U.S. patent application number 15/206762 was filed with the patent office on 2018-01-11 for liquid gypsum set accelerator.
The applicant listed for this patent is NATIONAL GYPSUM PROPERTIES, LLC. Invention is credited to Joseph J. Bailey, Chris Fewox.
Application Number | 20180009713 15/206762 |
Document ID | / |
Family ID | 60893097 |
Filed Date | 2018-01-11 |
United States Patent
Application |
20180009713 |
Kind Code |
A1 |
Fewox; Chris ; et
al. |
January 11, 2018 |
LIQUID GYPSUM SET ACCELERATOR
Abstract
A liquid accelerator composition for accelerating the setting
reaction of calcium sulfate hemihydrate and water and methods of
forming a liquid gypsum accelerator are provided. The liquid
accelerator composition includes a liquid media in which calcium
sulfate dihydrate is less than fully soluble and a ground product
of a mill grinding of a mixture comprising calcium sulfate
dihydrate.
Inventors: |
Fewox; Chris; (Pineville,
NC) ; Bailey; Joseph J.; (Charlotte, NC) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
NATIONAL GYPSUM PROPERTIES, LLC |
Charlotte |
NC |
US |
|
|
Family ID: |
60893097 |
Appl. No.: |
15/206762 |
Filed: |
July 11, 2016 |
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
C04B 20/008 20130101;
C04B 24/38 20130101; C04B 22/143 20130101; C04B 2103/408 20130101;
C04B 38/106 20130101; C04B 24/08 20130101; C04B 20/008 20130101;
C04B 2103/0086 20130101; C04B 24/223 20130101; C04B 2103/40
20130101; C04B 20/026 20130101; C04B 22/16 20130101; C04B 24/02
20130101; C04B 22/143 20130101; C04B 22/143 20130101; C04B 24/02
20130101; C04B 24/18 20130101; C04B 22/143 20130101; C04B 40/0039
20130101; C04B 28/14 20130101; C04B 28/14 20130101; C04B 2103/12
20130101; C04B 40/0039 20130101; C04B 22/143 20130101; C04B 40/0039
20130101; C04B 2111/0062 20130101 |
International
Class: |
C04B 28/14 20060101
C04B028/14; C04B 24/38 20060101 C04B024/38 |
Claims
1. A gypsum set accelerator composition, comprising: a slurry
including: ground gypsum in an amount of about 95 wt % to about 20
wt % of the slurry, the ground gypsum having a particle size
distribution with at least about 15% of the mass of ground gypsum
having a particle size of about 5.5 .mu.m or less; and a
non-aqueous liquid medium in which gypsum has a solubility of about
10 g/l or less at 25.degree. C.
2. The gypsum set accelerator composition of claim 1, wherein the
ground gypsum is in an amount of about 40 wt % to about 20 wt % of
the slurry.
3. The gypsum set accelerator composition of claim 1, wherein the
ground gypsum is in an amount of about 35 wt % of the slurry.
4. The gypsum set accelerator composition of claim 1, wherein
gypsum has a solubility of about 2.5 g/l or less in the liquid
medium.
5. The gypsum set accelerator composition of claim 1, wherein
gypsum has a solubility of about 1 g/l or less in the liquid
medium.
6. The gypsum set accelerator composition of claim 1, wherein the
liquid medium is selected from the group consisting of: an alcohol,
glycerin and combinations thereof.
7. (canceled)
8. The gypsum set accelerator composition of claim 1, wherein the
liquid medium is anhydrous isopropyl alcohol.
9. The gypsum set accelerator composition of claim 1, wherein the
liquid medium includes a solubility inhibitor.
10. The gypsum set accelerator composition of claim 9, wherein the
solubility inhibitor is a phosphate.
11. The gypsum set accelerator composition of claim 9, wherein the
solubility inhibitor is sodium trimetaphosphate.
12. The gypsum set accelerator composition of claim 1, further
comprising an additive selected from the group consisting of: a
soap, a surfactant, a dispersant, naphthalene sulfonate, a
lignosulfonate, an alginate, a saccharide, a phosphate, a
complexing agent and combinations thereof.
13. The gypsum set accelerator composition of claim 1, wherein the
ground gypsum has a particle size distribution with at least about
40 wt % of the mass of ground gypsum having a particle size of
about 5.5 .mu.m or less.
14. The gypsum set accelerator composition of claim 1, wherein the
ground gypsum has a particle size distribution with a mass median
diameter of less than 15 .mu.m.
15. The gypsum set accelerator composition of claim 1, wherein the
ground gypsum has a particle size distribution with a mass median
diameter of about 5.5 .mu.m or less.
16. A method of making a gypsum set accelerator, comprising the
steps of: providing gypsum and a non-aqueous liquid medium in which
gypsum has a solubility of about 10 g/l or less at 25.degree. C.;
grinding the gypsum to a particle size distribution with at least
about 15% of the mass of ground gypsum having a particle size of
about 5.5 .mu.m or less; and combining the liquid medium and the
ground gypsum to form a slurry comprising about 95 wt % to about 20
wt % gypsum.
17. The method of claim 16, wherein the slurry comprises about 40
wt % to about 20 wt % gypsum.
18. The method of claim 16, wherein gypsum has a solubility in the
liquid medium of about 2.5 g/l or less.
19. (canceled)
20. The method of claim 16, wherein the liquid medium is anhydrous
isopropyl alcohol.
21. The method of claim 16, wherein the liquid medium includes a
solubility inhibitor.
22. The method of claim 22, wherein the solubility inhibitor is a
phosphate.
23. The method of claim 16, wherein the gypsum is ground to a
particle size distribution with a mass median diameter of less than
15 .mu.m.
24. The method of claim 16, wherein the gypsum is ground to a
particle size distribution with a mass median diameter of about 5.5
.mu.m or less.
25. The method of claim 16, wherein the gypsum is ground in at
least a portion of the liquid medium.
26. The method of claim 16, wherein the gypsum is ground in a
planetary ball mill.
27. (canceled)
28. (canceled)
29. A method of making a gypsum board composition, comprising the
steps of: providing dry ingredients including stucco, and wet
ingredients including water; mixing the dry and wet ingredients to
form a gypsum slurry; providing gypsum and a liquid medium in which
gypsum has a solubility of about 10 g/l or less at 25.degree. C.;
grinding the gypsum to a particle size distribution with at least
about 15% of the mass of ground gypsum having a particle size of
about 5.5 .mu.m or less; combining the liquid medium and the gypsum
to form a gypsum set accelerator comprising about 95 wt % to about
20 wt % gypsum; adding an aqueous foam to the gypsum slurry; and
adding the gypsum set accelerator to the gypsum slurry with the
foam.
30. (canceled)
31. A method of making a gypsum set accelerator, comprising the
steps of: combining stucco and an aqueous liquid medium in which
gypsum has a solubility of about 10 g/l or less at 25.degree. C.,
to undergo a hydration reaction and precipitate gypsum from the
aqueous liquid medium; and grinding the gypsum during precipitation
to a particle size distribution with at least about 15% of the mass
of ground gypsum having a particle size of about 5.5 .mu.m or less;
wherein the liquid medium and the ground gypsum form a slurry
comprising about 95 wt % to about 20 wt % gypsum.
32. The method of claim 31, wherein the liquid medium includes a
phosphate.
33. The method of claim 32, wherein the solubility inhibitor is
sodium trimetaphosphate.
Description
BACKGROUND OF THE INVENTION
[0001] The present invention relates to compositions for gypsum
board, and more specifically to liquid gypsum set accelerators used
in the manufacture of gypsum board.
[0002] Gypsum board (e.g., wallboard or drywall) is commonly used
in the building industry for the construction of walls and other
structures. Gypsum has a number of desirable physical properties,
including fire resistance, thermal and hydrometric dimensional
stability, compressive strength, and neutral pH. A major ingredient
in the manufacture of gypsum wallboard is calcium sulfate
hemihydrate, commonly referred to as "calcined gypsum" or "stucco."
Stucco is prepared by drying, grinding, and calcining raw gypsum
(i.e. calcium sulfate dihydrate). The raw gypsum is dried in a kiln
to remove free moisture and ground in a mill to a desired fineness.
Dried, fine-ground gypsum is also referred to as "land plaster."
The land plaster is calcined by heating to undergo a dehydration
reaction that produces calcium sulfate hemihydrate (stucco) and
water vapor, as described by the following chemical equation:
CaSO.sub.4.2H.sub.2O+heat.fwdarw.CaSO.sub.4.1/2H.sub.2O+11/2H.sub.2O
[0003] The calcined gypsum, or stucco, has the desirable property
of being chemically reactive with water and will "set" rather
quickly when the two are mixed together, to form a matrix of
calcium sulfate dihydrate crystals. The hydration or setting
reaction is the reverse of the calcination reaction, and proceeds
according to the following chemical equation:
CaSO.sub.4.1/2H.sub.2O+11/2H.sub.2O.fwdarw.CaSO.sub.4.2H.sub.2O+heat
As shown by the chemical equation, the setting reaction is
exothermic and is accompanied by the release of heat.
[0004] Gypsum wallboard comprises a gypsum core sandwiched between
two sheets of facing material (e.g., paper or fiberglass). The
gypsum core is commonly produced from a gypsum slurry that is
prepared as a mixture of dry and wet ingredients. The dry
ingredients consist primarily of stucco, and may include, but are
not limited to, any combination of fiberglass, set accelerators,
functional fillers (e.g., vermiculite), potash, crystal modifiers
(e.g., boric acid), binders (e.g., natural polymers such as
starch), and/or other ingredients as are known in the art. The wet
ingredients consist of water and may include paper pulp (the "pulp
paper solution"), and/or one or more additional components that are
known in the art, including, potash, dispersants, set retarders,
polymers, wax emulsion, silicone, surfactants, and thickening
agents. If present, the pulp paper solution along with the gauging
water provide a significant portion of the water that forms the
gypsum slurry of the core composition of the wallboard. The dry
ingredients, gauging water, and the pulp paper solution contain the
basic chemical components of a piece of wallboard.
[0005] The commercial manufacture of gypsum wallboard typically
involves a continuous, high-speed process. The dry and wet
ingredients, gauging water, and pulp paper solution are combined in
a mixer (e.g., a pin mixer) to create a fluid mixture or slurry.
The gypsum slurry exits the pin mixer into a canister and is
discharged through an outlet chute or "boot," which spreads the
slurry onto a moving, continuous sheet of bottom facing material
(back). A moving, continuous sheet of top facing material (face) is
placed on the slurry, so that the slurry is sandwiched between the
top and bottom facing materials to form the gypsum board. The board
passes through a forming station which forms the wallboard to the
desired thickness and width. Although the facing material is
described as paper, other materials known in the art may be used as
a facing material, such as fiberglass mat.
[0006] The board travels along a belt line for several minutes,
during which time the board stiffens and "sets" as the stucco and
water rapidly undergo a hydration reaction to form crystals of
calcium sulfate dihydrate, as described above. The boards are cut
to a desired length and fed into a large, continuous kiln for
drying. During the drying process, the excess water (free water) is
evaporated from the gypsum core while the chemically bound water is
retained in the newly formed gypsum crystals.
[0007] The time required to complete the setting reaction is
generally governed by the speed and length of the production line
and typically ranges from about 5 to 15 minutes. The rate of the
stucco hydration reaction can vary based on factors such as the
method of calcination, slurry temperature, and the type of raw
gypsum (e.g., natural or synthetic). Gypsum set accelerators and
retarders are commonly added to the gypsum slurry to adjust the
rate of the setting reaction and ensure that the gypsum slurry has
sufficiently set and hardened to allow the board to be cut, and
that the hydration reaction is substantially complete before drying
in the kiln. The ratio between the accelerator and retarder, as
well as the quality of these agents, along with other factors such
as mix temperature and the water to stucco ratio will affect the
hardening rate of the stucco.
[0008] A common accelerator used to reduce the set time of the
gypsum slurry is calcium sulfate dihydrate, which is produced as a
dry powder from crushed and dried gypsum. The gypsum may be
synthetic or naturally occurring. The raw gypsum is ground in a
high energy mill to produce a fine gypsum powder that is used as a
catalyst and crystal seed source for gypsum hydration and crystal
nucleation during gypsum board manufacture.
[0009] Land plaster based accelerators are susceptible to
degradation and reduced potency before they can be added to the
gypsum slurry. The process of grinding the gypsum to produce land
plaster generates heat, which may cause partial calcination and can
require intermediate cooling stages that interrupt the
manufacturing process. Calcination of the accelerator may also
occur upon mixing with stucco that is still warm from the
calcination processor in elevated process temperatures. Humid
conditions also lead to a loss in potency. The exposure to moisture
may cause clumping of the calcium sulfate dihydrate particles and
may also reduce crystallinity. The loss in potency can cause
inconsistent hydration reaction rates and may increase the amount
of the accelerator required to achieve the desired setting time.
Furthermore, the limited shelf life of the accelerator increases
the difficulty in maintaining a store of accelerator to support a
continuous production process.
[0010] Land plaster based accelerators can also be difficult to
disperse in the gypsum slurry, and can cause problems in the
manufacturing process. Fine dry powders are susceptible to caking
and clumping during storage, and can also form insoluble
agglomerates when introduced to water. To ensure that the
accelerator is adequately dispersed in the gypsum slurry,
conventional accelerators are typically introduced to the
manufacturing process at the pin mixer, with the stucco and other
dry ingredients. However, the accelerator begins to promote the
setting reaction in the mixer and can cause lumps to form in the
gypsum slurry. These lumps can clog and obstruct the flow of the
gypsum slurry through the equipment, may result in uneven discharge
and spreading of the gypsum slurry onto the facing material, may
interfere with the forming of the gypsum board, and may cause
breaks in the paper facing material which can create process upsets
and downtime. Thus, the use of conventional accelerators often
requires interruption of manufacturing for periodic cleaning of the
mixer and other equipment, resulting in substantial process
downtime.
[0011] Therefore, it would be desirable to provide a gypsum set
accelerator that has reduced susceptibility to degradation and loss
of potency, and that reduces process upset and the need for
equipment maintenance and downtime. It would also be useful to
minimize the dwell time of the accelerator while the gypsum slurry
is in the equipment, to allow the majority of the setting reaction
to occur after the gypsum slurry has been applied to the facing
material and the board is formed. Thus, it would be desirable to
provide a gypsum set accelerator that is more easily dispersed in
the gypsum slurry, to allow the accelerator to be introduced into
the manufacturing process downstream of the mixer--e.g., at the
canister or boot.
SUMMARY OF THE INVENTION
[0012] Liquid gypsum accelerators are disclosed that comprise a
slurry including ground gypsum and a liquid medium. The ground
gypsum is in an amount of about 95 wt % to about 20 wt % of the
slurry and has a particle size distribution with at least about 15%
of the mass of ground gypsum having a particle size of about 5.5
.mu.m or less. The liquid medium is selected wherein gypsum has a
solubility of about 10 g/l or less at 25.degree. C.
[0013] In another embodiment, a method of making a gypsum set
accelerator comprises the steps of providing gypsum and a liquid
medium in which gypsum has a solubility of about 10 g/l or less at
25.degree. C. The gypsum is ground to a particle size distribution
with at least about 15% of the mass of ground gypsum having a
particle size of about 5.5 .mu.m or less. The liquid medium is
added to the gypsum to form a slurry comprising about 95 wt % to
about 20 wt % gypsum. In a further embodiment, the gypsum is
provided by the steps of providing stucco and an aqueous liquid
medium. The stucco and aqueous liquid medium are combined to
undergo a hydration reaction and precipitate the gypsum from the
aqueous liquid medium. The gypsum may be ground during
precipitation.
[0014] In another embodiment, a method of making a gypsum board
composition comprises the steps of providing dry ingredients
including stucco, wet ingredients including water, gypsum and a
liquid medium in which gypsum has a solubility of about 10 g/l or
less at 25.degree. C. The dry and wet ingredients are mixed to form
a gypsum slurry. The gypsum is ground to a particle size
distribution with at least about 15% of the mass of ground gypsum
having a particle size of about 5.5 .mu.m or less. The liquid
medium is added to the gypsum to form a gypsum set accelerator
comprising about 95 wt % to about 20 wt % gypsum. The gypsum set
accelerator is added to the gypsum slurry.
BRIEF DESCRIPTION OF THE DRAWINGS
[0015] The embodiments described herein and other features,
advantages, and disclosures contained herein, and the manner of
attaining them, will be better understood from the following
description in conjunction with the accompanying drawing figures,
in which like reference numerals identify like elements, and
wherein:
[0016] FIG. 1 is a data plot of the stucco hydration rate using a
conventional and a liquid gypsum set accelerator, as measured by
the temperature of the gypsum slurry over time.
[0017] FIG. 2 is a data plot showing the crystal morphology of a
wallboard produced using a conventional gypsum accelerator; and
[0018] FIG. 3 is a data plot showing the crystal morphology of a
wallboard produced using a liquid gypsum set accelerator.
DETAILED DESCRIPTION OF THE INVENTION
[0019] In the following detailed description of embodiments of the
present disclosure, reference is made to the accompanying drawings
that form a part hereof, and in which is shown by way of
illustration, and not by way of limitation, such specific
embodiments. It is to be understood that other embodiments may be
utilized and that changes may be made without departing from the
spirit and scope of the present disclosure.
[0020] Compositions for liquid gypsum set accelerators used in the
manufacture of gypsum board are described. The liquid accelerator
comprises a slurry of land plaster in a liquid medium in which the
calcium sulfate dihydrate is no more than moderately soluble. Those
of skill in the art will appreciate that the solubility of the
calcium sulfate dihydrate will vary according to the process
conditions, such as the temperature. In one embodiment, the calcium
sulfate dihydrate is no more than moderately soluble under normal
process conditions--e.g., a solubility of about 10 g/l or less at
25.degree. C. In a preferred embodiment, the land plaster has a
solubility in the liquid medium that is similar to water--e.g.,
about 2.5 g/l at 25.degree. C. or less. More preferably, the land
plaster is substantially insoluble in the liquid medium--e.g., a
solubility of about 1 g/l at 25.degree. C. or less.
[0021] The liquid accelerator composition may comprise land plaster
in an amount between about 95 wt % to about 20 wt %, and liquid
media in an amount between about 5 wt % to about 80 wt %. In a
preferred embodiment, the liquid accelerator composition comprises
land plaster in an amount between about 40 wt % to about 20 wt %,
and liquid media in an amount between about 60 wt % to about 80 wt
%. In a particularly preferred embodiment, the liquid accelerator
composition comprises land plaster in an amount of about 35 wt
%.
[0022] Suitable liquid media include alcohols, glycerin, water and
other liquid media as are known in the art. Combinations of liquid
media may also be used, including multiphase mixtures liquid media
(e.g., organic and aqueous phases). In one embodiment, the liquid
medium comprises water or other aqueous composition. In a preferred
embodiment, the liquid media is non-aqueous, and more preferably is
anhydrous. In a particularly preferred embodiment, the liquid media
is reagent grade (anhydrous) isopropyl alcohol.
[0023] In some cases, the use of an aqueous liquid media may
produce accelerators that have reduced potency in comparison to
accelerators based on non-aqueous liquid media. Where water or
other aqueous composition is used, the liquid medium may include a
solubility inhibitor(s). Suitable solubility inhibitors include
phosphates, such as sodium trimetaphosphate (STMP). Without being
limited by any particular theory, it is believed that the
solubility inhibitors function to reduce the loss of active sites
and the decrease in crystallinity of the land plaster particles
which may occur in an aqueous liquid medium.
[0024] The land plaster may be derived from gypsum that is
naturally occurring or synthetic (e.g., a byproduct of an
industrial process). High grade and low grade land plasters may be
used. High grade land plaster typically comprises at least about 80
wt % calcium sulfate dihydrate. Low grade land plasters commonly
include anhydrites, sand, clay and/or other inert materials and
impurities. The inert materials and impurities are typically
present in amounts small enough that they are not believed to
significantly affect the setting reaction or impair activity of the
accelerator. In one embodiment, the calcium sulfate dihydrate is
substantially free of phosphogypsum.
[0025] The land plaster may undergo additional grinding to further
reduce the size and increase the number of particles. In one
embodiment, the gypsum set accelerator has a particle size
distribution with at least about 15% of the mass of land plaster
having a particle size of about 5.5 .mu.m or less, and preferably
at least about 40%. In a preferred embodiment, the gypsum set
accelerator has a particle size distribution with a mass median
diameter (D.sub.50) of less than 15 .mu.m, and preferably about 5.5
.mu.m or less.
[0026] The additional grinding increases the crystalline surface
area and number of active sites for accelerating the setting
reaction of the gypsum slurry. The active sites promote the stucco
hydration reaction by acting as nucleation sites for the formation
of calcium sulfate dihydrate crystals in the gypsum slurry. The
higher the number of active sites, the greater the potency of the
accelerator and the shorter the time period required for the gypsum
slurry to set (set time). The improved hydration reaction rate
reduces the amount of accelerator needed for manufacture, and
allows increased rates of wallboard production and shortened
manufacturing line lengths. The increased number of accelerator
particles also results in gypsum board having increased gypsum
crystal counts per unit volume of wallboard.
[0027] A variety of methods may be used to further grind the land
plaster, including a ball mill, an attritor mill, a vibration mill,
bead mill, and other methods known in the art. Grinding aids and/or
additional grinding media may also be used, as are known in the
art. In a preferred embodiment, the land plaster is ground in a
planetary ball mill. The planetary ball mill utilizes several
grinding mechanisms that involve a combination of compressive,
shear and abrasive forces--including bearing on bearing collisions,
bearing on wall collisions, and particle on particle collisions.
Without being limited to any particular theory, the combination of
grinding mechanisms is believed to produce a particle morphology
and/or size distribution with an unexpectedly high number of active
sites compared to other methods of grinding--e.g., a jet mill which
essentially operates by particle on particle collisions.
[0028] The land plaster may be ground separately and then mixed
with the liquid media to form the liquid gypsum set accelerator
slurry. In one embodiment, the land plaster is ground in the
presence of the liquid medium, which is believed to produce finer
particles that are well dispersed in the resulting liquid
accelerator slurry. In an alternative embodiment, the liquid gypsum
set accelerator may be produced by combining stucco with an aqueous
liquid medium such as water or other aqueous composition. As the
hydration reaction proceeds, the newly formed gypsum crystals
precipitate from the liquid medium. In a further embodiment, the
stucco and aqueous liquid medium are combined in a mill, and the
newly formed gypsum crystals are ground during precipitation to
form a slurry of fine land plaster particles. The aqueous liquid
medium preferably includes a solubility inhibitor, such as a
phosphate.
[0029] The presence of the liquid medium is also believed to
protect the gypsum set accelerator from degradation and the loss of
potency during grinding and storage. Grinding in liquid media
reduces friction and exposure to high temperatures, which reduces
the risk of calcination and the need to interrupt the grinding
process for cooling. Furthermore, the liquid gypsum set accelerator
is found to be shelf stable, with minimal loss of effectiveness
over time due to aging when maintained in solution. X-ray powder
diffraction analysis shows that conventional dry land plaster loses
crystallinity after prolonged exposure to humid conditions. The
presence of the liquid medium, particularly an anhydrous liquid
medium (e.g., alcohol or glycerin), is found to protect the freshly
created active sites from degradation. The increased storage life
facilitates continuous wallboard manufacturing, and the improved
effectiveness and stability of the liquid gypsum set accelerator
reduces the amount of accelerator required in the manufacturing
process.
[0030] The liquid gypsum set accelerator may be introduced to the
manufacturing process at any point in production process. In
contrast to conventional dry accelerators which are typically added
to the pin mixer, the fluidity and consistency of the liquid gypsum
set accelerator reduces the need for aggressive mixing to ensure
dispersion in the gypsum slurry. The liquid gypsum accelerator may
be effectively introduced to the gypsum slurry at any point in the
manufacturing process, including at the pin mixer, foam generator
and/or roll coater. In a preferred embodiment, the liquid gypsum
set accelerator is introduced at a point after the wet and dry
ingredients are combined in the pin mixer (e.g., at the canister or
boot), to reduce the formation of lumps and build up in the pin
mixer and minimize the dwell time of the accelerator in the gypsum
slurry. As a result, the mixer requires less frequent cleaning, and
the problems of process downtime and upset are reduced.
[0031] The liquid gypsum set accelerator may also comprise one or
more additives. For example, the aqueous liquid media may also
include additives that protect the land plaster from degradation.
Such additives include soaps or surfactants, dispersants such as
polycarboxylate ethers (PCE), naphthalene sulfonates,
lignosulfonates, alginates, saccharides, phosphates, complexing
agents such as EDTA, and other additives known in the art. The
liquid media may also be a multiphase mixture containing varied
fractions of organic and aqueous phases of additives and liquid
media or combinations of liquid media.
[0032] The following examples are included to demonstrate preferred
embodiments of the invention. It should be appreciated by those of
skill in the art that the techniques disclosed in the examples
which follow represent techniques discovered by the inventors to
function well in the practice of the invention, and thus can be
considered to constitute preferred modes for its practice. However,
those of skill in the art should, in light of the present
disclosure, appreciate that many changes can be made in the
specific embodiments which are disclosed and still obtain a like or
similar result without departing from the scope of the
invention.
Example 1
[0033] Liquid gypsum set accelerator was prepared in a planetary
ball mill (Retsch--Newtown, Pa.) by grinding a mixture of 30 g land
plaster and 60 ml isopropyl alcohol (isopropanol) for 1 hour at 500
rpm in a 125 ml stainless steel vessel equipped with thirty 5 mm
stainless steel bearings. The resulting slurry comprised about 35
wt % land plaster. A conventional ball mill accelerator was used as
a control.
[0034] The particle size distribution of the liquid gypsum set
accelerator and control were measured using laser diffraction
analysis (Microtrac--York, Pa.), and are shown in Table 1. The
liquid gypsum set accelerator had a particle size distribution that
was substantially smaller than the control. Approximately 50% of
the mass of the liquid gypsum set accelerator particles had a
diameter (D.sub.50) of about 5.52 .mu.m, and about 45.74% of the
particles had a diameter less than 5.5 .mu.m (<5.5 .mu.m). In
contrast, land plaster without grinding had a D.sub.50 of about
39.79 .mu.m. The dry accelerator comprised of a ground mixture of
land plaster and starch (1:1, land plaster:starch) had a D.sub.50
of about 15.71 .mu.m.
TABLE-US-00001 TABLE 1 Particle Size Distribution Sample D.sub.50
(.mu.m) <5.5 .mu.m (%) Land Plaster (no grinding) 39.79 11.29
Starch (no grinding) 26.70 9.75 Dry Accelerator (1 hr grinding)
15.71 9.66 Liquid Accelerator (1 hr grinding) 5.52 45.74 Liquid
Accelerator (2 hr grinding) 4.32 56.82
Example 2
[0035] The gypsum set time was measured for gypsum boards prepared
using either the liquid gypsum set accelerator or a control
accelerator as described in Example 1. Experimental 1/2 inch, 1250
lb/msf gypsum boards were prepared in a laboratory, having a gypsum
slurry composition as set forth in Table 2, comprising about 1%
accelerator on stucco (equivalent land plaster basis). The control
accelerator was added to the gypsum board composition before liquid
reagents, as in conventional manufacturing processes. The liquid
gypsum set accelerator was added to the gypsum board composition
with liquid reagents, as in at the boot or canister.
TABLE-US-00002 TABLE 2 Gypsum Board Composition Component Weight
(g) Stucco 783 Dispersant 2.5 Accelerator 9.25 Retarder 0.04 Starch
16.4 Paper Pulp 0.54 Soap Solution 14 Total Water 744.44 Dextrose
1.0 Coalescing Agent 0.14 Total 1571.31
[0036] The rate of the hydration reaction was measured as the
temperature of the gypsum slurry over time, and is shown in FIG. 1.
The gypsum board prepared with the liquid gypsum set accelerator
reached a higher peak temperature and exhibited a rate of increase
in temperature that was substantially greater than the control
gypsum board prepared with conventional ball mill accelerator. In
particular, the control gypsum boards reached a peak temperature of
about 45-46.degree. C. in about 340 seconds, whereas the gypsum
board prepared with liquid gypsum set accelerator reached the same
temperature in about 190 seconds--i.e. in a little more than half
the time observed using a conventional accelerator.
Example 3
[0037] The crystal morphology of gypsum board samples prepared
using conventional and liquid gypsum set accelerators was compared.
Samples of set gypsum board compositions were prepared using the
liquid gypsum set accelerator and control conventional dry
ball-milled accelerator of Example 1. The crystal morphology of the
samples was analyzed by scanning electron micrograph (SEM), and
crystal habit and numbers were tabulated by analyzing a known area
of the SEM micrograph. The control sample was found to have a
gypsum crystal count of 91 over an area of 112.5.mu..sup.2, with an
average length of 2.18 .mu.m, an average width of 0.49 .mu.m, and
an average aspect ratio of 6.44, as shown in FIG. 2. The sample
prepared using the liquid gypsum set accelerator was found to have
a significantly higher gypsum crystal count of 137, with smaller
gypsum crystals having an average length of 1.65 .mu.m, an average
width of 0.42 .mu.m, and an average aspect ratio of 4.56, as shown
in FIG. 3.
Example 4
[0038] The compressive strength was measured for samples of set
gypsum prepared using the liquid gypsum set accelerator and control
accelerator. The samples were prepared as described in Example 2,
except with a water to stucco ratio (w/s) of 1.3:1 (425 g water and
325 g stucco). The samples were mixed in a blender and formed into
2 inch cubes. Compositions containing the liquid gypsum set
accelerator experienced some foaming in the blender due to the
presence of isopropanol. A defoaming agent was used to ensure that
the cubes had a consistent weight (density) across the samples. The
compressive strength of the sample cubes was measured pursuant to
the ASTM C472 standard as is known in the art, and the results
shown in Table 3.
TABLE-US-00003 TABLE 3 Compressive Strength Sample Weight (g)
Compressive Strength (psi) Control 95.47 913.60 Land
Plaster/Isopropanol 93.86 945.10
[0039] The physical properties of the set gypsum samples were not
affected by the liquid gypsum set accelerator and the increased
activity of the accelerator in promoting the hydration reaction.
Samples prepared using the liquid gypsum set accelerator were found
to have similar or improved compressive strength in comparison to
samples prepared with the control accelerator. Tests also showed
comparable nail pull strength for boards prepared using the liquid
gypsum set accelerator in comparison to conventional ball mill
accelerator.
[0040] While particular embodiments of the present disclosure have
been illustrated and described, it would be obvious to those
skilled in the art that various other changes and modifications can
be made without departing from the spirit and scope of the present
disclosure. It is therefore intended to cover in the appended
claims all such changes and modifications that are within the scope
of this disclosure.
* * * * *