U.S. patent application number 15/465718 was filed with the patent office on 2018-09-27 for golf balls having an inner core made of latex rubber foam.
This patent application is currently assigned to Acushnet Company. The applicant listed for this patent is Acushnet Company. Invention is credited to Mark L. Binette, Brian Comeau, Douglas S. Goguen, Michael Michalewich, Shawn Ricci, Michael J. Sullivan.
Application Number | 20180272195 15/465718 |
Document ID | / |
Family ID | 63581481 |
Filed Date | 2018-09-27 |
United States Patent
Application |
20180272195 |
Kind Code |
A1 |
Sullivan; Michael J. ; et
al. |
September 27, 2018 |
GOLF BALLS HAVING AN INNER CORE MADE OF LATEX RUBBER FOAM
Abstract
Golf balls having a multi-layered core made of a foamed
composition are provided. The core assembly preferably includes a
foam inner core (center) and surrounding outer core layer.
Preferably, a latex rubber foam composition is used to form the
inner core. The foam composition has relatively good resiliency and
rebounding action. In other instances, the latex rubber foam
composition can be used to make the outer core layer. The core
layers can have different hardness gradients and specific gravity
values. The ball further includes a cover that can be
multi-layered.
Inventors: |
Sullivan; Michael J.; (Old
Lyme, CT) ; Binette; Mark L.; (Mattapoisett, MA)
; Comeau; Brian; (Berkley, MA) ; Michalewich;
Michael; (Norton, MA) ; Ricci; Shawn; (New
Bedford, MA) ; Goguen; Douglas S.; (New Bedford,
MA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Acushnet Company |
Fairhaven |
MA |
US |
|
|
Assignee: |
Acushnet Company
Fairhaven
MA
|
Family ID: |
63581481 |
Appl. No.: |
15/465718 |
Filed: |
March 22, 2017 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
A63B 37/0092 20130101;
A63B 37/0044 20130101; A63B 37/0039 20130101; A63B 37/0091
20130101; A63B 37/0062 20130101; A63B 37/0047 20130101; A63B
37/0075 20130101; A63B 37/0045 20130101; A63B 37/0051 20130101;
A63B 37/0063 20130101; A63B 37/0064 20130101; A63B 37/0066
20130101 |
International
Class: |
A63B 37/00 20060101
A63B037/00 |
Claims
1. A golf ball, comprising a core assembly and a cover, the core
assembly comprising: i) an inner core comprising a latex rubber
foam composition having a geometric center and outer surface, the
inner core having a diameter in the range of about 0.100 to about
1.100 inches and an outer surface hardness (H.sub.inner core
surface) and a center hardness (H.sub.inner core center), the
H.sub.inner core surface being greater than the H.sub.inner core
center to provide a positive hardness gradient in the inner core;
and ii) an outer core layer comprising a non-foamed thermoset or
thermoplastic composition, the outer core layer being disposed
about the inner core layer and having a thickness in the range of
about 0.100 to about 0.750 inches, and having an outer surface
hardness (H.sub.outer surface of OC) and a midpoint hardness
(H.sub.midpoint of OC), the H.sub.outer surface of OC being greater
than the (H.sub.midpoint of OC), to provide a positive hardness
gradient in the outer core.
2. The golf ball of claim 1, wherein the outer core layer comprises
at least one thermoset rubber material selected from the group
consisting of polybutadiene, ethylene-propylene rubber,
ethylene-propylene-diene rubber, polyisoprene, styrene-butadiene
rubber, polyalkenamers, butyl rubber, halobutyl rubber, polystyrene
elastomers, copolymers of isobutylene and p-alkylstyrene,
halogenated copolymers of isobutylene and p-alkylstyrene,
copolymers of butadiene with acrylonitrile, polychloroprene, alkyl
acrylate rubber, chlorinated isoprene rubber, acrylonitrile
chlorinated isoprene rubber, and mixtures thereof
3. The golf ball of claim 2, wherein the outer core layer comprises
a thermoset polybutadiene rubber composition.
4. The golf ball of claim 1, wherein the outer core layer comprises
a thermoplastic polymer selected from the group consisting of
partially-neutralized ionomers; highly-neutralized ionomers;
polyesters; polyamides; polyamide-ethers, polyamide-esters;
polyurethanes, polyureas; fluoropolymers; polystyrenes;
polypropylenes; polyethylenes; polyvinyl chlorides; polyvinyl
acetates; polycarbonates; polyvinyl alcohols; polyester-ethers;
polyethers; polyimides, polyetherketones, polyamideimides; and
mixtures thereof.
5. The golf ball of claim 4, wherein the thermoplastic material is
an ionomer composition comprising an O/X-type copolymer, wherein O
is selected from the group consisting of ethylene and propylene,
and X is selected from the group consisting of methacrylic acid,
acrylic acid, ethacrylic acid, crotonic acid, maleic acid, fumaric
acid, and itaconic acid.
6. The golf ball of claim 5, wherein the O of the O/X-type acid
copolymer is ethylene and the X is methacrylic acid or acrylic
acid.
7. The golf ball of claim 1, wherein the H.sub.inner core center is
in the range of about 10 to about 55 Shore C and the H.sub.inner
core surface is in the range of about 15 to about 60 Shore C.
8. The golf ball of claim 1, wherein the H.sub.midpoint of OC is in
the range of about 45 to about 90 Shore C and the H.sub.outer
surface of OC is in the range of about 50 to about 98 Shore C.
9. The golf ball of claim 1, wherein the inner core has a specific
gravity (SG.sub.inner core) and the outer core has a specific
gravity (SG.sub.outer core), the SG.sub.inner core being greater
than the SG.sub.outer core.
10. The golf ball of claim 1, wherein the inner core has a specific
gravity (SG.sub.inner core) and the outer core has a specific
gravity (SG.sub.outer core), the SG.sub.outer core being greater
than the SG.sub.inner core.
11. The golf ball of claim 1, wherein the center hardness of the
inner core (H.sub.inner core center) is in the range of about 12
Shore C to about 62 Shore C and the outer surface hardness of the
outer core layer (H.sub.outer surface of OC) is in the range of
about 42 Shore C to about 92 Shore C to provide a positive hardness
gradient across the core assembly.
12. A golf ball, comprising a core assembly and a cover, the core
assembly comprising: i) an inner core comprising a latex rubber
foam composition having a geometric center and outer surface, the
inner core having a diameter in the range of about 0.100 to about
1.100 inches and an outer surface hardness (H.sub.inner core
surface) and a center hardness (H.sub.inner core center), the
H.sub.inner core surface being the same or less than the
H.sub.inner core center to provide a zero or negative hardness
gradient in the inner core; and ii) an outer core layer comprising
a non-foamed thermoset or thermoplastic composition, the outer core
layer being disposed about the inner core layer and having a
thickness in the range of about 0.100 to about 0.750 inches, and
having an outer surface hardness (H.sub.outer surface of OC) and a
midpoint hardness (H.sub.midpoint of OC), the H.sub.outer surface
of OC being greater than the (H.sub.midpoint of OC), to provide a
positive hardness gradient in the outer core.
Description
BACKGROUND OF THE INVENTION
Field of the Invention
[0001] The present invention relates generally to golf balls having
a multi-layered core assembly including an inner core and
surrounding outer core layer, wherein at least one of the core
layers is made from natural or synthetic latex rubber foam. In one
embodiment, the foamed inner core is made of latex rubber foam and
the outer core layer is made of a non-foam composition. In another
embodiment, the inner core is made of a non-foam composition such
as rubber or thermoplastic material and the outer core layer is
made of latex rubber foam. The ball further includes a cover having
at least one layer.
Brief Review of the Related Art
[0002] Both professional and amateur golfer use multi-piece, solid
golf balls today. Basically, a two-piece solid golf ball includes a
solid inner core protected by an outer cover. The inner core is
made of a natural or synthetic rubber such as polybutadiene,
styrene butadiene, or polyisoprene. The cover surrounds the inner
core and may be made of a variety of materials including, for
example, ethylene acid copolymer ionomers, polyamides, polyesters,
polyurethanes, and polyureas.
[0003] In recent years, three-piece, four-piece, and even
five-piece balls have become more popular. New manufacturing
technologies, lower material costs, and desirable performance
properties have contributed to these multi-piece balls becoming
more popular. Many golf balls used today have multi-layered cores
comprising an inner core and at least one surrounding outer core
layer. For example, the inner core may be made of a relatively soft
and resilient material, while the outer core may be made of a
harder and more rigid material. The "dual-core" sub-assembly is
encapsulated by a cover having at least one layer to provide a
final ball assembly. Different materials can be used to manufacture
the core and cover thus imparting desirable properties to the final
ball.
[0004] In general, dual-cores comprising an inner core (or center)
and a surrounding outer core layer are known in the industry. For
example, Sugimoto, U.S. Pat. No. 6,390,935 discloses a three-piece
golf ball comprising a core having a center and outer shell and a
cover disposed about the core. The specific gravity of the outer
shell is greater than the specific gravity of the center. The
center has a JIS-C hardness (X) at the center point thereof and a
JIS-C hardness (Y) at a surface thereof satisfying the equation:
(Y-X).gtoreq.8. The core structure (center and outer shell) has a
JIS-C hardness (Z) at a surface of 80 or greater. The cover has a
Shore D hardness of less than 60.
[0005] Endo, U.S. Pat. No. 6,520,872 discloses a three-piece golf
ball comprising a center, an intermediate layer formed over the
center, and a cover formed over the intermediate layer. The center
is preferably made of high-cis polybutadiene rubber; and the
intermediate and cover layers are preferably made of an ionomer
resin such as an ethylene acid copolymer.
[0006] Watanabe, U.S. Pat. No. 7,160,208 discloses a three-piece
golf ball comprising a rubber-based inner core; a rubber-based
outer core layer; and a polyurethane elastomer-based cover. The
inner core layer has a JIS-C hardness of 50 to 85; the outer core
layer has a JIS-C hardness of 70 to 90; and the cover has a Shore D
hardness of 46 to 55. Also, the inner core has a specific gravity
of more than 1.0, and the core outer layer has a specific gravity
equal to or greater than that of that of the inner core.
[0007] The core sub-structure located inside of the golf ball acts
as an engine or spring for the ball. Thus, the composition and
construction of the core is a key factor in determining the
resiliency and rebounding performance of the ball. In general, the
rebounding performance of the ball is determined by calculating its
initial velocity after being struck by the face of the golf club
and its outgoing velocity after making impact with a hard surface.
More particularly, the "Coefficient of Restitution" or "COR" of a
golf ball refers to the ratio of a ball's rebound velocity to its
initial incoming velocity when the ball is fired out of an air
cannon into a rigid vertical plate. The COR for a golf ball is
written as a decimal value between zero and one. A golf ball may
have different COR values at different initial velocities. The
United States Golf Association (USGA) sets limits on the initial
velocity of the ball so one objective of golf ball manufacturers is
to maximize COR under such conditions. Balls with a higher rebound
velocity have a higher COR value. Such golf balls rebound faster,
retain more total energy when struck with a club, and have longer
flight distance versus balls with low COR values. These properties
are particularly important for long distance shots. For example,
balls having high resiliency and COR values tend to travel a
relatively far distance when struck by a driver club from a
tee.
[0008] The durability, spin rate, and feel of the ball also are
important properties. In general, the durability of the ball refers
to the impact-resistance of the ball. Balls having low durability
appear worn and damaged even when such balls are used only for
brief time periods. In some instances, the cover may be cracked or
torn. The spin rate refers to the ball's rate of rotation after it
is hit by a club. Balls having a relatively high spin rate are
advantageous for short distance shots made with irons and wedges.
Professional and highly skilled amateur golfers can place a back
spin more easily on such balls. This helps a player better control
the ball and improves shot accuracy and placement. By placing the
right amount of spin on the ball, the player can get the ball to
stop precisely on the green or place a fade on the ball during
approach shots. On the other hand, recreational players who cannot
intentionally control the spin of the ball when hitting it with a
club are less likely to use high spin balls. For such players, the
ball can spin sideways more easily and drift far-off the course,
especially if the ball is hooked or sliced. Meanwhile, the "feel"
of the ball generally refers to the sensation that a player
experiences when striking the ball with the club and it is a
difficult property to quantify. Most players prefer balls having a
soft feel, because the player experience a more natural and
comfortable sensation when their club face makes contact with these
balls. Balls having a softer feel are particularly desirable when
making short shots around the green, because the player senses more
with such balls. The feel of the ball primarily depends upon the
hardness and compression of the ball.
[0009] Manufacturers of golf balls are constantly looking to
different materials for improving the playing performance and other
properties of the ball. For example, golf balls containing cores
made from foam compositions are generally known in the industry.
Puckett and Cadorniga, U.S. Pat. Nos. 4,836,552 and 4,839,116
disclose one-piece, short distance golf balls made of a foam
composition comprising a thermoplastic polymer (ethylene acid
copolymer ionomer such as Surlyn.RTM.) and filler material
(microscopic glass bubbles). The density of the composition
increases from the center to the surface of the ball. Thus, the
ball has relatively dense outer skin and a cellular inner core.
According to the '552 and '116 patents, by providing a short
distance golf ball, which will play approximately 50% of the
distance of a conventional golf ball, the land requirements for a
golf course can be reduced 67% to 50%.
[0010] Gentiluomo, U.S. Pat. No. 5,104,126 discloses a three-piece
golf ball (FIG. 2) containing a high density center (3) made of
steel, surrounded by an outer core (4) of low density resilient
syntactic foam composition, and encapsulated by an ethylene acid
copolymer ionomer (Surlyn.RTM.) cover (5). The '126 patent defines
the syntactic foam as being a low density composition consisting of
granulated cork or hollow spheres of either phenolic, epoxy,
ceramic or glass, dispersed within a resilient elastomer.
[0011] Aoyama, U.S. Pat. Nos. 5,688,192 and 5,823,889 disclose a
golf ball containing a core, wherein the core comprising an inner
and outer portion, and a cover made of a material such as balata
rubber or ethylene acid copolymer ionomer. The core is made by
foaming, injecting a compressible material, gasses, blowing agents,
or gas-containing microspheres into polybutadiene or other core
material. According to the '889 patent, polyurethane compositions
may be used. The compressible material, for example, gas-containing
compressible cells may be dispersed in a limited part of the core
so that the portion containing the compressible material has a
specific gravity of greater than 1.00. Alternatively, the
compressible material may be dispersed throughout the entire core.
In one embodiment, the core comprises an inner and outer portion.
In another embodiment, the core comprises inner and outer
layers.
[0012] Sullivan and Ladd, U.S. Pat. No. 6,688,991 discloses a golf
ball containing a low specific gravity core, optional intermediate
layer, and high specific gravity cover with Shore D hardness in the
range of about 40 to about 80. The core is preferably made from a
highly neutralized thermoplastic polymer such as ethylene acid
copolymer which has been foamed.
[0013] Nesbitt, U.S. Pat. No. 6,767,294 discloses a golf ball
comprising: i) a pressurized foamed inner center formed from a
thermoset material, a thermoplastic material, or combinations
thereof, a blowing agent and a cross-linking agent and, ii) an
outer core layer formed from a second thermoset material, a
thermoplastic material, or combinations thereof. Additionally, a
barrier resin or film can be applied over the outer core layer to
reduce the diffusion of the internal gas and pressure from the
nucleus (center and outer core layer). Preferred polymers for the
barrier layer have low permeability such as Saran.RTM. film (poly
(vinylidene chloride), Barex.RTM. resin (acyrlonitrile-co-methyl
acrylate), poly (vinyl alcohol), and PET film (polyethylene
terephthalate). The '294 patent does not disclose core layers
having different hardness gradients.
[0014] Sullivan, Ladd, and Hebert, U.S. Pat. No. 7,708,654
discloses a golf ball having a foamed intermediate layer. Referring
to FIG. 1 in the '654 patent, the golf ball includes a core (12),
an intermediate layer (14) made of a highly neutralized polymer
having a reduced specific gravity (less than 0.95), and a cover
(16). According to the '654 patent, the intermediate layer can be
an outer core, a mantle layer, or an inner cover. The reduction in
specific gravity of the intermediate layer is caused by foaming the
composition of the layer and this reduction can be as high as 30%.
The '654 patent discloses that other foamed compositions such as
foamed polyurethanes and polyureas may be used to form the
intermediate layer.
[0015] Tutmark, U.S. Pat. No. 8,272,971 is directed to golf balls
containing an element that reduces the distance of the ball's
flight path. In one embodiment, the ball includes a core and cover.
A cavity is formed between core and cover and this may be filled by
a foamed polyurethane "middle layer" in order to dampen the ball's
flight properties. The foam of the middle layer is relatively light
in weight; and the core is relatively heavy and dense. According to
the '971 patent, when a golfer strikes the ball with a club, the
foam in the middle layer actuates and compresses, thereby absorbing
much of the impact from the impact of the ball.
[0016] Although some foam core constructions for golf balls have
been considered over the years, there are drawbacks with using some
foam materials. For example, one disadvantage with some golf balls
having a foam core is the ball tends to have low resiliency
(rebounding performance). That is, the velocity of the ball tends
to be low after being hit by a club and the ball generally travels
short distances. There is a need for new balls having a foam core
with improved resiliency that will allow players to generate higher
initial ball speed. This will allow players to make longer distance
shots. The present invention provides new foam core constructions
having improved resiliency and other advantageous properties; and
new methods for making such cores. The invention also encompasses
new golf balls containing the improved core constructions.
SUMMARY OF THE INVENTION
[0017] The present invention provides a golf ball comprising a core
assembly and cover. In one embodiment, the golf ball contains an
inner core layer comprising a natural or synthetic latex rubber
foam composition. The inner core generally has a diameter in the
range of about 0.100 to about 1.100 inches, and preferably about
0.100 to about 0.900 inches. The inner core has an outer surface
hardness (H.sub.inner core surface) and center hardness
(H.sub.inner core center), the H.sub.inner core surface being
greater than the H.sub.inner core center to provide a positive
hardness gradient in the inner core. The outer core layer is
preferably made of a non-foam thermoset or thermoplastic
composition. The outer core layer is disposed about the inner core
layer and has a thickness in the range of about 0.100 to about
0.750 inches and has an outer surface hardness (H.sub.outer surface
of OC) and midpoint hardness (H.sub.midpoint of OC), the
H.sub.outer surface of OC being greater than the (H.sub.midpoint of
OC), to provide a positive hardness gradient.
[0018] For example, the H.sub.inner core center can be in the range
of about 10 to about 55 Shore C and the H.sub.inner core surface
can be in the range of about 15 to about 60 Shore C. Also, the
H.sub.midpoint of OC can be in the range of about 45 to about 90
Shore C and the H.sub.outer surface of OC can be in the range of
about 50 to about 98 Shore C. The inner core has a specific gravity
(SG.sub.inner core) and the outer core has a specific gravity
(SG.sub.outer core). In one example, the SG.sub.inner core is
greater than the SG.sub.outer core. In another example, the
SG.sub.outer core is greater than the SG.sub.inner core.
[0019] In another embodiment, the H.sub.inner core surface is the
same or less than the H.sub.inner core center to provide a zero or
negative hardness gradient in the inner core. In yet another
embodiment, the foamed inner core is made of a non-foam composition
such as thermoset rubber or thermoplastic material and the outer
core layer is made of the latex rubber foam.
BRIEF DESCRIPTION OF THE DRAWINGS
[0020] The novel features that are characteristic of the present
invention are set forth in the appended claims. However, the
preferred embodiments of the invention, together with further
objects and attendant advantages, are best understood by reference
to the following detailed description in connection with the
accompanying drawings in which:
[0021] FIG. 1 is a is a cross-sectional view of a spherical inner
core showing a foamed geometric center, outer region, and outer
surface skin made in accordance with the present invention;
[0022] FIG. 2 is a perspective view of one embodiment of upper and
lower mold cavities used to make the inner core in accordance with
the present invention;
[0023] FIG. 3 is a cross-sectional view of a three-piece golf ball
comprising an inner core, outer core, and cover layer made in
accordance with the present invention;
[0024] FIG. 4 is a cross-sectional view of a four-piece golf ball
comprising an inner core, outer core, inner cover layer, and outer
cover layer made in accordance with the present invention; and
[0025] FIG. 5 is a perspective view of a finished golf ball made in
accordance with the present invention.
DETAILED DESCRIPTION OF THE INVENTION
[0026] Golf Ball Constructions
[0027] Golf balls having various constructions may be made in
accordance with this invention. For example, golf balls having
two-piece, three-piece, four-piece, and five-piece constructions
with single or multi-layered cover materials may be made.
Representative illustrations of such golf ball constructions are
provided and discussed further below. The term, "layer" as used
herein means generally any spherical portion of the golf ball. More
particularly, in one version, a three-piece golf ball containing a
dual-layered core and single-layered cover is made. The dual-core
includes an inner core (center) and surrounding outer core layer.
In another version, a four-piece golf ball containing a dual-core
and dual-cover (inner cover and outer cover layers) is made. In yet
another construction, a four-piece or five-piece golf ball
containing a dual-core; casing layer(s); and cover layer(s) may be
made. As used herein, the term, "casing layer" means a layer of the
ball disposed between the multi-layered core assembly and cover.
The casing layer also may be referred to as a mantle or
intermediate layer. The diameter and thickness of the different
layers along with properties such as hardness and compression may
vary depending upon the construction and desired playing
performance properties of the golf ball.
[0028] Inner Core
[0029] Preferably, the golf balls of this invention contain a core
structure comprising an inner core (center) and encapsulating outer
core layer. In the present invention, a foam composition is
preferably used to make the inner core. This molding process is
described in further detail below. Referring to FIG. 1, an inner
core (4) is made from a foamed composition that includes a
geometric center (6) and surrounding outer region (7) and outer
surface (8). The center (6) is a foamed region and the outer
surface (8) is generally a relatively thin and dense non-foamed
surface. The geometric center (6) and surrounding outer region (7)
are generally fully-foamed. The outer surface (8) of the inner core
is generally a non-foamed, and relatively thin and dense layer.
This surface may be referred to as the "skin" of the foamed
composition. In one embodiment, the thickness of the outer skin (8)
is in the range of about 0.001 inches (1 mil) to about 0.500 inches
(500 mils) and preferably in the range of about 0.100 to about
0.300 inches. More preferably, the thickness of the outer skin (8)
is preferably less than about 0.250 inches and even more preferably
less than 0.150 inches.
[0030] In general, foam compositions are made by forming gas
bubbles in a polymer mixture using a foaming (blowing) agent. As
the bubbles form, the mixture expands and forms a foam composition
having either an open or closed cellular structure. Flexible foams
generally have an open cell structure, where the cells walls are
incomplete and contain small holes through which liquid and air can
permeate. Rigid foams generally have a closed cell structure, where
the cell walls are continuous and complete. Many foams contain both
open and closed cells. It also is possible to formulate flexible
foams having a closed cell structure and likewise to formulate
rigid foams having an open cell structure.
[0031] For example, polyurethane foams can be made by forming gas
bubbles in a polymer mixture using a foaming (blowing) agent. As
the bubbles form, the mixture expands and forms a foam. The foaming
(blowing) agents used to form the foam are typically are in the
form of powder, pellets, or liquids and they are added to the
composition, where they decompose or react during heating and
generate gaseous by-products (for example, nitrogen or carbon
dioxide). The gas is dispersed and trapped throughout the
composition and foams it. For example, water may be used as the
foaming agent. Air bubbles are introduced into the mixture of the
isocyanate and polyol compounds and water by high-speed mixing
equipment. The isocyanates react with the water to generate carbon
dioxide which fills and expands the cells created during the mixing
process.
[0032] Latex Rubber Foam
[0033] In one embodiment of this invention, a rubber latex foam
composition is used to form the foamed inner core. Any suitable
natural or synthetic rubber can be used to form the rubber latex
foam composition. These rubbers include, for example, natural
rubbers obtained from plants, particularly rubber trees; and
synthetic rubbers such as polybutadiene, polyisoprene, ethylene
propylene rubber ("EPR"), ethylene-propylene-diene ("EPDM") rubber,
styrene-butadiene rubber, styrenic block copolymer rubbers (such as
"SI", "SIS", "SB", "SBS", "SIBS", and the like, where "S" is
styrene, "I" is isobutylene, and "B" is butadiene), polyalkenamers
such as, for example, polyoctenamer, butyl rubber, halobutyl
rubber, polystyrene elastomers, polyethylene elastomers,
polyurethane elastomers, polyurea elastomers, metallocene-catalyzed
elastomers and plastomers, copolymers of isobutylene and
p-alkylstyrene, halogenated copolymers of isobutylene and
p-alkylstyrene, copolymers of butadiene with acrylonitrile,
polychloroprene, alkyl acrylate rubber, chlorinated isoprene
rubber, acrylonitrile chlorinated isoprene rubber, and blends of
two or more thereof.
[0034] In general methods for making rubber latex foams are known
in the art and include the Dunlop method and Talalay method. In
general, the Dunlop method involves pouring the liquid rubber latex
formulation onto a conveyor belt. The liquid latex is slowly heated
so that it gels into a permanent solid form. Then, the cooled solid
latex is removed from the conveyor belt. The latex can be molded
into a sphere or other desired shape so that it can be used as an
inner core or other component in the golf ball in accordance with
this invention.
[0035] Particularly, in the Dunlop method, the foam can be produced
by introducing air into the compounded latex formulation. Batch or
continuous foaming methods can be used. As discussed above, natural
and synthetic rubbers can be used to prepare the compounded latex.
Other ingredients include, for example, potassium oleate soap
solution, which acts as a frothing agent. This soap has a fast and
controllable frothing rate. In general, if the amount of frothing
agent in the composition is increased, this allows for more air to
be whipped into the compounded latex and this decreases the density
of the foam. Sulfur compounds also can be included for curing.
Suitable curing processes include, for example, peroxide-curing,
sulfur-curing, high-energy radiation, and combinations thereof.
Zinc oxide, which acts as a catalyst, also can be included. Other
additives for the composition include accelerators, dyes and
pigments, sufactants, and antioxidants. Sodium silicofluoride can
be used as the gelling agent.
[0036] In the foaming process, the soap film in the rubber
composition breaks-up as the soap is deactivated. The rubber
particles coalesce and form a continuous rubber phase in the
aqueous phase. Then, the air bubbles break-up and form an
interconnecting cellular structure in the coagulated foam.
[0037] In an alternative process (for example, the Talalay method),
a mold having lower and upper mold cavities is used to form the
spherical core. When the lower and upper mold cavities are joined
together, they define an interior spherical cavity that houses the
spherical core. The mold cavity is filled with the latex compound
and the upper and lower mold cavities are mated together. A vacuum
is applied. The expanded foam is rapidly frozen. For example, a
glycol-water mixture at a temperature of -34.degree. C. can be
circulated through channels in the mold to freeze the foam. Then,
carbon dioxide can be introduced into the mold cavity and this
breaks the vacuum. At the same time, the carbon dioxide permeates
the foam and the latex is coagulated. The latex foam is then
flash-heated to gel into a permanent solid form. For example, a
glycol-water mixture having a temperature in the range of 21 to
27.degree. C. can be circulated through channels in the mold. The
foam is cured by passing hot glycol-water mix (110.degree. C.)
through the channels. After curing, a glycol-water mixture
(23.degree. C.) is passed through the mold to cool the foam. The
mold is opened and the foam is removed.
[0038] One advantage of golf balls having a foam core made of the
latex rubber foam composition of this invention is the ball tends
to have higher resiliency (rebounding performance) than balls
containing cores made of other foam compositions. That is, the
velocity of the ball tends to be higher after being hit by a club
and the ball generally travels longer distances. These foam core
constructions tend to have improved resiliency and durability and
other advantageous properties.
[0039] The rubber latex foam may be cured using any suitable curing
process, for example, peroxide-curing, sulfur-curing, high-energy
radiation, and combinations thereof. In one version, the rubber
composition is peroxide-cured. Suitable organic peroxides include,
but are not limited to, dicumyl peroxide;
n-butyl-4,4-di(t-butylperoxy) valerate;
1,1-di(t-butylperoxy)3,3,5-trimethylcyclohexane;
2,5-dimethyl-2,5-di(t-butylperoxy) hexane; di-t-butyl peroxide;
di-t-amyl peroxide; t-butyl peroxide; t-butyl cumyl peroxide;
2,5-dimethyl-2,5-di(t-butylperoxy)hexyne-3;
di(2-t-butyl-peroxyisopropyl)benzene; dilauroyl peroxide; dibenzoyl
peroxide; t-butyl hydroperoxide; and combinations thereof. In a
particular embodiment, the free radical initiator is dicumyl
peroxide, including, but not limited to Perkadox.RTM. BC,
commercially available from Akzo Nobel. Peroxide free-radical
initiators are generally present in the rubber composition in an
amount of at least 0.05 parts by weight per 100 parts of the total
rubber, or an amount within the range having a lower limit of 0.05
parts or 0.1 parts or 1 part or 1.25 parts or 1.5 parts or 2.5
parts or 5 parts by weight per 100 parts of the total rubbers, and
an upper limit of 2.5 parts or 3 parts or 5 parts or 6 parts or 10
parts or 15 parts by weight per 100 parts of the total rubber.
Concentrations are in parts per hundred (phr) unless otherwise
indicated. As used herein, the term, "parts per hundred," also
known as "phr" or "pph" is defined as the number of parts by weight
of a particular component present in a mixture, relative to 100
parts by weight of the polymer component. Mathematically, this can
be expressed as the weight of an ingredient divided by the total
weight of the polymer, multiplied by a factor of 100.
[0040] The rubber compositions may further include a reactive
cross-linking co-agent. Suitable co-agents include, but are not
limited to, metal salts of unsaturated carboxylic acids having from
3 to 8 carbon atoms; unsaturated vinyl compounds and polyfunctional
monomers (e.g., trimethylolpropane trimethacrylate); phenylene
bismaleimide; and combinations thereof. Particular examples of
suitable metal salts include, but are not limited to, one or more
metal salts of acrylates, diacrylates, methacrylates, and
dimethacrylates, wherein the metal is selected from magnesium,
calcium, zinc, aluminum, lithium, and nickel. In a particular
embodiment, the co-agent is selected from zinc salts of acrylates,
diacrylates, methacrylates, and dimethacrylates. In another
particular embodiment, the agent is zinc diacrylate (ZDA). When the
co-agent is zinc diacrylate and/or zinc dimethacrylate, the
co-agent is typically included in the rubber composition in an
amount within the range having a lower limit of 1 or 5 or 10 or 15
or 19 or 20 parts by weight per 100 parts of the total rubber, and
an upper limit of 24 or 25 or 30 or 35 or 40 or 45 or 50 or 60
parts by weight per 100 parts of the base rubber.
[0041] Radical scavengers such as a halogenated organosulfur,
organic disulfide, or inorganic disulfide compounds may be added to
the rubber composition. These compounds also may function as "soft
and fast agents." As used herein, "soft and fast agent" means any
compound or a blend thereof that is capable of making a core: 1)
softer (having a lower compression) at a constant "coefficient of
restitution" (COR); and/or 2) faster (having a higher COR at equal
compression), when compared to a core equivalently prepared without
a soft and fast agent. Preferred halogenated organosulfur compounds
include, but are not limited to, pentachlorothiophenol (PCTP) and
salts of PCTP such as zinc pentachlorothiophenol (ZnPCTP). Using
PCTP and ZnPCTP in golf ball inner cores helps produce softer and
faster inner cores. The PCTP and ZnPCTP compounds help increase the
resiliency and the coefficient of restitution of the core. In a
particular embodiment, the soft and fast agent is selected from
ZnPCTP, PCTP, ditolyl disulfide, diphenyl disulfide, dixylyl
disulfide, 2-nitroresorcinol, and combinations thereof.
[0042] The rubber composition also may include filler(s) such as
materials selected from carbon black, clay and nanoclay particles
as discussed above, talc (e.g., Luzenac HAR.RTM. high aspect ratio
talcs, commercially available from Luzenac America, Inc.), glass
(e.g., glass flake, milled glass, and microglass), mica and
mica-based pigments (e.g., Iriodin.RTM. pearl luster pigments,
commercially available from The Merck Group), and combinations
thereof. Metal fillers such as, for example, particulate; powders;
flakes; and fibers of copper, steel, brass, tungsten, titanium,
aluminum, magnesium, molybdenum, cobalt, nickel, iron, lead, tin,
zinc, barium, bismuth, bronze, silver, gold, and platinum, and
alloys and combinations thereof also may be added to the rubber
composition to adjust the specific gravity of the composition as
needed. As discussed further below, in one preferred embodiment,
the specific gravity of the inner core layer (for example, foamed
polyurethane) has a specific gravity less than the outer core layer
(for example, polybutadiene rubber). In such an event, if mineral,
metal, or other fillers are added to the polybutadiene rubber
composition used to form the outer core, it is important the
concentration of such fillers be sufficient so that the specific
gravity of the outer core layer is greater than the specific
gravity of the inner core. For example, the concentration of the
fillers may be in an amount of at least about 5% by weight based on
total weight of composition
[0043] In addition, the rubber compositions may include
antioxidants. Also, processing aids such as high molecular weight
organic acids and salts thereof may be added to the composition.
Suitable organic acids are aliphatic organic acids, aromatic
organic acids, saturated mono-functional organic acids, unsaturated
monofunctional organic acids, multi-unsaturated mono-functional
organic acids, and dimerized derivatives thereof. Particular
examples of suitable organic acids include, but are not limited to,
caproic acid, caprylic acid, capric acid, lauric acid, stearic
acid, behenic acid, erucic acid, oleic acid, linoleic acid,
myristic acid, benzoic acid, palmitic acid, phenylacetic acid,
naphthalenoic acid, and dimerized derivatives thereof. The organic
acids are aliphatic, mono-functional (saturated, unsaturated, or
multi-unsaturated) organic acids. Salts of these organic acids may
also be employed. The salts of organic acids include the salts of
barium, lithium, sodium, zinc, bismuth, chromium, cobalt, copper,
potassium, strontium, titanium, tungsten, magnesium, cesium, iron,
nickel, silver, aluminum, tin, or calcium, salts of fatty acids,
particularly stearic, behenic, erucic, oleic, linoelic or dimerized
derivatives thereof. It is preferred that the organic acids and
salts of the present invention be relatively non-migratory (they do
not bloom to the surface of the polymer under ambient temperatures)
and non-volatile (they do not volatilize at temperatures required
for melt-blending.) Other ingredients such as accelerators (for
example, tetra methylthiuram), processing aids, dyes and pigments,
wetting agents, surfactants, plasticizers, coloring agents,
fluorescent agents, chemical blowing and foaming agents, defoaming
agents, stabilizers, softening agents, impact modifiers,
antiozonants, as well as other additives known in the art may be
added to the rubber composition.
[0044] In the process of this invention, the materials used to
prepare the foam are charged to the mold for producing the inner
core. The mold may be equipped with steam nozzles so that steam can
be injected into the mold cavity. The temperature inside of the
mold can vary, for example, the temperature can range from about
80.degree. C. to about 1800.degree. C. Steam, hot air, hot water,
or radiant heat may be used to foam the composition. The
composition expands as it is heated. The temperature must be chosen
carefully and must be sufficiently high so that it activates the
blowing agents and foams the mixture. In general, the temperature
should be in the range of about room temperature (RT) to about
180.degree. F. and preferably in the range of about room
temperature (RT) to about 150.degree. F. so that it activates the
blowing agents. Once the polymer materials, blowing agent, and any
optional ingredients (for example, fillers) are charged to the mold
and treated with sufficient heat and pressure, the blowing agents
are activated. This causes the polymer mixture to foam and form the
foam composition in the mold.
[0045] Referring to FIG. 2, one version of a mold for preparing the
foamed inner core is shown. The mold includes lower and upper mold
cavities (9, 10) that are placed in lower and upper mold frame
plates (11, 12). The frame plates (11, 12) contain guide pins and
complementary alignment holes (not shown in drawing). The guide
pins are inserted into the alignment holes to secure the lower
plate (11) to the upper plate (12). The lower and upper mold
cavities (9, 10) are mated together as the frame plates (11, 12)
are fastened. When the lower and upper mold cavities (9, 10) are
joined together, they define an interior spherical cavity that
houses the spherical core. The upper mold contains a vent or hole
(14) to allow for the expanding foam to fill the cavities
uniformly. A secondary overflow chamber (16), which is located
above the vent (14), can be used to adjust the amount of foam
overflow and thus adjust the density of the core structure being
molded in the cavities. As the lower and upper mold cavities (9,
10) are mated together and sufficient heat and pressure is applied,
the reactants of the foam composition react, cure, and solidify to
form a relatively rigid or flexible and lightweight spherical foam
core. The resulting cores are cooled and then removed from the
mold.
[0046] Foam Polymers.
[0047] As discussed above, latex rubber foam is preferably prepared
in accordance with this invention. It is recognized, however, that
a wide variety of thermoplastic and thermoset materials may be used
in forming the foam compositions of this invention including, for
example, polyurethanes; polyureas; copolymers, blends and hybrids
of polyurethane and polyurea; olefin-based copolymer ionomer resins
(for example, Surlyn.RTM. ionomer resins and DuPont HPF.RTM. 1000
and HPF.RTM. 2000, commercially available from DuPont; Iotek.RTM.
ionomers, commercially available from ExxonMobil Chemical Company;
Amplify.RTM. 10 ionomers of ethylene acrylic acid copolymers,
commercially available from Dow Chemical Company; and Clarix.RTM.
ionomer resins, commercially available from A. Schulman Inc.);
polyethylene, including, for example, low density polyethylene,
linear low density polyethylene, and high density polyethylene;
polypropylene; rubber-toughened olefin polymers; acid copolymers,
for example, poly(meth)acrylic acid, which do not become part of an
ionomeric copolymer; plastomers; flexomers;
styrene/butadiene/styrene block copolymers;
styrene/ethylene-butylene/styrene block copolymers; dynamically
vulcanized elastomers; copolymers of ethylene and vinyl acetates;
copolymers of ethylene and methyl acrylates; polyvinyl chloride
resins; polyamides, poly(amide-ester) elastomers, and graft
copolymers of ionomer and polyamide including, for example,
Pebax.RTM. thermoplastic polyether block amides, commercially
available from Arkema Inc; cross-linked trans-polyisoprene and
blends thereof; polyester-based thermoplastic elastomers, such as
Hytrel.RTM., commercially available from DuPont or RiteFlex.RTM.,
commercially available from Ticona Engineering Polymers;
polyurethane-based thermoplastic elastomers, such as
Elastollan.RTM., commercially available from BASF; synthetic or
natural vulcanized rubber; and combinations thereof.
[0048] Foaming Agents.
[0049] The foaming agent may be any foaming agent compatible with
the other components of the polymer composition such as, for
example, chemical blowing agents, physical blowing agents, and the
like. The chemical foaming agents may be inorganic, such as
ammonium carbonate and carbonates of alkalai metals, or may be
organic, such as azo and diazo compounds, such as nitrogen-based
azo compounds. Suitable azo compounds include, but are not limited
to, 2,2'-azobis(2-cyanobutane), 2,2'-azobis(methylbutyronitrile),
and azodicarbonamide. Other compounds include, for example,
p,p'-oxybis(benzene sulfonyl hydrazide), p-toluene sulfonyl
semicarbazide, and p-toluene sulfonyl hydrazide. Other suitable
blowing agents that may be added to the formulation that will be
foamed in accordance with this invention include, for example,
expandable gas-containing microspheres. Such expandable
microspheres are commercially available as Expancel.RTM. from
Expancel of Sweden or Akzo Nobel.
[0050] Fillers.
[0051] The foam composition may contain fillers such as, for
example, mineral filler particulate. Suitable mineral filler
particulates include compounds such as zinc oxide, limestone,
silica, mica, barytes, lithopone, zinc sulfide, talc, calcium
carbonate, magnesium carbonate, clays, powdered metals and alloys
such as bismuth, brass, bronze, cobalt, copper, iron, nickel,
tungsten, aluminum, tin, precipitated hydrated silica, fumed
silica, mica, calcium metasilicate, barium sulfate, zinc sulfide,
lithopone, silicates, silicon carbide, diatomaceous earth,
carbonates such as calcium or magnesium or barium carbonate,
sulfates such as calcium or magnesium or barium sulfate. Adding
fillers to the composition provides many benefits including helping
improve the stiffness and strength of the composition. The mineral
fillers tend to help decrease the size of the foam cells and
increase cell density. The mineral fillers also tend to help
improve the physical properties of the foam such as hardness,
compression set, and tensile strength.
[0052] More particularly, clay particulate fillers, such as
Garamite.RTM. mixed mineral thixotropes and Cloisite.RTM. and
Nanofil.RTM. nanoclays, commercially available from Southern Clay
Products, Inc., and Nanomax.RTM. and Nanomer.RTM. nanoclays,
commercially available from Nanocor, Inc may be used. Other
nano-scale materials such as nanotubes and nanoflakes also may be
used. Also, talc particulate (e.g., Luzenac HAR.RTM. high aspect
ratio talcs, commercially available from Luzenac America, Inc.),
glass (e.g., glass flake, milled glass, and microglass), and
combinations thereof may be used. Metal oxide fillers have good
heat-stability and include, for example, aluminum oxide, zinc
oxide, tin oxide, barium sulfate, zinc sulfate, calcium oxide,
calcium carbonate, zinc carbonate, barium carbonate, tungsten,
tungsten carbide, and lead silicate fillers. These metal oxides and
other metal fillers such as, for example, particulate; powders;
flakes; and fibers of copper, steel, brass, tungsten, titanium,
aluminum, magnesium, molybdenum, cobalt, nickel, iron, lead, tin,
zinc, barium, bismuth, bronze, silver, gold, and platinum, and
alloys and combinations thereof may be added to the foam
composition.
[0053] As discussed further below, in one preferred embodiment, the
specific gravity (or density) of the foamed inner core is less than
the specific gravity of the outer core. In this embodiment, if an
excess amount of mineral filler or other additives are included in
the foam composition, they should not be added in an amount that
would increase the specific gravity of the foam inner core to a
level such that it would be greater than the specific gravity of
the outer core layer. If the ball's mass is concentrated towards
the outer surface (for example, outer core layers), and the outer
core layer has a higher specific gravity than the inner core, the
ball has a relatively high Moment of Inertia (MOI). In such balls,
most of the mass is located away from the ball's axis of rotation
and thus more force is needed to generate spin. These balls have a
generally low spin rate as the ball leaves the club's face after
contact between the ball and club. Such core structures (wherein
the specific gravity of the outer core is greater than the specific
gravity of the inner core) are preferred in the present invention.
Thus, in one preferred embodiment, the concentration of mineral
filler particulate in the foam composition is in the range of about
0.1 to about 9.0% by weight.
[0054] Hardness of the Inner Core
[0055] As shown in FIG. 1, a foamed inner core (4) having a foamed
geometric center (6) and non-foamed outer skin (8) may be prepared
per the methods discussed above.
[0056] The resulting inner core preferably has a diameter within a
range of about 0.100 to about 1.100 inches. For example, the inner
core may have a diameter within a range of about 0.250 to about
1.000 inches. In another example, the inner core may have a
diameter within a range of about 0.300 to about 0.800 inches. More
particularly, the inner core preferably has a diameter size with a
lower limit of about 0.10 or 0.12 or 0.15 or 0.17 or 0.25 or 0.30
or 0.35 or 0.38 or 0.45 or 0.50 or 0.52 or 0.55 inches and an upper
limit of about 0.60 or 0.63 or 0.65 or 0.70 or 0.74 or 0.80 or 0.86
or 0.90 or 0.95 or 1.00 or 1.02 or 1.10 inches. The outer skin (8)
of the inner core is relatively thin preferably having a thickness
of less than about 0.020 inches and more preferably less than 0.010
inches. In one preferred embodiment, the foamed core has a
"positive" hardness gradient (that is, the outer skin of the inner
core is harder than its geometric center.) In another embodiment,
the foamed core has a "zero" or "negative" hardness gradient (that
is, the outer skin of the inner core has the same or lower hardness
than its geometric center.)
[0057] For example, the geometric center hardness of the inner core
(H.sub.inner core center), as measured in Shore C units, may be
about 10 Shore C or greater and preferably has a lower limit of
about 10 or 13 or 16 or 20 or 25 or 30 or 32 or 34 or 36 or 40
Shore C and an upper limit of about 42 or 44 or 48 or 50 or 52 or
56 or 60 or 62 or 65 or 68 or 70 or 74 or 78 or 80 or 84 or 90
Shore C. In one preferred version, the geometric center hardness of
the inner core (H.sub.inner core center) is about 40 Shore C.
[0058] When a flexible, relatively soft foam is used, the
(H.sub.inner core center) of the foam may have a Shore A hardness
of about 10 or greater, and preferably has a lower limit of 15, 18,
20, 25, 28, 30, 35, 38, or 40 Shore A hardness and an upper limit
of about 45 or 48, or 50, 54, 58, 60, 65, 70, 80, 85, or 90 Shore A
hardness. In one preferred embodiment, the (H.sub.inner core
center) of the foam is about 55 Shore A.
[0059] The H.sub.inner core center, as measured in Shore D units,
is about 15 Shore D or greater and more preferably within a range
having a lower limit of about 15 or 18 or 20 or 22 or 25 or 28 or
30 or 32 or 36 or 40 or 44 Shore D and an upper limit of about 45
or 48 or 50 or 52 or 55 or 58 or 60 or 62 or 64 or 66 or 70 or 72
or 74 or 78 or 80 or 82 or 84 or 88 or 90 Shore D.
[0060] Meanwhile, the outer surface hardness of the inner core
(H.sub.inner core surface), as measured in Shore C, is preferably
about 20 Shore C or greater and may have, for example, a lower
limit of about 10 or 14 or 17 or 20 or 22 or 24 or 28 or 30 or 32
or 35 or 36 or 40 or 42 or 44 or 48 or 50 Shore C and an upper
limit of about 52 or 55 or 58 or 60 or 62 or 64 or 66 or 70 or 74
or 78 or 80 or 86 or 88 or 90 or 92 or 95 Shore C. When a flexible,
relatively soft foam is used, the (H.sub.inner core surface) of the
foam may have a Shore A hardness of about 12 or greater, and
preferably has a lower limit of 12, 16, 20, 24, 26, 28, 30, 34, 40,
42, 46, or 50 Shore A hardness and an upper limit of about 52, 55,
58, 60, 62, 66, 70, 74, 78, 80, 84, 88, 90, or 95 Shore A hardness.
In one preferred embodiment, the (H.sub.inner core surface) is
about 60 Shore A. The (H.sub.inner core surface), as measured in
Shore D units, preferably has a lower limit of about 25 or 28 or 30
or 32 or 36 or 40 or 44 Shore D and an upper limit of about 45 or
48 or 50 or 52 or 55 or 58 or 60 or 62 or 64 or 66 or 70 or 74 or
78 or 80 or 82 or 84 or 88 or 90 or 94 or 96 Shore D.
[0061] Specific Gravity of the Inner Core
[0062] The foamed inner core preferably has a specific gravity (or
density) of about 0.20 to about 1.00 g/cc. That is, the density of
the inner core (as measured at any point of the inner core
structure) is preferably within the range of about 0.20 to about
1.00 g/cc. By the term, "specific gravity of the inner core"
("SG.sub.inner"), it is generally meant the specific gravity (or
density) of the inner core as measured at any point of the inner
core structure. It should be understood, however, that the specific
gravity values, as taken at different particular points of the
inner core structure, may vary. For example, the foamed inner core
may have a "positive" density gradient (that is, the outer surface
(skin) of the inner core may have a density greater than the
geometric center of the inner core.) In one preferred version, the
specific gravity of the geometric center of the inner core
(SG.sub.center of inner core) is less than 0.80 g/cc and more
preferably less than 0.70 g/cc. More particularly, in one version,
the (SG.sub.center of inner core) is in the range of about 0.10 to
about 0.06 g/cc. For example, the (SG.sub.center of inner core) may
be within a range having a lower limit of about 0.10 or 0.15 of
0.20 or 0.24 or 0.30 or 0.35 or 0.37 or 0.40 or 0.42 or 0.45 or
0.47 or 0.50 and an upper limit of about 0.60 or 0.65 or 0.70 or
0.74 or 0.78 or 0.80, or 0.82 or 0.84 or 0.85 or 0.88 or 0.90 g/cc.
Meanwhile, the specific gravity of the outer surface (skin) of the
inner core (SG.sub.skin of inner core), in one preferred version,
is greater than about 0.90 g/cc and more preferably greater than
1.00 g/cc. For example, the (SG.sub.skin of inner core) may fall
within the range of about 0.90 to about 1.25 g/cc. More
particularly, in one version, the (SG.sub.skin of inner core) may
have a specific gravity with a lower limit of about 0.90 or 0.92 or
0.95 or 0.98 or 1.00 or 1.02 or 1.06 or 1.10 g/cc and an upper
limit of about 1.12 or 1.15 or 1.18 or 1.20 or 1.24 or 1.30 or 1.32
or 1.35 g/cc. In other instances, the outer skin may have a
specific gravity of less than 0.90 g/cc. For example, the specific
gravity of the outer skin (SG.sub.skin of inner core) may be about
0.75 or 0.80 or 0.82 or 0.85 or 0.88 g/cc. In such instances,
wherein both the (SG.sub.center of inner core) and (SG.sub.skin of
inner core) are less than 0.90 g/cc, it is still preferred that the
(SG.sub.center of inner core) be less than the (SG.sub.skin of
inner core).
[0063] Outer Core
[0064] As discussed above, the inner core (center) is made
preferably from a foamed composition comprising natural or
synthetic latex rubber foam. In one preferred embodiment, a
two-layered or dual-core is made, wherein the inner core is
surrounded by an outer core layer. The outer core layer can be made
from any suitable thermoplastic or thermoset material. In one
example, a non-foamed thermoset rubber composition is used to form
the outer core layer. In another example, the outer core layer is
formed from a non-foamed thermoplastic composition. In another
example, the natural or synthetic latex rubber foam composition is
used to form the inner core and a viscoelastic polyurethane
shape-memory foam is used to form the surrounding outer core layer.
In yet another embodiment, the viscoelastic polyurethane
shape-memory foam composition is used to form the inner core and
the latex rubber foam is used to form the surrounding outer core
layer.
[0065] As mentioned above, in some embodiments, a polyurethane
shape-memory foam composition can be used to form the foamed inner
core (4). The ingredients and methods used to prepare the
polyurethane memory foam composition make the foam
temperature-sensitive. The formulations used to prepare the
polyurethane foam preferably contain a polyol, polyisocyanate,
water (or other blowing agent), an amine or hydroxyl curing agent,
surfactant, and a catalyst. Once the polymer materials, blowing
(foaming) agents, and any optional ingredients (for example,
fillers) are charged to the mold and treated with sufficient heat
and pressure, the blowing agents are activated. Also, hybrid latex
shape-memory foams can be used.
[0066] The resulting shape-memory foam softens in reaction to heat
and when the heat is removed, it will recover to its original
shape. Today, polyurethane memory foam compositions are used to
make conventional shape-memory foam mattresses. In these
conventional applications, when body weight is placed on the foam
mattress, it becomes softer and molds to the body shape. The
mattress holds this shape for a short time, and the imprint of the
shape can be seen. When the weight is removed, it "springs-back" to
its original shape. The time period for springing back to its
original shape is often referred to as speed of recovery.
[0067] As discussed above, in one embodiment, the natural or
synthetic latex rubber foam composition can be used to form the
inner core and a non-foamed thermoset rubber composition can be
used to form the outer core layer. Suitable thermoset rubber
materials that may be used to form the outer core layer include,
but are not limited to, polybutadiene, polyisoprene, ethylene
propylene rubber ("EPR"), ethylene-propylene-diene ("EPDM") rubber,
styrene-butadiene rubber, styrenic block copolymer rubbers (such as
"SI", "SIS", "SB", "SBS", "SIBS", and the like, where "S" is
styrene, "I" is isobutylene, and "B" is butadiene), polyalkenamers
such as, for example, polyoctenamer, butyl rubber, halobutyl
rubber, polystyrene elastomers, polyethylene elastomers,
polyurethane elastomers, polyurea elastomers, metallocene-catalyzed
elastomers and plastomers, copolymers of isobutylene and
p-alkylstyrene, halogenated copolymers of isobutylene and
p-alkylstyrene, copolymers of butadiene with acrylonitrile,
polychloroprene, alkyl acrylate rubber, chlorinated isoprene
rubber, acrylonitrile chlorinated isoprene rubber, and blends of
two or more thereof. Preferably, the outer core layer is formed
from a polybutadiene rubber composition.
[0068] Examples of commercially-available polybutadiene rubbers
that can be used in accordance with this invention, include, but
are not limited to, BR 01 and BR 1220, available from BST
Elastomers of Bangkok, Thailand; SE BR 1220LA and SE BR1203,
available from DOW Chemical Co of Midland, Mich.; BUDENE 1207,
1207s, 1208, and 1280 available from Goodyear, Inc of Akron, Ohio;
BR 01, 51 and 730, available from Japan Synthetic Rubber (JSR) of
Tokyo, Japan; BUNA CB 21, CB 22, CB 23, CB 24, CB 25, CB 29 MES, CB
60, CB Nd 60, CB 55 NF, CB 70 B, CB KA 8967, and CB 1221, available
from Lanxess Corp. of Pittsburgh. Pa.; BR1208, available from LG
Chemical of Seoul, South Korea; UBEPOL BR130B, BR150, BR150B,
BR150L, BR230, BR360L, BR710, and VCR617, available from UBE
Industries, Ltd. of Tokyo, Japan; EUROPRENE NEOCIS BR 60, INTENE 60
AF and P30AF, and EUROPRENE BR HV80, available from Polimeri Europa
of Rome, Italy; AFDENE 50 and NEODENE BR40, BR45, BR50 and BR60,
available from Karbochem (PTY) Ltd. of Bruma, South Africa; KBR 01,
NdBr 40, NdBR-45, NdBr 60, KBR 710S, KBR 710H, and KBR 750,
available from Kumho Petrochemical Co., Ltd. Of Seoul, South Korea;
and DIENE 55NF, 70AC, and 320 AC, available from Firestone Polymers
of Akron, Ohio.
[0069] These non-foamed rubber compositions can be cured using
conventional rubber curing methods. For example, the rubber
compositions can contain peroxide free-radical initiators, reactive
co agents, and various additives. Preferably, the polybutadiene
rubber is used in an amount of at least about 5% by weight based on
total weight of composition and is generally present in an amount
of about 5% to about 100%, or an amount within a range having a
lower limit of 5% or 10% or 20% or 30% or 40% or 50% and an upper
limit of 55% or 60% or 70% or 80% or 90% or 95% or 100%.
Preferably, the concentration of polybutadiene rubber is about 40
to about 95 weight percent. If desirable, lesser amounts of other
thermoset materials may be incorporated into the base rubber. Such
materials include the rubbers discussed above, for example,
cis-polyisoprene, trans-polyisoprene, balata, polychloroprene,
polynorbornene, polyoctenamer, polypentenamer, butyl rubber, EPR,
EPDM, styrene-butadiene, and the like.
[0070] In other instances, non-foamed or foamed thermoplastic
compositions can be used to form the outer core layer. Suitable
thermoplastic polymers that may be used to form the outer core in
accordance with the present invention include, but are not limited
to, the following polymers (including homopolymers, copolymers, and
derivatives thereof.): (a) polyesters, particularly those modified
with a compatibilizing group such as sulfonate or phosphonate,
including modified poly(ethylene terephthalate), modified
poly(butylene terephthalate), modified poly(propylene
terephthalate), modified poly(trimethylene terephthalate), modified
poly(ethylene naphthenate), and those disclosed in U.S. Pat. Nos.
6,353,050, 6,274,298, and 6,001,930, the entire disclosures of
which are hereby incorporated herein by reference, and blends of
two or more thereof; (b) polyamides, polyamide-ethers, and
polyamide-esters, and those disclosed in U.S. Pat. Nos. 6,187,864,
6,001,930, and 5,981,654, the entire disclosures of which are
hereby incorporated herein by reference, and blends of two or more
thereof; (c) polyurethanes, polyureas, polyurethane-polyurea
hybrids, and blends of two or more thereof; (d) fluoropolymers,
such as those disclosed in U.S. Pat. Nos. 5,691,066, 6,747,110 and
7,009,002, the entire disclosures of which are hereby incorporated
herein by reference, and blends of two or more thereof; (e)
polystyrenes, such as poly(styrene-co-maleic anhydride),
acrylonitrile-butadiene-styrene, poly(styrene sulfonate),
polyethylene styrene, and blends of two or more thereof; (f)
polyvinyl chlorides and grafted polyvinyl chlorides, and blends of
two or more thereof; (g) polycarbonates, blends of
polycarbonate/acrylonitrile-butadiene-styrene, blends of
polycarbonate/polyurethane, blends of polycarbonate/polyester, and
blends of two or more thereof; (h) polyethers, such as polyarylene
ethers, polyphenylene oxides, block copolymers of alkenyl aromatics
with vinyl aromatics and polyamicesters, and blends of two or more
thereof; (i) polyimides, polyetherketones, polyamideimides, and
blends of two or more thereof; and (j) polycarbonate/polyester
copolymers and blends.
[0071] It is recognized that the above-described thermoset and
thermoplastic non-foamed compositions can be used to form any of
the inner (center) core and/or outer core layers, and/or inner,
intermediate, or outer cover layers may comprise the foamed
compositions of this invention. For example, the latex rubber foam
composition can be used to form both core layers of the core
sub-assembly (inner core and outer core); while the thermoset and
thermoplastic non-foamed compositions can be used to form the
surrounding cover layers.
[0072] Molding of Outer Core Over the Inner Core
[0073] In the present invention, the inner core (center) of the
golf ball preferably comprises a latex rubber foamed composition.
The foam may have an open or closed cellular structure or
combinations thereof and may range from relatively rigid foam to
very flexible foam. Referring back to FIG. 1, the foamed inner core
(4) has a foamed geometric center (6) and non-foamed outer surface
skin (8).
[0074] Referring to FIGS. 3 and 4, in a second step, an outer core
layer (24, 34) is formed over the foamed inner core (22, 32). For
example, retractable pin injection-molding (RPIM), casting,
coating, or dipping methods may be used. In an over-molding
process, the outer core layer (24, 34) is prepared by molding the
outer core composition over the inner core. Suitable thermoset and
thermoplastic materials that may be used to form the outer core
layer are described above. The outer core layer (24, 34) may be
molded over the foamed inner core (22, 32) using a variety of
molding techniques.
[0075] For example, the outer core composition may be
injection-molded or compression-molded to produce half-shells.
These smooth-surfaced or textured hemispherical shells are then
placed around the foamed, spherical inner core in a compression
mold. Under sufficient heating and pressure, the shells fuse
together to form an outer core layer that encapsulates the foamed
inner core. In another method, the outer core composition may be
added to an injection-molding machine. After the foamed inner core
has been positioned properly in the injection-molding cavity, the
outer core composition is injection-molded directly over the inner
core.
[0076] Referring to FIG. 3, a dual-layered core assembly comprising
an inner core (32) and surrounding outer core layer (34) produced
in accordance with this invention is shown. The dual-core assembly
is surrounded by a cover (36) to form a finished golf ball
(30).
[0077] Other multi-layered golf ball constructions may be made in
accordance with this invention. For example, in FIG. 4, a golf ball
(20) having a dual-layered core assembly comprising an inner core
(22) and surrounding outer core layer (24) is prepared. A
multi-layered cover comprising an inner cover (26) and outer cover
(28) is disposed about the core assembly.
[0078] Core Structure
[0079] As discussed above, the core of the golf ball of this
invention preferably has a dual-layered structure comprising an
inner core and outer core layer. The hardness of the core is an
important property. In general, cores with relatively high hardness
values have higher compression and tend to have good durability and
resiliency. However, some high compression balls are stiff and this
may have a detrimental effect on shot control and placement. Thus,
the optimum balance of hardness in the core assembly needs to be
attained.
[0080] In one preferred golf ball, the inner core (center) has a
"positive" hardness gradient (that is, the outer surface of the
inner core is harder than its geometric center); and the outer core
layer has a "positive" hardness gradient (that is, the outer
surface of the outer core layer is harder than the inner surface of
the outer core layer.) In such cases where both the inner core and
outer core layer each has a "positive" hardness gradient, the outer
surface hardness of the outer core layer is preferably greater than
the hardness of the geometric center of the inner core. In one
preferred version, the positive hardness gradient of the inner core
is in the range of about 2 to about 40 Shore C units and even more
preferably about 10 to about 25 Shore C units; while the positive
hardness gradient of the outer core is in the range of about 2 to
about 20 Shore C and even more preferably about 3 to about 10 Shore
C.
[0081] In an alternative version, the inner core may have a
positive hardness gradient; and the outer core layer may have a
"zero" hardness gradient (that is, the hardness values of the outer
surface of the outer core layer and the inner surface of the outer
core layer are substantially the same) or a "negative" hardness
gradient (that is, the outer surface of the outer core layer is
softer than the inner surface of the outer core layer.) For
example, in one version, the inner core has a positive hardness
gradient; and the outer core layer has a negative hardness gradient
in the range of about 2 to about 25 Shore C. In a second
alternative version, the inner core may have a zero or negative
hardness gradient; and the outer core layer may have a positive
hardness gradient. Still yet, in another embodiment, both the inner
core and outer core layers have zero or negative hardness
gradients.
[0082] In general, hardness gradients are further described in
Bulpett et al., U.S. Pat. Nos. 7,537,529 and 7,410,429, the
disclosures of which are hereby incorporated by reference. Methods
for measuring the hardness of the inner core and outer core layers
along with other layers in the golf ball and determining the
hardness gradients of the various layers are described in further
detail below. The core layers have positive, negative, or zero
hardness gradients defined by hardness measurements made at the
outer surface of the inner core (or outer surface of the outer core
layer) and radially inward towards the center of the inner core (or
inner surface of the outer core layer). These measurements are made
typically at 2-mm increments as described in the test methods
below. In general, the hardness gradient is determined by
subtracting the hardness value at the innermost portion of the
component being measured (for example, the center of the inner core
or inner surface of the outer core layer) from the hardness value
at the outer surface of the component being measured (for example,
the outer surface of the inner core or outer surface of the outer
core layer).
[0083] Positive Hardness Gradient.
[0084] For example, if the hardness value of the outer surface of
the inner core is greater than the hardness value of the inner
core's geometric center (that is, the inner core has a surface
harder than its geometric center), the hardness gradient will be
deemed "positive" (a larger number minus a smaller number equals a
positive number.) For example, if the outer surface of the inner
core has a hardness of 67 Shore C and the geometric center of the
inner core has a hardness of 60 Shore C, then the inner core has a
positive hardness gradient of 7. Likewise, if the outer surface of
the outer core layer has a greater hardness value than the inner
surface of the outer core layer, the given outer core layer will be
considered to have a positive hardness gradient.
[0085] Negative Hardness Gradient.
[0086] On the other hand, if the hardness value of the outer
surface of the inner core is less than the hardness value of the
inner core's geometric center (that is, the inner core has a
surface softer than its geometric center), the hardness gradient
will be deemed "negative." For example, if the outer surface of the
inner core has a hardness of 68 Shore C and the geometric center of
the inner core has a hardness of 70 Shore C, then the inner core
has a negative hardness gradient of 2. Likewise, if the outer
surface of the outer core layer has a lesser hardness value than
the inner surface of the outer core layer, the given outer core
layer will be considered to have a negative hardness gradient.
[0087] Zero Hardness Gradient.
[0088] In another example, if the hardness value of the outer
surface of the inner core is substantially the same as the hardness
value of the inner core's geometric center (that is, the surface of
the inner core has about the same hardness as the geometric
center), the hardness gradient will be deemed "zero." For example,
if the outer surface of the inner core and the geometric center of
the inner core each has a hardness of 65 Shore C, then the inner
core has a zero hardness gradient. Likewise, if the outer surface
of the outer core layer has a hardness value approximately the same
as the inner surface of the outer core layer, the outer core layer
will be considered to have a zero hardness gradient.
[0089] More particularly, the term, "positive hardness gradient" as
used herein means a hardness gradient of positive 3 Shore C or
greater, preferably 7 Shore C or greater, more preferably 10 Shore
C, and even more preferably 20 Shore C or greater. The term, "zero
hardness gradient" as used herein means a hardness gradient of less
than 3 Shore C, preferably less than 1 Shore C and may have a value
of zero or negative 1 to negative 10 Shore C. The term, "negative
hardness gradient" as used herein means a hardness value of less
than zero, for example, negative 3, negative 5, negative 7,
negative 10, negative 15, or negative 20 or negative 25. The terms,
"zero hardness gradient" and "negative hardness gradient" may be
used herein interchangeably to refer to hardness gradients of
negative 1 to negative 10.
[0090] The inner core preferably has a geometric center hardness
(H.sub.inner core center) of about 5 Shore D or greater. For
example, the (H.sub.inner core center) may be in the range of about
5 to about 88 Shore D and more particularly within a range having a
lower limit of about 5 or 10 or 18 or 20 or 26 or 30 or 34 or 36 or
38 or 42 or 48 or 50 or 52 Shore D and an upper limit of about 54
or 56 or 58 or 60 or 62 or 64 or 68 or 70 or 74 or 76 or 80 or 82
or 84 or 88 Shore D. In another example, the center hardness of the
inner core (H.sub.inner core center), as measured in Shore C units,
is preferably about 10 Shore C or greater; for example, the
H.sub.inner core center may have a lower limit of about 10 or 14 or
16 or 20 or 23 or 24 or 28 or 31 or 34 or 37 or 40 or 44 Shore C
and an upper limit of about 46 or 48 or 50 or 51 or 53 or 55 or 58
or 61 or 62 or 65 or 68 or 71 or 74 or 76 or 78 or 79 or 80 or 84
or 90 Shore C. Concerning the outer surface hardness of the inner
core (H.sub.inner core surface), this hardness is preferably about
12 Shore D or greater; for example, the H.sub.inner core surface
may fall within a range having a lower limit of about 12 or 15 or
18 or 20 or 22 or 26 or 30 or 34 or 36 or 38 or 42 or 48 or 50 or
52 Shore D and an upper limit of about 54 or 56 or 58 or 60 or 62
or 70 or 72 or 75 or 78 or 80 or 82 or 84 or 86 or 90 Shore D. In
one version, the outer surface hardness of the inner core
(H.sub.inner core surface), as measured in Shore C units, has a
lower limit of about 13 or 15 or 18 or 20 or 22 or 24 or 27 or 28
or 30 or 32 or 34 or 38 or 44 or 47 or 48 Shore C and an upper
limit of about 50 or 54 or 56 or 61 or 65 or 66 or 68 or 70 or 73
or 76 or 78 or 80 or 84 or 86 or 88 or 90 or 92 Shore C. In another
version, the geometric center hardness (H.sub.inner core center) is
in the range of about 10 Shore C to about 50 Shore C; and the outer
surface hardness of the inner core (H.sub.inner core surface) is in
the range of about 5 Shore C to about 50 Shore C.
[0091] On the other hand, the outer core layer preferably has an
outer surface hardness (H.sub.outer surface of OC) of about 40
Shore D or greater, and more preferably within a range having a
lower limit of about 40 or 42 or 44 or 46 or 48 or 50 or 52 and an
upper limit of about 54 or 56 or 58 or 60 or 62 or 64 or 70 or 74
or 78 or 80 or 82 or 85 or 87 or 88 or 90 Shore D. The outer
surface hardness of the outer core layer (H.sub.outer surface of
OC), as measured in Shore C units, preferably has a lower limit of
about 40 or 42 or 45 or 48 or 50 or 54 or 58 or 60 or 63 or 65 or
67 or 720 or 72 or 73 or 76 Shore C, and an upper limit of about 78
or 80 or 84 or 87 or 88 or 89 or 90 or 92 or 95 Shore C. And, the
inner surface of the outer core layer (H.sub.inner surface of OC)
or midpoint hardness of the outer core layer (H.sub.midpoint of
OC), preferably has a hardness of about 40 Shore D or greater, and
more preferably within a range having a lower limit of about 40 or
42 or 44 or 46 or 48 or 50 or 52 and an upper limit of about 54 or
56 or 58 or 60 or 62 or 64 or 70 or 74 or 78 or 80 or 82 or 85 or
87 or 88 or 90 Shore D. The inner surface hardness (H.sub.inner
surface of OC) or midpoint hardness (H.sub.midpoint of OC) of the
outer core layer, as measured in Shore C units, preferably has a
lower limit of about 40 or 42 or 44 or 45 or 47 or 50 or 52 or 54
or 55 or 58 or 60 or 63 or 65 or 67 or 70 or 73 or 75 Shore C, and
an upper limit of about 78 or 80 or 85 or 88 or 89 or 90 or 92 or
95 Shore C. Likewise, the midpoint of a core layer is taken at a
point equidistant from the inner surface and outer surface of the
layer to be measured, most typically an outer core layer. Once one
or more core layers surround a layer of interest, the exact
midpoint may be difficult to determine, therefore, for the purposes
of the present invention, the measurement of "midpoint" hardness of
a layer is taken within plus or minus 1 mm of the measured midpoint
of the layer.
[0092] In one embodiment, the outer surface hardness of the outer
core layer (H.sub.outer surface of OC), is less than the outer
surface hardness (H.sub.inner core surface) or midpoint hardness
(H.sub.midpoint of OC), of the inner core by at least 3 Shore C
units and more preferably by at least 5 Shore C.
[0093] In a second embodiment, the outer surface hardness of the
outer core layer (H.sub.outer surface of OC), is greater than the
outer surface hardness (H.sub.inner core surface) or midpoint
hardness (H.sub.midpoint of OC), of the inner core by at least 3
Shore C units and more preferably by at least 5 Shore C.
[0094] As discussed above, the inner core is preferably formed from
a foamed thermoplastic or thermoset composition and more preferably
foamed polyurethanes. And, the outer core layer is formed
preferably from a non-foamed thermoset composition such as
polybutadiene rubber. The outer core layer also may be formed from
non-foamed thermoplastic compositions.
[0095] The core structure also has a hardness gradient across the
entire core assembly. In one embodiment, the (H.sub.inner core
center) is in the range of about 10 Shore C to about 60 Shore C,
preferably about 13 Shore C to about 55 Shore C; and the
(H.sub.outer surface of OC) is in the range of about 65 to about 96
Shore C, preferably about 68 Shore C to about 94 Shore C or about
75 Shore C to about 93 Shore C, to provide a positive hardness
gradient across the core assembly. The gradient across the core
assembly will vary based on several factors including, but not
limited to, the dimensions of the inner core, intermediate core,
and outer core layers.
[0096] The inner core preferably has a diameter in the range of
about 0.100 to about 1.100 inches. For example, the inner core may
have a diameter within a range of about 0.100 to about 0.500
inches. In another example, the inner core may have a diameter
within a range of about 0.300 to about 0.800 inches. More
particularly, the inner core may have a diameter size with a lower
limit of about 0.10 or 0.12 or 0.15 or 0.25 or 0.30 or 0.35 or 0.45
or 0.55 inches and an upper limit of about 0.60 or 0.65 or 0.70 or
0.80 or 0.90 or 1.00 or 1.10 inches. As far as the outer core layer
is concerned, it preferably has a thickness in the range of about
0.100 to about 0.750 inches. For example, the lower limit of
thickness may be about 0.050 or 0.100 or 0.150 or 0.200 or 0.250 or
0.300 or 0.340 or 0.400 and the upper limit may be about 0.500 or
0.550 or 0.600 or 0.650 or 0.700 or 0.750 inches.
[0097] As discussed above, in one preferred embodiment, the inner
core has a specific gravity in the range of about 0.25 to about
1.50 g/cc. Also, as discussed above, the specific gravity of the
inner core may vary at different points of the inner core
structure. That is, there may be a specific gravity gradient in the
inner core. For example, in one preferred version, the geometric
center of the inner core has a density in the range of about 0.25
to about 0.75 g/cc; while the outer skin of the inner core has a
density in the range of about 0.75 to about 1.50 g/cc.
[0098] Meanwhile, the outer core layer preferably has a relatively
high specific gravity. Thus, the specific gravity of the inner core
layer (SG.sub.inner) is preferably less than the specific gravity
of the outer core layer (SG.sub.outer). By the term, "specific
gravity of the outer core layer" ("SG.sub.outer"), it is generally
meant the specific gravity of the outer core layer as measured at
any point of the outer core layer. The specific gravity values at
different points in the outer core layer may vary. That is, there
may be specific gravity gradients in the outer core layer similar
to the inner core. For example, the outer core layer may have a
specific gravity within a range having a lower limit of about 0.50
or 0.60 or 0.70 or 0.75 or 0.85 or 0.95 or 1.00 or 1.10 or 1.25 or
1.30 or 1.36 or 1.40 or 1.42 or 1.48 or 1.50 or 1.60 or 1.66 or
1.75 or 2.00 and an upper limit of 2.50 or 2.60 or 2.80 or 2.90 or
3.00 or 3.10 or 3.25 or 3.50 or 3.60 or 3.80 or 4.00, 4.25 or 5.00
or 5.10 or 5.20 or 5.30 or 5.40 or 6.00 or 6.20 or 6.25 or 6.30 or
6.40 or 6.50 or 7.00 or 7.10 or 7.25 or 7.50 or 7.60 or 7.65 or
7.80 or 8.00 or 8.20 or 8.50 or 9.00 or 9.75 or 10.008/cc.
[0099] In general, the specific gravities of the respective pieces
of an object affect the Moment of Inertia (MOI) of the object. The
Moment of Inertia of a ball (or other object) about a given axis
generally refers to how difficult it is to change the ball's
angular motion about that axis. If the ball's mass is concentrated
towards the center (the center piece (for example, inner core) has
a higher specific gravity than the outer piece (for example, outer
core layers), less force is required to change its rotational rate,
and the ball has a relatively low Moment of Inertia. In such balls,
most of the mass is located close to the ball's axis of rotation
and less force is needed to generate spin. Thus, the ball has a
generally high spin rate as the ball leaves the club's face after
making impact. Conversely, if the ball's mass is concentrated
towards the outer surface (the outer piece (for example, outer core
layers) has a higher specific gravity than the center piece (for
example, inner core), more force is required to change its
rotational rate, and the ball has a relatively high Moment of
Inertia. That is, in such balls, most of the mass is located away
from the ball's axis of rotation and more force is needed to
generate spin. Such balls have a generally low spin rate as the
ball leaves the club's face after making impact.
[0100] More particularly, as described in Sullivan, U.S. Pat. No.
6,494,795 and Ladd et al., U.S. Pat. No. 7,651,415, the formula for
the Moment of Inertia for a sphere through any diameter is given in
the CRC Standard Mathematical Tables, 24th Edition, 1976 at 20
(hereinafter CRC reference). The term, "specific gravity" as used
herein, has its ordinary and customary meaning, that is, the ratio
of the density of a substance to the density of water at 4.degree.
C., and the density of water at this temperature is 1
g/cm.sup.3.
[0101] In one embodiment, the golf balls of this invention are
relatively low spin and long distance. That is, the foam core
construction, as described above, wherein the inner core is made of
a foamed composition helps provide a relatively low spin ball
having good resiliency. The inner foam cores of this invention
preferably have a Coefficient of Restitution (COR) of about 0.300
or greater; more preferably about 0.400 or greater, and even more
preferably about 0.450 or greater. The resulting balls containing
the dual-layered core constructions of this invention and cover of
at least one layer preferably have a COR of about 0.700 or greater,
more preferably about 0.730 or greater; and even more preferably
about 0.750 to 0.810 or greater. The inner foam cores preferably
have a Soft Center Deflection Index ("SCDI") compression, as
described in the Test Methods below, in the range of about 50 to
about 190, and more preferably in the range of about 60 to about
170.
[0102] The USGA has established a maximum weight of 45.93 g (1.62
ounces) for golf balls. For play outside of USGA rules, the golf
balls can be heavier. In one preferred embodiment, the weight of
the multi-layered core is in the range of about 28 to about 38
grams. Also, golf balls made in accordance with this invention can
be of any size, although the USGA requires that golf balls used in
competition have a diameter of at least 1.68 inches. For play
outside of United States Golf Association (USGA) rules, the golf
balls can be of a smaller size. Normally, golf balls are
manufactured in accordance with USGA requirements and have a
diameter in the range of about 1.68 to about 1.80 inches. As
discussed further below, the golf ball contains a cover which may
be multi-layered and in addition may contain intermediate (casing)
layers, and the thickness levels of these layers also must be
considered. Thus, in general, the dual-layer core structure
normally has an overall diameter within a range having a lower
limit of about 1.00 or 1.20 or 1.30 or 1.40 inches and an upper
limit of about 1.58 or 1.60 or 1.62 or 1.66 inches, and more
preferably in the range of about 1.3 to 1.65 inches. In one
embodiment, the diameter of the core assembly is in the range of
about 1.45 to about 1.62 inches.
[0103] Cover Structure
[0104] The golf ball assemblies of this invention may be enclosed
with one or more cover layers. The golf ball assembly may comprise
the multi-layered core structure as discussed above. In other
versions, the golf ball assembly includes the core structure and
one or more casing (mantle) layers disposed about the core. In one
particularly preferred version, the golf ball includes a
multi-layered cover comprising inner and outer cover layers. The
inner cover layer is preferably formed from a composition
comprising an ionomer or a blend of two or more ionomers that helps
impart hardness to the ball. In a particular embodiment, the inner
cover layer is formed from a composition comprising a high acid
ionomer. A particularly suitable high acid ionomer is Surlyn
8150.RTM. (DuPont). Surlyn 8150.RTM. is a copolymer of ethylene and
methacrylic acid, having an acid content of 19 wt %, which is 45%
neutralized with sodium. In another particular embodiment, the
inner cover layer is formed from a composition comprising a high
acid ionomer and a maleic anhydride-grafted non-ionomeric polymer.
A particularly suitable maleic anhydride-grafted polymer is
Fusabond 525D.RTM. (DuPont). Fusabond 525D.RTM. is a maleic
anhydride-grafted, metallocene-catalyzed ethylene-butene copolymer
having about 0.9 wt % maleic anhydride grafted onto the copolymer.
A particularly preferred blend of high acid ionomer and maleic
anhydride-grafted polymer is an 84 wt %/16 wt % blend of Surlyn
8150.RTM. and Fusabond 525D.RTM.. Blends of high acid ionomers with
maleic anhydride-grafted polymers are further disclosed, for
example, in U.S. Pat. Nos. 6,992,135 and 6,677,401, the entire
disclosures of which are hereby incorporated herein by
reference.
[0105] The inner cover layer also may be formed from a composition
comprising a 50/45/5 blend of Surlyn.RTM. 8940/Surlyn.RTM.
9650/Nucrel.RTM. 960, and, in a particularly preferred embodiment,
the composition has a material hardness of from 80 to 85 Shore C.
In yet another version, the inner cover layer is formed from a
composition comprising a 50/25/25 blend of Surlyn.RTM.
8940/Surlyn.RTM. 9650/Surlyn.RTM. 9910, preferably having a
material hardness of about 90 Shore C. The inner cover layer also
may be formed from a composition comprising a 50/50 blend of
Surlyn.RTM. 8940/Surlyn.RTM. 9650, preferably having a material
hardness of about 86 Shore C. A composition comprising a 50/50
blend of Surlyn.RTM. 8940 and Surlyn.RTM. 7940 also may be used.
Surlyn.RTM. 8940 is an E/MAA copolymer in which the MAA acid groups
have been partially neutralized with sodium ions. Surlyn.RTM. 9650
and Surlyn.RTM. 9910 are two different grades of E/MAA copolymer in
which the MAA acid groups have been partially neutralized with zinc
ions. Nucrel.RTM. 960 is an E/MAA copolymer resin nominally made
with 15 wt % methacrylic acid.
[0106] A wide variety of materials may be used for forming the
outer cover including, for example, polyurethanes; polyureas;
copolymers, blends and hybrids of polyurethane and polyurea;
olefin-based copolymer ionomer resins (for example, Surlyn.RTM.
ionomer resins and DuPont HPF.RTM. 1000 and HPF.RTM. 2000,
commercially available from DuPont; Iotek.RTM. ionomers,
commercially available from ExxonMobil Chemical Company;
Amplify.RTM. IO ionomers of ethylene acrylic acid copolymers,
commercially available from The Dow Chemical Company; and
Clarix.RTM. ionomer resins, commercially available from A. Schulman
Inc.); polyethylene, including, for example, low density
polyethylene, linear low density polyethylene, and high density
polyethylene; polypropylene; rubber-toughened olefin polymers; acid
copolymers, for example, poly(meth)acrylic acid, which do not
become part of an ionomeric copolymer; plastomers; flexomers;
styrene/butadiene/styrene block copolymers;
styrene/ethylene-butylene/styrene block copolymers; dynamically
vulcanized elastomers; copolymers of ethylene and vinyl acetates;
copolymers of ethylene and methyl acrylates; polyvinyl chloride
resins; polyamides, poly(amide-ester) elastomers, and graft
copolymers of ionomer and polyamide including, for example,
Pebax.RTM. thermoplastic polyether block amides, commercially
available from Arkema Inc; cross-linked trans-polyisoprene and
blends thereof; polyester-based thermoplastic elastomers, such as
Hytrel.RTM., commercially available from DuPont or RiteFlex.RTM.,
commercially available from Ticona Engineering Polymers;
polyurethane-based thermoplastic elastomers, such as
Elastollan.RTM., commercially available from BASF; synthetic or
natural vulcanized rubber; and combinations thereof. Castable
polyurethanes, polyureas, and hybrids of polyurethanes-polyureas
are particularly desirable because these materials can be used to
make a golf ball having high resiliency and a soft feel. By the
term, "hybrids of polyurethane and polyurea," it is meant to
include copolymers and blends thereof.
[0107] Polyurethanes, polyureas, and blends, copolymers, and
hybrids of polyurethane/polyurea are also particularly suitable for
forming cover layers. When used as cover layer materials,
polyurethanes and polyureas can be thermoset or thermoplastic.
Thermoset materials can be formed into golf ball layers by
conventional casting or reaction injection molding techniques.
Thermoplastic materials can be formed into golf ball layers by
conventional compression or injection molding techniques.
[0108] The compositions used to make the casing (mantle) and cover
layers may contain a wide variety of fillers and additives to
impart specific properties to the ball. For example, relatively
heavy-weight and light-weight metal fillers such as, particulate;
powders; flakes; and fibers of copper, steel, brass, tungsten,
titanium, aluminum, magnesium, molybdenum, cobalt, nickel, iron,
lead, tin, zinc, barium, bismuth, bronze, silver, gold, and
platinum, and alloys and combinations thereof may be used to adjust
the specific gravity of the ball. Other additives and fillers
include, but are not limited to, optical brighteners, coloring
agents, fluorescent agents, whitening agents, UV absorbers, light
stabilizers, surfactants, processing aids, antioxidants,
stabilizers, softening agents, fragrance components, plasticizers,
impact modifiers, titanium dioxide, clay, mica, talc, glass flakes,
milled glass, and mixtures thereof.
[0109] The inner cover layer preferably has a material hardness
within a range having a lower limit of 70 or 75 or 80 or 82 Shore C
and an upper limit of 85 or 86 or 90 or 92 Shore C. The thickness
of the intermediate layer is preferably within a range having a
lower limit of 0.010 or 0.015 or 0.020 or 0.030 inches and an upper
limit of 0.035 or 0.045 or 0.080 or 0.120 inches. The outer cover
layer preferably has a material hardness of 85 Shore C or less. The
thickness of the outer cover layer is preferably within a range
having a lower limit of 0.010 or 0.015 or 0.025 inches and an upper
limit of 0.035 or 0.040 or 0.055 or 0.080 inches. Methods for
measuring hardness of the layers in the golf ball are described in
further detail below.
[0110] A single cover or, preferably, an inner cover layer is
formed around the outer core layer. When an inner cover layer is
present, an outer cover layer is formed over the inner cover layer.
Most preferably, the inner cover is formed from an ionomeric
material and the outer cover layer is formed from a polyurethane
material, and the outer cover layer has a hardness that is less
than that of the inner cover layer. Preferably, the inner cover has
a hardness of greater than about 60 Shore D and the outer cover
layer has a hardness of less than about 60 Shore D. In an
alternative embodiment, the inner cover layer is comprised of a
partially or fully neutralized ionomer, a thermoplastic polyester
elastomer such as Hytrel.TM., commercially available form DuPont, a
thermoplastic polyether block amide, such as Pebax.TM.,
commercially available from Arkema, Inc., or a thermoplastic or
thermosetting polyurethane or polyurea, and the outer cover layer
is comprised of an ionomeric material. In this alternative
embodiment, the inner cover layer has a hardness of less than about
60 Shore D and the outer cover layer has a hardness of greater than
about 55 Shore D and the inner cover layer hardness is less than
the outer cover layer hardness.
[0111] As discussed above, the core structure of this invention may
be enclosed with one or more cover layers. In one embodiment, a
multi-layered cover comprising inner and outer cover layers is
formed, where the inner cover layer has a thickness of about 0.01
inches to about 0.06 inches, more preferably about 0.015 inches to
about 0.040 inches, and most preferably about 0.02 inches to about
0.035 inches. In this version, the inner cover layer is formed from
a partially- or fully-neutralized ionomer having a Shore D hardness
of greater than about 55, more preferably greater than about 60,
and most preferably greater than about 65. The outer cover layer,
in this embodiment, preferably has a thickness of about 0.015
inches to about 0.055 inches, more preferably about 0.02 inches to
about 0.04 inches, and most preferably about 0.025 inches to about
0.035 inches, with a hardness of about Shore D 80 or less, more
preferably 70 or less, and most preferably about 60 or less. The
inner cover layer is harder than the outer cover layer in this
version. A preferred outer cover layer is a castable or reaction
injection molded polyurethane, polyurea or copolymer, blend, or
hybrid thereof having a Shore D hardness of about 40 to about 50.
In another multi-layer cover, dual-core embodiment, the outer cover
and inner cover layer materials and thickness are the same but, the
hardness range is reversed, that is, the outer cover layer is
harder than the inner cover layer. For this harder outer
cover/softer inner cover embodiment, the ionomer resins described
above would preferably be used as outer cover material.
[0112] Manufacturing of Golf Balls
[0113] As described above, the inner core preferably is formed by
molding a foamed composition containing heat-activated blowing
agents. The outer core layer, which surrounds the inner core, is
formed by molding a composition over the inner core. Then, the
casing and/or cover layers are applied over the core assembly.
Prior to this step, the core structure may be surface-treated to
increase the adhesion between its outer surface and the next layer
that will be applied over the core. Such surface-treatment may
include mechanically or chemically-abrading the outer surface of
the core. For example, the core may be subjected to
corona-discharge, plasma-treatment, silane-dipping, or other
treatment methods known to those in the art.
[0114] The cover layers are formed over the core or ball assembly
(the core structure and any casing layers disposed about the core)
using a suitable technique such as, for example,
compression-molding, flip-molding, injection-molding, retractable
pin injection-molding, reaction injection-molding (RIM), liquid
injection-molding, casting, spraying, powder-coating,
vacuum-forming, flow-coating, dipping, spin-coating, and the like.
Preferably, each cover layer is separately formed over the ball
sub-assembly. For example, an ethylene acid copolymer ionomer
composition may be injection-molded to produce half-shells.
Alternatively, the ionomer composition can be placed into a
compression mold and molded under sufficient pressure, temperature,
and time to produce the hemispherical shells. The smooth-surfaced
hemispherical shells are then placed around the core assembly in a
compression mold. Under sufficient heating and pressure, the shells
fuse together to form an inner cover layer that surrounds the
assembly. In another method, the ionomer composition is
injection-molded directly onto the core assembly using retractable
pin injection molding. An outer cover layer comprising a
polyurethane or polyurea composition over the ball assembly may be
formed by using a casting process.
[0115] After the golf balls have been removed from the mold, they
may be subjected to finishing steps such as flash-trimming,
surface-treatment, marking, coating, and the like using techniques
known in the art. For example, in traditional white-colored golf
balls, the white-pigmented cover may be surface-treated using a
suitable method such as, for example, corona, plasma, or
ultraviolet (UV) light-treatment. Then, indicia such as trademarks,
symbols, logos, letters, and the like may be printed on the ball's
cover using pad-printing, ink-jet printing, dye-sublimation, or
other suitable printing methods. Clear surface coatings (for
example, primer and top-coats), which may contain a fluorescent
whitening agent, are applied to the cover. The resulting golf ball
has a glossy and durable surface finish.
[0116] In another finishing process, the golf balls are painted
with one or more paint coatings. For example, white primer paint
may be applied first to the surface of the ball and then a white
top-coat of paint may be applied over the primer. Of course, the
golf ball may be painted with other colors, for example, red, blue,
orange, and yellow. As noted above, markings such as trademarks and
logos may be applied to the painted cover of the golf ball.
Finally, a clear surface coating may be applied to the cover to
provide a shiny appearance and protect any logos and other markings
printed on the ball. In FIG. 5, a finished golf ball (38) having a
dimpled outer cover (40) made in accordance with the present
invention is shown. As discussed above, various patterns and
geometric shapes of the dimples (40) can be used to modify the
aerodynamic properties of the golf ball.
[0117] Different ball constructions can be made using the methods
and core constructions of this invention as shown in FIGS. 1-5.
Such golf ball constructions include, for example, five-piece, and
six-piece constructions. It should be understood that the golf ball
components and finished golf balls shown in FIGS. 1-5 are for
illustrative purposes only, and they are not meant to be
restrictive. Other golf ball constructions can be made in
accordance with this invention. For example, the foam composition
of this invention is primarily discussed herein as being suitable
for producing a foam inner core or center for a golf ball. However,
it is recognized that this foam composition may be used for
producing an outer core layer, casing layer, cover, or any other
suitable component layer for the golf ball in accordance with this
invention.
[0118] Test Methods
[0119] Hardness.
[0120] The center hardness of a core is obtained according to the
following procedure. The core is gently pressed into a
hemispherical holder having an internal diameter approximately
slightly smaller than the diameter of the core, such that the core
is held in place in the hemispherical portion of the holder while
concurrently leaving the geometric central plane of the core
exposed. The core is secured in the holder by friction, such that
it will not move during the cutting and grinding steps, but the
friction is not so excessive that distortion of the natural shape
of the core would result. The core is secured such that the parting
line of the core is roughly parallel to the top of the holder. The
diameter of the core is measured 90 degrees to this orientation
prior to securing. A measurement is also made from the bottom of
the holder to the top of the core to provide a reference point for
future calculations. A rough cut is made slightly above the exposed
geometric center of the core using a band saw or other appropriate
cutting tool, making sure that the core does not move in the holder
during this step. The remainder of the core, still in the holder,
is secured to the base plate of a surface grinding machine. The
exposed `rough` surface is ground to a smooth, flat surface,
revealing the geometric center of the core, which can be verified
by measuring the height from the bottom of the holder to the
exposed surface of the core, making sure that exactly half of the
original height of the core, as measured above, has been removed to
within 0.004 inches. Leaving the core in the holder, the center of
the core is found with a center square and carefully marked and the
hardness is measured at the center mark according to ASTM D-2240.
Additional hardness measurements at any distance from the center of
the core can then be made by drawing a line radially outward from
the center mark, and measuring the hardness at any given distance
along the line, typically in 2 mm increments from the center. The
hardness at a particular distance from the center should be
measured along at least two, preferably four, radial arms located
180.degree. apart, or 90.degree. apart, respectively, and then
averaged. All hardness measurements performed on a plane passing
through the geometric center are performed while the core is still
in the holder and without having disturbed its orientation, such
that the test surface is constantly parallel to the bottom of the
holder, and thus also parallel to the properly aligned foot of the
durometer.
[0121] The outer surface hardness of a golf ball layer is measured
on the actual outer surface of the layer and is obtained from the
average of a number of measurements taken from opposing
hemispheres, taking care to avoid making measurements on the
parting line of the core or on surface defects, such as holes or
protrusions. Hardness measurements are made pursuant to ASTM D-2240
"Indentation Hardness of Rubber and Plastic by Means of a
Durometer." Because of the curved surface, care must be taken to
ensure that the golf ball or golf ball sub-assembly is centered
under the durometer indenter before a surface hardness reading is
obtained. A calibrated, digital durometer, capable of reading to
0.1 hardness units is used for the hardness measurements. The
digital durometer must be attached to, and its foot made parallel
to, the base of an automatic stand. The weight on the durometer and
attack rate conforms to ASTM D-2240.
[0122] In certain embodiments, a point or plurality of points
measured along the "positive" or "negative" gradients may be above
or below a line fit through the gradient and its outermost and
innermost hardness values. In an alternative preferred embodiment,
the hardest point along a particular steep "positive" or "negative"
gradient may be higher than the value at the innermost portion of
the inner core (the geometric center) or outer core layer (the
inner surface)--as long as the outermost point (i.e., the outer
surface of the inner core) is greater than (for "positive") or
lower than (for "negative") the innermost point (i.e., the
geometric center of the inner core or the inner surface of the
outer core layer), such that the "positive" and "negative"
gradients remain intact.
[0123] As discussed above, the direction of the hardness gradient
of a golf ball layer is defined by the difference in hardness
measurements taken at the outer and inner surfaces of a particular
layer. The center hardness of an inner core and hardness of the
outer surface of an inner core in a single-core ball or outer core
layer are readily determined according to the test procedures
provided above. The outer surface of the inner core layer (or other
optional intermediate core layers) in a dual-core ball are also
readily determined according to the procedures given herein for
measuring the outer surface hardness of a golf ball layer, if the
measurement is made prior to surrounding the layer with an
additional core layer. Once an additional core layer surrounds a
layer of interest, the hardness of the inner and outer surfaces of
any inner or intermediate layers can be difficult to determine.
Therefore, for purposes of the present invention, when the hardness
of the inner or outer surface of a core layer is needed after the
inner layer has been surrounded with another core layer, the test
procedure described above for measuring a point located 1 mm from
an interface is used. Likewise, the midpoint of a core layer is
taken at a point equidistant from the inner surface and outer
surface of the layer to be measured, most typically an outer core
layer. Once again, once one or more core layers surround a layer of
interest, the exact midpoint may be difficult to determine,
therefore, for the purposes of the present invention, the
measurement of "midpoint" hardness of a layer is taken within plus
or minus 1 mm of the measured midpoint of the layer.
[0124] Also, it should be understood that there is a fundamental
difference between "material hardness" and "hardness as measured
directly on a golf ball." For purposes of the present invention,
material hardness is measured according to ASTM D2240 and generally
involves measuring the hardness of a flat "slab" or "button" formed
of the material. Surface hardness as measured directly on a golf
ball (or other spherical surface) typically results in a different
hardness value. The difference in "surface hardness" and "material
hardness" values is due to several factors including, but not
limited to, ball construction (that is, core type, number of cores
and/or cover layers, and the like); ball (or sphere) diameter; and
the material composition of adjacent layers. It also should be
understood that the two measurement techniques are not linearly
related and, therefore, one hardness value cannot easily be
correlated to the other. Shore hardness (for example, Shore C or
Shore D hardness) was measured according to the test method ASTM
D-2240.
[0125] Compression.
[0126] As disclosed in Jeff Dalton's Compression by Any Other Name,
Science and Golf IV, Proceedings of the World Scientific Congress
of Golf (Eric Thain ed., Routledge, 2002) ("J. Dalton"), several
different methods can be used to measure compression, including
Atti compression, Riehle compression, load/deflection measurements
at a variety of fixed loads and offsets, and effective modulus. For
purposes of the present invention, compression refers to Soft
Center Deflection Index ("SCDI"). The SCDI is a program change for
the Dynamic Compression Machine ("DCM") that allows determination
of the pounds required to deflect a core 10% of its diameter. The
DCM is an apparatus that applies a load to a core or ball and
measures the number of inches the core or ball is deflected at
measured loads. A crude load/deflection curve is generated that is
fit to the Atti compression scale that results in a number being
generated that represents an Atti compression. The DCM does this
via a load cell attached to the bottom of a hydraulic cylinder that
is triggered pneumatically at a fixed rate (typically about 1.0
ft/s) towards a stationary core. Attached to the cylinder is an
LVDT that measures the distance the cylinder travels during the
testing timeframe. A software-based logarithmic algorithm ensures
that measurements are not taken until at least five successive
increases in load are detected during the initial phase of the
test. The SCDI is a slight variation of this set up. The hardware
is the same, but the software and output has changed. With the
SCDI, the interest is in the pounds of force required to deflect a
core x amount of inches. That amount of deflection is 10% percent
of the core diameter. The DCM is triggered, the cylinder deflects
the core by 10% of its diameter, and the DCM reports back the
pounds of force required (as measured from the attached load cell)
to deflect the core by that amount. The value displayed is a single
number in units of pounds.
[0127] Coefficient of Restitution ("COR").
[0128] The COR is determined according to a known procedure,
wherein a golf ball or golf ball sub-assembly (for example, a golf
ball core) is fired from an air cannon at two given velocities and
a velocity of 125 ft/s is used for the calculations. Ballistic
light screens are located between the air cannon and steel plate at
a fixed distance to measure ball velocity. As the ball travels
toward the steel plate, it activates each light screen and the
ball's time period at each light screen is measured. This provides
an incoming transit time period which is inversely proportional to
the ball's incoming velocity. The ball makes impact with the steel
plate and rebounds so it passes again through the light screens. As
the rebounding ball activates each light screen, the ball's time
period at each screen is measured. This provides an outgoing
transit time period which is inversely proportional to the ball's
outgoing velocity. The COR is then calculated as the ratio of the
ball's outgoing transit time period to the ball's incoming transit
time period (COR=V.sub.out/V.sub.in=T.sub.in/T.sub.out).
[0129] Density.
[0130] The density refers to the weight per unit volume (typically,
g/cm.sup.3) of the material and can be measured per ASTM
D-1622.
[0131] It is understood that the golf ball compositions,
constructions, and products described and illustrated herein
represent only some embodiments of the invention. It is appreciated
by those skilled in the art that various changes and additions can
be made to compositions, constructions, and products without
departing from the spirit and scope of this invention. It is
intended that all such embodiments be covered by the appended
claims.
* * * * *