U.S. patent application number 15/639669 was filed with the patent office on 2017-11-30 for low refractive layer and anti-reflective film comprising the same.
The applicant listed for this patent is LG CHEM, LTD.. Invention is credited to Jin Seok BYUN, Yeong Rae CHANG, Eun Kyu HER, Seok Hoon JANG, Boo Kyung KIM.
Application Number | 20170343704 15/639669 |
Document ID | / |
Family ID | 58543438 |
Filed Date | 2017-11-30 |
United States Patent
Application |
20170343704 |
Kind Code |
A1 |
KIM; Boo Kyung ; et
al. |
November 30, 2017 |
LOW REFRACTIVE LAYER AND ANTI-REFLECTIVE FILM COMPRISING THE
SAME
Abstract
The present invention relates to a low refractive layer and an
anti-reflective film comprising the same. The low refractive layer
can exhibit excellent optical properties such as a low reflectance
and a high light transmittance, and excellent mechanical properties
such as high wear resistance and scratch resistance at the same
time, without adversely affecting the color of the polymer resin
forming the low refractive layer. In particular, due to the
excellent alkali resistance, the low refractive layer can maintain
excellent physical properties even after alkali treatment.
Therefore, when introducing a low refractive layer to the display
device, it is expected that the production process can be
simplified and further the production rate and the productivity can
significantly increase.
Inventors: |
KIM; Boo Kyung; (Daejeon,
KR) ; CHANG; Yeong Rae; (Daejeon, KR) ; JANG;
Seok Hoon; (Daejeon, KR) ; HER; Eun Kyu;
(Daejeon, KR) ; BYUN; Jin Seok; (Daejeon,
KR) |
|
Applicant: |
Name |
City |
State |
Country |
Type |
LG CHEM, LTD. |
Seoul |
|
KR |
|
|
Family ID: |
58543438 |
Appl. No.: |
15/639669 |
Filed: |
June 30, 2017 |
Related U.S. Patent Documents
|
|
|
|
|
|
Application
Number |
Filing Date |
Patent Number |
|
|
PCT/KR2016/009111 |
Aug 18, 2016 |
|
|
|
15639669 |
|
|
|
|
Current U.S.
Class: |
1/1 |
Current CPC
Class: |
G02B 1/111 20130101;
G02B 1/14 20150115 |
International
Class: |
G02B 1/111 20060101
G02B001/111; G02B 1/14 20060101 G02B001/14 |
Foreign Application Data
Date |
Code |
Application Number |
Aug 18, 2015 |
KR |
10-2015-0116260 |
Aug 17, 2016 |
KR |
10-2016-0104409 |
Claims
1. A low refractive layer satisfying the following formula 1.
0.5.gtoreq..DELTA.b*=|b*.sub.1-b*.sub.0| [Formula 1] in the formula
1, b*.sub.0 is a b* value in a L*a*b* color coordinate system as
defined by the International Commission on Illumination as to the
low refractive layer; and b*.sub.1 is a b* value in a L*a*b* color
coordinate system as measured in the same manner as a method for
measuring b*.sub.0 as to the film prepared by immersing the low
refractive layer for 2 minutes in 10 wt % sodium hydroxide aqueous
solution heated to 30.degree. C., washing the immersed layer with
water, wiping off moisture, followed by immersing the wiped layer
for 30 seconds in 10 wt % sodium hydroxide aqueous solution heated
to 55.degree. C., washing it with water and wiping off
moisture.
2. The low refractive layer according to claim 1 wherein the
b*.sub.0 value in the formula 1 is from 1 to -8.
3. The low refractive layer according to claim 1 wherein the
b*.sub.1 value in the formula 1 is from 1.5 to -8.5.
4. The low refractive layer according to claim 1, satisfying the
following formula 2:
30%.gtoreq..DELTA.S=[(S.sub.0-S.sub.1)/S.sub.0].times.100 [Formula
2] in the formula 2, S.sub.0 is the maximum load that scratches are
not generated, when rubbing the surface of the low refractive layer
while applying a load to a grade #0000 steel wool and reciprocating
ten times at a speed of 24 rpm; and S.sub.1 is the maximum load
that scratches are not generated, as measured in the same manner as
a method of measuring S.sub.0 with respect to the film prepared by
immersing the low refractive layer for 2 minutes in 10 wt % sodium
hydroxide aqueous solution heated to 30.degree. C., washing the
immersed layer with water, wiping moisture off, followed by
immersing the resulting layer for 30 seconds in 10 wt % sodium
hydroxide aqueous solution heated to 55.degree. C., and then
washing it with water and wiping moisture off.
5. The low refractive layer according to claim 4 wherein the
S.sub.0 value in the formula 2 is from about 250 to 800 g.
6. The low refractive layer according to claim 4 wherein the
S.sub.1 value in the formula 2 is from about 200 to 800 g.
7. The low refractive layer according to claim 1 wherein the low
refractive layer exhibits a minimum reflectance in the wavelength
range of about 480 to 680 nm.
8. The low refractive layer according to claim 1 wherein an average
reflectance for light in the wavelength range of 380 to 780 nm is
from 0.9 to 2.5%.
9. The low refractive layer according to claim 1 wherein the low
refractive layer includes a photo-cured product obtained by
photo-curing a photocurable coating composition comprising a
photopolymerizable compound, a polysilsesquioxane substituted with
at least one reactive functional group, a fluorine-based compound
containing --O--CF.sub.2CF.sub.2--O--CF.sub.3, an inorganic
particle and a photopolymerization initiator.
10. The low refractive layer according to claim 1 wherein the
b*.sub.0 value in the formula 1 is from -2.27 to -8.
11. The low refractive layer according to claim 1 wherein the
b*.sub.1 value in the formula 1 is from -1.84 to -8.5.
12. An anti-reflective film comprising a low refractive layer of
claim 1; and a hard coating layer formed on one surface of the low
refractive layer.
13. The anti-reflective film according to claim 12 wherein the hard
coating layer includes a binder resin containing a photocurable
resin; and an organic or inorganic fine particle dispersed in the
binder resin.
14. The anti-reflective film according to claim 13 wherein the
organic or inorganic fine particle has a particle diameter of 1 to
10 .mu.m.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is a Continuation Bypass of International
Application No. PCT/KR2016/009111, filed Aug. 18, 2016, and claims
the benefit of Korean Patent Application No. 10-2015-0116260 on
Aug. 18, 2015 and Korean Patent Application No. 10-2016-0104409 on
Aug. 17, 2016 with the Korean Intellectual Property Office, the
disclosures of which are herein incorporated by reference in their
entirety.
TECHNICAL FIELD
[0002] The present invention relates to a low refractive layer and
an anti-reflective film comprising the low refractive layer and a
hard coating layer.
BACKGROUND OF ART
[0003] In general, a flat panel display device such as PDP or LCD
is equipped with an anti-reflective film to minimize the reflection
of light made incident from the outside.
[0004] As a method for minimizing the reflection of light, a method
of dispersing a filler such as inorganic fine particle to a resin
and coating the filler on a substrate film to impart irregularities
(anti-glare: AG coating); a method of utilizing an interference of
light by forming a plurality of layers having refractive indexes
different from each other on a substrate film (anti-reflection: AR
coating); or a method of utilizing a combination thereof have been
known.
[0005] Among them, in case of the AG coating, the absolute amount
of the reflected light is a level equivalent to a conventional hard
coating, but a low-reflection effect can be obtained by reducing
the amount of light entering the eye using the scattering of light
through the irregularities. However, in the AG coating, the screen
resolution degrades due to surface irregularities. Thus, in recent
years, many studies have been made about the AR coating.
[0006] As the film using the AR coating, those having a multilayer
structure wherein a hard coating layer (high refractive index
layer), a low-reflection coating layer or the like are laminated on
a substrate film have been commercialized. However, a method of
forming a plurality of layers as described above has a drawback
that as the steps of forming the respective layers are separately
performed, the interlayer adhesion (interfacial adhesion) is
weakened, and thereby the scratch resistance is poor and the
production cost is high.
[0007] Accordingly, many studies have been performed to reduce the
absolute amount of reflection of light made incident from the
outside and to improve the scratch resistance of the surface, but
the degree of improving the physical properties associated
therewith is insufficient. In addition, a method of adding an
inorganic additive or the like in order to improve the scratch
resistance of a polymer film that is applied to the anti-reflective
film, has been known. However, according to this known method,
since the alkali resistance of the polymer film is greatly
decreased, there was a limit that applying to the process for the
production of a polarizing plate or the is incompatible.
DETAILED DESCRIPTION OF THE INVENTION
Technical Problem
[0008] An object of the present invention is to provide a low
refractive layer capable of exhibiting excellent optical properties
and mechanical properties.
[0009] Another object of the present invention is to provide an
anti-reflective film comprising the low refractive layer.
Technical Solution
[0010] Hereinafter, a low refractive layer and an anti-reflective
film comprising the same according to specific embodiments of the
present invention will be described in more detail.
[0011] According to an embodiment of the invention, there is
provided a low refractive layer satisfying the following formula
1.
0.5.gtoreq..DELTA.b*=|b*.sub.1-b*.sub.0| [Formula 1]
[0012] In the formula 1,
[0013] b*.sub.0 is a b* value in a L*a*b* color coordinate system
as defined by the International Commission on Illumination as to
the low refractive layer; and
[0014] b*.sub.1 is a b* value in a L*a*b* color coordinate system
as measured in the same manner as a method for measuring b*.sub.0
as to the film prepared by immersing the low refractive layer for 2
minutes in 10 wt % sodium hydroxide aqueous solution heated to
30.degree. C., washing the immersed layer with water, wiping
moisture off, followed by immersing the wiped layer for 30 seconds
in 10 wt % sodium hydroxide aqueous solution heated to 55.degree.
C., washing it with water and wiping off moisture.
[0015] As used herein, the term "low refractive layer" may refer to
a layer having a low refractive index. For example, it may refer to
a layer exhibiting a refractive index of about 1.2 to 1.6.
[0016] The low refractive layer according to an embodiment of The
invention has excellent properties including optical properties
such as reflectance and color in visible light region and
mechanical properties such as scratch resistance. Therefore, the
low refractive layer is used in a display device and can greatly
prevent a glaring phenomenon caused by light made incident from the
outside of the device without deterioration of the image. The
surface of the device can be effectively protected from external
impact or stimulation and the like.
[0017] In addition, the low refractive layer has properties that
cause very little change in the above-described physical
properties, even when exposed to an alkali. Due to this high alkali
resistance, the low refractive layer can omit the process for
attaching and detaching a protective film which is essentially
performed to protect a low refractive layer during the production
process of the display device. Thereby, the production process of
the display device is simplified and the production costs can be
reduced. In particular, it is expected that the low refractive
layer is excellent in alkali resistance at high temperature and
thus the conditions for the production process of the display
device can be adjusted to more severe conditions, thereby greatly
improving the production rate and the productivity without
degrading the quality of the device.
[0018] More specifically, the low refractive layer can satisfy the
above-described formula 1. In the formula 1, b*.sub.0 is a value
that can evaluate an initial color of the low refractive layer, and
b*.sub.1 is a value that can evaluate a color of the alkali-treated
low refractive layer. In this case, the low refractive layer is
treated with alkali twice. In particular, the second alkali
treatment is carried out by a sodium hydroxide aqueous solution at
high temperature. Thus, the alkali resistance of the low refractive
layer at high temperature can be evaluated through the extent of
the change in the color of the low refractive layer before and
after the alkali treatment according to the formula 1. The alkali
treatment conditions are as described in the formula 1, and for
more details related to the alkali treatment refer to Experimental
Examples which will be described later. In addition, for more
details related to the evaluation method of the b* value in L*a*b*
color coordinate system as to the low refractive layer before and
after the alkali treatment refer to Experimental Examples which
will be described below.
[0019] The low refractive layer according to one embodiment of the
invention has excellent alkali resistance and thereby the degree of
color change (.DELTA.b*) before and after the alkali treatment
according to the formula 1 may be 0.5 or less, 0.45 or less, or 0.4
or less. The low refractive layer is likely to have no color change
even after alkali treatment at high temperature, and thus .DELTA.b*
in the formula 1 may be zero.
[0020] In a conventional refractive layer, inorganic fillers have
been added to exhibit a low refractive index in a visible light
range or to improve a scratch resistance. However, these fillers
greatly decreased the alkali resistance of the low refractive
layer, and this made it difficult to apply the low refractive layer
to the production process of the display which is essentially
accompanied by the alkali treatment process. There was a problem
that it adversely affects the image quality of the display device
by coloring the low refractive layer.
[0021] However, the low refractive layer according to one
embodiment of the invention can exhibit properties such as
excellent scratch resistance and alkali resistance, without color
change, or while minimizing color change, for the polymer resin
contained in the low refractive layer. As one example, the b* value
(b*.sub.0 value in the formula 1) before and after the alkali
treatment of the low refractive layer may be from 1 to -8, from
-2.27 to -8 or from 1 to -5.
[0022] If the b* value in the L*a*b* color coordinate system is a
positive number, it represents a color biased toward yellow. If the
b* value is a negative number, it represents a color biased toward
blue. Therefore, the low refractive layer according to one
embodiment of the invention represents a color coordinate value as
described above, and thus can effectively prevent the glaring
phenomenon while transmitting an image as it is, without changing
the image quality of the display device.
[0023] Additionally, the low refractive layer according to one
embodiment of the invention exhibits excellent alkali resistance
and thus characteristics having no color change even when exposed
to an alkali at high temperature. As an example, the b* value
(b*.sub.1 value in the formula 1) after alkali treatment of the low
refractive layer may be from 1.5 to -8.5, from -1.84 to -8.5, from
1 to -8, from 0 to -8 or from 1.5 to -5.5.
[0024] Meanwhile, the low refractive layer according to an
embodiment of the invention can satisfy the following formula 2 due
to its excellent alkali resistance:
30%.gtoreq..DELTA.S=[(S.sub.0-S.sub.1)/S.sub.0].times.100 [Formula
2]
[0025] in the formula 2,
[0026] S.sub.0 is the maximum load that scratches are not
generated, when rubbing the surface of the low refractive layer
while applying a load to a grade #0000 steel wool and reciprocating
ten times at a speed of 24 rpm; and
[0027] S.sub.1 is the maximum load that scratches are not
generated, as measured in the same manner as a method of measuring
S.sub.0 as to the film prepared by immersing the low refractive
layer for 2 minutes in 10 wt % sodium hydroxide aqueous solution
heated to 30.degree. C., washing the immersed layer with water,
wiping moisture off, followed by immersing the wiped layer for 30
seconds in 10 wt % sodium hydroxide aqueous solution heated to
55.degree. C., and then washing it with water and wiping moisture
off.
[0028] The unit of the load in the formula 2 is g/(2*2 cm.sup.2),
which means weight (g) per area (2*2 cm.sup.2) having a width of 2
cm and a length of 2 cm.
[0029] In the formula 2, S.sub.0 is a value that can evaluate an
initial scratch resistance of the low refractive layer, and S.sub.1
is a value that can evaluate a scratch resistance of the
alkali-treated low refractive layer. In this case, the alkali
treatment conditions are the same in the formula 1, and the scratch
resistance of the low refractive layer before and after the alkali
treatment can be evaluated as described in the formula 2. For
details related to the evaluation method of the scratch resistance
refer to Experimental Examples described which will be described
below.
[0030] Because the low refractive layer according to one embodiment
of the invention exhibits excellent alkali resistance as described
above, the change rate (.DELTA.S) in the scratch resistance before
and after alkali treatments according to the formula 2 may be 30%
or less, 25% or less, 20% or less, or 15% or less. Also, the low
refractive layer can exhibit a scratch resistance which does not
change even after alkali treatment at high temperature, and thus
.DELTA.S in the formula 2 may be 0%.
[0031] On the other hand, the low refractive layer has excellent
mechanical properties such as a scratch resistance as described
above. As an example, the scratch resistance before alkali
treatment of the low refractive layer (S.sub.0 value in the formula
2) may be about 250 to 800 g/(2*2 cm.sup.2) or about 300 to 800
g/(2*2 cm.sup.2). Additionally, the low refractive layer can
exhibit excellent scratch resistance even after alkali treatment,
due to its excellent alkali resistance. As an example, the scratch
resistance after alkali resistance of the low refractive layer
(S.sub.1 value in the formula 2) may be about 200 to 800 g/(2*2
cm.sup.2) or about 230 to 800 g/(2*2 cm.sup.2).
[0032] The low refractive layer according to an embodiment of the
invention may exhibit a minimum reflectance in the visible light
region together with excellent optical and mechanical properties
described above. More specifically, the low refractive layer can
exhibit a minimum reflectance in the wavelength range of about 480
to 680 nm or in the wavelength range of about 500 to 580 nm,
thereby effectively preventing a glaring phenomenon of the display
device.
[0033] Further, the low refractive layer according to an embodiment
of the invention can exhibit a very low reflectance in the visible
light region. More specifically, for the low refractive layer, an
average reflectance for light in the wavelength range of 380 to 780
nm may be from 0.9 to 2.5%, from 0.9 to 2.2%, from 0.9% to 2.0%,
from 0.9 to 1.5%, or from 1 to 1.3%. Accordingly, the low
refractive layer can, when introduced into the display device,
prevent the glaring phenomenon caused by light made incident from
the outside.
[0034] The average reflectance and the color coordinate value of
the low refractive layer can be measured using a spectrophotometer.
Specifically, the reflectance and the color coordinate value can be
measured by setting the following measurement conditions at room
temperature: sampling interval 1 nm (preferably 2 nm or less, but
also adjustable to 5 nm), time constant 0.1 sec, slit width 20 nm,
and medium scanning speed; darkening the opposite surface to the
surface for irradiating light among the both surfaces of the low
refract the layer so as to prevent transmission of light; and then
irradiating the light in the wavelength range of 380 nm to 780 nm.
At this time, if the low refractive layer is formed on a substrate
film; or on a hard coating layer formed on the substrate film as
described below, the surface not formed of a low refractive layer
or a hard coating layer of the substrate film can be darkened so as
to prevent transmission of light. As an example, the darkening may
be carried out by attaching a black tape to the film surface.
[0035] In addition, if the low refractive layer has a flat surface
without irregularities, a light is irradiated at an incident angle
of 5.degree. to measure the light reflected at a reflection angle
of 5.degree.. Thus, on the basis of the measured value of the
standard sample substance (BaSO.sub.4 and 95% A1 mirror, available
from Shimadzu), the reflectance according to the wavelength of the
low refractive layer is measured (measure mode). Then, the average
reflectance and color coordinate value can be derived from said
reflectance through a UV-2401PC color analysis program.
[0036] On the other hand, if the low refractive layer has a surface
with irregularities, a light is made incident perpendicularly to
the low refractive layer to thereby measure the light that is
scattered and reflected in all directions. Thus, on the basis of
the measured value of the standard sample material (BaSO.sub.4,
available from Shimadzu), the reflectance according to the
wavelength of the low refractive layer is measured (100% T mode).
Then, the average reflectance and color coordinate values can be
derived from said reflectance through a UV-2401PC color analysis
program.
[0037] The low refractive layer of one embodiment of the invention
that can exhibit excellent optical and mechanical properties as
described above may include a photo-cured product obtained by
photo-curing a photocurable coating composition comprising a
photopolymerizable compound, a polysilsesquioxane substituted with
at least one reactive functional group, a fluorine-based compound
containing O--CF.sub.2CF.sub.2--O--CF.sub.3, an inorganic particle
and a photopolymerization initiator.
[0038] The photopolymerizable compound used herein collectively
refers to a compound that causes a polymerization reaction when
irradiated with a light, for example when irradiated with visible
light or ultraviolet light.
[0039] The photocurable coating composition may include, as a
photopolymerizable compound, a monomer or oligomer containing a
(meth)acryloyl group or a vinyl group. The monomer or oligomer may
include one or more, two or more, or three or more (meth)acryloyl
groups or vinyl groups. The (meth)acryl is used herein to include
both acryl and methacryl.
[0040] Specific examples of the monomer or oligomer containing a
(meth)acryloyl group may include pentaerythritol tri(meth)acrylate,
pentaerythritol tetra(meth)acrylate, dipentaerythritol
penta(meth)acrylate, dipentaerythritol hexa(meth)acrylate,
tripentaerythritol hepta(meth)acrylate, trimethylolpropane
tri(meth)acrylate, trimethylolpropane polyethoxy tri(meth)acrylate,
ethyleneglycol di(meth)acrylate, butanediol di(meth)acrylate,
ethylhexyl (meth)acrylate, butyl (meth)acrylate or mixtures of two
or more thereof, or urethane modified acrylate oligomer, epoxide
acrylate oligomer, ether acrylate oligomer, dendritic acrylate
oligomer or mixtures of two or more thereof.
[0041] Specific examples of the monomer or oligomer containing a
vinyl group may include an oligomer or the like obtained by
polymerizing divinylbenzene, styrene, para-methyl styrene or one or
more thereof. The molecular weight of the oligomer used herein can
be adjusted to 1,000 to 10,000 g/mol.
[0042] The content of the photopolymerizable compound in the
photocurable coating composition may be adjusted to from 20% to 80%
by weight, from 30% to 70% by weight or from 30% to 65% by weight
based on the solid content of the photo-curable coating
composition, in consideration of the mechanical properties of the
low refractive layer to be finally prepared.
[0043] The solid content of the photocurable coating composition
refers to only a solid component in the photocurable coating
composition, excluding a liquid component, for example, a component
such as an organic solvent that can be optionally included as
described below.
[0044] The photocurable coating composition can include one or more
reactive functional groups-substituted polysilsesquioxane, thereby
implementing a low reflectance and a high light transmittance
without coloration, and providing the low refractive layer that can
improve the alkali resistance and at the same time ensure the
scratch resistance.
[0045] The one or more reactive functional groups-substituted
polysilsesquioxane can be included in an amount of 0.5 to 25 parts
by weight, 1 to 20 parts by weight, 1.5 to 19 parts by weight or 2
to 15 parts by weight based on 100 parts by weight of the
photopolymerizable compound. Also, the content of the one or more
reactive functional groups-substituted polysilsesquioxane in the
photocurable coating composition can be adjusted to from 1% to 25%
by weight, from 1% to 20% by weight, from 1% to 15% by weight, or
from 1% to 10% by weight based on the solid content of the photo
curable coating composition.
[0046] If the content of the one or more reactive functional
groups-substituted polysilsesquioxane is less than the
above-described range, it may be difficult to sufficiently ensure
the alkali resistance or scratch resistance of the coating film or
the polymer resin which is formed during a photo-curing process of
the photocurable coating composition. Meanwhile, if the content of
the one or more reactive functional groups-substituted
polysilsesquioxane exceeds the above-described range, the
transparency of the low refractive layer prepared from the
photocurable coating composition may be lowered and the scratch
resistance can be rather reduced.
[0047] The reactive functional group which can be substituted in
the polysilsesquioxane may include one or more functional groups
selected from the group consisting of alcohol, amine, carboxylic
acid, epoxide, imide, (meth)acrylate, nitrile, norbornene, olefin
(allyl, cycloalkenyl or vinyl dimethyl silyl, etc.], polyethylene
glycol, thiol and vinyl groups. Preferably, it may include epoxide
or (meth)acrylate.
[0048] More specifically, when the reactive functional group is an
epoxide, 2-[3,4-epoxycyclohexyl]ethyl group 3-glycidoxypropyl group
or the like can be introduced as the reactive functional group.
When the reactive functional group is (meth)acrylate,
(meth)acryloyloxy alkyl group (wherein the alkyl group may have 1
to 6 carbon atoms) or the like can be introduced as the reactive
functional group.
[0049] Even if polysilsesquioxane includes the same functional
group as a photopolymerizable compound as a reactive functional
group, polysilsesquioxane with a siloxane bond (--Si--O--) as
skeleton is defined as not including in the photopolymerizable
compound.
[0050] On the other hand, the one or more reactive functional
groups-substituted polysilsesquioxanes may be further substituted
with one or more non-reactive functional groups selected from the
group consisting of a straight chain or branched alkyl group having
1 to 30 carbon atoms, a cycloalkyl group having 6 to 30 carbon
atoms and an aryl group having 6 to 30 carbon atoms, in addition to
the above-described reactive functional group. In this way, as the
surface of the polysilsesquioxane is substituted by a reactive
functional group and a non-reactive functional group, a siloxane
bond (--Si--O--) in the one or more reactive functional
groups-substituted polysilsesquioxane is located within the
molecule and thus not exposed to the outside, thereby further
improving the alkali resistance of a coating film or a polymer
resin formed during the photo-curing process of the photocurable
coating composition. In particular, when the non-reactive
functional group, which is introduced together with a reactive
functional group in the polysilsesquioxane, is a straight chain or
branched alkyl group having 6 or more carbon atoms; a straight
chain or branched alkyl group having 6 to 30 carbon atoms; or a
cycloalkyl group having 6 to 30 carbon atoms, the alkali resistance
of the low refractive layer can be further improved.
[0051] The polysilsesquioxane can be represented by
(RSiO.sub.1.5).sub.n (wherein n is from 4 to 30 or from 8 to 20,
each R is independently a reactive functional group; or a
non-reactive functional group selected from the group consisting of
a straight chain or branched alkyl group having 1 to 30 carbon
atoms, a cycloalkyl group having 6 to 30 carbon atoms and an aryl
group having 6 to 30 carbon atoms), and may have various structures
such as random, ladder, cage and partial cage types.
[0052] Among them, in order to further improve the above-described
characteristics, as the polysilsesquioxane substituted by one or
more reactive functional groups, polyhedral oligomeric
silsesquioxane substituted by one or more reactive functional
groups and having a cage structure can be used.
[0053] More specifically, the polyhedral oligomeric silsesquioxane
may include 8 to 20 silicones in the molecular.
[0054] Examples of the polyhedral oligomeric silsesquioxane (POSS)
substituted by one or more reactive functional groups and having a
cage structure may include one or more alcohols-substituted POSS
such as TMP DiolIsobutyl POSS, Cyclohexanediol Isobutyl POSS,
1,2-PropanediolIsobutyl POSS, Octa(3-hydroxy-3
methylbutyldimethylsiloxy) POSS; one or more amines-substituted
POSS such as AminopropylIsobutyl POSS, AminopropylIsooctyl POSS,
Aminoethylaminopropyl Isobutyl POSS, N-Phenylaminopropyl POSS,
N-Methylaminopropyl Isobutyl POSS, OctaAmmonium POSS,
AminophenylCyclohexyl POSS, AminophenylIsobutyl POSS; one or more
carboxylic acids-substituted POSS such as Maleamic Acid-Cyclohexyl
POSS, Maleamic Acid-Isobutyl POSS, Octa Maleamic Acid POSS; one or
more epoxides-substituted POSS such as EpoxyCyclohexylIsobutyl
POSS, Epoxycyclohexyl POSS, Glycidyl POSS, GlycidylEthyl POSS,
GlycidylIsobutyl POSS, GlycidylIsooctyl POSS; one or more
amides-substituted POSS such as POSS Maleimide Cyclohexyl, POSS
Maleimide Isobutyl; one or more (meth)acrylates-substituted POSS
such as AcryloIsobutyl POSS, (Meth)acrylIsobutyl POSS,
(Meth)acrylate Cyclohexyl POSS, (Meth)acrylate Isobutyl POSS,
(Meth)acrylate Ethyl POSS, (Meth)acrylEthyl POSS, (Meth)acrylate
Isooctyl POSS, (Meth)acrylIsooctyl POSS, (Meth)acrylPhenyl POSS,
(Meth)acryl POSS, Acrylo POSS; one or more nitrile
groups-substituted such as CyanopropylIsobutyl POSS; one or more
norbornene groups-substituted POSS such as NorbornenylethylEthyl
POSS, NorbornenylethylIsobutyl POSS, Norbornenylethyl
DiSilanoIsobutyl POSS, Trisnorbornenyl Isobutyl POSS; one or more
vinyl groups-substituted POSS such as AllylIsobutyl POSS,
MonoVinylIsobutyl POSS, OctaCyclohexenyldimethylsilyl POSS,
OctaVinyldimethylsilyl POSS, OctaVinyl POSS; one or more
olefins-substituted POSS such as AllylIsobutyl POSS,
MonoVinylIsobutyl POSS, OctaCyclohexenyldimethylsilyl POSS,
OctaVinyldimethylsilyl POSS, OctaVinyl POSS; POSS substituted with
PEG group having 5 to 30 carbon atoms; one or more thiol
groups-substituted POSS such as MercaptopropylIsobutyl POSS or
MercaptopropylIsooctyl POSS; or the like.
[0055] Further, a reactive functional group can be introduced in at
least one or more of silicones of the polyhedral oligomeric
silsesquioxane, and silicones having no introduced reactive
functional group may be substituted with the above-described
non-reactive functional group.
[0056] When a reactive functional group is introduced in at least
one or more of silicones of the polyhedral oligomeric
silsesquioxane, it is possible to greatly improve the mechanical
properties of a coating film or a polymer resin formed during the
photo-curing process of the photocurable coating composition. And,
a non-reactive functional group is introduced to the remaining
silicones, a molecular structurally steric hindrance appears and
thereby the possibility of the exposure of a siloxane bond
(--Si--O--) to the outside can be greatly reduced. Thus, it
possible to greatly improve the alkali resistance of a coating film
or a polymer resin formed during the photo-curing of the
photocurable coating composition.
[0057] More specifically, when the polysilsesquioxane is
substituted with both a reactive functional group and a
non-reactive functional group, the molar ratio of as a reactive
functional group to a non-reactive functional group substituted in
the polysilsesquioxane (mole number of the reactive functional
group/mole number of the non-reactive functional group) may be 0.20
or more, or 0.30 or more, and it may be from 0.20 to 6.00, from
0.30 to 4.00, or from 0.40 to 3.00.
[0058] When the ratio between a reactive functional group and a
non-reactive functional group substituted in the polysilsesquioxane
is within the above range, the steric hindrance in the molecule of
the polysilsesquioxane can be maximized, whereby the possibility
that a siloxane bond (--Si--O--) is exposed to the outside is
significantly reduced, thereby greatly improving the mechanical
properties or alkali resistance of a coating film or a polymer
resin formed during the photo-curing of the photo-curable coating
composition.
[0059] The photocurable coating composition comprises a
fluorine-based compound containing
--O--CF.sub.2CF.sub.2--O--CF.sub.3.
[0060] As used herein, the fluorine-based compound refers to a
compound having a weight average molecular weight of at least 2,000
g/mol and substituted with a fluorine. Such a compound is defined
as not including in the definition of the above-described
photopolymerizable compounds.
[0061] In particular, the fluorine-based compound contains
--O--CF.sub.2CF.sub.2--O--CF.sub.3, and thus the low refractive
layer prepared from the photocurable coating composition may have
lower reflectance and improved light transmittance and also it may
have a more improved alkali resistance and scratch resistance.
[0062] The fluorine-based compound contains
--O--(CF.sub.2).sub.n--O-- (wherein n is an integer of 1 to 3) and
--O--CF.sub.2CF.sub.2CF.sub.3 together with
--O--CF.sub.2CF.sub.2--O--CF.sub.3, thereby more improving the
above-described physical properties.
[0063] The fluorine-based compound introduces one or more
photoreactive functional groups, and the photoreactive functional
group refers to a functional group that can participate in a
polymerization reaction by irradiation with light, for example, by
irradiation with visible light or ultraviolet light. The
photoreactive functional group may include various functional
groups known to be able to participate in the polymerization
reaction by light irradiation, and specific examples thereof may
include (meth)acryloyl group, epoxy group, vinyl group or mercapto
group, and the like.
[0064] The fluorine-based compound may have a fluorine content of
1% to 25% by weight. If the content of fluorine in the
fluorine-based compound is less than the above range, the fluorine
component is not sufficiently arranged on the surface of the final
product obtained from the photocurable coating composition, and
thus it may be difficult to sufficiently secure the physical
properties such as alkali resistance. If the content of fluorine in
the fluorine-based compound exceeds the above range, the surface
properties of the final product obtained from the photocurable
coating composition is lowered or the incidence of defective
products during subsequent process for obtaining the final products
can be increased.
[0065] The fluorine-based compound may further include a silicone;
or a side chain or a repeating unit derived from the silicone
compound. When the fluorine-based compound includes a silicone, or
a side chain or a repeating unit derived from the silicone
compound, the content of silicone may be from 0.1% to 20% by weight
relative to the fluorine-based compound. The silicone contained in
the fluorine-based compound serves to prevent the occurrence of
haze on the low refractive layer obtained from the photocurable
coating composition of the embodiment of the invention, thus
increasing the transparency. On the other hand, when the content of
silicon in the fluorine-based compound exceeds the above range, the
alkali resistance of the low refractive layer obtained from the
photocurable coating composition can be lowered.
[0066] The fluorine-based compound may have a weight average
molecular weight of 2,000 to 200,000 g/mol. If the weight average
molecular weight of the fluorine-based compound is too small, the
low refractive layer obtained from the photocurable coating
composition may not have sufficient alkali resistance. In addition,
when the weight average molecular weight of the fluorine-based
compound is too large, the low refractive layer obtained from the
photocurable coating composition may not have sufficient durability
and scratch resistance. The weight average molecular weight as used
herein refers to a converted value with respect to a standard
polystyrene as measured by GPC (Gel Permeation Chromatograph).
[0067] Specifically, the fluorine-based compound may include i) an
aliphatic compound or an alicyclic compound substituted by one or
more photoreactive functional groups, in which at least one
hydrogen is replaced by fluorine; ii) a silicon-based compound in
which one or more carbons of the aliphatic compound or the
alicyclic compound are substituted by silicone; iii) a
siloxane-based compound in which one or more carbons of the
aliphatic compound or the alicyclic compound are substituted by
silicone and one or more --CH.sub.2-- is substituted by oxygen; iv)
fluoropolyether in which one or more --CH.sub.2-- of the aliphatic
compound or the alicyclic compound is substituted by oxygen; or a
mixture or a copolymer of two or more of these compounds.
[0068] For the low refractive layer to exhibit an alkali resistance
at high temperature to such an extent that the above formula 1 is
satisfied, a sufficient quantity of fluorine should be distributed
on the surface of the low refractive layer so that an alkali
solution is not penetrated or absorbed into the low refractive
layer. Even if an alkali solution is penetrated or absorbed into
the low refractive layer, the crosslinking density should be high
so as to withstand such an alkali solution.
[0069] A cured product of the fluorine-based compound is
distributed on the surface of the low refractive layer of the
present invention and thus, even if treated with an alkali, it is
possible to prevent an alkali solution from penetrating or
absorbing into the low refractive layer. However, the
fluorine-based compound has a larger molecular weight as compared
with the photopolymerizable compound described above and has a
lower amount of photoreactive functional groups relative to the
same volume or weight. Thus, when the content of the
photopolymerizable compound reduces and the content of the
fluorine-based compound increases, there is a tendency that the
crosslinking density of the low refractive layer is lowered.
[0070] Therefore, when a cured product of the fluorine-based
compound is presented in an excessive amount from the surface to
the inside of the low refractive layer, the crosslinking density of
the low refractive layer is lowered and thus it is difficult to
exhibit excellent alkali resistance.
[0071] For the low refractive layer to exhibit an alkali resistance
at a high temperature to such an extent that the above formula 1 is
satisfied, the cured product of the fluorine-based compound should
be mostly presented on the surface of the low refractive layer. For
the cured product of the fluorine-based compound to mostly present
on the surface of the low refractive layer, it is important to
adjust the content of the fluorine-based compound in the
photocurable coating composition.
[0072] Specifically, the photocurable coating composition may
include 1 to 75 parts by weight, 1 to 50 parts by weight, 1 to 30
parts by weight, 1 to 20 parts by weight or 1 to 15 parts by weight
of a fluorine-based compound, based on 100 parts by weight of the
photopolymerizable compound. In addition, the content of the
fluorine-based compound in the photocurable coating composition can
be adjusted from 0.5% to 50% by weight, from 0.5% to 30% by weight,
from 0.5% to 20% by weight or from 1% to 15% by weight relative to
the solid content of the photocurable coating composition.
[0073] When the fluorine-based compound is in an excessive amount
relative to the photopolymerizable compound, the coating property
of the photocurable coating composition is decreased or the
crosslinking density of the low refractive layer obtained from the
photocurable coating composition is decreased, and thus it is not
possible to exhibit sufficient alkali resistance, durability,
scratch resistance or the like. In addition, when the amount of the
fluorine-based compound is too small relative to the
photopolymerizable compound, a sufficient amount of fluorine is not
distributed on the surface of the low refractive layer obtained
from the photocurable coating composition and thus the low
refractive layer may not have sufficient alkali resistance.
[0074] On the other hand, the photocurable coating composition
includes inorganic particles having a diameter in the nanometer or
micrometer units.
[0075] Specifically, the inorganic particle may be a hollow silica
particle having a number average particle diameter of 10 to 100 nm.
And the hollow silica particle is a silica particle that is derived
from the silicon compound or an organic silicon compound and refers
to a silica particle in which a free space is present in the
surface and/or the inside of the particle. The hollow silica
particle has a lower refractive index as compared with a non-hollow
particle, thus exhibiting excellent antireflection properties.
[0076] The inorganic particle may have a number average particle
diameter of 10 to 100 nm, 20 to 70 nm, or 30 to 70 nm, and the
shape of the particle is preferably spherical, but it may be
amorphous.
[0077] Further, as the inorganic particle, a particle that is
surface-coated with a fluorine-based compound can be used alone, or
it can be used in combination of the inorganic particle that is not
surface-coated with a fluorine-based compound. When the surface of
the inorganic particle is coated with a fluorine-based compound, it
can more reduce the surface energy and thus, the inorganic particle
can be more uniformly distributed in the photocurable coating
composition. Accordingly, the film obtained from the photocurable
coating composition comprising such inorganic particle can exhibit
more improved durability and scratch resistance.
[0078] As the method for coating a fluorine-based compound to the
surface of the inorganic particle, a particle coating method or a
polymerization method or the like which are generally known can be
used without any particular limitation. As a non-limiting example,
a method of reacting the inorganic particle and the fluorine-based
compound in the presence of water and catalyst through a sol-gel
process and then attaching the fluorine-based compound to the
surface of the inorganic particle through a hydrolysis and
condensation reaction, and the like can be used.
[0079] Further, the inorganic particle may be included in the
composition as a colloidal phase dispersed in a predetermined
dispersion medium. The colloidal phase containing the inorganic
particle may include an organic solvent as a dispersion medium.
[0080] In the colloidal phase of the inorganic particle, the amount
of the solid content of the inorganic particle may be determined in
consideration of the content range of the inorganic particles in
the photocurable coating composition or the viscosity of the
photocurable coating composition or the like. As an example, the
amount of the solid content of the inorganic particle in the
colloidal phase may be 5% to 60% by weight.
[0081] Here, as the organic solvent in the dispersion medium,
alcohols such as methanol, isopropyl alcohol, ethylene glycol,
butanol; ketones such as methyl ethyl ketone, methyl isobutyl
ketone; aromatic hydrocarbons such as toluene, xylene; amides such
as dimethylformamide, dimethylacetamide, N-methylpyrrolidone;
esters such as ethyl acetate, butyl acetate, gamma-butyrolactone;
ethers such as tetrahydrofuran, 1,4-dioxane; or a mixture thereof
may be used.
[0082] The photocurable coating composition may include the
inorganic particle in an amount of 10 to 320 parts by weight, 20 to
200 parts by weight or 30 to 200 parts by weight based on 100 parts
by weight of the photopolymerizable compound. In addition, the
content of the inorganic particle in the photocurable coating
composition can be adjusted to 10% to 80% by weight, 20% to 70% by
weight or 20% to 60% by weight relative to the solid content of the
photocurable coating composition.
[0083] If the inorganic particle is excessively added, a scratch
resistance or a wear resistance of the coating film may be lowered
due to a decrease in the content of the polymer resin.
[0084] As the photopolymerization initiator, any compound can be
used without particular limitation as long as it is known that the
compound is generally used in the photocurable coating composition.
Specifically, benzophenone-based compounds, acetophenone-based
compounds, non-imidazole-based compounds, triazine-based compounds,
oxime-based compound, or mixtures of two or more of these compounds
can be used.
[0085] The photopolymerization initiator can be used in an amount
of 1 to 100 parts by weight, 1 to 50 parts by weight or 1 to 20
parts by weight based on 100 parts by weight of the
photopolymerizable compound. Further, the content of the
photopolymerization initiator in the photocurable coating
composition can be adjusted to 0.1% to 15% by weight, 1% to 10% by
weight or 3% to 7% by weight relative to the solid content in the
photocurable coating composition.
[0086] When the amount of the photopolymerization initiator is too
small, it can cause uncured coating during the photo-curing step of
the photocurable coating composition, thereby occurring a residual
material. When the amount of the photopolymerization initiator is
too large, the unreacted initiator remains as impurities or the
crosslinking density is lowered, and thus the mechanical properties
of the produced film may decrease or the reflectance may increase
greatly.
[0087] On the other hand, the photocurable coating composition can
further comprise an organic solvent. Non-limiting examples of the
organic solvent, may include ketones, alcohols, acetates and
ethers, or mixtures of two or more thereof. Specific examples of
such organic solvent may include ketones such as methyl ethyl
ketone, methyl isobutyl ketone, acetyl acetone or isobutyl ketone;
alcohols such as methanol, ethanol, n-propanol, iso-propanol,
n-butanol, iso-butanol, or t-butanol; acetates such ethyl acetate,
iso-propyl acetate, or polyethylene glycol monomethyl ether
acetate; ethers such as tetrahydrofuran or propylene glycol
monomethyl ether; or mixtures of two or more thereof.
[0088] The organic solvent is added at a time point when mixing the
respective components contained in the photocurable coating
composition or it can be contained in the photocurable coating
composition while the respective components are added in a
dispersed or mixed state. When the content of the organic solvent
in the photocurable coating composition is too small, the
flowability of the photocurable coating composition is decreased
and thus defects may occur, for example, a stripe pattern is
generated in the film finally produced. Further, when the organic
solvent is excessively added, the amount of the solid content is
lowered and coating and film formation are not sufficient. Thus,
the physical properties or surface properties of the film can be
lowered and further, defects can occur in the drying and curing
process. Accordingly, the photocurable coating composition may
include an organic solvent so that the entire solid content
concentration of the components contained becomes 1 to 50% by
weight or 2 to 20% by weight.
[0089] The photocurable coating composition is coated and
photo-cured according to the method known in the technical field to
which the invention pertains, thereby providing the above-mentioned
low refractive layer.
[0090] First, the photocurable coating composition can be coated on
a predetermined substrate. At this time, specific types or
thickness of the substrate are not particularly limited, and the
substrate known to be used in the preparation of the low refractive
layer can be used without any particular limitation.
[0091] The photocurable coating composition can be coated using the
method and apparatus known in the technical field to which the
invention pertains. For example, the photocurable coating
composition can be coated through a bar coating method such as
Meyer bar, a gravure coating method, a 2 roll reverse coating
method, a vacuum slot die coating method or 2 roll coating
method.
[0092] The low refractive layer may have a thickness of 1 nm to 300
nm or 50 nm to 200 nm. Accordingly, the thickness of the
photocurable coating composition to be coated onto a predetermined
substrate may be adjusted to about 1 nm to 300 nm, or 50 nm to 200
nm.
[0093] After coating onto a photocurable coating composition as
described above, the photocurable coating composition can be
photo-cured by irradiation with ultraviolet light or visible light
in the wavelength range of 200 to 400 nm. At this time, the
exposure amount of light to be irradiated can be adjusted in the
range of 100 to 4,000 mJ/cm.sup.2, and the exposure time may be
appropriately adjusted depending on the exposure apparatus, the
wavelength or the exposure amount of the irradiation light to be
used.
[0094] The photo-curing step can be carried out under a nitrogen
atmosphere. Accordingly, nitrogen purging can be further carried
out before the photo-curing step or during the photo-curing
step.
[0095] The low refractive layer prepared from a photocurable
coating composition as described above may include a polymer resin
containing a cross-linked polymer between a photopolymerizable
compound, a polysilsesquioxane substituted with at least one or
more reactive functional groups, a fluorine-based compound
containing O--CF.sub.2CF.sub.2--O--CF.sub.3, and an inorganic
particle dispersed in the polymer resin.
[0096] However, the low refractive layer of the present invention
is not intended to be formed only by the above-described components
and compositions, and if the above formula 1 is satisfied, the low
refractive layer can be formed by various components and
compositions with reference to the above-described contents.
[0097] On the other hand, according to another embodiment of the
invention, an anti-reflective film comprising a low refractive
layer; and a hard coating layer formed on one surface of the low
refractive layer is provided. The low refractive layer is described
in detail previously, and so detailed description thereof will be
omitted for simplicity.
[0098] As the above hard coating layer, a commonly known hard
coating layer can be employed without particular limitation.
[0099] As an example, the hard coating layer may include a binder
resin containing a photocurable resin and a (co)polymer with the
weight average molecular weight of 10,000 g/mol or more
(hereinafter, referred to as a high molecular weight (co)polymer);
and an organic or inorganic fine particle dispersed in the binder
resin. Herein, the (co)polymer is meant to include both co-polymer
and homo-polymer.
[0100] The high molecular weight (co)polymer may comprise one or
more polymers selected from the group consisting of cellulosic
polymers, acrylic polymers, styrenic polymers, epoxide-based
polymer, nylon-based polymer, polyurethane-based polymer and
polyolefin-based polymer.
[0101] The photocurable resin contained in the hard coating layer
is a polymer the photopolymerizable compound that can cause a
polymerization reaction when irradiated with light such as
ultraviolet light, and those that are conventionally used in the
art to which the invention belongs may be used. Specifically, the
photopolymerizable compound may include one or more selected a
reactive acrylate oligomer group consisting of urethane acrylate
oligomer, epoxide acrylate oligomer, polyester acrylate, and
polyether acrylate; and a polyfunctional acrylate monomer group
consisting of dipentaerythritol hexaacrylate, dipentaerythritol
pentaacrylate, pentaerythritol tetraacrylate, pentaerythritol
triacrylate, trimethylolpropane triacrylate, glycerol propoxylate
triacrylate, trimethylpropane ethoxylate triacrylate,
1,6-hexanediol diacrylate, tripropylene glycol diacrylate and
ethylene glycol diacrylate.
[0102] The organic or inorganic fine particles may have a particle
diameter of 1 to 10 .mu.m.
[0103] The organic or inorganic fine particles are organic fine
particles selected from the group consisting of acrylic resin,
styrene-based resin, epoxy-based resin, and nylon-based resin or
inorganic fine particles selected from the group consisting of
silicon oxide, titanium dioxide, indium oxide, tin oxide, zirconium
oxide and zinc oxide.
[0104] The hard coating layer can be formed from a coating
composition comprising an organic or inorganic fine particle, a
photopolymerizable compound, a photo-initiator and a high molecular
weight (co)polymer. The anti-reflective film comprising such a hard
coating layer has excellent anti-glare effect.
[0105] On the other hand, as another example of the hard coating
layer, a hard coating layer comprising a binder resin containing a
photocurable resin; and an antistatic agent dispersed in the binder
resin can be mentioned.
[0106] The photocurable resin contained in the hard coating layer
is a polymer of a photopolymerizable compound that can cause a
polymerization reaction when irradiated with light such as
ultraviolet light, and those that are conventionally used in the
art to which the invention belongs may be used. Specifically, the
photopolymerizable compound that may be used herein includes a
polyfunctional (meth)acrylate-based monomer or oligomer, wherein
the number of the (meth)acrylate-based functional groups can be
adjusted to 2 to 10, 2 to 8 or 2 to 7, thereby ensuring the desired
physical properties of the hard coating layer. More specifically,
the photopolymerizable compound can include one or more selected
from the group consisting of pentaerythritol tri(meth)acrylate,
pentaerythritol tetra(meth)acrylate, dipentaerythritol
penta(meth)acrylate, dipentaerythritol hexa(meth)acrylate,
tripentaerythritol hepta(meth)acrylate, toluene diisocyanate,
xylene diisocyanate, hexamethylene diisocyanate, trimethylolpropane
tri(meth)acrylate, and trimethylolpropane polyethoxy
tri(meth)acrylate.
[0107] The antistatic agent may be a quaternary ammonium salt
compound, a conductive polymer, or a mixture thereof. Here, the
quaternary ammonium salt compound may be a compound having at least
one quaternary ammonium salt in a molecule, and a low molecular
type or a polymer type can be used without limitation. Thus, as the
conductive polymer, a low molecular type or a polymer type can be
used without limitation, and the type thereof may be conventional
in the technical field to which the invention pertains, and thus it
is riot particularly limited.
[0108] The hard coating layer comprising a binder resin of the
photocurable resin; and an antistatic agent dispersed in the binder
resin can further include one or more compounds selected from the
group consisting of an alkoxysilane-based oligomer and a metal
alkoxide-based oligomer.
[0109] The alkoxy silane-based compound may be conventional in the
art, but preferably, it may be one or more compounds selected from
the group consisting of tetramethoxysilane, tetraethoxysilane,
tetraisopropoxysilane, methyltrimethoxysilane,
methyltriethoxysilane, methacryloxypropyltrimethoxysilane,
glycidoxypropyltrimethoxysilane, and
glycidoxypropyltriethoxysilane.
[0110] In addition, the metal alkoxide-based oligomer can be
prepared through the sol-gel reaction of the composition containing
metal alkoxide-based compound and water. The sol-gel reaction can
be carried out by a method similar to the method for preparing
alkoxysilane-based oligomer as described above.
[0111] However, the metal alkoxide-based compounds can be rapidly
reacted with water, and thus the sol-gel reaction can be carried
out by diluting the metal alkoxide-based compound in an organic
solvent and then slowly adding dropwise water thereto. At this
time, in view of the reaction efficiency, etc., the molar ratio of
metal alkoxide compound to water (based on metal ion) is preferably
adjusted in the range of 3 to 170.
[0112] Here, the metal alkoxide-based compound may be one or more
compounds selected from the group consisting of titanium
tetra-isopropoxide, zirconium isopropoxide and aluminum
isopropoxide.
[0113] On the other hand, the anti-reflective film may further
include a substrate bonded to the other surface of the hard coating
layer. The substrate may be a transparent film having a light
having a light transmittance of 90% or more and a haze value of 1%
or less. Further, the material of the substrate may be triacetyl
cellulose, cycloolefin polymer, polyacrylate, polycarbonate,
polyethylene terephthalate or the like. In addition, the thickness
of the substrate film may be 10 to 300 .mu.m in consideration of
productivity or the like. However, it is not intended to limit the
present invention thereto.
Advantageous Effects
[0114] The low refractive layer according to an embodiment of the
invention can exhibit excellent optical properties such as a low
reflectance and a high light transmittance, and excellent
mechanical properties such as high wear resistance and scratch
resistance at the same time, without adversely affecting the color
of the polymer resin. In particular, due to the excellent alkali
resistance, the low refractive layer can exhibit the excellent
physical properties even after alkali treatment. Therefore, when
introducing a low refractive layer to the display device, it is
expected that the production process can be simplified and further
the production rate and the productivity can significantly
increase.
BRIEF DESCRIPTION OF DRAWINGS
[0115] FIG. 1 is a graph showing the reflectance according to the
wavelength of the anti-reflective film prepared in Example 1.
[0116] FIG. 2 is a graph showing the reflectance according to the
wavelength of the anti-reflective film prepared in Example 2.
[0117] FIG. 3 is a graph showing the reflectance according to the
wavelength of the anti-reflective film prepared in Example 3.
[0118] FIG. 4 is a graph showing the reflectance according to the
wavelength of the anti-reflective film prepared in Comparative
Example 1.
[0119] FIG. 5 is a graph showing the reflectance according to the
wavelength of the anti-reflective film prepared in Comparative
Example 2.
[0120] FIG. 6 is a graph showing the reflectance according to the
wavelength of the anti-reflective film prepared in Comparative
Example 3.
[0121] FIG. 7 is a graph showing the reflectance according to the
wavelength of the anti-reflective film prepared in Comparative
Example 4.
[0122] FIG. 8 is a graph showing the reflectance according to the
wavelength of the anti-reflective film prepared in Comparative
Example 5.
DETAILED DESCRIPTION OF THE EMBODIMENTS
[0123] Hereinafter, the action and effect of the invention will be
described in detail, through specific examples of the invention.
However, the examples are provided only to illustrate the present
invention, and the scope of the invention is not limited
thereto.
PREPARATION EXAMPLE
Preparation Example 1
Preparation of Hard Coating Film 1 (HD1)
[0124] A salt type of antistatic hard coating solution
(manufactured by KYOEISHA Chemical Co., Ltd., solid content: 50 wt
%, product name: LJD-1000) was coated onto triacetylcellulose film
with #10 mayer bar and dried at 90.degree. C. for one minute,
followed by irradiation with ultraviolet light of 150 mJ/cm.sup.2
to prepare a hard coating film (HD1) having a thickness of 5
.mu.m.
Preparation Example 2
Preparation of Hard Coating Film 2 (HD2)
[0125] 30 g of pentaerythritol triacrylate, 2.5 g of high molecular
weight copolymer (BEAMSET 371, Arakawa Corporation, Epoxy Acrylate,
molecular weight: 40,000), 20 g of methyl ethyl ketone and 0.5 g of
leveling agent (Tego wet 270) were uniformly mixed. Then, 2 g of
acrylic-styrene copolymer (volume average particle size: 2 .mu.m,
manufactured by Sekisui Plastic) with a refractive index of 1.525
as a fine particle was added to the mixture to prepare a hard
coating composition. The hard coating composition thus obtained was
coated onto triacetylcellulose film with a #10 mayer bar and dried
at 90.degree. C. for one minute. The dried product was irradiated
with ultraviolet light of 150 mJ/cm.sup.2 to prepare a hard coating
film (HD2) having a thickness of 5 .mu.m.
Preparation Example 3
Preparation of Polysilsesquioxane 1
[0126] 36.57 g (0.156 mol) of isooctyltrimethoxy silane, 23.34 g
(0.094 mol) of 3-methacryloxypropyl trimethoxysilane and 500 mL of
methanol were added to a 1 L reactor equipped with a nitrogen gas
inlet tube, a condenser and a stirrer, and stirred at room
temperature for 10 minutes. Then, tetramethylammonium hydroxide
(280 g, 0.77 mol, 25 wt % in methanol) was added thereto, and the
reaction was carried out for 8 hours by raising the reactor
temperature under a nitrogen atmosphere to 60.degree. C. After
completion of the reaction, 15 g of polyhedral oligomeric
silsesquioxane (POSS) substituted by an isooctyl group and a
methacryloxypropyl group was obtained through column chromatography
and recrystallization. The confirmation result of GP Chromatography
showed that the molar ratio of a methacryloxypropyl group to an
isooctyl group (mole number of methacryloxypropyl group/mole number
of isooctyl group) which is substituted at silicon of
polysilsesquioxane is about 0.6 to 1.67.
Preparation Example 4
Preparation of Fluorine-Based Compound 2
[0127] After sufficiently replacing with nitrogen gas, a 2.0 L
stainless steel autoclave equipped with an electronic stirrer was
charged with 400 g of ethyl acetate, 53.2 g of perfluoro(propyl
vinyl ether), 36.1 g of ethyl vinyl ether, 44.0 g of hydroxyethyl
vinyl ether, 1.00 g of lauroyl peroxide, 6.0 g of an azo
group-containing polydimethylsiloxane represented by the following
formula 1 (VPS1001 (trade name), Wako Pure Chemical industries,
Ltd.) and 20.0 g of nonionic reactive emulsifier (NE-30 (trade
name), manufactured by Asahi Denka Co., Ltd.) and cooled to
-50.degree. C. in methanol dry-ice bath, and then oxygen within the
system was again removed with nitrogen gas.
##STR00001##
[0128] Then, 120.0 g hexafluoropropylene was added thereto and the
temperature stated to rise. The pressure at a time point when the
temperature in the autoclave reached 60.degree. C. exhibited
5.3.times.10.sup.5 Pa. Thereafter, the reaction was continued while
stirring at 70.degree. C. for 20 hours, and the reaction was
stopped by cooling the autoclave at a time point when the pressure
was reduced to 1.7.times.10.sup.5 Pa. After reaching the room
temperature, the unreacted monomers were released, and the
autoclave was opened to obtain a polymer solution with a solid
content concentration of 26.4%. The resulting polymer solution was
added to methanol to precipitate a polymer, and then washed with
methanol and dried in vacuum at 50.degree. C. to obtain 220 g of a
hydroxyl group-containing fluoropolymer.
[0129] 50.0 g of a hydroxyl group-containing fluoropolymer prepared
previously, 0.01 g of 2,6-di-t-butylmethylphenol as a
polymerization inhibitor and 370 g of methyl isobutyl ketone (MIBK)
were added to a 1 L flask equipped with an electronic stirrer, a
cooling tube made of glass and a thermometer, and then stirred
until the hydroxyl group-containing fluoropolymer was dissolved in
MIBK at 20.degree. C. and the solution became transparent.
[0130] Then, 13.7 g of 2-acryloxyethyl isocyanate was added to the
system and stirred until the solution became homogeneous.
Thereafter, 0.1 g of dibutyltin dilaurate was added thereto and
then stirred for 5 hours while maintaining the temperature in the
system to 55 to 65.degree. C., thereby obtaining a MIBK solution of
the ethylenically unsaturated group-containing fluoropolymer
(acrylic modified fluoropolymer). 2 g of this solution was weighed
and dropped into an aluminum plate, dried for 5 minutes on a hot
plate at 150.degree. C. and re-weighed to calculate the amount of
the solid content. As a result, the amount of the solid content was
15.0 wt %.
EXAMPLES AND COMPARATIVE EXAMPLE, PREPARATION OF ANTI-REFLECTIVE
FILM
(1) Preparation of the Photocurable Coating Composition for the
Production of a Low Refractive Layer
[0131] The ingredients shown in Table 1 were mixed and diluted so
that the solid content in MIBK (methyl isobutyl ketone) solvent
became 3 wt %.
TABLE-US-00001 TABLE 1 LR1 LR2 LR3 LR4 LR5 LR6 Hollow silica
dispersion.sup.1) 220 (44) 130 (26) 220 (44) 130 (26) 220 (44) 40
(8) Trimethylolpropane triacrylate 41 (41) 62 (62) 47 (47) 67 (67)
41 (41) 0 (0) Polysilsesquioxane 1.sup.2) 6 (6) 5 (5) 0 (0) 0 (0) 0
(0) 0 (0) Polysilsesquioxane 2.sup.3) 0 (0) 0 (0) 0 (0) 0 (0) 6 (6)
30 (30) Fluorine-based compound 1.sup.4) 13.333 (4) 6.667 (2)
13.333 (4) 6.667 (2) 0 (0) 0 (0) Fluorine-based compound 2.sup.5) 0
(0) 0 (0) 0 (0) 0 (0) 26.667 (4) 400 (60) Photoinitiator
(Irgacure-127, 5 (5) 5 (5) 5 (5) 5 (5) 5 (5) 2 (2) Ciba Specialty
Chemicals Inc.) (Unit: g; the number in parentheses refers to the
amount of the solid content) .sup.1)Hollow silica dispersion:
THRULYA 4320 in which hollow silica particles with a number average
diameter of 50 nm were dispersed at 20 wt % in MIBK (manufactured
by Catalysts & Chemicals Ind. Co., Ltd.)
.sup.2)Polysilsesquioxane 1: Polysilsesquioxane 1 prepared
according to Preparation Example 3 .sup.3)Polysilsesquioxane 2:
MAC-SQ-F (manufactured by TOAGOSEI CO., Ltd.) .sup.4)Fluorine-based
compound 1: Fluorine-based compound containing a photoreactive
functional group, --O--CF.sub.2CF.sub.2--O--CF.sub.3,
--O--(CF.sub.2).sub.3--O-- and --O--CF.sub.2CF.sub.2CF.sub.3; RS907
(manufactured by DIC Corporation) diluted at 30 wt % in MIBK.
.sup.5)Fluorine-based compound 2: Fluorine-based compound 2 in
which 15 wt % of the solid content was dispersed in MIBK, which was
prepared according to Preparation Example 4.
(2) Preparation of Low Refractive Layer and Anti-Reflective Film
(Examples 1 to 3 and Comparative Examples 1 to 5)
[0132] The respective photocurable coating compositions obtained in
Table 1 were coated onto the hard coating film described in Table 2
below by #3 mayer bar and dried at 60.degree. C. for one minute.
Then, the dried product was irradiated with ultraviolet light of
180 mJ/cm.sup.2 while purging the nitrogen gas to form a low
refractive layer having a thickness of 110 m, thereby preparing a
desired anti-reflective film.
EXPERIMENTAL EXAMPLE
Measurement of Physical Properties of Anti-Reflective Film
[0133] The experiments given in the following items were carried
out for the anti-reflective films obtained in Examples and
Comparative Examples.
[0134] 1. Alkaline Pretreatment
[0135] The respective anti-reflective films obtained in Examples 1
to 3 and Comparative Examples 1 to 5 were immersed in NaOH aqueous
solution (solution in which 10 wt % of NaOH was diluted in
distilled water) at 30.degree. C. for two minutes and washed with
flowing water, and then moisture was wiped off. The anti-reflective
films in which moisture has been wiped off was again immersed in
NaOH aqueous solution (solution in which NaOH was diluted at 10 wt
% in distilled water) at 55.degree. C. for 30 seconds and washed
with flowing water, and then moisture was wiped off.
[0136] 2. Measurement of Reflectance (Y) and Color Coordinate Value
(b*)
[0137] The average reflectance and the color coordinate value of
the anti-reflective films prepared in Examples and Comparative
Examples were measured using SolidSpec 3700 (SHIMADZU) before and
after alkaline pretreatment.
[0138] Specifically, to the surface in which the hard coating layer
of the substrate film was not formed, a black tape was attached so
as to prevent transmission of light, and the measurement conditions
were set as follows: sampling interval 1 nm, time constant 0.1 sec,
slit width 20 nm, medium scanning speed. Then, the low refractive
layer of the anti-reflective film was irradiated with a light in
the wavelength range of 380 nm to 780 nm at room temperature.
[0139] When using HD2 as a hard coating layer, a 100% T mode was
applied. When using HD1 as a hard coating layer, a Measure mode was
applied. Then, the reflectance in the wavelength range of 380 nm to
780 nm was measured. The measurement results of the reflectance in
the wavelength range of 380 nm to 780 nm of the anti-reflective
films prepared in Examples and Comparative Examples were shown in
FIGS. 1-8. In FIGS. 1 to 8, the dotted lines (-) are graphs showing
the reflectance (y-axis) according to the wavelength (x-axis) of
the anti-reflective film before alkali treatment, and solid lines
(-) are graphs showing the reflectance (y-axis) according to the
wavelength (x-axis) of the anti-reflective film after alkali
treatment.
[0140] The average reflectance and the color coordinate value (b*)
in wavelength range of 380 nm to 780 nm of the anti-reflective
films prepared in Examples and Comparative Examples were derived
from the above reflectance through UV-2401PC color analysis program
and shown in Table 2 below.
[0141] 3. Measurement of Scratch Resistance
[0142] The surfaces of the low refractive layers obtained in
Examples and Comparative Examples were rubbed while applying a load
to a grade #0000 steel wool and reciprocating ten times at a speed
of 24 rpm. The maximum load that scratches are generated, as
observed with the naked eye under a LED50W ceiling illumination,
was measured. The load is defined as weight (g) per area (2*2
cm.sup.2) having a width of 2 cm and a length of 2 cm.
TABLE-US-00002 TABLE 2 Compar- Compar- Compar- Compar- Compar-
ative ative ative ative ative Exam- Exam- Exam- Exam- Exam- Exam-
Exam- Exam- ple 1 ple 1 ple 2 ple 2 ple 3 ple 3 ple 4 ple 5 Hard
coating HD2 HD2 HD1 HD1 HD1 HD2 HD2 HD2 layer Low refractive LR1
LR3 LR1 LR3 LR5 LR2 LR4 LR6 layer Wavelength 540~550 480~530
510~540 510~530 550~610 510~520 540~590 560~610 range showing the
minimum reflectance [nm] Average Before 1.23% 1.32% 1.07% 1.20%
1.19% 2.09% 2.00% 2.28% reflectance pretreatment After 1.24% 1.33%
1.01% 1.18% 1.24% 2.15% 2.02% 2.25% pretreatment color Before -3.48
-1.05 -2.27 -2.78 -6.92 -1.04 -2.62 -2.30 coordinate pretreatment
value (b*.sub.0) (b*) After -3.04 -0.15 -1.84 -1.93 -5.87 -0.74
-1.54 -0.86 pretreatment (b*.sub.1) .DELTA.b* = b*.sub.1 - b*.sub.0
0.44 0.9 0.43 0.85 1.05 0.3 1.08 1.44 Scratch Before 350 200 400
150 200 600 500 450 resistance pretreatment [unit: g/(2*2
cm.sup.2)] After 250 50 350 50 100 600 300 250 pretreatment [unit:
g/(2*2 cm.sup.2)] .DELTA.S = [(S.sub.0 - S.sub.1)/ 28.57% 75.00%
12.50% 66.67% 50.00% 0.00% 40.00% 44.44% S.sub.0] .times. 100
[0143] Referring to Table 2 and FIGS. 1 to 8, it was confirmed that
the anti-reflective films of Examples 1 and 2 exhibited a
significantly low reflectance and a high scratch resistance in the
visible light range (480 to 680 nm) and these characteristics
maintained superior levels even after the alkali treatment. In
contrast, the anti-reflective films of Comparative Examples 1 to 3
exhibited poor scratch resistance, in particular, the scratch
resistance was remarkably degraded after the alkali treatment.
[0144] On the other hand, it was confirmed that the anti-reflective
films of Example 3 and Comparative Examples 4 and 5 have achieved
high scratch resistance by reducing the content of the hollow
silica contained in the low refractive layer, but similarly, the
anti-reflective films of Comparative Examples 4 and 5 exhibited a
remarkably degraded scratch resistance even after the alkali
treatment.
[0145] Accordingly, it was confirmed that only when using the low
refractive layer satisfying the specific conditions of the present
invention, the low refractive layer exhibited excellent alkali
resistance, thus providing the anti-reflective films showing little
change in physical properties before and after the alkali
treatment. In particular, although such a low refractive layer was
exposed to an alkali according to the preparation process of the
polarizing plate, there was less reduction in optical properties
such as reflectance and transmittance or in mechanical properties
such as wear resistance or scratch resistance. Therefore, it was
possible to omit the application of additional protective films for
the outer surface protection, and thus the production process was
simplified and production costs were reduced. In addition, since
the low refractive layer maintained excellent optical and
mechanical properties even in the alkali treatment at high
temperature, they are expected to contribute greatly to the
improvement of productivity and production rate.
* * * * *