U.S. patent application number 16/033394 was filed with the patent office on 2018-11-08 for thickened polymer.
This patent application is currently assigned to BEIERSDORF AG. The applicant listed for this patent is Vesna ALEKSANDROVIC-BONDZIC, Stephan FOERSTER, Sascha MERTENS. Invention is credited to Vesna ALEKSANDROVIC-BONDZIC, Stephan FOERSTER, Sascha MERTENS.
Application Number | 20180319911 16/033394 |
Document ID | / |
Family ID | 43920861 |
Filed Date | 2018-11-08 |
United States Patent
Application |
20180319911 |
Kind Code |
A1 |
ALEKSANDROVIC-BONDZIC; Vesna ;
et al. |
November 8, 2018 |
THICKENED POLYMER
Abstract
The invention relates to a thickened preparation comprising a
polymer which can be obtained by radical emulsion polymerization of
at least one acidic vinyl monomer or salt thereof, at least one
non-ionic vinyl monomer, in particular preferably a hydrophobic
non-ionic vinyl monomer, at least one monomer containing an
unsaturated terminal group and a polyoxyalkyene portion, at least
one crosslinking monomer, optionally a protective colloid, and is
characterized in that the polymerization is controlled such that
the gelling effect occurs at least at times, which is achieved by
the monomer addition (dosing time) taking place for 40 minutes,
particularly preferably for 30 minutes.
Inventors: |
ALEKSANDROVIC-BONDZIC; Vesna;
(Hamburg, DE) ; MERTENS; Sascha; (Reinbek, DE)
; FOERSTER; Stephan; (Hamburg, DE) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
ALEKSANDROVIC-BONDZIC; Vesna
MERTENS; Sascha
FOERSTER; Stephan |
Hamburg
Reinbek
Hamburg |
|
DE
DE
DE |
|
|
Assignee: |
BEIERSDORF AG
Hamburg
DE
|
Family ID: |
43920861 |
Appl. No.: |
16/033394 |
Filed: |
July 12, 2018 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
13700406 |
Apr 19, 2013 |
10023668 |
|
|
PCT/EP2011/054247 |
Mar 21, 2011 |
|
|
|
16033394 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C08F 128/02 20130101;
A61K 8/8152 20130101; C08F 2/22 20130101; C08F 220/18 20130101;
C08F 216/145 20200201; C08F 222/1006 20130101; C08F 220/04
20130101; A61Q 19/00 20130101; C08F 120/68 20130101; C08F 220/06
20130101; A61K 2800/10 20130101; A61K 2800/48 20130101; C08F
220/1818 20200201 |
International
Class: |
C08F 120/68 20060101
C08F120/68; C08F 220/04 20060101 C08F220/04; A61Q 19/00 20060101
A61Q019/00; C08F 2/22 20060101 C08F002/22; C08F 128/02 20060101
C08F128/02; A61K 8/81 20060101 A61K008/81; C08F 220/18 20060101
C08F220/18 |
Foreign Application Data
Date |
Code |
Application Number |
May 31, 2010 |
DE |
102010022063.9 |
Claims
1. A thickened preparation, wherein the preparation is present as
one or more of a cosmetic or dermatological product, a medicinal
product, a body cleansing composition, a cream, a shower gel, a
household cleaning composition, a paint, an ink, an adhesive, a
dispersant, an anti-settling agent, a concrete or cement additive,
and a coating composition, and wherein the preparation comprises as
thickener one or more polymers which are obtained by free-radical
emulsion polymerization of monomers comprising (A) at least one
acidic vinyl monomer or salt thereof, (B) at least one nonionic
vinyl monomer, (C) at least one monomer comprising an unsaturated
end group and a polyoxyalkylene portion, (D) at least one
crosslinking monomer, and (E) optionally, a protective colloid, the
polymerization being controlled such that at least at times a gel
effect arises, achieved by monomer addition (dosing time) taking
place over not more than 40 minutes.
2. The preparation of claim 1, wherein (B) comprises at least one
of a C.sub.12 alkyl acrylate and a C.sub.18 alkyl acrylate.
3. The preparation of claim 1, wherein the monomer addition takes
place over not more than 30 minutes.
4. The preparation of claim 1, wherein not more than 0.1% by weight
of associative monomers are present.
5. The preparation of claim 1, wherein (A) comprises one or more
monomers selected from vinyl monomers having carboxyl groups and
alkali, alkaline earth, ammonium, and alkylammonium salts
thereof.
6. The preparation of claim 1, wherein (A) comprises one or more
monomers selected from acrylic acid, methacrylic acid, and alkali,
alkaline earth, ammonium, and alkyl ammonium salts thereof.
7. The preparation of claim 1, wherein (B) comprises one or more
monomers selected from C1-C22-alkyl (meth)acrylates.
8. The preparation of claim 1, wherein (C) comprises one or more
monomers selected from vinylpolyalkylene glycols and polymerizable
surfactants.
9. The preparation of claim 8, wherein (C) comprises one or more
monomers selected from EO/PO 1,4-butanediol vinyl ether (EO/PO 30
mol), allylpolyalkylene glycol ether (EO 30 mol), allylpolyalkylene
glycol ether (EO 20 mol, PO 20 mol), vinylpolyalkylene glycol ether
(EO 20 mol), allyl alcohol alkoxylates, polyalkyleneglycol allyl
butyl ether (EO 25 mol, PO 8 mol).
10. The preparation of claim 1, wherein (D) comprises one or more
monomers selected from polyol (meth)acrylates comprising at least
two (meth)acrylate groups, and mixed esters of polyols with at
least one of acrylic acid and methacrylic acid.
11. The preparation of claim 1, wherein the polymer comprises from
10% to 75% by weight of (A), from 10% to 90% by weight of (B), from
0.5% to 40% by weight of (C), and up to 1% by weight of (D).
12. The preparation of claim 1, wherein a weight ratio (A):(B) is
from 1:2 to 2:1.
13. The preparation of claim 1, wherein the preparation comprises
from 2% to 3% by weight of the one or more polymers.
14. The preparation of claim 1, wherein the preparation has a tan
.delta. of from 0.05 to 0.6.
15. The preparation of claim 1, wherein at a pH of <6.2 the
preparation has a turbidity value of NTU<20.
16. The preparation of claim 1, wherein the preparation is present
as a cosmetic or dermatological composition.
17. The preparation of claim 1, wherein the preparation is present
as a body cleansing composition.
18. The preparation of claim 1, wherein the preparation is present
as a shower gel.
19. The preparation of claim 1, wherein the preparation is present
as a cream.
20. The preparation of claim 1, wherein the preparation is present
as a coating composition.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] The present application is a continuation of application
Ser. No. 13/700,406, which is a National Stage of International
Application PCT/EP2011/054247, filed Mar. 21, 2011; the entire
disclosures of both applications are expressly incorporated by
reference herein.
BACKGROUND OF THE INVENTION
1. Field of the Invention
[0002] The invention relates to a new type of thickening polymer
with special properties which is free from associative monomers
and/or whose chain contains no such associative monomers.
Definitions
[0003] Unless stated otherwise, all quantitative data are
percentages by mass based on the total mass of the preparation.
[0004] Within the context of the present specification, associative
monomers are monomers of the type U-S-L, where U contains an
ethylenically unsaturated group such as methacrylate, acrylate,
allyl or vinyl groups, S is a spacer from a polyoxyalkylene chain
having 2 to 300 alkyleneoxy units such as polyethylene glycol,
polypropylene glycol or polybutylene glycol, and L is a hydrophobic
group such as an alkyl and/or aryl group, which has at least 4,
preferably at least 8 carbon atoms, for example a lauryl group.
[0005] Within the context of the present specification, tan .delta.
value means the quotient of the loss modulus and the storage
modulus, in each case measured at 40.degree. C. The measuring
device used here is not important. The values given in this
specification were determined using the Malvern Gemini HR nano.
2. Discussion of Background Information
[0006] In general, thickening polymers serve to thicken water or
water-containing preparations. In this connection, the water allows
the polymers to swell to gels in order, in so doing, to influence
viscosity and flow behavior. Thickening polymers are of importance
in the manufacture of body cleansing compositions, creams, cleaning
compositions, finishes, printing inks, coatings, emulsion paints
and other coating materials, adhesives, paper, foods and so on.
[0007] Known from EP 1465932 B1 were alkali-swellable and
alkali-soluble associative multipurpose polymers which is the
polymerization product of a monomer mixture of [0008] a) at least
one acid-containing vinyl monomer, [0009] b) at least one nonionic
vinyl monomer, [0010] c) a first associative monomer which has a
first hydrophobic end group, [0011] d) a second associative monomer
with a second hydrophobic end group, a semi-hydrophobic monomer and
of a combination thereof and optionally [0012] e) one or more
crosslinking monomers or chain-transfer agents.
[0013] Such polymers are prepared by emulsion polymerization. For
this, firstly the monomer mixture is emulsified or suspended with a
surfactant in water in the form of micelles. The actual reactor is
charged with the initiator in aqueous solution or suspension, and
the monomer suspension is slowly added. The rate at which the
monomer is added is controlled so as to avoid a considerable
increase in the reaction temperature as a result of the Trommsdorff
effect (gel effect). The gel effect arises in the event of too
great an increase in the conversion and leads to the rate of the
polymerization increasing as a result of diffusion of the polymer
radicals being hindered, and the polymerization in itself is
accelerated. Attempts are made to prevent this for reasons of
safety and to obtain a narrow molar mass distribution. If the gel
effect does arise, then a bimodal molar mass distribution is
obtained. Further prior art can be found in EP 1272159, WO03062288,
WO03061615, WO03062288, WO2007090759, U.S. Pat. No. 6,242,531.
[0014] Thickening polymers with which it is possible to thicken
aqueous preparations such that gels which are as clear as possible
are formed are desirable.
[0015] Thickening polymers with which tan .delta. values which are
as low as possible can be achieved in aqueous solution are also
desirable.
[0016] Thickening polymers with a considerably extended storage
stability are likewise desirable.
[0017] The prior art lacked thickening polymers which make it
possible to produce clear gels coupled with simultaneously low tan
.delta. values.
SUMMARY OF THE INVENTION
[0018] Surprisingly and unforeseeably to the person skilled in the
art, it has now been found that a polymer obtainable by
free-radical emulsion polymerization of
[0019] (A) at least one acidic vinyl monomer or salt thereof,
[0020] (B) at least one nonionic vinyl monomer, particularly
preferably a hydrophobic nonionic vinyl monomer,
[0021] (C) at least one monomer containing an unsaturated end group
and a polyoxyalkylene portion,
[0022] (D) at least one crosslinking monomer,
[0023] (E) optionally a protective colloid, characterized in that
the polymerization is controlled such that at least at times the
gel effect arises, achieved by the fact that the monomer addition
(dosing time) takes place over the course of 40 minutes,
particularly preferably over the course of 30 minutes, overcomes
the defects of the prior art. In the case of such a polymerization
utilizing the Trommsdorff effect, i.e. with the constant addition
of the monomers and simultaneously high addition rate of the
monomers, a monomer excess is formed which leads to an
autoacceleration of the polymerization (Trommsdorff effect). The
result is an increase in the molecular weights coupled with
simultaneously advantageous morphology of the polymers. In this
connection, it is particularly preferred if (F) associative
monomers are not present or have at most a concentration of 15% by
weight, preferably 10% by weight, particularly preferably 5% by
weight, very particularly preferably 2.5% by weight, very
extraordinarily preferably 1% by weight, very particularly
extraordinarily preferably 0.1% by weight. It is particularly
preferred if the acidic vinyl monomer (A) is selected from vinyl
monomers with carboxyl groups, particularly preferably acrylic acid
or methacrylic acid or alkali metal, alkaline earth metal, ammonium
or alkylammonium salts thereof, very particularly preferably
methacrylic acid or alkali metal, alkaline earth metal, ammonium or
alkylammonium salts thereof. It is particularly preferred if the
nonionic vinyl monomer (B) is selected from C1-C22-alkyl
(meth)acrylates and mixtures thereof. As a result, good flow
properties and thus an advantageous rheological profile are
achieved.
[0024] Additional long-chain alkyl acrylates (C12 and C18) are
particularly preferred because they increase the viscosity that can
be achieved. It is particularly preferred if the monomer (C)
containing an unsaturated end group and a polyoxyalkylene portion
is selected from vinylpolyalkylene glycols or polymerizable
surfactants or mixtures thereof, is particularly preferably
selected from R307, RAL307, A11/1800, R1100, A111R, AB25-8. It is
particularly preferred if the crosslinking monomer (D) is selected
from polyol (meth)acrylates with at least two (meth)acrylate groups
and the mixed esters of polyols with acrylic acid and/or
methacrylic acid. It is further particularly preferred if the
monomers (A) are present in contents of from 10 to 75%, preferably
30 to 50%, particularly preferably 35 to 49%, (B) are present in
contents of from 10 to 90%, preferably 30 to 80%, particularly
preferably 47 to 60%, (C) are present in contents of from 0.5 to
40%, preferably 1 to 10%, particularly preferably 2 to 6%, (D) are
present in contents of up to 1%, preferably 0.05 to 0.5%,
particularly preferably 0.1 to 0.35%. It is very particularly
preferred if the monomers (A):(B) are present in mass ratios of
from 1:2 to 2:1. It is very particularly preferred if the polymer
is selected from example 22, 24, 25, 28, 35, 37, 40 or 52. The
invention also encompasses a thickened preparation comprising a
polymer as claimed in any one of the preceding claims. It is
particularly preferred if the use concentration of the polymer for
thickening aqueous, preferably surfactant-containing aqueous,
preparations is 2 to 3%. As a result, the preparation becomes
transparent at pH values <6.5 and has a viscosity of at least
3000 mPas, which means that added suspended substances do not
settle out, possible suspended substances being beads, pigments or
air bubbles. It is particularly preferred if the preparations
according to the invention are a health product, cleaning product,
household product, shower gel, paint, inks, dispersant,
antisettling agent, concrete and cement additive, coatings,
medicinal product, cosmetic product or dermatological product. The
invention also encompasses the use of a polymer according to the
invention as thickener, emulsifier, dispersant or consistency
regulator.
[0025] The preparations--if they are gel-like preparations with
yield point--are advantageously designed such that they have a
yield point of 0.5-20 Pa, preferably 1-6 Pa.
[0026] The yield point is considered to be the critical shear
stress of the flow curve. It can be ascertained according to the
invention as follows:
[0027] The flow curve is measured on a shear-stress-controlled
rheometer at 25.degree. C..+-.1.degree. C. with 20 mm plate/plate
geometry with a gap between 0.8 mm and 1.2 mm, with charging being
carried out in a structure-preserving manner. A suitable constant
shear stress gradient is pregiven and, before the test, a
corresponding structure recovery time is observed and the critical
shear stress at the maximum of the flow curve is given.
[0028] Advantageously, the preparations are designed such that they
have a tan .delta. of 0.05-0.6, preferably 0.1-0.5.
[0029] According to the invention, tan .delta. is understood as
meaning the quotient of the loss modulus and the storage modulus.
The tan .delta. is ascertained as follows:
[0030] Loss and storage moduli are measured by a dynamic frequency
test on a shear-stress-controlled rheometer at 40.degree.
C..+-.1.degree. C. with 20 mm plate/plate geometry with a gap
between 0.8 mm and 1.2 mm, charging being carried out in a
structure-preserving manner. The frequency test is carried out
according to the prior art with an appropriate structure recovery
time before the test, and the tan .delta. in the frequency range
between 0.05 rad/s and 3.0 rad/s is quoted, preferably between 0.08
rad/s and 1.0 rad/s.
[0031] The preparations are advantageously designed such that, at
pH<6.2, they have a turbidity value of NTU (Nephelometric
Turbidity Unit)<20. The turbidity value is measured using a
turbidity measuring device, with distilled water having a value of
NTU=0 serving as standard.
[0032] It is also in accordance with the invention if not water,
but other polar liquids are thickened by polymers according to the
invention. In particular, alcohols, glycols, polyols, amines and
organic acids such as for example acrylic acid can be
thickened.
[0033] The use of polymers according to the invention as emulsifier
is also in accordance with the invention. In this way, creams and
lotions can be provided.
[0034] The polymers are also suitable as dispersants and
antisettling agents.
DETAILED DESCRIPTION OF EMBODIMENTS OF THE INVENTION
Examples
[0035] Synthesis of the Copolymers
[0036] The examples below aim to illustrate the present invention
without limiting it. The preparation of the examples takes place in
accordance with the method described below, the type and amounts of
the monomers, chain-transfer agents and protective colloids each
used as starting components being summarized in Table 2. Parts and
percentages refer to the weight.
Example 1
TABLE-US-00001 [0037] Monomer phase Methacrylic acid 37.000 parts
Ethyl acrylate 51.800 parts Octadecyl acrylate 5.000 parts
Emulsogen R307 6.000 parts Trimethylolpropane triacrylate 0.300
parts Water phase Water 33.060 parts Sodium lauryl sulfate 0.984
parts Reaction vessel Water 173.146 parts Sodium lauryl sulfate
0.300 parts Initiator phase A Water 1.911 parts Ammonium persulfate
0.069 parts Initiator phase B Water 2.909 parts Ammonium persulfate
0.021 parts
[0038] The reaction vessel, which is equipped with stirrer, reflux
condenser, nitrogen feed, dosing device and internal thermometer,
is charged with 173.146 parts of water and 0.300 parts of sodium
lauryl sulfate. The mixture is heated to 82.degree. C. with
stirring and under a nitrogen atmosphere.
[0039] The monomer mixture is prepared in a second stirred vessel
which is equipped with stirrer and nitrogen feed. For this purpose,
the monomer phase with 37.000 parts methacrylic acid, 51.800 parts
ethyl acrylate, 5.000 parts octadecyl acrylate, 6.000 parts
Emulsogen R307 and 0.300 parts trimethylpropane triacrylate is
introduced, and into this is mixed the water phase with 33.060
parts water and 0.984 parts sodium lauryl sulfate with stirring and
under a nitrogen atmosphere.
[0040] As soon as a temperature of 82.degree. C. is reached in the
reaction vessel, an initiator phase A, consisting of 0.069 parts
ammonium persulfate and 1.911 parts of water, is added and the
monomer mixture is metered in uniformly at 85-88.degree. C. over
the course of 30 minutes. Then, an initiator phase B, consisting of
0.021 parts ammonium persulfate and 2.909 parts water, is added and
then the reaction mixture is post-polymerized for a further 4 hours
at 90.degree. C. before being cooled to <40.degree. C.
Examples 2-52
[0041] The examples below (Table 1) are prepared analogously to
Example 1. In most examples, sodium lauryl sulfate was used as
emulsifier. In a departure from this, Examples 5 and 11 were
prepared from a combination of sodium lauryl sulfate and
ethoxylated isotridecyl alcohol (Genapol X1005, Clamant), and
Example 10 was prepared with isotridecyl alcohol (Genapol X1005,
Clamant).
Abbreviations
[0042] MAA Methacrylic acid [0043] EA Ethyl acrylate [0044] LA
Lauryl acrylate [0045] ODA Octadecyl acrylate [0046] S20W
Bisomer.RTM. S20W (Cognis) [0047] Methoxypolyethylene glycol
methacrylate (EO 45 mol) [0048] M5010 Maxemul.RTM. 5010 (Croda)
[0049] C.sub.12H.sub.23HCCH(C.sub.2H.sub.4O.sub.25CH.sub.3 [0050]
R307 Emulsogen.RTM. R307 (Clariant) [0051] EO/PO 30 1,4-butanediol
vinyl ether (EO/PO 30 mol) [0052] RAL307 Emulsogen.RTM. RAL307
(Clariant) [0053] Allylpolyalkylene glycol ether (EO 30 mol) [0054]
R208 Emulsogen.RTM. R208 (Clariant) [0055] 1,4-Butanediol vinyl
ether (EO/PO 25 mol) [0056] A11/1800 Polyglycol A11/1800 (Clariant)
[0057] Allylpolyalkylene glycol ether (EO 20 mol, PO 20 mol) [0058]
R500 Polyglycol R500 (Clariant) [0059] Vinylpolyalkylene glycol
ether (EO 9 mol) [0060] R1100 Polyglycol R1100 (Clariant) [0061]
Vinylpolyalkylene glycol ether (EO 20 mol) [0062] R2000 Polyglycol
R2000 (Clariant) [0063] Vinylpolyalkylene glycol ether (EO 40 mol)
[0064] AM 20/20 Polyglycol AM 20/20 (Clariant) [0065] Polyalkylene
glycol allyl methyl ether (EO 20 mol, PO 20 mol) [0066] AB 1500
Polyglycol AB1500 (Clariant) [0067] Polypropylene glycol allyl
butyl ether (PO 25 mol) [0068] AB/25-8 Polyglycol AB/25-8
(Clariant) [0069] Polyalkylene glycol allyl butyl ether (EO 25 mol,
PO 8 mol) [0070] A31/1600 Polyglycol A31/1600 (Clariant) [0071]
Polyalkylene glycol allyl ether (EO 25 mol, PO 8 mol) [0072] A 10 R
Pluriol.RTM. A10R (BASF) [0073] Allyl alcohol alkoxylates [0074] A
111 R Pluriol.RTM. AMR (BASF) [0075] Allyl alcohol alkoxylates
[0076] SPE RALU.RTM.MER SPE (Raschig) [0077]
Dimethyl[2-[(2-methyl-1-oxoallyl)oxy]ethyl](3-sulfopropyl)ammonium
hydroxide [0078] SPM RALU.RTM.MER SPM (Raschig) [0079] Potassium
3-sulfopropylmethacrylate [0080] SPP RALU.RTM.MER SPP (Raschig)
[0081]
Dimethyl[3-[(2-methyl-1-oxoallyl)amino]propyl]-3-sulfopropylammonium
hydroxide [0082] HMP Bisomer.RTM. HMP (Cognis) [0083] Monoester of
maleic acid and C16-18 fatty alcohol [0084] KH-10 Hitenol.RTM.
KH-10 (Dai-Ichi Kogyo Seiyaku) [0085] Ammonium
polyoxyalkylene-1-(allyloxymethyl)alkyl ether sulfate
[0085] ##STR00001## [0086] BC-10 Hitenol.RTM. BC-10 (Dai-Ichi Kogyo
Seiyaku) [0087] Ammonium nonylphenol polyoxyethylene alkyl ether
sulfate
[0087] ##STR00002## [0088] BEM Behenyl ethylene glycol-1100
methacrylate [0089] TMPTA Trimethylolpropane triacrylate [0090]
TMPTMA Trimethylolpropane trimethacrylate [0091] IMP Isooctyl
3-mercaptopropionate [0092] AMHEC Tylose AM H40 YP2 (SE Tylose)
[0093] Allyl-modified hydroxyethylcellulose
TABLE-US-00002 [0093] TABLE 1 Examples 1-52 1 2 3 4 5 6 7 8 9 10 11
12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 MAA 37 37 37 37 37
37 37 37 37 37 37 37 37 37 37 37 37 37 37 37 37 37 37 37 37 37 37
EA 51. 53. 53. 53. 51. 53. 53. 53. 53. 53. 53. 47. 53. 53. 53. 53.
51. 51. 51.6 53. 53. 51. 53. 52. 54. 33. 56. ODA 5 5 5 5 5 5 5 5 5
5 5 5 5 5 5 5 5 5 5 5 5 5 5 5 5 5 5 LA 2 2 S20W 2 2 2 M5010 2 2 2 2
2 2 2 2 R307 6 2 2 2 2 4 2 2 2 10 2 2 2 2 6 6 6 2 2 RAL307 6 2 R208
24 A11/18 5.4 R500 R1100 2.9 R2000 AM AB AB/25-8 A31/16 A 10 R 1.7
A 111 R SPE 2 SPM 2 SPP 2 HMP 2 KH-10 2 BC-10 2 BEM TMPTA 0.3 0.3
0.3 0.3 0.3 0.3 0.3 0.5 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3
0.3 0.3 0.3 0.3 0.3 0.3 0.3 TMPTM 0.3 IMP 0.15 AMHEC 0.0 Ex. 28 29
30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51
52 MAA 37 37 37 37 37 37 37 37 28. 45. 37 37 37 37 37 37 37 37 37
37 37 37 47. 47. 37 EA 52. 52. 52. 51. 51. 53. 52. 53.1 60. 44 54.
49. 57. 51.8 49. 55. 57. 52. 52.2 52.5 56. 52. 46. 46. 52. ODA 5 5
5 5 5 5 5 5 5 5 2.5 7.5 5 5 5 5 5 5 5 5 5 5 LA S20W 5.4 M5010 R307
RAL307 R208 A11/180 5.4 5.4 5.4 5.4 5.4 5.4 5.4 5.4 8.1 2.7 5.4 5.4
5.4 5.4 5.4 R500 1.4 R1100 R2000 5.4 AM 5.4 AB 3.9 AB/25-8 4.63
A31/160 5.94 A 10 R A 111 R 5.4 5.4 SPE SPM SPP HMP KH-10 BC-10 BEM
5 TMPTA 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3
0.3 0.3 0.45 0.15 0.3 0.3 0.3 0.3 0.3 TMPTM IMP 0.1 0.1 AMHEC 0.1
0.1
TABLE-US-00003 TABLE 2 Results for polymer emulsions Example pH
value Particle size* in nm 1 2.48 108 2 2.47 103 3 n.d. n.d. 4 n.d.
n.d. 5 n.d. n.d. 6 n.d. n.d. 7 n.d. n.d. 8 n.d. n.d. 9 n.d. n.d. 10
n.d. n.d. 11 n.d. n.d. 12 n.d. n.d. 14 2.57 102 14 2.62 129 15 3.13
95 16 2.14 186 17 2.53 88 18 2.52 107 19 2.51 101 20 2.53 79 21
2.54 79 22 2.50 96 23 2.52 89 24 2.55 87 25 2.47 111 26 2.67 165 27
2.76 89 28 2.50 87 29 2.56 103 30 2.58 87 31 2.57 95 32 2.48 79 33
2.30 104 34 2.37 96 35 2.46 85 36 2.36 85 37 2.46 113 38 2.39 89 39
2.37 96 40 2.38 94 41 2.65 85 42 2.32 103 43 2.42 91 44 2.39 90 45
2.36 87 46 2.42 101 47 2.34 84 48 2.40 106 49 2.40 123 50 2.69 100
51 2.46 99 52 2.50 124 *The particle size in the polymer emulsion
is determined using dynamic light scattering (DLS) in a dilute
aqueous sample of the emulsion at 25.degree. C. .+-. 1.degree.
C.
Example 53
[0094] The preparation below is intended to illustrate the present
invention without limiting it. Unless stated otherwise, all
quantitative data, fractions and percentages are based on the
weight and the total amount or on the total weight of the
preparation.
[0095] The polymer according to the invention is diluted with some
of the water phase and added to the surfactant phase with stirring.
The other formulation constituents apart from NaOH and the
suspended bodies are then added with stirring. After the pH has
been adjusted, the suspended bodies are stirred into the finished
gel base with as little shear as possible.
TABLE-US-00004 TABLE 3 Preparation shower gel Sodium laureth
sulfate 6.50 Cocoamidopropylbetaine 4.60 Sodium cocoyl glutamate
0.50 Polymer 2.25 PEG-40 hydrogenated castor oil 0.80 PEG-7
glyceryl cocoate 1.75 Pigments q.s. NaOH q.s. Perfume q.s. Water ad
100
TABLE-US-00005 TABLE 4 Results for preparation shower gel Example
tan .delta. Viscosity in mPas pH of shower gel 1 0.30 3544 6.19 2
0.29 2600 6.21 3* 0.89 2605 6.15 4* 8.58 1977 6.18 5* 1.89 2014
6.15 6* 0.59 2234 6.20 7* 1.56 1967 6.18 8* 5.03 1548 6.19 9* 1.54
2043 6.18 10* n.d. n.d. n.d. 11* n.d. n.d. n.d. 12* 8.14 1465 6.11
13 0.32 2404 6.18 14 4.54 2055 6.25 15 0.70 1964 6.18 16 0.27 2423
6.15 17 3.57 3356 6.18 18 0.31 2092 6.20 19 1.12 1998 6.18 20 1.92
2754 6.17 21 4.42 2090 6.23 22 0.37 3118 6.23 23 0.35 3089 6.22 24
0.17 3409 6.20 25 0.19 4100 6.22 26 4.42 3592 5.86 27 0.15 2967
6.17 28 0.14 3301 6.15 29 2.58 2442 6.18 30 2.54 1941 6.21 31 0.52
2233 6.15 32 1.83 2752 6.15 33 0.79 2953 6.20 34 0.83 2208 6.21 35
0.24 3501 6.20 36 0.34 2833 6.38 37 0.23 3432 5.91 38 0.20 3262
6.18 38 0.26 3580 6.11 40 0.16 4120 6.25 41 0.39 3317 6.19 42 0.17
3230 6.15 43 0.25 3690 6.15 44 0.22 4167 6.28 45 5.97 3196 5.97 46
0.60 2385 6.14 47 0.26 4349 6.17 48 0.22 4073 6.29 49 0.42 3313
6.09 50 0.37 3827 5.87 51 0.83 3580 5.93 52 0.14 7344 6.07 *The
examples were prepared without perfume in the shower gel.
[0096] The viscosity of the preparations is measured on a rheometer
at 25.degree. C..+-.1.degree. C. with 40 mm cone/plate geometry
(1.degree. cone angle) with a gap of 0.03 mm, charging being
carried out in a structure-preserving manner. A suitable constant
shear rate time ramp is pregiven and a corresponding structure
recovery time is observed before the test. The viscosity is given
for a shear rate of 10 s.sup.-1.
Example 54
[0097] It has surprisingly been found that the morphology of the
polymers produced by a rapid dosing of the monomer mixture is
advantageous within the context of the present invention. Table 4
shows the various properties of two polymers when the dosing time
is varied. The dosing time is preferably 40 minutes and
particularly preferably 30 minutes.
TABLE-US-00006 TABLE 5 Dosing time and results Polymer Dosing time
tan .delta. Viscosity in mPas Example 35 30 minutes 0.24 3501
Example 35 40 minutes 0.21 4114 Example 35 50 minutes 0.49 4056
Example 35 60 minutes 1.45 3585 Example 24 30 minutes 0.17 3409
Example 24 50 minutes 24.26 1805
Example 55
[0098] The polymers according to the invention must have adequate
storage stability. For this purpose, a shower gel according to
Example 53 was produced again after one year from Examples 1, 22,
24, 25 and 28. It is found that the polymers according to the
invention are also advantageous after prolonged storage at room
temperature.
TABLE-US-00007 TABLE 6 Results of storage stability after 24 h
after storage Viscosity in Viscosity in Polymer tan .delta. mPas
Time tan .delta. mPas Example 1 0.30 3544 15 months 0.24 4285
Example 22 0.37 3118 13 months 0.29 4247 Example 24 0.17 3409 13
months 0.20 4083 Example 25 0.19 4100 13 months 0.22 4823 Example
28 0.14 3301 10 months 0.20 3754
Example 56
[0099] Compared to other polymers, the polymers according to the
invention overcome deficiencies in the prior art compared to other
polymers.
[0100] In order to illustrate this, a shower gel according to
Example 53 was prepared in each case from Examples 24, 37 and
Carbopol.RTM. AQUA SF-1 (Lubrizol).
TABLE-US-00008 TABLE 7 Results compared to AQUA SF-1 Example 24
Example 37 Carbopol .RTM. AQUA SF-1 tan .delta. 0.17 0.23 0.42
Viscosity in mPas 3409 3432 3834 Yield point in Pa 3.6 3.4 3.3 pH
6.20 5.91 6.45 Turbidity in NTU 8 9 18 (58 at pH 6.20)
[0101] At a lower pH than AQUA SF-1, the polymers according to the
invention have a better tan .delta. and a lower turbidity.
Turbidity values of <10 are comparable with spring water. Upon
adjusting a preparation containing AQUA SF-1 to a lower pH value,
e.g.: 6.20, the preparation is distinctly perceptibly turbid
(NTU=58).
* * * * *