U.S. patent application number 15/899622 was filed with the patent office on 2018-06-21 for three dimensional integrated circuit.
The applicant listed for this patent is Silicon Genesis Corporation. Invention is credited to Michael I. CURRENT, Theodore E. FONG.
Application Number | 20180175008 15/899622 |
Document ID | / |
Family ID | 62561845 |
Filed Date | 2018-06-21 |
United States Patent
Application |
20180175008 |
Kind Code |
A1 |
FONG; Theodore E. ; et
al. |
June 21, 2018 |
THREE DIMENSIONAL INTEGRATED CIRCUIT
Abstract
A device is formed by providing a first substrate, depositing a
thickness of range compensating material on a first surface of the
first substrate, implanting ions into the first substrate, the ions
traveling through the range compensating material to define a
cleave profile in the first substrate, the cleave profile including
a contour that corresponds to the thickness of absorber material,
removing the absorber material, and cleaving the first substrate at
the cleave profile, thereby exposing the contour. A substrate with
high thermal conductivity in which the contour defines a coolant
channel effectively removes heat from a three-dimensional
integrated circuit.
Inventors: |
FONG; Theodore E.;
(Pleasanton, CA) ; CURRENT; Michael I.; (San Jose,
CA) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
Silicon Genesis Corporation |
Santa Clara |
CA |
US |
|
|
Family ID: |
62561845 |
Appl. No.: |
15/899622 |
Filed: |
February 20, 2018 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
15829442 |
Dec 1, 2017 |
|
|
|
15899622 |
|
|
|
|
15618048 |
Jun 8, 2017 |
|
|
|
15829442 |
|
|
|
|
14993015 |
Jan 11, 2016 |
9704835 |
|
|
15618048 |
|
|
|
|
62460653 |
Feb 17, 2017 |
|
|
|
62120265 |
Feb 24, 2015 |
|
|
|
62101954 |
Jan 9, 2015 |
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
H01L 25/50 20130101;
H01L 21/8221 20130101; H01L 2924/00 20130101; H01L 2225/1094
20130101; H01L 2924/0002 20130101; H01L 21/76254 20130101; H01L
25/105 20130101; H01L 27/0688 20130101 |
International
Class: |
H01L 25/10 20060101
H01L025/10; H01L 21/822 20060101 H01L021/822; H01L 25/00 20060101
H01L025/00; H01L 21/762 20060101 H01L021/762 |
Claims
1. A method of forming a device, the method comprising: providing a
first substrate; depositing a thickness of range compensating
material on a first surface of the first substrate; implanting ions
into the first substrate, the ions traveling through the range
compensating material to define a cleave profile in the first
substrate, the cleave profile including at least one contour that
corresponds to the thickness of absorber material; removing the
absorber material; and cleaving the first substrate at the cleave
profile, thereby exposing the at least one contour.
2. The method of claim 1, wherein the at least one contour is a
coolant channel.
3. The method of claim 2, further comprising: after cleaving the
first substrate, coating exposed surfaces of the coolant channel
with a coating layer.
4. The method of claim 3, wherein the coating material is a
material that prevents a chemical reaction between a coolant fluid
and the first substrate material.
5. The method of claim 3, wherein the coating layer is a nitride
material or an oxide material.
6. The method of claim 3, wherein a thermal conductivity of the
coating material is higher than a thermal conductivity of the first
substrate.
7. The method of claim 1, wherein the range compensating material
is a photoresist material.
8. The method of claim 1, wherein the first substrate has a thermal
conductivity of at least 130 W/m-K at a temperature of 25 degrees
Celsius.
9. The method of claim 8, wherein the first substrate comprises
carbon.
10. The method of claim 9, wherein the first substrate is a diamond
material or a graphite material.
11. The method of claim 1, further comprising: bonding the cleaved
surface of the first substrate to a second substrate having a
circuit layer.
12. The method of claim 11, wherein the first substrate is bonded
to the second substrate by an oxide layer deposited on a surface of
the second substrate.
13. The method of claim 12, further comprising: after removing the
range compensating layer, depositing a bonding layer on the first
surface of the first substrate; and bonding a third substrate
comprising a circuit layer to the bonding layer on the first
surface of the first substrate.
14. The method of claim 13, wherein the first, second and third
substrates are wafer scale substrates.
15. A method of forming a three-dimensional integrated circuit, the
method comprising: providing a first substrate; depositing a
thickness of range compensating material on a first surface of the
first substrate; implanting ions into the first substrate, the ions
traveling through the range compensating material to define a
cleave profile in the first substrate, the cleave profile including
at least one contour that corresponds to the thickness of absorber
material; removing the absorber material; cleaving the first
substrate at the cleave profile, thereby exposing the at least one
contour; and bonding the first substrate to a second substrate that
includes a circuit layer.
16. The method of claim 15, wherein the at least one contour is a
coolant channel.
17. The method of claim 16, further comprising: depositing a
coating that covers the at least one contour before bonding the
first substrate to the second substrate.
18. The method of claim 17, wherein a thermal conductivity of the
coating layer is greater than a thermal conductivity of the first
substrate.
19. A method of forming a semiconductor device, the method
comprising: providing a first substrate having dielectric and
conductive structures; depositing a thickness of range compensating
material on a first surface of the first substrate; implanting ions
into the first substrate, the ions traveling through the dielectric
and conductive structures and the range compensating material to
define a cleave profile in the first substrate, the cleave profile
including at least one contour that corresponds to the thickness of
absorber material; removing the absorber material; and cleaving the
first substrate at the cleave profile, thereby exposing the at
least one contour.
20. The method of claim 19, further comprising: after implanting
the ions, exposing the first substrate to an atmosphere that
includes a hydrogen gas and an inert gas at a temperature of from
350 degrees Celsius to 500 degrees Celsius for at least one half
hour to repair damage to the dielectric and conductive structures.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] The instant nonprovisional patent application claims
priority to provisional application No. 62/460,653, filed Feb. 17,
2017, and is a continuation in part of U.S. application Ser. No.
15/829,442, filed Dec. 1, 2017 which is a continuation in part of
U.S. application Ser. No. 15/618,048, filed Jun. 8, 2017 which is a
continuation of U.S. Pat. No. 9,704,835, which claims priority to
each of the following provisional applications: U.S. Provisional
Patent Application No. 62/101,954, filed Jan. 9, 2015, and U.S.
Provisional Patent Application No. 62/120,265, filed Feb. 24, 2015.
Each of these documents is incorporated in its entirety herein.
BACKGROUND
[0002] The present disclosure relates generally to the manufacture
of integrated circuit devices. More particularly, the present
disclosure provides a method and resulting devices for stacking and
interconnecting three-dimensional devices using heterogeneous and
non-uniform layers, such as fully fabricated integrated circuits.
By way of example, the integrated circuits can include, among
others, memory devices, processor devices, digital signal
processing devices, application specific devices, controller
devices, communication devices, and others.
[0003] Semiconductor substrates in conventional chip stacks are
typically thinned using a mechanical backgrinding process.
Backgrinding imparts a high level of mechanical stress to the
devices, and can result in substantial thickness variation.
[0004] Excessive heat is an ongoing problem for semiconductor
devices. The heat problem is exacerbated when multiple device
layers are stacked in a three-dimensional integrated circuit.
SUMMARY
[0005] Embodiments of the present disclosure relate to
semiconductor devices including three-dimensional integrated
circuit (3DIC) technologies.
[0006] A method of forming a device includes providing a first
substrate, depositing a thickness of range compensating material on
a first surface of the first substrate, implanting ions into the
first substrate, the ions traveling through the range compensating
material to define a cleave profile in the first substrate, the
cleave profile including at least one contour that corresponds to
the thickness of absorber material, removing the absorber material,
and cleaving the first substrate at the cleave profile, thereby
exposing the at least one contour. In an embodiment, the at least
one contour is a coolant channel. The range compensating material
may be a photoresist material.
[0007] The method of forming a device may include, after cleaving
the first substrate, coating exposed surfaces of the coolant
channel with a coating layer. The coating material may be a
material that prevents a chemical reaction between a coolant fluid
and the first substrate material. For example, the coating material
may be a nitride material or an oxide material. The thermal
conductivity of the coating material may be higher than a thermal
conductivity of a bulk material of the first substrate. In some
embodiments, the first substrate has a thermal conductivity that is
greater than 130 W/m-K at a temperature of 25 degrees Celsius. The
first substrate may include carbon, for example in embodiments in
which the first substrate is a diamond or graphite material.
[0008] After cleaving, the cleaved surface of the first substrate
may be bonded to a second substrate having a circuit layer. In such
an embodiment, the bond may be formed by an oxide layer deposited
on a surface of the second substrate. When the range compensating
layer is removed, a bond layer may be deposited on the first
surface of the first substrate, and used to bond a third substrate
comprising a circuit layer to the bonding layer on the first
surface of the first substrate. The first, second and third
substrates may be wafer scale substrates.
[0009] In some embodiments, hydrogen ions are implanted through one
or more circuit layer that includes high-K dielectric and
conductive elements. In such embodiments, ion implantation may
damage the dielectric and conductive elements. The damage may be
repaired by exposing the substrate to an atmosphere that includes a
hydrogen gas and an inert gas at a temperature of from 350 degrees
Celsius to 500 degrees Celsius for at least one half hour to repair
damage to the dielectric and conductive structures.
[0010] In an embodiment, a method for forming a stacked
semiconductor device includes implanting ions through dielectric
and conductive structures of a first substrate to define a cleave
plane in the first substrate, cleaving the first substrate at the
cleave plane to obtain a cleaved layer including the dielectric and
conductive structures, bonding at least one die to the first
substrate, the at least one die having a smaller width than a width
of the first substrate, depositing a planarization material over
the at least one die, planarizing the planarization material to
form a planarized upper surface over the at least one die, and
stacking a third substrate on the planarized upper surface.
[0011] The ions may be implanted at a temperature of 100 degrees
Celsius or less. In an embodiment the ions are implanted at room
temperature.
[0012] In some embodiments, a total thickness variation (TTV) of
material cleaved from the substrate is 4% or less, 2% or less, or
1% or less. The first, second and third substrates may be wafer
scale substrates. Furthermore, after cleaving the first substrate,
the first substrate may be annealed to repair damage to the
dielectric and conductive structures caused by the ions.
[0013] In an embodiment, an annealing process that repairs damage
to the dielectric and conductive structures is performed at a
temperature of 350 Celsius or greater in an environment that
includes hydrogen gas. Conditions in a repair process should be
sufficient to allow hydrogen to penetrate the device surface and
bond to a molecule that was damaged by an implantation process. In
one specific embodiment, the repair annealing is conducted at a
temperature of 400 Celsius in an atmosphere that includes from 2 to
5 percent hydrogen, with a remainder being one or more inert gas.
In an embodiment, the repair annealing is conducted for a period of
time that is sufficient to allow the hydrogen gas to diffuse though
circuit structures in a device, which may include an interconnect
network of metal and low-dielectric constant dielectric material,
and to occupy passivating sites at damaged dielectric bonds. In an
embodiment, annealing is conducted at a temperature of 400 Celsius
for one hour.
[0014] An embodiment may include depositing a dielectric material
over the at least one die after bonding the at least one die to the
first substrate and before bonding the third substrate over the at
least one die.
[0015] Before implanting the ions, a range compensating layer may
be formed over the first substrate.
[0016] After the first substrate is cleaved, the first substrate
may be bonded to a second substrate. In an embodiment, the second
substrate has second dielectric and conductive structures, and the
second substrate is formed by implanting ions through the second
dielectric and conductive structures. The first, second and third
substrates may be wafers.
[0017] A small die may be one of several types of devices,
including an amplifier, a RF tuner, a radio tuner, a Light Emitting
Diode, and an optical sensor.
[0018] The plurality of conductive structures bay be a plurality of
transistors with a respective plurality of conductive gates that
are separated from respective channel regions by gate
dielectrics.
[0019] In an embodiment, a method of forming a three-dimensional
integrated circuit includes providing a first semiconductor
substrate with a first circuit layer including conductive metal and
dielectric materials, implanting ions through the plurality of
conductive metal and dielectric materials of the first circuit
layer to create a first cleave plane in the first substrate,
cleaving the first substrate at the first cleave plane, providing a
second semiconductor substrate with a second circuit layer
including conductive metal and dielectric materials, implanting
ions through the conductive metal and dielectric materials of the
second circuit layer to create a second cleave plane in the second
substrate, cleaving the second substrate at the second cleave
plane, bonding the first substrate to the second substrate,
stacking at least one die on the second substrate, the die having a
width that is less than a width of the first plurality of circuit
structures, depositing a planarization material over the at least
one die, planarizing the planarization material to form a
planarized upper surface over the at least one die, and stacking a
third substrate on the planarized upper surface.
[0020] In an embodiment, a method of forming a semiconductor device
includes forming an ion range compensating layer over a surface of
a first substrate, implanting ions through the ion range
compensating layer and dielectric and conductive structures of the
first substrate to define a cleave plane in the first substrate,
cleaving the first substrate at the cleave plane to obtain a
cleaved layer including the dielectric and conductive structures,
bonding at least one die to the first substrate, the at least one
die having a smaller width than a width of the first substrate;
depositing a planarization material over the at least one die,
planarizing the planarization material to form a planarized upper
surface over the at least one die, and stacking a third substrate
on the planarized upper surface.
[0021] According to the present disclosure, techniques generally
related to the manufacture of integrated circuit devices are
provided. More particularly, the present disclosure provides a
method and resulting devices for stacking and interconnecting
three-dimensional (3-D) devices using heterogeneous and non-uniform
layers, such as fully fabricated integrated circuits. By way of
example, the integrated circuits can include, among others, memory
devices, processor devices, application specific devices,
controller devices, communication devices, and others.
[0022] A method comprises providing a first substrate having
dielectric structures and conductive structures. Ions are implanted
into the first substrate, the ions traveling through the dielectric
structures and the conductive structures to define a cleave plane
in the first substrate. The first substrate is cleaved at the
cleave plane to obtain a cleaved layer having the dielectric
structure and the conductive structures. The cleaved layer is used
to form a three-dimensional integrated circuit device having a
plurality of stacked integrated circuit (IC) layers, the cleaved
layer being one of the stacked IC layers.
[0023] Three-dimensional stacking and interconnection of
heterogeneous and non-uniform layers, such as fully fabricated
integrated circuits are provided. Techniques are included for a
substantial reduction in inter-layer separation and increase in the
available inter-layer connection density, leading to increased
signal bandwidth and system functionality, compared to existing
chip stacking methods using interposers and through-Silicon vias
(TSVs). The present techniques extend the use of high-energy proton
implants for splitting and layer transfer developed for homogeneous
materials, such as the fabrication of Silicon-on-Insulator (SOI)
wafers, with modifications appropriate for layer transfer of
heterogeneous layers and consideration for damage effects in device
structures.
[0024] In an example, the present disclosure provides techniques
including a method for fabricating an integrated circuit. The
method includes providing a semiconductor substrate comprising a
surface region, a plurality of transistor devices formed overlying
the surface region, an interlayer interconnect region comprising a
structured metal layer and a structured dielectric layer and an
inter-layer connection overlying the plurality of transistor
devices, and a dielectric material overlying the interconnection
region to provide a bonding interface, although there can be
variations. The method includes forming an unpatterned photoresist
material overlying the bonding interface provided from the
dielectric material. In an example, the unpatterned photoresist
material is configured to shield one or more of the plurality of
transistors from electromagnetic radiation in a wavelength range of
below 400 nm and to selectively adjust a depth of a subsequent
implanting process. The method subjects the unpatterned photoresist
material to the implantation process to introduce a plurality of
hydrogen particles through the unpatterned photoresist material to
a selected depth to a cleave region underlying the surface region
of the semiconductor substrate to define a transfer device between
the cleave region and a surface of the dielectric material to form
a thickness of a multi-layer of a plurality of interconnected
conductive metal layers and insulating dielectric having a total
metal thickness of 3 to 5 microns or less. The method removes the
unpatterned photoresist material after the hydrogen implant step.
The method bonds the surface of the dielectric material overlying
the transfer device to a transfer substrate to temporarily bond the
semiconductor substrate to the transfer substrate.
[0025] In an example, the method subjects sufficient energy to a
portion of the cleave region to remove an upper portion of the
semiconductor substrate from a lower bulk substrate material, while
using the transfer substrate to hold the upper portion of the
semiconductor substrate such that the upper portion comprises a
hydrogen damaged region. The energy can be provided spatially or
globally as described in U.S. Pat. No. 6,013,563 (the '563 patent)
assigned to Silicon Genesis Corporation, claims priority to May 12,
1997, and lists Francois J. Henley and Dr. Nathan Cheung, as
inventors, commonly assigned, and hereby incorporated by reference
in its entirety. In an example, the method subjects the hydrogen
damaged region overlying the transfer device to a smoothing process
to remove a portion or all of the hydrogen damaged region and to
form a backside surface. In an example, the method forms a
thickness of dielectric material overlying the backside
surface.
[0026] In an example the backside surface is configured with one or
more provisions for formation of an inter-layer conductive path
linking to a bottom landing pad in the structured metal layer of
the transfer device and a landing pad for a bonded conductive path
to an adjacent device layers.
[0027] In an example, the method further comprises depositing a
dielectric layer to form a suitable bonding interface on the
structured metal layer, the structured metal layer comprising a 5
to 10 microns thick conducting layer formed over a densely
patterned metal interconnect multi-layers for provision of a device
power signal, a ground signal and a frequency synchronization
signal, and the dielectric layer having a plurality of conductive
paths through the dielectric layer on for bonding with inter-layer
conductors in an upper, transfer device layer.
[0028] In an example, the method further comprises aligning of the
transfer device layer to the semiconductor substrate to permanently
bond the inter-layer conducting path. In an example, the method
further comprises removing the temporary bonded semiconductor
substrate from the transfer device. In an example, the method
further comprises forming an internal flow path to allow coolant to
traverse there through to cool the transfer device. The inter-layer
coolant channels may be formed by use of a patterned photo resist
layer added over the unpatterned photoresist layer. The thickness
and/or location of the patterned photo resist layer may be chosen
to adjust the local penetration depth of the proton beam to form a
non-planar cleave surface in the substrate containing the top
surfaces of the coolant channels, with the bottom surface provided
by the lower bond plane.
[0029] In an example, the plurality of transistor devices are
selected from at least one of CMOS devices, bipolar transistors,
logic devices, memory devices, digital signal processing devices,
analog devices, light absorbing and imaging devices, photo-voltaic
cells or micro-electrical mechanical structures (MEMS), or any
combination thereof.
[0030] In an example, the implantation process, proton energy
ranges from 500 kilovolts to 2 MeV. In an example, the cleave
region is positioned 1 to 10 microns from a top surface of the
dielectric material. In an example, the unpatterned photoresist
material is selected with high absorptivity of electromagnetic
radiation with a wavelength less than 400 nm. In an example, the
semiconductor substrate comprises a silicon or other suitable
material for formation of electrical, optical or electromechanical
devices.
[0031] In an example, the implantation process is provided at a
dose ranging from 5E16 to 5E17 particles/centimeter.sup.2. In an
example, the implantation process is provided using a beam line
implanter. In an example, the implantation process is provided by a
linear accelerator (LINAC) or other variation.
[0032] In an example, the cleave region having a peak concentration
at an edge of an implantation range. In an example, the cleave
region comprises a plurality of hydrogen gas-filled
micro-platelets. In an example, the cleave region is characterized
by a stress sufficient to induce propagation of an approximately
planar cleave region. In an example, the cleave region is
configured as a uniform implantation region or a patterned
implantation region. In an example, the cleave region is patterned
or graded to facilitate a controlled cleaving action.
[0033] In an example, the method comprises forming a plurality of
interconnect structures between the backside surface and either the
plurality of transistors or the inter-connect region. In an
example, the method further comprises providing a second
semiconductor substrate comprising a plurality of second transistor
devices and an overlying second dielectric material; and bonding
the second dielectric material configured with the second
semiconductor substrate to form a stacked semiconductor structure.
In an example, the method further comprises forming a patterned
photoresist material overlying the unpatterned photoresist
material.
[0034] In an example, the plurality of transistor devices and the
interconnect region are characterized by a thickness of three
microns and less; wherein the implantation process is characterized
by a range of five microns to ten microns such that a
characteristic size of the plurality of transistor devices and the
interconnect region does not influence the implantation process. In
an example, the plurality of transistor devices and the
interconnect region are characterized by a thickness of three
microns and less; wherein the implantation process is characterized
by a range of five microns to ten microns such that a
characteristic spatial dimension of the range of the implantation
is not interfered by the thickness of the plurality of transistor
devices and the interconnect region. In an example, the plurality
of transistor devices is provided for a memory array or a logic
array.
[0035] In an example, the energy is selected from thermal,
mechanical, chemical, electrical, or combinations thereof to
provide a cleave inducing energy. In an example, the energy is
provided to cause a controlled cleaving action including an
initiation of cleaving and propagation of cleaving. In an example,
the energy is provided to form a plurality of micro-platelet
bubbles in the cleave region. A cleave surface may connect a
network of the micro-platelet bubbles
[0036] The present disclosure achieves these benefits and others in
the context of known process technology. However, a further
understanding of the nature and advantages of the present
disclosure may be realized by reference to the latter portions of
the specification and attached drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
[0037] FIG. 1 is a schematic view of an embodiment of this
disclosure.
[0038] FIG. 2 illustrates a heterogeneous structure containing a
layer of transistor devices and an upper network of metal and
low-dielectric constant materials, with provisions for inter-layer
coolant channels provided by implantation through an additional,
patterned photo resist layer in an example.
[0039] FIGS. 2A-B are simplified cross-sectional views showing use
of patterned oxide as an absorber.
[0040] FIG. 3 is a schematic view of the transferred device layer
viewed at the point of non-uniform surface cleaving after proton
implants through patterned dual-layer photoresist (PR) layers,
viewed after removal of the PR layers and attachment of a
temporary-bonded transfer holder in an example.
[0041] FIG. 4 sketches a to-be-transferred IC device at the point
of the high-dose proton implant with a uniform PR layer in place
over the device metal interconnect layers in an example.
[0042] FIG. 5 is a simplified view of the transfer device layer
after the proton implant, removal of the PR layer attachment of the
temporary bonded transfer holder and completion of the wafer level
cleaving process in an example.
[0043] FIG. 6 shows the major steps applied to the bottom region of
the transferred device layer comprising the formation of an oxide
layer suitable for bonding after removal of the implant damage
layer and final adjustment of the device layer substrate layer
thickness and formation of the dense array of inter-layer metal
connections and bonding pads in an example.
[0044] FIG. 7 shows the cleaved and prepared transferred device
layer at the point of precision alignment with mating interconnect
structures on the upper surface of a lower device layer in the
developing 3D device stack in an example.
[0045] FIG. 8 shows a completed intimate 3D stack of a transferred
IC device bonded to a lower device layer, with aligned inter-level
metal lines in place and bonded at landing pads along the oxide
layer bond interface in an example.
[0046] FIG. 9 shows a schematic example of two device layers
stacked with thick metal interconnect layers in an example.
[0047] FIG. 10 shows one example of a process flow for preparing a
separable substrate according to an embodiment.
[0048] FIG. 10A shows IC processing and/or thinning steps performed
downstream of the process flow shown in FIG. 10.
[0049] FIG. 11 shows a simplified view of a general IC process flow
according to an embodiment.
[0050] FIGS. 12-15 show simplified processing flows according to
various alternative embodiments.
[0051] FIG. 16 is a simplified cross-sectional view showing a
patterned high-K layer in place, incorporating coolant
channels.
[0052] FIG. 17A is a simplified cross-sectional view showing an
example of a detached, unsupported, device layer, under net
compressive stress after its fabrication, on a thin substrate
layer, deforming its thin substrate layer into a concave shape.
[0053] FIG. 17B is a simplified cross-sectional view of the effect
of the addition of a stress-compensating layer to the backside of a
thin substrate containing a stressed device layer on the top
side.
[0054] FIG. 18 is a simplified view of the bonding a high-purity,
single crystalline transfer layer onto a chemically or mechanically
"weak" separation layer on a substrate.
[0055] FIG. 19A shows a simplified cross-sectional view of
high-energy, high dose proton implant to form a Hydrogen-rich layer
placed several microns below the CMOS transistor layer.
[0056] FIG. 19B is a simplified cross-sectional view of CMOS device
layers after completion of the formation of final gate stack and
metal interconnect structures, with a Hydrogen-rich layer formed by
a high-energy, high-dose proton implant performed just prior to the
"replacement gate" fabrication steps.
[0057] FIG. 20 shows a simplified cross-sectional view of a
"top-to-top" metal layer bonding of a transfer device layer and a
lower device layer in a 3DIC stack.
[0058] FIG. 21 illustrates a process for forming a 3DIC structure
with different die sizes.
[0059] FIG. 22 is a simplified cross-sectional view showing an
example of a lower device structure.
[0060] FIG. 23 is a simplified cross-sectional view showing an
example of a stacked device structure.
[0061] FIG. 24 is a simplified cross-sectional view showing an
example of smaller die size devices bonded on a 3DIC.
[0062] FIG. 25 is a simplified cross-sectional view showing an
example of materials deposited over smaller die size devices bonded
on a 3DIC.
[0063] FIG. 26 is a simplified cross-sectional view showing an
example of a 3DIC structure with different die sizes.
[0064] FIG. 27 is a simplified cross-sectional view showing another
example of a 3DIC structure with different die sizes.
[0065] FIG. 28 is a simplified cross-sectional view showing an
example of proton implantation.
[0066] FIG. 29 is a simplified cross-sectional view showing an
example of proton implantation through a range compensating
layer.
[0067] FIG. 30 illustrates thermal conductivity of a silicon
substrate at various phosphorus dopant concentrations and
temperatures.
[0068] FIG. 31 illustrates thermal conductivity of a silicon
substrate at various boron dopant concentrations and
temperatures.
[0069] FIG. 32 illustrates thermal conductivity according to
temperature for 6H--SiC at various temperatures and dopant
concentrations.
[0070] FIG. 33 illustrates thermal conductivity of various carbon
materials.
[0071] FIG. 34 illustrates a bonding step for a transfer layer.
[0072] FIG. 35 illustrates forming a buried Hydrogen profile below
a partially completed device layer.
[0073] FIG. 36 illustrates a complete device layer over the
Hydrogen profile.
DETAILED DESCRIPTION OF THE SPECIFIC EXAMPLES
[0074] According to the present disclosure, techniques generally
related to the manufacture of integrated circuit devices are
provided. More particularly, the present disclosure provides a
method and resulting devices for stacking and interconnecting
three-dimensional (3-D) devices using heterogeneous and non-uniform
layers, such as fully fabricated integrated circuits. By way of
example, the integrated circuits can include, among others, memory
devices, processor devices, digital signal processing devices,
application specific devices, controller devices, communication
devices, and others.
[0075] An embodiment builds and extends the capabilities of two
large areas of technology, layer transfer methods for formation of
bonded stacks of homogeneous layers, such as the formation of
Silicon-on-Insulator (SOI) wafers and diverse methods in present
use and development to form 3-D stacks of electrical devices
through the use of complex interposer layers and sparse arrays of
metal vias for inter-device connections.
[0076] An embodiment provides for methods of stacking and
interconnection of diverse electrical and electro-mechanical layers
with simplified bond and interconnect structures with physical
scales that are a factor of 10 or more smaller than presently
available interposer/TSV methods and providing for greatly
increased number of inter-device electrical connection paths,
resulting in greatly expanded data transfer bandwidth and 3-D
device functionality. The present disclosure also provides for
protection of sensitive device layers from harmful ultraviolet
radiation associated with the use of high-energy proton beam lines
and for construction of inter-level networks of coolant flow
channels for removal of heat from the volume of the functions 3-D
device stack. Further details of the present disclosure can be
found throughout the present specification and more particularly
below.
[0077] Embodiments may combine Silicon-On-Insulator (SOI) wafer
formation approaches utilizing techniques such as H-cut separation
and plasma-activated bonding to achieve a room temperature transfer
process, combined with Si separation utilizing MeV proton
technology, to achieve full-CMOS 3D stacking.
[0078] Such Layer-Transfer (LT) applied to 3D Wafer-Scale Packaging
(WSP) can allow substantial benefits due to its high parallel
connectivity and ability to use different processes. Embedded
RAM/Cache layers are a natural application.
[0079] Conventional WSP approaches may experience challenges in one
or more of the various areas of: bonding, layer alignment, layer
thinning, and layer strata interconnect. For example, layer
thinning to less than 10 um can desirably lead to vias with smaller
aspect ratios.
[0080] Use of plasma fusion bonding allows favorable alignment.
And, embodiments as described herein may make layer alignment and
interconnect practically achievable goals.
[0081] Embodiments utilizing LT technology involving cold
processing, allow processing of wafers with Interlayer Dielectric
(ILD)/metal interconnects. The plasma-activated fusion bond confers
bond strength, ultra-thin bond, no glue layers. As described below,
fast thinning operation is possible, without necessarily requiring
chemical mechanical polishing (CMP), polishing, or grinding
operations.
[0082] Embodiments may be compatible with a variety of IC
processes, including those used to fabricate complementary metal
oxide semiconductor (CMOS) and Random Access Memory (RAM) devices,
etc.
[0083] The use of implantation at MeV energies allows thicker
implantation through an entire device layer (10 .mu.m). Thus, a
full CMOS device layer can be transferred instead of partial
layers.
[0084] Implant scanning techniques may be used. Examples can
include obtaining channeling improvements through "dithering".
[0085] Utilization of MeV protons by embodiments for full CMOS
stacking, may offer certain benefits. Embodiments may allow
avoidance of shadowing due to CMOS layers that include transistor,
dielectric, and/or metal layer structures.
[0086] A 1 MeV proton beam is sufficient to perform H-cut implants
through 8 Cu metal interconnect layers and a full-depth CMOS
microprocessor unit (MPU) with .apprxeq.10 um Si penetration.
[0087] Such a 10 um depth in Si, for a 1 MeV proton beam through a
model 8-layer Cu interconnect array and connected CMOS transistor
layer, is more than adequate for separation of damage peak from
CMOS device region. A figure of merit for the desired minimum
separation below the CMOS transistor layer of the proton damage
region and bond oxide surface of the transferred layer substrate
layer is the depletion depth into the substrate material of a
biased, powered on, bulk CMOS array, on the order of 1 micrometer
for a 1 V supply voltage and a 10 Ohm-cm substrate material. CMOS
transistor layers comprising bulk "finFET" and "fully-depleted SOI"
devices can have somewhat thinner substrate depletion thickness,
depending on the device design and supply voltage. Relative
precision (straggling/range) of 1 MeV proton profiles is much
sharper than standard SOI wafer fabrication implants (at
.apprxeq.40 keV).
[0088] It is further noted that H peak depth can be reduced by
spin-on resist absorber layers. This aspect is further described in
connection with FIGS. 1-9 discussed later below.
[0089] FIG. 10 shows one example of a process flow 1000 for
preparing a separable substrate according to an embodiment. Here, a
donor substrate 1002 is subjected to cleave plane formation 1004,
e.g., by the implantation of hydrogen ions.
[0090] Then, the donor substrate including the cleave plane is
bonded to a handle substrate 1006, e.g. by a plasma-activated
bonding process 1008. Next, the LT occurs by the performance of a
room Temperature-Controlled Cleaving Process (rT-CCP.TM.), such
that a portion of the donor remains with the handle substrate.
Alternatively, a portion of the donor may remain with a temporary
carrier substrate if this layer is to be retransferred again to a
permanent handle substrate (e.g., for back side illumination CMOS
image sensors).
[0091] The remaining portion of the donor substrate is reclaimed
1011 for further use. The handle including the transferred layer
1010 may be subjected to further processing--e.g., epitaxial (EPI)
smoothing and thickening 1012, to produce the separable substrate
1014.
[0092] FIG. 10A shows a simplified process flow 1050 illustrating
downstream steps performed upon the substrate provided by a
substrate manufacturer of FIG. 10. Those steps may comprise IC
processing 1052 (see, e.g., FIG. 11 below) and/or thinning 1054
(see, e.g., FIGS. 12-15 below).
[0093] Specifically, FIG. 11 shows a simplified view of a general
IC process flow 1100 according to an embodiment. Here, the IC Maker
received "special wafer" 1102 and processes IC layer "n+1" 1104
without any modifications.
[0094] Then, the IC layer is bonded onto the Wafer Scale Processing
(WSP) stack (1 to n) 1106. After bonding, the wafer 1102 can be
released.
[0095] Shown last in FIG. 11 is the performance of steps to such as
interconnect processing, Chemical Mechanical Polishing (CMP), etc.
to finish a layer 1108. This can be repeated for a layer "n+2".
[0096] At least four layer transfer (LT) packaging variants are
possible. FIGS. 12-15 describe four options of LT for thinning.
[0097] FIG. 12 shows an embodiment of LT after IC processing. The
simplified process flow 1200 shown in this figure involves putting
a cleave plane 1202 within the substrate 1203, and then cleaving
1204 after IC processing 1206. It requires more intrusive post-IC
process steps.
[0098] FIG. 13 shows an embodiment utilizing cleave onto an
etchable substrate. The simplified process flow 1300 according to
this embodiment allows the substrate 1302 to be more easily etched
1304 than SOI bond-grind back processes.
[0099] In such embodiments, the etchable substrate may be thin. An
electrostatic (ES) chuck can be used to help stiffen cleave and
handle the thin substrate. Transparent substrates can help with
layer alignment.
[0100] FIG. 14 shows an embodiment of a process flow 1400 where the
substrate 1402 comprises a "thin" substrate attached to a
releasable base substrate. The thin substrate can be utilized in
the final 3D product. The releasable substrate is solely used for
handling during the IC process.
[0101] FIG. 15 shows a simplified process flow 1500 according to
another embodiment. Here, the silicon film 1502 is mounted to a
releasable substrate 1504. The releasable substrate is solely used
for handling during IC process 1506 resulting in processed layer
1508. An internal release layer is used after LT. The release layer
is put within the bond plane. LT is used to release the processed
Si-layer, followed by thickening if necessary.
[0102] Certain features and benefits may accrue with one or more
embodiments. For example, H-cut splitting and layer transfer
techniques may be extended to beyond lamination of uniform
composition layers to enable wafer-scale stacking of heterogeneous
and non-uniform individual layers, with the specific application of
intimate stacking of fully-fabricated integrated circuits,
including transistor layers and multi-layer interconnect
networks.
[0103] Embodiments may achieve high data transfer bandwidth with
high-density inter-die interconnect with thin device stacking using
"intimate bonding" with H-cut and layer transfer techniques.
[0104] Embodiments may increase manufacturability and device yield
by use of room to modest-temperature process throughout the
stacking process.
[0105] Some implementations may outline device layer lamination
with H-cut and plasma-bonding operations (using high-alignment
accuracy bonding tools).
[0106] Particular embodiments may utilize variations on front-back
stack and front-front stack bonding, with corresponding
interconnect depths and locations.
[0107] Some embodiments may thin total device layer elements (no
need for interposers), with decreases in RC losses even for
high-density inter-device via connections.
[0108] Various embodiments may lower stress via connections with
much reduced "keep out" area from Cu/Si stress.
[0109] Certain embodiments may implement methods for post-splitting
damage layer removal and substrate thickness reduction (selective
etching)--appropriate for bonding and heat transfer requirements
(much less stringent than SOI wafer layer lamination).
[0110] Certain additional factors of particular embodiments are
also now described. Some such factors may deal with non-uniform
total Cu-interconnect thickness in various IC designs.
[0111] For example, metrology can be used. A scan effect of
non-uniform Cu density collects backscattered proton current from a
large-angle collection electrode facing IC metal surface with a
.apprxeq.1.times.1 um.sup.2 aperture for MeV proton beam. A
precision stage scanner for IC motion under aperture maps out net
Cu density by backscatter current.
[0112] Design rules can be used to address non-uniformity. These
design rules may specify allowable variations in total Cu thickness
across IC device areas. Note: limitation is on cleave plane
roughness (and ability of post-splitting damage removal process to
recover a bondable surface). Wafer-level splitting can be achieved
with large-area checkerboard H distributions.
[0113] A manufacturing process can be used to address
non-uniformity. For example, a "dummy" Cu layer material may be
added at positions of low-Cu thickness, such as inter-layer metal
via channels.
[0114] Embodiments may set the cleave plane depth, not directly
affected by proton energy or variation in total Cu-layer densities,
by constructing IC devices over a high-stress epi layer, such as a
graded Si--Ge thin layer, to localize post-stopping H concentration
along high-stress interfaces. The cleave plane will be set by the
location of the high-concentration H distribution accumulated at
the built in high-stress interface.
[0115] Total proton dose and related risk of dielectric bond damage
(in low-k interconnect and high-k gate dielectrics) from electronic
stopping events may be reduced, by increasing proton lattice damage
accumulation (via nuclear stopping events) by lowered wafer
temperature during proton implantation.
[0116] 1A. A method, comprising:
[0117] providing a first substrate having dielectric structures and
conductive structures;
[0118] implanting ions into the first substrate, the ions traveling
through the dielectric structures and the conductive structures to
define a cleave plane in the first substrate; and
[0119] cleaving the first substrate at the cleave plane to obtain a
cleaved layer having the dielectric structure and the conductive
structures,
[0120] wherein the cleaved layer is used to form a
three-dimensional integrated circuit device having a plurality of
stacked integrated circuit (IC) layers, the cleaved layer being one
of the stacked IC layers.
[0121] The method of clause 1A, wherein the implantation is
performed while keeping the first substrate at a temperature of 100
degrees Celsius or less.
[0122] In one embodiment, the implantation is performed at room
temperature.
[0123] The method of clause 1A, wherein the implantation energy is
greater than 100 KeV and the ions are protons.
[0124] The method of clause 3A, wherein the implantation energy is
300 KeV or greater.
[0125] The method of clause 3A, wherein the implantation energy is
500 KeV or greater.
[0126] The method of clause 3A, wherein the implantation energy is
1 MeV or greater.
[0127] The method of clause 1A, wherein the dielectric structures
and the conductive structures are formed on the first substrate by
performing a plurality of processing steps on the first
substrate.
[0128] As mentioned above, certain embodiments may reduce H peak
depth by spin-on resist absorber layers. This is now discussed
below.
[0129] FIG. 1 is a schematic view of an embodiment at completion of
a two-device 3D stacking process. The upper device layer,
containing heterogeneous layers of transistors formed in
semiconductor materials, usually Si, and a dense network of metal,
usually Cu with various other metals for liners and vias, layers
separated by low-dielectric constant electrical insulator
materials, is separated from a semiconductor wafer after formation
processing by hydrogen implant and associated cleaving process.
During proton implant, the transfer device structure is covered
with a uniform photoresist layer of sufficient thickness and
properties to protect the device layers from damaging exposure to
ultra-violet radiation from recombination processes in the proton
beam line plasma. For the case shown in FIG. 1, the transferred
device layer is also coated with a second photoresist layer
patterned to adjust the depth of the proton beam and the resulting
cleave surface along the paths of a network of coolant flow
channels designed to remove heat from the volume of the completed
3-D device stack. Conductive structures include transistor
junctions in the substrate and a metal interconnect network
contacted to the transistor layer.
[0130] After mounting of the upper device layer to a temporary bond
handle waver, the cleaved lower surface of the transfer device is
processed to remove implant damage in the region of the cleave
surface and adjust the thickness of the transfer device substrate
layer. Then a CVD oxide layer is deposited on the lower surface to
provide an efficient bonding surface and to provide an electrically
insulating and passivated surface for the coolant flow channels, if
present. The lower device surface is then etched and filled with
metal to form inter-level electrical connection to the transfer
device interconnect layers, through a substrate and deposited oxide
layer thickness of the order of 1 or more microns. The inter-level
metal lines in upper transfer device layers are terminated with
metal bond pads with bond surfaces at the same plane as the
deposited oxide bonding layer.
[0131] A similar deposited oxide is formed on the lower device top
surface to provide efficient bonding, a network of vias are etched
and filled with metal to provide electrical connections with the
lower device interconnect layers. The lower metal lines are
terminated by metal bond pads at the same plane as the lower
deposited oxide surface.
[0132] The two sets of metal bonding pads are aligned in a
precision bonding apparatus and subjected to bond anneal
processing, completing the 2-level stack shown in FIG. 1 (with
coolant channels).
[0133] FIG. 2 shows a view of patterned PR and device layer after
layer transfer to lower device layer. In FIG. 2, a heterogeneous
structure containing a layer of transistor devices and an upper
network of metal and low-dielectric constant materials providing
interconnects for an integrated circuit (IC) is coated with a
uniform photoresist (PR) layer, where the resist properties and
thickness is chosen to provide adequate protection for sensitive IC
layers and interfaces from exposure to ultra-violet (wavelength
less than 400 nm) radiation arising from recombination events in
the proton accelerator beam line plasma. The thickness and stopping
of the uniform PR layer is also chosen to adjust the range of the
proton beam to a desired depth below the IC device transistor and
depletion layers.
[0134] In FIG. 2, a second, patterned, PR layer is added over the
uniform PR layer with the thickness and stopping of the second PR
layer chosen to locally adjust the depth of the implanted proton
distribution to provide a non-planar material splitting surface.
When the transferred device layer is bonded to a lower device
layer, after removal of the PR layers and temporary bonding to a
holder layer, the non-planar splitting surface provides a network
path, reflecting the patterning of the upper PR layer, for flow of
coolant in the finished IC device stack for removal of heat during
device operation.
[0135] Also shown in FIG. 2 are inter-level metal vias and bonding
landing pads and oxide bonding interfaces which are added to the
lower section of the upper transferred device layer before bonding
to the lower device layers, described in more detail in later
figures.
[0136] Top absorber layers may be used to (1) locally control the
depth of the peak of the proton damage profile in the transfer
device substrate, thereby controlling the location of cleave
surface at separation; (2) define the lateral location and depth of
coolant channels formed by the depth variations in the cleave
surface; and/or (3) provide a protective layer to absorb
UV-radiation arising from electron capture and subsequent radiative
processes by proton ions in the accelerator beam line.
[0137] Certain embodiments of this process use an un-patterned,
cross-linked photo-resist (PR) layer with a second PR layer
deposited above, lithographically exposed and developed to leave a
patterned PR over layer.
[0138] Other embodiments of this process may use CVD deposited
dielectric films. In certain embodiments, an un-patterned CVD oxide
layer is deposited on the top surface of the metal interconnect
network of the device layer to be transferred to the 3DIC stack.
The thickness of this first CVD oxide layer may be chosen so that
the combined stopping power effects of the CVD oxide, device metal
interconnect network and the device substrate places the proton and
damage peaks at the desired depth of the main cleave plane surface
below the transfer device transistor layer.
[0139] A CVD nitride layer is then deposited on the first CVD oxide
layer to act as an etch stop to protect the underlying oxide layer
during the etching of the top CVD oxide layer.
[0140] Then a second CVD oxide layer is deposited on the nitride
layer. The thickness of the top CVD oxide layer may be chosen to
locally shift the location of the peak of incident proton beam to
be shallower than the location of the main cleave surface by the
desired height of coolant flow channels to be formed by the
subsequent bonding of the transferred device layers to a planar
bonding surface on the top of an underlying device layer in the
3DIC stack.
[0141] A PR layer may then be deposited on the top oxide,
lithographically exposed and developed to leave a patterned PR
over-layer. This patterned PR layer protects the top CVD oxide
layer in the locations where the coolant channels will be formed
during the subsequent oxide etch step, with the nitride layer
protecting the lower oxide layer.
[0142] FIG. 2A is a simplified cross-sectional view of the transfer
device layer at proton implant showing an un-patterned top CVD
layer with thicknesses chosen to shift the peak of the proton
profile to be at a depth of the desired location of the cleave
surface. A patterned second CVD oxide layer, with thickness chosen
to shift the proton beam peak to the height of the (optional)
coolant channels to be formed during the subsequent bonding step to
the 3DIC device stack. A CVD nitride layer deposited between the
two oxide layers act as an etch stop for the top oxide patterning
etch.
[0143] FIG. 2B is a simplified view of upper layers of the transfer
device after deposition of un-patterned CVD oxide and nitride
layers, deposition of a top CVD oxide and PR layers. After
lithographic exposure and development of the PR pattern, exposed
top CVD layer material is etched off. The nitride layer protects to
the lower CVD layer from etch removal. The PR layer is removed
prior to proton implant.
[0144] The use of CVD dielectric layers to form the top absorber
layers may offer the manufacturing benefit of avoiding the process
complications that accompany high-energy implants through polymer
PR films, such as out-gassing of Hydrogen and other volatile
materials due to the bond-breaking in the PR materials by
collisions with the passing proton beam.
[0145] The local control of the proton implant profile into the
device and substrate layer through the use of patterned and
un-patterned CVD top layers can be used to compensate for local
variations pattern density and total layer thickness in metal
interconnect networks both across complex chip die and for
processing diverse chip designs on in-process, large-area wafers.
This capability for local control on the proton profile depth and
location of the cleave surface at separation enables the use of a
constant energy proton beam for processing of diverse device types,
improving in-line wafer manufacturing efficiency.
[0146] FIG. 3 is a schematic view of the transferred device layer
viewed at the point of non-uniform surface cleaving after proton
implants through patterned dual-layer PR layers, viewed after
removal of the PR layers and attachment of a temporary-bonded
transfer holder. Following the non-uniform surface splitting, the
damaged material surrounding the cleave planes, containing H-filled
platelets and adjacent lattice damage regions, is removed and
additional bottom layer material is removed leaving the desired
depth of substrate material containing the IC device transistor and
depletion regions.
[0147] In addition, the non-planar splitting surface is then
treated with deposited oxide films to form passivated surface walls
for coolant channels as well as formation of efficient bonding
surfaces for attachment to adjacent device layers. The lower region
of the transferred device layer is also processed to form
inter-layer metal connection paths between the device layers,
described in later figures and discussions.
[0148] FIGS. 4 through 9 illustrate the 3D stacking process for a
generic set of IC layers using a uniform top PR layer, with no
provisions for incorporated coolant channels, for simplicity.
Further details of these drawings can be found throughout the
present specification and more particularly below.
[0149] FIG. 4 sketches a to-be-transferred IC device at the point
of the high-dose proton implant, with a uniform PR layer in place
over the device metal interconnect layers. The metal interconnect
layers are typically a densely patterned, multi-layer structure,
comprising 10 to 15 layers of Cu metal, for advanced logic devices,
less for memory devices. The Cu metal layers and vias are
electrically isolated by interleaved layers of low-dielectric
constant insulating materials. The net Cu layer thickness is
typically 3 microns or less in modern practice, without the 5 to 8
micron thick metal layers used for accurate distribution of device
synchronization, or "clock", signals, power and ground. Provisions
for additional of thick metal interconnects are offered as part of
the inter-level stacking process.
[0150] The density, optical properties and thickness of PR are
chosen to provide adequate protection of the underlying device
layers from exposure to UV-wavelength recombination radiation from
the proton accelerator beam line plasma and to adjust the depth of
the proton peak and cleave plane below the transistor doping and
depletion layers.
[0151] A view of the transfer device layer after the proton
implant, removal of the PR layer attachment of the temporary bonded
transfer holder and completion of the wafer level cleaving process
is shown in FIG. 5. The cleaving action can be effected by local
application of energy in the form of mechanical, chemical, laser or
other thermal exposure or global energy or any combination thereof.
Cleaving can occur using any of the techniques disclosed in the
'563 patent, which had been incorporated by reference, a blister
technique, or others.
[0152] FIG. 6 shows the major steps applied to the bottom region of
the transferred device layer which include removal of
proton-damaged material in the immediate vicinity of the cleave
plane as well as any additional material in order to obtain the
desired transfer substrate thickness, formation by chemical vapor
deposition (CVD) of a planar bonding interface and formation of
inter-level metal lines connecting the transferred device metal
interconnect network with lower bonding pads at the plane of the
deposited bonding oxide interface. Inter-layer via formation is
shown.
[0153] FIG. 7 shows the cleaved and prepared transferred device
layer at the point of precision alignment with mating interconnect
structures on the upper surface of a lower device layer in the
developing 3D device stack. An embodiment exploits the capabilities
of advanced alignment and bonding apparatus with wafer level
alignment tolerances in the range of 150 nm for 300 mm wafers. Vias
and via landing pads are shown.
[0154] FIG. 8 shows a completed intimate 3D stack of a transferred
IC device bonded to a lower device layer, with aligned inter-level
metal lines in place and bonded at landing pads along the oxide
layer bond interface. Also shown in FIG. 8 is a top deposited oxide
layer with metal vias and landing pads at the bond interface level
for subsequent stacking of an additional device layer on top of the
present transferred device layer.
[0155] For 3D stacking of large-area, high performance logic IC
devices, accurate delivery of power, clock and signal pulses
require low-resistance paths provided by several micron thick metal
lines. These metal layers are too thick to be implanted through
with modest (1 or 2 MeV) energy proton beams but can be provided
for, where needed, as part of the inter-level processing post
implant and cleaving and before the stacking of subsequent device
layers. FIG. 9 shows a schematic example of two device layers
stacked with thick metal interconnect layers, the power device with
the completed metal layers in place if it is the bottom device
layer and the upper transferred device with the thick metal
interconnects added after device transfer and permanent bonding and
before the deposition of bonding oxide and formation of inter-level
metal lines and bond landing pads. The dual device stack has
incorporated thick metal clock & power distribution layers.
[0156] The discussion here is in terms of a stack of generic CMOS
devices. A useful example is a stack of extended memory elements
connected to a data transfer layer for high-bandwidth signal
processing and computation, such as memory stacks presently formed
with the use of interposer layers and metal connection lines, known
as Through-Silicon vias (TSVs), with length of the order of 30 to
50 microns, over 10 times longer than the inter-level connections
envisioned in an embodiment.
[0157] The utility of embodiments can be exploited to provide
fabrication methods for intimate 3-D stacks of diverse electrical
and electro-mechanical devices incorporating heterogeneous device
layers for sensing of visual images, chemical environments and
diverse physical conditions combined with stacked integrated
circuits to provide signal processing, memory and data transmission
in an integrated and robust 3-D device.
[0158] Although the above description is in terms of a silicon
wafer, other substrates may also be used. For example, the
substrate can be almost any monocrystalline, polycrystalline, or
even amorphous type substrate. Additionally, the substrate can be
made of III/V materials such as gallium arsenide, gallium nitride
(GaN), and others. The multi-layered substrate can also be used
according to an embodiment. The multi-layered substrate includes a
silicon-on-insulator substrate, a variety of sandwiched layers on a
semiconductor substrate, and numerous other types of substrates.
One of ordinary skill in the art would easily recognize a variety
of alternatives, modifications, and variations.
[0159] 1B. A method for fabricating an integrated circuit, the
method comprising:
[0160] providing a semiconductor substrate comprising a surface
region, a plurality of transistor devices formed overlying the
surface region, an interlayer interconnect region comprising a
structured metal layer and a structured dielectric layer and an
inter-layer connection overlying the plurality of transistor
devices, and a dielectric material overlying the interconnection
region to provide a bonding interface;
[0161] forming an unpatterned photoresist material overlying the
bonding interface provided from the dielectric material, the
unpatterned photoresist material is configured to shield one or
more of the plurality of transistors from electromagnetic radiation
in a wavelength range of below 400 nm and to selectively adjust a
depth of a subsequent implanting process;
[0162] subjecting the unpatterned photoresist material to the
implantation process to introduce a plurality of hydrogen particles
through the unpatterned photoresist material to a selected depth to
a cleave region underlying the surface region of the semiconductor
substrate to define a transfer device between the cleave region and
a surface of the dielectric material to form a thickness of a
multi-layer of a plurality of interconnected conductive metal
layers and insulating dielectric having a total metal thickness of
3 to 5 microns or less;
[0163] removing the unpatterned photoresist material after the
hydrogen implant step;
[0164] bonding the surface of the dielectric material overlying the
transfer device to a transfer substrate to temporarily bond the
semiconductor substrate to the transfer substrate;
[0165] subjecting sufficient energy to a portion of the cleave
region to remove an upper portion of the semiconductor substrate
from a lower bulk substrate material, while using the transfer
substrate to hold the upper portion of the semiconductor substrate
such that the upper portion comprises a hydrogen damaged
region;
[0166] subjecting the hydrogen damaged region overlying the
transfer device to a smoothing process to remove a portion or all
of the portion or all of the hydrogen damaged region and to form a
backside surface; and
[0167] forming a thickness of dielectric material overlying the
backside surface.
[0168] 2B. The method of clause 1B wherein the backside surface is
configured with one or more provisions for formation of an
inter-layer conductive path to linking to a bottom landing pad in
the structured metal layer of the transfer device and a landing pad
for a bonded conductive path to an adjacent device layers.
[0169] 3B. The method of clause 2B further comprising depositing a
dielectric layer to form a suitable bonding interface on the
structured metal layer, the structured metal layer comprising a 5
to 10 microns thick conducting layer formed over a densely
patterned metal interconnect multi-layers for provision of a device
power signal, a ground signal and a frequency synchronization
signal, and the dielectric layer having a plurality of conductive
paths through the dielectric layer for bonding with inter-layer
conductors in an upper, transfer device layer.
[0170] 4B. The method of clause 3B further comprising aligning of
the transfer device layer to the semiconductor substrate to
permanently bond the inter-layer conducting path.
[0171] 5B. The method of clause 4B further comprising removing the
temporary bonded semiconductor substrate from the transfer
device.
[0172] 6B. The method of clause 5B further comprising forming an
internal flow path to allow coolant to traverse there through to
cool the transfer device.
[0173] 7B. The method of clause 1B wherein the plurality of
transistor devices are selected from at least one of CMOS devices,
bipolar transistors, logic devices, memory devices, digital signal
processing devices, analog devices, light absorbing and imaging
devices, photo-voltaic cells or micro-electrical mechanical
structures (MEMS), or any combination thereof.
[0174] 8B. The method of clause 1B wherein implantation process
ranges from 500 kilovolts to 2 MeV.
[0175] 9B. The method of clause 1B wherein the cleave region is
positioned 1 to 10 microns from a top surface of the dielectric
material.
[0176] 10B. The method of clause 1B wherein the unpatterned
photoresist material is selected with high absorptivity of
electromagnetic radiation with a wavelength less than 400 nm.
[0177] 11B. The method of clause 1B wherein the semiconductor
substrate comprises a silicon or other suitable material for
formation of electrical, optical or electromechanical devices.
[0178] 12B. The method of clause 1B wherein the implantation
process is provided at a dose ranging from 5E16 to 5E17
particles/centimeter.sup.2.
[0179] 13B. The method of clause 1B wherein the implantation
process is provided using a beamline implanter.
[0180] 14B. The method of clause 1B wherein the implantation
process is provided by a linear accelerator (LINAC) process.
[0181] 15B. The method of clause 1B wherein the cleave region
having a peak concentration at an edge of an implantation
range.
[0182] 16B. The method of clause 1B wherein the cleave region
comprises a plurality of hydrogen gas-filled micro-platelets.
[0183] 17B. The method of clause 1B wherein the cleave region is
characterized by a stress sufficient to induce propagation of an
approximately planar cleave region.
[0184] 18B. The method of clause 1B further comprising forming a
plurality of interconnect structures between the backside surface
and either the plurality of transistors or the inter-connect
region.
[0185] 19B. The method of clause 1B further comprising providing a
second semiconductor substrate comprising a plurality of second
transistor devices and an overlying second dielectric material; and
bonding the second dielectric material configured with the second
semiconductor substrate to form a stacked semiconductor
structure.
[0186] 20B. The method of clause 1B further comprising forming a
patterned photoresist material overlying the unpatterned
photoresist material.
[0187] 21B. The method of clause 1B wherein the cleave region is
configured as a uniform implantation region or a patterned
implantation region.
[0188] 22B. The method of clause 1B wherein the plurality of
transistor devices and the interconnect region are characterized by
a thickness of three microns and less; wherein the implantation
process is characterized by a range of five microns to ten microns
such that a characteristic size of the plurality of transistor
devices and the interconnect region does not influence the
implantation process.
[0189] 23B. The method of clause 1B wherein the plurality of
transistor devices and the interconnect region are characterized by
a thickness of three microns and less; wherein the implantation
process is characterized by a range of five microns to ten microns
such that a characteristic spatial dimension of the range of the
implantation is not interfered by the thickness of the plurality of
transistor devices and the interconnect region.
[0190] 24B. The method of clause 1B wherein energy is selected from
thermal, mechanical, chemical, electrical, or combinations thereof
to provide a cleave inducing energy.
[0191] 25B. The method of clause 1B wherein the energy is provided
to cause a controlled cleaving action including an initiation of
cleaving and propagation of cleaving.
[0192] 26B. The method of clause 1B wherein the energy is provided
to form a plurality of micro-platelet bubbles in the cleave
region.
[0193] 27B. The method of clause 1B wherein the plurality of
transistor devices is provided for a memory array or a logic
array.
[0194] 28B. The method of clause 1B wherein the cleave region is
patterned or graded to facilitate a controlled cleaving action.
[0195] 29B. A method for fabricating an integrated circuit, the
method comprising:
[0196] providing a semiconductor substrate comprising a surface
region, a plurality of transistor devices formed overlying the
surface region, an interlayer interconnect region comprising a
structured metal layer and a structured dielectric layer and an
inter-layer connection overlying the plurality of transistor
devices, and a dielectric material overlying the interconnection
region to provide a bonding interface;
[0197] forming an absorber material overlying the bonding interface
provided from the dielectric material, the absorber material
configured to shield one or more of the plurality of transistors
from electromagnetic radiation in a wavelength range of below 400
nm and to selectively adjust a depth of a subsequent implanting
process;
[0198] subjecting the absorber material to the implantation process
to introduce a plurality of hydrogen particles through the absorber
material to a selected depth to a cleave region underlying the
surface region of the semiconductor substrate to define a transfer
device between the cleave region and a surface of the dielectric
material to form a thickness of a multi-layer of a plurality of
interconnected conductive metal layers and insulating dielectric
having a total metal thickness of 3 to 5 microns or less;
[0199] removing the absorber material after the hydrogen implant
step;
[0200] bonding the surface of the dielectric material overlying the
transfer device to a transfer substrate to temporarily bond the
semiconductor substrate to the transfer substrate;
[0201] subjecting sufficient energy to a portion of the cleave
region to remove an upper portion of the semiconductor substrate
from a lower bulk substrate material, while using the transfer
substrate to hold the upper portion of the semiconductor substrate
such that the upper portion comprises a hydrogen damaged
region;
[0202] subjecting the hydrogen damaged region overlying the
transfer device to a smoothing process to remove a portion or all
of the portion or all of the hydrogen damaged region and to form a
backside surface; and
[0203] forming a thickness of dielectric material overlying the
backside surface.
[0204] 30B. The method of clause 29B wherein the absorber material
comprises photoresist.
[0205] 31B. The method of clause 29B wherein the absorber material
comprises oxide.
[0206] 32B. The method of clause 31B wherein the oxide comprises
CVD silicon oxide.
[0207] 33B. The method of clause 29B wherein the absorber material
comprises a patterned layer over an unpatterned layer.
[0208] 34B. The method of clause 33B wherein a thickness of the
unpatterned layer shifts a peak of the proton profile to be at a
depth of the desired location of a cleave surface, and a thickness
of the patterned layer shifts the peak to a height of a coolant
channels to be formed.
[0209] 35B. The method of clause 29B wherein the absorber material
comprises nitride.
[0210] Generally, high-performance logic devices generate heat in
regions of high switching activity in the logic core. These sources
of switching heating are well known design concerns in complex
system on a chip (SOC) and central processing unit (CPU) devices.
The retention of data in memory devices is generally degraded with
increasing temperature, so the integrated stacking of logic and
memory layers is challenged by these thermal concerns. Thermal
controls become more important as the density and diversity of the
3D device stack increases.
[0211] While beneficial for thermal bonding efficiency, use of
oxide layers in the bonding stack may be limited as a heat transfer
layer by the relatively low thermal conductivity of SiO.sub.2. The
use of higher thermal conductivity, electrically insulating
materials as inter-layer structures can increase the heat transfer
from local device thermal source regions.
[0212] Accordingly, in certain embodiments it may be desirable to
add structured high-thermal conductivity layers between heat
generating device layers, in order to facilitate thermal spreading
and removal of heat from the device stack. Specifically, using
high-energy proton implantation, low-thermal budget layer cleaving
and transfer bonding, may facilitate heat spreading from local
device structure "hot spots" and efficiently remove device thermal
energy through the use of local coolant flows.
[0213] Proton cleaving and layer transfer methods, combined with
the patterned cleave regions formed by use of a patterned top layer
of photo-resist (or oxide as discussed below) at the proton implant
step, bonded to a planar device surface to form inter-layer
channels for stack coolant flows, and the use of inter-layer
structures with high-thermal conductivity (and low electrical
conductivity), provide flexible design elements for controlling the
thermal environment in a complex 3D device stack.
[0214] Comparing the thermal conductivity of a variety of common
semiconductor materials indicates a variety of materials with
substantially higher thermal conductivity than SiO.sub.2, with SiC
and Al.sub.2O.sub.3 (sapphire) comprising candidates for this
purpose. Other high thermal conductivity materials may also be used
for the purpose enhancing heat spreading and transport by factors
of .apprxeq.10 to .apprxeq.100, compared to equivalent SiO.sub.2
layers.
[0215] The following Table 1 lists thermal conductivity (in W/m-K)
of several common semiconductor and insulator films:
Si: 130 (W/m-K)
SiO.sub.2: 1.3 (W/m-K)
SiC: 120 (W/m-K)
Ge: 58 (W/m-K)
GaAs: 52 (W/m-K)
[0216] Al.sub.2O.sub.3: 30 (W/m-K)
[0217] Inter-layer thermal spreading layer thickness of
.apprxeq.0.5 to 2 um, may be expected for efficient heat flows.
[0218] FIG. 16 shows a simplified cross-sectional view including a
high-K layer in place, incorporating coolant channels.
[0219] 1C. An apparatus comprising:
[0220] a first integrated circuit including a first metal
interconnect layer;
[0221] a second integrated circuit including a second metal
interconnect layer; and
[0222] an inter-layer structure including a high-thermal
conductivity, low electrical conductivity material and bonded to
the first metal interconnect layer by a CVD oxide bond layer.
[0223] 2C. An apparatus of clause 1C wherein the inter layer
structure further comprises inter-layer channels for stack coolant
flows.
[0224] 3C. An apparatus of clause 1C wherein the high-thermal
conductivity material exhibits a thermal conductivity greater than
1.3 (W/m-K).
[0225] 4C. An apparatus of clause 1C wherein the first integrated
circuit is formed by proton implant into the first metal
interconnect layer followed by cleaving.
[0226] Integrated circuit devices, containing diverse layers of
semiconductor, dielectric and metal materials, may develop
substantial internal stresses during fabrication. Unaddressed,
these stresses may be sufficiently high to warp full thickness Si
wafers, with thickness greater than 700 micrometers, into a variety
of concave, convex, and complex "potato chip" shapes. These
deformations may be sufficiently large to create issues in
fine-line lithography optics during device fabrication.
[0227] If a stress-containing device layer on a detached thin
(e.g., several micrometers) substrate were placed in an unsupported
fashion on a planar surface, the stress-induced deformation of a
wafer-scale combination could pose a challenge for bonding to a
planar substrate surface. Because of these effects, thin device
layers may be attached to stiff bonding structures, capable of
maintaining a planar bond interface with the stressed layer
attached, before they are detached from their initial substrate
wafers.
[0228] FIG. 17A shows a simplified view of an example of a
detached, unsupported, device layer, under net compressive stress
after its fabrication, on a thin substrate layer, deforming its
thin substrate layer into a concave shape. Actual device layer
deformations can be in concave, convex, and complex "potato chip"
shapes. These deformations can lead to challenges when bonding to a
planar surface as well as to bond failures and device degradation
due to excess local stresses during subsequent thermal cycles
during additional fabrication steps and during device
operation.
[0229] Even with the use of a stiff temporary bond holder to form a
stress-containing layer into a planar form suitable for bonding,
un-compensated stresses in a complex bonded stack can lead to bond
failures and IC device degradation from thermal stress during
subsequent fabrication steps and during device operation.
[0230] Accordingly, embodiments may provide for the addition of
stress-compensating layer(s) to the back side of stressed device
thin transfer layers to facilitate a bonding process, including
improved inter-layer device and bond pad alignment, and to
compensate for deleterious effects of subsequent fabrication and
device operation thermal cycles. U.S. Pat. No. 7,772,088 is hereby
incorporated by reference for all purposes.
[0231] The backside stress compensation materials can be chosen of
materials with complementary thermal expansion properties to the
device layer and with thickness sufficient to offset the distortion
effect of the device structure internal stress
[0232] FIG. 17B is a simplified cross-sectional view showing the
effect of the addition of a stress-compensating layer to the
backside of a thin substrate containing a stressed device layer on
the top side. The role of the stress-compensating backside layers
is to (1) facilitate bonding to a planar bond surface, (2) improve
bond pad alignment accuracy during wafer-level bonding, and/or (3)
counteract the effects of differential thermal stress during
subsequent fabrication steps and during device stack operation.
[0233] The stress compensating layers can be formed by direct layer
transfer to the transfer device layer backside while the transfer
device layer is attached to temporary bonding structure. In some
cases, a stress compensating layer can be deposited by CVD or other
approaches.
[0234] Note that the planar, stress compensated, transfer layer can
provide a desirable geometry for achieving a high degree of bond
pad alignment during wafer level bonding, which is one
consideration for successful wafer-level bonding for 3DIC
manufacturing.
[0235] Embodiments may employ single crystal layer transfer onto
chemical or mechanically "weak" separation layers. In particular,
it may be desirable to allow attaching a high-purity, single
crystalline material layer onto a temporary holding layer that is
sufficiently robust to survive the thermal, chemical and mechanical
stresses of IC or other device fabrication processes, but is "weak"
enough to form a separation path under directed chemical or
mechanical action.
[0236] Examples of these weak temporary separation layers can
include but are not limited to (1) oxide layers formed by thermal
growth, CVD deposition or by direct implantation and subsequent
thermal processing, that can form a separation path under an
overlying layer by chemical action of a selective etchant, such as
HF attack on an underlying SiO2 layer, and (2) various forms of
poly-crystalline or porous forms of the general substrate material
that are susceptible to form a separation path under selected
chemical or mechanical attack. Forms of directed mechanical attack
can include but are not limited to, (1) stress-assisted crack
formation initiated by a laterally directed force on a separating
wedge-shaped tool, and (2) kinetic attack by laterally directed
fluid jets into a mechanically weak layer, such as a porous
substrate material region.
[0237] Some forms of chemically or mechanically weak separation
layers may lack the high-level crystalline interface required for
epitaxial growth of high-purity and high-quality crystalline upper
layers useful for fabrication of high performance semiconductor
devices.
[0238] Employing high-energy proton implants to form Hydrogen-rich
layers for mechanical, room-temperature separation along
well-defined cleave surfaces, embodiments can be used to separate
and bond entire device structures, including a fully-formed
transistor layers and multi-level metal interconnect networks onto
suitably chosen temporary separation layers for later fabrication
and device integration processing. This may be followed by
subsequent separation from the carrier substrate.
[0239] The methods and apparatuses according to embodiments can
also be used to separate and bond uniform, high-purity and
crystalline layers to be formed into electrical, mechanical or
optical devices followed by subsequent separation from the carrier
substrate.
[0240] FIG. 18 is a simplified view of the bonding a high-purity,
single crystalline transfer layer onto a chemically or mechanically
"weak" separation layer on a substrate. The upper crystalline
transfer layer is formed to the desired thickness by the use of
high-energy proton implantation and room-temperature separation
along the peak of the proton distribution. The upper transfer layer
can be a uniform crystalline layer or including a combination of
IC, mechanical or optical devices and their corresponding metal
interconnect networks.
[0241] Embodiments may also provide proton implants useful for
separation and layer transfer stacking of highly-sensitive CMOS
device structures. As previously mentioned, embodiments utilize
high-energy proton implants to form a Hydrogen-rich cleave surface
several microns below the combined thickness and stopping power
effects of a combination of top layers of photo-resist or CVD
dielectrics, and a multi-layer metal interconnect network and
transistor layers.
[0242] Radiation damage effects arising from the passage of a
high-dose, high-energy proton beam through the metal interconnect
and transistor layers, may be at manageable levels--recoverable by
standard annealing cycles at modest temperatures. Moreover, where
specific radiation damage effects are of particular concern,
embodiments can include an implementation that bypasses concerns
for radiation damage effects in device dielectric layers.
[0243] One issue relating to possible radiation damage during
high-dose, high-energy proton implants into CMOS device layers and
their associated metal interconnect network layers, is
bond-breaking effects in various dielectric layers. This can be due
to electronic stopping events from the passage of the energetic
proton beam or from UV-radiation from ion-electron relaxation
following recombination event in the accelerator beam line.
[0244] When the high-dose, high-energy proton implantation is
performed at specific points during the CMOS device fabrication
process, radiation effects from the proton beam can be
substantially avoided. One point in the CMOS process can be
identified as occurring after the high temperature (e.g., greater
than 500.degree. C.) processes associated with activation of
dopants in CMOS junctions are completed, and before the deposition
of sensitive gate stack oxides and subsequent incorporation of
inter-layer dielectrics in the metal interconnect network.
[0245] At such a point in the CMOS fabrication process, the
principal material in the device wafer is crystalline silicon in
doped junctions, with poly-silicon filled lateral isolation
regions, and the substrate wafer. The only substantial, long-term
radiation damage effects in predominantly silicon material are
associated with lattice damage arising from the nuclear stopping
components of the proton slowing down process.
[0246] Lattice damage events for a high-energy proton beam may be
localized near the peak of the proton profile. According to
embodiments, that peak may be placed several microns below the CMOS
junctions in the transistor layer and provide key hydrogen-trapping
sites for localization of the cleave surface during layer
separation. The several micron separation between the CMOS
transistor layer and its associated carrier depletion layers and
the proton-induced lattice damage in the region of the subsequent
layer separation, may be sufficient to avoid risk for deleterious
device effects from the proton lattice damage layer.
[0247] In many advanced CMOS devices, the gate stack regions are
initially defined by temporary films and structures which are
"replaced", after completion of the high-temperature thermal
cycles, by final device structures incorporating high-dielectric
constant ("high-k") gate oxides and multi-layer metal gate
electrodes. Following the "replacement gate" fabrication cycles,
the material properties of the final gate and inter-metal layer
("low-k") dielectrics limit allowable thermal cycles for the final
CMOS device fabrication process to be less than 500.degree. C.
[0248] A high-dose proton implant performed at the point just
before the "replacement gate" fabrication, would avoid risk of
damage to the final device gate and inter-metal layer dielectrics
and would not be exposed to 500.degree. C. or higher thermal
cycles, that could lead to spontaneous layer separation prior to
the desired non-thermal separation process at layer separation
after the fabrication of the transfer device layers is
completed.
[0249] FIG. 19A shows a simplified cross-sectional view of
high-energy, high dose proton implant to form a Hydrogen-rich layer
placed several microns below the CMOS transistor layer. This is
performed after completion of >500.degree. C. anneals associated
with dopant activation in the transistor junctions and before
fabrication of "replacement gates" including final device gate
dielectrics and metal gate electrodes.
[0250] FIG. 19B is a simplified cross-sectional view of CMOS device
layers after completion of the formation of final gate stack and
metal interconnect structures, with a Hydrogen-rich layer formed by
a high-energy, high-dose proton implant performed just prior to the
"replacement gate" fabrication steps. The materials properties of
the final gate and inter-metal layer dielectrics limit the
fabrication process temperatures to be below 500.degree. C., which
also avoids conditions leading to spontaneous splitting along the
Hydrogen-rich region prior to the desired separation, by
non-thermal approaches, after completion of the full device
structure.
[0251] Utilization of methods and apparatuses according to
embodiments may permit modulation of inter-layer bandwidth by
stacking order and inter-layer thickness. Specifically, a principal
goal of 3DIC stacking is to provide an alternative path for
increasing the bandwidth for signal processing communications
between devices.
[0252] Bandwidth is the product of the data signal frequency, often
approximated by the CPU clock frequency, and the number of external
communication channels. For much of its history, IC development has
focused on increasing the CPU and other data processing chip cycle
frequencies, possibly at the cost of increasing chip power use. The
number of communication channels has been limited by the density of
bond pads available along the periphery of a planar device.
[0253] The development of 3DIC stacking methods has increased the
possible number of vertical channels, measured by the density
inter-layer communication lines. This density of inter-layer
communication channels increases as vertical connection channel
density increases. A convenient measure of the density of
inter-layer connections is the inverse square of the communication
pin separation or "pitch". Specifically, IO density=1/(pin
pitch).sup.2.
[0254] The minimum metal channel or "pin" pitch, depends on a
variety of process and device considerations. One factor is the
aspect ratio (AR) of the inter-layer metal channels: the ratio of
the metal line diameter to the length of the via hole to be filled.
Conventional "Through Silicon Via" (TSV) structures may typically
exhibit an AR of between about 5 to 20. This is significantly
higher than the typical design rules for vias in high-density
metallization for IC devices--often with an AR of less than 2.
[0255] One device consideration affecting the packing density of
conventional TSV structures, is the inter-device stress arising
from the different thermal expansion of micrometer-scale Cu
cylinders and Si device materials. The undesirable local stress in
the immediate surroundings of a Cu via line can lead to design
rules defining micrometer-scale "keep out" zones, where active
circuit element are excluded from the vicinity of Cu via landing
pads. This affects circuit density, performance, and yield.
[0256] Accordingly, methods and apparatus of specific embodiments
may provide one or more procedures to locally increase the
inter-level metal channel density and corresponding communication
bandwidth between adjacent device layers. Use of high-energy,
high-dose proton implants through a substantially completed metal
interconnect network and fully formed CMOS transistor layer for
formation of a Hydrogen-rich region for non-thermal layer
separation and bonding onto a 3DIC stack, provides an inter-layer
separation of a few micrometers (or less, for the cases of device
layers on SOI buried oxides or other device types with minimal
carrier depletion layer thicknesses). This allows substantially
less inter-layer separation than the tens of micrometers typical of
present day TSV and interposer stacking methods. The thinner
inter-device Si layers and elimination interposer and associated
adhesive layers provide by embodiments allows for fabrication
shorter and thinner inter-device metal signal connections and
greatly reduces the "dead zone" effects arising from thermal stress
of present day several microns thick Cu TSV channels.
[0257] Where high inter-layer bandwidth is desired (e.g.,
connections from CMOS image sensor layers and signal processing
devices), some embodiments may employ a variety of layer transfer
techniques to align and bond the top layer of the metal
interconnect network of the transfer device to inter-layer
connection channels in the top layer of the metal network of the
lower device layer in the 3DIC stack. Such layer transfer
approaches are outlined in FIGS. 12 through 15.
[0258] With this particular procedure, the inter-layer
communication channel density can be expected to be similar to the
pin density in the top layer metallization layers in the two device
layers, with pin pitch on the order of a few micrometers or less.
This "top-to-top" layer bonding results in a factor of 100 to
1,000.times. higher inter-layer connection density, and
corresponding increased bandwidth, than existing 2.5D and 3D chip
stacking technologies.
[0259] FIG. 20 shows a simplified cross-sectional view of a
"top-to-top" metal layer bonding of a transfer device layer and a
lower device layer in a 3DIC stack. This approach can provide
inter-level metal connection channel densities, and corresponding
increased bandwidth, similar to via densities of the top metal
layers of CMOS devices.
[0260] Specific examples of 3DIC structures according to
embodiments may be characterized by an TO density (in Pins/cm2) of
between about 1.0E+06-1.0E+08, over a pin pitch range (in nm) of
1.E+02-1.E+04. In an example, for a TSV depth of 1 .mu.m, aspect
ratios (depth:minimum width of diameter) may range from between 10
to 1 over a range of TSV diameters from about 0.1 to 1 .mu.m.
[0261] As mentioned above, proton implantation to form a 3DIC
structure according to embodiments, may take place at energies of
about 1 MeV, including energies of between about 300 keV-5 MeV,
about 500 keV-3 MeV, about 700 keV-2 MeV, or about 800 keV-1 MeV.
Incorporated by reference herein for all purposes, is U.S. Patent
Publ. No. 2008/0206962.
[0262] It is noted that implant properties of hydrogen ions at such
higher energy ranges may vary as between the 40 keV energies
typical of layer transfer processes for SOI wafer manufacturing. A
first order description is the ratio of the "half-width" of the
proton profile reflecting "straggling" (<.DELTA.X>), to the
depth of the "projected range" profile (<X>).
[0263] Comparison of such <.DELTA.X>/<X> results in an
example, is as follows:
[0264] proton implant energy 40 keV:
<.DELTA.X>/<X>=0.196.apprxeq.0.2
[0265] proton implant energy 1 MeV:
<.DELTA.X>/<X>=0.048.apprxeq.0.05
Thus, the 1 MeV proton profile is .apprxeq.4.times. "sharper" than
the 40 keV profile.
[0266] 3DIC structures are commonly stacked at the wafer level.
Wafer-level processing, especially when combined with the
directness of the transfer methods for fully-metallized CMOS
devices described herein, has substantial advantages for economic
and efficient processing.
[0267] Wafer-level processing of bonded structures typically
assumes that the same size wafers are used, and the placement of
dies on the joined wafers are closely coordinated to result in
vertical stacked 3DIC structures after separation into discrete
systems. These conditions are commonly met for large-area logic and
memory devices fabricated on 200 or 300 mm Si wafers in
mass-production foundry processing.
[0268] Many desirable components for communication linkage, such as
RF tuners, amplifiers and the like, are considerably smaller in die
size than cm.sup.2-sized logic and memory devices. These smaller
die sized devices may be fabricated on diverse wafer sizes such as
100 and 150 mm, and may use non-bulk silicon substrates such as
Radio-Frequency Silicon on Insulator (RF-SOI), GaAs, etc.
[0269] There are many challenges associated with stacked structures
with diverse die sizes. Device alignment is important, and can be
complicated by the thickness variation inherent to backgrinding
processes used to thin dies. Total Thickness Variation (TTV) for
backgrinding processes are typically in the range of about 5%. Such
variation can compound when multiple layers are stacked, making it
difficult to perform semiconductor forming processes to facilitate
interlayer connection. As a result, stacked devices employ
relatively large solder bumps and interposer layers to connect
devices in a vertical stack. In addition, many devices use bonding
wires to connect multiple layers that are disposed side-by-side in
a package.
[0270] Embodiments of the present disclosure include devices and
processes for 3DIC structures that include heterogeneous die sizes.
Dies that are formed by performing ion implantation through circuit
structures including dielectric and conductive materials to cleave
base substrates simplify the thinning process, and have less
variation than backgrinding processes. TTV values that can be
obtained by ionic cleaving may be, for example, less than 2%, less
than 1.5%, and less than 1.0%. In addition, backgrinding applies a
substantial amount of mechanical stress to semiconductor devices,
which may disrupt structures in the device, causing further
alignment and performance issues.
[0271] FIG. 21 shows an embodiment of a process 2100 for forming a
3DIC structure with different die sizes. An advantage of process
2100 is that it combines the economic advantages of wafer-level
processing with the flexibility of incorporating layers of smaller
area dies, which may be fabricated on a diverse variety of
substrate materials and wafer sizes into composite 3DIC
structures.
[0272] A base device structure is prepared at 2102. FIG. 22
illustrates an embodiment in which a base device structure 2202 is
prepared using high-energy hydrogen implantation, where the peak
concentration of a high-dose hydrogen implant is located in the
substrate region below a metallized layer which may be, for
example, a CMOS or MEMS device layer.
[0273] Following cleaving along an approximate location of the
hydrogen concentration peak, residual damage along the cleave plane
is removed and the transferred device layer is bonded to another
wafer-scale device layer as shown in FIG. 23. In the embodiment
shown in FIG. 23, the base device structure 2202 includes two
wafer-level bonded semiconductor layers, 2202A and 2202B, which are
formed by implanting ions through dielectric and conductive
structures that are formed on semiconductor wafers. In some
embodiments, the base device structure 2202 may be more than two
stacked semiconductor layers or a single stacked semiconductor
layer.
[0274] FIG. 23 illustrates wafer-level bonding in a device
orientation where the bonding occurs along the metalized layers of
the two layers, where the upper (second) device layer 2202B is face
down compared to the lower (first) device layer 2202A, which is
face up. Although only a single device of each of the first and
second device layers are illustrated in FIG. 23, in an embodiment,
cleaving and bonding operations are performed on a plurality of
devices on a wafer.
[0275] Before the two device layers 2202A and 2202B are bonded
together, there is an opportunity for deposition and patterning of
one or more intermediate layers 2204, insulated by inter-metal
dielectric materials, that can provide both vertical (device to
device) and lateral connections for signal, timing, poser and
ground connections. Such inter-device metal connection layers 2204
are analogous in function to redistribution layers (RDL) in modern
2.5 D multi-chip packaging schemes.
[0276] After bonding of the first device layer 2202A to second
device layer 2202B, with inclusion of the intermediate connection
layer 2204, vertical vias 2206 are etched and filled with metal to
provide connections between the device layers and a top surface
array of bond signal pads.
[0277] An interconnect layer 2208 is formed on the exposed upper
surface of base device structure 2202 in process 2104. The
interconnect layer 2208 may include appropriate bonding pads on the
top layer of the base device structure 2202 for direct pick and
place addition of various smaller die components, as well as
lateral wiring connections to interface between the contact pads
exposed by the base device structure 2202.
[0278] In an embodiment, the top metal layers of interconnection
layer 2208 include multi-level metal networks for lateral
communication, power and ground connections for a composite device,
with the addition of bonding pad arrays designed for placement and
bonding of face-down metal connections with smaller, diverse die
types.
[0279] As illustrated in FIG. 24, one or more die 2210 is placed on
the interconnect layer 2208 in process 2106. The one or more
smaller die 2210 may be placed using known pick and place
techniques to align terminals of the one or more smaller die 2210
with the bonding pads exposed on the upper surface of the
interconnect layer 2208. The location and metal-to-metal bonding of
discrete die types on a composite wafer-level bonded structure 2202
can be accomplished by an automated die pick, place and bond
apparatus.
[0280] In some embodiments, smaller dies 2210 have different sizes
and thicknesses from one another. The smaller dies 2210 may be a
heterogenous set of devices that perform different functions, or a
homogenous set of devices.
[0281] Since dies 2210 may have various thicknesses, and in some
embodiments may be thicker than the desired substrate thickness
(e.g., in the range of 1 to 10 um), a layer of deposited material
with a similar erosion rate under CMP processes as the substrate
die of the added smaller devices may be formed between and over the
dies 2210 at 2108.
[0282] For example, as seen in FIG. 25, dielectric material 2212
may be deposited over exposed surfaces of the device structure
including dies 2210 in process 2108. The dielectric material 2212
provides for electrical isolation of the smaller dies 2210. The
dielectric material 2212 may be one or more of a variety of
materials commonly used in the semiconductor industry that provide
insulation from stray current flows, including a CVD oxide or other
suitable insulating material.
[0283] In some embodiments, a filler material 2214 is deposited
over the dielectric material 2212 at 2110. When the dies 2210 are
Si devices, the deposited layer may be plasma deposited poly-Si or
amorphous-Si. The filler material 2214 may be selected to have a
similar erosion rate to the dielectric material 2212 and the
substrate material of the smaller die devices 2210 when planarizing
the structure at 2112, for example by performing CMP.
[0284] Although process 2100 and the associated figures describe
forming a separate dielectric material 2212 and filler material
2214, in some embodiments only a single material or more than two
materials are deposited over the dies 2210.
[0285] A planarization process is performed at 2112 to planarize
the upper surface of the device until contact pads are exposed. The
slurry chemistry for the CMP process may be selected based on the
dielectric material 2212 and the filler material 2214 to achieve
approximately equal erosion rates of the substrates in the added
smaller die structures 2210 and the deposited over-layer materials.
In an embodiment, planarization process 2112 thins the added
smaller die 2210 substrates to thicknesses of about 10 .mu.m or
less for later formation of vertical metal vias for interconnection
with later added structures and bonding pads. In an embodiment,
planarization 2112 is performed until in an overall layer thickness
of 10 to 30 .mu.m is obtained.
[0286] In addition, planarization process 2112 provides a planar
top surface for the newly enlarged composite device structure for
subsequent addition of multi-level metal interconnects for lateral
signal, power and ground connections as well as bonding pads
designed for connections of additional layers added to the
composite structure with wafer-level or discrete die placement
methods. In an embodiment, the planarization process 2112 may be
performed on the top surface until the surface roughness has an RA
value that is 5 Angstroms or less, or 3 Angstroms or less.
[0287] The deposition and planarization elements of process 2100
may be performed such that substrates of the smaller dies 2110 are
thinned to a desired thickness. In addition, the dielectric and
filler materials 2208 and 2210 provide mechanical support, and in
some embodiments one or more of the layers formed over dies 2110
facilitate heat transfer out of a final 3DIC structure.
[0288] In some embodiments, no additional layers are placed on the
smaller dies 2210. In those embodiments, the device may be packaged
after planarization 2112 without placing upper device structures on
the smaller dies 2210.
[0289] As illustrated in FIG. 26, interconnect structures 2216 to
electrically couple at least one of the one or more smaller dies
2210 to upper device layers 2218 of the 3DIC are formed at process.
The interconnect structures 2216 may be formed on exposed surfaces
of smaller dies 2210, and/or on an exposed surface of upper device
structure 2218 before it is placed onto the smaller dies. In
various embodiments, the upper device structure 2218 may be a
single substrate as illustrated in FIG. 23, two wafer level bonded
substrates, or more than two substrates.
[0290] Embodiments of process 2100 provide for the addition of
layers of discrete dies to a wafer-level process flow for bonding
of multi-level device structures into a composite 3DIC structure. A
device made according to process 2100 may have lateral electrical
isolation of diverse added dies in the multi-chip layer, and may
include vertical metal connections in dense, high-band width
networks as well as lateral metal connection networks for the
composite device structure containing wafer-level and discrete die
placements. When smaller dies of different thicknesses are
provided, process 2100 can accommodate these structures by
planarization and thinning of the diverse substrates in the
composite device layer.
[0291] In the course of 3DIC fabrication using wafer-level transfer
of metalized transistor and MEMS device layers, situations arise
where it is advantageous to locally adjust the depth of the
hydrogen implantation, which determines the approximate local
location of the cleave plane in the in-process step for layer
transfer.
[0292] A major challenge for operation of dense high-performance
circuit elements with 3DIC stack arrays, such as micro-processor
logic and graphics processors for image analysis and display
drivers, is the removal of heat from active device cores.
[0293] As described above, a network of channels for flow of
coolant fluids can be formed in close proximity to a
heat-generating transistor layer by adjusting the local penetration
depth of the hydrogen implant profile by adding a patterned "range
adjusting" layer comprised of materials formed at a sufficient
thickness to result in a local offset in the hydrogen depth and
subsequent cleave surface. After cleaving of the device transfer
layer along the variable depth cleave surface, a network of
channels can be formed in the bottom surface by bonding the
transfer device layer to a planar surface, such as the planarized
top layer of another device layer, as shown in FIG. 1.
[0294] The range compensating layers may comprise patterned layers
of CVD silicon oxide of appropriate thickness combined with an
unpatterned silicon nitride layer, which acts as an etch stop for
the removal of the patterned oxide layer after the implant step. In
another embodiment, the range compensating layer is a patterned
layer of thick photoresist.
[0295] FIG. 27 shows an embodiment of a device that includes
diverse sized dies 2710 disposed between a lower which has several
features that are not present in the device of FIG. 26. The diverse
dies 2710 are formed over a base device structure 2702, which
includes upper and lower parts that may be formed by implanting
ions through metal and dielectric structures to form a cleave layer
at the wafer level, and bonding the upper and lower parts to form
the lower device structure 2702. In addition, the device of FIG. 27
shows a plurality of cooling channels 2720 that are disposed at the
interface between the upper and lower parts of the base device
structure 2702, and at a lower surface of the substrate of upper
device structure 2718.
[0296] Another feature of the device shown in FIG. 27 that is
different from the device of FIG. 26 is the location of vertical
interconnect structures. While the embodiment of FIG. 26 has
vertical vias 2206 that penetrate the upper device structure 2218
and filler material 2214, FIG. 27 shows vertical vias 2722 that
pass through small die structures 2710 to provide electrical
communication between devices of the lower structure 2702, the
small dies 2710, and the upper structure 2718. Persons of skill in
the art will recognize that numerous variations are possible beyond
the specific features shown in FIG. 26 and FIG. 27.
[0297] Processes according to the present disclosure may be applied
for transferring devices which contain large variations in the
density of total metal layers in local regions of the transferred
device. When implanting hydrogen ions through metal and dielectric
structures of a semiconductor device, the depth of the cleave plane
may be affected by the arrangement of conductive and dielectric
structures in a circuit layer. For example, as seen in FIG. 28, the
depth of peak energy, which manifests as a cleave plane, may be
less in a high-density area of a device than a low-density, or
sparse area. In some circumstances, it may be desirable, for
purposes of process simplicity in the layer transfer bonding, to
have the implanted hydrogen profile depth at the same planar
location below a circuit layer.
[0298] Hydrogen cleave plane depth can vary in between different
areas of a high-performance microprocessor where a dense,
multi-layer metallization layer over the logic core is surrounded
by more sparse metal interconnect networks in memory (e.g. embedded
SRAMs) and timing and input/output circuits. Other examples include
optical sensor (cellphone cameras, etc.) devices where densely
metalized image processing circuits are surrounded with more
sparsely metalized photosensor arrays. In addition, MEMS devices
often contain multiple layers and open spaces of various material
densities. These variations can translate to different stopping
powers for hydrogen ions, which can vary the depth of a cleave
plane. In an embodiment that includes transferring devices
containing MEMS devices.
[0299] As seen in FIG. 29, local hydrogen profile shifts can be
compensated for by a patterned range compensating layer 2902 of
appropriate thickness and hydrogen stopping power to result in an
approximately planar hydrogen peak profile depth and cleave plane.
Accordingly, embodiments of the present disclosure may include
forming a range compensating layer 2902 over a top surface of a
semiconductor device to compensate for variations in ion
penetration depth resulting from variations in density and/or the
types of materials present between an upper surface of the
semiconductor device and a cleave plane.
[0300] In some embodiments such as the example illustrated in FIG.
29, the compensating layer 2902 has an even thickness, and is
selectively deposited over areas of the device which would
otherwise have a higher ion penetration depth than areas with no
compensating layer. In other embodiments, the compensating layer
2902 has variations in thickness to account for multiple variations
in ion penetration depth. For example, a shape of the compensating
layer 2902 can be developed by performing ion implantation on a
device that lacks a compensating layer, measuring depth variation
in the cleave plane, and forming a compensating layer whose
thickness varies as a mirror image of the depth variation, e.g.
greater depth ion penetration areas would correlate with thicker
sections of the compensating layer, and vice versa.
[0301] Closely spaced stopping power variations over lateral scales
approximately equal to the lateral straggling of high-energy
hydrogen ions, on the order of 1 or more microns, are not generally
replicated in variations in hydrogen profile depth. Accordingly,
the thickness of the range compensating layer 2902 may vary from
one functional region of a circuit to another, as opposed to
varying based on individual nano-scale structures within a
region.
[0302] In an embodiment, provisions are made for active removal of
heat generated by circuit switching and resistive power losses in a
volumetric 3D composite multidevice layer system by formation of
cooling channels formed along the cleave surface defined by a
high-concentration Hydrogen profile. The cleave surface depth is
defined by the thickness, stopping power and location of patterned
layers added to the device surface before Hydrogen
implantation.
[0303] As illustrated in FIG. 2A, embodiments of the present
disclosure include a cooling channel. In the example of FIG. 2A,
the cooling channel was created by modulating a depth profile of
implanted Hydrogen with a patterned CVD oxide overlayer that is
present when hydrogen is implanted to form a cleave layer. An
associated CVD nitride layer is used to provide an etch stop for
the CVD oxide layer patterning. Both of the CVD nitride and oxide
layers are removed in later processing.
[0304] FIG. 2 illustrates an embodiment of cooling channels formed
along the cleave surface by offsetting the proton depth with a
patterned stopping layer photoresist (PR) layer. In other
embodiments, the stopping layer may be a similar dense material
deposited on the device wafer surface. The thickness and stopping
power of the underlying un-patterned PR layer can be used to
modulate the depth of the cleave surface features in the substrate
material below the transferred device layers. FIG. 2 shows the
formation of a completed cooling fluid channel by bonding the
modulated cleave surface to a planar top surface of an underlying
device or substrate layer.
[0305] In an embodiment, cooling channels are enhanced by applying
a surface coating. A surface coating material may be selected to
improve heat transfer from the active device layers to a cooling
fluid in the cooling channels, and/or to reduce or eliminate
chemical reactions between a heat transfer fluid in the cooling
channel and a substrate material. For example, in some embodiments,
a cooling channel is disposed in a layer with high thermal
conductivity, and the high thermal conductivity material reacts
with a heat transfer fluid that flows through the coolant channel.
In such an embodiment, exposed surfaces of the coolant channel may
be coated with an inert material such as an oxide or nitride
material that prevents chemical reactions between the heat transfer
fluid and the high thermal conductivity layer material. For
example, the inert material may be SiO.sub.2 or
Si.sub.3N.sub.4.
[0306] Persons of skill in the art will recognize that
characteristics of the coating material including material type,
thickness, and deposition technique may be selected based on the
particular thermal conductivity layer material and heat transfer
fluid used in an embodiment. In some embodiments, the coating
material assists in heat transfer, and has a higher thermal
conductivity than a substrate material over which the coating is
formed. Other favorable characteristics of a coating layer on
coolant channels include excellent adhesion to the coolant channel
wall material, uniform conformal coating thickness for good thermal
conductivity and free flow of coolant materials and, being inert to
the coolant fluid material at device operating temperatures.
[0307] In an embodiment, a fluid in the coolant channels may be a
heat transfer fluid with a relatively high thermal conductivity. In
some embodiments, the fluid is an inert substance such as water, or
a highly dilute solution. In other embodiments, the heat transfer
fluid may be a nanofluid that comprises nanoparticles that enhance
the thermal conductivity of the fluid compared to the liquid phase
component. The heat transfer fluid may circulate through an
external heat exchanger to transfer heat away from the device.
[0308] The location of the cooling channel can be chosen to be at a
transfer device bond layer as seen in FIG. 2, or in an alternate
location for cases where direct bonding of device metal layers is
desired, for high-bandwidth circuit connections, as seen in FIG.
20. In FIG. 20, the cooling channels are located near a planar bond
surface for a subsequently added device layer.
[0309] In some embodiments, one or more heat transfer layer may be
included in a 3DIC device. A heat transfer layer may be a material
that has superior heat transfer characteristics to materials used
in an active layer. The heat transfer layer may be disposed
adjacent to the cooling channels, so that a heat transfer fluid
travelling through the cooling channels transfers heat from device
circuitry to the heat transfer layer. In other embodiments, cooling
channels are formed directly in a high thermal conductivity heat
transfer layer.
[0310] Multi-layer lamination of devices allows for the insertion
of layers of high-thermal conductivity materials and interfaces to
improve both the lateral spreading of heat from local active
circuit regions and the vertical transfer of heat to the network of
fluid flowing in cooling channels. The provisions for controlling
the local depth of the cleave surface in materials also allows for
the formation of cooling channels in subsequently laminated
high-thermal conductivity layers in a similar fashion as the
transferred device layers. For example, FIG. 16 illustrates a high
thermal conductivity heat spreading layer with coolant flow
channels that is bonded between two circuit layers by CVD oxide
bond layers.
[0311] As indicated in Table 1 above, the room-temperature thermal
conductivity of Silicon, the dominant substrate material for
current IC fabrication, has a relatively high thermal conductivity,
matched closely only by Silicon Carbide (SiC). In an embodiment, it
is desirable to use a material that has higher thermal conductivity
than Si as a high thermal conductivity layer.
[0312] A consideration for a material for a high thermal
conductivity heat transfer material is the thermal conductivity
properties of materials at temperatures characteristic of active
circuit operations, which are generally in the range of 80 to 120
C. For Si at room temperature (25 C, 300 K) and above, thermal
conductivity decreases strongly with increased temperature, leading
to a risk of "thermal runaway" for local regions heated by active
circuit power. As seen in FIGS. 30 and 31, Si thermal conductivity
decreases at all temperatures for increased dopant concentrations
due to phonon-dopant scattering. For commonly used Si substrates,
the dopant levels are relatively low (.apprxeq.10.sup.15
dopants/cm.sup.3) leading to relatively high thermal conductivity
compared to the higher concentrations illustrated in FIGS. 30 and
31.
[0313] FIG. 32 illustrates thermal conductivity of 6H--SiC at
various temperatures and doping concentrations as reported by
Morelli et al. (1993). In the FIG. 32, sample 1 is a very pure or
highly compensated sample, and the remaining samples have electron
concentrations as follows: sample 2--n=3.5.times.10.sup.16
cm.sup.-3; sample 3--n=2.5.times.10.sup.16 cm.sup.-3; sample
4--n=8.0.times.10.sup.17 cm.sup.-3; sample 5--n=2.0.times.10.sup.17
cm.sup.-3; and sample 6--n=3.0.times.10.sup.18 cm.sup.-3. Thermal
conductivity values of various forms of silicon carbide are
reported as being higher than silicon, with conductivity values of
3C, 4H and 6H polytypes being twice as high as silicon at 300K.
[0314] As illustrated in FIG. 33, thermal conductivity of some
carbon-based materials is much higher than silicon. In particular,
diamond, graphite, graphene and Carbon nano-tubes all have thermal
conductivity values that are substantially higher than thermal
conductivity of silicon, especially at higher temperatures. While
FIGS. 30 and 31 show a steep decline in silicon's thermal
conductivity above room temperature, the decline in thermal
conductivity of carbon-based materials is relatively shallow, and
in the case of amorphous carbon, thermal conductivity increases
above room temperature. In particular, thermal conductivity values
reported for diamond and graphene are an order of magnitude greater
than thermal conductivity of silicon at 300K. Another material with
a high thermal conductivity that is comparable to forms of diamond
is cubic Boron Arsenide. In embodiments of the present disclosure,
one of these materials may be used as a bulk substrate
material.
[0315] In the present disclosure, the term "plane" is used to
describe a cleave plane, which is generally understood to be a
location at which a cleaved layer is separated from a substrate.
However, as explained above, a range compensating layer may be
applied to a substrate before ion implantation, which can result in
an as-cleaved surface that includes one or more contours which may
define, for example, a cooling channel. Accordingly, use of the
term "cleave plane" in the present disclosure should not be
construed as limiting embodiments of this disclosure to cleaved
surfaces that are perfectly flat.
[0316] In an embodiment, a chemically or mechanically weak cleave
surface is formed by ion implantation prior to the formation of any
sensitive or reliability concerned device layers, interfaces of
structures. Such an embodiment may be used in the formation of a
full device structure, including a full network of metal
interconnects and inter-metal layer dielectrics, to be followed by
initiation of cleave action at the pre-formed cleave surface for
transfer to a 3DIC stack structure.
[0317] Such an embodiment would reduce concerns for device yield
and reliability problems related to the formation of the buried
cleave surface. In the case of Hydrogen-based cleave surface
formation, this embodiment allows for use of substantially lower
proton ion energies for the implant step for a desired cleave
surface depth.
[0318] Benefits of such an embodiment include that the mechanical,
thermal and chemical conditions for the post-cleave plane formation
device fabrication and testing process should be conducted to avoid
premature initiation of the cleave action. In an embodiment that
uses Hydrogen-driven cleaving, this involves restricting the
post-cleave surface formation processing to temperatures below
.apprxeq.500 C.
[0319] Many advanced devices, for example those which contain
high-dielectric constant, or high-K, gate oxides, such as HfO.sub.2
and related forms, have thermal budget restrictions in this general
area.
[0320] FIG. 34 illustrates a bonding step for a transfer layer. In
an embodiment, the transfer layer is a high-purity, crystalline
transfer layer that is bonded to a substrate layer containing a
chemically of mechanically weak separation layer that can
subsequently be cleaved after initiation of appropriate cleave
surface formation conditions.
[0321] FIGS. 35 and 36 illustrate an embodiment of forming a buried
Hydrogen profile with peak concentration appropriate for formation
of a cleave surface at a depth below a partially completed device
layer, prior to formation of sensitive device layers, interfaces or
structures. FIG. 36 illustrates a fully completed device structure,
including fully constructed metal interconnect and inter-metal
dielectric layers prior to introduction of process conditions for
initiation of a cleave surface at the buried Hydrogen-rich cleave
surface.
[0322] A process may be performed where a chemically or
mechanically weak layer is formed in a partially completed device
substrate prior to the formation of sensitive device layers,
interface or structures. Thermal, mechanical and chemical
processing of the subsequent device fabrication may be restricted
to conditions which do not initiate cleaving action at the cleave
surface locations. The sensitive structures may include gate
dielectric and inter-metal layer dielectric layers. An example of a
subsequent process restriction for the case of a Hydrogen implant
formed cleave surfaces include processing at temperatures at or
below 500 C. In an embodiment, the completed, fully-metallized
device structure is transferred to a 3DIC stack following cleaving
initiated at the cleave surface.
[0323] In embodiments of the present disclosure, a network of
channels for flow of cooling fluids is defined by modulation of
implanted Hydrogen depth by a patterned layer of materials at the
device wafer surface during Hydrogen implant with thickness,
stopping power and location chosen to create a non-planar cleave
surface in the transfer device substrate. Similar methods for
modulating the depth of the cleave plane may be used to define
cooling channels in a selected high-thermal conductivity material
layer for subsequent insertion into a laminated multi-layer,
multi-device 3DIC stack. In an embodiment, the surface regions of a
cooling fluid flow network are coated with material chosen to
increase thermal conductivity between the heated device layer and
substrate and the flowing cooling fluid, and to prevent chemical
reactions between the device substrate and cooling fluids.
[0324] Embodiments incorporate the advantages of wafer-level
bonding processes, including incorporation of cooling fluid network
channels, with a design flexibility for incorporation of dies
fabricated on different wafer sizes, different wafer thickness and
different substrate materials. Devices formed using the cleaving
and stacking techniques provided in this disclosure have numerous
advantages over conventional technologies. Substrates that are
formed by backgrinding are subject to substantially higher levels
of mechanical stress and higher levels of thickness variation over
the substrate surface. Ionic cleaving can be performed with fewer
process steps than backgrinding, simplifying the process and
reducing the amount of handling required. Layers of the 3DIC
structures according to the present disclosure may be
interconnected through dense high bandwidth vertical and lateral
metal connections, which may displace the need for interposer and
solder bump structures, leading to smaller, more tightly
integrated, higher speed devices that are more efficient to
manufacture.
[0325] While the above is a full description of specific
embodiments, various modifications, alternative constructions and
equivalents may be used. Therefore, the above description and
illustrations should not be taken as limiting the scope of the
present disclosure.
* * * * *