-2 flame retardant
molecules can result in substituted flame-retardant vanillin
derivatives with both phosphoryl and phosphonyl FR groups. However,
in some instances, adding a mixture of phosphate-240-1 and
phosphonate-based 240-2 flame retardant molecules can result in the
production of substituted flame-retardant vanillin derivatives with
all phosphoryl or all phosphonyl FR groups. Additionally, adding
both phosphate-240-1 and phosphonate-based 240-2 flame retardant
molecules to the reaction can yield a mixture of products that
includes some combination of derivatives with either all phosphoryl
or all phosphonyl FR groups and derivatives with both phosphoryl
and phosphonyl FR groups.
[0055] Further, in some embodiments, the processes of forming
thioether-linked flame-retardant vanillin derivatives illustrated
in FIGS. 4B, 4E, and 4H are carried out with mixtures of more than
one type of thiol molecule. This can result in the production of
thioether-linked flame-retardant vanillin derivatives that have two
different types of thioether-linked FR group. However, in some
instances, adding more than one type of thiol molecule to the
reaction mixture can result in thioether-linked flame-retardant
vanillin derivatives that have two identical thioether-linked FR
groups. Adding more than one type of thiol molecule to the reaction
mixture can also result in a mixture of products that includes some
combination of derivatives with either two different
thioether-linked FR groups or two identical thioether-linked FR
groups.
[0056] The flame-retardant vanillin-derived cross-linkers 106
disclosed herein can be bound to polymers via their R functional
groups, imparting flame-retardant properties to the polymers. One
example of a polymer that can be made flame-retardant by the
addition of flame-retardant vanillin-derived cross-linkers 106 is
polycarbonate-acrylonitrile butadiene styrene (PC-ABS), a plastic
that is often used in electronics hardware. Flame-retardant
vanillin-derived cross-linkers 106 can also be incorporated into
polyurethane. Polyurethane is a versatile polymer used in
applications that can include acoustic dampening, cushioning,
plastics, synthetic fibers, insulation, adhesives, etc. The
vanillin-based flame-resistant cross-linkers 106 can also be added
to adhesives such as bio-adhesives, elastomers, thermoplastics,
emulsions, thermosets, etc. Further, materials containing the
vanillin-based flame-resistant cross-linkers 106 can be
incorporated into various devices with electronic components that
can include printed circuit boards (PCBs), semiconductors,
transistors, optoelectronics, capacitors, resistors, etc.
[0057] Resins for printed circuit boards (PCBs) can be made
flame-retardant by incorporating flame-retardant vanillin-derived
cross-linkers 106. PCBs are electrical circuits that can be found
in most types of electronic device, and they support and
electronically connect electrical components in the device. PCBs
are formed by etching a copper conductive layer laminated onto an
insulating substrate. The insulating substrate can be a laminate
comprising a resin and a fiber. Many resins in PCBs contain a
polymer, such as an epoxy, a polyhydroxyurethane, a polycarbonate,
a polyester, a polyacrylate, a polyimide, a polyamide, a polyurea,
a poly(vinyl-ester), etc. Flame-retardant vanillin-derived vanillin
cross-linkers 106 can be bound to the polymers in the PCB resin in
order to prevent the PCB from catching fire when exposed to high
temperature environments or electrical power overloads.
[0058] It should be noted that, in some embodiments, the compounds
described herein can contain one or more chiral centers. These can
include racemic mixtures, diastereomers, enantiomers, and mixtures
containing one or more stereoisomer. Further, the disclosed can
encompass racemic forms of the compounds in addition to individual
stereoisomers, as well as mixtures containing any of these.
[0059] The synthetic processes discussed herein and their
accompanying drawings are prophetic examples, and are not limiting;
they can vary in reaction conditions, components, methods, etc. In
addition, the reaction conditions can optionally be changed over
the course of a process. In some instances, reactions that involve
multiple steps can be carried out sequentially, and, in other
instances, they can be carried out in one pot. Further, in some
embodiments, processes can be added or omitted while still
remaining within the scope of the disclosure, as will be understood
by a person of ordinary skill in the art.
* * * * *