U.S. patent application number 15/538981 was filed with the patent office on 2018-09-20 for water-based pressure-sensitive adhesive compositions.
The applicant listed for this patent is 3M INNOVATIVE PROPERTIES COMPANY. Invention is credited to Zhong Chen, John R. Jacobsen, Lili Qie, Jayshree Seth, Zhipeng Song.
Application Number | 20180265754 15/538981 |
Document ID | / |
Family ID | 55275157 |
Filed Date | 2018-09-20 |
United States Patent
Application |
20180265754 |
Kind Code |
A1 |
Qie; Lili ; et al. |
September 20, 2018 |
WATER-BASED PRESSURE-SENSITIVE ADHESIVE COMPOSITIONS
Abstract
A pressure-sensitive adhesive is provided that is a dried
product of a latex composition, which is formed from an emulsion
composition. The latex composition and the emulsion composition are
also provided. The emulsion composition has droplets that contain
various monomers plus a (meth)acrylate polymer dissolved in the
monomers. Additionally, an article containing a layer of the
pressure-sensitive adhesive and a method of forming the
pressure-sensitive adhesive are provided. The pressure-sensitive
adhesives often have both high peel adhesion and high shear
strength (i.e., high cohesive strength or high shear holding
power).
Inventors: |
Qie; Lili; (Woodbury,
MN) ; Chen; Zhong; (Woodbury, MN) ; Song;
Zhipeng; (Chadds Ford, PA) ; Jacobsen; John R.;
(Woodbury, MN) ; Seth; Jayshree; (Woodbury,
MN) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
3M INNOVATIVE PROPERTIES COMPANY |
St. Paul |
MN |
US |
|
|
Family ID: |
55275157 |
Appl. No.: |
15/538981 |
Filed: |
December 14, 2015 |
PCT Filed: |
December 14, 2015 |
PCT NO: |
PCT/US2015/065534 |
371 Date: |
June 22, 2017 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
62097784 |
Dec 30, 2014 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C08F 220/06 20130101;
C09J 151/003 20130101; C08F 265/06 20130101; C08F 2500/02 20130101;
C08F 2800/10 20130101; C08F 2/26 20130101; C09J 7/385 20180101;
C08F 220/1811 20200201; C08F 220/06 20130101; C08F 220/1811
20200201; C08F 220/06 20130101 |
International
Class: |
C09J 151/00 20060101
C09J151/00; C09J 7/38 20060101 C09J007/38; C08F 2/26 20060101
C08F002/26 |
Claims
1. An emulsion composition comprising: a) water; b) a polymerizable
surfactant having an unsaturated group that can undergo free
radical polymerization; c) a first monomer composition comprising
1) an alkyl (meth)acrylate having a linear or branched alkyl group
with at least six carbon atoms; and d) a second (meth)acrylate
polymer in an amount of 0.5 to 15 wt % based on a total weight of
monomers in the first monomer composition, wherein the second
(meth)acrylate polymer has a T.sub.g greater than or equal to
50.degree. C. and wherein the second (meth)acrylate polymer is
formed from a second monomer composition comprising 1) at least 50
weight percent of a cyclic alkyl (meth)acrylate based on a total
weight of monomers in the second monomer composition, wherein the
cyclic alkyl group has at least six carbon atoms; wherein the
emulsion has a first phase comprising the water and a second phase
dispersed as droplets within the first phase; and the droplets
comprise a mixture comprising 1) the second (meth)acrylate polymer;
and 2) at least 90 weight percent of the first monomer composition,
wherein the second (meth)acrylate polymer is not miscible with the
first phase and is dissolved in the first monomer composition
within the droplets.
2. The emulsion composition of claim 1, wherein the first monomer
composition further comprises a cyclic alkyl (meth)acrylate, a
polar monomer, or both.
3. The emulsion composition of claim 1, wherein the first monomer
composition comprises 60 to 98 weight percent of the alkyl
(meth)acrylate having a linear or branched alkyl group with at
least six carbon atoms, 1 to 30 weight percent of a cyclic alkyl
(meth)acrylate, and 1 to 10 weight percent of the polar
monomer.
4. The emulsion composition of claim 1, wherein the second monomer
composition comprises 50 to 100 weight percent of a cyclic alkyl
(meth)acrylate and 0 to 50 weight percent of an optional monomer
that is a polar monomer, an alkyl (meth)acrylate having a linear or
branched alkyl group, and a vinyl monomer that does not have a
(meth)acryloyl group, (meth)acrylamide, (meth)acrylonitrile, an
N-alkyl (meth)acrylamide, N,N-dialkyl (meth)acrylamide, or a
mixture thereof.
5. The emulsion composition of claim 1, wherein the second monomer
composition comprises 90 to 100 weight percent of the cyclic alkyl
(meth)acrylate and 0 to 10 percent polar monomer.
6. The emulsion composition of claim 1, wherein the first monomer
composition is different than the second monomer composition.
7. The emulsion composition of claim 1, wherein the second
(meth)acrylate polymer has a weight average molecular weight in a
range of 3,000 to 150,000 grams/mole.
8. The emulsion composition of claim 1, wherein the emulsion does
not contain a tackifier.
9. A latex composition comprising a polymerized product of the
emulsion composition of claim 1, wherein the latex composition
comprises polymeric latex particles.
10. The latex composition of claim 9, wherein the polymeric latex
particles have a single glass transition temperature as determined
using a Differential Scanning Calorimeter.
11. The latex composition of claim 9, wherein the second
(meth)acrylate polymer and a polymerized product of the first
monomer composition are together in the same polymeric
particles.
12. The latex composition of claim 9, further comprising a
tackifier that is water dispersible.
13. A pressure-sensitive adhesive comprising a dried product of the
latex composition of claim 9.
14. An article comprising: a) a substrate; and b) a first
pressure-sensitive adhesive layer positioned adjacent to a first
major surface of the substrate, wherein the first
pressure-sensitive adhesive layer comprises the pressure-sensitive
adhesive of claim 13.
15. A method of forming a pressure-sensitive adhesive, the method
comprising a) forming an emulsion composition of claim 1; b)
polymerizing the emulsion composition to form a latex composition
comprising polymeric latex particles; and c) drying the latex
composition to form the pressure-sensitive adhesive.
Description
CROSS REFERENCE TO RELATED APPLICATION
[0001] This application claims the benefit of U.S. Provisional
Patent Application No. 62/097784, filed Dec. 30, 2014, the
disclosure of which is incorporated by reference herein in its
entirety.
TECHNICAL FIELD
[0002] A pressure-sensitive adhesive, a latex composition used to
form the pressure-sensitive adhesive, and an emulsion composition
used to form the latex composition are provided.
BACKGROUND
[0003] Pressure-sensitive adhesive (PSA) tapes are virtually
ubiquitous in the home and workplace. In one of its simplest
configurations, a pressure-sensitive tape includes a backing layer
and an adhesive layer attached to the backing layer. According to
the Pressure-Sensitive Tape Council, pressure-sensitive adhesives
are known to possess properties including the following: (1)
aggressive and permanent tack, (2) adherence with no more than
finger pressure, (3) sufficient ability to hold onto an adherend,
and (4) sufficient cohesive strength to be removed cleanly from the
adherend. Materials that have been found to function well as PSAs
include polymers designed and formulated to exhibit the requisite
viscoelastic properties resulting in a desired balance of tack,
peel adhesion, and shear holding power. PSAs are characterized by
being normally tacky at room temperature (e.g., about 20.degree. C.
to 25.degree. C.). Materials that are merely sticky or that adhere
to a surface do not necessarily constitute a PSA; the term PSA
encompasses materials with additional viscoelastic properties.
[0004] Acrylic-based pressure-sensitive adhesives have been widely
used. These pressure-sensitive adhesive compositions can be
prepared with or without an organic solvent. PSA compositions
containing organic solvents, while currently dominant in the
marketplace, are decreasing in importance due to various issues
such as pollution, high energy consumption, and flammability
associated with the use of organic solvents. That is, the adhesive
industry is increasingly focused on adhesive compositions that have
either low or no organic solvent content.
[0005] Some such adhesive compositions can, for example, be
prepared from water-based latex compositions formed by emulsion
polymerization. Such adhesives are described, for example, in U.S.
Pat. No. 5,686,518 (Fontenot et al.), U.S. Pat. No. 6,710,128
(Helmer et al.), U.S. Pat. No. 6,511,744 (Centner et al.), U.S.
Pat. No. 6,048,611 (Lu et al.), U.S. Pat. No. 4,912,169 (Whitmire
et al.), U.S. Pat. No. 6,657,011 (Lau et al.), U.S. Pat. No.
8,258,240 (Suzuki et al.), and U.S. Patent Application Publication
No. 2010/0081764 (Ouzineb et al.).
SUMMARY
[0006] A pressure-sensitive adhesive is provided that is the dried
product of a latex composition, which is formed from an emulsion
composition. The latex composition and the emulsion composition are
also provided. Additionally, an article containing the
pressure-sensitive adhesive and a method of forming the
pressure-sensitive adhesive are provided. The pressure-sensitive
adhesive has a good balance of peel adhesion and shear strength
(i.e., cohesion) at both room temperature (e.g., about 20.degree.
C. to about 25.degree. C.) and elevated temperatures (e.g., around
about 70.degree. C.), particularly when adhered to low surface
energy substrates.
[0007] In a first aspect, an emulsion composition is provided that
contains a) water, b) a polymerizable surfactant having an
unsaturated group that can undergo free radical polymerization, c)
a first monomer composition, and d) a second (meth)acrylate
polymer. The first monomer composition includes an alkyl
(meth)acrylate having a linear or branched alkyl group with at
least six carbon atoms. The second (meth)acrylate polymer is
present in an amount of 0.5 to 15 weight percent based on a total
weight of monomers in the first monomer composition and has a glass
transition temperature greater than or equal to 50.degree. C. The
second (meth)acrylate polymer is formed from a second monomer
composition containing at least 50 weight percent of a cyclic alkyl
(meth)acrylate based on a total weight of monomers in the second
monomer composition, wherein the cyclic alkyl group has at least
six carbon atoms. The emulsion composition contains a first phase
that includes the water and a second phase dispersed as droplets
within the first phase. The droplets contain a mixture of i) at
least 90 weight percent of the first monomer composition and ii)
the second (meth)acrylate polymer. The second (meth)acrylate
polymer is not miscible with the first phase and is dissolved in
the first monomer composition within the droplets.
[0008] In a second aspect, a latex composition is provided that
contains a reaction product (i.e., polymerized product) of an
emulsion composition, wherein the latex composition contains
polymeric latex particles. The emulsion composition is the same as
described above.
[0009] In a third aspect, a pressure-sensitive adhesive is provided
that is a dried product of a latex composition. The latex
composition contains a reaction product (i.e., polymerized product)
of an emulsion composition, wherein the latex composition contains
polymeric latex particles. The emulsion composition is the same as
described above.
[0010] In a fourth aspect, an article is provided. The article
contains a substrate and a first pressure-sensitive adhesive layer
positioned adjacent to (and adhered to directly or indirectly) a
first major surface of the substrate. The pressure-sensitive
adhesive layer is a dried product of a latex composition. The latex
composition contains a reaction product (i.e., polymerized product)
of an emulsion composition, wherein the latex composition contains
polymeric latex particles. The emulsion composition is the same as
described above.
[0011] In a fifth aspect, a method of forming a pressure-sensitive
adhesive is provided. The method includes a) forming an emulsion
composition as described above; b) polymerizing the emulsion
composition to form a latex composition comprising polymeric latex
particles; and c) drying the latex composition to form the
pressure-sensitive adhesive.
BRIEF DESCRIPTION OF THE DRAWINGS
[0012] FIG. 1 is the Modulated Differential Scanning Calorimetry
plot from the second heating (2H) cycle for the polymeric latex
particles of Example 1. Heat flow is plotted as a function of
temperature in a nitrogen atmosphere.
[0013] FIG. 2 is the Modulated Differential Scanning Calorimetry
plot from the second heating (2H) cycle for the polymeric latex
particles of Example 2. Heat flow is plotted as a function of
temperature in a nitrogen atmosphere.
DETAILED DESCRIPTION
[0014] A pressure-sensitive adhesive is provided that is a dried
product of a latex composition, which is formed from an emulsion
composition. The latex composition and the emulsion composition are
also provided. The emulsion composition has droplets suspended in a
first phase that is mainly water. The droplets contain various
monomers plus a (meth)acrylate polymer dissolved in the monomers.
The content of the droplets in the emulsion composition are
polymerized to form polymeric latex particles in the latex
composition. A pressure-sensitive adhesive is provided by drying
the latex composition. Additionally, an article containing a layer
of the pressure-sensitive adhesive and a method of forming the
pressure-sensitive adhesive are provided.
[0015] The pressure-sensitive adhesives often have a good balance
between peel strength and shear strength (i.e., cohesive strength
or shear holding power), particularly when adhered to low surface
energy surfaces. It can be a challenge to make pressure-sensitive
adhesives with this good balance of adhesive properties. Increasing
the peel strength often is accompanied by a decrease in shear
strength while increasing the shear strength often is accompanied
by a decrease in peel strength. The addition of the second
(meth)acrylate polymer into the emulsion composition contributed to
the formation of pressure-sensitive adhesives with the improved
balance between peel strength and sheer strength. That is, shear
strength could be improved while maintaining good peel strength (or
without unduly sacrificing peel strength) and peel strength could
be improved while maintaining good shear strength (or without
unduly sacrificing shear strength).
[0016] As used herein, the terms "polymer" and "polymeric" and
"polymeric material" are used interchangeably to refer to a
homopolymer, copolymer, terpolymer, and the like.
[0017] As used herein, the term "(meth)acrylate" refers to both
methacrylate and acrylate monomers, polymeric materials derived
from these monomers, or both. Likewise, the term "(meth)acrylic"
refers to both acrylic and methacrylic materials, the term
"(meth)acrylamide" refers to both acrylamide and methacrylamide,
and the term "(meth)acrylonitrile" refers to both methacrylonitrile
and acrylonitrile.
[0018] As used herein, the term "(meth)acrylate polymer" refers to
a polymeric material formed from one or more ethylenically
unsaturated monomers, wherein greater than 50 weight percent of the
monomers have an ethylenically unsaturated group that is a
(meth)acryloyl group of formula H.sub.2C.dbd.CR.sup.a--(CO)-- where
Ra is hydrogen or methyl and --(CO)-- is a carbonyl group. Some
example (meth)acrylate polymers are formed from monomer
compositions having greater than 60 weight percent, greater than 70
weight percent, greater than 80 weight percent, greater than 90
weight percent, greater than 95 weight percent, greater than 98
weight percent, or greater than 99 weight percent monomers having a
(meth)acryloyl group. The weight percent is based on the total
weight of monomers in the monomer composition used to form the
(meth)acrylate polymer.
[0019] The term "glass transition temperature" or "T.sub.g" refers
to the temperature at which a material changes from a glassy state
to a rubbery state. In this context, the term "glassy" means that
the material is hard and brittle (and therefore relatively easy to
break) while the term "rubbery" means that the material is elastic
and flexible. For polymeric materials, the T.sub.g is the critical
temperature that separates their glassy and rubbery behaviors. If a
polymeric material is at a temperature below its T.sub.g,
large-scale molecular motion is severely restricted because the
material is essentially frozen. On the other hand, if the polymeric
material is at a temperature above its T.sub.g, molecular motion on
the scale of its repeat unit takes place, allowing it to be soft or
rubbery. Any reference herein to the T.sub.g of a monomer refers to
the T.sub.g of a homopolymer formed from that monomer. The glass
transition temperature of a polymeric material is often determined
using methods such as Differential Scanning Calorimetry (e.g.,
Modulated Differential Scanning Calorimetry). Alternatively, the
glass transition of a polymeric material can be calculated using
the Fox Equation if the amount and T.sub.g of each monomer used to
form the polymeric material are known.
[0020] When referring to a range, the endpoints of the range are
considered to be in the range. For example, the expressions "in a
range from x to y", "in a range of x to y", "in an amount from x to
y", "in an amount of x to y", or similar expressions include the
endpoints x and y.
[0021] As used herein, the term "and/or" such as in the expression
A and/or B means A alone, B alone, or both A and B.
[0022] The emulsion composition that is used to form the latex
composition and, ultimately, the pressure-sensitive adhesive
contains a) water, b) a polymerizable surfactant having an
unsaturated group that can undergo a free radical polymerization
reaction (e.g., an ethylenically unsaturated group), c) a first
monomer composition, and d) a second (meth)acrylate polymer. The
emulsion has a first phase that includes water and a second phase
dispersed as droplets within the first phase. The polymerizable
surfactant is typically predominately (e.g., at least 95 weight
percent or more, at least 97 weight percent, at least 98 weight
percent, at least 99 weight percent, at least 99.5 weight percent,
at least 99.8 weight percent, or at least 99.9 weight percent)
present in the first phase and/or at the interface between the
droplets and the first phase. The second (meth)acrylate polymer is
dissolved in the monomers of the first monomer composition within
the droplets of the second phase of the emulsion composition. The
second (meth)acrylate polymer typically is not miscible with the
first phase of the emulsion composition. The second (meth)acrylate
polymer is formed from a second monomer composition that is
different than the first monomer composition contained in the
emulsion composition.
[0023] A major component of the emulsion composition is water. The
percent solids of the emulsion composition are often up to 70
weight percent or higher such as up to 75 weight percent. If the
percent solids are higher, the viscosity of the emulsion may be too
high to adequately disperse the droplets. In some embodiments, the
percent solids are up to 65 weight percent, up to 60 weight
percent, up to 55 weight percent, or up to 50 weight percent. The
percent solids are typically at least 10 weight percent. If the
solids are lower, the efficiency of preparation of the latex
particles may be unacceptably low. In some embodiments, the percent
solids are at least 15 weight percent, at least 20 weight percent,
at least 25 weight percent, at least 30 weight percent, at least 35
weight percent, at least 40 weight percent, or at least 45 weight
percent. In some examples, the percent solids are in a range of 10
to 75 weight percent, 10 to 70 weight percent, 20 to 70 weight
percent, 30 to 70 weight percent, 40 to 70 weight percent, or 40 to
60 weight percent. The percent solids are based on the total weight
of the emulsion composition.
[0024] The portion of the emulsion composition that is not a solid
is typically water. Thus, the water content of the emulsion is
often at least 25 weight percent or at least 30 weight percent. In
some embodiments, the water content can be up to 90 weight percent,
up to 85 weight percent, up to 80 weight percent, up to 75 weight
percent, up to 70 weight percent, up to 65 weight percent, up to 60
weight percent, or up to 55 weight percent. The water content can
be at least 35 weight percent, at least 40 weight percent, at least
45 weight percent, or at least 50 weight percent. In some examples,
the water content is in a range of 25 to 90 weight percent, 30 to
90 weight percent, 30 to 80 weight percent, 30 to 70 weight
percent, 30 to 60 weight percent, or 40 to 60 weight percent. The
amount of water is based on the total weight of the emulsion
composition.
[0025] Some of the water can be replaced with a polar organic
solvent that is miscible with water such as a polar solvent. If
present, no more than 20 weight percent, no more than 15 weight
percent, no more than 10 weight percent, or no more than 5 weight
percent of the first phase is the water-miscible, polar organic
solvent. The polar solvent is often an alcohol such as an alcohol
having 1 to 10 carbon atoms, 1 to 6 carbon atoms, or 1 to 4 carbon
atoms. In many embodiments, no water-miscible, polar organic
solvent is purposefully added to the emulsion composition but may
be present as a contaminant or diluent in one of the other
components.
[0026] The emulsion composition contains a polymerizable
surfactant. As used herein, the term "polymerizable surfactant"
refers to a surfactant with a polymerizable group, which is an
unsaturated group that can undergo a free radical polymerization
reaction. In the emulsion composition, the polymerizable surfactant
is typically in the first phase and/or at the interface between
first phase and the droplets that are suspended in the first phase.
The polymerizable surfactant facilitates the formation of a latex
composition having good stability (e.g., the polymeric latex
particles remain suspended and do not coalesce). The polymerizable
surfactant may become part of the polymeric latex particles during
the polymerization reaction of the emulsion composition.
[0027] Using a polymerizable surfactant rather than a surfactant
without a polymerizable group tends to improve the peel strength
and the shear strength of the resulting pressure-sensitive
adhesive. Under high humidity conditions, a surfactant without a
polymerizable group tends to migrate to the surface of a
pressure-sensitive adhesive. The presence of the surfactant on the
surface of the pressure-sensitive adhesive can decrease the
adhesive properties of the pressure-sensitive adhesive. In
contrast, the polymerizable surfactant can polymerize with the
monomers in the first monomer composition and become part of the
polymeric latex particles. Polymerization into the polymeric latex
particle tends to restrict the mobility of the surfactant.
[0028] Example polymerizable surfactants include propenyl
polyoxyethylene alkylphenyl compounds such as those commercially
available from Montello, Inc. (Tulsa, Okla., USA) under the trade
designation NOIGEN RN (e.g., RN-10, RN-20, RN-30, RN-40, and
RN-5065), which have a structure shown below where n is at least 2
and where x is an integer such as one close to or equal to 9.
##STR00001##
Other example polymerizable surfactants include propenyl
polyoxyethylene alkylphenyl ether ammonium sulfate compounds such
as those commercially available from Montello, Inc. under the trade
designation HITENOL BC (e.g., BC-10, BC-1025, BC-20, BC-2020, and
BC-30), which have a structure shown below where n is at least 2
and where x is an integer such as one close to or equal to 9.
##STR00002##
Another example polymerizable surfactant is sodium dodecylallyl
sulfosuccinate,
CH.sub.3--(CH.sub.2).sub.11--O--(CO)--CH.sub.2--CH(SO.sub.3Na)--(CO)--O---
CH.sub.2--CH.dbd.CH.sub.2, which may be commercially available
under the trade designation TREM LF40 from Cognis Corporation
(North Rhime-Westphalia, Germany). Yet other example polymerizable
surfactants are phosphate esters such as those commercially
available from Croda (Edison, NY, USA) under the trade designation
MAXENUL (e.g., MAXEMUL 6106 and 6112).
[0029] The polymerizable surfactant is typically used in an amount
up to about 2 weight percent, up to 1.8 weight percent, or up to
1.5 weight percent. The amount of the polymerizable surfactant is
usually at least 0.5 weight percent, at least 0.7 weight percent,
or at least 1 weight percent. The weight percents are based on the
total weight of monomers in the first monomer composition.
[0030] The emulsion composition contains a first monomer
composition. The first monomer composition is typically selected
such that the polymerized product of the first monomer composition,
which is referred to as the "first (meth)acrylate polymer", has a
glass transition temperature no greater than 20.degree. C., no
greater than 10.degree. C., no greater than 0.degree. C., no
greater than -10.degree. C., or no greater than -20.degree. C.
[0031] The first monomer composition in the emulsion composition
typically includes an alkyl (meth)acrylate having a linear or
branched alkyl group with at least six carbon atoms. In many
embodiments, other optional monomers can be included provided that
the polymerized product has a sufficiently low glass transition
temperature. The amount and type of any optional monomers are
selected so that at least 90 weight percent of the monomers within
the first monomer composition are within droplets dispersed in the
first phase of the emulsion composition. The alkyl (meth)acrylate
monomer having a linear or branched alkyl group with at least six
carbon atoms is likely to have a low solubility in the first phase
and is likely to be predominately (e.g., at least 95 weight percent
or more, at least 97 weight percent, at least 98 weight percent, at
least 99 weight percent, at least 99.5 weight percent, at least
99.8 weight percent, or at least 99.9 weight percent) in the
droplets, which are dispersed in the first phase. If optional polar
monomers or other optional monomers are included in the first
monomer composition that are less hydrophobic that the alkyl
(meth)acrylate monomer having a linear or branched alkyl group with
at least six carbon atoms, the solubility of these optional
monomers may be greater in water (e.g., in the first phase)
compared to the alkyl (meth)acrylate monomer having a linear or
branched alkyl group with at least six carbon atoms. As
polymerization occurs within the droplet, some of these optional
monomers in the first phase may diffuse into the droplet and become
part of polymeric latex particles that are formed.
[0032] The alkyl (meth)acrylate in the first monomer composition
has a linear or branched alkyl group with at least six carbon
atoms. Alkyl (meth)acrylate monomers with an alkyl group having
less than six carbon atoms are less hydrophobic and are less likely
to reside predominately within the droplets. In some embodiments,
the alkyl group can have at least 8 carbon atoms, at least 10
carbon atoms, or at least 12 carbon atoms. The alkyl group of the
alkyl (meth)acrylate can have up to 28 carbon atoms or more, up to
24 carbon atoms, up to 20 carbon atoms, or up to 18 carbon atoms.
In many embodiments, particularly when the number of carbon atoms
is greater than 12, the alkyl group is branched. Some alkyl
(meth)acrylates having an alkyl group greater than 12 carbon atoms
can crystallize if the alkyl group is linear. Crystallization of
the alkyl (meth)acrylate is not desirable in the emulsion
composition.
[0033] Example alkyl (meth)acrylate monomers having a linear or
branched alkyl group with at least six carbon atoms for use in the
first monomer composition include, but are not limited to, n-hexyl
acrylate, 4-methyl-2-pentyl acrylate, 3-methylpentyl acrylate,
2-ethylbutyl acrylate, 2-ethylhexyl acrylate, 2-methylhexyl
acrylate, n-octyl acrylate, isooctyl acrylate, 2-octyl acrylate,
isononyl acrylate, isoamyl acrylate, n-decyl acrylate, isodecyl
acrylate, 2-propylheptyl acrylate, isotridecyl acrylate, isostearyl
acrylate, 2-octyldecyl acrylate, lauryl acrylate, heptadecanyl
acrylate, n-hexyl methacrylate, isodecyl methacrylate, 2-ethylhexyl
methacrylate, isooctyl methacrylate, and lauryl methacrylate.
[0034] Still others alkyl (meth)acrylates having a linear or
branched alkyl group with at least six carbon atoms for use in the
first monomer composition are of Formula (I).
##STR00003##
In Formula (I), group R.sup.3 is hydrogen or methyl and groups
R.sup.1 and R.sup.2 are each independently a linear or branched
alkyl group having 4 to 14 carbon atoms. These monomers are often
formed from a Guerbet alcohol, which is a 2-alkyl alkanol. Example
monomers of Formula (I) include 2-butyloctyl acrylate, 2-butyldecyl
acrylate, 2-hexyloctyl acrylate, 2-hexyldecyl acrylate,
2-tetradecyloctadecyl acrylate, 2-dodecylhexadecyl acrylate,
2-decyltetradecyl acrylate, 2-octyldodecyl acrylate, 2-hexyldecyl
acrylate, 2-octyldecyl acrylate, 2-hexyldodecyl acrylate, and
2-octyldodecyl acrylate.
[0035] The first monomer composition typically contains at least 50
weight percent alkyl (meth)acrylate having a linear or branched
alkyl group with at least six carbon atoms. The first monomer
composition often contains at least 60 weight percent, at least 70
weight percent, or at least 80 weight percent of the alkyl
(meth)acrylate having a linear or branched alkyl group with at
least six carbon atoms. The amount of the alkyl (meth)acrylate
having an alkyl group with at least six carbon atoms can be up to
100 weight percent. The first monomer composition often contains up
to 95 weight percent, up to 90 weight percent, or up to 85 weight
percent of the alkyl (meth)acrylate having a linear or branched
alkyl group with at least six carbon atoms. In some embodiments,
the amount of the alkyl (meth)acrylate is in a range of 50 to 100
weight percent, in a range of 50 to 95 weight percent, in a range
of 60 to 95 weight percent, in a range of 70 to 95 weight percent,
or in a range of 75 to 90 weight percent. The amount of the alkyl
(meth)acrylate is based on a total weight of monomers in the first
monomer composition.
[0036] In many embodiments, the alkyl (meth)acrylate having a
linear or branched alkyl group with at least six carbon atoms is
combined with an optional cyclic alkyl (meth)acrylate within the
first monomer composition. As used herein, the term "cyclic alkyl"
refers to a mono-cyclic alkyl, a bicyclic alkyl, or a tricyclic
alkyl group. Examples of cyclic alkyl (meth)acrylate monomers
include, but are not limited to, isobornyl (meth)acrylate,
3,3,5-trimethylcyclohexyl (meth)acrylate, cyclohexyl
(meth)acrylate, adamantyl (meth)acrylate 3,5-dimethyladamantyl
(meth)acrylate, and 4-tert-butylcylcohexyl (meth)acrylate.
[0037] Some of these cyclic alkyl (meth)acrylates have a high glass
transition temperature (such as at least 80.degree. C.) and must be
used in sufficiently low amounts so that the polymerized product of
the first monomer composition has a glass transition temperature no
greater than 20.degree. C. The presence of the cyclic alkyl
(meth)acrylate can enhance the solubility of the second
(meth)acrylate polymer within the first monomer composition. In
many embodiments that contain the optional cyclic alkyl
(meth)acrylate, the first monomer composition contains at least 0.5
weight percent, at least 1 weight percent, at least 2 weight
percent, at least 5 weight percent, or at least 10 weight percent
of the cyclic alkyl (meth)acrylate. The amount of the cyclic alkyl
(meth)acrylate can be up to 30 weight percent, up to 25 weight
percent, up to 20 weight percent, or up to 15 weight percent. For
example, the amount of the cyclic alkyl (meth)acrylate in the first
monomer composition can be in a range of 0 to 30 weight percent, 1
to 30 weight percent, 0 to 20 weight percent, 1 to 20 weight
percent, or 5 to 20 weight percent. The weight percent of the
cyclic alkyl (meth)acrylate is based on a total weight of monomers
in the first monomer composition.
[0038] The first monomer composition optionally can include a polar
monomer such as an optional acid-containing monomer (i.e., a
monomer with an acidic group) or an optional hydroxyl-containing
monomer (i.e., a monomer with a hydroxyl group). These optional
monomers can be added to increase the cohesive strength of the
final polymeric material. Suitable optional acid-containing
monomers include, but are not limited to, (meth)acrylic acid,
itaconic acid, maleic acid, 2-carboxyethyl acrylate, crotonic acid,
citraconic acid, maleic acid, maleic anhydride (which hydrolyzes to
have two carboxylic acid groups), oleic acid, and
mono-2-acryloyloxyethyl succinate. Suitable optional
hydroxyl-containing monomers include, but are not limited to,
hydroxyalkyl (meth)acrylates (e.g., 2-hydroxyethyl (meth)acrylate,
2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, and
4-hydroxybuty(meth)acrylate), or hydroxyalkyl (meth)acrylamides
(e.g., 2-hydroxyethyl (meth)acrylamide or 3-hydroxypropyl
(meth)acrylamide). In many embodiments, the polar monomer is an
acidic monomer. In many embodiments, the optional polar monomer has
a (meth)acryloyl group. The first monomer composition typically
contains 0 to 15 weight percent, 0.5 to 15 weight percent, 1 to 15
weight percent, 0 to 10 weight percent, 0.5 to 10 weight percent, 1
to 10 weight percent, 0 to 5 weight percent, 0.5 to 5 weight
percent, or 1 to 5 weight percent of the optional polar monomer.
The amount of the optional polar monomer used is selected so that
at least 85 weight percent of the monomers in the first monomer
composition are within the droplets of the second phase. The weight
percent is based on the total weight of monomers within the first
monomer composition.
[0039] The first monomer composition optionally can contain up to
20 weight percent alkyl (meth)acrylate having an alkyl group with
one to five carbon atoms. The alkyl group can be linear or
branched. If larger amounts of an alkyl (meth)acrylate having an
alkyl group with one to five carbon atoms are used, too much of the
overall first monomer composition may be in the first phase rather
than in the droplets. In many embodiments, the amount of alkyl
(meth)acrylate having an alkyl group with one to five carbon atoms
is present in an amount no greater than 15 weight percent, no
greater than 10 weight percent, or no greater than 5 weight
percent. In some embodiments, there is no alkyl (meth)acrylate
having an alkyl group with one to five carbon atoms. In other
embodiments, the first monomer composition can contain at least 0.5
weight percent, at least 1 weight percent, at least 2 weight
percent, or at least 5 weight percent of the alkyl (meth)acrylate
having an alkyl group with one to five carbon atoms. The amount of
the alkyl (meth)acrylate with an alkyl group having one to five
carbon atoms is usually in a range of 0 to 20 weight percent, 1 to
20 weight percent, 5 to 20 weight percent, 10 to 20 weight percent,
0 to 15 weight percent, 1 to 15 weight percent, 5 to 15 weigh
percent, 0 to 10 weight percent, 1 to 10 weight percent, 0 to 5
weight percent, or 1 to 5 weight percent. The amount of the alkyl
(meth)acrylate is based on a total weight of monomers in the first
monomer composition.
[0040] The first monomer composition can contain 50 to 100 weight
percent of the alkyl (meth)acrylate having a linear or branched
alkyl group with at least six carbon atoms, 0 to 30 weight percent
of a cyclic alkyl (meth)acrylate, 0 to 20 weight percent of the
alkyl (meth)acrylate having an alkyl group with one to five carbon
atoms, and 0 to 15 weight percent of a polar monomer. In some
examples, the first monomer composition contains 60 to 98 weight
percent of the alkyl (meth)acrylate having a linear or branched
alkyl group with at least six carbon atoms, 1 to 25 weight percent
of a cyclic alkyl (meth)acrylate, 0 to 15 weight percent of the
alkyl (meth)acrylate having an alkyl group with one to five carbon
atoms, and 1 to 15 weight percent of the polar monomer. In some
examples, the first monomer composition contains 70 to 98 weight
percent of the alkyl (meth)acrylate having a linear or branched
alkyl group with at least six carbon atoms, 1 to 20 weight percent
of a cyclic alkyl (meth)acrylate, 0 to 10 weight percent of the
alkyl (meth)acrylate having an alkyl group with one to five carbon
atoms, and 1 to 10 weight percent of the polar monomer.
[0041] In other examples, the first monomer composition contains 60
to 98 weight percent of the alkyl (meth)acrylate having a linear or
branched alkyl group with at least six carbon atoms, 1 to 30 weight
percent of a cyclic alkyl (meth)acrylate, and 1 to 10 weight
percent of the polar monomer. For example, the first monomer
composition contains 70 to 98 weight percent of the alkyl
(meth)acrylate having a linear or branched alkyl group with at
least six carbon atoms, 1 to 20 weight percent of a cyclic
(meth)acrylate, and 1 to 10 weight percent of the polar monomer
such as a (meth)acrylic acid.
[0042] The emulsion composition has droplets dispersed in the first
phase. Prior to polymerization of the emulsion composition to form
a latex composition, the droplets contain a solution of the second
(meth)acrylate polymer dissolved in the components of the first
monomer composition that are in the droplets. Typically, at least
90 weight percent of the monomers in the first monomer composition
are within the droplets of the emulsion and no more than 10 weight
percent of the monomers of the first composition are within the
first phase of the emulsion composition. Polar monomers or other
monomers that are less hydrophobic than the alkyl (meth)acrylate
having a linear or branched alkyl group with at least six carbon
atoms may be distributed within both the droplets and the first
phase. As polymerization proceeds, any of these polar monomers or
less hydrophobic monomers in the first phase may diffuse into the
droplets and become part of the polymeric latex particles. In some
embodiments, at least 92 weight percent, at least 95 weight
percent, at least 98 weight percent, or at least 99 weight percent
of the monomers in the first monomer composition are in the
droplets of the emulsion composition.
[0043] The second (meth)acrylate polymer is selected so that is can
be dissolved in the first monomer composition within the droplets
of the emulsion composition and so that it is not miscible with the
first phase. The second (meth)acrylate polymer is formed prior to
dissolution by the components of the first monomer composition
within the droplets. The second (meth)acrylate polymer facilitates
the formation of stable droplets within the first phase of the
emulsion composition.
[0044] The second (meth)acrylate polymer is typically formed from a
second monomer composition. The second monomer composition is
selected to provide a second (meth)acrylate polymer that can be
dissolved in the first monomer composition. The second monomer
composition is not identical to the first monomer composition.
Additionally, it is often desirable that the second (meth)acrylate
polymer be distributed fairly uniformly throughout the droplets
within the emulsion composition. That is, it is often desirable
that the second (meth)acrylate polymer and the polymeric material
formed by polymerization of the first monomer composition (i.e.,
the first (meth)acrylate polymer) are both fairly uniformly
distributed throughout the resulting polymeric latex particles even
though their compositions are not identical. The first
(meth)acrylate polymer and the second (meth)acrylate polymer are
within the same latex particles.
[0045] The second monomer composition is selected to provide a
second (meth)acrylate polymer that has a glass transition
temperature that is at least 50.degree. C. as measured using
Differential Scanning Calorimetry (e.g., Modulated Differential
Calorimetry). For example, the glass transition temperature is at
least 60.degree. C., at least 70.degree. C., at least 80.degree.
C., at least 90.degree. C., or at least 100.degree. C. The glass
transition temperature can be up to 250.degree. C., up to
200.degree. C., or up to 175.degree. C. Often, the glass transition
temperature is no greater than 150.degree. C., no greater than
140.degree. C., no greater than 130.degree. C., or no greater than
120.degree. C.
[0046] The second monomer composition usually includes at least 50
weight percent of a cyclic alkyl (meth)acrylate based on a total
weight of monomers in the second monomer composition, wherein the
cyclic group has at least six carbon atoms. For example, the cyclic
group can have up to 12 carbon atoms, up to 10 carbon atoms, or up
to 8 carbon atoms. Examples of cyclic alkyl (meth)acrylate monomers
include, but are not limited to, isobornyl (meth)acrylate,
3,3,5-trimethylcyclohexyl (meth)acrylate, cyclohexyl
(meth)acrylate, adamantyl (meth)acrylate, 3,5-dimethyladamantyl
(meth)acrylate, and 4-tert-butylcylcohexyl (meth)acrylate.
[0047] In many embodiments, the cyclic alkyl (meth)acrylate has a
glass transition temperature that is at least 80.degree. C. when
polymerized as a homopolymer. Suitable monomers include, but are
not limited to, isobornyl (meth)acrylate, 3,3,5-trimethylcyclohexyl
methacrylate, cyclohexyl methacrylate, 3,5-dimethyladamantyl
acrylate, and 4-tert-butylcylcohexyl methacrylate.
[0048] The cyclic alkyl (meth)acrylate can be the only monomer in
the second monomer composition or it can be combined with other
optional monomers provided that 1) the resulting second
(meth)acrylate polymer has a glass transition temperature equal to
at least 50.degree. C. as measured using Differential Scanning
Calorimetry (e.g., Modulated Differential Scanning Calorimetry), 2)
the resulting second (meth)acrylate polymer can be dissolved in the
first monomer composition, and 3) the second (meth)acrylate polymer
remains within the droplets of the emulsion composition and is not
miscible with the first phase of the emulsion composition. These
optional monomers include, for example, a polar monomer, an alkyl
(meth)acrylate having a linear or branched alkyl group,
(meth)acrylamide, a (meth)acrylonitrile, an N-alkyl
(meth)acrylamide, an N,N-dialkyl (meth)acrylamide, and a vinyl
monomer that does not have a (meth)acryloyl group.
[0049] The second monomer composition can optionally include a
polar monomer such as an optional acid-containing monomer (i.e., a
monomer with an acidic group) or an optional hydroxyl-containing
monomer (i.e., a monomer with a hydroxyl group). Suitable optional
acid-containing monomers include, but are not limited to,
(meth)acrylic acid, itaconic acid, maleic acid, 2-carboxyethyl
acrylate, crotonic acid, citraconic acid, maleic acid, maleic
anhydride (which hydrolyzes to have two carboxylic acid groups),
oleic acid, and mono-2-acryloyloxyethyl succinate. Suitable
optional hydroxyl-containing monomers include, but are not limited
to, hydroxyalkyl (meth)acrylates (e.g., 2-hydroxyethyl
(meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl
(meth)acrylate, and 4-hydroxybutyl (meth)acrylate), or hydroxyalkyl
(meth)acrylamides (e.g., 2-hydroxyethyl (meth)acrylamide or
3-hydroxypropyl (meth)acrylamide). In many embodiments, the
optional polar monomer has a (meth)acryloyl group. In many
embodiments, the optional polar monomer is (meth)acrylic acid. The
second monomer composition typically contains 0 to 10 weight
percent, 1 to 10 weight percent, 0 to 5 weight percent, or 1 to 5
weight percent of the optional acid-containing monomer and/or
optional hydroxyl-containing monomer. The weight percent values are
based on the total weight of monomers within the second monomer
composition.
[0050] The second monomer composition can optionally include an
alkyl (meth)acrylate having a linear or branched alkyl group.
Example monomers include methyl (meth)acrylate, ethyl
(meth)acrylate, isopropyl (meth)acrylate, isobutyl (meth)acrylate,
n-butyl (meth)acrylate, teat-butyl (meth)acrylate, n-pentyl
(meth)acrylate, isopentyl (meth)acrylate, 2-methylbutyl
(meth)acrylate, n-hexyl (meth)acrylate, 4-methyl-2-pentyl
(meth)acrylate, 2-methylhexyl (meth)acrylate, 2-ethylhexyl
(meth)acrylate, isooctyl (meth)acrylate, n-octyl (meth)acrylate,
2-octyl (meth)acrylate, isononyl (meth)acrylate, isoamyl
(meth)acrylate, n-decyl (meth)acrylate, isodecyl (meth)acrylate,
2-propylheptyl (meth)acrylate, isotridecyl (meth)acrylate, and
lauryl (meth)acrylate. The amount of the alkyl methacrylate is
often limited by the desired glass transition temperature of the
second (meth)acrylate polymer.
[0051] Other suitable optional monomers for use in second monomer
composition include (meth)acrylamide, (meth)acrylonitrile, an
N-alkyl (meth)acrylamide having an alkyl group with 1 to 10 carbon
atoms (e.g., 2 to 10 carbon atoms or 4 to 10 carbon atoms) such as
N-octyl acrylamide, N-isopropyl acrylamide, or N-tert-butyl
acrylamide, or an N,N-dialkyl (meth)acrylamide having alkyl groups
with 1 to 10 carbon atoms (e.g., 1 to 6 carbon atoms or 1 to 4
carbon atoms) such as N,N-dimethyl acrylamide.
[0052] Still other optional monomers can be included in the second
monomer composition provided that there is suitable compatibility
between the resulting second (meth)acrylate polymer and first
monomer composition within the emulsion composition and provided
that the second (meth)acrylate polymer can be dissolved within the
droplets of the emulsion composition. Examples of other optional
monomers include various vinyl monomers, wherein the vinyl group is
not a (meth)acryloyl group. Optional vinyl monomers include, for
example, vinyl esters such as vinyl butyrate, and various vinyl
non-aromatic heterocyclic monomers such as N-vinyl pyrollidone and
N-vinyl caprolactam.
[0053] A crosslinking monomer typically is not included in the
second monomer composition. A crosslinked (meth)acrylate polymer
would be difficult to dissolve in the first monomer composition. In
many embodiments, the second monomer composition does not contain
an aromatic monomer (i.e., a monomer with an aromatic group such as
a styrenic monomer or aryl (meth)acrylate).
[0054] In many embodiments, the second monomer composition includes
50 to 100 weight percent of a cyclic alkyl (meth)acrylate and 0 to
50 percent optional monomers such as those selected from a polar
monomer, an alkyl (meth)acrylate having a linear or branched alkyl
group, and a vinyl monomer that does not have a (meth)acryloyl
group, (meth)acrylamide, (meth)acrylonitrile, N-alkyl
(meth)acrylamide, N,N-dialkyl (meth)acrylamide, and a mixture
thereof. For example, the second monomer composition can include 60
to 100 weight percent of the cyclic alkyl (meth)acrylate and 0 to
40 percent optional monomers, 70 to 100 weight percent of the
cyclic alkyl (meth)acrylate and 0 to 30 percent optional monomers,
80 to 100 weight percent of the cyclic alkyl (meth)acrylate and 0
to 20 percent optional monomers, 90 to 100 weight percent of the
cyclic alkyl (meth)acrylate and 0 to 10 percent optional monomers,
90 to 99 weight percent of the cyclic alkyl (meth)acrylate and 1 to
10 percent optional monomers, 95 to 100 weight percent of the
cyclic alkyl (meth)acrylate and 0 to 5 percent optional monomers,
or 95 to 99 weight percent of the cyclic alkyl (meth)acrylate and 1
to 5 percent optional monomers. The weight percents are based on
the total weight of monomers within the second monomer
composition.
[0055] In some more specific embodiments, the second monomer
composition contains 1) 50 to 100 weight percent of the cyclic
alkyl (meth)acrylate, 2) 0 to 50 weight percent of a second monomer
selected from an alkyl (meth)acrylate having a linear or branched
alkyl group, and a vinyl monomer that does not have a
(meth)acryloyl group, (meth)acrylamide, (meth)acrylonitrile,
N-alkyl (meth)acrylamide, and N,N-dialkyl (meth)acrylamide, and 3)
0 to 10 weight percent of a polar monomer. For example, the second
monomer composition contains 1) 50 to 99 weight percent of the
cyclic alkyl (meth)acrylate, 2) 0 to 50 weight percent of the
second monomer, and 3) 1 to 10 weight percent of a polar monomer;
or 1) 50 to 99 weight percent of the cyclic alkyl (meth)acrylate,
2) 0 to 40 weight percent of the second monomer, and 3) 1 to 10
weight percent of a polar monomer; or 1) 70 to 99 weight percent of
the cyclic alkyl (meth)acrylate, 2) 0 to 20 weight percent of the
second monomer, and 3) 1 to 10 weight percent of a polar
monomer.
[0056] In some particular embodiments, the second monomer
composition contains 90 to 99 weight percent of the cyclic alkyl
(meth)acrylate and 1 to 10 percent polar monomer, 95 to 100 weight
percent of the cyclic alkyl (meth)acrylate and 0 to 5 percent
polar, or 95 to 99 weight percent of the cyclic alkyl
(meth)acrylate and 1 to 5 percent polar. The weight percents are
based on the total weight of monomers within the second monomer
composition. In many embodiments, the polar monomer is an
acid-containing monomer such as, for example, a (meth)acrylic
acid.
[0057] In addition to the second monomer composition, the
polymerizable composition used to form the second (meth)acrylate
polymer often contains a chain transfer agent. The chain transfer
agent is used to control the molecular weight of the second
(meth)acrylate polymer. Examples of useful chain transfer agents
include, but are not limited to, carbon tetrabromide, alcohols
(e.g., ethanol and isopropanol), thiols (e.g., lauryl mercaptan,
butyl mercaptan, ethanethiol, isooctylthioglycolate, 2-ethylhexyl
thioglycolate, 2-ethylhexyl mercaptopropionate, ethyleneglycol
bisthioglycolate), and mixtures thereof. In many embodiments, the
preferred chain transfer agent is iso-octyl thioglycolate (IOTG),
carbon tetrabromide, tert-dodecylmercaptan (TDDM), or
n-dodecylmercaptan. The amount of the optional chain transfer agent
is often in a range of 0 to 5 weight percent based on the total
weight of monomers in the second monomer composition. If present,
the chain transfer agent is often used in an amount of at least
0.01 weight percent, at least 0.02 weight percent, at least 0.05
weight percent, or at least 0.1 weight percent. The amount can be
up to 5 weight percent, up to 3 weight percent, up to 2 weight
percent, up to 1 weight percent, or up to 0.5 weight percent.
[0058] Other optional components can be added along with the second
monomer composition to the polymerizable composition used to form
the high second (meth)acrylate polymer. For example, the
polymerizable composition can include an inhibitor and/or
antioxidant. Suitable inhibitors and/or antioxidants include, but
are not limited to, mono-methyl ether of hydroquinone (MEQH) and
pentaerythritol tetrakis (3-(3,5-di-tert-butyl-4-hydroxyphenyl)
propionate), which is commercially available from BASF (Florham
Park, N.J., USA) under the trade designation IRGANOX 1010.
[0059] The polymerizable composition used to form the second
(meth)acrylate polymer typically includes a free radical initiator
to commence polymerization of the monomers. The free radical
initiator can be a photoinitator or a thermal initiator. The free
radical initiator is typically present in an amount up to 5 weight
percent based on the total weight of the monomers in the second
monomer composition. In some embodiments, the amount of free
radical initiator is up to 4 weight percent, up to 3 weight
percent, up to 2 weight percent, or up to 1 weight percent. The
amount of free radical initiator included in the polymerizable
composition is typically at least 0.005 weight percent. For
example, the polymerizable composition often contains at least 0.01
weight percent, at least 0.02 weight percent, at least 0.05 weight
percent, at least 0.1 weight percent, at least 0.2 weight percent,
or at least 0.5 weight percent free radical initiator.
[0060] Suitable thermal initiators include various azo compound
such as those commercially available under the trade designation
VAZO from E. I. DuPont de Nemours Co. (Wilmington, Del., USA)
including VAZO 67, which is 2,2'-azobis(2-methylbutane nitrile),
VAZO 64, which is 2,2'-azobis(isobutyronitrile), VAZO 52, which is
2,2'-azobis(2,4-dimethylpentanenitrile), and VAZO 88, which is
1,1'-azobis(cyclohexanecarbonitrile); various peroxides such as
benzoyl peroxide, cyclohexane peroxide, lauroyl peroxide,
di-tert-amyl peroxide, tert-butyl peroxy benzoate, di-cumyl
peroxide, and peroxides commercially available from Atofina
Chemical, Inc. (Philadelphia, Pa., USA) under the trade designation
LUPERSOL (e.g., LUPERSOL 101, which is
2,5-bis(tert-butylperoxy)-2,5-dimethylhexane, and LUPERSOL 130,
which is 2,5-dimethyl-2,5-di-(tert-butylperoxy)-3-hexyne); various
hydroperoxides such as tert-amyl hydroperoxide and tert-butyl
hydroperoxide; and mixtures thereof.
[0061] In some embodiments, a photoinitiator is used. Some
exemplary photoinitiators are benzoin ethers (e.g., benzoin methyl
ether or benzoin isopropyl ether) or substituted benzoin ethers
(e.g., anisoin methyl ether). Other exemplary photoinitiators are
substituted acetophenones such as 2,2-diethoxyacetophenone or
2,2-dimethoxy-2-phenylacetophenone (commercially available under
the trade designation IRGACURE 651 from BASF Corp. (Florham Park,
N.J., USA) or under the trade designation ESACURE KB-1 from
Sartomer (Exton, Pa., USA)). Still other exemplary photoinitiators
are substituted alpha-ketols such as
2-methyl-2-hydroxypropiophenone, aromatic sulfonyl chlorides such
as 2-naphthalenesulfonyl chloride, and photoactive oximes such as
1-phenyl-1,2-propanedione-2-(O-ethoxycarbonyl)oxime. Other suitable
photoinitiators include, for example, 1-hydroxycyclohexyl phenyl
ketone (commercially available under the trade designation IRGACURE
184), bis(2,4,6-trimethylbenzoyl)phenylphosphineoxide (commercially
available under the trade designation IRGACURE 819),
1-[4-(2-hydroxyethoxy)phenyl]-2-hydroxy-2-methyl-1-propane-1-one
(commercially available under the trade designation IRGACURE 2959),
2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)butanone
(commercially available under the trade designation IRGACURE 369),
2-methyl-1-[4-(methylthio)phenyl]-2-morpholinopropan-1-one
(commercially available under the trade designation IRGACURE 907),
and 2-hydroxy-2-methyl-1-phenyl propan-1-one (commercially
available under the trade designation DAROCUR 1173 from Ciba
Specialty Chemicals Corp. (Tarrytown, N.Y., USA)).
[0062] Additionally, an organic solvent can be added, if desired,
to control the viscosity of the polymerizable composition used to
form the second (meth)acrylate polymer. The amount of organic
solvent, if any, is typically determined by the polymerization
method. In some solvent-based polymerization methods, the
polymerizable composition can contain up to 70 weight percent
organic solvent. For adiabatic polymerization methods, however, the
amount of organic solvent is typically no greater than 10 weight
percent, no greater than 8 weight percent, no greater than 5 weight
percent, no greater than 3 weight percent, or no greater than 1
weight percent of the polymerizable composition. Any organic
solvent used in the polymerizable composition is typically removed
at the completion of the polymerization reaction. Suitable organic
solvents include, but are not limited to, methanol,
tetrahydrofuran, ethanol, isopropanol, heptane, acetone, methyl
ethyl ketone, methyl acetate, ethyl acetate, toluene, xylene, and
ethylene glycol alkyl ether. Those solvents can be used alone or as
mixtures thereof. In many embodiments (such in some adiabatic
polymerization processes), the polymerization occurs with little or
no organic solvent present.
[0063] The monomers used to form the second (meth)acrylate polymer
can be polymerized using any suitable method such as, for example,
solution (i.e., with a solvent) polymerization, dispersion
polymerization, suspension polymerization, and solventless
polymerization (for example, bulk polymerization with either UV or
thermal initiator). The polymerization can occur in a single step
or in multiple steps. That is, all or a portion of the
polymerizable composition may be charged into a suitable reaction
vessel and polymerized. If multiple steps are used, an initial
charge of monomers and initiator are added to the reactor. After
polymerization of the initial charge, another portion of any
remaining monomers and/or initiator are added. Multiple
polymerization steps can help narrow the polydispersity of the
polymerized product (e.g., the amount of low molecular weight
chains can be reduced), can help minimize or control the heat of
reaction, and can allow for adjustment of the type and amount of
monomer available during polymerization.
[0064] In many embodiments, the second (meth)acrylate polymer is
not formed using emulsion or dispersion polymerization methods.
Rather, the second (meth)acrylate polymer is prepared using a
solventless bulk polymerization method or a solution polymerization
method. Either a thermal initiator or a photoinitiator can be used.
In some embodiments, polymerization occurs using an adiabatic
process as described, for example, in U.S. Pat. Nos. 5,986,011
(Ellis et al.) and U.S. Pat. No. 5,637,646 (Ellis). A thermal
initiator is used with this process.
[0065] The weight average molecular weight of the second
(meth)acrylate polymer is typically at least 3,000 grams/mole. If
the weight average molecular weight is lower, the resulting
pressure-sensitive adhesive may have an unacceptably low cohesive
strength. The second (meth)acrylate polymer often has a weight
average molecular weight of at least 5,000 grams/mole, at least
10,000 grams/mole, or at least 20,000 grams/mole. The weight
average molecular weight can be up to 150,000 grams/mole. If the
molecular weight is higher, the second (meth)acrylate polymer might
not dissolve in the first monomer composition of the emulsion
composition. If not dissolved in the first monomer composition, the
second (meth)acrylate polymer can undesirably be present in
separate droplets from the first monomer composition within the
emulsion composition and/or can phase separate during
polymerization. The weight average molecular weight is often up to
120,000 grams/mole, up to 100,000 grams/mole, up to 80,000
grams/mole, up to 60,000 grams/mole, or up to 50,000 grams/mole.
For example, the weight average molecular weight can be in a range
of 3,000 to 150,000 grams/mole, in the range of 10,000 to 150,000
grams/mole, in a range of 3,000 to 100,000 grams/mole, in the range
of 10,000 to 100,000 grams/mole, in a range of 3,000 to 50,000
grams/mole, or in the range of 10,000 to 50,000 grams/mole.
[0066] The second (meth)acrylate polymer is added to the emulsion
composition. That is, this polymeric material is prepared prior to
combination with the other components of the emulsion composition.
The second (meth)acrylate polymer typically does not undergo
further free radical polymerization within the emulsion composition
or with other components of the emulsion composition. The second
(meth)acrylate can, however, undergo a crosslinking reaction within
the emulsion composition.
[0067] The second (meth)acrylate polymer is usually added to the
emulsion composition after being dissolved in the first monomer
composition. That is, a solution containing the second
(meth)acrylate polymer and the first monomer composition are added
together to the first phase of the emulsion. The solution is
typically added under conditions of high shear mixing to form
droplets suspended within the first phase. In some embodiments, the
second (meth)acrylate polymer is initially dissolved in a portion
of the first monomer composition and then the resulting polymer
solution is then mixed with the remaining monomers of the first
monomer composition.
[0068] The amount of second (meth)acrylate polymer added to the
emulsion composition is typically at least 0.5 weight percent or at
least 1 weight percent. If a lower amount of the second
(meth)acrylate polymer is added, the stability of the emulsion
composition may be poor. That is, it can be difficult to form and
maintain droplets in the emulsion composition. In some embodiments,
the emulsion composition contains at least 2 weight percent, at
least 3 weight percent, or at least 5 weight percent of the second
(meth)acrylate polymer. The amount of the second (meth)acrylate
polymer added is typically up to 15 weight percent. If a higher
amount of the second (meth)acrylate polymer is added, the
polymerization of the first monomer composition within the droplets
may be undesirably slow. Additionally, the polymeric material
formed from the first monomer composition may have an undesirably
low molecular weight and the resulting pressure-sensitive adhesive
may have an undesirably low cohesive strength. In some embodiments,
the emulsion composition contains up to 12 weight percent, up to 10
weight percent, or up to 8 weight percent of the second
(meth)acrylate polymer. The weight percents are based on a total
weight of the first monomer composition in the emulsion composition
(i.e., the total weight of monomers in the first monomer
composition).
[0069] The emulsion composition contains both the first monomer
composition and the second (meth)acrylate polymer within the same
droplets. More specifically, the emulsion composition often
contains 0.5 to 15 weight percent of the second (meth)acrylate
polymer and 85 to 99.5 weight percent first monomer composition
based on the total weight of the second (meth)acrylate polymer plus
the weight of monomers in the first monomer composition (this does
not include the small amount of polymerizable surfactant). This is
the total polymerized and polymerizable material in the emulsion
composition. Most of this polymerized and polymerizable material
are present within the droplets of the emulsion (e.g., some of the
acidic monomers may be dissolved in the first phase). In some
examples, the emulsion composition can contain 1 to 15 weight
percent of the second (meth)acrylate polymer and 85 to 99 weight
percent of the first monomer composition, 2 to 12 weight percent of
the second (meth)acrylate polymer and 88 to 98 weight percent first
monomer composition, 2 to 10 weight percent of the second
(meth)acrylate polymer and 90 to 98 weight percent first monomer
composition, or 2 to 8 weight percent of the second (meth)acrylate
polymer and 92 to 98 weight percent first monomer composition based
on the total weight of the second (meth)acrylate polymer plus the
weight of monomers in the first monomer composition.
[0070] In some particular embodiments, the first monomer
composition contains a mixture of one or more alkyl (meth)acrylates
having a linear or branched alkyl group with at least six carbon
atoms, one or more cyclic alkyl (meth)acrylates, and one or more
(meth)acrylic acids. The second (meth)acrylate is formed from a
second monomer composition that contains one or more cyclic alkyl
(meth)acrylates and one or more (meth)acrylic acids.
[0071] Other optional reactants can be included in the emulsion
composition. For example, in some embodiments, a crosslinker is
added that can react with multiple carboxylic acid groups (--COOH).
The carboxylic acid groups can be on the second (meth)acrylate
polymer, on the polymeric material formed from the first monomer
composition, or on a combination of both polymeric materials. The
use of the optional crosslinkers may increase the shear strength of
the resulting pressure-sensitive adhesive.
[0072] Suitable crosslinkers capable of reacting with multiple
carboxylic acid groups include, but are not limited to,
polyoxazolines such as those commercially available under the trade
designation EPOCROS from Nippon Shokubai Co., LTD (Japan),
polyaziridines (e.g., trimehtylolpropane tris(2-methyl-laziridine
propionate from PolyAziridine LCC (Medford, N.J., USA)),
polyamines, or the like. Other suitable crosslinkers include metal
salts that can complex with multiple carboxylic acid groups.
Suitable metals include, for example, zinc salts. If used, the
optional crosslinker is often added in an amount equal to at least
0.01 weight percent based on the total weight of monomers in the
first monomer composition. For example, the emulsion can contain at
least 0.05 weight percent, at least 0.1 weight percent, or at least
0.5 weight percent of the crosslinker. The amount of the optional
crosslinker is often up to 3 weight percent based on the total
weight of monomers in the first monomer composition. For example,
the emulsion composition can contain up to 2.5 weight percent, up
to 2 weight percent, up to 1.5 weight percent, or up to 1 weight
percent of the optional crosslinker.
[0073] In many embodiments, an optional neutralizing agent is added
to the emulsion composition. The neutralizing agent can be added,
for example, to improve the reactivity of the crosslinker, to
improve the stability of the resulting latex composition, or the
like. Suitable neutralizing agents are often strong or weak bases
such as, for example, ammonium hydroxide, ammonia, sodium acetate,
potassium acetate, sodium hydroxide, potassium hydroxide, and
lithium hydroxide. The neutralizing agent is often added to
increase the pH of the emulsion composition to at least 4.0, at
least 4.5, at least 5.0, at least 5.5, at least 6.0, at least 6.5,
or at least 7.0.
[0074] The emulsion composition typically further includes an
initiator. While either a water soluble or oil soluble initiator
can be used, the initiator is typically selected to be soluble in
water. If the initiator is oil soluble, it is typically added to
the mixture (solution) of monomers of the first monomer composition
and the second (meth)acrylate polymer before this mixture
(solution) is combined with the first phase of the emulsion
composition. If the initiator is water soluble, it is often added
after formation of the droplets within the first phase of the
emulsion composition. If a reducing agent is used, it is usually
water soluble and is added to the first phase.
[0075] Examples of water soluble initiators include, but are not
limited to, hydrogen peroxide and various persulfate salts such as
sodium persulfate, potassium persulfate, and ammonium persulfate.
Optional reducing agents can be added to lower the temperature
needed for initiation of the polymerization reaction. Suitable
reducing agents include, but are not limited to, ascorbic acid,
bisulfite salts (e.g., sodium bisulfite, potassium bisulfite, and
ammonium bisulfite), and sodium formaldehyde sulfoxylate. The
amount of initiator and optional reducing agent can each be up to 1
weight percent based on the weight of monomers in the first monomer
composition. For example, the amounts can be up to 0.8 weight
percent, up to 0.5 weight percent, up to 0.3 weight percent, or up
to 0.2 weight percent based on a total weight of monomers in the
first monomer composition. The amount is initiator and optional
reducing agent each can be at least 0.01 weight percent, at least
0.05 weight percent, or at least 0.1 weight percent based on the
total weight of monomers in the first monomer composition.
[0076] Examples of oil soluble initiators include, but are not
limited to, azo compounds or peroxides such as those mentioned
above for the formation of the second (meth)acrylate polymer. If
such initiators are used, they are used in the same amount as
described above for water soluble initiators.
[0077] In many emulsion compositions, a chain transfer agent is not
used. As described above, however, a chain transfer agent can be
used (and usually is used) in the formation of the second
(meth)acrylate polymer.
[0078] The emulsion composition does not include a tackifier.
[0079] The emulsion composition can be prepared by any suitable
process that results in the formation of droplets containing the
second (meth)acrylate polymer dissolved in monomers of the first
monomer composition. In many embodiments, the second (meth)acrylate
polymer is initially mixed with monomers included in the first
monomer composition. The monomers are often used in their neat form
without the addition of any solvent. Once the second (meth)acrylate
polymer has dissolved, the mixture (solution) is combined with
water or with water and other components of the emulsion
composition using high shear mixing. In some embodiments, the
polymerizable surfactant and neutralizing agent can be dissolved in
(or combined with) the water prior to mixing.
[0080] With high shear mixing, droplets form within the first phase
(i.e., aqueous phase). Prior to any polymerization of the first
monomer composition, the droplets contain a mixture of i) the
second (meth)acrylate polymer and ii) at least 90 weight percent of
the first monomer composition, wherein the second (meth)acrylate
polymer is dissolved in the first monomer composition within the
droplets. Typically, the droplets include at least 92 weight
percent, at least 95 weight percent, at least 97 weight percent, at
least 98 weight percent, or at least 99 weight percent of the
monomers in the first monomer composition. The polymerizable
surfactant is likely to be at the interface between the droplets
and the first phase or dissolved in first phase. Most of the
polymerizable surfactant is likely to be at the interface.
[0081] In many embodiments, any initiator, and/or reducing agent,
and/or neutralizing agent included in the emulsion composition are
likely to be dissolved in the first phase.
[0082] The droplets suspended in the first phase typically have an
average diameter up to about 2000 nanometers, up to 1500
nanometers, up to 1000 nanometers, up to 900 nanometers, up to 800
nanometers, up to 700 nanometers, up to 600 nanometers, or up to
500 nanometers. The average diameter is typically at least 100
nanometers, at least 200 nanometers, at least 300 nanometers, or at
least 400 nanometers. The average size can be determined using
dynamic light scattering methods. In some embodiments, the average
droplet size (diameter) is in a range of 100 to 2000 nanometers, in
a range of 200 to 1000 nanometers, in a range of 300 to 1000
nanometers, in a range of 200 to 800 nanometers, or in a range of
400 to 700 nanometers.
[0083] In many embodiments, the emulsion composition is considered
to be a mini-emulsion. As used herein, the term "mini-emulsion"
refers to an emulsion method that uses high shear to make droplets
having an average diameter no greater than 1 micrometer.
Polymerization occurs within the droplets to form polymeric latex
particles. Polymerization is limited to that which occurs within
the droplets.
[0084] The first monomer composition is typically polymerized at
room temperature (e.g., about 20.degree. C. to about 25.degree. C.)
or at a temperature above room temperature. The temperature is
often at least 30.degree. C., at least 40.degree. C., or at least
50.degree. C. The temperature can be up to the boiling temperature
of the emulsion composition (e.g., about 100.degree. C.). In some
embodiments, the temperature can be up to 80.degree. C., up to
70.degree. C., or up to 60.degree. C. Any heat generated during
polymerization is rapidly moderated by the effect of the heat
capacity of the first phase. The reaction time can be any length of
time needed to complete the polymerization reaction. In some
embodiments, the reaction time can be at least 1 hour, at least 2
hours, at least 3 hours, or at least 4 hours. The reaction time is
up to 24 hours or longer, up to 16 hours, or up to 8 hours. The
reactor is often purged with an inert gas such as nitrogen.
[0085] The polymerized product of the emulsion composition is a
latex composition. That is, the latex composition contains water
and polymeric particles that are a polymerized product of the
emulsion composition as described above. The terms "latex" and
"latex composition" may be used interchangeably. The terms
"polymeric particle" and "latex particles" and "polymeric latex
particles" may be used interchangeably. Both i) the second
(meth)acrylate polymer plus ii) the polymerized product of the
first monomer composition (the first (meth)acrylate polymer) are
present within the same latex particles. The latex composition
contains latex particles having an average size comparable to the
average size of the droplets within the emulsion composition prior
to polymerization. More particularly, the average particle size of
the latex particles is roughly equal to or slightly larger than the
average droplet size within the emulsion composition due to density
differences.
[0086] The latex particles are typically suspended (e.g.,
dispersed) in the water phase (first phase). Preferably, the latex
particles are not coagulated together. The latex particles include
both the second (meth)acrylate polymer and the first (meth)acrylate
polymer. The molecular weight of the first (meth)acrylate polymer
is typically higher than the molecular weight of polymeric
materials of the same overall chemical composition formed using
other processes. More specifically, the molecular weight of the
first (meth)acrylate polymer formed by emulsion polymerization can
be close to 1 million Daltons.
[0087] In contrast to the emulsion polymerization method used to
form the first (meth)acrylate polymer, a typical molecular weight
of polymers formed from the same monomers using solution
polymerization or bulk polymerization methods is often less than
500,000 Daltons. With both solution polymerization and bulk
polymerization methods, the molecular weight is usually controlled
by the initiator concentration. That is, higher initiator
concentrations tend to produce lower molecular weight polymers.
Therefore, in order to produce high molecular weight polymers using
solution polymerization or bulk polymerization methods, extremely
low initiator concentrations are required. However, if extremely
low initiator concentrations are used, the polymerization time may
be unacceptably long. Such processes may be economically
impractical to prepare high molecular weight polymeric materials.
The high molecular weight polymeric materials, however, are often
desirable for some adhesive applications such as where high shear
strength is necessary.
[0088] With emulsion polymerization methods, the molecular weight
of the polymeric material (e.g., the molecular weight of the first
(meth)acrylate polymer) can be controlled by both initiator
concentration and the number of particles (i.e., number of droplets
in the emulsion). Higher initiator concentrations often result in
lower molecular weights and faster reaction times. Higher particle
numbers, however, tend to favor higher molecular weights and faster
reaction times.
[0089] Due to the high molecular weight of the polymeric materials
formed from emulsion compositions, crosslinking structures can
often form more easily compared to polymeric materials formed using
solution polymerization and bulk polymerization methods even in the
absence of additional crosslinkers. Two possible types of
crosslinking can occur in the polymeric materials formed by
emulsion polymerization: 1) physical entanglement and 2) chemical
crosslinking due to the chain transfer reactions to a polymeric
chain. Physical entanglement can be enhanced with longer polymeric
chains resulting from the increased average molecular weight. Chain
transfer reactions can form crosslinking structures for long
polymeric chains.
[0090] The latex particles typically have a single glass transition
temperature as determined using a Differential Scanning
Calorimeter. More specifically, there is a single peak in the plot
of reversible heat flow versus temperature for the dry polymeric
material (dry polymeric latex particles) during the second heating
cycle using Modulated Differential Scanning Calorimetry. The
T.sub.g is typically no greater than 0.degree. C., no greater than
-10.degree. C., or no greater than -20.degree. C.
[0091] The latex composition can be combined with an optional
tackifier. The addition of a tackifier can be used to increase
adhesion. Any suitable tackifier can be used such as rosin acids
and their derivatives (e.g., rosin esters); terpene resins such as
polyterpenes (e.g., alpha pinene-based resins, beta pinene-based
resins, and limonene-based resins, and aromatic-modified
polyterpene resins (e.g., phenol modified polyterpene resins));
coumarone-indene resins; and petroleum-based hydrocarbon resins
such as CS-based hydrocarbon resins, C9-based hydrocarbon resins,
C5/C9-based hydrocarbon resins, and dicyclopentadiene-based resins.
These tackifying resins, if added, can be hydrogenated to lower
their color contribution to the pressure-sensitive adhesive
composition. Combinations of various tackifiers can be used, if
desired.
[0092] In many embodiments, the tackifier is a rosin ester or
includes a rosin ester. Tackifiers that are rosin esters are the
reaction products of various rosin acids and alcohols. These
include, but are not limited to, methyl esters of rosin acids,
triethylene glycol esters of rosin acids, glycerol esters of rosin
acids, and pentaertythritol esters of rosin acids. These rosin
esters can be hydrogenated partially or fully to improve stability
and reduce their color contribution to the pressure-sensitive
adhesive composition. The rosin resin tackifiers are commercially
available, for example, from Eastman Chemical Company (Kingsport,
Tenn., USA) under the trade designations PERMALYN, STAYBELITE, and
FORAL as well as from Newport Industries (London, England) under
the trade designations NUROZ and NUTAC. A fully hydrogenated rosin
resin is commercially available, for example, from Eastman Chemical
Company under the trade designation FORAL AX-E. A partially
hydrogenated rosin resin is commercially available, for example,
from Eastman Chemical Company under the trade designation
STAYBELITE-E.
[0093] Often, it is desirable to use a tackifier that can be
dispersed in water. Water dispersion of rosin esters are available
under the trade designation SNOWTACK from Lawter, Inc. (Chicago,
Ill., USA). Other suitable water dispersed tackifiers are
commercially available under the trade designation TACOLYN from
Eastman Chemical Company that include, for example, rosin ester
resin dispersions, hydrogenated rosin ester resin dispersions,
aliphatic hydrocarbon resin dispersions, and aromatic modified
hydrocarbon resin dispersion.
[0094] If present, the optional tackifier in the latex composition
is often used in an amount in a range of 1 to 40 weight percent
based on the total weight of the polymeric latex particles. In some
embodiments, the amount of tackifier is at least 5 weight percent,
or at least 10 weight percent and can be up to 35 weight percent,
up to 30 weight percent, up to 25 weight percent, or up to 20
weight percent.
[0095] Other optional components that can be added to the latex
composition are thickeners. Example thickeners are typically
aqueous polymer solutions such as those available under the trade
designation PARAGUM from Royal Coatings and Specialty Polymers
(South Bend, Ind., USA). If added, the optional thickeners can be
used in an amount up to 5 weight percent based on the total weight
of the latex composition (e.g., water and polymeric latex
particles). For example, the thickener can be used in an amount up
to 4 weight percent, up to 3 weight percent, up to 2 weight
percent, or up to 1 weight percent.
[0096] In some embodiments, the thickener is in a range of 0 to 5
weight percent, 0.1 to 5 weight percent, 0.1 to 2 weight percent,
0.1 to 1 weight percent, 0.2 to 0.8 weight percent, or 0.4 to 0.6
weight percent.
[0097] The latex composition typically is dried to form a
pressure-sensitive adhesive. The compositions are typically dried
to remove at least 90 weight percent of the water. For example, at
least 95 weight percent, at least 97 weight percent, at least 98
weight percent, or at least 99 weight percent of the water is
removed. The water content of the dried pressure-sensitive adhesive
many increase or decrease depending on the environmental humidity.
In some embodiments, the latex composition is coated on a substrate
such as a backing layer or release liner prior to drying. Drying
typically occurs at temperatures above room temperature but not at
a temperature that would distort or degrade the substrate and/or
the pressure-sensitive adhesive layer. In some embodiments, the
drying occurs at temperatures in a range of about 40.degree. C. to
about 120.degree. C. and for a time sufficient to lower the water
content to the desired level.
[0098] The pressure-sensitive adhesive layer can have any desired
thickness. In many embodiments, the adhesive layer has a thickness
no greater than 20 mils (500 micrometers), no greater than 10 mils
(250 micrometers), no greater than 5 mils (125 micrometers), no
greater than 4 mils (100 micrometers), no greater than 3 mils (75
micrometers), or no greater than 2 mils (50 micrometers). The
thickness is often at least 0.5 mils (12.5 micrometers) or at least
1 mil (25 micrometers). For example, the thickness of the adhesive
layer can be in the range of 0.5 mils (2.5 micrometers) to 20 mils
(500 micrometers), in the range of 0.5 mils (5 micrometers) to 10
mils (250 micrometers), in the range of 0.5 mils (12.5 micrometers)
to 5 mils (125 micrometers), in the range of 1 mil (25 micrometers)
to 3 mils (75 micrometers), or in the range of 1 mil (25
micrometers) to 2 mils (50 micrometers).
[0099] The pressure-sensitive adhesives can have a good balance of
peel strength and adhesive strength. The presence of the second
(meth)acrylate polymer in the droplets of the emulsion may
contribute to this good balance. Without the use of the second
(meth)acrylate in the emulsion composition, it can be difficult to
prepare pressure-sensitive adhesives with this good balance. That
is, the peel strength can be increased while maintaining good
cohesive strength. Likewise, the cohesive strength can be increased
while maintaining good peel strength.
[0100] Various types of articles can be prepared that include a
substrate and a pressure-sensitive adhesive layer positioned
adjacent to (and adhered to) a major surface of the substrate. Any
suitable substrate can be used in the article and the substrate is
often selected depending on the particular application. For
example, the substrate can be flexible or inflexible and can be
formed from a polymeric material, glass or ceramic material, metal
or metal alloy, or combination thereof Some substrates are
polymeric materials such as those prepared, for example, from
polyolefins (e.g., polyethylene, polypropylene, or copolymers
thereof), polyurethanes, polyvinyl acetates, polyvinyl chlorides,
polyesters (e.g., polyethylene terephthalate or polyethylene
naphthalate), polycarbonates, polyacrylates such as
polymethyl(meth)acrylates (PMMA), ethylene-vinyl acetate
copolymers, neoprenes, and cellulosic materials (e.g., cellulose
acetate, cellulose triacetate, and ethyl cellulose). The substrate
can be in the form of foils, films, or sheets, nonwoven materials
(e.g., paper, fabric, nonwoven scrims), foams, and the like.
[0101] For some substrates, it may be desirable to treat the
surface of the substrate to improve adhesion to the
pressure-sensitive adhesive layer. Such treatments include, for
example, application of primer layers, surface modification layer
(e.g., corona treatment or surface abrasion), or both. Illustrative
examples of suitable chemical primer layer types include urethanes,
silicones, epoxy resins, vinyl acetate resins, ethyleneimines, and
the like. Urethane and silicone types are particularly effective
chemical primers for use with polyester film substrates. One
suitable silicone type of primer layer has a continuous gelled
network structure of inorganic particles, and is described in
Japanese Unexamined Pat. Publication (Kokai) No. 2-200476. This
primer layer has a strong affinity for polyester resins and
polyolefin resins. Illustrative examples of chemical primers for
vinyl and polyethylene terephthalate films include the crosslinked
acrylic ester/acrylic acid copolymers disclosed in U.S. Pat. No.
3,578,622 (Brown).
[0102] In some embodiments, the substrate is a release liner.
Release liners typically have low affinity for the
pressure-sensitive adhesive layer. Exemplary release liners can be
prepared from paper (e.g., Kraft paper) or other types of polymeric
material. Some release liners are coated with an outer layer of a
release agent such as a silicone-containing material or a
fluorocarbon-containing material.
[0103] Some articles are adhesive tapes. The adhesive tapes can be
single-sided adhesive tapes with the pressure-sensitive adhesive on
a single side of the backing layer or can be double-sided adhesive
tape with a pressure-sensitive adhesive layer on both major
surfaces of the backing layer. The backing layer is often a
polymeric film, fabric, or foam. Each pressure-sensitive adhesive
layer may be positioned, if desired, between the backing layer and
a release layer.
[0104] Any suitable backing layer can be used. In some embodiments,
the backing layer is an oriented polyolefin film. For example, the
oriented polyolefin film can prepared as described in U.S. Pat. No.
6,638,637 (Hager et al.). Such backings layers often include
multiple layers of polyolefins with at least two different melting
points and that are biaxially oriented. In another example, the
oriented polyolefin film can be prepared as described in U.S. Pat.
No. 6,451,425 (Kozulla et al.). Such backings often include an
isotactic polypropylene that is blended or mixed with at least one
second polyolefin such as polyethylene, polybutylene, or
syndiotactic polypropylene. These backings are typically biaxially
oriented.
[0105] For adhesive tapes with a single pressure-sensitive adhesive
layer, the backing layer often has a first surface that has been
treated (i.e., primed) to improve adhesion to the
pressure-sensitive adhesive layer. The backing layer has a second
surface opposite the first surface that has a low adhesion to the
pressure-sensitive adhesive layer. Such an adhesive tape can be
formed into a roll. In some embodiments, the adhesive tapes are
packaging tapes.
[0106] Other articles are transfer tapes in which a
pressure-sensitive adhesive layer is positioned adjacent to a
release liner. The transfer tape can be used to transfer the
pressure-sensitive adhesive layer to another substrate or surface.
Any suitable release liner can be used. In many embodiments, the
release liner has a release layer coating adjacent to a substrate.
Suitable substrates include, but are not limited to, paper such as
poly-coated Kraft paper and super-calendered or glassine Kraft
paper; cloth (fabric); nonwoven web; metal or metal alloy including
metal foil; polyesters such as poly(alkylene terephthalate) such as
poly(ethylene terephthalate), poly(alkylene naphthalate) such as
poly(ethylene naphthalate); polycarbonate; polyolefins such as
polypropylene, polyethylene, polybutylene, and copolymers thereof;
polyamide; cellulosic materials such as cellulose acetate or ethyl
cellulose; and combinations thereof.
[0107] In some exemplary embodiments, the release liners have a
release coating containing a polymerized product of a
vinyl-silicone copolymers as described in U.S. Pat. No. 5,032,460
(Kantner et al.). In other exemplary embodiments, the release liner
has a release coating containing a polymerized product of a
(meth)acrylate-functionalized siloxane as described in U.S. Patent
Application Publication No. 2013/059105 (Wright et al.). Such
release coatings can be prepared by applying a coating of a
polymerizable composition containing the
(meth)acrylate-functionalized polysiloxane to a surface of a
substrate and then irradiating the coating with ultraviolet
radiation. The ultraviolet radiation is often provided by short
wavelength polychromatic ultraviolet light source having at least
one peak with intensity at a wavelength in the range of about 160
to about 240 nanometers. Suitable short wavelength polychromatic
ultraviolet light sources include, for example, low pressure
mercury vapor lamps, low pressure mercury amalgam lamps, pulsed
Xenon lamps, and glow discharge from a polychromic plasma emission
source. The coatings applied to the substrate can be free or
substantially free (e.g., less than 0.1 weight percent, less than
0.01 weight percent, or less than 0.001 weight percent) of a
photoinitiator based on the total weight of the coatings.
[0108] The pressure-sensitive adhesive layers often have both high
peel adhesion (i.e., peel strength) and high shear strength (i.e.,
cohesion) to both smooth and rough surfaces. As such, the
pressure-sensitive adhesives can be used in articles having a
diverse range of uses and can be adhered to a variety of
substrates. In some embodiments, the substrate is a polymeric film
or sheet, metal or metal alloy, fabric, or foam.
[0109] In embodiments where no tackifier or low amounts of
tackifier are used, the pressure-sensitive adhesives are well
suited for applications where low volatile organic content is
needed such as for automotive interior applications. The
pressure-sensitive adhesives often have both high peel adhesion and
high shear strength (i.e., cohesion), particularly when adhered to
low surface energy substrates such as polyolefin (e.g.,
polypropylene, polyethylene, polybutylene, and copolymers thereof)
and clear coats. The good adhesive characteristics (e.g., high peel
adhesion and high shear strength) can typically be maintained even
at temperatures above room temperature such as those near
70.degree. C.
[0110] In embodiments where a tackifier is included, the
pressure-sensitive adhesives often have both high peel adhesion and
high shear strength, particularly when adhered to polar surfaces
such as metals or metal alloys (e.g., carbon steel and stainless
steel).
[0111] Embodiment 1 is an emulsion composition that contains a)
water, b) a polymerizable surfactant having an unsaturated group
that can undergo free radical polymerization, c) a first monomer
composition, and d) a second (meth)acrylate polymer. The first
monomer composition includes an alkyl (meth)acrylate having a
linear or branched alkyl group with at least six carbon atoms. The
second (meth)acrylate polymer is present in an amount of 0.5 to 15
weight percent based on a total weight of monomers in the first
monomer composition and has a glass transition temperature greater
than or equal to 50.degree. C. The second (meth)acrylate polymer is
formed from a second monomer composition containing at least 50
weight percent of a cyclic alkyl (meth)acrylate based on a total
weight of monomers in the second monomer composition, wherein the
cyclic alkyl group has at least six carbon atoms. The emulsion
composition contains a first phase that includes the water and a
second phase dispersed as droplets within the first phase. The
droplets contain a mixture of i) at least 90 weight percent of the
first monomer composition and ii) the second (meth)acrylate
polymer. The second (meth)acrylate polymer is not miscible with the
first phase and is dissolved in the first monomer composition
within the droplets.
[0112] Embodiment 2 is the emulsion composition of embodiment 1,
wherein the cyclic alkyl (meth)acrylate in the second monomer
composition has a glass transition temperature equal to at least
80.degree. C. when measured as a homopolymer.
[0113] Embodiment 3 is the emulsion composition of embodiment 1 or
2, wherein the first monomer composition further comprises a cyclic
alkyl (meth)acrylate, polar monomer, or both.
[0114] Embodiment 4 is the emulsion composition of any one of
embodiments 1 to 3, wherein the first monomer composition comprises
60 to 98 weight percent of the alkyl (meth)acrylate having a linear
or branched alkyl group with at least six carbon atoms, 1 to 30
weight percent of a cyclic alkyl (meth)acrylate, and 1 to 10 weight
percent of the polar monomer based on a total weight of monomers in
the first monomer composition.
[0115] Embodiment 5 is the emulsion composition of any one of
embodiments 1 to 4, wherein the second monomer composition
comprises 50 to 100 weight percent of a cyclic alkyl (meth)acrylate
and 0 to 50 weight percent of an optional monomer that is a polar
monomer, an alkyl (meth)acrylate having a linear or branched alkyl
group, a vinyl monomer that does not have a (meth)acryloyl group,
(meth)acrylamide, (meth)acrylonitrile, N-alkyl (meth)acrylamide,
N,N-dialkyl (meth)acrylamide, or a mixture thereof based on a total
weight of monomers in the second monomer composition.
[0116] Embodiment 6 is the emulsion composition of any one of
claims 1 to 5, wherein the second monomer composition comprises 90
to 99 weight percent of the cyclic alkyl (meth)acrylate and 1 to 10
percent polar monomer or 90 to 100 weight percent of the cyclic
alkyl (meth)acrylate and 0 to 10 weight percent polar monomer based
on a total weight of monomers in the second monomer mixture.
[0117] Embodiment 7 is the emulsion composition of any one of
embodiments 1 to 6, wherein the first monomer composition is
different than the second monomer composition.
[0118] Embodiment 8 is the emulsion composition of any one of
embodiments 1 to 7, wherein the second (meth)acrylate polymer has a
weight average molecular weight in a range of 3,000 to 150,000
grams/mole.
[0119] Embodiment 9 is the emulsion composition of any one of
embodiments 1 to 8, wherein the emulsion composition does not
contain a tackifier.
[0120] Embodiment 10 is the emulsion composition of any one of
embodiments 1 to 9, wherein the emulsion composition contains at
least 25 weight percent water based on a total weight of the
emulsion composition.
[0121] Embodiment 11 is the emulsion composition of any one of
embodiments 1 to 10, wherein the emulsion composition contains up
to 90 weight percent water based on the total weight of the
emulsion composition.
[0122] Embodiment 12 is the emulsion composition of any one of
embodiments 1 to 11, wherein the polymerizable surfactant is a
propenyl polyoxyethylene alkylphenyl compound or propenyl
polyoxyethylene alkylphenyl ether ammonium sulfate compound.
[0123] Embodiment 13 is the emulsion composition of any one of
embodiments 1 to 12, wherein the polymerizable surfactant is sodium
dodecylallyl sulfosuccinate or a phosphate ester.
[0124] Embodiment 14 is the emulsion composition of any one of
embodiments 1 to 13, wherein the emulsion composition contains at
least 0.5 weight percent polymerizable surfactant based on the
total weight of monomers in the first monomer composition.
[0125] Embodiment 15 is the emulsion composition of any one of
embodiments 1 to 14, wherein the emulsion composition contains up
to 2 weight percent polymerizable surfactant based on the total
weight of monomers in the first monomers composition.
[0126] Embodiment 16 is a latex composition comprising a
polymerized product of the emulsion composition of any one of
embodiments 1 to 15, wherein the latex composition comprises
polymeric latex particles.
[0127] Embodiment 17 is the latex composition of embodiment 16,
wherein the polymeric latex particles have a single glass
transition temperature as determined using a Differential Scanning
Calorimeter. Embodiment 18 is the latex composition of embodiment
16 or 17, wherein the second (meth)acrylate polymer and a
polymerized product of the first monomer composition are together
in the same polymeric particles.
[0128] Embodiment 19 is the latex composition of any one of
embodiments 16 to 18, further comprising a tackifier that is water
dispersible. Embodiment 20 is the latex composition of any one of
embodiments 16 to 19, wherein the polymerized product of the
emulsion composition comprises polymerized surfactant in an amount
in a range of 1 to 2 weight percent based on a total weight of the
polymeric latex particles.
[0129] Embodiment 21 is a pressure-sensitive adhesive comprising a
dried product of the latex composition of any one of embodiments 16
to 20.
[0130] Embodiment 22 is an article comprising (a) a substrate and
(b) a first pressure-sensitive adhesive layer positioned adjacent
to a first major surface of the substrate, wherein the first
pressure-sensitive adhesive layer comprises the pressure-sensitive
adhesive of embodiment 21.
[0131] Embodiment 23 is the article of embodiment 22, further
comprising a second layer of pressure-sensitive adhesive of
embodiment 21 positioned adjacent to a second major surface of the
substrate.
[0132] Embodiment 24 is the article of embodiment 22 or 23, wherein
the substrate is a foam or polymeric film.
[0133] Embodiment 25 is the article of any one of embodiments 22 to
24, wherein the substrate is a biaxially oriented polyolefin
film.
[0134] Embodiment 26 is the article of any one of embodiments 22 to
24, wherein the substrate is a release liner.
[0135] Embodiment 27 is the article of embodiment 26, wherein the
release liner comprises a release coating comprising a polymerized
product of a vinyl-silicone copolymer or a
(meth)acrylate-functionalized siloxane.
[0136] Embodiment 28 is the article of embodiment 26 or 27, wherein
the article is a transfer tape.
[0137] Embodiment 29 is the article of embodiment 22 to 25, wherein
the article is an adhesive tape.
[0138] Embodiment 30 is the article of embodiment 29, wherein the
adhesive tape is a packaging tape.
[0139] Embodiment 31 is the article of any one of embodiments 22 to
25, wherein the substrate has a low energy surface.
[0140] Embodiment 32 is the article of embodiment 31, wherein the
low energy surface comprises a polyolefin or a clear coat.
[0141] Embodiment 33 is a method of forming a pressure-sensitive
adhesive. The method includes (a) forming an emulsion composition
of any one of embodiments 1 to 15, (b) polymerizing the emulsion
composition to form a latex composition comprising polymeric latex
particles, and (c) drying the latex composition to form the
pressure-sensitive adhesive.
[0142] Embodiment 34 is the method of embodiment 33, wherein
forming the emulsion composition comprises forming the second
(meth)acrylate polymer, dissolving the second (meth)acrylate
polymer in one or more monomers in the first monomer composition to
form a polymer solution, adding the polymer solution to the first
phase, and forming droplets of the polymer solution within the
first phase by mixing with high shear.
EXAMPLES
[0143] All parts, percentages, ratios, etc. used in the Examples
are by weight unless indicated otherwise. As used herein, the term
"pph" refers to parts per hundred.
TABLE-US-00001 TABLE 1 Materials Abbreviation Description Supplier
EHA 2-Ethylhexyl acrylate Dow Chemical (Midland, MI, USA) IBOA
Isobornyl acrylate San Esters (New York, NY, USA) IBOMA Isobornyl
methacrylate Sigma Aldrich (St. Louis, MO, USA) IOA Isooctyl
acrylate 3M Company (St. Paul, MN, USA) AA Acrylic acid (99%) Alfa
Aesar (Ward Hill, MA, USA) MAA Methacrylic acid (99%) Alfa Aesar
(Ward Hill, MA, USA) EtOAc Ethyl acetate Sigma Aldrich (St. Louis,
MO, USA) MEHQ Methoxyether hydroquinone Sigma Aldrich (St. Louis,
MO, USA) IOTG Isooctyl thioglycolate Sigma Aldrich (St. Louis, MO,
USA) IRGACURE 2,2-Dimethoxy-1,2-diphenyl-ethanone BASF
(Ludwigshafen, Germany) 651 IRGANOX Pentaerythritol tetrakis
(3-(3,5-di-tert- BASF (Ludwigshafen, Germany) 1010
butyl-4-hydroxyphenyl) propionate) LUPERSOL 2,5-Dimethyl-2,5-di(t-
Atofina (Philadelphia, PA, USA) 101 butylperoxy)hexene LUPERSOL
2,5-Dimethyl-2,5-di(t- Atofina (Philadelphia, PA, USA) 130
butylperoxy)hexyne-3 VAZO 52
2,2'-Azobis(2,4-dimethylpentanenitrile) DuPont (Wilmington, DE,
USA) VAZO 67 2,2'-Azobis(2-methylbutanenitrile) DuPont (Wilmington,
DE, USA) VAZO 88 1,1'-Azobis(cyclohexanecarbonitrile) DuPont
(Wilmington, DE, USA) KPS Potassium persulfate (99.9% purity) Alfa
Aesar (Ward Hill, MA, USA) Na.sub.2S.sub.2O.sub.5 Sodium bisulfate
(97% purity) Alfa Aesar (Ward Hill, MA, USA)
FeSO.sub.4.cndot.7H.sub.2O Ferrous sulfate heptahydrate Sigma
Aldrich (St. Louis, MO, USA) DIANAL Described by vendor as a methyl
Dianal America, Inc. (Pasadena, TX, BR113 methacrylate resin; the
M.sub.w was about USA) 30 kg/mol DIANAL Described by vendor as a
butyl Dianal America, Inc. (Pasadena, TX, MB2543 methacrylate resin
with a molecular USA) weight of about 35 kg/mole TRITON X-100
Nonionic surfactant Dow Chemical (Midland, MI, USA) DS-4 Sodium
dodecyl benzene sulfonate Rhodia Inc., which is a member of the
surfactant Solvay Group (Cranbury, NJ, USA) DS-10 Sodium dodecyl
benzene sulfonate Rhodia Inc., which is a member of the surfactant
Solvay Group (Cranbury, NJ, USA) HITENOL Polyoxyethylene
alkylphenyl propenyl Dai-Ichi Kogyo Seiyaku Co., Ltd. BC-1025 ether
ammonium sulfate (25 wt. % solids (Japan) solution in water), which
is a polymerizable surfactant SNOWTACK Water-dispersed tackifier,
polymeric Lawter Inc. (Chicago, IL, USA) SE780G material based on
rosin adduction and esterification TEGO RC-902 Silicone acrylate
with a high silicone to Evonik North America, Inc. acrylate ratio
(Parsippany, NJ, USA) TEGO Silicone acrylate with a low silicone to
Evonik North America, Inc. RC-711 acrylate ratio (Parsippany, NJ,
USA) PARAGUM Polyacrylate thickener Royal Coatings & Specialty
Polymers 500 (South Bend, IN, USA)
Test Method 1: Polymer Molecular Weight Measurement
[0144] The molecular weight distribution of the compounds was
characterized using gel permeation chromatography (GPC). The GPC
instrumentation, which was obtained from Waters Corporation
(Milford, Mass., USA), included a high pressure liquid
chromatography pump (Model 1515HPLC), an auto-sampler (Model 717),
a UV detector (Model 2487), and a refractive index detector (Model
2410). The chromatograph was equipped with two 5 micrometer PLgel
MIXED-D columns available from Varian Inc. (Palo Alto, Calif.,
USA).
[0145] Samples of polymeric solutions were prepared by dissolving
dried polymer samples in tetrahydrofuran at a concentration of 0.5
percent (weight/volume) and filtering through a 0.2 micrometer
polytetrafluoroethylene filter that is available from VWR
International (West Chester, Pa., USA). The resulting samples were
injected into the GPC and eluted at a rate of 1 milliliter per
minute through the columns maintained at 35.degree. C. The system
was calibrated with polystyrene standards using a linear least
squares analysis to establish a standard calibration curve. The
weight average molecular weight (M.sub.W) and the polydispersity
index (weight average molecular weight divided by number average
molecular weight (M.sub.n)) were calculated for each sample against
this standard calibration curve.
Test Method 2: Viscosity
[0146] The viscosity was measured with a Brookfield viscometer with
spindle 3 (obtained from Brookfield Engineering (Middleboro, Mass.,
USA)) at a rotating speed of 30 revolutions per minute (rpm).
Test Method 3: Latex Weight Percent (wt. %) Solids
[0147] To measure solid content, first an aluminum dish was
weighed, then about 0.2 to 0.3 grams of latex was added in the
dish. The latex was diluted by adding about 0.5 grams distilled
deionized water. The dish was heated in an 80.degree. C. oven for
about 4 hours until the weight did not change any more. The weight
percent solids (wt. % solids) was calculated according to the
following equation:
Wt.% solids=100.times.(W2-W1)/(W3-W1)
In this equation, W2 is the weight of the dish plus the weight of
the dried polymer latex, W1 is the weight of the dish, and W3 is
the weight of the dish plus the weight of the wet polymer
latex.
Test Method 4: Latex pH
[0148] The latex pH was measured with a pH meter (from Chemtrix,
Rolling Hills Estates, Calif., USA under the trade designation
"MODEL 60A pH METER").
Test Method 5: Glass Transition of Polymer (T.sub.a) by
Differential Scanning Calorimetry (DSC)
[0149] Polymer samples were dried to remove water and/or organic
solvent. The dried samples were then weighed and loaded into TA
Instruments T. aluminum hermetic DSC sample pans. The samples were
analyzed using a TA Instruments Q2000 MODULATED DIFFERENTIAL
SCANNING CALORIMETER ("Q2000 MDSC", including RC-03761 sample
cell), utilizing a heat-cool-heat method in temperature-modulated
mode (-90.degree. C. to 125.degree. C. at 5.degree. C./min. with a
modulation amplitude of .+-.0.796.degree. C. and a period of 60
seconds) under a nitrogen atmosphere. TA Instruments is located in
New Castle, Del., USA.
[0150] In temperature modulated mode, the Q2000 MDSC gave three
signals: cumulative (standard) heat flow, reversing (Rev) heat
flow, and nonreversing (Nonrev) heat flow. The cumulative heat flow
signal was the sum of the reversing and nonreversing heat flow
signals. The reversing signal was the heat capacity (Cp) component,
which exhibited changes in heat capacity and included transitions
such as the T.sub.g (glass transition). The nonreversing signal was
the kinetic component and included kinetic transitions such as
crystallization and chemical reactions.
[0151] Following data collection, the thermal transitions were
analyzed using the TA UNIVERSAL ANALYSIS program. If present, any
glass transitions (T.sub.g) or significant endothermic or
exothermic peaks were evaluated. The glass transition temperatures
were evaluated using the step change in the standard heat flow (HF)
or reversing heat flow (Cp related/REV HF) curves. The onset,
midpoint (half height), and end temperatures of the transition were
noted as well as the change in heat capacity observed at the glass
transition were calculated. Any peak transitions were evaluated
using the heat flow (HF), reversing heat flow (Rev HF) or
non-reversing heat flow (Nonrev HF) curves. Peak area values and/or
peak minimum/maximum temperatures were also determined. The peak
integration results were normalized for sample weight and reported
in J/g.
Test Method 6: Particle Size Via Dynamic Light Scattering
[0152] For a polymer dispersion (or latex) with average particle
size smaller than 1 micrometer, the average particle size of latex
samples was measured with dynamic light scattering instrument
(ZETASIZER NANO ZS, available from Malvern Instruments Ltd.
(Worcestershire, UK)) with diluted latex sample (approximately one
drop of latex in 5 mL of water), following the manufacturer's
instructions, and using polystyrene bead calibration standards.
Test Method 7: Particle Size Via Laser Diffraction
[0153] For a polymer dispersion (or latex) with average particle
size larger than 1 micrometer, the average particle size was
measured by laser diffraction with an HORIBA LA-950 LASER
DIFFRACTION PARTICLE SIZE ANALYZER (Horiba Instruments, Inc.,
Kyoto, Japan) with a diluted latex sample (approximately 1:5 weight
ratio of polymer dispersion to 1% DS-10 surfactant solution in
deionized water), following the manufacturer's instructions.
Test Method 8: 90 Degree Peel Adhesion Test to Polypropylene
Substrate A sample of pressure-sensitive adhesive to be tested was
coated with a hand-spread knife onto a 2.0 mil (0.002 inches,
approximately 51 micrometer) polyester film (HOSTAPHAN 3 SAB,
primed PET film, available from Mitsubishi Polyester Film Inc.
(Greer, S.C., USA)), and dried in a 70.degree. C. oven for 15
minutes to give a dry PSA thickness in a range of 0.9 to 1.2 mil
(approximately 23 to 30 micrometers). The coated film was
conditioned at 23.degree. C. and 50 percent relative humidity for
about 24 hours, and then cut into strips of tape that were 0.5 inch
(approximately 1.3 cm) wide.
[0154] Polypropylene (PP) test panels (5 cm.times.12.5 cm panels
obtained from Aeromat Plastics (Burnsville, Minn., USA) were
prepared by wiping the panels 8 to 10 times using hand pressure
with a tissue wetted with the isopropyl alcohol. The procedure was
repeated two more times with clean tissues wetted with isopropyl
alcohol. The cleaned panels were air dried.
[0155] To do the PP peel adhesion test, first the 0.5 inch (1.25
cm) wide strip of tape was applied to the PP substrate with a 2
kilograms (4.5 pounds) roller. Then the peel test was performed at
a removal angle of 90 degrees according to the procedure described
in the ASTM International standard D3330/D3330M-04 (reproved in
2010), Method F.
[0156] Peel adhesion was assessed with an IMASS SP-2000 slip/peel
tester (available from IMASS, Inc., Accord, Mass., USA) at a peel
rate of 305 mm/minute (12 inches/minute). Peel adhesion values were
reported as both ounces per inch (oz/in) and Newtons per decimeter
(N/dm).
Test Method 9: 180 Degree Peel Adhesion Test to Stainless Steel
Substrate
[0157] A sample of pressure-sensitive adhesive to be tested was
coated with a hand-spread knife onto a 2.0 mil (0.002 inches,
approximately 51 micrometer) polyester film (HOSTAPHAN 3 SAB,
primed PET film, available from Mitsubishi Polyester Film Inc.
(Greer, S.C., USA)), and dried in a 70.degree. C. oven for 15
minutes to give a dry PSA thickness in a range of 0.9 to 1.2 mil
(approximately 23 to 30 micrometers). The coated film was
conditioned at 23.degree. C. and 50 percent relative humidity for
24 hours, and then cut into strips of tape that were 0.5 inch
(approximately 1.3 cm) wide.
[0158] The 0.5 inch (approximately 1.3 cm) wide strips of tape were
applied to a stainless steel (SS) plate with a 2 kg (4.5 pound)
roller and then peel adhesion was assessed with an IMASS SP-2000
slip/peel tester (available from IMASS, Inc. (Accord, Mass., USA))
using a peel angle of 180 degrees and speed of 12 inches
(approximately 30 cm) per minute. Peel adhesion values were
reported as both ounces per inch (oz/in) and Newtons per decimeter
(N/dm).
Test Method 10: Static Shear Strength at 70.degree. C.
[0159] A sample of pressure-sensitive adhesive to be tested was
coated with a hand-spread knife onto a 2.0 mil (0.002 inches,
approximately 51 micrometer) polyester film (HOSTAPHAN 3 SAB,
primed PET film, available from Mitsubishi Polyester Film Inc.
(Greer, S.C., USA)), and dried in a 70.degree. C. oven for 15
minutes to give a dry PSA thickness in a range of 0.9 to 1.2 mil
(approximately 23 to 30 micrometers). The coated film was
conditioned at 23.degree. C. and 50 percent relative humidity for
24 hours, and then cut into strips of tape 0.5 inch (approximately
1.3 cm) wide.
[0160] The static shear strength of an adhesive was determined
according to ASTM International standard, D3654/D3654M-06
(reapproved in 2011)--Procedure A, using a 500 grams load inside an
oven set at 70.degree. C. A test specimen was prepared by
laminating a 0.5 in..times.1 in. (1.3 cm.times.2.5 cm) piece of
adhesive or tape on a polypropylene (PP) or stainless steel (SS)
panel. The time to failure, i.e., time in minutes for the weight to
pull the adhesive away from panel was recorded. If no failure was
observed after 10,000 minutes, the test was stopped and a value of
10,000+ minutes was recorded.
Testing Method 11: Fabric bonding adhesion test
[0161] The fabric, which was a sport nylon (obtained from Joann
Fabrics as item number 1997147, royal blue color) was cut into 1
inch (about 2.5 cm) wide and 6 inch (15.2 cm) long strips. The
adhesive tape was cut into 0.5 inch (1.3 cm) wide and 7-8 inches
(18 to 20 cm) long strips. The tape strip was laid on the fabric
strip. This testing sample was laminated together with a 2 kg (4.5
pound) roller, and then dwelled for 1 hour before testing. The end
of fabric was then placed in the bottom jaw of an Instron device
and the end of tape in the top jaw. The Instron settings were set
as follows: crosshead speed of 12 inch/min (30.5 cm/min), and
average load was taken between 2 inch (5.1 cm) and 5 inch (12.7
cm), which part was the middle portion of the sample. Three
readings were recorded, averaged and reported as the peel
adhesion.
Preparatory Example 1
PE-1
[0162] A polymer was made with two steps. In the first step of the
polymerization, the reactor (an agitated stainless steel reactor)
was charged with a mixture consisting of 88 kg of IBOA and 2.72 kg
of acrylic acid (AA), along with 90.8 grams of IRGANOX 1010, 381
grams of IOTG, 18.2 grams of MEHQ, and 1.8 grams of VAZO 52. The
reactor was sealed and purged of oxygen and then held at
approximately 5 psig (34.5 kPa) nitrogen pressure. The reaction
mixture was heated to 60.degree. C. (140.degree. F.) and the
reaction proceeded adiabatically and peaked at a temperature of
127.degree. C. (260.degree. F.). When the reaction was complete,
the mixture was cooled to below 50.degree. C.
[0163] In the second step, to the reaction product of the first
step was added 10.9 grams of VAZO 52, 3.6 grams of VAZO 67, 5.4
grams of VAZO 88, 5.4 grams of LUPERSOL 101, and 7.3 grams of
LUPERSOL 130 (the initiator components were added as a solution
dissolved in a small amount of ethyl acetate). An additional 191
grams of IOTG was then added. The reactor was sealed and purged
with nitrogen and held at 5 psig (34.5 kPa) nitrogen pressure. The
reaction mixture was heated to 60.degree. C. (140.degree. F.) and
the reaction proceeded adiabatically. After the reaction reached
peak temperature of 176.degree. C. (350.degree. F.), the mixture
was heated at this temperature for 2 hours. The resulting polymeric
material is referred to as PE-1. To get PE-1 out of the reactor,
the heating jacket was drained and EHA is added over a period of 2
hours. The resulting polymer solution, which contained PE-1
dissolved in the added EHA, was then cooled to 93.degree. C.
(200.degree. F.) and stirred overnight.
[0164] As used herein, the term "PE-1" refers to the polymeric
material formed from IBOA/AA (97/3) and having a weight average
molecular weight of 35 kg/mole. All formulations below using PE-1
are based on the weight of the polymer rather than on the weight of
the polymer solution formed by dissolving PE-1 in EHA. The EHA
added to form the polymer solution is considered to be part of the
first monomer composition.
Preparatory Example 2
PE-2
[0165] The polymerization was carried out by a two step reaction
using a VSP2 adiabatic reaction apparatus equipped with a 316
stainless steel test can (available from Fauske and Associates
Inc., Burr Ridge, Ill., USA).
[0166] In the first step of the polymerization, the test can in the
VSP2 reactor was charged with 80 grams of a monomer mixture
(IBOA/AA: 97/3 weight ratio). To the monomer mixture was added 0.1
pph of IRGANOX 1010, 2 pph of chain transfer agent (IOTG), 0.02 pph
of MEHQ, and 0.002 pph of VAZO 52 with each pph based on the total
weight of monomers in the monomer mixture. The reactor was sealed
and purged with nitrogen and then held at approximately 100 psig
(689 kPa) nitrogen pressure. The reaction mixture was heated to
60.degree. C. and the reaction proceeded adiabatically. The
approximate peak temperature was about 180.degree. C. After the
temperature peaked, the mixture was cooled to below 50.degree.
C.
[0167] In a second step, an initiator solution was added to 75
grams of the reaction product of the first step. The solution
contained 0.012 pph of VAZO 52, 0.004 pph of VAZO 67, 0.006 pph of
VAZO 88, 0.006 pph of LUPERSOL 101, and 0.008 pph of LUPERSOL 130
with each pph based on the weight of the polymeric material in the
reaction product. The initiators were dissolved in a small amount
of ethyl acetate and the total initiator solution weighed 0.7
grams. An additional amount of IOTG (1 pph) was then added. The
reactor was sealed, purged of oxygen, and held at 100 psig (793
kPa) nitrogen pressure. The reaction mixture was heated to
60.degree. C. and the reaction proceeded adiabatically, with a peak
temperature of about 124.degree. C. The reaction mixture was warmed
to 170.degree. C. and held at that temperature for 1 hour. The
polymer was then cooled. The resulting polymer had a composition of
IBOA/AA of 97/3 and M.sub.W of 8 kg/mol.
Preparatory Example 3
PE-3
[0168] The formulation and procedure was the same as PE-2 except
the amount of chain transfer agent and the reaction peak
temperatures were altered. In step 1, 1.1 pph of IOTG was added and
the peak temperature was about 134.degree. C. In step 2, 0.55 pph
of IOTG was added and the peak temperature was about 138.degree. C.
The resulting polymer had a composition of IOBA/AA of 97/3 and
M.sub.W of 14 kg/mol.
Preparatory Example 4
PE-4
[0169] The formulation and procedure was the same as PE-2 except
the amount of chain transfer agent and the reaction peak
temperatures were altered. In step 1, 0.6 ppph of IOTG was added
and the peak temperature was about 130.degree. C. In step 2, 0.3
pph of IOTG was added and the peak temperature was about
133.degree. C. The resulting polymer had a composition of IOBA/AA
of 97/3 and M.sub.W of 23 kg/mol.
Preparatory Example 5
PE-5
[0170] 150 grams ethyl acetate, 37.50 grams IBOA, 11 grams IBOMA,
1.50 grams AA, 0.25 grams VAZO 67, and 0.125 grams IOTG were
charged into a bottle. Then the reactants were purged with nitrogen
to remove the oxygen. The bottle was then sealed and put in a
launderometer to react at 60.degree. C. for 24 hours. Then the
polymer solution was placed in an aluminum dish and dried in an
oven to remove the solvent. The dried polymer had a composition of
IBOA/IBOMA/AA of 75/22/3 and M.sub.W of about 34 kg/mol.
Preparatory Example 6
PE-6
[0171] A polymer was prepared by a bulk polymerization within a
polymeric pouch initiated by ultra-violet radiation according to
the method described in Patent Application Publication No. WO
96/07522 and U.S. Pat. No. 5,804,610 (Hamer et al.). The polymer
was made with the formulation of IOA (84.3 pph), IBOA (12.7 pph),
AA (3 pph), IOTG (0.03 pph) and IRGACURE 651 (0.15 pph). Each pph
was based on the total weight of all the monomers. The polymer had
composition of IOA/IBOA/AA (84.3/12.7/3) and Mw of about 625
kg/mol.
Preparatory Example 7
PE-7
[0172] A polymer was prepared by a bulk polymerization within a
polymeric pouch initiated by ultra-violet radiation according to
the method described in Patent Application Publication No. WO
96/07522 and U.S. Pat. No. 5,804,610 (Hamer et al.). The polymer
was made with the formulation of IOA (97 pph), AA (3 pph), IOTG
(0.03 pph) and IRGACURE 651 (0.15 pph). Each pph was based on the
total weight of all the monomers. The polymer had composition of
IOA/AA (97/3) and Mw of about 576 kg/mol.
Preparatory Example 8
PE-8
[0173] DS-10 (3.80 grams) along with 225 grams of deionized water
were added into a beaker and stirred to form an aqueous solution.
AA (9.5 grams), CBr.sub.4 (0.18 grams), and IBOA (180.5 grams) were
added to a separate beaker and mixed well to form an oil phase. The
aqueous and oil phases were then both poured into a 2-liter resin
flask equipped with a thermometer, mechanical agitator with glass
retreat blade impeller, condenser, and nitrogen inlet tube. The
reaction mixture was then stirred at 300 revolutions per minute
(rpm) under a blanket of nitrogen. The reactants were heated to
29.degree. C., and then KPS (0.38 grams), Na.sub.2S.sub.2O.sub.5
(0.10 grams), and a solution of FeSO.sub.4.7H.sub.2O (0.0011 grams
dissolved in 0.5 grams H.sub.2O) were added. The reaction resulted
in an exotherm peak temperature of 48.degree. C. After the exotherm
peak was reached, the reactants were heated to 75.degree. C. and
maintained at that temperature for 1.5 hours. The latex was then
cooled and filtered through cheese cloth to yield a latex having 39
weight percent solids, pH about 4.6, viscosity about 2,000
centipoises, and average particle diameter of about 126 nanometers.
This latex polymer had a composition of IBOA/AA (97/3) and M.sub.W
of 162 kg/mol.
Preparatory Example 9
PE-9
[0174] First, an IBOA/AA (97/3) copolymer with M.sub.W of about
34,000 g/mol was prepared by a bulk polymerization within a
polymeric pouch initiated by ultra-violet radiation according to
the method described in in Patent Application Publication No. WO
96/07522 and U.S. Pat. No. 5,804,610 (Hamer et al.). The polymer
was made with the formulation of IBOA (97 pph), AA (3 pph),
IRGACURE 651 (1 pph), and IOTG (0.75 pph) where each pph is based
on the total weight of monomers. Then 50 grams of the resulting
polymer, 50 grams of toluene, 0.64 grams TRITON X-100, 0.115 grams
DS-4 were mixed together to form an oil phase. The aqueous phase
was prepared by mixing together 25 grams water and 0.115 grams
DS-4. The aqueous phase solution and then the oil phase solution
were added to a 1L stainless steel Waring blender. The mixture was
blended at the high speed setting for 2 minutes to give a polymer
emulsion having about 40 weight percent solids, a viscosity of 3960
centipoises, and an average particle diameter of about 2.9
micrometers.
TABLE-US-00002 TABLE 2 Summary of Preparatory Examples (PE-1 to
PE-9) and DIANAL Polymers Sample Composition M.sub.w (kg/mol)
T.sub.g (.degree. C.) PE-1 IBOA/AA (97/3) 35 95 PE-2 IOBA/AA (97/3)
8 74 PE-3 IBOA/AA (97/3) 14 85 PE-4 IBOA/AA (97/3) 23 93 PE-5
IBOA/IBO/MA/AA 34 83 (75/22/3) PE-6 IOA/IBOA/AA 625 -50
(84.3/12.7/3) PE-7 IOA/AA (97/3) 576 -52 PE-8 IBOA/AA (97/3) 162 95
PE-9 IBOA/AA (97/3) 34 95 DIANAL Described by vendor as 35 60 BR113
a methyl methacrylate resin DIANAL Described by vendor as 30 88
MB2543 a butyl methacrylate resin
The T.sub.g for PE-6 and PE-9 were calculated using the Fox
Equation while the T.sub.g for PE-1 to PE-5, DIANAL BR113, and
DIANAL MB2543 were measured using modulated DSC.
Preparatory Example 10
(PE-10): Preparation of a Short-Wave UV-Cured Liner
[0175] A blend of 70 weight percent TEGO RC-902 and 30 weight
percent TEGO RC-711 was coated onto one side of a 50 micrometer
thick unprimed PET film substrate (available from Mitsubishi
Polyester Film, Inc. (Greer, S.C., USA)) to give a wet coating
thickness of less than 1.0 micrometer. The coated film was then
exposed to the output of three 150W low-pressure mercury amalgam
lamps (manufactured by Heraeus Noblelight (Hanau, Germany)) with a
peak intensity at 185 nm in a nitrogen atmosphere and at a web
speed of 15.2 meters per minute (mpm) to provide a short-wave
UV-cured liner having a cured release surface. Other information
about this liner can be found in U.S. Patent Application
Publication No. 2013/0059105 (Wright et al.).
Example 1
EX-1
[0176] The aqueous phase was prepared by mixing 15.6 grams of
HITENOL BC1025 and 208 grams of de-ionized water in a beaker. The
oil phase was prepared by mixing 267 grams of 2-ethylhexyl acrylate
(EHA), 40.5 grams isobornyl acrylate (IBOA), 5.7 grams of acrylic
acid (AA), 3.8 grams of methacrylic acid (MAA), and 9.5 grams of
the polymer of Preparatory Example 1 (PE-1) in a beaker until of
solution was formed. For further clarification, PE-1 refers to the
polymer formed from IBOA/AA (97/3). The amount of EHA included in
the polymer solution containing dissolved PE-1 (the amount of EHA
added to remove PE-1 from the reactor in which it was prepared) was
included in the total amount of EHA added (267 grams). The oil
phase had a total weight of 326.5 grams. The oil phase was then
poured into the aqueous phase and mixed well. The content was
poured into a 1-liter stainless steel Waring blender container and
homogenized with the blender at the high speed setting for 2
minutes. The mixture was then poured into a 2-liter resin flask
equipped with a thermometer, mechanical agitator with glass retreat
blade impeller, condenser, and nitrogen inlet tube. Then, 0.4 grams
of potassium persulfate (KPS) was added. The reaction mixture was
stirred under a nitrogen blanket and heated to 60.degree. C. and
maintained at 60.degree. C. for 4 hours. The temperature was then
increased to 80.degree. C. within 30 min and maintained at this
temperature for 1 hour. The latex was then cooled and filtered
through cheesecloth to give the latex of EX-1. The latex was
EHA/IBOA/AA/MMA/PE-1 (84/13/2/1/3). The pH was about 2.8.
[0177] FIG. 1 shows the Modulated DSC heat flow signal from the
second heating (2H) cycle for the latex polymer of EX-1 as a
function of temperature in a nitrogen atmosphere.
Example 2 to Example 5
EX-2 to EX-5
[0178] These latexes were made the same way (mini-emulsion process)
with the same formulation as in EX-1, except PE-2 (for EX-2), PE-3
(for EX-3), PE-4 (for EX-4), and PE-5 (for EX-5) were used in place
of PE-1.
[0179] FIG. 2 shows the Modulated DSC heat flow signal from the
second heating (2H) cycle for the latex particle of EX-2 as a
function of temperature in a nitrogen atmosphere.
Comparative Examples 1 and 2
CE-1 and CE-2
[0180] These two latexes were made the same way (mini-emulsion
process) with the same formulation as in EX-1 except that either
DIANAL BR113 (for CE-1) or DIANAL MB2543 (for CE-2) was used in
place of PE-1. Unlike PE-1, neither DIANAL MB2543 nor DIANAL BR113
was prepared from a monomer having a ring structure. The solid
content of CE-1 and CE-2 were both about 60 weight percent. The
viscosities were 270 centipoises for CE-1 and 220 centipoises for
CE-2. The average particle diameters were about 413 nm for CE-1 and
426 nm for CE-2.
Comparative Example 3
CE-3
[0181] This latex was made the same way (mini-emulsion process)
with the same formulation as in EX-1 except that Preparatory
Example 6 (PE-6) was used in place of PE-1. The resulting latex had
a solid of 60 weight percent, a viscosity of 92 centipoises, and an
average particle diameter of 548 nm.
Comparative Example 4
CE-4
[0182] This latex was made the same way (mini-emulsion process)
with the same formulation as in EX-1 except for that Preparatory
Example 7 (PE-7) was used in place of PE-1. After polymerization,
ammonia was added in the latex to adjust the latex pH to about 4.
The resulting latex had a solids content of 58 weight percent.
Comparative Example 5
CE-5
[0183] This latex according to the same method as EX-1, except that
neither PE-1 nor any other previously formed polymer was added. The
reactants coagulated during the polymerization reaction and no
latex was obtained.
TABLE-US-00003 TABLE 3 Composition of EX-1 to EX-5 and CE-1 to CE-5
Average Solids particle Approximate content, Viscosity, diameter,
T.sub.g, Example Composition wt. % cps nm .degree. C. EX-1
EHA/IBOA/AA/MMA/PE-1 62 390 392 -48 (84/13/2/1/3) EX-2
EHA/IBOA/AA/MMA/PE-2 62 612 385 -47 (84/13/2/1/3) EX-3
EHA/IBOA/AA/MMA/PE-3 60 440 437 -47 (84/13/2/1/3) EX-4
EHA/IBOA/AA/MMA/PE-4 63 936 447 -47 (84/13/2/1/3) EX-5
EHA/IBOA/AA/MMA/PE-5 59 136 400 -47 (84/13/2/1/3) CE-1
EHA/IBOA/AA/MMA/ 60 270 413 -50 DIANAL MB2543 (84/13/2/1/3) CE-2
EHA/IBOA/AA/MMA/ 60 220 420 -50 DIANAL BR113 (84/13/2/1/3) CE-3
EHA/IBOA/AA/MMA/PE-6 60 92 548 -50 (84/13/2/1/3) CE-4
EHA/IBOA/AA/MMA/PE-7 58 110 508 -50 (84/13/2/1/3) CE-5
EHA/IBOA/AA/MMA N/A N/A N/A N/A (87/13/2/1)
The T.sub.g for CE-4 was calculated using the Fox Equation while
the T.sub.g of EX-1 to EX-5 and CE-1 to CE-3 were measured using
modulated DSC. N/A means not analyzed because a latex did not
form.
TABLE-US-00004 TABLE 4 Adhesive Properties of EX-1 to EX-5 and CE-1
to CE-4 70.degree. C. Shear 70.degree. C. Shear Peel - SS, Peel -
PP, on SS, on PP, Example oz/in (N/dm) oz/in (N/dm) minutes minutes
EX-1 53.4 (58.4) 24.5 (26.9) 10000 10000 EX-2 48.8 (53.4) 25.5
(27.9) 10000 309 EX-3 52.9 (57.9) 25.5 (27.9) 10000 369 EX-4 51.3
(56.2) 24.58 (26.9) 10000 394 EX-5 49.6 (54.3) 16.7 (18.3) 10000
10000 CE-1 46.8 (51.3) 13.8 (15.1) 10000 171 CE-2 44.6 (48.8) 16.6
(18.2) 10000 151 CE-3 44.6 (48.8) 16.1 (17.6) 10000 159 CE-4 25.7
(28.2) 18.2 (20.0) 10,000 115
Comparative Example 6
CE-6
[0184] 30 grams of CE-3 (60 weight percent solids) having a T.sub.g
of -50.degree. C. was blended with 1.43 grams of PE-8 (39 wt. %
solids) having a T.sub.g of 95.degree. C. The weight ratio of the
CE-3 polymer to the PE-8 polymer was 100 to 3 (100:3). The
adhesives properties of the blend were measured using Test Methods
8, 9, and 10 and are shown in Table 5.
Comparative Example 7
CE-7
[0185] 30 grams of CE-4 (58 weight percent solids) having a T.sub.g
of -50.degree. C. was blended with 1.3 grams of PE-9 (40 wt. %
solids) having a T.sub.g of 95.degree. C. The weight ratio of the
CE-4 polymer to the PE-9 polymer was 100 to 3 (100:3). The adhesive
properties of the blend were measured using Test Methods 8, 9, and
10 and are shown in Table 5.
TABLE-US-00005 TABLE 5 Comparison of Adhesive Properties for CE-3,
CE-4, CE-6, CE-7, and EX-1 70.degree. C. 70.degree. C. Peel - SS,
Peel - PP, Shear Shear oz/in oz/in on SS, on PP, Sample Composition
(N/dm) (N/dm) minutes minutes CE-3 EHA/IBOA/AA/MMA/PE-6
(84/13/2/1/3) 44.6 16.1 10000 159 where PE-6 has a T.sub.g of
-50.degree. C. (48.8) (17.6) CE-4 EHA/IBOA/AA/MMA/PE-7
(84/13/2/1/3) 25.7 18.2 10000 115 where PE-7 has a T.sub.g of
-52.degree. C. (28.2) (20.0) CE-6 100:3 blend of CE-3 with a
T.sub.g of -50.degree. C. and 45.2 12.0 10000 166 PE-8 with a
T.sub.g of 95.degree. C. (49.4) (13.2) CE-7 100:3 blend of CE-4
with a T.sub.g of -50.degree. C. and 20.6 8.1 N/A 147 PE-9 with a
T.sub.g of 95.degree. C. (22.5) (8.9) EX-1 EHA/IBOA/AA/MMA/PE-1
(84/13/2/1/3) 53.4 24.6 10000 10000 where PE-1 has a T.sub.g of
95.degree. C. (58.4) (26.9)
Example 6
EX-6
[0186] A 30 gram sample of the polymeric latex of EX-1 (60% solid)
was blended with 0.22 grams of PARAGUM 500 thickener. Ammonium was
added into the mixture to adjust the pH to about 9.
[0187] A sample of the polymeric latex blend of EX-6 was coated
with a hand-spread knife coater onto the cured release surface of
the release liner of Preparatory Example 10 (PE-10) and then dried
in a 70.degree. C. oven for 20 minutes to give a "transfer tape"
having a latex PSA layer with dry thickness of about 2 mil (0.002
inches, about 51 micrometers).
Example 7
EX-7
[0188] A 30 gram sample of the polymeric latex of EX-1 (60% solid)
was blended with 0.3 grams of PARAGUM 500 thickener and 6.1 grams
of SNOWTACK SE780G (55% solid) tackifier. The ratio of EX-1 dry
polymer to dry tackifier was about 100:20. The pH of the resulting
polymeric latex blend was adjusted to about 9.
[0189] A sample of the polymeric latex blend of EX-7 was coated
with hand-spread knife coater onto the cured release surface of the
release liner of Preparatory Example 10 (PE-10) and then dried in a
70.degree. C. oven for 20 minutes to give a "transfer tape" having
a latex PSA layer with dry thickness of about 2 mil (about 51
micrometers).
Release and Re-adhesion Testing Preparation of EX-6 and EX-7
"Transfer Tapes"
[0190] Samples of "transfer tape" from Examples 6 and 7 were aged
and/or conditioned under one of the three following conditions:
[0191] Condition 1: 23.degree. C. at 50% relative humidity for 24
hours.
[0192] Condition 2: 23.degree. C. at 50% relative humidity (RH) for
24 hours, followed by 32.degree. C. at 90% RH for 48 hours, and
then equilibrating for 1 hour at 23.degree. C. at 50% relative
humidity.
[0193] Condition 3: 23.degree. C. at 50% relative humidity for 24
hours, followed by heating in a 70.degree. C. oven (humidity not
controlled) for 48 hours, and then equilibrating for 1 hour at
23.degree. C. at 50% relative humidity.
[0194] After the conditioning steps, a 25 micrometer (1.0 mil)
primed PET film was laminated to the conditioned latex PSA layer to
form laminated test samples. The primed PET film was prepared by
application of a sol-gel primer as described in Japanese Patent No.
J02200476-A and as further described in U.S. Pat. No. 5,204,219
(Van Ooij et al.), European Patent No. 0301827 B 1 (Woo et al.),
and European Patent No. 0372756 (Strobel et al).
[0195] The peel adhesion value was a measure of the force required
to pull the PET-backed adhesive tape from the short-wave UV-cured
liner at an angle of 180 degrees at a rate of 30.5 cm/min (12
inches/minute). The IMASS MODEL SP2000 PEEL TESTER (IMASS Corp.
(Accord, Mass., USA)) was used to record the peel adhesion value,
summarized as "Release" value in Table 6.
[0196] To determine the re-adhesion value, PET-backed tape samples
were peeled from the short-wave UV-cured liner using the Release
testing method (Test Method 11), and the resulting PET-backed tape
was then applied to the surface of a clean stainless steel panel.
The PET-backed tape sample was rolled down against the panel by
means of two passes with a 2 kg rubber roller at 61 cm/min (24
inches/min). The re-adhesion value was a measure of the force
required to pull the PET-backed tape from the steel surface at an
angle of 180 degrees at a rate of 30.5 cm/min (12 inches/minute).
The IMASS MODEL SP2000 PEEL TESTER was used to record the peel
force, summarized as "Re-adhesion" value in Table 6.
TABLE-US-00006 TABLE 6 Performance of transfer tape samples EX-6
and EX-7 Condition 1 Condition 2 Condition 3 Re- Re- Re- "Transfer
adhesion, adhesion, adhesion, Tape" Release, oz/in Release, oz/in
Release, oz/in Sample g/in (g/cm) (N/dm) g/in (g/cm) (N/dm) g/in
(g/cm) (N/dm) EX-6 11.3 (4.4) 31.4 (34.4) 10.5 (4.1) 30.2 (33.1)
19.4 (7.6) 28.8 (31.5) EX-7 11.1 (4.4) 35.1 (38.4) 10.2 (4.0) 32.7
(35.8) 16.4 (6.5) 35.1 (38.4)
Example 8
EX-8
[0197] The latex of Example 1 (EX-1) was coated with hand-spread
knife coater on 1 mil (0.001 inches, 0.0025 cm) primed PET film,
which was prepared by application of a sol-gel primer as described
in Japanese Patent No. J02200476-A. The latex was dried in
70.degree. C. oven for 20 minutes to give dry adhesive thickness of
2 mil (0.002 inches, 0.005 cm). After being conditioned in a
constant temperature and humidity (23.degree. C. and 50 percent
relative humidity) room for 24 hours, the PSA was evaluated using
the fabric adhesion test (Test Method 11), with the result shown in
Table 7.
Example 9
EX-9
[0198] The latex of Example 2 (EX-2) was coated with hand-spread
knife coater on 1 mil (0.001 inches, 0.0025 cm) primed PET film,
which was prepared by application of a sol-gel primer as described
in Japanese Patent No. J02200476-A. The latex was dried in
70.degree. C. oven for 20 minutes to give dry adhesive thickness of
2 mil (0.002 inches, 0.005 cm). After being conditioned in a
constant temperature and humidity (23.degree. C. and 50 percent
relative humidity) room for 24 hours, the PSA was evaluated using
the fabric adhesion test (Test Method 11), with the result shown in
Table 7.
TABLE-US-00007 TABLE 7 Performance of fabric bonding samples EX-8
and EX-9 "Fabric bonding" Fabric bonding peel Sample adhesion,
oz/in (N/dm) EX-8 10.6 (11.6) EX-9 10.9 (11.9)
* * * * *