U.S. patent application number 15/209803 was filed with the patent office on 2018-01-18 for magnetic inductor stacks with multilayer isolation layers.
The applicant listed for this patent is International Business Machines Corporation. Invention is credited to Hariklia Deligianni, Bruce B. Doris, Eugene J. O'Sullivan, Naigang Wang.
Application Number | 20180019295 15/209803 |
Document ID | / |
Family ID | 60788957 |
Filed Date | 2018-01-18 |
United States Patent
Application |
20180019295 |
Kind Code |
A1 |
Deligianni; Hariklia ; et
al. |
January 18, 2018 |
MAGNETIC INDUCTOR STACKS WITH MULTILAYER ISOLATION LAYERS
Abstract
A magnetic laminating structure and process includes alternating
layers of a magnetic material and a multilayered insulating
material, wherein the multilayered insulating material is
intermediate adjacent magnetic material layers and comprises a
first insulating layer abutting at least one additional insulating
layer, wherein the first insulating layer and the at least one
additional insulating layer comprise different dielectric materials
and/or are formed by a different deposition process, and wherein
the layers of the magnetic material have a cumulative thickness
greater than 1 micron.
Inventors: |
Deligianni; Hariklia;
(Alpine, NJ) ; Doris; Bruce B.; (Hartsdale,
NY) ; O'Sullivan; Eugene J.; (Nyack, NY) ;
Wang; Naigang; (Ossining, NY) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
International Business Machines Corporation |
Armonk |
NY |
US |
|
|
Family ID: |
60788957 |
Appl. No.: |
15/209803 |
Filed: |
July 14, 2016 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
H01L 28/26 20130101;
H01L 28/10 20130101; H01L 28/40 20130101; H01L 23/5227
20130101 |
International
Class: |
H01L 49/02 20060101
H01L049/02 |
Claims
1. An inductor structure comprising: a plurality of metal lines;
and a laminated film stack comprising alternating layers of a
magnetic material and a multilayered insulating material enclosing
the metal lines, wherein the multilayered insulating material is
intermediate adjacent magnetic material layers and comprises a
first insulating layer abutting at least one additional insulating
layer, and wherein the first insulating layer and the at least one
additional insulating layer comprise different dielectric materials
and/or are formed by a different deposition process.
2. The inductor structure of claim 1, wherein the first insulating
layer and/or the at least one additional insulating layer comprises
one or more pinholes and are discontinuous between the first
insulating layer and the at least one additional insulating
layer.
3. The inductor structure of claim 1, wherein the magnetic material
is selected from the group consisting of CoFe, CoFeB, CoZrTi,
CoZrTa, CoZr, CoZrNb, CoZrMo, CoTi, CoNb, CoHf, CoW, FeCoN,
FeCoAlN, CoP, FeCoP, CoPW, CoBW, CoPBW, FeTaN, FeCoBSi, FeNi,
CoFeHfO, CoFeSiO, CoZrO, CoFeAlO, and combinations thereof.
4. The inductor structure of claim 1, wherein the dielectric
materials are selected from the group consisting of silicon
dioxide, thermal oxide Si, silicon oxynitride, magnesium oxide,
aluminum oxide, boron oxide, tantalum oxide, titanium oxide,
silicon nitride, and combinations thereof.
5. The inductor structure of claim 1, wherein the multilayered
insulating material layer has a thickness of about one half of a
thickness of the magnetic material layer.
6. The inductor structure of claim 1, wherein the multilayered
insulating material layer has a thickness effective to electrically
isolate each magnetic material layer from other magnetic material
layers in the inductor structure.
7. The inductor structure of claim 1, wherein first insulating
layer comprises silicon dioxide and the insulating layer abutting
at least one additional comprises insulating layer silicon
nitride.
8. The inductor structure of claim 1, wherein the multilayered
insulating material layer comprises a first silicon dioxide layer
overlaying a silicon nitride layer, wherein the silicon nitride
layer overlays a second silicon dioxide layer.
9. The inductor structure of claim 1, wherein the multilayered
insulating material layer comprises a first silicon nitride layer
overlaying a silicon dioxide layer, wherein the silicon dioxide
layer overlays a second silicon nitride layer.
10-17. (canceled)
18. An inductor structure, comprising: a laminated film stack
comprising alternating layers of a magnetic material and a
multilayered insulating material, wherein the multilayered
insulating material is intermediate adjacent magnetic material
layers and comprises a first insulating layer abutting at least one
additional insulating layer, and wherein the first insulating layer
and the at least one additional insulating layer comprise different
dielectric materials and/or are formed by a different deposition
process.
19-20. (canceled)
Description
BACKGROUND
[0001] The present invention relates to on-chip magnetic devices,
and more specifically, to on-chip magnetic structures and methods
for minimizing magnetic losses for magnetic inductors.
[0002] On-chip magnetic inductor stacks are important passive
elements with applications in the fields such as on-chip power
converters and radio frequency (RF) integrated circuits. In order
to achieve the high energy storage required for power management,
on-chip inductors typically require relatively thick magnetic yoke
materials (e.g., several microns or more).
[0003] Magnetic inductor stacks generally include alternating
layers of magnetic material and dielectric material. The dielectric
material helps prevent eddy current losses. The dielectric material
used in the magnetic inductor stacks is generally deposited at low
temperatures in order not to destroy the magnetic properties of the
magnetic material. Low temperature oxides and nitrides have been
used in the past but are prone to have pinholes, which can allow
magnetic materials from adjacent layers to be electrically
connected and unwanted eddy currents resulting in magnetic loss.
The pinholes are particularly problematic for low temperature high
throughput dielectric processes.
SUMMARY
[0004] Exemplary embodiments include inductor structures and
methods for forming the inductor structures In one or more
embodiments, the inductor structure includes a plurality of metal
lines; and a laminated film stack comprising alternating layers of
a magnetic material and a multilayered insulating material
enclosing the metal lines, wherein the multilayered insulating
material is intermediate adjacent magnetic material layers and
comprises a first insulating layer abutting at least one additional
insulating layer, and wherein the first insulating layer and the at
least one additional insulating layer comprise different dielectric
materials and/or are formed by a different deposition process.
[0005] In one or more embodiments, a method of forming an inductor
structure includes depositing a laminated film stack comprising
alternating layers of a magnetic material and a multilayered
insulating material, wherein the multilayered insulating material
is intermediate adjacent magnetic material layers and comprises a
first insulating layer abutting at least one additional insulating
layer, and wherein the first insulating layer and the at least one
additional insulating layer comprise different dielectric materials
and/or are formed by a different deposition process.
[0006] In one or more embodiments, the inductor structure includes
a laminated film stack comprising alternating layers of a magnetic
material and a multilayered insulating material, wherein the
multilayered insulating material is intermediate adjacent magnetic
material layers and comprises a first insulating layer abutting at
least one additional insulating layer, and wherein the first
insulating layer and the at least one additional insulating layer
comprise different dielectric materials and/or are formed by a
different deposition process.
[0007] Additional features and advantages are realized through the
techniques of the present invention. Other embodiments and aspects
of the invention are described in detail herein and are considered
a part of the claimed invention. For a better understanding of the
invention with the advantages and the features, refer to the
description and to the drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
[0008] The subject matter which is regarded as the invention is
particularly pointed out and distinctly claimed in the claims at
the conclusion of the specification. The forgoing and other
features and advantages of the invention are apparent from the
following detailed description taken in conjunction with the
accompanying drawings in which:
[0009] Prior Art FIG. 1 ("FIG") illustrates a cross section of an
inductor structure;
[0010] FIG. 2 illustrates a cross section of an inductor structure
including multilayer isolation layers in accordance with the
present invention; and
[0011] FIG. 3 is a process flow for forming an inductor structure
in accordance with one or more embodiments of the present
invention.
DETAILED DESCRIPTION
[0012] The present invention addresses problems in the prior art by
providing in one or more embodiments a method and a magnetic
inductor structure that eliminates issues resulting from pinhole
formation in the dielectric layer while advantageously being low
temperature and high throughput. The methods and structure
eliminate the effects of pinhole formation by utilizing a
multilayer isolation scheme. In one or more embodiments, the
multilayer isolation scheme can be performed by depositing two or
more layers of different dielectric materials intermediate adjacent
magnetic layers in the magnetic inductor laminate structure. While
each deposited dielectric layer can include pinholes, it has been
discovered that the pinholes between layers is discontinuous. By
way of example, the multilayer isolation scheme can include
depositing a first layer of silicon dioxide followed by deposition
of silicon nitride followed by deposition of silicon dioxide. In
other examples, one can deposit a silicon nitride/silicon
dioxide/silicon nitride stack. In addition, the stack can be
fabricated using more than two different types of dielectric
materials. By utilizing the multilayer isolation scheme, the
multilayer dielectric can have an overall thinner film thickness
compared to a single layer dielectric while overcoming issues
associated with pinholes. In addition, the thinner film provides
lower aspect ratio for ease of downstream processing.
[0013] Prior art FIG. 1 illustrates a known magnetic inductor
structure 10 illustrating one of the problems associated with low
temperature deposition of dielectric materials. By low temperature
deposition, it is meant that the temperatures utilized to deposit
the dielectric material within the magnetic inductor structure are
generally at temperatures that do not affect the magnetic
properties associated with the magnetic layers, which is generally
less than 300.degree. C. although the particular temperature will
generally depend on the deposition process. The exemplary magnetic
inductor structure 10 includes a substrate 12 upon which the
inductor structure is formed. Substrate 12 can be a processed
wafer. A "processed wafer" is herein defined as a wafer that has
undergone semiconductor front end of line processing (FEOL) middle
of the line processing (MOL), and back end of the line processing
(BEOL), wherein the various desired devices and circuits have been
formed.
[0014] The typical FEOL processes include wafer preparation,
isolation, well formation, gate patterning, spacer, extension and
source/drain implantation, silicide formation, and dual stress
liner formation. The MOL is mainly gate and source-drain contact
formation, which is an increasingly challenging part of the whole
fabrication flow, particularly for lithography patterning. The
state-of-the-art semiconductor chips, the so called 14 nm node of
Complementary Metal-Oxide-Semiconductor (CMOS) chips, in mass
production features a second generation three dimensional (3D)
FinFET, a metal one pitch of about 55 nm and copper (Cu)/low-k (and
air-gap) interconnects. In the BEOL, the Cu/low-k interconnects are
fabricated predominantly with a dual damascene process using
plasma-enhanced CVD (PECVD) deposited interlayer dielectric (ILDs),
PVD Cu barrier and electrochemically plated Cu wire materials.
[0015] Disposed on the substrate 12 are alternating layers of
dielectric material 14 and magnetic material 16, wherein the
cumulative thickness of the magnetic material is greater than 1
micron to several microns. As discussed above, one of the problems
with current low temperature deposition processes of dielectric
materials used in the formation of magnetic inductor film stacks
includes the formation of pinholes 18 randomly formed during
deposition of the dielectric material layers. The pinholes can
extend from a bottom surface to a top surface of the dielectric
layer or partially therethrough, which deleteriously results in
unwanted electrical connections between adjacent magnetic layers
and eddy currents that cause magnetic loss.
[0016] The low temperature deposition processes are varied and
generally include physical vapor deposition (PVD), chemical vapor
deposition (CVD), plasma enhanced chemical vapor deposition
(PECVD), thermal oxidation, or any combination thereof. The
temperatures of these various deposition processes also vary
depending on the particular process. In one or more embodiments,
the dielectric deposition process includes PECVD at temperatures of
less than 300.degree. C.
[0017] In one or more other embodiments, the second dielectric
layer (and/or each additional dielectric layer) can be formed of a
different material (e.g., silicon nitride) compared to the first
dielectric layer (e.g., silicon dioxide) while the deposition
technique is the same 114.sup.n=1. In one or more other
embodiments, the second layer (and/or each additional dielectric
layer) can be the same material as the first material (e.g.,
silicon dioxide) but utilizes different deposition techniques,
e.g., PECVD, PVD, spin-on and atomic layer deposition). In one or
more other embodiments, the materials for the first and second
dielectric layers are different and the deposition technique to
form each layer is different.
[0018] Turning now to FIG. 2, there is depicted a cross section of
an exemplary inductor structure in accordance with one or more
embodiments of the present invention. The inductor structure 100
generally includes a plurality of alternating magnetic layers 112
and insulating layers 114 disposed on a substrate 116 such as a
processed wafer.
[0019] Each of the insulating layers 114 comprises multiple
dielectric layers 114A, 114B deposited utilizing a low temperature
deposition process particular to the dielectric material and
process the dielectric material is being deposited. At least two or
more of the dielectric layers 114A and 114B within a multilayer
isolation scheme are formed of different materials or by different
deposition techniques. As used herein, the term multilayer
isolation scheme generally refers to two or more dielectric layers,
wherein at least two of the dielectric materials are different.
While each deposited layer can include pinholes, it has been
discovered that the pinholes between layers is discontinuous. Thus,
eddy current losses between adjacent magnetic layers that were
previously effected by pinhole formation in the dielectric layer
are prevented. The maximum number of dielectric layers between
adjacent magnetic layers is not intended to be limited and is
generally limited by the desired thickness of the insulating layer
wherein minimal thickness to electrically isolate the magnetic
layers is generally desired while preventing eddy current losses.
Generally, the utilization of multiple dielectric layers 114A to
114B instead of a single insulating layer permits thinner layer
thickness as well as an overall lower aspect ratio for the magnetic
stack, which is desirable as components become smaller and
smaller.
[0020] The multiple dielectric layers 114A to 114B are not intended
to be limited to any specific material and can include dielectric
materials such as oxides, nitrides, and the like. Exemplary oxides
include, but are not limited to, silicon dioxide (SiO.sub.2),
thermal oxide Si, silicon oxynitride (SiO.sub.xN.sub.y), magnesium
oxide (MgO), aluminum oxide (AlO.sub.2) and/or (Al.sub.2O.sub.3),
boron oxide (B.sub.2O.sub.3), tantalum oxide (Ta.sub.2O.sub.5),
titanium oxide (TiO.sub.2), or the like. Exemplary nitrides include
silicon nitride.
[0021] The bulk resistivity and the eddy current loss of the
magnetic structure can be controlled by the multilayer dielectric
layer 114. As noted above, the cumulative thickness of the
insulating layer 114 in its entirety (i.e., thickness of the
multiple dielectric layers 114A to 114B that define the particular
insulating layer 114A, 114B) should be minimal and is generally at
a thickness effective to electrically isolate the magnetic layer
upon which it is disposed from other magnetic layers in the film
stack. Generally, the insulating layer 114A, 114B has a thickness
of about 1 nanometer to about 500 nanometers and can be at least
about one half or more of the magnetic layer thickness. In one or
more embodiments, the thickness of the insulator layer is about 2
to about 100 nanometers.
[0022] Each of the magnetic layers 112 in the laminate stack 100
can have a thickness of about 100 nanometers or more and can be
deposited through vacuum deposition technologies (i.e., sputtering)
or electrodepositing through an aqueous solution. Vacuum methods
have the ability to deposit a large variety of magnetic materials
and to easily produce laminated structures. However, they usually
have low deposition rates, poor conformal coverage, and the derived
magnetic films are difficult to pattern. Electroplating has been a
standard technique for the deposition of thick metal films due to
its high deposition rate, conformal coverage and low cost.
[0023] The magnetic layers are not intended to be limited to any
specific material and can include CoFe, CoFeB, CoZrTi, CoZrTa,
CoZr, CoZrNb, CoZrMo, CoTi, CoNb, CoHf, CoW, FeCoN, FeCoAlN, CoP,
FeCoP, CoPW, CoBW, CoPBW, FeTaN, FeCoBSi, FeNi, CoFeHfO, CoFeSiO,
CoZrO, CoFeAlO, combinations thereof, or the like. Inductor core
structures from these materials have generally been shown to have
low eddy losses, high magnetic permeability, and high saturation
flux density.
[0024] The magnetic inductor including the laminate structure as
described can be integrated in a variety of devices. Two basic
configurations are closed yoke and solenoid structure inductors.
The closed yoke has copper wire with magnetic material wrapped
around it and the solenoid inductor has magnetic material with
copper wire wrapped around it. Both inductor types benefit by
having very thick magnetic materials, wherein the total magnetic
film thickness requirement is typically greater than 1 micrometer
(m).
[0025] A non-limiting example of inductor integration is a
transformer, which can include metal lines (conductors) formed
parallel to each other by standard silicon processing techniques
directed to forming metal features. The inductor structures can be
formed about the parallel metal lines to form a closed magnetic
circuit and to provide a large inductance and magnetic coupling
among the metal lines. The inclusion of the magnetic material and
the substantial or complete enclosure of the metal lines can
increase the magnetic coupling between the metal lines and the
inductor for a given size of the inductor. Inductors magnetic
materials are also useful for RF and wireless circuits as well as
power converters and EMI noise reduction.
[0026] Referring now to FIG. 3, a process 100 of forming the on
chip magnetic inductor is shown and generally begins with a first
step 110 of depositing a first dielectric layer 114A onto the
processed wafer 116, which after FEOL, MOL, and BEOL processing has
a planar uppermost surface.
[0027] In step 120, a second dielectric layer 114B is then
deposited onto the first dielectric layer 114A. The second
dielectric layer 114B can be formed of a different material.
Optionally, one or more additional dielectric layers can be
deposited onto the second dielectric layer 114B, which is a
different material than the second dielectric layer 114B. In one or
more embodiments, the additional dielectric layer is formed of the
same material as the first dielectric layer 114A. In one or more
other embodiments, the second dielectric layer 114B (and/or each
additional dielectric layer) can be formed of a different material
than the first dielectric layer 114A while the deposition technique
used to form the second dielectric layer 114B is the same as the
deposition method used to form the first dielectric layer 114A. In
one or more other embodiments, the second layer (and/or each
additional dielectric layer) can be the same material but utilizes
different deposition technique. In one or more other embodiments,
the materials for the first and second dielectric layers 114A, 114B
are different and the deposition technique to form each layer is
different.
[0028] As shown in step 130, once the desired thickness of the
dielectric layer 114A, 114B is formed, a magnetic layer 112 is
deposited onto the uppermost dielectric layer. The preceding
process steps are repeated to provide alternating magnetic layer
and multilayer isolation schemes until the desired magnetic
inductor structure is formed, which includes a magnetic film having
a total thickness in excess of 1 micron. By utilizing a laminate
structure including the multilayer isolation scheme as described,
eddy current losses between adjacent magnetic layers is
prevented.
[0029] Once the desired laminate structure is formed, the process
can further include deposition of a hard mask onto the laminate
structure followed by lithography to complete the device, wherein
lithography can then be performed.
[0030] The terminology used herein is for the purpose of describing
particular embodiments only and is not intended to be limiting of
the invention. As used herein, the singular forms "a", "an" and
"the" are intended to include the plural forms as well, unless the
context clearly indicates otherwise. It will be further understood
that the terms "comprises" and/or "comprising," when used in this
specification, specify the presence of stated features, integers,
steps, operations, elements, and/or components, but do not preclude
the presence or addition of one more other features, integers,
steps, operations, element components, and/or groups thereof.
[0031] The corresponding structures, materials, acts, and
equivalents of all means or step plus function elements in the
claims below are intended to include any structure, material, or
act for performing the function in combination with other claimed
elements as specifically claimed. The description of the present
invention has been presented for purposes of illustration and
description, but is not intended to be exhaustive or limited to the
invention in the form described. Many modifications and variations
will be apparent to those of ordinary skill in the art without
departing from the scope and spirit of the invention. The
embodiment was chosen and described in order to best explain the
principles of the invention and the practical application, and to
enable others of ordinary skill in the art to understand the
invention for various embodiments with various modifications as are
suited to the particular use contemplated
[0032] It should be apparent that there can be many variations to
this diagram or the steps (or operations) described herein without
departing from the spirit of the invention. For instance, the steps
can be performed in a differing order or steps can be added,
deleted or modified. All of these variations are considered a part
of the claimed invention.
[0033] While the preferred embodiment to the invention had been
described, it will be understood that those skilled in the art,
both now and in the future, can make various improvements and
enhancements which fall within the scope of the claims which
follow. These claims should be construed to maintain the proper
protection for the invention first described.
* * * * *